JP6492176B2 - 音響波プローブ用組成物、これを用いた音響波プローブ用シリコーン樹脂、音響波プローブおよび超音波プローブならびに音響波測定装置、超音波診断装置、光音響波測定装置および超音波内視鏡 - Google Patents
音響波プローブ用組成物、これを用いた音響波プローブ用シリコーン樹脂、音響波プローブおよび超音波プローブならびに音響波測定装置、超音波診断装置、光音響波測定装置および超音波内視鏡 Download PDFInfo
- Publication number
- JP6492176B2 JP6492176B2 JP2017526333A JP2017526333A JP6492176B2 JP 6492176 B2 JP6492176 B2 JP 6492176B2 JP 2017526333 A JP2017526333 A JP 2017526333A JP 2017526333 A JP2017526333 A JP 2017526333A JP 6492176 B2 JP6492176 B2 JP 6492176B2
- Authority
- JP
- Japan
- Prior art keywords
- acoustic wave
- polysiloxane
- group
- ultrasonic
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
例えば、超音波診断装置は、被検対象内部に向けて超音波を送信し、被検対象内部の組織で反射された超音波を受信し、画像として表示する。光音響波測定装置は、光音響効果によって被検対象内部から放射される音響波を受信し、画像として表示する。光音響効果とは、可視光、近赤外光、マイクロ波等の電磁波パルスを被検対象に照射した際に、被検対象が電磁波を吸収して発熱し熱膨張することにより、音響波(典型的には超音波)が発生する現象である。
音響波測定装置は、被検対象である生体との間で音響波の送受信を行うため、生体(典型的には人体)との音響インピーダンスの整合性および、音響波減衰量の低減といった要件を満たすことが求められる。
このため、音響レンズの材料の1つとして、生体の音響インピーダンス(人体の場合、1.4〜1.7×106kg/m2/sec)に近く、超音波減衰量の小さいシリコーン樹脂が用いられている。
しかしながら、特許文献1に記載の組成物から形成されるシリコーン樹脂および特許文献2に記載の超音波伝搬媒体は、耐摩耗性が低い。上記特許文献1に記載の音響レンズ組成物から調製されるシリコーン樹脂および特許文献2に記載の超音波伝搬媒体は、音響波プローブに要求される、樹脂硬度および耐摩耗性ならびに音響波減衰量の低減の全てを高いレベルで満足することは困難である。
<1>ビニル基とフェニル基とを有するポリシロキサンと、分子鎖中に2個以上のSi−H基を有するポリシロキサンと、酸化亜鉛とを少なくとも含むポリシロキサン混合物を含有する音響波プローブ用組成物であって、
ポリシロキサン混合物の合計100質量部中に、酸化亜鉛を20〜52質量部含有する音響波プローブ用組成物。
<2>ポリシロキサン混合物の合計100質量部中に、酸化亜鉛を20〜50質量部含有する<1>に記載の音響波プローブ用組成物。
<3>ポリシロキサン混合物の合計100質量部中に、ビニル基とフェニル基とを有するポリシロキサンを10〜99.6質量部、分子鎖中に2個以上のSi−H基を有するポリシロキサンを0.4〜90質量部含有する<1>または<2>に記載の音響波プローブ用組成物。
<4>酸化亜鉛の平均一次粒子径が10〜200nmである<1>〜<3>のいずれか1つに記載の音響波プローブ用組成物。
<5>酸化亜鉛がシラン化合物で表面処理されたものである<1>〜<4>のいずれか1つに記載の音響波プローブ用組成物。
<6>ビニル基とフェニル基とを有するポリシロキサンの質量平均分子量が、10,000〜200,000である<1>〜<5>のいずれか1つに記載の音響波プローブ用組成物。
<7>ビニル基とフェニル基とを有するポリシロキサンの質量平均分子量が、30,000〜150,000である<1>〜<6>のいずれか1つに記載の音響波プローブ用組成物。
<8>分子鎖中に2個以上のSi−H基を有するポリシロキサンのSi−H当量が50〜1,300g/molである<1>〜<7>のいずれか1つに記載の音響波プローブ用組成物。
<9>分子鎖中に2個以上のSi−H基を有するポリシロキサンが、フェニル基を有する<1>〜<8>のいずれか1つに記載の音響波プローブ用組成物。
<10>ポリシロキサン混合物100質量部に対し、白金または白金含有化合物を0.0001〜0.1質量部含有する<1>〜<9>のいずれか1つに記載の音響波プローブ用組成物。
