JP7508197B2 - 偏光板 - Google Patents
偏光板 Download PDFInfo
- Publication number
- JP7508197B2 JP7508197B2 JP2018246120A JP2018246120A JP7508197B2 JP 7508197 B2 JP7508197 B2 JP 7508197B2 JP 2018246120 A JP2018246120 A JP 2018246120A JP 2018246120 A JP2018246120 A JP 2018246120A JP 7508197 B2 JP7508197 B2 JP 7508197B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- adhesive layer
- thickness
- polarizing plate
- retardation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]偏光子と、第1の粘着剤層と、位相差層と、第2の粘着剤層と、をこの順に含み、前記第1の粘着剤層の厚みT1(μm)と前記第2の粘着剤層の厚みT2(μm)との和であるTa(μm)を偏光板の総厚みTp(μm)で除した値であるTa/Tpが0.40以下であり、前記偏光子の厚みが15μm以下である偏光板。
[2]接着剤層を更に含み、第1の位相差層と、前記接着剤層と、第2の位相差層と、をこの順に含む[1]に記載の偏光板。
[3]偏光子と、第1の粘着剤層と、第1の位相差層と、第3の粘着剤層と、第2の位相差層と、第2の粘着剤層と、をこの順に含む偏光板であって、前記第1の粘着剤層の厚みT1(μm)と前記第2の粘着剤層の厚みT2(μm)と前記第3の粘着剤層の厚みT3(μm)との和であるTa’(μm)を前記偏光板の総厚みTp’(μm)で除した値であるTa’/Tp’が0.40以下であり、前記偏光子の厚みが15μm以下である偏光板。
<偏光板>
本明細書において「偏光板」とは、偏光子及び位相差層を備える光学フィルムである。
第1実施形態の偏光板は、偏光子と、第1の粘着剤層と、位相差層と、第2の粘着剤層と、をこの順で備える。
図1は、第1実施形態に係る偏光板の構成を示す概略断面図の一例である。図1に示すように、偏光板100は、偏光子11と、第1の粘着剤層12と、位相差層14と、第2の粘着剤層13とがこの順で積層されている。
本明細書において、「λ/2の位相差を与える層」とは、ある特定の波長の直線偏光の偏光方位を90°変換する位相差層である。
本明細書において、「λ/4の位相差を与える層」とは、ある特定の波長の直線偏光を円偏光に(又は、円偏光を直線偏光に)変換する位相差層である。位相差層14がλ/4の位相差を与える層である場合、偏光子11と、位相差層14を備える偏光板100は、円偏光板として機能し得る。
本明細書において、「ポジティブC層」とは、面内における遅相軸方向の屈折率をNx、その面内における進相軸方向の屈折率をNy、その厚み方向における屈折率をNzとしたときに、Nz>Nx≧Nyの関係を満足する層である。Nxの値とNyの値との差は、Nyの値の0.5%以内であることが好ましく、0.3%以内であることがより好ましい。0.5%以内であれば、実質的にNx=Nyと見なすことができる。
本実施形態の偏光板100は偏光子11を有する。本明細書において「偏光子」とは、無偏光の光を入射させたとき、吸収軸に直交する振動面をもつ直線偏光を透過させる性質を有する光学フィルムのことである。
偏光子の厚みが薄くなると高温、高湿の環境下において偏光子端部のヨウ素が抜けやすくなる。そのため、偏光子の厚みは2μm以上であることが好ましい。また、偏光子の厚みが厚い場合には、冷熱交換試験において偏光子のワレが発生しやすくなる。本発明の偏光板は、位相差層に加わる応力を抑制できるので、優れた耐久性も示しうる。
偏光子の片面、又は両面に後述する保護フィルムが積層されている場合、前記偏光子の厚みに前記保護フィルムの厚みは含めない。
