JPH031943A - Granite-like molded product with superior resistance to boiling water - Google Patents
Granite-like molded product with superior resistance to boiling waterInfo
- Publication number
- JPH031943A JPH031943A JP13473889A JP13473889A JPH031943A JP H031943 A JPH031943 A JP H031943A JP 13473889 A JP13473889 A JP 13473889A JP 13473889 A JP13473889 A JP 13473889A JP H031943 A JPH031943 A JP H031943A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- resin
- granite
- frp
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明はゲルコート層とＦＲＰ層を通して、不透明で
均一な御影調人造大理石部が透視でき、耐熱水性に優れ
た人造大理石の製造方法に関するものである。特に、本
発明は浴槽等の如く立面を有する成形体を熱硬化性樹脂
で成形する際に、自然な御影調を与える製造方法を提供
するものである。[Detailed Description of the Invention] [Industrial Field of Application] This invention relates to a method for manufacturing artificial marble that has an opaque and uniform granite-like artificial marble part that can be seen through a gel coat layer and an FRP layer and has excellent hot water resistance. be. In particular, the present invention provides a manufacturing method that gives a natural shading tone when molding a molded body having an vertical surface, such as a bathtub, using a thermosetting resin.
浴槽等を熱硬化性樹脂で製造する方法については、従来
から種々の方法が知られている９例えば特開昭４９−１
０７３７７号は、金型面に骨材入りのポリエステルモル
タルを流し込むことによる製造方法を開示している。ま
た透明な大理石を有する合成樹脂成形品の製造について
は、日本特許第１４１８６８３号が知られており、有機
または無機のフィラーやトナーを配合した熱硬化性樹脂
を型内に注入して硬化させることによって、天然の大理
石模様を示す成形体を製造する方法を開示している。Various methods have been known for manufacturing bathtubs and the like using thermosetting resins.
No. 07377 discloses a manufacturing method by pouring polyester mortar with aggregate into the mold surface. Furthermore, Japanese Patent No. 1418683 is known for producing synthetic resin molded products with transparent marble, which involves injecting a thermosetting resin containing organic or inorganic fillers and toner into a mold and curing it. discloses a method for producing a molded article exhibiting a natural marble pattern.
これらの公知技術においては、立面がなく水平面に成形
する場合、また立面があってもフィラーやトナーが微細
粒子であったり、比重差が小さく重力による分離がない
場合は問題ないが、成形体が立面を有しかつ骨材の比重
が大きい場合は、骨材の分離が問題になる。特に、石目
調成形体、例えば御影石のような御影調を有する成形体
を製造する場合には、骨材として０．３〜５ｘｘ程度の
粒径の大きい無機物もしくはプラスチック粉砕物の、無
着色および着色品を配合したレジンコンクリートを使用
して成形するが、たいていの場合、コンパウンドとの比
重差が大であるばかりでなく、骨材間の比重差が大であ
るために自然沈降があり、硬化が完了する前に骨材の分
散に偏りが生じ、均一な調子の御影調模様を出すことが
困難であった。In these known techniques, there is no problem when molding is performed on a horizontal surface without vertical surfaces, or even if there is an vertical surface, if the filler or toner is fine particles or the difference in specific gravity is small and there is no separation due to gravity, molding When the body has an elevation and the specific gravity of the aggregate is high, separation of the aggregate becomes a problem. In particular, when producing a stone-grained molded body, for example, a molded body with a granite tone such as granite, uncolored and Resin concrete mixed with colored products is used to form the concrete, but in most cases there is not only a large difference in specific gravity from the compound, but also a large difference in specific gravity between the aggregates, which causes natural settling and hardening. Before the process was completed, the aggregate became unevenly distributed, making it difficult to produce a uniformly textured pattern.
このため、安易な解決方法としては、レジンコンクリー
トのコンパウンドと同じ比重のプラスチック粒子の着色
品を使用する方法も考えられるが、高価であったり、色
調が不自然であったり、コンパウンド比重に合わせるの
はかなり大変な作業である。Therefore, an easy solution could be to use colored plastic particles with the same specific gravity as the resin concrete compound, but this would be expensive, the color tone would be unnatural, or it would be difficult to match the specific gravity of the compound. is quite a difficult task.
また御影調の人造大理石を、浴槽等のような温水、熱水
を取り扱う環境下で使用する場合、第１層のゲルコート
のみでは、人造大理石部に含まれるフィラー類、骨材へ
の水の浸透が懸念され、−船釣に耐熱水性が悪くなると
ともに、気泡の偉績膨張等によりゲルコートにフクレ、
クラック、変色を引き起こす問題が生ずる。In addition, when using Mikage-style artificial marble in an environment where hot water or hot water is handled, such as in a bathtub, the first layer of gel coat alone will not allow water to penetrate into the fillers and aggregate contained in the artificial marble. - There is a concern that the hot water resistance for boat fishing will deteriorate, and the gel coat will become blistered due to the expansion of air bubbles.
