JP7211445B2 - High frequency component and its manufacturing method - Google Patents

High frequency component and its manufacturing method Download PDF

Info

Publication number
JP7211445B2
JP7211445B2 JP2021047843A JP2021047843A JP7211445B2 JP 7211445 B2 JP7211445 B2 JP 7211445B2 JP 2021047843 A JP2021047843 A JP 2021047843A JP 2021047843 A JP2021047843 A JP 2021047843A JP 7211445 B2 JP7211445 B2 JP 7211445B2
Authority
JP
Japan
Prior art keywords
conductive layer
insulating layer
layer
frequency component
substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2021047843A
Other languages
Japanese (ja)
Other versions
JP2021101483A (en
Inventor
佑美 吉井
悟 倉持
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Publication of JP2021101483A publication Critical patent/JP2021101483A/en
Priority to JP2023002629A priority Critical patent/JP2023040216A/en
Application granted granted Critical
Publication of JP7211445B2 publication Critical patent/JP7211445B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本開示の実施形態は、キャパシタを備える高周波部品及びその製造方法に関する。 TECHNICAL FIELD Embodiments of the present disclosure relate to a high frequency component including a capacitor and a manufacturing method thereof.

近年、半導体メモリに代表される集積回路が高速化、高集積化するにつれて、集積回路の周辺に使用される受動部品についても同様に小型化、広帯域化が求められている。例えば、コンデンサが、電源電圧の変動を抑えるためのバイパスコンデンサとして使用される場合、電源電圧に重畳する高周波のノイズを除去するため、コンデンサが広帯域であることが求められる。例えば特許文献１は、第１導電層と、第１導電層上に設けられた高誘電率薄膜と、高誘電率薄膜上に設けられた第２導電層と、を備える薄膜コンデンサを提案している。薄膜コンデンサにおいては、高い誘電率を有する高誘電率薄膜を用いることにより、小型で大容量のコンデンサを実現することができる。 2. Description of the Related Art In recent years, as integrated circuits represented by semiconductor memories have become faster and more highly integrated, passive components used in the periphery of integrated circuits have also been required to be smaller and broader in bandwidth. For example, when a capacitor is used as a bypass capacitor for suppressing fluctuations in power supply voltage, the capacitor is required to have a wide band in order to remove high-frequency noise superimposed on the power supply voltage. For example, Patent Document 1 proposes a thin film capacitor comprising a first conductive layer, a high dielectric thin film provided on the first conductive layer, and a second conductive layer provided on the high dielectric thin film. there is In a thin film capacitor, a small-sized capacitor with a large capacity can be realized by using a high dielectric constant thin film having a high dielectric constant.

特開平６－８９８３１号公報JP-A-6-89831

従来の薄膜コンデンサは、半導体プロセスの場合と同様に、主にシリコンの上に形成されていた。シリコンは、一定の導電性を有しており、このため、従来の薄膜コンデンサの耐電圧を高めることは容易ではない。 Conventional thin-film capacitors were mainly formed on silicon, as in the case of semiconductor processes. Silicon has a certain conductivity, so it is not easy to increase the withstand voltage of conventional thin film capacitors.

本開示の実施形態は、このような点を考慮してなされたものであり、改善された耐電圧特性を有する高周波部品を提供することを目的とする。 Embodiments of the present disclosure have been made in consideration of such points, and an object thereof is to provide a high frequency component having improved withstand voltage characteristics.

本開示の一実施形態は、第１側に位置する第１面及び前記第１側とは反対の第２側に位置する第２面を含み、ガラスを有する基板と、前記基板の前記第１面に位置するキャパシタと、を備え、前記キャパシタは、前記基板の前記第１面に位置する第１面第１導電層と、前記第１面第１導電層上に位置する第１面第１絶縁層と、前記第１面第１絶縁層上に位置する第１面第２導電層と、を有し、前記第１面第１絶縁層は、６ＭＶ／ｃｍ以上の絶縁破壊電界を有する無機材料を含む、高周波部品である。 An embodiment of the present disclosure includes a substrate comprising glass, comprising a first surface located on a first side and a second surface located on a second side opposite said first side; a first surface first conductive layer located on the first surface of the substrate; and a first surface first conductive layer located on the first surface first conductive layer. and a first surface second conductive layer positioned on the first surface first insulating layer, the first surface first insulating layer being an inorganic material having a dielectric breakdown electric field of 6 MV/cm or more. It is a high frequency component, including materials.

本開示の一実施形態による高周波部品において、前記第１面第１絶縁層の前記無機材料の漏れ電流は、好ましくは１×１０-１２Ａ以下である。 In the high-frequency component according to one embodiment of the present disclosure, the leakage current of the inorganic material of the first insulating layer on the first surface is preferably 1×10 −12 A or less.

本開示の一実施形態による高周波部品において、前記第１面第１絶縁層の前記無機材料は、珪素窒化物を含んでいてもよい。 In the high frequency component according to one embodiment of the present disclosure, the inorganic material of the first surface first insulating layer may contain silicon nitride.

本開示の一実施形態による高周波部品において、前記第１面第１絶縁層の厚みは、５０ｎｍ以上且つ４００ｎｍ以下であってもよい。 In the high-frequency component according to one embodiment of the present disclosure, the first surface first insulating layer may have a thickness of 50 nm or more and 400 nm or less.

本開示の一実施形態による高周波部品において、前記第１面第１導電層の厚みは、５μｍ以上且つ２０μｍ以下であってもよい。 In the high-frequency component according to one embodiment of the present disclosure, the first surface first conductive layer may have a thickness of 5 μm or more and 20 μm or less.

本開示の一実施形態による高周波部品は、前記第１面第１絶縁層上に位置し、０．００３以下の誘電正接を有する有機材料を含む第１面第２絶縁層を更に備えていてもよい。 A high frequency component according to an embodiment of the present disclosure may further include a first surface second insulating layer located on the first surface first insulating layer and containing an organic material having a dielectric loss tangent of 0.003 or less. good.

本開示の一実施形態による高周波部品において、前記基板には貫通孔が設けられており、前記高周波部品は、前記キャパシタに電気的に接続されたインダクタを更に備え、前記インダクタは、前記第１面第１導電層と、前記第１面第１導電層に接続されるとともに前記貫通孔の側壁に沿って広がる貫通電極と、前記貫通電極に接続されるとともに前記基板の前記第２面に位置する第２面第１導電層と、を有していてもよい。 In the high-frequency component according to one embodiment of the present disclosure, the substrate is provided with a through hole, the high-frequency component further includes an inductor electrically connected to the capacitor, the inductor being connected to the first surface. a first conductive layer; a through electrode connected to the first surface first conductive layer and extending along a sidewall of the through hole; and a through electrode connected to the through electrode and located on the second surface of the substrate. and a second surface first conductive layer.

本開示の一実施形態による高周波部品は、前記貫通電極よりも前記貫通孔の中心側に位置し、０．００３以下の誘電正接を有する有機材料を含む有機層を更に備えていてもよい。 The high-frequency component according to an embodiment of the present disclosure may further include an organic layer located closer to the center of the through-hole than the through-electrode and containing an organic material having a dielectric loss tangent of 0.003 or less.

本開示の一実施形態による高周波部品において、前記第１面第１絶縁層は、前記第１面第１導電層の上面に位置する第１部分と、前記第１部分に接続され、前記第１面第１導電層の側面に位置する第２部分と、を含んでいてもよい。 In the high-frequency component according to one embodiment of the present disclosure, the first surface first insulating layer includes a first portion located on an upper surface of the first surface first conductive layer, a first portion connected to the first portion, and the first and a second portion located on a side of the surface first conductive layer.

本開示の一実施形態による高周波部品において、前記第２部分の厚みは、前記第１部分の厚みよりも小さく、且つ前記第１部分の厚みの１／４以上であってもよい。 In the high-frequency component according to one embodiment of the present disclosure, the thickness of the second portion may be smaller than the thickness of the first portion and 1/4 or more of the thickness of the first portion.

本開示の一実施形態による高周波部品において、前記第１面第１導電層の側面は、前記基板側に位置する下側湾曲部を含み、前記下側湾曲部は、少なくとも部分的に前記第１面第１絶縁層から露出していてもよい。 In the high-frequency component according to one embodiment of the present disclosure, a side surface of the first surface first conductive layer includes a lower curved portion located on the substrate side, the lower curved portion at least partially It may be exposed from the surface first insulating layer.

本開示の一実施形態は、第１側に位置する第１面及び前記第１側とは反対の第２側に位置する第２面を含み、ガラスを有する基板を準備する工程と、前記基板の前記第１面に第１面第１導電層を形成する工程と、前記第１面第１導電層上に、６ＭＶ／ｃｍ以上の絶縁破壊電界を有する無機材料を含む第１面第１絶縁層を形成する工程と、前記第１面第１絶縁層上に第１面第２導電層を形成する工程と、を備え、前記第１面第１導電層、前記第１面第１絶縁層及び前記第１面第２導電層がキャパシタを構成する、高周波部品の製造方法である。 An embodiment of the present disclosure comprises the steps of providing a substrate comprising glass, comprising a first surface located on a first side and a second surface located on a second side opposite said first side, said substrate comprising: forming a first surface first conductive layer on the first surface of the first surface first insulation containing an inorganic material having a breakdown electric field of 6 MV/cm or more on the first surface first conductive layer and forming a first surface second conductive layer on the first surface first insulating layer, wherein the first surface first conductive layer and the first surface first insulating layer are formed. and a method of manufacturing a high frequency component, wherein the first surface second conductive layer constitutes a capacitor.

本開示の一実施形態による高周波部品の製造方法において、前記第１面第１絶縁層の前記無機材料の漏れ電流は、好ましくは１×１０－１２Ａ以下である。 In the method of manufacturing a high-frequency component according to an embodiment of the present disclosure, the leakage current of the inorganic material of the first insulating layer on the first surface is preferably 1×10 −12 A or less.

本開示の一実施形態による高周波部品の製造方法において、前記第１面第１絶縁層の前記無機材料は、珪素窒化物を含んでいてもよい。 In the method of manufacturing a high frequency component according to an embodiment of the present disclosure, the inorganic material of the first surface first insulating layer may contain silicon nitride.

本開示の一実施形態による高周波部品の製造方法において、前記第１面第１絶縁層の厚みは、５０ｎｍ以上且つ４００ｎｍ以下であってもよい。 In the method for manufacturing a high-frequency component according to an embodiment of the present disclosure, the thickness of the first insulating layer on the first surface may be 50 nm or more and 400 nm or less.

本開示の一実施形態による高周波部品の製造方法において、前記第１面第１導電層の厚みは、５μｍ以上且つ２０μｍ以下であってもよい。 In the method of manufacturing a high-frequency component according to an embodiment of the present disclosure, the thickness of the first conductive layer on the first surface may be 5 μm or more and 20 μm or less.

本開示の一実施形態による高周波部品の製造方法は、前記第１面第１絶縁層を形成する工程に先行して前記第１面第１導電層の表面をＮＨ３プラズマに晒す表面処理工程を更に備えていてもよい。 A method for manufacturing a high-frequency component according to an embodiment of the present disclosure includes a surface treatment step of exposing the surface of the first surface first conductive layer to NH3 plasma prior to the step of forming the first surface first insulating layer. It may be further provided.

本開示の一実施形態による高周波部品の製造方法は、前記第１面第１絶縁層上に、０．００３以下の誘電正接を有する有機材料を含む第１面第２絶縁層を形成する工程を更に備えていてもよい。 A method for manufacturing a high-frequency component according to an embodiment of the present disclosure includes forming a first surface second insulating layer containing an organic material having a dielectric loss tangent of 0.003 or less on the first surface first insulating layer. It may be further provided.

本開示の一実施形態による高周波部品の製造方法において、前記基板には貫通孔が設けられており、前記高周波部品の製造方法は、前記第１面第１導電層に接続されるとともに前記貫通孔の側壁に沿って広がる貫通電極を形成する工程と、前記貫通電極に接続されるとともに前記基板の前記第２面に位置する第２面第１導電層を形成する工程と、を更に備えていてもよい。この場合、前記第１面第１導電層、前記貫通電極及び前記第２面第１導電層がインダクタを構成する。 In the method of manufacturing a high-frequency component according to an embodiment of the present disclosure, the substrate is provided with a through hole, and the method of manufacturing the high-frequency component is connected to the first surface first conductive layer and the through hole and forming a second surface first conductive layer connected to the through electrode and located on the second surface of the substrate. good too. In this case, the first surface first conductive layer, the through electrode, and the second surface first conductive layer form an inductor.

本開示の一実施形態による高周波部品の製造方法は、前記貫通電極よりも前記貫通孔の中心側に位置し、０．００３以下の誘電正接を有する有機材料を含む有機層を形成する工程を更に備えていてもよい。 The method for manufacturing a high-frequency component according to an embodiment of the present disclosure further includes forming an organic layer located closer to the center of the through hole than the through electrode and containing an organic material having a dielectric loss tangent of 0.003 or less. may be provided.

本開示の実施形態によれば、改善された耐電圧特性を有する高周波部品を提供することができる。 According to embodiments of the present disclosure, it is possible to provide a high frequency component having improved withstand voltage characteristics.

