JP6442474B2 - 疎水性の仕上げ剤を含むセメント質の物品 - Google Patents
疎水性の仕上げ剤を含むセメント質の物品 Download PDFInfo
- Publication number
- JP6442474B2 JP6442474B2 JP2016501439A JP2016501439A JP6442474B2 JP 6442474 B2 JP6442474 B2 JP 6442474B2 JP 2016501439 A JP2016501439 A JP 2016501439A JP 2016501439 A JP2016501439 A JP 2016501439A JP 6442474 B2 JP6442474 B2 JP 6442474B2
- Authority
- JP
- Japan
- Prior art keywords
- finish
- ethylene
- copolymers
- mat
- vinyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
(RO)3−Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)のシラン化合物を含む。疎水性の仕上げ剤は、ボード芯に面する内面と反対側の、マットの外面に面する。一部の実施形態において、マットは、石膏系芯の両側にマットを備えた状態で、2つの部分を有して、サンドイッチ構造を形成する。
(RO)3−Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)のシラン化合物を含む、セメント質の芯に面している仕上げ剤組成物を含む物品を提供する。
(RO)3−Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)
の内である。ROアルコキシ基に関しては、一部の実施形態において、メトキシまたはエトキシであってよいが、他のアルコキシ基が予期されかつ含まれ得る。X有機官能基は、任意のこうした疎水性を提供する基、例えば、メチル、エチル、プロピル、ブチル、ペンチル、ヘキシルまたはオクチルなどであってよい。ブチル、ペンチル、ヘキシルおよびオクチル基などの長鎖有機官能基は、増大された疎水性を与えることにおけるそれらの有益な役割のために本発明の一部の実施形態において選択される。
(RO)3−Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)
の内である。
アクリルポリマーおよびコポリマー、ゴム系ポリマーおよびコポリマー、例えばスチレン−ブタジエンゴム、スチレンとアクリルとのコポリマー、酢酸ビニルとエチレンとのコポリマー、塩化ビニルとエチレンとのコポリマー、酢酸ビニルとVeoVa(バーサチック酸のビニルエステル)とのコポリマー、ラウリン酸ビニルとエチレンとのコポリマー、酢酸ビニル、エチレンおよびメタクリル酸メチルのターポリマー、酢酸ビニル、エチレンおよびラウリン酸ビニルのターポリマー、酢酸ビニル、エチレンおよびVeoVa(バーサチック酸のビニルエステル)のターポリマーならびにそれらの任意の組み合わせのうちの1種または複数を含み、膜形成ポリマーが、湿式仕上げ剤の約5重量%から約25重量%の量であり、シラン化合物が、湿式仕上げ剤の約0.1重量%から約5重量%の量のアルキルアルコキシシランであり、ボードが、ANSI A118.10(2008年10月改訂)に従う防水性に関する試験に合格し、ボードが1/2インチ(約12.7mm)厚さのボードとして注型される場合、ボードはASTM C1178/C1178M−11に従って少なくとも約70ポンド(約32kg)の釘引き抜き抵抗を有し、ボードが1/2インチ(約12.7mm)厚さのボードとして注型される場合、ボードは、ASTM C1178/C1178M−11に従って、ボード縁部に平行な少なくとも約80ポンド(約36kg)を支持する縁部および/またはボード縁部に直交する少なくとも約100ポンド(約45kg)を支持する縁部の曲げ強度を有し、水硬性成分が、湿式仕上げ剤の約50重量%から約85重量%の量であり、ならびに/あるいは仕上げ剤が、少なくとも約9のpHを有する。
