JP6943646B2 - Method for manufacturing restrictive damping material and restrictive damping material - Google Patents

Method for manufacturing restrictive damping material and restrictive damping material Download PDF

Info

Publication number
JP6943646B2
JP6943646B2 JP2017127080A JP2017127080A JP6943646B2 JP 6943646 B2 JP6943646 B2 JP 6943646B2 JP 2017127080 A JP2017127080 A JP 2017127080A JP 2017127080 A JP2017127080 A JP 2017127080A JP 6943646 B2 JP6943646 B2 JP 6943646B2
Authority
JP
Japan
Prior art keywords
vibration damping
layer
restraint
damping material
resin layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2017127080A
Other languages
Japanese (ja)
Other versions
JP2019010745A (en
Inventor
隼人 中坊
隼人 中坊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Risho Kogyo Co Ltd
Original Assignee
Risho Kogyo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Risho Kogyo Co Ltd filed Critical Risho Kogyo Co Ltd
Priority to JP2017127080A priority Critical patent/JP6943646B2/en
Publication of JP2019010745A publication Critical patent/JP2019010745A/en
Application granted granted Critical
Publication of JP6943646B2 publication Critical patent/JP6943646B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、車両、船舶、建築・土木構造物などにおいて発生する振動および騒音を低減するために使用される拘束型制振材および拘束型制振材の製造方法に関する。 The present invention relates to a restraint type vibration damping material and a method for manufacturing a restraint type vibration damping material used for reducing vibration and noise generated in a vehicle, a ship, a building / civil engineering structure, or the like.

自動車および鉄道などの車両、船舶、住宅およびビルなどの建築構造物、土木構造物などにおいて振動の防止、あるいは、固体伝搬音低減の目的で従来から用いられている制振材の１つとして、拘束型制振材がある。 As one of the damping materials conventionally used for the purpose of preventing vibration or reducing solid propagating noise in vehicles such as automobiles and railways, building structures such as ships, houses and buildings, and civil engineering structures. There is a restraint type damping material.

拘束型制振材は、金属などからなる拘束層、および、粘弾性を有する制振層から構成され、拘束層と制振層の剛性の差により、加振された時に制振層にせん断力が加わることで、振動のエネルギーを熱に変換し振動を減衰させるものであり、金属からなる拘束層に、アスファルトを含む粘弾性組成物が接着された拘束型制振材（特許文献１参照）、金属からなる拘束層に、制振樹脂組成物からなる制振樹脂層および樹脂組成物からなる粘着樹脂層を設けた拘束型制振材（特許文献２参照）などがある。 The restraint type vibration damping material is composed of a restraint layer made of metal or the like and a vibration damping layer having viscoelasticity. Due to the difference in rigidity between the restraint layer and the vibration damping layer, a shearing force is applied to the vibration damping layer when vibration is applied. Is added to convert the energy of vibration into heat and dampen the vibration. A restraining type damping material in which a viscoelastic composition containing asphalt is adhered to a restraining layer made of metal (see Patent Document 1). , There is a restraint type vibration damping material (see Patent Document 2) in which a vibration damping resin layer made of a vibration damping resin composition and an adhesive resin layer made of a resin composition are provided in a restraining layer made of metal.

特開平５−１２６２０６号公報Japanese Unexamined Patent Publication No. 5-126206 特開２００６−１２６７３６号公報Japanese Unexamined Patent Publication No. 2006-126736

近年、自動車などの輸送機は燃費向上の観点から軽量化が図られているが、従来の拘束型制振材は、拘束層に鋼板を用いた場合、制振性は高いが重量が重くなるという問題があり、特許文献１，２には、拘束層にアルミニウム板を用いることも記載されているが、アルミニウム板を用いると重量を軽くすることはできるが、鉄を用いた場合と比べると制振性が低下するという問題がある。 In recent years, the weight of transport aircraft such as automobiles has been reduced from the viewpoint of improving fuel efficiency. However, when a steel plate is used for the restraint layer, the conventional restraint type damping material has high vibration damping property but is heavy. Patent Documents 1 and 2 also describe that an aluminum plate is used for the restraining layer. Although the weight can be reduced by using the aluminum plate, it is compared with the case where iron is used. There is a problem that the damping property is lowered.