偏光子の両面に保護フィルムが積層されている場合、二つの保護フィルムの樹脂組成は同一でもよいし、異なっていてもよい。
熱可塑性樹脂から形成されたフィルムは、PVA系樹脂及び二色性物質からなる偏光子との密着性を向上するため、表面処理(例えば、コロナ処理等)が施されていてもよく、プライマー層(下塗り層ともいう)等の薄層が形成されていてもよい。
偏光子の片面又は両面に保護フィルムを有する場合、偏光子を十分に補強できるので、偏光板の各種耐久性を更に向上することができる。
偏光子と位相差層とは、第1の粘着剤層を介して積層されている。
本明細書において、「粘着剤」とは、柔軟なゴム状であり、それ自体を前記偏光子、前記保護フィルム等の被着体に張り付けることで接着性を発現するものとする。後述する活性エネルギー線硬化型粘着剤は、エネルギー線を照射することにより、接着力を調整することができる。
本実施形態において、第1の粘着剤層を構成する粘着剤組成物に含まれる(メタ)アクリル系樹脂(1)は、下記式(I)で示される(メタ)アクリル酸アルキルエステルに由来する構造単位(以下、「構造単位(I)」ともいう。)を主成分(例えば、これを50質量%以上含む。)とする重合体(以下、「(メタ)アクリル酸エステル重合体」ともいう。)であることが好ましい。
本明細書において「由来」とは、(メタ)アクリル酸アルキルエステル等の化合物が重合するために、化学構造が変化することを意味する。
本明細書において、「(メタ)アクリル酸」とは、アクリル酸またはメタクリル酸のいずれでもよいことを意味する。(メタ)アクリレートなどの「(メタ)」も同様の意味である。
第1の粘着剤層を形成する粘着剤組成物は、架橋剤(2)を含むことが好ましい。架橋剤(2)としては、慣用の架橋剤(イソシアネート化合物、エポキシ化合物、アジリジン化合物、金属キレート化合物、過酸化物など)が挙げられ、特に粘着剤組成物のポットライフ、架橋速度、及び偏光板の耐久性などの観点から、イソシアネート系化合物であることが好ましい。
粘着剤組成物は、シラン化合物(3)を含有することができる。シラン化合物(3)を含有することにより第1の粘着剤層と、前記第1の粘着剤層に積層される層との密着性を高めることができる。2種以上のシラン化合物(3)を使用してもよい。
第1の粘着剤層を形成する粘着剤組成物は、紫外線吸収剤、帯電防止剤、溶媒、架橋触媒、粘着付与樹脂(タッキファイヤー)、可塑剤等の添加剤を単独または2種以上含むことができる。また、粘着剤組成物に紫外線硬化性化合物を配合し、第1の粘着剤層を形成した後に紫外線を照射して硬化させ、より硬い粘着剤層とすることも有用である。
第1の粘着剤層の厚みが前記下限値以上であると、偏光子と位相差層とを十分に貼合することができる。第1の粘着剤層の厚みが前記上限値以下であると、位相差層のずれが生じにくく、位相差層の変形に伴う偏光板のしわの発生を抑制する効果が高まる。
第2の粘着剤層は、位相差層の第1の粘着剤層と接する面とは反対側の面に積層されている。偏光板は、第2の粘着剤層を介して表示パネル等に積層される。
第2の粘着剤層を構成する粘着剤として、上述した第1の粘着剤層を構成する粘着剤として例示したものと同様のものを使用することができる。第1の粘着剤層と第2の粘着剤層とは、厚みがそれぞれ同じであってもよいし、異なっていてもよい。
第2の粘着剤層の厚みが前記下限値以上であると、位相差層と、表示パネル等とを十分に貼合することができる。第2の粘着剤層の厚みが前記上限値以下であると、第2の粘着剤層を介して積層される位相差層と、例えば表示パネルとのずれが生じにくい。そのため、位相差層が強固に固定され、偏光子と位相差層とがずれにくくなる結果として、位相差層の変形に伴う偏光板のしわの発生の抑制効果が高まる。第2の粘着剤層の厚みは、第1の粘着剤層の厚みより大きくてもよい。
前記Ta/Tpは、0.10以上であることが好ましく、0.20以上であることがより好ましく、0.25以上であることがさらに好ましい。前記Ta/Tpは、0.38以下であることが好ましい。上述した上限値及び下限値は、任意に組み合わせることができる。
