JP6323580B1 - 粘着剤および粘着シート - Google Patents
粘着剤および粘着シート Download PDFInfo
- Publication number
- JP6323580B1 JP6323580B1 JP2017024749A JP2017024749A JP6323580B1 JP 6323580 B1 JP6323580 B1 JP 6323580B1 JP 2017024749 A JP2017024749 A JP 2017024749A JP 2017024749 A JP2017024749 A JP 2017024749A JP 6323580 B1 JP6323580 B1 JP 6323580B1
- Authority
- JP
- Japan
- Prior art keywords
- polyol
- pressure
- sensitive adhesive
- bifunctional
- examples
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
本明細書において、「粘着剤」は再剥離性を有する粘着剤(再剥離型粘着剤)であり、「粘着シート」は再剥離性を有する粘着シート(再剥離粘着シート)である。
ウレタン系粘着シートは、フラットパネルディスプレイおよびタッチパネルディスプレイ、並びに、これらの製造工程で製造または使用される基板(ガラス基板、およびガラス基板上にITO(インジウム酸化錫)膜が形成されたITO/ガラス基板等)および光学部材等の表面保護シートとして好適に用いられる。
特許文献1において、好ましくは、ポリエーテルポリオール(a)はポリエーテルジオールとポリエーテルトリオールとの混合物である(請求項3)。
特許文献2には、ポリウレタンポリオールの原料ポリオールとして、2官能ポリオールと3官能以上のポリオールとを併用したポリウレタンポリオールの合成例が開示されている(合成例1〜5)。
本発明者の知見によれば、特許文献1の実施例1〜12のウレタン系粘着剤は濡れ性が不充分であり、粘着シートを被着体に貼着する際に貼着界面に気泡を巻き込みやすい(後記[実施例]の項の比較例2を参照されたい。)。
本発明者の知見によれば、上記合成例1〜3、5のポリウレタンポリオールを用いた特許文献2の実施例1〜15、17、18のウレタン系粘着剤では、良好な湾曲性を有する粘着層を形成することは難しい(後記[実施例]の項の比較例1を参照されたい。)。また、特許文献2のこれらの実施例では、濡れ性を向上するために、可塑剤((C)成分)が用いられており、再剥離後に被着体の表面に粘着剤が残る被着体汚染の課題もある(後記[実施例]の項の比較例1を参照されたい。)。
3官能以上のポリオール(x2)を含むポリオール(x)とポリイソシアネート(y)との反応生成物であるポリウレタンポリオール(A)と、
多官能イソシアネート化合物(B)とを含む粘着剤であって、
3官能以上のポリオール(x2)が、1分子中に1つ以上のエチレンオキシ(EO)基を有し、数平均分子量(Mn)が3,000超である3官能以上のポリエーテルポリオール(x2H)を含み、
ポリイソシアネート(y)が2官能イソシアネート化合物(y1)を含むものである。
一般的に、シート状物は、厚みおよび幅に応じて、「テープ」、「フィルム」、または「シート」と称される。本明細書では、これらを特に区別せず、これらを包括する概念を表す用語として「シート」の用語を使用するものとする。
3官能以上のポリオール(x2)を含むポリオール(x)とポリイソシアネート(y)との反応生成物であるポリウレタンポリオール(A)と、
多官能イソシアネート化合物(B)とを含み、
3官能以上のポリオール(x2)が、1分子中に1つ以上のエチレンオキシ(EO)基を有し、数平均分子量(Mn)が3,000超である3官能以上のポリエーテルポリオール(x2H)を含み、
ポリイソシアネート(y)が2官能イソシアネート化合物(y1)を含むウレタン系粘着剤である。
本発明の粘着シートは、テープ、ラベル、シール、および両面テープ等の形態で、使用することができる。本発明の粘着シートは、表面保護シート、化粧用シート、および滑り止めシート等として好適に使用される。
液晶ディスプレイ(LCD)および有機エレクトロルミネセンスディスプレイ(OELD)等のフラットパネルディスプレイ、並びに、かかるフラットパネルディスプレイとタッチパネルとを組み合わせたタッチパネルディスプレイは、テレビ(TV)、パーソナルコンピュータ(PC)、携帯電話、および携帯情報端末等の電子機器に広く使用されている。