また、船舶などでは、拘束型制振材は溶接で取り付けられることが多いことから、拘束層には溶接できる鋼板が用いられることが多く、軽量化は困難であった。 Further, in ships and the like, since the restraint type damping material is often attached by welding, a weldable steel plate is often used for the restraint layer, and it is difficult to reduce the weight.

そこで、本発明は、高い制振性を有し、軽量化が可能であり、さらに、鉄からなる部材などに対して溶接での取付を可能とする拘束型制振材を提供することを目的とする。 Therefore, it is an object of the present invention to provide a restrictive type damping material which has high vibration damping property, can be reduced in weight, and can be attached to a member made of iron by welding. And.

本発明の拘束型制振材は、拘束層および制振樹脂層からなる拘束型制振材であって、前記制振樹脂層は複数のプリプレグが積層されて形成されており、前記拘束層に前記制振樹脂層が積層され一体化されていることを特徴とする。 The restraint type vibration damping material of the present invention is a restraint type vibration damping material composed of a restraint layer and a vibration damping resin layer, and the vibration damping resin layer is formed by laminating a plurality of prepregs on the restraint layer. The damping resin layer is laminated and integrated.

前記プリプレグは、熱硬化性制振樹脂が、繊維基材に含浸または塗布されて形成されており、前記熱硬化性制振樹脂はゴム変性エポキシ樹脂を含む。 The prepreg is formed by impregnating or coating a fiber base material with a thermosetting vibration damping resin, and the thermosetting vibration damping resin contains a rubber-modified epoxy resin.

前記拘束層は、軽金属、ガラスクロス、カーボンクロス、または繊維強化プラスチックからなる。 The restraint layer is made of light metal, glass cloth, carbon cloth, or fiber reinforced plastic.

さらに、鉄からなる溶接部が、前記拘束層または前記制振樹脂層に設けられている。 Further, a welded portion made of iron is provided on the restraint layer or the vibration damping resin layer.

本発明の拘束型制振材の製造方法は、拘束層および制振樹脂層からなる拘束型制振材の製造方法であって、複数のプリプレグを積層して、前記制振樹脂層を形成し、前記拘束層と前記制振樹脂層とを積層し、加熱プレスによって一体成形することを特徴とする。 The method for producing a restraint type vibration damping material of the present invention is a method for manufacturing a restraint type vibration damping material composed of a restraint layer and a vibration damping resin layer, in which a plurality of prepregs are laminated to form the vibration damping resin layer. The restraining layer and the vibration damping resin layer are laminated and integrally molded by a heating press.

熱硬化性制振樹脂を、繊維基材に含浸または塗布して、前記プリプレグを形成し、前記熱硬化性制振樹脂はゴム変性エポキシ樹脂を含む。 A thermosetting vibration damping resin is impregnated or applied to a fiber base material to form the prepreg, and the thermosetting vibration damping resin contains a rubber-modified epoxy resin.

前記拘束層は、軽金属、ガラスクロス、カーボンクロス、または繊維強化プラスチックからなる。 The restraint layer is made of light metal, glass cloth, carbon cloth, or fiber reinforced plastic.

さらに、鉄からなる溶接部を、前記拘束層または前記制振樹脂層に設ける。 Further, a welded portion made of iron is provided on the restraint layer or the vibration damping resin layer.

本発明の拘束型制振材は、拘束層および制振樹脂層からなる拘束型制振材であって、前記制振樹脂層は複数のプリプレグが積層されて形成されており、前記拘束層に前記制振樹脂層が積層され一体化されていることにより、拘束層の材質に関係なく、優れた制振性能を有することができる。 The restraint type vibration damping material of the present invention is a restraint type vibration damping material composed of a restraint layer and a vibration damping resin layer, and the vibration damping resin layer is formed by laminating a plurality of prepregs on the restraint layer. By laminating and integrating the vibration damping resin layer, it is possible to have excellent vibration damping performance regardless of the material of the restraining layer.

