JP6497132B2 - 空気入りタイヤ - Google Patents
空気入りタイヤ Download PDFInfo
- Publication number
- JP6497132B2 JP6497132B2 JP2015040835A JP2015040835A JP6497132B2 JP 6497132 B2 JP6497132 B2 JP 6497132B2 JP 2015040835 A JP2015040835 A JP 2015040835A JP 2015040835 A JP2015040835 A JP 2015040835A JP 6497132 B2 JP6497132 B2 JP 6497132B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- rubber
- parts
- belt
- tire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
53〜63である。ベルトクッション用ゴム組成物のゴム硬度が50未満であると、ショルダー部の歪量増加によりタイヤ耐久性が低下する。またゴム硬度が65を超えるとクッション性の低下によりタイヤ耐久性が低下する。本明細書において、ベルトクッション用ゴム組成物のゴム硬度は、JIS K6253に準拠しデュロメータのタイプAにより温度20℃で測定するゴムの硬さをいう。
得られた試験片のゴム硬度を、JIS K6253に準拠しデュロメータのタイプAにより温度20℃で測定した。得られた結果は、表1,2の「ゴム硬度」の欄に示した。
得られた試験片の動的粘弾性を、レオメトリックス社製RDA−IIを用いて、初期歪み10%、振幅±2%、周波数20Hzで測定し、雰囲気温度60℃におけるtanδを測定した。得られた結果は、比較例1の値を100とする指数にして表1,2の「tanδ(60℃)」の欄に示した。この値が小さいほどtanδ(60℃)が小さく、タイヤにしたとき転がり抵抗が小さく燃費性能が優れることを意味する。
得られた試験片の耐亀裂成長性をJIS K6260に準拠しデマッチャ屈曲試験機により温度20℃で測定した。ストローク57mm、速度300±10rpmの条件で、屈曲回数10万回後の亀裂成長[単位mm]を測定した。得られた結果は、比較例1の逆数を100とする指数にして表1,2の「耐亀裂成長性」の欄に示した。この指数が大きいほど亀裂成長が小さく、耐クラック性が優れることを意味する。
湿熱試験後のタイヤカットサンプルについて、ベルトクッションとカーカス層とを引き剥がすときの剥離力を測定した。得られた結果は、比較例1の値を100とする指数にして表1,2の「耐剥離性」の欄に示した。この指数が大きいほど、ベルトクッションおよびカーカス層の接着性が高く優れることを意味する。
湿熱試験後のタイヤカットサンプルについて、カーカス層の被覆ゴムを引き剥がし、スチールコードに付着するゴム量を評価した。得られた結果は、比較例1の値を100とする指数にして表1,2の「ゴム付き」の欄に示した。この指数が大きいほど、スチールコードへのゴム付きが多く優れることを意味する。
得られた空気入りタイヤをJATMA標準リムに取り付け、酸素67.5%、空気22.5%をタイヤ内圧で850kPaに充填した。このタイヤをJIS D4230に準拠する室内ドラム試験機(ドラム径1707mm)にかけて、荷重を標準荷重の170%、速度40km/h、温度30℃で、故障が起きるまで走行させ、走行距離を求めた。得られた結果は、比較例1の値を100とする指数にして表1,2の「タイヤ耐久性」の欄に示した。この指数が大きいほど、故障が起きるまでの走行距離が長く、タイヤ耐久性が優れることを意味する。
・NR:天然ゴム、TSR20
・BR:ブタジエンゴム、日本合成ゴム社製Nipol BR1220
・カーボンブラック:キャボットジャパン社製ショウブラックN330T、窒素吸着比表面積が79m2/g
・プロセスオイル:昭和シェル石油社製エキストラクト4号S
・酸化亜鉛:正同化学社製酸化亜鉛3種
・ステアリン酸:NOFコーポレーション社製ステアリン酸YR
・老化防止剤:Solutia Europe社製Santoflex 6PPD
・硫黄:軽井沢製錬所製印処理イオウ
・加硫促進剤:大内新興化学社製ノクセラーNS
2 サイドウォール部
3 ショルダー部
4 カーカス層
5 ベルト層
6 インナーライナー層
7 ベルトクッション
T 空気入りタイヤ
Claims (4)
- スチールコードからなるカーカス層のタイヤ径方向外側に、スチールコードからなる複数のベルト層が配置され、該ベルト層のタイヤ幅方向外側端部と前記カーカス層との間およびそのタイヤ幅方向外側にベルトクッションを有する空気入りタイヤであって、前記ベルトクッションが、ブタジエンゴム5〜50重量%を含むジエン系ゴム100重量部に、脂肪酸を0.8〜1.6重量部、加硫促進剤を0.3〜1.2重量部配合したベルトクッション用ゴム組成物により構成され、かつそのゴム硬度が50〜65であることを特徴とする空気入りタイヤ。
- 前記ベルトクッション用ゴム組成物が、前記ジエン系ゴム100重量部に対し、亜鉛華を2.0〜5.0重量部配合したことを特徴とする請求項1に記載の空気入りタイヤ。
- 前記ベルトクッション用ゴム組成物が、窒素吸着比表面積が40〜100m2/gであるカーボンブラックを、前記ジエン系ゴム100重量部に対し20〜45重量部配合したことを特徴とする請求項1または2に記載の空気入りタイヤ。
- 前記ベルトクッション用ゴム組成物が、硫黄を前記ジエン系ゴム100重量部に対し2.0〜6.0重量部配合したことを特徴とする請求項1〜3のいずれかに記載の空気入りタイヤ。