JP6542436B2 - Skin material and method of manufacturing the same - Google Patents
Skin material and method of manufacturing the same Download PDFInfo
- Publication number
- JP6542436B2 JP6542436B2 JP2018115174A JP2018115174A JP6542436B2 JP 6542436 B2 JP6542436 B2 JP 6542436B2 JP 2018115174 A JP2018115174 A JP 2018115174A JP 2018115174 A JP2018115174 A JP 2018115174A JP 6542436 B2 JP6542436 B2 JP 6542436B2
- Authority
- JP
- Japan
- Prior art keywords
- melt adhesive
- hot melt
- resin foam
- natural leather
- moisture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、樹脂発泡体に天然皮革が接着された表皮材とその製造方法に関する。 The present invention relates to a skin material in which natural leather is adhered to a resin foam, and a method of manufacturing the same.
従来、自動車、鉄道、航空機、家具等の座席や内装材等の表皮材として、ポリウレタン発泡体に天然皮革を接着した表皮材がある。 Conventionally, as a skin material of a seat such as a car, a railway, an aircraft, a furniture, or an interior material, there is a skin material in which a natural leather is adhered to a polyurethane foam.
ポリウレタン発泡体と天然皮革の接着方法として、ポリウレタン発泡体と天然皮革を不織布状のホットメルト接着剤を挟んで積層し、加圧・加熱下でホットメルト接着剤を溶融し、天然皮革とポリウレタン発泡体を接着するものがある（特許文献１）。 As a bonding method of polyurethane foam and natural leather, polyurethane foam and natural leather are laminated with a non-woven hot melt adhesive interposed, and the hot melt adhesive is melted under pressure and heat, and natural leather and polyurethane foam are formed. There is a thing which adheres a body (patent documents 1).
また、他の接着方法として、ポリウレタン発泡体の片面に粉末状のホットメルト接着剤を塗布して接着層を形成し、その接着層に天然皮革を積層し、熱盤でプレスすることにより接着層のホットメルト接着剤を溶融し、天然皮革とポリウレタン発泡体を接着するものがある（特許文献２）。 Also, as another bonding method, a powdery hot melt adhesive is applied on one side of a polyurethane foam to form a bonding layer, natural leather is laminated on the bonding layer, and pressed with a hot platen. No. 4,648,095, which melts a hot melt adhesive and bonds a natural leather and a polyurethane foam.
しかし、不織布状のホットメルト接着剤あるいは粉末状のホットメルト接着剤を用いる方法では、天然皮革とポリウレタン発泡体を接着する際に、ポリウレタン発泡体側から加熱する場合、表皮材の感触を向上させるためにポリウレタン発泡体の厚みを１０ｍｍ以上にすると、ポリウレタン発泡体の断熱効果によってポリウレタン発泡体と天然皮革間のホットメルト接着剤に充分な熱が伝わらず、ポリウレタン発泡体と天然皮革を確実に接着できなくなる。また、接着性を高めるために加熱温度を上げると、ポリウレタン発泡体が熱劣化を生じる問題が発生する。さらに、表皮材の縫製作業を良好にするため、ポリウレタン発泡体の裏面にナイロントリコット等からなる裏基布を予め接着した場合、裏基布が熱によって収縮する等の問題が発生する。 However, in the method of using a non-woven hot melt adhesive or a powdered hot melt adhesive, when bonding a natural leather and a polyurethane foam, when heating from the polyurethane foam side, the feel of the surface material is improved. If the thickness of the polyurethane foam is 10 mm or more, sufficient heat is not transmitted to the hot melt adhesive between the polyurethane foam and the natural leather by the heat insulation effect of the polyurethane foam, and the polyurethane foam and the natural leather can be bonded reliably. It disappears. In addition, when the heating temperature is increased to improve the adhesion, there is a problem that the polyurethane foam may be thermally deteriorated. Furthermore, when the back base fabric made of nylon tricot or the like is bonded in advance to the back surface of the polyurethane foam in order to improve the sewing work of the surface material, problems such as shrinkage of the back base fabric due to heat occur.
また、ホットメルト接着剤による天然皮革とポリウレタン発泡体の接着を確実にするため、天然皮革側から加熱してホットメルト接着剤に熱が伝わり易くする場合、熱が直接天然皮革に加わるため、天然皮革本来の表面に有する自然なシボ（微細な凹凸）が熱で伸びて平坦な表面になり、天然皮革本来の意匠性が損なわれたり、熱によって天然皮革が収縮したりする問題が発生し、良好な表皮材が得られなくなる。 Also, in order to ensure the adhesion between the natural leather and the polyurethane foam by the hot melt adhesive, if heat is easily transmitted to the hot melt adhesive from the natural leather side, the heat is directly applied to the natural leather, so natural The natural emboss (fine asperity) on the surface of the leather grows by heat and becomes a flat surface, and the original design of the natural leather is impaired, or the heat shrinks due to heat. A good skin material can not be obtained.
また、天然皮革は天然素材のために水分を保持しており、加熱によって天然皮革内の水分が蒸発し、ホットメルトの接着性を損ねる問題がある。
さらに、不織布状のホットメルト接着剤を用いる方法では、連続した繊維構造が天然皮革とポリウレタン発泡体間に少なからず残存することになるため、表皮材の撓み性、柔軟性を損ない、硬くなる問題がある。
なお、加熱によって生じる前記の問題を防ぐために加熱温度を下げると、今度はホットメルト接着剤の接着性が低下して天然皮革とポリウレタン発泡体の接着不良を生じるようになる。
In addition, natural leather holds moisture because of natural materials, and the water in natural leather evaporates by heating, which causes a problem of impairing hot melt adhesion.
Furthermore, in the method of using a non-woven hot melt adhesive, the continuous fiber structure remains in a small amount between the natural leather and the polyurethane foam, so the flexibility and the flexibility of the surface material are impaired, and the problem of hardening becomes difficult. There is.
