JP7471679B1 - Powder deodorant - Google Patents
Powder deodorant Download PDFInfo
- Publication number
- JP7471679B1 JP7471679B1 JP2022204316A JP2022204316A JP7471679B1 JP 7471679 B1 JP7471679 B1 JP 7471679B1 JP 2022204316 A JP2022204316 A JP 2022204316A JP 2022204316 A JP2022204316 A JP 2022204316A JP 7471679 B1 JP7471679 B1 JP 7471679B1
- Authority
- JP
- Japan
- Prior art keywords
- weight
- adsorbent
- basic
- less
- acidic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
【課題】複合臭に対しても、消臭効果を十分に発揮することができる粉末消臭剤を提供する。【解決手段】本発明に係る粉末洗浄剤は、酸性の吸着剤と、塩基性の吸着剤とを含み、前記塩基性の吸着剤が、マグネシウム・アルミニウム・酸化物を含む。【選択図】なし[Problem] To provide a powder deodorant that can fully exert a deodorizing effect even against complex odors. [Solution] The powder detergent according to the present invention contains an acidic adsorbent and a basic adsorbent, and the basic adsorbent contains magnesium aluminum oxide. [Selected Figure] None
Description
本発明は、粉末消臭剤に関する。 The present invention relates to a powder deodorant.
近年、生活環境を快適にするために、臭気に対する意識が高まっている。生活環境における臭気としては、例えば、汗臭、靴及び靴下の悪臭、加齢臭、たばこ臭、生ごみ臭、ペット臭、及び***臭等が挙げられる。 In recent years, there has been growing awareness of odors in order to make the living environment more comfortable. Examples of odors in the living environment include sweat odor, bad odors from shoes and socks, body odor, cigarette odor, food waste odor, pet odor, and excretion odor.
日常生活における臭気対策として、スプレー状、又は液体状の消臭剤が用いられることがある。 To combat odors in everyday life, spray or liquid deodorants are sometimes used.
しかしながら、スプレー状、及び液体状の消臭剤では、時間が経過して乾燥状態になると消臭効果が消失するため、消臭効果が持続しないという課題がある。また、特に液体状の消臭剤では、消臭剤を大量に塗布した場合に塗布部位が湿ってしまい、塗布部位の素材を傷めてしまうことがある。 However, spray and liquid deodorants have the problem that their deodorant effect disappears over time as they dry out, meaning that their deodorant effect does not last. In addition, particularly with liquid deodorants, applying a large amount of the deodorant can cause the area to become damp, which can damage the material of the area to which it is applied.
そこで、消臭効果の持続性を高め、かつ、使用部位が濡れることを防ぐために、粉末状の消臭剤（粉末消臭剤）が用いられることがある。 Therefore, in order to increase the durability of the deodorizing effect and prevent the area where it is used from getting wet, powdered deodorants (powder deodorants) are sometimes used.
下記の特許文献１には、メントールと、消臭及び／又は抗菌作用のある柿タンニン及び酸化銀とを含有し、靴の内部に散布して使用される靴用消臭剤が開示されている。該靴用消臭剤は、粉末状（粒状）である。 The following Patent Document 1 discloses a shoe deodorizer that contains menthol, persimmon tannin and silver oxide, which have deodorizing and/or antibacterial properties, and is used by being sprinkled inside shoes. The shoe deodorizer is in powder (granular) form.
また、下記の特許文献２には、粉体で用いられる靴の消臭剤が開示されている。該靴の消臭剤は、チタニア粒子の表面に光触媒として不活性なセラミックスを島状に担持した光触媒粒子と、重炭酸ナトリウム粒子とを含む。 The following Patent Document 2 discloses a powdered shoe deodorizer. The shoe deodorizer contains photocatalyst particles in which inactive ceramics are supported as photocatalysts in the form of islands on the surface of titania particles, and sodium bicarbonate particles.
生活環境における臭気の原因物質（臭気成分）としては、有機酸、アルデヒド類、アンモニア、アミン類、エステル類、硫黄系化合物、及びアルコール類等が挙げられる。一般に、酸性の臭気成分に対しては、塩基性の消臭成分を配合することにより、中和反応（化学吸着）を利用して消臭することができる。また、塩基性の臭気成分に対しては、酸性の消臭成分を配合することにより、中和反応（化学吸着）を利用して消臭することができる。 Substances that cause odors in the living environment (odor components) include organic acids, aldehydes, ammonia, amines, esters, sulfur-based compounds, and alcohols. In general, for acidic odor components, neutralization reactions (chemical adsorption) can be used to eliminate the odors by blending in basic deodorizing components. For basic odor components, neutralization reactions (chemical adsorption) can be used to eliminate the odors by blending in acidic deodorizing components.
しかしながら、生活環境における臭気は、単一臭（単一の臭気成分により発生する臭気）だけでなく、複合臭（複数の臭気成分により発生する臭気）である場合がある。臭気が複合臭である場合、特に、臭気が酸性の臭気成分と塩基性の臭気成分とを含む場合には、酸性の消臭成分と塩基性の消臭成分とを配合すると、消臭成分同士の中和反応が起こり、消臭効果を十分に発揮することが困難である。 However, odors in the living environment can be not only simple odors (odors caused by a single odor component) but also complex odors (odors caused by multiple odor components). When an odor is complex, particularly when the odor contains an acidic odor component and a basic odor component, combining an acidic deodorizing component with a basic deodorizing component causes a neutralization reaction between the deodorizing components, making it difficult to fully exert the deodorizing effect.
本発明の目的は、複合臭に対しても、消臭効果を十分に発揮することができる粉末消臭剤を提供することである。 The object of the present invention is to provide a powder deodorant that can fully exert its deodorizing effect even against complex odors.
本発明の広い局面によれば、酸性の吸着剤と、塩基性の吸着剤とを含み、前記塩基性の吸着剤が、マグネシウム・アルミニウム・酸化物を含む、粉末消臭剤が提供される。 According to a broad aspect of the present invention, there is provided a powder deodorant comprising an acidic adsorbent and a basic adsorbent, the basic adsorbent comprising magnesium aluminum oxide.
本発明の広い局面によれば、酸性の吸着剤と、塩基性の吸着剤とを含み、前記塩基性の吸着剤が、酸化マグネシウムと、酸化アルミニウムとを含む、粉末消臭剤が提供される。 According to a broad aspect of the present invention, there is provided a powder deodorant comprising an acidic adsorbent and a basic adsorbent, the basic adsorbent comprising magnesium oxide and aluminum oxide.
本発明に係る粉末消臭剤のある特定の局面では、粉末消臭剤１００重量％中、前記マグネシウム・アルミニウム・酸化物の含有量が、３重量％以上２０重量％以下である。 In a particular aspect of the powder deodorant according to the present invention, the content of the magnesium aluminum oxide is 3% by weight or more and 20% by weight or less in 100% by weight of the powder deodorant.
本発明に係る粉末消臭剤のある特定の局面では、粉末消臭剤１００重量％中、前記酸化マグネシウムと前記酸化アルミニウムとの合計の含有量が、３重量％以上２０重量％以下である。 In a particular aspect of the powder deodorant according to the present invention, the total content of the magnesium oxide and the aluminum oxide is 3% by weight or more and 20% by weight or less in 100% by weight of the powder deodorant.
本発明に係る粉末消臭剤のある特定の局面では、前記酸性の吸着剤が、ポリ塩化アルミニウム、又は硫酸アルミニウムカリウムを含む。 In a particular aspect of the powder deodorant according to the present invention, the acidic adsorbent includes polyaluminum chloride or potassium aluminum sulfate.
本発明に係る粉末消臭剤のある特定の局面では、前記塩基性の吸着剤が、金属を含むゼオライトをさらに含む。 In a particular aspect of the powder deodorant according to the present invention, the basic adsorbent further includes a zeolite containing a metal.
本発明に係る粉末消臭剤のある特定の局面では、粉末消臭剤が、吸湿剤をさらに含む。 In a particular aspect of the powder deodorant of the present invention, the powder deodorant further comprises a moisture absorbent.
本発明に係る粉末消臭剤のある特定の局面では、前記吸湿剤が、シリカ、タルク、ケイ酸カルシウム、又は活性炭を含む。 In a particular aspect of the powder deodorant according to the present invention, the moisture absorbent includes silica, talc, calcium silicate, or activated carbon.
本発明に係る粉末消臭剤のある特定の局面では、粉末消臭剤は、靴用消臭剤である。 In a particular aspect of the powder deodorizer of the present invention, the powder deodorizer is a shoe deodorizer.
本発明に係る粉末消臭剤は、酸性の吸着剤と、塩基性の吸着剤とを含み、上記塩基性の吸着剤が、マグネシウム・アルミニウム・酸化物を含む。本発明に係る粉末消臭剤では、上記の構成が備えられているので、複合臭に対しても、消臭効果を十分に発揮することができる。 The powder deodorant according to the present invention contains an acidic adsorbent and a basic adsorbent, and the basic adsorbent contains magnesium aluminum oxide. Since the powder deodorant according to the present invention has the above-mentioned configuration, it can fully exert a deodorizing effect even against complex odors.
