JP7125631B2 - Light-emitting device and lamp equipped with the same - Google Patents

Light-emitting device and lamp equipped with the same Download PDF

Info

Publication number
JP7125631B2
JP7125631B2 JP2021011944A JP2021011944A JP7125631B2 JP 7125631 B2 JP7125631 B2 JP 7125631B2 JP 2021011944 A JP2021011944 A JP 2021011944A JP 2021011944 A JP2021011944 A JP 2021011944A JP 7125631 B2 JP7125631 B2 JP 7125631B2
Authority
JP
Japan
Prior art keywords
phosphor
light
range
emitting device
less
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2021011944A
Other languages
Japanese (ja)
Other versions
JP2021158345A (en
Inventor
篤史 板東
圭吾 西田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nichia Corp
Original Assignee
Nichia Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nichia Corp filed Critical Nichia Corp
Priority to CN202180022520.0A priority Critical patent/CN115315821A/en
Priority to EP21774206.3A priority patent/EP4131433A4/en
Priority to PCT/JP2021/005874 priority patent/WO2021192743A1/en
Priority to BR112022018956A priority patent/BR112022018956A2/en
Priority to US17/907,403 priority patent/US20230151273A1/en
Publication of JP2021158345A publication Critical patent/JP2021158345A/en
Priority to JP2022121848A priority patent/JP7311819B2/en
Application granted granted Critical
Publication of JP7125631B2 publication Critical patent/JP7125631B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本開示は、発光装置及びそれを備えた灯具に関する。 TECHNICAL FIELD The present disclosure relates to a light emitting device and a lamp having the same.

発光ダイオード（以下、「ＬＥＤ」とも記載する。）と呼ばれる発光素子を用いる発光装置が注目されている。例えば、青色に発光するＬＥＤと黄色発光の蛍光体とを組み合わせた発光装置である。これは、青色ＬＥＤの青色光と、その光によって励起された蛍光体の黄色発光とが混色することにより白色光を放出する発光装置である。 Light-emitting devices using light-emitting elements called light-emitting diodes (hereinafter also referred to as "LEDs") have attracted attention. For example, it is a light-emitting device that combines an LED that emits blue light and a phosphor that emits yellow light. This is a light-emitting device that emits white light by mixing blue light from a blue LED and yellow light emitted from a phosphor excited by the light.

青色光を発する発光素子と黄色に発光する蛍光体とを組み合わせた発光装置は、可視光領域における放射強度が強いので、発光効率が高い。さらに、照射物の色の見え方（演色性）の指数である平均演色評価指数が高い発光装置が求められる場合がある。 A light-emitting device that combines a light-emitting element that emits blue light and a phosphor that emits yellow light has a high radiant intensity in the visible light region, and thus has high luminous efficiency. Furthermore, there are cases where a light-emitting device with a high general color rendering index, which is an index of how colors appear (color rendering properties) of an illuminated object, is required.

光源の演色性の評価手順はＪＩＳ Ｚ８７２６によって、所定の反射率特性を有する試験色（Ｒ１からＲ１５）を、試験光源と基準光源とでそれぞれ測色した場合の色差ΔＥｉ（ｉは１から１５の整数）がどうなるかを数値計算して算出すると定められている。ここで演色評価数Ｒｉ（ｉは１から１５の整数）の上限は１００である。つまり、試験光源とそれに対応する色温度の基準光源の色差が小さいほど、演色性評価値は１００に近づき高くなる。 In accordance with JIS Z8726, the color rendering property evaluation procedure of a light source is the color difference ΔEi (i is from 1 to 15) when test colors (R1 to R15) having predetermined reflectance characteristics are measured with a test light source and a reference light source. Integer) is calculated by numerical calculation. Here, the upper limit of the color rendering index Ri (i is an integer from 1 to 15) is 100. That is, the smaller the color difference between the test light source and the corresponding reference light source of color temperature, the higher the color rendering evaluation value approaches 100.

上記に関連して、青色に発光するＬＥＤと、黄色から緑色に発光する２種類の蛍光体とを用いる発光装置が提案され、高度な色の再現性が達成できるとされている（例えば、特許文献１及び２参照）。 In relation to the above, a light-emitting device using an LED that emits blue light and two types of phosphors that emit yellow to green light has been proposed, and is said to be able to achieve high color reproducibility (for example, patent References 1 and 2).

特表２００３－５３５４７７号公報Japanese Patent Publication No. 2003-535477 特表２００３－５３５４７８号公報Japanese Patent Publication No. 2003-535478

しかしながら、平均演色性評価数Ｒａを高くしようとすると、発光装置の発光効率が低下する傾向がある。また、近年、ＬＥＤを用いる発光装置について、平均演色性評価数Ｒａだけでなく、特定の演色性評価数、例えば、Ｒ１５を高くするとともに、発光効率が高い発光装置が求められることもある。 However, when trying to increase the general color rendering index Ra, the luminous efficiency of the light emitting device tends to decrease. In recent years, there is also a demand for light emitting devices using LEDs that not only have a general color rendering index Ra but also have a specific color rendering index, such as R15, and high luminous efficiency.

本開示の一実施形態は、特定の演色性評価数及び発光効率が高い、発光装置及びそれを備えた灯具を提供することを目的とする。 An object of one embodiment of the present disclosure is to provide a light-emitting device and a lamp having the same, which have a specific color rendering index and high luminous efficiency.

本発明は、以下の態様を包含する。
第一の態様は、４３０ｎｍ以上４７０ｎｍ以下の範囲内に発光ピーク波長を有する発光素子と、下記式（Ｉ）で表される組成を有する第一蛍光体、下記式（ＩＩ）で表される組成を有する第二蛍光体及び下記式（ＩＩＩ）で表される組成を有する第三蛍光体からなる群から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、下記式（ＩＶ）で表わされる組成を有する第四蛍光体と、下記式（Ｖ）で表わされる組成を有する第五蛍光体と、を含む蛍光部材と、を備える発光装置。
Ｙ３（Ａｌ，Ｇａ）５Ｏ１２：Ｃｅ （Ｉ）
Ｌｕ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩ）
Ｙ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩＩ）
Ａ２[Ｍ１１-ｐＭｎ４＋ ｐＦ６] （ＩＶ）
（Ｓｒ，Ｃａ）ＡｌＳｉＮ３：Ｅｕ （Ｖ）
（式（ＩＶ）中、Ａは、Ｋ、Ｌｉ、Ｎａ、Ｒｂ、Ｃｓ及びＮＨ４ ＋からなる群から選ばれる少なくとも１種を含み、Ｍ１は、第４族元素、第１３族元素及び第１４族元素からなる群から選ばれる少なくとも１種の元素を含み、ｐは０＜ｐ＜０．２を満たす数を示す。） The present invention includes the following aspects.
A first aspect includes a light emitting element having an emission peak wavelength in the range of 430 nm or more and 470 nm or less, a first phosphor having a composition represented by the following formula (I), and a composition represented by the following formula (II) and at least one rare earth aluminate phosphor selected from the group consisting of a second phosphor having a composition represented by the following formula (III) and a third phosphor having a composition represented by the following formula: A light-emitting device comprising a fluorescent member including a fourth phosphor having a composition represented by (IV) and a fifth phosphor having a composition represented by formula (V) below.
Y3 ( Al,Ga) 5O12 :Ce(I)
Lu3Al5O12 : Ce ( II)
Y3Al5O12 : Ce ( III )
A2 [M11 - pMn4 +pF6 ] (IV)
(Sr, Ca) AlSiN3 :Eu(V)
(In formula (IV), A contains at least one selected from the group consisting of K, Li, Na, Rb, Cs and NH 4 + , M1 is a Group 4 element, a Group 13 element and a Group 14 At least one element selected from the group consisting of group elements is included, and p indicates a number that satisfies 0<p<0.2.)

第二の態様は、前記発光装置を備えた灯具である。 A second aspect is a lamp including the light emitting device.

本開示に係る一態様によれば、優れた演色性と高い発光効率を達成可能な発光装置及びそれを備えた灯具を提供することができる。 According to one aspect of the present disclosure, it is possible to provide a light-emitting device capable of achieving excellent color rendering properties and high luminous efficiency, and a lamp including the same.

本発明に係る発光装置の一例を示す概略断面図である。1 is a schematic cross-sectional view showing an example of a light emitting device according to the present invention; FIG. 実施例１に係る発光装置の発光スペクトル、比較例１に係る発光装置の発光スペクトル及び相関色温度６５００Ｋの基準光源のスペクトルを示す図である。3A and 3B are diagrams showing an emission spectrum of a light emitting device according to Example 1, an emission spectrum of a light emitting device according to Comparative Example 1, and a spectrum of a reference light source with a correlated color temperature of 6500K; 実施例２に係る発光装置の発光スペクトル、比較例２に係る発光装置の発光スペクトル及び相関色温度５０００Ｋの基準光源のスペクトルを示す図である。FIG. 11 shows the emission spectrum of a light emitting device according to Example 2, the emission spectrum of a light emitting device according to Comparative Example 2, and the spectrum of a reference light source with a correlated color temperature of 5000K; 実施例３に係る発光装置の発光スペクトル、比較例３に係る発光装置の発光スペクトル及び相関色温度４０００Ｋの基準光源のスペクトルを示す図である。10A and 10B are diagrams showing an emission spectrum of a light emitting device according to Example 3, an emission spectrum of a light emitting device according to Comparative Example 3, and a spectrum of a reference light source with a correlated color temperature of 4000K; FIG. 実施例４に係る発光装置の発光スペクトル、比較例４に係る発光装置の発光スペクトル及び相関色温度３５００Ｋの基準光源のスペクトルを示す図である。FIG. 10 shows the emission spectrum of a light emitting device according to Example 4, the emission spectrum of a light emitting device according to Comparative Example 4, and the spectrum of a reference light source with a correlated color temperature of 3500K; 実施例５に係る発光装置の発光スペクトル、比較例５に係る発光装置の発光スペクトル及び相関色温度３０００Ｋの基準光源のスペクトルを示す図である。FIG. 11 shows the emission spectrum of a light emitting device according to Example 5, the emission spectrum of a light emitting device according to Comparative Example 5, and the spectrum of a reference light source with a correlated color temperature of 3000K. 実施例６に係る発光装置の発光スペクトル、比較例６に係る発光装置の発光スペクトル及び相関色温度２７００Ｋの基準光源のスペクトルを示す図である。FIG. 11 shows the emission spectrum of a light emitting device according to Example 6, the emission spectrum of a light emitting device according to Comparative Example 6, and the spectrum of a reference light source with a correlated color temperature of 2700K.

以下、本開示に係る発光装置及びそれを備えた灯具を、実施の形態に基づいて説明する。ただし、以下に示す実施の形態は、本発明の技術思想を具体化するためのものであって、本発明を以下のものに特定するものではない。なお、本明細書において色名と色度座標との関係、光の波長範囲と単色光の色名との関係等は、ＪＩＳ Ｚ８１１０に従う。組成物中の各成分の含有量は、組成物中に各成分に該当する物質が複数存在する場合、特に断らない限り、組成物中に存在する当該複数の物質の合計量を意味する。蛍光体の平均粒径は、フィッシャー・サブ・シーブ・サイザーズ・ナンバー（Ｆｉｓｈｅｒ Ｓｕｂ Ｓｉｅｖｅ Ｓｉｚｅｒ‘ｓ Ｎｏ．）と呼ばれる数値であり、空気透過法を用いて測定される。 Hereinafter, a light-emitting device according to the present disclosure and a lamp including the same will be described based on embodiments. However, the embodiments shown below are for embodying the technical idea of the present invention, and the present invention is not limited to the following. In this specification, the relationship between color names and chromaticity coordinates, the relationship between wavelength ranges of light and color names of monochromatic light, etc. conform to JIS Z8110. The content of each component in the composition means the total amount of the plurality of substances present in the composition unless otherwise specified when there are multiple substances corresponding to each component in the composition. The average particle size of the phosphor is a numerical value called Fisher Sub Sieve Sizer's No., which is measured using an air permeation method.

