JP6270587B2 - Silver ink composition and method for producing the same - Google Patents
Silver ink composition and method for producing the same Download PDFInfo
- Publication number
- JP6270587B2 JP6270587B2 JP2014070356A JP2014070356A JP6270587B2 JP 6270587 B2 JP6270587 B2 JP 6270587B2 JP 2014070356 A JP2014070356 A JP 2014070356A JP 2014070356 A JP2014070356 A JP 2014070356A JP 6270587 B2 JP6270587 B2 JP 6270587B2
- Authority
- JP
- Japan
- Prior art keywords
- group
- silver
- carbon atoms
- ink composition
- aliphatic hydrocarbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、銀インク組成物及びその製造方法に関する。 The present invention relates to a silver ink composition and a method for producing the same.
金属銀は、記録材料や印刷刷版の材料として、また、導電性に優れることから高導電性材料として幅広く使用されている。
これまでに金属銀の一般的な製造方法としては、例えば、ベヘン酸銀、ステアリン酸銀、α−ケトカルボン酸銀、β−ケトカルボン酸銀等の有機酸銀を用いる方法が開示されている。例えば、β−ケトカルボン酸銀は、約２１０℃以下の低温で加熱処理しても速やかに金属銀を形成する（特許文献１参照）。このような優れた特性を生かして、β−ケトカルボン酸銀を溶媒に溶解させて銀インク組成物を調製し、これを基材上に付着させて加熱処理することで、金属銀を形成する方法が開示されている（特許文献１参照）。
Metallic silver is widely used as a recording material, a printing plate material, and a highly conductive material because of its excellent conductivity.
So far, as a general production method of metallic silver, for example, a method using organic acid silver such as silver behenate, silver stearate, silver α-ketocarboxylate and silver β-ketocarboxylate has been disclosed. For example, silver β-ketocarboxylate quickly forms metallic silver even when heat-treated at a low temperature of about 210 ° C. or lower (see Patent Document 1). Utilizing such excellent characteristics, a silver ink composition is prepared by dissolving silver β-ketocarboxylate in a solvent, and this is deposited on a substrate and heat-treated to form metallic silver. Is disclosed (see Patent Document 1).
一方で、金属銀形成時の加熱処理については、加熱温度のさらなる低温化が期待されている。その理由は、加熱温度が低温となることで、銀インク組成物を印刷して加熱処理を行う基材の材質に関する制約が少なくなり、耐熱性が高くない材質の基材も用いることができるようになり、銀インク組成物の利用範囲が大きく広がるからである。例えば、通信機器の筐体に、このような耐熱性が高くない材質を用いた場合に、筐体の一部を電子回路の基材として用いることが可能になるなど、通信機器の設計の自由度が飛躍的に向上する。
これに対して、ギ酸銀とアミン化合物が配合されてなる液状組成物を基材上に塗工して、９０℃で加熱処理を行うことにより、金属銀被膜を形成する方法が開示されている（特許文献２参照）。
On the other hand, regarding the heat treatment during the formation of metallic silver, further reduction in the heating temperature is expected. The reason is that, since the heating temperature is low, there are less restrictions on the material of the base material on which the silver ink composition is printed and the heat treatment is performed, and it is possible to use a base material having a high heat resistance. This is because the range of use of the silver ink composition is greatly expanded. For example, when such a material that does not have high heat resistance is used for the housing of the communication device, it is possible to use a part of the housing as a base material for an electronic circuit. The degree improves dramatically.
On the other hand, a method of forming a metallic silver coating by applying a liquid composition comprising silver formate and an amine compound on a substrate and performing a heat treatment at 90 ° C. is disclosed. (See Patent Document 2).
しかしながら、特許文献２に記載の方法では、液状組成物の銀濃度が極めて低いため、十分な導電性を有する金属銀を形成するためには、液状組成物の塗工を繰り返し行う必要があり、十分な導電性を有する金属銀を形成することは、実質的に困難である場合があった。このように、より低温での加熱処理によって、十分な導電性を有する金属銀を形成可能な銀インク組成物は、これまでに開示されていないのが実情であった。 However, in the method described in Patent Document 2, since the silver concentration of the liquid composition is extremely low, in order to form metallic silver having sufficient conductivity, it is necessary to repeatedly apply the liquid composition, In some cases, it was substantially difficult to form metallic silver having sufficient conductivity. As described above, a silver ink composition capable of forming metallic silver having sufficient conductivity by heat treatment at a lower temperature has not been disclosed so far.
これに対し、発明者らは、式「−ＣＯＯＡｇ」で表される基を有するカルボン酸銀と、炭素数２５以下のアミン化合物及び第４級アンモニウム塩、アンモニア、並びに前記アミン化合物又はアンモニアが酸と反応してなるアンモニウム塩からなる群から選択される一種以上の含窒素化合物と、シュウ酸、ヒドラジン及び下記一般式（５）で表される化合物からなる群から選択される一種以上の還元性化合物と、が混合されてなることを特徴とする銀インク組成物が、より低温での加熱処理によって、十分な導電性を有する金属銀を形成可能であることを見出した。
Ｈ−Ｃ（＝Ｏ）−Ｒ２１ ・・・・（５）
（式中、Ｒ２１は、炭素数２０以下のアルキル基、アルコキシ基若しくはＮ，Ｎ−ジアルキルアミノ基、水酸基又はアミノ基である。）
On the other hand, the inventors have made silver carboxylate having a group represented by the formula “—COOAg”, an amine compound having a carbon number of 25 or less, a quaternary ammonium salt, ammonia, and the amine compound or ammonia as an acid. One or more nitrogen-containing compounds selected from the group consisting of ammonium salts formed by reaction with oxalic acid, hydrazine and one or more reducing properties selected from the group consisting of compounds represented by the following general formula (5) It has been found that a silver ink composition characterized by being mixed with a compound can form metallic silver having sufficient conductivity by heat treatment at a lower temperature.
HC (= O) -R 21 (5)
(In the formula, R 21 represents an alkyl group having 20 or less carbon atoms, an alkoxy group, an N, N-dialkylamino group, a hydroxyl group, or an amino group.)
しかしながら、発明者らは更に、上記の銀インク組成物は、チキソトロピー性に向上の余地があることを見出した。インク組成物のチキソトロピー性が向上することは、印刷物の描画の正確性が高まる点で好ましい。 However, the inventors have further found that the silver ink composition has room for improvement in thixotropy. An improvement in the thixotropy of the ink composition is preferable in that the accuracy of drawing a printed matter is increased.
そこで、本発明は、より低温での加熱処理によって、十分な導電性を有する金属銀を形成可能であり、向上したチキソトロピー性を有する銀インク組成物及びその製造方法を提供することを目的とする。 Accordingly, an object of the present invention is to provide a silver ink composition having improved thixotropy, which can form metallic silver having sufficient conductivity by heat treatment at a lower temperature, and a method for producing the same. .
