JPH0245371A - Package for microwave oven - Google Patents
Package for microwave ovenInfo
- Publication number
- JPH0245371A JPH0245371A JP63190679A JP19067988A JPH0245371A JP H0245371 A JPH0245371 A JP H0245371A JP 63190679 A JP63190679 A JP 63190679A JP 19067988 A JP19067988 A JP 19067988A JP H0245371 A JPH0245371 A JP H0245371A
- Authority
- JP
- Japan
- Prior art keywords
- sealant layer
- weight
- heat
- package
- container body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、高周波加熱調理用包装体に関する。[Detailed description of the invention] [Industrial application field] The present invention relates to a package for high-frequency heating and cooking.
より詳しく言うと、本発明は、使用前は、高い密封性を
有し、調理や殺菌のためのボイル、レトルト処理を行っ
ても密封性が低下することなく、内容食品を食する直前
の調理のための高周波加熱処理により剥離強度が低下し
、易開封性となる等の優れた利点を有する高周波加熱調
理用の調理法食品の包装分野に好適に使用することがで
きる易開封性密封包装体に関する。More specifically, the present invention has a high sealing property before use, and the sealing property does not deteriorate even after cooking, boiling for sterilization, and retort processing, and the food can be cooked just before eating. An easy-to-open sealed packaging body that can be suitably used in the food packaging field using recipes for high-frequency heating cooking, which has excellent advantages such as reduced peel strength and easy-to-open properties due to high-frequency heating treatment. Regarding.
近年、高周波加熱処理やボイル等の加熱調理により内容
物を食する直前に温めるタイプの調理法食品の密封包装
体が盛んに用いられている。BACKGROUND ART In recent years, hermetically sealed packages for cooked foods in which the contents are warmed immediately before consumption by high-frequency heating treatment, boiling, or the like have been widely used.
特に、電子レンジの普及により、高周波加熱処理による
調理を行うタイプの調理法食品の密封包装体がますます
重要となってきている。In particular, with the spread of microwave ovens, sealed packages for food prepared using high-frequency heating are becoming increasingly important.
これらの包装体は、通常、調理法食品をトレー状または
カップ状等の容器本体に収納し、その開口部を蓋材によ
りヒートシールして密封したのち、熱水殺菌、レトルト
殺菌等により殺菌処理され、密封性の高い状態で市場に
供給される。These packages usually store the cooked food in a tray-shaped or cup-shaped container body, heat-seal the opening with a lid, and then sterilize it by hot water sterilization, retort sterilization, etc. It is supplied to the market in a highly sealed state.
そして、それらの包装体は、使用時すなわち内容食品を
食する際に、蓋を容易に剥離開封できることが必要であ
る。It is necessary that the lid of these packages can be easily peeled off and opened when used, that is, when the food contained therein is eaten.
すなわち、これらの包装体は、上記の各処理時を含めた
使用前の密封性と使用時の易開封性との両方を十分に満
たしていなければならず、そのため容器本体および蓋材
のヒートシール面（シーラント層）の材質およびその組
み合わせの選定が重要となる。In other words, these packages must satisfactorily satisfy both the sealability before use, including during each of the above-mentioned treatments, and the ease of opening during use. The selection of the material of the surface (sealant layer) and its combination is important.
従来の加熱調理用易開封性密封包装体としては、ヒート
シールするシーラント層の材質およびその組み合わせを
、■オレフィン系樹脂層とＰＰ （２０〜８０！量％）
とＰＥ（８０〜２０重量％）とからなる異樹脂ブレンド
樹脂層とＰＰ等の加工性改善樹脂層とするもの（特公昭
６０−４９４３２号公報）、■ＰＰ（２０〜６５重量％
）とＨＤＰＥ（３５〜８０重量％）とからなる組成物と
ＰＰとするもの（特公昭６２−２６３１３号公報）、■
エチレンープロピレンコポリマーとＬＤＰＥ（１０〜３
０重量％）とからなる組成物とエチレン−プロピレンコ
ポリマーと密度０．９２０−０．９３５ＬＬＤＰＥまた
は密度０．９３５〜０．９４０のＰＥ（１０〜５０重量
％）とからなる組成物とするもの（実開昭６１−４８１
６２号公報）、■蓋材をホモＰＰとし、シーラント層を
ＰＰとＰＥ等のＰＰを含むブレンドポリマーとするもの
（特開昭６２−１０９７６８号公報）が提案されている
。Conventional easy-to-open sealed packaging for heating cooking uses the following materials and combinations of heat-sealing sealant layers: ■ Olefin resin layer and PP (20 to 80% by weight)
and PE (80 to 20% by weight), and a processability-improving resin layer such as PP (Japanese Patent Publication No. 60-49432), ■ PP (20 to 65% by weight)
) and HDPE (35 to 80% by weight) and PP (Japanese Patent Publication No. 62-26313), ■
Ethylene-propylene copolymer and LDPE (10-3
A composition consisting of an ethylene-propylene copolymer and PE having a density of 0.920-0.935 LLDPE or a density of 0.935-0.940 (10-50% by weight) ( Jitsukai 61-481
(Japanese Patent Laid-Open No. 109768/1983) has been proposed in which the lid material is made of homo-PP and the sealant layer is made of a blend polymer containing PP and PE such as PP.
