JP6716071B1 - Ornaments - Google Patents

Ornaments Download PDF

Info

Publication number
JP6716071B1
JP6716071B1 JP2019149365A JP2019149365A JP6716071B1 JP 6716071 B1 JP6716071 B1 JP 6716071B1 JP 2019149365 A JP2019149365 A JP 2019149365A JP 2019149365 A JP2019149365 A JP 2019149365A JP 6716071 B1 JP6716071 B1 JP 6716071B1
Authority
JP
Japan
Prior art keywords
gold
alloy body
metal diffusion
gradation
color
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2019149365A
Other languages
Japanese (ja)
Other versions
JP2021029289A (en
Inventor
ラブロ コロマー ジャウム
ラブロ コロマー ジャウム
Original Assignee
ラブロ コロマー ジャウム
ラブロ コロマー ジャウム
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ラブロ コロマー ジャウム, ラブロ コロマー ジャウム filed Critical ラブロ コロマー ジャウム
Priority to JP2019149365A priority Critical patent/JP6716071B1/en
Priority to CN201911044490.4A priority patent/CN111000339A/en
Application granted granted Critical
Publication of JP6716071B1 publication Critical patent/JP6716071B1/en
Publication of JP2021029289A publication Critical patent/JP2021029289A/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

【課題】表面に現れる色のグラデーションを有する金の合金体を含む装飾品を提供する。【解決手段】ネックレス１１は、首に巻き掛けられるチェーン１２と、チェーン１２に結合されるペンダント１３とを有する。ペンダント１３は金属拡散に基づき形成され表面に現れる色のグラデーションを有する金の合金体１３ａを含む。合金体は異なる色を有する複数の金合金を含む。金の合金はいずれも同系色であることから、相違する色の金合金同士が金属拡散で結合すると、金合金同士の境界で金属拡散に基づき色が良好に混ざり合う。【選択図】図１PROBLEM TO BE SOLVED: To provide a decorative article including a gold alloy body having a gradation of colors appearing on the surface. A necklace (11) has a chain (12) wrapped around a neck and a pendant (13) coupled to the chain (12). The pendant 13 includes a gold alloy body 13a formed by metal diffusion and having a color gradation that appears on the surface. The alloy body includes a plurality of gold alloys having different colors. Since all gold alloys have the same color, when gold alloys of different colors are bonded by metal diffusion, the colors are mixed well at the boundary between gold alloys due to metal diffusion. [Selection diagram] Figure 1

Description

本発明は、指輪やネックレス、イヤリング、ブレスレットといったジュエリーおよび腕時計を含む装飾品に関する。 The present invention relates to jewelry, such as rings, necklaces, earrings, bracelets and ornaments including watches.

特許文献１には、第１色の第１金属バルクと、第１色から相違する第２色の第２金属バルクとに基づき成型されて、表面に色のグラデーションを有するジュエリー用素材が開示される。ジュエリー用素材の鋳造にあたって筒形状の鋳型に第１金属バルクおよび第２金属バルクはセットされる。第１金属バルクは鋳型の入り口に向かって徐々に縮小する断面を有する一方で、第２金属バルクは鋳型の入り口に向かって徐々に拡大する断面を有する。誘導コイルは第１金属バルクおよび第２金属バルクの断面に沿って溶融層を形成する。平たい溶融層が鋳型の入り口に向かって徐々に移動することで、溶融層内で第１金属バルクおよび第２金属バルクの比率が変化し、色のグラデーションが作られる。 Patent Document 1 discloses a jewelry material having a color gradation on the surface, which is molded based on a first metal bulk of a first color and a second metal bulk of a second color different from the first color. It When casting the jewelry material, the first metal bulk and the second metal bulk are set in a cylindrical mold. The first metal bulk has a cross-section that gradually decreases toward the mold inlet, while the second metal bulk has a cross-section that gradually decreases toward the mold inlet. The induction coil forms a molten layer along the cross section of the first metal bulk and the second metal bulk. Gradually moving the flat molten layer towards the inlet of the mold changes the ratio of the first metal bulk and the second metal bulk in the molten layer, creating a color gradation.

