JP6840843B2 - 電気・電子、自動車部品用銅合金の錫めっき方法及びこれにより製造された銅合金の錫めっき材 - Google Patents
電気・電子、自動車部品用銅合金の錫めっき方法及びこれにより製造された銅合金の錫めっき材 Download PDFInfo
- Publication number
- JP6840843B2 JP6840843B2 JP2019520834A JP2019520834A JP6840843B2 JP 6840843 B2 JP6840843 B2 JP 6840843B2 JP 2019520834 A JP2019520834 A JP 2019520834A JP 2019520834 A JP2019520834 A JP 2019520834A JP 6840843 B2 JP6840843 B2 JP 6840843B2
- Authority
- JP
- Japan
- Prior art keywords
- plating
- tin
- copper
- layer
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
法は、銅めっき又はニッケルめっきと銅めっきを混合した下地めっき後、錫めっきを順に実施し、リフロー処理によりスズ被覆中にCu−Sn化合物又はCuSnNi化合物を露出させて挿入力を低減する方式であるが、この場合、スズ層の面積率が相対的に低くなるので、スズ層の耐熱剥離性及び半田付け性が落ちる問題がある。
CuSO4)が不足し過ぎると、元素材の表面に銅めっき層が均一に形成されないので、
以後の工程である錫めっき層の形成において錫めっきの光沢及び均一電着性が低下して局部的粗いめっきが生成されるなどのめっき不良が発生する可能性が高い。また、硫酸銅が多すぎると、硫酸の濃度が高くなって電流密度が増加し、その結果、硫酸銅の結晶化が発
生する。
02}/I{022}を同時に満たす。ニッケル下地めっき層の結晶配向性については後に
詳しく説明する。
ethane sulfonic acid)100〜200ml/L、及びアルコールを
含む揮発性系列の添加剤50〜150ml/Lを混合して用意する。アルコールが含む揮発性系列の添加剤は、亜セレン酸、亜セレン酸ナトリウム、亜砒酸ナトリウム、チオシアン酸カリウム、炭酸鉛及び亜鉛からなるグループから選択される1つ以上を揮発性アルコールと混合したものである。添加剤は組織の微細化及び平滑度を確保できるようにする。錫めっきは、例えば、温度40〜60℃、電流1〜10ASD、時間10〜1000秒の条件で実施できる。錫めっき層の種類はSn、Sn−Ag合金、Sn−Bi合金、Sn−Zn合金又はSn−Pb合金から選択できる。
成されて摩擦係数が増加し、半田付け性が低下し、後述される炭素(C)、リン(P)、酸素(O)の化合物(C、P、O化合物)に対する関係式(C+P)/Oが2.5を超える。
えるか、又は2段階熱処理が700℃を超えるか1200秒を超えると、Cu−Sn化合物(Cu6Sn5)の<2−1−10>||[001]結晶方向の分率が60%を超えるか、又はスズ合金層の<123>||[001]結晶方向の分率が60%を超えると、耐熱剥離性が低下する。
の結晶方向の成長が促進され、同時に錫めっき層の表面にリン酸塩系列の炭素(C)、リン(P)、酸素(O)の化合物が形成される。より具体的には、化合物は表面のリフロー段階を経て、Snめっき層と反応して潤滑性を有する化合物が表面上に酸化物の形態で形成されるが、化合物はFE−SEM/EDSで化合物元素成分の確認結果、炭素、リン、酸素化合物を含み、化合物の潤滑性によって最終的に生成された銅合金錫めっき材の挿入力、耐熱剥離性及び半田付け性が同時に確保された。
上述した方法でめっきされた銅合金錫めっき材の表面において、Cu−Sn化合物(C
u6Sn5)の<2−1−10>||[001]結晶方向の分率は10〜60%である。また
、Sn層の<123>||[001]結晶方向の分率は10〜60%であり、<014>||[
001]結晶方向は分率10%以下である。3つの条件を満たす場合、挿入力、耐熱剥離
性及び半田付け性が同時に優れる。これは、錫めっき層表面の形状だけではなく、端子の挿入過程において、錫めっき層のCu−Sn化合物(Cu6Sn5)層の<2−1−10>