しかしながら、上記の■および■のものは、いずれも、
シール強度が低く、一方、■および■のものは、どちら
も、シール強度が高いものは、剥離性が悪く、シール強
度と剥離性が相反するという問題点がある。However, both of the above ■ and ■
The sealing strength is low, while the sealing strength and the peeling strength are poor, whereas the sealing strength and the peeling strength are poor.
尚、上記の■および■のものには、ヒートシールするシ
ーラント層にブレンド樹脂が用いられているが、高周波
加熱包装体への応用については記載されていない。Incidentally, in the above cases (1) and (2), a blended resin is used in the sealant layer to be heat-sealed, but there is no description of its application to high-frequency heating packages.
このように、従来の加熱調理用包装体においては、使用
前の密封性と使用時の易開封性との両者を共に十分に満
足するものはなかった。As described above, none of the conventional cooking packages satisfactorily satisfy both the sealability before use and the ease of opening during use.
本発明の目的は、充填密封、レトルト等の殺菌処理時、
流通時等の使用前には高い密封性を有し、しかも、高周
波調理後は、容易に開封することができる等の優れた利
点を有する高周波加熱調理用包装体を提供するものであ
る。The purpose of the present invention is to
To provide a package for high frequency heating cooking which has excellent advantages such as having high sealing performance before use during distribution, etc., and being easily openable after high frequency cooking.
本発明者は、前記課題を解決すべく、ヒートシールする
シーラント層の材質および組み合わせについて鋭意研究
を重ねた結果、容器本体のシーラント層および蓋材のシ
ーラント層として、どちらもポリプロピレン系樹脂とポ
リエチレン系樹脂との混合組成物を用い、かつ、それら
のシーラント層のうちのいずれか一方のポリエチレン系
樹脂の含有率と他方のそれとの差を１５重量％以上７０
重量％以下とすることにより、使用前には高い密封性を
有し、調理や殺菌のためのボイル、レトルト処理を行っ
ても密封性が低下することなく、内容食品を食する直前
の調理のための高周波加熱処理により剥離強度が低下し
、易開封性となる等の優れた利点を有するところのヒー
トシールを有し、高周波加熱調理用の調理済食品の包装
分野に好適に使用することができる易開封性密封包装体
となることを見出し、その知見に基づいて本発明を完成
するに至った。In order to solve the above problem, the present inventor has conducted intensive research on the materials and combinations of heat-sealing sealant layers, and has found that both the sealant layer of the container body and the sealant layer of the lid material are based on polypropylene resin and polyethylene resin. A mixed composition with a resin is used, and the difference between the content of polyethylene resin in one of the sealant layers and that in the other is 15% by weight or more and 70% by weight.
% by weight or less, it has a high sealing property before use, and the sealing property does not deteriorate even after cooking, boiling for sterilization, and retort processing, and it is possible to maintain the sealing property even when the food is cooked just before eating. It has a heat seal which has excellent advantages such as the peel strength is reduced by high frequency heat treatment and it becomes easy to open, so it can be suitably used in the field of packaging cooked foods for high frequency heating cooking. The present inventors have discovered that an easily openable sealed package can be obtained, and have completed the present invention based on this knowledge.