前記プリプレグは、熱硬化性制振樹脂が、繊維基材に含浸または塗布されて形成されており、前記熱硬化性制振樹脂はゴム変性エポキシ樹脂を含むことにより、より優れた制振機能を有することができる。 The prepreg is formed by impregnating or coating a fiber base material with a thermosetting damping resin, and the thermosetting damping resin contains a rubber-modified epoxy resin to provide a more excellent damping function. Can have.

前記拘束層は、軽金属または繊維強化プラスチックからなることにより、拘束型制振材を軽量化することができる。 Since the restraint layer is made of a light metal or a fiber reinforced plastic, the weight of the restraint type damping material can be reduced.

拘束型制振材には、鉄からなる溶接部が設けられていることにより、前記拘束層の材質に関係なく、前記拘束型制振材を溶接して取り付けることができる。 Since the restraint type vibration damping material is provided with a welded portion made of iron, the restraint type vibration damping material can be attached by welding regardless of the material of the restraint layer.

本発明の拘束型制振材の製造方法は、拘束層および制振樹脂層からなる拘束型制振材の製造方法であって、複数のプリプレグを積層して、前記制振樹脂層を形成し、前記拘束層と前記制振樹脂層とを積層し、加熱プレスによって一体成形することにより、軽量で制振性に優れた拘束型制振材を製造することが可能となる。 The method for producing a restraint type vibration damping material of the present invention is a method for manufacturing a restraint type vibration damping material composed of a restraint layer and a vibration damping resin layer, in which a plurality of prepregs are laminated to form the vibration damping resin layer. By laminating the restraint layer and the vibration damping resin layer and integrally molding them by a heating press, it is possible to manufacture a lightweight restraint type vibration damping material having excellent vibration damping properties.

本発明の拘束型制振材の斜視図である。It is a perspective view of the restraint type vibration damping material of this invention. 拘束層に溶接部を設けた拘束型制振材の斜視図である。It is a perspective view of the restraint type vibration damping material which provided the welded part in the restraint layer. 制振樹脂層に溶接部を設けた拘束型制振材の斜視図である。It is a perspective view of the restraint type vibration damping material which provided the welded part in the vibration damping resin layer.

本発明の拘束型制振材１および拘束型制振材１の製造方法について、図を用いて詳しく説明する。図１に示すのは、本発明の拘束型制振材１の斜視図である。まず初めに、本発明の拘束型制振材１について説明する。 The method for manufacturing the restrictive vibration damping material 1 and the restrictive vibration damping material 1 of the present invention will be described in detail with reference to the drawings. FIG. 1 is a perspective view of the restrictive damping material 1 of the present invention. First, the restrictive damping material 1 of the present invention will be described.

本発明の拘束型制振材１は、図１に示すように、拘束層２および制振樹脂層３からなり、前記拘束層２および前記制振樹脂層３が互いに積層されて一体成形されている。前記制振樹脂層３は複数のプリプレグが積層されて形成されており、前記拘束型制振材１は、複数のプリプレグからなる前記制振樹脂層３が前記拘束層２と共に、加熱プレスによって一体成形されたものである。 As shown in FIG. 1, the restraint type vibration damping material 1 of the present invention is composed of a restraint layer 2 and a vibration damping resin layer 3, and the restraint layer 2 and the vibration damping resin layer 3 are laminated and integrally molded with each other. There is. The vibration damping resin layer 3 is formed by laminating a plurality of prepregs, and in the restraint type vibration damping material 1, the vibration damping resin layer 3 composed of a plurality of prepregs is integrated with the restraint layer 2 by a heating press. It is molded.

