JP6484028B2 - Covering structure - Google Patents
Covering structure Download PDFInfo
- Publication number
- JP6484028B2 JP6484028B2 JP2014261554A JP2014261554A JP6484028B2 JP 6484028 B2 JP6484028 B2 JP 6484028B2 JP 2014261554 A JP2014261554 A JP 2014261554A JP 2014261554 A JP2014261554 A JP 2014261554A JP 6484028 B2 JP6484028 B2 JP 6484028B2
- Authority
- JP
- Japan
- Prior art keywords
- storage member
- resin sheet
- foamable resin
- heat
- thermally foamable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、新規な収納部材の被覆構造体に関するものである。 The present invention relates to a covering structure for a novel storage member.
従来、建築物等において、各種収納部材が使用されている。例えば、発電所、工場、工業用ビル、あるいは商業用ビル等の大規模建築では、電力ケーブルや通信ケーブル等の多数のケーブルをケーブル収納部材内に収納し、各フロアに配線している。このような多数のケーブルを配線する場合、火災等により一部のケーブルが損傷するおそれがあるため、保護対策が必要とされている。 Conventionally, various storage members are used in buildings and the like. For example, in a large-scale building such as a power plant, a factory, an industrial building, or a commercial building, a large number of cables such as power cables and communication cables are housed in a cable housing member and wired on each floor. When such a large number of cables are wired, some cables may be damaged by a fire or the like, and therefore, a protective measure is required.
このような保護対策としては、例えば、ケーブル収納部材内あるいはケーブルの上に防火材料を充填または塗布する方法(例えば、特許文献1)、ケーブル収納部材に防火シートを巻き付ける方法(例えば、特許文献2)、またはこれらの組み合わせた方法(例えば特許文献3)等が知られている。 Such protection measures include, for example, a method of filling or applying a fireproof material in or on the cable housing member (for example, Patent Document 1), and a method of winding a fireproof sheet around the cable housing member (for example, Patent Document 2). Or a combination of these methods (for example, Patent Document 3) is known.
上記特許文献1は、防火材料でケーブルを被覆した状態となるためケーブルの燃焼を抑制することはできる。しかし、ケーブル収納部材外部が高温に曝された場合、ケーブル収納部材が変形してしまうおそれがある。これに対して、特許文献2や特許文献3は、ケーブル収納部材に防火シート等を巻き付け、さらにステンレスバンド等を締め付けて固定するものであり、耐熱保護性は向上する。しかし、このような被覆構造は、美観性に欠ける。また、ケーブルの布設代えを行う際には、防火シートを取り外し、再度防火シートを被覆する必要があり、作業工程が多く煩雑となるおそれがある。また、防火シートを取り外し可能な態様とすることにより、耐熱性が不十分となるおそれもある。
Since the said
本発明は、上述のような問題点に鑑みなされたものであり、施工性、美観性、耐熱保護性等に優れ、さらには収納後の取り扱いが容易な収納部材の被覆構造を提供することを目的とするものである。 The present invention has been made in view of the above-described problems, and provides a covering structure for a storage member that is excellent in workability, aesthetics, heat-resistant protection, and the like, and that is easy to handle after storage. It is the purpose.
上記課題を解決するため、本発明者は鋭意検討の結果、収納部材の外周面に熱発泡性樹脂シートを被覆し、かつ当該収納部材の開口部において熱発泡性樹脂シートの端部を収納部材の内側に折り返すことを特徴とする被覆構造体に想到し、本発明を完成させるに到った。 In order to solve the above-mentioned problems, the present inventor has conducted extensive studies and covered the outer peripheral surface of the storage member with a heat-foamable resin sheet and the end of the heat-foamable resin sheet at the opening of the storage member. The present invention has been completed by conceiving a covering structure characterized by being folded inside.
すなわち、本発明は以下の特徴を有するものである。 That is, the present invention has the following characteristics.
1. ケーブルを収納する収納部材の被覆構造体であり、
上記収納部材は、上部開口部を有し、ケーブルが収納・取り出し可能な構造であり、
収納部材の外周面に熱発泡性樹脂シートが被覆され、かつ当該収納部材の上部開口部において当該熱発泡性樹脂シートの端部が収納部材内側に折り返されていることを特徴とする被覆構造体。
2.少なくとも収納部材内側に折り返された熱発泡性樹脂シートが、接着剤で固定されていることを特徴とする1.に記載の被覆構造体。
3.上記収納部材が、上部開口部にカバーを有し、
当該カバーの少なくとも外周面に熱発泡性樹脂シートが被覆されたことを特徴とする1.または2.に記載の被覆構造体。
1. A covering structure of a storage member for storing a cable ,
The storage member has an upper opening, and has a structure in which a cable can be stored and taken out.
A covering structure characterized in that a heat foamable resin sheet is coated on an outer peripheral surface of a storage member, and an end portion of the heat foamable resin sheet is folded back inside the storage member at an upper opening of the storage member. .
2. 1. A heat-foamable resin sheet folded back at least on the inside of a storage member is fixed with an adhesive. The covering structure according to 1.
3. The storage member has a cover in the upper opening,
1. A thermally foamable resin sheet is coated on at least the outer peripheral surface of the cover. Or 2. The covering structure according to 1.
上記1.の被覆構造体は、収納部材の被覆構造体であり、収納部材の外周面に熱発泡性樹脂シートが被覆され、かつ当該収納部材の開口部において当該熱発泡性樹脂シートの端部が収納部材内側に折り返されていることを特徴とするものである。このような被覆構造体によれば、すっきりとした仕上がりとなり、美観性に優れる。また、収納部材が高温にさらされた場合は、優れた耐熱保護性が得られる。さらに、収納後に、収納部材内のケーブル等の布設代えを行う場合にも取り扱いが容易である。 Above 1. The covering structure is a covering structure for a storage member, and the outer peripheral surface of the storage member is covered with a thermally foamable resin sheet, and the end of the thermally foamable resin sheet is the storage member at the opening of the storage member. It is characterized by being folded inside. According to such a covering structure, it has a clean finish and excellent aesthetics. Moreover, when the storage member is exposed to a high temperature, excellent heat protection can be obtained. Furthermore, handling is also easy when replacing a cable or the like in the storage member after storage.