本発明は、式「−ＣＯＯＡｇ」で表される基を有するカルボン酸銀と、炭素数２５以下のアミン化合物、炭素数２５以下の第４級アンモニウム塩、アンモニア及び前記アミン化合物又はアンモニアが酸と反応してなるアンモニウム塩からなる群から選択される１種以上の含窒素化合物と、シュウ酸、ヒドラジン及び下記一般式（５）で表される化合物からなる群から選択される１種以上の還元性化合物と、が配合されてなり、下記式（Ｔ１）で定義されるチキソトロピー指数が１５以上であることを特徴とする銀インク組成物を提供する。
Ｈ−Ｃ（＝Ｏ）−Ｒ２１…（５）
（式中、Ｒ２１は、炭素数２０以下のアルキル基、アルコキシ基若しくはＮ，Ｎ−ジアルキルアミノ基、水酸基又はアミノ基である。）
チキソトロピー指数＝（２５℃、せん断速度１０ｓ−１で測定した粘度）／（２５℃、せん断速度１０００ｓ−１で測定した粘度）…（Ｔ１）
The present invention provides a silver carboxylate having a group represented by the formula “—COOAg”, an amine compound having 25 or less carbon atoms, a quaternary ammonium salt having 25 or less carbon atoms, ammonia and the amine compound or ammonia as an acid. One or more nitrogen-containing compounds selected from the group consisting of reacted ammonium salts, and one or more reductions selected from the group consisting of oxalic acid, hydrazine and compounds represented by the following general formula (5) A silver ink composition characterized by having a thixotropy index defined by the following formula (T1) of 15 or more.
H-C (= O) -R 21 ... (5)
(In the formula, R 21 represents an alkyl group having 20 or less carbon atoms, an alkoxy group, an N, N-dialkylamino group, a hydroxyl group, or an amino group.)
Thixotropic index = (viscosity measured at 25 ° C., shear rate 10 s −1 ) / (viscosity measured at 25 ° C., shear rate 1000 s −1 ) (T1)
本発明はまた、前記銀インク組成物の製造方法であって、前記カルボン酸銀と、前記含窒素化合物と、を混合し、第一の混合物を得る第１工程と、前記第一の混合物又は前記第一の混合物と二酸化炭素とを混合して得られる第二の混合物と、炭素数１〜７の有機溶媒に溶解又は分散された前記還元性化合物と、を混合し、銀インク組成物を得る第２工程と、を含む、製造方法を提供する。 The present invention is also a method for producing the silver ink composition, wherein the silver carboxylate and the nitrogen-containing compound are mixed to obtain a first mixture, and the first mixture or A silver ink composition is prepared by mixing a second mixture obtained by mixing the first mixture and carbon dioxide and the reducing compound dissolved or dispersed in an organic solvent having 1 to 7 carbon atoms. And a second step of obtaining a manufacturing method.
本発明によれば、より低温での加熱処理によって、十分な導電性を有する金属銀を形成可能であり、向上したチキソトロピー性を有する銀インク組成物及びその製造方法を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the silver ink composition which can form the metal silver which has sufficient electroconductivity by heat processing at lower temperature, and has the improved thixotropic property, and its manufacturing method can be provided.
＜銀インク組成物＞
本発明の銀インク組成物は、式「−ＣＯＯＡｇ」で表される基を有するカルボン酸銀と、炭素数２５以下のアミン化合物、炭素数２５以下の第４級アンモニウム塩、アンモニア及び前記アミン化合物又はアンモニアが酸と反応してなるアンモニウム塩からなる群から選択される１種以上の含窒素化合物と、シュウ酸、ヒドラジン及び下記一般式（５）で表される化合物からなる群から選択される１種以上の還元性化合物と、が配合されてなり、チキソトロピー指数が１５以上である。
Ｈ−Ｃ（＝Ｏ）−Ｒ２１…（５）
（式中、Ｒ２１は、炭素数２０以下のアルキル基、アルコキシ基若しくはＮ，Ｎ−ジアルキルアミノ基、水酸基又はアミノ基である。）
<Silver ink composition>
The silver ink composition of the present invention includes a silver carboxylate having a group represented by the formula “—COOAg”, an amine compound having 25 or less carbon atoms, a quaternary ammonium salt having 25 or less carbon atoms, ammonia, and the amine compound. Or selected from the group consisting of one or more nitrogen-containing compounds selected from the group consisting of ammonium salts formed by reaction of ammonia with an acid, and oxalic acid, hydrazine and a compound represented by the following general formula (5) One or more reducing compounds are blended, and the thixotropic index is 15 or more.
H-C (= O) -R 21 ... (5)
(In the formula, R 21 represents an alkyl group having 20 or less carbon atoms, an alkoxy group, an N, N-dialkylamino group, a hydroxyl group, or an amino group.)
前記還元性化合物を配合することで、前記銀インク組成物は、金属銀をより形成し易くなり、例えば、低温での加熱処理でも十分な導電性を有する金属銀（導電体）を形成できる。 By blending the reducing compound, the silver ink composition can more easily form metallic silver. For example, metallic silver (conductor) having sufficient conductivity can be formed even by heat treatment at a low temperature.
チキソトロピー性が高いとは、チキソトロピー指数が高いことを意味する。本明細書において、チキソトロピー指数は、２５℃、せん断速度１０ｓ−１で測定した粘度と、２５℃、せん断速度１０００ｓ−１で測定した粘度の比［せん断速度１０ｓ−１で測定した粘度（Ｐａ・ｓ）／せん断速度１０００ｓ−１で測定した粘度（Ｐａ・ｓ）］として定義する。チキソトロピー指数を算出するための粘度は、例えば粘弾性測定装置（レオメータ）を用いて測定することができる。本明細書においては、特定のせん断速度での粘度を「せん断粘度」と略記することがある。 High thixotropy means that the thixotropy index is high. In this specification, the thixotropy index is the ratio of the viscosity measured at 25 ° C. and a shear rate of 10 s −1 to the viscosity measured at 25 ° C. and a shear rate of 1000 s −1 [viscosity measured at a shear rate of 10 s −1 (Pa · s) / viscosity measured at a shear rate of 1000 s −1 (Pa · s)]. The viscosity for calculating the thixotropy index can be measured using, for example, a viscoelasticity measuring device (rheometer). In the present specification, the viscosity at a specific shear rate may be abbreviated as “shear viscosity”.
銀インク組成物のチキソトロピー指数は、１５以上であり、好ましくは１６以上であり、より好ましくは１７以上であり、更に好ましくは２０以上である。好ましいチキソトロピー指数に上限は特にないが、実際に製造可能な銀インク組成物のチキソトロピー指数の上限は、概ね４０程度であると考えられる。 The thixotropy index of the silver ink composition is 15 or more, preferably 16 or more, more preferably 17 or more, and further preferably 20 or more. Although there is no particular upper limit to the preferred thixotropy index, the upper limit of the thixotropy index of a silver ink composition that can be actually produced is considered to be approximately 40.