韓国特許公開第１０−２０１６−００２４１４９号公報Korean Patent Publication No. 10-2016-0024149

特許文献１のジュエリー用素材の製造方法では水平面に沿って平たい溶融層が形成される。溶融層には磁力線が作用するものの、溶融層内で水平方向に対流は生じにくい。溶融層は水平面に沿って平たいことから、溶融層内で色むらが生じやすい。その結果、仕上がった素材内で思い通りに色の配置を実現することは難しい。 In the method for manufacturing a material for jewelry of Patent Document 1, a flat molten layer is formed along a horizontal plane. Although magnetic lines of force act on the molten layer, horizontal convection is unlikely to occur in the molten layer. Since the molten layer is flat along the horizontal plane, color unevenness easily occurs in the molten layer. As a result, it is difficult to achieve the desired color arrangement in the finished material.

本発明は、良好に計算された配置で色のグラデーションを有する装飾品を提供することを目的とする。 The present invention aims to provide an ornament having a color gradation in a well-calculated arrangement.

本発明の第１側面によれば、金属拡散に基づき形成され表面に現れる色のグラデーションを有する金の合金体を含む装飾品は提供される。 According to a first aspect of the present invention, there is provided a decorative article including a gold alloy body formed by metal diffusion and having a color gradation that appears on the surface.

第２側面によれば、前記合金体は、異なる色を有する複数の金合金を含む。 According to a second aspect, the alloy body comprises a plurality of gold alloys having different colors.

本発明の第３側面によれば、異なる色を有する複数の金合金の素材を重ねる工程と、前記素材を加熱し、前記素材同士の境界面で金属拡散に基づき前記金合金を混合し、前記境界面を跨いで前記素材のグラデーションを形成する工程と、前記素材の塊を加工し、金属拡散に基づき形成され表面に現れる色のグラデーションを有する金の合金体を調整する工程とを備える装飾品向け合金体の製造方法は提供される。 According to a third aspect of the present invention, a step of stacking a plurality of gold alloy materials having different colors, heating the materials, and mixing the gold alloy based on metal diffusion at a boundary surface between the materials, A decorative article comprising a step of forming a gradation of the material across a boundary surface, and a step of processing a lump of the material to adjust a gold alloy body having a color gradation that appears on the surface and is formed based on metal diffusion. A method of manufacturing an alloy body is provided.

第１側面によれば、金の合金（以下、「金合金」という）はいずれも同系色であることから、相違する色の金合金同士が金属拡散で結合すると、金合金同士の境界で金属拡散に基づき色が良好に混ざり合う。金合金同士の境界は消失する。金属拡散は境界面から遠ざかるにつれて減少することから、境界面を跨いで混ざり合う素材のグラデーションは形成される。合金体の表面には、一方の色から他方の色に向かって徐々に変化する美しい色のグラデーションが現れる。金属拡散は固体の金属で実現されることから、金合金同士の境界面は固体の形状に基づき思い通りの位置に配置されることができる。こうして良好に計算された配置で色のグラデーションを有する装飾品は提供されることができる。 According to the first aspect, all gold alloys (hereinafter, referred to as “gold alloys”) have the same color. Therefore, when gold alloys of different colors are bonded by metal diffusion, the metal at the boundary between gold alloys The colors mix well due to diffusion. The boundaries between the gold alloys disappear. Since the metal diffusion decreases as the distance from the boundary surface increases, a gradation of the material that mixes across the boundary surface is formed. On the surface of the alloy body, a beautiful color gradation that gradually changes from one color to the other appears. Since metal diffusion is realized by a solid metal, the boundary surface between gold alloys can be arranged at a desired position based on the shape of the solid. An ornament with a color gradation in a well-calculated arrangement can thus be provided.