(RO)3−Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)の内であり、かつ/またはシランが、少なくとも約150の分子量を有する、仕上げ剤組成物を含む。
(RO)3−Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)
のシラン化合物を含む、繊維質マットの外表面に面する疎水性の仕上げ剤を含む。
本実施例は、耐透水性が乏しい未仕上げのガラスマット強化石膏パネルを例示する。
本実施例は、本発明の実施形態による仕上げ済みのパネルに関する改善した耐水性を例示する。
本実施例は、本発明の実施形態による仕上げ済みのパネルに関する改善した耐水性を例示する。半インチ(約12.7mm)厚さのSECUROCK(登録商標)屋根ボードを、セメント質の仕上げ剤の適用のためのベースパネルとして用いた。石膏パネルを製造するために用いたガラスマットは、実質的に多孔質であり、かつ始めは追加の仕上げ剤の存在無しで石膏芯に表面接着していた。
本実施例は、本発明の実施形態による仕上げ済みのパネルに関する改善した耐水性を例示する。半インチ(約12.7mm)厚さのSECUROCK(登録商標)屋根ボードを、セメント質の仕上げ剤の適用のためのベースパネルとして用いた。石膏パネルを製造するために用いたガラスマットは、実質的に多孔質であり、かつ始めは追加の仕上げ剤の存在無しで石膏芯に表面接着していた。
本実施例は、本発明の実施形態による仕上げ済みのパネルに関する改善した耐水性を例示する。半インチ(約12.7mm)厚さのSECUROCK(登録商標)屋根ボードを、セメント質の仕上げ剤の適用のためのベースパネルとして用いた。石膏パネルを製造するために用いたガラスマットは、実質的に多孔質であり、かつ始めは追加の仕上げ剤の存在無しで石膏芯に表面接着していた。
本実施例は、本発明の実施形態による仕上げ済みのパネルに関する改善した耐水性を例示する。本発明の実施形態による仕上げ済みのガラスマットパネルを、表24に示す通りの配合物を有する特別な可撓性のセメント質の仕上げ剤を用いて調製した。具体的には、本実施例は、本発明の実施形態の薄い、可撓性のセメント質の仕上げ剤の耐水性へのシラン、特にオクチルトリエトキシシランの影響を例示する。オクチルトリエトキシシランを、配合物の総重量の0.33%の調剤率(またはフライアッシュ量の0.50wt%)で加えた。
本実施例は、本発明の実施形態による仕上げ済みのパネルに関する改善した耐水性を例示する。本発明の実施形態による仕上げ済みのガラスマットパネルを、表27に示す通りの配合物を有する特別な可撓性のセメント質の仕上げ剤を用いて調製した。具体的には、本実施例は、本発明の実施形態の薄い、可撓性のセメント質の仕上げ剤の耐水性へのオクチルトリエトキシシランなどのシランの影響を例示する。オクチルトリエトキシシランを、配合物の総重量の0.66%の調剤率(またはフライアッシュ量の1.00wt%)で加えた。
