JP7313243B2 - Powder deodorant composition for shoes, containerized powder deodorant composition, and deodorizing method - Google Patents
Powder deodorant composition for shoes, containerized powder deodorant composition, and deodorizing method Download PDFInfo
- Publication number
- JP7313243B2 JP7313243B2 JP2019169445A JP2019169445A JP7313243B2 JP 7313243 B2 JP7313243 B2 JP 7313243B2 JP 2019169445 A JP2019169445 A JP 2019169445A JP 2019169445 A JP2019169445 A JP 2019169445A JP 7313243 B2 JP7313243 B2 JP 7313243B2
- Authority
- JP
- Japan
- Prior art keywords
- component
- shoes
- deodorant composition
- powder deodorant
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、靴用粉末消臭剤組成物、容器入り粉末消臭剤組成物、及び消臭方法に関する。 TECHNICAL FIELD The present invention relates to a powder deodorant composition for shoes, a containerized powder deodorant composition, and a deodorizing method.
臭気に対する意識の高まりから、消臭を目的としたケア用品が使用されている。ケア用品としては、例えば、液体の消臭剤組成物をトリガースプレー容器又はエアゾール容器に封入した製品が汎用されている。
しかし、液体の消臭剤組成物は、靴や靴下の臭気に対する消臭効果が低かった。
こうした問題に対して、靴等の消臭を目的とした粉末消臭剤組成物が提案されている（特許文献１～４）。
このうち特許文献４では、消臭成分と共にメントールを配合している。
Due to the heightened awareness of odors, care products for the purpose of deodorizing are used. As care products, for example, products in which a liquid deodorant composition is sealed in a trigger spray container or an aerosol container are widely used.
However, the liquid deodorant composition has a low deodorizing effect on the odor of shoes and socks.
To address these problems, powder deodorant compositions have been proposed for the purpose of deodorizing shoes and the like (Patent Documents 1 to 4).
Among them, in Patent Document 4, menthol is blended together with a deodorizing component.
特許文献４において、メントールは、その昇華作用により消臭成分の拡散を助けると共に、昇華する際に足に清涼感を与え、消臭成分等の存在を体感させる効果を奏する。
しかしメントールのような冷感付与物質は、皮膚に直接触れた際には充分な冷感付与効果を奏するが、靴下をはいている場合は、靴下ごしに冷感を感じられない場合がある。また、冷感を感じるまでに長時間を要する場合がある。
そこで、本発明は、冷感又は温感を付与する物質を含み、使用者が靴下をはいたときであっても、冷感や温感を迅速に感じさせることが可能な、靴用粉末消臭剤組成物、容器入り粉末消臭剤組成物、及び消臭方法を提供することを目的とする。
In Patent Document 4, menthol aids diffusion of the deodorizing component by its sublimation action, and gives a cool feeling to the feet when sublimated, and has the effect of making the presence of the deodorant component feel.
However, although a cooling sensation imparting substance such as menthol exerts a sufficient cooling sensation imparting effect when in direct contact with the skin, the cooling sensation may not be felt through socks when wearing socks. In addition, it may take a long time to feel a cold sensation.
Accordingly, an object of the present invention is to provide a powder deodorant composition for shoes, a container-packaged powder deodorant composition, and a deodorizing method, which contain a substance that imparts a cold or warm feeling and can quickly make the user feel cold or warm even when wearing socks.
上記の課題を達成するために、本発明は以下の構成を採用した。
［１］下記（Ａ）成分及び（Ｂ）成分を含む靴用粉末消臭剤組成物であって、
粒径が５０μｍ以下の粒子の質量が、前記靴用粉末消臭剤組成物の総質量に対して３０質量％以上であることを特徴とする靴用粉末消臭剤組成物。
（Ａ）成分：消臭成分
（Ｂ）成分：皮膚に接触したときに冷感又は温感を付与する物質
［２］前記（Ｂ）成分からなる粒子又は前記（Ｂ）成分を含む粒子の体積平均粒子径が５０μｍ以下である、［１］に記載の靴用粉末消臭剤組成物。
［３］前記（Ｂ）成分が、メントール、メントン、カンファー、プレゴール、イソプレゴール、シネオール、ハッカオイル、ペパーミントオイル、スペアーミントオイル、ユーカリプタスオイル、３－ｌ－メントキシプロパン－１，２－ジオール、Ｎ－アルキル－ｐ－メンタン－３－カルボキサミド、３－ｌ－メントキシ－２－メチルプロパン－１，２－ジオール、ｐ－メンタン－３，８－ジオール、２－ｌ－メントキシエタン－１－オール、３－ｌ－メントキシプロパン－１－オール、４－ｌ－メントキシブタン－１－オール（３－ヒドロキシブタン酸メンチル）、乳酸メンチル、メントールグリセリンケタール、Ｎ－メチル－２，２－イソプロピルメチル－３－メチルブタンアミド、グリオキシル酸メンチル、及びこれらの化合物を含有する植物抽出物からなる群から選択される１以上の冷感付与物質である、［１］又は［２］に記載の靴用粉末消臭剤組成物。
［４］前記（Ｂ）成分が、カプサイシン、バニリルエチルエーテル、バニリルプロピルエーテル、バニリンプロピレングリコールアセタール、エチルバニリンプロピレングリコールアセタール、ギンゲロール、バニリルブチルエーテル、４－（ｌ－メントキシメチル）－２－（３'－メトキシ－４'－ヒドロキシフェニル）－１，３－ジオキソラン、トウガラシ油、トウガラシオレオレジン、ジンジャーオレオレジン、ノニル酸バニリルアミド、ジャンブーオレオレジン、サンショウエキス、サンショール－Ｉ、サンショール－II、サンショウアミド、黒胡椒エキス、カビシン、ピペリン、及びスピラントールからなる群から選択される１以上の温感付与物質である、［１］又は［２］に記載の靴用粉末消臭剤組成物。
［５］［１］～［４］のいずれか一項に記載の靴用粉末消臭剤組成物と、前記靴用粉末消臭剤組成物を収容した容器とを有する、容器入り粉末消臭剤組成物。
［６］［１］～［４］のいずれか一項に記載の靴用粉末消臭剤組成物を、靴内に散布する、消臭方法。
In order to achieve the above objects, the present invention employs the following configurations.
[1] A powder deodorant composition for shoes containing the following components (A) and (B),
A powder deodorant composition for shoes, wherein the mass of particles having a particle size of 50 μm or less is 30% by mass or more of the total mass of the powder deodorant composition for shoes.
(A) component: deodorant component (B) component: substance that imparts a cool or warm sensation when in contact with the skin [2] The powder deodorant composition for shoes according to [1], wherein the particles comprising the component (B) or the particles containing the component (B) have a volume average particle size of 50 μm or less.
[3] Component (B) is menthol, menthone, camphor, pulegol, isopulegol, cineol, peppermint oil, peppermint oil, spearmint oil, eucalyptus oil, 3-l-menthoxypropane-1,2-diol, N-alkyl-p-menthane-3-carboxamide, 3-l-menthoxy-2-methylpropane-1,2-diol, p-menthane-3,8-diol, 2-l-menthoxye The powder deodorant composition for shoes according to [1] or [2], which is one or more cooling sensation imparting substances selected from the group consisting of tan-1-ol, 3-l-menthoxypropan-1-ol, 4-l-menthoxybutan-1-ol (menthyl 3-hydroxybutanoate), menthyl lactate, menthol glycerol ketal, N-methyl-2,2-isopropylmethyl-3-methylbutanamide, menthyl glyoxylate, and plant extracts containing these compounds. .