第２側面によれば、グラデーションの形成にあたって金合金は起点となる２以上の色を提供する。境界面を跨いで一方の色から他方の色に向かって徐々に色は変化する。こうして合金体の表面には美しい色のグラデーションが現れる。ここでは、装飾品は、金属拡散に基づき合金体に結合される金、パラジウムまたはプラチナの金属体を含んでもよい。結合される金合金が金、パラジウムまたはプラチナと同系色であれば、相違する色の金合金と金属体とが金属拡散で結合すると、金合金と金属体との境界で金属拡散に基づき色が良好に混ざり合う。金合金と金属体との境界は消失する。前述と同様に素材のグラデーションは形成される。 According to the second aspect, the gold alloy provides two or more starting colors for forming the gradation. The color gradually changes from one color to the other across the boundary surface. In this way, a beautiful color gradation appears on the surface of the alloy body. Here, the ornament may comprise a metal body of gold, palladium or platinum which is bonded to the alloy body on the basis of metal diffusion. If the gold alloy to be bonded has the same color as gold, palladium, or platinum, when the gold alloy and the metal body of different colors are bonded by metal diffusion, the color is based on the metal diffusion at the boundary between the gold alloy and the metal body. Mixes well. The boundary between the gold alloy and the metal body disappears. The gradation of the material is formed as described above.

第３側面によれば、金の合金はいずれも同系色であることから、相違する色の金合金同士が金属拡散で結合すると、金合金同士の境界で金属拡散に基づき色が良好に混ざり合う。金合金同士の境界は消失する。金属拡散は境界面から遠ざかるにつれて減少することから、境界面を跨いでグラデーションは形成される。合金体の表面には、一方の色から他方の色に向かって徐々に変化する美しい色のグラデーションが現れる。金属拡散は固体の金属で実現されることから、金合金同士の境界面は固体の形状に基づき思い通りの位置に配置されることができる。 According to the third aspect, since all gold alloys have the same color, when gold alloys of different colors are bonded by metal diffusion, the colors are mixed well at the boundary between gold alloys based on the metal diffusion. .. The boundaries between the gold alloys disappear. Since the metal diffusion decreases as the distance from the boundary surface increases, a gradation is formed across the boundary surface. On the surface of the alloy body, a beautiful color gradation that gradually changes from one color to the other appears. Since metal diffusion is realized by a solid metal, the boundary surface between gold alloys can be arranged at a desired position based on the shape of the solid.

本発明の一実施形態に係る装飾品としてのネックレスを概略的に示す概念図である。It is a conceptual diagram which shows the necklace as an ornamental goods concerning one embodiment of the present invention roughly. 合金体の製造方法を概略的に示す概念図である。It is a conceptual diagram which shows the manufacturing method of an alloy body roughly. ビレットの写真である。This is a picture of a billet. 他の実施形態に係る装飾品としてのリングを概略的に示す概念図である。It is a conceptual diagram which shows schematically the ring as an ornamental article which concerns on other embodiment. さらに他の実施形態に係る装飾品としてのイヤリングを概略的に示す概念図である。It is a conceptual diagram which shows schematically the earring as a decorative article which concerns on other embodiment. さらに他の実施形態に係る装飾品としてのブレスレットを概略的に示す概念図である。It is a conceptual diagram which shows roughly the bracelet as a decorative article which concerns on other embodiment.

以下、添付図面を参照しつつ本発明の一実施形態を説明する。 An embodiment of the present invention will be described below with reference to the accompanying drawings.

図１は本発明の一実施形態に係る装飾品としてのネックレスを概略的に示す。ネックレス１１は、首に巻き掛けられるチェーン１２と、チェーン１２に結合されるペンダント１３とを有する。ペンダント１３は、例えば、金属拡散に基づき形成され表面に現れる色のグラデーションを有する金の合金体１３ａを含む。合金体１３ａの表面には複数のダイヤモンド粒１３ｂが埋め込まれる。 FIG. 1 schematically shows a necklace as a decorative article according to an embodiment of the present invention. The necklace 11 has a chain 12 wound around the neck and a pendant 13 coupled to the chain 12. The pendant 13 includes, for example, a gold alloy body 13a formed based on metal diffusion and having a color gradation that appears on the surface. A plurality of diamond grains 13b are embedded on the surface of the alloy body 13a.