チキソトロピー指数が高いということは、銀インク組成物を高速度で移動させているときには粘度が低く、低速度で移動又は静止しているときには粘度が高いことを意味する。このような特性は、例えば、銀インク組成物を設計通りの幅に印刷するのに好適である。印刷によって基板上に供給された銀インク組成物のチキソトロピー指数が低い場合、銀インク組成物は、粘度が低いためにダレ等を発生させ、印刷形状が設計値からずれてしまう傾向にある。 A high thixotropy index means that the viscosity is low when the silver ink composition is moved at a high speed, and the viscosity is high when it is moved or stationary at a low speed. Such characteristics are suitable, for example, for printing a silver ink composition in a designed width. When the thixotropy index of the silver ink composition supplied onto the substrate by printing is low, the silver ink composition tends to sag due to its low viscosity, and the printed shape tends to deviate from the design value.
［カルボン酸銀］
金属銀の形成材料としては、式「−ＣＯＯＡｇ」で表される基を有するカルボン酸銀が例示できる。
本発明において、カルボン酸銀は、一種を単独で使用してもよいし、二種以上を併用してもよい。二種以上を併用する場合、その組み合わせ及び比率は、任意に調節できる。
前記カルボン酸銀は、式「−ＣＯＯＡｇ」で表される基を有していれば特に限定されない。例えば、式「−ＣＯＯＡｇ」で表される基の数は１個のみでもよいし、２個以上でもよい。また、カルボン酸銀中の式「−ＣＯＯＡｇ」で表される基の位置も特に限定されない。
[Silver carboxylate]
Examples of the metal silver forming material include silver carboxylate having a group represented by the formula “—COOAg”.
In this invention, silver carboxylate may be used individually by 1 type, and may use 2 or more types together. When using 2 or more types together, the combination and ratio can be adjusted arbitrarily.
The silver carboxylate is not particularly limited as long as it has a group represented by the formula “—COOAg”. For example, the number of groups represented by the formula “—COOAg” may be only one, or two or more. Further, the position of the group represented by the formula “—COOAg” in the silver carboxylate is not particularly limited.
前記カルボン酸銀は、下記一般式（１）で表わされるβ−ケトカルボン酸銀（以下、「β−ケトカルボン酸銀（１）」と略記することがある）及び下記一般式（４）で表されるカルボン酸銀（以下、「カルボン酸銀（４）」と略記することがある）からなる群から選択される一種以上であることが好ましい。
なお、本明細書においては、単なる「カルボン酸銀」との記載は、特に断りの無い限り、「β−ケトカルボン酸銀（１）」及び「カルボン酸銀（４）」だけではなく、これらを包括する、「式「−ＣＯＯＡｇ」で表される基を有するカルボン酸銀」を意味するものとする。
The silver carboxylate is represented by the following general formula (1) β-ketocarboxylate silver (hereinafter sometimes abbreviated as “β-ketocarboxylate (1)”) and the following general formula (4). It is preferably one or more selected from the group consisting of silver carboxylates (hereinafter sometimes abbreviated as "silver carboxylate (4)").
In the present specification, the simple description of “silver carboxylate” is not limited to “silver β-ketocarboxylate (1)” and “silver carboxylate (4)”, unless otherwise specified. It is intended to mean “silver carboxylate having a group represented by the formula“ —COOAg ””.
Ｙ１はそれぞれ独立にフッ素原子、塩素原子、臭素原子又は水素原子であり；Ｒ１は炭素数１〜１９の脂肪族炭化水素基又はフェニル基であり；Ｒ２は炭素数１〜２０の脂肪族炭化水素基であり；Ｒ３は炭素数１〜１６の脂肪族炭化水素基であり；Ｒ４及びＲ５はそれぞれ独立に炭素数１〜１８の脂肪族炭化水素基であり；Ｒ６は炭素数１〜１９の脂肪族炭化水素基、水酸基又は式「ＡｇＯ−」で表される基であり；
Ｘ１はそれぞれ独立に水素原子、炭素数１〜２０の脂肪族炭化水素基、ハロゲン原子、１個以上の水素原子が置換基で置換されていてもよいフェニル基若しくはベンジル基、シアノ基、Ｎ−フタロイル−３−アミノプロピル基、２−エトキシビニル基、又は一般式「Ｒ７Ｏ−」、「Ｒ７Ｓ−」、「Ｒ７−Ｃ（＝Ｏ）−」若しくは「Ｒ７−Ｃ（＝Ｏ）−Ｏ−」で表される基であり；
Ｒ７は、炭素数１〜１０の脂肪族炭化水素基、チエニル基、又は１個以上の水素原子が置換基で置換されていてもよいフェニル基若しくはジフェニル基である。）
Y 1 is each independently a fluorine atom, a chlorine atom, a bromine atom or a hydrogen atom; R 1 is an aliphatic hydrocarbon group having 1 to 19 carbon atoms or a phenyl group; R 2 is an aliphatic having 1 to 20 carbon atoms R 3 is an aliphatic hydrocarbon group having 1 to 16 carbon atoms; R 4 and R 5 are each independently an aliphatic hydrocarbon group having 1 to 18 carbon atoms; R 6 is An aliphatic hydrocarbon group having 1 to 19 carbon atoms, a hydroxyl group or a group represented by the formula “AgO—”;
X 1 is independently a hydrogen atom, an aliphatic hydrocarbon group having 1 to 20 carbon atoms, a halogen atom, a phenyl group or benzyl group in which one or more hydrogen atoms may be substituted with a substituent, a cyano group, N - phthaloyl-3-aminopropyl group, 2-ethoxyethyl vinyl group, or the general formula "R 7 O -", "R 7 S -", "R 7 -C (= O) -" or "R 7 -C ( ═O) —O— ”;
R 7 is an aliphatic hydrocarbon group having 1 to 10 carbon atoms, a thienyl group, or a phenyl group or diphenyl group in which one or more hydrogen atoms may be substituted with a substituent. )
（β−ケトカルボン酸銀（１））
β−ケトカルボン酸銀（１）は、前記一般式（１）で表される。
式中、Ｒは１個以上の水素原子が置換基で置換されていてもよい炭素数１〜２０の脂肪族炭化水素基若しくはフェニル基、水酸基、アミノ基、又は一般式「Ｒ１−ＣＹ１ ２−」、「ＣＹ１ ３−」、「Ｒ１−ＣＨＹ１−」、「Ｒ２Ｏ−」、「Ｒ５Ｒ４Ｎ−」、「（Ｒ３Ｏ）２ＣＹ１−」若しくは「Ｒ６−Ｃ（＝Ｏ）−ＣＹ１ ２−」で表される基である。
(Silver β-ketocarboxylate (1))
The β-ketocarboxylate silver (1) is represented by the general formula (1).