[4] Component (B) is capsaicin, vanillyl ethyl ether, vanillyl propyl ether, vanillin propylene glycol acetal, ethyl vanillin propylene glycol acetal, gingerol, vanillyl butyl ether, 4-(l-menthoxymethyl)-2-(3'-methoxy-4'-hydroxyphenyl)-1,3-dioxolane, hot pepper oil, hot pepper oleoresin, ginger oleoresin, nonylic acid vanillylamide, jambu oleoresin. , Sansho extract, Sanshool-I, Sanshool-II, Sanshoamide, black pepper extract, moldin, piperine, and spilanthol. The powder deodorant composition for shoes according to [1] or [2].
[5] A containerized powder deodorant composition comprising the powder deodorant composition for shoes according to any one of [1] to [4] and a container containing the powder deodorant composition for shoes.
[6] A deodorizing method comprising spraying the powder deodorant composition for shoes according to any one of [1] to [4] in shoes.
本発明の靴用粉末消臭剤組成物、容器入り粉末消臭剤組成物、及び消臭方法は、使用者が靴下をはいたときであっても、冷感や温感を迅速に感じさせることが可能である。 The powder deodorant composition for shoes, the container-packaged powder deodorant composition, and the deodorant method of the present invention can make the user quickly feel a cold or warm sensation even when wearing socks.
≪靴用粉末消臭剤組成物≫
本発明の靴用粉末消臭剤組成物は、下記（Ａ）成分及び（Ｂ）成分を含み、粒径が５０μｍ以下の粒子の質量が、靴用粉末消臭剤組成物の総質量に対して３０質量％以上である。
（Ａ）成分：消臭成分
（Ｂ）成分：皮膚に接触したときに冷感又は温感を付与する物質
本発明の靴用粉末消臭剤組成物は、前記（Ａ）成分及び（Ｂ）成分に加えて、バランス剤（（Ｃ）成分）、香料、その他の任意成分を含んでいてもよい。
<<Powder deodorant composition for shoes>>
The powder deodorant composition for shoes of the present invention contains the following components (A) and (B), and the mass of particles having a particle size of 50 μm or less is 30% by mass or more of the total mass of the powder deodorant composition for shoes.
(A) component: deodorant component (B) component: a substance that imparts a cool or warm sensation when in contact with the skin The powder deodorant composition for shoes of the present invention may contain, in addition to the components (A) and (B), a balance agent (component (C)), perfume, and other optional components.
＜粒度分布＞
本発明において、粒径が５０μｍ以下の粒子の質量の靴用粉末消臭剤組成物の総質量に対する割合は、ＪＩＳ Ｋ３３６２：２００８に準拠して、ふるい分け法によって目開き５０μｍのふるいを用いて測定できる。
体積平均粒子径は、レーザ回折式粒度分布測定装置（ＢＥＣＫＭＡＮ ＣＯＵＬＴＥＲ社製 ＬＳ １３ ３２０）を用いて測定したＤ５０である。
<Particle size distribution>
In the present invention, the ratio of the mass of particles having a particle size of 50 μm or less to the total mass of the powder deodorant composition for shoes can be measured by a sieving method using a sieve with an opening of 50 μm in accordance with JIS K3362:2008.
The volume average particle diameter is D50 measured using a laser diffraction particle size distribution analyzer (LS 13 320 manufactured by BECKMAN COULTER).
本発明の靴用粉末消臭剤組成物に含まれる（Ａ）成分、（Ｂ）成分及びその他の任意成分は、それぞれ単独で粒子を形成していてもよいし、ある粒子に含まれていてもよい。
ある成分がある粒子に含まれる態様としては、他の成分の粒子の表面に付着した態様、他の成分の粒子の内部に含まれる態様が挙げられる。この態様の具体例としては、当該成分が液体で、他成分の粒子の表面や内部に付着している態様が挙げられる。この場合の粒径は、液体成分が付着した粒子の径である。
The components (A), (B) and other optional components contained in the powder deodorant composition for shoes of the present invention may form particles by themselves, or may be contained in a certain particle.
Examples of a mode in which a certain component is contained in a certain particle include a mode in which the other component adheres to the surface of the particle, and a mode in which the other component is contained inside the particle. A specific example of this aspect is an aspect in which the component is liquid and adheres to the surface or inside of particles of other components. The particle diameter in this case is the diameter of the particles to which the liquid component adheres.
ある成分がある粒子に含まれる態様としては、当該成分の粒子と他の成分の粒子が造粒体を形成している態様も挙げられる。この場合の粒径は、造粒体の粒径である。
また、液体成分が付着した粒子が他の成分の粒子と共に造粒体を形成している態様が挙げられる。この場合の粒径も、造粒体の粒径である。
Examples of an aspect in which a certain component is contained in a certain particle include an aspect in which particles of the component and particles of another component form a granule. The particle size in this case is the particle size of the granules.
Further, there is an aspect in which the particles to which the liquid component is adhered form a granule together with particles of other components. The particle size in this case is also the particle size of the granules.
粒径が５０μｍ以下の粒子の質量の靴用粉末消臭剤組成物の総質量に対する割合は３０質量％以上であり、３０質量％以上１００質量％未満であることが好ましく、５０～９０質量％であることがより好ましく、７０～９０質量％であることがさらに好ましい。 The ratio of the mass of particles having a particle size of 50 μm or less to the total mass of the powder deodorant composition for shoes is 30% by mass or more, preferably 30% by mass or more and less than 100% by mass, more preferably 50 to 90% by mass, and even more preferably 70 to 90% by mass.
本発明の靴用粉末消臭剤組成物は、前記割合が３０質量％以上であることにより、使用者が靴下をはいたときであっても、冷感や温感を迅速に感じさせることが可能である。
これは、小さい粒子が多く存在することにより、（Ｂ）成分を含む組成物が、迅速に靴下を透過し、皮膚に到達できるからであると考えられる。
また、本発明の靴用粉末消臭剤組成物は、前記割合が好ましい上限値以下であることにより、靴全体に行き渡る良好な流動性を確保しやすい。そのため、冷感や温感を均一に感じやすくなる。
The powder deodorant composition for shoes of the present invention has a ratio of 30% by mass or more, so that even when the user wears socks, it is possible to quickly feel a cold or warm sensation.
Presumably, this is because the presence of many small particles allows the composition containing the component (B) to quickly permeate the socks and reach the skin.
In addition, the powder deodorant composition for shoes of the present invention tends to ensure good fluidity throughout the shoe because the ratio is not more than the preferred upper limit. Therefore, it becomes easy to feel a cold sensation and a warm sensation uniformly.
＜（Ａ）成分＞
（Ａ）成分は消臭成分、すなわち、本発明の靴用粉末消臭剤組成物中で消臭効果を発揮する成分である。
（Ａ）成分としては、（Ａ１）多孔質基剤、（Ａ２）包接基剤、（Ａ３）アルカリ基剤、（Ａ４）抗菌剤が挙げられる。
（Ａ）成分は、１種単独でもよいし、２種以上の組み合わせでもよい。
<(A) Component>
Component (A) is a deodorizing component, that is, a component that exerts a deodorizing effect in the powder deodorant composition for shoes of the present invention.