［発光装置］
発光装置は、発光ピーク波長が４３０ｎｍ以上４７０ｎｍ以下の範囲内にある発光素子と、下記式（Ｉ）で表される組成を有する第一蛍光体、下記式（ＩＩ）で表される組成を有する第二蛍光体及び下記式（ＩＩＩ）で表される組成を有する第三蛍光体からなる群から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、下記式（ＩＶ）で表わされる組成を有する第四蛍光体と、下記式（Ｖ）で表わされる組成を有する第五蛍光体と、を含む蛍光部材と、を備える。 [Light emitting device]
The light-emitting device has a light-emitting element having an emission peak wavelength in the range of 430 nm or more and 470 nm or less, a first phosphor having a composition represented by the following formula (I), and a composition represented by the following formula (II). Two or more rare earth aluminate phosphors, including at least one selected from the group consisting of a second phosphor and a third phosphor having a composition represented by the following formula (III), and the following formula (IV ) and a fifth phosphor having a composition represented by the following formula (V).

Ｙ３（Ａｌ，Ｇａ）５Ｏ１２：Ｃｅ （Ｉ）
Ｌｕ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩ）
Ｙ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩＩ）
Ａ２[Ｍ１１-ｐＭｎ４＋ ｐＦ６] （ＩＶ）
（Ｓｒ，Ｃａ）ＡｌＳｉＮ３：Ｅｕ （Ｖ） Y3 ( Al,Ga) 5O12 :Ce(I)
Lu3Al5O12 : Ce ( II)
Y3Al5O12 : Ce ( III )
A2 [M11 - pMn4 +pF6 ] (IV)
(Sr, Ca) AlSiN3 :Eu(V)

式（ＩＶ）中、Ａは、Ｋ、Ｌｉ、Ｎａ、Ｒｂ、Ｃｓ及びＮＨ４ ＋からなる群から選ばれる少なくとも１種を含み、Ｍ１は、第４族元素、第１３族元素及び第１４族元素からなる群から選ばれる少なくとも１種の元素を含む。ｐは０＜ｐ＜０．２を満たす数を示す。 In formula (IV), A contains at least one selected from the group consisting of K, Li, Na, Rb, Cs and NH 4 + , and M1 is a group 4 element, a group 13 element and a group 14 It contains at least one element selected from the group consisting of elements. p indicates a number that satisfies 0<p<0.2.

発光ピーク波長が４３０ｎｍ以上４７０ｎｍ以下の範囲内にある青紫色から青色に発光する発光素子に、赤色発光の第四蛍光体及び第五蛍光体に加えて、第一蛍光体、第二蛍光体及び第三蛍光体からなる群から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体を組み合わせて用いる。これにより、４３０ｎｍ以上４７０ｎｍ以下の範囲にある青紫色から青色の発光スペクトルが突出して高い強度とならないように抑制し、黄色から緑色発光の波長領域における発光スペクトルの発光強度を大きく向上させることができる。特に、青紫色から青色の波長領域における発光スペクトルのみが突出して高い強度とならにように抑制し、黄色から緑色発光の波長領域における発光スペクトルを、基準光源により近似させて、視感度が高い緑色発光の発光成分も増やすことができるので、優れた演色性と高い発光効率を達成することが可能となる。 In addition to the fourth phosphor and fifth phosphor emitting red light, a first phosphor, a second phosphor, and Two or more rare earth aluminate phosphors, including at least one selected from the group consisting of the third phosphor, are used in combination. As a result, it is possible to suppress the emission spectrum from bluish purple to blue in the range of 430 nm or more and 470 nm or less from becoming high intensity, and to greatly improve the emission intensity of the emission spectrum in the wavelength region from yellow to green emission. . In particular, only the emission spectrum in the blue-violet to blue wavelength region is suppressed to have a high intensity, and the emission spectrum in the yellow to green emission wavelength region is approximated by the reference light source, resulting in a green color with high luminosity. Since the luminous component of the emitted light can also be increased, it is possible to achieve excellent color rendering properties and high luminous efficiency.

演色性についてＣＩＥ（国際照明委員会）は、蛍光ランプが具備すべき演色性の指針を１９８６年に公表しており、その指針によれば、使用される場所に応じた好ましい平均演色評価数（以下、「Ｒａ」と記載する。）は、一般作業を行う工場では６０以上８０未満、住宅、ホテル、レストラン、店舗、オフィス、学校、病院、精密作業を行う工場等では８０以上９０未満、高い演色性が求められる臨床検査を行う場所、美術館等では９０以上とされている。 In 1986, the CIE (International Commission on Illumination) published guidelines for color rendering that fluorescent lamps should possess. hereinafter referred to as "Ra") is 60 or more and less than 80 for factories that perform general work, and 80 or more and less than 90 for houses, hotels, restaurants, stores, offices, schools, hospitals, factories that perform precision work, etc. It is set to 90 or more in places where clinical examinations, art museums, etc., where color rendering properties are required.

発光装置のＲａは、例えば８０以上であり、９０以上が好ましく、９５以上がより好ましい。なお、Ｒａの上限は１００である。また特殊演色評価数はＲ９からＲ１５の評価数で表わされ、Ｒ９は赤色、Ｒ１０は黄色、Ｒ１１は緑色、Ｒ１２は青色、Ｒ１３は西洋人の肌の色、Ｒ１４は木の葉の色、Ｒ１５は日本人の肌の色とされている。特殊演色性評価数においても高いほど好ましいとされ、本実施形態の発光装置のＲ９からＲ１５は例えば、５０以上であり、６０以上が好ましく、７０以上がより好ましく、８０以上が更に好ましい。Ｒ９からＲ１５の上限はそれぞれ１００である。発光装置のＲ１５は、より高い数値であることが好ましく、８５以上、９０以上、９２以上、９３以上が特に好ましい。 Ra of the light-emitting device is, for example, 80 or higher, preferably 90 or higher, and more preferably 95 or higher. Note that the upper limit of Ra is 100. The special color rendering index is represented by the evaluation numbers from R9 to R15, where R9 is red, R10 is yellow, R11 is green, R12 is blue, R13 is the skin color of Westerners, R14 is the color of leaves, and R15 is the color of leaves. It is said to be the skin color of Japanese people. The higher the special color rendering index, the better. The upper limits of R9 to R15 are 100 each. R15 of the light-emitting device is preferably a higher numerical value, and particularly preferably 85 or more, 90 or more, 92 or more, or 93 or more.

発光装置が発する光は、発光素子の光と、第一蛍光体、第二蛍光体及び第三蛍光体からなる群から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、第四蛍光体と、第五蛍光体と、が発する蛍光との混合色であり、例えば、ＣＩＥ１９３１に規定される色度座標が、ｘ＝０．２０から０．５０且つｙ＝０．２０から０．５０の範囲に含まれる光とすることができ、ｘ＝０．３０から０．５０且つｙ＝０．３０から０．４５の範囲に含まれる光とすることもできる。
発光装置が発する光の相関色温度は、例えば２０００Ｋ以上とすることができ、２５００Ｋ以上とすることもでる。また相関色温度は８０００Ｋ以下とすることができ、７０００Ｋ以下とすることもできる。 The light emitted by the light-emitting device includes light from the light-emitting element and at least one rare earth aluminate phosphor selected from the group consisting of the first phosphor, the second phosphor, and the third phosphor. , the fourth phosphor, and the fifth phosphor. The light can be in the range of 20 to 0.50, and the light can be in the range of x=0.30 to 0.50 and y=0.30 to 0.45.
The correlated color temperature of light emitted by the light emitting device can be, for example, 2000K or higher, and can be 2500K or higher. Also, the correlated color temperature can be 8000K or less, and can be 7000K or less.

発光装置の一例である発光装置１００を図面に基づいて説明する。図１は、発光装置１００を示す概略断面図である。
発光装置１００は、可視光の短波長側（例えば、３８０ｎｍ以上４８５ｎｍ以下の範囲）の光を発し、発光ピーク波長が４３０ｎｍ以上４７０ｎｍ以下の範囲内にある窒化ガリウム系化合物半導体の発光素子１０と、発光素子１０を載置する成形体４０と、を有する。成形体４０は、第１のリード２０及び第２のリード３０と、熱可塑性樹脂又は熱硬化性樹脂を含む樹脂部４２とが一体的に成形されてなるものである。成形体４０は底面と側面を持つ凹部を形成しており、凹部の底面に発光素子１０が載置されている。発光素子１０は一対の正負の電極を有しており、その一対の正負の電極はそれぞれ第１のリード２０及び第２のリード３０とワイヤ６０を介して電気的に接続されている。発光素子１０は蛍光部材５０により被覆されている。蛍光部材５０は、例えば、発光素子１０からの光を波長変換する蛍光体７０として、第一蛍光体、第二蛍光体及び第三蛍光体からなる群から選択された少なくとも１種を含む、２種の希土類アルミン酸塩蛍光体７１、７２、第四蛍光体７３並びに第五蛍光体７４と、樹脂とを含有してなる。 A light-emitting device 100, which is an example of a light-emitting device, will be described with reference to the drawings. FIG. 1 is a schematic cross-sectional view showing a light emitting device 100. FIG.
The light emitting device 100 emits light on the short wavelength side of visible light (for example, in the range of 380 nm or more and 485 nm or less), and has an emission peak wavelength in the range of 430 nm or more and 470 nm or less. and a molded body 40 on which the light emitting element 10 is mounted. The molded body 40 is formed by integrally molding the first lead 20, the second lead 30, and a resin portion 42 containing a thermoplastic resin or a thermosetting resin. The molded body 40 forms a recess having a bottom surface and a side surface, and the light emitting element 10 is placed on the bottom surface of the recess. The light emitting element 10 has a pair of positive and negative electrodes, and the pair of positive and negative electrodes are electrically connected to the first lead 20 and the second lead 30 via wires 60, respectively. The light emitting element 10 is covered with a fluorescent member 50 . The fluorescent member 50 includes, for example, at least one selected from the group consisting of a first fluorescent substance, a second fluorescent substance, and a third fluorescent substance as a fluorescent substance 70 that converts the wavelength of light from the light emitting element 10. It contains rare earth aluminate phosphors 71 and 72, a fourth phosphor 73 and a fifth phosphor 74, and a resin.

蛍光部材５０は、発光素子１０が発する光を波長変換するだけではなく、外部環境から発光素子１０を保護するための部材としても機能する。図１では、蛍光体７０は蛍光部材５０中で偏在している。このように発光素子１０に接近して蛍光体７０を配置することにより、発光素子１０からの光を効率よく波長変換することができ、発光効率の優れた発光装置とできる。なお、蛍光体７０を含む蛍光部材５０と、発光素子１０との配置は、それらを接近して配置させる形態に限定されることなく、蛍光体７０への熱の影響を考慮して、蛍光部材５０中で発光素子１０と、蛍光体７０との間隔を空けて配置することもできる。また蛍光体７０を蛍光部材５０の全体にほぼ均一の割合で混合することによって、色ムラがより抑制された光を得るようにすることもできる。 The fluorescent member 50 not only converts the wavelength of the light emitted by the light emitting element 10, but also functions as a member for protecting the light emitting element 10 from the external environment. In FIG. 1, the phosphors 70 are unevenly distributed in the phosphor member 50 . By arranging the phosphor 70 close to the light emitting element 10 in this way, the wavelength of the light from the light emitting element 10 can be efficiently converted, and a light emitting device with excellent luminous efficiency can be obtained. In addition, the arrangement of the fluorescent member 50 including the fluorescent substance 70 and the light emitting element 10 is not limited to a form in which they are arranged close to each other. The light-emitting element 10 and the phosphor 70 can be arranged in the space 50 . Further, by mixing the phosphor 70 in the entire fluorescent member 50 at a substantially uniform ratio, it is possible to obtain light with more suppressed color unevenness.