本発明の粘着シートは、フラットパネルディスプレイおよびタッチパネルディスプレイ(これらを総称して単に「ディスプレイ」ともいう)、並びに、これらの製造工程で製造または使用される基板(ガラス基板、およびガラス基板上にITO(インジウム酸化錫)膜が形成されたITO/ガラス基板等)および光学部材等の表面保護シートとして好適に用いられる。
(ポリウレタンポリオール(A))
ポリウレタンポリオール(A)は、1種以上のポリオール(x)と1種以上のポリイソシアネート(y)とを共重合反応させて得られる反応生成物である。ポリウレタンポリオール(A)は、1種以上用いることができる。共重合反応は必要に応じて、触媒存在下で行うことができる。共重合反応には必要に応じて、溶媒を用いることができる。
ポリオール(x)は、少なくとも、1種以上の3官能以上のポリオール(x2)を含む。好ましくは、ポリオール(x)は、1種以上の2官能ポリオール(x1)と1種以上の3官能以上のポリオール(x2)とを含む。
ポリオール(x)としてポリエステルポリオールおよび/またはポリエーテルポリオールを用いる場合、好ましい数平均分子量(Mn)は以下の通りである。
ポリエステルポリオールの数平均分子量(Mn)は、好ましくは500〜5,000、より好ましくは600〜4,000、特に好ましくは800〜3,000である。Mnが500以上であることで、ポリウレタンポリオール(A)のゲル化が効果的に抑制される。Mnが5,000以下であることで、ポリウレタンポリオール(A)の凝集力が好適となる。
ポリエーテルポリオールの数平均分子量(Mn)は、好ましくは500〜5,000、より好ましくは600〜4,000、特に好ましくは800〜3,000である。Mnが500以上であることで、ポリウレタンポリオール(A)のゲル化が効果的に抑制される。Mnが5,000以下であることで、ポリウレタンポリオール(A)の凝集力が好適となる。
好ましくは、1種以上の2官能ポリオール(x1)と1種以上の3官能以上のポリオール(x2)とを併用する。一般的に、2官能ポリオール(x1)は2次元架橋性を有し、粘着層に適度な柔軟性を付与することができ、3官能以上のポリオール(x2)は3次元架橋性を有し、粘着層に適度な硬さを付与することができる。これらを併用することで、好適な凝集力と粘着力を有する粘着層を得ることが可能となる。
ポリウレタンポリオール(A)の原料ポリオールとして、EO基を有し、数平均分子量(Mn)が3,000超である3官能以上のポリエーテルポリオール(x2H)を用いることで、湾曲性に優れた粘着層を形成することが可能な粘着剤を提供することができる。3官能以上のポリオールの分子量を従来よりも高くすることで、3官能以上のポリオールの架橋点の数を低減できる結果、粘着層にエラストマー性/ゴム弾性に近いような性質が発現し、粘着層の湾曲性が向上すると考えられる。
3官能以上のポリエーテルポリオール(x2H)の数平均分子量(Mn)の上限は特に制限されない。ポリウレタンポリオール(A)の凝集力が好適となることから、3官能以上のポリエーテルポリオール(x2H)の数平均分子量(Mn)は、好ましくは25,000以下、より好ましくは20,000以下、特に好ましくは15,000以下、最も好ましくは10,000以下である。
3官能以上のポリオール(x2)として、比較的分子量の大きいポリエーテルポリオール(x2H)のみを用いる場合、粘着層の粘着力が高めになる傾向がある。比較的分子量の小さいポリオール(x2L)を併用することで、比較的分子量の大きいポリエーテルポリオール(x2H)を用いたことによって増加する粘着層の粘着力を下げて好適な範囲内に調整することができる。なお、3官能以上のポリオール(x2L)は、EO基を有するものであってもよいし、有さないものであってもよい。
基材密着性および被着体汚染抑制等の観点から、2官能ポリオール(x1)は、2官能ポリエーテルポリオールを含むことが好ましい。
EO基を有する2官能ポリエーテルポリオールは、上記の2官能開始剤にエチレンオキシド(EO)を含む1種以上のオキシラン化合物を付加重合させて得られる化合物(付加重合物)である。中でも、上記の2官能開始剤にエチレンオキシド(EO)を含む1種以上のアルキレンオキシド(AO)を付加重合させて得られるポリアルキレングリコールが好ましい。ポリアルキレングリコール中のEO基の含有量は、多い程好ましい。EO基の含有量が多いことから、EO基を有する2官能ポリエーテルポリオールとしては、ポリエチレングリコール(PEG)が特に好ましい。すなわち、1種以上のEO基を有する2官能ポリエーテルポリオールは、PEGを含むことが好ましい。なお、EO基を有する3官能以上のポリエーテルポリオール中のEO基量の上限は特に制限されず、好ましくはポリオールの分子量中50質量%である。
