JP7337333B1 - タイヤ - Google Patents
タイヤ Download PDFInfo
- Publication number
- JP7337333B1 JP7337333B1 JP2022101537A JP2022101537A JP7337333B1 JP 7337333 B1 JP7337333 B1 JP 7337333B1 JP 2022101537 A JP2022101537 A JP 2022101537A JP 2022101537 A JP2022101537 A JP 2022101537A JP 7337333 B1 JP7337333 B1 JP 7337333B1
- Authority
- JP
- Japan
- Prior art keywords
- mass
- less
- parts
- rubber
- rubber layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量20質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、80質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成され
ており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)と前記トレッド部の厚みG(mm)とが、(30℃E * ×G)≦80を満足していることを特徴とするタイヤである。
最初に、本発明に係るタイヤの特徴について説明する。
本発明に係るタイヤは、トレッド部を備えたタイヤであって、トレッド部を形成するキャップゴム層が、スチレン量20質量%以下のSBRを、ゴム成分100質量部中に60質量部以上、80質量部以下含有すると共に、ゴム成分100質量部に対してシリカを100質量部以下含有し、温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成されている。そして、トレッド部の厚みが、6mm以上、12mm以下であり、キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)と前記トレッド部の厚みG(mm)とが、(30℃E * ×G)≦80を満足している。
本発明に係るタイヤにおける前記の効果発現のメカニズムについては、以下のように考えられる。
本発明に係るタイヤは、以下の態様を採ることにより、さらに大きな効果を得ることができる。
本発明において、キャップゴム層のガラス転移温度(Tg)は、-10℃以下であることが好ましく、―30℃以下であるとより好ましい。ガラス転移温度(Tg)が-10℃以下である場合、走行温度である常温においてゴムが軟らかくなり、路面に対して力を伝え易くなるため、発進時の転がり抵抗性が向上する。なお、Tgの下限は特に限定されないが、-60℃以上であることが好ましく、―50℃以上であるとより好ましい。
複素弾性率E*は、ゴム層の剛性を示すパラメータであり、キャップゴム層の複素弾性率が小さいほどゴム層の剛性は小さく路面に力を伝えやすくなるため、発進時の転がり抵抗性が向上すると考えられる。また、前記したように、トレッドの厚み(ゲージ)を薄くした方が、力の伝達効率がよくなるため、発進時の転がり抵抗性が向上すると考えられる。
30℃E*×G≦80
本発明において、トレッド部は、キャップゴム層の1層のみで形成されていてもよく、キャップゴム層の内側にベースゴム層を設けて、2層にされていてもよく、また、3層でもよく、4層以上であってもよい。この場合、トレッド部全体におけるキャップゴム層の厚みは、10%以上であることが好ましい。これにより、トレッド部表面と路面との間に生じたエネルギーを十分に伝達できるため、発進時の転がり抵抗性をさらに向上させることができると考えられる。なお、トレッド部全体におけるキャップゴム層の厚みは、70%以上であるとより好ましい。
本発明において、シリカの粒子径(平均一次粒子径)としては、ポリマーとの摩擦のし易さなどを考慮すると、17nm以下であることが好ましい。
本発明において、キャップゴム層を形成するゴム組成物には、樹脂成分が含有されていることが好ましい。
本発明において、キャップゴム層のアセトン抽出分(AE)は、13質量%以上であることが好ましく、19質量%以上であるとより好ましく、25質量%以上であるとさらに好ましい。一方、上限としては特に限定されないが、34質量%以下であることが好ましく、32質量%以下であるとより好ましく、30質量%以下であるとさらに好ましい。
アセトン抽出量(%)={(抽出前のゴム試験片の質量-抽出後のゴム試験片の質量)