上記2.の被覆構造体は、少なくとも収納部材内側に折り返された熱発泡性樹脂シートが、接着剤で接着されていることを特徴とするものである。これにより、施工性、及び美観性を高めることができる。 2. This covering structure is characterized in that at least the thermally foamable resin sheet folded back inside the housing member is bonded with an adhesive. Thereby, workability and aesthetics can be improved.
上記3.の被覆構造体は、上記収納部材の上部開口部に、少なくとも外周面に熱発泡性樹脂シートが被覆されたカバーを有するものである。これにより、よりいっそう耐熱保護性を高めることができる。 3. above. This covering structure has a cover in which at least the outer peripheral surface is covered with a thermally foamable resin sheet at the upper opening of the housing member. Thereby, heat-resistant protection can be improved further.
1.収納部材
1a.開口部
2.熱発泡性樹脂シート
2a.折り返し部
2L.折り返し部の長さ
3.接着剤
4.断熱層
4a.空気層
5.カバー
6.ケーブル
7.スペーサー
8.無機繊維質シート
1.
6).
以下、本発明を実施するための形態について説明する。 Hereinafter, modes for carrying out the present invention will be described.
図1は、ケーブルが収納された収納部材の一例を示す斜視図である。
[収納部材]
本発明は、各種収納部材の被覆構造体に関するものであり、特に各種ケーブル等を収納する収納部材(1)(「ケーブル収納部材」ともいう。)に好ましく適用できるものである。本発明のケーブル収納部材は、ケーブル(6)が収納・取り出し可能な構造であり、上部開口部(1a)を有する長尺体であれば特に限定されない。例えば、図1に示すような、横断面形状が底面と少なくとも2つ以上の側面からなる凹型の他、断面形状が半円状、V字状、U字状、等のものが挙げられる。その材質は、鋼板、ステンレス鋼板、亜鉛めっき鋼板、等が使用できる。
FIG. 1 is a perspective view illustrating an example of a storage member in which a cable is stored.
[Storage material]
The present invention relates to a covering structure for various storage members, and is particularly applicable to a storage member (1) (also referred to as a “cable storage member”) that stores various cables and the like. The cable storage member of the present invention is not particularly limited as long as the cable (6) can be stored and taken out and is a long body having an upper opening (1a). For example, as shown in FIG. 1, the cross-sectional shape may be a concave shape having a bottom surface and at least two or more side surfaces, and the cross-sectional shape may be a semicircular shape, a V shape, a U shape, or the like. As the material, a steel plate, a stainless steel plate, a galvanized steel plate, or the like can be used.
[熱発泡性樹脂シート]
本発明の熱発泡性樹脂シート(2)は、火災等により周囲温度が所定の発泡温度に達すると発泡し、炭化断熱層を形成するものである。熱発泡性樹脂シート(2)としては、構成成分として樹脂成分、難燃剤、発泡剤、炭化剤及び充填剤を含有するものが好適である。このうち、樹脂成分としてはビニル系樹脂、ポリスチレン系樹脂、ポリプロピレン系樹脂、アクリル系樹脂、ポリアミド系樹脂、ポリウレタン系樹脂、酢酸ビニル樹脂等の熱可塑性樹脂等、難燃剤としてはポリリン酸アンモニウム等、発泡剤としてはメラミン、ジシアンジアミド、アゾジカーボンアミド等、炭化剤としてはペンタエリスリトール、ジペンタエリスリトール等、充填剤としては二酸化チタン等が挙げられる。
[Heat-foaming resin sheet]
The thermally foamable resin sheet (2) of the present invention foams when the ambient temperature reaches a predetermined foaming temperature due to a fire or the like, and forms a carbonized heat insulating layer. As the thermally foamable resin sheet (2), those containing a resin component, a flame retardant, a foaming agent, a carbonizing agent and a filler as the constituent components are suitable. Among these, as a resin component, a vinyl resin, a polystyrene resin, a polypropylene resin, an acrylic resin, a polyamide resin, a polyurethane resin, a thermoplastic resin such as a vinyl acetate resin, and the like as a flame retardant, ammonium polyphosphate, Examples of the foaming agent include melamine, dicyandiamide, and azodicarbonamide, examples of the carbonizing agent include pentaerythritol and dipentaerythritol, and examples of the filler include titanium dioxide.
各成分の配合比率は、好ましくは、固形分換算で、樹脂成分100重量部に対して、難燃剤50〜1000重量部、発泡剤5〜500重量部、炭化剤5〜600重量部、及び充填剤10〜300重量部である。熱発泡性樹脂シート(2)の厚みは、適用部位等により適宜設定すれば良いが、好ましくは0.2〜10mm程度、より好ましく0.5〜6mm程度である。 The blending ratio of each component is preferably 50 to 1000 parts by weight of a flame retardant, 5 to 500 parts by weight of a foaming agent, 5 to 600 parts by weight of a carbonizing agent, and filled with respect to 100 parts by weight of a resin component in terms of solid content. 10 to 300 parts by weight of the agent. The thickness of the thermally foamable resin sheet (2) may be appropriately set depending on the application site and the like, but is preferably about 0.2 to 10 mm, more preferably about 0.5 to 6 mm.
また、本発明の熱発泡性樹脂シート(2)は、上記構成成分を含むシートのみから構成されていてもよいが、少なくとも一方の面に繊維質シートが積層されていることが好ましい。これにより、形成された炭化断熱層の脱落防止効果を高めることができる。 Moreover, although the thermally foamable resin sheet (2) of this invention may be comprised only from the sheet | seat containing the said structural component, it is preferable that the fibrous sheet is laminated | stacked on the at least one surface. Thereby, the fall prevention effect of the formed carbonized heat insulation layer can be heightened.
このような繊維質シートとしては、有機繊維、及び/または無機繊維等を含むシートが挙げられ、好ましくは目付け100g/m2未満(より好ましくは5g/m2以上95g/m2以下、さらに好ましくは10g/m2以上90g/m2以下)である。 Examples of such a fibrous sheet include a sheet containing organic fibers and / or inorganic fibers, and preferably have a basis weight of less than 100 g / m 2 (more preferably 5 g / m 2 or more and 95 g / m 2 or less, more preferably Is 10 g / m 2 or more and 90 g / m 2 or less).
