JP7311043B2 - 合金化亜鉛めっき鋼板,電着塗装鋼板,自動車部品,電着塗装鋼板の製造方法,及び合金化亜鉛めっき鋼板の製造方法 - Google Patents
合金化亜鉛めっき鋼板,電着塗装鋼板,自動車部品,電着塗装鋼板の製造方法,及び合金化亜鉛めっき鋼板の製造方法 Download PDFInfo
- Publication number
- JP7311043B2 JP7311043B2 JP2022520152A JP2022520152A JP7311043B2 JP 7311043 B2 JP7311043 B2 JP 7311043B2 JP 2022520152 A JP2022520152 A JP 2022520152A JP 2022520152 A JP2022520152 A JP 2022520152A JP 7311043 B2 JP7311043 B2 JP 7311043B2
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- layer
- less
- based electroplating
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記Si含有冷延鋼板の少なくとも片面に形成されたFe系電気めっき層と,
前記Fe系電気めっき層上に形成された合金化亜鉛めっき層と,を有し,
グロー放電発光分析法にて測定した強度プロファイルにおいて,前記合金化亜鉛めっき層中のFe含有量をめっき層としての厚みに換算し,前記合金化亜鉛めっき層と前記Fe系電気めっき層との界面から,前記合金化亜鉛めっき層側へ前記厚み分移動した位置を起点とし,前記Fe系電気めっき層と前記Si含有冷延鋼板との界面を終点とした範囲の平均Si強度(ISi,Fe)を,Si含有冷延鋼板中の平均Si強度(ISi,bulk)で除した値(ISi,Fe)/(ISi,bulk)が0.30以上であり,
前記合金化亜鉛めっき層と前記Fe系電気めっき層との界面から前記Fe系電気めっき層側に向かって板厚方向10μm以上20μm以下の範囲におけるC濃度の平均値が0.10質量%以下であり,
前記Fe系電気めっき層と前記Si含有冷延鋼板との界面において,前記Si含有冷延鋼板に接する前記Fe系電気めっき層の結晶粒界の数が,前記Si含有冷延鋼板の観察視野における鋼板幅方向10μmあたり10以上である,合金化亜鉛めっき鋼板。
0.8×(C.W.Fe1)+(Cd)≧70・・・(1)
C:0.8%以下,
Mn:1.0%以上12.0%以下,
P:0.1%以下,
S:0.03%以下,
N:0.010%以下及び
Al:1.0%以下を含有し,残部がFe及び不可避的不純物からなる成分組成を有する,前記[1]から[6]のいずれか1項に記載の合金化亜鉛めっき鋼板。
B:0.005%以下,
Ti:0.2%以下,
Cr:1.0%以下,
Cu:1.0%以下,
Ni:1.0%以下,
Mo:1.0%以下,
Nb:0.20%以下,
V:0.5%以下,
Sb:0.020%以下,
Ta:0.1%以下,
W:0.5%以下,
Zr:0.1%以下,
Sn:0.20%以下,
Ca:0.005%以下,
Mg:0.005%以下及び
REM:0.005%以下
からなる群から選ばれる1種または2種以上を含有する,前記[7]に記載の合金化亜鉛めっき鋼板。
前記化成処理鋼板に電着塗装処理を施して,前記化成処理皮膜上に電着塗装皮膜が形成された電着塗装鋼板を得る,電着塗装工程と,
を含む,電着塗装鋼板の製造方法。
次いで,前記焼鈍前Fe系電気めっき鋼板を400℃以上650℃以下の温度域における平均昇温速度を10℃/秒以上として加熱し,加熱後の温度域にて露点-30℃超の雰囲気下で保持して,Fe系電気めっき鋼板とし,
次いで,前記Fe系電気めっき鋼板に亜鉛めっきを施して,亜鉛めっき鋼板とし,
次いで,前記亜鉛めっき鋼板に,合金化処理をさらに施して,片面あたりの付着量が0g/m2超のFe系電気めっき層と,該Fe系電気めっき層上に形成された合金化亜鉛めっき層とを有する合金化亜鉛めっき鋼板を得る,合金化亜鉛めっき鋼板の製造方法。
(C.W.Fe0)-(C.W.Zn)×[mass%Fe]/100 >0・・・(2)
ここで,C.W.Zn:前記合金化亜鉛めっき層の片面あたりの付着量の目標値(g/m2)
ただし,25.0g/m2≦C.W.Zn≦80.0g/m2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%)
0.83×{(C.W.Fe0)-(C.W.Zn)×[mass%Fe]/100}+(D.P.)≧-5・・・(3)
ここで,C.W.Zn:前記合金化亜鉛めっき層の片面あたりの付着量の目標値(g/m2)
ただし,25.0g/m2≦C.W.Zn≦80.0g/m2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%)
(C.W.Fe0)-(C.W.Zn)×[mass%Fe]/100 ≧2・・・(4)
ここで,C.W.Zn:前記合金化亜鉛めっき層の片面あたりの付着量の目標値(g/m2)
ただし,25.0g/m2≦C.W.≦80.0g/m2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%)