<12> <11>に記載の音響波プローブ用シリコーン樹脂を含んでなる、音響レンズおよび音響整合層からなる群から選択される少なくとも1つを有する音響波プローブ。
<13>容量性マイクロマシン超音波振動子および<11>に記載の音響波プローブ用シリコーン樹脂を含んでなる音響レンズを備える超音波プローブ。
<14> <12>に記載の音響波プローブを備える音響波測定装置。
<15> <12>に記載の音響波プローブを備える超音波診断装置。
<16> <11>に記載の音響波プローブ用シリコーン樹脂を含んでなる音響レンズを備える光音響波測定装置。
<17> <11>に記載の音響波プローブ用シリコーン樹脂を含んでなる音響レンズを備える超音波内視鏡。
また、本発明の説明において、「〜」とは、その前後に記載される数値を下限値および上限値として含む意味で使用される。
なお、本発明における質量平均分子量は、特に断りのない限り、ゲル浸透クロマトグラフィー(Gel Permeation Chromatography:GPC)による測定値(ポリスチレン換算)である。
また、cMUTを超音波診断用トランスデューサアレイとして用いる超音波プローブ、光音響波測定装置および超音波内視鏡における感度を向上させることが可能な音響波プローブ用シリコーン樹脂を提供することができる。
本発明の上記及び他の特徴及び利点は、適宜添付の図面を参照して、下記の記載からより明らかになるであろう。
本発明の音響波プローブ用組成物(以下、単に「組成物」とも称す。)は、ビニル基とフェニル基とを有するポリシロキサンと、分子鎖中に2個以上のSi−H基を有するポリシロキサンと、酸化亜鉛とを少なくとも含むポリシロキサン混合物を含有する音響波プローブ用組成物である。
酸化亜鉛の含有量が上記範囲内にあることにより、音響インピーダンスを人体の値に近くし、耐摩耗性を向上させ、かつ、音響波感度を高くすることができる。
なお、ポリシロキサン混合物とは、ビニル基とフェニル基とを有するポリシロキサンと分子鎖中に2個以上のSi−H基を有するポリシロキサンとを架橋重合させる触媒を含まない混合物である。従って、ポリシロキサン混合物中には、触媒でない酸化亜鉛が含まれる。
従って、本発明では、ポリシロキサン混合物中に、ビニル基とフェニル基とを有するポリシロキサン(A)と、分子鎖中に2個以上のSi−H基を有するポリシロキサン(B)と、酸化亜鉛とを少なくとも含有することが好ましい。
以降の詳細な説明においては、好ましい態様である、ビニル基とフェニル基とを有するポリシロキサン(A)および分子鎖中に2個以上のSi−H基を有するポリシロキサン(B)について記載する。しかし、本発明は以下に記載する態様に限定されるものではない。
本発明に用いられるビニル基とフェニル基とを有するポリシロキサン(A)(以下、単にポリシロキサン(A)とも称す。)は、分子鎖中に2個以上のビニル基を有する。
ビニル基とフェニル基とを有するポリシロキサン(A)としては、例えば、少なくとも分子鎖両末端にビニル基を有するポリシロキサン(a)(以下、単にポリシロキサン(a)とも称す。)、または分子鎖中に−O−Si(CH3)2(CH=CH2)を少なくとも2つ有するポリシロキサン(b)(以下、単にポリシロキサン(b)とも称す。)が挙げられる。なかでも、少なくとも分子鎖両末端にビニル基を有するポリシロキサン(a)が好ましい。
ポリシロキサン(a)は直鎖状が好ましく、ポリシロキサン(b)は、−O−Si(CH3)2(CH=CH2)が主鎖を構成するSi原子に結合しているポリシロキサン(b)が好ましい。
また、ポリシロキサン(A)のフェニル基の含有量は、特に限定されない。音響波プローブ用シリコーン樹脂としたときの機械的強度の観点から、例えば、1〜80モル%であり、好ましくは2〜40モル%である。
同じく、フェニル基の含有量とは、ポリシロキサン(A)を構成する全ユニットを100モル%としたときのフェニル基含有シロキサンユニットのモル%であり、主鎖を構成するSi−O単位および末端のSiの全てのSi原子が少なくとも1つのフェニル基で置換されている場合、100モル%となる。
なお、ポリシロキサンの「ユニット」とは、主鎖を構成するSi−O単位および末端のSiを言う。
なお、動粘度は、JIS Z8803に従い、ウベローデ型粘度計(例えば、柴田化学社製、商品名SU)を用い、温度23℃にて測定して求めることができる。
置換基を有する基としては、例えば、ハロゲン化アルキル基が挙げられる。
Ra2はなかでもメチル基が好ましく、Ra3はなかでもフェニル基が好ましい。また、x1の繰り返し中のRa3が両方ともフェニル基であること好ましい。