すなわち、本発明は、容器本体に内容物を収納し、その
容器本体の開口部をヒートシールして密封する包装体に
おいて、容器本体（１）のシーラント層（１ａ）および
蓋材（２）のシーラント層（２ａ）が、各々、ポリプロ
ピレン系樹脂とポリエチレン系樹脂との混合組成物から
なっており、シーラント層（１ａ）に用いる混合組成物
（１）とシーラント層（２ａ）に用いる混合組成物（■
）のうちの一方のポリエチレン系樹脂の含有量と他方の
それとの差が１５重量％以上７０重置火以下であること
を特徴とする高周波加熱調理用包装体からなるものであ
る。That is, the present invention provides a package in which contents are stored in a container body and the opening of the container body is sealed by heat sealing, in which the sealant layer (1a) of the container body (1) and the lid material (2) are sealed. Each of the sealant layers (2a) is made of a mixed composition of a polypropylene resin and a polyethylene resin, and the mixed composition (1) used for the sealant layer (1a) and the mixed composition used for the sealant layer (2a) (■
), the difference between the content of polyethylene resin in one of them and that in the other is 15% by weight or more and 70% by weight or less.
以下、本発明を図面を参照しつつ詳細に説明する。Hereinafter, the present invention will be explained in detail with reference to the drawings.
第１図は、本発明の高周波加熱調理用包装体の一例を表
す断面図である。FIG. 1 is a sectional view showing an example of the high-frequency heating cooking package of the present invention.
第１図に例示されているように、本発明の包装体は、少
なくとも基材１ｂとその面上に設けられたシーラント層
１ａからなる容器本体１と少なくとも基材２ｂとその面
上に設けられたシーラントＮ２ａからなる蓋材２とを、
容器本体１の開口部においてシーラント層１ａとシーラ
ント層２ａを介してヒートシールすることにより内容物
（調理法食品）を容器本体１内に密封充填シールし、次
いで該内容物を容器とともに密封状態で、熱水処理もし
くはレトルト処理等によって殺菌処理して、市場に供給
し、使用時すなわち内容食品を食するに際し、電子レン
ジ等を用いて、高周波加熱調理により温めたのち該開口
部のヒートシール部において咳蓋材２を剥離する形式の
ものである。３は開封用のタブである。As illustrated in FIG. 1, the package of the present invention comprises a container body 1 comprising at least a base material 1b and a sealant layer 1a provided on the surface thereof, and a container body 1 comprising at least a base material 2b and a sealant layer 1a provided on the surface thereof. and a lid material 2 made of sealant N2a,
The contents (cooked food) are hermetically filled and sealed in the container body 1 by heat-sealing the opening of the container body 1 through the sealant layer 1a and the sealant layer 2a, and then the contents are sealed together with the container. , sterilize it by hot water treatment or retort treatment, supply it to the market, and when using it, that is, when eating the contents, heat it by high-frequency heating using a microwave oven etc., and then heat seal the opening. This is a type of device in which the cough cover material 2 is peeled off. 3 is a tab for opening.
前記シーラント層１ａおよびシーラント層２ａの成分と
して用いることができるポリプロピレン系樹脂としては
、Ｈ−ＰＰ （ホモポリプロピレフ）、Ｒ−ＰＰ（ラン
ダムポリプロピレン系樹脂）Ｂ−ＰＰ （ブロックポリ
プロピレン系樹脂）あるいは、これらの混合物などを挙
げることができ、一方、ポリエチレン系樹脂としては、
ＨＤＰＥ（高密度ポリエチレン系樹脂）、ＬＤＰＥ （
低密度ポリエチレン系樹脂）、ＬＬＤＰＥ （直鎖状低
密度ポリエチレン系樹脂）、あるいは、それらの混合物
などを挙げることができる。Examples of the polypropylene resin that can be used as a component of the sealant layer 1a and the sealant layer 2a include H-PP (homopolypropylene resin), R-PP (random polypropylene resin), B-PP (block polypropylene resin), Mixtures of these can be mentioned, while polyethylene resins include:
HDPE (high density polyethylene resin), LDPE (
(low-density polyethylene resin), LLDPE (linear low-density polyethylene resin), or a mixture thereof.
但し、本発明の包装体は、所望により、容器本体１をシ
ーラント層１ａのみの単層として構成することができ、
また、蓋材２をシーラント層２ａの単層として構成する
こともできる。However, in the package of the present invention, the container body 1 can be configured as a single layer of only the sealant layer 1a, if desired.
Moreover, the lid material 2 can also be configured as a single layer of the sealant layer 2a.