/(抽出前のゴム試験片の質量)}×100
本発明に係るタイヤにおいては、正規リムに組み込み、正規内圧としたタイヤのトレッド部におけるランド比が、55%以上であることが好ましく、60%以上がより好ましい。
V={(Dt/2)2-(Dt/2-Ht)2}×π×Wt
WL=0.000011×V+175
WL:正規荷重(kg)
V:タイヤの仮想体積(mm3)
Dt:タイヤ外径Dt(mm)
Ht:タイヤの断面高さ(mm)
Wt:タイヤの断面幅(mm)
扁平率は後述の通り、タイヤ断面幅に対する断面高さであり、この比率が小さいほどトレッド部で得られた摩擦に対して、タイヤ幅方向に変形する部分の割合を小さくし、力を伝達しやすくなると考えられ、発進時の転がり抵抗性をさらに向上させることができると考えられる。その一方、扁平率が低くなると、サイド部でのたわみ量が小さくなるため、乗り心地性能の悪化を招く恐れがある。
扁平率(%)=(Ht/Wt)×100(%)
Ht=(Dt-R)/2
以下、実施の形態に基づいて、本発明を具体的に説明する。
本発明に係るタイヤにおいて、キャップゴム層を形成するゴム組成物は、以下に記載するゴム成分、充填剤、軟化剤、加硫剤および加硫促進剤等の各種配合材料について、その種類や量を、適宜、調整することにより得ることができる。
(a)ゴム成分
ゴム成分としては特に限定されず、イソプレン系ゴム、ブタジエンゴム(BR)、スチレンブタジエンゴム(SBR)、ニトリルゴム(NBR)などのジエン系ゴム、ブチルゴムなどのブチル系ゴム、スチレンブタジエンスチレンブロック共重合体(SBS)、スチレンブタジエンブロック共重合体(SB)などの熱可塑性エラストマーなど、タイヤの製造に一般的に用いられるゴム(ポリマー)を用いることができる。
SBRの重量平均分子量は、例えば、10万超、200万未満である。そして、本発明においては、前記したように、SBR成分中におけるスチレン量を25質量%以下とする。SBRのビニル含量(1,2-結合ブタジエン含量)は、例えば、5質量%超、70質量%未満である。なお、SBRのビニル含量とは、SBR成分内におけるブタジエン部全体に対する1,2-結合ブタジエン含量を指す。また、SBRの構造同定(スチレン量、ビニル含量の測定)は、例えば、日本電子(株)製JNM-ECAシリーズの装置を用いて行うことができる。
本発明において、ゴム組成物には、BRを含んでもよい。この場合、ゴム成分100質量部中のBRの含有量は、20質量部以上、40質量部以下であることが好ましく、25質量部以上、35質量部以下であるとより好ましい。
本発明において、ゴム組成物には、必要に応じて、イソプレン系ゴムを含んでもよい。この場合、ゴム成分100質量部中のイソプレン系ゴムの含有量は、10質量部以上、30質量部以下であることが好ましく、15質量部以上、25質量部以下であるとより好ましい。
また、その他のゴム成分として、ニトリルゴム(NBR)等のタイヤの製造に一般的に用いられるゴム(ポリマー)を含んでもよい。
(イ)充填剤
本発明において、ゴム組成物には、前記したように、充填剤として、シリカを含有しているが、その他の充填剤を含有してもよい。シリカ以外の具体的な充填剤としては、例えば、カーボンブラック、グラファイト、炭酸カルシウム、タルク、アルミナ、クレー、水酸化アルミニウム、マイカなどを挙げることができる。
本発明において、ゴム組成物に含有されるシリカのBET比表面積は、良好な耐久性能が得られる観点から140m2/g超が好ましく、160m2/g超がより好ましい。一方、良好な高速走行時の転がり抵抗性を得られる観点からは250m2/g未満が好ましく、220m2/g未満であることがより好ましい。なお、上記したBET比表面積は、ASTM D3037-93に準じてBET法で測定されるN2SAの値である。
本発明のキャップゴム層を形成するゴム組成物には、シリカと共にシランカップリング剤を含有することが好ましい。
本発明において、ゴム組成物には、補強性の観点からカーボンブラックを含むことが好ましい。
ゴム組成物には、必要に応じて、前記したシリカ(シランカップリング剤)やカーボンブラックの他に、タイヤ工業において一般的に用いられている、例えば、グラファイト、炭酸カルシウム、タルク、アルミナ、クレー、水酸化アルミニウム、マイカ等の充填剤をさらに含有してもよい。これらの含有量は、ゴム成分100質量部に対して、例えば、0.1質量部超、200質量部未満である。