Incidentally, if the heating temperature is lowered to prevent the above-mentioned problems caused by heating, then the adhesion of the hot melt adhesive is lowered to cause adhesion failure between natural leather and polyurethane foam.
本発明は前記の点に鑑みなされたものであって、天然皮革と樹脂発泡体との接着が強固で、かつ良好な天然皮革の風合いを有する表皮材とその製造方法の提供を目的とする。 The present invention has been made in view of the above-mentioned point, and an object of the present invention is to provide a surface material having strong adhesion between natural leather and a resin foam and having good natural leather texture and a method for producing the same.
請求項１の発明は、軟質スラブポリウレタン発泡体からなる樹脂発泡体と、前記樹脂発泡体のセル骨格が切断されて凹凸となって露出した表面に溶融状態で塗布されて係合した湿気硬化型ホットメルト接着剤で接着された含水の天然皮革とよりなる表皮材に係る。
The invention of
請求項２の発明は、請求項１において、前記天然皮革は、溶融状態で塗布された前記湿気硬化型ホットメルト接着剤を挟んで前記樹脂発泡体の表面に積層されて、空気中の湿気と前記天然皮革から自然に放出される湿気とによる前記湿気硬化型ホットメルト接着剤の硬化で接着されたことを特徴とする。
According to the invention of
請求項３の発明は、請求項１または２において、前記湿気硬化型ホットメルト接着剤は、無溶剤系ウレタン系反応性熱溶融樹脂であることを特徴とする。
The invention according to
請求項４の発明は、請求項１から３の何れか一項において、前記樹脂発泡体は、前記天然皮革と接着されない面に裏基布が設けられていることを特徴とする。
The invention of
請求項５の発明は、セル骨格が切断されて凹凸となって露出した樹脂発泡体の表面に、加熱により溶融した湿気硬化型ホットメルト接着剤を塗布し、溶融状態の前記湿気硬化型ホットメルト接着剤を挟んで前記樹脂発泡体の表面に含水の天然皮革を積層する表皮材の製造方法であって、前記天然皮革の積層後に常温で圧縮する工程と、前記圧縮中に空気中の湿気と前記天然皮革から自然放出される湿気により前記湿気硬化型ホットメルト接着剤を硬化させる工程とを含むことを特徴とする表皮材の製造方法に係る。
According to the invention of
請求項６の発明は、請求項５において、前記樹脂発泡体は、前記天然皮革と接着されない面に裏基布が予め設けられていることを特徴とする。
The invention of
請求項７の発明は、請求項５または６において、前記湿気硬化型ホットメルト接着剤の塗布の際に、前記樹脂発泡体の下面側に位置する送りロールによって前記樹脂発泡体が一方向へ送られている状態で、接着剤貯留槽の吐出部から、接着剤の供給ロールと塗布ロール間に供給貯留される溶融状態のホットメルト接着剤を、前記接着剤の溶融温度よりも低い温度の前記供給ロールと前記塗布ロールの回転によって前記樹脂発泡体の上側表面に供給塗布することで、前記樹脂発泡体の上面に露出した凹凸に溶融状態のホットメルト接着剤を係合させる工程を行い、前記天然皮革の積層に際し、溶融状態の前記ホットメルト接着剤が塗布された前記樹脂発泡体を下型の上面に載置した後、溶融状態の前記ホットメルト接着剤の上に、前記天然皮革を裏面が下向きとなるように積層して積層体とする工程を行い、前記圧縮する際に、上型により、前記積層体を常温で圧縮する工程と、前記ホットメルト接着剤を、空気中の湿気と前記天然皮革から自然放出される湿気により硬化させる工程を行うことを特徴とする。
According to the invention of
請求項１の発明によれば、軟質スラブポリウレタン発泡体からなる樹脂発泡体の表面に溶融状態のホットメルト接着剤が塗布されているため、天然皮革の積層後にホットメルト接着剤を溶融するための加熱を行わなくても樹脂発泡体と天然皮革の接着が良好なものになり、かつ加熱によって天然皮革の表面のシボが伸びたり、天然皮革本来の意匠性が損なわれたりすることがなく、良好な風合いの表皮材が得られる。さらに、天然皮革積層後の加熱が不要なため、加熱による樹脂発泡体の熱劣化や変形のおそれがなく、良好な品質の表皮材が得られる。
請求項１の発明によれば、樹脂発泡体の表面はセル骨格の切断部が凹凸となって露出しているため、ホットメルト接着剤が樹脂発泡体の表面に係合して樹脂発泡体と天然皮革の接着強度が高くなる。
請求項１及び２の発明によれば、ホットメルト接着剤が湿気硬化型ホットメルト接着剤からなるため、天然皮革から蒸発する水分によっても湿気硬化型ホットメルト接着剤の硬化が進行し、樹脂発泡体と天然皮革の接着が良好なものになる。
According to the invention of
According to the invention of
According to the first and second aspects of the invention, since the hot melt adhesive is made of a moisture curing type hot melt adhesive, the curing of the moisture curing type hot melt adhesive proceeds even with the moisture evaporating from the natural leather, and resin foaming Adhesion between the body and the natural leather will be good.