Problems arise that cause cracks and discoloration.
本発明はこれらの点を克服し、耐熱水性に優れた御影調
成形体、およびその製造方法を提供するものである。The present invention overcomes these problems and provides a grain-like molded article with excellent hot water resistance and a method for producing the same.
すなわち本発明の一つは、第１層としてのゲルコート層
、第２層としての熱硬化性樹脂を３０ｇ〜６００ｙ／ｍ
２のガラス繊維もしくは不織布に含浸した透明なＦＲＰ
層、第３層としての不透明な御影調のレジンコンクリー
ト、および第４層としてのＦＲＰバックアップ層からな
る、耐熱水性に優れた御影調成形体を提供するものであ
る。That is, one of the aspects of the present invention is that the gel coat layer as the first layer and the thermosetting resin as the second layer are mixed in an amount of 30 g to 600 y/m.
2. Transparent FRP impregnated with glass fiber or nonwoven fabric
The object of the present invention is to provide a granite-like molded article having excellent hot water resistance, which is composed of an opaque granite-like resin concrete as a third layer, and an FRP backup layer as a fourth layer.
さらに本発明の他の一つは、水平巾に対する高さの比が
、０．１／１以上であり、かつ水平巾が４００ｍｍ以上
で高さが４０１１以トである立面を有する成形体を製造
する方法において、成形体の一面を規制する第１の型の
表面に、第１層としての透明なゲルコート層、第２層と
しての熱硬化性樹脂を３０ｇ〜６００Ｉ？／ｍ”のガラ
ス繊維もしくは不織布に含浸した透明なＦＲＰ層を順次
形成し、成形体の他の一面の規制する第２の型の表面に
、第４層としてのＦＲＰバックアップ層を形成し、該第
１および第２の型により規制される空間に、第３層とし
てのレジンコンクリートが］００重量部の合成樹脂およ
び２種以上の色で大きさ０．３〜５ｉｉ＋の骨材１０〜
３００重量部を含み、揺変性を有したレジンコンクリー
トを注入することからなる、御影調成形体の製造方法を
提供するものである。Furthermore, another aspect of the present invention provides a molded body having an elevational surface having a height to horizontal width ratio of 0.1/1 or more, a horizontal width of 400 mm or more, and a height of 4011 mm or more. In the manufacturing method, a transparent gel coat layer as a first layer and a thermosetting resin as a second layer are placed on the surface of a first mold that regulates one side of a molded article, in an amount of 30 g to 600 I? /m'' of transparent FRP layers impregnated with glass fiber or nonwoven fabric, and an FRP backup layer as a fourth layer is formed on the surface of the second mold, which controls the other side of the molded object. Resin concrete as a third layer is placed in the space regulated by the first and second molds] 00 parts by weight of synthetic resin and aggregates of size 0.3 to 5ii+ in two or more colors.
300 parts by weight of resin concrete having thixotropy is injected into the molded body.
本発明の成形体およびその製造方法を、以下に浴槽を例
にとり説明する。The molded article of the present invention and its manufacturing method will be explained below using a bathtub as an example.
浴槽は基本的には、浴槽の内部表面の形状を規制する雄
型と外部表面を規制する雌型を使用し、雌雄型をセット
し、その空間にレジンコンクリートを注入する方法と、
レジンコンクリートを雌型に入れ雄型を雌をに押し込む
コールドプレス法で成形する方法がある。Bathtubs are basically made using a male mold that regulates the shape of the internal surface of the bathtub and a female mold that regulates the external surface.
There is a cold press method in which resin concrete is placed in a female mold and a male mold is pushed into the female mold.
本発明においては、まず雄型に透明なゲルコートを均一
に塗布する（以下第１層と称する）。塗布の方法は従来
の任意の方法でよいが、スプレー塗装が便利である０次
に第２Ｎとしては透明なＦＲＰを積層する。この方法と
しては、透明な樹脂を使用して、マットを積層もしくは
スプレーアップする方法があるが、形状的にスプレーア
ップ成形の法が適しており、便利である。また別に第４
層はバックアツプ層であるので、透明な樹脂を特に使用
する必要はなく、−最的な樹脂を使用してもよい。第２
層に使用した積層方法を採るのが一般的である。また第
４層は第１、第２、第３層の成形脱型後必要に応じて積
層をしてもよい。In the present invention, first, a transparent gel coat is uniformly applied to the male mold (hereinafter referred to as the first layer). Any conventional coating method may be used, but transparent FRP is laminated as the 0th and 2nd N layers, for which spray painting is convenient. This method includes laminating or spraying mats using transparent resin, but spray-up molding is suitable and convenient in terms of shape. There is also a fourth
Since the layer is a back-up layer, it is not necessary to specifically use a transparent resin; any suitable resin may be used. Second
It is common to use the lamination method used for layers. Further, the fourth layer may be laminated as necessary after molding and demolding the first, second, and third layers.
