JP6432762B2 - ハードコートフィルム及び画像表示装置 - Google Patents
ハードコートフィルム及び画像表示装置 Download PDFInfo
- Publication number
- JP6432762B2 JP6432762B2 JP2014147720A JP2014147720A JP6432762B2 JP 6432762 B2 JP6432762 B2 JP 6432762B2 JP 2014147720 A JP2014147720 A JP 2014147720A JP 2014147720 A JP2014147720 A JP 2014147720A JP 6432762 B2 JP6432762 B2 JP 6432762B2
- Authority
- JP
- Japan
- Prior art keywords
- hard coat
- coat layer
- film
- hardness
- coat film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
なお、上記マルテンス硬さは、本発明のハードコートフィルムを構成する第一のハードコート層(X)及び第二のハードコート層(Y)の表面を、フィッシャースコープHM2000Xyp(フィッシャーインストルメンツ社)を用い、稜間角136°のビッカース圧子を1mN荷重にて押し込んで測定した値であって、ビッカース圧子によりハードコート層の表面を押し込んだときの試験荷重と押し込み表面積から求められるハードコート層の硬さ(凹み難さ)を表し、ハードコート層の表面の硬さの指標となるものである。
本発明のハードコートフィルムを構成する基材としては、厚さが50μm〜160μmのものを使用することが好ましく、60μm〜130μmのものを使用することがより好ましく、70μm〜130μmのものを使用することがさらに好ましい。前記範囲の厚さの基材を使用することによって、薄型で、かつ、カールの発生させにくいハードコートフィルムを得ることができる。
本発明のハードコートフィルムは、前記基材の一方の面に第一のハードコート層(X)を有する。
本発明のハードコートフィルムは、前記基材の他方の面に第二のハードコート層(Y)を有する。具体的には、本発明のハードコートフィルムは、前記基材のうち、前記第一のハードコート層(X)が設けられた面とは逆の面に、前記第二のハードコート層(Y)が設けられたものである。
本発明のハードコートフィルムは、はじめに前記基材の一方の面に、第一のハードコート層(X)を形成するハードコート剤を塗布し、乾燥させた後、硬化させることで第一のハードコート層(X)を形成する工程(1)、第一のハードコート層(X)が設けられた面に対して逆の面に、第二のハードコート層(Y)を形成するハードコート剤を塗布し乾燥させた後、硬化させることで第二のハードコート層(Y)を形成する工程(2)を経ることによって製造することができる。
また、前記ハードコートフィルムは、はじめに前記基材の一方の面に第二のハードコート層(Y)を形成し、次に、前記基材の他方の面(第二のハードコート層(Y)が設けられた面に対して逆側の面)に第一のハードコート層(X)を形成することによって製造することもできる。
上記方法で得た本発明のハードコートフィルムは、例えば第二のハードコート層(Y)側から打ち抜き加工刃を挿入させた場合であっても、その加工刃と接触する第二のハードコート層(Y)とは他面を構成する第一のハードコート層(X)の変形を抑制でき、その結果、ハードコート層(X)及び(Y)の両方の割れを好適に抑制できる。
前記強化ガラスとしては、例えば板状の強化ガラスであればその表裏面が物理的強化法または化学的強化法等によって強化されたもの、その表裏側面の全6面が物理的強化法または化学的強化法等によって強化された、いわゆる6面強化ガラスを使用することもできる。
<ウレタンアクリレート(A1)の合成>
攪拌機、ガス導入管、冷却管及び温度計を備えたフラスコに、酢酸ブチル250質量部、ノルボルナンジイソシアネート206質量部、p−メトキシフェノール0.5質量部、ジブチル錫ジアセテート0.5質量部を仕込み、空気を吹き込みながら、70℃に昇温した後、ペンタエリスリトールトリアクリレート(以下、「PE3A」と省略。)とペンタエリスリトールテトラアクリレート(以下、「PE4A」と省略。)との混合物(質量比PE3A/PE4A=75/25の混合物)795質量部を1時間かけて滴下した。
