JP6799070B2 - 光硬化性シリコーン組成物及びその硬化物 - Google Patents
光硬化性シリコーン組成物及びその硬化物 Download PDFInfo
- Publication number
- JP6799070B2 JP6799070B2 JP2018542719A JP2018542719A JP6799070B2 JP 6799070 B2 JP6799070 B2 JP 6799070B2 JP 2018542719 A JP2018542719 A JP 2018542719A JP 2018542719 A JP2018542719 A JP 2018542719A JP 6799070 B2 JP6799070 B2 JP 6799070B2
- Authority
- JP
- Japan
- Prior art keywords
- component
- mass
- parts
- group
- silicone composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の光硬化性シリコーン組成物は、
(A)以下の平均組成式:
R1 aR2 bSiO(4−a−b)/2
(式中、R1は炭素数2〜12のアルケニル基であり、R2は炭素数1〜12のアルキル基、炭素数6〜12のアリール基、又は炭素数7〜12のアラルキル基であり、但し、少なくとも30mol%のR2はアリール基又はアラルキル基であり、「a」及び「b」は1≦a+b≦2.5及び0.001≦a/(a+b)≦0.2を満たす正の数である)によって表されるオルガノポリシロキサン100質量部と、
(B)分子中に少なくとも2つのエーテル結合及び少なくとも1つの脂肪族炭素−炭素二重結合を有する有機化合物3〜30質量部と、
(C)分子中に少なくとも2つのチオール基を有する化合物であって、本成分中のチオール基の量が、本組成物中の全脂肪族炭素−炭素二重結合1mol当たり0.2〜2.0molである量の化合物と、
(D)リン原子を有する光ラジカル開始剤0.05〜1.0質量部と、
(E)ヒンダードフェノール化合物0.001〜1.0質量部と、を含む。
本発明の光硬化性シリコーン組成物は、活性エネルギー線の照射により硬化し、照射部分近傍の未照射部分をも硬化させることができる。更に、本発明の硬化物は、透明性を維持し、高温/高湿条件に放置しても着色及びヘイズが発生しにくい。
R1 aR2 bSiO(4−a−b)/2によって表されるオルガノポリシロキサンである。
Vi0.03Me1.03Ph0.97SiO0.99:ViMe2SiO(MePhSiO)65SiMe2Vi
Vi0.10Me1.10Ph0.90SiO0.95:ViMe2SiO(MePhSiO)18.4SiMe2Vi
Vi0.09Me1.06Ph0.91SiO0.97:PhSi{O(PhMeSiO)10SiMe2Vi}3
Hex0.09Me1.07Ph0.89SiO0.98:Si{O(PhMeSiO)10SiMe2Hex}4
Hex0.12Me1.12Ph0.88SiO0.94:HexMe2SiO(PhMeSiO)15SiMe2Hex
Vi0.06Me1.38Phe0.63SiO0.97:ViMe2SiO(PheMeSiO)20(Me2SiO)10SiMe2Vi
Hex0.06Me1.38Php0.63SiO0.97:HexMe2SiO(PhpMeSiO)20(Me2SiO)10SiMe2Hex
光硬化性シリコーン組成物の25℃における粘度を、コーンプレート型粘度計を使用して測定した。
一方の側が閉じられ、長さ20cm、内径5mmの黒色のチューブに光硬化性シリコーン組成物を充填した。一方の開口部から、高圧水銀ランプを使用して200mW/cm2のUV照度で紫外光を20秒間照射した。照射後、チューブを切断し、硬化により流動性が失われた部分の長さを測定した。
光硬化性シリコーン組成物を、所定形状の凹部を有する金型に充填し、累積放射線(cumulative radiation)が4000mJ/cm2となるように高圧水銀ランプを使用して最上部の液面から照射した。得られた硬化物の硬度を、ASTM2240−00に規定された方法によって、Type 00ショア押し込み硬度計を使用して測定した。
上記のように硬化させた厚さ500μmの板状硬化物を、ASTM D1003に規定された方法に従って、透過率及びヘイズを測定した。その後、板状硬化物を105℃で1000時間保持することによって得られた試料及び板状硬化物を85℃で85%RHの環境下に1000時間保持することによって得られた試料に関して、上記の方法と同様に透過率及びヘイズの各々を測定した。
上記のように硬化させた厚さ500μmの板状硬化物を、ASTM D6290に規定された方法に従って、黄色度指数b*を測定した。その後、板状硬化物を105℃で1000時間保持することによって得られた試料及び板状硬化物を85℃で85%RHの環境下に1000時間保持することによって得られた試料に関して、上記の方法と同様に各黄色度指数b*を測定した。
(a1)40000mPa・sの粘度を有し、以下の平均式:
ViMe2SiO(MePhSiO)65SiMe2Vi
(平均組成式:Vi0.03Me1.03Ph0.97SiO0.99)で表されるオルガノポリシロキサン。
(a2)2000mPa・sの粘度を有し、以下の平均式:
ViMe2SiO(MePhSiO)18.4SiMe2Vi
(平均組成式:Vi0.10Me1.10Ph0.90SiO0.95)で表されるオルガノポリシロキサン。
(a3)2000mPa・sの粘度を有し、以下の平均式:
ViMe2SiO(Me2SiO)300SiMe2Vi
(平均組成式:Vi0.01Me2.00SiO1.00)で表されるオルガノポリシロキサン。
(b1):35mPa・sの粘度を有するフェノキシテトラエチレングリコールアクリレート
(b2):90mPa・sの粘度を有するメトキシノナエチレングリコールアクリレート
(b3):100mPa・sの粘度を有するノニルフェノキシテトラエチレングリコールアクリレート
(b4):125mPa・sの粘度を有するノニルフェノキシジプロピレングリコールアクリレート
(b5):55mPa・sの粘度を有するノナエチレングリコールジアクリレート
(b6):150mPa・sの粘度を有するノニルフェノキシオクタエチレングリコールアクリレート
(c1):トリメチロールプロパントリス(3−チオプロピオネート)
(c2):ペンタエリスリトールテトラキス(チオグリコレート)
(c3):ペンタエリスリトールテトラキス(3−チオプロピオネート)
(d2):エチル(2,4,6−トリメチルベンゾイル)フェニルホスフィネート
(d3):フェニルビス(2,4,6−トリメチルベンゾイル)ホスフィンオキシド
(d4):2−ヒドロキシ−2−メチル−1−フェニルプロパン−1−オン
(d5):1−ヒドロキシシクロヘキシルフェニルケトン
(e1):ジ−tert−ブチルヒドロキシトルエン
(f1):tert−ブチルヒドロキノン
(f2):ピロガロール
(f3):アルミニウム−N−ニトロソ−N−フェニルヒドロキシルアミン
(f4):4−メトキシナフトール
(g1):15mPa・sの粘度を有するイソボルニルアクリレート
(g2):10mPa・sの粘度を有するテトラヒドロフルフリルアクリレート
(g3):10mPa・sの粘度を有するイソオクチルアクリレート
