JP6588433B2 - リグニンを処理し、結合剤組成物を生成するための方法 - Google Patents
リグニンを処理し、結合剤組成物を生成するための方法 Download PDFInfo
- Publication number
- JP6588433B2 JP6588433B2 JP2016534209A JP2016534209A JP6588433B2 JP 6588433 B2 JP6588433 B2 JP 6588433B2 JP 2016534209 A JP2016534209 A JP 2016534209A JP 2016534209 A JP2016534209 A JP 2016534209A JP 6588433 B2 JP6588433 B2 JP 6588433B2
- Authority
- JP
- Japan
- Prior art keywords
- composition
- lignin
- value
- temperature
- maintained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
a)組成物の温度を0〜60℃に保ちながら、フェノールのクラスから選択される化合物を含有する水性組成物にリグニンを溶解するステップ、および
b)組成物の温度を60〜100℃に保ち、かつ組成物のpHを6〜14のpH値に保ちながら、組成物を反応させるステップ。
a)組成物の温度を0〜60℃に保ちながら、フェノールのクラスから選択される化合物を含有する水性組成物にリグニンを溶解するステップ、
b)組成物の温度を60〜100℃に保ち、かつ組成物のpHを6〜14のpH値に保ちながら、組成物を反応させるステップ、および
c)ステップb)において形成された組成物を架橋剤と混合し、組成物のpHを6〜14のpH値に保ちながら組成物を60〜100℃の温度で加熱するステップ。
この実施例においては、最初にリグニンをフェノールおよび水酸化ナトリウムで処理した。以下の成分およびそれらの量を使用した。
この実施例においては、最初にリグニンをフェノールおよび水酸化ナトリウムで処理した。以下の成分およびそれらの量を使用した。
実施例1において生成した結合剤組成物に含浸したクラフト紙のいくつかの層を加熱および圧力の下でともに融合することによって、高圧ラミネートを製造した。その後、形成したラミネートの沸騰水および熱許容性をテストした。このテストは、規格SFS−EN 438−2(高圧装飾用ラミネート(high−pressure decorative laminates:HPL))に従って行った。サンプルの層間剥離およびブリスターを評価した。どちらのテストも、沸騰水中に2時間浸漬した後、および150℃のオーブン中で30分間加熱した後の視覚的外観の評価に基づくものであった。40%および50%のフェノールがリグニンで置換された結合剤組成物の熱ならびに沸騰水および熱許容性は良好であり、ブリスターは観察されなかった。
この実施例においては、最初にリグニンをフェノールおよび水酸化ナトリウムで処理した。以下の成分およびそれらの量を使用した。
この実施例においては、最初にリグニンをフェノールで処理した。以下の成分およびそれらの量を使用した。
この実施例においては、最初にリグニンをフェノールおよび水酸化ナトリウムで処理した。以下の成分およびそれらの量を使用した。
この実施例においては、最初にリグニンをフェノールおよび水酸化ナトリウムで処理した。以下の成分およびそれらの量を使用した。
Claims (21)
- リグニンを処理するための方法であって、前記方法は以下のステップ:
a)組成物の温度を20〜45℃に保ち、かつ前記組成物のpHを4〜10のpH値に保ちながら、フェノール、クレゾール、レゾルシノール、およびそれらの組み合わせからなる群より選択される化合物を含有する水性組成物にリグニンを溶解するステップと、
b)リグニンをアルカリ化するため、リグニンの溶解した前記組成物の温度を65〜90℃に保ち、かつ前記組成物のpHを7〜10のpH値に保ちながら、前記組成物をアルカリと反応させるステップと
を含むことを特徴とする、方法。 - 前記アルカリはアルカリ金属の水酸化物を含む、請求項1に記載の方法。
- ステップa)における前記組成物のpHは4.5〜9.5のpH値に保たれる、請求項1または2に記載の方法。
- 結合剤組成物を生成するための方法であって、前記方法は以下のステップ:
a)組成物の温度を20〜45℃に保ち、かつ前記組成物のpHを4〜10のpH値に保ちながら、フェノール、クレゾール、レゾルシノール、およびそれらの組み合わせからなる群より選択される化合物を含有する水性組成物にリグニンを溶解するステップと、
b)リグニンをアルカリ化するため、リグニンの溶解した前記組成物の温度を65〜90℃に保ち、かつ前記組成物のpHを7〜10のpH値に保ちながら、前記組成物をアルカリと反応させるステップと、
c)ステップb)において形成された前記組成物を架橋剤と混合し、前記組成物のpHを7〜10のpH値に保ちながら前記組成物を65〜90℃の温度で加熱するステップと
を含むことを特徴とする、方法。 - ステップa)における前記組成物のpHは4.5〜9.5のpH値に保たれる、請求項4に記載の方法。
- 前記架橋剤はアルデヒドである、請求項4または5に記載の方法。
- 結合剤組成物の生成のための、請求項1〜3のいずれか一項に記載の方法によって処理されたリグニンの使用。
- ラミネートを製造するための、請求項4または請求項5に記載の方法によって得ることのできる結合剤組成物の使用。
- 鋳造材料、保護コーティング、摩擦材料、研磨材料、グラスウール、ロックウール、プリプレグ、シャッタリングフィルム、オーバーレイ、成形構成要素、または繊維強化複合物を製造するための、請求項4または請求項5に記載の方法によって得ることのできる結合剤組成物の使用。
- ステップa)における前記組成物の温度は、30〜45℃に保たれる、請求項1または2に記載の方法。
- ステップa)における前記組成物のpHは5〜9のpH値に保たれる、請求項1または2に記載の方法。
- ステップa)における前記組成物のpHは5.5〜8.5のpH値に保たれる、請求項1または2に記載の方法。
- ステップb)における前記組成物のpHは7〜9のpH値に保たれる、請求項3に記載の方法。
- ステップb)において、前記組成物は75〜90℃の温度で加熱される、請求項1〜3のいずれか一項に記載の方法。
- ステップc)は、前記組成物を70〜90℃の温度で加熱するステップを含む、請求項4に記載の方法。
- ステップc)は、前記組成物を75〜85℃の温度で加熱するステップを含む、請求項4に記載の方法。
- ステップa)における前記組成物のpHは5〜9のpH値に保たれる、請求項4に記載の方法。
- ステップa)における前記組成物のpHは5.5〜8.5のpH値に保たれる、請求項4に記載の方法。
- ステップb)における前記組成物のpHは7〜9のpH値に保たれる、請求項5に記載の方法。
- 前記架橋剤はホルムアルデヒド、パラホルムアルデヒド、またはそれらの組み合わせである、請求項4または5に記載の方法。
- 高圧ラミネートを製造するための、請求項4または請求項5に記載の方法によって得ることのできる結合剤組成物の使用。