<ウレタンアクリレート(A2)の合成>
攪拌機、ガス導入管、冷却管及び温度計を備えたフラスコに、酢酸ブチル254質量部、イソホロンジイソシアネート222質量部、p−メトキシフェノール0.5質量部、ジブチル錫ジアセテート0.5質量部を仕込み、70℃に昇温した後、PE3AとPE4Aとの混合物(質量比PE3A/PE4A=75/25の混合物)795質量部を1時間かけて滴下した。
<ウレタンアクリレート(A3)の合成>
攪拌機、ガス導入管、冷却管及び温度計を備えたフラスコに、酢酸ブチル254質量部、イソホロンジイソシアネート222質量部、p−メトキシフェノール0.5質量部、ジブチル錫ジアセテート0.5質量部を仕込み、70℃に昇温した後、ビス(アクリロキシエチル)ヒドロキシエチルイソシアヌレート369質量部、及び、PE3AとPE4Aとの混合物(質量比PE3A/PE4A=75/25の混合物)398質量部を1時間かけて滴下した。
<ウレタンアクリレート(A4)の合成>
撹拌機、ガス導入管、コンデンサー及び温度計を備えたフラスコに、PE3AとPEA4との混合物(質量比PE3A/PE4A=60/40の混合物)549.1質量部、ジブチル錫ジアセテート0.1質量部、スミライザーBHT〔住友化学工業(株)製、酸化防止剤〕0.6質量部、メトキノン〔精工化学工業(株)製、重合禁止剤〕0.1質量部、および、酢酸ブチル160.0質量部を加え、均一に混合しながら徐々に昇温した。60℃に達したところでデスモジュールH〔住友バイエルウレタン(株)製、ヘキサメチレンジイソシアネート、NCO%=50質量%)90.9質量部を加えた後、80℃で5時間反応させることによって、ウレタンアクリレート(A4)とPE4Aとを含有する酢酸ブチル溶液(不揮発分80質量%)を得た。
<ウレタンアクリレート(A5)>
撹拌機、空気導入管、コンデンサー及び温度計を備えたフラスコに、アロニックスM−305〔東亜合成(株)製、PE3AとPE4Aとの混合物〕535.5質量部、ジブチル錫ジアセテート0.1質量部、スミライザーBHT〔住友化学工業(株)製、酸化防止剤〕1.9質量部、メトキノン〔精工化学工業(株)製、重合禁止剤〕0.2質量部、および、酢酸ブチル161.6質量部を加え、均一に混合しながら徐々に昇温した。60℃に達したところでデスモジュールI〔住友バイエルウレタン(株)製、イソホロンジイソシアネート〕111質量部を加えた後、80℃で5時間反応させることによって、ウレタンアクリレート(A5)とPE4Aとを含有する酢酸ブチル溶液(不揮発分80質量%)を得た。
酢酸エチル23.01質量部、合成例1で得たウレタンアクリレート(A1)とPE4Aとを含有する酢酸ブチル溶液19.64質量部、合成例2で得たウレタンアクリレート(A2)とPE4Aとを含有する酢酸ブチル溶液19.64質量部、合成例3で得たウレタンアクリレート(A3)とPE4Aとを含有する酢酸ブチル溶液15.71質量部、ジペンタエリスリトールヘキサアクリレート18.86質量部、光開始剤である1−ヒドロキシシクロヘキシルフェニルケトン2.51質量部、光開始剤であるジフェニル2,4,6−トリメチルベンゾイルホスフィンオキシド0.63質量部、反応性フッ素防汚剤(オプツールDAC−HP;ダイキン工業株式会社製、不揮発分20質量%)2.0質量部を均一に混合した後、不揮発分が40質量%になるようにプロピレングリコールモノメチルエーテルで希釈することによってハードコート剤(1)を調製した。
酢酸エチル23.01質量部、合成例1で得たウレタンアクリレート(A1)とPE4Aとを含有する酢酸ブチル溶液19.64質量部、合成例2で得たウレタンアクリレート(A2)とPE4Aとを含有する酢酸ブチル溶液19.64質量部、合成例3で得たウレタンアクリレート(A3)とPE4Aとを含有する酢酸ブチル溶液15.71質量部、ジペンタエリスリトールヘキサアクリレート18.86質量部、光開始剤である1−ヒドロキシシクロヘキシルフェニルケトン2.51質量部、光開始剤であるジフェニル2,4,6−トリメチルベンゾイルホスフィンオキシド0.63質量部を均一に混合した後、不揮発分が40質量%になるようにプロピレングリコールモノメチルエーテルで希釈することによってハードコート剤(2)を調製した。なお、前記ハードコート剤(2)を前記標準基材に塗布等し形成されたハードコート層それ自体の塑性硬さは、682N/mm2であり、マルテンス硬さは257N/mm2であった。
