JP6897227B2 - 紙力増強剤、紙の製造方法、及び紙 - Google Patents
紙力増強剤、紙の製造方法、及び紙 Download PDFInfo
- Publication number
- JP6897227B2 JP6897227B2 JP2017064281A JP2017064281A JP6897227B2 JP 6897227 B2 JP6897227 B2 JP 6897227B2 JP 2017064281 A JP2017064281 A JP 2017064281A JP 2017064281 A JP2017064281 A JP 2017064281A JP 6897227 B2 JP6897227 B2 JP 6897227B2
- Authority
- JP
- Japan
- Prior art keywords
- component
- paper
- mol
- paper strength
- ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
〔1〕その構成成分(1)がアクリルアミド(a)、αメチル基含有カチオン性ビニルモノマー(b)、アニオン性ビニルモノマー(c)を含む
〔2〕その構成成分(1)における(b)成分の比率が1〜15モル%であり、かつ、(c)成分の比率が1〜10モル%である
〔3〕その1H−NMRスペクトルの0.9ppm〜1.35ppmの範囲に該(b)成分のαメチル基に帰属する高磁場側吸収帯Aと低磁場側吸収帯Bがあり、かつ、該吸収帯Aの面積(As)及び該吸収帯Bの面積(Bs)の合計面積に対する該吸収帯Aの面積(As)の比率[As/(As+Bs)]が10〜35%である
〔4〕その15重量%水溶液(25℃)の粘度が2,000〜60,000mPa・sである
〔5〕その重量平均分子量(Mw)と数平均分子量(Mn)の比率(Mw/Mn)が3.5以下である
より好ましくは(a)成分50〜80モル%程度、(b’)成分0〜5モル%程度、(c)成分1〜20モル%程度又は0モル%、(d)成分0.1〜2モル%程度又は0モル%、及び(e)成分0.1〜10モル%程度である。
撹拌機、温度計、還流冷却管、窒素ガス導入管及び3つの滴下ロート(以下、順にロート1、ロート2及びロート3という。)を備えた反応容器にイオン交換水401.4部を仕込み、該イオン交換水に窒素ガスを直接吹き込むことにより該反応容器内の酸素を除去した後、該イオン交換水の温度を90℃に設定した。
次いで、ロート1に、モノマー混合物(I)として、50%アクリルアミド水溶液79.04部、ジメチルアミノエチルメタクリレート24.37部、80%アクリル酸3.99部、N,N−ジメチルアクリルアミド0.18部、メタリルスルホン酸ナトリウム0.292部、62.5%硫酸11.91部及びイオン交換水61.42部からなる水溶液を更に硫酸でpH4.5に調整したものを仕込んだ。
次いで、ロート2に、モノマー混合物(II)として、50%アクリルアミド水溶液386.98部、ジメチルアミノエチルメタクリレート10.44部、75%ジメチルアミノエチルアクリレートのベンジルクロライド4級化物13.27部、80%アクリル酸9.31部、N,N−ジメチルアクリルアミド0.18部、メタリルスルホン酸ナトリウム0.292部、62.5%硫酸5.10部及びイオン交換水231.16部からなる水溶液を更に硫酸でpH4.5に調整したものを仕込んだ。
次いで、ロート3に、過硫酸アンモニウム0.21部及びイオン交換水180部からなる開始剤溶液を仕込んだ。
次いで、ロート1とロート3のコックを同時に開き、前記モノマー混合物(I)の全量及び前記開始剤溶液の半量をそれぞれ2時間かけて滴下させた。その後直ちにロート2のコックを開き、前記モノマー混合物(II)の全量と、該開始剤溶液の残り半量とを2時間かけて滴下させた。
次いで、反応系を90℃で1時間保温した後、更にイオン交換水562部を仕込むことにより、重量平均分子量121万及び粘度8,900mPa・sの両性ポリアクリルアミド(固形分濃度15.0%)を得た。
モノマー混合物(I)とモノマー混合物(II)及び開始剤溶液を表1に示す組成のものに変更した以外は実施例1と同じ方法で両性ポリアクリルアミド(いずれも固形分濃度15.0%)を得た。
モノマー混合物(I)とモノマー混合物(II)を表1に示す組成のものに変更した以外は実施例1と同じ方法で両性ポリアクリルアミド(いずれも固形分濃度15.0%)を得た。
撹拌機、温度計、還流冷却管、窒素ガス導入管及び3つの滴下ロート(以下、順にロート1、ロート2及びロート3という。)を備えた反応容器にイオン交換水276.2部を仕込み、該イオン交換水に窒素ガスを直接吹き込むことにより該反応容器内の酸素を除去した後、該イオン交換水の温度を90℃に設定した。