(g4):10mPa・sの粘度を有するイソデシルアクリレート
4970mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)54質量部及び成分(a2)46質量部からなり、10200mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b1)5.2質量部と、成分(c1)10.6質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d1)0.4質量部と、成分(e1)0.1質量部と、成分(f1)0.005質量部と、成分(g1)2.9質量部と、成分(g2)0.6質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
4072mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)54質量部及び成分(a2)46質量部からなり、10200mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b1)10質量部と、成分(c1)20質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.6molである量)と、成分(d1)0.4質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.6質量部と、成分(g3)2.4質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
3230mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)54質量部及び成分(a2)46質量部からなり、10200mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)10質量部と、成分(b3)8質量部と、成分(c1)5.9質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり0.5molである量)と、成分(d1)0.4質量部と、成分(e1)0.3質量部と、成分(f1)0.01質量部と、成分(g2)0.65質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
3450mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)61質量部及び成分(a2)39質量部からなり、12000mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)9質量部と、成分(b4)5質量部と、成分(c2)16質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.5molである量)と、成分(d1)0.4質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)4.6質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
3270mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)61質量部及び成分(a2)39質量部からなり、12000mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)13質量部と、成分(b5)2質量部と、成分(c3)12.4質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d1)0.4質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)5.2質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
4.210mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)47質量部及び成分(a2)53質量部からなり、8200mPa・sの粘度を有し、以下の平均組成式:
Vi0.07Me1.07Ph0.93SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)9質量部と、成分(c1)3.8質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり0.4molである量)と、成分(d1)0.4質量部と、成分(e1)0.3質量部と、成分(f1)0.01質量部と、成分(g2)0.6質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
3170mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b6)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d1)0.4質量部と、成分(e1)0.1質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
3050mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b6)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d1)0.7質量部と、成分(e1)0.1質量部と、成分(f2)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
3110mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b6)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d2)0.4質量部と、成分(e1)0.1質量部と、成分(f3)0.005質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
3060mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b6)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d3)0.27質量部と、成分(e1)0.1質量部と、成分(f4)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表1に示す。
1120mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a3)100質量部と、成分(b2)10質量部と、成分(b3)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d1)0.4質量部と、成分(e1)0.1質量部と、成分(f1)0.005質量部と、成分(g2)0.6質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