請求項３の発明によれば、湿気硬化型ホットメルト接着剤は無溶剤系ウレタン系反応性熱溶融樹脂であるため、車両用途におけるＶＯＣ規格等を合格するうえで好ましい。
According to the invention of
請求項４の発明によれば、樹脂発泡体において天然皮革と接着されない面に設けられた裏基布は、樹脂発泡体が加熱されないために収縮などの熱劣化のおそれがなく、裏基布の良好な品質を保つことができ、裏基布によって表皮材の縫製作業を良好なものにできる。
According to the invention of
請求項５の発明によれば、天然皮革の積層後にホットメルト接着剤を溶融するための加熱を行わなくても樹脂発泡体と天然皮革の良好な接着を行うことができ、かつ加熱によって天然皮革の表面のシボが伸びたり、天然皮革本来の意匠性が損なわれたりすることがなく、良好な風合いの表皮材が得られる。さらに、天然皮革積層後の加熱が不要なため、加熱による樹脂発泡体の熱劣化や変形のおそれがなく、良好な品質の表皮材が得られる。
請求項５の発明によれば、ホットメルト接着剤が湿気硬化型ホットメルト接着剤からなるため、天然皮革から蒸発する水分によっても湿気硬化型ホットメルト接着剤の硬化が進行し、樹脂発泡体と天然皮革の接着が良好なものになる。さらに、樹脂発泡体の表面はセル骨格の切断部が凹凸となって露出しているため、ホットメルト接着剤が樹脂発泡体の表面に係合して樹脂発泡体と天然皮革の接着強度が高くなる。
According to the invention of
According to the invention of
請求項６の発明によれば、樹脂発泡体において天然皮革と接着されない面に設けられた裏基布は、樹脂発泡体が加熱されないために収縮などの熱劣化のおそれがなく、裏基布の良好な品質を保つことができ、得られる表皮材の縫製作業を裏基布によって良好なものにできる。
According to the invention of
以下に、本発明の実施形態について説明する。
図１に示す第１実施形態の表皮材１０は、自動車、鉄道、航空機、家具等の座席や内装材等の表皮材として好適なものであって、樹脂発泡体１１と、前記樹脂発泡体１１の表面に溶融状態で塗布されたホットメルト接着剤２１を挟んで前記樹脂発泡体１１の表面に積層されて接着した天然皮革３１とで構成されている。
Hereinafter, embodiments of the present invention will be described.
The
前記樹脂発泡体１１としては特に限定されるものではなく、例えば軟質ポリウレタン発泡体、ポリエチレン発泡体、ポリプロピレン発泡体等を挙げることができる。特に、常温・常圧下で連続的に発泡させるスラブ発泡により製造されたブロック状の軟質ポリウレタン発泡体をシート状に裁断した軟質スラブポリウレタン発泡体は、前記樹脂発泡体１１として好適なものである。前記軟質スラブポリウレタン発泡体は、裁断表面にセル骨格の切断部が凹凸となって露出しているため、ホットメルト接着剤２１が軟質スラブポリウレタン発泡体の表面に係合して前記樹脂発泡体１１と前記天然皮革３１の接着強度が高くなる。
It does not specifically limit as said resin foam 11, For example, a soft polyurethane foam, a polyethylene foam, a polypropylene foam etc. can be mentioned. In particular, a flexible slab polyurethane foam obtained by cutting a block-like flexible polyurethane foam produced by slab foaming continuously foaming at normal temperature and normal pressure into a sheet is suitable as the resin foam 11. In the soft slab polyurethane foam, since the cut portion of the cell skeleton is exposed as unevenness on the cut surface, the
また、前記表皮材１０は、前記表皮材１０の製造時に高温に加熱されないため、融点の低いポリエチレンフォームなども前記樹脂発泡体１１として使用可能である。
前記樹脂発泡体１１の厚みは、前記表皮材１０の用途に応じて適宜設定されるが、例として２〜２０ｍｍを挙げる。
In addition, since the
Although the thickness of the said resin foam 11 is suitably set according to the use of the said
前記樹脂発泡体１１は、前記天然皮革３１と接着されない面に、裏基布１５がフレームラミネートやエマルジョン接着剤などで予め接着されている。前記裏基布１５は、前記表皮材１１の縫製等の際に表皮材１１の伸びを抑えたり、前記表皮材１１の裏面の滑りを良好にし、ミシン台での布送りを容易にする。あるいは前記表皮材１１の使用時に裏面を保護したりする作用を有するものであり、布材（編物、織物）、不織布等からなるものを挙げる。
On the surface of the resin foam 11 which is not bonded to the natural leather 31, the
前記樹脂発泡体１１において前記天然皮革３１が接着される表面に溶融状態で塗布されるホットメルト接着剤２１としては、酢酸ビニル樹脂のような熱可塑性プラスチックからなる通常のもの、あるいは加熱により溶融して湿気により反応硬化する湿気硬化型のものなどが挙げられる。特に湿気硬化型のホットメルト接着剤は、空気中の湿分のみならず、前記天然皮革３１に自然に含まれる水分を利用して硬化が促進されるため、前記天然皮革３１に含まれる水分によって接着性が損なわれず、却って接着性を向上させることができることから、前記ホットメルト接着剤２１として好ましいものである。湿気硬化型ホットメルト接着剤としては、ウレタン系、ポリエステル系、アクリル系等のものがあるが、ウレタン系の湿気硬化型接着剤が扱い易さ、入手し易さ等の点から好ましい。具体的には、ウレタン系反応性ホットメルト接着剤であり、有機溶剤などの希釈剤が含まれない無溶剤系反応性熱溶融樹脂が、車両用途におけるＶＯＣ規格等を合格するうえで好ましい。この接着剤は、イソシアネート基末端のウレタンポリマーを主成分として、ポリオール成分はポリエステルポリオール、ポリエーテルポリオールなどが汎用に使用されるが、その他のポリオールでもよい。反応基としてイソシアネート基を有しているウレタン化合物であればよい。熱溶融温度は７０℃〜２００℃であり、好ましくは８０℃〜１６０℃が望ましい。
The
前記天然皮革３１は、前記表皮材１０の用途に応じて、牛革、豚革、カンガルー、ダチョウ、ワニほか爬虫類といった種類や厚み等が決定される。特に、牛革からなる天然皮革は、耐久性に優れることから好適なものである。天然皮革の厚みは、０．５〜３ｍｍとされる。
The type and thickness of the natural leather 31 such as cowhide, pig leather, kangaroo, ostrich, crocodile and reptiles are determined according to the application of the
前記表皮材１０の製造方法について説明する。前記表皮材１０の製造は、ホットメルト接着剤の塗布工程と、天然皮革の積層工程と、圧縮硬化工程とにより行われる。
The method of manufacturing the
ホットメルト接着剤の塗布工程では、前記樹脂発泡体１１の一側表面に、加熱により溶融した前記ホットメルト接着剤２１を塗布装置により塗布する。前記樹脂発泡体１１は、予め所定厚みのシート状にされ、下面（裏面）に前記裏基布１５が接着されている場合には、前記裏基布１５とは反対側の樹脂発泡体１１の表面に前記ホットメルト接着剤２１が塗布される。
In the hot melt adhesive application step, the hot melt adhesive 21 melted by heating is applied to one surface of the resin foam 11 by a coating device. The resin foam 11 is previously formed into a sheet having a predetermined thickness, and in the case where the