なお,以下の説明において,Si含有冷延鋼板の成分組成の各元素の含有量,めっき層成分組成の各元素の含有量の単位はいずれも「質量%」であり,特に断らない限り単に「%」で示す。また,本明細書中において,「~」を用いて表される数値範囲は,「~」の前後に記載される数値を下限値及び上限値として含む範囲を意味する。また,本明細書において,鋼板が「高強度」であるとは,JIS Z 2241(2011)に準拠して測定した鋼板の引張強さTSが590MPa以上であることを意味する。
Siは,加工性を大きく損なうことなく,固溶により鋼の強度を高める効果(固溶強化能)が大きいため,鋼板の高強度化を達成するのに有効な元素である。一方で,Siは溶接部における耐抵抗溶接割れ特性に悪影響を及ぼす元素でもある。Siを鋼板の高強度化を達成するために添加する場合には,0.1%以上の添加が必要である。また,Siを含有さえしていれば,後述する通りFe系電気めっき層の結晶粒界にSiの内部酸化物を形成させることができるが,Siが0.50%未満では,従来の0.24秒程度のホールドタイムによる溶接では,溶接部における耐抵抗溶接割れ特性に特に問題は生じにくい。しかしながら,自動車部品の組み立て工程におけるスポット溶接時のタクトタイムが生産コストの観点で課題となり,ホールドタイム低減による対策が取られた場合,Si量が0.50%未満でも溶接部における耐抵抗溶接割れ特性が不十分となる場合がある。一方,Siの含有量が3.0%を超えると,熱間圧延性及び冷間圧延性が大きく低下し,生産性に悪影響を及ぼしたり,鋼板自体の延性の低下を招いたりするおそれがある。よって,Siは0.1%以上3.0%以下の範囲で添加する。Si量は,好ましくは0.50%以上,より好ましくは0.7%以上,さらに好ましくは溶接部における耐抵抗溶接割れ特性への影響がより大きい0.9%以上とする。また,Si量は,好ましくは2.5%以下,より好ましくは2.0%以下,さらに好ましくは1.7%以下とする。
Cは,鋼組織としてマルテンサイトなどを形成させることで加工性を向上する。Cを含有させる場合,良好な溶接性を得るため,C量は0.8%以下とすることが好ましく,0.3%以下とすることがより好ましい。Cの下限は特に限定されないが,良好な加工性を得るためにはC量は0%超であることが好ましく,0.03%以上とすることがより好ましく,0.08%以上含有させることがさらに好ましい。
Mnは,鋼を固溶強化して高強度化するとともに,焼入性を高め,残留オーステナイト,ベイナイト,及びマルテンサイトの生成を促進する作用を有する元素である。このような効果は,Mnを1.0%以上添加することで発現する。一方,Mn量が12.0%以下であれば,コストの上昇を招かずに上記効果が得られる。よって,Mn量は1.0%以上とすることが好ましく,12.0%以下とすることが好ましい。Mn量は1.3%以上とすることがより好ましく,1.5%以上とすることがさらに好ましく,1.8%以上とすることが最も好ましい。また,Mn量は3.5%以下とすることがより好ましく,3.3%以下とすることがさらに好ましい。
Pの含有量を抑制することで,溶接性の低下を防ぐことができる。さらにPが粒界に偏析することを防いで,延性,曲げ性,及び靭性が劣化することを防ぐことができる。また,Pを多量に添加すると,フェライト変態を促進することで結晶粒径も大きくなってしまう。そのため,P量は0.1%以下とすることが好ましい。Pの下限は特に限定されず,生産技術上の制約から0%超であり得,0.001%以上であり得る。
S量は0.03%以下とすることが好ましく,0.02%以下とすることがより好ましい。S量を抑制することで,溶接性の低下を防ぐとともに,熱間時の延性の低下を防いで,熱間割れを抑制し,表面性状を著しく向上することができる。さらに,S量を抑制することで,不純物元素として粗大な硫化物を形成することにより,鋼板の延性,曲げ性,伸びフランジ性の低下を防ぐことができる。これらの問題はS量が0.03%を超えると顕著となり,Sの含有量は極力低減することが好ましい。Sの下限は特に限定されず,生産技術上の制約から0%超であり得,0.0001%以上であり得る。
Nの含有量は0.010%以下とすることが好ましい。Nの含有量を0.010%以下とすることで,NがTi,Nb,Vと高温で粗大な窒化物を形成することでTi,Nb,V添加による鋼板の高強度化の効果が損なわれることを防ぐことができる。また,Nの含有量を0.010%以下とすることで靭性の低下も防ぐことができる。さらに,Nの含有量を0.010%以下とすることで,熱間圧延中にスラブ割れ,表面疵が発生することを防ぐことができる。Nの含有量は,好ましくは0.005%以下であり,より好ましくは0.003%以下であり,さらに好ましくは0.002%以下である。Nの含有量の下限は特に限定されず,生産技術上の制約から0%超であり得,0.0005%以上であり得る。
Alは熱力学的に最も酸化しやすいため,Si及びMnに先だって酸化し,Si及びMnの鋼板最表層での酸化を抑制し,Si及びMnの鋼板内部での酸化を促進する効果がある。この効果はAl量が0.01%以上で得られる。一方,Al量が1.0%を超えるとコストアップになる。したがって,添加する場合,Al量は1.0%以下とすることが好ましい。Al量は0.1%以下とすることがより好ましい。Alの下限は特に限定されず,0%超であり得,0.001%以上であり得る。
