JP6687693B2 - 表面保護フィルム - Google Patents
表面保護フィルム Download PDFInfo
- Publication number
- JP6687693B2 JP6687693B2 JP2018170352A JP2018170352A JP6687693B2 JP 6687693 B2 JP6687693 B2 JP 6687693B2 JP 2018170352 A JP2018170352 A JP 2018170352A JP 2018170352 A JP2018170352 A JP 2018170352A JP 6687693 B2 JP6687693 B2 JP 6687693B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- acrylate
- weight
- group
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、偏光板、位相差板などの光学部材は、表面保護フィルムを貼り合わされた状態で、液晶表示板の表示能力、色相、コントラスト、異物混入などの光学的評価を伴う製品検査を行うため、表面保護フィルムに対する要求性能としては、粘着剤層に気泡や異物が付着していないことが求められている。
また、近年では、偏光板、位相差板などの光学部材から表面保護フィルムを剥がすときに、粘着剤層を被着体が剥がす時に発生する静電気に伴って生じる剥離帯電が、液晶ディスプレイの電気制御回路の故障に影響することが懸念され、粘着剤層に対して優れた帯電防止性能が求められている。
また、偏光板、位相差板などの光学部材に表面保護フィルムを貼り合わせるときに、各種の理由により、一旦、表面保護フィルムを剥がして、再度、表面保護フィルムを貼り直すことがあり、そのときに被着体の光学部材から剥がし易いこと(リワーク性)が求められている。
また、最終的に偏光板、位相差板などの光学部材から表面保護フィルムを剥がすときには、速やかに剥離できることが求められている。いわゆる、高速剥離によっても、速やかに剥離できるように、粘着力が剥離速度によっても変化が少ないことが求められている。
しかし、表面保護フィルムを構成する粘着剤層に対する要求性能である、これら(1)〜(4)のそれぞれ、個々の要求性能を満たすことは出来ても、表面保護フィルムの粘着剤層に求められる(1)〜(4)の全ての要求性能を、同時に満たすことは非常に困難な課題であった。
また、上記と同様の共重合体に、(メタ)アクリル酸アルキルエステルと、カルボキシル基含有共重合性化合物との共重合体を少量配合し、これを架橋剤で架橋処理した粘着剤層を設けたものなどが提案されている。しかし、これらは、表面張力が低くて表面が平滑なプラスチック板などの表面保護に使用すると、加工時や保存時の加熱により浮きなどの剥離現象を生じる問題や、手作業領域である高速での剥離時の再剥離性に劣るという問題もあった。
特許文献2に記載の粘着剤組成物では、加工時や保存時において、浮きなどの剥離現象を生じることがなく、その上、接着力の経時上昇性が小さくて再剥離性に優れており、長期保存、特に高温雰囲気下で長期保存しても小さな力で再剥離でき、その際被着体上に糊残りを生じず、また高速剥離を行ったときでも小さな力で再剥離できるとしている。
また、近年では、このような帯電防止剤を基材フィルムに含有させたり、あるいは基材フィルムの表面に塗布するのではなく、直接に粘着剤層に含有させたりすることが提案されている。
特許文献4では、アルキル基の炭素数が2〜12程度のアクリル酸アルキルエステルやアルキル基の炭素数が4〜12程度のメタクリル酸アルキルエステル等を主モノマー成分とし、例えば、カルボキシル基含有モノマーなどの他の官能基含有モノマー成分を含むことができるとしている。一般的には上記主モノマーを50重量%以上含有させることが好ましい、又、官能基含有モノマー成分の含有量は0.001〜50重量%、好ましくは0.001〜25重量%、更に好ましくは0.01〜25重量%であることが望まれる、としている。このような特許文献4に記載の粘着剤組成物は、高温下又は高温高湿下でも凝集力及び接着力の経時変化が小さく、かつ、曲面に対する接着力にも優れた効果を示すことから、リワーク性を有するとしている。