In the formula, R represents an aliphatic hydrocarbon group having 1 to 20 carbon atoms, a phenyl group, a hydroxyl group, an amino group, or a general formula “R 1 -CY 1 ” in which one or more hydrogen atoms may be substituted with a substituent. " 2- ", "CY 1 3- ", "R 1 -CHY 1- ", "R 2 O-", "R 5 R 4 N-", "(R 3 O) 2 CY 1- " or "R 6- C (═O) —CY 1 2 — ”.
Ｒにおける炭素数１〜２０の脂肪族炭化水素基は、直鎖状、分岐鎖状及び環状（脂肪族環式基）のいずれでもよく、環状である場合、単環状及び多環状のいずれでもよい。また、前記脂肪族炭化水素基は、飽和脂肪族炭化水素基及び不飽和脂肪族炭化水素基のいずれでもよい。そして、前記脂肪族炭化水素基は、炭素数が１〜１０であることが好ましく、１〜６であることがより好ましい。Ｒにおける好ましい前記脂肪族炭化水素基としては、アルキル基、アルケニル基、アルキニル基が例示できる。 The aliphatic hydrocarbon group having 1 to 20 carbon atoms in R may be any of linear, branched and cyclic (aliphatic cyclic group), and when it is cyclic, it may be monocyclic or polycyclic. . Further, the aliphatic hydrocarbon group may be either a saturated aliphatic hydrocarbon group or an unsaturated aliphatic hydrocarbon group. The aliphatic hydrocarbon group preferably has 1 to 10 carbon atoms, and more preferably 1 to 6 carbon atoms. Preferred examples of the aliphatic hydrocarbon group for R include an alkyl group, an alkenyl group, and an alkynyl group.
Ｒにおける直鎖状又は分枝鎖状の前記アルキル基としては、メチル基、エチル基、ｎ−プロピル基、イソプロピル基、ｎ−ブチル基、イソブチル基、ｓｅｃ−ブチル基、ｔｅｒｔ−ブチル基、ｎ−ペンチル基、イソペンチル基、ネオペンチル基、ｔｅｒｔ−ペンチル基、１−メチルブチル基、２−メチルブチル基、ｎ−ヘキシル基、１−メチルペンチル基、２−メチルペンチル基、３−メチルペンチル基、４−メチルペンチル基、１，１−ジメチルブチル基、２，２−ジメチルブチル基、３，３−ジメチルブチル基、２，３−ジメチルブチル基、１−エチルブチル基、２−エチルブチル基、３−エチルブチル基、１−エチル−１−メチルプロピル基、ｎ−ヘプチル基、１−メチルヘキシル基、２−メチルヘキシル基、３−メチルヘキシル基、４−メチルヘキシル基、５−メチルヘキシル基、１，１−ジメチルペンチル基、２，２−ジメチルペンチル基、２，３−ジメチルペンチル基、２，４−ジメチルペンチル基、３，３−ジメチルペンチル基、４，４−ジメチルペンチル基、１−エチルペンチル基、２−エチルペンチル基、３−エチルペンチル基、４−エチルペンチル基、２，２，３−トリメチルブチル基、１−プロピルブチル基、ｎ−オクチル基、イソオクチル基、１−メチルヘプチル基、２−メチルヘプチル基、３−メチルヘプチル基、４−メチルヘプチル基、５−メチルヘプチル基、１−エチルヘキシル基、２−エチルヘキシル基、３−エチルヘキシル基、４−エチルヘキシル基、５−エチルヘキシル基、１，１−ジメチルヘキシル基、２，２−ジメチルヘキシル基、３，３−ジメチルヘキシル基、４，４−ジメチルヘキシル基、５，５−ジメチルヘキシル基、１−プロピルペンチル基、２−プロピルペンチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、イコシル基が例示できる。
Ｒにおける環状の前記アルキル基としては、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基、シクロノニル基、シクロデシル基、ノルボルニル基、イソボルニル基、１−アダマンチル基、２−アダマンチル基、トリシクロデシル基が例示できる。
Examples of the linear or branched alkyl group represented by R include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, n -Pentyl group, isopentyl group, neopentyl group, tert-pentyl group, 1-methylbutyl group, 2-methylbutyl group, n-hexyl group, 1-methylpentyl group, 2-methylpentyl group, 3-methylpentyl group, 4- Methylpentyl group, 1,1-dimethylbutyl group, 2,2-dimethylbutyl group, 3,3-dimethylbutyl group, 2,3-dimethylbutyl group, 1-ethylbutyl group, 2-ethylbutyl group, 3-ethylbutyl group 1-ethyl-1-methylpropyl group, n-heptyl group, 1-methylhexyl group, 2-methylhexyl group, 3-methylhexyl group, -Methylhexyl group, 5-methylhexyl group, 1,1-dimethylpentyl group, 2,2-dimethylpentyl group, 2,3-dimethylpentyl group, 2,4-dimethylpentyl group, 3,3-dimethylpentyl group 4,4-dimethylpentyl group, 1-ethylpentyl group, 2-ethylpentyl group, 3-ethylpentyl group, 4-ethylpentyl group, 2,2,3-trimethylbutyl group, 1-propylbutyl group, n -Octyl group, isooctyl group, 1-methylheptyl group, 2-methylheptyl group, 3-methylheptyl group, 4-methylheptyl group, 5-methylheptyl group, 1-ethylhexyl group, 2-ethylhexyl group, 3-ethylhexyl Group, 4-ethylhexyl group, 5-ethylhexyl group, 1,1-dimethylhexyl group, 2,2-dimethylhexyl group, 3, -Dimethylhexyl group, 4,4-dimethylhexyl group, 5,5-dimethylhexyl group, 1-propylpentyl group, 2-propylpentyl group, nonyl group, decyl group, undecyl group, dodecyl group, tridecyl group, tetradecyl group And pentadecyl group, hexadecyl group, heptadecyl group, octadecyl group, nonadecyl group and icosyl group.
Examples of the cyclic alkyl group in R include cyclopropyl group, cyclobutyl group, cyclopentyl group, cyclohexyl group, cycloheptyl group, cyclooctyl group, cyclononyl group, cyclodecyl group, norbornyl group, isobornyl group, 1-adamantyl group, 2- Examples thereof include an adamantyl group and a tricyclodecyl group.