（発光素子）
発光素子の発光ピーク波長は、４３０ｎｍ以上４７０ｎｍ以下の範囲内にあり、発光効率と演色性の観点から、４４０ｎｍ以上４６５ｎｍ以下の範囲内にあることが好ましく、４４５ｎｍ以上４６０ｎｍ以下の範囲内にあることがより好ましく、４５０ｎｍ以上４６０ｎｍ以下の範囲内にあってもよい。このような発光素子を励起光源として用い、発光素子からの光と蛍光体からの蛍光との混色光を発する発光装置を構成する。 (light emitting element)
The emission peak wavelength of the light emitting element is in the range of 430 nm or more and 470 nm or less, preferably in the range of 440 nm or more and 465 nm or less, and in the range of 445 nm or more and 460 nm or less from the viewpoint of luminous efficiency and color rendering properties. is more preferable, and may be in the range of 450 nm or more and 460 nm or less. Using such a light-emitting element as an excitation light source, a light-emitting device that emits mixed-color light of light from the light-emitting element and fluorescence from the phosphor is configured.

発光素子の発光スペクトルの半値幅は、例えば、３０ｎｍ以下であってもよい。
発光素子にはＬＥＤ等の半導体発光素子を用いることが好ましい。光源として半導体発光素子を用いることによって、高効率で入力に対する出力のリニアリティが高く、機械的衝撃にも強い安定した発光装置を得ることができる。
半導体発光素子としては、例えば、窒化物系半導体（ＩｎＸＡｌＹＧａ１－Ｘ－ＹＮ、ここでＸ及びＹは、０≦Ｘ、０≦Ｙ、Ｘ＋Ｙ≦１を満たす。）を用いた青色等に発光する半導体発光素子を用いることができる。
本明細書において、半値幅は、発光スペクトルにおける発光ピークの半値全幅（Ｆｕｌｌ Ｗｉｄｔｈ ａｔ Ｈａｌｆ Ｍａｘｉｍｕｍ）をいい、発光スペクトルにおける発光ピークの最大値の５０％の値を示す発光ピークの波長幅をいう。 The half width of the emission spectrum of the light emitting element may be, for example, 30 nm or less.
It is preferable to use a semiconductor light-emitting element such as an LED as the light-emitting element. By using a semiconductor light-emitting element as a light source, it is possible to obtain a stable light-emitting device with high efficiency, high output linearity with respect to input, and resistance to mechanical impact.
As the semiconductor light emitting device, for example, a nitride semiconductor (In X Al Y Ga 1-XY N, where X and Y satisfy 0≦X, 0≦Y, and X+Y≦1) is used. A semiconductor light-emitting element that emits blue light or the like can be used.
As used herein, the half width refers to the full width at half maximum of an emission peak in an emission spectrum, and refers to the wavelength width of an emission peak that is 50% of the maximum value of the emission peak in the emission spectrum.

（蛍光体）
発光装置は、発光素子から発せられる光の一部を吸収し、上記式（Ｉ）で表される組成を有する第一蛍光体、上記式（ＩＩ）で表される組成を有する第二蛍光体及び上記式（ＩＩＩ）で表される組成を有する第三蛍光体からなる群から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、上記式（ＩＶ）で表わされる組成を有する第四蛍光体と、上記式（Ｖ）で表わされる組成を有する第五蛍光体と、を含む蛍光部材を備える。第一蛍光体、第二蛍光体、第三蛍光体、第四蛍光体及び第五蛍光体は、それぞれ上記各式で表される特定の組成を有している。蛍光部材に含まれる第一蛍光体、第二蛍光体及び第三蛍光体からなる群から選択される少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体、第四蛍光体及び第五蛍光体の各蛍光体の構成比率を適宜選択することで発光装置の光束を高めつつ、演色性を所望の範囲、例えば、発光装置の平均演色評価数Ｒａを９０以上、特殊演色評価数Ｒ１５を８５以上とすることができる。 (Phosphor)
The light-emitting device absorbs part of the light emitted from the light-emitting element, and includes a first phosphor having a composition represented by formula (I) above and a second phosphor having a composition represented by formula (II) above. and two or more rare earth aluminate phosphors, including at least one selected from the group consisting of a third phosphor having a composition represented by the formula (III), and a phosphor represented by the formula (IV) and a fifth phosphor having a composition represented by formula (V) above. The first phosphor, the second phosphor, the third phosphor, the fourth phosphor, and the fifth phosphor each have specific compositions represented by the above formulas. Two or more rare earth aluminate phosphors, a fourth phosphor, and a fifth phosphor, including at least one selected from the group consisting of the first phosphor, the second phosphor, and the third phosphor contained in the fluorescent member While increasing the luminous flux of the light emitting device by appropriately selecting the composition ratio of each phosphor of the phosphor, the color rendering property is set to a desired range, for example, the general color rendering index Ra of the light emitting device is 90 or more, and the special color rendering index R15. 85 or more.

希土類アルミン酸塩蛍光体の総含有量に対する第四蛍光体の含有率は、発光装置が目的とする相関色温度に応じて、選択してもよい。例えば、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置とする場合、希土類アルミン酸塩蛍光体の総含有量に対する第四蛍光体の含有率は、光束及び演色性の観点から、０．３５以上０．７以下の範囲内であることが好ましく、０．４以上０．６５以下の範囲内であることがより好ましい。相関色温度が２５００Ｋ以上４７５０Ｋ以下の範囲内の光を発する発光装置とする場合、希土類アルミン酸塩蛍光体の総含有量に対する第四蛍光体の含有率は、光束及び演色性の観点から、０．７以上１．３以下の範囲内であることが好ましく、０．７５以上１．２以下の範囲内であることがより好ましい。 The content of the fourth phosphor relative to the total content of the rare earth aluminate phosphors may be selected according to the correlated color temperature desired for the light emitting device. For example, in the case of a light emitting device that emits light with a correlated color temperature in the range of 4750 K or more and 7000 K or less, the content ratio of the fourth phosphor with respect to the total content of the rare earth aluminate phosphor is, from the viewpoint of luminous flux and color rendering properties , preferably in the range of 0.35 to 0.7, more preferably in the range of 0.4 to 0.65. In the case of a light emitting device that emits light with a correlated color temperature in the range of 2500 K or more and 4750 K or less, the content ratio of the fourth phosphor with respect to the total content of the rare earth aluminate phosphor is 0 from the viewpoint of luminous flux and color rendering properties. .7 or more and 1.3 or less, and more preferably 0.75 or more and 1.2 or less.

希土類アルミン酸塩蛍光体、第四蛍光体及び第五蛍光体の総含有量（以下、「蛍光体総含有量」と呼ぶことがある。）に対する第四蛍光体の含有率は、発光装置が目的とする相関色温度に応じて、選択してもよい。例えば、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置とする場合、蛍光体総含有量に対する第四蛍光体の含有率は、光束及び演色性の観点から、０．２５以上０．４５以下の範囲内であることが好ましく、０．２７以上０．４以下の範囲内であることがより好ましい。相関色温度が２５００Ｋ以上４７５０Ｋ以下の範囲内の光を発する発光装置とする場合、蛍光体総含有量に対する第四蛍光体の含有率は、光束及び演色性の観点から、０．４以上０．６以下の範囲内であることが好ましく、０．４以上０．５５以下の範囲内であることがより好ましい。 The content ratio of the fourth phosphor to the total content of the rare earth aluminate phosphor, the fourth phosphor, and the fifth phosphor (hereinafter sometimes referred to as the "total phosphor content") is It may be selected according to the desired correlated color temperature. For example, in the case of a light emitting device that emits light with a correlated color temperature in the range of 4750 K or more and 7000 K or less, the content rate of the fourth phosphor with respect to the total phosphor content is 0.25 or more from the viewpoint of luminous flux and color rendering properties. It is preferably within the range of 0.45 or less, and more preferably within the range of 0.27 or more and 0.4 or less. In the case of a light emitting device that emits light with a correlated color temperature in the range of 2500K or more and 4750K or less, the content ratio of the fourth phosphor with respect to the total phosphor content is 0.4 or more and 0.4 or more from the viewpoint of luminous flux and color rendering properties. It is preferably in the range of 6 or less, and more preferably in the range of 0.4 to 0.55.

蛍光体総含有量に対する希土類アルミン酸塩蛍光体の総含有量の含有率は、発光装置が目的とする相関色温度に応じて、選択してもよい。例えば、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置とする場合、蛍光体総含有量に対する希土類アルミン酸塩蛍光体の総含有量の含有率は、光束及び演色性の観点から、０．５以上０．７５以下の範囲内であることが好ましく、０．５５以上０．７以下の範囲内であることがより好ましい。相関色温度が２５００Ｋ以上４７５０Ｋ以下の範囲内の光を発する発光装置とする場合、蛍光体総含有量に対する希土類アルミン酸塩蛍光体の総含有量の含有率は、光束及び演色性の観点から、０．４以上０．６以下の範囲内であることが好ましく、０．４以上０．５５以下の範囲内であることがより好ましい。 The content ratio of the total rare earth aluminate phosphor content to the total phosphor content may be selected according to the correlated color temperature desired for the light emitting device. For example, in the case of a light emitting device that emits light with a correlated color temperature in the range of 4750 K or more and 7000 K or less, the content ratio of the total content of the rare earth aluminate phosphor to the total content of the phosphor is from the viewpoint of luminous flux and color rendering properties. Therefore, it is preferably in the range of 0.5 to 0.75, more preferably in the range of 0.55 to 0.7. In the case of a light emitting device that emits light with a correlated color temperature in the range of 2500 K or more and 4750 K or less, the content ratio of the total content of the rare earth aluminate phosphor to the total content of the phosphor is, from the viewpoint of luminous flux and color rendering properties, It is preferably within the range of 0.4 or more and 0.6 or less, and more preferably within the range of 0.4 or more and 0.55 or less.

蛍光体総含有量に対する、第四蛍光体及び第五蛍光体（以下、第四蛍光体及び第五蛍光体を纏めて「赤色発光蛍光体」と呼ぶことがある。）の総含有量の含有率は、発光装置が目的とする相関色温度に応じて、選択してもよい。例えば、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置とする場合、光束及び演色性の観点から、０．２５以上０．５以下の範囲内であることが好ましく、０．３以上０．４５以下の範囲内であることがより好ましい。相関色温度が２５００Ｋ以上４７５０Ｋ以下の範囲内の光を発する発光装置とする場合、蛍光体総含有量に対する赤色発光蛍光体の含有率は、光束及び演色性の観点から、０．４以上０．６以下の範囲内であることが好ましく、０．４５以上０．５５以下の範囲内であることがより好ましい。 Containment of the total content of the fourth phosphor and the fifth phosphor (hereinafter, the fourth phosphor and the fifth phosphor may be collectively referred to as "red-emitting phosphor") relative to the total phosphor content The ratio may be selected according to the correlated color temperature that the light emitting device is intended for. For example, in the case of a light-emitting device that emits light with a correlated color temperature in the range of 4750K or more and 7000K or less, it is preferably in the range of 0.25 or more and 0.5 or less from the viewpoint of luminous flux and color rendering properties. It is more preferably within the range of 3 or more and 0.45 or less. In the case of a light-emitting device that emits light with a correlated color temperature in the range of 2500K or more and 4750K or less, the content ratio of the red light-emitting phosphor with respect to the total phosphor content is 0.4 or more and 0.4 or more from the viewpoint of luminous flux and color rendering properties. It is preferably within the range of 6 or less, and more preferably within the range of 0.45 or more and 0.55 or less.