本実施例は、本発明の実施形態による仕上げ済みのパネルに関する改善した耐水性を例示する。本発明の仕上げ済みのガラスマットパネルを、表30に示す通りの配合物を有する特別な可撓性のセメント質の仕上げ剤を用いて調製した。具体的には、本実施例は、本発明の実施形態の薄い、可撓性のセメント質の仕上げ剤の耐水性へのオクチルトリエトキシシランなどのシランの影響を例示する。オクチルトリエトキシシランを、配合物の総重量の0.99%の調剤率(またはフライアッシュ量の1.50wt%)で加えた。半インチ(約12.7mm)厚さのSECUROCK(登録商標)屋根ボードを、セメント質の仕上げ剤の適用のためのベースパネルとして用いた。石膏パネルを製造するために用いたガラスマットは、実質的に多孔質でありかつ始めは追加の仕上げ剤の存在無しで石膏芯に表面接着していた。
本実施例は、本発明の実施形態による仕上げ済みのパネルに関する改善した耐水性を例示する。本発明の実施形態による仕上げ済みのガラスマットパネルを、表33に示す通りの配合物を有する特別な可撓性のセメント質の仕上げ剤を用いて調製した。具体的には、本実施例は、本発明の薄い、可撓性のセメント質の仕上げ剤の耐水性へのオクチルトリエトキシシランなどのシランの影響を例示する。オクチルトリエトキシシランを、配合物の総重量の1.97%の調剤率(またはフライアッシュ量の3.00wt%)で加えた。
本実施例は、本発明の実施形態による仕上げ済みのガラスマットパネルによって達成されるASTM C1178(被覆されたガラスマット耐水性石膏下地パネルのための標準仕様)によって要求される機械的特性を例示する。ガラスマットパネルを、表36に示す通りシランを含めた配合物を有する特別な可撓性のセメント質の仕上げ剤を用いて仕上げした。
本実施例は、本発明の実施形態による仕上げ済みのガラスマットパネルに関する釘引き抜き抵抗、曲げ強度、および接着性を例示する。パネルを、表38に示す通りシランを含めた配合物を有する特別な可撓性のセメント質の仕上げ剤を用いて調製した。オクチルトリエトキシシランを、配合物の総重量の0.99%の調剤率(またはフライアッシュ量の1.50wt%)で加えた。半インチ(約12.7mm)厚さのSECUROCK(登録商標)屋根ボードを、セメント質の仕上げ剤の適用のためのベースパネルとして用いた。石膏パネルを製造するために用いたガラスマットは、実質的に多孔質であり、かつ始めは追加の仕上げ剤の存在無しで石膏芯に表面接着していた。
本実施例は、エージングを促進した後の本発明の実施形態による仕上げ済みのガラスマットの引張強度を例示する。具体的には、クラスCフライアッシュが高アルカリ性でありガラスマットを場合によっては劣化させ得るので、本実施例は、スラリーに長期間暴露した後のガラスマットの長期性能を例示する。ガラスマットを、表39に従って調製したスラリーで両面上に手仕上げした。
[付記]
[付記1]
(a)石膏系芯と、
(b)前記石膏系芯の少なくとも1つの面に面している内表面、および反対側の外表面を有する、繊維質マットと、
(c)前記繊維質マットの前記外表面に面している疎水性の仕上げ剤であって、
(i)クラスCフライアッシュと、
(ii)膜形成ポリマーと、
(iii)一般化学式:
(RO) 3 −Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)
のシラン化合物と
を含む、仕上げ剤と
を含む、マット表面の石膏ボード。
[付記2]
前記ボードが、ANSI A118.10(2008年10月改訂)に従う防水性に関する試験に合格する、付記1に記載のボード。
[付記3]
前記ボードが1/2インチ厚さのボードとして注型される場合、前記ボードは、ASTM C1178/C1178M−11に従って少なくとも約70ポンドの釘引き抜き抵抗を有する、付記1または2に記載のボード。
[付記4]
前記膜形成ポリマーが、アクリルポリマーおよびコポリマー、ゴム系ポリマーおよびコポリマー、例えばスチレン−ブタジエンゴム、スチレンとアクリルとのコポリマー、酢酸ビニルとエチレンとのコポリマー、塩化ビニルとエチレンとのコポリマー、酢酸ビニルとVeoVa(バーサチック酸のビニルエステル)とのコポリマー、ラウリン酸ビニルとエチレンとのコポリマー、酢酸ビニル、エチレンおよびメタクリル酸メチルのターポリマー、酢酸ビニル、エチレンおよびラウリン酸ビニルのターポリマー、酢酸ビニル、エチレンおよびVeoVa(バーサチック酸のビニルエステル)のターポリマー、ならびにそれらの任意の組み合わせのうちの1種または複数を含む、付記1〜3のいずれか一つに記載のボード。