Bは鋼の焼入れ性を向上させるのに有効な元素である。焼入れ性を向上するためには,B量は0.0003%以上とすることが好ましく,0.0005%以上とすることがより好ましい。しかし,Bを過度に添加すると成形性が低下するため,B量は0.005%以下とすることが好ましい。
Tiは鋼の析出強化に有効である。Tiの下限は特に限定されないが,強度調整の効果を得るためには,0.005%以上とすることが好ましい。しかし,Tiを過度に添加すると,硬質相が過大となり,成形性が低下するため,Tiを添加する場合,Ti量は0.2%以下とすることが好ましく,0.05%以下とすることがより好ましい。
Cr量は0.005%以上とすることが好ましい。Cr量を0.005%以上とすることで,焼き入れ性を向上し,強度と延性とのバランスを向上することができる。添加する場合,コストアップを防ぐ観点から,Cr量は1.0%以下とすることが好ましい。
Cu量は0.005%以上とすることが好ましい。Cu量を0.005%以上とすることで,残留γ相の形成を促進することができる。また,Cu量を添加する場合,コストアップを防ぐ観点から,Cu量は1.0%以下とすることが好ましい。
Ni量は0.005%以上とすることが好ましい。Ni量を0.005%以上とすることで,残留γ相の形成を促進することができる。また,Niを添加する場合,コストアップを防ぐ観点から,Ni量は1.0%以下とすることが好ましい。
Mo量は0.005%以上とすることが好ましい。Mo量を0.005%以上とすることで,強度調整の効果を得ることができる。Mo量はより好ましくは0.05%以上とする。また,Moを添加する場合,コストアップを防ぐ観点から,Mo量は1.0%以下が好ましい。
Nbは,0.005%以上含有することで強度向上の効果が得られる。また,Nbを含有する場合,コストアップを防ぐ観点から,Nb量は0.20%以下とすることが好ましい。
Vは,0.005%以上含有することで強度向上の効果が得られる。また,Vを含有する場合,コストアップを防ぐ観点から,V量は0.5%以下とすることが好ましい。
Sbは鋼板表面の酸化を抑制する観点から含有することができる。Sbは鋼板の酸化を抑制することで,めっきの濡れ性を改善する。このような効果を得るためには,Sb量は0.001%以上とすることが好ましい。一方,Sbは脱炭層の形成を抑制する。良好な耐抵抗溶接割れ特性を得るためには,Sb量は0.020%以下とすることが好ましい。Sb量はより好ましくは0.015%以下であり,より好ましくは0.012%以下である。
Taは,0.001%以上含有することで強度向上の効果が得られる。また,Taを含有する場合,コストアップを防ぐ観点から,Ta量は0.1%以下とすることが好ましい。
Wは,0.005%以上含有することで強度向上の効果が得られる。また,Wを含有する場合,コストアップを防ぐ観点から,W量は0.5%以下とすることが好ましい。
Zrは,0.0005%以上含有することで強度向上の効果が得られる。また,Zrを含有する場合,コストアップを防ぐ観点から,Zr量は0.1%以下とすることが好ましい。
Snは脱窒,脱硼等を抑制して,鋼の強度低下抑制に有効な元素である。こうした効果を得るにはそれぞれ0.002%以上とすることが好ましい。一方,良好な耐衝撃性を得るために,Sn量は0.20%以下とすることが好ましい。
Caは,0.0005%以上含有することで硫化物の形態を制御し,延性,靭性を向上させることができる。また,良好な延性を得る観点から,Ca量は0.005%以下とすることが好ましい。
Mgは,0.0005%以上含有することで硫化物の形態を制御し,延性,靭性を向上させることができる。また,Mgを含有する場合,コストアップを防ぐ観点から,Mg量は0.005%以下とすることが好ましい。
REMは,0.0005%以上含有することで硫化物の形態を制御し,延性,靭性を向上させることができる。また,REMを含有する場合,良好な靭性を得る観点から,REM量は0.005%以下とすることが好ましい。
Fe系電気めっき層:0g/m2超
合金化後の亜鉛めっき鋼板において,Fe系電気めっき層の片面あたりの付着量を0g/m2超とすることが必要である。一方,Fe系電気めっき層を形成後に,―30℃以下の低露点の雰囲気下にて焼鈍前Fe系電気めっき鋼板に焼鈍を施すと,Fe系電気めっき層の結晶粒径が粗大化する虞がある。そのため,溶融した亜鉛がFe系電気めっき層の結晶粒界を経由してSi含有冷延鋼板の結晶粒界に侵入しやすくなる。本実施形態においては,焼鈍時の雰囲気の露点を-30℃超に制御することにより,焼鈍時にSi含有冷延鋼板からFe系電気めっき層へと拡散するSiをFe系電気めっき層の結晶粒界に内部酸化物として形成させる。このSiの内部酸化物(以下,Si内部酸化物とも称する)が焼鈍工程におけるFe系電気めっき層の結晶成長を阻害し,Fe系電気めっき層の結晶を細粒化する。結晶を細粒化することによってFe系電気めっき層において結晶粒界が多数形成されて合金化後も残っている結果,抵抗溶接時に溶融した亜鉛が侵入する経路が分散され,抵抗溶接時に溶融した亜鉛がSi含有冷延鋼板の結晶粒界に到達する時間を遅延させ,溶接部における耐抵抗溶接割れ特性,特に内割れを防ぐ特性を改善することができると考えられる(亜鉛の粒界侵入抑制効果)。Fe系電気めっき層は軟質層として機能し,溶接時に鋼板表面に付与される応力を緩和することができ,抵抗溶接部の残留応力を低減することにより,溶接部における耐抵抗溶接割れ特性,特に内割れを防ぐ特性を向上させることができ得ると考えられる(応力緩和効果)。