本発明に係る粉末消臭剤は、酸性の吸着剤と、塩基性の吸着剤とを含み、上記塩基性の吸着剤が、酸化マグネシウムと、酸化アルミニウムとを含む。本発明に係る粉末消臭剤では、上記の構成が備えられているので、複合臭に対しても、消臭効果を十分に発揮することができる。 The powder deodorant according to the present invention contains an acidic adsorbent and a basic adsorbent, and the basic adsorbent contains magnesium oxide and aluminum oxide. Since the powder deodorant according to the present invention has the above-mentioned configuration, it can fully exert a deodorizing effect even against complex odors.
以下、本発明の詳細を説明する。 The details of the present invention are explained below.
（粉末消臭剤）
本発明に係る粉末消臭剤は、酸性の吸着剤と、塩基性の吸着剤とを含み、上記塩基性の吸着剤が、マグネシウム・アルミニウム・酸化物を含む。また、本発明に係る粉末消臭剤は、酸性の吸着剤と、塩基性の吸着剤とを含み、上記塩基性の吸着剤が、酸化マグネシウムと、酸化アルミニウムとを含む。
(Powder deodorant)
The powder deodorant according to the present invention includes an acidic adsorbent and a basic adsorbent, the basic adsorbent including magnesium aluminum oxide. Also, the powder deodorant according to the present invention includes an acidic adsorbent and a basic adsorbent, the basic adsorbent including magnesium oxide and aluminum oxide.
なお、本明細書において、「酸性の吸着剤」とは、吸着剤を２５℃の水に混合して１重量％混合液を得たときに、該混合液が酸性（ｐＨ７未満）である吸着剤のことをいう。また、「塩基性の吸着剤」とは、吸着剤を２５℃の水に混合して１重量％混合液を得たときに、該混合液が塩基性（ｐＨ７を超える）である吸着剤のことをいう。 In this specification, an "acidic adsorbent" refers to an adsorbent that, when mixed with water at 25°C to obtain a 1% by weight mixed solution, produces an acidic mixture (pH less than 7). Also, a "basic adsorbent" refers to an adsorbent that, when mixed with water at 25°C to obtain a 1% by weight mixed solution, produces a basic mixture (pH greater than 7).
生活環境における臭気は、単一臭（単一の臭気成分により発生する臭気）だけでなく、複合臭（複数の臭気成分により発生する臭気）である場合がある。臭気が複合臭である場合、特に、臭気が酸性の臭気成分と塩基性の臭気成分とを含む場合に、酸性の消臭成分と、塩基性の消臭成分とを配合すると、消臭成分同士の中和反応が起こり、消臭効果を十分に発揮することが困難である。 Odors in the living environment can be not only simple odors (odors caused by a single odor component) but also complex odors (odors caused by multiple odor components). When an odor is complex, particularly when the odor contains an acidic odor component and a basic odor component, combining an acidic deodorizing component with a basic deodorizing component will cause a neutralization reaction between the deodorizing components, making it difficult to fully exert the deodorizing effect.
本発明者らは、鋭意検討の結果、特定の金属酸化物を用いることにより、上記の課題を解決することができることを見出した。 As a result of extensive research, the inventors have discovered that the above problems can be solved by using a specific metal oxide.
本発明に係る粉末消臭剤では、マグネシウム・アルミニウム・酸化物（酸化マグネシウム及び酸化アルミニウム）が用いられているので、酸性の吸着剤と、塩基性の吸着剤とが、互いに中和反応を過度に起こさず、消臭効果を発揮することができる。本発明に係る粉末消臭剤では、上記の構成が備えられているので、単一臭だけでなく、複合臭に対しても、消臭効果を十分に発揮することができる。すなわち、本発明に係る粉末消臭剤では、単一臭及び複合臭に対して、消臭効果を十分に発揮することができる。また、本発明に係る粉末消臭剤では、酸性の臭気成分と塩基性の臭気成分との双方に対して、消臭効果を十分に発揮することができる。また、本発明に係る粉末消臭剤では、消臭効果の持続性を高め、かつ、使用部位が濡れることを防ぐことができる。 The powder deodorant according to the present invention uses magnesium aluminum oxide (magnesium oxide and aluminum oxide), so the acidic adsorbent and the basic adsorbent do not undergo excessive neutralization reactions with each other, and can exert a deodorizing effect. Since the powder deodorant according to the present invention has the above-mentioned configuration, it can fully exert a deodorizing effect not only on single odors, but also on complex odors. That is, the powder deodorant according to the present invention can fully exert a deodorizing effect on single odors and complex odors. Furthermore, the powder deodorant according to the present invention can fully exert a deodorizing effect on both acidic odor components and basic odor components. Furthermore, the powder deodorant according to the present invention can increase the durability of the deodorizing effect and prevent the area where it is used from getting wet.
汗臭、靴及び靴下の悪臭、加齢臭、及びたばこ臭等は、酸性の臭気成分と塩基性の臭気成分とを含む複合臭として知られている。上記酸性の臭気成分としては、イソ吉草酸、酢酸、硫化水素、ノルマル酪酸及びメチルメルカプタン等が挙げられる。上記塩基性の臭気成分としては、アンモニア、トリメチルアミン及びピリジン等が挙げられる。 Sweat odor, bad shoe and sock odor, aging odor, and cigarette odor are known as complex odors that contain acidic and basic odor components. Examples of the acidic odor components include isovaleric acid, acetic acid, hydrogen sulfide, normal butyric acid, and methyl mercaptan. Examples of the basic odor components include ammonia, trimethylamine, and pyridine.
上記粉末消臭剤は、汗臭、靴及び靴下の悪臭、加齢臭、及びたばこ臭等の消臭に好適に用いられる。上記粉末消臭剤は、特に、靴及び靴下の悪臭の消臭に好適に用いられる。上記粉末消臭剤は、靴用消臭剤であることが好ましい。上記粉末消臭剤では、上記の構成が備えられているので、酸性の吸着剤と塩基性の吸着剤とが用いられているにもかかわらず、靴及び靴下の素材を傷めることなく、靴及び靴下の悪臭を消臭することができる。上記粉末消臭剤は、靴に振りかけて用いられることが好ましい。 The powder deodorant is preferably used to deodorize sweat odor, bad odors in shoes and socks, aging odor, and cigarette odor. The powder deodorant is particularly preferably used to deodorize bad odors in shoes and socks. The powder deodorant is preferably a shoe deodorant. Since the powder deodorant has the above-mentioned configuration, it can deodorize bad odors in shoes and socks without damaging the materials of the shoes and socks, despite the use of an acidic adsorbent and a basic adsorbent. The powder deodorant is preferably used by sprinkling it on shoes.
上記粉末消臭剤により消臭可能な素材（上記粉末消臭剤を使用可能な素材）としては、綿、ポリエステル、ナイロン、絹、毛、及び皮等が挙げられる。上記皮は、豚革であってもよく、牛革であってもよく、馬革であってもよく、合成皮革であってもよい。 Materials that can be deodorized by the powder deodorant (materials for which the powder deodorant can be used) include cotton, polyester, nylon, silk, wool, and leather. The leather may be pigskin, cowhide, horsehide, or synthetic leather.
粉末消臭剤の流動性を高める観点からは、上記粉末消臭剤の粒子径は、好ましくは０．０１μｍ以上、より好ましくは０．０５μｍ以上であり、好ましくは１００μｍ以下、より好ましくは９０μｍ以下である。 From the viewpoint of increasing the fluidity of the powder deodorant, the particle size of the powder deodorant is preferably 0.01 μm or more, more preferably 0.05 μm or more, and is preferably 100 μm or less, more preferably 90 μm or less.
上記粉末消臭剤の粒子径は、平均粒子径であることが好ましく、体積平均粒子径であることがより好ましい。上記粉末消臭剤の体積平均粒子径は、以下の方法で測定することができる。レーザー回折式粒度分布測定装置を用いて、乾式、及び体積濃度（測定部容積１００％中の粒子容積）６％の条件で、粉末消臭剤２０ｇについて体積平均粒子径（Ｄ５０）を測定する。上記レーザー回折式粒度分布測定装置としては、ベックマンコールター社製「ＬＳ １３ ３２０」等が挙げられる。 The particle size of the powder deodorant is preferably an average particle size, and more preferably a volume average particle size. The volume average particle size of the powder deodorant can be measured by the following method. Using a laser diffraction particle size distribution measuring device, the volume average particle size (D50) of 20 g of the powder deodorant is measured under dry conditions and a volume concentration (particle volume in 100% of the measurement section volume) of 6%. An example of the laser diffraction particle size distribution measuring device is the "LS 13 320" manufactured by Beckman Coulter.
