JP7008421B2 - シラン架橋ポリエチレン管 - Google Patents
シラン架橋ポリエチレン管 Download PDFInfo
- Publication number
- JP7008421B2 JP7008421B2 JP2017065015A JP2017065015A JP7008421B2 JP 7008421 B2 JP7008421 B2 JP 7008421B2 JP 2017065015 A JP2017065015 A JP 2017065015A JP 2017065015 A JP2017065015 A JP 2017065015A JP 7008421 B2 JP7008421 B2 JP 7008421B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- parts
- polyethylene
- density
- cross
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]下記要件(1)および(2)を満たす高密度ポリエチレン(A)65~95質量部、下記要件(3)および(4)を満たす直鎖状低密度ポリエチレン(B)5~35質量部(ただし、(A)と(B)の合計を100質量部とする)、シラン化合物(C)1.5~2.5質量部、過酸化物(D)0.03~0.15質量部、およびスズ化合物(E)0.05~0.08質量部のみからなる樹脂組成物(X)の架橋体を含み、ゲル分率が70質量%以上であることを特徴とする管状成形体:
(1)MFR(190℃、2.16kg)が0.80~1.35g/10分である。
(2)密度が947~952kg/m3である。
(3)MFR(190℃、2.16kg)が1.50~4.50g/10分である。
(4)密度が910~925kg/m3である。
(1)MFR(190℃、2.16kg)が0.80~1.35g/10分である。
(2)密度が947~952kg/m3である。
(3)MFR(190℃、2.16kg)が1.50~4.50g/10分である。
(4)密度が910~925kg/m3である。
高密度ポリエチレン(以下、「HDPE」とも称する)(A)は、(1)MFR(190℃、2.16kg)が0.80~1.35g/10分であり、(2)密度が947~952kg/m3であることを特徴とする。このような特性を満たすHDPE(A)は、マルチサイト触媒を用いた重合により得られる。
直鎖状低密度ポリエチレン(以下、「LLDPE」とも称する)(B)は、(3)MFR(190℃、2.16kg)が1.50~4.50g/10分であり、(4)密度が910~925kg/m3であることを特徴とする。このような特性を満たすLLDPE(B)は、シングルサイト触媒を用いた重合により得られる。
シラン架橋に用いられるシラン化合物(C)は、オレフィン系不飽和結合、および、加水分解可能な有機基を有するシラン化合物であれば特に限定されない。シラン化合物のオレフィン系不飽和結合部位は、後述するラジカル発生剤の存在下でポリエチレン系樹脂中に発生した遊離ラジカル部位と反応する。シラン化合物としては、例えば、ビニルトリメトキシシラン、ビニルトリエトキシシラン、ビニルトリス(2-メトキシエトキシ)シラン等のビニルトリアルコキシシランや、ビニルメチルジメトキシシラン、ビニルフェニルジメトキシシランが挙げられる。これらは、1種を単独でまたは2種以上を組み合わせて用いることができる。シラン化合物(C)の配合量は、HDPE(A)とLLDPE(B)の合計100質量部に対し、1.5~2.5質量部が好ましく、1.7~2.0質量部がより好ましい。
ラジカル発生剤として用いる過酸化物(D)としては、シラン架橋に用いられるものであれば特に限定されない。例えば、ベンゾイルパーオキサイド、ジクミルパーオキサイド、ジクロロベンゾイルパーオキサイド、ジ-t-ブチルパーオキサイド、ジ-(t-ブチルパーオキシ)-m-ジ-イソプロピルベンゼン、2,5-ジメチル-2,5-ジ(t-ブチルパーオキシ)ヘキサン、2,5-ジメチル-2,5-ジ-(t-ブチルパーオキシ)-ヘキシン-3、α,α’-ビス(t-ブチルパーオキシジイソプロピル)ベンゼン、t-ブチルパーオキシクメン、4,4’-ジ(t-ブチルパーオキシ)バレリック酸n-ブチルエステル、1,1-ジ(t-ブチルパーオキシ)-3,3,5-トリメチルシクロヘキサン等が挙げられる。これらは、1種を単独でまたは2種以上を組み合わせて用いることができる。過酸化物(D)の配合量は、過酸化物の種類や、ラジカル捕捉機能を有する添加剤の存在量にもよるが、HDPE(A)とLLDPE(B)の合計100質量部に対し、0.03~0.15質量部が好ましく、0.05~0.10質量部がより好ましい。
シラノール縮合触媒(架橋促進剤)として用いるスズ化合物(E)は、シラン架橋に用いられるものであれば特に限定されない。例えば、ジブチルスズジラウレート、ジブチルスズジアセテート、ジブチルスズジオクテート、ジオクチルスズジラウレート、スズ(II)オクテート、酢酸第一スズ、ナフテン酸スズ等が挙げられる。これらは、1種を単独でまたは2種以上を組み合わせて用いることができる。スズ化合物(E)の配合量は、HDPE(A)とLLDPE(B)の合計100質量部に対し、0.05~0.08質量部が好ましく、0.06~0.07質量部がより好ましい。