一実施形態に係る高周波部品を示す断面図である。1 is a cross-sectional view showing a high frequency component according to one embodiment; FIG. 図１の高周波部品を拡大して示す断面図である。2 is an enlarged cross-sectional view showing the high-frequency component of FIG. 1; FIG. 高周波部品を示す平面図である。It is a top view which shows a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of a high frequency component. 一変形例に係る高周波部品を示す断面図である。It is a cross-sectional view showing a high-frequency component according to a modified example. 第２変形例に係る高周波部品のキャパシタを拡大して示す平面図である。FIG. 11 is an enlarged plan view showing a capacitor of a high-frequency component according to a second modified example; 図１７のキャパシタを線Ｂ－Ｂに沿って切断した場合の断面図である。FIG. 18 is a cross-sectional view of the capacitor of FIG. 17 taken along line BB; 第２変形例に係る高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of the high frequency component based on a 2nd modification. 第２変形例に係る高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of the high frequency component based on a 2nd modification. 第２変形例に係る高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of the high frequency component based on a 2nd modification. 第２変形例に係る高周波部品の製造工程を示す図である。It is a figure which shows the manufacturing process of the high frequency component based on a 2nd modification. 第２変形例に係る高周波部品のキャパシタの一応用例を示す断面図である。FIG. 11 is a cross-sectional view showing an application example of the capacitor of the high-frequency component according to the second modified example;

以下、本開示の実施形態に係る高周波部品の構成及びその製造方法について、図面を参照しながら詳細に説明する。なお、以下に示す実施形態は本開示の実施形態の一例であって、本開示はこれらの実施形態に限定して解釈されるものではない。また、本明細書において、「基板」、「基材」、「シート」や「フィルム」など用語は、呼称の違いのみに基づいて、互いから区別されるものではない。例えば、「基板」や「基材」は、シートやフィルムと呼ばれ得るような部材も含む概念である。更に、本明細書において用いる、形状や幾何学的条件並びにそれらの程度を特定する、例えば、「平行」や「直交」等の用語や長さや角度の値等については、厳密な意味に縛られることなく、同様の機能を期待し得る程度の範囲を含めて解釈することとする。また、本実施形態で参照する図面において、同一部分または同様な機能を有する部分には同一の符号または類似の符号を付し、その繰り返しの説明は省略する場合がある。また、図面の寸法比率は説明の都合上実際の比率とは異なる場合や、構成の一部が図面から省略される場合がある。 A configuration of a high-frequency component and a method of manufacturing the same according to embodiments of the present disclosure will be described in detail below with reference to the drawings. The embodiments shown below are examples of the embodiments of the present disclosure, and the present disclosure should not be construed as being limited to these embodiments. Also, in this specification, terms such as "substrate", "base material", "sheet" and "film" are not to be distinguished from each other based only on the difference in designation. For example, "substrate" and "base material" are concepts that include members that can be called sheets and films. Furthermore, terms used herein to specify shapes and geometric conditions and their degrees, such as terms such as "parallel" and "perpendicular", length and angle values, etc., are bound by strict meanings. However, it is interpreted to include the extent to which similar functions can be expected. In addition, in the drawings referred to in this embodiment, the same reference numerals or similar reference numerals may be assigned to the same portions or portions having similar functions, and repeated description thereof may be omitted. Also, the dimensional ratios in the drawings may differ from the actual ratios for convenience of explanation, and some of the configurations may be omitted from the drawings.

高周波部品
以下、本開示の実施の形態について説明する。まず、図１乃至図３を参照して、本実施の形態に係る高周波部品１０の構成について説明する。図１は、高周波部品１０を示す断面図である。図２は、図１の高周波部品１０を拡大して示す断面図である。図３は、高周波部品１０を示す平面図である。図１は、図３に示す高周波部品１０を線Ａ－Ａに沿って切断した場合の断面図に相当する。なお高周波部品とは、0.1ＧＨｚ以上の高周波信号に対して使用可能な電子部品を意味する。 High- Frequency Components Embodiments of the present disclosure will be described below. First, the configuration of a high-frequency component 10 according to the present embodiment will be described with reference to FIGS. 1 to 3. FIG. FIG. 1 is a cross-sectional view showing a high frequency component 10. As shown in FIG. FIG. 2 is an enlarged cross-sectional view showing the high-frequency component 10 of FIG. FIG. 3 is a plan view showing the high frequency component 10. FIG. FIG. 1 corresponds to a cross-sectional view of the high-frequency component 10 shown in FIG. 3 taken along line AA. High-frequency components mean electronic components that can be used for high-frequency signals of 0.1 GHz or higher.

高周波部品１０は、基板１２、キャパシタ１５及びインダクタ１６を備える。キャパシタ１５は、第１配線構造部３０の一部によって構成されている。インダクタ１６は、第１配線構造部３０の一部と、貫通電極２２と、第２配線構造部４０の一部とによって構成されている。以下、高周波部品１０の各構成要素について説明する。 A high frequency component 10 includes a substrate 12 , a capacitor 15 and an inductor 16 . The capacitor 15 is configured by part of the first wiring structure portion 30 . The inductor 16 is composed of a portion of the first wiring structure portion 30 , the through electrode 22 and a portion of the second wiring structure portion 40 . Each component of the high-frequency component 10 will be described below.

（基板）
基板１２は、第１面１３、及び、第１面１３の反対側に位置する第２面１４を含む。また、基板１２には、第１面１３から第２面１４に至る複数の貫通孔２０が設けられている。 (substrate)
Substrate 12 includes a first side 13 and a second side 14 opposite first side 13 . Further, the substrate 12 is provided with a plurality of through holes 20 extending from the first surface 13 to the second surface 14 .

基板１２は、ガラスを有する。基板１２で用いるガラスの例としては、無アルカリガラスなどを挙げることができる。無アルカリガラスとは、ナトリウムやカリウムなどのアルカリ成分を含まないガラスである。無アルカリガラスは、例えば、アルカリ成分の代わりにホウ酸を含む。また、無アルカリガラスは、例えば、酸化カルシウムや酸化バリウムなどのアルカリ土類金属酸化物を含む。無アルカリガラスの例としては、旭硝子製のＥＮ－Ａ１や、コーニング製のイーグルＸＧなどを挙げることができる。基板１２の厚みは、例えば０．２５ｍｍ以上且つ０．４５ｍｍ以下である。基板１２がガラスを含むことにより、基板１２がシリコンからなる場合に比べて、基板１２の絶縁性を高めることができ、これにより、基板１２上に位置するキャパシタ１５の耐電圧特性を改善することができる。 Substrate 12 comprises glass. Examples of the glass used for the substrate 12 include alkali-free glass. Alkali-free glass is glass that does not contain alkaline components such as sodium and potassium. Alkali-free glass includes, for example, boric acid instead of an alkaline component. Alkali-free glass also contains, for example, alkaline earth metal oxides such as calcium oxide and barium oxide. Examples of alkali-free glass include EN-A1 manufactured by Asahi Glass and Eagle XG manufactured by Corning. The thickness of the substrate 12 is, for example, 0.25 mm or more and 0.45 mm or less. Since the substrate 12 contains glass, the insulation of the substrate 12 can be improved compared to the case where the substrate 12 is made of silicon, thereby improving the withstand voltage characteristics of the capacitor 15 located on the substrate 12. can be done.

貫通孔２０の側壁２１は、図１に示すように基板１２の第１面１３の法線方向に沿って広がっていてもよい。若しくは、図示はしないが、側壁２１が、基板１２の第１面１３の法線方向からずれた方向で広がっていてもよく、また、側壁２１の一部が湾曲していてもよい。 The sidewall 21 of the through hole 20 may extend along the normal direction of the first surface 13 of the substrate 12 as shown in FIG. Alternatively, although not shown, the side wall 21 may extend in a direction deviated from the normal direction of the first surface 13 of the substrate 12, or the side wall 21 may be partially curved.

貫通孔２０の長さ、すなわち第１面１３の法線方向における貫通孔２０の寸法は、基板１２の厚みに等しい。貫通孔２０の幅、すなわち第１面１３の面方向における貫通孔２０の寸法Ｓ（図４参照）は、例えば４０μｍ以上且つ１５０μｍ以下である。また、貫通孔２０の幅に対する長さの比、すなわち貫通孔２０のアスペクト比は、例えば４以上且つ１０以下である。 The length of the through hole 20 , that is, the dimension of the through hole 20 in the normal direction of the first surface 13 is equal to the thickness of the substrate 12 . The width of the through hole 20, that is, the dimension S (see FIG. 4) of the through hole 20 in the surface direction of the first surface 13 is, for example, 40 μm or more and 150 μm or less. Also, the ratio of the length to the width of the through hole 20, that is, the aspect ratio of the through hole 20 is, for example, 4 or more and 10 or less.

（貫通電極）
貫通電極２２は、貫通孔２０の内部に少なくとも部分的に位置し、且つ導電性を有する部材である。本実施の形態において、貫通電極２２の厚みは、貫通孔２０の幅よりも小さく、このため、貫通電極２２の内部には、貫通電極２２が存在しない空間がある。すなわち、貫通電極２２は、いわゆるコンフォーマルビアである。 (through electrode)
The through electrode 22 is a member positioned at least partially inside the through hole 20 and having electrical conductivity. In the present embodiment, the thickness of the through electrode 22 is smaller than the width of the through hole 20, so there is a space inside the through electrode 22 where the through electrode 22 does not exist. That is, the through electrode 22 is a so-called conformal via.

貫通電極２２が導電性を有する限りにおいて、貫通電極２２の形成方法は特には限定されない。例えば、貫通電極２２は、蒸着法やスパッタリング法などの物理成膜法で形成されていてもよく、化学成膜法やめっき法で形成されていてもよい。また、貫通電極２２は、導電性を有する単一の層から構成されていてもよく、若しくは、導電性を有する複数の層を含んでいてもよい。ここでは、図２に示すように、貫通電極２２が、貫通孔２０の側壁２１側から貫通孔２０の中心側へ順に並ぶ密着層３６１、シード層３６２及びめっき層３６３を含む例について説明する。 The method of forming the through electrode 22 is not particularly limited as long as the through electrode 22 has conductivity. For example, the through electrode 22 may be formed by a physical film forming method such as a vapor deposition method or a sputtering method, or may be formed by a chemical film forming method or a plating method. Further, the through electrode 22 may be composed of a single conductive layer, or may include a plurality of conductive layers. Here, as shown in FIG. 2, an example in which the through electrode 22 includes an adhesion layer 361, a seed layer 362, and a plating layer 363 arranged in order from the sidewall 21 side of the through hole 20 to the center side of the through hole 20 will be described.

密着層３６１は、シード層３６２やめっき層３６３などのその他の貫通電極２２の構成要素と基板１２の貫通孔２０の側壁２１との間に、必要に応じて形成される層である。密着層３６１は、シード層３６２やめっき層３６３などのその他の貫通電極２２の構成要素に比べて、基板１２に対する高い密着性を有する。また、密着層３６１は、シード層３６２やめっき層３６３などのその他の貫通電極２２の構成要素中の金属元素が貫通孔２０の側壁２１を介して基板１２の内部に拡散することを抑制するという役割を果たしてもよい。シード層３６２又はめっき層３６３が銅を含む場合、密着層３６１の材料として、例えば、チタン、チタン窒化物、モリブデン、モリブデン窒化物、タンタル、タンタル窒化物等、又はこれらを積層したものを用いることができる。また、密着層３６１の材料として、基板１２に対する高い密着性を有する導電性材料を用いてもよい。例えば、密着層３６１の材料として、チタン、モリブデン、タングステン、タンタル、ニッケル、クロム、アルミニウム、これらの化合物、これらの合金など、又はこれらを積層したものを使用することができる。密着層３６１の厚みは、例えば１０ｎｍ以上且つ１μｍ以下である。密着層３６１は、例えば、蒸着法やスパッタリング法などの物理成膜法で形成される。 The adhesion layer 361 is a layer formed as necessary between the sidewalls 21 of the through holes 20 of the substrate 12 and other components of the through electrodes 22 such as the seed layer 362 and the plating layer 363 . The adhesion layer 361 has higher adhesion to the substrate 12 than other components of the through electrode 22 such as the seed layer 362 and the plating layer 363 . In addition, the adhesion layer 361 is said to suppress the diffusion of metal elements in other components of the through electrode 22 such as the seed layer 362 and the plating layer 363 into the substrate 12 through the sidewall 21 of the through hole 20 . may play a role. When the seed layer 362 or the plating layer 363 contains copper, the material of the adhesion layer 361 may be, for example, titanium, titanium nitride, molybdenum, molybdenum nitride, tantalum, tantalum nitride, or a laminate thereof. can be done. Also, as the material of the adhesion layer 361, a conductive material having high adhesion to the substrate 12 may be used. For example, as the material of the adhesion layer 361, titanium, molybdenum, tungsten, tantalum, nickel, chromium, aluminum, compounds thereof, alloys thereof, or a laminate thereof can be used. The thickness of the adhesion layer 361 is, for example, 10 nm or more and 1 μm or less. The adhesion layer 361 is formed, for example, by a physical film forming method such as a vapor deposition method or a sputtering method.

シード層３６２は、電解めっき処理によってめっき層３６３を形成する電解めっき工程の際に、めっき液中の金属イオンを析出させてめっき層３６３を成長させるための土台となる、導電性を有する層である。シード層３６２の材料としては、例えば、銅などの、めっき層３６３と同一の金属材料を用いることができる。シード層３６２の厚みは、例えば１００ｎｍ以上且つ３μｍ以下である。シード層３６２は、例えば、無電解めっき処理によって形成される。 The seed layer 362 is a conductive layer that serves as a base for depositing metal ions in the plating solution and growing the plating layer 363 during the electroplating process for forming the plating layer 363 by electroplating. be. As the material of the seed layer 362, the same metal material as the plating layer 363, such as copper, can be used. The thickness of the seed layer 362 is, for example, 100 nm or more and 3 μm or less. The seed layer 362 is formed by electroless plating, for example.

なお、図示はしないが、貫通孔２０の側壁２１とめっき層３６３との間に、密着層としての役割及びシード層としての役割の両方を果たすことができる１つの層を設けてもよい。 Although not shown, a single layer that can serve as both an adhesion layer and a seed layer may be provided between the side wall 21 of the through-hole 20 and the plating layer 363 .

めっき層３６３は、めっき処理によって形成される、導電性を有する層である。めっき層３６３を構成する材料としては、銅、金、銀、白金、ロジウム、スズ、アルミニウム、ニッケル、クロムなどの金属又はこれらを用いた合金など、あるいはこれらを積層したものを使用することができる。 The plating layer 363 is a conductive layer formed by plating. As a material for forming the plated layer 363, metals such as copper, gold, silver, platinum, rhodium, tin, aluminum, nickel, chromium, alloys using these, or laminates thereof can be used. .