ゴム組成物は、ゴムを軟化させる成分として、オイル(伸展油を含む)、液状ゴム、および樹脂を可塑剤成分として含んでもよい。なお、可塑剤成分は、加硫ゴム中からアセトンにより抽出可能な成分である。可塑剤成分の合計含有量は、ゴム成分100質量部に対して、30質量部以上であることが好ましく、50質量部以上であるとより好ましく、70質量部以上であるとさらに好ましい。一方、110質量部以下であることが好ましく、100質量部以下であるとより好ましく、90質量部以下であるとさらに好ましい。なお、ゴム成分として油展ゴムが使用されている場合には、油展オイル量も、オイルの含有量に含まれる。
オイルとしては、例えば、鉱物油(一般にプロセスオイルと言われる)、植物油脂、またはその混合物が挙げられる。鉱物油(プロセスオイル)としては、例えば、パラフィン系プロセスオイル、アロマ系プロセスオイル、ナフテン系プロセスオイルなどを用いることができる。植物油脂としては、ひまし油、綿実油、あまに油、なたね油、大豆油、パーム油、やし油、落花生油、ロジン、パインオイル、パインタール、トール油、コーン油、こめ油、べに花油、ごま油、オリーブ油、ひまわり油、パーム核油、椿油、ホホバ油、マカデミアナッツ油、桐油等が挙げられる。これらは、単独で用いてもよく、2種以上を併用してもよい。また、ライフサイクルアセスメントの観点から、ゴム混合用のミキサーや自動車用エンジンなどの潤滑油として用いられた後の廃オイルや、廃食用油などを適宜用いてもよい。
可塑剤成分として用いる液状ゴムとは、常温(25℃)で液体状態の重合体であり、加硫後のタイヤからアセトン抽出により抽出可能なゴム成分である。液状ゴムとしては、ファルネセン系ポリマー、液状ジエン系重合体及びそれらの水素添加物等が挙げられる。
樹脂成分は、粘着性付与成分としても機能し、常温で固体であっても、液体であってもよく、具体的な樹脂成分としては、例えば、ロジン系樹脂、スチレン系樹脂、クマロン系樹脂、テルペン系樹脂、C5樹脂、C9樹脂、C5C9樹脂、アクリル系樹脂などの樹脂が挙げられ、2種以上を併用しても良い。樹脂成分の含有量は、ゴム成分100質量部に対して、2質量部超で、45質量部未満が好ましく、30質量部未満がより好ましい。なお、これらの樹脂成分は、必要に応じて、シリカ等と反応できる変性基を付与してもよい。
本発明において、ゴム組成物には、ステアリン酸を含むことが好ましい。ステアリン酸の含有量は、ゴム成分100質量部に対して、例えば、0.5質量部超、10.0質量部未満である。ステアリン酸としては、従来公知のものを使用でき、例えば、日油(株)、NOF社、花王(株)、富士フイルム和光純薬(株)、千葉脂肪酸(株)等の製品を使用できる。
本発明において、ゴム組成物には、老化防止剤を含むことが好ましい。老化防止剤の含有量は、ゴム成分100質量部に対して、例えば、0.5質量部超、10質量部未満であり、1質量部以上がより好ましい。
本発明において、ゴム組成物には、ワックスを含むことが好ましい。ワックスの含有量は、ゴム成分100質量部に対して、例えば、0.5~20質量部、好ましくは1.0~15質量部、より好ましくは1.5~10質量部である。
ゴム組成物は、酸化亜鉛を含んでもよい。酸化亜鉛の含有量は、ゴム成分100質量部に対し、例えば、0.5質量部超、10質量部未満である。酸化亜鉛としては、従来公知のものを使用でき、例えば、三井金属鉱業(株)、東邦亜鉛(株)、ハクスイテック(株)、正同化学工業(株)、堺化学工業(株)等の製品を使用できる。
ゴム組成物は、硫黄等の架橋剤を含むことが好ましい。架橋剤の含有量は、ゴム成分100質量部に対して、例えば、0.1質量部超、10.0質量部未満である。
ゴム組成物には、前記成分の他、タイヤ工業において一般的に用いられている添加剤、例えば、脂肪酸金属塩、カルボン酸金属塩、有機過酸化物、リバージョン(加硫戻り)防止剤等を、必要に応じて、さらに配合してもよい。これらの添加剤の含有量は、ゴム成分100質量部に対して、例えば、0.1質量部超、200質量部未満である。
キャップゴム層を形成するゴム組成物は、前記した各種配合材料の適宜、調整して、一般的な方法、例えば、ゴム成分とカーボンブラック等のフィラーとを混練するベース練り工程と、前記ベース練り工程で得られた混練物と架橋剤とを混練する仕上げ練り工程とを含む製造方法により作製される。
本発明に係るタイヤは、前記で得られたゴム組成物をキャップゴム層として、所定の形状のトレッドゴムに成形した後、他のタイヤ部材と共に、タイヤ成型機上にて通常の方法で成形することにより、未加硫タイヤとして作製することができる。
(1)配合材料
(a)ゴム成分
(イ)NR:TSR20
(ロ)BR:宇部興産(株)製のウベポールBR150B(ハイシスBR)
(シス含量97質量%、トランス含量2質量%、ビニル含量1質量%)
(ハ)SBR-1:下記(製造例1)に示す方法により得られる変性S-SBR
(スチレン量:25質量%、ビニル含量:25質量%)
(ニ)SBR-2:JSR(株)製のHPR850(変性S-SBR)