8650mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(c1)5.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり0.72molである量)と、成分(d1)0.4質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
5440mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b1)1.5質量部と、成分(c1)6.3質量部(本成分物におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり0.74molである量)と、成分(d1)0.4質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
1330mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b1)40質量部と、成分(c1)6.3質量部(本成分物におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり0.90molである量)と、成分(d1)0.4質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
3700mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b4)8質量部と、成分(c1)1.9質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり0.15molである量)と、成分(d1)0.4質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
2710mPa・sの粘度を有する光硬化性シリコーン組成物は、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b4)8質量部と、成分(c1)28質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり2.2molである量)と、成分(d1)0.4質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
3080mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b4)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d1)0.02質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
3010mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b4)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d1)1.2質量部と、成分(e1)0.2質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
3110mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b4)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d4)0.40質量部と、成分(e1)0.1質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
2960mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b4)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d4)1.08質量部と、成分(e1)0.1質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
2960mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b4)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d5)1.08質量部と、成分(e1)0.1質量部と、成分(f1)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
3080mPa・sの粘度を有する光硬化性シリコーン組成物を、成分(a1)60質量部及び成分(a2)40質量部からなり、12500mPa・sの粘度を有し、以下の平均組成式:
Vi0.06Me1.06Ph0.94SiO0.97によって表されるオルガノポリシロキサン100質量部と、
成分(b2)11質量部と、成分(b6)8質量部と、成分(c1)12.7質量部(本成分におけるチオール基の量が、本組成物における全脂肪族炭素−炭素二重結合1mol当たり1.0molである量)と、成分(d3)0.27質量部と、成分(f4)0.01質量部と、成分(g2)0.7質量部と、成分(g4)2.7質量部と、を混合することによって調製した。光硬化性シリコーン組成物及びその硬化物の特性を表2に示す。
本組成物は、紫外線及び可視光等の高エネルギー線を照射すると容易に硬化し、透明な硬化物を提供し、優れた深部硬化性を有する。従って、本組成物は、様々なポッティング剤、シーリング剤、及び接着剤として有用である。
Claims (5)
- 光硬化性シリコーン組成物であって、
(A)以下の平均組成式:
R1 aR2 bSiO(4−a−b)/2
(式中、R1は炭素数2〜12のアルケニル基であり、R2は炭素数1〜12のアルキル基、炭素数6〜12のアリール基、又は炭素数7〜12のアラルキル基であり、但し、少なくとも30mol%のR2はアリール基又はアラルキル基であり、「a」及び「b」は1≦a+b≦2.5及び0.001≦a/(a+b)≦0.2を満たす正の数である)によって表されるオルガノポリシロキサン100質量部と、
(B)分子中に少なくとも2つのエーテル結合及び少なくとも1つの脂肪族炭素−炭素二重結合を有する有機化合物3〜30質量部と、
(C)分子中に少なくとも2つのチオール基を有する化合物であって、本成分中の前記チオール基の量が、本組成物中の全脂肪族炭素−炭素二重結合1mol当たり0.2〜2.0molである量の化合物と、
(D)リン原子を有する光ラジカル開始剤0.05〜1.0質量部と、
(E)ヒンダードフェノール化合物0.001〜1.0質量部と、を含む、硬化性シリコーン組成物。 - 成分(B)が、分子中に、少なくとも2つのエーテル結合及び少なくとも1つのアクリロイル基又はメタクリロイル基を有する有機化合物である、請求項1に記載の光硬化性シリコーン組成物。
- 成分(E)以外のラジカル捕捉剤(F)を、成分(A)100質量部当たり0.0001〜1質量部の量で更に含む、請求項1又は2に記載の光硬化性シリコーン組成物。
- 成分(A)及び(B)以外に、脂肪族炭素−炭素二重結合を有する有機化合物(G)を、成分(A)100質量部当たり10質量部以下の量で更に含む、請求項1〜3のいずれか一項に記載の光硬化性シリコーン組成物。
- 請求項1〜4のいずれか一項に記載の光硬化性シリコーン組成物に光を照射することによって得られる硬化物。