2官能ポリオール(x1)の数平均分子量(Mn)は、好ましくは200〜6,000、より好ましくは200〜4,000、特に好ましくは200〜2,000である。
ポリオール(x)の合計量を100質量部としたとき、
2官能ポリオール(x1)の量が0〜90質量部であり、3官能以上のポリオール(x2)の量が100〜10質量部であることが好ましく、
2官能ポリオール(x1)の量が5〜70質量部であり、3官能以上のポリオール(x2)の量が95〜30質量部であることがより好ましく、
2官能ポリオール(x1)の量が10〜50質量部であり、3官能以上のポリオール(x2)の量が90〜50質量部であることが特に好ましい。
ポリオール(x)の合計量を100質量部としたとき、
2官能ポリオール(x1)の量が0〜90質量部であり、3官能以上のポリエーテルポリオール(x2H)の量が100〜5質量部であり、3官能以上のポリオール(x2L)の量が0〜50質量部であることが好ましく、
ポリオール(x)の合計量を100質量部としたとき、
2官能ポリオール(x1)の量が2〜70質量部であり、3官能以上のポリエーテルポリオール(x2H)の量が98〜25質量部であり、3官能以上のポリオール(x2L)の量が0〜40質量部であることがより好ましく、
ポリオール(x)の合計量を100質量部としたとき、
2官能ポリオール(x1)の量が5〜50質量部であり、3官能以上のポリエーテルポリオール(x2H)の量が95〜50質量部であり、3官能以上のポリオール(x2L)の量が0〜30質量部であることが特に好ましい。
また、3官能以上のポリオール(x2)の量を2官能ポリオール(x1)の量より過剰とすることが好ましい。これにより粘着層のエラストマー的な性質がより高まる。
ポリイソシアネート化合物(y)としては公知のものを使用でき、芳香族ポリイソシアネート、脂肪族ポリイソシアネート、芳香脂肪族ポリイソシアネート、および脂環族ポリイソシアネート等が挙げられる。
アダクト体とは、ジイソシアネートとトリメチロールプロパン(CH3−CH2−C(CH2−OH) 3)との付加体である。ビュウレット体は、ジイソシアネートと、水または3級アルコールとの反応物である。イソシアヌレート体は、ジイソシアネートの3量体(この3量体はイソシアヌレート環を含む。)である。
ポリイソシアネート(y)は、2官能イソシアネート化合物(y1)のみを用いることが好ましい。ポリイソシアネート(y)は、ポリイソシアネート(y)は必要に応じて、1種以上の3官能以上のイソシアネート化合物を含むことができる。
ポリウレタンポリオールの原料ポリオールとして架橋性の高い3官能以上のポリオールのみと3官能以上のポリイソシアネートのみとを用いる場合、ポリウレタンポリオールの分子構造が剛直となり、粘着層の凝集力が好適な範囲より高くなる恐れがある。
ポリウレタンポリオールの原料ポリオールとして3官能以上のポリオールを用いる本発明の粘着剤では、ポリイソシアネート(y)として2官能イソシアネート化合物(y1)を含む1種以上のポリイソシアネート、好ましくは2官能イソシアネート化合物(y1)のみを用いることで、過度な架橋を抑えて、好適な凝集力と粘着力を有する粘着層が得ることが可能となる。
触媒としては公知のものを使用でき、3級アミン系化合物および有機金属系化合物等が挙げられる。
錫系化合物としては、例えば、ジブチル錫ジクロライド、ジブチル錫オキシド、ジブチル錫ジブロマイド、ジブチル錫ジマレエート、ジブチル錫ジラウレート(DBTDL)、ジブチル錫ジアセテート、ジブチル錫スルファイド、トリブチル錫スルファイド、トリブチル錫オキシド、トリブチル錫アセテート、トリエチル錫エトキサイド、トリブチル錫エトキサイド、ジオクチル錫オキシド、ジオクチル錫ジラウレート、トリブチル錫クロライド、トリブチル錫トリクロロアセテート、および2−エチルヘキサン酸錫等が挙げられる。
非錫系化合物としては、例えば、ジブチルチタニウムジクロライド、テトラブチルチタネート、およびブトキシチタニウムトリクロライド等のチタン系;オレイン酸鉛、2−エチルヘキサン酸鉛、安息香酸鉛、およびナフテン酸鉛等の鉛系;2−エチルヘキサン酸鉄および鉄アセチルアセトネート等の鉄系;安息香酸コバルトおよび2−エチルヘキサン酸コバルト等のコバルト系;ナフテン酸亜鉛および2−エチルヘキサン酸亜鉛等の亜鉛系;ナフテン酸ジルコニウム等のジルコニウム系が挙げられる。
2−エチルヘキサン酸錫とジブチル錫ジラウレートとの質量比(2−エチルヘキサン酸錫/ジブチル錫ジラウレート)は特に制限されず、好ましくは0超1未満、より好ましくは0.2〜0.6である。当該質量比が1未満であれば、触媒活性のバランスが良く、反応溶液のゲル化および白濁を効果的に抑制し、重合安定性がより向上する。