前記拘束層２は、アルミニウム、チタンなどの軽金属およびその合金、または、ガラスクロス、カーボンファイバークロス、または、ガラスクロス、カーボンファイバークロスに樹脂を含浸させた繊維強化プラスチック（ＦＲＰ）からなる板材であり、ＦＲＰは積層して用いることも可能である。前記拘束層２の厚みは、特に限定するものではないが、０．５〜２．０ｍｍとすることが好ましい。 The restraint layer 2 is a plate material made of a light metal such as aluminum or titanium and an alloy thereof, or a glass cloth, a carbon fiber cloth, or a fiber reinforced plastic (FRP) obtained by impregnating the glass cloth or carbon fiber cloth with a resin. , FRP can also be used in layers. The thickness of the restraint layer 2 is not particularly limited, but is preferably 0.5 to 2.0 mm.

前記制振樹脂層３は、複数のプリプレグが積層されて構成されているが、前記プリプレグは、熱硬化性制振樹脂が繊維基材に含浸または塗布されて形成されている。前記プリプレグの繊維基材としては、炭素繊維、ガラス繊維、金属繊維などの無機繊維、および、アラミド繊維、ポリアミド繊維などの有機繊維を用いることができる。 The vibration damping resin layer 3 is formed by laminating a plurality of prepregs, and the prepreg is formed by impregnating or applying a thermosetting vibration damping resin to a fiber base material. As the fiber base material of the prepreg, inorganic fibers such as carbon fiber, glass fiber and metal fiber, and organic fiber such as aramid fiber and polyamide fiber can be used.

前記プリプレグの熱硬化性制振樹脂は、熱硬化性樹脂としてゴム変性エポキシ樹脂を含むことが好ましい。さらに、前記熱硬化性制振樹脂は、熱硬化性樹脂としてエポキシ当量２００〜５００ｇ／ｅｑのゴム変性エポキシ樹脂１００重量部、硬化剤として酸無水物硬化剤１５〜３０重量部、および、硬化促進剤としてイミダゾール０．４〜０．７重量部を含む樹脂組成物を用いることが好ましい。また、前記樹脂組成物には、難燃剤を添加することも可能であり、難燃剤としては、リン系、窒素系、膨張黒鉛などを用いることができ、特に、制振性への影響が少ないという観点から、膨張黒鉛を用いることが好ましい。さらに、難燃剤と併せて、前記樹脂組成物に分散剤、沈殿防止剤を添加することも可能である。 The thermosetting vibration damping resin of the prepreg preferably contains a rubber-modified epoxy resin as the thermosetting resin. Further, the thermosetting vibration damping resin includes 100 parts by weight of a rubber-modified epoxy resin having an epoxy equivalent of 200 to 500 g / eq as a thermosetting resin, 15 to 30 parts by weight of an acid anhydride curing agent as a curing agent, and curing acceleration. It is preferable to use a resin composition containing 0.4 to 0.7 parts by weight of imidazole as the agent. Further, a flame retardant can be added to the resin composition, and as the flame retardant, phosphorus-based, nitrogen-based, expanded graphite, or the like can be used, and the influence on the vibration damping property is particularly small. From this point of view, it is preferable to use expanded graphite. Further, it is also possible to add a dispersant and a precipitation inhibitor to the resin composition together with the flame retardant.

次に、本発明の拘束型制振材の製造方法について、前記拘束型制振材１を用いて説明する。まず初めに、熱硬化性樹脂であるゴム変性エポキシ樹脂、硬化剤、および、硬化促進剤を所定の割合で混合し、熱硬化性制振樹脂を作成する。この際に、適宜、難燃剤、沈殿防止剤などを添加して混合する。そして、得られた前記熱硬化性制振樹脂を繊維基材に含浸または塗布し、その後、乾燥温度：１４０〜１８０℃、乾燥時間：２〜４分の条件で乾燥させて、複数のプリプレグを作成する。そして、得られたプリプレグを複数積層して制振樹脂層３とする。この際、前記プリプレグは、積層数を３枚以上とし、厚みは１．６ｍｍ以上とすることが好ましい。 Next, the method for producing the restraint type vibration damping material of the present invention will be described using the restraint type vibration damping material 1. First, a rubber-modified epoxy resin which is a thermosetting resin, a curing agent, and a curing accelerator are mixed at a predetermined ratio to prepare a thermosetting vibration damping resin. At this time, a flame retardant, a precipitation inhibitor, etc. are appropriately added and mixed. Then, the obtained thermosetting damping resin is impregnated or applied to the fiber base material, and then dried under the conditions of a drying temperature of 140 to 180 ° C. and a drying time of 2 to 4 minutes to obtain a plurality of prepregs. create. Then, a plurality of the obtained prepregs are laminated to form the vibration damping resin layer 3. At this time, it is preferable that the number of laminated prepregs is 3 or more and the thickness is 1.6 mm or more.