すなわち、別の基材１ｂを特に用いることなしに、シー
ラント層１ａにより基材１ｂをも兼ねることができ、ま
た、別の基材２ｂを特に用いることなしに、シーラント
層２ａにより基材２ｂをも兼ねることもできる。That is, the sealant layer 1a can also serve as the base material 1b without using another base material 1b, and the sealant layer 2a can also serve as the base material 1b without using another base material 2b. It can also serve as
シーラント層１ａおよびシーラント層２ａに用いるそれ
ぞれの混合組成物は、これらのポリエチレン系樹脂およ
びポリプロピレン系樹脂を公知の方法によりブレンドす
ることにより得ることができる。The respective mixed compositions used for the sealant layer 1a and the sealant layer 2a can be obtained by blending these polyethylene resins and polypropylene resins by a known method.
ここで、シーラント層１ａの混合組成物中のポリエチレ
ン系樹脂の配合割合（Ｗ ＋重量％）とシーラントＮ２
ａの混合組成物中のポリエチレン系樹脂の配合割合（Ｗ
Ｚ重量％）との差（Ｓ）が、１５重量％以上７０重量％
以下、好ましくは２０〜６０重量％の範囲内に設定する
。Here, the blending ratio of the polyethylene resin in the mixed composition of the sealant layer 1a (W + weight %) and the sealant N2
The blending ratio of polyethylene resin in the mixed composition of a (W
The difference (S) from Z weight %) is 15 weight % or more and 70 weight %
Hereinafter, it is preferably set within the range of 20 to 60% by weight.
但し、Ｗ、をＷ２より大きい値としてもよく、あるいは
、Ｗ２をＷｌより大きい値としてもよくどちらでもよい
。However, W may be set to a larger value than W2, or W2 may be set to a larger value than Wl.
なお、前記の差（Ｓ）は、前者の場合には、Ｗ、−Ｗ、
を意味し、一方、後者の場合には、Ｗ２−Ｗ、を意味す
るものとする。In addition, in the former case, the above-mentioned difference (S) is W, -W,
On the other hand, in the latter case, it means W2-W.
ここで、もし、前記の差（Ｓ）が、１５重量％未満であ
ったり、あるいは、７０重量％より高い値であると、使
用時の高周波加熱処理により剥離強度が十分に低下せず
、所望の易開封性が得られなかったり、シール強度が十
分に高い値にならないことがある。Here, if the above-mentioned difference (S) is less than 15% by weight or higher than 70% by weight, the peel strength will not be sufficiently reduced by high-frequency heat treatment during use, and the desired It may not be easy to open the seal, or the seal strength may not be high enough.
シーラント層１ａの材質とシーラント層２ａの材質との
組み合わせとしては、上記の配合割合が満足されている
ならば、種々の組み合わせが可能である。好適な組み合
わせの具体例としては、たとえば、ＰＰとＨＤＰＥとの
混合組成物とＨ−ＰＰとＨＤＰＥとの混合組成物との組
み合わせ、Ｈ−ＰＰとＨＤＰＥとの混合組成物とＨ−Ｐ
ＰとＬＤＰＥもしくはＬＬＤＰＥとの混合組成物との組
み合わせ、などを挙げることができる。Various combinations of the material of the sealant layer 1a and the material of the sealant layer 2a are possible as long as the above-mentioned mixing ratio is satisfied. Specific examples of suitable combinations include, for example, a combination of a mixed composition of PP and HDPE and a mixed composition of H-PP and HDPE, and a combination of a mixed composition of H-PP and HDPE and H-P.
Examples include a combination of P and a mixed composition of LDPE or LLDPE.
容器本体ｌの基材１ｂの材質としては、公知のものなど
各種のものを使用することができ、具体的には、たとえ
ば、ポリオレフィン、ＥＶＯＦ（（エチレン−酢酸ビニ
ル共重合体ケン化物）、ＮＹ（ナイロン）、無機充填材
人ポリオレフィンなどを挙げることができる。As the material of the base material 1b of the container body 1, various known materials can be used. Specifically, for example, polyolefin, EVOF ((saponified ethylene-vinyl acetate copolymer), NY (nylon), inorganic fillers and polyolefins.
前記無機充填材としては、通常用いられるものを使用す
ることができ、具体的には、たとえば、タルク等を挙げ
ることができる。As the inorganic filler, commonly used ones can be used, and specific examples include talc and the like.