上記の成形で施した雄型、雌型をセットし、その空間に
２種以上の色で、大きさ０．３〜５ｚｘの骨材を１０〜
３００重量部を含み、横変性を有したレジンコンクリー
トを注入する。このレジンコンクリートは、不飽和ポリ
エステル等の横変性を有した樹脂あるいはレジンに横変
性を付与する無機質、フィラー、有機物を添加したもの
である。Set the male mold and female mold made in the above molding process, and fill the space with 10 to 10 aggregates of size 0.3 to 5zx in two or more colors.
A resin concrete containing 300 parts by weight and having lateral modification is poured. This resin concrete is made by adding inorganic substances, fillers, and organic substances to impart lateral modification to a resin or resin having lateral modification such as unsaturated polyester.
この状態では、御影調を形成する０、３〜５■の大きさ
の骨材は下方に沈降することもなく、均一な態様で、骨
材、粒子が見える御影石側を有する浴槽が得られる。In this state, the aggregate with a size of 0.3 to 5 cm, which forms the granite tone, does not settle downward, and a bathtub having a granite side where the aggregate and particles can be seen in a uniform manner is obtained.
この浴槽は熱硬化性樹脂を主体として形成され、表面に
はゲルコートおよびクリアーな中間層、背面には補強の
ＦＲＰバックアップ層があるため、耐熱水性、機械的強
度ともに、浴槽としては十分満足できるものである。This bathtub is mainly made of thermosetting resin, and has a gel coat and clear intermediate layer on the surface, and a reinforcing FRP backup layer on the back, so it has sufficient hot water resistance and mechanical strength as a bathtub. It is.
本発明の第１層に使用するゲルコートは、成形品の表面
の平滑性や光沢をもたらし、その第３層の御影調模様が
透視でき、かつ十分な耐熱水性と表面硬度を有するもの
でなければならない。The gel coat used for the first layer of the present invention must provide smoothness and gloss to the surface of the molded product, allow the granite pattern of the third layer to be seen through, and have sufficient hot water resistance and surface hardness. No.
このようなゲルコート剤として、通常ビニルエステル、
ビスフェノール、イソ系の樹脂がよく塗布量は４００〜
１０００ｇ／ｌ１１２、厚さ０．１〜０．５ＩＩＩが好
適である。Such gel coat agents usually include vinyl esters,
Bisphenol and iso-based resins are good, and the coating amount is 400~
1000g/l112 and thickness 0.1-0.5III are suitable.
第２層に使用する樹脂は、透明性を有し、かつ御影調人
造大理石の耐熱水性の低さを補うための樹脂であり、通
常のＦＲＰであってもよい。The resin used for the second layer is a resin that has transparency and is used to compensate for the low hot water resistance of the granite-like artificial marble, and may be ordinary FRP.
第３Ｎに使用するレジンコンクリートは、熱硬化性樹脂
を主成分として、これらに無機質、フィラーおよび０．
３〜５ｚｘの骨材を１０〜３００重量部を入れ、さらに
レジンコンクリートに横変性をもたせたものである。レ
ジンコンクリート用の樹脂は、樹脂自体が横変性である
か、あるいは横変性を付与するフィラーや有機物を添加
して、レジンコンクリートの横変性を１．ｇ〜１０、好
ましくは１．ｇ〜５．０の範囲としたものがよい。The resin concrete used for No. 3N has a thermosetting resin as its main component, plus minerals, fillers and 0.5%.
10 to 300 parts by weight of 3 to 5zx aggregate is added, and the resin concrete is made to have lateral modification. The resin for resin concrete is either lateral modified by itself, or a filler or organic substance that imparts lateral modification is added to improve the lateral modification of resin concrete. g to 10, preferably 1. It is preferable to set it in the range of g to 5.0.
熱硬化性樹脂の粘度は１〜３０ボイズ、好ましくは３〜
１５ボイズである。硬化系は常温硬化系でもよいが、作
業性の面からいえば、４０〜８０°Ｃの中温硬化をとる
のが好ましい。The viscosity of the thermosetting resin is 1 to 30 voids, preferably 3 to 30 voids.
There are 15 voices. The curing system may be a room temperature curing system, but from the viewpoint of workability, medium temperature curing of 40 to 80°C is preferable.