一般に、粘着剤層を柔らかい性状のものにすると、糊残りが発生し易くなり、リワーク性が低下しやすい。すなわち、誤って貼合したときに再剥離することが難しく、貼り直しが困難となり易い。このことから、カルボキシル基などの官能基を有するモノマーを主剤に架橋させて、粘着剤層を一定の硬さにすることが、リワーク性を持たせるためには必要と考えられる。
(A)アルキル基の炭素数がC4〜C18の(メタ)アクリル酸エステルモノマーを50〜91重量部、
(B)水酸基を含有する共重合可能なモノマーを0.1〜10重量部、
(C)カルボキシル基を含有する共重合可能なモノマーを0〜1.0重量部、
(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーまたはアルコキシポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーを0〜49.9重量部、
(E)水酸基及びイソシアネート基を含有しない窒素含有ビニルモノマーまたは水酸基を含有しないアルコキシ基含有アルキル(メタ)アクリレートモノマーを0〜20重量部の割合で含有していることが好ましい。
また、(F)3官能以上のイソシアネート化合物に、(G)2官能非環式脂肪族イソシアネート化合物を併用することで、架橋性に優れ、耐汚染性が良好となり、さらには低速の剥離速度、及び高速の剥離速度において、粘着力のバランスが優れている。
本発明の粘着剤組成物は、その主剤が、(A)アルキル基の炭素数がC4〜C18の(メタ)アクリル酸エステルモノマーの少なくとも一種と、共重合可能なモノマー群として(B)水酸基を含有する共重合可能なモノマーと、(C)カルボキシル基を含有する共重合可能なモノマーと、(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーと、(E)水酸基を含有しない窒素含有ビニルモノマーまたはアルコキシ基含有アルキル(メタ)アクリレートモノマーと、からなる共重合可能なモノマー群の中から選択された少なくとも一種と、を含む共重合体のアクリル系ポリマーからなり、さらに、(F)3官能以上のイソシアネート化合物と、(G)2官能非環式脂肪族イソシアネート化合物と、(H)帯電防止剤と、を含有することを特徴とする。
また、前記共重合体のアクリル系ポリマーの合計を100重量部とする時、前記(A)アルキル基の炭素数がC4〜C18の(メタ)アクリル酸エステルモノマーを50〜91重量部、前記(B)水酸基を含有する共重合可能なモノマーを0.1〜10重量部、前記(C)カルボキシル基を含有する共重合可能なモノマーを0〜1.0重量部、前記(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーを0〜50重量部、前記(E)水酸基を含有しない窒素含有ビニルモノマーまたはアルコキシ基含有アルキル(メタ)アクリレートモノマーを0〜20重量部の割合で含有していることが好ましい。
共重合体のアクリル系ポリマーの合計を100重量部とする時、(A)アルキル基の炭素数がC4〜C18の(メタ)アクリル酸エステルモノマーを50〜91重量部の割合で含有していることが好ましい。
8−ヒドロキシオクチル(メタ)アクリレート、6−ヒドロキシヘキシル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、2−ヒドロキシエチル(メタ)アクリレート、N−ヒドロキシ(メタ)アクリルアミド、N−ヒドロキシメチル(メタ)アクリルアミド、N−ヒドロキシエチル(メタ)アクリルアミドからなる化合物群の中から選択された、少なくとも一種以上であることが好ましい。
共重合体のアクリル系ポリマーの合計を100重量部とする時、前記(B)水酸基を含有する共重合可能なモノマーを0.1〜10重量部の割合で含有していることが好ましい。