(スチレン量:27.5質量%、ビニル含量:59.0質量%)
(ホ)SBR-3:下記(製造例2)に示す方法により得られる変性S-SBR
(スチレン量:36質量%、ビニル含量:49質量%、25%油展品)
(ヘ)SBR-4:JSR(株)製のHPR840(S-SBR)
(スチレン量:10質量%、ビニル含量:42質量%)
上記SBR-1は、以下の手順に従って作製する。まず、内容積10Lで、底部に入口、頭部に出口を有し、撹拌機およびジャケットを付けたオートクレーブを反応器として2基直列に連結し、ブタジエン、スチレン、シクロヘキサンを各々所定の比率で混合する。この混合溶液を、活性アルミナを充填した脱水カラムを経由し、不純物を除去するためにn-ブチルリチウムをスタティックミキサー中で混合した後、1基目の反応器底部より連続的に供給し、さらに極性物質として2,2-ビス(2-オキソラニル)プロパンを、重合開始剤としてn-ブチルリチウムを所定の速度でそれぞれ1基目の反応器底部より連続的に供給し、反応器内温を95℃に保持する。反応器頭部より重合体溶液を連続的に抜き出し、2基目の反応器へ供給した。2基目の反応器の温度を95℃に保ち、変性剤としてテトラグリシジル-1,3-ビスアミノメチルシクロヘキサン(単量体)と、オリゴマー成分との混合物を所定の速度でシクロヘキサン1000倍希釈液として連続的に加えて変性反応を行なう。この重合体溶液を反応器から連続的に抜き出し、スタティックミキサーで連続的に酸化防止剤を添加した後、溶媒を除去し目的とする変性ジエン系重合体(SBR-1)を得る。
上記SBR-3は、以下の手順に従って作製する。窒素置換されたオートクレーブ反応器に、シクロヘキサン、テトラヒドロフラン、スチレン、及び1,3-ブタジエンを仕込む。反応器の内容物の温度を20℃に調整した後、n-ブチルリチウムを添加して重合を開始する。断熱条件で重合し、最高温度は85℃以下に保持する。重合転化率が99%に達した時点で1,3-ブタジエンを追加し、更に5分重合させた後、N,N-ビス(トリメチルシリル)-3-アミノプロピルトリメトキシシランを変性剤として加えて反応を行う。重合反応終了後、2,6-ジ-tert-ブチル-p-クレゾールを添加する。次いで、スチームストリッピングにより脱溶媒を行い、110℃に調温された熱ロールにより乾燥した後、重合体100質量部に対して25質量部のオイルを練り込み、目的とする油展変性ジエン系重合体(SBR-3)SBR-3を得る。
上記SBR-1、SBR-3のビニル含量(単位:質量%)は、赤外分光分析法により、ビニル基の吸収ピークである910cm-1付近の吸収強度より求める。また、スチレン量(単位:質量%)は、JIS K6383(1995)に従って、屈折率より求める。
(イ)カーボンブラック:三菱化学社製のダイヤブラックN220
(N2SA:115m2/g)
(ロ)シリカ:エボニックインダストリーズ社製のウルトラシルVN3
(N2SA:175m2/g、平均一次粒子径:17nm)
(ハ)シランカップリング剤:エボニックインダストリーズ社製のSi266
(ビス(3-トリエトキシシリルプロピル)ジスルフィド)
(ニ)樹脂:クレイトン社製のSYLVATRAXX4401
(α-メチルスチレン系樹脂)
(ホ)オイル:出光興産(株)製のダイアナプロセスNH-70S
(アロマ系プロセスオイル)
(ヘ)ステアリン酸:日油(株)製のビーズステアリン酸「椿」
(ト)酸化亜鉛:三井金属鉱業(株)製の酸化亜鉛2種
(チ)硫黄:鶴見化学工業(株)製の粉末硫黄(5%オイル含有)
(リ)加硫促進剤-1:大内新興化学工業(株)製のノクセラーCZ
(N-シクロヘキシル-2-ベンゾチアジルスルフェンアミド(CBS))
(ヌ)加硫促進剤-2:住友化学工業(株)製のソクシールD(DPG)
(N,N’-ジフェニルグアニジン)
表2、表3に示す各配合内容に従い、バンバリーミキサーを用いて、硫黄および加硫促進剤以外の材料を150℃の条件下で5分間混練りして、混練物を得る。なお、各配合量は、質量部である。
並行して、ベースゴム層を形成するゴム組成物を表1に示す配合に基づいて、キャップゴム層を形成するゴム組成物の製造と同様にして、ベースゴム層を形成するゴム組成物を得る。
得られた各ゴム組成物を用いて、(キャップゴム層/ベースゴム層)比率が80:20となるように、所定の形状で押出成形して、表2~表4に示す厚みG(mm)のトレッド部を形成させる。
その後、各試験用タイヤについて、以下のパラメータを求める。
各試験用タイヤのトレッド部のキャップゴム層から、タイヤ周方向が長辺となるように、長さ20mm×幅4mm×厚さ2mmで切り出して、粘弾性測定用ゴム試験片を作製し、各ゴム試験片について、GABO社製のイプレクサーシリーズを用いて、測定温度:30℃、周波数10Hz、初期歪5%、動歪1%、変形モード:引張の条件下、tanδを測定する(30℃tanδ)。なお、ベースゴム層の30℃tanδは、0.07とする。