||[001]結晶方向、及びSn層の<123>||[001]結晶方向の分率増加により、応力の集中を低減して摩擦係数を下げ、挿入力低減の効果が奏されたものと思われる。また、<014>||[001]結晶方向は<123>||[001]結晶方向の成長配列性と逆に動き、<014>||[001]結晶方向が10%を超える範囲では挿入力が落ちる傾向がある。
本発明では表面処理及びリフロー処理により銅合金の錫めっき材表面の潤滑性を有する化合物を形成し、化合物は、FE−SEM/EDSで化合物の元素成分を分析した結果、C、P、O元素が存在し、この時、関係式0.5<(C+P)/O<2.5が維持される。範囲内にいる場合、化合物はめっき材の耐熱剥離性、半田付け性に影響を及ぼさず、端子の挿入過程で表面エネルギーが減少するので挿入力が低減する。
選択的なニッケル下地めっきの後、めっき材のXRD分析結果、ピークの強度によるニッケルめっき層結晶面の結晶配向は回折強度値で示すことができる。本発明において、ニッケルめっき後、XRD分析のための結晶面は{111}、{002}、{022}面である。上述した本発明のニッケルめっき段階、{002}、{111}結晶面の強度比は1.25<I{002}/I{111}<2を満たし、同時に{002}、{022}結晶面の強度比が10<I{002}/I{022}範囲を満たす時、摩擦係数、耐熱剥離性及び半田付け性が良好である。即ち、摩擦力を低減するためには表面処理、スズ層の結晶面の制御だけではなく、下地層であるニッケル及びニッケル合金の結晶面の制御も重要である。
錫めっきを実施する前に密着性と平滑性を高めるために銅下地めっきを施す。下地めっきを施さない場合、光沢不良、粗いめっき、めっき剥離などの様々な欠陥が発生することができる。本発明では、銅及び銅合金材の表面に下地めっきとして銅めっきを施し、選択的に銅めっきの前又は後にニッケル又はニッケル合金めっきをさらに施すことができる。
本発明によると、上述した下地層上に錫めっき層を形成する。錫めっき層の総厚さは0.2〜3.0μmである。上述した表面処理及びリフロー処理後、Cu−Sn化合物のめ
っき厚さは0.1〜1.5μmであり、スズの厚さも0.1〜1.5μmである。Cu−Sn化合物のめっき層厚さが0.1μm未満であると、錫めっき表面の摩擦力が増加し、1.5μmを超えると、半田付け性が低下する。また、スズ厚さが0.1μm未満であると、半田付け性が低下し、スズ厚さが1.5μmを超えると、錫めっき表面の摩擦力が増加して挿入力が低下する。
コルソン系合金(Cu−Ni−Si)の銅合金母材をサイズ10cm×10cmに切断する。このサンプルを、電解脱脂薬品であるUDC−5030Lを70g/L濃度に実施した後、濃硫酸10%濃度で10秒間酸洗い処理する((a)電解脱脂及び酸洗い処理段階)。
ne sulfonic acid)150ml/L、及び亜セレン酸、亜セレン酸ナトリ
ウム、チオシアン酸カリウム、メタノールを1:1:2:5に混合した添加剤を揮発性アルコール系列と混合した添加剤80ml/Lを含む錫めっき液を使用して、温度30℃、電流2ASDで60秒間実施する。その結果、錫めっき層0.4μmが生成される((c)
錫めっき段階)。
学(韓国、仁川))10ml/Lを使用して用意したニッケルめっき液を用いて、めっき条
件を温度55℃、電流3ASD、めっき時間40秒としてニッケルめっきする段階を含むことを除いては、実施例1と同様にして錫めっき材を製造し、最終的に得られた試験片を発明例2とする。
実施例1又は実施例2を参考しながら、表1及び表2に示した詳しい製造条件に従って実施例3〜実施例4を実施した。実施例3〜実施例14によって各々試験片を制作して、発明例3〜発明例14とする。
上述した実施例と同様の方式により、表1及び表2に示した条件下で各々試験片を制作して、比較例1〜比較例14とする。
実施例及び比較例により得られた試料の各々に対して、以下の評価を実施する。各試料に対するCu−Sn化合物(Cu6Sn5)、Sn層の結晶方向分率の測定、摩擦係数の測定、耐熱剥離性、半田付け性、めっき厚さの測定、表面成分分析、XRD分析を以下の方法で評価する。
得られた試験片をイオンミリング(ion milling)より断面研磨した後、FE
−SEMのEBSD装備を活用して測定し、その後、TSL OIM分析器を活用して結
晶方向分率を分析する。結晶面分率はEBSD結果から方位を測定して分率を計算する。