図１に示すように、高周波部品１０は、貫通電極２２よりも貫通孔２０の中心側に位置する有機層２６を備えていてもよい。なお、「中心側」とは、貫通孔２０の内部において、有機層２６と側壁２１との間の距離が貫通電極２２と側壁２１との間の距離よりも大きいことを意味する。有機層２６は、０．００３以下、より好ましくは０．００２以下、更に好ましくは０．００１以下の誘電正接を有する有機材料を含む。有機層２６の有機材料としては、ポリイミド、エポキシなどを用いることができる。誘電正接の小さい有機材料を用いて有機層２６を構成することにより、キャパシタ１５やインダクタ１６を通るべき電気信号の一部が有機層２６を通ってしまうことを抑制することができる。これにより、キャパシタ１５やインダクタ１６を備える高周波部品１０の帯域を高周波側に広げることができる。 As shown in FIG. 1 , the high-frequency component 10 may include an organic layer 26 located closer to the center of the through hole 20 than the through electrode 22 is. The “center side” means that the distance between the organic layer 26 and the side wall 21 is greater than the distance between the through electrode 22 and the side wall 21 inside the through hole 20 . Organic layer 26 comprises an organic material having a dielectric loss tangent of 0.003 or less, more preferably 0.002 or less, and even more preferably 0.001 or less. As an organic material for the organic layer 26, polyimide, epoxy, or the like can be used. By configuring the organic layer 26 using an organic material with a small dielectric loss tangent, it is possible to suppress part of the electrical signal that should pass through the capacitor 15 and the inductor 16 from passing through the organic layer 26 . As a result, the band of the high frequency component 10 including the capacitor 15 and the inductor 16 can be widened to the high frequency side.

（第１配線構造部）
図１に示すように、第１配線構造部３０は、基板１２の第１面１３上に位置する第１面第１配線層３１、第１面第１配線層３１上に位置する第１面第２配線層３２、及び第１面第２配線層３２上に位置する第１面第３配線層３３を含む。以下、第１面第１配線層３１、第１面第２配線層３２及び第１面第３配線層３３の構成について説明する。 (First wiring structure part)
As shown in FIG. 1, the first wiring structure portion 30 has a first surface first wiring layer 31 located on the first surface 13 of the substrate 12, and a first surface located on the first surface first wiring layer 31. It includes a second wiring layer 32 and a first surface third wiring layer 33 located on the first surface second wiring layer 32 . The configurations of the first surface first wiring layer 31, the first surface second wiring layer 32, and the first surface third wiring layer 33 will be described below.

〔第１面第１配線層〕
図１に示すように、第１面第１配線層３１は、第１面第１導電層３１１及び第１面第１絶縁層３１２を有する。第１面第１導電層３１１は、基板１２の第１面１３上に位置する、導電性を有する層である。第１面第１導電層３１１は、貫通電極２２に接続されていてもよい。また、第１面第１導電層３１１は、貫通電極２２と同様に、基板１２の第１面１３上に順に積層された密着層３６１、シード層３６２及びめっき層３６３を含んでいてもよい。第１面第１導電層３１１を構成する材料は、貫通電極２２を構成する材料と同様である。第１面第１導電層３１１の厚みは、例えば５μｍ以上且つ２０μｍ以下である。 [First Wiring Layer on First Surface]
As shown in FIG. 1 , the first surface first wiring layer 31 has a first surface first conductive layer 311 and a first surface first insulating layer 312 . The first surface first conductive layer 311 is a conductive layer located on the first surface 13 of the substrate 12 . The first surface first conductive layer 311 may be connected to the through electrode 22 . Also, the first surface first conductive layer 311 may include an adhesion layer 361 , a seed layer 362 and a plating layer 363 that are laminated in order on the first surface 13 of the substrate 12 , similar to the through electrode 22 . The material forming the first surface first conductive layer 311 is the same as the material forming the through electrode 22 . The thickness of the first surface first conductive layer 311 is, for example, 5 μm or more and 20 μm or less.

第１面第１絶縁層３１２は、少なくとも部分的に第１面第１導電層３１１上に位置する、絶縁性を有する層である。第１面第１絶縁層３１２は、第１面第１導電層３１１を部分的に覆っていてもよい。この場合、第１面第１絶縁層３１２は、第１面第１導電層３１１だけでなく基板１２の第１面１３にも接していてもよい。なお「覆う」とは、図３に示すように、基板１２の第１面１３の法線方向に沿って高周波部品１０を見た場合に、第１面第１導電層３１１の端部３１１ｅと第１面第１絶縁層３１２とが少なくとも部分的に重なっていることを意味する。 The first surface first insulating layer 312 is a layer that is located at least partially on the first surface first conductive layer 311 and has insulating properties. The first surface first insulating layer 312 may partially cover the first surface first conductive layer 311 . In this case, the first surface first insulating layer 312 may be in contact with not only the first surface first conductive layer 311 but also the first surface 13 of the substrate 12 . Note that "covering" means that when the high-frequency component 10 is viewed along the normal direction of the first surface 13 of the substrate 12 as shown in FIG. It means that the first surface and the first insulating layer 312 are at least partially overlapped.

第１面第１絶縁層３１２は、少なくとも６ＭＶ／ｃｍ以上、より好ましくは８ＭＶ／ｃｍ以上の絶縁破壊電界を有する無機材料を含む。第１面第１絶縁層３１２の無機材料としては、ＳｉＮなどの珪素窒化物を用いることができる。その他にも、第１面第１絶縁層３１２の無機材料の例として、酸化シリコン、酸化アルミ、五酸化タンタルなどを挙げることができる。これにより、第１面第１絶縁層３１２を含むキャパシタ１５の耐電圧特性を更に改善することができる。なお、絶縁破壊電界の測定方法については、実施例において後述する。第１面第１絶縁層３１２の無機材料の比誘電率は、例えば３以上且つ５０以下である。また、第１面第１絶縁層３１２の厚みは、例えば５０ｎｍ以上且つ４００ｎｍ以下である。 The first surface first insulating layer 312 includes an inorganic material having a dielectric breakdown field of at least 6 MV/cm or more, more preferably 8 MV/cm or more. Silicon nitride such as SiN can be used as the inorganic material for the first surface first insulating layer 312 . In addition, examples of inorganic materials for the first surface first insulating layer 312 include silicon oxide, aluminum oxide, and tantalum pentoxide. Thereby, the withstand voltage characteristics of the capacitor 15 including the first surface first insulating layer 312 can be further improved. A method for measuring the dielectric breakdown electric field will be described later in Examples. The dielectric constant of the inorganic material of the first surface first insulating layer 312 is, for example, 3 or more and 50 or less. Also, the thickness of the first surface first insulating layer 312 is, for example, 50 nm or more and 400 nm or less.

好ましくは、第１面第１絶縁層３１２の無機材料における漏れ電流は、１×１０－１２Ａ以下である。これにより、第１面第１絶縁層３１２を含むキャパシタ１５の電気特性を更に改善することができる。なお、漏れ電流の測定方法については、実施例において後述する。 Preferably, the leakage current in the inorganic material of the first surface first insulating layer 312 is 1×10 −12 A or less. Thereby, the electrical characteristics of the capacitor 15 including the first surface first insulating layer 312 can be further improved. A method for measuring leakage current will be described later in Examples.

〔第１面第２配線層〕
第１面第２配線層３２は、第１面第２導電層３２１及び第１面第２絶縁層３２２を有する。第１面第２導電層３２１は、第１面第１絶縁層３１２上に位置する、導電性を有する層である。図１に示すように、第１面第１導電層３１１と、第１面第１導電層３１１上に位置する第１面第１絶縁層３１２と、第１面第１絶縁層３１２上に位置する第１面第２導電層３２１とによって、キャパシタ１５が構成されている。 [First surface, second wiring layer]
The first surface second wiring layer 32 has a first surface second conductive layer 321 and a first surface second insulating layer 322 . The first surface second conductive layer 321 is a conductive layer located on the first surface first insulating layer 312 . As shown in FIG. 1 , a first surface first conductive layer 311 , a first surface first insulating layer 312 located on the first surface first conductive layer 311 , and a first surface first insulating layer 312 located on the first surface first insulating layer 312 . The capacitor 15 is configured by the first surface second conductive layer 321 .

第１面第２導電層３２１は、貫通電極２２や第１面第１導電層３１１と同様に、第１面第１絶縁層３１２上に順に積層された密着層、シード層及びめっき層を含んでいてもよい。第１面第２導電層３２１を構成する材料は、貫通電極２２や第１面第１導電層３１１を構成する材料と同様である。第１面第２導電層３２１の厚みは、例えば５μｍ以上且つ２０μｍ以下である。 The first surface second conductive layer 321 includes an adhesion layer, a seed layer and a plating layer, which are laminated in order on the first surface first insulating layer 312, like the through electrodes 22 and the first surface first conductive layer 311. You can stay. The material forming the first surface second conductive layer 321 is the same as the material forming the through electrode 22 and the first surface first conductive layer 311 . The thickness of the first surface second conductive layer 321 is, for example, 5 μm or more and 20 μm or less.

第１面第２絶縁層３２２は、第１面第１絶縁層３１２上及び第１面第２導電層３２１に位置する、絶縁性を有する層である。第１面第２絶縁層３２２は、０．００３以下、より好ましくは０．００２以下、更に好ましくは０．００１以下の誘電正接を有する有機材料を含む。第１面第２絶縁層３２２の有機材料としては、ポリイミド、エポキシなどを用いることができる。誘電正接の小さい有機材料を用いて第１面第２絶縁層３２２を構成することにより、キャパシタ１５やインダクタ１６を通るべき電気信号が第１面第２絶縁層３２２を通ってしまうことを抑制することができる。これにより、キャパシタ１５やインダクタ１６を備える高周波部品１０の帯域を高周波側に広げることができる。 The first surface second insulating layer 322 is an insulating layer located on the first surface first insulating layer 312 and on the first surface second conductive layer 321 . The first surface second insulating layer 322 includes an organic material having a dielectric loss tangent of 0.003 or less, more preferably 0.002 or less, and even more preferably 0.001 or less. As an organic material for the first surface second insulating layer 322, polyimide, epoxy, or the like can be used. By forming the first surface second insulating layer 322 using an organic material having a small dielectric loss tangent, it is possible to suppress the electric signal that should pass through the capacitor 15 and the inductor 16 from passing through the first surface second insulating layer 322. be able to. As a result, the band of the high frequency component 10 including the capacitor 15 and the inductor 16 can be widened to the high frequency side.

第１面第２絶縁層３２２の有機材料の比誘電率は、好ましくは３．４以下である。また、５ＧＨｚにおける第１面第２絶縁層３２２の有機材料の透過損失は、好ましくは０．０７ｄＢ以下、より好ましくは０．０６ｄＢ以下、更に好ましくは０．０５ｄＢ以下である。 The dielectric constant of the organic material of the first surface second insulating layer 322 is preferably 3.4 or less. Also, the transmission loss of the organic material of the first surface second insulating layer 322 at 5 GHz is preferably 0.07 dB or less, more preferably 0.06 dB or less, and even more preferably 0.05 dB or less.

〔第１面第３配線層〕
第１面第３配線層３３は、第１面第３導電層３３１及び第１面第３絶縁層３３２を有する。第１面第３導電層３３１は、第１面第１導電層３１１上又は第１面第２導電層３２１上に位置する、導電性を有する層である。図１に示す例において、第１面第３導電層３３１は、キャパシタ１５の一方の電極である第１面第１導電層３１１に接続された部分、及び、キャパシタ１５の他方の電極である第１面第２導電層３２１に接続された部分を含む。 [First surface, third wiring layer]
The first surface third wiring layer 33 has a first surface third conductive layer 331 and a first surface third insulating layer 332 . The first surface third conductive layer 331 is a conductive layer located on the first surface first conductive layer 311 or the first surface second conductive layer 321 . In the example shown in FIG. 1 , the first surface third conductive layer 331 includes a portion connected to the first surface first conductive layer 311 which is one electrode of the capacitor 15 and a portion connected to the first surface first conductive layer 311 which is the other electrode of the capacitor 15 . One surface includes a portion connected to the second conductive layer 321 .

第１面第３導電層３３１は、貫通電極２２や第１面第１導電層３１１と同様に、順に積層された密着層、シード層及びめっき層を含んでいてもよい。第１面第３導電層３３１を構成する材料は、貫通電極２２や第１面第１導電層３１１を構成する材料と同様である。 The first-surface third conductive layer 331 may include an adhesion layer, a seed layer, and a plating layer, which are laminated in order, like the through electrodes 22 and the first-surface first conductive layer 311 . The material forming the first surface third conductive layer 331 is the same as the material forming the through electrode 22 and the first surface first conductive layer 311 .

第１面第３絶縁層３３２は、第１面第２絶縁層３２２上及び第１面第３導電層３３１上に位置する、絶縁性を有する層である。第１面第３絶縁層３３２は、第１面第２絶縁層３２２と同様に、０．００３以下、より好ましくは０．００２以下、更に好ましくは０．００１以下の誘電正接を有する有機材料を含む。第１面第３絶縁層３３２の有機材料としては、第１面第２絶縁層３２２と同様に、ポリイミド、エポキシなどを用いることができる。 The first surface third insulating layer 332 is an insulating layer located on the first surface second insulating layer 322 and the first surface third conductive layer 331 . Like the first surface second insulating layer 322, the first surface third insulating layer 332 is made of an organic material having a dielectric loss tangent of 0.003 or less, more preferably 0.002 or less, and still more preferably 0.001 or less. include. As the organic material for the first surface third insulating layer 332, polyimide, epoxy, or the like can be used similarly to the first surface second insulating layer 322. FIG.