さらに,露点を-30℃超とすることで,焼鈍時に鋼板よりFe系電気めっき層に拡散するSiが該Fe系電気めっき層内部で酸化物として形成し,固溶Si量が少なくなることで溶接部における耐抵抗溶接割れ特性に優れた鋼板を得ることができる。片面あたりの付着量が0g/m2超のFe系電気めっき層により溶接部における耐抵抗溶接割れ特性が向上するメカニズムは明らかではないが,鋼板表面における固溶Si量が多い場合には溶接部で靭性が低下して溶接部における耐抵抗溶接割れ特性が劣化するものと考えられる。これに対し,一定量以上のFe系電気めっき層を鋼板表面に有し,かつある一定以上の露点で制御する場合,該Fe系電気めっき層内部に酸化物が形成して固溶Si欠乏層として働き,溶接部に固溶するSi量が減少するため,溶接部の靭性の低下が抑制されて溶接部における耐抵抗溶接割れ特性,特に内割れを防ぐ特性が改善し得ると考えられる(靭性低下抑制効果)。これらFe系電気めっき層付与による応力緩和効果,靭性低下抑制効果,及び亜鉛の粒界侵入抑制効果の耐抵抗溶接割れ特性への寄与は複雑ゆえ定量的には明らかではないが,複合的に作用して耐抵抗溶接割れ特性を改善しているものと考えられる。溶接部における耐抵抗溶接割れ特性を向上させる効果を生じさせるためには,合金化後の亜鉛めっき鋼板において,Fe系電気めっき層の片面あたりの付着量を0g/m2超とすることが必要である。Fe系電気めっき層の片面あたりの付着量の上限は特に限定されないが,コストの観点から,Fe系電気めっき層の片面あたりの付着量を60g/m2以下とすることが好ましい。Fe系電気めっき層の付着量は,好ましくは50g/m2以下,より好ましくは40g/m2以下,さらに好ましくは30g/m2以下とする。Fe系電気めっき鋼板は,好ましくはSi含有冷延鋼板の表裏両面にFe系電気めっき層を有する。Fe系電気めっき層の付着量を0g/m2超とすることで,溶接部における耐抵抗溶接割れ特性が特に良好となる。前述した亜鉛めっきの粒界侵入抑制効果,応力緩和効果,及び靭性低下抑制効果による内割れを防ぐ特性は,Fe系電気めっき層の付着量0g/m2超で発現するが,亜鉛の粒界侵入抑制効果をさらに発現させるためには,Fe系電気めっき層の片面あたりの付着量は,2.0g/m2以上とすることがより好ましい。Fe系電気めっき層の付着量が0g/m2超,かつ,結晶が細粒化することによって,上述の通り,抵抗溶接時に溶融した亜鉛が侵入する経路が分散されると考えられる。さらにFe系電気めっき層の片面あたりの付着量を2.0g/m2以上とすることで,分散した経路をさらに伸ばすことができ,ひいては,抵抗溶接時に溶融した亜鉛がSi含有冷延鋼板の結晶粒界に到達する時間をさらに遅延させることができると考えられるからである。
参考文献1:山下ら「高精度FE-EPMAによる低炭素鋼の初析フェライト変態初期における炭素の分配」,鉄と鋼,Vol.103(2017) No.11.p14-20
ただし,測定時のコンタミネーション対策の必要性は,使用する機種やコンディションによるため,必ずしも上記構成は必須ではない。すなわち,測定条件は十分な精度が得られていることが確認できていればよく,測定条件は本発明の効果に本質的に関わるものではない。
0.8×(C.W.Fe1)+(Cd)≧70・・・(1)
合金化後のFe系電気めっき層の片面あたりの付着量C.W.Fe1(g/m2)と脱炭層の厚さCd(μm)とが,式(1)を満足すれば,耐抵抗溶接割れ特性が特に良好となるためである。
次に,合金化亜鉛めっき鋼板の製造方法について説明する。
一実施形態に係る亜鉛めっき鋼板の製造方法は,Siを0.1質量%以上3.0質量%以下含有する冷延鋼板にFe系電気めっきを施して,焼鈍前Fe系電気めっき層が少なくとも片面に形成された焼鈍前Fe系電気めっき鋼板とし,
次いで,前記焼鈍前Fe系電気めっき鋼板を400℃以上650℃以下の温度域における平均昇温速度を10℃/秒以上として加熱し,加熱後の温度域にて露点-30℃超の雰囲気下で保持して,Fe系電気めっき鋼板とし,
次いで,前記Fe系電気めっき鋼板に亜鉛めっきを施して,亜鉛めっき鋼板とし,
次いで,前記亜鉛めっき鋼板に,合金化処理をさらに施して,片面あたりの付着量が0g/m2超のFe系電気めっき層と,該Fe系電気めっき層上に形成された合金化亜鉛めっき層とを有する合金化亜鉛めっき鋼板を得る,合金化亜鉛めっき鋼板の製造方法であり得る。
(C.W.Fe0)-(C.W.Zn)×[mass%Fe]/100>0・・・(2)
ここで,C.W.Zn:前記合金化亜鉛めっき層の片面あたりの付着量の目標値(g/m2)
ただし,25.0g/m2≦C.W.Zn≦80.0g/m2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%)
つまり,合金化亜鉛めっき鋼板の合金化亜鉛めっき層中に含まれるFe量の目標値(g/m2)超の量の焼鈍前Fe系電気めっき層を形成すれば,合金化後に0g/m2超のFe系電気めっき層を得ることができる。
