JP6572225B2 - 放射線照射前架橋ポリオレフィン粘着フィルム及び作製方法並びにパッケージ用の方法及びアセンブリ - Google Patents
放射線照射前架橋ポリオレフィン粘着フィルム及び作製方法並びにパッケージ用の方法及びアセンブリ Download PDFInfo
- Publication number
- JP6572225B2 JP6572225B2 JP2016549359A JP2016549359A JP6572225B2 JP 6572225 B2 JP6572225 B2 JP 6572225B2 JP 2016549359 A JP2016549359 A JP 2016549359A JP 2016549359 A JP2016549359 A JP 2016549359A JP 6572225 B2 JP6572225 B2 JP 6572225B2
- Authority
- JP
- Japan
- Prior art keywords
- adhesive film
- film
- irradiation
- polyolefin
- crosslinked
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前架橋型フィルムと、同成分の非架橋型フィルムはA4サイズのものをそれぞれ5枚取り、別々に畳んで35℃のオーブンに入れ、その上に1000gの分銅を24時間放置して取り出した。接着度を比較すると、放射線照射前架橋型フィルムの接着度は同成分の非放射線架橋型フィルムを著しく下回ったことが分かる。
前架橋型フィルムと、同成分の非架橋型フィルムはA4サイズのものをそれぞれ5枚取り、別々に畳んで35℃のオーブンに入れ、その上に1000gの分銅を24時間放置して取り出した。接着度を比較すると、放射線照射前架橋型フィルムの接着度は同成分の非放射線架橋型フィルムを著しく下回ったことが分かる。
Claims (86)
- ポリオレフィン原材料を混合して粘着フィルムを製造するステップと、
前記ポリオレフィン原材料の架橋反応を直接励起可能な照射エネルギーを用いて前記粘着フィルムを照射するステップと、
前記照射エネルギーの照射線量を調整して、前記粘着フィルムでの架橋された部分の架橋度を3〜95%にするステップと、
前記照射エネルギーの照射線量を調整して、前記粘着フィルムの厚さに占める前記架橋部の割合を5〜100%にし、そのうち100%は前記粘着フィルムのすべてが架橋された場合を指すステップと、
を含み、
前記照射エネルギーがβ線、γ線、X線、α線または中性子線のうちの1種類であることを特徴とするパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。 - 前記粘着フィルムの前架橋された部分が少なくとも前記粘着フィルムの表層を構成することを特徴とする請求項1に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記ポリオレフィン原材料を混合して粘着フィルムを製造する方法は、T型プレート金型で押し出して製膜する、または2つのカレンダーロールで製膜することを含むことを特徴とする請求項1に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記製膜温度が70〜200℃で、金型温度が70〜200℃であることを特徴とする請求項3に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記照射エネルギーの照射線量の調整はポリオレフィン粘着フィルムの積層後の照射または展開後の照射であることを特徴とする請求項1に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記ポリオレフィン粘着フィルムがエチレン酢酸ビニル樹脂フィルムであることを特徴とする請求項1に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記エチレン酢酸ビニル樹脂フィルムはEVA樹脂51〜99.58部、有機過酸化物系架橋剤0.3〜2部、共架橋剤0.01〜5部、酸化防止剤0.1〜2部、シランカップリング剤0.01〜2部、顔料0〜40部、ポリオレフィンエラストマー0〜40部を重量部とすることを特徴とする請求項6に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記放射線量が0.2〜100KGYであることを特徴とする請求項6に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記粘着フィルムがすべて前架橋された場合、前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムの前架橋度が5〜74%であることを特徴とする請求項6に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムが単一層、2層または多層の共押出フィルムであることを特徴とする請求項6に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムの厚さが0.01〜2mmであることを特徴とする請求項6に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記EVA樹脂はVA重量の百分率が20〜35%のEVA樹脂であることを特徴とする請求項7に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記有機過酸化物系架橋剤はジアルキルペルオキシド、アルキルアリールペルオキシド、ジアリールペルオキシド、ヒドロペルオキシド、ジアシルペルオキシド、ペルオキシエステル、ケトンパーオキサイド、ペルオキシ炭酸エステル、ペルオキシケタールのうちの1種類または