有機繊維としては、例えば、パルプ繊維、ポリエステル繊維、ポリプロピレン繊維、アラミド繊維、ビニロン繊維、ポリエチレン繊維、ポリアリレート繊維、PBO繊維、ナイロン繊維、アクリル繊維、塩化ビニル繊維、セルロース繊維等、またはそれらの織布、不織布等が挙げられる。有機繊維は、150℃程度の温度領域で溶融して液体状態になるようなものであってもよいが、かかる温度領域で溶融しないものの方が好ましい。 Examples of the organic fiber include pulp fiber, polyester fiber, polypropylene fiber, aramid fiber, vinylon fiber, polyethylene fiber, polyarylate fiber, PBO fiber, nylon fiber, acrylic fiber, vinyl chloride fiber, cellulose fiber, and their woven fabric. A cloth, a nonwoven fabric, etc. are mentioned. The organic fiber may be melted in a temperature range of about 150 ° C. to be in a liquid state, but is preferably not melted in such a temperature range.
無機繊維としては、例えば、ロックウール、ガラス繊維、シリカ繊維、シリカ−アルミナ繊維、カーボン繊維、炭化珪素繊維等、またはそれらの織布、不織布等、さらに鉄、銅等の金属細線が挙げられる。このような無機繊維は、熱を加えても溶融せず、さらに補強材としても作用し、発泡した炭化断熱層を保持できるので、収納部材(1)からの脱落防止効果に優れている。特に無機繊維が網目構造を有していれば、熱発泡性樹脂シート(2)及びこれに熱を加えることにより形成される炭化断熱層をより効率よく補強することができ、収納部材(1)からの脱落を防止することができるので好ましい。 Examples of the inorganic fiber include rock wool, glass fiber, silica fiber, silica-alumina fiber, carbon fiber, silicon carbide fiber, or the like, or woven fabric, nonwoven fabric, and the like, and fine metal wires such as iron and copper. Such an inorganic fiber does not melt even when heat is applied, and also acts as a reinforcing material, and can hold the foamed carbonized heat insulating layer, and therefore has an excellent effect of preventing dropping from the storage member (1). In particular, if the inorganic fiber has a network structure, the heat-foamable resin sheet (2) and the carbonized heat insulation layer formed by applying heat thereto can be more efficiently reinforced, and the storage member (1). It is preferable because it can be prevented from falling off.
繊維質シートは、無機繊維と有機繊維からなる複合シートであって、該無機繊維が網目状に配列されたシートであり、その少なくとも一方(一面)に有機繊維の織布又は不織布が積層され、無機繊維の網目の一部又は全部が有機繊維で塞がれているようなものが好ましい。無機繊維と有機繊維を組み合わせることにより、熱による溶融成分が吸着され、継ぎ目部分の剥れ等を防止することができる。また、網目を有機繊維で塞いでいれば、熱発泡性樹脂シート(2)製造時に無機繊維の網目構造が崩れにくく、簡便に製造することができる。 The fibrous sheet is a composite sheet composed of inorganic fibers and organic fibers, wherein the inorganic fibers are arranged in a mesh pattern, and a woven or non-woven fabric of organic fibers is laminated on at least one side (one side), It is preferable that part or all of the network of inorganic fibers is closed with organic fibers. By combining the inorganic fiber and the organic fiber, the molten component due to heat is adsorbed, and peeling of the joint portion can be prevented. Moreover, if the mesh is closed with organic fibers, the network structure of the inorganic fibers is not easily broken during the production of the heat-foamable resin sheet (2), and can be easily produced.
図2は、本発明の被覆構造体の一例を示す斜視図である。また、図3は、本発明の被覆構造体の一例を示す横断面図である。
面図を示す。
FIG. 2 is a perspective view showing an example of the covering structure of the present invention. FIG. 3 is a cross-sectional view showing an example of the covering structure of the present invention.
A plane view is shown.
本発明の被覆構造体は、収納部材(1)外周面の長手方向に複数の熱発泡性樹脂シート(2)を設けることができる。該熱発泡性樹脂シート(2)同士の継ぎ目部分は、つき合わせても、重なり部を有していてもよいが、重なり部を有する方が好ましい。また、熱発泡性樹脂シート(2)は、所望の耐熱保護性に合わせて、2枚以上重ねて被覆してもよい。 The covering structure of the present invention can be provided with a plurality of thermally foamable resin sheets (2) in the longitudinal direction of the outer peripheral surface of the storage member (1). The joint portion of the thermally foamable resin sheets (2) may be attached or may have an overlapping portion, but preferably has an overlapping portion. Further, two or more heat-foamable resin sheets (2) may be coated in accordance with the desired heat-resistant protective properties.