前記塗布装置としてロールコータを用いる場合を図２に示す。ロールコータ４０は、送りロール４１、供給ロール４２、塗布ロール４３、ホットメルト接着剤貯留槽４４を備える。
The case where a roll coater is used as the coating device is shown in FIG. The
前記送りロール４１は、前記樹脂発泡体１１の下方に配置されて前記樹脂発泡体１１の下面の前記裏基布１５と接触しながら一方向へ回転し、その回転により前記樹脂発泡体１１を一方向へ送る。
前記供給ロール４２と前記塗布ロール４３は、互いの回転軸を平行にし、かつ互いの外周面間に隙間を設けて、前記樹脂発泡体１１の上方に配置されている。前記供給ロール４２は、外周面が前記樹脂発泡体１１の上面と接することなく前記樹脂発泡体１１の送り方向とは逆方向へ回転する。一方、前記塗布ロール４３は、外周面と前記樹脂発泡体１１の上面との距離（クリアランス）を所定量にして前記樹脂発泡体１１の送り方向へ回転する。また、前記供給ロール４２と塗布ロール４３は、外周面が加熱可能に構成されている。
The feed roll 41 is disposed below the resin foam 11 and rotates in one direction while being in contact with the
The
前記ホットメルト接着剤貯留槽４４は、下端の吐出部４５が前記供給ロール４２と前記塗布ロール４３間の上方に位置するように配置され、内部に収容された前記ホットメルト接着剤２１をヒーター等の加熱手段で加熱して溶融状態で貯留する。
The hot melt adhesive storage tank 44 is disposed such that the discharge portion 45 at the lower end is located above the
前記ホットメルト接着剤貯留槽４４に貯留されている溶融状態のホットメルト接着剤２１は、前記送りロール４１によって前記樹脂発泡体１１が一方向へ送られている状態で、前記吐出部４５から前記供給ロール４２と前記塗布ロール４３間に供給される。前記供給ロール４２と前記塗布ロール４３間に供給された溶融状態のホットメルト接着剤２１は、前記供給ロール４２と前記塗布ロール４３の回転によって前記樹脂発泡体１１の上側表面に供給される。前記樹脂発泡体１１の上側表面に供給された溶融状態のホットメルト接着剤２１は、回転する塗布ロール４３の外周面下端と接触して前記樹脂発泡体１１の上側表面に塗布される。
The molten hot melt adhesive 21 stored in the hot melt adhesive storage tank 44 is fed from the discharge unit 45 while the resin foam 11 is fed in one direction by the feed roll 41. It is supplied between the
なお、前記樹脂発泡体１１に対する前記ホットメルト接着剤２１の塗布量は、前記ホットメルト接着剤貯留槽４４と前記供給ロール４２及び前記塗布ロール４３の加熱温度によるホットメルト接着剤２１の溶融粘度の調節、前記供給ロール４２と前記塗布ロール４３の回転速度、前記塗布ロール４３の外周面と前記樹脂発泡体１１の上面との距離（クリアランス）、前記樹脂発泡体１１の送り速度によって調節することができる。
The application amount of the hot melt adhesive 21 to the resin foam 11 is the melt viscosity of the hot melt adhesive 21 depending on the heating temperature of the hot melt adhesive storage tank 44, the
天然皮革の積層工程では、図３に示すように溶融状態の前記ホットメルト接着剤２１を挟んで前記樹脂発泡体１１の表面に前記天然皮革３１を積層する。図３に示す実施形態では、溶融状態の前記ホットメルト接着剤２１が塗布された樹脂発泡体１１を、プレス装置の下型５１の上面に載置した後、溶融状態の前記ホットメルト接着剤２１の上に、前記天然皮革３１を裏面が下向きとなるようにして積層する。なお、符号５２はプレス装置の上型である。
In the step of laminating natural leather, as shown in FIG. 3, the natural leather 31 is laminated on the surface of the resin foam 11 with the hot melt adhesive 21 in a molten state interposed therebetween. In the embodiment shown in FIG. 3, after the resin foam 11 to which the hot melt adhesive 21 in a molten state is applied is placed on the upper surface of the lower die 51 of the press, the hot melt adhesive 21 in the molten state is The natural leather 31 is laminated on top of the other with the back surface facing downward. In addition, the code |
圧縮硬化工程では、図４に示すように前記樹脂発泡体１１の上側表面に溶融状態の前記ホットメルト接着剤２１を挟んで前記天然皮革３１が積層された積層体１０Ａを圧縮し、前記ホットメルト接着剤２１を硬化させて前記天然皮革３１と前記樹脂発泡体１１が接着した前記表皮材１０を形成する。前記圧縮は、前記ホットメルト接着剤２１の融点より低い温度で行われる。例えば常温で行う。なお、常温とは、日本工業規格で規定されている２０±１５℃の範囲をいう。また、圧縮程度は特に限定されず、例えば総厚みの４０〜８０％となるように圧縮する。
In the compression curing step, as shown in FIG. 4, the laminated body 10A in which the natural leather 31 is laminated is compressed by sandwiching the hot melt adhesive 21 in a molten state on the upper surface of the resin foam 11; The adhesive 21 is cured to form the
前記ホットメルト接着剤２１は、前記圧縮中に自然冷却されて硬化し、前記天然皮革３１と前記樹脂発泡体１１を接着する。また、前記ホットメルト接着剤２１は、湿気硬化型ホットメルト接着剤の場合、自然冷却と空気中の湿気及び前記天然皮革３１から自然放出される湿気によって硬化が進行し、前記天然皮革３１と前記樹脂発泡体１１の接着が強固なものとなる。 The hot melt adhesive 21 is naturally cooled and hardened during the compression to bond the natural leather 31 and the resin foam 11. Further, in the case of a moisture curing type hot melt adhesive, the curing of the hot melt adhesive 21 proceeds by natural cooling, moisture in the air, and moisture naturally released from the natural leather 31, and the natural leather 31 and the above-mentioned natural leather 31 Adhesion of the resin foam 11 becomes strong.