合金体１３ａは、異なる色を有する複数の金合金を含む。金合金には、例えば、ホワイトゴールド、イエローゴールド、ローズゴールド、レッドゴールド、ピンクゴールド、グリーンゴールド、ブルーゴールド、パープルゴールド、グレイゴールド、その他が含まれることができる。ホワイトゴールドは、例えば、７５重量％の金および２５重量％のパラジウムまたはプラチナで構成される。イエローゴールドは、例えば、７５重量％の金、１２．５重量％の銅および１２．５重量％の銀で構成される。ローズゴールドは、例えば、７５重量％の金、２２．２５重量％の銅および２．７５重量％の銀で構成される。レッドゴールドは、例えば、７５重量％の金および２５重量％の銅で構成される。あるいは、レッドゴールドは、例えば、５０重量％の金および５０重量％の銅で構成されてもよい。ピンクゴールドは、例えば、７５重量％の金、２０重量％の銅および５重量％の銀で構成される。あるいは、ピンクゴールドは、例えば、７５重量％の金、１９重量％の銅、４重量％の銀および２重量％のパラジウムで構成されてもよい。グリーンゴールドは、例えば、７５重量％の金、６重量％の銀、１０重量％の銅および９重量％の亜鉛で構成される。あるいは、グリーンゴールドは、例えば、７５重量％の金、２０重量％の銀および５重量％の銅で構成されてもよい。ブルーゴールドは、例えば、７５重量％の金および２５重量％の鉄で構成される。パープルゴールドは、例えば、８０重量％の金および２０重量％のアルミニウムで構成される。グレイゴールドは、例えば、７５重要％の金、１７重量％の鉄および８重量％の銅で構成される。金合金の色は例えば金と銅と銀との重量比（ここにパラジウムが加わってもよい）に応じて変化する。ただし、成分の重量比はあくまで例示にすぎない。ここでは、合金体は、金属拡散に基づき金合金に結合される金、パラジウムおよびプラチナのいずれか１以上を含んでもよい。 The alloy body 13a includes a plurality of gold alloys having different colors. Gold alloys can include, for example, white gold, yellow gold, rose gold, red gold, pink gold, green gold, blue gold, purple gold, gray gold, and others. White gold is, for example, composed of 75% by weight gold and 25% by weight palladium or platinum. Yellow gold is, for example, composed of 75% by weight gold, 12.5% by weight copper and 12.5% by weight silver. Rose gold is composed, for example, of 75% by weight gold, 22.25% by weight copper and 2.75% by weight silver. Red gold is, for example, composed of 75% by weight gold and 25% by weight copper. Alternatively, the red gold may be composed of, for example, 50% by weight gold and 50% by weight copper. Pink gold is composed of, for example, 75% by weight gold, 20% by weight copper and 5% by weight silver. Alternatively, pink gold may be composed of, for example, 75% by weight gold, 19% by weight copper, 4% by weight silver and 2% by weight palladium. Green gold is composed, for example, of 75% by weight gold, 6% by weight silver, 10% by weight copper and 9% by weight zinc. Alternatively, the green gold may be composed of, for example, 75% by weight gold, 20% by weight silver and 5% by weight copper. Blue gold is composed of, for example, 75 wt% gold and 25 wt% iron. Purple gold is composed of, for example, 80 wt% gold and 20 wt% aluminum. Gray gold is composed, for example, of 75% by weight gold, 17% by weight iron and 8% by weight copper. The color of the gold alloy changes depending on, for example, the weight ratio of gold, copper, and silver (palladium may be added here). However, the weight ratio of the components is merely an example. Here, the alloy body may include any one or more of gold, palladium and platinum that are bonded to the gold alloy based on metal diffusion.