なお、基材１ｂは、単層構造としてもよく、あるいは、
多層構造としてもよく、いずれでもよい。Note that the base material 1b may have a single layer structure, or
It may have a multilayer structure, or any structure may be used.
容器本体１は、通常、はとんどの場合、トレイ状、カッ
プ状に成形して使用されるが、所望により他の形状のも
のとすることができる。The container main body 1 is usually used in the form of a tray or a cup, but it can be formed into other shapes as desired.
容器本体１は、前記基材１ｂの材質と前記シーラント層
１ａの材質とを公知の方法等の各種の方法、たとえば、
共押出による多層シート成形等により積層・成形するこ
とにより得ることがてきる。The container body 1 is prepared by changing the material of the base material 1b and the material of the sealant layer 1a by various methods such as known methods, for example,
It can be obtained by laminating and molding, such as multilayer sheet molding by coextrusion.
蓋材２の基材２ｂの材質としては、公知のものなど各種
のものを使用することができ、具体的には、たとえば、
アルミニウム、ＰＥＴ （ポリエチレンテＬ／７タレー
ト）、ＮＹＳＥＶＯＨ，ＰＶＤＣ（ポリ塩化ビニリデン
）、ポリオレフィンなどを挙げることができる。As the material of the base material 2b of the lid material 2, various known materials can be used, and specifically, for example,
Examples include aluminum, PET (polyethylene tere L/7 tallate), NYSEVOH, PVDC (polyvinylidene chloride), and polyolefin.
なお、基材２ｂは、単層構造としてもよく、あるいは、
多層構造としてもよく、いずれでもよい。Note that the base material 2b may have a single layer structure, or
It may have a multilayer structure, or any structure may be used.
蓋材２は、通常、はとんどの場合、平なシート状に成形
して使用されるが、所望により他の形状のものとするこ
とができる。The lid material 2 is usually used in the form of a flat sheet, but it can be formed into other shapes if desired.
蓋材２は、前記基材２ｂの材質と前記シーラント層２ａ
の材質とを公知の方法等の各種の方法、たとえば、共押
出による多層シート成形等により積層・成形することに
より得ることができる。The lid material 2 includes the material of the base material 2b and the sealant layer 2a.
It can be obtained by laminating and molding the materials by various methods such as known methods, such as multilayer sheet molding by coextrusion.
本発明の包装体において、シーラント層１ａの層厚は、
通常、２０〜２００μｍ程度の範囲内に設定するのが適
当である。また、シーラント層２ａの層厚は、通常１０
〜８０μｍ程度の範囲内に設定するのが適当である。In the package of the present invention, the layer thickness of the sealant layer 1a is:
Usually, it is appropriate to set the thickness within a range of about 20 to 200 μm. Further, the layer thickness of the sealant layer 2a is usually 10
It is appropriate to set the thickness within a range of about 80 μm.
本発明の包装体は、内容物（Ｊ’理済食品）を容器本体
１に収納し、前記容器本体１と前記蓋材２を、第１図に
例示の如く、開口部において、シーラント層１ａとシー
ラント層２ａにより、ヒートシールする。In the package of the present invention, the contents (J' Risa Foods) are stored in a container body 1, and the container body 1 and the lid material 2 are connected to each other at the opening, as illustrated in FIG. and heat sealing with the sealant layer 2a.
このヒートシールは、公知の方法等の各種の方法を用い
て行うことができる。その際の、ヒートシール温度とし
ては、通常、２２０〜２５０°Ｃ程度の範囲内とし、２
回にわけてヒートシールするのが適当である。This heat sealing can be performed using various methods such as known methods. At that time, the heat sealing temperature is usually within the range of about 220 to 250°C.
It is appropriate to heat seal in batches.
前記殺菌処理は、通常、ボイルもしくは熱水処理、レト
ルト処理などによって行うことができる。The sterilization treatment can usually be performed by boiling, hot water treatment, retort treatment, or the like.
この殺菌処理の温度としては、通常、８０〜１３０’Ｃ
程度の範囲内とするのが適当である。The temperature for this sterilization treatment is usually 80 to 130'C.
It is appropriate to keep it within a certain range.