Ta/Tpが前記上限値以下であると、位相差層のずれが生じにくく、位相差層の変形に伴う偏光板のしわの発生を抑制する効果が高まる。これは、偏光板に占める粘着剤層の割合を一定値以下とすることにより、水蒸気を通しにくい層構成にすることができるためであると考えられる。
偏光板の総厚みが前記上限値以下であると、偏光板の薄層化に貢献し得る。偏光板の総厚みが前記下限値以上であると、偏光板の強度が向上する。
粘着剤層の水蒸気透過度が高いと、粘着剤が高温、高湿環境の影響を強く受ける為、位相差層の変形に伴う偏光板のしわが発生しやすくなる。粘着剤単体で水蒸気透過度を測定するのが難しい場合は、透湿性の高い基材に粘着剤を貼合した上で透湿性の高い基材との比から、水蒸気透過度を算出してもよい。
位相差層14は、液晶化合物を含む液晶材料(液晶組成物ともいう)から構成される層を有する。液晶化合物を含む液晶材料から構成される層とは、具体的には、液晶化合物が硬化した層を意味する。本明細書において、λ/2の位相差を与える層、λ/4の位相差を与える層及びポジティブC層等を総称して、位相差層ということがある。さらに、位相差層は後述の透明基材、配向層を含んでいてもよい。
有機溶媒としては、例えば、アミド(例えば、N,N-ジメチルホルムアミド)、スルホキシド(例えば、ジメチルスルホキシド)、ヘテロ環化合物(例えば、ピリジン)、炭化水素(例えば、ベンゼン、ヘキサン)、アルキルハライド(例えば、クロロホルム、ジクロロメタン)、エステル(例えば、酢酸メチル、酢酸エチル、酢酸ブチル)、ケトン(例えば、アセトン、メチルエチルケトン)、エーテル(例えば、テトラヒドロフラン、1,2-ジメトキシエタン)が挙げられる。その中でも、アルキルハライド、ケトンが好ましい。前記塗工液として、2種類以上の有機溶媒を併用してもよい。
位相差層の厚みが前記下限値以上であると、十分な耐久性が得られる。位相差層の厚みが前記上限値以下であると、偏光板の薄層化に貢献し得る。
位相差層の厚みは、λ/4の位相差を与える層、λ/2の位相差を与える層、又はポジティブC層の所望の面内位相差値、及び厚み方向の位相差値が得られるよう調整され得る。
透湿度比が低いほど、高温、高湿環境下でのシワの抑制に効果的である。
第2実施形態の偏光板は、偏光子と、第1の粘着剤層と、第1の位相差層と、接着剤層又は第3の粘着剤層と、第2の位相差層と、第2の粘着剤層と、をこの順で備える偏光板である。すなわち、第2実施形態の偏光板は、少なくとも2層の位相差層を含む。
図2は、第2実施形態に係る偏光板の構成を示す概略断面図の一例である。図2に示すように、偏光板101は、偏光子11と、第1の粘着剤層12と、第1の位相差層15と、接着剤層又は第3の粘着剤層17と、第2の位相差層16と、第2の粘着剤層13とがこの順で積層されている。
第1の位相差層15と、第2の位相差層16とは、接着剤層又は第3の粘着剤層17を介して積層される。第1の位相差層15及び第2の位相差層16は、それぞれλ/2の位相差を与える層、λ/4の位相差を与える層、又はポジティブC層であることができる。本実施形態の1つの側面としては、第1の位相差層15及び第2の位相差層16のいずれか一方がλ/4の位相差を与える層として機能し、他方がλ/2の位相差を与える層として機能すること、又は第1の位相差層15及び第2の位相差層16のいずれか一方がλ/4の位相差を与える層として機能し、他方がポジティブC層として機能することが好ましい。したがって、第1の位相差層15及び第2の位相差層16の厚み並びにこれらの層を構成する材料は、λ/4の位相差を与える層、λ/2の位相差を与える層、又はポジティブC層の所望の面内位相差値、厚み方向の位相差値が得られるよう調整され得る。
第2実施形態の偏光板は、好ましくは、第1の位相差層と、接着剤層と、第2の位相差層とをこの順に含む。
より具体的には、「接着剤」とは被着部材同士を接着しているときのガラス転移温度(Tg)が25℃以上であるものである。一方で「粘着剤」とは、被着部材同士を接着しているときのガラス転移温度(Tg)が25℃未満であるものである。