キャップゴム層から同様に切り出して作製した粘弾性測定用ゴム試験片について、GABO社製「イプレクサー(登録商標)」を用いて、周波数10Hz、初期歪2%、振幅±1%及び昇温速度2℃/minの条件下、-60℃から40℃まで温度を変化させてtanδを測定し、得られた温度分布曲線における最も大きいtanδ値に対応する温度を、Tg(℃)として求める。
キャップゴム層から同様に切り出して作製した粘弾性測定用ゴム試験片について、GABO社製のイプレクサーシリーズを用いて、測定温度30℃、周波数10Hz、初期歪5%、動歪1%、変形モード:伸長の条件下、E*(MPa)を測定する(30℃E*)。なお、ベースゴム層の30℃E*は、5MPaとする。
各試験用タイヤのトレッド部のキャップゴム層から切り出した加硫ゴム試験片を用い、JIS K 6229:2015に準拠してAE(質量%)を求める。
そして、各試験用タイヤの仕様、および、配合内容に基づいて、スチレン量25質量%以下のスチレンブタジエンゴム(SBR)の含有量(質量部)とランド比(%)との積を求めると共に、充填剤の含有量(質量部)と扁平率(%)との積を求める。
各試験用タイヤを車輌(国産のFR乗用車、排気量2000cc)の全輪に装着させて、内圧が250kPa(乗用車の正規内圧)となるように空気を充填した後、ドライアスファルト路面のテストコース上で走行を開始し、静止状態から10km/hに到達するまで加速距離を測定する。
(発進時の転がり抵抗性能指数)
=(比較例1の結果)/(各試験用タイヤの結果)×100
トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量20質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、80質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成されており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)と前記トレッド部の厚みG(mm)とが、(30℃E * ×G)≦80を満足していることを特徴とするタイヤである。
トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量25質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、80質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成され
ており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)と前記トレッド部の厚みG(mm)とが、(30℃E * ×G)≦80を満足しており、
前記キャップゴム層の内側にベースゴム層が設けられ、前記ベースゴム層の周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)が、前記キャップゴム層の30℃E * (MPa)より小さいことを特徴とするタイヤである。
トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量25質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、75質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成され
ており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
ランド比が、55%以上であり、
前記キャップゴム層のゴム成分100質量部中におけるスチレン量25質量%以下のSBR含有量(質量部)に対する前記ランド比(%)の比[ランド比(%)]/[ゴム成分100質量中におけるスチレン量25質量%以下のSBR含有量(質量部)]が、1.5未満であることを特徴とするタイヤである。
トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量25質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、80質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成され
ており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