ポリウレタンポリオール(A)の重合には必要に応じて、溶剤を用いることができる。溶剤としては公知のものを使用でき、メチルエチルケトン、酢酸エチル、トルエン、キシレン、およびアセトン等が挙げられる。ポリウレタンポリオール(A)の溶解性および溶剤の沸点等の点から、酢酸エチルおよびトルエン等が特に好ましい。
ポリウレタンポリオール(A)の重合方法としては特に制限されず、塊状重合法および溶液重合法等の公知重合方法を適用することができる。
重合手順は特に制限されず、
手順1)ポリオール(x)、ポリイソシアネート(y)、必要に応じて触媒、および必要に応じて溶剤を一括してフラスコに仕込む手順;
手順2)ポリオール(x)、必要に応じて触媒、および必要に応じて溶剤をフラスコに仕込み、これにポリイソシアネート(y)を滴下添加する手順が挙げられる。
反応を制御しやすいことから、手順2)が好ましい。
触媒を使用しない場合、反応温度は好ましくは100℃以上、より好ましくは110℃以上であり、反応時間は好ましくは3時間以上である。
多官能イソシアネート化合物(B)としては公知のものを使用でき、ポリウレタンポリオール(A)の原料であるポリイソシアネート(y)で例示した化合物(具体的には、芳香族ポリイソシアネート、脂肪族ポリイソシアネート、芳香脂肪族ポリイソシアネート、脂環族ポリイソシアネート、および、これらのトリメチロールプロパンアダクト体/ビュウレット体/3量体)を用いることができる。
上記したように、本発明では、可塑剤(P)の添加量が少ない/好ましくは可塑剤(P)の添加量がない配合組成でも良好な濡れ性を有する粘着剤を提供することができる。したがって、本発明の粘着剤では、濡れ性を向上するために可塑剤(P)は必須成分ではないが、本発明の粘着剤は必要に応じて1種以上の可塑剤(P)を含むことができる。ただし、可塑剤(P)を添加する場合も、その量は低レベルに抑えることが可能である。ポリウレタンポリオール(A)100質量部に対する可塑剤(P)の量は、例えば50質量部以下(0〜50質量部)でよく、好ましくは40質量部以下(0〜40質量部)、より好ましくは30質量部以下(0〜30質量部)、さらに好ましくは20質量部以下(0〜20質量部)、特に好ましくは10質量部以下(0〜10質量部)、最も好ましくは5質量部以下(0〜5質量部)である。
本発明の粘着剤は必要に応じて、溶剤を含むことができる。溶剤としては公知のものを使用でき、メチルエチルケトン、酢酸エチル、トルエン、キシレン、およびアセトン等が挙げられる。ポリウレタンポリオール(A)の溶解性および溶剤の沸点等の観点から、酢酸エチルおよびトルエン等が特に好ましい。
本発明の粘着剤は必要に応じて、1種以上の変質防止剤(D)を含むことができる。これにより、粘着層の長期使用による各種特性の低下を抑制することができる。変質防止剤(D)としては、耐加水分解剤、酸化防止剤、紫外線吸収剤、および光安定剤等が挙げられる。
高温高湿環境下等において粘着層に加水分解反応が生じてカルボキシ基が生成した場合、このカルボキシ基を封鎖するために、耐加水分解剤を用いることができる。
耐加水分解剤としては、カルボジイミド系、イソシアネート系、オキサゾリン系、およびエポキシ系等が挙げられる。中でも、加水分解抑制効果の観点から、カルボジイミド系が好ましい。
モノカルボジイミド化合物としては、例えば、ジシクロヘキシルカルボジイミド、ジイソプロピルカルボジイミド、ジメチルカルボジイミド、ジイソブチルカルボジイミド、ジオクチルカルボジイミド、ジフェニルカルボジイミド、およびナフチルカルボジイミド等が挙げられる。
ポリカルボジイミド化合物は、カルボジイミド化触媒の存在下でジイソシアネートを脱炭酸縮合反応させて生成することができる。ここで、ジイソシアネートとしては、例えば、4,4’−ジフェニルメタンジイソシアネート、3,3’−ジメトキシ−4,4’−ジフェニルメタンジイソシアネート、3,3’−ジメチル−4,4’−ジフェニルメタンジイソシアネート、4,4’−ジフェニルエーテルジイソシアネート、3,3’−ジメチル−4,4’−ジフェニルエーテルジイソシアネート、2,4−トリレンジイソシアネート、2,6−トリレンジイソシアネート、1−メトキシフェニル−2,4−ジイソシアネート、イソホロンジイソシアネート、4,4’−ジシクロヘキシルメタンジイソシアネート、およびテトラメチルキシリレンジイソシアネート等が挙げられる。カルボジイミド化触媒としては、1−フェニル−2−ホスホレン−1−オキシド、3−メチル−2−ホスホレン−1−オキシド、1−エチル−3−メチル−2−ホスホレン−1−オキシド、1−エチル−2−ホスホレン−1−オキシド、およびこれらの3−ホスホレン異性体等のホスホレンオキシド等が挙げられる。
