JP6282604B2 - オンデマンド印刷用塗工紙 - Google Patents
オンデマンド印刷用塗工紙 Download PDFInfo
- Publication number
- JP6282604B2 JP6282604B2 JP2015024519A JP2015024519A JP6282604B2 JP 6282604 B2 JP6282604 B2 JP 6282604B2 JP 2015024519 A JP2015024519 A JP 2015024519A JP 2015024519 A JP2015024519 A JP 2015024519A JP 6282604 B2 JP6282604 B2 JP 6282604B2
- Authority
- JP
- Japan
- Prior art keywords
- paper
- printing
- ink
- calcium carbonate
- coated paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(基紙Aの作製)
パルプとしてECF漂白したLBKP100部をフリーネス550mlに叩解してパルプスラリーとし、このパルプスラリーに、内添紙力増強剤としてカチオン化澱粉(ネオタック30T:日本食品加工社製)1.5部と、填料として軽質炭酸カルシウム(TP121:奥多摩工業社製)15部と、硫酸バンド1部とを添加し、紙料を調製した。この紙料をオントップ型ツインワイヤー式抄紙機で抄紙して坪量60g/m2の原紙を作製した。次いで、ゲートロール装置にて、表面紙力増強剤として酸化澱粉(エースA:王子コーンスターチ社製)12%濃度の塗布液を、原紙の両面に、両面あたりの塗布量が固形分で2.4g/m2となるように塗布し、乾燥し、坪量62.4g/m2の基紙Aを作製した。
顔料として軽質炭酸カルシウム(TP123CS:奥多摩工業社製)40部、カオリン(ウルトラホワイト90、エンゲルハード社製)60部、分散剤(アロンT‐50、東亜合成社製)0.1部を水中に添加しコーレス分散機を用いて水分散し、顔料スラリーを作製した。この顔料スラリーに、バインダーとして澱粉(MS4600、日本食品加工社製)2部及びスチレンブタジエンラテックス(PA0372、日本エイアンドエル株式会社)10部、潤滑剤として高級脂肪酸塩(DEF−963TF、日新化学研究所社製)0.2部を加え、更に水を加えて固形分濃度が60%のインク受理層用の塗工液Aを調製した。
基紙Aの両面に、塗工液Aを、オンマシンブレードコーターを用いて基紙Aの片面当たりの塗工量が固形分換算で10g/m2になるように基紙Aの両面に塗工、乾燥した。その後、カレンダー処理としてハードニップカレンダー処理を行い、坪量が82.4g/m2のオンデマンド印刷用塗工紙を作製した。
実施例1において、基紙AのLBKPのフリーネスを380mlに変更し、内添紙力増強剤としてカチオン化澱粉(ネオタック30T:日本食品加工社製)の配合量を0.2部に変更した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、塗工液Aにおける軽質炭酸カルシウム(TP123CS:奥多摩工業社製)40部を、重質炭酸カルシウム(カービタル75:イメリスミネラルス社製)40部に変更した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、塗工液Aにおける軽質炭酸カルシウム(TP123CS:奥多摩工業社製)の配合量を75部に変更し、カオリン(ウルトラホワイト90、エンゲルハード社製)の配合量を25部に変更した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、塗工液Aにおける軽質炭酸カルシウム(TP123CS:奥多摩工業社製)の配合量を85部に変更し、カオリン(ウルトラホワイト90、エンゲルハード社製)の配合量を15部に変更した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、塗工液Aにおける顔料の配合を、軽質炭酸カルシウム(TP123CS:奥多摩工業社製)60部、重質炭酸カルシウム(カービタル75:イメリスミネラルス社製)25部、カオリン(ウルトラホワイト90、エンゲルハード社製)15部に変更した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、ゲートロール装置を用いて原紙に塗布する塗布液を、表面紙力増強剤として酸化澱粉(エースA:王子コーンスターチ社製)6%濃度の塗布液に変更し、原紙の両面に、両面あたりの塗布量が固形分で1.0g/m2となるように塗布した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。基紙の坪量は61.0g/m2であった。