x2は、1〜3000の整数が好ましく、40〜1000の整数がより好ましい。
本発明において、上記一般式(A)中の繰り返し単位「−Si(Ra3)2−O−」と「−Si(Ra2)2−O−」は、それぞれ、ブロック重合した形態で存在していてもよいし、ランダムに存在する形態であってもよい。
なお、DMS−V31S15は、予めフュームドシリカが配合されているため、特別な装置での混練は不要である。
本発明に用いられる分子鎖中に2個以上のSi−H基を有するポリシロキサン(B)(以下、単にポリシロキサン(B)とも称す。)は、分子鎖中に2個以上のSi−H基を有する。ここで、ポリシロキサン(B)が「−SiH2−」構造を有する場合、「−SiH2−」構造中のSi−H基は2個と数えられる。また、ポリシロキサン(B)が「−SiH3」構造を有する場合、「−SiH3」構造中のSi−H基は3個と数えられる。
分子鎖中にSi−H基を2つ以上有することで、重合性不飽和基を少なくとも2つ有するポリシロキサンを架橋することができる。
直鎖状構造の質量平均分子量は、機械強度および硬度の点から、500〜100,000が好ましく、1,500〜50,000がより好ましい。
ここで、フェニル基の含有量は、上記ポリシロキサン(A)におけるフェニル基の含有量において、ポリシロキサン(A)をポリシロキサン(B)に置き換えて算出される含有量である。
本発明のシリコーン音響波プローブ用シリコーン樹脂は、嵩高いフェニル基を有することで、音速を高め、かつ、硬度および比重を大きくすることができる。そのため、音響インピーダンスを高めることができる。その結果、酸化亜鉛の添加量を少なくすることができる。
Rb3およびRb4は水素原子、アルキル基、アルケニル基、アリール基または−O−Si(Rb8)2(Rb7)が好ましく、水素原子、炭素数1〜4のアルキル基、ビニル基、フェニル基または−O−Si(CH3)2Hがより好ましい。
Rb3は、水素原子、アルキル基、アルケニル基、アリール基または−O−Si(Rb8)2(Rb7)が好ましく、水素原子またはアルキル基がより好ましく、水素原子が特に好ましい。
y1+y2は5〜2000の整数が好ましく、7〜1000の整数がより好ましく、10〜50の整数がさらに好ましく、15〜30の整数がなかでも好ましい。
本発明において、上記一般式(B)中の「−Si(Rb3)2−O−」と「−Si(Rb4)2−O−」は、それぞれ、ポリシロキサン中にブロック重合した形態で存在していてもよいし、ランダムに存在する形態であってもよい。
比重は、0.9〜0.95が好ましい。
分岐状構造のポリシロキサン(B)は、下記平均組成式(b)で表されるものが好ましい。
aは、好ましくは1である。
a/3で表されるヒドロシリル基の含有率は、0.1を超え0.6未満が好ましく、0.1を超え0.4未満がより好ましい。
なお、MeはCH3である。
本発明において、音響インピーダンスを高め、音響減衰率を低減するため、酸化亜鉛を添加する。本発明に用いられる酸化亜鉛の平均一次粒子径は、10nm〜200nmが好ましく、15nm〜100nmがより好ましく、20nm〜50nm未満が特に好ましい。
この結果、音響インピーダンスを高め、音響波減衰量の上昇が抑制され、かつ音響波プローブ用シリコーン樹脂の硬度および機械強度(引裂強度および耐摩耗性)が向上するものと思われる。
また、酸化亜鉛に後述する表面処理が施されている場合は、表面処理された状態での平均一次粒子径を意味する。
酸化亜鉛は、1種のみを単独で用いてもよいし、2種以上を組み合わせて用いてもよい。
酸化亜鉛粒子をシラン化合物で表面処理することでシリコーン樹脂との相互作用が強くなり、また、シリコーン樹脂との親和性が高くなるため、平均一次粒子径の小さい酸化亜鉛粒子の微分散が可能になると考えられる。このため、酸化亜鉛微粒子は、機械適応力が加わった際のストッパーとしての機能をより発揮し、シリコーン樹脂の硬度および機械強度が向上するものと考えられる。
表面処理の手法は通常の手法であればよい。シラン化合物での表面処理の手法としては、例えば、シランカップリング剤で表面処理する手法およびシリコーン化合物で被覆する手法が挙げられる。本発明においては、シリコーン化合物で被覆する手法が好ましい。
シランカップリング剤は、シリコーン樹脂の硬度および機械強度の向上の点から、加水分解性基を有するシランカップリング剤が好ましい。シランカップリング剤における加水分解性基は、水により加水分解されて水酸基となり、この水酸基が酸化亜鉛粒子表面の水酸基と脱水縮合反応することで、酸化亜鉛粒子の表面改質が行われ、得られるシリコーン樹脂の硬度および機械強度が向上される。加水分解性基は、例えば、アルコキシ基、アシルオキシ基、ハロゲン原子が挙げられる。