予め用意しておいた拘束層２を、複数のプリプレグが積層された状態の前記制振樹脂層３と積層し、温度：１２０〜１８０℃、圧力：３０〜６０ｋｇ／ｃｍ２、時間：６０分以上の条件で加熱プレスを行うことにより、前記拘束層２および前記制振樹脂層３を一体成形すると、本発明の拘束型制振材１が完成する。 The restraint layer 2 prepared in advance is laminated with the vibration damping resin layer 3 in which a plurality of prepregs are laminated, and the temperature is 120 to 180 ° C., the pressure is 30 to 60 kg / cm2, and the time is 60 minutes or more. When the restraint layer 2 and the vibration damping resin layer 3 are integrally molded by performing a heating press under the conditions of the above, the restraint type vibration damping material 1 of the present invention is completed.

このように、本発明の拘束型制振材１は、前記拘束層２に直接、熱硬化性制振樹脂のみによって制振樹脂層が形成されているのではなく、熱硬化性制振樹脂を繊維基材に含浸または塗布してプリプレグを作成し、前記プリプレグによって制振樹脂層３を形成し、前記拘束層２と複数のプリプレグからなる前記制振樹脂層３とを加熱プレスすることによって一体成形されている。これにより、本発明の拘束型制振材１は、前記拘束層２に重量増の原因となる鉄などを用いることなく、十分な制振性を有することができるようになり、そして、拘束型制振材１の軽量化を実現することができる。 As described above, in the restraint type vibration damping material 1 of the present invention, the vibration damping resin layer is not directly formed on the restraining layer 2 only by the thermosetting vibration damping resin, but the thermosetting vibration damping resin is formed. A prepreg is prepared by impregnating or coating a fiber base material, a vibration damping resin layer 3 is formed by the prepreg, and the restraining layer 2 and the vibration damping resin layer 3 composed of a plurality of prepregs are integrally heat-pressed. It is molded. As a result, the restraint type vibration damping material 1 of the present invention can have sufficient vibration damping properties without using iron or the like that causes weight increase in the restraint layer 2, and is a restraint type. The weight of the damping material 1 can be reduced.

本発明の拘束型制振材１は、拘束型制振材１を船舶などに使用する際に溶接で取り付けることができるように、鉄からなる溶接部４，５を設けることができる。図２に示すのは、拘束層２に４つの溶接部４を設けた拘束型制振材１であり、図３に示すのは、制振樹脂層３に４つの溶接部５を設けた拘束型制振材１である。 The restrictive damping material 1 of the present invention may be provided with welded portions 4 and 5 made of iron so that the restrictive damping material 1 can be attached by welding when the restrictive damping material 1 is used on a ship or the like. FIG. 2 shows a restraint type damping material 1 having four welds 4 provided on the restraint layer 2, and FIG. 3 shows a restraint having four welds 5 provided on the damping resin layer 3. Mold damping material 1.