Component (A) includes (A1) a porous base, (A2) an inclusion base, (A3) an alkaline base, and (A4) an antibacterial agent.
The component (A) may be used singly or in combination of two or more.
（Ａ１）成分である多孔質基剤は、無機鉱物であり、構造内に悪臭物質を吸着可能な空孔を有する多孔質の化合物である。
（Ａ１）成分としては、ハイドロタルサイト、ハイドロタルサイト焼成物、活性炭、ゼオライト、多孔質シリカ等、及び、これらに金属を担持したものが挙げられる。
The (A1) component, the porous base material, is an inorganic mineral, and is a porous compound having pores capable of adsorbing malodorous substances in its structure.
Component (A1) includes hydrotalcite, calcined hydrotalcite, activated carbon, zeolite, porous silica, etc., and metal-supported materials thereof.
ハイドロタルサイトとは、例えば下記式（１）で表される層状複水酸化物である。
［Ｍ２＋
１－ｘＭ３＋
ｘ（ＯＨ）２］ｘ＋［（Ａｎ－
ｘ／ｎ）・ｍＨ２Ｏ］ｘ－ ・・・（１）
Hydrotalcite is, for example, a layered double hydroxide represented by the following formula (1).
[M 2+ 1−x M 3+ x (OH) 2 ] x+ [(A n− x/n )·mH 2 O] x− (1)
式（１）中、Ｍ２＋はＭｇ２＋、Ｃａ２＋、Ｚｎ２＋、Ｃｏ２＋、Ｎｉ２＋、Ｃｕ２＋、Ｆｅ２＋、Ｃｒ２＋、Ｃｄ２＋、Ｍｎ２＋等の２価金属イオンであり、Ｍ３＋はＡｌ３＋、Ｆｅ３＋、Ｎｉ３＋、Ｃｏ３＋、Ｍｎ３＋、Ｃｒ３＋等の３価金属イオンであり、Ａｎ－はＯＨ－、Ｃｌ－、ＣＯ３ ２－、ＳＯ４ ２－等のｎ価のアニオンである。ｘは、０より大きい数であり、０．１０～０．５０が好ましく、０．２０～０．３３がより好ましい。ｍは、０又は０より大きい数であり、０～１０が好ましく、０～４がより好ましい。 In formula (1), M 2+ is a divalent metal ion such as Mg 2+ , Ca 2+ , Zn 2+ , Co 2+ , Ni 2+ , Cu 2+ , Fe 2+ , Cr 2+ , Cd 2+ , Mn 2+ , and M 3+ is Al 3+ , Fe 3+ , Ni 3+ , Co 3+ , Mn 3+ , C r 3+ is a trivalent metal ion, and A n- is an n-valent anion such as OH − , Cl − , CO 3 2− , SO 4 2− . x is a number greater than 0, preferably 0.10 to 0.50, more preferably 0.20 to 0.33. m is 0 or a number greater than 0, preferably 0 to 10, more preferably 0 to 4.
ハイドロタルサイト焼成物は、例えば下記一般式（２）で表すことができる複酸化物である。
Ｍ２＋
１－ｘＭ３＋ｘＯ１＋ｘ／２ ・・・（２）
The hydrotalcite calcined product is, for example, a composite oxide represented by the following general formula (2).
M 2+ 1−x M 3+ xO 1+x/2 (2)
式（２）中、Ｍ２＋、ｘは上記式（１）と同じである。 In formula (2), M 2+ and x are the same as in formula (1) above.
また、ハイドロタルサイトとしては、Ｍｇ３ＺｎＡｌ２（ＯＨ）１２ＣＯ３・ｗＨ２Ｏ、Ｍｇ３ＺｎＡｌ２（ＯＨ）１２ＣＯ３等の亜鉛変性ハイドロタルサイト系化合物を用いることもできる（ｗは実数である）。
ハイドロタルサイト焼成物は酸性基及び塩基性基を有する金属塩に担持して金属複合体を形成していてもよい。
ハイドロタルサイト及びその焼成物は、天然ハイドロタルサイトでもよいし、合成ハイドロタルサイトでもよい。
ハイドロタルサイト及びその焼成物におけるＭｇＯ／Ａｌ２Ｏ３で表されるモル比は、２．５～６が好ましく、４～６がより好ましい。
As hydrotalcite, zinc- modified hydrotalcite compounds such as Mg3ZnAl2 (OH) 12CO3.wH2O and Mg3ZnAl2 (OH ) 12CO3 can also be used (w is a real number).
The hydrotalcite calcined product may be supported on a metal salt having an acidic group and a basic group to form a metal composite.
The hydrotalcite and its calcined product may be natural hydrotalcite or synthetic hydrotalcite.
The molar ratio represented by MgO/Al 2 O 3 in hydrotalcite and its sintered product is preferably 2.5-6, more preferably 4-6.
（Ａ２）成分である包接基剤は、悪臭物質を吸着するサイト、乃至は包接可能な部位を持つ有機化合物である。
（Ａ２）成分としては、シクロデキストリン、高度分岐環状デキストリン等が挙げられる。
高度分岐環状デキストリンとしては、内分岐環状構造部分と外分岐構造部分とを有する重合度が５０～１００００の範囲にあるグルカンが挙げられる。内分岐環状構造部分は、例えばα－１，４－グルコシド結合とα－１，６－グルコシド結合とで形成される環状のグルカン鎖であり、外分岐構造部分は例えば内分岐環状構造部分に結合した非環状のグルカン鎖である。
高度分岐環状デキストリンの市販品としては、クラスターデキストリン（グリコ栄養食品株式会社製）等が挙げられる。
The clathrate base, which is the component (A2), is an organic compound having a site that adsorbs the malodorous substance or a site that can be clathrated.
The (A2) component includes cyclodextrin, highly branched cyclic dextrin, and the like.
Examples of highly branched cyclic dextrins include glucans having an inner branched cyclic structure portion and an outer branched structure portion and having a degree of polymerization in the range of 50 to 10,000. The inner branched cyclic structural portion is, for example, a cyclic glucan chain formed by α-1,4-glucosidic bonds and α-1,6-glucosidic bonds, and the outer branched structural portion is, for example, an acyclic glucan chain bonded to the inner branched cyclic structural portion.
Commercially available products of highly branched cyclic dextrin include cluster dextrin (manufactured by Glico Nutrition Foods Co., Ltd.).
（Ａ３）成分であるアルカリ基剤は、２０℃の水に対する溶解度が１ｇ／Ｌを超え、その飽和水溶液のｐＨが７を超え１２以下である無機粉体である。
アルカリ基剤は、その飽和水溶液のｐＨが７．５～１１であることが好ましい。飽和水溶液のｐＨが７を超えるアルカリ性であれば、酸性の悪臭物質を中和して消臭する作用を奏する。ｐＨは、測定対象を２５℃とし、ｐＨメーター（製品名：ＨＭ－３０Ｇ、東亜ディーケーケー株式会社製）により測定される値である。
（Ａ３）成分としては、重炭酸カリウム、炭酸カリウム、炭酸水素ナトリウム、炭酸ナトリウム、水酸化カルシウム、リン酸水素二ナトリウム、リン酸二水素ナトリウム、リン酸水素二カリウム、リン酸二水素カリウム等が挙げられる。
The alkali base as component (A3) is an inorganic powder having a solubility in water at 20° C. of more than 1 g/L and a saturated aqueous solution having a pH of more than 7 and not more than 12.