結果を表3に示す。
摩擦係数は挿入力を示す指標であり、摩擦係数測定装備Triboger type:
14FW(製造社:HEIDON、日本東京)を活用して摩擦係数を測定する。Snめっき材の板試料の試料台上に固定させ、図面の接触子はφ10mmステンレスボール(Sta
inless ball)を用い、荷重は30gとする。資料台の移動速度は13mm/secであり、移動距離は10mmである。摩擦係数式はμ=F/Wで算出する。結果を表3に示す。本発明による試験片の場合、摩擦係数は0.1〜0.4範囲に該当する。
耐熱剥離性を以下の方法で判断する。得られた試験片を長さ60mm、幅10mmに切断して180℃で1時間加熱した後、試験片を取り出して冷却する。その後90°に曲げて広げる。試験片の曲げ部分の内径部に接着テープ(3M Masking Tape、#
851A)を付着して密着した後、すぐ試験片から除去して、曲げ部分の内径部を光学顕
微鏡で観察する。めっき表面に剥離跡がない場合は良好と判定し、めっき表面に剥離跡が残った場合には剥離と判定する。結果を表3に示す。
半田付け性は試験片を平衡システム(一般的にスプリングシステム)に吊り、235±5℃の溶融半田槽内の所定の深さまで端部を浸す。浸した試験片は、作用する浮力と表面張力により発生する垂直方向の合成力を変換器で検出して、高速チャート記録計に時間の関数として連続して記録し、素材の表面と半田(solder)との接触角と荷重を求めて半田付け性(ぬれ時間、秒)を測定した。得られた結果を表3に示す。
X線チューブから発生した1次X線が試料表面に照射されて2次蛍光X線が発生する。素材の表面から発生する2次蛍光X線の強度は表面にめっきされた厚さに比例して増減する。この過程をめっき厚さと2次蛍光X線の強度との相関関係で計算してめっき層の厚さを5回測定した後、平均値を測定する。銅下地めっき層、ニッケル下地めっき層、錫めっき層の各々のめっき厚さは表1に示す。
表面処理、及びリフロー処理した試験片の表面をイオンミリングした後、FE−SEM/EDSにより成分を分析する。結果を表3に示す。
試験片を1cm×1cm切断後、XRDによりニッケルめっき層の結晶構造を分析し、その後、High score plus機器(製造社:Panalytical、オラン
ダ)を活用して主要ピーク(Peak)の強度比を計算する。結果を表4に示す。
試験片を5cm×5cm切断後、光学顕微鏡で試験片表面における染み発生の有無を確認する。目視で確認して染みがない場合は未発生、染みがある場合は発生と判定する。結果を表3に示す。
比較例1は、リン酸塩系列の濃度1g/mlで添加した溶液を浸漬後、リフローによる熱処理後に(C+P)/Oの関係式の結果が0.3であり、良好ではなかった。比較例2では、リン酸塩系列の濃度50g/mlの溶液で表面処理、リフロー処理した後、(C+P)/Oの関係式は3.2であり、半田付け性は4.52秒であり、不良であった。比較例3は、表面処理、リフロー処理過程で1段階熱処理は100℃で1秒間、2段階熱処理は200℃で2秒間実施してCu−Sn化合物(Cu6Sn5)の<2−1−10>||[001]結晶方向分率は4%、スズ層の<123>||[001]結晶方向分率は5%、<014>||[
001]結晶方向分率は18%であり、摩擦係数が0.53であるので、求められる特性
に到達できなかった。比較例4は、表面処理後、リフロー処理の過程において、1段階熱処理では300℃で35秒、2段階熱処理では800℃で1500秒間熱処理を実施して、Cu−Sn金属間化合物(Cu6Sn5)の<2−1−10>||[001]結晶方向分率は73%、Sn層の<123>||[001]結晶方向分率は68%、<014>||[001]結晶方向は分率は2%であり、耐熱剥離性試験で剥離が発生した。比較例5は、スズ合金めっき厚さを4μmとし、スズ層のCu−Sn化合物(Cu6Sn5)<2−1−10>||[
001]結晶方向分率は8%、Sn層の<123>||[001]結晶方向分率は9%、<0
14>||[001]結晶方向は分率は15%を有し、摩擦係数が落ちた。比較例6では、錫めっき厚さが0.05μmである場合に、耐熱剥離性が落ちた。比較例7及び8では、沈漬方式で表面処理を実施した結果、表面染みが発生し、これにより摩擦係数、半田付け性が落ち、リン酸塩の関係式では炭素(C)の増加により(C+P)/O値が2.5を超えた。比較例9及び10は、スプレー方式で表面処理を実施した結果、微量の染みが発生して摩擦係数、半田付け性が落ち、炭素(C)によって(C+P)/O値が2.5を超えた。比較例10及び11は、表面処理後、1段階リフロー処理を実施した結果、Cu−Sn化合物(