前記拘束型制振材１を対象物に取り付ける際、制振樹脂層３を対象物と接触させることから、前記溶接部４は、前記拘束層２から対象物に向かって湾曲する形状を有している。そして、前記溶接部５は、前記制振樹脂層３の周囲から水平方向に突出する大きさに形成されている。前記溶接部４，５は、対象物に対して溶接し易くするために、様々な形状を用いることができる。 When the restraint type vibration damping material 1 is attached to the object, the vibration damping resin layer 3 is brought into contact with the object, so that the welded portion 4 has a shape curved from the restraint layer 2 toward the object. ing. The welded portion 5 is formed so as to protrude in the horizontal direction from the periphery of the vibration damping resin layer 3. Various shapes can be used for the welded portions 4 and 5 in order to facilitate welding with the object.

前記溶接部４，５は、図２，３に示すように、前記拘束層２および前記制振樹脂層３のどちらに設けても良く、その数および形状についても特に限定するものではなく、前記拘束型制振材１の大きさ、用途などに応じて適宜設定することができる。また、前記溶接部４，５を固定する方法については、リベット、接着剤、摩擦攪拌接合、および、これらの組み合わせなど様々な方法を用いることができる。 As shown in FIGS. 2 and 3, the welded portions 4 and 5 may be provided on either the restraint layer 2 or the vibration damping resin layer 3, and the number and shape thereof are not particularly limited. It can be appropriately set according to the size, use, and the like of the restraint type damping material 1. Further, as a method for fixing the welded portions 4 and 5, various methods such as rivets, adhesives, friction stir welding, and combinations thereof can be used.

このように、鉄からなる溶接部４，５を前記拘束型制振材１に設けることにより、前記拘束型制振材１を溶接で簡単にそして確実に鉄からなる対象物に取り付けることができるようになる。 In this way, by providing the welded portions 4 and 5 made of iron on the restrictive damping material 1, the restrictive damping material 1 can be easily and surely attached to the object made of iron by welding. Will be.

前記拘束型制振材１を対象物に取り付ける手段として、前記溶接部４，５以外に、前記制振樹脂層３の表面に粘着層を設けることができる。前記粘着層としては、従来の拘束型制振材に用いられているものを使用することが可能であり、例えば、粘着または接着フィルム及びテープ、粘着樹脂、接着樹脂の塗工などを用いることができる。粘着樹脂としては、例えば、アクリル、ウレタン、シリコーン系などを用いる。接着樹脂としては、例えば、アクリル、エポキシ、シリコーン、フェノール、ゴム系などを用いる。前記粘着層は、用途などに応じて、前記溶接部４，５と併用、あるいは、単体で前記拘束型制振材１に設けることができる。 As a means for attaching the restrictive damping material 1 to an object, an adhesive layer can be provided on the surface of the damping resin layer 3 in addition to the welded portions 4 and 5. As the adhesive layer, those used in conventional restraint type vibration damping materials can be used, and for example, adhesive or adhesive films and tapes, adhesive resins, adhesive resin coatings, and the like can be used. can. As the adhesive resin, for example, acrylic, urethane, silicone, or the like is used. As the adhesive resin, for example, acrylic, epoxy, silicone, phenol, rubber, etc. are used. The adhesive layer can be provided on the restrictive damping material 1 in combination with the welded portions 4 and 5 or as a single unit, depending on the intended use.

本発明の拘束型制振材１について実施例および比較例１，２を用いてさらに説明する。 The restrictive damping material 1 of the present invention will be further described with reference to Examples and Comparative Examples 1 and 2.