第1の位相差層と第2の位相差層とを貼合する接着剤としては、例えば、水系接着剤、及び活性エネルギー線硬化性接着剤が挙げられる。水系接着剤としては、例えば、ポリビニルアルコール系樹脂を水に溶解、及び分散させた接着剤が挙げられる。活性エネルギー線硬化性接着剤としては、例えば、紫外線、可視光、電子線、X線のような活性エネルギー線の照射によって硬化する硬化性化合物を含有する接着剤が挙げられる。硬化後の活性エネルギー線硬化性接着剤の硬さを示す指標である貯蔵弾性率は、水系接着剤の貯蔵弾性率よりも高い場合が多い。位相差層間の接着剤層の貯蔵弾性率が高いと位相差層間のずれが生じにくいため、活性エネルギー線硬化性接着剤を使用することが好ましい。
接着剤層の厚みが前記上限値以下であると、第1の位相差層と第2の位相差層との間に浮きや剥がれを生じにくい。
前記Ta/Tpは、0.10以上であることが好ましく、0.20以上であることがより好ましく、0.25以上であることがさらに好ましい。また、前記Ta/Tpは、0.38以下であることが好ましい。上述した上限値及び下限値は、任意に組み合わせることができる。
Ta/Tpが前記上限値以下であると、位相差層のずれが生じにくく、位相差層の変形に伴う偏光板のしわの発生を抑制する効果が高まる。
偏光板の総厚みが前記上限値以下であると、偏光板の薄層化に貢献し得る。偏光板の総厚みが前記下限値以上であると、偏光板の強度が向上する。
本実施形態に係る第1の位相差層と第2の位相差層を介する第3の粘着剤としては、従来公知の光学的な透明性に優れる粘着剤を特に制限なく用いることができる。第3の粘着剤層を構成する粘着剤として、上述した第1の粘着剤層を構成する粘着剤と同様のものを使用することができる。また、活性エネルギー線硬化型粘着剤を用いてもよい。第1の粘着剤層と第2の粘着剤層と第3の粘着剤層とは、厚みがそれぞれ同じであってもよいし、異なっていてもよい。
第3の粘着剤層の厚みが前記下限値以上であると、第1の位相差層と第2の位相差層を十分に貼合することができる。第3の粘着剤層の厚みが前記上限値以下であると、第1の位相差層と第2の位相差層のずれが生じにくく、位相差層の変形に伴う偏光板のしわの発生を抑制する効果が高まる。
前記Ta’/Tp’は、0.10以上であることが好ましく、0.20以上であることがより好ましく、0.25以上であることがさらに好ましい。前記Ta’/Tp’は、0.40以下であることが好ましく、0.38以下であることがより好ましい。上述した上限値及び下限値は、任意に組み合わせることができる。
Ta’/Tp’が前記上限値以下であると、位相差層のずれが生じにくく、位相差層の変形に伴う偏光板のしわの発生を抑制する効果が高まる。
偏光板の総厚みが前記上限値以下であると、偏光板の薄層化に貢献し得る。偏光板の総厚みが前記下限値以上であると、偏光板の強度が向上する。
本発明に係る偏光板を製造する方法の例について以下に説明する。
偏光子は、通常、PVA系フィルムを一軸延伸する工程、PVA系フィルムを二色性色素で染色することにより二色性色素を吸着させる工程、二色性色素が吸着されたPVA系フィルムをホウ酸水溶液で処理して架橋させる工程、及びホウ酸水溶液による架橋処理後に水洗する工程(以下、ホウ酸処理ともいう。)を経て、製造される。
前述した通り、第1の粘着剤層、第2の粘着剤層、及び第3の粘着剤層は、アクリル系樹脂をベースポリマーとした粘着剤により形成されることが好ましい。
また、剥離層は、例えば剥離層形成用組成物から形成することができる。剥離層形成用組成物を構成する主な成分(樹脂)としては、特に限定されるもではないが、シリコーン樹脂、アルキド樹脂、アクリル樹脂、及び長鎖アルキル樹脂等が挙げられる。
位相差層は、前述した通り、液晶化合物が硬化した層を有し、さらに透明基材、及び配向層を有していてもよい。
第2実施形態に係る偏光板に含まれる2層の位相差層から形成される積層体の製造方法について説明する。第1の位相差層と第2の位相差層とは、接着剤層又は第3の粘着剤層を介して積層される。