希土類アルミン酸塩蛍光体
希土類アルミン酸塩蛍光体は、以下に説明する第一蛍光体、第二蛍光体及び第三蛍光体から選択された少なくとも１種を含み、２種以上の蛍光体を含む。
第一蛍光体は、下記式（Ｉ）で表される組成を有する３価のセリウムで賦活される蛍光体である。
Ｙ３（Ａｌ，Ｇａ）５Ｏ１２：Ｃｅ （Ｉ）
第一蛍光体の発光ピーク波長は、５２０ｎｍ以上５５０ｎｍ以下の範囲内にあることが好ましい。第一蛍光体の半値幅は、９５ｎｍ以上１２０ｎｍ以下の範囲内であることが好ましい。
第二蛍光体は、下記式（ＩＩ）で表される組成を有する３価のセリウムで賦活される蛍光体である。
Ｌｕ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩ）
第二蛍光体の発光ピーク波長は、５００ｎｍ以上５４５ｎｍ以下の範囲内にあることが好ましい。第二蛍光体の半値幅は、９５ｎｍ以上１０５ｎｍ以下の範囲内であることが好ましい。
第三蛍光体は、下記式（ＩＩＩ）で表される組成を有する３価のセリウムで賦活される蛍光体である。
Ｙ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩＩ）
第三蛍光体の発光ピーク波長は、５３５ｎｍ以上５５５ｎｍ以下の範囲内にあることが好ましい。第三蛍光体の半値幅は、１００ｎｍ以上１２０ｎｍ以下の範囲内であることが好ましい。 Rare earth aluminate phosphor The rare earth aluminate phosphor contains at least one selected from the following first phosphor, second phosphor and third phosphor, and contains two or more phosphors. .
The first phosphor is a trivalent cerium-activated phosphor having a composition represented by the following formula (I).
Y3 ( Al,Ga) 5O12 :Ce(I)
The emission peak wavelength of the first phosphor is preferably in the range of 520 nm or more and 550 nm or less. The half width of the first phosphor is preferably in the range of 95 nm or more and 120 nm or less.
The second phosphor is a trivalent cerium-activated phosphor having a composition represented by the following formula (II).
Lu3Al5O12 : Ce ( II)
The emission peak wavelength of the second phosphor is preferably in the range of 500 nm or more and 545 nm or less. The half width of the second phosphor is preferably in the range of 95 nm or more and 105 nm or less.
The third phosphor is a trivalent cerium-activated phosphor having a composition represented by the following formula (III).
Y3Al5O12 : Ce ( III )
The emission peak wavelength of the third phosphor is preferably in the range of 535 nm or more and 555 nm or less. The half width of the third phosphor is preferably in the range of 100 nm or more and 120 nm or less.

希土類アルミン酸塩蛍光体の極大励起波長は、発光効率を考慮して、２２０ｎｍ以上４９０ｎｍ以下の範囲内にあることが好ましく、４３０ｎｍ以上４７０ｎｍ以下の範囲内にあることがより好ましく、４４０ｎｍ以上４６０ｎｍ以下の範囲内にあることがさらに好ましい。 The maximum excitation wavelength of the rare earth aluminate phosphor is preferably in the range of 220 nm or more and 490 nm or less, more preferably in the range of 430 nm or more and 470 nm or less, and 440 nm or more and 460 nm or less, in consideration of luminous efficiency. is more preferably within the range of

希土類アルミン酸塩蛍光体の平均粒径は、発光強度及び発光装置の製造工程における作業性の向上を考慮して、例えば５μｍ以上３０μｍ以下の範囲内であり、２０μｍ以上２５μｍ以下の範囲内であることが好ましい。 The average particle diameter of the rare earth aluminate phosphor is, for example, in the range of 5 μm or more and 30 μm or less, and in the range of 20 μm or more and 25 μm or less, in consideration of the improvement of luminous intensity and workability in the manufacturing process of the light emitting device. is preferred.

第四蛍光体
第四蛍光体は、下記式（ＩＶ）で表される組成を有し、４価のマンガンで賦活され、赤色発光する、フッ化物蛍光体である。第四蛍光体は、６１０ｎｍ以上６５０ｎｍ以下の範囲内に発光ピーク波長を有することが好ましい。
Ａ２[Ｍ１１-ｐＭｎ４＋ ｐＦ６] （ＩＶ）
ただし、上記式（ＩＶ）中、Ａは、Ｋ、Ｌｉ、Ｎａ、Ｒｂ、Ｃｓ及びＮＨ４ ＋からなる群から選ばれる少なくとも１種の元素を含み、Ａは、Ｋであることが好ましく、Ｍ１は、第４族元素、第１３族元素及び第１４族元素からなる群から選ばれる少なくとも１種の元素を含む。Ｍ１は、好ましくはケイ素、アルミニウム、ゲルマニウム及びチタンからなる群から選ばれる少なくとも１種の元素を含み、より好ましくは、ケイ素及びアルミニウムからなる群から選ばれる少なくとも１種の元素を含む。ｐは０＜ｐ＜０．２を満たす数を示す。 Fourth Phosphor The fourth phosphor is a fluoride phosphor that has a composition represented by the following formula (IV), is activated by tetravalent manganese, and emits red light. The fourth phosphor preferably has an emission peak wavelength within the range of 610 nm or more and 650 nm or less.
A2 [M11 - pMn4 +pF6 ] (IV)
However, in the above formula (IV), A contains at least one element selected from the group consisting of K, Li, Na, Rb, Cs and NH 4 + , A is preferably K, M1 contains at least one element selected from the group consisting of Group 4 elements, Group 13 elements and Group 14 elements. M1 preferably contains at least one element selected from the group consisting of silicon, aluminum, germanium and titanium, more preferably at least one element selected from the group consisting of silicon and aluminum. p indicates a number that satisfies 0<p<0.2.

第四蛍光体の発光スペクトルにおける半値幅は、小さいことが好ましく、例えば１０ｎｍ以下である。第四蛍光体の極大励起波長は、発光効率を考慮して、４３０ｎｍ以上４７０ｎｍ以下の範囲内にあることが好ましく、４４０ｎｍ以上４６０ｎｍ以下の範囲内にあることがより好ましい。 The half width of the emission spectrum of the fourth phosphor is preferably small, for example 10 nm or less. The maximum excitation wavelength of the fourth phosphor is preferably in the range of 430 nm or more and 470 nm or less, and more preferably in the range of 440 nm or more and 460 nm or less, in consideration of luminous efficiency.

第四蛍光体の平均粒径は、発光強度及び発光装置の製造工程における作業性の向上を考慮して、例えば５μｍ以上５０μｍ以下の範囲内でもよく、１０μｍ以上３０μｍ以下の範囲内であることが好ましい。
発光装置は、第四蛍光体を１種単独でも、組成が異なる第四蛍光体の２種以上を組合せて含んでいてもよい。 The average particle diameter of the fourth phosphor may be, for example, in the range of 5 μm or more and 50 μm or less, and may be in the range of 10 μm or more and 30 μm or less, in consideration of the improvement of the light emission intensity and workability in the manufacturing process of the light emitting device. preferable.
The light-emitting device may contain a single fourth phosphor or a combination of two or more fourth phosphors having different compositions.

第五蛍光体
第五蛍光体は下記式（Ｖ）で表される組成を有する２価のユーロピウムで賦活される赤色発光する、窒化物蛍光体である。
（Ｓｒ，Ｃａ）ＡｌＳｉＮ３：Ｅｕ （Ｖ）
第五蛍光体はＳｒ及びＣａからなる群から選択される少なくとも１種を含むが、ＳｒとＣａの両方を含むことが好ましく、Ｓｒ及びＣａのうちのＳｒ含有率が０．８モル％以上であることがより好ましい。 Fifth Phosphor The fifth phosphor is a nitride phosphor that emits red light and is activated by divalent europium having a composition represented by the following formula (V).
(Sr, Ca) AlSiN3 :Eu(V)
The fifth phosphor contains at least one selected from the group consisting of Sr and Ca, and preferably contains both Sr and Ca. It is more preferable to have

第五蛍光体の発光ピーク波長は、６００ｎｍ以上にあることが好ましく、６１５ｎｍ以上にあることがより好ましい。第五蛍光体の発光ピーク波長は、６３０ｎｍ以下にあることが好ましく、６２０ｎｍ以下にあることがより好ましい。第五蛍光体の発光ピーク波長は、光束及び演色性の観点から、発光装置が目的とする相関色温度に応じて、選択してもよい。例えば、相関色温度が３２５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置とする場合、第五蛍光体の発光ピーク波長は、６００ｎｍ以上６２０ｎｍ以下の範囲内にあることが好ましい。相関色温度が２５００Ｋ以上３２５０Ｋ以下の光を発する発光装置とする場合、第五蛍光体の発光ピーク波長は、６１５ｎｍ以上６３０ｎｍ以下の範囲内にあることが好ましい。 The emission peak wavelength of the fifth phosphor is preferably 600 nm or longer, more preferably 615 nm or longer. The emission peak wavelength of the fifth phosphor is preferably 630 nm or less, more preferably 620 nm or less. The emission peak wavelength of the fifth phosphor may be selected from the viewpoint of luminous flux and color rendering properties according to the correlated color temperature intended for the light emitting device. For example, when the light emitting device emits light with a correlated color temperature in the range of 3250K to 7000K, the emission peak wavelength of the fifth phosphor is preferably in the range of 600 nm to 620 nm. When the light emitting device emits light with a correlated color temperature of 2500 K or more and 3250 K or less, the emission peak wavelength of the fifth phosphor is preferably in the range of 615 nm or more and 630 nm or less.

第五蛍光体の発光スペクトルにおける半値幅は、光束及び演色性の観点から、例えば１００ｎｍ以下であり、８０ｎｍ以下が好ましい。第五蛍光体の極大励起波長は、発光効率を考慮して、２２０ｎｍ以上４９０ｎｍ以下の範囲内にあることが好ましく、４３０ｎｍ以上４７０ｎｍ以下の範囲内にあることがより好ましく、４４０ｎｍ以上４６０ｎｍ以下の範囲内にあることがさらに好ましい。 The half width of the emission spectrum of the fifth phosphor is, for example, 100 nm or less, preferably 80 nm or less, from the viewpoint of luminous flux and color rendering properties. The maximum excitation wavelength of the fifth phosphor is preferably in the range of 220 nm or more and 490 nm or less, more preferably in the range of 430 nm or more and 470 nm or less, in consideration of luminous efficiency, and 440 nm or more and 460 nm or less. more preferably within.

第五蛍光体の平均粒径は、発光強度及び発光装置の製造工程における作業性の向上を考慮して、例えば５μｍ以上３０μｍ以下の範囲内であり、１０μｍ以上２０μｍ以下の範囲内であることが好ましい。
発光装置は、第五蛍光体を１種単独でも、組成が異なる第五蛍光体の２種以上を組合せて含んでいてもよい。 The average particle size of the fifth phosphor is, for example, in the range of 5 μm or more and 30 μm or less, and in the range of 10 μm or more and 20 μm or less, in consideration of the improvement of the workability in the light emission intensity and the manufacturing process of the light emitting device. preferable.
The light-emitting device may contain one type of the fifth phosphor, or a combination of two or more types of fifth phosphors having different compositions.