レジンコンクリートに使用する熱硬化性樹脂は、好適に
は不飽和ポリエステル樹脂である。本発明に使用できる
不飽和ポリエステルとしては、特に制限はなく、有機多
塩基酸類と多価アルコールから合成されるもの、あるい
はその変性物である、分子量５００〜１０，０００、好
適には１．０００〜５，０００程度の不飽和ポリエステ
ル樹脂である。有機多塩基酸類としては、一般の不飽和
ポリエステルの製造に用いられているマレイン酸、フマ
ル酸、イタコン酸、シトラコン酸などの不飽和多塩基酸
、あるいは無水マレイン酸などの不飽和多塩基酸の無水
物を必須成分として含み５フタル酸、テレフタル酸、イ
ソフタル酸、アジピン酸等の飽和酸を任意成分として含
むものである。有機多塩基酸は、単独または併用して使
用されることができる。The thermosetting resin used in resin concrete is preferably an unsaturated polyester resin. The unsaturated polyester that can be used in the present invention is not particularly limited, and is one synthesized from an organic polybasic acid and a polyhydric alcohol, or a modified product thereof, and has a molecular weight of 500 to 10,000, preferably 1.000. ~5,000 unsaturated polyester resin. Examples of organic polybasic acids include unsaturated polybasic acids such as maleic acid, fumaric acid, itaconic acid, and citraconic acid, which are used in the production of general unsaturated polyesters, and unsaturated polybasic acids such as maleic anhydride. It contains an anhydride as an essential component and saturated acids such as pentaphthalic acid, terephthalic acid, isophthalic acid, and adipic acid as an optional component. Organic polybasic acids can be used alone or in combination.
多価アルコールとしては、エチレングリコール、プロピ
レングリコール、ジエチレングリコール、トリエチレン
グリコール、ジプロピレングリコール、１，３−ブタン
ジオール、１，３−ブチレングリコール、１．６−ヘキ
サンジオール、１．６−シクロヘキサンジオール、ネオ
ペンチルグリコール、グリセリン、トリメチロールプロ
パン、ペンタエリスリトール、ソルビトール、水添ビス
フェノールＡ、ポリブタジェングリコール、ビスラエノ
ールＡのプロピレンオキサイド２付加体などが、単独ま
たは併用して使用される。Examples of polyhydric alcohols include ethylene glycol, propylene glycol, diethylene glycol, triethylene glycol, dipropylene glycol, 1,3-butanediol, 1,3-butylene glycol, 1.6-hexanediol, 1.6-cyclohexanediol, Neopentyl glycol, glycerin, trimethylolpropane, pentaerythritol, sorbitol, hydrogenated bisphenol A, polybutadiene glycol, propylene oxide diadduct of bislaenol A, and the like are used alone or in combination.
不飽和ポリエステルの変性物としては、ジシクロペンタ
ジェンまたはその誘導体、さらに空気乾燥性付与剤であ
る、ペンタエリスリトールトリアリルエーテル、グリセ
リンのモノまたはジアリルエーテル、アリルグリコール
、アリルグリシジルエーテルなどのアリル化合物を、不
飽和ポリエステルの一成分に用いたものが使用できる。Examples of modified unsaturated polyesters include dicyclopentadiene or its derivatives, and allyl compounds such as pentaerythritol triallyl ether, mono- or diallyl ether of glycerin, allyl glycol, and allyl glycidyl ether, which are air-drying agents. , those used as one component of unsaturated polyester can be used.
本発明における不飽和ポリエステルの製法については、
何等制限はなく、公知の反応方法を用いて製造すること
ができる。Regarding the method for producing unsaturated polyester in the present invention,
There are no restrictions and it can be produced using any known reaction method.
例えば、反応温度１００〜２３０℃で有機多塩基酸と多
価アルコールとを反応させ、生成する縮合水を系外に留
出させて反応を進め、必要に応じて酸価などで反応の終
点を求める。酸価は好適には約５〜４０である。For example, an organic polybasic acid and a polyhydric alcohol are reacted at a reaction temperature of 100 to 230°C, and the resulting condensed water is distilled out of the system to proceed with the reaction. If necessary, the end point of the reaction is determined by adjusting the acid value, etc. demand. The acid number is preferably about 5-40.
本発明で用いる有機多塩基酸は、その金髪を同時に仕込
んで多価アルコールと反応させてもよいし、有機多塩基
酸の一部を、あらかじめ多価アルコールと反応させた後
、残りの有機多塩基酸を加えて反応させてもよい。The organic polybasic acid used in the present invention may be reacted with a polyhydric alcohol by simultaneously charging the blonde hair, or a part of the organic polybasic acid may be reacted with the polyhydric alcohol in advance, and then the remaining organic polybasic acid may be reacted with the polyhydric alcohol. A basic acid may be added to cause the reaction.
また必要に応じて、ジシクロペンタジェンやその誘導体
あるいはアリル化合物を加えて反応させてもよい。Further, if necessary, dicyclopentadiene, a derivative thereof, or an allyl compound may be added for reaction.