扁平率が、30%以上、60%以下であり、
前記扁平率と前記キャップゴム層のゴム成分100質量部に対する充填剤の含有量の積[扁平率(%)]×[充填剤の含有量(質量部)]が、7500未満であることを特徴とするタイヤである。
前記スチレンブタジエンゴム(SBR)のスチレン量が、20質量%以下であることを特徴とし、本発明(2)から(4)のいずれかとの任意の組合せのタイヤである。
前記スチレンブタジエンゴム(SBR)のスチレン量が、15質量%以下であることを特徴とし、本発明(1)から(4)のいずれかとの任意の組合せのタイヤである。
前記30℃tanδが、0.20以下であることを特徴とし、本発明(1)から(4)のいずれかとの任意の組合せのタイヤである。
前記トレッド部の厚みが、7mm以上、10mm以下であることを特徴とし、本発明(1)から(4)のいずれかとの任意の組合せのタイヤである。
前記キャップゴム層のガラス転移温度(Tg)が、-10℃以下であることを特徴とし、本発明(1)から(4)のいずれかとの任意の組合せのタイヤである。
前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E*)(MPa)と前記トレッド部の厚みG(mm)とが、(30℃E * ×G)≦80を満足していることを特徴とし、本発明(3)または(4)に記載のタイヤである。
前記(30℃E * ×G)が、60以下であることを特徴とし、本発明(1)、(2)、(10)のいずれかとの任意の組合せのタイヤである。
前記(30℃E * ×G)が、40以下であることを特徴とし、本発明(11)に記載のタイヤである。
前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)が、8.00MPa以下であることを特徴とし、本発明(1)、(2)、(10)のいずれかとの任意の組合せのタイヤである。
前記トレッド部が、前記キャップゴム層および前記キャップゴム層の内側に設けられたベースゴム層とで形成されており、前記キャップゴム層の厚みが、前記トレッド部全体の厚みに対して、10%以上、100%未満であることを特徴とし、本発明(1)から(4)のいずれかとの任意の組み合わせのタイヤである。
本発明(15)は、
前記キャップゴム層を形成するゴム組成物における前記シリカの含有量が、ゴム成分100質量部に対して90質量部以下であることを特徴とし、本発明(1)から(4)のいずれかとの任意の組み合わせのタイヤである。
本発明(16)は、
ランド比が、55%以上であり、
前記キャップゴム層のゴム成分100質量部中におけるスチレン量25質量%以下のSBR含有量(質量部)に対する前記ランド比(%)の比[ランド比(%)]/[ゴム成分100質量中におけるスチレン量25質量%以下のSBR含有量(質量部)]が、1.5未満であることを特徴とし、本発明(1)、(2)、(4)のいずれかとの任意に組み合わせのタイヤである。
本発明(17)は、
扁平率が、30%以上、60%以下であり、
前記扁平率と前記キャップゴム層のゴム成分100質量部に対する充填剤の含有量の積[扁平率(%)]×[充填剤の含有量(質量部)]が、7500未満であることを特徴とし、本発明(1)から(3)のいずれかとの任意の組み合わせのタイヤである。
Claims (17)
- トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量20質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、80質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成されており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)と前記トレッド部の厚みG(mm)とが、(30℃E * ×G)≦80を満足していることを特徴とするタイヤ。 - トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量25質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、80質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成されており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)と前記トレッド部の厚みG(mm)とが、(30℃E * ×G)≦80を満足しており、