Cu6Sn5)の<2−1−10>結晶方向の分率が10%以下であり、染みが発生し、
200〜250℃熱処理過程の省略による炭素(C)、リン(P)、酸素(O)の結合が安定して形成されず、(C+P)/O値が2.5を超えた。
02}、{022}結晶面の強度比を表4に示す。{111}、{002}、{022}結晶面に
おいて、{002}、{111}結晶面の強度比は1.25<I{002}/I{111}<2を満たし、{002}、{022}結晶面では強度比10<I{002}/I{022}を同時に満たす。
002}/I{022}は6.7であり、摩擦係数が落ちた。比較例14(電流:10ASD、時間1500秒)は、得られた錫めっき材のI{002}/I{111}は1.1、I{002}/I{022}は1であり、耐熱剥離性が劣化した。
n5)、及びSn層の結晶構造を制御することにより、優れた挿入力を得ている。又はリ
フロー処理時に使用される表面処理剤のリサイクルが可能であり、表面処理後に別に熱処理することなくリフローで2段階熱処理を実施するので、製造費用の側面でも有利である。
Claims (5)
- 電気・電子又は自動車部品用銅合金の錫めっき方法であって、
(a)銅合金母材を電解脱脂及び酸洗いする段階、
(b)段階(a)により得られた生成物を銅下地めっきする段階、及び選択的に銅下地めっきの前又は後にニッケル又はニッケル合金めっきを施す段階を含み、前記ニッケル又はニッケル合金のめっきは温度40〜60℃、電流2〜7ASD、及び時間10〜1000秒で実施してもよく、
(c)段階(b)により得られた生成物をスズ又はスズ合金めっきする段階、
(d)段階(c)により得られた生成物を、表面処理剤をミスト噴射して表面処理する段階、及び
(e)段階(d)により得られた生成物を200〜250℃で1〜30秒間実施する1段階熱処理と300〜700℃で3〜1200秒間実施する2段階熱処理とからなる2段階のリフロー処理する段階からなり、
前記表面処理剤が、リン酸とリン酸エステルの対、亜燐酸と亜燐酸エステルの対、及び次亜燐酸と次亜燐酸エステルの対からなるグループのうちのいずれか1つの対が選択され、及び表面処理剤の濃度は2〜10g/mLであり、
錫めっき層の厚さは0.2〜3.0μmであり、リフロー処理後のCu−Sn化合物の厚さは0.1〜1.5μmであり、及びリフロー処理後のスズの厚さは0.1〜1.5μmであり、
得られた銅合金の錫めっき材は、スズ及びスズ合金の断面のEBSDの分析結果、Cu−Sn化合物(Cu6Sn5)の<2−1−10>||[001]結晶方向分率10〜60%、スズ又はスズ合金層の<123>||[001]結晶方向分率10〜60%、及びスズ又はスズ合金層の<014>||[001]結晶方向分率10%以下であり、並びに
前記スズ又はスズ合金めっき層の表面に炭素(C)、リン(P)、酸素(O)の化合物が存在し、C、P及びOの間の関係式が0.5<(C+P)/O<2.5である、
電気・電子又は自動車部品用銅合金の錫めっき方法。 - ニッケルめっき層のXRDの分析時、{111}、{002}、{022}結晶面において{
002}、{111}結晶面の強度比は1.25<I{002}/I{111}<2を満たし、{002}、{022}結晶面の強度比は10<I{002}/I{022}を満たす、請求項1
に記載の電気・電子又は自動車部品用銅合金の錫めっき方法。 - 下地めっきの厚さは0.1〜2.0μmであり、下地めっきは銅めっきを意味する、またはニッケルめっきが実施されたときには、下地めっきは銅めっき及びニッケルめっきを意味する、請求項1又は2に記載の電気・電子又は自動車部品用銅合金の錫めっき方法。
- 錫めっき層はSn、Sn−Ag、Sn−Bi、Sn−Zn、Sn−Pb又はこれらの組み合わせから選択されるものである、請求項1〜3のいずれか一項に記載の電気・電子又は自動車部品用銅合金の錫めっき方法。
- ニッケルめっき層はNi、Ni−Pd、Ni−Co、Ni−Sn、Ni−P又はこれらの組み合わせから選択されるものである、請求項1〜4のいずれか一項に記載の電気・電子又は自動車部品用銅合金の錫めっき方法。