発光装置の発光スペクトル
上述した蛍光体を含む蛍光部材を備えた発光装置の発光スペクトルは、横軸に波長、縦軸に発光強度を有する分光分布で表される。発光装置の発光スペクトルにおいて、第四蛍光体の発光ピークの発光素子の発光ピークに対する発光ピーク強度比は、発光装置が目的とする相関色温度に応じて、選択してもよい。例えば、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置とする場合、発光素子の発光ピークに対する第四蛍光体の発光ピークの発光ピーク強度比は、光束及び演色性の観点から、１．０以上２．０以下の範囲内であることが好ましく、１．１以上１．９以下の範囲内であることがより好ましい。相関色温度が３７５０Ｋ以上４７５０Ｋ以下の範囲内の光を発する発光装置とする場合、発光素子の発光ピークに対する第四蛍光体の発光ピークの発光ピーク強度比は、光束及び演色性の観点から、２．０以上３．５以下の範囲内であることが好ましく、２．５以上３．０以下の範囲内であることがより好ましい。相関色温度が２８５０Ｋ以上３７５０Ｋ以下の範囲内の光を発する発光装置とする場合、発光素子の発光ピークに対する第四蛍光体の発光ピークの発光ピーク強度比は、光束及び演色性の観点から、３．５以上５．５以下の範囲内であることが好ましく、４．０以上５．２以下の範囲内であることがより好ましい。相関色温度が２５００Ｋ以上２８５０Ｋ以下の範囲内の光を発する発光装置とする場合、発光素子の発光ピークに対する第四蛍光体の発光ピークの発光ピーク強度比は、光束及び演色性の観点から、５．５以上７．０以下の範囲内であることが好ましく、６．０以上６．５以下の範囲内であることがより好ましい。 Emission Spectrum of Light-Emitting Device The emission spectrum of the light-emitting device including the fluorescent member containing the phosphor described above is represented by a spectral distribution having the wavelength on the horizontal axis and the emission intensity on the vertical axis. In the emission spectrum of the light-emitting device, the emission peak intensity ratio of the emission peak of the fourth phosphor to the emission peak of the light-emitting element may be selected according to the correlated color temperature intended for the light-emitting device. For example, when the correlated color temperature is a light emitting device that emits light within the range of 4750 K or more and 7000 K or less, the emission peak intensity ratio of the emission peak of the fourth phosphor to the emission peak of the light emitting element is, from the viewpoint of luminous flux and color rendering properties , preferably in the range of 1.0 to 2.0, more preferably in the range of 1.1 to 1.9. In the case of a light emitting device that emits light with a correlated color temperature in the range of 3750 K or more and 4750 K or less, the emission peak intensity ratio of the emission peak of the fourth phosphor to the emission peak of the light emitting element is 2 from the viewpoint of luminous flux and color rendering properties. .0 or more and 3.5 or less, and more preferably 2.5 or more and 3.0 or less. In the case of a light emitting device that emits light with a correlated color temperature in the range of 2850 K or more and 3750 K or less, the emission peak intensity ratio of the emission peak of the fourth phosphor to the emission peak of the light emitting element is 3 from the viewpoint of luminous flux and color rendering properties. 0.5 or more and 5.5 or less, and more preferably 4.0 or more and 5.2 or less. In the case of a light emitting device that emits light with a correlated color temperature in the range of 2500 K or more and 2850 K or less, the emission peak intensity ratio of the emission peak of the fourth phosphor to the emission peak of the light emitting element is 5 from the viewpoint of luminous flux and color rendering properties. 0.5 or more and 7.0 or less, and more preferably 6.0 or more and 6.5 or less.

その他の蛍光体
発光装置は、第一蛍光体から第五蛍光体以外のその他の蛍光体を必要に応じて含んでいてもよい。その他の蛍光体としては、（Ｓｒ、Ｂａ、Ｃａ）１０（ＰＯ４）６（Ｂｒ、Ｃｌ）２：Ｅｕ、（Ｙ，Ｇｄ，Ｔｂ，Ｌｕ）３（Ａｌ，Ｇａ）５Ｏ１２：Ｃｅ（ただし、第一乃至第三蛍光体の組成を除く。）、Ｃａ３Ｓｃ２Ｓｉ３Ｏ１２：Ｃｅ、ＣａＳｃ２Ｏ４：Ｃｅ、（Ｌａ，Ｙ）３Ｓｉ６Ｎ１１：Ｃｅ、（Ｃａ，Ｓｒ，Ｂａ）３Ｓｉ６Ｏ９Ｎ４：Ｅｕ、（Ｃａ，Ｓｒ，Ｂａ）３Ｓｉ６Ｏ１２Ｎ２：Ｅｕ、（Ｂａ，Ｓｒ，Ｃａ)Ｓｉ２Ｏ２Ｎ２：Ｅｕ、（Ｃａ，Ｓｒ，Ｂａ）２Ｓｉ５Ｎ８：Ｅｕ、（Ｃａ，Ｓｒ，Ｂａ）Ｓ：Ｅｕ、（Ｂａ，Ｓｒ，Ｃａ）Ｇａ２Ｓ４：Ｅｕ等を挙げることができる。発光装置がその他の蛍光体を含む場合、その含有量は、特定の発光特性が得られるように適宜調整される。 Other Phosphors The light-emitting device may contain phosphors other than the first to fifth phosphors, if necessary. Other phosphors include (Sr, Ba, Ca) 10 (PO 4 ) 6 (Br, Cl) 2 :Eu, (Y, Gd, Tb, Lu) 3 (Al, Ga) 5 O 12 :Ce( However, except for the composition of the first to third phosphors.), Ca3Sc2Si3O12 :Ce, CaSc2O4 :Ce, ( La , Y) 3Si6N11 : Ce , ( Ca , Sr,Ba) 3Si6O9N4 :Eu, ( Ca , Sr, Ba ) 3Si6O12N2 : Eu , ( Ba, Sr ,Ca) Si2O2N2 : Eu , ( Ca, Sr,Ba) 2Si5N8 :Eu, ( Ca,Sr,Ba)S: Eu , ( Ba,Sr,Ca) Ga2S4 :Eu and the like. When the light-emitting device contains other phosphors, the content thereof is appropriately adjusted so as to obtain specific light-emitting properties.

蛍光体は、市販の蛍光体を使用する他、例えば、第四蛍光体は、出願人が先に出願した特願２０１４－２０２２６６号、特願２０２０－２１２５３２号に記載の製造方法を参照して製造することができる。また、その他の蛍光体について、例えば以下のようにして製造することができる。蛍光体の組成に含有される元素の単体や酸化物、炭酸塩、窒化物、塩化物、フッ化物、硫化物等を原料とし、これらの各原料を所定の組成比となるように秤量する。また、原料にさらにフラックス等の添加材料を適宜加え、混合機を用いて湿式又は乾式で混合する。これにより、固相反応を促進させて均一な大きさの粒子を形成することが可能となる。また、混合機は工業的に通常用いられているボールミルの他、振動ミル、ロールミル、ジェットミル等の粉砕機を用いてもよい。粉砕機を用いて粉砕することで比表面積を大きくすることもできる。また、得られる蛍光体粒子の比表面積を一定範囲とするために、工業的に通常用いられている沈降槽、ハイドロサイクロン、遠心分離器等の湿式分離機、サイクロン、エアセパレータ等の乾式分級機を用いて分級することもできる。上記の混合した原料をＳｉＣ、石英、アルミナ、ＢＮ等の坩堝に詰め、アルゴン、窒素等の不活性雰囲気、水素を含む還元雰囲気にて焼成を行う。焼成は所定の温度及び時間で行う。焼成されたものを粉砕、分散、濾過等して目的の蛍光体粉末を得る。固液分離は濾過、吸引濾過、加圧濾過、遠心分離、デカンテーション等の工業的に通常用いられる方法により行うことができる。乾燥は、真空乾燥機、熱風加熱乾燥機、コニカルドライヤー、ロータリーエバポレーター等の工業的に通常用いられる装置により行うことができる。 In addition to using a commercially available phosphor as the phosphor, for example, the fourth phosphor is the applicant's previously filed Japanese Patent Application No. 2014-202266, Japanese Patent Application No. 2020-212532. can be manufactured. Further, other phosphors can be produced, for example, as follows. Elements, oxides, carbonates, nitrides, chlorides, fluorides, sulfides, and the like of the elements contained in the composition of the phosphor are used as raw materials, and these raw materials are weighed so as to obtain a predetermined composition ratio. Further, additive materials such as flux are added to the raw materials as appropriate, and the mixture is wet- or dry-mixed using a mixer. This makes it possible to promote the solid phase reaction and form particles of uniform size. Further, as the mixer, in addition to the ball mill that is usually used industrially, a pulverizer such as a vibration mill, a roll mill, and a jet mill may be used. The specific surface area can be increased by pulverizing with a pulverizer. In addition, in order to keep the specific surface area of the obtained phosphor particles within a certain range, a settling tank, a hydrocyclone, a wet separator such as a centrifugal separator, and a dry classifier such as a cyclone and air separator, which are commonly used industrially, can be used. can also be used for classification. The above mixed raw materials are packed in a crucible made of SiC, quartz, alumina, BN, or the like, and fired in an inert atmosphere such as argon or nitrogen or a reducing atmosphere containing hydrogen. Firing is performed at a predetermined temperature and time. The calcined material is pulverized, dispersed, filtered, etc. to obtain the target phosphor powder. Solid-liquid separation can be carried out by a method commonly used industrially, such as filtration, suction filtration, pressure filtration, centrifugation, decantation, and the like. Drying can be carried out by means of equipment commonly used industrially, such as vacuum dryers, hot air dryers, conical dryers and rotary evaporators.

蛍光部材
発光装置は、例えば、蛍光体及び樹脂を含み、発光素子を被覆する蛍光部材を備える。蛍光部材を構成する樹脂としては、熱可塑性樹脂及び熱硬化性樹脂が挙げられる。熱硬化性樹脂として、具体的には、エポキシ樹脂、シリコーン樹脂、エポキシ変性シリコーン樹脂等の変性シリコーン樹脂等を挙げることができる。 Fluorescent Member The light-emitting device includes, for example, a fluorescent member that contains a phosphor and a resin and covers the light-emitting element. Thermoplastic resins and thermosetting resins are examples of resins that constitute the fluorescent member. Specific examples of thermosetting resins include epoxy resins, silicone resins, and modified silicone resins such as epoxy-modified silicone resins.

蛍光部材は、蛍光体及び樹脂に加えてその他の成分を必要に応じて含んでいてもよい。その他の成分としては、シリカ、チタン酸バリウム、酸化チタン、酸化アルミニウム等のフィラー、光安定化剤、着色剤等を挙げることができる。蛍光部材がその他の成分を含む場合、その含有量は特に制限されず、目的等に応じて適宜選択することができる。例えば、その他の成分として、フィラーを含む場合、その含有量は樹脂に対して、０．０１から２０質量％とすることができる。 The fluorescent member may optionally contain other components in addition to the fluorescent material and resin. Other components include fillers such as silica, barium titanate, titanium oxide and aluminum oxide, light stabilizers, colorants and the like. When the fluorescent member contains other components, the content is not particularly limited and can be appropriately selected according to the purpose. For example, when a filler is included as another component, its content can be 0.01 to 20% by mass with respect to the resin.

［灯具］
灯具は、上述した発光装置の少なくとも１種を備えていればよい。さらに、灯具は、上述した発光装置の少なくとも１種と、既に公知の白色系の混色光を発光する発光装置とを組み合わせて備えることもできる。灯具は、上述した発光装置の他、反射部材、保護部材、発光装置に電力を供給するための付属装置等をさらに備えていてもよい。なお、灯具は上述した発光装置を複数備えていてもよい。灯具が複数の発光装置を備える場合、同一の発光装置を複数備えていてもよく、例えば相関色温度が異なる発光装置を複数備えていてもよい。また、複数の発光装置を個別に駆動して、明るさや相関色温度を好みに合わせて調節可能な駆動装置を備えていてもよい。灯具の使用形態としては、直付型、埋め込み型、吊り下げ型等のいずれであってもよい。 [Light fixture]
The lamp may include at least one of the light emitting devices described above. Furthermore, the lamp may be equipped with a combination of at least one of the light emitting devices described above and a known light emitting device that emits mixed white light. In addition to the light emitting device described above, the lamp may further include a reflecting member, a protective member, an accessory device for supplying power to the light emitting device, and the like. Note that the lamp may include a plurality of the light emitting devices described above. When the lamp has a plurality of light emitting devices, it may have a plurality of identical light emitting devices, or may have a plurality of light emitting devices with different correlated color temperatures, for example. Further, a driving device may be provided that can individually drive a plurality of light emitting devices to adjust brightness and correlated color temperature according to preference. The lighting fixture may be used in any of a direct mounting type, an embedded type, a hanging type, and the like.