ゴム変成エポキシ樹脂（アデカ製 ＥＰＲ−１４１５−１）１００重量部、酸無水物硬化剤（日立化成製 ＨＮ−５５００）９．５重量部、イミダゾール（四国化成製 ２Ｅ４ＭＺ）０．６重量部、膨張黒鉛（伊藤黒鉛製 ９５１００１５０）６重量部、および、沈殿防止剤（共栄社化学製 ターレン７２００−２０）２．７重量部を均一に混合し、得られた混合物を、ガラスクロスに含浸し、乾燥させて５枚のプリプレグを作成する。５枚のプリプレグを積層して制振樹脂層３を形成し、厚さ１．０ｍｍのアルミニウム板である拘束層２と共に加熱プレスして一体成形し、実施例の拘束型制振材１を作成した。得られた前記拘束型制振材１の厚みは、２．０ｍｍであった。 Rubber modified epoxy resin (EPR-1415-1 manufactured by Adeca) 100 parts by weight, acid anhydride curing agent (HN-5500 manufactured by Hitachi Kasei) 9.5 parts by weight, imidazole (2E4MZ manufactured by Shikoku Kasei) 0.6 parts by weight, expansion 6 parts by weight of graphite (95100150 manufactured by Ito Graphite) and 2.7 parts by weight of anti-precipitation agent (Tarren 7200-20 manufactured by Kyoeisha Chemical Co., Ltd.) were uniformly mixed, and the obtained mixture was impregnated into a glass cloth and dried. Create 5 prepregs. Five prepregs are laminated to form a vibration damping resin layer 3, and the restraint type vibration damping material 1 of the embodiment is created by heat-pressing together with a restraint layer 2 which is an aluminum plate having a thickness of 1.0 mm and integrally molding. bottom. The thickness of the obtained restraint type damping material 1 was 2.0 mm.

比較例１として、実施例のアルミニウム板を冷間圧延鋼板（ＳＰＣＣ）に、その他は全て同じ条件で作成した制振材を用意した。比較例２として、実施例１と同様に、ゴム変成エポキシ樹脂、酸無水物硬化剤、イミダゾール、膨張黒鉛、および、沈殿防止剤を均一に混合し、得られた混合物を、直接、厚さ１．０ｍｍのアルミニウム板に塗布して乾燥させることにより、樹脂だけで制振樹脂層を設けて制振材を形成した。 As Comparative Example 1, a damping material prepared by using a cold-rolled steel plate (SPCC) as the aluminum plate of the example and all other materials under the same conditions was prepared. As Comparative Example 2, the rubber modified epoxy resin, the acid anhydride curing agent, the imidazole, the expanded graphite, and the precipitation inhibitor were uniformly mixed in the same manner as in Example 1, and the obtained mixture was directly mixed to a thickness of 1 By applying it to a 0.0 mm aluminum plate and drying it, a vibration-damping resin layer was provided only with resin to form a vibration-damping material.

このようにして用意した実施例の拘束型制振材１および比較例１，２の制振材について、それぞれ、損失係数測定装置を用いて片持ち梁法によって２０℃における損失係数ηを測定し、以下の表１に記載した。損失係数ηは、半値幅法で算出し、周波数５００Ｈｚの結果を記載した。 The loss coefficient η at 20 ° C. was measured by the cantilever method using the loss coefficient measuring device for each of the restraint type damping material 1 and the damping materials of Comparative Examples 1 and 2 prepared in this manner. , Listed in Table 1 below. The loss coefficient η was calculated by the full width at half maximum method, and the result with a frequency of 500 Hz was described.

Figure 0006943646
Figure 0006943646

表１に示すように、実施例の拘束型制振材１は、比較例１，２よりも損失係数が大きくなっており、制振性に優れていることがわかる。特に、プリプレグを用いないで樹脂だけで制振樹脂層を形成した比較例２に対して実施例の損失係数は２倍以上となっており、プリプレグを用いることによって本発明の拘束型制振材１の制振性が大きく向上することを示している。 As shown in Table 1, the restraint type vibration damping material 1 of the example has a larger loss coefficient than that of Comparative Examples 1 and 2, and it can be seen that the damping type damping material 1 is excellent in vibration damping property. In particular, the loss coefficient of the example is more than twice that of Comparative Example 2 in which the vibration damping resin layer is formed only with the resin without using the prepreg, and the restraint type vibration damping material of the present invention is used by using the prepreg. It shows that the vibration damping property of 1 is greatly improved.