The alkaline base preferably has a pH of 7.5 to 11 in its saturated aqueous solution. If the saturated aqueous solution is alkaline with a pH exceeding 7, it has the effect of neutralizing and deodorizing acidic malodorous substances. The pH is a value measured with a pH meter (product name: HM-30G, manufactured by Toa DKK Co., Ltd.) at 25°C.
(A3) Component includes potassium bicarbonate, potassium carbonate, sodium hydrogen carbonate, sodium carbonate, calcium hydroxide, disodium hydrogen phosphate, sodium dihydrogen phosphate, dipotassium hydrogen phosphate, potassium dihydrogen phosphate and the like.
（Ａ４）成分である抗菌剤は、抗菌作用を有する固体又は液体の化合物である。
（Ａ４）成分としては、銀担持ゼオライト、四級アンモニウム塩（塩化ベンザルコニウム、ジデシルジメチルアンモニウムクロライド）、４，４’－ジクロロ－２－ヒドロキシジフェニルエーテル（慣用名：ダイクロサン）、５－クロロ－２－（２，４－ジクロロフェノキシ）フェノール（慣用名：トリクロサン）、ビス－（２－ピリジルチオ－１－オキシド）亜鉛、ポリヘキサメチレンビグアニジン塩酸塩、８－オキシキノリン、ポリリジン、塩酸クロロヘキシジン、１，３，５－トリアジン－１，３，５－トリエタノール、１，３，５－トリメチルヘキサヒドロ－１，３，５－トリアジン等が挙げられる。
The (A4) component antibacterial agent is a solid or liquid compound having an antibacterial action.
(A4) components include silver-supported zeolite, quaternary ammonium salts (benzalkonium chloride, didecyldimethylammonium chloride), 4,4′-dichloro-2-hydroxydiphenyl ether (common name: diclosan), 5-chloro-2-(2,4-dichlorophenoxy)phenol (common name: triclosan), bis-(2-pyridylthio-1-oxide)zinc, polyhexamethylenebiguanidine hydrochloride, 8-oxyquinoline, poly gin, chlorhexidine hydrochloride, 1,3,5-triazine-1,3,5-triethanol, 1,3,5-trimethylhexahydro-1,3,5-triazine and the like.
（Ａ）成分は、ハイドロタルサイト、ハイドロタルサイト焼成物、活性炭、ゼオライト、多孔質シリカ、炭酸水素ナトリウム、及び銀担持ゼオライトから選択される１以上であることが好ましい。 Component (A) is preferably one or more selected from hydrotalcite, calcined hydrotalcite, activated carbon, zeolite, porous silica, sodium hydrogen carbonate, and silver-supported zeolite.
（Ａ）成分は、液体でも、粒子であってもよい。固体状の（Ａ）成分を適当な溶媒に溶解した溶液でもよい。
（Ａ）成分の一部又は全部が液体又は溶液である場合、液体又は溶液の（Ａ）成分を他の粒子、好ましくは（Ｂ）成分やバランス剤等の粒子に噴霧することで、（Ａ）成分を粉末消臭剤組成物に配合できる。（Ａ）成分の総てが液体又は溶液の場合、（Ｂ）成分が粉体であるか、（Ｃ）成分のバランス剤を配合することが必要である。
The component (A) may be liquid or particles. A solution obtained by dissolving the solid component (A) in an appropriate solvent may also be used.
When part or all of the component (A) is a liquid or a solution, the component (A) can be blended into the powder deodorant composition by spraying the liquid or solution of the component (A) onto other particles, preferably the particles of the component (B) or the balance agent. When all of the components (A) are liquid or solution, it is necessary to either powder the component (B) or add a balance agent for the component (C).
（Ａ）成分からなる粒子又は（Ａ）成分を含む粒子の体積平均粒子径は、０．１～２５０μｍであることが好ましく、１～１５０μｍであることがより好ましく、３～１００μｍであることがさらに好ましい。
（Ａ）成分からなる粒子又は（Ａ）成分を含む粒子の体積平均粒子径が好ましい上限値以下であれば、消臭効果を発揮しやすい。
（Ａ）成分からなる粒子又は（Ａ）成分を含む粒子の体積平均粒子径が好ましい下限値以上であれば、使用時の粉の舞い上がりを抑制できる。
The volume-average particle size of the particles consisting of component (A) or the particles containing component (A) is preferably 0.1 to 250 μm, more preferably 1 to 150 μm, even more preferably 3 to 100 μm.
If the volume-average particle size of the particles comprising the component (A) or the particles containing the component (A) is equal to or less than the preferred upper limit, the deodorizing effect is likely to be exhibited.
If the volume-average particle size of the particles comprising component (A) or the particles containing component (A) is at least the preferred lower limit, it is possible to suppress the rise of powder during use.
靴用粉末消臭剤組成物中の（Ａ）成分の含有量は靴用粉末消臭剤組成物の総質量に対して、０．００１～９０質量％が好ましく、０．０１～５０質量％がより好ましく、０．０１～３０質量％がさらに好ましい。
上記下限値以上であれば、靴用粉末消臭剤組成物の消臭効果をさらに高められ、上記上限値以下であれば、吸湿を抑え、固化を抑制しやすい。
The content of component (A) in the powder deodorant composition for shoes is preferably 0.001 to 90% by mass, more preferably 0.01 to 50% by mass, and even more preferably 0.01 to 30% by mass, relative to the total mass of the powder deodorant composition for shoes.
When it is at least the above lower limit, the deodorizing effect of the powder deodorant composition for shoes can be further enhanced, and when it is at most the above upper limit, moisture absorption is suppressed and solidification is easily suppressed.
＜（Ｂ）成分＞
（Ｂ）成分は皮膚に接触したときに冷感又は温感を付与する物質である。
（Ｂ）成分としては、皮膚に接触したときに冷感を付与する（Ｂ１）冷感付与物質、皮膚に接触したときに温感を付与する（Ｂ２）温感付与物質が挙げられる。
<(B) Component>
Component (B) is a substance that imparts a feeling of coldness or warmth upon contact with the skin.
Examples of the component (B) include (B1) a cooling sensation imparting substance that imparts a cooling sensation upon contact with the skin and (B2) a warming sensation imparting substance that imparts a warm sensation upon contact with the skin.
（Ｂ１）成分としては、メントール、メントン、カンファー、プレゴール、イソプレゴール、シネオール、ハッカオイル、ペパーミントオイル、スペアーミントオイル、ユーカリプタスオイル、３－ｌ－メントキシプロパン－１，２－ジオール、Ｎ－アルキル－ｐ－メンタン－３－カルボキサミド、３－ｌ－メントキシ－２－メチルプロパン－１，２－ジオール、ｐ－メンタン－３，８－ジオール、２－ｌ－メントキシエタン－１－オール、３－ｌ－メントキシプロパン－１－オール、４－ｌ－メントキシブタン－１－オール（３－ヒドロキシブタン酸メンチル）、乳酸メンチル、メントールグリセリンケタール、Ｎ－メチル－２，２－イソプロピルメチル－３－メチルブタンアミド、グリオキシル酸メンチル、及びこれらの化合物を含有する植物抽出物からなる群から選択される１以上の冷感付与物質が挙げられる。 Components (B1) include menthol, menthone, camphor, pulegol, isopulegol, cineol, peppermint oil, peppermint oil, spearmint oil, eucalyptus oil, 3-l-menthoxypropane-1,2-diol, N-alkyl-p-menthane-3-carboxamide, 3-l-menthoxy-2-methylpropane-1,2-diol, p-menthane-3,8-diol, and 2-l-menthoxyethane- 1-ol, 3-l-menthoxypropan-1-ol, 4-l-menthoxybutan-1-ol (menthyl 3-hydroxybutanoate), menthyl lactate, menthol glycerin ketal, N-methyl-2,2-isopropylmethyl-3-methylbutanamide, menthyl glyoxylate, and one or more cooling sensation imparting substances selected from the group consisting of plant extracts containing these compounds.