以下、上記粉末消臭剤に含まれる各成分を説明する。 Below, we will explain each ingredient contained in the powder deodorant.
（塩基性の吸着剤）
上記塩基性の吸着剤は、酸性の臭気成分を吸着可能な吸着剤である。上記塩基性の吸着剤は、化学吸着により酸性の臭気成分を良好に吸着することができる。上記塩基性の吸着剤は、塩基性の臭気成分を吸着可能な吸着剤であってもよい。上記塩基性の吸着剤は、物理吸着により塩基性の臭気成分を吸着してもよい。
(Basic adsorbent)
The basic adsorbent is an adsorbent capable of adsorbing acidic odor components. The basic adsorbent can effectively adsorb acidic odor components by chemical adsorption. The basic adsorbent may be an adsorbent capable of adsorbing basic odor components. The basic adsorbent may adsorb basic odor components by physical adsorption.
上記塩基性の吸着剤は、固体であることが好ましく、粉末状であることがより好ましい。なお、顆粒状は、粉末状に含まれることとする。 The basic adsorbent is preferably a solid, and more preferably a powder. Granular adsorbents are considered to be included in the powder form.
酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高める観点からは、上記塩基性の吸着剤を２５℃の水に混合して得られる１重量％混合液のｐＨは、好ましくは７．２以上、より好ましくは７．５以上、さらに好ましくは８．０以上、特に好ましくは９．０以上であり、好ましくは１４．０以下、より好ましくは１３．０以下、さらに好ましくは１２．０以下、特に好ましくは１１．５以下である。 From the viewpoint of more effectively adsorbing acidic odor components and effectively enhancing the deodorizing effect, the pH of a 1 wt % mixed solution obtained by mixing the above-mentioned basic adsorbent with water at 25°C is preferably 7.2 or more, more preferably 7.5 or more, even more preferably 8.0 or more, particularly preferably 9.0 or more, and is preferably 14.0 or less, more preferably 13.0 or less, even more preferably 12.0 or less, particularly preferably 11.5 or less.
上記塩基性の吸着剤は、マグネシウム・アルミニウム・酸化物を含むか、又は、酸化マグネシウムと、酸化アルミニウムとを含む。上記塩基性の吸着剤は、マグネシウム・アルミニウム・酸化物を含んでいてもよい。上記塩基性の吸着剤は、酸化マグネシウムと、酸化アルミニウムとを含んでいてもよい。上記マグネシウム・アルミニウム・酸化物は、酸化マグネシウムと、酸化アルミニウムとの混合物である。酸化マグネシウムと、酸化アルミニウムとの混合物が、ＣＡＳ番号１１１３７－９８－７における化学名又は一般名として、マグネシウム・アルミニウム・酸化物と呼ばれることがある。 The basic adsorbent includes magnesium aluminum oxide, or includes magnesium oxide and aluminum oxide. The basic adsorbent may include magnesium aluminum oxide. The basic adsorbent may include magnesium oxide and aluminum oxide. The magnesium aluminum oxide is a mixture of magnesium oxide and aluminum oxide. The mixture of magnesium oxide and aluminum oxide is sometimes called magnesium aluminum oxide as a chemical name or common name in CAS number 11137-98-7.
上記マグネシウム・アルミニウム・酸化物において、酸化マグネシウムの含有量（重量％）の酸化アルミニウムの含有量（重量％）に対する重量比（ＭｇＯ／Ａｌ２Ｏ３）は、好ましくは１．０以上、より好ましくは１．５以上であり、好ましくは３．０以下、より好ましくは２．５以下である。上記重量比（ＭｇＯ／Ａｌ２Ｏ３）が上記下限以上及び上記上限以下であると、酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。 In the magnesium aluminum oxide, the weight ratio (MgO/ Al2O3 ) of the magnesium oxide content (wt%) to the aluminum oxide content (wt%) is preferably 1.0 or more, more preferably 1.5 or more, and preferably 3.0 or less, more preferably 2.5 or less. When the weight ratio (MgO / Al2O3 ) is equal to or more than the lower limit and equal to or less than the upper limit, acidic odor components can be more effectively adsorbed , and the deodorizing effect can be effectively enhanced.
酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高める観点からは、上記マグネシウム・アルミニウム・酸化物の粒子径は、好ましくは０．０５μｍ以上、より好ましくは０．１μｍ以上であり、好ましくは４０μｍ以下、より好ましくは３５μｍ以下、さらに好ましくは３０μｍ以下である。 From the viewpoint of more effectively absorbing acidic odor components and effectively enhancing the deodorizing effect, the particle size of the magnesium aluminum oxide is preferably 0.05 μm or more, more preferably 0.1 μm or more, and is preferably 40 μm or less, more preferably 35 μm or less, and even more preferably 30 μm or less.
上記塩基性の吸着剤は、マグネシウム・アルミニウム・酸化物とは異なる塩基性の吸着剤（他の塩基性の吸着剤ともいう）をさらに含んでいてもよく、酸化マグネシウム及び酸化アルミニウムの双方と異なる塩基性の吸着剤（他の塩基性の吸着剤ともいう）をさらに含んでいてもよい。 The basic adsorbent may further include a basic adsorbent other than magnesium aluminum oxide (also referred to as other basic adsorbents), or may further include a basic adsorbent other than both magnesium oxide and aluminum oxide (also referred to as other basic adsorbents).
上記他の塩基性の吸着剤としては、炭酸水素ナトリウム、セスキ炭酸ナトリウム、炭酸ナトリウム、ケイ酸アルミニウム、アルミノケイ酸塩、及びゼオライト等が挙げられる。上記他の塩基性の吸着剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。 The other basic adsorbents include sodium bicarbonate, sodium sesquicarbonate, sodium carbonate, aluminum silicate, aluminosilicate, zeolite, etc. The other basic adsorbents may be used alone or in combination of two or more.
上記アルミノケイ酸塩としては、アルミノケイ酸亜鉛、アルミノケイ酸銀、アルミノケイ酸ナトリウム、及びアルミノケイ酸銅等が挙げられる。 Examples of the aluminosilicates include zinc aluminosilicate, silver aluminosilicate, sodium aluminosilicate, and copper aluminosilicate.
上記ゼオライトは、アルミノケイ酸塩の結晶材料である。上記ゼオライトは、天然ゼオライトであってもよく、合成ゼオライトであってもよい。 The zeolite is a crystalline aluminosilicate material. The zeolite may be a natural zeolite or a synthetic zeolite.
上記天然ゼオライトとしては、クリノプチロライト（斜プチロル沸石）、モルデナイト（モルデン沸石）、菱沸石、ナトロライト、ゴンナルダイト、エディングトナイト、アナルシム、リューサイト、ユガワラライト、ギスモンダイン、ポーリンジャイト、フィリップサイト、チャバザイト、エリオナイト、ホージャサイト、フェリエライト、ミューティナアイト、チェルニヒアイト、ヒューランダイト、スティルバイト、コウレサイト、ベリロケイ酸塩（ロギアナイト、シャンハライト等）、及びジンコケイ酸塩（ガウルタイト）等が挙げられる。 Examples of the natural zeolites include clinoptilolite, mordenite, chabazite, natrolite, gonnardite, edingtonite, analcime, leucite, yugawallerite, gismondine, paulingite, phillipsite, chabazite, erionite, faujasite, ferrierite, mutinaite, chernigite, heulandite, stilbite, kolesite, beryllosilicates (logianite, shanhalite, etc.), and zincosilicates (gaulthite).
上記合成ゼオライトとしては、Ａ型ゼオライト、Ｘ型ゼオライト、Ｙ型ゼオライト、Ｌ型ゼオライト、ベータ型ゼオライト、フェリエライト、モルデナイト、オフレタイト、チャバザイト、ＭＣＭ－２２、ＺＳＭ－５、ＺＳＭ－１１、及びＳＡＰＯ－１１等が挙げられる。なお、上記合成ゼオライトは、人工ゼオライトであってもよい。 Examples of the synthetic zeolite include A-type zeolite, X-type zeolite, Y-type zeolite, L-type zeolite, beta-type zeolite, ferrierite, mordenite, offretite, chabazite, MCM-22, ZSM-5, ZSM-11, and SAPO-11. The synthetic zeolite may be an artificial zeolite.
酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高める観点からは、上記ゼオライトは、金属を含むことが好ましい。上記ゼオライトが金属を含む場合に、上記金属は、イオンの形態で含まれていてもよい。金属を含むゼオライトは、金属イオンを含むゼオライトであってもよい。 From the viewpoint of more effectively adsorbing acidic odor components and effectively enhancing the deodorizing effect, it is preferable that the zeolite contains a metal. When the zeolite contains a metal, the metal may be contained in the form of an ion. The zeolite containing a metal may be a zeolite containing a metal ion.