(基紙Bの作製)
パルプとしてECF漂白したLBKP100部をフリーネス550mlに叩解してパルプスラリーとし、このパルプスラリーに、内添紙力増強剤としてカチオン化澱粉(ネオタック30T:日本食品加工社製)1.5部と、填料として軽質炭酸カルシウム(TP121:奥多摩工業社製)15部と、硫酸バンド1部とを添加し、紙料を調製した。この紙料をオントップ型ツインワイヤー式抄紙機で抄紙して坪量60g/m2の基紙Bを作製した。
基紙Bの両面に、実施例1の塗工液Aを、オンマシンブレードコーターを用いて基紙の片面当たりの塗工量が固形分換算で10g/m2になるように基紙の両面に塗工し、乾燥した。その後、カレンダー処理としてハードニップカレンダー処理を行い、坪量が80.0g/m2のオンデマンド印刷用塗工紙を作製した。
実施例8おいて、基紙BのLBKPのフリーネスを380mlに変更し、内添紙力増強剤をカチオン化澱粉(ネオタック30T:日本食品加工社製)1.5部から両性澱粉(CATO308:日本NSC社製)0.4部に変更した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、塗工液Aの軽質炭酸カルシウム(TP123CS:奥多摩工業社製)40部を重質炭酸カルシウム(カービタル75:イメリスミネラルス社製)40部に変更した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、軽質炭酸カルシウム(TP123CS:奥多摩工業社製)40部を、軽質炭酸カルシウム(TP221GS:奥多摩工業社製)40部に変更した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、塗工液Aにおける軽質炭酸カルシウム(TP123CS:奥多摩工業社製)の配合量を75部に変更し、カオリン(ウルトラホワイト90、エンゲルハード社製)の配合量を25部に変更した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、塗工液Aにおける軽質炭酸カルシウム(TP123CS:奥多摩工業社製)の配合量を85部に変更し、カオリン(ウルトラホワイト90、エンゲルハード社製)の配合量を15部に変更した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、塗工液Aにおける顔料の配合を、軽質炭酸カルシウム(TP123CS:奥多摩工業社製)60部、重質炭酸カルシウム(カービタル75:イメリスミネラルス社製)25部、カオリン(ウルトラホワイト90、エンゲルハード社製)15部に変更した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、カレンダー処理をハードニップカレンダー処理からスーパーカレンダー処理に変更した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。作製したオンデマンド印刷用紙は光沢紙の外観を有するものであった。
(インク受理層用の塗工液Bの調製)
重質炭酸カルシウム(カービタル75:イメリスミネラルス社製)90部、カオリン(ウルトラホワイト90、エンゲルハード社製)10部、分散剤(アロンT‐50、東亜合成社製)0.1部を水中に添加しコーレス分散機を用いて水分散し、顔料スラリーを作製した。この顔料スラリーに、バインダーとして澱粉(MS4600、日本食品加工社製)2部及びスチレンブタジエンラテックス(PA0372、日本エイアンドエル株式会社)8部を加え、更に水を加えて固形分濃度が60%のインク受理層用の塗工液Bを調製した。