共重合体のアクリル系ポリマーの合計を100重量部とする時、前記(C)カルボキシル基を含有する共重合可能なモノマーを0〜1.0重量部の割合で含有していることが好ましい。本発明に係わる粘着剤層において、粘着剤組成物に(C)カルボキシル基を含有する共重合可能なモノマーを含有させなくてもよい。
ポリアルキレングリコールの有するアルキレン基としては、エチレン基、プロピレン基、ブチレン基などが挙げられるが、これらに限定されない。ポリアルキレングリコールが、ポリエチレングリコール、ポリプロピレングリコール、ポリブチレングリコール等の2種以上のポリアルキレングリコールの共重合体であってもよい。ポリアルキレングリコールの共重合体としては、ポリエチレングリコール−ポリプロピレングリコール、ポリエチレングリコール−ポリブチレングリコール、ポリプロピレングリコール−ポリブチレングリコール、ポリエチレングリコール−ポリプロピレングリコール−ポリブチレングリコール等が挙げられ、該共重合体は、ブロック共重合体、ランダム共重合体であってもよい。
(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーが、ポリアルキレングリコール鎖を構成するアルキレンオキサイドの平均繰り返し数が3〜14であることが好ましい。「アルキレンオキサイドの平均繰り返し数」とは、(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーの分子構造に含まれる「ポリアルキレングリコール鎖」の部分において、アルキレンオキサイド単位が繰り返す平均の数である。
より具体的には、ポリエチレングリコール−モノ(メタ)アクリレート、ポリプロピレングリコール−モノ(メタ)アクリレート、ポリブチレングリコール−モノ(メタ)アクリレート、ポリエチレングリコール−ポリプロピレングリコール−モノ(メタ)アクリレート、ポリエチレングリコール−ポリブチレングリコール−モノ(メタ)アクリレート、ポリプロピレングリコール−ポリブチレングリコール−モノ(メタ)アクリレート、ポリエチレングリコール−ポリプロピレングリコール−ポリブチレングリコール−モノ(メタ)アクリレート;メトキシポリエチレングリコール−(メタ)アクリレート、メトキシポリプロピレングリコール−(メタ)アクリレート、メトキシポリブチレングリコール−(メタ)アクリレート、メトキシ−ポリエチレングリコール−ポリプロピレングリコール−(メタ)アクリレート、メトキシ−ポリエチレングリコール−ポリブチレングリコール−(メタ)アクリレート、メトキシ−ポリプロピレングリコール−ポリブチレングリコール−(メタ)アクリレート、メトキシ−ポリエチレングリコール−ポリプロピレングリコール−ポリブチレングリコール−(メタ)アクリレート;エトキシポリエチレングリコール−(メタ)アクリレート、エトキシポリプロピレングリコール−(メタ)アクリレート、エトキシポリブチレングリコール−(メタ)アクリレート、エトキシ−ポリエチレングリコール−ポリプロピレングリコール−(メタ)アクリレート、エトキシ−ポリエチレングリコール−ポリブチレングリコール−(メタ)アクリレート、エトキシ−ポリプロピレングリコール−ポリブチレングリコール−(メタ)アクリレート、エトキシ−ポリエチレングリコール−ポリプロピレングリコール−ポリブチレングリコール−(メタ)アクリレートなどが挙げられる。
共重合体のアクリル系ポリマーの合計を100重量部とする時、前記(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーを0〜50重量部の割合で含有していることが好ましい。本発明に係わる粘着剤層において、粘着剤組成物に(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーを含有させなくてもよい。
これらのアルコキシ基含有アルキル(メタ)アクリレートモノマーは、アルキル(メタ)アクリレートにおけるアルキル基の原子がアルコキシ基で置換された構造を有する。
3官能以上のイソシアネート化合物としては、ジイソシアネート類(1分子中に2個のNCO基を有する化合物)のビュレット変性体やイソシアヌレート変性体、トリメチロールプロパン(TMP)やグリセリン等の3価以上のポリオール(1分子中に少なくとも3個以上のOH基を有する化合物)とのアダクト体(ポリオール変性体)などが挙げられる。前記(F)3官能以上のイソシアネート化合物が、前記共重合体の100重量部に対して、0.5〜5.0重量部含まれることが好ましい。