酢酸エチル34.66質量部、合成例2で得たウレタンアクリレート(A2)とPE4Aとを含有する酢酸ブチル溶液47.08質量部、ジペンタエリスリトールヘキサアクリレート12.74質量部、光開始剤である1−ヒドロキシシクロヘキシルフェニルケトン1.30質量部、光開始剤であるジフェニル2,4,6−トリメチルベンゾイルホスフィンオキシド0.92質量部、反応性フッ素防汚剤(オプツールDAC−HP;ダイキン工業株式会社製、不揮発分20質量%)2.0質量部を均一に混合した後、不揮発分が40質量%になるようにプロピレングリコールモノメチルエーテルで希釈することによってハードコート剤(3)を調製した。なお、前記ハードコート剤(3)を前記標準基材に塗布等し形成されたハードコート層それ自体の塑性硬さは、530N/mm2であり、マルテンス硬さは220N/mm2であった。
合成例4で得たウレタンアクリレート(A4)とPE4Aとを含有する酢酸ブチル溶液と、酢酸ブチルとを混合し不揮発分濃度が35質量%である混合液を調製した後、イルガキュア#184〔チバ・スペシャリテイー・ケミカルズ(株)製、光重合開始剤、1−ヒドロキシ−シクロヘキシル−フェニル−ケトン〕3.2質量部を配合することによってハードコート剤(4)を調製した。なお、前記ハードコート剤(4)を前記標準基材に塗布等し形成されたハードコート層それ自体の塑性硬さは、804N/mm2であり、マルテンス硬さは262N/mm2であった。
合成例5で得たウレタンアクリレート(A5)の酢酸ブチル溶液と、酢酸ブチルとを混合することによって不揮発分濃度を35質量%に調整した後、イルガキュア#184〔チバ・スペシャリテイー・ケミカルズ(株)製、光重合開始剤、1−ヒドロキシ−シクロヘキシル−フェニル−ケトン〕5質量部を配合することによってハードコート剤(5)を調製した。なお、前記ハードコート剤(5)を前記標準基材に塗布等し形成されたハードコート層それ自体の塑性硬さは、646N/mm2であり、マルテンス硬さは222N/mm2であった。
基材として、厚さ125μmのポリエチレンテレフタレートからなるフィルム(コスモシャインA4300、東洋紡株式会社製、弾性率4GPa)を使用し、当該基材の片面に、上記で調製したハードコート剤(2)を塗布し、60℃で90秒間乾燥した後、空気雰囲気下で紫外線照射装置(フュージョンUVシステムズ・ジャパン株式会社製「F450」、ランプ:120W/cm、Hバルブ)を用いて、照射光量0.5J/cm2で紫外線を照射することによって、厚さが3μmの第一のハードコート層を形成した。
基材として厚さ125μmのポリエチレンテレフタレートからなるフィルムの代わりに、厚さ100μmのポリエチレンテレフタレートからなるフィルム(コスモシャインA4300、東洋紡株式会社製、弾性率4GPa)を使用したこと以外は、実施例1と同様にして、総厚113μmのハードコートフィルム(X−2)を得た。
基材として厚さ125μmのポリエチレンテレフタレートからなるフィルムの代わりに、厚さ75μmのポリエチレンテレフタレートからなるフィルム(コスモシャインA4300、東洋紡株式会社製、弾性率4GPa)を使用したこと以外は、実施例1と同様にして、総厚88μmのハードコートフィルム(X−3)を得た。
第一のハードコート層の厚さを3μmから6μmに変更したこと以外は、実施例3と同様にして、総厚91μmのハードコートフィルム(X−4)を得た。
ハードコート剤(2)の代わりにハードコート剤(5)を使用したこと以外は、実施例1と同様の方法で、総厚138μmのハードコートフィルム(X−5)を得た。
ハードコート剤(2)の代わりにハードコート剤(3)を使用したこと以外は、実施例1と同様の方法で、総厚138μmのハードコートフィルム(X−6)を得た。
ハードコート剤(1)の代わりにハードコート剤(4)を使用したこと以外は、実施例1と同様の方法で、総厚138μmのハードコートフィルム(X−7)を得た。
ハードコート剤(2)の代わりにハードコート剤(3)を使用し、ハードコート剤(1)の代わりにハードコート剤(5)を使用したこと以外は、実施例1と同様の方法で、総厚138μmのハードコートフィルム(X−8)を得た。
ハードコート剤(2)の代わりにハードコート剤(5)を使用し、ハードコート剤(1)の代わりにハードコート剤(2)を使用したこと以外は、実施例1と同様の方法で、総厚138μmのハードコートフィルム(X−9)を得た。