なお、酸化亜鉛粒子の表面が疎水性に表面改質されていると、酸化亜鉛粒子とポリシロキサン(A)およびポリシロキサン(B)との親和性が良好となり、得られるシリコーン樹脂の硬度および機械強度が向上するため好ましい。
シラン化合物としては、例えば、上記シランカップリング剤および、シランカップリング剤における官能基がアルキル基で置換されたシランカップリング剤が挙げられる。
また、トリメチルシリル化剤としては、例えば、上記シランカップリング剤に記載のトリメチルクロロシラン、ヘキサメチルジシラザン(HMDS)および、官能基がアルキル基で置換されたシランカップリング剤であるトリメチルメトキシシランが挙げられる。
酸化亜鉛粒子表面に存在する水酸基は、ヘキサメチルジシラザン(HMDS)との反応によりトリメチルシリル基で覆われ、酸化亜鉛粒子表面が疎水性に改質される。
酸化亜鉛粒子を被覆するシリコーン化合物は、シロキサン結合で構成されたポリマーであればよい。
シリコーン化合物としては、例えば、ポリシロキサンの側鎖および/または末端の全部または一部がメチル基になっているシリコーン化合物、側鎖の一部が水素原子であるシリコーン化合物、側鎖および/または末端の全部または一部にアミノ基、エポキシ基等の有機基を導入した変性シリコーン化合物、分岐構造を有するシリコーンレジンが挙げられる。なお、シリコーン化合物は直鎖状、環状のいずれの構造でもよい。
また、シリコーン化合物として反応性の変性シリコーンを用いる場合には、有機基が酸化亜鉛粒子表面の水酸基と反応することで、酸化亜鉛粒子の表面改質が行われ、得られるシリコーン樹脂の硬度および機械強度が向上される。
しかしながら、本発明においては、酸化亜鉛粒子が、ポリシロキサン(A)および(B)の隙間に密に充填されているため、ポリシロキサン(A)および(B)の分子鎖の運動は制限されている。
従って、全てのビニル基がSi−H基と反応するためには、ポリシロキサン(A)の有するビニル基に対するポリシロキサン(B)の有するSi−H基の当量は、ビニル基:Si−H基=1:1.1〜1:8が好ましく、1:1.2〜1:5がより好ましい。
本発明の音響波プローブ用組成物は、ビニル基とフェニル基とを有するポリシロキサン(A)、分子鎖中に2個以上のSi−H基を有するポリシロキサン(B)および酸化亜鉛以外に、付加重合反応のための白金触媒、硬化遅延剤、溶媒、分散剤、顔料、染料、帯電防止剤、酸化防止剤、難燃剤、熱伝導性向上剤等を適宜配合することができる。
触媒としては、例えば、白金または白金含有化合物(以下、「白金化合物」ともいう。)が挙げられる。白金または白金化合物としては、任意のものを使用することができる。
具体的には、白金黒、白金を無機化合物またはカーボンブラック等に担持させたもの、塩化白金酸または塩化白金酸のアルコール溶液、塩化白金酸とオレフィンの錯塩、塩化白金酸とビニルシロキサンとの錯塩等が挙げられる。触媒は1種のみを単独で用いてもよいし、2種以上を組み合わせて用いてもよい。
触媒は、ポリシロキサン(B)のSi−H基が、ポリシロキサン(A)のビニル基に対して付加するヒドロシリル化反応において必要である。ヒドロシリル化による付加硬化反応によって、ポリシロキサン(A)がポリシロキサン(B)により架橋され、シリコーン樹脂が形成される。
ここで、触媒は本発明の音響波プローブ用組成物中に含有させてもよく、また、音響波プローブ用組成物に含有させずに、音響波プローブ用組成物と接触させてもよい。なお、後者の方が好ましい。
本発明の音響波プローブ用組成物は、常法により調製することが可能である。
例えば、音響波プローブ用組成物を構成する成分を、ニーダー、加圧ニーダー、バンバリーミキサー(連続ニーダー)、2本ロールの混練装置で混練りすることにより得ることができる。各成分の混合順序は特に限定されない。
なお、均一な組成物を得る観点からは、まず、ビニル基とフェニル基とを有するポリシロキサン(A)および分子鎖中に2個以上のSi−H基を有するポリシロキサン(B)に、酸化亜鉛を分散させたポリシロキサン混合物とすることが好ましい。その後、酸化亜鉛を分散させたポリシロキサン混合物に触媒を添加し、減圧脱泡することで、音響波プローブ用組成物を調製することができる。
以下に、シリコーン樹脂の機械強度および音響波特性について詳細に記載する。
ここで、音響波特性は、超音波特性について記載する。ただし、音響波特性は超音波特性に限定されるものではなく、被検対象または測定条件等に応じて選択される、適切な周波数の音響波特性に関するものである。