また、(F)3官能以上のイソシアネート化合物は、前記(F−1)第1の脂肪族系のイソシアネート化合物群の中から選択された、少なくとも一種以上と、前記(F−2)第2の芳香族系のイソシアネート化合物群の中から選択された、少なくとも一種以上とを含み、前記共重合体の100重量部に対して、合計して0.5〜5.0重量部含まれることが好ましい。また、(F−1)第1の脂肪族系のイソシアネート化合物群の中から選択された、少なくとも一種以上と、(F−2)第2の芳香族系のイソシアネート化合物群の中から選択された、少なくとも一種以上との混合比率は、(F−1):(F−2)が重量比で10%:90%〜90%:10%の範囲内であることが好ましい。
例えば、一般式「O=C=N−X−N=C=O」(ただし、Xは2価基)でジイソシアネート化合物を、一般式「HO−Y−OH」(ただし、Yは2価基)でジオール化合物を表すとき、ジイソシアネート化合物とジオール化合物とを反応させて生成された化合物としては、例えば、次の一般式Zで表される化合物が挙げられる。
O=C=N−X−(NH−CO−O−Y−O−CO−NH−X)n−N=C=O
前記アクリル系ポリマー100重量部に対して、前記(F)3官能以上のイソシアネート化合物と、(G)2官能非環式脂肪族イソシアネート化合物との合計が、0.1〜5.0重量部であることが好ましい。
本発明では、(H)帯電防止剤として、(H−1)融点が30〜50℃であるイオン性化合物を共重合体に添加し、又は(H−2)アクリロイル基含有イオン性化合物を共重合体中に共重合する。これらの(H)帯電防止剤は、融点が低いため、また、長鎖のアルキル基を有するため、アクリル共重合体との親和性は高いと推測される。
(H−1)融点が30〜50℃であるイオン性化合物は、共重合体の100重量部に対して0.01〜5.0重量部含まれることが好ましい。
(H−2)アクリロイル基含有イオン性化合物は、共重合体中に0.1〜5.0重量%共重合されることが好ましい。
ポリエーテル変性シロキサン化合物は、HLB値が7〜12であるポリエーテル変性シロキサン化合物であることが好ましい。また、共重合体の100重量部に対して、ポリエーテル変性シロキサン化合物が0.01〜0.5重量部含まれることが好ましい。より好ましくは、0.1〜0.5重量部である。
HLBとは、例えばJIS K3211(界面活性剤用語)等に規定する親水親油バランス(親水性親油性比)である。
ポリエーテル変性シロキサン化合物は、例えば、水素化ケイ素基を有するポリオルガノシロキサン主鎖に対し、不飽和結合及びポリオキシアルキレン基を有する有機化合物をヒドロシリル化反応によりグラフトさせることによって得ることができる。具体的には、ジメチルシロキサン・メチル(ポリオキシエチレン)シロキサン共重合体、ジメチルシロキサン・メチル(ポリオキシエチレン)シロキサン・メチル(ポリオキシプロピレン)シロキサン共重合体、ジメチルシロキサン・メチル(ポリオキシプロピレン)シロキサン重合体等が挙げられる。
ポリエーテル変性シロキサン化合物を粘着剤組成物に配合することにより、粘着剤の粘着力及びリワーク性能を改善することができる。粘着剤組成物がポリエーテル変性シロキサン化合物を含有しない場合、より低コストとなる。
(H)帯電防止剤として、(H−2)アクリロイル基含有イオン性化合物を用いる場合、本発明の粘着剤組成物に用いられる主剤の共重合体は、(A)アルキル基の炭素数がC4〜C18の(メタ)アクリル酸エステルモノマーの少なくとも一種と、共重合可能なモノマー群として(B)水酸基を含有する共重合可能なモノマーと、(C)カルボキシル基を含有する共重合可能なモノマーと、(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーと、(E)水酸基を含有しない窒素含有ビニルモノマーまたはアルコキシ基含有アルキル(メタ)アクリレートモノマーからなる共重合可能なモノマー群中から選択された少なくとも一種と、(H−2)アクリロイル基含有イオン性化合物と、を共重合させることで合成することができる。