前記キャップゴム層の内側にベースゴム層が設けられ、前記ベースゴム層の周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E * )(MPa)が、前記キャップゴム層の30℃E * (MPa)より小さいことを特徴とするタイヤ。 - トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量25質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、75質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成されており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
ランド比が、55%以上であり、
前記キャップゴム層のゴム成分100質量部中におけるスチレン量25質量%以下のSBR含有量(質量部)に対する前記ランド比(%)の比[ランド比(%)]/[ゴム成分100質量中におけるスチレン量25質量%以下のSBR含有量(質量部)]が、1.5未満であることを特徴とするタイヤ。 - トレッド部を備えたタイヤであって、
前記トレッド部を形成するキャップゴム層が、
スチレン量25質量%以下のスチレンブタジエンゴム(SBR)を、ゴム成分100質量部中に60質量部以上、80質量部以下含有すると共に、
前記ゴム成分100質量部に対して、シリカを100質量部以下含有し、
温度30℃、周波数10Hz、初期歪5%、動歪率1%の条件下、変形モード:引張で測定された損失正接(30℃tanδ)が、0.25以下であるゴム組成物から形成されており、
前記トレッド部の厚みが、6mm以上、12mm以下であり、
扁平率が、30%以上、60%以下であり、
前記扁平率と前記キャップゴム層のゴム成分100質量部に対する充填剤の含有量の積[扁平率(%)]×[充填剤の含有量(質量部)]が、7500未満であることを特徴とするタイヤ。 - 前記スチレンブタジエンゴム(SBR)のスチレン量が、20質量%以下であることを特徴とする請求項2ないし請求項4のいずれか1項に記載のタイヤ。
- 前記スチレンブタジエンゴム(SBR)のスチレン量が、15質量%以下であることを特徴とする請求項1ないし請求項4のいずれか1項に記載のタイヤ。
- 前記30℃tanδが、0.20以下であることを特徴とする請求項1ないし請求項4のいずれか1項に記載のタイヤ。
- 前記トレッド部の厚みが、7mm以上、10mm以下であることを特徴とする請求項1ないし請求項4のいずれか1項に記載のタイヤ。
- 前記キャップゴム層のガラス転移温度(Tg)が、-10℃以下であることを特徴とする請求項1ないし請求項4のいずれか1項に記載のタイヤ。
- 前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E*)(MPa)と前記トレッド部の厚みG(mm)とが、(30℃E*×G)≦80を満足していることを特徴とする請求項3または請求項4に記載のタイヤ。
- 前記(30℃E*×G)が、60以下であることを特徴とする請求項1、請求項2、請求項10のいずれか1項に記載のタイヤ。
- 前記(30℃E*×G)が、40以下であることを特徴とする請求項11に記載のタイヤ。
- 前記キャップゴム層の温度30℃、周波数10Hz、初期歪5%、動歪率1%、変形モード:伸長で測定された複素弾性率(30℃E*)(MPa)が、8.00MPa以下であることを特徴とする請求項1、請求項2、請求項10のいずれか1項に記載のタイヤ。
- 前記トレッド部が、前記キャップゴム層および前記キャップゴム層の内側に設けられたベースゴム層とで形成されており、前記キャップゴム層の厚みが、前記トレッド部全体の厚みに対して、10%以上、100%未満であることを特徴とする請求項1ないし請求項4のいずれか1項に記載のタイヤ。
- 前記キャップゴム層を形成するゴム組成物における前記シリカの含有量が、ゴム成分100質量部に対して90質量部以下であることを特徴とする請求項1ないし請求項4のいずれか1項に記載のタイヤ。
- ランド比が、55%以上であり、
前記キャップゴム層のゴム成分100質量部中におけるスチレン量25質量%以下のSBR含有量(質量部)に対する前記ランド比(%)の比[ランド比(%)]/[ゴム成分100質量中におけるスチレン量25質量%以下のSBR含有量(質量部)]が、1.5未満であることを特徴とする請求項1、請求項2、請求項4のいずれか1項に記載のタイヤ。 - 扁平率が、30%以上、60%以下であり、
前記扁平率と前記キャップゴム層のゴム成分100質量部に対する充填剤の含有量の積[扁平率(%)]×[充填剤の含有量(質量部)]が、7500未満であることを特徴とする請求項1ないし請求項3のいずれか1項に記載のタイヤ。