硬度は25以上が好ましく、30以上がより好ましい。なお、現実的な上限値は80以下である。上記範囲内にあることで、音響波プローブの一部として組み込み使用する際の変形を防止することができる。
なお、シリコーン樹脂シートの硬度は後述の実施例の項に記載の測定方法により求めることができる。
引裂強度は、6N/cm以上が好ましく、10N/cm以上がより好ましい。なお、現実的な上限値は100N/cm以下である。
なお、引裂強度は後述の実施例の項に記載の測定方法により求めることができる。
厚み2mmのシリコーン樹脂シートについて、JIS K6264−2(2005)に従い、テーバー磨耗試験を行い、耐摩耗性を評価する。
人体と接触するプローブの摩耗を抑制する観点から、試験前後の質量減少分は、0.5%以下が好ましく、0.4%以下がより好ましく、0.3%以下がさらに好ましく、値が小さい程好ましい。
シリコーン樹脂シートの音響インピーダンスは、生体のもの(1.4〜1.7×106kg/m2/sec)に近い程好ましい。本発明のシリコーン樹脂シートの音響インピーダンスは、1.2〜1.8kg/m2/secが好ましく、1.3〜1.7kg/m2/secがより好ましく、1.4〜1.6kg/m2/secが特に好ましい。
なお、音響インピーダンスは後述の実施例の項に記載の方法により求めることができる。
本発明における評価系においては、音響波(超音波)感度は、−74dB以上が好ましく、−73dB以上がより好ましい。
なお、音響波(超音波)感度は、後述の実施例の項に記載の方法により求めることができる。
特に、本発明の音響波プローブ用組成物は、超音波診断装置の音響レンズ、あるいは圧電素子と音響レンズの間に設けられて圧電素子と音響レンズとの間の音響インピーダンスを整合させる役割を有する音響整合層の材料、光音響波測定装置または超音波内視鏡における音響レンズの材料ならびに超音波トランスデューサアレイとして容量性マイクロマシン超音波振動子(cMUT:Capacitive Micromachined Ultrasonic Transducers)を備える超音波プローブにおける音響レンズの材料等に好適に用いることができる。
本発明の音響波プローブ用シリコーン樹脂は、具体的には、例えば、特開2005−253751号公報、特開2003−169802号公報などに記載の超音波診断装置および、特開2013−202050号公報、特開2013−188465号公報、特開2013−180330号公報、特開2013−158435号公報、特開2013−154139号公報などに記載の光音響波測定装置などの音響波測定装置などに好ましく適用される。
以下に、本発明の音響波プローブの構成を、図1に記載する、超音波診断装置における超音波プローブの構成に基づき、より詳細に説明する。なお、超音波プローブとは、音響波プローブにおける音響波として、特に超音波を使用するプローブである。そのため、超音波プローブの基本的な構造は音響波プローブに適用することができる。
超音波プローブ10は、超音波診断装置の主要構成部品であって、超音波を発生するとともに、超音波ビームを送受信する機能を有するものである。超音波プローブ10の構成は、図1に示すように、先端(被検対象である生体に接する面)部分から音響レンズ1、音響整合層2、圧電素子層3、バッキング材4の順に設けられている。なお、近年、高次高調波を受信することを目的に、送信用超音波振動子(圧電素子)と、受信用超音波振動子(圧電素子)を異なる材料で構成し、積層構造としたものも提案されている。
圧電素子層3は、超音波を発生する部分であり、圧電素子の両側に電極が貼り付けられており、電圧を加えると圧電素子が伸縮と膨張を繰り返し振動することにより、超音波が発生する。
また、高周波側の受信波を検知する圧電素子には、より広い帯域幅の感度が必要である。このため、高周波、広帯域に適した圧電素子として、ポリフッ化ビニリデン(PVDF)などの有機系高分子物質を利用した有機圧電体が使用されている。
さらに、特開2011−071842号公報等には、優れた短パルス特性、広帯域特性を示し、量産性に優れ、特性ばらつきの少ないアレイ構造が得られる、MEMS(Micro Electro Mechanical Systems)技術を利用したcMUTが記載されている。
本発明においては、いずれの圧電素子材料も好ましく用いることができる。
バッキング材4は、圧電素子層3の背面に設けられており、余分な振動を抑制することにより超音波のパルス幅を短くし、超音波診断画像における距離分解能の向上に寄与する。
音響整合層2は、圧電素子層3と被検対象間での音響インピーダンスの差を小さくし、超音波を効率よく送受信するために設けられる。