本発明の粘着剤組成物は、上記の共重合体に、(F)3官能以上のイソシアネート化合物、(G)2官能非環式脂肪族イソシアネート化合物、(H)帯電防止剤、さらに適宜任意の添加剤を配合することで調製することができる。なお、(H−2)アクリロイル基含有イオン性化合物を主剤の共重合体中に重合させた場合、該共重合体に対して(H)帯電防止剤をさらに添加しても良いし、添加しなくても構わない。
また、アクリル系ポリマーの酸価は、0.01〜8.0であることが好ましい。これにより、汚染性を改善し、糊残りの発生防止性能を向上することができる。
ここで、「酸価」とは、酸の含有量を表す指標の一つであり、カルボキシル基を含有するポリマー1gを中和するのに要する、水酸化カリウムのmg数で表される。
基材フィルムには、樹脂フィルムの粘着剤層が形成された側とは反対面に、シリコーン系、フッ素系の離型剤やコート剤、シリカ微粒子等による防汚処理、帯電防止剤の塗布や練り込み等による帯電防止処理を施すことができる。
剥離フィルムには、粘着剤層の粘着面と合わされる側の面に、シリコーン系、フッ素系の離型剤などにより離型処理が施される。
[実施例1]
撹拌機、温度計、還流冷却器及び窒素導入管を備えた反応装置に、窒素ガスを導入して、反応装置内の空気を窒素ガスで置換した。その後、反応装置に2−エチルヘキシルアクリレート100重量部、8−ヒドロキシオクチルアクリレート3.0重量部、ポリプロピレングリコールモノアクリレート(ポリアルキレングリコール鎖を構成するアルキレンオキサイドの平均繰り返し数n=12)10重量部とともに溶剤(酢酸エチル)を60重量部加えた。その後、重合開始剤としてアゾビスイソブチロニトリル0.1重量部を2時間かけて滴下させ、65℃で6時間反応させ、重量平均分子量50万の、実施例1に用いるアクリル共重合体溶液1を得た。アクリル共重合体の一部を採取し、後述する酸価の測定試料として用いた。
[実施例2〜9及び比較例1〜4]
単量体の組成を各々、表1の(A)〜(E)及び(H−2)の記載のようにする以外は、上記の実施例1に用いるアクリル共重合体溶液1と同様にして、実施例2〜9及び比較例1〜4に用いるアクリル共重合体溶液を得た。
[実施例1]
上記のとおり製造した、実施例1のアクリル共重合体溶液1に対して、1−オクチルピリジニウム 六フッ化リン酸塩1.5重量部を加え撹拌したのち、コロネートHX(ヘキサメチレンジイソシアネート化合物のイソシアヌレート体)を2.0重量部、合成例1の2官能非環式脂肪族イソシアネート化合物G−1を0.5重量部を加えて撹拌混合して実施例1の粘着剤組成物を得た。この粘着剤組成物をシリコーン樹脂コートされたポリエチレンテレフタレート(PET)フィルムからなる剥離フィルムの上に塗布後、90℃で乾燥することによって溶剤を除去し、粘着剤層の厚さが25μmである粘着シートを得た。
その後、一方の面に帯電防止及び防汚処理されたポリエチレンテレフタレート(PET)フィルムの帯電防止及び防汚処理された面とは反対の面に粘着シートを転写させ、「帯電防止及び防汚処理されたPETフィルム/粘着剤層/剥離フィルム(シリコーン樹脂コートされたPETフィルム)」の積層構成を有する実施例1の表面保護フィルムを得た。
[実施例2〜9及び比較例1〜4]
添加剤の組成を各々、表2の(F)〜(H)の記載のようにする以外は、上記の実施例1の表面保護フィルムと同様にして、実施例2〜9及び比較例1〜4の表面保護フィルムを得た。
表1で、(H)帯電防止剤のうち、共重合体中に共重合された、(H−2)アクリロイル基含有の4級アンモニウム塩型イオン性化合物は、重合後に添加される(H)帯電防止剤とは別の欄に記載した。
合成例1〜3の、2官能非環式脂肪族イソシアネート化合物は、下記の方法で合成した。表5及び表6に示すように、ジイソシアネートとジオール化合物を、モル比:NCO/OH=16の比率で混合し、120℃で3時間反応させ、その後、薄膜蒸発装置を使用して減圧下で未反応のジイソシアネートを除去し、目的の2官能非環式脂肪族イソシアネート化合物を得た。
