JP6496143B2 - 絶縁電線 - Google Patents
絶縁電線 Download PDFInfo
- Publication number
- JP6496143B2 JP6496143B2 JP2014266519A JP2014266519A JP6496143B2 JP 6496143 B2 JP6496143 B2 JP 6496143B2 JP 2014266519 A JP2014266519 A JP 2014266519A JP 2014266519 A JP2014266519 A JP 2014266519A JP 6496143 B2 JP6496143 B2 JP 6496143B2
- Authority
- JP
- Japan
- Prior art keywords
- thermal expansion
- layer
- foaming agent
- matrix
- insulated wire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の一態様に係る絶縁電線は、線状の導体と、この導体の外周面側に被覆される絶縁層と、この絶縁層の外周面側に積層され、加熱により膨張する熱膨張層とを備える絶縁電線であって、上記熱膨張層が合成樹脂を主成分とするマトリックス及びこのマトリックス中に分散する発泡剤を有し、上記発泡剤の発泡開始温度での上記マトリックスの弾性率が1kPa以上1×104kPa以下である。
以下、本発明に係る絶縁電線の各実施形態について図面を参照しつつ詳説する。
導体1は、例えば断面が円形状の丸線とされるが、断面が正方形状の角線又は長方形状の平角線や、複数の素線を撚り合わせた撚り線であってもよい。
絶縁層2は、絶縁性を有する樹脂組成物で形成される。絶縁層2を形成する樹脂組成物としては、特に限定されないが、例えばポリビニルホルマール、熱硬化ポリウレタン、熱硬化アクリル、エポキシ樹脂、熱硬化ポリエステル、熱硬化ポリエステルイミド、熱硬化ポリエステルアミドイミド、芳香族ポリアミド、熱硬化ポリアミドイミド、熱硬化ポリイミド等の熱硬化性樹脂や、例えば熱可塑性ポリイミド、ポリフェニルサルフォン、ポリフェニレンスルフィド、ポリエーテルイミド、ポリエーテルエーテルケトン、ポリエーテルサルフォン等の熱可塑性樹脂を主成分とするものが使用できる。絶縁層2は2種類以上の樹脂の複合体又は積層体であってもよく、また熱硬化性樹脂と熱可塑性樹脂との複合体又は積層体であってもよい。
熱膨張層3は、合成樹脂を主成分とするマトリックス4と、このマトリックス4中に分散する発泡剤5とを有する。
熱膨張層3のマトリックス4は、合成樹脂を主成分とし、発泡剤5の発泡開始温度で流動性を示す絶縁性の樹脂組成物で構成される。つまり、マトリックス4を構成する樹脂組成物のガラス転移温度は、発泡剤5の発泡開始温度に近く、例えば100℃以上350℃以下である。このように、マトリックス4が発泡剤5の発泡温度領域において流動性を示す樹脂であることによって、熱膨張層3の膨張を均一にできると共に膨張率を所望の値に制御することが容易となる。
発泡剤5としては、化学発泡剤又は熱膨張性マイクロカプセルを用いることができる。
発泡剤5として用いられる化学発泡剤は、加熱することにより分解して、例えば窒素ガス、炭酸ガス、一酸化炭素、アンモニアガス等を発生するものであり、有機発泡剤又は無機発泡剤が使用できる。
発泡剤5として用いられる熱膨張性マイクロカプセルは、内部発泡剤からなる芯材(内包物)と、この芯材を包む外殻とを有し、芯材の膨張によって外殻が膨張する。
当該絶縁電線は、絶縁層2の主成分が熱硬化性樹脂であり、マトリックス4の主成分が熱可塑性である場合、導体1の外周面側に絶縁層形成用樹脂組成物を塗布する工程と、加熱により塗布した絶縁層形成用樹脂組成物を硬化する工程と、硬化した絶縁層形成用樹脂組成物の外周面側に、低沸点溶媒で希釈したマトリックス4中に発泡剤5を分散した熱膨張層形成用組成物を塗布する工程と、低沸点溶媒を揮発させて熱膨張層形成用組成物を乾燥する工程と備える方法により製造できる。