位相差層が1層である、第1実施形態に係る偏光板100の製造方法の例を以下で説明する。なお、本実施形態で使用される偏光子、粘着剤層、及び位相差層は上述の方法によって製造されたものを使用することができる。
第2実施形態に係る偏光板101の製造方法の例を以下で説明する。本実施形態で使用される偏光子、粘着剤層、及び位相差層は上述の方法によって製造されたものを使用することができる。
本発明の偏光板は、さまざまな表示装置に用いることができる。表示装置とは、表示素子を有する装置であり、発光源として発光素子又は発光装置を含む。表示装置としては、例えば、液晶表示装置、有機EL表示装置、無機エレクトロルミネッセンス(以下、無機ELともいう)表示装置、電子放出表示装置(例えば電場放出表示装置(FEDともいう)、表面電界放出表示装置(SEDともいう))、電子ペーパー(電子インクや電気泳動素子を用いた表示装置)、プラズマ表示装置、投射型表示装置(例えばグレーティングライトバルブ(GLVともいう)表示装置、デジタルマイクロミラーデバイス(DMDともいう)を有する表示装置)及び圧電セラミックディスプレイなどが挙げられる。
液晶表示装置は、透過型液晶表示装置、半透過型液晶表示装置などのいずれをも含む。
これらの表示装置は、2次元画像を表示する表示装置であってもよいし、3次元画像を表示する立体表示装置であってもよい。
本偏光板は、特に有機EL表示装置又は無機EL表示装置に特に有効に用いることができる。
粘着剤層形成用の(メタ)アクリル樹脂の重量平均分子量(Mw)は、ゲル浸透クロマトグラフィー(GPC)を用いて以下の条件で測定したポリスチレン換算の重量平均分子量である。
〔測定条件〕
・GPC測定装置:東ソー株式会社製,HLC-8020
・GPCカラム(以下の順に通過):東ソー株式会社製
TSK guard column HXL-H
TSK gel GMHXL(×2)
TSK gel G2000HXL
・測定溶媒:テトラヒドロフラン
・測定温度:40℃
偏光板及び粘着剤層の厚みは、株式会社ニコン製のデジタルマイクロメーターMH-15Mにより測定した。
位相差層の透湿度比は、以下のように測定した。
後述する粘着剤組成物Fを基材上にバーコーターを使用して塗布して、厚さが2~3μmの粘着剤組成物層を形成し、基材の透湿度評価用積層体を得た。基材には、コニカミノルタ株式会社製のトリアセチルセルロースフィルムを使用した。
前記基材の透湿度評価用積層体における粘着剤組成物層に位相差層をさらに積層し、位相差層の透湿度評価用積層体を得た。
得られた評価用積層体の透湿度を、JIS Z 0208:1976「防湿包装材料の透湿度試験方法(カップ法)」に準拠し、温度40℃、湿度90%RHにて測定した。
なお、使用したトリアセチルセルロースフィルムの厚さは、20μmであった。また、上記と同様にして求めたトリアセチルセルロースフィルム透湿度は、1200g/m2・24hであった。
前記基材の透湿度評価用積層体の透湿度は、1000g/m2・24hであった。
位相差層の透湿度評価用積層体の透湿度を測定し、前記基材の透湿度評価用積層体の透湿度で除すことにより、透湿度比を算出した。
温度40℃、湿度90%RHの条件において、水蒸気透過度測定機(Lyssy社製、機種名「Lyssy-L80-5000」)を用いて、粘着剤層の透湿度を測定した。
粘着剤は以下の方法により製造した。
攪拌機、温度計、還流冷却器、滴下装置及び窒素導入管を備えた反応容器に、アクリル酸n-ブチル97.0質量部、アクリル酸1.0質量部、アクリル酸2-ヒドロキシエチル0.5質量部、酢酸エチル200質量部、及び2,2'-アゾビスイソブチロニトリル0.08質量部を仕込み、上記反応容器内の空気を窒素ガスで置換した。窒素雰囲気下で攪拌しながら、反応溶液を60℃に昇温し、6時間反応させた後、室温まで冷却した。得られた溶液の一部の重量平均分子量を測定した所、180万の(メタ)アクリル酸エステル重合体の生成を確認した。