Ｒにおける前記アルケニル基としては、ビニル基（エテニル基、−ＣＨ＝ＣＨ２）、アリル基（２−プロペニル基、−ＣＨ２−ＣＨ＝ＣＨ２）、１−プロペニル基（−ＣＨ＝ＣＨ−ＣＨ３）、イソプロペニル基（−Ｃ（ＣＨ３）＝ＣＨ２）、１−ブテニル基（−ＣＨ＝ＣＨ−ＣＨ２−ＣＨ３）、２−ブテニル基（−ＣＨ２−ＣＨ＝ＣＨ−ＣＨ３）、３−ブテニル基（−ＣＨ２−ＣＨ２−ＣＨ＝ＣＨ２）、シクロヘキセニル基、シクロペンテニル基等の、Ｒにおける前記アルキル基の炭素原子間の１個の単結合（Ｃ−Ｃ）が二重結合（Ｃ＝Ｃ）に置換された基が例示できる。
Ｒにおける前記アルキニル基としては、エチニル基（−Ｃ≡ＣＨ）、プロパルギル基（−ＣＨ２−Ｃ≡ＣＨ）等の、Ｒにおける前記アルキル基の炭素原子間の１個の単結合（Ｃ−Ｃ）が三重結合（Ｃ≡Ｃ）に置換された基が例示できる。
Examples of the alkenyl group in R include a vinyl group (ethenyl group, —CH═CH 2 ), an allyl group (2-propenyl group, —CH 2 —CH═CH 2 ), and a 1-propenyl group (—CH═CH—CH). 3 ), isopropenyl group (—C (CH 3 ) ═CH 2 ), 1-butenyl group (—CH═CH—CH 2 —CH 3 ), 2-butenyl group (—CH 2 —CH═CH—CH 3). ), 3-butenyl group (—CH 2 —CH 2 —CH═CH 2 ), cyclohexenyl group, cyclopentenyl group and the like, one single bond (C—C) between carbon atoms of the alkyl group in R Is a group in which is substituted with a double bond (C═C).
As the alkynyl group in R, one single bond (C—C) between carbon atoms of the alkyl group in R, such as ethynyl group (—C≡CH), propargyl group (—CH 2 —C≡CH) and the like. ) Is substituted with a triple bond (C≡C).
Ｒにおける炭素数１〜２０の脂肪族炭化水素基は、１個以上の水素原子が置換基で置換されていてもよく、好ましい前記置換基としては、フッ素原子、塩素原子、臭素原子が例示できる。また、置換基の数及び位置は特に限定されない。そして、置換基の数が複数である場合、これら複数個の置換基は互いに同一でも異なっていてもよい。すなわち、すべての置換基が同一であってもよいし、すべての置換基が異なっていてもよく、一部の置換基のみが異なっていてもよい。 In the aliphatic hydrocarbon group having 1 to 20 carbon atoms in R, one or more hydrogen atoms may be substituted with a substituent, and preferred examples of the substituent include a fluorine atom, a chlorine atom, and a bromine atom. . Moreover, the number and position of substituents are not particularly limited. When the number of substituents is plural, the plural substituents may be the same as or different from each other. That is, all the substituents may be the same, all the substituents may be different, or only some of the substituents may be different.
Ｒにおけるフェニル基は、１個以上の水素原子が置換基で置換されていてもよく、好ましい前記置換基としては、炭素数が１〜１６の飽和又は不飽和の一価の脂肪族炭化水素基、該脂肪族炭化水素基が酸素原子に結合してなる一価の基、フッ素原子、塩素原子、臭素原子、水酸基（−ＯＨ）、シアノ基（−Ｃ≡Ｎ）、フェノキシ基（−Ｏ−Ｃ６Ｈ５）等が例示でき、置換基の数及び位置は特に限定されない。そして、置換基の数が複数である場合、これら複数個の置換基は互いに同一でも異なっていてもよい。
置換基である前記脂肪族炭化水素基としては、炭素数が１〜１６である点以外は、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。
The phenyl group in R may have one or more hydrogen atoms substituted with a substituent, and the preferred substituent is a saturated or unsaturated monovalent aliphatic hydrocarbon group having 1 to 16 carbon atoms. , A monovalent group formed by bonding the aliphatic hydrocarbon group to an oxygen atom, a fluorine atom, a chlorine atom, a bromine atom, a hydroxyl group (—OH), a cyano group (—C≡N), a phenoxy group (—O— C 6 H 5 ) and the like can be exemplified, and the number and position of substituents are not particularly limited. When the number of substituents is plural, the plural substituents may be the same as or different from each other.
Examples of the aliphatic hydrocarbon group that is a substituent include the same aliphatic hydrocarbon groups as those described above for R except that the number of carbon atoms is 1 to 16.
ＲにおけるＹ１は、それぞれ独立にフッ素原子、塩素原子、臭素原子又は水素原子である。そして、一般式「Ｒ１−ＣＹ１ ２−」、「ＣＹ１ ３−」及び「Ｒ６−Ｃ（＝Ｏ）−ＣＹ１ ２−」においては、それぞれ複数個のＹ１は、互いに同一でも異なっていてもよい。 Y 1 in R is independently a fluorine atom, a chlorine atom, a bromine atom or a hydrogen atom. In the general formulas “R 1 —CY 1 2 —”, “CY 1 3 —” and “R 6 —C (═O) —CY 1 2 —”, a plurality of Y 1 may be the same as each other. May be different.
ＲにおけるＲ１は、炭素数１〜１９の脂肪族炭化水素基又はフェニル基（Ｃ６Ｈ５−）であり、Ｒ１における前記脂肪族炭化水素基としては、炭素数が１〜１９である点以外は、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。
ＲにおけるＲ２は、炭素数１〜２０の脂肪族炭化水素基であり、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。
ＲにおけるＲ３は、炭素数１〜１６の脂肪族炭化水素基であり、炭素数が１〜１６である点以外は、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。
ＲにおけるＲ４及びＲ５は、それぞれ独立に炭素数１〜１８の脂肪族炭化水素基である。すなわち、Ｒ４及びＲ５は、互いに同一でも異なっていてもよく、炭素数が１〜１８である点以外は、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。
ＲにおけるＲ６は、炭素数１〜１９の脂肪族炭化水素基、水酸基又は式「ＡｇＯ−」で表される基であり、Ｒ６における前記脂肪族炭化水素基としては、炭素数が１〜１９である点以外は、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。
R 1 in R is an aliphatic hydrocarbon group having 1 to 19 carbon atoms or a phenyl group (C 6 H 5 —), and the aliphatic hydrocarbon group in R 1 has 1 to 19 carbon atoms. Except for this point, the same aliphatic hydrocarbon groups as those in R can be exemplified.
R 2 in R is an aliphatic hydrocarbon group having 1 to 20 carbon atoms, and examples thereof are the same as the aliphatic hydrocarbon group in R.
R 3 in R is an aliphatic hydrocarbon group having 1 to 16 carbon atoms, and examples thereof are the same as the aliphatic hydrocarbon group in R except that the carbon number is 1 to 16.
R 4 and R 5 in R are each independently an aliphatic hydrocarbon group having 1 to 18 carbon atoms. That is, R 4 and R 5 may be the same as or different from each other, and examples thereof are the same as the aliphatic hydrocarbon group in R except that the number of carbon atoms is 1 to 18.