通常は、このようにして得られた不飽和ポリエステルに
、重合性単量体例えばスチレン、タロロスチレン、ビニ
ルトルエン、ジビニルベンゼン、アクリル酸エステル、
メタクリル酸エステル等を、不飽和ポリエステル１００
重量部に対して２０〜３００重量部の割合で使用するこ
とができる。Usually, the unsaturated polyester thus obtained is added with polymerizable monomers such as styrene, talolostyrene, vinyltoluene, divinylbenzene, acrylic ester, etc.
Methacrylic acid ester etc., unsaturated polyester 100
It can be used in a proportion of 20 to 300 parts by weight.
フィラーとしては、炭酸カルシウム、水酸化アルミニウ
ム、ガラスパウダー、ガラスフレーク等が好適に使用さ
れる。As the filler, calcium carbonate, aluminum hydroxide, glass powder, glass flakes, etc. are preferably used.
骨材は、無機質のものとしては、寒水、ケイ石、セラミ
ック、ガラス等がある。また有機質としては熱可塑性樹
脂は例えばＰＥＴ、ＰＥ、ＰＰ、アクリルポリマーの着
色品、熱硬化性樹脂はエリア、ポリエステル、フェノー
ル等の着色品がある。Examples of inorganic aggregates include cold water, silica, ceramic, and glass. Examples of organic materials include colored thermoplastic resins such as PET, PE, PP, and acrylic polymers, and colored thermosetting resins such as area, polyester, and phenol.
レジンコンクリートに配合する骨材は、異色の組み合わ
せからなる石あるいは樹脂硬化物の扮砕品等からなり、
好適には０．３〜５１Ｊの粒径の粗粒状物である。The aggregate used in resin concrete consists of stones with unique combinations or crushed pieces of cured resin.
Coarse particles with a particle size of 0.3 to 51 J are preferred.
骨材として使用する石の色は、最終成形品に求める石目
調の模様によって異なるが、天然に近く、重厚な味わい
を出すには、白石および黒石を使用して御影石の模様を
出すのが、本発明には好適である。また樹脂によって黒
ずんだり、汚れた色を出すようなものは使用できない。The color of the stone used as aggregate varies depending on the stone-like pattern desired for the final molded product, but in order to create a rich, natural-looking stone, it is best to use white and black stones to create a granite pattern. , suitable for the present invention. Also, resins that darken or give a dirty color cannot be used.
白石としては、寒水石、大理石くず等があるが、寒水石
が最適である。黒石としては、黒い色を有するものなら
使用できるが、珪石を黒色に染色したものも使用できる
。Examples of white stone include Kansui stone and marble scraps, but Kansui stone is the best. As the black stone, any black stone can be used, but silica stone dyed black can also be used.
石の比重は、−ｍに白石の方が黒石よりも大きい１例え
ば、白石の代表例である寒水石は、比重２．７であるの
に対し、黒石の例である珪石を染色したものは、比重２
．５である。The specific gravity of a stone is -m, where white stone is larger than black stone1.For example, kansuite, which is a typical example of white stone, has a specific gravity of 2.7, whereas dyed silica stone, which is an example of black stone, has a specific gravity of 2.7. , specific gravity 2
．． It is 5.
熱硬化性樹脂に対する配合量は、熱硬化性樹脂１００重
量部に対して骨材１０〜３００重量部、さらに好ましく
は、５０〜２００重量部である。The blending amount for the thermosetting resin is 10 to 300 parts by weight, more preferably 50 to 200 parts by weight, of the aggregate based on 100 parts by weight of the thermosetting resin.
さらに、このレジンコンクリートには、成形品に要求さ
れる色、風合に応じて、種々の顔料、フィラー、つなぎ
材、例えば炭酸カルシウム、水酸化アルミニウム、ガラ
スパウダー、ガラスフレーク等を配合してもよい。Furthermore, various pigments, fillers, and binders such as calcium carbonate, aluminum hydroxide, glass powder, and glass flakes may be added to this resin concrete depending on the color and texture required for the molded product. good.
レジンコンクリートにはまた、硬化剤および場合によっ
ては硬化促進剤を配合する。硬化剤としては、アゾ化合
物例えばアゾイソブチロニトリル、或は有機過酸化物例
えばジクミルパーオキサイド、ベンゾイルパーオキサイ
ド、メチルエチルゲトンバーオキサイド、ｔ−ブチルパ
ーベンゾエート、ｔ−プチルバーオクトエート等がある
。硬化促進剤としては、ナフテン酸コバルト、ナフテン
酸銅、オクチル酸コバルト等の他、ジメチルアニリン、
ジメチルパラトルイジン等も使用される。The resin concrete also contains a curing agent and, in some cases, a curing accelerator. As the curing agent, an azo compound such as azoisobutyronitrile, or an organic peroxide such as dicumyl peroxide, benzoyl peroxide, methyl ethyl getone peroxide, t-butyl perbenzoate, t-butyl per octoate, etc. be. As curing accelerators, in addition to cobalt naphthenate, copper naphthenate, cobalt octylate, etc., dimethylaniline,
Dimethyl para-toluidine and the like are also used.