実施例1〜9及び比較例1〜4における表面保護フィルムを、23℃、50%RHの雰囲気下で7日間エージングした後、剥離フィルム(シリコーン樹脂コートされたPETフィルム)を剥がして、粘着剤層を表出させたものを、表面抵抗率の測定試料とした。
さらに、この粘着剤層を表出させた表面保護フィルムを、粘着剤層を介して液晶セルに貼られた偏光板の表面に貼り合わせ、1日放置した後、50℃、5気圧、20分間オートクレーブ処理し、室温でさらに12時間放置したものを、粘着力、剥離帯電圧、リワーク性及び耐久性の測定試料とした。
上記で得られた測定試料(25mm幅の表面保護フィルムを偏光板の表面に貼り合わせたもの)を、180°方向に引張試験機を用いて低速の剥離速度(0.3m/min)及び高速の剥離速度(30m/min)において剥がして、測定した剥離強度を粘着力とした。
エージングした後、偏光板に貼り合わせる前に、剥離フィルム(シリコーン樹脂コートされたPETフィルム)を剥がして粘着剤層を表出し、抵抗率計ハイレスタUP−HT450(三菱化学アナリテック製)を用いて粘着剤層の表面抵抗率を測定した。
上記で得られた測定試料を、30m/minの引張速度で180°剥離した際に偏光板が帯電して発生する電圧(帯電圧)を、高精度静電気センサSK−035、SK−200(株式会社キーエンス製)を用いて測定し、測定値の最大値を剥離帯電圧とした。
上記で得られた測定試料の、表面保護フィルムの上をボールペンで(荷重500g、3往復)なぞった後、偏光板から表面保護フィルムを剥離して偏光板の表面を観察し、偏光板に汚染移行の無いことを確認した。評価目標基準は、偏光板に汚染移行の無い場合を「○」、ボールペンでなぞった軌跡に沿って少なくとも一部に汚染移行が確認された場合を「△」、ボールペンでなぞった軌跡に沿って汚染移行が確認され、粘着剤表面からも粘着剤の離脱が確認された場合を「×」と評価した。
上記で得られた測定試料を、60℃、90%RHの雰囲気下に250時間放置後、室温に取り出し、さらに12時間放置した後、粘着力を測定して初期の粘着力と比較して明らかな増加が無いことを確認した。評価目標基準は、試験後の粘着力が初期粘着力の1.5倍以下である場合を「○」、1.5倍を超えた場合を「×」と評価した。
すなわち、(1)低速の剥離速度、及び高速の剥離速度において、粘着力のバランスを取ること、(2)糊残りの発生を防止すること、(3)優れた帯電防止性能、及び(4)リワーク性能の全ての要求性能を、同時に満たしている。
比較例2の表面保護フィルムは、(G)2官能非環式脂肪族イソシアネート化合物を含まない代わりに、2官能環式イソシアネート化合物であるウレトジオン環含有ジイソシアネート化合物を含むためか、高速の剥離速度30m/minでの粘着力が大きすぎ、耐久性が劣っていた。
比較例3の表面保護フィルムは、(F)3官能以上のイソシアネート化合物が過多で、
(G)2官能非環式脂肪族イソシアネート化合物を含まないためか、ポットライフが短くなりすぎ、塗布前に架橋が進行したため、塗工をすることができなかった。
比較例4の表面保護フィルムは、(F)3官能以上のイソシアネート化合物に比べて、(G)2官能非環式脂肪族イソシアネート化合物の方が多いためか、高速の剥離速度30m/minでの粘着力が大きすぎ、耐久性が劣っていた。
このように、比較例1〜4の表面保護フィルムでは、(1)低速の剥離速度、及び高速の剥離速度において、粘着力のバランスを取ること、(2)糊残りの発生を防止すること、(3)優れた帯電防止性能、及び(4)リワーク性能の全ての要求性能を、同時に満たすことができなかった。
Claims (3)
- アクリル系ポリマーと、(H)帯電防止剤と、架橋剤とを含有する粘着剤組成物を架橋させた粘着剤層を、樹脂フィルムの片面に形成してなる表面保護フィルムであって、
前記アクリル系ポリマーが、前記アクリル系ポリマーの合計を100重量部とする時、
(A)アルキル基の炭素数がC4〜C18の(メタ)アクリル酸エステルモノマーの少なくとも1種の合計を50〜91重量部と、
(B)水酸基を含有する共重合可能なモノマーの少なくとも1種の合計を0.1〜10重量部と、