上記金属としては、亜鉛、錫、鉄、白金、パラジウム、チタン、銀、銅、マンガン、及びコバルト等が挙げられる。 The above metals include zinc, tin, iron, platinum, palladium, titanium, silver, copper, manganese, and cobalt.
上記粉末消臭剤に除菌抗菌効果を付与したり、消臭効果をより一層効果的に高めたりする観点からは、上記ゼオライトは、銀又は亜鉛を含むことが好ましく、上記塩基性の吸着剤は、銀及び亜鉛を含むゼオライトを含むことがより好ましい。上記粉末消臭剤に除菌抗菌効果を付与したり、消臭効果をより一層効果的に高めたりする観点からは、上記塩基性の吸着剤は、銀又は亜鉛を含むゼオライトを含むことが好ましく、銀及び亜鉛を含むゼオライトを含むことがより好ましい。上記粉末消臭剤に除菌抗菌効果を付与する観点からは、上記ゼオライトは、銀を含むことが好ましく、上記塩基性の吸着剤は、銀を含むゼオライトを含むことが好ましい。消臭効果をより一層効果的に高める観点からは、上記ゼオライトは、亜鉛を含むことが好ましく、上記塩基性の吸着剤は、亜鉛を含むゼオライトを含むことが好ましい。 From the viewpoint of imparting a disinfecting and antibacterial effect to the powder deodorant and more effectively enhancing the deodorizing effect, the zeolite preferably contains silver or zinc, and the basic adsorbent preferably contains a zeolite containing silver and zinc. From the viewpoint of imparting a disinfecting and antibacterial effect to the powder deodorant and more effectively enhancing the deodorizing effect, the basic adsorbent preferably contains a zeolite containing silver or zinc, and more preferably contains a zeolite containing silver and zinc. From the viewpoint of imparting a disinfecting and antibacterial effect to the powder deodorant, the zeolite preferably contains silver, and the basic adsorbent preferably contains a zeolite containing silver. From the viewpoint of more effectively enhancing the deodorizing effect, the zeolite preferably contains zinc, and the basic adsorbent preferably contains a zeolite containing zinc.
酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高める観点からは、上記ゼオライトは、骨格構造中に陽イオンを含むことが好ましい。上記陽イオンとしては、水素イオン、アンモニウムイオン、アルキル置換のアンモニウムイオン、アリール又はアラルキル置換のアンモニウムイオン、アルカリ金属イオン、アルカリ土類金属イオン、金属イオン、及びガリウムイオン等が挙げられる。上記陽イオンは１種のみが用いられてもよく、２種以上が併用されてもよい。上記ゼオライト中の上記陽イオンの含有量は、特に限定されない。 From the viewpoint of more effectively adsorbing acidic odor components and effectively enhancing the deodorizing effect, it is preferable that the zeolite contains cations in the framework structure. Examples of the cations include hydrogen ions, ammonium ions, alkyl-substituted ammonium ions, aryl- or aralkyl-substituted ammonium ions, alkali metal ions, alkaline earth metal ions, metal ions, and gallium ions. Only one type of the cations may be used, or two or more types may be used in combination. There is no particular limit to the amount of the cations contained in the zeolite.
上記アラルキル置換のアンモニウムイオンとしては、メチルアンモニウムイオン、ジメチルアンモニウムイオン、トリメチルアンモニウムイオン、及びテトラメチルアンモニウムイオン等が挙げられる。 Examples of the aralkyl-substituted ammonium ion include methylammonium ion, dimethylammonium ion, trimethylammonium ion, and tetramethylammonium ion.
上記アルカリ金属イオンとしては、リチウムイオン、ナトリウムイオン、及びカリウムイオン等が挙げられる。 Examples of the alkali metal ions include lithium ions, sodium ions, and potassium ions.
上記アルカリ土類金属イオンとしては、マグネシウムイオン、カルシウムイオン、及びバリウムイオン等が挙げられる。 Examples of the alkaline earth metal ions include magnesium ions, calcium ions, and barium ions.
上記金属イオンとしては、亜鉛イオン、錫イオン、鉄イオン、白金イオン、パラジウムイオン、チタンイオン、銀イオン、銅イオン、マンガンイオン、及びコバルトイオン等が挙げられる。 The above metal ions include zinc ions, tin ions, iron ions, platinum ions, palladium ions, titanium ions, silver ions, copper ions, manganese ions, and cobalt ions.
消臭効果をより一層効果的に高める観点からは、上記陽イオンは、金属イオンを含むことが好ましい。消臭効果をより一層効果的に高める観点からは、上記塩基性の吸着剤は、金属イオンを含むゼオライトをさらに含むことが好ましい。上記粉末消臭剤に除菌抗菌効果を付与したり、消臭効果をより一層効果的に高めたりする観点からは、上記ゼオライトは、銀イオン又は亜鉛イオンを含むことが好ましく、上記塩基性の吸着剤は、銀イオン及び亜鉛イオンを含むゼオライトを含むことがより好ましい。上記粉末消臭剤に除菌抗菌効果を付与したり、消臭効果をより一層効果的に高めたりする観点からは、上記塩基性の吸着剤は、銀イオン又は亜鉛イオンを含むゼオライトを含むことが好ましく、銀イオン及び亜鉛イオンを含むゼオライトを含むことがより好ましい。上記粉末消臭剤に除菌抗菌効果を付与する観点からは、上記ゼオライトは、銀イオンを含むことが好ましく、上記塩基性の吸着剤は、銀イオンを含むゼオライトを含むことが好ましい。消臭効果をより一層効果的に高める観点からは、上記ゼオライトは、亜鉛イオンを含むことが好ましく、上記塩基性の吸着剤は、亜鉛イオンを含むゼオライトを含むことが好ましい。 From the viewpoint of more effectively enhancing the deodorizing effect, the cations preferably contain metal ions. From the viewpoint of more effectively enhancing the deodorizing effect, the basic adsorbent preferably further contains zeolite containing metal ions. From the viewpoint of imparting a disinfecting and antibacterial effect to the powder deodorant and more effectively enhancing the deodorizing effect, the zeolite preferably contains silver ions or zinc ions, and the basic adsorbent more preferably contains zeolite containing silver ions and zinc ions. From the viewpoint of imparting a disinfecting and antibacterial effect to the powder deodorant and more effectively enhancing the deodorizing effect, the basic adsorbent preferably contains zeolite containing silver ions or zinc ions, and more preferably contains zeolite containing silver ions and zinc ions. From the viewpoint of imparting a disinfecting and antibacterial effect to the powder deodorant, the zeolite preferably contains silver ions, and the basic adsorbent preferably contains zeolite containing silver ions. From the viewpoint of further effectively enhancing the deodorizing effect, it is preferable that the zeolite contains zinc ions, and it is preferable that the basic adsorbent contains zeolite containing zinc ions.
酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高める観点からは、上記塩基性の吸着剤は、アルミノケイ酸塩、又はゼオライトをさらに含むことが好ましい。上記粉末消臭剤に除菌抗菌効果を付与する観点からは、上記塩基性の吸着剤は、アルミノケイ酸銀、又は銀（銀イオンであってもよい）を含むゼオライトをさらに含むことが特に好ましい。 From the viewpoint of more effectively adsorbing acidic odor components and effectively enhancing the deodorizing effect, it is preferable that the basic adsorbent further contains an aluminosilicate or a zeolite. From the viewpoint of imparting a disinfecting and antibacterial effect to the powder deodorant, it is particularly preferable that the basic adsorbent further contains silver aluminosilicate or a zeolite containing silver (which may be silver ions).
上記粉末消臭剤は、ハイドロタルサイトを含んでいてもよく、含んでいなくてもよい。上記粉末消臭剤は、マグネシウム・アルミニウム・酸化物に代えて、ハイドロタルサイトを含んでいてもよく、含んでいなくてもよい。上記ハイドロタルサイトとしては、Ｍｇ４．５Ａｌ２（ＯＨ）１３（ＣＯ３）・３．５Ｈ２Ｏ、及びＭｇ６Ａｌ２（ＯＨ）１６（ＣＯ３）・４Ｈ２Ｏ等が挙げられる。上記粉末消臭剤は、Ｍｇ４．５Ａｌ２（ＯＨ）１３（ＣＯ３）・３．５Ｈ２Ｏを含んでいてもよく、含んでいなくてもよい。上記粉末消臭剤は、Ｍｇ６Ａｌ２（ＯＨ）１６（ＣＯ３）・４Ｈ２Ｏを含んでいてもよく、含んでいなくてもよい。 The powder deodorant may or may not contain hydrotalcite. The powder deodorant may or may not contain hydrotalcite instead of magnesium aluminum oxide. Examples of the hydrotalcite include Mg 4.5 Al 2 (OH) 13 (CO 3 ). 3.5H 2 O and Mg 6 Al 2 (OH) 16 (CO 3 ). 4H 2 O. The powder deodorant may or may not contain Mg 4.5 Al 2 (OH) 13 (CO 3 ). 3.5H 2 O. The powder deodorant may or may not contain Mg 6 Al 2 (OH) 16 (CO 3 ). 4H 2 O.