前記圧縮工程では、前記ホットメルト接着剤２１を溶融させるための高温加熱を行わないため、前記天然皮革３１の表面のシボが伸びたり、天然皮革３１本来の意匠性が損なわれたりすることがなく、良好な風合いの表皮材１０が得られる。さらに、前記裏基布１５が熱によって劣化することがなく、良好な品質の表皮材１０が得られる。
In the compression step, high temperature heating for melting the hot melt adhesive 21 is not performed, so that the emboss of the surface of the natural leather 31 does not extend, and the original design property of the natural leather 31 is not lost. The
図５に第２実施形態の表皮材６０を示す。第２実施形態の表皮材６０は、第１実施形態の表皮材１０における前記裏基布１５を有しないものであり、他の構成は第１実施形態の表皮材１０と同様の構成からなる。符号６１は樹脂発泡体、７１はホットメルト接着剤、８１は天然皮革である。
第２実施形態の表皮材６０の製造方法は、前記第１実施形態の表皮材１０の製造方法において、前記樹脂発泡体１１の下側表面に裏基布１５が接着されていないことを除き、第１実施形態の表皮材１０の製造方法と同様である。
The
The method of manufacturing the
・実施例１〜３（湿気硬化型ホットメルト接着剤、裏基布有り）
密度３０ｋｇ／ｍ３、硬さ（ＪＩＳ Ｋ６４００−２：２０１２）５０Ｎ、セル数（ＪＩＳ Ｋ６４００−１：２００４）４２個／２５ｍｍ、品番：ＥＬ−６８ＷＳ、イノアックコーポレーション社製のポリエーテル系の軟質スラブポリウレタン発泡体を、２５０×４００ｍｍ×厚み１０ｍｍにして樹脂発泡体として使用し、裏面にナイロントリコットの１５デニールを裏基布としてアクリル系エマルジョン接着剤で接着した。
Examples 1 to 3 (moisture curing type hot melt adhesive, with back base cloth)
Density 30 kg / m 3 Hardness (JIS K 6400-2: 2012) 50 N Cell number (JIS K 6400-1: 2004) 42 pieces / 25 mm, product number: EL-68WS, polyether-based soft slab manufactured by Inoac Corporation The polyurethane foam was used as a resin foam in a size of 250 × 400 mm ×
ホットメルト接着剤として、ウレタン系の湿気硬化型接着剤、日立化成ポリマー株式会社製のポリウレタン系ホットメルト湿気硬化型樹脂、ハイボン、溶融塗布温度：１５０℃を用い、前記ロールコータ４０によって１５０℃に加熱して溶融させた状態で樹脂発泡体の裏基布とは反対側の表面に塗布し付着させた。前記ホットメルト接着剤貯留槽４４に貯留したホットメルト接着剤の温度、前記供給ロール４２と前記塗布ロール４３の温度は何れも８０℃であり、前記供給ロール４２と前記塗布ロール４３の回転速度及び前記クリアランスの値を固定し、樹脂発泡体の送り速度を４〜６ｍ／分で変化させて表１に示す実施例１〜３の付着量（塗布量）とした。
As a hot melt adhesive, a urethane-based moisture-curable adhesive, a polyurethane-based hot-melt moisture-curable resin manufactured by Hitachi Chemical Polymer Co., Ltd., HIBON, a melt coating temperature: 150 ° C., 150 ° C. by the
次に、プレス下型上にホットメルト接着剤を上向きにして樹脂発泡体を載置し、樹脂発泡体表面のホットメルト接着剤を挟んで天然皮革（牛革）を樹脂発泡体に積層し、プレス上型を下降させて圧縮し、表１に示す実施例１〜３の表皮材を形成した。なお圧縮は常温で４０秒間行い、圧縮量は６０％に設定した。 Next, the resin foam is placed on the press lower mold with the hot melt adhesive facing upward, the natural leather (cowhide) is laminated on the resin foam with the hot melt adhesive on the surface of the resin foam, and the press is performed. The upper mold was lowered and compressed to form the skin materials of Examples 1 to 3 shown in Table 1. The compression was performed at normal temperature for 40 seconds, and the amount of compression was set to 60%.