金の合金は同系色であることから、相違する色の金合金同士が金属拡散で結合すると、金合金同士の境界で金属拡散に基づき色が良好に混ざり合う。金合金同士の境界は消失する。金属拡散は境界面から遠ざかるにつれて減少することから、境界面を跨いでグラデーションは形成される。合金体１３ａの表面には、一方の色から他方の色に向かって徐々に変化する美しい色のグラデーションが現れる。金属拡散は固体の金属で実現されることから、金合金同士の境界面は固体の形状に基づき思い通りの位置に配置されることができる。こうして良好に計算された配置で色のグラデーションを有する装飾品は提供されることができる。 Since gold alloys have similar colors, when gold alloys of different colors are bonded by metal diffusion, the colors are mixed well at the boundary between gold alloys due to metal diffusion. The boundaries between the gold alloys disappear. Since the metal diffusion decreases as the distance from the boundary surface increases, a gradation is formed across the boundary surface. On the surface of the alloy body 13a, a beautiful color gradation that gradually changes from one color to the other appears. Since metal diffusion is realized by a solid metal, the boundary surface between gold alloys can be arranged at a desired position based on the shape of the solid. An ornament with a color gradation in a well-calculated arrangement can thus be provided.

次に合金体１３ａの製造方法を説明する。図２（Ａ）に示されるように、異なる色を有する複数の素材１４ａ、１４ｂ、１４ｃ、１４ｄ、１４ｅは用意される。素材１４ａ〜１４ｅは板材に形成される。個々の素材１４ａ〜１４ｅはＫ２２金、Ｋ２０金、Ｋ１８金、Ｋ１４金といった金合金から構成される。これら金合金の板材に加えて、金単体（Ｋ２４金）の板材やパラジウム単独の板材、プラチナ単独の板材が用いられてもよい。ただし、素材は５つに限られるわけではない。少なくとも隣接する素材１４ａ〜１４ｅ同士は同系色を有する。 Next, a method for manufacturing the alloy body 13a will be described. As shown in FIG. 2A, a plurality of materials 14a, 14b, 14c, 14d, 14e having different colors are prepared. The materials 14a to 14e are formed into plate materials. The individual materials 14a to 14e are made of gold alloy such as K22 gold, K20 gold, K18 gold, and K14 gold. In addition to these gold alloy plates, a plate of gold alone (K24 gold), a plate of palladium alone, or a plate of platinum alone may be used. However, the material is not limited to five. At least adjacent materials 14a to 14e have similar colors.

板材は順番に重ねられる。重ねの順番は最終的なグラデーションの色相に基づき決定される。金合金は金と銅と銀との重量比（ここにパラジウムが加わってもよい）に応じて特有の色を有する。最終的なグラデーション内で色の位置は隣接する板材の境界面の位置で調整されることができる。境界面の位置は板材の板厚で調整されることができる。このとき、パラジウム単独の板材やプラチナ単独の板材は、銀色（白色）を有することから、例えばホワイトゴールドまたはグレイゴールドに重ねられることが望まれる。そうすれば、パラジウム単独の板材やプラチナ単独の板材と金合金の板材とは良好に混ざり合う。境界は消失し色のグラデーションは形成される。 Plates are stacked in order. The order of overlapping is determined based on the hue of the final gradation. Gold alloys have a unique color depending on the weight ratio of gold to copper to silver (where palladium may be added). The position of the color in the final gradation can be adjusted at the position of the boundary surface between the adjacent plate materials. The position of the boundary surface can be adjusted by the plate thickness of the plate material. At this time, since a plate material made of only palladium or a plate made of only platinum has a silver color (white), it is desired to be stacked on, for example, white gold or gray gold. Then, the plate material of palladium alone or the plate material of platinum alone and the plate material of gold alloy are mixed well. The border disappears and a color gradation is formed.