複数種類を含むことを特徴とする請求項7に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記共架橋剤はアクリル酸類、メタクリル酸類、アクリルアミド類、アリル類、エポキシ類化合物のうちの1種類または複数種類を含むことを特徴とする請求項7に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記酸化防止剤が光安定剤、UV吸収剤と熱酸化エージング分解剤のうちの1種類または複数種類を含むことを特徴とする請求項7に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記シランカップリング剤とは分子に化学的性質が異なる2種類の基が同時に含まれる有機けい素化合物を指すことを特徴とする請求項7に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記顔料とはEVAフィルムの色を変えられる添加剤を指し、カーボンブラック、リトポン、硫化亜鉛、二酸化チタン粉末、超微粒子硫酸バリウム、グラスバブルズのうちの1種類または数種類であることを特徴とする請求項7に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記ポリオレフィンエラストマーとは、低密度ポリエチレン、エチレンとブチレンまたはオクテンの共重合体のうちの少なくとも1種類である、EVAと混合可能な炭素−炭素鎖樹脂を指すことを特徴とする請求項7に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記ポリオレフィンフィルムがポリオレフィンエラストマーフィルムであることを特徴とする請求項1に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記ポリオレフィンエラストマーフィルムはポリオレフィンエラストマー69〜99.8部、共架橋剤0.01〜5部、酸化防止剤0.01〜2部、シランカップリング剤0〜2部、有機過酸化物架橋剤0〜2部、顔料0〜20部を重量部とし、
前記ポリオレフィンエラストマーはエチレンとブチレン、アミレン、エチレンまたはオクテンの共重合体の中の1種類または数種類の混合物であり、
前記粘着フィルムのすべてが前架橋した場合、前記放射線照射前架橋ポリオレフィンエラストマーフィルムの架橋度が3〜70%で、前記照射線量が10〜200KGYであることを特徴とする、請求項19に記載のパッケージ用の放射線照射前架橋ポリオレフィンフィルムの作製方法。 - 前記放射線量が10〜200KGYであることを特徴とする請求項19に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記粘着フィルムがすべて前架橋された場合、前記放射線照射前架橋ポリオレフィンエラストマーフィルムの架橋度が3〜70%であることを特徴とする請求項19に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記放射線照射前架橋ポリオレフィンエラストマーフィルムの厚さが0.2〜1mmであることを特徴とする請求項19に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記ポリオレフィンエラストマーがエチレンとブチレン、アミレン、ヘキセンまたはオクテンの共重合体の中の1種類または数種類の混合物であることを特徴とする請求項19に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記ポリオレフィンエラストマーが極性基によってグラフトされたものまたはグラフトされていないもので、製膜時に極性基小分子添加剤を加え、極性基が、シランカップリング剤、グラフト率が3%を下回る、エラストマー製膜前にエラストマー分子鎖にグラフトされたシランカップリング剤、又はグラフト率が0.6%の、ビニルトリメトキシシランをグラフトしたエチレン−ヘキセン共重合体であることを特徴とする請求項20に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記共架橋剤とは多官能モノマーを指し、トリアリルイソシアヌレート、シアヌル酸トリアリル、トリメチロールプロパントリアクリレート、トリメチロールプロパントリメタクリラートのうちの1種類または数種類であることを特徴とする請求項20に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記酸化防止剤とは熱酸化エージング分解剤とUV吸収剤を指し、ペンタエリトリトールテトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオナート]、セバシン酸ビス(2,2,6,6−テトラメチル−4−ピペリジル)とN,N’−ジ−SEC−ブチル−1,4−フェニレンジアミンのうちの1種類または数種類、フェノール系酸化防止剤、ヒンダードアミン系酸化防止剤、亜リン酸類、ベンゾフェノン類、ベンゾトリアゾール類であることを特徴とする請求項20に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記シランカップリング剤とは分子に化学的性質が異なる2種類の基が同時に含まれる有機けい素化合物であることを特徴とする請求項20に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記有機過酸化物系架橋剤とは、プラスチックに常用される熱架橋用の有機過酸化物系架橋剤を指し、ジクミルペルオキシド、tert−ブチル=2−エチルペルオキシヘキサノアート、2,5−ジメチル−2,5−ビス(tert−ブチルパーオキシ)ヘキサンのうちの1種類または数種類であることを特徴とする請求項20に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- 前記顔料とはポリオレフィンエラストマーフィルムの色を変えられる添加剤を指し、カーボンブラック、リトポン、硫化亜鉛、二酸化チタン粉末、グラスバブルズであることを特徴とする請求項20に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルムの作製方法。
