JP7353461B2 - コンパクトなアルミニウム合金熱処理方法 - Google Patents
コンパクトなアルミニウム合金熱処理方法 Download PDFInfo
- Publication number
- JP7353461B2 JP7353461B2 JP2022507538A JP2022507538A JP7353461B2 JP 7353461 B2 JP7353461 B2 JP 7353461B2 JP 2022507538 A JP2022507538 A JP 2022507538A JP 2022507538 A JP2022507538 A JP 2022507538A JP 7353461 B2 JP7353461 B2 JP 7353461B2
- Authority
- JP
- Japan
- Prior art keywords
- aluminum alloy
- alloy strip
- aluminum
- roll
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
一連の実験により、AA6016シリーズの1mmシート材料の場合、周囲温度から溶体化熱処理温度540℃に達するまでの時間は、片側から加熱した場合に30秒未満、540℃の温度を有する2つの金属ブロック間で直接的な接触させて両側から加熱したときに約10~15秒であることが示されている。誘導加熱などの追加の外部熱源を使用するなどして熱の投入を増やすことにより、この加熱時間を10秒未満に短縮できる。一方、工業規模の継続的なアニーリングの時間では、この溶体化熱処理温度になるまでに必要な加熱時間は、通常、45~55秒の範囲である。本発明の方法におけるこの相当な加熱時間の短縮は、とりわけ、アルミニウム合金ストリップの加熱速度の増加、及びこの効果を達成するのに必要な装置のサイズの大幅な縮小に起因し、より良好でより均一な結晶粒再結晶をもたらす。
- アルミニウム合金ストリップを使用して移動または移送する一方で、回転可能な加熱ロールの外面と熱伝達接触して、アルミニウム合金ストリップに熱を誘導して、アニーリング温度でアルミニウム合金ストリップを加熱するように適合された2つ以上の回転可能な加熱ロールを含む加熱セクション
- アルミニウム合金ストリップをアニーリング温度から100℃未満に急冷またはクエンチし、好ましくは少なくとも1つの回転可能な冷却ロールを含むクエンチセクション、
- 任意選択で、移動するアルミニウム合金ストリップの熱損失を調整し、回転可能な加熱ロールの外面と熱伝達接触していないアルミニウム合金ストリップの側面に面するように配置された、内部反射面を備えた1つ以上のヒートシールドまたはスクリーン、
- 任意選択で、回転可能な加熱ロールの外面と熱伝達接触している間のアルミニウム合金ストリップへの熱の投入に加えて、アルミニウム合金ストリップに熱を誘導するための、1つ以上の加熱手段、
- 任意選択で、レベラーが設けられるテンションコントローラ、及び
- 任意選択で、レベラーと第1の回転可能な加熱ロールの入口セクションとの間に設けられた張力コントローラ。
Tcが15秒、vが1 m/秒、Nが3、Kが0.75である第1次の大きさを設けるには、3つの加熱ロールのそれぞれについて2.12メートルの加熱ロールの直径になる。
Claims (11)
- 移動するアルミニウム合金ストリップの熱処理のための方法であって、前記アルミニウム合金ストリップは、上面及び下面を有し、前記方法は、前記アルミニウム合金ストリップを少なくとも2つの回転する加熱ロールに亘り移動させることを含む熱処理を含み、前記加熱ロールは外面を含み、前記アルミニウム合金ストリップの表面が前記加熱ロールの前記外面の一部と熱伝達接触して、前記アルミニウム合金ストリップに熱を誘導して前記アルミニウム合金ストリップをアニーリング温度に加熱するようにし、また前記アルミニウム合金ストリップを第1の回転する加熱ロールに亘り移動させ、続いて前記アルミニウム合金ストリップを第2の回転する加熱ロールに亘り移動させて、前記アルミニウム合金ストリップの前記上面と前記下面とが、前記回転する加熱ロールの前記外面と交互に熱伝達接触しているようにすること、を含み、
前記加熱ロールの前記外面が、窒化チタン、炭化タングステン、及び窒化クロムからなる群から選択されるセラミックコーティングでコーティングされている、方法。 - 前記アルミニウム合金ストリップが、一方の表面が回転する加熱ロールと熱伝達接触している間に移動し、前記アルミニウム合金ストリップの他方の表面の熱損失が、スクリーンの存在により調整される、請求項1に記載の方法。
- 前記熱処理後の前記アルミニウム合金ストリップを100℃未満にクエンチする、請求項1または2に記載の方法。
- 前記熱処理後の前記アルミニウム合金ストリップが、前記アルミニウム合金ストリップを少なくとも1つの回転する冷却ロールに亘り移動させることによって100℃未満にクエンチされ、前記回転する冷却ロールが外面を含み、前記アルミニウム合金ストリップの表面が前記回転する冷却ロールの前記外面と熱伝達接触して、前記アルミニウム合金ストリップから熱を除去し、前記アルミニウム合金ストリップを100℃未満の温度で冷却する、請求項1から3のいずれか一項に記載の方法。
- 前記アニーリング温度が400℃から590℃の範囲である、請求項1から4のいずれか一項に記載の方法。
- 前記加熱ロールが1から3メートルの範囲の直径を有する、請求項1から5のいずれか一項に記載の方法。
- 前記加熱ロールが金属から作られ、前記金属が鋳鉄、鋼、ステンレス鋼、銅、銅ベースの合金、及びアルミニウム合金の群から選択される、請求項1から6のいずれか一項に記載の方法。
- 前記アルミニウム合金ストリップが、0.3mmから4.5mmの範囲の厚さを有する、請求項1から7のいずれか一項に記載の方法。
- 前記アルミニウム合金ストリップが、AA2XXX、AA5XXX、AA6XXX、またはAA7XXXシリーズのアルミニウム合金の中の組成を有する、請求項1から8のいずれか一項に記載の方法。
- 請求項3または4に記載の方法を実施するための設備であって、アルミニウム合金ストリップを使用して移動または移送する一方で、回転可能な加熱ロールの前記外面と熱伝達接触して、前記アルミニウム合金ストリップに熱を誘導して、アニーリング温度で前記アルミニウム合金ストリップを加熱するように適合された2つ以上の回転可能な加熱ロールを含む加熱セクション、及び前記アルミニウム合金ストリップを前記アニーリング温度から100℃未満に急冷またはクエンチするためのクエンチセクションを含むことを特徴とする、設備。
- 移動するアルミニウム合金ストリップの熱損失を調整するために、アルミニウム合金ストリップの一方の表面が回転可能な加熱ロールの前記外面と熱伝達接触している間に、前記アルミニウム合金ストリップの他方の表面に面するように配置された1つまたは複数のスクリーンを備える、請求項10に記載の設備。