（第２配線構造部）
図１に示すように、第２配線構造部４０は、基板１２の第２面１４上に位置する第２面第１配線層４１を含む。第２面第１配線層４１は、第２面第１導電層４１１及び第２面第１絶縁層４１２を有する。 (Second wiring structure part)
As shown in FIG. 1 , the second wiring structure 40 includes a second surface first wiring layer 41 located on the second surface 14 of the substrate 12 . The second surface first wiring layer 41 has a second surface first conductive layer 411 and a second surface first insulating layer 412 .

第２面第１導電層４１１は、基板１２の第２面１４上に位置する、導電性を有する層である。第２面第１導電層４１１は、貫通電極２２に接続されていてもよい。また、第２面第１導電層４１１は、貫通電極２２や第１面第１導電層３１１と同様に、基板１２の第２面１４上に順に積層された密着層３６１、シード層３６２及びめっき層３６３を含んでいてもよい。第２面第１導電層４１１を構成する材料は、貫通電極２２や第１面第１導電層３１１を構成する材料と同様である。第２面第１導電層４１１の厚みは、例えば５μｍ以上且つ２０μｍ以下である。 The second surface first conductive layer 411 is a conductive layer located on the second surface 14 of the substrate 12 . The second surface first conductive layer 411 may be connected to the through electrode 22 . In addition, the second surface first conductive layer 411 includes an adhesion layer 361, a seed layer 362, and a plating layer which are laminated in order on the second surface 14 of the substrate 12 in the same manner as the through electrodes 22 and the first surface first conductive layer 311. A layer 363 may be included. The material forming the second surface first conductive layer 411 is the same as the material forming the through electrode 22 and the first surface first conductive layer 311 . The thickness of the second surface first conductive layer 411 is, for example, 5 μm or more and 20 μm or less.

図１及び図３に示すように、第２面第１導電層４１１と、第２面第１導電層４１１に接続された貫通電極２２と、貫通電極２２に接続された第１面第１導電層３１１とによって、インダクタ１６が構成される。 As shown in FIGS. 1 and 3, a second surface first conductive layer 411, a through electrode 22 connected to the second surface first conductive layer 411, and a first surface first conductive layer connected to the through electrode 22 Inductor 16 is configured by layer 311 .

第２面第１絶縁層４１２は、第２面第１導電層４１１上及び基板１２の第２面１４上に位置する、絶縁性を有する層である。第２面第１絶縁層４１２は、第１面第２絶縁層３２２や第１面第３絶縁層３３２と同様に、０．００３以下、より好ましくは０．００２以下、更に好ましくは０．００１以下の誘電正接を有する有機材料を含む。第２面第１絶縁層４１２の有機材料としては、第１面第２絶縁層３２２や第１面第３絶縁層３３２と同様に、ポリイミド、エポキシなどを用いることができる。 The second surface first insulating layer 412 is a layer having insulating properties located on the second surface first conductive layer 411 and on the second surface 14 of the substrate 12 . Like the first surface second insulating layer 322 and the first surface third insulating layer 332, the second surface first insulating layer 412 has a thickness of 0.003 or less, more preferably 0.002 or less, and still more preferably 0.001. Contains organic materials with the following dielectric loss tangents: As the organic material of the second surface first insulating layer 412, polyimide, epoxy, or the like can be used similarly to the first surface second insulating layer 322 and the first surface third insulating layer 332. FIG.

高周波部品の製造方法
以下、高周波部品１０の製造方法の一例について、図４乃至図１５を参照して説明する。 Manufacturing Method of High-Frequency Component An example of a manufacturing method of the high-frequency component 10 will be described below with reference to FIGS. 4 to 15. FIG.

（貫通孔形成工程）
まず、基板１２を準備する。次に、第１面１３又は第２面１４の少なくともいずれかにレジスト層を設ける。その後、レジスト層のうち貫通孔２０に対応する位置に開口を設ける。次に、レジスト層の開口において基板１２を加工することにより、図４に示すように、基板１２に貫通孔２０を形成することができる。基板１２を加工する方法としては、反応性イオンエッチング法、深掘り反応性イオンエッチング法などのドライエッチング法や、ウェットエッチング法などを用いることができる。 (Through hole forming step)
First, the substrate 12 is prepared. Next, a resist layer is provided on at least one of the first surface 13 and the second surface 14 . After that, openings are provided in the resist layer at positions corresponding to the through holes 20 . Next, by processing the substrate 12 in the openings of the resist layer, through holes 20 can be formed in the substrate 12 as shown in FIG. As a method for processing the substrate 12, a dry etching method such as a reactive ion etching method or a deep reactive ion etching method, a wet etching method, or the like can be used.

なお、基板１２にレーザを照射することによって基板１２に貫通孔２０を形成してもよい。この場合、レジスト層は設けられていなくてもよい。レーザ加工のためのレーザとしては、エキシマレーザ、Ｎｄ：ＹＡＧレーザ、フェムト秒レーザ等を用いることができる。Ｎｄ：ＹＡＧレーザを採用する場合、波長が１０６４ｎｍの基本波、波長が５３２ｎｍの第２高調波、波長が３５５ｎｍの第３高調波等を用いることができる。 The through holes 20 may be formed in the substrate 12 by irradiating the substrate 12 with a laser. In this case, the resist layer may not be provided. As a laser for laser processing, an excimer laser, Nd:YAG laser, femtosecond laser, or the like can be used. When an Nd:YAG laser is employed, a fundamental wave with a wavelength of 1064 nm, a second harmonic with a wavelength of 532 nm, a third harmonic with a wavelength of 355 nm, or the like can be used.

また、レーザ照射とウェットエッチングを適宜組み合わせることもできる。具体的には、まず、レーザ照射によって基板１２のうち貫通孔２０が形成されるべき領域に変質層を形成する。続いて、基板１２をフッ化水素などに浸漬して、変質層をエッチングする。これによって、基板１２に貫通孔２０を形成することができる。 Alternatively, laser irradiation and wet etching can be combined as appropriate. Specifically, first, an altered layer is formed in a region of the substrate 12 where the through hole 20 is to be formed by laser irradiation. Subsequently, the substrate 12 is immersed in hydrogen fluoride or the like to etch the altered layer. Through holes 20 can thus be formed in the substrate 12 .

その他にも、基板１２に研磨材を吹き付けるブラスト処理によって基板１２に貫通孔２０を形成してもよい。 Alternatively, the through holes 20 may be formed in the substrate 12 by blasting the substrate 12 with an abrasive.

（貫通電極形成工程）
次に、貫通孔２０の側壁２１に貫通電極２２を形成する。本実施の形態においては、貫通電極２２と同時に上述の第１面第１導電層３１１及び第２面第１導電層４１１を形成する例について説明する。 (Through electrode forming step)
Next, the through electrodes 22 are formed on the sidewalls 21 of the through holes 20 . In the present embodiment, an example in which the first surface first conductive layer 311 and the second surface first conductive layer 411 are formed at the same time as the through electrode 22 will be described.

図５に示すように、基板１２の第１面１３上、第２面１４及び側壁２１上に、蒸着法やスパッタリング法などの物理成膜法によって密着層３６１を形成する。続いて、無電解めっきによって密着層３６１上にシード層３６２を形成する。その後、密着層３６１及びシード層３６２をアニールする工程を実施してもよい。 As shown in FIG. 5, an adhesion layer 361 is formed on the first surface 13, the second surface 14 and the sidewalls 21 of the substrate 12 by a physical film forming method such as vapor deposition or sputtering. Subsequently, a seed layer 362 is formed on the adhesion layer 361 by electroless plating. After that, a step of annealing the adhesion layer 361 and the seed layer 362 may be performed.

なお、密着層３６１及びシード層３６２を形成する方法が、上述の方法に限られることはない。例えば、ゾルゲル法によって酸化亜鉛などを含む密着層３６１を形成し、続いて、密着層３６１上に無電解めっき法によってシード層３６２を形成してもよい。また、密着層３６１及びシード層３６２の両方を、蒸着法やスパッタリング法などの物理成膜法によって形成してもよい。 Note that the method of forming the adhesion layer 361 and the seed layer 362 is not limited to the method described above. For example, the adhesion layer 361 containing zinc oxide or the like may be formed by a sol-gel method, and then the seed layer 362 may be formed on the adhesion layer 361 by an electroless plating method. Also, both the adhesion layer 361 and the seed layer 362 may be formed by a physical film formation method such as a vapor deposition method or a sputtering method.

次に、図６に示すように、シード層３６２上に部分的にレジスト層３７を形成する。続いて、図７に示すように、電解めっきによって、レジスト層３７によって覆われていないシード層３６２上にめっき層３６３を形成する。その後、図８に示すように、レジスト層３７を除去する。また、密着層３６１及びシード層３６２のうちレジスト層３７によって覆われていた部分を、例えばウェットエッチングにより除去する。このようにして、貫通電極２２、第１面第１導電層３１１及び第２面第１導電層４１１を形成することができる。これにより、第２面第１導電層４１１と、第２面第１導電層４１１に接続された貫通電極２２と、貫通電極２２に接続された第１面第１導電層３１１とを備えるインダクタ１６を構成することができる。なお、めっき層３６３をアニールする工程を実施してもよい。 Next, as shown in FIG. 6, a resist layer 37 is partially formed on the seed layer 362 . Subsequently, as shown in FIG. 7, a plating layer 363 is formed on the seed layer 362 not covered with the resist layer 37 by electroplating. After that, as shown in FIG. 8, the resist layer 37 is removed. Also, the portions of the adhesion layer 361 and the seed layer 362 that are covered with the resist layer 37 are removed by wet etching, for example. In this manner, the through electrode 22, the first surface first conductive layer 311, and the second surface first conductive layer 411 can be formed. As a result, the inductor 16 includes the second surface first conductive layer 411 , the through electrode 22 connected to the second surface first conductive layer 411 , and the first surface first conductive layer 311 connected to the through electrode 22 . can be configured. Note that a step of annealing the plating layer 363 may be performed.

（表面処理工程）
次に、第１面第１導電層３１１の表面をＮＨ３プラズマなどのプラズマに晒す表面処理工程を実施してもよい。これにより、第１面第１導電層３１１の表面の酸化物を除去することができる。例えば、第１面第１導電層３１１が銅を含む場合、第１面第１導電層３１１の表面の酸化銅を除去することができる。このことにより、第１面第１導電層３１１と、第１面第１導電層３１１上に形成される第１面第１絶縁層３１２との間の密着性を高めることができる。 (Surface treatment process)
Next, a surface treatment step of exposing the surface of the first surface first conductive layer 311 to plasma such as NH 3 plasma may be performed. Thereby, the oxide on the surface of the first surface first conductive layer 311 can be removed. For example, if the first surface first conductive layer 311 contains copper, the copper oxide on the surface of the first surface first conductive layer 311 can be removed. As a result, the adhesion between the first surface first conductive layer 311 and the first surface first insulating layer 312 formed on the first surface first conductive layer 311 can be enhanced.

（第１面第１絶縁層の形成工程）
次に、第１面第１導電層３１１上に第１面第１絶縁層３１２を形成する。まず、図９に示すように、第１面第１導電層３１１上に部分的にレジスト層３８を形成する。続いて、図１０に示すように、第１面第１導電層３１１及び基板１２の第１面１３のうちレジスト層３８によって覆われていない部分に、第１面第１絶縁層３１２を形成する。第１面第１絶縁層３１２を形成する方法としては、例えば、プラズマＣＶＤ、スパッタリングなどを採用することができる。その後、図１１に示すように、レジスト層３８を除去する。このようにして、第１面第１導電層３１１上に部分的に第１面第１絶縁層３１２を形成することができる。 (Step of forming first insulating layer on first surface)
Next, a first surface first insulating layer 312 is formed on the first surface first conductive layer 311 . First, as shown in FIG. 9, a resist layer 38 is partially formed on the first surface first conductive layer 311 . Subsequently, as shown in FIG. 10, a first surface first conductive layer 311 and a first surface first insulating layer 312 are formed on portions of the first surface 13 of the substrate 12 that are not covered with the resist layer 38. . As a method for forming the first surface first insulating layer 312, for example, plasma CVD, sputtering, or the like can be adopted. After that, as shown in FIG. 11, the resist layer 38 is removed. In this manner, the first surface first insulating layer 312 can be partially formed on the first surface first conductive layer 311 .

（第１面第２導電層の形成工程）
次に、図１２に示すように、第１面第１絶縁層３１２上に第１面第２導電層３２１を形成する。これにより、第１面第１導電層３１１と、第１面第１導電層３１１上の第１面第１絶縁層３１２と、第１面第１絶縁層３１２上の第１面第２導電層３２１と、を備えるキャパシタ１５を構成することができる。第１面第２導電層３２１を形成する工程は、第１面第１導電層３１１を形成する工程と同様であるので、説明を省略する。 (Step of forming second conductive layer on first surface)
Next, as shown in FIG. 12, a first surface second conductive layer 321 is formed on the first surface first insulating layer 312 . As a result, a first surface first conductive layer 311, a first surface first insulating layer 312 on the first surface first conductive layer 311, and a first surface second conductive layer on the first surface first insulating layer 312 are formed. 321 can be configured. The process of forming the first surface second conductive layer 321 is the same as the process of forming the first surface first conductive layer 311, so the description thereof is omitted.

（第１面第２絶縁層の形成工程）
次に、図１３に示すように、第１面第１絶縁層３１２上及び第１面第２導電層３２１上に第１面第２絶縁層３２２を形成する。また、基板１２の第２面１４上及び第２面第１導電層４１１上に第２面第１絶縁層４１２を形成する。 (Step of Forming First Surface Second Insulating Layer)
Next, as shown in FIG. 13, a first surface second insulating layer 322 is formed on the first surface first insulating layer 312 and on the first surface second conductive layer 321 . Also, a second surface first insulating layer 412 is formed on the second surface 14 of the substrate 12 and on the second surface first conductive layer 411 .