- ポリオレフィンの粘着フィルムにおける照射エネルギーの照射によって架橋された部分がポリオレフィン粘着フィルムの厚さの5〜100%を占め、そのうち100%は前記粘着フィルムがすべて架橋された場合を指し、前記架橋された部分の架橋度が3〜95%であり、
前記照射エネルギーがβ線、γ線、X線、α線または中性子線のうちの1種類であることを特徴とするパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。 - 前記粘着フィルムの架橋された部分が前記粘着フィルムの表層を構成することを特徴とする請求項31に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記ポリオレフィン粘着フィルムがエチレン酢酸ビニル樹脂フィルムであることを特徴とする請求項31に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記エチレン酢酸ビニル樹脂フィルムはEVA樹脂51〜99.58部、有機過酸化物系架橋剤0.3〜2部、共架橋剤0.01〜5部、酸化防止剤0.1〜2部、シランカップリング剤0.01〜2部、顔料0〜40部、ポリオレフィンエラストマー0〜40部を重量部とすることを特徴とする請求項33に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記粘着フィルムがすべて前架橋された場合、前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムの前架橋度が5〜74%であることを特徴とする請求項33に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムが単一層、2層または多層の共押出フィルムであることを特徴とする請求項33に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムの厚さが0.01〜2mmであることを特徴とする請求項33に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記EVA樹脂はVA重量の百分率が20〜35%のEVA樹脂であることを特徴とする請求項34に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記有機過酸化物系架橋剤はジアルキルペルオキシド、アルキルアリールペルオキシド、ジアリールペルオキシド、ヒドロペルオキシド、ジアシルペルオキシド、ペルオキシエステル、ケトンパーオキサイド、ペルオキシ炭酸エステル、ペルオキシケタールのうちの1種または複数種類を含むことを特徴とする請求項34に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記共架橋剤はアクリル酸類、メタクリル酸類、アクリルアミド類、アリル類、エポキシ類化合物のうちの1種類または複数種類を含むことを特徴とする請求項34に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記酸化防止剤は光安定剤、UV吸収剤と熱酸化エージング分解剤のうちの1種類または複数種類を含むことを特徴とする請求項34に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記シランカップリング剤とは分子に化学的性質が異なる2種類の基が同時に含まれる有機けい素化合物を指すことを特徴とする請求項34に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記顔料とはEVAフィルムの色を変えられる添加剤を指し、カーボンブラック、リトポン、硫化亜鉛、二酸化チタン粉末、超微粒子硫酸バリウム、グラスバブルズのうちの1種類または数種類であることを特徴とする請求項34に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記ポリオレフィンエラストマーとは、低密度ポリエチレン、エチレンとブチレンまたはオクテンの共重合体のうちの少なくとも1種類である、EVAと混合可能な炭素−炭素鎖樹脂を指すことを特徴とする請求項34に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記ポリオレフィン粘着フィルムがポリオレフィンエラストマーフィルムであることを特徴とする請求項31に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記ポリオレフィンエラストマーフィルムはポリオレフィンエラストマー69〜99.8部、共架橋剤0.01〜5部、酸化防止剤0.01〜2部、シランカップリング剤0〜2部、有機過酸化物系架橋剤0〜2部、顔料0〜20部を重量部とすることを特徴とする請求項45に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記粘着フィルムがすべて前架橋された場合、前記放射線照射前架橋ポリオレフィンエラストマーフィルムの架橋度が3〜70%であることを特徴とする請求項45に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記放射線照射前架橋ポリオレフィンエラストマーフィルムの厚さが0.2〜1mmであることを特徴とする請求項45に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