本発明の超音波プローブ用組成物は、人体の音響インピーダンス(1.4〜1.7×106kg/m2/sec)との差が小さいことから、音響整合層の材料として好ましく用いることができる。本発明の音響整合層は、本発明の音響波プローブ用組成物を硬化反応させてなる音響波プローブ用シリコーン樹脂を10質量%以上含むことが好ましい。
音響レンズ1は、屈折を利用して超音波をスライス方向に集束し、分解能を向上させるために設けられる。また、被検対象である生体と密着し、超音波を生体の音響インピーダンス(人体では、1.4〜1.7×106kg/m2/sec)と整合させること、および、音響レンズ1自体の超音波減衰量が小さいことが求められている。
すなわち、音響レンズ1の材料としては、音速が人体の音速よりも十分小さく、超音波の減衰が少なく、また、音響インピーダンスが人体のような生体の皮膚の値に近ければ、超音波の送受信感度がよくなる。
本発明の超音波プローブ用組成物は、音響レンズ材としても、好ましく用いることができる。本発明の音響レンズは、本発明の音響波プローブ用組成物を硬化反応させてなる音響波プローブ用シリコーン樹脂を10質量%以上含むことが好ましい。
以下、本発明の超音波プローブ用組成物から得られる音響レンズが、従来の課題に対し特に機能を発揮する装置について、詳細に記載する。
なお、下記に記載する以外の装置に対しても、本発明の超音波プローブ用組成物は優れた効果を示す。
特開2006−157320号公報、特開2011−71842号公報などに記載のcMUTデバイスを超音波診断用トランスデューサアレイに用いる場合、一般的な圧電セラミックス(PZT)を用いたトランスデューサと比較して、一般的には、その感度が低くなる。
しかし、本発明の音響波プローブ用組成物から得られる音響レンズを用いることで、cMUTの感度不足を補うことが可能である。これにより、cMUTの感度を、従来のトランスデューサの性能に近づけることができる。
なお、cMUTデバイスはMEMS技術により作製されるため、圧電セラミックスプローブよりも量産性が高く、低コストな超音波プローブを市場に提供することができる。
特開2013−158435号公報などに記載の光超音波イメージング(PAI:Photo Acoustic Imaging)は、人体内部へ光(電磁波)を照射し、照射した光によって人体組織が断熱膨張する際に発生する超音波を画像化したもの、または超音波の信号強度を表示する。
ここで、光照射によって発生する超音波の音圧は微量であるため、人体深部の観察が困難であるという課題がある。
しかし、本発明の音響波プローブ用組成物から得られる音響レンズを用いることで、この課題に対して有効な効果を発揮することができる。
特開2008−311700号公報などに記載の超音波内視鏡における超音波は、その構造上、信号線ケーブルが体表用トランスデューサと比較して長いため、ケーブル損失によるトランスデューサの感度向上が課題である。また、この課題に対しては、下記の理由により、効果的な感度向上手段がないと言われている。
第二に、体表用の超音波診断装置におけるトランスデューサで採用されている圧電単結晶は、その物理特性およびプロセス適性上、超音波の送信周波数7〜8MHz以上のトランスデューサへの適用は困難である。しかしながら、内視鏡用超音波は概して超音波の送信周波数7〜8MHz以上のプローブであるため、圧電単結晶材による感度向上も困難である。
また、同一の超音波の送信周波数(例えば10MHz)を使用する場合でも、内視鏡用超音波トランスデューサにおいて本発明の音響波プローブ用組成物から得られる音響レンズ用いる場合には、特に有効性が発揮される。
以下の実施例において「部」および「%」というときには、特に断らない限り質量基準である。また、表中で使用する「−」は、その組成を有さないことを意味する。
ポリシロキサン(A)として、ビニル末端ジフェニルシロキサン−ジメチルシロキサンコポリマー(下記表1の成分(A)、Gelest社製、商品名「PDV−0541」、質量平均分子量60,000、ジフェニルシロキサン量5mol%)55.3質量部、ポリシロキサン(B)として、メチルヒドロシロキサンポリマー(下記表1の成分(B)、Gelest社製、商品名「HMS−991」、質量平均分子量1,600、Si−H当量67g/mol)0.7質量部、酸化亜鉛(堺化学工業社製「FINEX(登録商標)−50S−LPT」、平均一次粒子径20nm、シリコーン表面処理)44.0質量部をニーダーにより、温度23℃で2時間混練りし、均一なペースト(ポリシロキサン混合物)とした。これに白金触媒溶液(Gelest社製、商品名「SIP6832.3」、Pt濃度2質量%)を500ppm添加して混合した後、減圧(1mmHg)下で脱泡し、縦150mm×横150mm×深さ2mmの金属型に入れ、60℃で3時間熱処理をして、音響波プローブ用シリコーン樹脂(縦150mm×横150mm×厚み2mmのシート)を作製した。以下、このようにして作製した音響波プローブ用シリコーン樹脂を「シリコーン樹脂シート」と称す。