[付記5]
前記シランは、前記湿式仕上げ剤の約0.1重量%から約5重量%の量である、付記1〜4のいずれか一つに記載のボード。
[付記6]
前記シランが、オクチルトリエトキシシラン、イソオクチルトリエトキシシラン、オクチルトリメトキシシラン、イソオクチルトリメトキシシラン、ブチルトリエトキシシラン、イソブチルトリエトキシシラン、ブチルトリメトキシシラン、またはイソブチルトリメトキシシランのうちの1種または複数を含む、付記1〜5のいずれか一つに記載のボード。
[付記7]
前記膜形成ポリマーが、アクリルポリマーおよびコポリマー、ゴム系ポリマーおよびコポリマー、例えばスチレン−ブタジエンゴム、スチレンとアクリルとのコポリマー、酢酸ビニルとエチレンとのコポリマー、塩化ビニルとエチレンとのコポリマー、酢酸ビニルとVeoVa(バーサチック酸のビニルエステル)とのコポリマー、ラウリン酸ビニルとエチレンとのコポリマー、酢酸ビニル、エチレンおよびメタクリル酸メチルのターポリマー、酢酸ビニル、エチレンおよびラウリン酸ビニルのターポリマー、酢酸ビニル、エチレンおよびVeoVa(バーサチック酸のビニルエステル)のターポリマー、ならびにそれらの任意の組み合わせであって、前記膜形成ポリマーが、前記湿式仕上げ剤の約5重量%から約25重量%の量であり、
前記シラン化合物が、前記湿式仕上げ剤の約0.1重量%から約5重量%の量のアルキルアルコキシシランであり、
前記ボードが、ANSI A118.10(2008年10月改訂)に従う防水性に関する前記試験に合格し、
前記ボードが、1/2インチ厚さのボードとして注型される場合、前記ボードは、ASTM C1178/C1178M−11に従って少なくとも約70ポンドの釘引き抜き抵抗を有し、
前記ボードが、1/2インチ厚さのボードとして注型される場合、前記ボードは、ASTM C1178/C1178M−11に従って、前記ボード縁部に平行な少なくとも約80ポンドを支持する縁部および/または前記ボード縁部に直交する少なくとも約100ポンドを支持する縁部の曲げ強度を有する、
付記1〜6のいずれか一つに記載のボード。
[付記8]
(a)セメント質の芯と、
(b)ポリマーまたは鉱物繊維を含む繊維質マットであって、前記マットが、前記石膏系芯の少なくとも1つの面に面している内表面、および反対側の外表面を有する、繊維質マットと、
(c)前記繊維質マットの前記外表面に面している疎水性の仕上げ剤であって、前記仕上げ剤が、本質的に
(i)クラスCフライアッシュを含む水硬性成分と、
(ii)アクリルポリマーおよびコポリマー、ゴム系ポリマーおよびコポリマー、例えばスチレン−ブタジエンゴム、スチレンとアクリルとのコポリマー、酢酸ビニルとエチレンとのコポリマー、塩化ビニルとエチレンとのコポリマー、酢酸ビニルとVeoVa(バーサチック酸のビニルエステル)とのコポリマー、ラウリン酸ビニルとエチレンとのコポリマー、酢酸ビニル、エチレンおよびメタクリル酸メチルのターポリマー、酢酸ビニル、エチレンおよびラウリン酸ビニルのターポリマー、酢酸ビニル、エチレンおよびVeoVa(バーサチック酸のビニルエステル)のターポリマー、ならびにそれらの任意の組み合わせの膜形成ポリマーのうちの1種または複数であって、前記湿式仕上げ剤の約5%から約25重量%の量である、膜形成ポリマーと、
(iii)前記湿式仕上げ剤の約0.1重量%から約5重量%の量のアルキルアルコキシシランと
からなる、疎水性の仕上げ剤と、
を含む、マット表面の石膏ボード。
[付記9]