次いで、ロート1に、モノマー混合物(I)として、50%アクリルアミド水溶液193.00部、ジメチルアミノエチルメタクリレート40.20部、60%ジメチルアミノエチルメタクリレートのベンジルクロライド4級化物24.20部、80%アクリル酸1.40部、N,N−ジメチルアクリルアミド0.300部、メチレンビスアクリルアミド0.250部、メタリルスルホン酸ナトリウム3.200部、62.5%硫酸19.70部及びイオン交換水168.1部からなる水溶液を更に硫酸でpH4.5に調整したものを仕込んだ。
次いで、ロート2に、モノマー混合物(II)として、50%アクリルアミド水溶液469.00部、80%アクリル酸9.200部、N,N−ジメチルアクリルアミド0.30部、メチレンビスアクリルアミド0.250部、メタリルスルホン酸ナトリウム0.800部及びイオン交換水212.30部からなる水溶液を仕込んだ。
次いで、ロート3に、過硫酸アンモニウム0.6部及びイオン交換水180部からなる開始剤溶液を仕込んだ。
次いで、ロート1とロート3のコックを同時に開き、前記モノマー混合物(I)の全量及び前記開始剤溶液の半量をそれぞれ2時間かけて滴下させた。その後直ちにロート2のコックを開き、前記モノマー混合物(II)の全量と、該開始剤溶液の残り半量とを2時間かけて滴下させた。
次いで、反応系を90℃で1時間保温した後、更にイオン交換水400部を仕込むことにより、重量平均分子量300万及び粘度8,500mPa・sの両性ポリアクリルアミド(固形分濃度20.3%)を得た。本サンプルをイオン交換水にて15.0%に希釈した粘度を測定すると1,200mPa・sであった。
AM:アクリルアミド(分子量71.1)
DM:ジメチルアミノエチルメタクリレート(分子量157.2)
DML:ジメチルアミノエチルメタクリレートのベンジルクロライド4級化物(分子量283.8)
APDM:ジメチルアミノプロピルアクリルアミド(分子量156.2)
DMAEA−BQ:ジメチルアミノエチルアクリレートのベンジルクロライド4級化物(分子量269.8)
IA:イタコン酸(分子量130.1)
AA:アクリル酸(分子量72.1)
DMAA:N,N−ジメチルアクリルアミド(分子量99.1)
MBAA:メチレンビスアクリルアミド(分子量154.2)
SMAS:メタリルスルホン酸ナトリウム(分子量158.2)
APS:過硫酸アンモニウム(分子量228.2)
V−50:2,2’−アゾビス−2−アミジノプロパン 二塩酸塩(分子量271.2)
実施例1〜15及び比較例1〜11の両性ポリアクリルアミド26.7mgと重水(D2O)0.8mlとを混合した後、当該混合液に、3−(トリメチルシリル)−1−プロパンスルホン酸ナトリウム(DSS)40.23mgとD2O1.0mlとを混合してなる内部標準液を、マイクロシリンジを用いて1μl滴下し、測定用サンプル(濃度:0.5%)を調製した。
プローブ:AutoX PFG probe(5mm)
プローブ温度:70℃
測定周波数:399.75MHz
測定溶媒:重水(D2O)
パルスシーケンス:presaturation スタンダードパラメーター使用
積算回数:128回
前記NMR測定器に付属する解析ソフトvNMRJ(Agilent Technologies製)を用い、シグナルの面積<As>及び<Bs>をそれぞれ計算機上で求めた上で、面積の比率[As/(As+Bs)]を算出した。結果を表4に示す。
実施例1〜15及び比較例1〜11の両性ポリアクリルアミドについて、以下の条件下、重量平均分子量及び多分散度(Mw/Mn)を測定した。結果を表4に示す。
カラム:東ソー(株)製ガードカラムPWXL1本及びGMPWXL2本(カラム温度40℃。)
溶離液:N/2酢酸緩衝液(N/2酢酸(和光純薬工業(株)製)+N/2酢酸ナトリウム(キシダ化学(株)製)水溶液、pH4.2)
流速:0.8ml/分
検出器:
RALLS法;ビスコテック社製TDA MODEL301(濃度検出器及び90°光散乱検出器及び粘度検出器の温度はそれぞれ40℃に設定)
実施例1〜15及び比較例1〜11の両性ポリアクリルアミドについて、B型粘度計(製品名「ビストメトロン」、芝浦システム社製)を用い、25℃、回転数6rpm、ローターNo.3の条件で粘度を測定した。結果を表4に示す。
晒クラフトパルプ(LBKP)をナイアガラ式ビーターにて叩解し、カナディアン・スタンダード・フリーネス(C.S.F)が350mlになるよう調成したスラリーを得た。次いで、当該スラリーに芒硝を添加して、その電気伝導度を0.5mS/cmに調節することにより、1%スラリーの紙料1を調製した。なお、当該電気伝導度は、市販の測定器(商品名「pH/COND METER D−54」、(株)堀場製作所製)を用いて測定した。