本発明の包装体においては、前記殺菌処理における加熱
によっては、ヒートシール部のシール強度および剥離強
度は実質的に低下せず、十分な密封性が保持されており
、一方、使用前に行う高周波加熱処理により剥離強度が
低下し、易開封性となると言う優れた効果を得ることが
できる。In the package of the present invention, the sealing strength and peel strength of the heat-sealed portion are not substantially reduced by heating in the sterilization treatment, and sufficient sealing performance is maintained. The heat treatment lowers the peel strength and makes it easier to open, which is an excellent effect.
この高周波加熱処理前後において剥離強度が有効に変化
する理由については、今のところ明らかではないが、た
とえば、次に示すような作用を考えることができる。The reason why the peel strength changes effectively before and after this high-frequency heat treatment is not clear at present, but the following effects can be considered, for example.
すなわち、シーラント層１ａとシーラント層２ａは、前
記したように特定の材質からなり、しかもポリエチレン
系樹脂の配合割合が適度に相違しているので、前記殺菌
処理前後における比較的緩やかな温度変化によっては、
剥離強度が実質的に低下しないが、高周波加熱処理によ
る急激な温度変化により、両シーラント層の膨張率およ
び収縮率に大きな違いもしくはズレが生じ、これにより
剥離強度が十分に低下し、好適な易開封性が得られるも
のと推定することができる。That is, since the sealant layer 1a and the sealant layer 2a are made of specific materials as described above, and have moderately different blending ratios of polyethylene resin, they may ,
Although the peel strength does not substantially decrease, the rapid temperature change caused by the high-frequency heat treatment causes a large difference or mismatch in the expansion and contraction rates of both sealant layers, which sufficiently reduces the peel strength and makes it possible to achieve a suitable ease. It can be assumed that ease of opening is obtained.
実施例１〜３
（ｉ）シーラント層１ａの材質として、第１表に示す割
合のポリエチレン系樹脂（ＰＥ）を含有するＨ−ＰＰと
ＨＤＰＥからなる混合組成物を用い、基材１ｂの材質と
して、（Ｈ−ＰＰ４０重量％とＨＤＰＥ６０重量％）５
０重量％とタルク５０重量％からなる組成物を用い、シ
ーラント層１ａの層厚１００μｍ、全層厚６００μｍの
積層シートとし、これを熱成形により径１００＋ａ、高
さ４０■の容器本体１とした。Examples 1 to 3 (i) As the material of the sealant layer 1a, a mixed composition consisting of H-PP and HDPE containing polyethylene resin (PE) in the proportions shown in Table 1 was used, and as the material of the base material 1b. , (40% by weight of H-PP and 60% by weight of HDPE) 5
Using a composition consisting of 0% by weight and 50% by weight of talc, a laminated sheet with a sealant layer 1a having a layer thickness of 100 μm and a total layer thickness of 600 μm was made into a container body 1 having a diameter of 100+a and a height of 40cm by thermoforming. .
一方、基材２ｂとして、ＰＰ／ＥＶＯＨ／ＰＰからなる
厚さ２００μｍの積層シートを用い、これにシーラント
層２ａとして第１表に示す割合のポリエチレン系樹脂（
ＰＥ）を含有するＨ−ＰＰとＬＬＤＰＥからなる混合組
成物からなる厚さ３０μｍのフィルムをドライラミネー
トし、蓋材２とした。On the other hand, as the base material 2b, a 200 μm thick laminated sheet made of PP/EVOH/PP is used, and as the sealant layer 2a, a polyethylene resin (
A film with a thickness of 30 μm made of a mixed composition of H-PP containing PE) and LLDPE was dry laminated to obtain a lid material 2.
（ｉｉ ）次に、上記の容器本体１に水を充填し、その
開口部に、２４０°Ｃ１２秒、帯巾２１１Ｉ１１の条件
で、上記の蓋材２をヒートシールし、第１図に例示の如
き構成の３種類の包装体（実施例１、実施例２、実施例
３）を作製した。(ii) Next, the above-mentioned container body 1 is filled with water, and the above-mentioned lid material 2 is heat-sealed to the opening of the container body 1 at 240°C for 12 seconds and with a band width of 211I11. Three types of packages (Example 1, Example 2, and Example 3) having the following configurations were produced.
（ｕｉ）（ｉｉ）で得られた各包装体に、１２０°Ｃ１
４５分間レトルトの加熱殺菌処理をした。(ui) Each package obtained in (ii) was heated at 120°C1.
The retort was heat sterilized for 45 minutes.
（ｉｖ）（ｉｉ）で得られた各包装体に、１００°Ｃ１
７分間ボイルの加熱殺菌処理をした。(iv) Each package obtained in (ii) was heated to 100°C1.