第４層は、ガラス繊維等で補強した不飽和ポリエステル
の層であり、バックアップ、スプレーアップ法等で雌型
の内型に施す。この層は浴槽全体の変形防止および強度
を持たせることを目的として、これに使用される樹脂お
よび繊維補強材は選択される。The fourth layer is a layer of unsaturated polyester reinforced with glass fiber or the like, and is applied to the inner mold of the female mold by a backup method, a spray-up method, or the like. The resin and fiber reinforcing material used in this layer are selected for the purpose of preventing deformation of the entire bathtub and providing strength.
本発明は、以上のような構成になるので、立面を有する
構造の成形品を、雄型および雌型の組み合わせで成形す
る場合、コンパウンドに対して比重差のある２種以上の
粒径０．３〜５ｍｍの骨材が混入されていても、成形中
に分離されることはなく、自然な模様が得られるととも
に、ゲルコート層とＦＲＰ層を通して透視できる御影調
人造大理石が得られる。またこの成形体は、９８℃−５
００時間の連続煮沸試験を行っても、ゲルコート面にフ
クロ、クラックの発生のないものが得られる。Since the present invention has the above-described configuration, when molding a molded product having a structure with an vertical surface using a combination of a male mold and a female mold, two or more types of grain size 0 with a difference in specific gravity are used for the compound. Even if 3 to 5 mm of aggregate is mixed, it will not separate during molding, and a natural pattern can be obtained, as well as a granite-like artificial marble that can be seen through the gel coat layer and the FRP layer. Moreover, this molded body is 98℃-5
Even when subjected to a continuous boiling test for 00 hours, the gel coated surface was free of flakes and cracks.
〔実施例１〕
巾約９０ｃｍＸ長さ約１２０ｃＬＩ＋ｘ深さ約６０ｃｍ
の浴槽の大きさに対応する、雄をおよび雌型を使用して
成形を行った。各層に使用した塗布剤の使用は、次のと
おりであった。なお、配合割合はすべて重量部である。[Example 1] Width approx. 90cm x length approx. 120cLI+x depth approx. 60cm
The molding was carried out using male and female molds corresponding to the size of the bathtub. The coating agents used for each layer were as follows. In addition, all compounding ratios are parts by weight.
（第１層）ゲルコート層
（５ＱＯＯＯＯＰ日本フェロー（株）製〕ビスフェノー
ル系不飽和ポリエステル樹脂
く第２層）ＦＲＰ中間層
ビスフェノール系不飽和ポリエステル樹脂（リボラック
４５０ＢＴＮ昭和高分子製）にて＃３８０チョツプドス
トランドマットを積層
（第３層）レジンコンクリート層
パテ〔アエロジル配合不飽和ポリエステル（リボラック
３１５７Ｔ、昭和高分子（株）製）〕粘度８ボイズ、稲
麦性４．０ １００部黒石〔新京陶材（株）製〕
Ｎｏ、２０ 比重２．５ １４０部白石〔
寒水石、大島層成（株）製〕
Ｓ旧０００比重２．７ １０部水酸化アルミ
ニウム
（ハイシライトＨ３１０、昭和電工製）１００部
バー力ドックス１６（硬化剤１） １．０部ＮＬ
Ｐ−１０（硬化促進剤） ０．４部パーキ
ュアー０（硬化剤２） ０．３部（第４層）
裏打層
リボラック１５８ＢＱＴ（昭和高分子（株）製不飽和ポ
リエステル〕
チョップドストランドマ、ト＃４５０
パーメツクル（日本油脂製硬化剤）
上記のような塑性の塗布剤を使用して、次のように成形
を行った。(1st layer) Gel coat layer (manufactured by 5QOOOOP Nippon Fellow Co., Ltd.) bisphenol-based unsaturated polyester resin 2nd layer) FRP intermediate layer bisphenol-based unsaturated polyester resin (Revolac 450BTN manufactured by Showa Kobunshi) #380 chop Lamination of Dostrand mat (3rd layer) Resin concrete layer putty [Unsaturated polyester containing Aerosil (Revolac 3157T, manufactured by Showa Kobunshi Co., Ltd.)] Viscosity 8 voids, Rice quality 4.0 100 parts Kuroishi [Shinkyotou] Made by Zai Co., Ltd.] No. 20 Specific gravity 2.5 140 parts Shiroishi [
Kansuiseki, manufactured by Oshima Straisei Co., Ltd.] S old 000 specific gravity 2.7 10 parts Aluminum hydroxide (Hisilite H310, manufactured by Showa Denko) 100 parts Burriki Dox 16 (hardening agent 1) 1.0 parts NL
P-10 (curing accelerator) 0.4 parts Percure 0 (curing agent 2) 0.3 parts (4th layer)
Backing layer Rivolac 158BQT (unsaturated polyester manufactured by Showa Kobunshi Co., Ltd.) Chopped stranded polymer, #450 Permeckle (hardening agent manufactured by NOF) Using the above plastic coating agent, mold as follows. went.