軽質炭酸カルシウム(TP123CS:奥多摩工業社製)60部、カオリン(ウルトラホワイト90、エンゲルハード社製)40部、分散剤(アロンT‐50、東亜合成社製)0.1部を水中に添加しコーレス分散機を用いて水分散し、顔料スラリーを作製した。この顔料スラリーに、バインダーとして澱粉(MS4600、日本食品加工社製)2部及びスチレンブタジエンラテックス(PA0372、日本エイアンドエル株式会社)6部、潤滑剤として高級脂肪酸塩(DEF−783TF、日新化学研究所社製)0.5部を加え、更に水を加えて固形分濃度65%のインクインク受理層用の塗工液Cを調製した。
実施例16において、カレンダー処理をハードニップカレンダー処理からスーパーカレンダー処理に変更した以外は、実施例16と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、基紙Aに内添サイズ剤として中性ロジンサイズ剤(CC1401:星光PMC社製)0.2部添加した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、ゲートロール装置を用いて原紙に塗布する塗布液を、表面紙力増強剤として酸化澱粉(エースA:王子コーンスターチ社製)12%、外添サイズ剤としてスチレン‐アクリル系サイズ剤(ポリマロン1308S:荒川化学工業社製)0.4%の濃度の塗布液に変更し、該塗布液を、基紙の両面に、両面あたりの塗布量が固形質量2.4g/m2となるように塗布した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、基紙Aに内添サイズ剤として中性ロジンサイズ剤(CC1401:星光PMC社製)0.2部添加し、ゲートロール装置を用いて原紙に塗布する塗布液を、表面紙力増強剤として酸化澱粉(エースA:王子コーンスターチ社製)12%、外添サイズ剤としてスチレン‐アクリル系サイズ剤(ポリマロン1308S:荒川化学工業社製)0.4%の濃度の塗布液に変更し、該塗布液を、基紙の両面に、両面あたりの塗布量が固形質量2.4g/m2となるように塗布した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、基紙Bに内添サイズ剤として中性ロジンサイズ剤(CC1401:星光PMC社製)0.2部を添加した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
参考例1において、塗工液Aにおける軽質炭酸カルシウム(TP123CS:奥多摩工業社製)の配合量を30部に変更し、カオリン(ウルトラホワイト90、エンゲルハード社製)の配合量を70部に変更した以外は、参考例1と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、塗工液Aにおける軽質炭酸カルシウム(TP123CS:奥多摩工業社製)の配合量を30部に変更し、カオリン(ウルトラホワイト90、エンゲルハード社製)の配合量を70部に変更した以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、基紙Bに内添サイズ剤として中性ロジンサイズ剤(CC1401:星光PMC社製)0.2部を添加し、且つ基紙Bの内添紙力増強剤を添加しなかった以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
実施例8において、基紙Bに内添サイズ剤として中性ロジンサイズ剤(CC1401:星光PMC社製)0.2部を添加し、且つ塗工液Aに潤滑剤を添加しなかった以外は、実施例8と同様にしてオンデマンド印刷用塗工紙を作製した。
以下の2機種のインクジェットプリンターを用いて白抜き文字の印字を行い、水性顔料インクの滲み具合を目視で以下のように評価した。
プリンターA:CM8060ColorMFP(ヒューレットパッカード社製)
ボンディングエージェント+水性染料4色(C,M,Y,K)、
印刷速度50枚/分 A4サイズ。
プリンターB:TruepressJet520(大日本スクリーン製造社製)
印刷速度64m/分。
◎:滲みが全くなく、良好である(実用レベル)。
○:滲みが僅かに発生するが、良好である(実用レベル)。
△:滲みが多少発生する(実用上下限レベル)。
×:滲みが著しく発生する(実用上不可レベル)。