R 6 in R is an aliphatic hydrocarbon group having 1 to 19 carbon atoms, a hydroxyl group, or a group represented by the formula “AgO—”, and the aliphatic hydrocarbon group in R 6 has 1 to 1 carbon atoms. Except for being 19, the same aliphatic hydrocarbon groups as those described above for R can be exemplified.
Ｒは、上記の中でも、直鎖状若しくは分枝鎖状のアルキル基、一般式「Ｒ６−Ｃ（＝Ｏ）−ＣＹ１ ２−」で表される基、水酸基又はフェニル基であることが好ましい。そして、Ｒ６は、直鎖状若しくは分枝鎖状のアルキル基、水酸基又は式「ＡｇＯ−」で表される基であることが好ましい。 R is, among these, a linear or branched alkyl group, the general formula "R 6 -C (= O) -CY 1 2 - " group represented by be a hydroxyl group or a phenyl group preferable. R 6 is preferably a linear or branched alkyl group, a hydroxyl group, or a group represented by the formula “AgO—”.
一般式（１）において、Ｘ１はそれぞれ独立に水素原子、炭素数１〜２０の脂肪族炭化水素基、ハロゲン原子、１個以上の水素原子が置換基で置換されていてもよいフェニル基若しくはベンジル基（Ｃ６Ｈ５−ＣＨ２−）、シアノ基、Ｎ−フタロイル−３−アミノプロピル基、２−エトキシビニル基（Ｃ２Ｈ５−Ｏ−ＣＨ＝ＣＨ−）、又は一般式「Ｒ７Ｏ−」、「Ｒ７Ｓ−」、「Ｒ７−Ｃ（＝Ｏ）−」若しくは「Ｒ７−Ｃ（＝Ｏ）−Ｏ−」で表される基である。
Ｘ１における炭素数１〜２０の脂肪族炭化水素基としては、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。
In the general formula (1), each X 1 is independently a hydrogen atom, an aliphatic hydrocarbon group having 1 to 20 carbon atoms, a halogen atom, a phenyl group in which one or more hydrogen atoms may be substituted with a substituent, or A benzyl group (C 6 H 5 —CH 2 —), a cyano group, an N-phthaloyl-3-aminopropyl group, a 2-ethoxyvinyl group (C 2 H 5 —O—CH═CH—), or a general formula “R 7 O— ”,“ R 7 S— ”,“ R 7 —C (═O) — ”or“ R 7 —C (═O) —O— ”.
Examples of the aliphatic hydrocarbon group having 1 to 20 carbon atoms in X 1 include those similar to the aliphatic hydrocarbon group in R.
Ｘ１におけるハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が例示できる。
Ｘ１におけるフェニル基及びベンジル基は、１個以上の水素原子が置換基で置換されていてもよく、好ましい前記置換基としては、ハロゲン原子（フッ素原子、塩素原子、臭素原子、ヨウ素原子）、ニトロ基（−ＮＯ２）等が例示でき、置換基の数及び位置は特に限定されない。そして、置換基の数が複数である場合、これら複数個の置換基は互いに同一でも異なっていてもよい。
Examples of the halogen atom in X 1 include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
In the phenyl group and benzyl group in X 1 , one or more hydrogen atoms may be substituted with a substituent. Preferred examples of the substituent include a halogen atom (a fluorine atom, a chlorine atom, a bromine atom, an iodine atom), nitro group (-NO 2) or the like can be exemplified, the number and position of the substituent is not particularly limited. When the number of substituents is plural, the plural substituents may be the same as or different from each other.
Ｘ１におけるＲ７は、炭素数１〜１０の脂肪族炭化水素基、チエニル基（Ｃ４Ｈ３Ｓ−）、又は１個以上の水素原子が置換基で置換されていてもよいフェニル基若しくはジフェニル基（ビフェニル基、Ｃ６Ｈ５−Ｃ６Ｈ４−）である。Ｒ７における前記脂肪族炭化水素基としては、炭素数が１〜１０である点以外は、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。また、Ｒ７におけるフェニル基及びジフェニル基の前記置換基としては、ハロゲン原子（フッ素原子、塩素原子、臭素原子、ヨウ素原子）等が例示でき、置換基の数及び位置は特に限定されない。そして、置換基の数が複数である場合、これら複数個の置換基は互いに同一でも異なっていてもよい。
Ｒ７がチエニル基又はジフェニル基である場合、これらの、Ｘ１において隣接する基又は原子（酸素原子、硫黄原子、カルボニル基、カルボニルオキシ基）との結合位置は、特に限定されない。例えば、チエニル基は、２−チエニル基及び３−チエニル基のいずれでもよい。
R 7 in X 1 is an aliphatic hydrocarbon group having 1 to 10 carbon atoms, a thienyl group (C 4 H 3 S—), a phenyl group in which one or more hydrogen atoms may be substituted with a substituent, or diphenyl group (a biphenyl group, C 6 H 5 -C 6 H 4 -) is. Examples of the aliphatic hydrocarbon group for R 7 include those similar to the aliphatic hydrocarbon group for R except that the aliphatic hydrocarbon group has 1 to 10 carbon atoms. Further, examples of the substituent of the phenyl group and a diphenyl group in R 7, halogen atom (fluorine atom, chlorine atom, bromine atom, iodine atom) can be exemplified the like, the number and position of the substituent is not particularly limited. When the number of substituents is plural, the plural substituents may be the same as or different from each other.
When R 7 is a thienyl group or a diphenyl group, there are no particular limitations on the bonding position of these groups with an adjacent group or atom (oxygen atom, sulfur atom, carbonyl group, carbonyloxy group) in X 1 . For example, the thienyl group may be a 2-thienyl group or a 3-thienyl group.
一般式（１）において、２個のＸ１は、２個のカルボニル基で挟まれた炭素原子と二重結合を介して１個の基として結合していてもよく、このようなものとしては式「＝ＣＨ−Ｃ６Ｈ４−ＮＯ２」で表される基が例示できる。 In the general formula (1), two X 1 s may be bonded as one group through a double bond with a carbon atom sandwiched between two carbonyl groups. A group represented by the formula “═CH—C 6 H 4 —NO 2 ” can be exemplified.
Ｘ１は、上記の中でも、水素原子、直鎖状若しくは分枝鎖状のアルキル基、ベンジル基、又は一般式「Ｒ７−Ｃ（＝Ｏ）−」で表される基であることが好ましく、少なくとも一方のＸ１が水素原子であることが好ましい。 X 1 is preferably a hydrogen atom, a linear or branched alkyl group, a benzyl group, or a group represented by the general formula “R 7 —C (═O) —” among the above. It is preferable that at least one X 1 is a hydrogen atom.