本発明は、図2、図3に示すように、収納部材の開口部(1a)において当該熱発泡性樹脂シート(2)の端部が収納部材内側に折り返され、折り返し部(2a)を形成している。折り返し部の長さ(2L)(収納部材の端部から熱発泡性樹脂シート(2)の端部までの長さ)は、収納部材の形状により適宜設定すればよいが、好ましくは20mm以上(より好ましくは30mm以上)である。このような範囲であることによって、火災等により収納部材が高温に晒された場合であっても、優れた耐熱保護性を有することができる。一般に、収納部材では、内部に収納されるケーブル等により熱が伝わり収納部材内部の温度が外部よりも先に上昇する場合がある。このような場合、熱発泡性樹脂シート(2)や後述の接着剤(3)が軟化するおそれがあり、場合によっては熱発泡性樹脂シート(2)が脱落する危険性がある。これに対して、本発明の被覆構造体のように、熱発泡性樹脂シートの端部が収納部材内側に折り返されている折り返し部(2a)を有することにより、収納部材内部の温度が外部よりも先に上昇した場合においても、熱発泡性樹脂シート(2)の脱落を防止することができ、耐熱保護性をいっそう高めることができる。また、収納部材外周面に沿って、熱発泡性樹脂シートを施工できるため、すっきりとした仕上がりとなり、美観性にすぐれた被覆構造体を得ることができる。また、施工性においても好適である。 In the present invention, as shown in FIGS. 2 and 3, the end of the thermally foamable resin sheet (2) is folded back inside the housing member at the opening (1a) of the housing member to form a folded portion (2a). doing. The length (2L) of the folded portion (the length from the end of the storage member to the end of the thermally foamable resin sheet (2)) may be appropriately set depending on the shape of the storage member, but is preferably 20 mm or more ( More preferably, it is 30 mm or more. By being in such a range, even when the storage member is exposed to a high temperature due to a fire or the like, it can have excellent heat protection. Generally, in a storage member, heat is transmitted by a cable or the like stored inside, and the temperature inside the storage member may rise before the outside. In such a case, the heat-foamable resin sheet (2) and the adhesive (3) described later may be softened, and in some cases, the heat-foamable resin sheet (2) may be dropped. On the other hand, as in the covering structure of the present invention, the end of the thermally foamable resin sheet has a folded portion (2a) that is folded back to the inside of the storage member, so that the temperature inside the storage member is externally increased. Even in the case where the temperature rises first, it is possible to prevent the heat-foamable resin sheet (2) from falling off and to further improve the heat-resistant protective property. Moreover, since a heat-foamable resin sheet can be constructed along the outer peripheral surface of the storage member, it is possible to obtain a coated structure with a clean finish and excellent aesthetics. Moreover, it is suitable also in workability.
本発明では、収納部材(1)の表面に熱発泡性樹脂シート(2)を被覆する場合、接着剤(3)を用いることが好ましい。接着剤(3)を用いる場合、少なくとも収納部材内側に折り返された熱発泡性樹脂シートが、接着剤で固定されていればよく(図3−1)、必要に応じ、収納部材外周面の任意の場所が接着剤で固定されてもよい。また、収納部材外周面全体が接着剤で固定されている態様も好適である(図3−2)。 In this invention, when coat | covering the heat-foamable resin sheet (2) on the surface of a storage member (1), it is preferable to use an adhesive agent (3). When the adhesive (3) is used, it is sufficient that at least the thermally foamable resin sheet folded inside the storage member is fixed with the adhesive (FIG. 3-1). May be fixed with an adhesive. Further, a mode in which the entire outer peripheral surface of the storage member is fixed with an adhesive is also suitable (FIG. 3-2).
本発明における接着剤(3)としては、例えば、アクリル樹脂、シリコン樹脂、エポキシ樹脂、ビニル樹脂、フェノール樹脂、ポリエステル樹脂、ウレタン樹脂、パラフィン等を主原料とした水分散型、水溶性型、溶剤型の接着剤等、公知のものを使用することができる。接着剤には、必要に応じて、上述した熱発泡性樹脂シートに配合されるような難燃剤、発泡剤、炭化剤、充填剤、等を添加することもできる。なお、本発明において、接着剤には粘着剤も包含される。 Examples of the adhesive (3) in the present invention include water-dispersed types, water-soluble types, and solvents mainly composed of acrylic resin, silicon resin, epoxy resin, vinyl resin, phenol resin, polyester resin, urethane resin, paraffin, and the like. A known type of adhesive such as a mold adhesive can be used. A flame retardant, a foaming agent, a carbonizing agent, a filler, etc. which are mix | blended with the heat-foamable resin sheet mentioned above can also be added to an adhesive agent as needed. In the present invention, the adhesive includes an adhesive.
本発明の被覆構造体の施工方法としては、上記被覆構造体が得られる限り、特に限定されない。接着剤を用いて被覆する場合、
・収納部材(1)に接着剤を塗付し、熱発泡性樹脂シート(2)を貼着させる方法、
・予め熱発泡性樹脂シート(2)片方の面に接着剤を塗付したものを使用し、収納部材(1)に貼着させる方法、
・あるいは上記2つの方法を組み合わせて貼着させる方法、
等が挙げられる。なお、接着剤は、少なくとも収納部材内側の折り返し部(2a)における熱発泡性樹脂シート(2)が固定されるように塗付しておけばよい。
The construction method of the covering structure of the present invention is not particularly limited as long as the covering structure is obtained. When covering with an adhesive,
A method of applying an adhesive to the storage member (1) and sticking the thermally foamable resin sheet (2);
-A method of applying a heat-foamable resin sheet (2) with an adhesive applied to one side in advance, and sticking it to the storage member (1),
・ Alternatively, a method of applying a combination of the above two methods,
Etc. The adhesive may be applied so that at least the thermally foamable resin sheet (2) in the folded portion (2a) inside the storage member is fixed.
さらに、本発明では、図4のように、収納部材(1)と熱発泡性樹脂シート(2)の間に断熱層(4)を設けることができる。断熱層(4)を設けることにより、よりいっそう本発明の効果を高めることができる。本発明における断熱層(4)としては、例えば、空気層(4a)及び/または断熱材層(4b)が挙げられる。また、断熱層(4)の厚さは、所望の性能により適宜設定すればよい。 Furthermore, in this invention, a heat insulation layer (4) can be provided between a storage member (1) and a thermally foamable resin sheet (2) like FIG. By providing the heat insulating layer (4), the effect of the present invention can be further enhanced. As a heat insulation layer (4) in this invention, an air layer (4a) and / or a heat insulating material layer (4b) are mentioned, for example. Moreover, what is necessary is just to set the thickness of a heat insulation layer (4) suitably by desired performance.
空気層(4a)を設ける方法としては、特に限定されないが、例えば、
・収納部材(1)の外周面にスペーサー(7)等を取り付けた後、熱発泡性樹脂シート(2)を被覆する方法(図5−1)、
・収納部材(1)の断面外周及び折り返し部の長さに対して、余剰の熱発泡樹脂シート(2)を用い、空気層(4a)が形成されるように被覆する方法(図5−2)、
等が挙げられる。なお、スペーサー(7)の形状は、空気層(4a)を設けることが可能であれば特に限定されない。また、その材質は、例えば、鉄、ステンレス、アルミニウム、アルミナ、チタン、銅等の金属が好ましい。本発明においてスペーサー(7)は、収納部材(1)の外周面の任意の箇所に設ければよいが、収納部材(1)の外周面を囲うように設けることもできる。このようなスペーサー(7)を設けることにより、耐熱保護性を高めるこができる。
The method for providing the air layer (4a) is not particularly limited.