（ゲルコートの塗布）
雄型面にゲルコート剤を約８００ｆＩ／ｌ１１２の量ス
プレー塗布し、硬化させた。(Application of Gel Coat) A gel coat agent was spray applied to the male mold surface in an amount of about 800 fI/l112 and cured.
（第２層の塗布）
雄型に上記の硬化させたゲルコートの上に上記の第２層
用の樹脂配合物を塗布させ硬化させる。(Coating of second layer) The resin composition for the second layer is coated on the cured gel coat of the male mold and cured.
（第４層の塗布）
雌型に、上記の裏打層間の樹脂配合物を塗布し硬化させ
た。(Coating of 4th layer) The above-mentioned resin composition between the backing layers was coated on the female mold and cured.
前記のように塗布調製した雄型および雄型を浴槽の底が
上になるようにして組立てて、型締めしたのち、中心層
（第３層）を構成するレジンコンクリートを雌型の天板
の中央部に設けた注入口から注型した。その後５直ちに
硬化炉にて硬化させた。After assembling the male and female molds coated and prepared as described above with the bottom of the bathtub facing up and clamping the molds, the resin concrete constituting the center layer (third layer) is placed on the top plate of the female mold. It was cast through the injection port provided in the center. Thereafter, it was immediately cured in a curing oven.
硬化完了後、成形品を型から取り出したところ、成形品
の内側表面には白と黒との模様からなる天然御影調の模
様が風合い良く現れていた。浴槽の内部側面にあたる立
面にも、白石および黒石の沈降や分離から生ずるような
斑模様は見られなかった。When the molded product was removed from the mold after curing was completed, a natural granite-like pattern consisting of white and black patterns appeared on the inner surface of the molded product. There were no mottled patterns that could be caused by sedimentation or separation of white and black stones on the elevation of the interior side of the bathtub.
〔実施例２〕
第１層、第２層、第４層は実施例１と同様に行い、レジ
ンコンクリート層として、
パテ（アエロジル配合不飽和ポリエステル）（リボラッ
ク３１５７Ｔ −１、昭和高分子（株）製）粘度８ボイ
ズ、稲麦性２゜５ １００部着色骨材〈赤） 比重１
．４ ９０部着色骨材（黒） ｎｌ、４
５部着色骨材（茶） ｎｌ、４ ５
部水酸化アルミニウム
（ハイジライ１〜） １００部パー力ドッ
クス１６（硬化剤１） １部ＮＬＰ−１０（硬化
促進剤） ０，４部バーキュアー０（硬化剤
２） ０．３部を同様に注入口から注型した。[Example 2] The first, second, and fourth layers were formed in the same manner as in Example 1, and as the resin concrete layer, putty (unsaturated polyester containing Aerosil) (Revolac 3157T-1, Showa Kobunshi Co., Ltd.) was used. (manufactured by) viscosity 8 boids, rice-wheat consistency 2゜5 100 parts colored aggregate (red) specific gravity 1
．． 4 90 parts colored aggregate (black) nl, 4
5 parts colored aggregate (brown) nl, 4 5
1 part Aluminum hydroxide (Hijirai 1~) 100 parts Parriki Dox 16 (hardening agent 1) 1 part NLP-10 (hardening accelerator) 0.4 parts Vercure 0 (hardening agent 2) 0.3 parts in the same way It was cast from the entrance.
その後直ちに硬化炉にて硬化させた。Thereafter, it was immediately cured in a curing oven.
実施例１の結果も同様に斑模様もなく赤御影調の模様が
風合い良く現れていた。The results of Example 1 also showed that there was no mottled pattern and a red granite pattern appeared with good texture.
また、上記の実施例で得られたバスタブについて、９８
℃熱水で５００時間の連続煮沸試験を行ったところ、フ
クレ、クラックの発生のないバスタブが得られた。In addition, regarding the bathtub obtained in the above example, 98
When a continuous boiling test was conducted for 500 hours in hot water at ℃, a bathtub with no blisters or cracks was obtained.