中でも、メントール、メントン、カンファー、乳酸メンチル、グリオキシル酸メンチルが好ましく、メントール、メントン、カンファー、乳酸メンチルがより好ましい。
（Ｂ１）成分は、１種単独でもよいし、２種以上の組み合わせでもよい。
Among them, menthol, menthone, camphor, menthyl lactate, and menthyl glyoxylate are preferred, and menthol, menthone, camphor, and menthyl lactate are more preferred.
The component (B1) may be used alone or in combination of two or more.
（Ｂ２）成分としては、カプサイシン、バニリルエチルエーテル、バニリルプロピルエーテル、バニリンプロピレングリコールアセタール、エチルバニリンプロピレングリコールアセタール、ギンゲロール、バニリルブチルエーテル、４－（ｌ－メントキシメチル）－２－（３'－メトキシ－４'－ヒドロキシフェニル）－１，３－ジオキソラン、トウガラシ油、トウガラシオレオレジン、ジンジャーオレオレジン、ノニル酸バニリルアミド、ジャンブーオレオレジン、サンショウエキス、サンショール－Ｉ、サンショール－II、サンショウアミド、黒胡椒エキス、カビシン、ピペリン、及びスピラントールからなる群から選択される１以上の温感付与物質が挙げられる。 (B2) components include capsaicin, vanillyl ethyl ether, vanillyl propyl ether, vanillin propylene glycol acetal, ethyl vanillin propylene glycol acetal, gingerol, vanillyl butyl ether, 4-(l-menthoxymethyl)-2-(3'-methoxy-4'-hydroxyphenyl)-1,3-dioxolane, capsicum oil, capsicum oleoresin, ginger oleoresin, nonylic acid vanillylamide, jambu oleoresin, sun One or more warming sensation-imparting substances selected from the group consisting of pepper extract, sanshool-I, sanshool-II, sanshoamide, black pepper extract, moldin, piperine, and spilanthol.
中でも、カプサイシン、バニリルエチルエーテル、トウガラシ油が好ましく、カプサイシン、トウガラシ油がより好ましい。
（Ｂ２）成分は、１種単独でもよいし、２種以上の組み合わせでもよい。
Among them, capsaicin, vanillyl ethyl ether, and capsicum oil are preferred, and capsaicin and capsicum oil are more preferred.
The component (B2) may be used singly or in combination of two or more.
（Ｂ）成分は、液体でも、粒子であってもよい。固体状の（Ｂ）成分を適当な溶媒に溶解した溶液でもよい。
（Ｂ）成分の一部又は全部が液体又は溶液である場合、液体又は溶液の（Ｂ）成分を他の粒子、好ましくは（Ａ）成分やバランス剤等の粒子に噴霧することで、（Ｂ）成分を粉末消臭剤組成物に配合できる。（Ｂ）成分の総てが液体又は溶液の場合、（Ａ）成分が粉体であるか、（Ｃ）成分のバランス剤を配合することが必要である。
Component (B) may be liquid or particulate. A solution obtained by dissolving the solid component (B) in an appropriate solvent may also be used.
When part or all of the component (B) is a liquid or a solution, the component (B) can be blended into the powder deodorant composition by spraying the liquid or solution of the component (B) onto other particles, preferably the particles of the component (A) or the balance agent. When all components (B) are liquids or solutions, it is necessary to either powder component (A) or add a balancing agent for component (C).
（Ｂ）成分からなる粒子又は（Ｂ）成分を含む粒子の体積平均粒子径は、２５０μｍ以下であることが好ましく、１～１５０μｍであることがより好ましく、１～５０μｍであることがさらに好ましい。
（Ｂ）成分からなる粒子又は（Ｂ）成分を含む粒子の体積平均粒子径が好ましい上限値以下であれば、（Ｂ）成分が皮膚により迅速に到達するので、使用者が靴下をはいたときであっても、冷感や温感をより迅速に感じさせることができる。
（Ｂ）成分からなる粒子又は（Ｂ）成分を含む粒子の体積平均粒子径が好ましい下限値以上であれば、保存時の固化を抑制できる。
The volume-average particle size of the particles comprising component (B) or the particles containing component (B) is preferably 250 μm or less, more preferably 1 to 150 μm, and even more preferably 1 to 50 μm.
If the volume-average particle size of the particles consisting of component (B) or the particles containing component (B) is equal to or less than the preferred upper limit, component (B) reaches the skin more quickly, so even when the user wears socks, it is possible to make the user feel a cold or warm sensation more quickly.
When the volume-average particle size of the particles comprising component (B) or the particles containing component (B) is at least the preferred lower limit, solidification during storage can be suppressed.
靴用粉末消臭剤組成物中の（Ｂ）成分の含有量は靴用粉末消臭剤組成物の総質量に対して、０．００１～２０質量％が好ましく、０．００１～１０質量％がより好ましく、０．０１～１０質量％がさらに好ましい。
上記下限値以上であれば、冷感又は温感の付与効果をさらに高められ、上記上限値以下であれば、吸湿を抑え、固化を抑制しやすい。
The content of component (B) in the powder deodorant composition for shoes is preferably 0.001 to 20% by mass, more preferably 0.001 to 10% by mass, and even more preferably 0.01 to 10% by mass, relative to the total mass of the powder deodorant composition for shoes.
If it is at least the above lower limit, the effect of imparting a cool or warm sensation can be further enhanced, and if it is at most the above upper limit, moisture absorption is suppressed and solidification is easily suppressed.
＜（Ｃ）成分＞
（Ｃ）成分であるバランス剤は、（Ａ）成分、（Ｂ）成分に該当しない無機顔料である。
（Ｃ）成分としては、（Ｃ１）に規定される化粧品顔料、（Ｃ２）その他の無機顔料（但し（Ａ）成分、（Ｂ）成分、（Ｃ１）成分を除く）が挙げられる。
（Ｃ）成分は、１種単独でもよいし、２種以上の組み合わせでもよい。
<(C) Component>
The balance agent, which is the component (C), is an inorganic pigment that does not correspond to the components (A) and (B).
Component (C) includes cosmetic pigments defined in (C1) and (C2) other inorganic pigments (excluding components (A), (B), and (C1)).
Component (C) may be used alone or in combination of two or more.
（Ｃ１）成分としては、アルミニウム末、カーボンブラック、カルミン、グンジョウ、酸化スズ、酸化チタン、酸化亜鉛、鉛白、リトポン、二酸化チタン、硫酸バリウム、ポリエチレン、及びセラミックパウダーからなる群から選択される１以上の化粧品顔料が挙げられる。 The component (C1) includes one or more cosmetic pigments selected from the group consisting of aluminum powder, carbon black, carmine, granite, tin oxide, titanium oxide, zinc oxide, white lead, lithopone, titanium dioxide, barium sulfate, polyethylene, and ceramic powder.