-A method of covering the thermally foamable resin sheet (2) after attaching the spacer (7) or the like to the outer peripheral surface of the storage member (1) (Fig. 5-1),
A method of covering an air layer (4a) by using an excess heat-foamed resin sheet (2) with respect to the length of the outer periphery of the storage member (1) and the folded portion (FIG. 5-2). ),
Etc. The shape of the spacer (7) is not particularly limited as long as the air layer (4a) can be provided. Further, the material is preferably a metal such as iron, stainless steel, aluminum, alumina, titanium, or copper. In the present invention, the spacer (7) may be provided at an arbitrary location on the outer peripheral surface of the storage member (1), but may be provided so as to surround the outer peripheral surface of the storage member (1). By providing such a spacer (7), the heat resistance can be improved.
また、断熱材層(4b)を設ける方法としては、特に限定されないが、例えば、
・収納部材(1)の外周面に断熱材を被覆した後、熱発泡性樹脂シート(2)を被覆する方法、
等が挙げられる。
In addition, the method for providing the heat insulating material layer (4b) is not particularly limited.
A method of coating the heat-foamable resin sheet (2) after coating the outer peripheral surface of the storage member (1) with a heat insulating material;
Etc.
断熱材としては、例えば、ウレタンフォーム、フェノールフォーム、ポリスチレンフォーム等の発泡系断熱材、グラスウール、ロックウール、セルロースファイバー等の繊維系断熱材等の公知の材料が使用でき、これらを収納部材(1)の外周面の少なくとも一部に被覆すればよい。これらの断熱材の被覆方法としては、乾式法あるいは湿式法のどちらでもよく、公知の方法で行えばよい。 As the heat insulating material, for example, known materials such as foam heat insulating materials such as urethane foam, phenol foam, and polystyrene foam, and fiber heat insulating materials such as glass wool, rock wool, and cellulose fiber can be used. It is sufficient to cover at least a part of the outer peripheral surface of As a method for coating these heat insulating materials, either a dry method or a wet method may be used, and a known method may be used.
断熱層(4)を設ける場合も、上記接着剤(3)を用いて熱発泡性樹脂シート(2)を被覆することが好ましい。接着剤(3)を用いる場合、少なくとも収納部材の内側に折り返された部分の熱発泡性樹脂シートが、接着剤で固定されていればよい(図4、図5)。また、必要に応じ、収納部材外周面、断熱材層(4b)、あるいはスペーサー等の任意の場所が接着剤で固定されてもよく、断熱材層(4b)の場合、外周面全体が接着剤(3)で固定されていてもよい。 Also when providing a heat insulation layer (4), it is preferable to coat | cover a thermally foamable resin sheet (2) using the said adhesive agent (3). When the adhesive (3) is used, it is only necessary that at least the portion of the thermally foamable resin sheet folded back inside the storage member is fixed with the adhesive (FIGS. 4 and 5). Further, if necessary, the outer peripheral surface of the storage member, the heat insulating material layer (4b), or any place such as a spacer may be fixed with an adhesive. In the case of the heat insulating material layer (4b), the entire outer peripheral surface is the adhesive. It may be fixed in (3).
断熱層(4)を設けた本発明の被覆構造体は、被覆方法に応じて熱発泡性樹脂シート(2)を発泡させる方向を設定することができる。熱発泡性樹脂シート(2)の発泡方向としては、収納部材(1)に対して、外側方向と内側方向がある。 The covering structure of the present invention provided with the heat insulating layer (4) can set the direction in which the thermally foamable resin sheet (2) is foamed depending on the coating method. The foaming direction of the thermally foamable resin sheet (2) includes an outer direction and an inner direction with respect to the storage member (1).
熱発泡性樹脂シート(2)の発泡方向が外側の場合、断熱層(4)としては空気層(4a)及び/または断熱材層(4b)が使用できる。具体的な被覆方法としては、例えば、
・断熱層(4)が空気層(4a)の場合は、収納部材(1)の外周面にスペーサー(7)等を取り付け、熱発泡性樹脂シート(2)をスペーサー(7)に接着剤等によりに固定させる方法、
・断熱層(4)が断熱材層(4b)の場合は、熱発泡性樹脂シート(2)を接着剤等により断熱材層(4b)に固定させる方法、
等が挙げられる。さらに、熱発泡性樹脂シート(2)として繊維質シートが積層されたものを使用する場合は、繊維質シートが断熱層側(収納部材側)となるように被覆することが好ましい。
When the foaming direction of the thermally foamable resin sheet (2) is the outside, an air layer (4a) and / or a heat insulating material layer (4b) can be used as the heat insulating layer (4). As a specific coating method, for example,
When the heat insulating layer (4) is an air layer (4a), a spacer (7) or the like is attached to the outer peripheral surface of the storage member (1), and the thermally foamable resin sheet (2) is attached to the spacer (7). How to fix by,
When the heat insulating layer (4) is a heat insulating material layer (4b), a method of fixing the heat-foamable resin sheet (2) to the heat insulating material layer (4b) with an adhesive or the like,
Etc. Furthermore, when using what laminated | stacked the fibrous sheet as a thermally foamable resin sheet (2), it is preferable to coat | cover so that a fibrous sheet may become the heat insulation layer side (storage member side).