なお、下記表1において、「ポリシロキサン混合物」を単に「混合物」と記載してある。
実施例1のポリシロキサン混合物の組成を下記表1に記載の組成に変えた以外は、実施例1と同様にして所定のシリコーン樹脂シートを得た。
ここで、比較例2および3は、特開2005−125071号公報の実施例を模した追試験である。
実施例1〜22および比較例1〜5のシリコーン樹脂シートについて、以下の評価を行った。
得られた厚み2mmのシリコーン樹脂シートについて、JIS K6253−3(2012)に従い、タイプAデュロメータ硬さを、ゴム硬度計(エクセル社製、商品名「RH−201A」)を用いて測定した。
得られた厚み2mmのシリコーン樹脂シートについて、JIS K6252(2007)に従い、トラウザー型試験片を作製し、引裂強度を測定した。
得られた厚み2mmのシリコーン樹脂シートについて、JIS K6264−2(2005)に従い、東洋精機社製テーバー磨耗試験機を用い、磨耗輪CS−10、荷重4.9N、回転数60rpmにて1,000回転させた。試験前後の質量を測定し、下記式から質量減少分(%)を算出した。下記表1において、質量減少分をテーバー摩耗量[%]と記載した。
(試験前のシリコーン樹脂シートの質量−試験後のシリコーン樹脂シートの質量)×100
得られた厚み2mmのシリコーン樹脂シートについて、25℃における密度をJIS K7112(1999)に記載のA法(水中置換法)の密度測定方法に準じて、電子比重計(アルファミラージュ社製、商品名「SD−200L」)を用いて測定した。超音波音速は、JIS Z2353(2003)に従い、シングアラウンド式音速測定装置(超音波工業株式会社製、商品名「UVM−2型」)を用いて25℃において測定し、測定した密度と音速の積から音響インピーダンスを求めた。
超音波発振器(岩通計測株式会社製、ファンクション・ジェネレータ、商品名「FG−350」)から出力された5MHzの正弦波信号(1波)を超音波プローブ(ジャパンプローブ株式会社製)に入力し、超音波プローブから中心周波数が5MHzの超音波パルス波を水中に発生させた。発生させた超音波が、得られた厚み2mmのシリコーン樹脂シートを通過する前と後の振幅の大きさを超音波受信機(松下電器産業株式会社製、オシロスコープ、商品名「VP−5204A」)により、水温25℃の環境で測定し、音響波(超音波)感度を比較することで、各素材の音響波(超音波)減衰量を比較した。
なお、音響波(超音波)感度は、超音波発振器による、半値幅50nsec以下の入力波の電圧ピーク値Vinに対し、発生させた音響波(超音波)がシートを通過し、シートの対面から反射してきた音響波(超音波)を超音波発振器が受信したときに得られる電圧値をVsとし、下記計算式より算出した。
なお、下記表1では、ポリシロキサン(A)および(B)の質量平均分子量を単に分子量として記載し、各成分の種類は商品名を記載した。また、Si−H当量を単に当量と記載した。
[ポリシロキサン成分(A)]
いずれもGelest社製のPDV(商品名)、DMS(商品名)シリーズ
・PDV−0541:商品名、ビニル末端ジフェニルシロキサン−ジメチルシロキサンコポリマー、質量平均分子量60,000、ジフェニルシロキサン量5mol%
・PDV−0535:商品名、ビニル末端ジフェニルシロキサン−ジメチルシロキサンコポリマー、質量平均分子量47,500、ジフェニルシロキサン量5mol%
・PDV−1641:商品名、ビニル末端ジフェニルシロキサン−ジメチルシロキサンコポリマー、質量平均分子量55,000、ジフェニルシロキサン量16mol%
・PDV−1635:商品名、ビニル末端ジフェニルシロキサン−ジメチルシロキサンコポリマー、質量平均分子量35,300、ジフェニルシロキサン量16mol%
・PDV−1631:商品名、ビニル末端ジフェニルシロキサン−ジメチルシロキサンコポリマー、質量平均分子量19,000、ジフェニルシロキサン量16mol%
・DMS−V41:商品名、ビニル末端ポリジメチルシロキサン、質量平均分子量62,700、Si−H当量67g/mol
[ポリシロキサン成分(B)]
・HMS−991:商品名、Gelest社製メチルヒドロシロキサンポリマー、質量平均分子量1,600、Si−H当量67g/mol