（Ｃ２）成分としては、タルク、カオリン、雲母、セリサイト、白雲母、金雲母、紅雲母、黒雲母、リチア雲母、バーミキュライト、シリカ（（Ａ１）成分の多孔質シリカを除く）、焼セッコウ、フッ素アパタイト、ヒドロキシアパタイト、酸化鉄、炭酸マグネシウム、炭酸カルシウム、酸化マグネシウム、酸化ジルコニウム、及び水酸化クロムからなる群から選択される１以上の無機顔料が挙げられる。 Component (C2) includes one or more inorganic pigments selected from the group consisting of talc, kaolin, mica, sericite, muscovite, phlogopite, mica mica, biotite, lithiamite, vermiculite, silica (excluding porous silica of component (A1)), calcined gypsum, fluoroapatite, hydroxyapatite, iron oxide, magnesium carbonate, calcium carbonate, magnesium oxide, zirconium oxide, and chromium hydroxide.
中でも、タルク、炭酸カルシウム、シリカが好ましく、タルクがより好ましい。 Among them, talc, calcium carbonate and silica are preferred, and talc is more preferred.
（Ｃ）成分からなる粒子又は（Ｃ）成分にその他の成分が付着した粒子の体積平均粒子径は、０．１～５００μｍであることが好ましく、１～２５０μｍであることがより好ましく、１０～１５０μｍであることがさらに好ましく、１０～７５μｍであることがとりわけ好ましく、１０～５０μｍであることが特に好ましい。 The volume-average particle diameter of the particles composed of component (C) or particles in which other components are attached to component (C) is preferably 0.1 to 500 μm, more preferably 1 to 250 μm, even more preferably 10 to 150 μm, particularly preferably 10 to 75 μm, particularly preferably 10 to 50 μm.
上記下限値以上であれば、吸湿を抑え、固化を抑制しやすく、流動性を高めやすい。上記上限値以下であれば、靴用粉末消臭剤組成物の総質量に対する粒径が５０μｍ以下の粒子の質量の割合を３０質量％以上としやすい。 If it is at least the above lower limit, moisture absorption is suppressed, solidification is easily suppressed, and fluidity is easily enhanced. If it is equal to or less than the above upper limit, the ratio of the mass of particles having a particle size of 50 μm or less to the total mass of the powder deodorant composition for shoes is likely to be 30% by mass or more.
靴用粉末消臭剤組成物中の（Ｃ）成分の含有量は靴用粉末消臭剤組成物の総質量に対して、３０～９５質量％が好ましく、５０～９０質量％がより好ましい。
上記下限値以上であれば、吸湿を抑え、固化を抑制しやすく、流動性を高めやすい。上記上限値以下であれば、（Ａ）成分と（Ｂ）成分とを充分な量配合しやすい。
The content of component (C) in the powder deodorant composition for shoes is preferably 30 to 95% by mass, more preferably 50 to 90% by mass, based on the total mass of the powder deodorant composition for shoes.
If it is at least the above lower limit, moisture absorption is suppressed, solidification is easily suppressed, and fluidity is easily enhanced. If it is below the said upper limit, it will be easy to mix|blend sufficient quantity of (A) component and (B) component.
＜その他の任意成分＞
靴用粉末消臭剤組成物は、さらに、バランス剤以外の任意成分を含んでいてもよい。
その他の任意成分としては、香料（（Ｂ）成分を除く。）、吸熱基剤、高分子ポリマー、染料が挙げられる。
<Other optional ingredients>
The powder deodorant composition for shoes may further contain optional ingredients other than the balance agent.
Other optional components include fragrances (excluding component (B)), endothermic bases, high molecular weight polymers, and dyes.
靴用粉末消臭剤組成物において、香料は、他の成分に付着した液体であってもよいし、粉末香料として存在していてもよい。
香料が粉末香料の場合、靴用粉末消臭剤組成物は、任意成分として香料を粉末状とするための賦形剤を含んでいてもよい。香料の賦形剤としては、デキストリン、トレハロース、シクロデキストリン、オクテニルコハク酸でんぷんナトリウム、でんぷん、でんぷん誘導体等が挙げられる。
In the powder deodorant composition for shoes, the perfume may be a liquid adhering to other ingredients, or may exist as a powder perfume.
When the perfume is a powdered perfume, the powder deodorant composition for shoes may optionally contain an excipient for powdering the perfume. Perfume excipients include dextrin, trehalose, cyclodextrin, sodium starch octenylsuccinate, starch, starch derivatives and the like.
香料の組成は、所望する香気を勘案して適宜決定される。
香料が液体香料の場合、靴用粉末消臭剤組成物の総質量に対する液体香料の含有量は、０．０１～５質量％が好ましく、０．１～２質量％がより好ましい。
香料が粉末香料の場合、粉末消臭剤組成物の総質量に対する粉末香料の含有量（賦形剤を除く）は、０．０１～１０質量％が好ましく、０．１～５質量％がより好ましく、１～５質量％がさらに好ましい。
The composition of the fragrance is appropriately determined in consideration of the desired fragrance.
When the perfume is a liquid perfume, the content of the liquid perfume is preferably 0.01 to 5% by mass, more preferably 0.1 to 2% by mass, relative to the total mass of the powder deodorant composition for shoes.
When the perfume is a powdered perfume, the content of the powdered perfume (excluding excipients) with respect to the total mass of the powder deodorant composition is preferably 0.01 to 10% by mass, more preferably 0.1 to 5% by mass, and even more preferably 1 to 5% by mass.
吸熱基剤は、水と反応して吸熱反応を起こす粉体である。吸熱基剤としては糖類、アミノ酸、尿素、プラスチックビーズ、プラスチックパウダー、コーンスターチを初めとする食用粉末等が挙げられる。 The endothermic base is a powder that reacts with water to cause an endothermic reaction. Endothermic bases include saccharides, amino acids, urea, plastic beads, plastic powders, edible powders such as corn starch, and the like.
≪靴用粉末消臭剤組成物の製造方法≫
各成分がいずれも粒子である場合、靴用粉末消臭剤組成物は、（Ａ）成分、（Ｂ）成分及び必要に応じて任意成分を粉体混合により混合する方法により製造できる。
また、（Ａ）成分、（Ｂ）成分及び必要に応じて任意成分の一部又は全部を造粒してもよい。造粒方法としては、特に限定されず、従来公知の流動層造粒法、乾式造粒法、湿式造粒法等が挙げられる。
また、一部の成分が液体又は溶液状である場合、液体又は溶液状の成分は、粉体混合前、若しくは粉体混合後、又は造粒後の他の成分に噴霧することにより配合できる。
なお、（Ｂ）成分の一部又は全部は、予め香料組成物に配合しておいてもよい。
<<Method for producing powder deodorant composition for shoes>>
When all of the components are particles, the powder deodorant composition for shoes can be produced by powder mixing the components (A), (B) and, if necessary, optional components.
Moreover, you may granulate a part or all of (A) component, (B) component, and an arbitrary component as needed. The granulation method is not particularly limited, and conventionally known fluid bed granulation methods, dry granulation methods, wet granulation methods, and the like can be mentioned.