次いで,焼鈍前Fe系電気めっき鋼板を,400℃以上650℃以下の温度域の平均昇温速度を平均10℃/秒以上として650℃以上900℃以下の温度域まで加熱する(昇温工程)。昇温工程の平均昇温速度を平均10℃/秒以上とすることで,昇温工程でのFe系電気めっき層中の結晶粒の成長を極力抑制する。昇温工程においては,後述するようにFe系電気めっき層の結晶粒界でSi内部酸化がほとんど形成しないため,昇温速度が平均10℃/秒未満であると,結晶粒の成長を抑制できないからである。昇温工程においてFe系電気めっき層中の結晶粒の成長を極力抑制した状態で,後述するように,露点:-30℃超の雰囲気下にて焼鈍を施すことで,Fe系電気めっき層の結晶を細粒化することができる。昇温工程における加熱帯には,例えば直火バーナ炉(Direct Fired Furnace:DFF),または無酸化炉(Non Oxidizing Furnace:NOF)が使用できる。ラジアントチューブ型加熱炉の場合,前段にIH(Induction Heater)などの予備加熱帯を設けてもよい。なお,上記平均昇温速度は,Fe系電気めっき鋼板の表面にて測定された温度を基準とする。
焼鈍工程は,水素濃度が1.0体積%以上30.0体積%以下の還元性雰囲気中で行う。水素は,焼鈍工程中の焼鈍前Fe系電気めっき鋼板表面のFeの酸化を抑制し,鋼板表面を活性化する役割を果たす。水素濃度が1.0体積%以上であれば,鋼板表面のFeが酸化することにより,後述するように亜鉛めっき層を設ける際にめっき密着性が劣化することを回避することができる。よって,焼鈍工程は水素濃度1.0体積%以上の還元性雰囲気にて行うことが好ましく,2.0体積%以上の還元性雰囲気にて行うことがより好ましい。焼鈍工程における水素濃度の上限は特に限定されないが,コストの観点から,水素濃度は30.0体積%以下とすることが好ましく,20.0体積%以下とすることがより好ましい。焼鈍雰囲気の水素以外の残部は,窒素とすることが好ましい。
焼鈍工程における焼鈍雰囲気の露点を-30℃超で行うことで,Fe系電気めっき層の結晶粒界にSi内部酸化物を形成させる。露点-30℃超の制御は650℃以上900℃以下の温度域にて行なうことが好ましい。これにより,昇温工程における平均昇温速度を平均10℃/秒以上としてFe系電気めっき層中の結晶粒の成長を極力抑制した状態で,Fe系電気めっき層の結晶粒界にSi内部酸化物を形成することができる。また,焼鈍工程における焼鈍雰囲気の露点を-30℃超で行うことで,脱炭反応が促進され,表層のC濃度を低減させることができる。Fe系電気めっき層の結晶粒界に存在するSi内部酸化物は,ピン止め効果により焼鈍工程におけるFe系電気めっき層の結晶粒の成長を抑制する。Si内部酸化物は冷延鋼板からのSiの拡散によるものであるため,Fe系電気めっき層の冷延鋼板側においてSi内部酸化物によるピン止め効果が特に強く発揮される。その結果,Fe系電気めっき層のSi含有冷延鋼板との界面側の結晶粒径が特に小さくなり,Si含有冷延鋼板との界面に接するFe系電気めっき層の粒界の数が増加すると考えられる。なお,ここでのピン止め効果とは,Zener drag機構を指す。組織中に第二相粒子を分散し,粒界が第二相粒子と交わっている場合,粒界が第二相粒子から離脱するためにはエネルギーを必要とする。すなわち,粒子と粒界との間には粒界移動を妨げるピン止め力が働くことになり,結晶粒の成長が抑制される。第二相粒子としては,炭化物及び硫化物がよく知られている。Si内部酸化物がこのピン止め効果を発現するかどうかは明らかになっていないが,実験的事実から考え,ピン止め効果を発現しているものと推定される。焼鈍雰囲気の露点は,好ましくは-20℃以上,より好ましくは-5℃以上である。焼鈍雰囲気の露点を-5℃以上とすることで,溶接部における耐抵抗溶接割れ特性,特に内割れを防ぐ特性が良好となる。焼鈍雰囲気の露点の上限は特に定めないが,Fe系電気めっき層表面の酸化を好適に防ぎ,後述するように亜鉛めっき層を設ける際のめっき密着性を良好にするため,焼鈍雰囲気の露点は30℃以下とすることが好ましい。
焼鈍工程において,650℃以上900℃以下の温度域での保持時間を,30秒以上600秒以下とすることが好ましい。当該温度域での保持時間を30秒以上とすることで,焼鈍前Fe系電気めっき層表面に形成したFeの自然酸化膜を好適に除去し,後述するように亜鉛めっき層を設ける際にめっき密着性を向上することができる。よって,当該温度域での保持時間は30秒以上とすることが好ましい。当該温度域での保持時間の上限は特に定めないが,生産性の観点から,当該温度域での保持時間は600秒以下とすることが好ましい。
焼鈍前Fe系電気めっき鋼板の最高到達温度は特に限定されないが,650℃以上900℃以下とすることが好ましい。焼鈍前Fe系電気めっき鋼板の最高到達温度を650℃以上とすることで,鋼板組織の再結晶が好適に進み,所望の強度を得ることができる。また,焼鈍前Fe系電気めっき層表面に形成したFeの自然酸化膜を好適に還元させ,後述するようにFe系電気めっき鋼板表面に亜鉛めっき層を設ける際のめっき密着性を向上することができる。また,Fe系電気めっき鋼板の最高到達温度が900℃以下であれば,鋼中のSi及びMnの拡散速度が増加しすぎることを防ぎ,鋼板表面へのSi及びMnの拡散を防ぐことができるため,後述するようにFe系電気めっき鋼板表面に亜鉛めっき層を設ける際のめっき密着性を向上することができる。また,最高到達温度が900℃以下であれば,熱処理炉の炉体ダメージを防ぐことができ,コストダウンすることもできる。よって,焼鈍前Fe系電気めっき鋼板の最高到達温度は900℃以下とすることが好ましい。なお,上記最高到達温度は,焼鈍前Fe系電気めっき鋼板の表面にて測定された温度を基準とする。
0.83×{(C.W.Fe0)-(C.W.Zn)×[mass%Fe]/100}+(D.P.)≧-5・・・(3)