セパレータ(リンテック株式会社製:SP-PLR382190)の離型処理面(剥離層面)に、アプリケーターにより、乾燥後の厚さが6μm(粘着剤A)、10μm(粘着剤B)、15μm(粘着剤C)、20μm(粘着剤D)、25μm(粘着剤E)となるように前記塗工溶液を塗工した後、100℃で1分間乾燥し、粘着剤層のセパレータが貼合された面とは反対面に、もう1枚のセパレータ(リンテック社製:SP-PLR381031)を貼合し、両面セパレータ付き粘着剤層を得た。
粘着剤A、粘着剤B、粘着剤C、粘着剤D、粘着剤Eの透湿度(水蒸気透過度)はそれぞれ、8200g/m2・24h、6800g/m2・24h、6300g/m2・24h、4700g/m2・24h、3600g/m2・24hであった。
攪拌機、温度計、還流冷却器、滴下装置及び窒素導入管を備えた反応容器に、アクリル酸n-ブチル95.0質量部、アクリル酸4.0質量部、アクリル酸2-ヒドロキシエチル1.0質量部、酢酸エチル200質量部、及び2,2'-アゾビスイソブチロニトリル0.08質量部を仕込み、上記反応容器内の空気を窒素ガスで置換した。窒素雰囲気下で攪拌しながら、反応溶液を60℃に昇温し、6時間反応させた後、室温まで冷却した。得られた溶液の一部の重量平均分子量を測定した所、180万の(メタ)アクリル酸エステル重合体の生成を確認した。
セパレータ(リンテック株式会社製:SP-PLR382190)の離型処理面(剥離層面)に、アプリケーターにより、乾燥後の厚さが5μm(粘着剤F)となるように前記塗工溶液を塗工した後、100℃で1分間乾燥し、粘着剤層のセパレータが貼合された面とは反対面に、もう1枚のセパレータ(リンテック株式会社製:SP-PLR381031)を貼合した。この粘着剤層にベルトコンベア付き紫外線照射装置(フュージョンUVシステムズ社製、ランプはDバルブを使用)を用いて剥離シート越しに紫外線(照射強度500mW/cm2、積算光量500mJ/cm2)を照射し、両面セパレータ付き粘着剤層を得た。
粘着剤Fの水蒸気透過度は、7600g/m2・24hであった。
平均重合度約2400、ケン化度99.9モル%以上で厚さ30μmポリビニルアルコールフィルムを、乾式延伸により約5倍に一軸延伸し、さらに緊張状態を保ったまま、60℃の純水に1分間浸漬した後、ヨウ素:ヨウ化カリウム:水の質量比が 0.05:5:100である28℃の水溶液に60秒間浸漬した。その後、ヨウ化カリウム:ホウ酸:水の質量比が8.5:8.5:100である72℃の水溶液に300秒間浸漬した。引き続き26℃の純水で20秒間洗浄した後、65℃で乾燥し、ポリビニルアルコールフィルムにヨウ素が吸着配向している厚さ12μmの偏光子を得た。次に、この偏光子の片側に、水100部に対し、カルボキシ基変性ポリビニルアルコール〔(株)クラレから入手した商品名“KL-318”〕を3部溶解し、その水溶液に水溶性エポキシ樹脂であるポリアミドエポキシ系添加剤〔田岡化学工業(株)から入手した商品名“スミレーズレジン(登録商標)650(30)”、固形分濃度30%の水溶液〕を 1.5部添加したエポキシ系接着剤を塗工し、透明保護フィルムとして、厚さ30μmのノルボルネン系樹脂フィルムを貼り合せた。このフィルムの一方の表面には、表面処理が施されており、他方の面が偏光子との貼合面となるように貼合した。偏光子のもう一方の側には前記の接着剤を用いて、厚み20μmのトリアセチルセルロース系樹脂フィルムを貼合した。このようにして、偏光子の両面に保護フィルムが積層された厚み62μmの偏光子(1)を得た。
第1の位相差層として、ネマチック液晶化合物が硬化した層、配向膜、及び透明基材からなるλ/4の位相差を与える層を準備した。なお、ネマチック液晶化合物が硬化した層と、配向層との合計の厚みは2μmであった。また、第1の位相差層の透湿度比は0.48であった。
厚み38μmのポリエチレンテレフタレート基材を透明基材として用い、その片面に垂直配向層用組成物を膜厚3μmになるようにコーティングし、20mJ/cm2の偏光紫外線を照射して配向層を作製した。なお、その垂直配向層用組成物としては、2-フェノキシエチルアクリレートと、テトラヒドロフルフリルアクリレートと、ジペンタエリスリトールトリアクリレートと、ビス(2-ビニルオキシエチル)エーテルとを1:1:4:5の割合で混合し、重合開始剤としてLUCIRIN(登録商標)TPOを4%の割合で添加した混合物を用いた。