酸性の臭気成分をより一層効果的に吸着し、消臭効果をより一層効果的に高める観点からは、上記他の塩基性の吸着剤の粒子径は、好ましくは０．０１μｍ以上、より好ましくは０．１μｍ以上であり、好ましくは１００μｍ以下、より好ましくは９０μｍ以下である。 From the viewpoint of more effectively adsorbing acidic odor components and more effectively enhancing the deodorizing effect, the particle size of the other basic adsorbents is preferably 0.01 μm or more, more preferably 0.1 μm or more, and is preferably 100 μm or less, more preferably 90 μm or less.
上記他の塩基性の吸着剤は、多孔質構造を有していてもよく、有していなくてもよい。臭気成分をより一層効果的に吸着する観点からは、上記他の塩基性の吸着剤は、多孔質構造を有することが好ましい。 The other basic adsorbents may or may not have a porous structure. From the viewpoint of more effectively adsorbing odorous components, it is preferable that the other basic adsorbents have a porous structure.
上記他の塩基性の吸着剤が多孔質構造を有する場合には、臭気成分をより一層効果的に吸着する観点からは、上記他の塩基性の吸着剤のＢＥＴ比表面積は、好ましくは１００ｍ２／ｇ以上、より好ましくは、３００ｍ２／ｇ以上、さらに好ましくは４００ｍ２／ｇ以上であり、好ましくは１０００ｍ２／ｇ以下、より好ましくは９００ｍ２／ｇ以下である。上記他の塩基性の吸着剤のＢＥＴ比表面積は、ガス吸着容量測定装置を用いて、測定することができる。 When the other basic adsorbent has a porous structure, from the viewpoint of more effectively adsorbing odor components, the BET specific surface area of the other basic adsorbent is preferably 100 m2/g or more, more preferably 300 m2/g or more, even more preferably 400 m2 /g or more, and is preferably 1000 m2 /g or less, more preferably 900 m2 /g or less. The BET specific surface area of the other basic adsorbent can be measured using a gas adsorption capacity measuring device.
上記他の塩基性の吸着剤が多孔質構造を有する場合には、臭気成分をより一層効果的に吸着する観点からは、上記他の塩基性の吸着剤の細孔容積は、好ましくは０．１ｍｌ／ｇ以上、より好ましくは０．３ｍｌ／ｇ以上であり、好ましくは１．５ｍｌ／ｇ以下、より好ましくは１．０ｍｌ／ｇ以下である。上記他の塩基性の吸着剤の細孔容積は、ガス吸着容量測定装置を用いて、測定することができる。 When the other basic adsorbent has a porous structure, from the viewpoint of more effectively adsorbing odor components, the pore volume of the other basic adsorbent is preferably 0.1 ml/g or more, more preferably 0.3 ml/g or more, and preferably 1.5 ml/g or less, more preferably 1.0 ml/g or less. The pore volume of the other basic adsorbent can be measured using a gas adsorption capacity measuring device.
上記粉末消臭剤１００重量％中、上記塩基性の吸着剤の含有量は、好ましくは１重量％以上、より好ましくは３重量％以上、さらに好ましくは５重量％以上であり、好ましくは３０重量％以下、より好ましくは２５重量％以下、さらに好ましくは２０重量％以下である。上記塩基性の吸着剤の含有量が上記下限以上であると、酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記塩基性の吸着剤の含有量が上記上限以下であると、後述する他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。なお、塩基性の吸着剤の含有量は、マグネシウム・アルミニウム・酸化物と上記他の塩基性の吸着剤との合計の含有量、又は、酸化マグネシウムと酸化アルミニウムと上記他の塩基性の吸着剤との合計の含有量である。上記粉末消臭剤が上記他の塩基性の吸着剤を含まない場合には、塩基性の吸着剤の含有量は、マグネシウム・アルミニウム・酸化物の含有量、又は、酸化マグネシウムと酸化アルミニウムとの合計の含有量である。 In the powder deodorant 100% by weight, the content of the basic adsorbent is preferably 1% by weight or more, more preferably 3% by weight or more, even more preferably 5% by weight or more, and preferably 30% by weight or less, more preferably 25% by weight or less, and even more preferably 20% by weight or less. When the content of the basic adsorbent is equal to or more than the lower limit, acidic odor components can be more effectively adsorbed, and the deodorizing effect can be effectively enhanced. When the content of the basic adsorbent is equal to or less than the upper limit, the blending amount of the other components described below can be increased, and the blending effect of the other components can be enhanced. The content of the basic adsorbent is the total content of magnesium aluminum oxide and the other basic adsorbent, or the total content of magnesium oxide, aluminum oxide, and the other basic adsorbent. When the powder deodorant does not contain the other basic adsorbent, the content of the basic adsorbent is the total content of magnesium aluminum oxide, or the total content of magnesium oxide and aluminum oxide.
上記粉末消臭剤１００重量％中、上記酸性の吸着剤と上記塩基性の吸着剤との合計の含有量は、好ましくは２重量％以上、より好ましくは５重量％以上、さらに好ましくは１０重量％以上であり、好ましくは５０重量％以下、より好ましくは４５重量％以下、さらに好ましくは４０重量％以下である。上記酸性の吸着剤と上記塩基性の吸着剤との合計の含有量が上記下限以上であると、複合臭の消臭効果を効果的に高めることができる。上記酸性の吸着剤と上記塩基性の吸着剤との合計の含有量が上記上限以下であると、他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。 In 100% by weight of the powder deodorant, the total content of the acidic adsorbent and the basic adsorbent is preferably 2% by weight or more, more preferably 5% by weight or more, even more preferably 10% by weight or more, and preferably 50% by weight or less, more preferably 45% by weight or less, even more preferably 40% by weight or less. When the total content of the acidic adsorbent and the basic adsorbent is equal to or more than the lower limit, the deodorizing effect of the complex odor can be effectively enhanced. When the total content of the acidic adsorbent and the basic adsorbent is equal to or less than the upper limit, the blending amount of the other components can be increased, and the blending effect of the other components can be enhanced.
上記酸性の吸着剤と上記塩基性の吸着剤との合計１００重量％中、上記塩基性の吸着剤の含有量は、好ましくは１０重量％以上、より好ましくは２０重量％以上、さらに好ましくは３０重量％以上であり、好ましくは８０重量％以下、より好ましくは７０重量％以下、さらに好ましくは６０重量％以下である。上記塩基性の吸着剤の含有量が上記下限以上であると、酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記塩基性の吸着剤の含有量が上記上限以下であると、他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。 Of the total of the acidic adsorbent and the basic adsorbent (100% by weight), the content of the basic adsorbent is preferably 10% by weight or more, more preferably 20% by weight or more, even more preferably 30% by weight or more, and preferably 80% by weight or less, more preferably 70% by weight or less, even more preferably 60% by weight or less. When the content of the basic adsorbent is equal to or more than the lower limit, acidic odor components can be more effectively adsorbed, and the deodorizing effect can be effectively enhanced. When the content of the basic adsorbent is equal to or less than the upper limit, the amount of other components can be increased, and the effect of the other components can be enhanced.
粉末消臭剤１００重量％中、上記マグネシウム・アルミニウム・酸化物の含有量は、好ましくは３重量％以上、より好ましくは３．５重量％以上であり、好ましくは２０重量％以下、より好ましくは１７重量％以下、さらに好ましくは１５重量％以下である。上記マグネシウム・アルミニウム・酸化物の含有量が上記下限以上であると、酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記マグネシウム・アルミニウム・酸化物の含有量が上記上限以下であると、他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。 In 100% by weight of the powder deodorant, the content of the magnesium aluminum oxide is preferably 3% by weight or more, more preferably 3.5% by weight or more, and preferably 20% by weight or less, more preferably 17% by weight or less, and even more preferably 15% by weight or less. When the content of the magnesium aluminum oxide is equal to or greater than the lower limit, acidic odor components can be more effectively adsorbed, and the deodorant effect can be effectively enhanced. When the content of the magnesium aluminum oxide is equal to or less than the upper limit, the amount of other components can be increased, and the effect of the other components can be enhanced.
上記塩基性の吸着剤１００重量％中、上記マグネシウム・アルミニウム・酸化物の含有量は、好ましくは１０重量％以上、より好ましくは２０重量％以上、さらに好ましくは３０重量％以上であり、好ましくは１００重量％以下、より好ましくは８０重量％以下、さらに好ましくは６０重量％以下である。上記マグネシウム・アルミニウム・酸化物の含有量が上記下限以上であると、酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記マグネシウム・アルミニウム・酸化物の含有量が上記上限以下であると、他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。 In 100% by weight of the basic adsorbent, the content of the magnesium aluminum oxide is preferably 10% by weight or more, more preferably 20% by weight or more, and even more preferably 30% by weight or more, and is preferably 100% by weight or less, more preferably 80% by weight or less, and even more preferably 60% by weight or less. When the content of the magnesium aluminum oxide is equal to or greater than the lower limit, acidic odor components can be more effectively adsorbed, and the deodorizing effect can be effectively enhanced. When the content of the magnesium aluminum oxide is equal to or less than the upper limit, the amount of other components can be increased, and the effect of the other components can be enhanced.