〔比較例１〕
比較のため、稲麦性を有しない下記の配合で行うと
樹脂〔リボラック１００ｇ昭和高分子（株）製〕粘度１
０ボイズ、稲麦性１．．０ １００部黒石〔新東陶材
〈株）製〕
Ｎｏ、２０ 比重２．５ １４０部白石
〔寒水石 大島製能（株）製〕
５Ｗ１００Ｏ比重２．７ １０部水酸化
アルミニウム
（ハイジ−ライト１（３１０） １００部パー力
ドックス１６ １部ＮＬＰ−１００，
４部
バーキュアー０ ０．３部を同様に注
型したところ、立面における石の沈降、分離があり、成
形品表面に不自然な斑模様が生じた。[Comparative Example 1] For comparison, when the following formulation without rice-wheat properties was used, the resin [Rivolac 100g manufactured by Showa Kobunshi Co., Ltd.] had a viscosity of 1.
0 boise, rice and wheat 1. ．． 0 100 parts Kuroishi [manufactured by Shinto Tozai Co., Ltd.] No. 20 Specific gravity 2.5 140 parts Shiroishi [Kansuiseki manufactured by Oshima Seino Co., Ltd.] 5W100O specific gravity 2.7 10 parts Aluminum hydroxide (Hygielite 1 (310) 100 parts Pariki Dox 16 1 part NLP-100,
When 4 parts and 0.3 parts of Vercure 0 were cast in the same manner, stones settled and separated on the vertical surface, and an unnatural mottled pattern appeared on the surface of the molded product.
〔比較ＰＡ２）
実施例１にて、第２層を省いて成形した製品を、９０’
Ｃの熱水にて煮沸したところ、５０時間に至らない時点
で多くのフクレが発生し、バスタブ等のように耐熱水性
を必要とする場所には使用できないものであった。[Comparison PA2] The product molded in Example 1 without the second layer was molded for 90'
When it was boiled in hot water (C), many blisters occurred within 50 hours, and it could not be used in places such as bathtubs that require hot water resistance.
以上のとおり、本発明においては５以上のように構成し
たので、浴槽のような立面を有する成形体を製造する場
合でも、骨材の沈降などによる模様の乱れを出すことな
く、自然に分散したまま硬化した耐熱水性の御影調成形
体を得ることができる。As described above, since the present invention is configured as described in item 5 or above, even when manufacturing a molded body having an elevation like a bathtub, the pattern can be naturally dispersed without disturbing the pattern due to settling of the aggregate. It is possible to obtain a hot water-resistant granite-like molded product that is cured while still being cured.
特許出願人 永真工業株式会社Patent applicant: Eishin Kogyo Co., Ltd.
Claims (1)
化性樹脂を３０ｇ〜６００ｇ／ｍ＾２のガラス繊維もし
くは不織布に含浸した透明なＦＲＰ層、第３層としての
不透明な御影調のレジンコンクリート、および第４層と
してのＦＲＰバックアップ層からなる、耐熱水性に優れ
た御影調成形体。 ２、水平巾に対する高さの比が、０．１／１以上であり
、かつ水平巾が４００ｍｍ以上で、高さが４０ｍｍ以上
である立面を有する成形体を製造する方法において、成
形体の一面を規制する第１の型の表面に、第１層として
のゲルコート層、第２層としての熱硬化性樹脂を３０ｇ
〜６００ｇ／ｍ＾２のガラス繊維もしくは不織布に含浸
した透明なＦＲＰ層を順次形成し、成形体の他の一面の
規制する第２の型の表面に、第４層としてのＦＲＰバッ
クアップ層を形成し、該第１および第２の型により規制
される空間に、第３層としてのレジンコンクリートが１
００重量部の合成樹脂および２種以上の色で大きさ０．
３〜５ｍｍの骨材１０〜３００重量部を含み、揺変性を
有したレジンコンクリートを注入することからなる、御
影調成形体の製造方法。[Claims] 1. A gel coat layer as the first layer, a transparent FRP layer in which glass fiber or nonwoven fabric is impregnated with 30 g to 600 g/m^2 of thermosetting resin as the second layer, and a third layer as the third layer. A granite-like molded body with excellent hot water resistance, consisting of an opaque granite-like resin concrete and an FRP backup layer as the fourth layer. 2. In a method for producing a molded body having an elevational surface having a height to horizontal width ratio of 0.1/1 or more, and a horizontal width of 400 mm or more and a height of 40 mm or more, 30g of gel coat layer as the first layer and thermosetting resin as the second layer on the surface of the first mold that regulates one side.
Transparent FRP layers impregnated with ~600g/m^2 glass fiber or nonwoven fabric are sequentially formed, and an FRP backup layer as a fourth layer is formed on the surface of the second mold that regulates the other side of the molded object. Then, a third layer of resin concrete is placed in the space regulated by the first and second molds.
00 parts by weight of synthetic resin and two or more colors with a size of 0.00 parts by weight.
A method for producing a granite-like molded body, which comprises injecting resin concrete containing 10 to 300 parts by weight of 3 to 5 mm aggregate and having thixotropy.