前記偏光子(1)のトリアセチルセルロース系樹脂フィルム側面に第1の粘着剤層として厚さ6μmの粘着剤Aを移着した。粘着剤Aに積層されたセパレートフィルムを剥がし、前記積層体(1)の第1の位相差層側の透明基材を剥がした面に積層した。前記積層体(1)における偏光子(1)に積層されている面と反対側の透明基材を剥がした。透明基材を剥がして露出した面に第2の粘着剤層として厚さ25μmの粘着剤Eを積層した。このようにして、保護フィルム、偏光子、保護フィルム、第1の粘着剤層、第1の位相差層(λ/4の位相差を与える層)、接着剤層、第2の位相差層(ポジティブC層)、及び第2の粘着剤層からなる偏光板を作製した。得られた偏光板の総厚みTpは、101μmであり、粘着剤層の厚みTaは31μmであった。
第1の粘着剤及び第2の粘着剤として表1に示す粘着剤を用いた以外は実施例1と同様に偏光板をそれぞれ作製した。得られた偏光板の総厚みTp及び粘着剤層の厚みTaを表1に示す。
[実施例7~8]
第1の粘着剤及び第2の粘着剤として表1に示すものを用い、位相差層として積層体(2)を用いた以外は実施例1と同様に偏光板を作製した。
第3の粘着剤層の厚さは、5μmであった。得られた偏光板の総厚みTp及び粘着剤層の厚みTaを表1に示す。
第1の粘着剤及び第2の粘着剤として表1に示すものを用い、位相差層として積層体(2)を用いた以外は実施例1と同様に偏光板を作製した。
第3の粘着剤層の厚さは、5μmであった。すなわち、偏光板の総厚みTp’は118μmであり、粘着剤層の厚みTa’は50μmであった。
[比較例2]
第1の粘着剤及び第2の粘着剤として表1に示す粘着剤を用いた以外は実施例1と同様に偏光板をそれぞれ作製した。得られた偏光板の総厚みTp及び粘着剤層の厚みTaを表1に示す。
上述の通り作製した偏光板の第2の粘着剤層のセパレートフィルムを剥がし無アルカリガラス板〔コーニング社製の“Eagle-XG”〕に貼合し、評価サンプルとした。前記評価サンプルをオートクレーブ中、温度50℃で圧力5MPaの条件下で20分間加圧処理を行ない、その後、温度23℃で相対湿度60%の雰囲気下で1日放置した。その後、65℃、湿度90%の環境に放置した。65℃、湿度90%の環境に評価サンプルを入れてから、168時間後、及び336時間後にサンプルの外観を目視にて確認した。
表1中、336時間経過時においても偏光板にしわが発生していなかったサンプルについては「A」、336時間の段階で偏光板にしわが確認されたサンプルは「B」、168時間の段階で偏光板にしわが確認されたサンプルは「C」と表記した。
Ta’/Tp’は、偏光板が第3の粘着剤層を含む場合の第1の粘着剤層の厚みT1(μm)と第2の粘着剤層の厚みT2(μm)と第3の粘着剤層の厚みT3(μm)の和であるTa’(μm)を偏光板の総厚みTp’(μm)で除した値を表す。
Claims (1)
- 単層の樹脂フィルムである偏光子の両面に保護フィルムが積層された両面保護フィルム付き偏光子と、第1の粘着剤層と、第1の位相差層と、第3の粘着剤層と、第2の位相差層と、第2の粘着剤層と、をこの順に含む偏光板であって、
前記第1の粘着剤層の厚みT1(μm)と前記第2の粘着剤層の厚みT2(μm)と前記第3の粘着剤層の厚みT3(μm)との和であるTa’(μm)を前記偏光板の総厚みTp’(μm)で除した値であるTa’/Tp’が0.40以下であり、
Tp’(μm)は、50μm以上113μm以下であり、
前記単層の樹脂フィルムである偏光子の厚みが15μm以下であり、
前記第1の位相差層および前記第2の位相差層は、液晶化合物が硬化した層であり、配向層を含んでいてもよく、
前記第1の位相差層および前記第2の位相差層の厚みは0.5μm以上5μm以下であり、
前記偏光子、前記第1の粘着剤層、前記第1の位相差層、前記第3の粘着剤層、前記第2の位相差層、および前記第2の粘着剤層のみが積層されている偏光板。