JP6678435B2 - 表面含浸材及び構造物 - Google Patents
表面含浸材及び構造物 Download PDFInfo
- Publication number
- JP6678435B2 JP6678435B2 JP2015229935A JP2015229935A JP6678435B2 JP 6678435 B2 JP6678435 B2 JP 6678435B2 JP 2015229935 A JP2015229935 A JP 2015229935A JP 2015229935 A JP2015229935 A JP 2015229935A JP 6678435 B2 JP6678435 B2 JP 6678435B2
- Authority
- JP
- Japan
- Prior art keywords
- styrene
- mass
- acid amide
- fatty acid
- diene copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
R1 nSi(OR2)4−n (1)
(式中、R1は炭素数5〜12のアルキル基又はフェニル基を示し、nは1又は2を示す。nが2のとき、R1は互いに同一であっても異なっていてもよい。R2は炭素数1〜4のアルキル基を示し、複数存在するR2は互いに同一であっても異なっていてもよい。)
本発明の表面含浸材の一実施形態について以下に説明する。本実施形態の表面含浸材は、コンクリート及びモルタル等の細孔を有する構造物の表面に塗布するために用いられる表面含浸材であり、アルコキシシランと、高級脂肪酸アミドと、スチレン−ジエン共重合体と、を含有する。
Ts’×Tc×0.886=トルエン溶液の25℃における粘度(mPa・s)
(式中、Ts’はトルエン溶液の流下時間(秒)を示し、Tcは粘度管係数を示す。なお、0.886はトルエンの25℃における比重(g/cm3)である。)
本実施形態の構造物は、上述の表面含浸材を、各種構造物に用いられるコンクリート及びモルタル等の表面に塗布することによって得られる。本実施形態の構造物は、上記表面含浸材と反応して形成される撥水層を有することから、水分、塩分及び二酸化炭素等の浸透を抑制又は防止し、長期にわたり耐久性に優れた構造を維持することができる。
[使用材料]
表1に示すアルコキシシラン1〜19を準備した。表1には、アルコキシシランの疎水基(R1)、該疎水基(R1)の炭素数、及び、分子量を併せて示す。
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「5.1.1モルタル基板の作製」に準拠して作製した。
(1)含浸深さ
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「6.2含浸深さ試験」に準拠して行った。
(2)透水抑制比
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「6.3透水量試験」に準拠して透水比(%)を算出し、100%から透水比(%)を差し引いた値を「透水抑制比」とした。
[使用材料]
下記(1)〜(4)に示す原材料を準備した。
A:スチレン−ブタジエンブロック共重合体(スチレンとブタジエンとの質量比:30/70、25質量%トルエン溶液の25℃における粘度:20200mPa・s、形状:粉末状)
B:スチレン−ブタジエンブロック共重合体(スチレンとブタジエンとの質量比:30/70、25質量%トルエン溶液の25℃における粘度:3100mPa・s、形状:粉末状)
C:スチレン−ブタジエンブロック共重合体(スチレンとブタジエンとの質量比:30/70、25質量%トルエン溶液の25℃における粘度:1700mPa・s、形状:粉末状)
(2)スチレン−ジエン共重合体以外の重合体
D:無水マレイン酸変性1−プロペン−1−ブテン共重合体(形状:粉末状)
E:アルキルアセタール化ポリビニルアルコール(10質量%エタノール−トルエン(1:1)溶液の25℃における粘度:115mPa・s、形状:粉末状)
(3)高級脂肪酸アミド
ペースト(高級脂肪酸アミド:炭素数22、高級脂肪酸アミドとベンジルアルコールを主成分とする溶剤との質量比:30/70)
(4)溶剤
ベンジルアルコール(純度99%以上)
表面含浸材1〜23の粘度、TI値(チキソトロピー係数)及びタレ性を評価した。結果を表4に示す。また、各評価は以下に示す方法で行った。
温度20℃の条件下にて、BH型粘度計(東機産業株式会社製 B型粘度計BH、ローターNo.3)を用いて回転数0.5rpm、20rpm及び100rpmにおける粘度を測定した。なお、rpmは1分間あたりの回転数を表す。
上述の回転数0.5rpmにおける粘度を回転数100rpmにおける粘度で除して求めた。
水平に静置したケイ酸カルシウム板に、アプリケーターを用いて表面含浸材を水平方向に厚さ225μmになるように塗布し、直後にケイ酸カルシウム板を垂直にし、タレ(下方向への流れ)の程度を目視で確認した。
A…タレなし
B…タレほぼなし
C…タレあり
表面含浸材1〜11、20、22、23を用いてモルタル基板に対する外観、含浸深さ及び透水抑制比を評価した。結果を表5に示す。ここで、試験体は、表面含浸材を表5に示す塗布量でローラー1回塗りにてモルタル基板に塗布して調製した。モルタル基板の作製方法、並びに各試験体の評価方法は以下のとおりである。
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「5.1.1モルタル基板の作製」に準拠して作製した。
(1)外観観察試験
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「6.1外観観察試験」に準拠して行った。
A…変化なし
B…ほぼ変化なし
C…白色
(2)含浸深さ
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「6.2含浸深さ試験」に準拠して、各実施例における試験体の含浸深さの評価を行った。
(3)透水抑制比
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「6.3透水量試験」に準拠して、各試験体の透水比(%)を算出し、100%から透水比(%)を差し引いた値を各実施例における「透水抑制比」とした。
表面含浸材14〜19、21を用いてモルタル基板に対する外観を評価した。結果を表6に示す。ここで、試験体は、表面含浸材を表6に示す塗布量でローラー1回塗りにてモルタル基板に塗布して調製した。モルタル基板の作製方法、並びに各試験体の評価方法は以下のとおりである。
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「5.1.1モルタル基板の作製」に準拠して作製した。
JSCE K−571−2010「17.表面含浸材の試験方法(案)」の「6.1外観観察試験」に準拠して行った。
A…変化なし
B…ほぼ変化なし
C…白色
Claims (3)
- アルコキシシランと、高級脂肪酸アミドと、スチレン−ジエン共重合体と、を含有し、
前記アルコキシシランが下記式(1)で表され、
前記スチレン−ジエン共重合体の25質量%トルエン溶液の25℃における粘度が2000〜30000mPa・sであり、
前記高級脂肪酸アミド及び前記スチレン−ジエン共重合体の合計量に対する前記スチレン−ジエン共重合体の質量比が0.50〜0.98である、表面含浸材。
R1 nSi(OR2)4−n (1)
(式中、R1は炭素数5〜12のアルキル基又はフェニル基を示し、nは1又は2を示す。nが2のとき、R1は互いに同一であっても異なっていてもよい。R2は炭素数1〜4のアルキル基を示し、複数存在するR2は互いに同一であっても異なっていてもよい。) - 前記アルコキシシラン100質量部に対し、
前記高級脂肪酸アミドの含有量が0.1〜5質量部、及び前記スチレン−ジエン共重合体の含有量が1.5〜8質量部である、請求項1に記載の表面含浸材。 - 請求項1又は2に記載の表面含浸材を構造物表面に塗布することによって得られる構造物。