Moreover, when some components are liquid or solution, the liquid or solution component can be blended by spraying to other components before powder mixing, after powder mixing, or after granulation.
Part or all of the component (B) may be previously blended with the perfume composition.
≪容器入り粉末消臭剤組成物≫
本発明の靴用粉末消臭剤組成物は、容器に収容されて、容器入り粉末消臭剤組成物（容器入り製品）となる。
容器としては、例えば、スタンディングパウチ、注出孔を有するボトル、広口瓶、缶等、粉体を収容する公知の容器が挙げられる。中でも、注出孔を有するボトルが好ましい。
容器は、容器本体と蓋体に加えて、注出孔を適切な大きさに調整する中栓を有することが好ましい。
≪Powder deodorant composition in a container≫
The powder deodorant composition for shoes of the present invention is accommodated in a container to form a container-packed powder deodorant composition (container-packed product).
Examples of the container include known containers for containing powder, such as standing pouches, bottles with pour holes, wide-mouthed bottles, and cans. Among them, a bottle having a pouring hole is preferable.
In addition to the container body and the lid, the container preferably has an inner plug for adjusting the pouring hole to an appropriate size.
≪消臭方法≫
本発明の消臭方法は、本発明の靴用粉末消臭剤組成物を、靴内に散布する方法である。
靴内への散布は、容器入り粉末消臭剤組成物の容器を振り動かして靴内に靴用粉末消臭剤組成物を振り出すことや、容器から靴用粉末消臭剤組成物をスプーンに取り出し、スプーンで靴内に散布することなどにより行うことができる。
靴内に散布した後には、靴に振動を与えて、粉末消臭剤組成物を靴の内部全体に広げることが好ましい。
≪Deodorization method≫
The deodorant method of the present invention is a method of spraying the powder deodorant composition for shoes of the present invention into shoes.
The powdered deodorant composition for shoes can be sprinkled into the shoes by shaking the container of the powdered deodorant composition in the container to shake the powdered deodorant composition for shoes into the shoes, or by taking out the powdered deodorant composition for shoes from the container with a spoon and spraying it into the shoes with the spoon.
After spraying inside the shoes, the shoes are preferably vibrated to spread the powder deodorant composition over the entire inside of the shoes.
靴用粉末消臭剤組成物の散布量は、片方の靴１つ当たり、０．１～２．０ｇが好ましく、０．３～１．５ｇがより好ましい。
使用量が上記下限値以上であることにより、充分な消臭効果を得やすい。
使用量が上記上限値以下であることにより、靴に過剰量が残留しにくく、良好な履き心地を得やすい。
The spray amount of the powder deodorant composition for shoes is preferably 0.1 to 2.0 g, more preferably 0.3 to 1.5 g, per one shoe.
When the amount used is at least the above lower limit, it is easy to obtain a sufficient deodorizing effect.
When the amount used is equal to or less than the above upper limit, it is difficult for an excessive amount to remain in shoes, and it is easy to obtain good wearing comfort.
以下、実施例を示して本発明を詳細に説明するが、本発明は以下の記載によって限定されるものではない。 [EXAMPLES] Hereafter, although an Example is shown and this invention is demonstrated in detail, this invention is not limited by the following description.
≪使用成分≫
＜（Ａ１）成分＞
・ハイドロタルサイト焼成物（酸化マグネシウムと酸化アルミニウム質量比の固溶体、ＫＷ－２０００、協和化学工業株式会社、化学組成：Ｍｇ０．７Ａｌ０．３Ｏ１．１５、平均粒子径：４０μｍ）。
・Ａゼオライト（タイシリケート、平均粒子径：５μｍ）。
≪Ingredients used≫
<(A1) Component>
· Hydrotalcite calcined product (solid solution of magnesium oxide and aluminum oxide mass ratio, KW-2000, Kyowa Chemical Industry Co., Ltd., chemical composition: Mg 0.7 Al 0.3 O 1.15 , average particle size: 40 μm).
- A zeolite (thai silicate, average particle size: 5 µm).
＜（Ａ２）成分＞
・クラスターデキストリン、高度分岐環状デキストリン（グリコ栄養食品株式会社製、平均粒子径：１００μｍ）。
＜（Ａ３）成分＞
・炭酸水素ナトリウム（東ソー株式会社、平均粒子径：２５０μｍ）。
＜（Ａ４）成分＞
・銀担持ゼオライト（ゼオミックＡＪ１０Ｎ、シナネンゼオミック株式会社製、平均粒子径：４μｍ）。
<(A2) component>
- Cluster dextrin, highly branched cyclic dextrin (manufactured by Glico Nutrition Foods Co., Ltd., average particle size: 100 µm).
<(A3) Component>
- Sodium hydrogen carbonate (Tosoh Corporation, average particle size: 250 µm).
<(A4) Component>
• Silver-supported zeolite (Zeomic AJ10N, manufactured by Sinanen Zeomic Co., Ltd., average particle size: 4 μm).
＜（Ｂ）成分＞
・ｌ－メントール（クラリアントジャパン、平均粒子径：３０μｍ（粉砕後））。
＜（Ｃ）成分＞
・タルク（ＭＳ－ＫＹ、日本タルク株式会社製、平均粒子径２５μｍ）。
・クラウンタルクＲＤ（松村産業株式会社、平均粒子径５０μｍ）。
＜香料＞
・粉末香料（シトラスパウダーＬＡ－７８１０、長谷川香料株式会社、平均粒子径４０μｍ）。
<(B) Component>
· l-menthol (Clariant Japan, average particle size: 30 μm (after pulverization)).
<(C) Component>
- Talc (MS-KY, manufactured by Nippon Talc Co., Ltd., average particle size 25 μm).
- Crown talc RD (Matsumura Sangyo Co., Ltd., average particle size 50 µm).
<Perfume>
・Powder perfume (Citrus powder LA-7810, Hasegawa perfume Co., Ltd., average particle size 40 μm).
≪測定方法、評価方法≫
＜５０μｍ以下の粒子量＞
測定対象の靴用粉末消臭剤組成物の１００ｇを直径２０ｃｍのＪＩＳＺ８８０１の篩（目開き５０μｍ）上にのせ、ＪＩＳ Ｋ３３６２：２００８に準拠して、ふるい分け、前記篩を通過した靴用粉末消臭剤組成物の質量Ｘ（ｇ）を測定し、下記式（３）により求めた。
Ｙ（質量％）＝Ｘ／１００×１００ ・・・（３）
≪Measuring method, evaluation method≫
<Amount of particles of 50 µm or less>
100 g of the powder deodorant composition for shoes to be measured was placed on a 20 cm diameter sieve of JIS Z8801 (50 μm opening), sieved according to JIS K3362: 2008, and the mass X (g) of the powder deodorant composition for shoes that passed through the sieve was measured and obtained by the following formula (3).
Y (% by mass)=X/100×100 (3)
＜体積平均粒子径＞
レーザ回折式粒度分布測定装置（ＢＥＣＫＭＡＮ ＣＯＵＬＴＥＲ社製 ＬＳ １３ ３２０）を用いて測定されるＤ５０を体積平均粒子径とした。
<Volume average particle size>
D50 measured using a laser diffraction particle size distribution analyzer (LS 13 320 manufactured by BECKMAN COULTER) was taken as the volume average particle size.