例えば、まず、有機材料を含む感光層と、基材とを有する第２面側フィルムを、基板１２の第２面１４側に貼り付ける。続いて、第２面側フィルムに露光処理及び現像処理を施す。これによって、第２面側フィルムの感光層からなる第２面第１絶縁層４１２を、基板１２の第２面１４側に形成することができる。
その後、有機材料を含む感光層と、基材とを有する第１面側フィルムを、基板１２の第１面１３側に貼り付ける。続いて、図１４に示す開口３２３が形成されるように第１面側フィルムに露光処理及び現像処理を施す。これによって、第１面第２導電層３２１上の一部及び第１面第１導電層３１１上の一部に開口３２３が形成された、第１面側フィルムの感光層からなる第１面第２絶縁層３２２を得ることができる。 For example, first, a second surface film having a photosensitive layer containing an organic material and a substrate is attached to the second surface 14 side of the substrate 12 . Subsequently, the second surface side film is subjected to exposure processing and development processing. Thereby, the second surface first insulating layer 412 made of the photosensitive layer of the second surface film can be formed on the second surface 14 side of the substrate 12 .
After that, a first surface side film having a photosensitive layer containing an organic material and a substrate is attached to the first surface 13 side of the substrate 12 . Subsequently, exposure processing and development processing are performed on the first surface side film so that the openings 323 shown in FIG. 14 are formed. As a result, the first surface made of the photosensitive layer of the first surface side film in which the openings 323 are formed in a part on the first surface second conductive layer 321 and a part on the first surface first conductive layer 311 is formed. 2 insulating layers 322 can be obtained.

図１３に示すように、第１面第２絶縁層３２２の一部や第２面第１絶縁層４１２の一部を貫通孔２０の内部に設けることにより、貫通孔２０を埋める有機層２６を形成してもよい。例えば、上述の第２面側フィルムや第１面側フィルムを貫通孔２０の内部に押し込むことによって、第１面第２絶縁層３２２や第２面第１絶縁層４１２と同時に貫通孔２０の内部に有機層２６を形成することができる。なお、第２面第１絶縁層４１２や第１面第２絶縁層３２２とは別の工程で有機層２６を形成してもよい。 As shown in FIG. 13, by providing a portion of the first surface second insulating layer 322 and a portion of the second surface first insulating layer 412 inside the through hole 20, the organic layer 26 filling the through hole 20 is formed. may be formed. For example, by pushing the above-described second surface side film or first surface side film into the through hole 20, the inside of the through hole 20 can be filled at the same time as the first surface second insulating layer 322 and the second surface first insulating layer 412. An organic layer 26 can be formed on the substrate. It should be noted that the organic layer 26 may be formed in a separate process from the second surface first insulating layer 412 and the first surface second insulating layer 322 .

なお、第２面第１絶縁層４１２や第１面第２絶縁層３２２の形成方法が、フィルムを用いる方法に限られることはない。例えば、まず、ポリイミドなどの有機材料を含む液を、スピンコート法などによって塗布し、乾燥させることによって有機層を形成する。続いて、有機層に露光処理及び現像処理を施すことにより、第２面第１絶縁層４１２や第１面第２絶縁層３２２を形成することもできる。 The method of forming the second surface first insulating layer 412 and the first surface second insulating layer 322 is not limited to the method using a film. For example, first, a liquid containing an organic material such as polyimide is applied by spin coating or the like and dried to form an organic layer. Subsequently, the second surface first insulating layer 412 and the first surface second insulating layer 322 can be formed by subjecting the organic layer to exposure processing and development processing.

（第１面第３導電層の形成工程）
次に、図１４に示すように、第１面第１絶縁層３１２のうち第１面第２絶縁層３２２の開口３２３と重なる部分をエッチングして、第１面第１絶縁層３１２に開口を形成する。続いて、第１面第２絶縁層３２２の開口３２３及び第１面第１絶縁層３１２の開口を介して第１面第１導電層３１１又は第１面第２導電層３２１に接続される第１面第３導電層３３１を形成する。第１面第３導電層３３１を形成する工程は、第１面第１導電層３１１を形成する工程と同様であるので、説明を省略する。 (Step of forming third conductive layer on first surface)
Next, as shown in FIG. 14, the portion of the first surface first insulating layer 312 overlapping the opening 323 of the first surface second insulating layer 322 is etched to form an opening in the first surface first insulating layer 312 . Form. Subsequently, the first conductive layer 311 or the first conductive layer 321 is connected to the first conductive layer 311 or the second conductive layer 321 through the opening 323 of the first surface second insulating layer 322 and the opening of the first surface first insulating layer 312 . A first surface third conductive layer 331 is formed. The process of forming the first-surface third conductive layer 331 is the same as the process of forming the first-surface first conductive layer 311, and thus the description thereof is omitted.

（第１面第３絶縁層の形成工程）
その後、第１面第２絶縁層３２２上及び第１面第３導電層３３１上に部分的に第１面第３絶縁層３３２を形成する。これによって、図１に示す高周波部品１０を得ることができる。第１面第３絶縁層３３２を形成する方法は特には限定されない。第１面第２絶縁層３２２の場合と同様に、有機材料を含むフィルムや液を用いることによって、第１面第３絶縁層３３２を形成することができる。 (Step of forming third insulating layer on first surface)
After that, a first surface third insulating layer 332 is partially formed on the first surface second insulating layer 322 and the first surface third conductive layer 331 . Thereby, the high frequency component 10 shown in FIG. 1 can be obtained. A method for forming the first surface third insulating layer 332 is not particularly limited. As in the case of the first surface second insulating layer 322, the first surface third insulating layer 332 can be formed by using a film or liquid containing an organic material.

（高周波部品の作用）
以下、本実施の形態による高周波部品１０の作用について説明する。 (Action of high-frequency components)
The operation of the high-frequency component 10 according to this embodiment will be described below.

本実施の形態においては、高周波部品１０の基板１２がガラスを含む。ガラスは、従来の高周波部品の基板として用いられているシリコンに比べて、高い絶縁性を有する。このため、キャパシタ１５やインダクタ１６を通る高周波信号の一部が基板１２を通ってしまうことを抑制することができる。これにより、キャパシタ１５やインダクタ１６の帯域を高周波側に広げることができる。また、キャパシタ１５やインダクタ１６の耐電圧特性を改善することができる。 In this embodiment, substrate 12 of high frequency component 10 contains glass. Glass has higher insulating properties than silicon, which is used as a substrate for conventional high-frequency components. Therefore, it is possible to prevent part of the high-frequency signal passing through the capacitor 15 and the inductor 16 from passing through the substrate 12 . Thereby, the band of the capacitor 15 and the inductor 16 can be widened to the high frequency side. Also, the withstand voltage characteristics of the capacitor 15 and the inductor 16 can be improved.

また、本実施の形態においては、キャパシタ１５を構成する第１面第１絶縁層３１２が、６ＭＶ／ｃｍ以上の絶縁破壊電界を有する無機材料を含む。これにより、キャパシタ１５の耐電圧特性を更に改善することができる。また、第１面第１絶縁層３１２の厚みを７０ｎｍ以上にすることにより、キャパシタ１５の耐電圧特性を更に改善することができる。 Further, in the present embodiment, first surface first insulating layer 312 constituting capacitor 15 contains an inorganic material having a dielectric breakdown electric field of 6 MV/cm or more. Thereby, the withstand voltage characteristic of the capacitor 15 can be further improved. Further, by setting the thickness of the first surface first insulating layer 312 to 70 nm or more, the withstand voltage characteristics of the capacitor 15 can be further improved.

また、本実施の形態においては、第１面第２絶縁層３２２、第１面第３絶縁層３３２、第２面第１絶縁層４１２、有機層２６などに含まれる有機材料が、０．００３以下の誘電正接を有する。このため、キャパシタ１５やインダクタ１６を通る高周波信号の一部が基板１２を通ってしまうことを抑制することができる。これにより、キャパシタ１５やインダクタ１６の帯域を更に高周波側に広げることができる。 Further, in the present embodiment, the organic material contained in the first surface second insulating layer 322, the first surface third insulating layer 332, the second surface first insulating layer 412, the organic layer 26, etc. is 0.003 It has a loss tangent of Therefore, it is possible to prevent part of the high-frequency signal passing through the capacitor 15 and the inductor 16 from passing through the substrate 12 . Thereby, the band of the capacitor 15 and the inductor 16 can be further widened to the high frequency side.

また、本実施の形態においては、キャパシタ１５やインダクタ１６を構成する第１面第１導電層３１１、貫通電極２２、第２面第１導電層４１１が、５μｍ以上の厚みを有する。このため、半導体プロセスで作成される薄膜導電層を用いてキャパシタやインダクタを用いる場合に比べて、導電層で生じる損失を軽減することができる。この点でも、キャパシタ１５やインダクタ１６の帯域を高周波側に広げることができる。 Further, in the present embodiment, the first surface first conductive layer 311, the through electrode 22, and the second surface first conductive layer 411, which constitute the capacitor 15 and the inductor 16, have a thickness of 5 μm or more. Therefore, the loss generated in the conductive layer can be reduced as compared with the case of using a capacitor or an inductor using a thin film conductive layer created by a semiconductor process. In this respect as well, the band of the capacitor 15 and the inductor 16 can be widened to the high frequency side.

また、本実施の形態においては、第１面第１導電層３１１上に第１面第１絶縁層３１２を形成する工程を実施する前に、第１面第１導電層３１１の表面をＮＨ３プラズマに晒す表面処理工程を実施する。これにより、第１面第１導電層３１１と第１面第１絶縁層３１２との間の密着性を高めることができる。 Further, in the present embodiment, the surface of the first surface first conductive layer 311 is treated with NH 3 before performing the step of forming the first surface first insulating layer 312 on the first surface first conductive layer 311 . A surface treatment step of exposure to plasma is performed. Thereby, the adhesion between the first surface first conductive layer 311 and the first surface first insulating layer 312 can be enhanced.

なお、上述した実施の形態に対して様々な変更を加えることが可能である。以下、必要に応じて図面を参照しながら、変形例について説明する。以下の説明および以下の説明で用いる図面では、上述の実施の形態と同様に構成され得る部分について、上述の実施の形態における対応する部分に対して用いた符号と同一の符号を用いることとし、重複する説明を省略する。また、上述の実施の形態において得られる作用効果が変形例においても得られることが明らかである場合、その説明を省略することもある。 Various modifications can be made to the above-described embodiment. Modifications will be described below with reference to the drawings as necessary. In the following description and the drawings used in the following description, the same reference numerals as those used for the corresponding portions in the above-described embodiment are used for the parts that can be configured in the same manner as in the above-described embodiment, Duplicate explanations are omitted. Further, when it is clear that the effects obtained in the above-described embodiment can also be obtained in the modified example, the explanation thereof may be omitted.

（第１変形例）
図１５は、第１変形例に係る高周波部品１０を示す断面図である。図１５に示すように、高周波部品１０の基板１２の貫通孔２０は、基板１２の第１面１３及び第２面１４から基板１２の厚み方向の中央部に向かうにつれて幅が小さくなる形状を有していてもよい。 (First modification)
FIG. 15 is a cross-sectional view showing a high frequency component 10 according to a first modified example. As shown in FIG. 15, the through-hole 20 of the substrate 12 of the high-frequency component 10 has a shape whose width decreases from the first surface 13 and the second surface 14 of the substrate 12 toward the central portion of the substrate 12 in the thickness direction. You may have

（第２変形例）
上述の実施の形態においては、キャパシタ１５の第１面第１絶縁層３１２が第１面第１導電層３１１を部分的に覆う例について説明した。本変形例においては、キャパシタ１５の第１面第１絶縁層３１２が第１面第１導電層３１１を部分的に覆う場合の、第１面第１導電層３１１及び第１面第１絶縁層３１２の構造の一例について、図１７乃至図２３を参照して具体的に説明する。 (Second modification)
In the above embodiments, the example in which the first surface first insulating layer 312 of the capacitor 15 partially covers the first surface first conductive layer 311 has been described. In this modification, when the first surface first insulating layer 312 of the capacitor 15 partially covers the first surface first conductive layer 311, the first surface first conductive layer 311 and the first surface first insulating layer An example of the structure of 312 will be specifically described with reference to FIGS. 17 to 23. FIG.

図１７は、本変形例に係る高周波部品１０のキャパシタ１５を拡大して示す平面図である。また、図１８は、図１７のキャパシタ１５を線Ｂ－Ｂに沿って切断した場合の断面図である。まず、本変形例に係るキャパシタ１５の第１面第１導電層３１１について説明する。 FIG. 17 is a plan view showing an enlarged capacitor 15 of the high frequency component 10 according to this modification. 18 is a cross-sectional view of the capacitor 15 of FIG. 17 cut along the line BB. First, the first surface first conductive layer 311 of the capacitor 15 according to this modification will be described.

図１８に示す例において、キャパシタ１５の下部電極を構成する第１面第１導電層３１１は、シード層３６２及びめっき層３６３を含む。図示はしないが、本変形例においても、上述の実施の形態の場合と同様に、第１面第１導電層３１１が、シード層３６２と基板１２の第１面１３との間に位置するバリア層を更に含んでいてもよい。 In the example shown in FIG. 18 , the first surface first conductive layer 311 forming the lower electrode of the capacitor 15 includes a seed layer 362 and a plating layer 363 . Although not shown, in this modified example as well, the first surface first conductive layer 311 serves as a barrier layer positioned between the seed layer 362 and the first surface 13 of the substrate 12 as in the above-described embodiment. Further layers may be included.