図２（Ｂ）に示されるように、重ねられた板材の重ね体１５には圧力が付加される。圧力は、重ね体１５に含まれる板材の材質や板厚、板材の枚数に応じて適宜に設定される。圧力は例えば３９［ｋＮ／ｃｍ２］〜９８１［ｋＮ／ｃｍ２］の間で設定されることができる。圧力の付加に応じて板材同士の境界で素材１４ａ〜１４ｅの密着度は高められることができる。 As shown in FIG. 2B, pressure is applied to the stacked body 15 of the stacked plate materials. The pressure is appropriately set according to the material and thickness of the plate material included in the stack 15 and the number of plate materials. The pressure can be set for example between 39 [kN / cm 2] ~981 [kN / c m 2]. The adhesion of the materials 14a to 14e can be increased at the boundary between the plate materials according to the application of pressure.

そして重ね体１５には熱が加えられる。加熱温度は、同様に、重ね体１５に含まれる板材の材質や板厚、板材の枚数に応じて適宜に設定される。加熱温度は例えば摂氏７００度〜摂氏１８００度の間で設定されることができる。加熱温度は素材の融点よりも低い温度であればよい。加熱に応じて素材１４ａ〜１４ｅ同士の境界で熱拡散が進行する。 Then, heat is applied to the stack 15. Similarly, the heating temperature is appropriately set according to the material and thickness of the plate material included in the stack 15 and the number of plate materials. The heating temperature can be set, for example, between 700 degrees Celsius and 1800 degrees Celsius. The heating temperature may be lower than the melting point of the material. The heat diffusion progresses at the boundaries between the materials 14a to 14e according to the heating.

加熱の持続時間は、同様に、重ね体１５に含まれる板材の材質や板厚、板材の枚数に応じて適宜に設定される。加熱の持続時間は、例えば、６０分〜１８時間の間で設定されることができる。加圧および加熱処理に基づき重ね体１５は一体化する。 Similarly, the duration of heating is appropriately set according to the material and thickness of the plate material and the number of plate materials included in the stack 15. The duration of heating can be set, for example, between 60 minutes and 18 hours. The stack 15 is integrated based on the pressure and heat treatment.

こうして図３に示されるようにビレット１６が形成される。ビレット１６では板材同士の境界面で金属拡散が発生する。境界面を跨いでグラデーションは形成される。図３から明らかなように、ビレット１６の切断面１６ａでは板材同士の境界は消失する。ビレット１６の表面（切断面１６ａを含む）には色のグラデーションが現れる。 Thus, the billet 16 is formed as shown in FIG. In the billet 16, metal diffusion occurs at the boundary surface between the plate materials. A gradation is formed across the boundary surface. As is clear from FIG. 3, the boundary between the plate materials disappears at the cut surface 16a of the billet 16. Color gradation appears on the surface of the billet 16 (including the cut surface 16a).

ビレット１６はプレス加工や鍛造加工に基づき特定の形状に整えられる。その後、整形されたビレット１６の表面は仕上げられる。こうして金の合金体１３ａは形成される。こうして得られた合金体１３ａに基づきペンダント１３は制作される。 The billet 16 is trimmed into a specific shape by pressing or forging. After that, the surface of the shaped billet 16 is finished. Thus, the gold alloy body 13a is formed. The pendant 13 is manufactured based on the alloy body 13a thus obtained.

図４は他の実施形態に係る装飾品としてのリングを概略的に示す。リング２１は、指の太さに合わせて成形された環状の合金体２１ａを有する。合金体２１ａは、例えば、金属拡散に基づき形成され表面に現れる色のグラデーションを有する。合金体２１ａは前述の合金体１３ａと同様に構成される。 FIG. 4 schematically shows a ring as a decorative article according to another embodiment. The ring 21 has an annular alloy body 21a formed to match the thickness of the finger. The alloy body 21a has, for example, a color gradation that is formed based on metal diffusion and appears on the surface. The alloy body 21a has the same structure as the alloy body 13a described above.

図５はさらに他の実施形態に係る装飾品としてのイヤリングを概略的に示す。イヤリング２２は、ばね力に応じて耳に固定される金具２３と、金具２３のカン２３ａに連結されるロッド形状の合金体２４とを有する。合金体２４は、例えば、金属拡散に基づき形成され表面に現れる色のグラデーションを有する。合金体２４は前述の合金体１３ａと同様に構成される。 FIG. 5 schematically shows an earring as a decorative article according to still another embodiment. The earring 22 has a metal fitting 23 fixed to the ear according to a spring force, and a rod-shaped alloy body 24 connected to the can 23 a of the metal fitting 23. The alloy body 24 has, for example, a gradation of colors that is formed based on metal diffusion and appears on the surface. The alloy body 24 is configured similarly to the alloy body 13a described above.