酸化防止剤としては、ラジカル補足剤および過酸化物分解剤等が挙げられる。ラジカル補足剤としては、フェノール系化合物およびアミン系化合物等が挙げられる。過酸化物分解剤としては、硫黄系化合物およびリン系化合物等が挙げられる。
酸化防止剤の添加量は特に制限されず、ポリウレタンポリオール(A)100質量部に対して、好ましくは0.01〜5質量部、より好ましくは0.1〜3質量部、特に好ましくは0.2〜2質量部である。
紫外線吸収剤としては、例えば、ベンゾフェノン系化合物、ベンゾトリアゾール系化合物、サリチル酸系化合物、シュウ酸アニリド系化合物、シアノアクリレート系化合物、およびトリアジン系化合物等が挙げられる。
紫外線吸収剤の添加量は特に制限されず、ポリウレタンポリオール(A)100質量部に対して、好ましくは0.01〜3質量部、より好ましくは0.1〜2.5質量部、特に好ましくは0.2〜2質量部である。
光安定剤としては、ヒンダードアミン系化合物およびヒンダードピペリジン系化合物等が挙げられる。光安定剤の添加量は特に制限されず、ポリウレタンポリオール(A)100質量部に対して、好ましくは0.01〜2質量部、より好ましくは0.1〜1.5質量部、特に好ましくは0.2〜1質量部である。
本発明の粘着剤は必要に応じて、1種以上の帯電防止剤(E)を含むことができる。
帯電防止剤としては、無機塩、多価アルコール化合物、イオン性液体、および界面活性剤等が挙げられ、中でもイオン性液体が好ましい。なお、「イオン性液体」は常温溶融塩ともいい、25℃で流動性がある塩である。
アニオン性の低分子界面活性剤としては、アルキルスルホン酸塩、アルキルベンゼンスルホン酸塩、およびアルキルホスフェート等が挙げられる。
カチオン性の低分子界面活性剤としては、テトラアルキルアンモニウム塩、トリアルキルベンジルアンモニウム塩等が挙げられる。
両性の低分子界面活性剤としては、アルキルベタインおよびアルキルイミダゾリウムベタイン等が挙げられる。
アニオン性の高分子界面活性剤としては、ポリスチレンスルホン酸型等が挙げられる。
カチオン性の高分子界面活性剤としては、第4級アンモニウム塩基含有アクリレート重合体型等が挙げられる。
両性の高分子界面活性剤としては、高級アルキルアミノプロピオン酸塩等のアミノ酸型両性界面活性剤、高級アルキルジメチルベタイン、および高級アルキルジヒドロキシエチルベタイン等のベタイン型両性界面活性剤等が挙げられる。
本発明の粘着剤は必要に応じて、レベリング剤を含むことができる。レベリング剤を添加することで、粘着層のレベリング性を向上させることができる。レベリング剤としては、アクリル系レベリング剤、フッ素系レベリング剤、およびシリコーン系レベリング剤等が挙げられる、粘着シート再剥離後の被着体汚染抑制の観点から、アクリル系レベリング剤等が好ましい。
本発明の粘着剤は、本発明の効果を損なわない範囲で、必要に応じて、他の任意成分を含むことができる。他の任意成分としては、触媒、ウレタン系樹脂以外の他の樹脂、充填剤(タルク、炭酸カルシウム、および酸化チタン等)、金属粉、着色剤(顔料等)、箔状物、軟化剤、導電剤、シランカップリング剤、潤滑剤、腐食防止剤、耐熱安定剤、耐候安定剤、重合禁止剤、および消泡剤等が挙げられる。
本発明の粘着シートは、基材シートと、上記の本発明の粘着剤の硬化物からなる粘着層とを含む。粘着層は、基材シートの片面または両面に形成することができる。必要に応じて、粘着層の露出面は、剥離シートで被覆することができる。なお、剥離シートは、粘着シートを被着体に貼着する際に剥離される。
図2に、本発明に係る第2実施形態の粘着シートの模式断面図を示す。図2中、符号20は粘着シート、符号21は基材シート、符号22A、22Bは粘着層、符号23A、23Bは剥離シートである。粘着シート20は、基材シートの両面に粘着層が形成された両面粘着シートである。
ポリウレタンシートを除く樹脂シートの厚みは特に制限されず、好ましくは15〜300μmである。ポリウレタンシート(発泡体を含む)の厚みは特に制限されず、好ましくは20〜50,000μmである。
紙としては特に制限されず、普通紙、コート紙、およびアート紙等が挙げられる。
金属箔の構成金属としては特に制限されず、アルミニウム、銅、およびこれらの組合せ等が挙げられる。
上記したように、本発明の粘着剤は優れた基材密着性を有するため、本発明の粘着シートでは、用いる基材シートの選択自由度が高く、好ましい。
はじめに、基材シートの表面に本発明の粘着剤を塗工して、本発明の粘着剤からなる塗工層を形成する。塗布方法は公知方法を適用でき、ロールコーター法、コンマコーター法、ダイコーター法、リバースコーター法、シルクスクリーン法、およびグラビアコーター法等が挙げられる。