以下の説明において、キャパシタ１５の第１面第１導電層３１１を構成する複数の層のうち、シード層３６２などの、基板１２側に位置する層のことを、下地層３６２とも称する。また、第１面第１導電層３１１を構成する複数の層のうち、めっき層３６３などの、下地層３６２よりも基板１２から遠い側に位置する層であり、且つ最も厚い層のことを、本体層３６３とも称する。第１面第１導電層３１１の側面３１１ｆは、下地層３６２の側面３６２ｆ及びめっき層３６３の側面３６３ｆを含む。なお「側面」とは、基板１２の第１面１３の面方向に沿って第１面第１導電層３１１を見た場合に視認される面である。 In the following description, among the layers forming the first surface first conductive layer 311 of the capacitor 15 , the layer positioned on the substrate 12 side, such as the seed layer 362 , is also referred to as an underlying layer 362 . Further, among the plurality of layers constituting the first surface first conductive layer 311, the thickest layer, such as the plating layer 363, which is positioned farther from the substrate 12 than the base layer 362 is Also referred to as body layer 363 . The side surface 311 f of the first surface first conductive layer 311 includes the side surface 362 f of the base layer 362 and the side surface 363 f of the plating layer 363 . The “side surface” is a surface that is visually recognized when the first surface first conductive layer 311 is viewed along the surface direction of the first surface 13 of the substrate 12 .

図１８に示すように、第１面第１導電層３１１の側面３１１ｆと基板１２の第１面１３との間に隙間３１１ｓが存在していてもよい。例えば、図１８に示すように、下地層３６２の側面３６２ｆは、本体層３６３の側面３６３ｆよりも内側に位置する。この結果、本体層３６３の側面３６３ｆと基板１２の第１面１３との間に、第１面第１導電層３１１が存在しない隙間３１１ｓが形成される。ここで「内側」とは、キャパシタ１５の断面図において、基板１２の第１面１３の面内方向におけるキャパシタ１５の中央位置に近い側を意味する。このような下地層３６２の側面３６２ｆは、後述するように、下地層３６２の側面３６２ｆがサイドエッチングされることによって生じる。 As shown in FIG. 18 , a gap 311 s may exist between the side surface 311 f of the first surface first conductive layer 311 and the first surface 13 of the substrate 12 . For example, as shown in FIG. 18, the side surface 362f of the base layer 362 is located inside the side surface 363f of the main layer 363. As shown in FIG. As a result, a gap 311 s in which the first surface first conductive layer 311 does not exist is formed between the side surface 363 f of the body layer 363 and the first surface 13 of the substrate 12 . Here, the “inner side” means the side near the center position of the capacitor 15 in the in-plane direction of the first surface 13 of the substrate 12 in the cross-sectional view of the capacitor 15 . Such a side surface 362f of the underlying layer 362 is produced by side-etching the side surface 362f of the underlying layer 362, as will be described later.

本体層３６３の側面３６３ｆのうち隙間３１１ｓに面する部分は、基板１２側に向かうにつれて内側に変位する形状を有する傾斜部を含んでいてもよい。傾斜部は、例えば、基板１２側に位置し、隙間３１１ｓに面する下側湾曲部３６３ｈである。下側湾曲部３６３ｈは、外側に凸となる形状を有する。なお「外側に凸」とは、下側湾曲部３６３ｈに外接する直線又は平面が本体層３６３と交わらないことを意味する。このような下側湾曲部３６３ｈは、後述するように、めっき処理によって本体層３６３を形成する際に本体層３６３に隣接するレジスト層３７の裾野部の形状に起因して生じる。また、側面３６３ｆは、基板１２から遠い側に位置する上側湾曲部３６３ｇを含んでいてもよい。なお、「下側」とは、基板１２の第１面１３の法線方向における本体層３６３の中央位置よりも基板１２に近い側を意味する。また、「上側」とは、基板１２の第１面１３の法線方向における本体層３６３の中央位置よりも基板１２から遠い側を意味する。 A portion of the side surface 363f of the body layer 363 facing the gap 311s may include an inclined portion having a shape that is displaced inward toward the substrate 12 side. The inclined portion is, for example, a lower curved portion 363h located on the substrate 12 side and facing the gap 311s. The lower curved portion 363h has an outwardly convex shape. Note that “outwardly convex” means that a straight line or plane circumscribing the lower curved portion 363 h does not intersect the main body layer 363 . Such a lower curved portion 363h is generated due to the shape of the skirt portion of the resist layer 37 adjacent to the body layer 363 when the body layer 363 is formed by plating, as will be described later. Also, the side surface 363f may include an upper curved portion 363g positioned farther from the substrate 12. As shown in FIG. The “lower side” means the side closer to the substrate 12 than the central position of the main body layer 363 in the normal direction of the first surface 13 of the substrate 12 . Further, the “upper side” means the side farther from the substrate 12 than the central position of the main body layer 363 in the normal direction of the first surface 13 of the substrate 12 .

続いて、キャパシタ１５の第１面第１絶縁層３１２について説明する。図１８に示すように、第１面第１絶縁層３１２は、第１面第１導電層３１１の上面３１１ａに位置する第１部分３１２ａに加えて、第１面第１導電層３１１の側面３１１ｆに位置する第２部分３１２ｂを更に含む。第２部分３１２ｂは、第１部分３１２ａに接続されている。言い換えると、第１面第１絶縁層３１２の第１部分３１２ａ及び第２部分３１２ｂは、第１面第１導電層３１１の側面３１１ｆの上側の端部を覆うように連続的に広がっている。 Next, the first surface first insulating layer 312 of the capacitor 15 will be described. As shown in FIG. 18 , the first surface first insulating layer 312 includes a first portion 312 a located on the top surface 311 a of the first surface first conductive layer 311 and a side surface 311 f of the first surface first conductive layer 311 . and a second portion 312b located at . The second portion 312b is connected to the first portion 312a. In other words, the first portion 312a and the second portion 312b of the first surface first insulating layer 312 extend continuously so as to cover the upper end of the side surface 311f of the first surface first conductive layer 311 .

図１８において、符号Ｔ１は、第１部分３１２ａの厚みを表し、符号Ｔ２は、第２部分３１２ｂの厚みを表す。第１部分３１２ａの厚みＴ１は、上述の実施の形態の場合と同様に、例えば５０ｎｍ以上且つ４００ｎｍ以下である。厚みＴ１は、例えば、基板１２の第１面１３の面内方向におけるキャパシタ１５の中央位置での第１部分３１２ａの厚みである。厚みＴ１は、第１部分３１２ａの厚みの最大値であってもよい。 In FIG. 18, reference T1 represents the thickness of the first portion 312a, and reference T2 represents the thickness of the second portion 312b. The thickness T1 of the first portion 312a is, for example, 50 nm or more and 400 nm or less, as in the above-described embodiments. The thickness T1 is, for example, the thickness of the first portion 312a at the center position of the capacitor 15 in the in-plane direction of the first surface 13 of the substrate 12 . The thickness T1 may be the maximum thickness of the first portion 312a.

好ましくは、第２部分３１２ｂの厚みＴ２は、第１部分３１２ａの厚みＴ１よりも小さい。また、好ましくは、第２部分３１２ｂの厚みＴ２は、第１部分３１２ａの厚みＴ１の１／４以上である。厚みＴ２は、例えば、第１面第１導電層３１１の厚み方向における中央位置での第２部分３１２ｂの厚みである。厚みＴ２は、第２部分３１２ｂの厚みの最大値であってもよい。 Preferably, the thickness T2 of the second portion 312b is less than the thickness T1 of the first portion 312a. Moreover, preferably, the thickness T2 of the second portion 312b is 1/4 or more of the thickness T1 of the first portion 312a. The thickness T2 is, for example, the thickness of the second portion 312b at the central position in the thickness direction of the first surface first conductive layer 311 . The thickness T2 may be the maximum thickness of the second portion 312b.

第１面第１絶縁層３１２の第２部分３１２ｂは、第１面第１導電層３１１の側面３１１ｆを完全には覆っていなくてもよい。例えば、第１面第１導電層３１１の側面３１１ｆの下側湾曲部３６３ｈなどの傾斜部が、少なくとも部分的に第１面第１絶縁層３１２から露出していてもよい。このような露出部は、後述するように、第１面第１絶縁層３１２が第１面第１導電層３１１の隙間３１１ｓに入り込み難いことに起因して生じる。 The second portion 312b of the first surface first insulating layer 312 does not have to completely cover the side surface 311f of the first surface first conductive layer 311 . For example, an inclined portion such as the lower curved portion 363 h of the side surface 311 f of the first surface first conductive layer 311 may be at least partially exposed from the first surface first insulating layer 312 . Such an exposed portion is caused because the first surface first insulating layer 312 is difficult to enter the gap 311s of the first surface first conductive layer 311, as will be described later.

図１８に示すように、第１面第１絶縁層３１２は、基板１２の第１面１３に位置する第３部分３１２ｃを更に含んでいてもよい。第３部分３１２ｃは、第２部分３１２ｂに接続されていない。すなわち、第３部分３１２ｃは、上述の露出部によって第２部分３１２ｂから断絶されている。第２部分３１２ｂと第３部分３１２ｃとの間には、上述の第１面第２絶縁層３２２などの、第１面第１導電層３１１以外の層や材料が存在していてもよい。 As shown in FIG. 18 , the first surface first insulating layer 312 may further include a third portion 312 c located on the first surface 13 of the substrate 12 . The third portion 312c is not connected to the second portion 312b. That is, the third portion 312c is separated from the second portion 312b by the exposed portion described above. A layer or material other than the first surface first conductive layer 311, such as the first surface second insulating layer 322 described above, may exist between the second portion 312b and the third portion 312c.

以下、本変形例に係る高周波部品１０のキャパシタ１５の製造方法について、図１９乃至図２２を参照して説明する。 A method of manufacturing the capacitor 15 of the high-frequency component 10 according to this modification will be described below with reference to FIGS. 19 to 22. FIG.

まず、上述の実施の形態の場合と同様に、基板１２を準備する。また、基板１２の第１面１３上、第２面１４及び側壁２１上に、例えば無電解めっきによって下地層３６２を形成する。続いて、下地層３６２上に部分的にレジスト層３７を形成する。その後、レジスト層３７を露光及び現像して、図１９に示すように、レジスト層３７に開口部３７ｃを形成する。レジスト層３７は、開口部３７ｃに面する側面３７ｆを含む。側面３７ｆは、下地層３６２に接する裾野部３７ｈを含んでいてもよい。裾野部３７ｈは、開口部３７ｃ側に突出するとともに、開口部３７ｃ側に向かうにつれて厚みが小さくなる形状を有する。このような裾野部３７ｈは、例えば、ネガ型の感光性樹脂をレジスト層３７として用いる場合に形成され得る。 First, the substrate 12 is prepared in the same manner as in the above-described embodiments. Further, a base layer 362 is formed on the first surface 13, the second surface 14 and the sidewalls 21 of the substrate 12 by electroless plating, for example. Subsequently, a resist layer 37 is partially formed on the underlying layer 362 . Thereafter, the resist layer 37 is exposed and developed to form openings 37c in the resist layer 37 as shown in FIG. The resist layer 37 includes a side surface 37f facing the opening 37c. The side surface 37 f may include a skirt portion 37 h contacting the underlying layer 362 . The skirt portion 37h protrudes toward the opening 37c and has a shape whose thickness decreases toward the opening 37c. Such a skirt portion 37 h can be formed, for example, when a negative photosensitive resin is used as the resist layer 37 .

次に、電解めっきによって、レジスト層３７によって覆われていない下地層３６２上に本体層３６３を形成する。続いて、図２０に示すように、レジスト層３７を除去する。本体層３６３は、レジスト層３７の側面３７ｆに対応する形状を有する側面３６３ｆと、レジスト層３７の裾野部３７ｈに対応する形状を有する下側湾曲部３６３ｈとを有する。 Next, a body layer 363 is formed on the base layer 362 not covered with the resist layer 37 by electroplating. Subsequently, as shown in FIG. 20, the resist layer 37 is removed. The body layer 363 has a side surface 363 f having a shape corresponding to the side surface 37 f of the resist layer 37 and a lower curved portion 363 h having a shape corresponding to the skirt portion 37 h of the resist layer 37 .

次に、図２１に示すように、下地層３６２のうちレジスト層３７によって覆われていた部分を、例えばウェットエッチングにより除去する。この際、下地層３６２がサイドエッチングされることにより、下地層３６２の側面３６２ｆが、本体層３６３の側面３６３ｆよりも内側に位置するようになる。また、下地層３６２に比べてエッチングレートは低いが、本体層３６３もエッチングされる。この結果、図２１に示すように、本体層３６３の側面３６３ｆの上側にも上側湾曲部３６３ｇが形成され得る。 Next, as shown in FIG. 21, the portion of the underlying layer 362 covered with the resist layer 37 is removed by wet etching, for example. At this time, the base layer 362 is side-etched, so that the side surface 362 f of the base layer 362 is located inside the side surface 363 f of the main layer 363 . Also, the main layer 363 is also etched, although the etching rate is lower than that of the underlying layer 362 . As a result, as shown in FIG. 21, an upper curved portion 363g can also be formed on the upper side of the side surface 363f of the body layer 363. As shown in FIG.

次に、上述の実施の形態の場合と同様に、第１面第１導電層３１１の表面をＮＨ３プラズマなどのプラズマに晒す表面処理工程を実施してもよい。次に、図２２に示すように、第１面第１導電層３１１上に第１面第１絶縁層３１２を形成する。例えば、プラズマＣＶＤやスパッタリングなどの成膜法によって第１面第１絶縁層３１２を形成する。この場合、図２２に示すように、第１面第１導電層３１１の上面３１１ａだけでなく側面３１１ｆにも第１面第１絶縁層３１２が形成され得る。例えば、上述の第２部分３１２ｂが本体層３６３の側面に形成される。 Next, as in the case of the above embodiments, a surface treatment step of exposing the surface of the first surface first conductive layer 311 to plasma such as NH 3 plasma may be performed. Next, as shown in FIG. 22, a first surface first insulating layer 312 is formed on the first surface first conductive layer 311 . For example, the first surface first insulating layer 312 is formed by a film formation method such as plasma CVD or sputtering. In this case, as shown in FIG. 22, the first surface first insulating layer 312 can be formed not only on the top surface 311a of the first surface first conductive layer 311 but also on the side surface 311f. For example, the second portion 312 b described above is formed on the side surface of the body layer 363 .