以下、本発明の実施例を具体的に説明する。 Examples of the present invention will be specifically described below.

（蛍光体）
発光装置の製造に先立ち、実施例及び比較例に使用する蛍光体として以下に示す蛍光体をそれぞれ準備した。
Ｙ３（Ａｌ，Ｇａ）５Ｏ１２：Ｃｅ （Ｉ）
Ｌｕ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩ）
Ｙ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩＩ）
Ａ２[Ｍ１１-ｐＭｎ４＋ ｐＦ６] （ＩＶ）
（ただし、上記式（ＩＶ）中、ＡはＫであり、Ｍ１はＳｉであり、ｐは０＜ｐ＜０．２を満たす数を示す。）
（Ｓｒ，Ｃａ）ＡｌＳｉＮ３：Ｅｕ （Ｖ）
第一蛍光体として、式（Ｉ）で表される組成を有し、発光ピーク波長が５４５ｎｍであり、半値幅が１０４．０ｎｍである、希土類アルミン酸塩蛍光体（以下、「ＧＹＡＧ１」ともいう。）と、式（Ｉ）で表される組成を有し、発光ピーク波長が５３３ｎｍであり、半値幅が１０７．０ｎｍである希土類アルミン酸塩蛍光体（以下、「ＧＹＡＧ２」ともいう。）を準備した。
第二蛍光体として、式（ＩＩ）で表される組成を有し、発光ピーク波長が５３３ｎｍであり、半値幅が１００．５ｎｍである希土類アルミン酸塩蛍光体（以下、「ＬＡＧ」ともいう。）を準備した。
第三蛍光体として、式（ＩＩＩ）で表される組成を有し、発光ピーク波長が５４５ｎｍであり、半値幅が１０９．５ｎｍである希土類アルミン酸塩蛍光体（以下、「ＹＡＧ」ともいう。）を準備した。
第四蛍光体として、式（ＩＶ）で表される組成を有し、発光ピーク波長が６３０ｎｍであり、半値幅が１４ｎｍである赤色発光のフッ化物蛍光体（以下、「ＫＳＦ」ともいう。）を準備した。
第五蛍光体として、式（Ｖ）で表される組成を有し、発光ピーク波長が６００ｎｍ以上６３０ｎｍ以下の範囲内であり、半値幅が８０ｎｍである赤色発光の窒化物蛍光体（以下、「ＳＣＡＳＮ」ともいう。）を準備した。
さらに、比較例の発光装置に使用する蛍光体として、下記式（ＶＩ）で表わされる組成を有し、発光ピーク波長が５２１ｎｍであり、半値幅が６３ｎｍであるクロロシリケート蛍光体を準備した。
Ｃａ８ＭｇＳｉ４Ｏ１６Ｃｌｌ２：Ｅｕ （ＶＩ）
なお、上述した各蛍光体の発光ピーク波長及び半値幅等は、蛍光体の製造条件、組成の変更等により調整することが可能である。 (Phosphor)
Prior to manufacturing the light-emitting device, the following phosphors were prepared as phosphors used in Examples and Comparative Examples.
Y3 ( Al,Ga) 5O12 :Ce(I)
Lu3Al5O12 : Ce ( II)
Y3Al5O12 : Ce ( III )
A2 [M11 - pMn4 +pF6 ] (IV)
(In formula (IV) above, A is K, M1 is Si, and p is a number satisfying 0<p<0.2.)
(Sr, Ca) AlSiN3 :Eu(V)
As the first phosphor, a rare earth aluminate phosphor (hereinafter also referred to as "GYAG1") having a composition represented by formula (I), an emission peak wavelength of 545 nm, and a half width of 104.0 nm ) and a rare earth aluminate phosphor (hereinafter also referred to as “GYAG2”) having a composition represented by formula (I) and having an emission peak wavelength of 533 nm and a half width of 107.0 nm. Got ready.
As the second phosphor, a rare earth aluminate phosphor (hereinafter also referred to as “LAG”) having a composition represented by formula (II), an emission peak wavelength of 533 nm, and a half width of 100.5 nm. ) was prepared.
As the third phosphor, a rare earth aluminate phosphor (hereinafter also referred to as “YAG”) having a composition represented by formula (III), an emission peak wavelength of 545 nm, and a half width of 109.5 nm. ) was prepared.
As the fourth phosphor, a red-emitting fluoride phosphor (hereinafter also referred to as “KSF”) having a composition represented by formula (IV), an emission peak wavelength of 630 nm, and a half width of 14 nm. prepared.
As the fifth phosphor, a red-emitting nitride phosphor having a composition represented by formula (V), an emission peak wavelength in the range of 600 nm or more and 630 nm or less, and a half width of 80 nm (hereinafter referred to as " SCASN”) was prepared.
Further, a chlorosilicate phosphor having a composition represented by the following formula (VI), an emission peak wavelength of 521 nm, and a half width of 63 nm was prepared as a phosphor used in the light emitting device of the comparative example.
Ca8MgSi4O16Cl12 : Eu ( VI)
The emission peak wavelength, half width, etc. of each phosphor described above can be adjusted by changing the manufacturing conditions and composition of the phosphor.

発光素子として、発光ピーク波長が４５０ｎｍである窒化ガリウム系の半導体発光素子をそれぞれ準備した。 A gallium nitride-based semiconductor light-emitting device having an emission peak wavelength of 450 nm was prepared as the light-emitting device.

（実施例１）
発光装置の作製
発光ピーク波長が４５０ｎｍの青色発光ＬＥＤ（発光素子）と、希土類アルミン酸塩蛍光体として第一蛍光体であるＧＹＡＧ１及び第二蛍光体であるＬＡＧ、第四蛍光体であるＫＳＦ、第五蛍光体であるＳＣＡＳＮを組合せて、発光装置を作製した。
相関色温度が６５００Ｋ付近になるように各蛍光体の含有率を以下の表１に示す値となるように調節して、配合した蛍光体をシリコーン樹脂に添加し、混合分散した後、更に脱泡することにより蛍光体含有樹脂組成物を得た。次にこの蛍光体含有樹脂組成物を発光素子の上に注入、充填し、さらに加熱することで樹脂組成物を硬化させた。このような工程により発光装置を作製した。 (Example 1)
Fabrication of light-emitting device A blue light-emitting LED (light-emitting element) having an emission peak wavelength of 450 nm, a first phosphor GYAG1 as a rare earth aluminate phosphor, a second phosphor LAG, a fourth phosphor KSF, A light-emitting device was fabricated by combining SCASN, which is the fifth phosphor.
The content of each phosphor is adjusted to the value shown in Table 1 below so that the correlated color temperature is around 6500K, and the blended phosphor is added to the silicone resin, mixed and dispersed, and then removed. A phosphor-containing resin composition was obtained by foaming. Next, this phosphor-containing resin composition was injected and filled on the light emitting element, and further heated to cure the resin composition. A light-emitting device was manufactured through such steps.

（実施例２から６）
第一蛍光体、第二蛍光体及び第三蛍光体からなる群から選択される少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体、第四蛍光体及び第五蛍光体の組合せと、各蛍光体の含有比率が以下の表１に示す値となるように変更したこと以外は実施例１と同様にして、相関色温度が２７００Ｋから５０００Ｋ付近となるように、実施例２から６の発光装置を作製した。 (Examples 2 to 6)
a combination of two or more rare earth aluminate phosphors, a fourth phosphor and a fifth phosphor, including at least one selected from the group consisting of a first phosphor, a second phosphor and a third phosphor; , in the same manner as in Example 1 except that the content ratio of each phosphor was changed to the value shown in Table 1 below, and the correlated color temperature was adjusted from 2700K to around 5000K in Examples 2 to 6. was fabricated.

Figure 0007125631000001
Figure 0007125631000001

実施例１から６に係る発光装置について、発光色の色度座標、相関色温度（Ｔｃｐ；Ｋ）、平均演色評価数（Ｒａ（Ｒ１からＲ８））、特殊演色評価数（Ｒ９からＲ１５）を測定した。具体的には、実施例及び比較例に用いた各発光装置について、分光測光装置（ＰＭＡ－１２、浜松ホトニクス株式会社）と積分球を組み合わせた光計測システムを用いて、ＣＩＥ１９３１色度図の色度座標系における色度座標（ｘ、ｙ）、光束、放射束（分光全放射束）を求めた。発光色の色度座標、相関色温度（Ｔｃｐ；Ｋ）の結果は、表１に併せて示す。演色評価数の結果は以下の表２に示す。
実施例及び後述する比較例の各発光装置の発光スペクトルは、分光蛍光光度計を用いて測定した。発光素子の発光ピークに対する第四蛍光体の発光ピークの発光ピーク強度比を上記表１に併せて示す。図２から図７に実施例１から６の各発光装置の各発光スペクトル及び基準光源のスペクトルを示す。 For the light emitting devices according to Examples 1 to 6, the chromaticity coordinates of the emitted color, the correlated color temperature (Tcp; K), the general color rendering index (Ra (R1 to R8)), and the special color rendering index (R9 to R15) were measured. It was measured. Specifically, for each light-emitting device used in Examples and Comparative Examples, a light measurement system combining a spectrophotometer (PMA-12, Hamamatsu Photonics Co., Ltd.) and an integrating sphere was used to measure the color of the CIE 1931 chromaticity diagram. Chromaticity coordinates (x, y), luminous flux, and radiant flux (spectral total radiant flux) in the degree coordinate system were obtained. Table 1 also shows the results of the chromaticity coordinates of the emitted light and the correlated color temperature (Tcp; K). The color rendering index results are shown in Table 2 below.
The emission spectrum of each light-emitting device of Examples and Comparative Examples described later was measured using a spectrofluorophotometer. Table 1 also shows the emission peak intensity ratio of the emission peak of the fourth phosphor to the emission peak of the light emitting element. 2 to 7 show the emission spectrum of each light emitting device of Examples 1 to 6 and the spectrum of the reference light source.

Figure 0007125631000002
Figure 0007125631000002

（比較例１）
蛍光体として、第四蛍光体を使用せず、式（ＶＩ）で表わされる組成を有し、発光ピーク波長が５２１ｎｍであるクロロシリケート蛍光体と、第一蛍光体ＧＹＡＧ２と、第五蛍光体ＳＣＡＳＮとを組み合わせて用い、各蛍光体の含有比率が以下の表３に示す値となるようにしたこと以外は実施例１と同様にして、相関色温度が６５００Ｋ付となるように発光装置を作製した。 (Comparative example 1)
As phosphors, a chlorosilicate phosphor that does not use a fourth phosphor, has a composition represented by formula (VI), and has an emission peak wavelength of 521 nm, a first phosphor GYAG2, and a fifth phosphor SCASN A light emitting device having a correlated color temperature of 6500 K was produced in the same manner as in Example 1 except that the content ratio of each phosphor was set to the value shown in Table 3 below. did.