・参考例４（通常タイプホットメルト接着剤、裏基布有り）
ホットメルト接着剤として、アイカ工業社製酢酸ビニル系ホットメルト接着剤、品名：Ａ−ＱＮＪを用い、樹脂発泡体及び裏基布を実施例１〜３と同一とし、前記ホットメルト接着剤貯留槽４４に貯留したホットメルト接着剤の温度及び前記供給ロール４２と前記塗布ロール４３の温度を９５℃とし、前記供給ロール４２と前記塗布ロール４３の回転速度及び前記クリアランスの値を固定し、樹脂発泡体の送り速度を調節して表１の参考例４の付着量（塗布量）にした。その他は実施例１〜３と同様にして表１に示す参考例４の表皮材を形成した。
・ Reference example 4 (normal type hot melt adhesive, with back base cloth)
As a hot melt adhesive, using a vinyl acetate-based hot melt adhesive manufactured by Aika Kogyo Co., Ltd., product name: A-QNJ, the resin foam and the back base cloth are made the same as in Examples 1 to 3, and the hot melt adhesive storage tank 44. The temperature of the hot melt adhesive stored in 44 and the temperature of the
・比較例１（不織布タイプのホットメルト接着剤、裏基布有り）
ウェブ状ホットメルト接着剤（不織布タイプのホットメルト接着剤）として、スパンボンド不織布、目付：２５ｇ／ｍ２、融点：１１５℃、品番：ダイナックＬＮＳ１２２５、呉羽テック社製を使用し、樹脂発泡体及び裏基布を実施例１〜３と同一とし、プレス下型上に樹脂発泡体を裏基布が下側となるようにして載置し、樹脂発泡体の上側表面にホットメルト接着剤を配置し、そのホットメルト接着剤を挟んで天然皮革（牛革）を積層し、プレス上型を下降させて加熱圧縮し、表１に示す比較例１の表皮材を形成した。なおプレス下型は常温、上型は１９０℃で４０秒間行い圧縮量は５０％に設定した。
Comparative example 1 (non-woven type hot melt adhesive, with back base cloth)
As a web-like hot melt adhesive (non-woven type hot melt adhesive), spun bond non-woven fabric, fabric weight: 25 g / m 2 , melting point: 115 ° C., product number: DINAC LNS 1225, manufactured by Toha Tech Co., Ltd., resin foam and The back base cloth is made the same as in Examples 1 to 3, and the resin foam is placed on the press lower mold so that the back base cloth is on the lower side, and the hot melt adhesive is placed on the upper surface of the resin foam. Then, natural leather (cowhide) was laminated on both sides of the hot melt adhesive, and the upper die was lowered and heated and compressed to form the skin material of Comparative Example 1 shown in Table 1. The press mold was at normal temperature, the upper mold was at 190 ° C. for 40 seconds, and the compression was set to 50%.
・実施例５〜７（湿気硬化型ホットメルト接着剤、裏基布無し）
密度３０ｋｇ／ｍ３、硬さ（ＪＩＳ Ｋ６４００-２：２０１２）７０Ｎ、セル数（ＪＩＳ Ｋ６４００-１：２００４）２５個／２５ｍｍ、品番：ＷＦ−１８、イノアックコーポレーション社製のポリエーテル系の軟質スラブポリウレタン発泡体を、２５０×４００ｍｍ×厚み１０ｍｍにして樹脂発泡体として使用し、裏基布は設けなかった。実施例１〜３と同じホットメルト接着剤を使用し、実施例１〜３と同様にして樹脂発泡体の一側表面に溶融状態のホットメルト接着剤を、表２の実施例５〜７に示す付着量で付着（塗布）した。
Examples 5 to 7 (moisture-setting hot melt adhesive, without back backing)
Density 30 kg / m 3 , hardness (JIS K 6400-2: 2012) 70 N, cell number (JIS K 6400-1: 2004) 25/25 mm, part number: WF-18, soft polyether-based slab made by Inoac Corporation The polyurethane foam was used as a resin foam in a size of 250 × 400 mm ×
次に、プレス下型上にホットメルト接着剤を上向きにして樹脂発泡体を載置し、樹脂発泡体表面のホットメルト接着剤を挟んで天然皮革（牛革）を樹脂発泡体に積層し、プレス上型を下降させて圧縮し、表２に示す実施例５〜７の表皮材を形成した。なお圧縮は常温で４０秒間行い、圧縮量は５０％に設定した。 Next, the resin foam is placed on the press lower mold with the hot melt adhesive facing upward, the natural leather (cowhide) is laminated on the resin foam with the hot melt adhesive on the surface of the resin foam, and the press is performed. The upper mold was lowered and compressed to form the skin materials of Examples 5 to 7 shown in Table 2. In addition, compression was performed at normal temperature for 40 seconds, and the amount of compression was set to 50%.
・参考例８（通常タイプホットメルト接着剤、裏基布無し）
ホットメルト接着剤として、アイカ工業社製酢酸ビニル系ホットメルト接着剤、品名：Ａ−ＱＮＪを用い、樹脂発泡体を実施例５〜７と同一とし、前記ホットメルト接着剤貯留槽４４に貯留したホットメルト接着剤の温度及び前記供給ロール４２と前記塗布ロール４３の温度を１３０℃とし、前記供給ロール４２と前記塗布ロール４３の回転速度及び前記クリアランスの値を固定し、樹脂発泡体の送り速度を５ｍ／分にして表２の参考例８の付着量（塗布量）にした。その他は実施例５〜７と同一にして表２に示す参考例８の表皮材を形成した。
Reference Example 8 (Normal Type Hot Melt Adhesive, No Back Base Cloth)
As a hot melt adhesive, using a vinyl acetate-based hot melt adhesive manufactured by Aika Kogyo Co., Ltd., product name: A-QNJ, the resin foam was made the same as in Examples 5 to 7, and stored in the hot melt adhesive storage tank 44. The temperature of the hot melt adhesive and the temperature of the
・比較例２（不織布ホットメルト接着剤、裏基布無し）
ウェブ状ホットメルト接着剤として、スパンボンド不織布、目付：２５ｇ／ｍ２、融点：１１５℃、品番：ダイナックＬＮＳ１２２５、呉羽テック社製を使用し、樹脂発泡体を実施例５〜７と同一のものを使用し、プレス下型上に樹脂発泡体を載置し、樹脂発泡体の表面にホットメルト接着剤を配置し、そのホットメルト接着剤を挟んで天然皮革（牛革）を積層し、プレス上型を下降させて加熱圧縮し、表２に示す比較例２の表皮材を形成した。なおプレス下型は常温、上型は１９０で４０秒間行い、圧縮量は５０％に設定した。
・ Comparative example 2 (non-woven fabric hot melt adhesive, without back backing)
As a web-like hot melt adhesive, spun bond non-woven fabric, fabric weight: 25 g / m 2 , melting point: 115 ° C., product number: Dynak LNS 1225, manufactured by Toha Tech Co., Ltd., resin foam is the same as Examples 5 to 7 Place the resin foam on the press lower mold, place the hot melt adhesive on the surface of the resin foam, laminate the natural leather (cowhide) with the hot melt adhesive, and press it on the press The mold was lowered and heated and compressed to form a skin material of Comparative Example 2 shown in Table 2. The pressing was performed at room temperature for the lower die and at 190 for the upper die for 40 seconds, and the amount of compression was set to 50%.