ところで、上述のように、下地層３６２の側面３６２ｆは、本体層３６３の側面３６３ｆよりも内側に位置している。このため、第１面第１導電層３１１の側面３１１ｆと基板１２の第１面１３との間には隙間３１１ｓが存在している。成膜工程の際、隙間３１１ｓには第１面第１絶縁層３１２を構成する材料が入り込み難い。このため、下地層３６２の側面３６２ｆや本体層３６３の下側湾曲部３６３ｈには、第１面第１絶縁層３１２が形成され難い。この結果、図２２に示すように、下地層３６２の側面３６２ｆや本体層３６３の下側湾曲部３６３ｈが、少なくとも部分的に第１面第１絶縁層３１２から露出するようになる。また、基板１２の第１面１３に形成される第１面第１絶縁層３１２の第３部分３１２ｃが、第１面第１導電層３１１の側面３１１ｆに形成される第１面第１絶縁層３１２の第２部分３１２ｂとは分断されることになる。 By the way, as described above, the side surface 362f of the base layer 362 is located inside the side surface 363f of the main layer 363. As shown in FIG. Therefore, a gap 311 s exists between the side surface 311 f of the first surface first conductive layer 311 and the first surface 13 of the substrate 12 . During the film formation process, it is difficult for the material forming the first surface first insulating layer 312 to enter the gap 311s. Therefore, it is difficult for the first surface first insulating layer 312 to be formed on the side surface 362 f of the underlying layer 362 and the lower curved portion 363 h of the main body layer 363 . As a result, as shown in FIG. 22, the side surface 362f of the underlying layer 362 and the lower curved portion 363h of the main layer 363 are at least partially exposed from the first surface first insulating layer 312. As shown in FIG. Also, the third portion 312c of the first surface first insulating layer 312 formed on the first surface 13 of the substrate 12 is the first surface first insulating layer formed on the side surface 311f of the first surface first conductive layer 311. 312 is separated from the second portion 312b.

その後、第１面第１絶縁層３１２の第１部分３１２ａ上に第１面第２導電層３２１を形成する。これにより、図１８に示すキャパシタ１５を得ることができる。 After that, a first surface second conductive layer 321 is formed on the first portion 312 a of the first surface first insulating layer 312 . Thereby, the capacitor 15 shown in FIG. 18 can be obtained.

（本変形例に係る高周波部品の効果）
本変形例に係る高周波部品１０のキャパシタ１５においては、第１面第１導電層３１１の上面３１１ａだけでなく側面３１１ｆにも第１面第１絶縁層３１２が設けられている。このため、製造公差などに起因して第１面第１導電層３１１に対する第１面第２導電層３２１の位置がずれた場合であっても、第１面第２導電層３２１が第１面第１導電層３１１の側面３１１ｆに接触してしまうことを抑制することができる。このことにより、第１面第１導電層３１１と第１面第２導電層３２１とが導通するという不具合が生じることを抑制することができる。 (Effect of high-frequency component according to this modified example)
In the capacitor 15 of the high frequency component 10 according to this modified example, the first surface first insulating layer 312 is provided not only on the upper surface 311a of the first surface first conductive layer 311 but also on the side surfaces 311f. Therefore, even if the position of the first surface second conductive layer 321 with respect to the first surface first conductive layer 311 is displaced due to manufacturing tolerances or the like, the first surface second conductive layer 321 Contact with the side surface 311f of the first conductive layer 311 can be suppressed. As a result, it is possible to suppress the occurrence of the problem that the first surface first conductive layer 311 and the first surface second conductive layer 321 are electrically connected.

また、本変形例に係るキャパシタ１５においては、第１面第１導電層３１１の側面３１１ｆに位置する第１面第１絶縁層３１２の第２部分３１２ｂと、基板１２の第１面１３に位置する第１面第１絶縁層３１２の第３部分３１２ｃとが断絶されている。これにより得られる効果について、図２３を参照して説明する。 Further, in the capacitor 15 according to this modification, the second portion 312 b of the first surface first insulating layer 312 located on the side surface 311 f of the first surface first conductive layer 311 and the second portion 312 b located on the first surface 13 of the substrate 12 The third portion 312c of the first surface first insulating layer 312 is disconnected. The effect obtained by this will be described with reference to FIG.

図２３は、基板１２の第１面１３の面内方向において複数の、例えば２つのキャパシタ１５が隣接する場合を示す断面図である。この場合、仮に第１面第１絶縁層３１２の第２部分３１２ｂと第３部分３１２ｃとが接続されていると、一方のキャパシタ１５と他方のキャパシタ１５とが電気的に影響を及ぼしあう可能性がある。この結果、例えば、キャパシタ１５の静電容量の値が設計値からずれてしまうことが考えられる。 FIG. 23 is a cross-sectional view showing a case where a plurality of, for example, two capacitors 15 are adjacent in the in-plane direction of the first surface 13 of the substrate 12. As shown in FIG. In this case, if the second portion 312b and the third portion 312c of the first surface first insulating layer 312 were connected, there is a possibility that one capacitor 15 and the other capacitor 15 would electrically affect each other. There is As a result, for example, the value of the capacitance of the capacitor 15 may deviate from the designed value.

これに対して、本変形例によれば、第１面第１絶縁層３１２の第２部分３１２ｂと第３部分３１２ｃとが断絶されているので、一方のキャパシタ１５と他方のキャパシタ１５とが電気的に影響を及ぼしあうことを抑制することができる。これにより、例えば、キャパシタ１５の静電容量の値が設計値からずれてしまうことを抑制することができる。 On the other hand, according to this modification, the second portion 312b and the third portion 312c of the first surface first insulating layer 312 are disconnected, so that the capacitor 15 on one side and the capacitor 15 on the other side are electrically connected. can be suppressed. As a result, for example, it is possible to prevent the value of the capacitance of the capacitor 15 from deviating from the design value.

次に、本開示の形態を実施例により更に具体的に説明するが、本開示の形態はその要旨を超えない限り、以下の実施例の記載に限定されるものではない。 Next, the embodiments of the present disclosure will be described in more detail with reference to examples, but the embodiments of the present disclosure are not limited to the description of the following examples as long as they do not exceed the gist thereof.

（無機材料の評価）
無機材料を含む絶縁層の絶縁破壊電界を、ＪＩＳ Ｃ ２１１０－１：２０１０に準拠して測定した。無機材料を含む絶縁層としては、下記の４種類を準備した。測定器としては、ケースレー製のピコアンメーターを用いた。
・プラズマＣＶＤ法によって作製した、厚み２００ｎｍのＳｉＮの層
・スパッタリング法によって作製した、厚み２００ｎｍのＳｉＮの層
・スパッタリング法によって作製した、厚２００ｎｍのＳｉＯ２の層
・スパッタリング法によって作製した、厚み１００ｎｍのＡｌＯｘの層（ｘは２～４） (Evaluation of inorganic materials)
The dielectric breakdown field of the insulating layer containing the inorganic material was measured according to JIS C 2110-1:2010. As the insulating layer containing the inorganic material, the following four types were prepared. As a measuring instrument, a Keithley picoammeter was used.
A layer of SiN with a thickness of 200 nm, made by a plasma CVD method A layer of SiN, made by a sputtering method, with a thickness of 200 nm A layer of SiO2 , made by a sputtering method, with a thickness of 200 nm A layer of AlO x (where x is 2 to 4)

また、上記４種類の絶縁層に２０Ｖの直流電圧を印加した場合に流れる電流、すなわち漏れ電流を測定した。測定器としては、ケースレー製のピコアンメーターを用いた。 In addition, the current flowing when a DC voltage of 20 V was applied to the four types of insulating layers, that is, the leakage current was measured. As a measuring instrument, a Keithley picoammeter was used.

表１に、絶縁破壊電界及び漏れ電流の測定結果を示す。プラズマＣＶＤ法によって形成された層を絶縁層として用いることにより、６ＭＶ／ｃｍ以上の絶縁破壊電界及び１×１０１２Ａ以下の漏れ電流を実現することができた。

Figure 0007211445000001
Table 1 shows the measurement results of dielectric breakdown electric field and leakage current. By using the layer formed by the plasma CVD method as the insulating layer, a breakdown electric field of 6 MV/cm or more and a leakage current of 1×10 12 A or less could be realized.
Figure 0007211445000001

（有機材料の評価）
有機材料を含む絶縁層の誘電正接及び比誘電率を、ＪＩＳ Ｃ ２１３８：２００７に準拠して測定した。有機材料を含む絶縁層としては、下記の５種類を準備した。測定器としては、キーサイト製のＰＮＡ Ｎｅｔｗｏｒｋ ａｎａｌｙｓｅｒを用いた。
・フィルムタイプのポリイミド 品名：ＬＰＡ１５２６ 厚み：１９μｍ
・塗布タイプのポリイミド 品名：ＨＤ７０１０ 厚み：９μｍ
・塗布タイプのポリイミド 品名：ＰＮ２０１０ 厚み：９μｍ
・フィルムタイプのエポキシ 品名：ＰＦＲ 厚み：２０μｍ
・フィルムタイプのエポキシ 品名：ＦＺ 厚み：２０μｍ (Evaluation of organic materials)
The dielectric loss tangent and dielectric constant of the insulating layer containing the organic material were measured according to JIS C 2138:2007. As the insulating layer containing an organic material, the following five types were prepared. As a measuring instrument, PNA Network analyzer manufactured by Keysight was used.
・Film type polyimide Product name: LPA1526 Thickness: 19 μm
・Coating type polyimide Product name: HD7010 Thickness: 9 μm
・Coating type polyimide Product name: PN2010 Thickness: 9 μm
・Film type epoxy Product name: PFR Thickness: 20 μm
・Film type epoxy Product name: FZ Thickness: 20 μm

また、上記５種類の絶縁層の、５ＧＨｚにおける透過損失を測定した。測定器としては、キーサイト製のＰＮＡ Ｎｅｔｗｏｒｋ ａｎａｌｙｓｅｒを用いた。 In addition, transmission loss at 5 GHz was measured for the above five types of insulating layers. As a measuring instrument, PNA Network analyzer manufactured by Keysight was used.

表２に、誘電正接、比誘電率、及び透過損失の測定結果を示す。ポリイミドによって形成された層を絶縁層として用いることにより、０．００３以下の誘電正接、３．４以下の誘電率、及び０．０７以下の透過損失を実現することができた。

Figure 0007211445000002
Table 2 shows the measurement results of dielectric loss tangent, relative permittivity, and transmission loss. By using a layer formed of polyimide as an insulating layer, a dielectric loss tangent of 0.003 or less, a dielectric constant of 3.4 or less, and a transmission loss of 0.07 or less could be achieved.
Figure 0007211445000002

１０ 高周波部品
１２ 基板
１３ 第１面
１４ 第２面
１５ キャパシタ
１６ インダクタ
２０ 貫通孔
２１ 側壁
２２ 貫通電極
２６ 有機層
３０ 第１配線構造部
３１ 第１面第１配線層
３１１ 第１面第１導電層
３１１ａ 上面
３１１ｆ 側面
３１２ 第１面第１絶縁層
３１２ａ 第１部分
３１２ｂ 第２部分
３１２ｃ 第３部分
３２ 第１面第２配線層
３２１ 第１面第２導電層
３２２ 第１面第２絶縁層
３３ 第１面第３配線層
３３１ 第１面第３導電層
３３２ 第１面第３絶縁層
３６１ 密着層
３６２ シード層（下地層）
３６２ｆ 側面
３６３ めっき層（本体層）
３６３ｆ 側面
３６３ｇ 上側湾曲部
３６３ｈ 下側湾曲部
４０ 第２配線構造部
４１ 第２面第１配線層
４１１ 第２面第１導電層
４１２ 第２面第１絶縁層 10 High frequency component 12 Substrate 13 First surface 14 Second surface 15 Capacitor 16 Inductor 20 Through hole 21 Side wall 22 Through electrode 26 Organic layer 30 First wiring structure 31 First surface first wiring layer 311 First surface first conductive layer 311a upper surface 311f side surface 312 first surface first insulating layer 312a first portion 312b second portion 312c third portion 32 first surface second wiring layer 321 first surface second conductive layer 322 first surface second insulating layer 33 third First surface third wiring layer 331 First surface third conductive layer 332 First surface third insulating layer 361 Adhesion layer 362 Seed layer (base layer)
362f side 363 plating layer (body layer)
363f side surface 363g upper curved portion 363h lower curved portion 40 second wiring structure portion 41 second surface first wiring layer 411 second surface first conductive layer 412 second surface first insulating layer

Claims (19)