(a)石膏系芯と、
(b)前記石膏系芯の少なくとも1つの面に面している内表面および反対側の外表面を有する繊維質マットと、
(c)前記繊維質マットの前記外表面に面している疎水性の仕上げ剤であって、
(i)クラスCフライアッシュと、
(ii)膜形成ポリマーと、
(iii)少なくとも約150の分子量を有するシラン化合物と
を含む前記仕上げ剤と
を含む、マット表面の石膏ボード。
[付記10]
セメント質の芯材料と、
前記セメント質の芯に面している仕上げ剤組成物であって、クラスCフライアッシュ、膜形成ポリマー、および一般式:
(RO) 3 −Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)
のシラン化合物を含む、仕上げ剤組成物と
を含む物品。
Claims (9)
- (a)石膏系芯と、
(b)前記石膏系芯の少なくとも1つの面に面している内表面、および反対側の外表面を有する、繊維質マットと、
(c)前記繊維質マットの前記外表面と直接的に接触している連続的な疎水性の仕上げであって、
(i)クラスCフライアッシュと、
(ii)膜形成ポリマーと、
(iii)一般化学式:
(RO)3−Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)
のシラン化合物と
を含む湿式疎水性仕上げ剤組成物から調整された、疎水性の仕上げと
を含み、
前記湿式疎水性仕上げ剤組成物は、少なくとも9のpHを有し、
前記湿式疎水性仕上げ剤組成物は、前記クラスCフライアッシュ以外の他の水硬性材料を実質的に含まず、
ANSI A118.10(2008年10月改訂)に従う防水性に関する試験に合格する、
マット表面の石膏ボード。 - 前記ボードが1/2インチ(約12.7mm)厚さのボードとして注型される場合、前記ボードは、ASTM C1178/C1178M−11に従って少なくとも70ポンド(約31.8kg)の釘引き抜き抵抗を有する、請求項1に記載のボード。
- 前記膜形成ポリマーが、アクリルポリマーおよびコポリマー、ゴム系ポリマーおよびコポリマー、スチレンとアクリルとのコポリマー、酢酸ビニルとエチレンとのコポリマー、塩化ビニルとエチレンとのコポリマー、酢酸ビニルとVeoVa(バーサチック酸のビニルエステル)とのコポリマー、ラウリン酸ビニルとエチレンとのコポリマー、酢酸ビニル、エチレンおよびメタクリル酸メチルのターポリマー、酢酸ビニル、エチレンおよびラウリン酸ビニルのターポリマー、酢酸ビニル、エチレンおよびVeoVa(バーサチック酸のビニルエステル)のターポリマー、ならびにそれらの任意の組み合わせのうちの1種または複数を含む、請求項1又は2に記載のボード。
- 前記シランは、前記湿式疎水性仕上げ剤組成物の0.1重量%から5重量%の量である、請求項1〜3のいずれか一項に記載のボード。
- 前記シランが、オクチルトリエトキシシラン、イソオクチルトリエトキシシラン、オクチルトリメトキシシラン、イソオクチルトリメトキシシラン、ブチルトリエトキシシラン、イソブチルトリエトキシシラン、ブチルトリメトキシシラン、またはイソブチルトリメトキシシランのうちの1種または複数を含む、請求項1〜4のいずれか一項に記載のボード。
- 前記膜形成ポリマーが、アクリルポリマーおよびコポリマー、ゴム系ポリマーおよびコポリマー、スチレンとアクリルとのコポリマー、酢酸ビニルとエチレンとのコポリマー、塩化ビニルとエチレンとのコポリマー、酢酸ビニルとVeoVa(バーサチック酸のビニルエステル)とのコポリマー、ラウリン酸ビニルとエチレンとのコポリマー、酢酸ビニル、エチレンおよびメタクリル酸メチルのターポリマー、酢酸ビニル、エチレンおよびラウリン酸ビニルのターポリマー、酢酸ビニル、エチレンおよびVeoVa(バーサチック酸のビニルエステル)のターポリマー、ならびにそれらの任意の組み合わせであって、前記膜形成ポリマーが、前記湿式疎水性仕上げ剤組成物の5重量%から25重量%の量であり、