(C)カルボキシル基を含有する共重合可能なモノマーの合計を0〜1.0重量部(但し、前記(C)カルボキシル基を含有する共重合可能なモノマーを含有しない場合も含む)と、
共重合可能なモノマー群として(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーまたはアルコキシポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーの少なくとも1種の合計を0重量部超過49.9重量部以下、及び/又は、(E)水酸基及びイソシアネート基を含有しない窒素含有ビニルモノマーまたは水酸基を含有しないアルコキシ基含有アルキル(メタ)アクリレートモノマーの少なくとも1種の合計を0重量部超過20重量部以下と、を共重合させた共重合体のアクリル系ポリマーであり、
前記(B)水酸基を含有する共重合可能なモノマーが、8−ヒドロキシオクチル(メタ)アクリレート、6−ヒドロキシヘキシル(メタ)アクリレート、4−ヒドロキシブチル(メタ)アクリレート、2−ヒドロキシエチル(メタ)アクリレート、N−ヒドロキシ(メタ)アクリルアミド、N−ヒドロキシメチル(メタ)アクリルアミド、N−ヒドロキシエチル(メタ)アクリルアミドからなる化合物群の中から選択された、少なくとも1種以上であり、
前記(H)帯電防止剤が、前記共重合体の100重量部に対して0.01〜5.0重量部含まれる、融点が30℃以上50℃以下の温度30℃で固体であるイオン性化合物、又は、前記共重合体中に0.1〜5.0重量%の割合で共重合されたアクリロイル基含有イオン性化合物であり、
前記架橋剤が、(F)3官能以上のイソシアネート化合物と、(G)2官能非環式脂肪族イソシアネート化合物とからなり、
前記粘着剤組成物が、前記アクリル系ポリマー100重量部に対して、前記(F)3官能以上のイソシアネート化合物と、前記(G)2官能非環式脂肪族イソシアネート化合物との合計を0.1〜5.0重量部の割合で含有してなり、
前記(F)3官能以上のイソシアネート化合物と、前記(G)2官能非環式脂肪族イソシアネート化合物との重量比(F/G)が1〜90であり、
前記(G)2官能非環式脂肪族イソシアネート化合物が、脂肪族ジイソシアネート化合物とジオール化合物とを反応させて生成された2官能非環式脂肪族イソシアネート化合物であることを特徴とする表面保護フィルム。 - 前記共重合体が、前記(C)カルボキシル基を含有する共重合可能なモノマーを含有しないで、又は、(メタ)アクリル酸、カルボキシエチル(メタ)アクリレート、カルボキシペンチル(メタ)アクリレート、2−(メタ)アクリロイロキシエチルヘキサヒドロフタル酸、2−(メタ)アクリロイロキシプロピルヘキサヒドロフタル酸、2−(メタ)アクリロイロキシエチルフタル酸、2−(メタ)アクリロイロキシエチルコハク酸、2−(メタ)アクリロイロキシエチルマレイン酸、カルボキシポリカプロラクトンモノ(メタ)アクリレート、2−(メタ)アクリロイロキシエチルテトラヒドロフタル酸からなる化合物群の中から選択された、少なくとも1種以上を0重量部超過1.0重量部以下の割合で共重合させてなり、
前記(D)ポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーまたはアルコキシポリアルキレングリコールモノ(メタ)アクリル酸エステルモノマーが、ポリアルキレングリコールモノ(メタ)アクリレート、メトキシポリアルキレングリコール(メタ)アクリレート、エトキシポリアルキレングリコール(メタ)アクリレートの中から選択された、少なくとも1種以上であり、
前記水酸基及びイソシアネート基を含有しない窒素含有ビニルモノマーが、ジアルキル置換(メタ)アクリルアミド、ジアルキルアミノアルキル(メタ)アクリレート、N,N−ジアルキル置換アミノプロピル(メタ)アクリルアミド、N−ビニル置換ラクタム類、N−(メタ)アクリロイル置換環状アミン類からなる化合物群から選択された化合物であることを特徴とする請求項1に記載の表面保護フィルム。 - 偏光板の表面保護フィルムの用途として使用する、請求項1又は2に記載の表面保護フィルム。