粉末消臭剤１００重量％中、上記酸化マグネシウムと上記酸化アルミニウムとの合計の含有量は、好ましくは３重量％以上、より好ましくは３．５重量％以上であり、好ましくは２０重量％以下、より好ましくは１７重量％以下、さらに好ましくは１５重量％以下である。上記酸化マグネシウムと上記酸化アルミニウムとの合計の含有量が上記下限以上であると、酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記酸化マグネシウムと上記酸化アルミニウムとの合計の含有量が上記上限以下であると、他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。 In 100% by weight of the powder deodorant, the total content of the magnesium oxide and aluminum oxide is preferably 3% by weight or more, more preferably 3.5% by weight or more, and preferably 20% by weight or less, more preferably 17% by weight or less, and even more preferably 15% by weight or less. When the total content of the magnesium oxide and aluminum oxide is equal to or greater than the lower limit, acidic odor components can be more effectively adsorbed, and the deodorant effect can be effectively enhanced. When the total content of the magnesium oxide and aluminum oxide is equal to or less than the upper limit, the amount of other components can be increased, and the effect of the other components can be enhanced.
上記塩基性の吸着剤１００重量％中、上記酸化マグネシウムと上記酸化アルミニウムとの合計の含有量は、好ましくは１０重量％以上、より好ましくは２０重量％以上、さらに好ましくは３０重量％以上であり、好ましくは１００重量％以下、より好ましくは８０重量％以下、さらに好ましくは６０重量％以下である。上記酸化マグネシウムと上記酸化アルミニウムとの合計の含有量が上記下限以上であると、酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記酸化マグネシウムと上記酸化アルミニウムとの合計の含有量が上記上限以下であると、他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。 In 100% by weight of the basic adsorbent, the total content of the magnesium oxide and the aluminum oxide is preferably 10% by weight or more, more preferably 20% by weight or more, and even more preferably 30% by weight or more, and is preferably 100% by weight or less, more preferably 80% by weight or less, and even more preferably 60% by weight or less. When the total content of the magnesium oxide and the aluminum oxide is equal to or more than the lower limit, acidic odor components can be more effectively adsorbed, and the deodorizing effect can be effectively enhanced. When the total content of the magnesium oxide and the aluminum oxide is equal to or less than the upper limit, the amount of other components can be increased, and the effect of the other components can be enhanced.
上記塩基性の吸着剤１００重量％中、上記金属（金属イオンであってもよい）を含むゼオライトの含有量は、好ましくは１０重量％以上、より好ましくは２０重量％以上、さらに好ましくは３０重量％以上であり、好ましくは８０重量％以下、より好ましくは７０重量％以下、さらに好ましくは６０重量％以下である。上記金属を含むゼオライトの含有量が上記下限以上であると、酸性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記金属を含むゼオライトの含有量が上記上限以下であると、粉末消臭剤の流動性を高めることができる。 In 100% by weight of the basic adsorbent, the content of the zeolite containing the metal (which may be a metal ion) is preferably 10% by weight or more, more preferably 20% by weight or more, even more preferably 30% by weight or more, and preferably 80% by weight or less, more preferably 70% by weight or less, even more preferably 60% by weight or less. When the content of the zeolite containing the metal is equal to or more than the lower limit, acidic odor components can be more effectively adsorbed, and the deodorizing effect can be effectively enhanced. When the content of the zeolite containing the metal is equal to or less than the upper limit, the fluidity of the powder deodorant can be enhanced.
（酸性の吸着剤）
上記酸性の吸着剤は、塩基性の臭気成分を吸着可能な吸着剤である。上記酸性の吸着剤は、化学吸着により塩基性の臭気成分を良好に吸着することができる。上記酸性の吸着剤は、酸性の臭気成分を吸着可能な吸着剤であってもよい。上記酸性の吸着剤は、物理吸着により酸性の臭気成分を吸着してもよい。
(acidic adsorbent)
The acidic adsorbent is an adsorbent capable of adsorbing basic odor components. The acidic adsorbent can effectively adsorb basic odor components by chemical adsorption. The acidic adsorbent may be an adsorbent capable of adsorbing acidic odor components. The acidic adsorbent may adsorb acidic odor components by physical adsorption.
上記酸性の吸着剤は、固体であることが好ましく、粉末状であることがより好ましい。なお、顆粒状は、粉末状に含まれることとする。 The acidic adsorbent is preferably a solid, and more preferably a powder. Note that granular adsorbents are considered to be in the powder form.
塩基性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高める観点からは、上記酸性の吸着剤を２５℃の水に混合して得られる１重量％混合液のｐＨは、好ましくは１．０以上、より好ましくは１．５以上、さらに好ましくは２．０以上であり、好ましくは６．８以下、より好ましくは６．５以下、さらに好ましくは６．２以下、特に好ましくは５．９以下である。 From the viewpoint of more effectively adsorbing basic odor components and effectively enhancing the deodorizing effect, the pH of a 1 wt % mixed solution obtained by mixing the above-mentioned acidic adsorbent with water at 25°C is preferably 1.0 or more, more preferably 1.5 or more, even more preferably 2.0 or more, and is preferably 6.8 or less, more preferably 6.5 or less, even more preferably 6.2 or less, and particularly preferably 5.9 or less.
上記酸性の吸着剤としては、ポリ塩化アルミニウム、硫酸アルミニウムカリウム、硫酸アルミニウム、クエン酸、コハク酸、酒石酸、リンゴ酸、フマル酸、マレイン酸及び塩化アルミニウム等が挙げられる。上記酸性の吸着剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。 The above-mentioned acidic adsorbents include polyaluminum chloride, aluminum potassium sulfate, aluminum sulfate, citric acid, succinic acid, tartaric acid, malic acid, fumaric acid, maleic acid, and aluminum chloride. The above-mentioned acidic adsorbents may be used alone or in combination of two or more kinds.
塩基性の臭気成分をより一層効果的に吸着し、消臭効果をより一層高める観点からは、上記酸性の吸着剤は、ポリ塩化アルミニウム、又は硫酸アルミニウムカリウムを含むことが好ましい。 From the viewpoint of more effectively adsorbing basic odor components and further enhancing the deodorizing effect, it is preferable that the acidic adsorbent contains polyaluminum chloride or potassium aluminum sulfate.
塩基性の臭気成分をより一層効果的に吸着し、消臭効果をより一層高める観点からは、上記酸性の吸着剤の粒子径は、好ましくは０．０１μｍ以上、より好ましくは０．５μｍ以上であり、好ましくは１００μｍ以下、より好ましくは９０μｍ以下である。 From the viewpoint of more effectively adsorbing basic odor components and further enhancing the deodorizing effect, the particle size of the acidic adsorbent is preferably 0.01 μm or more, more preferably 0.5 μm or more, and is preferably 100 μm or less, more preferably 90 μm or less.
上記酸性の吸着剤は、多孔質構造を有していてもよく、有していなくてもよい。 The acidic adsorbent may or may not have a porous structure.
上記粉末消臭剤１００重量％中、上記酸性の吸着剤の含有量は、好ましくは１重量％以上、より好ましくは３重量％以上、さらに好ましくは５重量％以上であり、好ましくは３０重量％以下、より好ましくは２５重量％以下、さらに好ましくは２０重量％以下である。上記酸性の吸着剤の含有量が上記下限以上であると、塩基性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記酸性の吸着剤の含有量が上記上限以下であると、他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。 In 100% by weight of the powder deodorant, the content of the acidic adsorbent is preferably 1% by weight or more, more preferably 3% by weight or more, even more preferably 5% by weight or more, and preferably 30% by weight or less, more preferably 25% by weight or less, even more preferably 20% by weight or less. When the content of the acidic adsorbent is equal to or more than the lower limit, basic odor components can be more effectively adsorbed, and the deodorant effect can be effectively enhanced. When the content of the acidic adsorbent is equal to or less than the upper limit, the blending amount of other components can be increased, and the blending effect of other components can be enhanced.