これに対して、熱発泡性樹脂シート(2)の発泡方向が内側の場合は、断熱層(4)として空気層(4a)を設け、好ましくは図5−2のように収納部材(1)の断面外周の長さに対して余剰の熱発泡性樹脂シート(2)を用い、空気層(4a)を形成する。具体的な被覆方法としては、例えば、
・熱発泡性樹脂シート(2)として繊維質シートが積層されたものを使用し、繊維質シートが外側となるように被覆する方法、
・熱発泡性樹脂シート(2)の外周面を無機繊維質シート(8)で覆う方法、
・熱発泡性樹脂シート(2)として繊維質シートが積層されたものを使用し、繊維質シートが外側となるように被覆し、さらにその外周面を無機繊維質シート(8)で覆う方法(図6)、
等が挙げられる。特に、上記無機繊維質シート(8)で覆うことにより、安定した発泡性を得ることができる。なお、無機繊維質シート(8)で覆う場合、少なくとも無機繊維質シート(8)の端部が接着剤、固定具(タッカー、ステープラ等)等(以下「接着剤等」ともいう。)で固定されていればよい。
On the other hand, when the foaming direction of the thermally foamable resin sheet (2) is the inside, an air layer (4a) is provided as the heat insulating layer (4), and preferably the storage member (1) as shown in FIG. An excess air-foamable resin sheet (2) with respect to the length of the outer periphery of the cross section is used to form an air layer (4a). As a specific coating method, for example,
-A method in which a fibrous sheet is used as the thermally foamable resin sheet (2), and the fibrous sheet is coated on the outside,
A method for covering the outer peripheral surface of the thermally foamable resin sheet (2) with the inorganic fibrous sheet (8),
A method in which a fibrous sheet is laminated as the thermally foamable resin sheet (2), the fibrous sheet is coated on the outside, and the outer peripheral surface is covered with the inorganic fibrous sheet (8) ( (Fig. 6)
Etc. In particular, stable foamability can be obtained by covering with the inorganic fibrous sheet (8). In addition, when covering with an inorganic fiber sheet (8), at least the edge part of an inorganic fiber sheet (8) is fixed with an adhesive agent, fixing tools (a tucker, a stapler, etc.) (henceforth "an adhesive agent"). It only has to be done.
上記無機繊維質シート(8)としては、不燃性を有するものが好ましい。上記無機繊維質シート(8)の目付けは、好ましくは100g/m2以上2000g/m2以下(より好ましくは200g/m2以上1500g/m2以下)である。このような範囲であることにより、高い遮炎性を発揮するとともに、高温下に晒された場合でも、形状保持性に優れ、かつ高い強度を保持することができる。また、熱発泡性樹脂シート(2)が均一な厚みの炭化断熱層を形成することができる。その作用機構は明らかではないが、火災時等の高温下に晒された場合、優れた強度を有する上記無機繊維質シート(8)は熱発泡性樹脂シート(2)の基材として作用するため、熱発泡性樹脂シート(2)が内側方向に均一に発泡し炭化断熱層を形成することができると推察される。 As said inorganic fibrous sheet (8), what has nonflammability is preferable. The basis weight of the inorganic fibrous sheet (8) is preferably 100 g / m 2 or more and 2000 g / m 2 or less (more preferably 200 g / m 2 or more and 1500 g / m 2 or less). By being in such a range, while exhibiting high flame-shielding properties, even when exposed to high temperatures, the shape retainability is excellent and high strength can be maintained. Further, the thermally foamable resin sheet (2) can form a carbonized heat insulating layer having a uniform thickness. The action mechanism is not clear, but when exposed to a high temperature such as in a fire, the inorganic fiber sheet (8) having excellent strength acts as a base material for the thermally foamable resin sheet (2). It is speculated that the thermally foamable resin sheet (2) can foam uniformly in the inner direction to form a carbonized heat insulating layer.
上記無機繊維質シート(8)に使用される無機繊維としては、特に限定されないが、例えば、ロックウール、ガラス繊維、シリカ繊維、アルミナ繊維、シリカ−アルミナ繊維、カーボン繊維、炭化珪素繊維、セラミック繊維、チタン酸カリウム繊維、金属繊維、等が挙げられる。これらは2種以上組み合わせて使用することもできる。このような無機繊維は、優れた耐熱性を有し、高温下でも溶融しにくいため、本発明の効果を発揮することができる。また、本発明では、必要に応じて、アクリル樹脂、ポリウレタン樹脂、シリコーン樹脂等の樹脂により処理された無機繊維を使用することもできる。 The inorganic fiber used in the inorganic fiber sheet (8) is not particularly limited. For example, rock wool, glass fiber, silica fiber, alumina fiber, silica-alumina fiber, carbon fiber, silicon carbide fiber, ceramic fiber. , Potassium titanate fibers, metal fibers, and the like. Two or more of these can be used in combination. Since such inorganic fibers have excellent heat resistance and are difficult to melt even at high temperatures, the effects of the present invention can be exhibited. Moreover, in this invention, the inorganic fiber processed with resin, such as an acrylic resin, a polyurethane resin, a silicone resin, can also be used as needed.
上記無機繊維質シート(8)の態様としては、上記範囲を満たすものであれば特に限定されないが、例えば、織物、不織布、組布、等いずれの態様であってもよい。また、これらは2種以上組み合わせて使用することもできる。その中でも特に、本発明では、織物を使用することが好ましい。これにより、本発明の効果をいっそう高めることができる。 The aspect of the inorganic fibrous sheet (8) is not particularly limited as long as it satisfies the above range, but may be any aspect such as a woven fabric, a nonwoven fabric, a braided fabric, and the like. Moreover, these can also be used in combination of 2 or more types. Among these, in the present invention, it is preferable to use a woven fabric. Thereby, the effect of the present invention can be further enhanced.
なお、本発明において、織物とは、無機繊維束を撚りなどで拘束した繊維糸群により形成されるものであり、たて糸とよこ糸がほぼ直角に上下交錯することにより構成されるものである。その構造としては、平織り、綾織り、朱子織り、たて二重織り、よこ二重織り、たてよこ二重織り、パイル織り、絡み織り、紋織り等が挙げられる。 In the present invention, the woven fabric is formed by a fiber yarn group in which inorganic fiber bundles are constrained by twisting or the like, and is configured by vertically intersecting the warp yarn and the weft yarn substantially at right angles. Examples of the structure include plain weave, twill weave, satin weave, warp double weave, weft double weave, warp double weave, pile weave, twine weave, and crest weave.