ここで,C.W.Zn:前記合金化亜鉛めっき層の片面あたりの付着量の目標値(g/m2)
ただし,25.0g/m2≦C.W.Zn≦80.0g/m2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%)
(C.W.Fe0)-(C.W.Zn)×[mass%Fe]/100≧2・・・(4)
ただし,25.0g/m2≦C.W.Zn≦80.0g/m2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%)
つまり,合金化亜鉛めっき鋼板の合金化亜鉛めっき層中に含まれるFe量の目標値(g/m2)+2g/m2以上の量の焼鈍前Fe系電気めっき層を形成すれば,合金化後に2g/m2以上のFe系電気めっき層を得ることができる。
前記焼鈍工程後に,Fe系電気めっき鋼板に亜鉛めっきを施す。焼鈍工程後にFe系電気めっき鋼板を冷却し,溶融亜鉛めっき浴中に浸漬して,鋼板表面に亜鉛めっきを施せばよい。亜鉛めっきは例えば溶融亜鉛めっきであり得る。溶融亜鉛めっき浴はAl,Zn及び不可避的不純物からなる。溶融亜鉛めっき浴の成分は特に規定しないが,一般的に浴中Al濃度が0.05質量%以上0.250質量%以下である。浴中Al濃度を0.05質量%以上とすれば,ボトムドロスの発生を防ぎ,ドロスが鋼板に付着して欠陥になることを防ぐことができる。また,浴中Al濃度を0.250質量%以下とすることで,トップドロスの増加を防ぎ,ドロスが鋼板に付着して欠陥になることを防ぐとともに,コストダウンにもつながる。溶融亜鉛めっき処理のその他の条件は制限されるものではないが,例えば,溶融亜鉛めっき浴の浴温度は通常の440~500℃の範囲で,板温440~550℃で鋼板を溶融亜鉛めっき浴中に浸漬させて行う。
まず,合金化亜鉛めっき鋼板から20×25mmサイズのサンプルを2か所採取する。それぞれの重量を測定した後,JIS H 0401(2013)またはISO17925(2004)に規定された試験液を用いてFe系電気めっき層を有する片側の合金化亜鉛めっき層の剥離を行い,再び重量測定を行う。めっき剥離前の重量からめっき剥離後の重量を差し引き,めっき剥離部分の表面積で除することにより,めっき付着量を算出することができる。ここでは,2か所の平均値を合金化亜鉛めっき層の片面あたりのめっき付着量とする。
また,本実施形態によれば,上述した合金化亜鉛めっき鋼板上に,前記合金化亜鉛めっき層上に形成された化成処理皮膜と,該化成皮膜上に形成された電着塗装皮膜とをさらに有する電着塗装鋼板を提供することもできる。本実施形態に係る合金化亜鉛めっき鋼板は,溶接部における耐抵抗溶接割れ特性に優れるため,該合金化亜鉛めっき鋼板を用いて形成した電着塗装鋼板は,自動車部品への適用に特に好適である。化成処理皮膜,及び電着塗装皮膜の種類は特に限定されず,公知の化成処理皮膜,及び電着塗装皮膜とすることができる。化成処理皮膜としては,リン酸亜鉛皮膜,ジルコニウム皮膜等が使用できる。電着塗装皮膜としては,自動車用の電着塗装皮膜であれば特に限定されない。電着塗装皮膜の厚みは,用途により異なるが,乾燥状態の塗膜で10μm以上30μm以下程度とすることが好ましい。また,本実施形態によれば,電着塗装を施すための電着塗装用合金化亜鉛めっき鋼板を提供することもできる。
次いで,上述した電着塗装鋼板の製造方法について説明する。上述した電着塗装鋼板は,合金化亜鉛めっき鋼板に化成処理を施して,前記合金化亜鉛めっき層上に化成処理皮膜が形成された化成処理鋼板を得る,化成処理工程と,前記化成処理鋼板に電着塗装処理を施して,前記化成処理皮膜上に電着塗装皮膜が形成された電着塗装鋼板を得る,電着塗装工程と,を含む,電着塗装鋼板の製造方法によって製造することができる。化成処理,及び電着塗装処理は,公知の方法によることができる。なお,化成処理を施す前の処理として,合金化亜鉛めっき鋼板表面を清浄化するための脱脂処理,水洗及び必要に応じて表面調整処理を施すことができる。これらの前処理に引き続いて化成処理を実施する。脱脂処理及び水洗の方法は特に限定されず,通常の方法を用いることができる。表面調整処理においては,Tiコロイド,あるいはリン酸亜鉛コロイドを有する表面調整剤等を使用できる。これらの表面調整剤を施すに際して,特別な工程を設ける必要はなく,常法に従い実施すればよい。例えば,所望の表面調整剤を所定の脱イオン水に溶解させ,十分攪拌したのち,既定の温度(通常は常温,25~30℃)の処理液とし,該処理液中に鋼板を所定時間(20~30秒)浸漬させる。引き続き乾燥させることなく,次工程の化成処理を行う。化成処理においても,常法に従い実施すればよい。例えば,所望の化成処理剤を所定の脱イオン水に溶解させ,十分攪拌したのち,所定の温度(通常35~45℃)の処理液とし,該処理液中に鋼板を所定時間(60~120秒)浸漬させる。化成処理剤としては,例えば鋼用のリン酸亜鉛処理剤,鋼・アルミニウム併用型のリン酸亜鉛処理剤,及びジルコニウム処理剤等を使用できる。引き続き,次工程の電着塗装を行う。電着塗装も,常法に従い実施すればよい。必要に応じて水洗処理等の前処理を施したのち,十分攪拌された電着塗料に鋼板を浸漬し,電着処理によって所望の厚みの電着塗装を得る。電着塗装としては,カチオン型の電着塗装の他,アニオン型電着塗装を使用できる。さらに,用途に応じて電着塗装後に上塗り塗装などを施してもよい。