第１側に位置する第１面及び前記第１側とは反対の第２側に位置する第２面を含み、ガラスを有する基板と、
前記基板の前記第１面に位置する第１面第１導電層と、
前記第１面第１導電層上に位置する第１面第１絶縁層と、
前記第１面第１絶縁層上に位置する第１面第２導電層と、
前記第１面第１絶縁層上及び前記第１面第２導電層上に位置する第１面第２絶縁層と、を備え、
前記第１面第２導電層に重なる前記第１面第１絶縁層は、前記第１面第１導電層及び前記第１面第２導電層とともにキャパシタを構成し、
前記第１面第１絶縁層は、６ＭＶ／ｃｍ以上の絶縁破壊電界を有する無機材料を含み、
前記第１面第２絶縁層は、前記第１面第２導電層に重ならない前記第１面第１絶縁層の上に位置し、
前記第１面第２絶縁層は、有機材料を含み、
前記第１面第１絶縁層は、前記第１面第１導電層の上面に位置する第１部分と、前記第１部分に接続され、前記第１面第１導電層の側面に位置する第２部分と、を含み、
前記第２部分の厚みは、前記第１部分の厚みよりも小さく、且つ前記第１部分の厚みの１／４以上である、高周波部品。 a substrate comprising a glass, comprising a first side located on a first side and a second side located on a second side opposite said first side;
a first surface first conductive layer located on the first surface of the substrate;
a first surface first insulating layer located on the first surface first conductive layer;
a first surface second conductive layer located on the first surface first insulating layer;
a first surface second insulating layer positioned on the first surface first insulating layer and on the first surface second conductive layer;
the first surface first insulating layer overlapping the first surface second conductive layer forms a capacitor together with the first surface first conductive layer and the first surface second conductive layer;
The first surface first insulating layer contains an inorganic material having a dielectric breakdown field of 6 MV/cm or more,
the first surface second insulating layer is located on the first surface first insulating layer not overlapping the first surface second conductive layer;
the first surface second insulating layer includes an organic material ;
The first surface first insulating layer has a first portion located on the upper surface of the first surface first conductive layer and a first portion connected to the first portion and located on a side surface of the first surface first conductive layer. 2 parts and
The high-frequency component , wherein the thickness of the second portion is smaller than the thickness of the first portion and is 1/4 or more of the thickness of the first portion . 第１側に位置する第１面及び前記第１側とは反対の第２側に位置する第２面を含み、ガラスを有する基板と、
前記基板の前記第１面に位置する第１面第１導電層と、
前記第１面第１導電層上に位置する第１面第１絶縁層と、
前記第１面第１絶縁層上に位置する第１面第２導電層と、
前記第１面第１絶縁層上及び前記第１面第２導電層上に位置する第１面第２絶縁層と、を備え、
前記第１面第２導電層に重なる前記第１面第１絶縁層は、前記第１面第１導電層及び前記第１面第２導電層とともにキャパシタを構成し、
前記第１面第１絶縁層は、６ＭＶ／ｃｍ以上の絶縁破壊電界を有する無機材料を含み、
前記第１面第２絶縁層は、前記第１面第２導電層に重ならない前記第１面第１絶縁層の上に位置し、
前記第１面第２絶縁層は、有機材料を含み、
前記第１面第１絶縁層は、前記第１面第１導電層の上面に位置する第１部分と、前記第１部分に接続され、前記第１面第１導電層の側面に位置する第２部分と、を含み、
前記第１面第１導電層の側面は、前記基板の前記第１面側に向かうにつれて内側に変位する形状を有する傾斜部を含み、
前記傾斜部は、少なくとも部分的に前記第１面第１絶縁層から露出している、高周波部品。 a substrate comprising a glass, comprising a first side located on a first side and a second side located on a second side opposite said first side;
a first surface first conductive layer located on the first surface of the substrate;
a first surface first insulating layer located on the first surface first conductive layer;
a first surface second conductive layer located on the first surface first insulating layer;
a first surface second insulating layer positioned on the first surface first insulating layer and on the first surface second conductive layer;
the first surface first insulating layer overlapping the first surface second conductive layer forms a capacitor together with the first surface first conductive layer and the first surface second conductive layer;
The first surface first insulating layer contains an inorganic material having a dielectric breakdown field of 6 MV/cm or more,
the first surface second insulating layer is located on the first surface first insulating layer not overlapping the first surface second conductive layer;
the first surface second insulating layer includes an organic material ;
The first surface first insulating layer has a first portion located on the upper surface of the first surface first conductive layer and a first portion connected to the first portion and located on a side surface of the first surface first conductive layer. 2 parts and
the side surface of the first surface first conductive layer includes an inclined portion having a shape that is displaced inward toward the first surface side of the substrate;
The high-frequency component , wherein the inclined portion is at least partially exposed from the first surface first insulating layer . 前記第１面第１絶縁層の前記無機材料の漏れ電流は、１×１０－１２Ａ以下である、請求項１又は２に記載の高周波部品。 3. The high-frequency component according to claim 1, wherein a leakage current of said inorganic material of said first surface first insulating layer is 1×10 −12 A or less. 前記第１面第１絶縁層の前記無機材料は、珪素窒化物を含む、請求項１乃至３のいずれか一項に記載の高周波部品。 4. The high frequency component according to claim 1, wherein said inorganic material of said first surface first insulating layer includes silicon nitride. 前記第１面第１絶縁層の厚みは、５０ｎｍ以上且つ４００ｎｍ以下である、請求項１乃至４のいずれか一項に記載の高周波部品。 5. The high-frequency component according to claim 1, wherein said first surface first insulating layer has a thickness of 50 nm or more and 400 nm or less. 前記第１面第１導電層の厚みは、５μｍ以上且つ２０μｍ以下である、請求項１乃至５のいずれか一項に記載の高周波部品。 6. The high frequency component according to claim 1, wherein said first surface first conductive layer has a thickness of 5 [mu]m or more and 20 [mu]m or less. 前記第１面第２絶縁層の前記有機材料は、０．００３以下の誘電正接を有する、請求項１乃至６のいずれか一項に記載の高周波部品。 7. The high frequency component according to claim 1 , wherein said organic material of said first surface second insulating layer has a dielectric loss tangent of 0.003 or less. 前記基板には貫通孔が設けられており、
前記高周波部品は、前記キャパシタに電気的に接続されたインダクタを更に備え、
前記インダクタは、前記第１面第１導電層と、前記第１面第１導電層に接続されるとともに前記貫通孔の側壁に沿って広がる貫通電極と、前記貫通電極に接続されるとともに前記基板の前記第２面に位置する第２面第１導電層と、を有する、請求項１乃至７のいずれか一項に記載の高周波部品。 The substrate is provided with a through hole,
The high-frequency component further comprises an inductor electrically connected to the capacitor,
The inductor includes: a first surface first conductive layer; a through electrode connected to the first surface first conductive layer and extending along a sidewall of the through hole; 8. The high-frequency component according to any one of claims 1 to 7 , further comprising a second surface first conductive layer located on said second surface of said second surface. 前記貫通電極よりも前記貫通孔の中心側に位置し、０．００３以下の誘電正接を有する有機材料を含む有機層を更に備える、請求項８に記載の高周波部品。 9. The high-frequency component according to claim 8 , further comprising an organic layer positioned closer to the center of said through hole than said through electrode and containing an organic material having a dielectric loss tangent of 0.003 or less. 第１側に位置する第１面及び前記第１側とは反対の第２側に位置する第２面を含み、ガラスを有する基板を準備する工程と、
前記基板の前記第１面に第１面第１導電層を形成する工程と、
前記第１面第１導電層上に、６ＭＶ／ｃｍ以上の絶縁破壊電界を有する無機材料を含む第１面第１絶縁層を形成する工程と、
前記第１面第１絶縁層上に第１面第２導電層を形成する工程と、
前記第１面第１絶縁層上及び前記第１面第２導電層上に第１面第２絶縁層を形成する工程と、を備え、
前記第１面第１導電層、前記第１面第１絶縁層及び前記第１面第２導電層がキャパシタを構成し、
前記第１面第２絶縁層は、前記第１面第２導電層に重ならない前記第１面第１絶縁層の上に位置し、
前記第１面第２絶縁層は、有機材料を含み、
前記第１面第１絶縁層は、前記第１面第１導電層の上面に位置する第１部分と、前記第１部分に接続され、前記第１面第１導電層の側面に位置する第２部分と、を含み、
前記第２部分の厚みは、前記第１部分の厚みよりも小さく、且つ前記第１部分の厚みの１／４以上である、高周波部品の製造方法。 providing a substrate comprising glass, comprising a first surface located on a first side and a second surface located on a second side opposite said first side;
forming a first surface first conductive layer on the first surface of the substrate;
forming a first surface first insulating layer containing an inorganic material having a breakdown electric field of 6 MV/cm or more on the first surface first conductive layer;
forming a first surface second conductive layer on the first surface first insulating layer;
forming a first surface second insulating layer on the first surface first insulating layer and on the first surface second conductive layer;
the first surface first conductive layer, the first surface first insulating layer and the first surface second conductive layer constitute a capacitor;
the first surface second insulating layer is located on the first surface first insulating layer not overlapping the first surface second conductive layer;
the first surface second insulating layer includes an organic material ;
The first surface first insulating layer has a first portion located on the upper surface of the first surface first conductive layer and a first portion connected to the first portion and located on a side surface of the first surface first conductive layer. 2 parts and
The method of manufacturing a high-frequency component , wherein the thickness of the second portion is smaller than the thickness of the first portion and is 1/4 or more of the thickness of the first portion . 第１側に位置する第１面及び前記第１側とは反対の第２側に位置する第２面を含み、ガラスを有する基板を準備する工程と、
前記基板の前記第１面に第１面第１導電層を形成する工程と、
前記第１面第１導電層上に、６ＭＶ／ｃｍ以上の絶縁破壊電界を有する無機材料を含む第１面第１絶縁層を形成する工程と、
前記第１面第１絶縁層上に第１面第２導電層を形成する工程と、
前記第１面第１絶縁層上及び前記第１面第２導電層上に第１面第２絶縁層を形成する工程と、を備え、
前記第１面第１導電層、前記第１面第１絶縁層及び前記第１面第２導電層がキャパシタを構成し、
前記第１面第２絶縁層は、前記第１面第２導電層に重ならない前記第１面第１絶縁層の上に位置し、
前記第１面第２絶縁層は、有機材料を含み、
前記第１面第１絶縁層は、前記第１面第１導電層の上面に位置する第１部分と、前記第１部分に接続され、前記第１面第１導電層の側面に位置する第２部分と、を含み、
前記第１面第１導電層の側面は、前記基板の前記第１面側に向かうにつれて内側に変位する形状を有する傾斜部を含み、
前記傾斜部は、少なくとも部分的に前記第１面第１絶縁層から露出している、高周波部品の製造方法。 providing a substrate comprising glass, comprising a first surface located on a first side and a second surface located on a second side opposite said first side;
forming a first surface first conductive layer on the first surface of the substrate;
forming a first surface first insulating layer containing an inorganic material having a breakdown electric field of 6 MV/cm or more on the first surface first conductive layer;
forming a first surface second conductive layer on the first surface first insulating layer;
forming a first surface second insulating layer on the first surface first insulating layer and on the first surface second conductive layer;
the first surface first conductive layer, the first surface first insulating layer and the first surface second conductive layer constitute a capacitor;
the first surface second insulating layer is located on the first surface first insulating layer not overlapping the first surface second conductive layer;
the first surface second insulating layer includes an organic material ;
The first surface first insulating layer has a first portion located on the upper surface of the first surface first conductive layer, and a first portion connected to the first portion and located on a side surface of the first surface first conductive layer. 2 parts and
the side surface of the first surface first conductive layer includes an inclined portion having a shape that is displaced inward toward the first surface side of the substrate;
The method of manufacturing a high-frequency component , wherein the inclined portion is at least partially exposed from the first surface first insulating layer . 前記第１面第１絶縁層の前記無機材料の漏れ電流は、１×１０－１２Ａ以下である、請求項１０又は１１に記載の高周波部品の製造方法。 12. The method of manufacturing a high-frequency component according to claim 10 , wherein a leakage current of said inorganic material of said first surface first insulating layer is 1×10 −12 A or less. 前記第１面第１絶縁層の前記無機材料は、珪素窒化物を含む、請求項１０乃至１２のいずれか一項に記載の高周波部品の製造方法。 13. The method of manufacturing a high frequency component according to claim 10 , wherein said inorganic material of said first surface first insulating layer includes silicon nitride. 前記第１面第１絶縁層の厚みは、５０ｎｍ以上且つ４００ｎｍ以下である、請求項１０乃至１３のいずれか一項に記載の高周波部品の製造方法。 14. The method of manufacturing a high-frequency component according to claim 10 , wherein said first surface first insulating layer has a thickness of 50 nm or more and 400 nm or less. 前記第１面第１導電層の厚みは、５μｍ以上且つ２０μｍ以下である、請求項１０乃至１４のいずれか一項に記載の高周波部品の製造方法。 15. The method of manufacturing a high-frequency component according to claim 10 , wherein said first surface first conductive layer has a thickness of 5 [mu]m or more and 20 [mu] m or less. 前記第１面第１絶縁層を形成する工程に先行して前記第１面第１導電層の表面をＮＨ３プラズマに晒す表面処理工程を更に備える、請求項１０乃至１５のいずれか一項に記載の高周波部品の製造方法。 16. The method according to any one of claims 10 to 15 , further comprising a surface treatment step of exposing the surface of said first surface first conductive layer to NH3 plasma prior to the step of forming said first surface first insulating layer. A method for manufacturing the described high frequency component. 前記第１面第２絶縁層の前記有機材料は、０．００３以下の誘電正接を有する、請求項１０乃至１６のいずれか一項に記載の高周波部品の製造方法。 17. The method of manufacturing a high frequency component according to claim 10 , wherein said organic material of said first surface second insulating layer has a dielectric loss tangent of 0.003 or less. 前記基板には貫通孔が設けられており、
前記高周波部品の製造方法は、前記第１面第１導電層に接続されるとともに前記貫通孔の側壁に沿って広がる貫通電極を形成する工程と、前記貫通電極に接続されるとともに前記基板の前記第２面に位置する第２面第１導電層を形成する工程と、を更に備え、
前記第１面第１導電層、前記貫通電極及び前記第２面第１導電層がインダクタを構成する、請求項１０乃至１７のいずれか一項に記載の高周波部品の製造方法。 The substrate is provided with a through hole,
The method for manufacturing the high-frequency component includes the steps of: forming a through electrode connected to the first surface first conductive layer and extending along the side wall of the through hole; forming a second surface first conductive layer located on the second surface;
18. The method of manufacturing a high-frequency component according to claim 10 , wherein said first surface first conductive layer, said through electrode and said second surface first conductive layer constitute an inductor. 前記貫通電極よりも前記貫通孔の中心側に位置し、０．００３以下の誘電正接を有する有機材料を含む有機層を形成する工程を更に備える、請求項１８に記載の高周波部品の製造方法。 19. The method of manufacturing a high-frequency component according to claim 18 , further comprising the step of forming an organic layer located closer to the center of said through-hole than said through-electrode and containing an organic material having a dielectric loss tangent of 0.003 or less.
JP2021047843A 2016-10-24 2021-03-22 High frequency component and its manufacturing method Active JP7211445B2 (en)