絶縁層形成用樹脂組成物塗布工程では、導体1の外周面側に絶縁層形成用樹脂組成物を塗布する。絶縁層形成用樹脂組成物を導体1の外周面側に塗布する方法としては、例えば液状の絶縁層形成用樹脂組成物を貯留した液状組成物槽と塗布ダイスとを備える塗布装置を用いた方法を挙げることができる。この塗布装置によれば、導体1が液状組成物槽内を挿通することで液状組成物が導体外周面側に付着し、その後塗布ダイスを通過することで、この液状組成物が略均一な厚さに塗布される。なお、この絶縁層形成用樹脂組成物の塗布に先駆けて導体1の外周面にプライマー処理層を公知の方法で形成してもよい。
絶縁層形成用樹脂組成物硬化工程では、加熱することによって絶縁層形成用樹脂組成物を硬化させて、絶縁層2を形成する。この加熱に用いる装置としては、特に限定されないが、例えば導体1の走行方向に長い筒状の焼き付け炉を用いることができる。加熱方法としては特に限定されないが、例えば熱風加熱、赤外線加熱、高周波加熱等、従来公知の方法により行うことができる。また、加熱温度としては、絶縁層形成用樹脂組成物に応じて適宜選択されるが、例えば300℃以上600℃以下とされる。
熱膨張層形成用組成物塗布工程では、マトリックス4を構成する樹脂組成物を上記マトリックス4中に含まれる揮発性溶剤よりもさらに低い沸点を有する低沸点溶媒で希釈した溶液に発泡剤5を分散した熱膨張層形成用組成物を、上記絶縁層2の外周面側に塗工する。熱膨張層形成用組成物の塗布方法としては、上記絶縁層形成用樹脂組成物塗布工程と同様とすることができる。
熱膨張層形成用組成物乾燥工程では、発泡剤5の膨張開始温度よりも低い温度で低沸点溶媒を蒸発させることにより、熱膨張層形成用組成物を乾燥して、熱膨張層3を形成する。乾燥方法としては、例えば熱風加熱、赤外線加熱、高周波加熱等、従来公知の方法により行うことができる。
当該絶縁電線は、熱膨張層3が合成樹脂を主成分とするマトリックス4中に発泡剤5を分散して形成されていることによって、発泡剤5の膨張に伴って確実かつ比較的均一に膨張することができる。
今回開示された実施の形態はすべての点で例示であって制限的なものではないと考えられるべきである。本発明の範囲は、上記実施形態の構成に限定されるものではなく、特許請求の範囲によって示され、特許請求の範囲と均等の意味及び範囲内でのすべての変更が含まれることが意図される。
プライマー処理層は、層間の密着性を高めるために設けられる層であり、例えば公知の樹脂組成物により形成することができる。
直径1.0mmの銅線に、平均厚さ40μmの絶縁層及び平均厚さ40μmの熱膨張層をこの順に積層することによって、絶縁電線No.1〜8を試作した。絶縁層及び熱膨張層は、それぞれ表1に記載する組成の樹脂組成物を塗布ダイスを用いて塗布し、炉長3mの横炉を用いて炉温200℃、線速4.8m/分の条件で乾燥(焼付)した。
絶縁層形成用樹脂組成物としては、ポリエステルイミドを主成分とするワニス、ポリアミドイミドを主成分とするワニス、ポリイミドを主成分とするワニス又はポリエーテルエーテルケトンを主成分とするワニスを使用した。
熱膨張層形成用組成物としては、合成樹脂を揮発性溶剤で溶解し低沸点溶媒で希釈したものを使用した。具体的には、マトリックスの主成分となる合成樹脂として、ガラス転移温度が130℃のポリヒドロキシポリエーテル(フェノキシ樹脂)(新日鉄住金社の「YPS−007A30」)をシクロヘキサノンで希釈したもの、ポリアミドイミドをN−メチルピロリドンで希釈したもの、ポリエステルイミドをクレゾールで希釈したもの又は耐熱ポリウレタンをクレゾールで希釈したものを使用した。熱膨張層形成用組成物のマトリックスの硬化剤としてはノボラック型エポキシ樹脂(新日鉄住金社の「YDCN−704」)又はポリイソシアネート(日本ポリウレタン工業社の「MILLIONATE MS−50」)を使用した。また、熱膨張層形成用組成物の発泡剤としては、発泡開始温度が190℃の化学発泡剤(永和化成工業社の「ビニホールAC#3C−K2」)又は発泡開始温度が180℃の熱膨張性マイクロカプセル(積水化学社の「EM501」)を使用した。