記ポリオレフィンエラストマーはエチレンとブチレン、アミレン、ヘキセンまたはオクテンの共重合体のうちの1種類または数種類の混合物であることを特徴とする請求項45に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記ポリオレフィンエラストマーが極性基によってグラフトされたものまたはグラフトされていないもので、製膜時に極性基小分子添加剤を加え、極性基が、シランカップリング剤、グラフト率が3%を下回る、エラストマー製膜前にエラストマー分子鎖にグラフトされたシランカップリング剤、又はグラフト率が0.6%の、ビニルトリメトキシシランをグラフトしたエチレン−ヘキセン共重合体であることを特徴とする請求項46に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記共架橋剤とは多官能モノマーを指し、トリアリルイソシアヌレート、シアヌル酸トリアリル、トリメチロールプロパントリアクリレート、トリメチロールプロパントリメタクリラートのうちの1種類または数種類であることを特徴とする請求項46に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記酸化防止剤とは熱酸化エージング分解剤とUV吸収剤を指し、ペンタエリトリトールテトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオナート]、セバシン酸ビス(2,2,6,6−テトラメチル−4−ピペリジル)とN,N’−ジ−SEC−ブチル−1,4−フェニレンジアミンのうちの1種類または数種類、フェノール系酸化防止剤、ヒンダードアミン系酸化防止剤、亜リン酸類、ベンゾフェノン類、ベンゾトリアゾール類であることを特徴とする請求項46に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記シランカップリング剤とは分子に化学的性質が異なる2種類の基が同時に含まれる有機けい素化合物であることを特徴とする請求項46に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記有機過酸化物系架橋剤とはプラスチックに常用される熱架橋用の有機過酸化物系架橋剤を指し、ジクミルペルオキシド、tert−ブチル=2−エチルペルオキシヘキサノアート、2,5−ジメチル−2,5−ビス(tert−ブチルパーオキシ)ヘキサンのうちの1種類または数種類であることを特徴とする請求項46に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- 前記顔料とはポリオレフィンエラストマーフィルムの色を変えられる添加剤を指し、カーボンブラック、リトポン、硫化亜鉛、二酸化チタン粉末、グラスバブルズであることを特徴とする請求項46に記載のパッケージ用の放射線照射前架橋ポリオレフィン粘着フィルム。
- ポリオレフィン原材料を混合してフィルムを製造するステップと、
前記ポリオレフィン原材料の架橋反応を直接励起可能な照射エネルギーを用いて前記フィルムを照射するステップと、
前記照射エネルギーの照射線量を調整して、前記フィルムでの架橋された部分の架橋度を5%〜95%にするステップと、
前記照射エネルギーの照射線量を調整して、前記フィルムの厚さに占める前記架橋された部分の割合を51〜100%にし、そのうち100%は前記フィルムのすべてが架橋された場合を指すステップと、
前記フィルムを前保護層とパッケージ基板との間に置いてパッケージ対象物と共にパッケージアセンブリを構成し、前記フィルムの前架橋部を前記パッケージ対象物に接触させるステップと、
前記パッケージアセンブリを加熱することにより前記フィルムに更なる架橋反応を起こさせてパッケージを完成させるステップと、
を含み、
前記照射エネルギーがβ線、γ線、X線、α線または中性子線のうちの1種類であることを特徴とする放射線照射前架橋ポリオレフィンフィルムを用いたパッケージ方法。 - 前記粘着フィルムの前架橋された部分が前記粘着フィルムの表層を構成することを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記ポリオレフィン原材料を混合して粘着フィルムを製造する方法はT型プレート金型で押し出して製膜する、または2つのカレンダーロールで製膜することを含むことを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記製膜温度が70〜200℃で、金型温度が70〜200℃であることを特徴とする請求項58に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記照射はポリオレフィン粘着フィルム全体に対する照射または展開後の照射であることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記ポリオレフィン粘着フィルムがエチレン酢酸ビニル樹脂フィルムであることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記エチレン酢酸ビニル樹脂フィルムはEVA樹脂51〜99.58部、有機過酸化物系架橋剤0.3〜2部、共架橋剤0.01〜5部、酸化防止剤0.1〜2部、シランカップリング剤0.01〜2部、顔料0〜40部、ポリオレフィンエラストマー0〜40部を重量部とすることを特徴とする請求項61に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 