樹脂組成物(X)には、以上の成分の他に、酸化防止剤、難燃剤、架橋助剤、耐候剤、着色剤、充填剤、他の安定剤などの添加物を適量配合してもよい。酸化防止剤としては、1,3,5-トリメチル-2,4,6-トリス(3,5-ジ-t-ブチル-4-ヒドロキシベンジル)ベンゼンや、ペンタエリトリトールテトラキス[3-(3,5-ジ-t-ブチル-4-ヒドロキシフェニル)プロピオネート]などが挙げられる。酸化防止剤を配合する場合、その配合量は、HDPE(A)とLLDPE(B)の合計100質量部に対し、0.05~0.6質量部が好ましく、0.1~0.5質量部がより好ましい。
本発明において、管状成形体は、ベース樹脂となる上記樹脂組成物(X)をシラン変性し、これを管状に成形し、シラン架橋法により架橋して作製することができる。ここで、管状成形体の製造方法としては、2段成形法および1段成形法が知られている。
高密度ポリエチレンおよび直鎖状低密度ポリエチレンの密度は、JIS K 6922-2に準拠して測定したMFR計のストランドを120℃で1時間熱処理し、1時間かけて直線的に室温まで徐冷した後、JIS K 7112に準拠して密度勾配管で測定した。シラン架橋ポリエチレン管の密度は、得られたポリエチレン管から切り出した試験片を、120℃で1時間熱処理し、1時間かけて直線的に室温まで徐冷した後、JIS K 7112に準拠して密度勾配管で測定した。
MFRは、JIS K7210に準拠して、測定温度190℃、荷重2.16kgf(21.2N)の条件で測定した。
ゲル分率は、JIS K 6769に準拠して測定した。
クリープ破壊時間は、ISO 9080に準拠して、温度95℃、周応力4.8MPaの条件で測定した。
HDPE(A)としてHZ3300FPU(商品名、(株)プライムポリマー製)を65質量部、LLDPE(B)としてSP2040P(商品名、(株)プライムポリマー製)を35質量部、シラン化合物(C)としてビニルトリメトキシシラン(商品名:KBM-1003、信越化学工業(株)製)を2質量部、過酸化物(D)として2,5-ジメチル-2,5-ジ(t-ブチルパーオキシ)ヘキサン(商品名:パーヘキサ(登録商標)25B、日本油脂(株)製)を0.05質量部、スズ化合物(E)としてジオクチルスズジラウレート(商品名:アデカスタブOT-1、(株)ADEKA製)を0.063質量部用いて、押出機((株)池貝製SF-65)内にて、250℃で加熱しながら溶融、混練、反応させるとともに、これを管状に押出して、1段成形法にて成形管を得た。得られた成形管を、80℃の温水中に12時間浸漬し、架橋処理を行うことにより、シラン架橋ポリエチレン管を作製した。
得られたシラン架橋ポリエチレン管について、密度(kg/m3)、ゲル分率(質量%)およびクリープ破壊時間(時間)を測定した。結果を表2に示す。
HDPE(A)およびLLDPE(B)の種類および配合量を表2に示すように変更した以外は、実施例1と同様にしてシラン架橋ポリエチレン管を作製し、各種物性を測定した。結果を表2に示す。
HDPE(A)およびLLDPE(B)の種類および配合量を表2に示すように変更した以外は実施例1と同様にしてシラン架橋ポリエチレン管を作製し、各種物性を測定した。なお、比較例1および2で用いたLLDPE(B)は、いずれもチーグラー触媒品である。また、比較例3では、LLDPE(B)を使用しなかった。結果を表2に示す。
Claims (3)
- 下記要件(1)および(2)を満たす高密度ポリエチレン(A)65~95質量部、
下記要件(3)および(4)を満たす直鎖状低密度ポリエチレン(B)5~35質量部(ただし、(A)と(B)の合計を100質量部とする)、
シラン化合物(C)1.5~2.5質量部、
過酸化物(D)0.03~0.15質量部、および
スズ化合物(E)0.05~0.08質量部
のみからなる樹脂組成物(X)の架橋体を含み、ゲル分率が70質量%以上であることを特徴とする管状成形体:
(1)MFR(190℃、2.16kg)が0.80~1.35g/10分である。
(2)密度が947~952kg/m3である。
(3)MFR(190℃、2.16kg)が1.50~4.50g/10分である。
(4)密度が910~925kg/m3である。 - 下記要件(1)および(2)を満たす高密度ポリエチレン(A)65~95質量部、
下記要件(3)および(4)を満たす直鎖状低密度ポリエチレン(B)5~35質量部(ただし、(A)と(B)の合計を100質量部とする)、
シラン化合物(C)1.5~2.5質量部、
過酸化物(D)0.03~0.15質量部、および
スズ化合物(E)0.05~0.08質量部
のみからなる樹脂組成物(X)を、押出機内でグラフト重合反応させた後、押出成形し、架橋処理を行うことを特徴とする、管状成形体の製造方法であって、該管状成形体のゲル分率が70質量%以上である、管状成形体の製造方法:
(1)MFR(190℃、2.16kg)が0.80~1.35g/10分である。
(2)密度が947~952kg/m3である。
(3)MFR(190℃、2.16kg)が1.50~4.50g/10分である。
(4)密度が910~925kg/m3である。 - 下記要件(1)および(2)を満たす高密度ポリエチレン(A)65~95質量部、
下記要件(3)および(4)を満たす直鎖状低密度ポリエチレン(B)5~35質量部(ただし、(A)と(B)の合計を100質量部とする)、
シラン化合物(C)1.5~2.5質量部、
過酸化物(D)0.03~0.15質量部、および
スズ化合物(E)0.05~0.08質量部
のみからなる樹脂組成物(X)であって、該樹脂組成物(X)の架橋体のゲル分率が70質量%以上であることを特徴とする、樹脂組成物(X):
(1)MFR(190℃、2.16kg)が0.80~1.35g/10分である。
(2)密度が947~952kg/m3である。
(3)MFR(190℃、2.16kg)が1.50~4.50g/10分である。
(4)密度が910~925kg/m3である。