β−ケトカルボン酸銀（１）は、２−メチルアセト酢酸銀（ＣＨ３−Ｃ（＝Ｏ）−ＣＨ（ＣＨ３）−Ｃ（＝Ｏ）−ＯＡｇ）、アセト酢酸銀（ＣＨ３−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）、２−エチルアセト酢酸銀（ＣＨ３−Ｃ（＝Ｏ）−ＣＨ（ＣＨ２ＣＨ３）−Ｃ（＝Ｏ）−ＯＡｇ）、プロピオニル酢酸銀（ＣＨ３ＣＨ２−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）、イソブチリル酢酸銀（（ＣＨ３）２ＣＨ−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）、ピバロイル酢酸銀（（ＣＨ３）３Ｃ−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）、カプロイル酢酸銀（ＣＨ３（ＣＨ２）３ＣＨ２−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）、２−ｎ−ブチルアセト酢酸銀（ＣＨ３−Ｃ（＝Ｏ）−ＣＨ（ＣＨ２ＣＨ２ＣＨ２ＣＨ３）−Ｃ（＝Ｏ）−ＯＡｇ）、２−ベンジルアセト酢酸銀（ＣＨ３−Ｃ（＝Ｏ）−ＣＨ（ＣＨ２Ｃ６Ｈ５）−Ｃ（＝Ｏ）−ＯＡｇ）、ベンゾイル酢酸銀（Ｃ６Ｈ５−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）、ピバロイルアセト酢酸銀（（ＣＨ３）３Ｃ−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）、イソブチリルアセト酢酸銀（（ＣＨ３）２ＣＨ−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）、２−アセチルピバロイル酢酸銀（（ＣＨ３）３Ｃ−Ｃ（＝Ｏ）−ＣＨ（−Ｃ（＝Ｏ）−ＣＨ３）−Ｃ（＝Ｏ）−ＯＡｇ）、２−アセチルイソブチリル酢酸銀（（ＣＨ３）２ＣＨ−Ｃ（＝Ｏ）−ＣＨ（−Ｃ（＝Ｏ）−ＣＨ３）−Ｃ（＝Ｏ）−ＯＡｇ）、又はアセトンジカルボン酸銀（ＡｇＯ−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）であることが好ましい。 β-ketocarboxylate silver (1) is silver 2-methylacetoacetate (CH 3 —C (═O) —CH (CH 3 ) —C (═O) —OAg), silver acetoacetate (CH 3 —C (= O) —CH 2 —C (═O) —OAg), silver 2-ethylacetoacetate (CH 3 —C (═O) —CH (CH 2 CH 3 ) —C (═O) —OAg), silver propionyl acetate (CH 3 CH 2 -C (= O) -CH 2 -C (= O) -OAg), isobutyryl silver acetate ((CH 3) 2 CH- C (= O) -CH 2 -C (= O) - OAg), silver pivaloyl acetate ((CH 3 ) 3 C—C (═O) —CH 2 —C (═O) —OAg), silver caproyl acetate (CH 3 (CH 2 ) 3 CH 2 —C (═O) ) -CH 2 -C (= O) -OAg), 2-n- Buchiruaseto silver acetate (CH 3 -C (= O) -CH (C H 2 CH 2 CH 2 CH 3 ) -C (= O) -OAg), 2- benzyl acetoacetate silver (CH 3 -C (= O) -CH (CH 2 C 6 H 5) -C (= O) -OAg), silver benzoylacetate (C 6 H 5 -C (= O) -CH 2 -C (= O) -OAg), Pibaroiruaseto silver acetate ((CH 3) 3 C- C (= O) -CH 2 -C (= O) -CH 2 -C (= O) -OAg), isobutyryl acetoacetate silver ((CH 3) 2 CH- C (= O) -CH 2 -C (= O) -CH 2 -C (= O) -OAg), 2- acetyl pivaloyl silver acetate ((CH 3) 3 C- C (= O) -CH (-C (= O) -CH 3) -C (= O) -OAg), 2- acetyl isobutyryl silver acetate ((CH 3) 2 CH- C (= O) -CH (-C (= O) -CH 3) -C (= O) - Ag), or is preferably acetone dicarboxylic silver (AgO-C (= O) -CH 2 -C (= O) -CH 2 -C (= O) -OAg).
β−ケトカルボン酸銀（１）は、乾燥処理や加熱（焼成）処理等の後処理により形成された導電体（金属銀）において、残存する原料や不純物の濃度をより低減できる。原料や不純物が少ない程、例えば、形成された金属銀同士の接触が良好となり、導通が容易となり、抵抗率が低下する。 The β-ketocarboxylate (1) can further reduce the concentration of the remaining raw materials and impurities in the conductor (metal silver) formed by post-treatment such as drying treatment or heating (firing) treatment. The smaller the raw materials and impurities, for example, the better the contact between the formed metal silvers, the easier the conduction, and the lower the resistivity.
β−ケトカルボン酸銀（１）は、後述するように、当該分野で公知の還元性化合物等を使用しなくても、好ましくは６０〜２１０℃、より好ましくは６０〜２００℃という低温で分解し、金属銀を形成することが可能である。そして、還元性化合物と併用することで、より低温で分解して金属銀を形成する。還元性化合物については後ほど説明する。 The β-ketocarboxylate (1) is decomposed at a low temperature of preferably 60 to 210 ° C., more preferably 60 to 200 ° C. without using a reducing compound known in the art as described later. It is possible to form metallic silver. And by using together with a reducing compound, it decomposes | disassembles at lower temperature and forms metallic silver. The reducing compound will be described later.
本発明において、β−ケトカルボン酸銀（１）は、一種を単独で使用してもよいし、二種以上を併用してもよい。二種以上を併用する場合、その組み合わせ及び比率は、任意に調節できる。 In this invention, (beta) -ketocarboxylate (1) may be used individually by 1 type, and may use 2 or more types together. When using 2 or more types together, the combination and ratio can be adjusted arbitrarily.
（カルボン酸銀（４））
カルボン酸銀（４）は、前記一般式（４）で表される
式中、Ｒ８は炭素数１〜１９の脂肪族炭化水素基、カルボキシ基（−ＣＯＯＨ）又は式「−Ｃ（＝Ｏ）−ＯＡｇ」で表される基である。
Ｒ８における前記脂肪族炭化水素基としては、炭素数が１〜１９である点以外は、Ｒにおける前記脂肪族炭化水素基と同様のものが例示できる。ただし、Ｒ８における前記脂肪族炭化水素基は、炭素数が１〜１５であることが好ましく、１〜１０であることがより好ましい。
(Silver carboxylate (4))
The carboxylate silver (4) is represented by the general formula (4). In the formula, R 8 is an aliphatic hydrocarbon group having 1 to 19 carbon atoms, a carboxy group (—COOH) or a formula “—C (═O ) -OAg ".
Examples of the aliphatic hydrocarbon group for R 8 include those similar to the aliphatic hydrocarbon group for R except that the aliphatic hydrocarbon group has 1 to 19 carbon atoms. However, the aliphatic hydrocarbon group for R 8 preferably has 1 to 15 carbon atoms, and more preferably 1 to 10 carbon atoms.