（比較例２から６）
各蛍光体の含有比率が以下の表３に示す値となるように蛍光体の量を変更したこと以外は比較例１と同様にして、相関色温度が２７００Ｋから５０００Ｋ付近となるように、比較例２から６の発光装置を作製した。 (Comparative Examples 2 to 6)
In the same manner as in Comparative Example 1 except that the amount of the phosphor was changed so that the content ratio of each phosphor was the value shown in Table 3 below, comparison was performed so that the correlated color temperature was from 2700K to around 5000K. Light emitting devices of Examples 2 to 6 were fabricated.

Figure 0007125631000003
Figure 0007125631000003

比較例１から比較例６に係る各発光装置について、実施例に係る発光装置と同様にして各発光装置の色度座標を測定し、表３に示し、演色評価数の結果を以下の表４に示す。 For each light emitting device according to Comparative Examples 1 to 6, the chromaticity coordinates of each light emitting device were measured in the same manner as the light emitting device according to the example, and the results are shown in Table 3, and the results of the color rendering index are shown in Table 4 below. shown in

Figure 0007125631000004
Figure 0007125631000004

表２及び表４に示されるように、相関色温度がほぼ同じ実施例及び比較例の各発光装置のＲａ、Ｒ１５を比べると、Ｒａについては、実施例及び比較例において、ほぼ同等の数値が得られた。一方、Ｒ１５については、各相関色温度において、実施例の発光装置のほうが比較例よりも高い数値が得られており、実施例の発光装置は、特定の演色性評価数において比較例の発光装置よりも演色性が高いことが分かる。また、実施例の各発光装置の相対光束は、相関色温度がほぼ同じ実施例の発光装置及び比較例の発光装置を比べると、各比較例の発光装置の光束を１００％として、実施例１の発光装置が１０８．６％、実施例２の発光装置が１１１．２％、実施例３の発光装置が１１５．５％、実施例４の発光装置が１１７．７％、実施例５の発光装置が１１４．０％、実施例６が１１１．８％となった。いずれの実施例の発光装置においても高い光束が得られた。
以上のことから、実施例に係る発光装置は、高い光束及び演色性を有することが分かる。 As shown in Tables 2 and 4, when comparing the Ra and R15 of the light emitting devices of Examples and Comparative Examples having substantially the same correlated color temperature, Ra values of Examples and Comparative Examples are substantially the same. Got. On the other hand, with respect to R15, the light emitting devices of the examples have higher values than the comparative examples at each correlated color temperature, and the light emitting devices of the examples have a specific color rendering index compared to the light emitting device of the comparative examples. It can be seen that the color rendering property is higher than Further, the relative luminous flux of each light-emitting device of the example is compared with the light-emitting device of the example and the light-emitting device of the comparative example having substantially the same correlated color temperature. 108.6% of the light emitting device of Example 2, 111.2% of the light emitting device of Example 3, 115.5% of the light emitting device of Example 3, 117.7% of the light emitting device of Example 4, and 117.7% of the light emitting device of Example 5 114.0% for the device and 111.8% for Example 6. A high luminous flux was obtained in the light emitting device of any of the examples.
From the above, it can be seen that the light emitting device according to the example has high luminous flux and color rendering properties.

図２から図７に、実施例１から６及び比較例１から６に係る各発光装置の発光スペクトル及び各相関色温度の基準光源のスペクトルを示した。実施例１から６に係る各発光装置は、それぞれ６５００Ｋ、５０００Ｋ、４０００Ｋ、３５００Ｋ、３０００Ｋ、２７００Ｋの相関色温度に近い相関色温度の光を発した。相関色温度が６５００Ｋ、５０００Ｋ、及び４０００Ｋに近い光を発する実施例１から３の各発光装置は、４３０ｎｍ以上４７０ｎｍ以下の範囲にある青紫色から青色の発光スペクトルが突出して高い強度とならないように抑制し、基準光源の発光スペクトルに近似させることができた。３５００Ｋ、３０００Ｋ、及び２７００Ｋに近い相関色温度の光を発する実施例４から６の各発光装置は、青紫色から青色の発光スペクトルが突出して高い強度とならないように抑制し、黄色から緑色発光の波長領域、ＪＩＳ Ｚ８１１０に準拠すると、４９５ｎｍから５８４ｎｍの波長範囲における発光スペクトルが、基準光源の発光スペクトルよりも強度が高くなることなく、基準光源により近似していた。 2 to 7 show the emission spectrum of each light emitting device according to Examples 1 to 6 and Comparative Examples 1 to 6 and the spectrum of the reference light source for each correlated color temperature. Each of the light emitting devices according to Examples 1 to 6 emitted light with correlated color temperatures close to the correlated color temperatures of 6500K, 5000K, 4000K, 3500K, 3000K, and 2700K, respectively. Each of the light-emitting devices of Examples 1 to 3, which emits light with correlated color temperatures close to 6500 K, 5000 K, and 4000 K, was adjusted so that the emission spectrum from bluish purple to blue in the range of 430 nm or more and 470 nm or less did not have a high intensity. It was possible to suppress and approximate the emission spectrum of the reference light source. Each of the light-emitting devices of Examples 4 to 6, which emit light with correlated color temperatures close to 3500 K, 3000 K, and 2700 K, suppresses the emission spectrum from bluish purple to blue to have a high intensity, and suppresses the emission spectrum from yellow to green. According to the wavelength region, JIS Z8110, the emission spectrum in the wavelength range from 495 nm to 584 nm was closer to the reference light source without increasing the intensity of the emission spectrum of the reference light source.

本開示の発光装置は、発光特性に優れた照明器具、ＬＥＤディスプレイ、カメラのフラッシュライト等に利用することができる。特に、高い光束と演色性が求められる照明装置や光源に好適に利用することができる。さらに、この発光装置を備えた灯具として利用することができる。 The light-emitting device of the present disclosure can be used for lighting fixtures, LED displays, camera flashlights, and the like, which have excellent light-emitting properties. In particular, it can be suitably used for lighting devices and light sources that require high luminous flux and color rendering properties. Furthermore, it can be used as a lamp equipped with this light emitting device.

１０：発光素子、５０：蛍光部材、７０：蛍光体、７１、７２：第一乃至第三蛍光体、７３：第四蛍光体、７４：第五蛍光体、１００：発光装置。 10: Light-emitting element, 50: Fluorescent member, 70: Phosphor, 71, 72: First to third phosphors, 73: Fourth phosphor, 74: Fifth phosphor, 100: Light-emitting device.

Claims (12)