本発明の拘束型制振材は、プリプレグおよび軽量な材質からなる拘束層を用いることにより、優れた制振性と軽量化を実現することができ、また、溶接部を設けることによって、従来と同様に、溶接によって簡単に取り付けることもできるという優れた効果を奏する。 The restraint type vibration damping material of the present invention can realize excellent vibration damping property and weight reduction by using a restraining layer made of a prepreg and a lightweight material, and by providing a welded portion, it can be compared with the conventional one. Similarly, it has the excellent effect that it can be easily attached by welding.

１ 拘束型制振材
２ 拘束層
３ 制振樹脂層
４，５ 溶接部 1 Restraint type damping material 2 Restraint layer 3 Vibration damping resin layer 4, 5 Welded part

Claims (8)

１つの拘束層および１つの制振樹脂層からなる拘束型制振材であって、
前記制振樹脂層は複数のプリプレグが積層されて形成されており、
前記拘束層に前記制振樹脂層が積層され一体化されており、
前記拘束層は、軽金属、ガラスクロス、またはカーボンクロスからなることを特徴とする拘束型制振材。 A restraining type damping material composed of one restraining layer and one damping resin layer.
The vibration damping resin layer is formed by laminating a plurality of prepregs.
The damping resin layer is laminated and integrated on the restraining layer .
The restraining layer is a restraining type damping material made of a light metal, a glass cloth, or a carbon cloth. 前記プリプレグは、熱硬化性制振樹脂が、繊維基材に含浸または塗布されて形成されていることを特徴とする請求項１に記載の拘束型制振材。 The restraint type damping material according to claim 1, wherein the prepreg is formed by impregnating or applying a thermosetting damping resin to a fiber base material. 前記熱硬化性制振樹脂はゴム変性エポキシ樹脂を含むことを特徴とする請求項２に記載の拘束型制振材。 The restraint type vibration damping material according to claim 2, wherein the thermosetting vibration damping resin contains a rubber-modified epoxy resin. 鉄からなる溶接部が、前記拘束層または前記制振樹脂層に設けられていることを特徴とする請求項１〜３のいずれか１項に記載の拘束型制振材。 The restraint type vibration damping material according to any one of claims 1 to 3 , wherein a welded portion made of iron is provided on the restraint layer or the vibration damping resin layer. １つの拘束層および１つの制振樹脂層からなる拘束型制振材の製造方法であって、
複数のプリプレグを積層して、前記制振樹脂層を形成し、
前記拘束層と前記制振樹脂層とを積層し、加熱プレスによって一体成形し、
前記拘束層は、軽金属、ガラスクロス、またはカーボンクロスからなることを特徴とする拘束型制振材の製造方法。 A method for manufacturing a restraining type damping material composed of one restraining layer and one damping resin layer.
A plurality of prepregs are laminated to form the vibration damping resin layer, and the vibration damping resin layer is formed.
The restraint layer and the vibration damping resin layer are laminated and integrally molded by a heating press .
A method for producing a restraint type damping material, wherein the restraint layer is made of a light metal, a glass cloth, or a carbon cloth. 熱硬化性制振樹脂を、繊維基材に含浸または塗布して、前記プリプレグを形成することを特徴とする請求項５に記載の拘束型制振材の製造方法。 The method for producing a restrictive damping material according to claim 5 , wherein the fiber base material is impregnated or coated with a thermosetting damping resin to form the prepreg. 前記熱硬化性制振樹脂はゴム変性エポキシ樹脂を含むことを特徴とする請求項６に記載の拘束型制振材の製造方法。 The method for producing a restraint type vibration damping material according to claim 6 , wherein the thermosetting vibration damping resin contains a rubber-modified epoxy resin. 鉄からなる溶接部を、前記拘束層または前記制振樹脂層に設けることを特徴とする請求項５〜７のいずれか１項に記載の拘束型制振材の製造方法。 The method for producing a restraint type vibration damping material according to any one of claims 5 to 7 , wherein a welded portion made of iron is provided on the restraint layer or the vibration damping resin layer.
JP2017127080A 2017-06-29 2017-06-29 Method for manufacturing restrictive damping material and restrictive damping material Active JP6943646B2 (en)