各実施例、各参考例及び各比較例の表皮材に対し、剥離強度、硬さ、外観、収縮、耐熱性接着強度を測定した。測定結果を表１及び表２に示す。 Peeling strength, hardness, appearance, shrinkage, and heat resistant adhesive strength were measured for the skin materials of Examples, Reference Examples, and Comparative Examples. The measurement results are shown in Tables 1 and 2.
剥離強度（単位Ｎ／２５ｍｍ）は、ＪＩＳ Ｋ ６８５４-２（接着剤−はく離接着強さ試験方法、第二部：１８０度剥離）に基づいて測定した。試験回数ｎは３。表皮材は、２５０ｍｍ×４００ｍｍに切り出すが、４００ｍｍの方向をタテとし、２５０ｍｍの方向をヨコとした。測定数値に併記されている「＊」は、接着強度が高くて剥離面が破壊したことを示す。
硬さ（単位Ｎ）は、プッシュプルゲージ（ＦＳプローブ）に基づいて測定した。数値が大ほど硬くなる。硬さの測定は、直径１０ｍｍの半球形状の当接部のあるプッシュプルシャフトを中心に備え、直径５０ｃｍの中空円盤で試料を垂直に位置させるプッシュプルゲージ（株式会社ＳＵＮＴＥＸ製、ＦＳ１００）を垂直に立て、上記当接部を試料側へ押し下げて数値を読み取った。
外観は、天然皮革の表面についてシボが減少しているか、見苦しいアバタ（凹凸）が発生しているかを目視で観察した。「シボ減少」の観察結果における「×」はシボの明確な減少が見られたことを示し、「〇」はシボの減少が見られないことを示す。「アバタ」の観察結果における「△」は見苦しいアバタ（凹凸）が部分的に見られたことを示し、「〇」は見苦しいアバタ（凹凸）が見られなかったことを示す。
Peeling strength (unit N / 25 mm) was measured based on JIS K 6854-2 (adhesive-peeling adhesive strength test method, part 2: 180 degree peeling). The number of tests n is three. The surface material was cut into 250 mm × 400 mm, but the direction of 400 mm was vertical and the direction of 250 mm was horizontal. The symbol “*” attached to the measured values indicates that the adhesive strength is high and the peeling surface is broken.
The hardness (unit N) was measured based on a push-pull gauge (FS probe). The larger the number, the harder it is. The hardness is measured by using a push-pull gauge (SUNTEX, FS100), which has a 50-mm diameter hollow disk with a push-pull shaft with a semi-spherical abutment of 10 mm in diameter, centered on a 50-cm diameter hollow disk. The above contact part was pushed down to the sample side to read the numerical value.
The appearance was visually observed whether the surface of the natural leather had wrinkles reduced or unsightly avatars (concave and convex) were generated. The “x” in the “shrinking reduction” observation indicates that a clear reduction in embossing was observed, and the “o” means that no embossing reduction was observed. "△" in the observation result of "avatar" indicates that unsightly avatar (concave and convex) was partially observed, and "o" indicates that unsightly avatar (concave and convex) was not observed.
収縮（ｍｍ）は、実際に成形した試料の収縮量を測定した。実施例でも、比較例でも、所定形状に切り出した成形前の原料革を標準として用意し、接着剤を溶融塗布した後、常温でプレスした後の樹脂発泡体が積層された原料革の収縮量を測定した。標準となる表皮材の大きさとして、２５０ｍｍ×４００ｍｍに切り出し、４００ｍｍの方向をタテとし、２５０ｍｍの方向をヨコとした。測定結果における「〇」は、タテ方向、ヨコ方向のいずれにおいても、積層された表皮材として使用可能な範囲内の３ｍｍ未満の収縮であることを示し、「×」は、標準となる原料革に対して、積層された表皮材に発生する収縮差が、３ｍｍ以上を超える収縮であることを示す。 Shrinkage (mm) was measured for the amount of shrinkage of the actually molded sample. In both the example and the comparative example, the amount of shrinkage of the raw material leather on which the resin foam is laminated after preparing the raw material leather before molding cut into a predetermined shape as a standard, melt-applying the adhesive and pressing at normal temperature Was measured. As a size of the surface material which becomes a standard, it cut out to 250 mm x 400 mm, made the direction of 400 mm vertical, and made the direction of 250 mm horizontal. “O” in the measurement result indicates that the shrinkage is less than 3 mm in the usable range as a laminated skin material in any of the vertical direction and the horizontal direction, and “x” is the standard raw material leather as a standard On the other hand, the shrinkage difference generated in the laminated skin material is a shrinkage exceeding 3 mm or more.