上記塩基性の吸着剤と上記酸性の吸着剤との合計１００重量％中、上記酸性の吸着剤の含有量は、好ましくは１０重量％以上、より好ましくは２０重量％以上、さらに好ましくは３０重量％以上であり、好ましくは８０重量％以下、より好ましくは７０重量％以下、さらに好ましくは６０重量％以下である。上記酸性の吸着剤の含有量が上記下限以上であると、塩基性の臭気成分をより一層効果的に吸着し、消臭効果を効果的に高めることができる。上記酸性の吸着剤の含有量が上記上限以下であると、他の成分の配合量を増やすことができ、他の成分の配合効果を高めることができる。 The content of the acidic adsorbent is preferably 10% by weight or more, more preferably 20% by weight or more, even more preferably 30% by weight or more, and preferably 80% by weight or less, more preferably 70% by weight or less, even more preferably 60% by weight or less, out of a total of 100% by weight of the basic adsorbent and the acidic adsorbent. When the content of the acidic adsorbent is equal to or more than the lower limit, the basic odor components can be more effectively adsorbed, and the deodorizing effect can be effectively enhanced. When the content of the acidic adsorbent is equal to or less than the upper limit, the amount of other components can be increased, and the effect of the other components can be enhanced.
（他の成分）
上記粉末消臭剤は、必要に応じて、例えば、吸湿剤、香料、流動改善剤、除菌抗菌剤、滑沢剤、結合剤、着色剤、キレート剤、ｐＨ調整剤、酵素、甘味料、発泡安定化剤、保存剤、防腐剤、増量剤、賦形剤、及び崩壊剤等の添加剤を含んでいてもよい。
(Other ingredients)
The powder deodorant may contain additives such as a moisture absorbent, a fragrance, a flow improver, a disinfecting antibacterial agent, a lubricant, a binder, a colorant, a chelating agent, a pH adjuster, an enzyme, a sweetener, a foam stabilizer, a preservative, an antiseptic, a bulking agent, an excipient, and a disintegrant, as necessary.
上記粉末消臭剤は、吸湿剤をさらに含むことが好ましい。上記粉末消臭剤が吸湿剤を含む場合には、靴や靴下に付着した汗を吸収し、蒸れを軽減し、菌の増殖を抑制することができる。これらの結果、臭気を低減し、消臭効果をより一層高めることができる。 It is preferable that the powder deodorant further contains a moisture absorbent. When the powder deodorant contains a moisture absorbent, it can absorb sweat adhering to shoes and socks, reduce stuffiness, and inhibit the growth of bacteria. As a result, odors can be reduced and the deodorant effect can be further enhanced.
上記吸湿剤としては、シリカ、タルク、ケイ酸カルシウム、及び活性炭等が挙げられる。上記吸湿剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。 Examples of the moisture absorbent include silica, talc, calcium silicate, and activated carbon. The moisture absorbent may be used alone or in combination of two or more.
消臭効果をより一層高める観点からは、上記吸湿剤は、シリカ、タルク、ケイ酸カルシウム、又は活性炭を含むことが好ましく、シリカを含むことがより好ましい。 To further enhance the deodorizing effect, the moisture absorbent preferably contains silica, talc, calcium silicate, or activated carbon, and more preferably contains silica.
上記吸湿剤は、酸性であってもよく、中性であってもよく、塩基性であってもよい。 The moisture absorbent may be acidic, neutral, or basic.
上記香料としては、メントール、サリチル酸、スペアミント、ペパーミント、及びハッカ油等が挙げられる。上記香料は、１種のみが用いられてもよく、２種以上が併用されてもよい。 The above-mentioned flavorings include menthol, salicylic acid, spearmint, peppermint, and peppermint oil. The above-mentioned flavorings may be used alone or in combination of two or more kinds.
上記流動改善剤としては、タルク、酸化亜鉛、ベントナイト、及びカオリン等が挙げられる。上記流動改善剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。 The above-mentioned flow improvers include talc, zinc oxide, bentonite, kaolin, etc. The above-mentioned flow improvers may be used alone or in combination of two or more kinds.
粉末消臭剤の流動性を高める観点からは、上記流動改善剤は、タルク、酸化亜鉛、ベントナイト、又はカオリンを含むことが好ましく、タルク、又は酸化亜鉛を含むことがより好ましい。 From the viewpoint of increasing the fluidity of the powder deodorant, the flow improver preferably contains talc, zinc oxide, bentonite, or kaolin, and more preferably contains talc or zinc oxide.
上記粉末消臭剤は、除菌抗菌剤をさらに含むことが好ましい。上記粉末消臭剤が除菌抗菌剤を含む場合には、使用部位の除菌抗菌効果を高めることができ、消臭効果をより一層効果的に発揮することができる。 It is preferable that the powder deodorant further contains a disinfecting antibacterial agent. When the powder deodorant contains a disinfecting antibacterial agent, the disinfecting and antibacterial effect on the application site can be enhanced, and the deodorizing effect can be exerted even more effectively.
上記除菌抗菌剤としては、イソプロピルメチルフェノール、塩化セチルピリニジウム、ポリリジン及び塩酸クロルヘキシジン等が挙げられる。上記除菌抗菌剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。 The above-mentioned disinfecting antibacterial agents include isopropyl methylphenol, cetylpyridinium chloride, polylysine, and chlorhexidine hydrochloride. The above-mentioned disinfecting antibacterial agents may be used alone or in combination of two or more kinds.
上記除菌抗菌剤は、上記銀を含むゼオライトであってもよい。 The disinfecting antibacterial agent may be a zeolite containing the silver.
以下、実施例及び比較例を挙げて、本発明を具体的に説明する。本発明は、以下の実施例のみに限定されない。 The present invention will be specifically described below with reference to examples and comparative examples. The present invention is not limited to the following examples.
以下の材料を用意した。 The following materials were prepared:
酸性の吸着剤：
ポリ塩化アルミニウム（１重量％混合液のｐＨ：４．０、大明化学工業社製「アルファインＰ」）
硫酸アルミニウムカリウム（１重量％混合液のｐＨ：３．６、大明化学工業社製「ミョウバン」）
Acidic adsorbents:
Polyaluminum chloride (pH of 1% by weight mixed solution: 4.0, "Alphain P" manufactured by Taimei Chemical Industry Co., Ltd.)
Potassium aluminum sulfate (pH of 1% by weight mixed solution: 3.6, "Alum" manufactured by Taimei Chemical Industry Co., Ltd.)
塩基性の吸着剤：
マグネシウム・アルミニウム・酸化物（酸化マグネシウムと酸化アルミニウムとの混合物、１重量％混合液のｐＨ：１０．８、協和化学工業社製「ＫＷ－２１００」）
亜鉛イオンを含むゼオライト（１重量％混合液のｐＨ：９．０、シナネンゼオミック社製「ダッシュライトＺＨ１０Ｎ」）
亜鉛イオン及び銀イオンを含むゼオライト（１重量％混合液のｐＨ：９．０、シナネンゼオミック社製「ゼオミックＡＪ－１０Ｎ」）
Basic adsorbents:
Magnesium aluminum oxide (a mixture of magnesium oxide and aluminum oxide, pH of 1% by weight mixture: 10.8, Kyowa Chemical Industry Co., Ltd. "KW-2100")
Zeolite containing zinc ions (pH of 1% by weight mixed solution: 9.0, "Dashlight ZH10N" manufactured by Sinanen Zeomic Co., Ltd.)
Zeolite containing zinc ions and silver ions (pH of 1% by weight mixed solution: 9.0, "Zeomic AJ-10N" manufactured by Sinanen Zeomic Co., Ltd.)
吸湿剤：
シリカ（富士シリシア化学社製「サイリシア７３２」）
Moisture absorbent:
Silica ("Silysia 732" manufactured by Fuji Silysia Chemical)
流動改善剤：
タルク（日本タルク社製「タルクＭＳ」）
酸化亜鉛（堺化学工業社製「微細酸化亜鉛」）
Flow improver:
Talc ("Talc MS" manufactured by Nippon Talc Co., Ltd.)
Zinc oxide ("Fine Zinc Oxide" manufactured by Sakai Chemical Industry Co., Ltd.)
香料：
Ｌ－メントール（ユニオン社製「Ｌ－メントール加工品ＩＴ」）
Fragrance:
L-Menthol (Union Co., Ltd. "L-Menthol Processed Product IT")
（実施例１，３～５、参考例２及び比較例１～４）
下記の表１～２に示す成分を下記の表１～２に示す配合量で混合して、粉末消臭剤を得た。
(Examples 1 , 3 to 5 , Reference Example 2 and Comparative Examples 1 to 4)
The components shown in Tables 1 and 2 below were mixed in the amounts shown in Tables 1 and 2 below to obtain powder deodorants.