次に、塗工層を乾燥および硬化して、本発明の粘着剤の硬化物からなる粘着層を形成する。加熱乾燥温度は特に制限されず、60〜150℃程度が好ましい。
粘着層の厚みは粘着シートの用途によって適宜設計でき、例えば5〜300μm程度である。なお、本明細書において、「粘着層の厚み」は特に明記しない限り、乾燥後の厚みである。
次に必要に応じて、公知方法により粘着層の露出面に剥離シートを貼着する。
以上のようにして、片面粘着シートを製造することができる。
上記操作を両面に行うことで、両面粘着シートを製造することができる。
本発明によれば、可塑剤の添加量が少ない/好ましくは可塑剤の添加量がない配合組成でも良好な濡れ性を有し、良好な湾曲性を有し、良好な再剥離性を有し、再剥離後の被着体汚染が少ない粘着層を形成することが可能な粘着剤を提供することができる。
重量平均分子量(Mw)および数平均分子量(Mn)は、ゲルパーミエーションクロマトグラフィ(GPC)法により測定した。測定条件は以下の通りである。なお、MwおよびMnはいずれも、ポリスチレン換算値である。
装置:SHIMADZU Prominence(株式会社島津製作所製)、
カラム:SHODEX LF−804(昭和電工株式会社製)を3本直列に接続、
検出器:示差屈折率検出器、
溶媒:テトラヒドロフラン(THF)、
流速:0.5mL/分、
溶媒温度:40℃、
試料濃度:0.02%、
試料注入量:200μL。
使用した材料は、以下の通りである。
<2官能ポリオール(x1)>
(x1−1):サンニックス PP−400(ポリエーテルポリオール、数平均分子量Mn400、水酸基数2、EO非含有、三洋化成工業社製)、
(x1−2):サンニックス PP−1000(ポリエーテルポリオール、数平均分子量Mn1000、水酸基数2、EO非含有、三洋化成工業社製)、
(x1−3):クラレポリオール P−1010(ポリエステルポリオール、数平均分子量Mn1000、水酸基数2、EO非含有、クラレ社製)、
(x1−4): クラレポリオール P−4010(ポリエステルポリオール、数平均分子量Mn4000、水酸基数2、EO非含有、クラレ社製)、
(x1−5):PEG−400(ポリエーテルポリオール、数平均分子量Mn400、水酸基数2、EO含有、東邦化学工業社製)、
(x1−6): PEG−1000(ポリエーテルポリオール、数平均分子量Mn1000、水酸基数2、EO含有、東邦化学工業社製)、
(x1−7):プレミノール 5001F(ポリエーテルポリオール、数平均分子量Mn4000、水酸基数2、EO含有、旭硝子社製)。
(x2−1):プレミノール 7012(ポリエーテルポリオール、数平均分子量Mn10000、水酸基数3、EO含有、旭硝子社製)、
(x2−2):エクセノール 851(ポリエーテルポリオール、数平均分子量Mn6700、水酸基数3、EO含有、旭硝子社製)、
(x2−3):エクセノール 828(ポリエーテルポリオール、数平均分子量Mn5000、水酸基数3、EO含有、旭硝子社製)、
(x2−4):アデカポリエーテル AM−302(ポリエーテルポリオール、数平均分子量Mn3000、水酸基数3、EO含有、ADEKA社製)、
(x2−5):エクセノール 5030(ポリエーテルポリオール、数平均分子量Mn5100、水酸基数3、EO非含有、旭硝子社製)、
(x2−6):DKポリオール G480(ポリエーテルポリオール、数平均分子量Mn350、水酸基数3、EO非含有、第一工業製薬社製)。
(y−1):デスモジュールH(ヘキサメチレンジイソシアネート、住化コベストロ社製)、
(y−2):タケネート 500(キシリレンジイソシアネート、三井化学社製)、
(y−3):スミジュール HT(ヘキサメチレンジイソシアネートのトリメチロールプロパンアダクト体、不揮発分75%、住化コベストロ社製)。
(B−1):スミジュール HT(ヘキサメチレンジイソシアネートのトリメチロールプロパンアダクト体、不揮発分75%、住化コベストロ社製)、
(B−2):タケネート D−110N(キシリレンジイソシアネートのトリメチロールプロパンアダクト体、不揮発分75%、三井化学社製)、
(B−3):コロネート HX(ヘキサメチレンジイソシアネートのヌレート体、不揮発分100%、東ソー社製)。
(D−1):IRGANOX 1010(BASF社製)、ヒンダードフェノール系酸化防止剤。
(P−1):モノサイザーW262(DIC社製)、ポリエーテルエステル化合物、
(P−2):ユニスターM−183(日油社製)、オレイン酸メチル。
(E−1):イオン性液体、トリ−n−ブチルメチルアンモニウム・ビストリフルオロメタンスルホンイミド。
