JP7103006B2 - 銅張積層板 - Google Patents
銅張積層板 Download PDFInfo
- Publication number
- JP7103006B2 JP7103006B2 JP2018134850A JP2018134850A JP7103006B2 JP 7103006 B2 JP7103006 B2 JP 7103006B2 JP 2018134850 A JP2018134850 A JP 2018134850A JP 2018134850 A JP2018134850 A JP 2018134850A JP 7103006 B2 JP7103006 B2 JP 7103006B2
- Authority
- JP
- Japan
- Prior art keywords
- copper
- copper plating
- plating film
- chlorine concentration
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
図1に示すように、本発明の一実施形態に係る銅張積層板1は、基材10と、基材10の表面に形成された銅めっき被膜20とからなる。図1に示すように基材10の片面のみに銅めっき被膜20が形成されてもよいし、基材10の両面に銅めっき被膜20が形成されてもよい。
めっき装置3は、ロールツーロールにより長尺帯状の基材10を搬送しつつ、基材10に対して電解めっきを行なう装置である。めっき装置3はロール状に巻回された基材10を繰り出す供給装置31と、めっき後の基材10(銅張積層板1)をロール状に巻き取る巻取装置32とを有する。
(実施例1)
つぎの手順で、基材を準備した。ベースフィルムとして、厚さ35μmのポリイミドフィルム(宇部興産社製 Upilex-35SGAV1)を用意した。ベースフィルムをマグネトロンスパッタリング装置にセットした。マグネトロンスパッタリング装置内にはニッケルクロム合金ターゲットと銅ターゲットとが設置されている。ニッケルクロム合金ターゲットの組成はCrが20質量%、Niが80質量%である。真空雰囲気下で、ベースフィルムの片面に、厚さ25nmのニッケルクロム合金からなる下地金属層を形成し、その上に厚さ100nmの銅薄膜層を形成した。
実施例1と同様の手順で銅張積層板を得た。ただし、電解めっきにおいて、空送期間が7回含まれるように電流密度を変化させた。その余の条件は実施例1と同様である。
実施例1と同様の手順で銅張積層板を得た。ただし、電解めっきにおいて、電流密度を3.2A/dm2とし、空送期間を設けなかった。その余の条件は実施例1と同様である。
実施例1と同様の手順で銅張積層板を得た。ただし、電解めっきにおいて、電流密度を0.33A/dm2とし、空送期間を設けなかった。その余の条件は実施例1と同様である。
実施例1、2および比較例1、2で得られた銅張積層板に対して、銅めっき被膜の塩素濃度を測定した。測定は二次イオン質量分析法によって行なった。測定装置としてアルバック・ファイ株式会社の四重極型二次イオン質量分析装置(PHI ADEPT-1010)を用いた。測定条件は、一次イオン種をCs+、一次加速電圧を5.0kV、検出領域を96×96μmとした。なお、本明細書における塩素濃度の値は、前記条件で測定した値を基準とする。
実施例1、2および比較例1、2で得られた銅張積層板について、めっき処理から7日経過後に断面を観察した。図6(A)に実施例1の断面のSEM画像を示す。図6(B)に実施例2の断面のSEM画像を示す。図7(A)に比較例1の断面のSEM画像を示す。図7(B)に比較例2の断面のSEM画像を示す。これらのSEM画像より、実施例1、2は比較例1、2に比べて、銅めっき被膜の結晶粒が微細であることが分かる。
実施例1、2および比較例1、2で得られた銅張積層板に対して、化学研磨前の銅めっき被膜の表面粗さを測定した。ここで、表面積比の測定にはキーエンス社製レーザー顕微鏡VK-9510を用いた。70×93μmの測定エリアの測定表面積から表面積比を求めた。
10 基材
11 ベースフィルム
12 金属層
13 下地金属層
14 銅薄膜層
20 銅めっき被膜
21 高塩素濃度層
22 低塩素濃度層
Claims (2)
- ベースフィルムと、
前記ベースフィルムの表面に形成された金属層と、
前記金属層の表面に形成され、二次イオン質量分析法により測定した塩素濃度が1×10 19 atoms/cm 3 以上の層を有する銅めっき被膜と、を備え、
前記銅めっき被膜の結晶粒の平均粒子径が300nm以下である
ことを特徴とする銅張積層板。 - 前記銅めっき被膜は、二次イオン質量分析法により測定した塩素濃度が1×10 19 atoms/cm 3 以上である高塩素濃度層と、二次イオン質量分析法により測定した塩素濃度が1×10 19 atoms/cm 3 未満である低塩素濃度層とが交互に積層されてなる
ことを特徴とする請求項1記載の銅張積層板。