また,本実施形態によれば,上述した電着塗装鋼板を少なくとも一部に用いてなる自動車部品を提供することができる。本実施形態に係る合金化亜鉛めっき鋼板は,溶接部における耐抵抗溶接割れ特性に優れるため,該合金化亜鉛めっき鋼板を用いた電着塗装鋼板は,自動車部品への適用に特に好適である。電着塗装鋼板を用いてなる自動車部品は,本実施形態に係る電着塗装鋼板以外の鋼板を,素材として含んでいてもよい。本実施形態に係る電着塗装鋼板は溶接部における耐抵抗溶接割れ特性に優れるため,該合金化亜鉛めっき鋼板を用いてなる自動車部品の溶接部におけるLME割れが好適に防がれる。電着塗装鋼板を少なくとも一部に用いてなる自動車部品の種類は特に限定されないが,例えば,サイドシル部品,ピラー部品,及び自動車車体等であり得る。
〔電解条件〕
浴温:50℃
pH:2.0
電流密度:45A/dm2
Fe系電気めっき浴:Fe2+イオンを1.5mol/L含む
電極(陽極):酸化イリジウム電極
上記のように作製した合金化溶融亜鉛めっき鋼板から,上述した方法に従って,Fe系電気めっき層の片面あたりの付着量,合金化亜鉛めっき層の片面あたりの付着量,合金化亜鉛めっき層中のFe濃度,ISi,Fe/ISi,bulk,ならびにFe系電気めっき層とSi含有冷延鋼板との界面において,Si含有冷延鋼板に接するFe系電気めっき層の結晶粒界の数を求めた。
合金化溶融亜鉛めっき鋼板について,板組相手が,0.18秒のホールドタイムにおいて耐抵抗溶接割れ特性が課題とならないSi量が0.50%以下の引張強さが980MPa級,及び片面あたりの付着量が50g/m2の試験用合金化溶融亜鉛めっき鋼板(板厚1.6mm)である場合の溶接部における耐抵抗溶接割れ特性を評価した。図11を用いて,溶接部における耐抵抗溶接割れ特性の評価方法について説明する。
◎ : ホールドタイム0.18秒で0.1mm以上の長さのき裂が認められない
○ : ホールドタイム0.18秒で0.1mm以上の長さのき裂が認められるが,ホールドタイム0.24秒で0.1mm以上の長さのき裂が認められない
× : ホールドタイム0.24秒で0.1mm以上の長さのき裂が認められる
〔電解条件〕
浴温:50℃
pH:2.0
電流密度:45A/dm2
Fe系電気めっき浴:Fe2+イオンを1.5mol/L含む
電極(陽極):酸化イリジウム電極
上記のように作製した合金化溶融亜鉛めっき鋼板から,上述した方法に従って,Fe系電気めっき層の片面あたりの付着量,合金化亜鉛めっき層の片面あたりの付着量,合金化亜鉛めっき層中のFe濃度,ISi,Fe/ISi,bulk,ならびにFe系電気めっき層とSi含有冷延鋼板との界面において,Si含有冷延鋼板に接するFe系電気めっき層の結晶粒界の数を求めた。
合金化溶融亜鉛めっき鋼板について,板組相手が,0.14秒のホールドタイムにおいて耐抵抗溶接割れ特性が課題とならないSi量が0.1%未満の引張強さが980MPa級,及び片面あたりの付着量が50g/m2の試験用合金化溶融亜鉛めっき鋼板(板厚1.6mm)である場合の溶接部における耐抵抗溶接割れ特性を評価した。図11を用いて,溶接部における耐抵抗溶接割れ特性の評価方法について説明する。
◎ : ホールドタイム0.14秒で0.1mm以上の長さのき裂が認められない
○ : ホールドタイム0.14秒で0.1mm以上の長さのき裂が認められるが,ホールドタイム0.16秒で0.1mm以上の長さのき裂が認められない
× : ホールドタイム0.16秒で0.1mm以上の長さのき裂が認められる
2 Si含有冷延鋼板
3 Fe系電気めっき層
4 合金化亜鉛めっき層
5 試験用合金化溶融亜鉛めっき鋼板
6 試験片
7 スペーサー
8 固定台
9 電極
10 ナゲット
11 き裂
Claims (15)
- Siを0.1質量%以上3.0質量%以下含有するSi含有冷延鋼板と,
前記Si含有冷延鋼板の少なくとも片面に形成されたFe系電気めっき層と,
前記Fe系電気めっき層上に形成された合金化亜鉛めっき層と,を有し,
グロー放電発光分析法にて測定した強度プロファイルにおいて,前記合金化亜鉛めっき層中のFe含有量をめっき層としての厚みに換算し,前記合金化亜鉛めっき層と前記Fe系電気めっき層との界面から,前記合金化亜鉛めっき層側へ前記厚み分移動した位置を起点とし,前記Fe系電気めっき層と前記Si含有冷延鋼板との界面を終点とした範囲の平均Si強度(ISi,Fe)を,Fe系電気めっき層とSi含有冷延鋼板との界面からSi含有冷延鋼板側に向かって板厚方向に20μm±0.5μmの範囲の平均Si強度(ISi,bulk)で除した値(ISi,Fe)/(ISi,bulk)が0.30以上であり,
前記合金化亜鉛めっき層と前記Fe系電気めっき層との界面から前記Fe系電気めっき層側に向かって板厚方向10μm以上20μm以下の範囲におけるC濃度の平均値が0.10質量%以下であり,
前記Fe系電気めっき層と前記Si含有冷延鋼板との界面において,前記Si含有冷延鋼板に接する前記Fe系電気めっき層の結晶粒界の数が,前記Si含有冷延鋼板の観察視野における鋼板幅方向10μmあたり10以上であって,
かつ,前記合金化亜鉛めっき層と前記Fe系電気めっき層との界面を起点とし,前記Fe系電気めっき層側に向かって脱炭層を有し,前記Fe系電気めっき層の片面あたりの付着量C.W. Fe1 (g/m 2 )と,前記脱炭層の厚さC d (μm)とが,下式(1)を満足する,合金化亜鉛めっき鋼板。