・HPM−502:商品名、Gelest社製メチルヒドロシロキサン−フェニルメチルシロキサンコポリマー、質量平均分子量4,500、Si−H当量165g/mol
・HMS−151:商品名、Gelest社製メチルヒドロシロキサン−ジメチルシロキサンコポリマー、質量平均分子量2,000、Si−H当量490g/mol
・HMS−301:商品名、Gelest社製メチルヒドロシロキサン−ジメチルシロキサンコポリマー、質量平均分子量2,000、Si−H当量245g/mol
・HMS−501:商品名、Gelest社製メチルヒドロシロキサン−ジメチルシロキサンコポリマー、質量平均分子量1,100、Si−H当量135g/mol
・HMS−064:商品名、Gelest社製メチルヒドロシロキサン−ジメチルシロキサンコポリマー、質量平均分子量60,000、Si−H当量1,240g/mol
[酸化亜鉛]
いずれも堺化学工業社製の酸化亜鉛、FINEX(登録商標)シリーズ、上記表では「FINEX−」を省略して記載してある。
・FINEX−50S−LPT:商品名、平均一次粒子径20nm、シリコーン表面処理
・FINEX−75:商品名、平均一次粒子径15nm、シリコーン表面処理なし
・FINEX−50S−LP2:商品名、平均一次粒子径20nm、シリコーン表面処理
・FINEX−50:商品名、平均一次粒子径20nm、シリコーン表面処理なし
・FINEX−30S−LPT:商品名、平均一次粒子径35nm、シリコーン表面処理
・FINEX−30W−LP2:商品名、平均一次粒子径35nm、シリカ/シリコーン表面処理
・FINEX−25−LPT:商品名、平均一次粒子径60nm、シリコーン表面処理
2 音響整合層
3 圧電素子層
4 バッキング材
7 筐体
9 コード
10 超音波探触子(プローブ)
Claims (17)
- ビニル基とフェニル基とを有するポリシロキサンと、分子鎖中に2個以上のSi−H基を有するポリシロキサンと、酸化亜鉛とを少なくとも含むポリシロキサン混合物を含有する音響波プローブ用組成物であって、
前記ポリシロキサン混合物の合計100質量部中に、前記酸化亜鉛を20〜52質量部含有する音響波プローブ用組成物。 - 前記ポリシロキサン混合物の合計100質量部中に、前記酸化亜鉛を20〜50質量部含有する請求項1に記載の音響波プローブ用組成物。
- 前記ポリシロキサン混合物の合計100質量部中に、前記ビニル基とフェニル基とを有するポリシロキサンを10〜99.6質量部、前記分子鎖中に2個以上のSi−H基を有するポリシロキサンを0.4〜90質量部含有する請求項1または2に記載の音響波プローブ用組成物。
- 前記酸化亜鉛の平均一次粒子径が10〜200nmである請求項1〜3のいずれか1項に記載の音響波プローブ用組成物。
- 前記酸化亜鉛がシラン化合物で表面処理されたものである請求項1〜4のいずれか1項に記載の音響波プローブ用組成物。
- 前記ビニル基とフェニル基とを有するポリシロキサンの質量平均分子量が、10,000〜200,000である請求項1〜5のいずれか1項に記載の音響波プローブ用組成物。
- 前記ビニル基とフェニル基とを有するポリシロキサンの質量平均分子量が、30,000〜150,000である請求項1〜6のいずれか1項に記載の音響波プローブ用組成物。
- 前記分子鎖中に2個以上のSi−H基を有するポリシロキサンのSi−H当量が50〜1,300g/molである請求項1〜7のいずれか1項に記載の音響波プローブ用組成物。
- 前記分子鎖中に2個以上のSi−H基を有するポリシロキサンが、フェニル基を有する請求項1〜8のいずれか1項に記載の音響波プローブ用組成物。
- 前記ポリシロキサン混合物100質量部に対し、白金または白金含有化合物を0.0001〜0.1質量部含有する請求項1〜9のいずれか1項に記載の音響波プローブ用組成物。
- 請求項1〜10のいずれか1項に記載の音響波プローブ用組成物を硬化反応させてなる音響波プローブ用シリコーン樹脂。
- 請求項11に記載の音響波プローブ用シリコーン樹脂を含んでなる、音響レンズおよび音響整合層からなる群から選択される少なくとも1つを有する音響波プローブ。
- 容量性マイクロマシン超音波振動子および請求項11に記載の音響波プローブ用シリコーン樹脂を含んでなる音響レンズを備える超音波プローブ。
- 請求項12に記載の音響波プローブを備える音響波測定装置。
- 請求項12に記載の音響波プローブを備える超音波診断装置。
- 請求項11に記載の音響波プローブ用シリコーン樹脂を含んでなる音響レンズを備える光音響波測定装置。
- 請求項11に記載の音響波プローブ用シリコーン樹脂を含んでなる音響レンズを備える超音波内視鏡。