図６はさらに他の実施形態に係る装飾品としてのブレスレットを概略的に示す。ブレスレット２５は、手首の太さに合わせて成形された環状の合金体２５ａを有する。合金体２５ａは、例えば、金属拡散に基づき形成され表面に現れる色のグラデーションを有する。合金体２５ａは前述の合金体１３ａと同様に構成される。 FIG. 6 schematically shows a bracelet as a decorative article according to still another embodiment. The bracelet 25 has an annular alloy body 25a that is shaped to match the thickness of the wrist. The alloy body 25a has, for example, a gradation of color that is formed based on metal diffusion and appears on the surface. The alloy body 25a has the same structure as the alloy body 13a described above.

その他、合金体１３ａと同様な合金体は、タイピンやヘアピンといった装飾品に用いられることもでき、装飾品の１つである腕時計のベゼルやバンド、ケースに用いられることもできる。合金体１３ａと同様な合金体は、バッグや財布、ベルトなどに取り付けられるアクセントや金具といった装飾品に用いられてもよい。 In addition, an alloy body similar to the alloy body 13a can be used for a decorative item such as a tie pin or a hairpin, and can also be used for a bezel, a band or a case of a wrist watch which is one of the decorative items. An alloy body similar to the alloy body 13a may be used for an ornament such as an accent or a metal fitting attached to a bag, a wallet, a belt, or the like.

１１…装飾品（ネックレス）、１３ａ…合金体、１４ａ…素材、１４ｂ…素材、１４ｃ…素材、１４ｄ…素材、１４ｅ…素材、１６…塊（ビレット）、２１…装飾品（リング）、２１ａ…合金体、２２…装飾品（イヤリング）、２４…合金体、２５…装飾品（ブレスレット）、２５ａ…合金体。 11... Ornament (necklace), 13a... Alloy body, 14a... Material, 14b... Material, 14c... Material, 14d... Material, 14e... Material, 16... Lump (billet), 21... Ornament (ring), 21a... Alloy body, 22... Ornaments (earrings), 24... Alloy bodies, 25... Ornaments (bracelets), 25a... Alloy bodies.

Claims (3)

加圧下で実現される金属拡散に基づき境界線の消失を伴って形成され表面に現れる色のグラデーションを有する金の合金体を含むことを特徴とする装飾品。 A decorative article, characterized in that it comprises a gold alloy body having a color gradation that is formed on the surface with the disappearance of a boundary line based on metal diffusion realized under pressure . 請求項１に記載の装飾品において、前記合金体は、異なる色を有する複数の金合金を含むことを特徴とする装飾品。 The ornamental article according to claim 1, wherein the alloy body includes a plurality of gold alloys having different colors. 異なる色を有する複数の金合金の素材を重ねる工程と、
圧力を加えながら前記素材を加熱し、前記素材同士の境界面で金属拡散に基づき前記金合金を混合し、前記境界面の消失を伴う前記素材のグラデーションを形成する工程と、
前記素材の塊を加工し、金属拡散に基づき境界線の消失を伴って形成され表面に現れる色のグラデーションを有する金の合金体を調整する工程と
を備えることを特徴とする装飾品向け合金体の製造方法。
A process of stacking a plurality of gold alloy materials having different colors,
Heating the material while applying pressure, mixing the gold alloy based on metal diffusion at the interface between the materials, and forming a gradation of the material with disappearance of the interface,
A step of processing the lump of the raw material, and adjusting a gold alloy body having a color gradation which is formed with disappearance of a boundary line based on metal diffusion and appears on the surface. Manufacturing method.
JP2019149365A 2019-08-16 2019-08-16 Ornaments Active JP6716071B1 (en)