絶縁電線No.1〜8のマトリックスについて、別途、発泡剤を含まない状態でマトリックスを調整し、発泡開始温度での弾性率を測定した。絶縁電線No.1〜4のマトリックスは、発泡剤の発泡開始温度での弾性率が2.0kPaであった。絶縁電線No.5のマトリックスは、発泡剤の発泡開始温度での弾性率が1.0×10kPaであった。絶縁電線No.6のマトリックスは、発泡剤の発泡開始温度での弾性率が0.01kPaであった。絶縁電線No.7のマトリックスは、発泡剤の発泡開始温度での弾性率が10Paであった。なお、「弾性率」は、ユービーエム社の粘弾性測定装置「Rheo−Station」を用いて測定した。
絶縁電線No.1〜8について、加熱により熱膨張層を膨張させる前の可とう性及び絶縁性を確認し、良好であったものを「A」、不良であったものを「B」たとした。なお、可とう性は、20%伸長後に自己径巻きで捲線を30ターン巻付けて、割れ及び浮きがないか目視で確認し、割れ及び浮きがなければ良好とした。また、絶縁性は、絶縁破壊電圧をJIS−C3003−5(2011)に従い、2個撚り線の線間に交流電圧を加え500V/秒で昇圧し、絶縁破壊したときの電圧を測定し、この絶縁破壊電圧が規格値以上のものを良好とした。この結果、表1に示すように、絶縁電線No.1〜8のいずれも、可とう性及び絶縁性が共に良好であった。
絶縁電線No.1〜8を加熱して熱膨張層を膨張させる前後において、熱膨張層の平均厚さを測定し、平均厚さ膨張率を算出した。具体的には、180℃の熱風循環型恒温槽で2時間加熱することにより絶縁電線の熱発泡層を膨張させ、マイクロメーターで膨張前の線径と膨張後の線径とを測定することにより、熱膨張層の平均厚さ膨張率を算出した。表1に示すように、絶縁電線No.1〜6の熱膨張層は、適度に膨張したが、絶縁電線No.7は、まったく膨張しなかった。これは、絶縁電線No.7の熱膨張層のマトリックスの弾性率が1kPa以上に上昇する温度が発泡剤の膨張開始温度よりも高いことに起因すると考えられる。
加熱後の絶縁電線No.1〜7について、熱膨張層に形成された空孔の平均径を測定した。なお、この空孔の平均径の測定は、熱膨張層の断面をPorus Materials社の「多孔質材料自動細孔径分布測定システム」を用いて測定した。表1に示すように、絶縁電線No.1〜6の熱膨張層に形成される空孔の平均径は、100μmから130μmの範囲内であった。一方、上述のように加熱により膨張させることができなかった絶縁電線No.7は、空孔が形成されなかったので、空孔の平均径を測定することができなかった。
また、加熱後の絶縁電線No.1〜7について、上記膨張前後の平均厚さの測定値を基に、熱膨張層の空隙率を算出した。表1に示すように、絶縁電線No.1〜6の膨張後の熱膨張層の空隙率は、65%から76%の範囲内であった。一方、上述のように加熱により膨張させることができなかった絶縁電線No.7は、空孔が形成されなかったので空隙率は0%とされる。
2 絶縁層
3 熱膨張層
4 マトリックス
5 発泡剤
6 熱融着層
Claims (6)
- 線状の導体と、この導体の外周面側に被覆される絶縁層と、この絶縁層の外周面側に積層され、加熱により膨張する熱膨張層とを備える絶縁電線であって、
上記熱膨張層が合成樹脂を主成分とするマトリックス及びこのマトリックス中に分散する発泡剤を有し、
上記マトリックスが熱反応性硬化剤をさらに含有し、
上記合成樹脂がフェノキシ樹脂であり、
上記発泡剤の発泡開始温度での上記マトリックスの弾性率が1kPa以上1×104kPa以下であり、
上記熱膨張層の外周面側に熱融着層が積層される絶縁電線。 - 上記熱膨張層における発泡剤の含有率が1質量%以上15質量%以下である請求項1に記載の絶縁電線。
- 上記熱膨張層の加熱後の平均厚さ膨張率が1.1倍以上5倍以下である請求項1又は請求項2に記載の絶縁電線。
- 捲線加工及び加熱により巻線束を形成可能な請求項1、請求項2又は請求項3に記載の絶縁電線。
- 上記導体と上記絶縁層との間に第1プライマー処理層を有する請求項1から請求項4のいずれか1項に記載の絶縁電線。
- 上記絶縁層と上記熱膨張層との間に第2プライマー処理層を有する請求項1から請求項5のいずれか1項に記載の絶縁電線。