前記シラン化合物が、前記湿式疎水性仕上げ剤組成物の0.1重量%から5重量%の量のアルキルアルコキシシランであり、
前記ボードが、1/2インチ(約12.7mm)厚さのボードとして注型される場合、前記ボードは、ASTM C1178/C1178M−11に従って少なくとも70ポンド(約31.8kg)の釘引き抜き抵抗を有する、
請求項1〜5のいずれか一項に記載のボード。 - (a)石膏系芯と、
(b)ポリマーまたは鉱物繊維を含む繊維質マットであって、前記マットが、前記石膏系芯の少なくとも1つの面に面している内表面、および反対側の外表面を有する、繊維質マットと、
(c)前記繊維質マットの前記外表面と直接的に接触している連続的な疎水性の仕上げであって、湿式疎水性仕上げ剤組成物から調整され、前記湿式疎水性仕上げ剤組成物が、本質的に
(i)クラスCフライアッシュを含む水硬性成分と、
(ii)アクリルポリマーおよびコポリマー、ゴム系ポリマーおよびコポリマー、スチレンとアクリルとのコポリマー、酢酸ビニルとエチレンとのコポリマー、塩化ビニルとエチレンとのコポリマー、酢酸ビニルとVeoVa(バーサチック酸のビニルエステル)とのコポリマー、ラウリン酸ビニルとエチレンとのコポリマー、酢酸ビニル、エチレンおよびメタクリル酸メチルのターポリマー、酢酸ビニル、エチレンおよびラウリン酸ビニルのターポリマー、酢酸ビニル、エチレンおよびVeoVa(バーサチック酸のビニルエステル)のターポリマー、ならびにそれらの任意の組み合わせの膜形成ポリマーのうちの1種または複数であって、前記湿式疎水性仕上げ剤組成物の5%から25重量%の量である、膜形成ポリマーと、
(iii)前記湿式疎水性仕上げ剤組成物の0.1重量%から5重量%の量のアルキルアルコキシシランと
からなる、疎水性の仕上げと、
を含み、
前記湿式疎水性仕上げ剤組成物は、少なくとも9のpHを有し、
前記湿式疎水性仕上げ剤組成物は、前記クラスCフライアッシュ以外の他の水硬性材料を実質的に含まず、
ANSI A118.10(2008年10月改訂)に従う防水性に関する試験に合格する、
マット表面の石膏ボード。 - (a)石膏系芯と、
(b)前記石膏系芯の少なくとも1つの面に面している内表面および反対側の外表面を有する繊維質マットと、
(c)前記繊維質マットの前記外表面と直接的に接触している連続的な疎水性の仕上げであって、
(i)クラスCフライアッシュと、
(ii)膜形成ポリマーと、
(iii)少なくとも150の分子量を有するシラン化合物と
を含む湿式疎水性仕上げ剤組成物から調整された、疎水性の仕上げと
を含み、
前記湿式疎水性仕上げ剤組成物は、少なくとも9のpHを有し、
前記湿式疎水性仕上げ剤組成物は、前記クラスCフライアッシュ以外の他の水硬性材料を実質的に含まず、
ANSI A118.10(2008年10月改訂)に従う防水性に関する試験に合格する、
マット表面の石膏ボード。 - (a)セメント質の芯材料と、
(b)前記セメント質の芯材料の少なくとも1つの面に面している内表面および反対側の外表面を有する繊維質マットと、
(c)前記セメント質の芯材料と直接的に接触している連続的な仕上げ剤組成物であって、クラスCフライアッシュ、膜形成ポリマー、および一般式:
(RO)3−Si−X、
(式中、ROはアルコキシ基およびXは有機官能基である)
のシラン化合物を含む湿式疎水性仕上げ剤組成物から調整された、疎水性の仕上げ剤組成物と
を含み、
前記湿式疎水性仕上げ剤組成物は、少なくとも9のpHを有し、
前記湿式疎水性仕上げ剤組成物は、前記クラスCフライアッシュ以外の他の水硬性材料を実質的に含まず、
ANSI A118.10(2008年10月改訂)に従う防水性に関する試験に合格する、
物品。