＜消臭効果＞
イソ吉草酸（疑似悪臭）０．０１質量％エタノール溶液５００μＬを６ｃｍ×６ｃｍの綿布に滴下し、一晩ドラフト内で放置したものを消臭対象品とした。各例の粉末消臭剤組成物０．５ｇを消臭対象品に散布し、直後の臭気強度の官能評価を行った。官能評価は、５名のパネラが下記の判断基準に基づき行い、その判断結果の平均値を求めた。
<Deodorizing effect>
500 μL of a 0.01% by mass ethanol solution of isovaleric acid (pseudo-malodor) was dropped on a cotton cloth of 6 cm×6 cm, and left overnight in a fume hood to be deodorized. 0.5 g of the powder deodorant composition of each example was sprayed on the article to be deodorized, and sensory evaluation of the odor intensity was performed immediately after the application. The sensory evaluation was performed by five panelists based on the following judgment criteria, and the average value of the judgment results was obtained.
（判断基準）
０点：消臭効果が非常に高い。悪臭を全く感じない。
１点：消臭効果が高い。悪臭をほとんど感じない。
２点：消臭効果がやや高い。悪臭をやや感じる。
３点：消臭効果が低い。悪臭がほとんど低減しない。
４点：消臭効果が全くない。悪臭が低減しない。
(Evaluation criteria)
0 point: Very high deodorizing effect. It doesn't smell bad at all.
1 point: High deodorizing effect. Almost no odor.
2 points: Slightly high deodorizing effect. Slightly foul odor.
3 points: Low deodorizing effect. Bad odor is hardly reduced.
4 points: No deodorizing effect at all. Does not reduce odors.
＜冷感効果＞
各例の粉末消臭剤組成物１ｇを靴（２６ｃｍ、右足）のかかと部分に乗せた。靴のつま先部分を下方４５°に向け、靴のかかと部分を３回叩くことで全体に広げた。
その後、２名のバネラが、各々靴下（ユニクロ製スーピマコットンカノコソックス）を着用した右足で靴を履き、冷感を感じるまでの時間を計測した。その時間の平均値（冷感効果発揮時間）に基づき、以下の判断基準で評価した。
<Chilling effect>
1 g of the powder deodorant composition of each example was placed on the heel of a shoe (26 cm, right foot). The toe portion of the shoe was turned 45° downward and the heel portion of the shoe was tapped three times to spread it all over.
After that, two vanera put on socks (Uniqlo Supima Cotton Kanoko Socks) on their right feet, and measured the time it took them to feel a cold sensation. Based on the average value of the time (duration of cooling sensation effect), evaluation was made according to the following criteria.
（判断基準）
◎１０分以内に冷感を感じる。
〇３０分以内に冷感を感じる。
△１時間以内に冷感を感じる。
×冷感を感じるまで１時間以上かかるか、または冷感を感じない。
(Evaluation criteria)
◎ Feel a cold sensation within 10 minutes.
〇I feel a cold sensation within 30 minutes.
△ You feel a cold sensation within 1 hour.
× It takes 1 hour or more to feel a cold sensation, or no cold sensation is felt.
≪各例の組成物の調製≫
表１の配合で各成分を混合し、各例の靴用粉末消臭剤組成物を調製した。なお、混合は、密閉したビニール袋内で３０回ほど振ることにより行った。
各例の５０μｍ以下の粒子量、消臭効果、冷感効果を表１に示す。
<<Preparation of the composition of each example>>
Each component was mixed according to the formulation shown in Table 1 to prepare a powder deodorant composition for shoes of each example. In addition, mixing was performed by shaking about 30 times in a sealed plastic bag.
Table 1 shows the amount of particles of 50 µm or less, the deodorant effect, and the cooling sensation effect of each example.
表１の結果に示されるように、実施例の靴用粉末消臭剤組成物は、消臭効果、冷感効果のいずれにおいても良好な評価が得られた。
これに対して、５０μｍ以下の粒子量が少ない比較例１、２は、冷感効果に劣っていた。また、（Ａ）成分を配合していない比較例３は、消臭効果に劣っていた。
また、実施例１、７と比較例１との対比から、５０μｍ以下の粒子量を充分な量とすることにより、冷感効果だけでなく消臭効果も向上することがわかった。
As shown in the results of Table 1, the powder deodorant compositions for shoes of Examples were evaluated to be good in both the deodorizing effect and the cooling sensation effect.
On the other hand, Comparative Examples 1 and 2, in which the amount of particles of 50 μm or less was small, were inferior in cooling effect. Moreover, Comparative Example 3, in which the component (A) was not blended, was inferior in deodorizing effect.
Also, from a comparison between Examples 1 and 7 and Comparative Example 1, it was found that not only the cooling sensation effect but also the deodorizing effect was improved by making the amount of particles of 50 μm or less a sufficient amount.
Claims (6)
粒径が５０μｍ以下の粒子の質量が、前記靴用粉末消臭剤組成物の総質量に対して３０質量％以上であり、前記（Ｃ）成分の含有量が、前記靴用粉末消臭剤組成物の総質量に対して５０～９０質量％である、靴の中に散布して使用することを特徴とする靴用粉末消臭剤組成物。
（Ａ）成分：消臭成分
（Ｂ）成分：皮膚に接触したときに冷感又は温感を付与する物質
（Ｃ１）成分：アルミニウム末、カーボンブラック、カルミン、グンジョウ、酸化スズ、酸化チタン、酸化亜鉛、鉛白、リトポン、二酸化チタン、硫酸バリウム、ポリエチレン、及びセラミックパウダーからなる群から選択される１以上の化粧品顔料
（Ｃ２）成分：タルク、カオリン、雲母、セリサイト、白雲母、金雲母、紅雲母、黒雲母、リチア雲母、バーミキュライト、シリカ（（Ａ）成分に該当する多孔質シリカを除く）、焼セッコウ、フッ素アパタイト、ヒドロキシアパタイト、酸化鉄、炭酸マグネシウム、炭酸カルシウム、酸化マグネシウム、酸化ジルコニウム、及び水酸化クロムからなる群から選択される１以上の無機顔料 A powder deodorant composition for shoes comprising a component (C) selected from the following components (A) and (B), and the following components (C1) and (C2),
A powder deodorant composition for shoes, characterized in that the mass of particles having a particle size of 50 μm or less is 30% by mass or more relative to the total mass of the powder deodorant composition for shoes, and the content of the component (C) is 50 to 90% by mass relative to the total mass of the powder deodorant composition for shoes, and is used by being dispersed in shoes.
（Ａ）成分：消臭成分（Ｂ）成分：皮膚に接触したときに冷感又は温感を付与する物質（Ｃ１）成分：アルミニウム末、カーボンブラック、カルミン、グンジョウ、酸化スズ、酸化チタン、酸化亜鉛、鉛白、リトポン、二酸化チタン、硫酸バリウム、ポリエチレン、及びセラミックパウダーからなる群から選択される１以上の化粧品顔料（Ｃ２）成分：タルク、カオリン、雲母、セリサイト、白雲母、金雲母、紅雲母、黒雲母、リチア雲母、バーミキュライト、シリカ（（Ａ）成分に該当する多孔質シリカを除く）、焼セッコウ、フッ素アパタイト、ヒドロキシアパタイト、酸化鉄、炭酸マグネシウム、炭酸カルシウム、酸化マグネシウム、酸化ジルコニウム、及び水酸化クロムからなる群から選択される１以上の無機顔料