撹拌機、還流冷却管、窒素導入管、温度計、および滴下漏斗を備えた4口フラスコに、2官能ポリオール(x1−1)2部、3官能ポリオール(x2−1)98部、および2官能ポリイソシアネート(y−1)1.0部(NCO/OHが0.5となる量)を仕込んだ。これに、トルエン100部、触媒としてジブチル錫ジラウレート0.03部および2−エチルヘキサン酸錫0.01部を加えて、90℃まで徐々に昇温し、90℃で2時間反応を行った。随時サンプリングを行い、赤外吸収(IR)スペクトルで残存イソシアネート基の消滅を確認した上で、反応溶液を冷却し反応を終了した。以上のようにして、ポリウレタンポリオール(A−1)の溶液(不揮発分:50%)を得た。得られたポリウレタンポリオール(A−1)のMwは、75,000であった。配合組成と得られたポリウレタンポリオール(A−1)のMwを表1−1に示す。表1−1〜表1−4、表2−1〜表2−4中、配合量の単位は[部]である。
なお、2官能ポリイソシアネート(y−1)の部量の算出方法は、下記の通りである。
((y−1)の部量)[部]=
(NCO/OH比)×((y−1)の分子量)/((y−1)のNCO基数)×
[((x1−1)の部量)/((x1−1)の分子量)×((x1−1)の水酸基数)
+((x2−1)の部量)/((x2−1)の分子量)×((x2−1)の水酸基数)]]
=0.5×168/2×(2/400×2+98/10000×3)
≒1.7部
合成例2〜21、合成例31、32の各例においては、表1−1〜表1−4に示す配合組成に変更した以外は合成例1と同様にして、ポリウレタンポリオール(A−2)〜(A−21)、(H−1)、(H−2)の溶液を得た。各合成例において、得られたポリウレタンポリオールのMwを表1−1〜表1−4に示す。
合成例1で得られたポリウレタンポリオール(A−1)の溶液を100部、多官能イソシアネート化合物(B−1)を10部、酸化防止剤(D−1)を1.0部、溶剤として酢酸エチルを100部配合し、ディスパーで攪拌することで、ウレタン系粘着剤を得た。なお、溶剤以外の各材料の使用量は、不揮発分換算値を示す。配合組成を表2−1に示す。
基材シートして、50μm厚のポリエチレンテレフタレートフィルム(PETフィルム、ルミラーT−60:東レ社製)を用意した。この基材シートの片面に、得られた粘着剤を乾燥後の粘着剤層の厚みが12μmになるように塗工し、100℃で2分間乾燥して、粘着層を形成した。この粘着層上に、厚さ38μmの剥離シート(スーパーステックSP−PET38:リンテック社製)を貼着して、粘着シートを得た。23℃−50%RHで1週間養生した後、各種評価に供した。
実施例2〜23、比較例1〜2の各例においては、配合組成を表2−1〜表2−4に示すように変更した以外は実施例1と同様の方法にて、粘着剤および粘着シートを得た。
3官能ポリオール(x2−2)を100部、多官能イソシアネート化合物(B−3)を12.6部、触媒としてジブチル錫ジラウレートを0.04部、溶剤として酢酸エチルを210部配合し、ディスパーで攪拌することで、ウレタン系粘着剤を得た。なお、溶剤以外の各材料の使用量は、不揮発分換算値を示す。配合組成を表2−3に示す。
得られたウレタン系粘着剤を用い、粘着層の乾燥条件を130℃で2分間とした以外は実施例1と同様の方法にて、粘着シートを得た。
評価項目および評価方法は、以下の通りである。
(再剥離性)
得られた粘着シートを幅25mm・長さ100mmの大きさに準備し、測定試料とした。次いで、23℃−50%RHの雰囲気下で、測定試料から剥離シートを剥離し、露出した粘着層を苛性ソーダガラス板に貼着し、2kgロールを用いて圧着した。その後、60℃−90%RH条件下で24時間放置した。23℃−50%RHの雰囲気にて30分空冷した後、JISZ0237に準拠し、引張試験機(テンシロン:オリエンテック社製)を用いて、剥離速度300mm/分、剥離角度180°の条件で粘着力を測定した。なお、粘着力が低い方が再剥離しやすい。評価基準は以下の通りである。
◎:10mN/25mm未満、優良。
○:10mN/25mm以上20mN/25mm未満、良好。
△:20mN/25mm以上50mN/25mm、実用可。
×:50mN/25mm超、実用不可。
得られた粘着テープを幅50mm・長さ100mmの大きさに準備し、測定試料とした。次いで、23℃−50%RH雰囲気下で30分間放置した後、測定試料から剥離シートを剥離した。粘着テープの両端を両手で持ちながら露出した粘着剤層の中心部をガラス板に接触させた後、両手を離した。測定試料の自重で粘着層全体がガラス板に密着するまでの時間を測定することで、粘着剤の濡れ性を評価した。ガラス板と密着するまでの時間が短いほどガラスに対する濡れ性(親和性)が良好であるため、ガラスを使用した製造工程でガラスを良好に保護することができる。評価基準は以下の通りである。