以下のインクジェットプリンターCを用いてブラック、シアン、マゼンタ、イエロー各水性顔料インク単色のベタ印字を行い、印刷物紙面のインク乾燥不良によるインク取られ跡を目視で以下のように評価した。
プリンターC:TruepressJet520(大日本スクリーン製造社製)
印刷速度64m/分。
乾燥80℃
◎:インク取られ跡が全くなく、良好である(実用レベル)。
○:インク取られ跡が僅かに発生する(実用上下限レベル)。
△:インク取られ跡が多少発生する(実用上不可レベル)。
×:インク取られ跡が著しく発生する(実用上不可レベル)。
オフセット印刷機として、小森社製「リスロン40(L−40)」を使用し、墨、藍、紅及び黄インキにて4色印刷を8500枚/時の印刷速度で印刷し、耐刷力を評価した。
◎:ブランケットの汚れがほとんど無く、良好である(実用レベル)。
○:ブランケットの汚れが多少あるが、画線部の抜けがほとんど無く、良好である(実用レベル)。
△:ブランケットの汚れが多く、画線部の抜けが有る(実用上不可レベル)。
×:ブランケットの汚れが酷く、画線部の抜けも多い(実用上不可レベル)。
カレンダーロール汚れを以下のように目視で評価した。
◎:カレンダーロール表面に汚れが全くなく、非常に良好である。(実用レベル)
○:カレンダーロール表面に僅かに汚れが発生するが、良好である。(実用レベル)
△:カレンダーロール表面の汚れが多く、劣る。(実用上不可レベル)
×:カレンダーロール表面の汚れがかなり多く、著しく劣る。(実用上不可レベル)
参考例1及び比較例1について、プリンターDを用いて、プリンターA,Bを用いたときと同様の評価法及び評価基準でインクの滲み評価を行った。その結果、参考例1は○であり、比較例1は△であった。
プリンターD:PX−G930(エプソン社製)
印刷速度3枚/分 A4サイズ。
参考例1及び比較例1について、プリンターDを用いて、ブラック、シアン、マゼンタ及びイエローの各水性顔料インク単色ベタ片面印字を行い、排紙トレイ上で印刷した紙を積層し、印刷物紙面のインク乾燥性不良によるインク転移を目視で以下の様に評価した。その結果、参考例1は◎であり、比較例1は○であった。
プリンターD:PX−G930(エプソン社製)
印刷速度3枚/分 A4サイズ
◎:インク転移が全くなく、良好である(実用レベル)。
○:インク転移が僅かに発生する(実用上下限レベル)。
△:インク転移が多少発生する(実用上不可レベル)。
×:インク転移が著しく発生する(実用上不可レベル)。
Claims (5)
- 基紙の少なくとも片面にインク受理層を設け、カレンダー処理してなる印刷用塗工紙であって、
前記基紙が内添サイズ剤及び外添サイズ剤を含有せず、かつ、内添紙力増強剤を含有し、かつ、前記基紙の表面への表面紙力増強剤の塗布量が固形分換算で両面当たり0g/m 2 以上0.5g/m 2 以下であり、
前記インク受理層が、顔料とスチレンブタジエンラテックスと潤滑剤とを含有し、
前記顔料の40質量%以上が軽質炭酸カルシウムであり、
印刷速度が枚葉紙では14.85m/分以上、ロール紙では20m/分以上の水性インクを用いた高速インクジェット印刷用であることを特徴とするオンデマンド印刷用塗工紙。 - 基紙の少なくとも片面にインク受理層を設け、カレンダー処理してなる印刷用塗工紙であって、
前記基紙が内添サイズ剤及び外添サイズ剤を含有せず、かつ、内添紙力増強剤を含有し、かつ、前記基紙の表面への表面紙力増強剤の塗布量が固形分換算で両面当たり0g/m 2 以上0.5g/m 2 以下であり、
前記インク受理層が、顔料とスチレンブタジエンラテックスと潤滑剤とを含有し、
前記顔料の40質量%以上が炭酸カルシウムであり、前記炭酸カルシウムとして軽質炭酸カルシウムと重質炭酸カルシウムとの両方を含有し、
印刷速度が枚葉紙では14.85m/分以上、ロール紙では20m/分以上の水性インクを用いた高速インクジェット印刷用であることを特徴とするオンデマンド印刷用塗工紙。 - 前記顔料の40質量%以上が軽質炭酸カルシウムであり、さらに重質炭酸カルシウムを含有することを特徴とする請求項2に記載のオンデマンド印刷用塗工紙。
- 前記潤滑剤が高級脂肪酸塩を1種以上含有することを特徴とする請求項1〜3のいずれか一つに記載のオンデマンド印刷用塗工紙。
- 前記インク受理層が、澱粉を更に含むことを特徴とする請求項1〜4のいずれか一つに記載のオンデマンド印刷用塗工紙。