また、上記無機繊維質シート(8)は、耐熱温度が500℃以上(より好ましくは700℃以上)であることが好ましい。このような無機繊維質シートとしては、シリカ繊維、アルミナ繊維、シリカ−アルミナ繊維、ステンレス鋼繊維、等の無機繊維より形成されるものが挙げられ、本発明では特に、シリカ繊維を含む繊維織物が好ましい。また、本発明では、必要に応じて、織物の片面及びまたは両面が、アクリル樹脂、ポリウレタン樹脂、シリコーン樹脂等の樹脂によりコーティング、ラミネート等されたものを使用することもできる。 The inorganic fibrous sheet (8) preferably has a heat resistant temperature of 500 ° C. or higher (more preferably 700 ° C. or higher). Examples of such inorganic fibrous sheets include those formed from inorganic fibers such as silica fibers, alumina fibers, silica-alumina fibers, stainless steel fibers, etc. In the present invention, fiber fabrics containing silica fibers are particularly preferred. preferable. Moreover, in this invention, what coated one side and / or both sides of the textile fabric with resin, such as an acrylic resin, a polyurethane resin, and a silicone resin, can also be used as needed.
上記無機繊維質シート(8)の厚みは、0.1〜5mm(より好ましくは0.3〜2mm)であることが好ましい。このような範囲であることにより、本発明の効果がよりいっそう得られやすい。 The inorganic fibrous sheet (8) preferably has a thickness of 0.1 to 5 mm (more preferably 0.3 to 2 mm). By being in such a range, the effects of the present invention are more easily obtained.
図7は、本発明の被覆構造体の別の一例を示す斜視図である。
図7に示すように、本発明の被覆構造体は、収納部材(1)の開口部にカバー(5)を有することができる。カバー(5)の形状は、収納部材(1)の開口部を覆うことができるものであれば特に限定されない。また、その材質は、特に限定されないが、収納部材(1)と同様のものを使用することが好ましい。図7は、当該カバー(5)の少なくとも外周面に熱発泡性樹脂シート(2)が被覆されているものである。これにより、本発明の効果をいっそう高めることができる。熱発泡性樹脂シート(2)の被覆方法としては、特に限定されないが、上記接着剤(3)を用いることが好ましい。また、カバー(5)と熱発泡性樹脂シート(2)の間にも断熱層(4)を設けることができる。
FIG. 7 is a perspective view showing another example of the covering structure of the present invention.
As shown in FIG. 7, the covering structure of the present invention can have a cover (5) at the opening of the storage member (1). The shape of the cover (5) is not particularly limited as long as it can cover the opening of the storage member (1). Moreover, the material is not particularly limited, but it is preferable to use the same material as the storage member (1). In FIG. 7, at least the outer peripheral surface of the cover (5) is covered with a thermally foamable resin sheet (2). Thereby, the effect of the present invention can be further enhanced. Although it does not specifically limit as a coating method of a thermally foamable resin sheet (2), It is preferable to use the said adhesive agent (3). Moreover, a heat insulation layer (4) can also be provided between a cover (5) and a thermally foamable resin sheet (2).
また、本発明の効果を著しく阻害しない範囲内であれば、表面保護性、意匠性等を高める目的で、公知の保護層及び/または化粧層を熱発泡性樹脂シートの上に積層することもできる。このような保護層及び/または化粧層としては、例えば、JIS A6909 建築用仕上塗材、JIS K5658建築用耐候性上塗り塗料、JIS K5660 つや有合成樹脂エマルションペイント、JIS K5663 合成樹脂エマルションペイント、JIS K5668合成樹脂エマルション模様塗料等に規定されるものや、各種シート材料等、あるいは、金属、プラスチック等からなるフィルム材料等が挙げられ、これらを公知の方法で積層すればよい。 In addition, a known protective layer and / or decorative layer may be laminated on the heat-foamable resin sheet for the purpose of improving surface protection, designability, etc., as long as the effect of the present invention is not significantly impaired. it can. Examples of such a protective layer and / or decorative layer include, for example, JIS A6909 building finish coating material, JIS K5658 building weather resistant top coating, JIS K5660 glossy synthetic resin emulsion paint, JIS K5663 synthetic resin emulsion paint, JIS K5668. Examples include those prescribed for synthetic resin emulsion pattern paints, various sheet materials, etc., or film materials made of metal, plastic, etc., and these may be laminated by a known method.
以下に具体的な実施例を示す。
(熱発泡性樹脂シートの製造)
アクリル樹脂100重量部、メラミン90重量部、ジペンタエリスリトール90重量部、ポリリン酸アンモニウム320重量部、酸化チタン100重量部を主成分する混合物を温度120℃に設定した加圧ニーダーで混練して熱発泡性樹脂シート用混練物を調製後、ガラス不織布(目付け30g/m2、厚さ0.25mm)上に混練物を積層し圧延ローラーによってシート状に加工し、膜厚1.5mmの熱発泡性樹脂シート(350mm×500mm)を作製した。
Specific examples are shown below.
(Manufacture of thermally foamable resin sheet)
A mixture containing 100 parts by weight of an acrylic resin, 90 parts by weight of melamine, 90 parts by weight of dipentaerythritol, 320 parts by weight of ammonium polyphosphate, and 100 parts by weight of titanium oxide was kneaded with a pressure kneader set at a temperature of 120 ° C. After preparing a kneaded product for a foamable resin sheet, the kneaded product is laminated on a glass nonwoven fabric (basis weight 30 g / m 2 , thickness 0.25 mm) and processed into a sheet shape by a rolling roller, and heat foaming with a film thickness of 1.5 mm Resin sheet (350 mm × 500 mm) was produced.