◎:密着まで2秒未満、優良。
○:密着まで2秒以上3秒未満、良好。
△:密着まで3秒以上5秒未満、実用可。
×:密着まで5秒以上、実用不可。
得られた粘着テープを幅10mm・長さ100mmの大きさに準備し、測定試料とした。次いで、23℃−50%RHの雰囲気下で、測定試料から剥離シートを剥離した。次いで、ガラス製の円柱(直径15mm)の円周面に沿って、この円周の半周分の長さ・幅10mmの粘着テープ試料を貼着した。60℃−90%RH条件下で72時間放置した後、測定試料の浮き状態を観察した。端部に浮きが見られた場合、浮いた部分の長さを測定した。評価基準は以下の通りである。
◎:端部に浮きなし、測定試料全体が密着、優良。
○:端部にわずかに浮きあり、0.3mm以下の浮き、良好。
△:端部に少しの浮きあり、0.3mm超1mm以下の浮き、実用可。
×:端部に浮きあり、1mm超の浮き、実用不可。
得られた粘着シートから剥離性シートを剥離した後、露出した粘着層を指で往復するようにこすり、粘着層が基材シートから脱落するかどうか評価した。評価基準は以下の通りである。
◎:30往復以上しても粘着剤が基材シートから脱落しない、優良。
○:21〜30往復で粘着剤が基材シートから脱落する、良好。
△:11〜20往復で粘着剤が基材シートから脱落する、実用可。
×:10往復以内に粘着剤が基材シートから脱落する、実用不可。
得られた粘着シートを幅70mm・長さ100mmの大きさに準備し、測定試料とした。次いで、23℃−50%RHの雰囲気下で、この測定試料から剥離シートを剥離し、露出した粘着層を苛性ソーダガラス板に貼着し、ラミネーターを用いて圧着した。その後、60℃−90%RH条件下で72時間放置した。23℃−50%RHの雰囲気下で1時間空冷した後、測定試料をガラス板から剥離し、ガラス面に測定試料が貼着されていた箇所に対して、暗室内でLEDランプ光を照射して、汚染状況を目視評価した。評価基準は以下の通りである。
◎:ガラス表面に何の汚染も認められない、優良。
○:ガラス表面の1箇所に微かに異物または曇りが認められる、良好。
△:ガラス表面の2〜3箇所に微かに異物または曇りが認められる、実用可。
×:ガラス表面の4箇所以上に微かに異物または曇りが認められる/もしくは3箇所以下にはっきりとわかる濃い異物または曇りが認められる、実用不可。
評価結果を表2−1〜表2−4に示す。
3官能以上のポリオール(x2)を含むポリオール(x)とポリイソシアネート(y)との反応生成物であるポリウレタンポリオール(A)と、
多官能イソシアネート化合物(B)とを含み、
3官能以上のポリオール(x2)が、EO基を有し、Mnが3,000超である3官能以上のポリエーテルポリオール(x2H)を含み、
ポリイソシアネート(y)が2官能イソシアネート化合物を含む粘着剤を製造した。
11、21 基材シート
12、22A、22B 粘着層
13、23A、23B 剥離シート
Claims (8)
- 3官能以上のポリオール(x2)を含むポリオール(x)とポリイソシアネート(y)との反応生成物であるポリウレタンポリオール(A)と、
多官能イソシアネート化合物(B)とを含む粘着剤であって、
3官能以上のポリオール(x2)が、1分子中に1つ以上のエチレンオキシ基を有し、数平均分子量が3,000超である3官能以上のポリエーテルポリオール(x2H)を含み、
ポリオール(x)の合計量100質量部に対する3官能以上のポリエーテルポリオール(x2 H )の量が50質量部以上であり、
ポリイソシアネート(y)が2官能イソシアネート化合物(y1)を含む、粘着剤。 - ポリオール(x)がさらに2官能ポリオール(x1)を含む、請求項1に記載の粘着剤。
- 2官能ポリオール(x1)が、2官能ポリエーテルポリオールおよび2官能ポリエステルポリオールからなる群より選ばれた1種以上のポリオールである、請求項2に記載の粘着剤。
- 2官能ポリオール(x1)が、1分子中に1つ以上のエチレンオキシ基を有する2官能ポリエーテルポリオールを含む、請求項3に記載の粘着剤。
- 2官能ポリオール(x1)の数平均分子量が200〜6,000である、請求項2〜4のいずれか1項に記載の粘着剤。
- さらに、酸化防止剤、耐加水分解剤、紫外線吸収剤、および光安定剤からなる群より選ばれた1種以上の変質防止剤を含む、請求項1〜5のいずれか1項に記載の粘着剤。
- さらに帯電防止剤を含む、請求項1〜6のいずれか1項に記載の粘着剤。
- 基材シートと、請求項1〜7のいずれか1項に記載の粘着剤の硬化物からなる粘着層とを含む、粘着シート。