耐熱性接着強度は、剥離試験用の試験片、幅２５ｍｍ、長さ１７５ｍｍを用意し、７５ｍｍを残して剥離し、剥離した表皮材の端に１０ｇの重りを取付け、剥離されていない試験片の一端を上端として垂下し、１４０℃の恒温槽に２４時間、放置することで、耐熱性接着強度を測定した。試験に合格するものは「〇」とし、剥離された距離が、５ｍｍ未満で重りが釣り下がったままだった。試験に不合格のものは「×」とし、試験終了時には試験片が剥離し、重りが落下していた。 Heat resistant adhesive strength prepares a test piece for peeling test, width 25 mm, length 175 mm, peels leaving 75 mm, attaches a 10 g weight to the end of peeled skin material, and does not peel the test piece The heat-resistant adhesive strength was measured by hanging down with one end as an upper end and leaving it to stand in a thermostat at 140 ° C. for 24 hours. Those who passed the test were marked with "o", and the peeled distance was less than 5 mm, and the weight remained at the bottom. Those that failed the test were marked "x", and at the end of the test, the test piece peeled off and the weight dropped.
表１及び表２に示すように、ホットメルト接着剤を溶融して樹脂発泡体側に付着した各実施例の表皮材は、天然皮革と樹脂発泡体の剥離強度が高く、硬さも柔らかく、天然皮革の外観が良好で、収縮が小さく、自動車、鉄道、航空機、家具等の座席や内装材等の表皮材として好適なものである。また、裏基布を有する実施例１〜３及び参考例４は裏基布に熱による劣化がなく、良好な品質であった。さらに、湿気硬化型の接着剤を使用した場合、高温環境下における剥離強度（耐熱性接着強度）が強く、耐久性があった。
一方、ホットメルト接着剤として不織布を使用し、天然皮革を積層した後に加熱プレスした各比較例は、天然皮革と樹脂発泡体の剥離強度が低く、硬さも硬く、天然皮革表面のシボが減少し、かつ見苦しいアバタが発生して天然皮革の風合いが損なわれ、しかも収縮が大きく、自動車、鉄道、航空機、家具等の座席や内装材等の表皮材としては不向きである。
As shown in Tables 1 and 2, the surface material of each example in which the hot melt adhesive is melted and attached to the resin foam side has high peel strength between natural leather and resin foam, and the hardness is also soft, and the natural leather It has a good appearance, a small shrinkage, and is suitable as a seat material for automobiles, railways, aircraft, furniture, etc., and as a skin material for interior materials and the like. In addition, Examples 1 to 3 and Reference Example 4 having the back base cloth had no deterioration due to heat in the back base cloth, and were of good quality. Furthermore, when a moisture curing type adhesive was used, the peel strength (heat resistant adhesive strength) under high temperature environment was strong and durable.
On the other hand, each comparative example which uses a non-woven fabric as a hot melt adhesive and heat-presses after laminating natural leather has low peel strength between natural leather and resin foam, hard hardness, and reduced emboss on the surface of natural leather In addition, an unsightly avatar is generated to impair the texture of natural leather, and the shrinkage is large, which is unsuitable as a surface material such as a seat for car, railway, aircraft, furniture, etc. and an interior material.
１０、６０ 表皮材
１０Ａ 積層体
１１、６１ 樹脂発泡体
１５ 裏基布
２１、７１ ホットメルト接着剤
３１、８１ 天然皮革
４０ ロールコータ
４１ 送りロール
４２ 供給ロール
４３ 塗布ロール
４４ ホットメルト接着剤貯留槽
Claims (7)
前記天然皮革の積層後に常温で圧縮する工程と、
前記圧縮中に空気中の湿気と前記天然皮革から自然放出される湿気により前記湿気硬化型ホットメルト接着剤を硬化させる工程とを含むことを特徴とする表皮材の製造方法。 The moisture curable hot melt adhesive melted by heating is applied to the surface of the resin foam exposed by cutting the cell skeleton and becoming uneven, and the resin is sandwiched between the moisture curable hot melt adhesive in a molten state. A method for producing a skin material, comprising laminating a water-containing natural leather on the surface of a foam, comprising:
Compressing at normal temperature after laminating the natural leather;
Curing the moisture-curable hot melt adhesive with moisture in the air and moisture spontaneously released from the natural leather during the compression.
前記天然皮革の積層に際し、溶融状態の前記ホットメルト接着剤が塗布された前記樹脂発泡体を下型の上面に載置した後、溶融状態の前記ホットメルト接着剤の上に、前記天然皮革を裏面が下向きとなるように積層して積層体とする工程を行い、
前記圧縮する際に、上型により、前記積層体を常温で圧縮する工程と、前記ホットメルト接着剤を、空気中の湿気と前記天然皮革から自然放出される湿気により硬化させる工程を行うことを特徴とする請求項５または６に記載の表皮材の製造方法。 At the time of application of the moisture-curable hot melt adhesive, from the discharge portion of the adhesive storage tank, in a state where the resin foam is fed in one direction by a feed roll positioned on the lower surface side of the resin foam. A hot-melt adhesive in a molten state supplied and stored between an adhesive supply roll and an application roll is made of the resin foam by rotation of the supply roll and the application roll at a temperature lower than the melting temperature of the adhesive. The step of causing the hot melt adhesive in a molten state to engage with the asperities exposed on the upper surface of the resin foam is performed by supplying and applying the upper surface.
After the resin foam to which the hot melt adhesive in a molten state is applied is placed on the upper surface of the lower mold when laminating the natural leather, the natural leather is placed on the hot melt adhesive in a molten state. Performing a process of laminating to form a laminate so that the back surface is facing downward,
At the time of the compression, a step of compressing the laminate at a normal temperature by an upper mold and a step of curing the hot melt adhesive by moisture in the air and moisture spontaneously released from the natural leather are performed. The manufacturing method of the surface material of Claim 5 or 6 characterized by the above-mentioned.