第一のハードコート層の厚さを1μmとし、第二のハードコート層の厚さを8μmとした以外は、実施例1と同様の方法で、総厚134μmのハードコートフィルム(X−10)を得た。
ハードコート剤(2)の代わりにハードコート剤(4)を使用したこと以外は、実施例1と同様の方法で、総厚138μmのハードコートフィルム(X’−1)を得た。
基材として、厚さ75μmのポリエチレンテレフタレートからなるフィルム(コスモシャインA4300、東洋紡株式会社製、弾性率4GPa)を使用した以外は、比較例1と同様にして、総厚88μmのハードコートフィルム(X’−2)を得た。
ハードコート剤(1)の代わりにハードコート剤(3)を使用したこと以外は、実施例1と同様の方法で、総厚138μmのハードコートフィルム(X’−3)を得た。
ハードコート剤(2)の代わりにハードコート剤(1)を使用したこと以外は、実施例1と同様の方法で、総厚138μmのハードコートフィルム(X’−4)を得た。
第一のハードコート層の厚さを10μmとし、第二のハードコート剤に使用するハードコート剤にハードコート剤(4)を使用したこと以外は、実施例1と同様の方法で、総厚145μmのハードコートフィルム(X’−5)を得た。
上記ハードコートフィルムを20cm×20cm角に切り、80℃環境下に1時間放置した試験フィルムを、黒地の平滑な面の上に置き、その試験フィルムの表面に映る光(蛍光灯の光)の歪みを目視で観察した。
×:歪みあり
上記ハードコートフィルムを10cm角に切り、25℃の環境下に1日静置した後、平滑な面の上に置いた。
○:4隅のカールの高さ(平均値)が3以上5mm未満
×:4隅のカールの高さ(平均値)が5mm超
上記ハードコートフィルムを10cm角に切り、80℃の環境下に1時間静置した後、25℃の環境下の平滑な面の上に置いて30分間静置した。
○:4隅のカールの高さ(平均値)が5以上8mm未満
×:4隅のカールの高さ(平均値)が8mm超
ビク刃(刃角42度)を用いてハードコートフィルムを構成する第二のハードコート層側から直径3mmの円形に打ち抜いた。第二のハードコート層の表面からマイクロスコープ(300倍)を用いて、第一のハードコート層および第二のハードコート層のクラック発生状況を観察した。判定基準は下記のとおりである。
○:第一および第二のハードコート層にごくわずかにクラックが発生していたが、実用上問題となるレベルの著しいクラックは発生していなかった。
△:第一および第二のハードコート層にわずかなクラックが発生していた。
×:第一および第二のハードコート層に著しいクラックが発生していた。
Claims (8)
- 基材の一方の面に厚さ1μm〜6μmの第一のハードコート層(X)が設けられ、他方の面に厚さ6μm超え15μm以下の第二のハードコート層(Y)が設けられたハードコートフィルムであって、前記第二のハードコート層(Y)の塑性硬さが、前記第一のハードコート層(X)の塑性硬さよりも大きく、前記ハードコートフィルムの前記第一のハードコート層(X)によって構成される面の鉛筆硬度がH以上であり、前記第二のハードコート層(Y)によって構成される面の鉛筆硬度が3H以上であることを特徴とするハードコートフィルム。
- 前記第一のハードコート層(X)の厚さが、前記第二のハードコート層(Y)の厚さの3/5以下である請求項1に記載のハードコートフィルム。
- 前記第一のハードコート層(X)及び第二のハードコート層(Y)の塑性硬さが850N/mm2以下である請求項1に記載のハードコートフィルム。
- 前記基材の厚さが50μm〜160μmである請求項1に記載のハードコートフィルム。
- 前記第一のハードコート層(X)の厚さと前記第二のハードコート層(Y)の厚さとの和が10μmを超える請求項1に記載のハードコートフィルム。
- 前記第一のハードコート層(X)の一部または全部に加飾層または粘着剤層が設けられたものである請求項1に記載のハードコートフィルム。
- 請求項1〜6のいずれか1項に記載のハードコートフィルムが画像表示部の上面に設置された画像表示装置。
- 前記ハードコートフィルムを構成する第一のハードコート層(X)が前記画像表示部と接する側の層を構成し、前記ハードコートフィルムを構成する第二のハードコート層(Y)がその反対側の層(表面層)を構成する請求項7に記載の画像表示装置。