Boil heat sterilization treatment was performed for 7 minutes.
（ｖ）次に、電子レンジを用いて、（ｊｉ）、（ｉｖ）
の加熱殺菌処理をした各包装体を５００Ｗ、２．５分、
高周波加熱処理を行った。(v) Next, using a microwave oven, (ji), (iv)
Each package that has been heat sterilized is heated at 500W for 2.5 minutes.
High frequency heat treatment was performed.
（ｖｉ）（ｉｉｉ）、（１ｖ）及び（Ｖ）の各処理を行
った包装体を取り出し、蓋材２のタブより４５度の方向
に剥離することにより、初期及び中間の剥離強度を測定
した。(vi) The initial and intermediate peel strength was measured by taking out the package that had undergone each of the treatments (iii), (1v), and (V) and peeling it off from the tab of lid material 2 in a 45-degree direction. .
結果を第１表に示す。尚、これらの包装体は上記の高周
波加熱時に、シール部よりの脱圧が観測された。The results are shown in Table 1. In addition, when these packages were subjected to the above-mentioned high-frequency heating, depressurization from the seal portion was observed.
比較例１〜３
容器本体１を、シーラント層１ａと基材１ｂとを兼ねて
第１表に示す割合のＰＥを含有するＨ−ＰＰとＬ−ＤＰ
Ｅからなる混合組成物の単層シートより作製し、これに
直接蓋材２をヒートシールした他は実施例と同様にして
３種類の包装体（比較例１、比較例２、比較例３）を作
製した。Comparative Examples 1 to 3 The container body 1 was made of H-PP and L-DP containing PE in the proportions shown in Table 1, which also served as the sealant layer 1a and the base material 1b.
Three types of packaging bodies (Comparative Example 1, Comparative Example 2, Comparative Example 3) were prepared in the same manner as in the example except that the lid material 2 was heat-sealed directly to the single-layer sheet of the mixed composition consisting of E. was created.
結果を第１表に示す。The results are shown in Table 1.
なお、第２図は蓋材の開口強度測定方法を示す断面図で
あり、第３図は蓋材の強度測定箇所を示す平面図である
０図中４はプッシュプルテスター５はビール方向を示し
ている。In addition, Fig. 2 is a cross-sectional view showing the method of measuring the opening strength of the lid material, and Fig. 3 is a plan view showing the strength measurement points of the lid material. ing.
本発明によると、容器本体と蓋材のそれぞれのヒートシ
ールするシーラント層として特定の材質からなる混合組
成物を用いており、しかも、特定の組成（配合割合）を
有するシーラント層を組み合わせているので、使用前に
は、シール強度が高図中の符号は、１：容器本体、１ａ
ニジ−ラント層、１ｂ：基材、２：蓋材、２ａニジ−ラ
ント層、２ｂ：基材、３：タブを表す。According to the present invention, a mixed composition made of a specific material is used as a heat-sealing sealant layer for each of the container body and lid material, and sealant layers having a specific composition (mixing ratio) are combined. , Before use, the seal strength is high.The symbols in the diagram are 1: Container body, 1a
1b: base material, 2: lid material, 2a: rainbow runt layer, 2b: base material, 3: tab.
Claims (1)
をヒートシールして密封する包装体において、容器本体
（１）のシーラント層（１ａ）および蓋材（２）のシー
ラント層（２ａ）が、各々、ポリプロピレン系樹脂とポ
リエチレン系樹脂との混合組成物からなっており、シー
ラント層（１ａ）に用いる混合組成物（ I ）とシーラ
ント層（２ａ）に用いる混合組成物（II）のうちの一方
のポリエチレン系樹脂の含有量と他方のそれとの差が１
５重量％以上７０重量％以下であることを特徴とする高
周波加熱調理用包装体。1. In a package in which contents are stored in a container body and the opening of the container body is heat-sealed, the sealant layer (1a) of the container body (1) and the sealant layer (2a) of the lid material (2) are ) are each made of a mixed composition of a polypropylene resin and a polyethylene resin, and the mixed composition (I) used for the sealant layer (1a) and the mixed composition (II) used for the sealant layer (2a). The difference between the polyethylene resin content on one side and the other side is 1
A package for high-frequency heating cooking, characterized in that the content is 5% by weight or more and 70% by weight or less.