0.8×(C.W. Fe1 )+(C d )≧70・・・(1) - 前記Si含有冷延鋼板は,Siを0.50質量%以上3.0質量%以下含有する,請求項1に記載の合金化亜鉛めっき鋼板。
- 前記脱炭層の厚さが30μm以上である,請求項1または2に記載の合金化亜鉛めっき鋼板。
- 前記Fe系電気めっき層の片面あたりの付着量C.W.Fe1(g/m2)が2g/m2以上である,請求項1から3のいずれか1項に記載の合金化亜鉛めっき鋼板。
- 前記Si含有冷延鋼板は,前記Siに加えて,質量%で,
C:0.8%以下,
Mn:1.0%以上12.0%以下,
P:0.1%以下,
S:0.03%以下,
N:0.010%以下及び
Al:1.0%以下を含有し,残部がFe及び不可避的不純物からなる成分組成を有する,請求項1から4のいずれか1項に記載の合金化亜鉛めっき鋼板。 - 前記成分組成がさらに,質量%で,
B:0.005%以下,
Ti:0.2%以下,
Cr:1.0%以下,
Cu:1.0%以下,
Ni:1.0%以下,
Mo:1.0%以下,
Nb:0.20%以下,
V:0.5%以下,
Sb:0.020%以下,
Ta:0.1%以下,
W:0.5%以下,
Zr:0.1%以下,
Sn:0.20%以下,
Ca:0.005%以下,
Mg:0.005%以下及び
REM:0.005%以下
からなる群から選ばれる1種または2種以上を含有する,請求項5に記載の合金化亜鉛めっき鋼板。 - 前記Fe系電気めっき層は,B,C,P,N,O,Ni,Mn,Mo,Zn,W,Pb,Sn,Cr,V及びCoからなる群から選ばれる1または2以上の元素を合計で10質量%以下含み,残部はFe及び不可避的不純物からなる成分組成を有する,請求項1から6のいずれか1項に記載の合金化亜鉛めっき鋼板。
- 請求項1から7のいずれか1項に記載の合金化亜鉛めっき鋼板上に,化成処理皮膜と,該化成処理皮膜上に形成された電着塗装皮膜とをさらに有する,電着塗装鋼板。
- 請求項8に記載の電着塗装鋼板を少なくとも一部に用いてなる,自動車部品。
- 請求項1から7のいずれか1項に記載の合金化亜鉛めっき鋼板に化成処理を施して,化成処理皮膜が形成された化成処理鋼板を得る,化成処理工程と,
前記化成処理鋼板に電着塗装処理を施して,前記化成処理皮膜上に電着塗装皮膜が形成された電着塗装鋼板を得る,電着塗装工程と,
を含む,電着塗装鋼板の製造方法。 - Siを0.1質量%以上3.0質量%以下含有する冷延鋼板にFe系電気めっきを施して,焼鈍前Fe系電気めっき層が少なくとも片面に形成された焼鈍前Fe系電気めっき鋼板とし,
次いで,前記焼鈍前Fe系電気めっき鋼板を400℃以上650℃以下の温度域における平均昇温速度を10℃/秒以上として加熱し,加熱後の温度域にて露点-30℃超の雰囲気下で,かつ,前記焼鈍前Fe系電気めっき層の片面あたりの付着量C.W. Fe0 (g/m 2 )と前記露点(D.P.)とが下式(3)を満足して保持して,Fe系電気めっき鋼板とし,
次いで,前記Fe系電気めっき鋼板に亜鉛めっきを施して,亜鉛めっき鋼板とし,
次いで,前記亜鉛めっき鋼板に,合金化処理をさらに施して,片面あたりの付着量が0g/m2超のFe系電気めっき層と,該Fe系電気めっき層上に形成された合金化亜鉛めっき層とを有する合金化亜鉛めっき鋼板を得る,合金化亜鉛めっき鋼板の製造方法。
0.83×{(C.W. Fe0 )-(C.W. Zn )×[mass%Fe]/100}+(D.P.)≧-5・・・(3)
ここで,C.W. Zn :前記合金化亜鉛めっき層の片面あたりの付着量の目標値(g/m 2 )
ただし,25.0g/m 2 ≦C.W. Zn ≦80.0g/m 2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%) - 前記冷延鋼板は,Siを0.50質量%以上3.0質量%以下含有する,請求項11に記載の合金化亜鉛めっき鋼板の製造方法。
- 前記焼鈍前Fe系電気めっき層の片面あたりの付着量C.W.Fe0(g/m2)が下式(2)を満足する,請求項11または12に記載の合金化亜鉛めっき鋼板の製造方法。
(C.W.Fe0)-(C.W.Zn)×[mass%Fe]/100 >0・・・(2)
ここで,C.W.Zn:前記合金化亜鉛めっき層の片面あたりの付着量の目標値(g/m2)
ただし,25.0g/m2≦C.W.Zn≦80.0g/m2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%) - 前記焼鈍前Fe系電気めっき層の片面あたりの付着量C.W.Fe0(g/m2)が下式(4)を満足する,請求項11から13のいずれか1項に記載の合金化亜鉛めっき鋼板の製造方法。
(C.W.Fe0)-(C.W.Zn)×[mass%Fe]/100 ≧2・・・(4)
ここで,C.W.Zn:前記合金化亜鉛めっき層の片面あたりの付着量の目標値(g/m2)
ただし,25.0g/m2≦C.W. Zn ≦80.0g/m2
[mass%Fe]:前記合金化亜鉛めっき層中のFe含有量の目標値(質量%) - B,C,P,N,O,Ni,Mn,Mo,Zn,W,Pb,Sn,Cr,V及びCoからなる群から選ばれる1または2以上の元素を,前記焼鈍前Fe系電気めっき層中でこれらの元素の合計含有量が10質量%以下となるように含有するFe系電気めっき浴を用いて,前記Fe系電気めっきを施す,請求項11から14のいずれか1項に記載の合金化亜鉛めっき鋼板の製造方法。