前記成紙1及び成紙2の比引張強さをJIS P 8113に準拠して測定した。比引張強さ等の紙力は添加された両性ポリアクリルアミドの種類だけでなく、紙中の灰分量に大きく影響を受ける。両性ポリアクリルアミドの種類により填料の凝集性、相互作用が異なり紙中への填料の歩留りが変化するため、各種両性ポリアクリルアミドを添加した紙の灰分量は通常同量にはならない。前述の通り、紙力は紙中灰分量に影響を受けるため、両性ポリアクリルアミドの添加による紙力向上効果の差は同等の紙中灰分量に補正したもので比較する必要がある。比引張強さは以下に従って補正した。
同じ両性ポリアクリルアミドを添加して調製した成紙1及び成紙2の紙中灰分率及び比引張強さの関係(図4)から次式により紙中灰分20%の強度を概算した。結果を表5に示す。
a=(Y2− Y1)/ (X2− X1)
X1:成紙1の紙中灰分率
X2:成紙2の紙中灰分率
Y1:成紙1の比引張強さ
Y2:成紙2の比引張強さ
前記成紙1及び成紙2の内部強度をJ.TAPPI No.18−2に準拠して測定した。比引張強さと同様に紙中灰分20%での内部強度を算出した結果を表5に示す。
前記成紙2からの通過光(輝度)を市販の測定器(商品名「パーソナル画像処理システムHyper−700」、OBS社製)に取り込み、輝度分布を統計解析することにより得られた値を、該成紙2の地合変動係数(変動係数)とした。地合変動係数は、その値が小さい程、地合が良好であることを意味する。結果を表5に示す。
前記成紙2と成紙3それぞれの窒素分を、市販の測定装置(製品名「TN−110」、三菱化学(株)製)を用いて求め、該窒素分の値を以下に示す計算式に代入し、両性ポリアクリルアミドの定着率を算出した。結果を表5に示す。
Claims (17)
- 下記要件〔1〕、〔2〕、〔3〕、〔4〕及び〔5〕を備える両性ポリアクリルアミドを含有する、無機填料を対パルプの重量(固形分)で10〜50重量%含有するパルプスラリー用紙力増強剤。
〔1〕その構成成分(1)がアクリルアミド(a)、αメチル基含有カチオン性ビニルモノマー(b)、アニオン性ビニルモノマー(c)を含み、
(c)成分がαメチル基不含有不飽和カルボン酸であり、αメチル基不含有不飽和カルボン酸がアクリル酸及び/又はその塩を含む
〔2〕その構成成分(1)における(b)成分の比率が1〜15モル%であり、かつ、(c)成分の比率が1〜10モル%である
〔3〕その1H−NMRスペクトルの0.9ppm〜1.35ppmの範囲に該(b)成分のαメチル基に帰属する高磁場側吸収帯Aと低磁場側吸収帯Bがあり、かつ、該吸収帯Aの面積(As)及び該吸収帯Bの面積(Bs)の合計面積に対する該吸収帯Aの面積(As)の比率[As/(As+Bs)]が12%以上25%未満である
〔4〕その15重量%水溶液(25℃)の粘度が3,000〜30,000mPa・sである
〔5〕その重量平均分子量(Mw)と数平均分子量(Mn)の比率(Mw/Mn)が3.5以下である - 構成成分(1)における(a)成分の比率が55〜97.8モル%である、請求項1の紙力増強剤。
- (b)成分が、第3級アミノ基含有メタクリレート、第3級アミノ基含有メタクリルアミド、第4級塩構造含有メタクリレート、及び第4級塩構造含有メタクリルアミドからなる群より選ばれる少なくとも一種である、請求項1又は2の紙力増強剤。
- 構成成分(1)が、更にαメチル基不含有カチオン性ビニルモノマー(b’)を含む、請求項1〜3のいずれかの紙力増強剤。
- (b’)成分が、第3級アミノ基含有アクリレート、第3級アミノ基含有アクリルアミド、第4級塩構造含有アクリレート、及び第4級塩構造含有アクリルアミドからなる群より選ばれる少なくとも一種である、請求項4の紙力増強剤。
- 構成成分(1)における(b’)成分の比率が0.1〜3モル%である、請求項4又は5の紙力増強剤。
- αメチル基不含有不飽和カルボン酸がアクリル酸及び/又はその塩を含み、かつその占有比率が50モル%以上である、請求項1の紙力増強剤。
- 構成成分(1)が更に架橋性モノマー(d)を含む、請求項1〜7のいずれかの紙力増強剤。
- (d)成分が、N,N−ジメチルアクリルアミド及びメチレンビスアクリルアミドからなる群より選ばれる少なくとも一種を含む、請求項8の紙力増強剤。
- 構成成分(1)における(d)成分の比率が0.01〜1モル%である、請求項8又は9の紙力増強剤。
- 構成成分(1)が更に連鎖移動性ビニルモノマー(e)を含む、請求項1〜10のいずれかの紙力増強剤。
- (e)成分が(メタ)アリルスルホン酸塩を含む、請求項11の紙力増強剤。
- 構成成分(1)における(e)成分の比率が0.05〜2モル%である、請求項11又は12の紙力増強剤。
- 請求項1〜13のいずれかの紙力増強剤を、無機填料を対パルプ濃度で10〜50重量%含有する抄紙系内に添加することを特徴とする、紙の製造方法。
- 無機填料が、タルク、カオリン及び炭酸カルシウムからなる群より選ばれる少なくとも一種である、請求項14の紙の製造方法。
- 請求項14又は15の紙の製造方法で得られる紙。
- 紙中灰分が10重量%以上である、請求項16の紙。