(試験例1)
ステンレス鋼製の収納部材(凹型:底面幅100mm、側面高さ60mm、長さ500mm、厚み3.2mm)に、作製した熱発泡性樹脂シートのガラス不織布側が収納部材側となるように熱発泡性樹脂シートをアクリル系接着剤で貼り付けた。このとき、開口部において、熱発泡性樹脂シートの端部を収納部材内面へ折り返し、折り返し部の長さ20mmとなるように被覆し、熱発泡性樹脂シートの余りは切断した。以上より、図2に例示される被覆構造体1を得た。
(評価1)
上記被覆構造体1を試験体とし、ISO834の標準加熱曲線に準じて1時間加熱試験を行った。その結果、均一な炭化断熱層が形成され、良好な耐熱保護性能を示した。
(評価2)
上記被覆構造体1を試験体とし、バーナーを使用し収納部材内部の温度を約500℃に上昇させた。その結果、熱発泡性樹脂シートは、脱落することなく形状を保持していた。
(Test Example 1)
Thermally foamable so that the stainless steel storage member (concave type: bottom width 100 mm, side height 60 mm, length 500 mm, thickness 3.2 mm) has a glass nonwoven fabric side of the produced thermally foamable resin sheet as the storage member side. The resin sheet was affixed with an acrylic adhesive. At this time, the end of the thermally foamable resin sheet was folded back to the inner surface of the storage member at the opening, and the folded portion was covered with a length of 20 mm, and the remainder of the thermally foamable resin sheet was cut. From the above, the covering
(Evaluation 1)
The
(Evaluation 2)
The covering
(試験例2)
ステンレス鋼製の収納部材(凹型:底面幅100mm、側面高さ60mm、長さ500mm、厚み3.2mm)の外周面に、断熱材としてロックウール(厚さ10mm)を被覆した。次いで、作製した熱発泡性樹脂シート1のガラス不織布側が断熱材層側となるように、熱発泡性樹脂シートをアクリル系接着剤で貼り付けた。このとき、開口部において、熱発泡性樹脂シートの端部を収納部材内面へ折り返し、折り返し部の長さ20mmとなるように被覆し、熱発泡性樹脂シートの余りは切断した。以上より、図4に例示される被覆構造体2を得た。
上記被覆構造体2について、上記評価1の評価を行った結果、収納部材の外側方向に均一な炭化断熱層が形成され、良好な耐熱保護性能を示した。またその際、収納部材内部の底面における温度変化を測定した。その結果、収納部材内部の温度上昇も200℃以下に抑制することができた。
さらに上記評価2の結果、熱発泡性樹脂シートは、脱落することなく形状を保持していた。
(Test Example 2)
Rock wool (thickness 10 mm) as a heat insulating material was coated on the outer peripheral surface of a stainless steel storage member (concave type: bottom width 100 mm, side height 60 mm, length 500 mm, thickness 3.2 mm). Next, the thermally foamable resin sheet was affixed with an acrylic adhesive so that the glass nonwoven fabric side of the produced thermally
As a result of performing the
Furthermore, as a result of the
(試験例3)
ステンレス鋼製の収納部材(凹型:底面幅100mm、側面高さ60mm、長さ500mm、厚み3.2mm)の外周面に、空気層(厚さ5mm)を形成するための、スペーサー(鉄製)を設置した。次いで、作製した熱発泡性樹脂シート1のガラス不織布側がスペーサー側(断熱層側)となるように、アクリル系接着剤で貼り付けた。このとき、開口部において、熱発泡性樹脂シートの端部を収納部材内面へ折り返し、折り返し部の長さ20mmとなるように被覆し、熱発泡性樹脂シートの余りは切断した。以上より、図5に例示される被覆構造体3を得た。
上記被覆構造体3について、上記評価1の評価を行った結果、収納部材の外側方向に均一な炭化断熱層が形成され、良好な耐熱保護性能を示した。またその際、収納部材内部の底面における温度変化を測定した。その結果、収納部材内部の温度上昇も200℃以下に抑制することができた。
さらに上記評価2の結果、熱発泡性樹脂シートは、脱落することなく形状を保持していた。
(Test Example 3)
A spacer (made of iron) for forming an air layer (
As a result of performing the
Furthermore, as a result of the
(試験例4)
ステンレス鋼製の収納部材(凹型:底面幅100mm、側面高さ60mm、長さ500mm、厚み3.2mm)の底面外側付近に、空気層が形成されるように、作製した熱発泡性樹脂シート1のガラス不織布側が外側となるように被覆し、収納部材の側面と熱発泡性樹脂シート1の端部をアクリル系接着剤で貼り付けた。このとき、開口部において、熱発泡性樹脂シートの端部を収納部材内面へ折り返し、折り返し部の長さ20mmとなるように被覆し、熱発泡性樹脂シートの余りは切断した。以上より、図5−2に例示される被覆構造体4を得た。
上記被覆構造体4について、上記評価1の評価を行った結果、収納部材の内側方向に均一な炭化断熱層が形成され、良好な耐熱保護性能を示した。またその際、収納部材内部の底面における温度変化を測定した。その結果、収納部材内部の温度上昇も200℃以下に抑制することができた。
さらに上記評価2の結果、熱発泡性樹脂シートは、脱落することなく形状を保持していた。
(Test Example 4)
A heat-
As a result of performing the
Furthermore, as a result of the
((試験例5)
試験例4で得られた被覆構造体4の外側を、さらに無機繊維質シート(シリカ繊維織物(朱子織り)、目付700g/m2、厚さ0.7mm)で覆い、その端部をアクリル系接着剤で貼り付け、図6に例示される被覆構造体5を得た。
上記被覆構造体5について、上記評価1の評価を行った結果、収納部材の内側方向に均一な炭化断熱層が形成され、良好な耐熱保護性能を示した。またその際、収納部材内部の底面における温度変化を測定した。その結果、収納部材内部の温度上昇も200℃以下に抑制することができた。
さらに上記評価2の結果、熱発泡性樹脂シートは、脱落することなく形状を保持していた。
((Test Example 5)
The outer side of the covering
As a result of performing the
Furthermore, as a result of the
Claims (3)
上記収納部材は、上部開口部を有し、ケーブルが収納・取り出し可能な構造であり、
収納部材の外周面に熱発泡性樹脂シートが被覆され、かつ当該収納部材の上部開口部において当該熱発泡性樹脂シートの端部が収納部材内側に折り返されていることを特徴とする被覆構造体。 A covering structure of a storage member for storing a cable ,
The storage member has an upper opening, and has a structure in which a cable can be stored and taken out.
A covering structure characterized in that a heat foamable resin sheet is coated on an outer peripheral surface of a storage member, and an end portion of the heat foamable resin sheet is folded back inside the storage member at an upper opening of the storage member. .
当該カバーの少なくとも外周面に熱発泡性樹脂シートが被覆されたことを特徴とする請求項1または請求項2に記載の被覆構造体。
The storage member has a cover in the upper opening,
The covering structure according to claim 1 or 2, wherein at least an outer peripheral surface of the cover is covered with a thermally foamable resin sheet.