４３０ｎｍ以上４７０ｎｍ以下の範囲内に発光ピーク波長を有する発光素子と、
下記式（Ｉ）で表される組成を有する第一蛍光体、下記式（ＩＩ）で表される組成を有する第二蛍光体及び下記式（ＩＩＩ）で表される組成を有する第三蛍光体から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、下記式（ＩＶ）で表わされる組成を有する第四蛍光体と、下記式（Ｖ）で表わされる組成を有する第五蛍光体と、を含む蛍光部材と、を備え、前記希土類アルミン酸塩蛍光体の総含有量に対する前記第四蛍光体の含有率が０．３５以上０．７以下の範囲内であり、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置。
Ｙ３（Ａｌ，Ｇａ）５Ｏ１２：Ｃｅ （Ｉ）
Ｌｕ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩ）
Ｙ３Ａｌ５Ｏ１２：Ｃｅ （ＩＩＩ）
Ａ２[Ｍ１１-ｐＭｎ４＋ ｐＦ６] （ＩＶ）
（Ｓｒ，Ｃａ）ＡｌＳｉＮ３：Ｅｕ （Ｖ）
（前記式（ＩＶ）中、Ａは、Ｋ、Ｌｉ、Ｎａ、Ｒｂ、Ｃｓ及びＮＨ４ ＋からなる群から選ばれる少なくとも１種を含み、Ｍ１は、第４族元素、第１３族元素及び第１４族元素からなる群から選ばれる少なくとも１種の元素を含む。ｐは０＜ｐ＜０．２を満たす数を示す。） a light-emitting element having an emission peak wavelength in the range of 430 nm or more and 470 nm or less;
A first phosphor having a composition represented by the following formula (I), a second phosphor having a composition represented by the following formula (II), and a third phosphor having a composition represented by the following formula (III) a fourth phosphor having a composition represented by the following formula (IV), and a composition represented by the following formula (V): and a fluorescent member containing a fifth phosphor , wherein the content ratio of the fourth phosphor with respect to the total content of the rare earth aluminate phosphor is in the range of 0.35 or more and 0.7 or less, A light-emitting device that emits light with a correlated color temperature in the range of 4750K to 7000K .
Y3 ( Al,Ga) 5O12 :Ce(I)
Lu3Al5O12 : Ce ( II)
Y3Al5O12 : Ce ( III )
A2 [M11 - pMn4 +pF6 ] (IV)
(Sr, Ca) AlSiN3 :Eu(V)
(In the formula (IV), A contains at least one selected from the group consisting of K, Li, Na, Rb, Cs and NH 4 + , M1 is a Group 4 element, a Group 13 element and It contains at least one element selected from the group consisting of Group 14 elements, and p represents a number that satisfies 0<p<0.2.) ４３０ｎｍ以上４７０ｎｍ以下の範囲内に発光ピーク波長を有する発光素子と、
下記式（Ｉ）で表される組成を有する第一蛍光体、下記式（ＩＩ）で表される組成を有する第二蛍光体及び下記式（ＩＩＩ）で表される組成を有する第三蛍光体から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、下記式（ＩＶ）で表わされる組成を有する第四蛍光体と、下記式（Ｖ）で表わされる組成を有する第五蛍光体と、を含む蛍光部材と、を備え、前記希土類アルミン酸塩蛍光体、前記第四蛍光体及び前記第五蛍光体の総含有量に対する前記第四蛍光体の含有率が０．２５以上０．４５以下の範囲内であり、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置。
Ｙ ３ （Ａｌ，Ｇａ） ５ Ｏ １２ ：Ｃｅ （Ｉ）
Ｌｕ ３ Ａｌ ５ Ｏ １２ ：Ｃｅ （ＩＩ）
Ｙ ３ Ａｌ ５ Ｏ １２ ：Ｃｅ （ＩＩＩ）
Ａ ２ [Ｍ１ １-ｐ Ｍｎ ４＋ ｐ Ｆ ６ ] （ＩＶ）
（Ｓｒ，Ｃａ）ＡｌＳｉＮ ３ ：Ｅｕ （Ｖ）
（前記式（ＩＶ）中、Ａは、Ｋ、Ｌｉ、Ｎａ、Ｒｂ、Ｃｓ及びＮＨ ４ ＋ からなる群から選ばれる少なくとも１種を含み、Ｍ１は、第４族元素、第１３族元素及び第１４族元素からなる群から選ばれる少なくとも１種の元素を含む。ｐは０＜ｐ＜０．２を満たす数を示す。） a light-emitting element having an emission peak wavelength in the range of 430 nm or more and 470 nm or less;
A first phosphor having a composition represented by the following formula (I), a second phosphor having a composition represented by the following formula (II), and a third phosphor having a composition represented by the following formula (III) a fourth phosphor having a composition represented by the following formula (IV), and a composition represented by the following formula (V): and a phosphor member containing a fifth phosphor, wherein the content ratio of the fourth phosphor with respect to the total content of the rare earth aluminate phosphor, the fourth phosphor and the fifth phosphor is 0.5. A light-emitting device that emits light having a correlated color temperature in the range of 25 to 0.45 and in the range of 4750K to 7000K.
Y3 ( Al,Ga) 5O12 : Ce ( I)
Lu3Al5O12 : Ce ( II ) _
Y3Al5O12 : Ce ( III ) _
A2 [M11 - pMn4 + pF6 ] ( IV )
(Sr , Ca)AlSiN3 :Eu(V)
(In the formula (IV), A contains at least one selected from the group consisting of K, Li, Na, Rb, Cs and NH 4 + , M1 is a Group 4 element, a Group 13 element and It contains at least one element selected from the group consisting of Group 14 elements, and p represents a number that satisfies 0<p<0.2.) ４３０ｎｍ以上４７０ｎｍ以下の範囲内に発光ピーク波長を有する発光素子と、
下記式（Ｉ）で表される組成を有する第一蛍光体、下記式（ＩＩ）で表される組成を有する第二蛍光体及び下記式（ＩＩＩ）で表される組成を有する第三蛍光体から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、下記式（ＩＶ）で表わされる組成を有する第四蛍光体と、下記式（Ｖ）で表わされる組成を有する第五蛍光体と、を含む蛍光部材と、を備え、前記希土類アルミン酸塩蛍光体、前記第四蛍光体及び前記第五蛍光体の総含有量に対する前記希土類アルミン酸塩蛍光体の総含有量の含有率が０．５以上０．７５以下の範囲内であり、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置。
Ｙ ３ （Ａｌ，Ｇａ） ５ Ｏ １２ ：Ｃｅ （Ｉ）
Ｌｕ ３ Ａｌ ５ Ｏ １２ ：Ｃｅ （ＩＩ）
Ｙ ３ Ａｌ ５ Ｏ １２ ：Ｃｅ （ＩＩＩ）
Ａ ２ [Ｍ１ １-ｐ Ｍｎ ４＋ ｐ Ｆ ６ ] （ＩＶ）
（Ｓｒ，Ｃａ）ＡｌＳｉＮ ３ ：Ｅｕ （Ｖ）
（前記式（ＩＶ）中、Ａは、Ｋ、Ｌｉ、Ｎａ、Ｒｂ、Ｃｓ及びＮＨ ４ ＋ からなる群から選ばれる少なくとも１種を含み、Ｍ１は、第４族元素、第１３族元素及び第１４族元素からなる群から選ばれる少なくとも１種の元素を含む。ｐは０＜ｐ＜０．２を満たす数を示す。） a light-emitting element having an emission peak wavelength in the range of 430 nm or more and 470 nm or less;
A first phosphor having a composition represented by the following formula (I), a second phosphor having a composition represented by the following formula (II), and a third phosphor having a composition represented by the following formula (III) a fourth phosphor having a composition represented by the following formula (IV), and a composition represented by the following formula (V): and a phosphor member containing a fifth phosphor , wherein the total content of the rare earth aluminate phosphor with respect to the total content of the rare earth aluminate phosphor, the fourth phosphor, and the fifth phosphor is within the range of 0.5 to 0.75 and the correlated color temperature is within the range of 4750K to 7000K.
Y3 ( Al,Ga) 5O12 : Ce ( I)
Lu3Al5O12 : Ce ( II ) _
Y3Al5O12 : Ce ( III ) _
A2 [M11 - pMn4 + pF6 ] ( IV )
(Sr , Ca)AlSiN3 :Eu(V)
(In the formula (IV), A contains at least one selected from the group consisting of K, Li, Na, Rb, Cs and NH 4 + , M1 is a Group 4 element, a Group 13 element and It contains at least one element selected from the group consisting of Group 14 elements, and p represents a number that satisfies 0<p<0.2.) ４３０ｎｍ以上４７０ｎｍ以下の範囲内に発光ピーク波長を有する発光素子と、
下記式（Ｉ）で表される組成を有する第一蛍光体、下記式（ＩＩ）で表される組成を有する第二蛍光体及び下記式（ＩＩＩ）で表される組成を有する第三蛍光体から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、下記式（ＩＶ）で表わされる組成を有する第四蛍光体と、下記式（Ｖ）で表わされる組成を有する第五蛍光体と、を含む蛍光部材と、を備え、前記希土類アルミン酸塩蛍光体、前記第四蛍光体及び前記第五蛍光体の総含有量に対する前記第四蛍光体及び前記第五蛍光体の含有率が０．２５以上０．５以下の範囲内であり、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置。
Ｙ ３ （Ａｌ，Ｇａ） ５ Ｏ １２ ：Ｃｅ （Ｉ）
Ｌｕ ３ Ａｌ ５ Ｏ １２ ：Ｃｅ （ＩＩ）
Ｙ ３ Ａｌ ５ Ｏ １２ ：Ｃｅ （ＩＩＩ）
Ａ ２ [Ｍ１ １-ｐ Ｍｎ ４＋ ｐ Ｆ ６ ] （ＩＶ）
（Ｓｒ，Ｃａ）ＡｌＳｉＮ ３ ：Ｅｕ （Ｖ）
（前記式（ＩＶ）中、Ａは、Ｋ、Ｌｉ、Ｎａ、Ｒｂ、Ｃｓ及びＮＨ ４ ＋ からなる群から選ばれる少なくとも１種を含み、Ｍ１は、第４族元素、第１３族元素及び第１４族元素からなる群から選ばれる少なくとも１種の元素を含む。ｐは０＜ｐ＜０．２を満たす数を示す。） a light-emitting element having an emission peak wavelength in the range of 430 nm or more and 470 nm or less;
A first phosphor having a composition represented by the following formula (I), a second phosphor having a composition represented by the following formula (II), and a third phosphor having a composition represented by the following formula (III) a fourth phosphor having a composition represented by the following formula (IV), and a composition represented by the following formula (V): and a phosphor member containing a fifth phosphor , wherein the fourth phosphor and the fifth phosphor with respect to the total content of the rare earth aluminate phosphor, the fourth phosphor and the fifth phosphor is in the range of 0.25 to 0.5 and the correlated color temperature is in the range of 4750K to 7000K.
Y3 ( Al,Ga) 5O12 : Ce ( I)
Lu3Al5O12 : Ce ( II ) _
Y3Al5O12 : Ce ( III ) _
A2 [M11 - pMn4 + pF6 ] ( IV )
(Sr , Ca)AlSiN3 :Eu(V)
(In the formula (IV), A contains at least one selected from the group consisting of K, Li, Na, Rb, Cs and NH 4 + , M1 is a Group 4 element, a Group 13 element and It contains at least one element selected from the group consisting of Group 14 elements, and p represents a number that satisfies 0<p<0.2.) ４３０ｎｍ以上４７０ｎｍ以下の範囲内に発光ピーク波長を有する発光素子と、
下記式（Ｉ）で表される組成を有する第一蛍光体、下記式（ＩＩ）で表される組成を有する第二蛍光体及び下記式（ＩＩＩ）で表される組成を有する第三蛍光体から選択された少なくとも１種を含む、２種以上の希土類アルミン酸塩蛍光体と、下記式（ＩＶ）で表わされる組成を有する第四蛍光体と、下記式（Ｖ）で表わされる組成を有する第五蛍光体と、を含む蛍光部材と、を備え、発光スペクトルにおける前記第四蛍光体の発光ピークの前記発光素子の発光ピークに対する発光ピーク強度比が、１．０以上２．０以下の範囲内であり、相関色温度が４７５０Ｋ以上７０００Ｋ以下の範囲内の光を発する発光装置。
Ｙ ３ （Ａｌ，Ｇａ） ５ Ｏ １２ ：Ｃｅ （Ｉ）
Ｌｕ ３ Ａｌ ５ Ｏ １２ ：Ｃｅ （ＩＩ）
Ｙ ３ Ａｌ ５ Ｏ １２ ：Ｃｅ （ＩＩＩ）
Ａ ２ [Ｍ１ １-ｐ Ｍｎ ４＋ ｐ Ｆ ６ ] （ＩＶ）
（Ｓｒ，Ｃａ）ＡｌＳｉＮ ３ ：Ｅｕ （Ｖ）
（前記式（ＩＶ）中、Ａは、Ｋ、Ｌｉ、Ｎａ、Ｒｂ、Ｃｓ及びＮＨ ４ ＋ からなる群から選ばれる少なくとも１種を含み、Ｍ１は、第４族元素、第１３族元素及び第１４族元素からなる群から選ばれる少なくとも１種の元素を含む。ｐは０＜ｐ＜０．２を満たす数を示す。） a light-emitting element having an emission peak wavelength in the range of 430 nm or more and 470 nm or less;
A first phosphor having a composition represented by the following formula (I), a second phosphor having a composition represented by the following formula (II), and a third phosphor having a composition represented by the following formula (III) a fourth phosphor having a composition represented by the following formula (IV), and a composition represented by the following formula (V): and a fluorescent member containing a fifth phosphor, wherein the emission peak intensity ratio of the emission peak of the fourth phosphor to the emission peak of the light emitting element in the emission spectrum is in the range of 1.0 or more and 2.0 or less. A light-emitting device that emits light with a correlated color temperature within the range of 4750K or more and 7000K or less.
Y3 ( Al,Ga) 5O12 : Ce ( I)
Lu3Al5O12 : Ce ( II ) _
Y3Al5O12 : Ce ( III ) _
A2 [M11 - pMn4 + pF6 ] ( IV )
(Sr , Ca)AlSiN3 :Eu(V)
(In the formula (IV), A contains at least one selected from the group consisting of K, Li, Na, Rb, Cs and NH 4 + , M1 is a Group 4 element, a Group 13 element and It contains at least one element selected from the group consisting of Group 14 elements, and p represents a number that satisfies 0<p<0.2.) 前記発光素子が、４４０ｎｍ以上４６０ｎｍ以下の範囲内に発光ピーク波長を有する請求項１から５のいずれか１項に記載の発光装置。 6. The light emitting device according to any one of claims 1 to 5, wherein the light emitting element has an emission peak wavelength within a range of 440 nm or more and 460 nm or less. 前記第一蛍光体の発光ピーク波長が５２０ｎｍ以上５５０ｎｍ以下の範囲内にあり、半値幅が９５ｎｍ以上１２０ｎｍ以下の範囲内である請求項１から６のいずれか１項に記載の発光装置。 The light emitting device according to any one of claims 1 to 6, wherein the first phosphor has an emission peak wavelength in the range of 520 nm or more and 550 nm or less, and a half width in the range of 95 nm or more and 120 nm or less. 前記第二蛍光体の発光ピーク波長が５００ｎｍ以上５４５ｎｍ以下の範囲内にあり、半値幅が９５ｎｍ以上１０５ｎｍ以下の範囲内である請求項１から７のいずれか１項に記載の発光装置。 The light emitting device according to any one of claims 1 to 7, wherein the second phosphor has an emission peak wavelength in the range of 500 nm or more and 545 nm or less, and a half width in the range of 95 nm or more and 105 nm or less. 前記第三蛍光体の発光ピーク波長が５３５ｎｍ以上５５５ｎｍ以下の範囲内にあり、半値幅が１００ｎｍ以上１２０ｎｍ以下の範囲内である請求項１から８のいずれか１項に記載の発光装置。 The light emitting device according to any one of claims 1 to 8, wherein the third phosphor has an emission peak wavelength in the range of 535 nm or more and 555 nm or less, and a half width in the range of 100 nm or more and 120 nm or less. 前記第五蛍光体の発光ピーク波長が６００ｎｍ以上６３０ｎｍ以下の範囲内にあり、半値幅が８０ｎｍ以下である請求項１から９のいずれか１項に記載の発光装置。 The light emitting device according to any one of claims 1 to 9, wherein the fifth phosphor has an emission peak wavelength in the range of 600 nm or more and 630 nm or less, and has a half width of 80 nm or less. 平均演色評価数Ｒａが９０以上又は特殊演色評価数Ｒ１５が８５以上である請求項１から１０のいずれか１項に記載の発光装置。 11. The light emitting device according to claim 1, wherein the general color rendering index Ra is 90 or more, or the special color rendering index R15 is 85 or more. 前記請求項１から１１のいずれか１項に記載の発光装置を備えた灯具。
A lamp comprising the light emitting device according to any one of claims 1 to 11 .
JP2021011944A 2020-03-27 2021-01-28 Light-emitting device and lamp equipped with the same Active JP7125631B2 (en)