放射線量が0.2〜100KGYであることを特徴とする請求項61に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記粘着フィルムがすべて前架橋された場合、前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムの前架橋度が5〜74%であることを特徴とする請求項61に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムが単一層、2層または多層の共押出フィルムであることを特徴とする請求項61に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記放射線照射前架橋エチレン酢酸ビニル樹脂フィルムの厚さが0.01〜2mmであることを特徴とする請求項61に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記ポリオレフィン粘着フィルムがポリオレフィンエラストマーフィルムであることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記ポリオレフィンエラストマーフィルムはポリオレフィンエラストマー69〜99.8部、共架橋剤0.01〜5部、酸化防止剤0.01〜2部、シランカップリング剤0〜2部、有機過酸化物系架橋剤0〜2部、顔料0〜20部を重量部とすることを特徴とする請求項67に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記放射線量が10〜200KGYであることを特徴とする請求項67に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記粘着フィルムがすべて前架橋された場合、前記放射線照射前架橋ポリオレフィンエラストマーフィルムの架橋度が3〜70%であることを特徴とする請求項67に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記放射線照射前架橋ポリオレフィンエラストマーフィルムの厚さが0.2〜1mmであることを特徴とする請求項67に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記ポリオレフィンエラストマーはエチレンとブチレン、アミレン、ヘキセンまたはオクテンの共重合体のうちの1種類または数種類の混合物であることを特徴とする請求項67に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記パッケージアセンブリの加熱・パッケージング時に、前記パッケージアセンブリに対する加圧または真空排気してパッケージすることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記パッケージ対象部は結晶シリコン太陽電池、発光半導体LED、有機発光半導体OLED、又はディスプレイを含むことを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記前保護層と前記パッケージ基板との間に、少なくとも1層が前記前架橋粘着フィルムである粘着フィルムが2層設けられ、その間にパッケージ対象部が設けられることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記前保護層が透明保護層で、具体的には透明ガラス、透明セラミックスまたは透明プラスチックであることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記粘着フィルムはEVA(エチレン酢酸ビニル樹脂)粘着フィルムと前架橋EVA粘着フィルムをそれぞれ1層備え、前記EVA粘着フィルムが前記前保護層に近い箇所に設けられることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記粘着フィルム2層がいずれも前架橋POE(ポリオレフィンエラストマー)粘着フィルムであることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- 前記パッケージ基板がガラス、セラミックスまたはプラスチックであることを特徴とする請求項56に記載の放射線照射前架橋ポリオレフィン粘着フィルムを用いたパッケージ方法。
- ポリオレフィンの粘着フィルムにおける照射エネルギーの照射によって架橋された部分がポリオレフィン粘着フィルムの厚さの51〜100%を占め、そのうち100%は前記粘着フィルムがすべて架橋された場合を指し、前記架橋された部分の架橋度が5〜95%であり、
前保護層とパッケージ基板との間にパッケージ対象部と共にパッケージアセンブリを構成する放射線照射前架橋ポリオレフィン粘着フィルムが設けられ、前記粘着フィルムの前架橋部が前記パッケージ対象部と接触し、
前記照射エネルギーがβ線、γ線、X線、α線または中性子線のうちの1種類であることを特徴とするパッケージアセンブリ。 - 前記パッケージ対象部は結晶シリコン太陽電池、発光半導体LED、有機発光半導体OLED、ディスプレイを含むことを特徴とする請求項80に記載のパッケージアセンブリ。
- 前記前保護層と前記パッケージ基板との間に、少なくとも1層が前記前架橋粘着フィルムである粘着フィルムが2層設けられ、その間にパッケージ対象部が設けられることを特徴とする請求項80に記載のパッケージアセンブリ。
- 前記前保護層が透明保護層で、具体的には透明ガラス、透明セラミックスまたは透明プラスチックであることを特徴とする請求項80に記載のパッケージアセンブリ。
- 前記粘着フィルムがEVA(エチレン酢酸ビニル樹脂)粘着フィルムと前架橋EVA粘着フィルムをそれぞれ1層備え、前記EVA粘着フィルムが前記前保護層に近い箇所に設けられることを特徴とする請求項80に記載のパッケージアセンブリ。
- 前記粘着フィルム2層がいずれも前架橋POE(ポリオレフィンエラストマー)粘着フィルムであることを特徴とする請求項80に記載のパッケージアセンブリ。
- 前記パッケージ基板がガラス、セラミックスまたはプラスチックであることを特徴とする請求項80に記載のパッケージアセンブリ。