（評価）
（１）消臭効果
５Ｌのスマートバッグに、得られた粉末消臭剤０．５ｇを入れ、次いで１００ｐｐｍに調整したアンモニアガス（塩基性の臭気成分）３Ｌを注入して、２４時間後の残留濃度を、検知管により測定した。同様にして、３０ｐｐｍに調整した酢酸ガス（酸性の臭気成分）３Ｌについても、２４時間後の残留濃度を、検知管により測定した。また、三角フラスコ（５００ｍＬ）に、得られた粉末消臭剤０．５ｇを入れ、次いでイソ吉草酸（酸性の臭気成分）の濃度が３８ｐｐｍとなるように調整した水溶液５μｌを注入して、２４時間後の残留濃度を、ガスクロマトグラフにより測定した。粉末消臭剤を添加しなかった場合のアンモニア、酢酸、及びイソ吉草酸の各残留濃度を１００％としたときの、アンモニア、酢酸、及びイソ吉草酸の残留濃度の割合（％）を求め、アンモニア、酢酸、及びイソ吉草酸に対する消臭効果を、以下の基準で判定した。
(evaluation)
(1) Deodorizing effect 0.5 g of the obtained powder deodorant was placed in a 5 L smart bag, and then 3 L of ammonia gas (basic odor component) adjusted to 100 ppm was poured in, and the residual concentration after 24 hours was measured by a detector tube. Similarly, the residual concentration after 24 hours for 3 L of acetic acid gas (acidic odor component) adjusted to 30 ppm was also measured by a detector tube. In addition, 0.5 g of the obtained powder deodorant was placed in an Erlenmeyer flask (500 mL), and then 5 μl of an aqueous solution adjusted to a concentration of isovaleric acid (acidic odor component) of 38 ppm was poured in, and the residual concentration after 24 hours was measured by gas chromatography. The percentages (%) of the residual concentrations of ammonia, acetic acid, and isovaleric acid were calculated based on the respective residual concentrations of ammonia, acetic acid, and isovaleric acid when the powder deodorant was not added, and the deodorizing effect on ammonia, acetic acid, and isovaleric acid was evaluated according to the following criteria.
［アンモニアに対する消臭効果の判定基準］
○○：残留濃度の割合（％）が、２０％未満
○：残留濃度の割合（％）が、２０％以上６０％未満
×：残留濃度の割合（％）が、６０％以上
[Criteria for determining deodorizing effect against ammonia]
○○: The percentage of residual concentration (%) is less than 20%. ○: The percentage of residual concentration (%) is 20% or more and less than 60%. ×: The percentage of residual concentration (%) is 60% or more.
［酢酸に対する消臭効果の判定基準］
○○：残留濃度の割合（％）が、３０％未満
○：残留濃度の割合（％）が、３０％以上６０％未満
×：残留濃度の割合（％）が、６０％以上
[Criteria for determining deodorizing effect against acetic acid]
○○: The percentage of residual concentration (%) is less than 30%. ○: The percentage of residual concentration (%) is 30% or more and less than 60%. ×: The percentage of residual concentration (%) is 60% or more.
［イソ吉草酸に対する消臭効果の判定基準］
○○：残留濃度の割合（％）が、５％未満
○：残留濃度の割合（％）が、５％以上６０％未満
×：残留濃度の割合（％）が、６０％以上
[Criteria for determining deodorizing effect against isovaleric acid]
○○: The percentage of residual concentration (%) is less than 5%. ○: The percentage of residual concentration (%) is 5% or more and less than 60%. ×: The percentage of residual concentration (%) is 60% or more.
（２）抗菌効果
界面活性剤（Ｔｗｅｅｎ８０）を０．０５重量％で含み、菌濃度１．２×１０５ＣＦＵ／ｍＬに調整した黄色ブドウ球菌の菌液を用意した。ＩＳＯ ２０７４３：２０１３菌液吸収法に準拠して、綿布０．４ｇに得られた粉末消臭剤０．１ｇを添加し、その後菌液を０．２ｍＬ滴下して、３７℃で１８時間培養した。培養後、生理食塩水２０ｍＬを綿布に加えて洗浄し、綿布から菌を洗い出した後、生菌数を求めた。粉末消臭剤を添加しなかった綿布に菌液を滴下して培養したときの生菌数を基準として、抗菌活性値を測定した。黄色ブドウ球菌に対する抗菌効果を、以下の基準で判定した。
(2) Antibacterial Effect A bacterial solution of Staphylococcus aureus containing 0.05% by weight of surfactant (Tween 80) and adjusted to a bacterial concentration of 1.2×10 5 CFU/mL was prepared. According to ISO 20743:2013 bacterial solution absorption method, 0.1 g of the obtained powder deodorant was added to 0.4 g of cotton cloth, and then 0.2 mL of the bacterial solution was dropped and cultured at 37° C. for 18 hours. After the culture, 20 mL of physiological saline was added to the cotton cloth to wash it, and the bacteria were washed out from the cotton cloth, and the viable bacterial count was determined. The antibacterial activity value was measured based on the viable bacterial count when the bacterial solution was dropped on cotton cloth to which the powder deodorant was not added and cultured. The antibacterial effect against Staphylococcus aureus was judged according to the following criteria.
［抗菌効果の判定基準］
○○：抗菌活性値が２．２以上
○：抗菌活性値が１．５以上２．２未満
×：抗菌活性値が１．５未満
[Criteria for determining antibacterial effect]
○○: Antibacterial activity value is 2.2 or more. ○: Antibacterial activity value is 1.5 or more and less than 2.2. ×: Antibacterial activity value is less than 1.5.
（３）除菌効果
界面活性剤（Ｔｗｅｅｎ８０）を０．０５重量％で含み、菌濃度１．２×１０５ＣＦＵ／ｍＬに調整した黄色ブドウ球菌の菌液を用意した。ＩＳＯ ２０７４３：２０１３菌液吸収法に準拠して、綿布０．４ｇに得られた粉末消臭剤０．１ｇを添加し、その後菌液を０．２ｍＬ滴下して、３７℃で１８時間培養した。培養後、生理食塩水２０ｍＬを綿布に加えて洗浄し、綿布を取り出した後の洗い出し液について１０倍希釈系列を作成し、希釈液各１ｍＬを混釈平板培養法により３７℃で１８時間培養し、コロニー数を数えた。肺炎桿菌についても、同様の試験を行い、コロニー数を数えた。黄色ブドウ球菌及び肺炎桿菌に対する除菌効果を、以下の基準で判定した。
(3) Bactericidal Effect A bacterial solution of Staphylococcus aureus containing 0.05% by weight of surfactant (Tween 80) and adjusted to a bacterial concentration of 1.2 x 105 CFU/mL was prepared. According to ISO 20743:2013 bacterial solution absorption method, 0.1 g of the obtained powder deodorant was added to 0.4 g of cotton cloth, and then 0.2 mL of the bacterial solution was dropped and cultured at 37°C for 18 hours. After culture, 20 mL of physiological saline was added to the cotton cloth to wash it, and a 10-fold dilution series was prepared for the washed liquid after removing the cotton cloth, and 1 mL of each diluted solution was cultured at 37°C for 18 hours by pour plate culture method, and the number of colonies was counted. A similar test was also performed for Klebsiella pneumoniae, and the number of colonies was counted. The sterilization effect against Staphylococcus aureus and Klebsiella pneumoniae was judged according to the following criteria.
［除菌効果の判定基準］
○○：コロニーが１０個以下
○：コロニーが１０個以上２００個未満
×：コロニーが２００個以上
[Criteria for judging sterilization effect]
○○: 10 or less colonies ○: 10 to less than 200 colonies ×: 200 or more colonies
結果を下記の表１～２に示す。 The results are shown in Tables 1 and 2 below.
Claims (7)
前記酸性の吸着剤が、ポリ塩化アルミニウムを含み、
前記塩基性の吸着剤が、マグネシウム・アルミニウム・酸化物を含み、
前記塩基性の吸着剤が、亜鉛イオンを含むゼオライトをさらに含み、
前記酸性の吸着剤と前記塩基性の吸着剤との合計１００重量％中、前記酸性の吸着剤の含有量が、１０重量％以上８０重量％以下である、粉末消臭剤。 The method includes the steps of:
the acidic adsorbent comprises polyaluminum chloride;
the basic adsorbent comprises magnesium aluminum oxide;
the basic adsorbent further comprises a zeolite containing zinc ions;
A powder deodorant in which the content of the acidic adsorbent is 10% by weight or more and 80% by weight or less, based on a total of 100% by weight of the acidic adsorbent and the basic adsorbent .
前記酸性の吸着剤が、ポリ塩化アルミニウムを含み、
前記塩基性の吸着剤が、酸化マグネシウムと、酸化アルミニウムとを含み、
前記塩基性の吸着剤が、亜鉛イオンを含むゼオライトをさらに含み、
前記酸性の吸着剤と前記塩基性の吸着剤との合計１００重量％中、前記酸性の吸着剤の含有量が、１０重量％以上８０重量％以下である、粉末消臭剤。 The method includes the steps of:
the acidic adsorbent comprises polyaluminum chloride;
the basic adsorbent comprises magnesium oxide and aluminum oxide;
the basic adsorbent further comprises a zeolite containing zinc ions;
A powder deodorant , wherein the content of the acidic adsorbent is 10% by weight or more and 80% by weight or less, based on a total of 100% by weight of the acidic adsorbent and the basic adsorbent .