Ｒ８における前記脂肪族炭化水素基がメチレン基（−ＣＨ２−）を有する場合、１個以上の該メチレン基はカルボニル基で置換されていてもよい。カルボニル基で置換されていてもよいメチレン基の数及び位置は特に限定されず、すべてのメチレン基がカルボニル基で置換されていてもよい。ここで「メチレン基」とは、単独の式「−ＣＨ２−」で表される基だけでなく、式「−ＣＨ２−」で表される基が複数個連なったアルキレン基中の１個の式「−ＣＨ２−」で表される基も含むものとする。 When the aliphatic hydrocarbon group for R 8 has a methylene group (—CH 2 —), one or more of the methylene groups may be substituted with a carbonyl group. The number and position of the methylene groups that may be substituted with a carbonyl group are not particularly limited, and all methylene groups may be substituted with a carbonyl group. Here, the “methylene group” is not only a single group represented by the formula “—CH 2 —” but also one alkylene group in which a plurality of groups represented by the formula “—CH 2 —” are linked. And a group represented by the formula “—CH 2 —”.
カルボン酸銀（４）は、ピルビン酸銀（ＣＨ３−Ｃ（＝Ｏ）−Ｃ（＝Ｏ）−ＯＡｇ）、酢酸銀（ＣＨ３−Ｃ（＝Ｏ）−ＯＡｇ）、酪酸銀（ＣＨ３−（ＣＨ２）２−Ｃ（＝Ｏ）−ＯＡｇ）、イソ酪酸銀（（ＣＨ３）２ＣＨ−Ｃ（＝Ｏ）−ＯＡｇ）、２−エチルへキサン酸銀（ＣＨ３−（ＣＨ２）３−ＣＨ（ＣＨ２ＣＨ３）−Ｃ（＝Ｏ）−ＯＡｇ）、ネオデカン酸銀（ＣＨ３−（ＣＨ２）５−Ｃ（ＣＨ３）２−Ｃ（＝Ｏ）−ＯＡｇ）、シュウ酸銀（ＡｇＯ−Ｃ（＝Ｏ）−Ｃ（＝Ｏ）−ＯＡｇ）、又はマロン酸銀（ＡｇＯ−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）であることが好ましい。また、上記のシュウ酸銀（ＡｇＯ−Ｃ（＝Ｏ）−Ｃ（＝Ｏ）−ＯＡｇ）及びマロン酸銀（ＡｇＯ−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）の２個の式「−ＣＯＯＡｇ」で表される基のうち、１個が式「−ＣＯＯＨ」で表される基となったもの（ＨＯ−Ｃ（＝Ｏ）−Ｃ（＝Ｏ）−ＯＡｇ、ＨＯ−Ｃ（＝Ｏ）−ＣＨ２−Ｃ（＝Ｏ）−ＯＡｇ）も好ましい。 Silver carboxylate (4) is silver pyruvate (CH 3 —C (═O) —C (═O) —OAg), silver acetate (CH 3 —C (═O) —OAg), silver butyrate (CH 3 - (CH 2) 2 -C ( = O) -OAg), isobutyric acid silver ((CH 3) 2 CH- C (= O) -OAg), hexane silver 2-ethylhexyl (CH 3 - (CH 2 ) 3 —CH (CH 2 CH 3 ) —C (═O) —OAg), silver neodecanoate (CH 3 — (CH 2 ) 5 —C (CH 3 ) 2 —C (═O) —OAg), Shu It is preferably silver oxide (AgO—C (═O) —C (═O) —OAg) or silver malonate (AgO—C (═O) —CH 2 —C (═O) —OAg). Also, 2 of the silver oxalate (AgO-C (= O) -C (= O) -OAg) and malonic silver (AgO-C (= O) -CH 2 -C (= O) -OAg) Of the groups represented by the formula “—COOAg”, one is a group represented by the formula “—COOH” (HO—C (═O) —C (═O) —OAg, HO) -C (= O) -CH 2 -C (= O) -OAg) it is also preferred.
カルボン酸銀（４）も、β−ケトカルボン酸銀（１）と同様に、乾燥処理や加熱（焼成）処理等の後処理により形成された導電体（金属銀）において、残存する原料や不純物の濃度をより低減できる。そして、還元性化合物と併用することで、より低温で分解して金属銀を形成する。 As in the case of silver β-ketocarboxylate (1), silver carboxylate (4) is also a conductor (metal silver) formed by post-treatment such as drying treatment or heating (firing) treatment. The concentration can be further reduced. And by using together with a reducing compound, it decomposes | disassembles at lower temperature and forms metallic silver.
本発明において、カルボン酸銀（４）は、一種を単独で使用してもよいし、二種以上を併用してもよい。二種以上を併用する場合、その組み合わせ及び比率は、任意に調節できる。 In this invention, silver carboxylate (4) may be used individually by 1 type, and may use 2 or more types together. When using 2 or more types together, the combination and ratio can be adjusted arbitrarily.
前記カルボン酸銀は、２−メチルアセト酢酸銀、アセト酢酸銀、２−エチルアセト酢酸銀、プロピオニル酢酸銀、イソブチリル酢酸銀、ピバロイル酢酸銀、カプロイル酢酸銀、２−ｎ−ブチルアセト酢酸銀、２−ベンジルアセト酢酸銀、ベンゾイル酢酸銀、ピバロイルアセト酢酸銀、イソブチリルアセト酢酸銀、アセトンジカルボン酸銀、ピルビン酸銀、酢酸銀、酪酸銀、イソ酪酸銀、２−エチルへキサン酸銀、ネオデカン酸銀、シュウ酸銀及びマロン酸銀からなる群から選択される一種以上であることが好ましい。
そして、これらカルボン酸銀の中でも、２−メチルアセト酢酸銀及びアセト酢酸銀は、後述する含窒素化合物（なかでもアミン化合物）との相溶性に優れ、銀インク組成物の高濃度化に、特に適したものとして挙げられる。
The silver carboxylate is silver 2-methylacetoacetate, silver acetoacetate, silver 2-ethylacetoacetate, silver propionylacetate, silver isobutyrylacetate, silver pivaloylacetate, silver caproylacetate, silver 2-n-butylacetoacetate, 2-benzylacetoacetate Silver acetate, silver benzoyl acetate, silver pivaloyl acetoacetate, silver isobutyryl acetoacetate, silver acetone dicarboxylate, silver pyruvate, silver acetate, silver butyrate, silver isobutyrate, silver 2-ethylhexanoate, silver neodecanoate, silver It is preferably at least one selected from the group consisting of silver oxide and silver malonate.
Among these silver carboxylates, silver 2-methylacetoacetate and silver acetoacetate are excellent in compatibility with the nitrogen-containing compounds (among others amine compounds) described later, and are particularly suitable for increasing the concentration of silver ink compositions. It is mentioned as a thing.
銀インク組成物において、前記金属銀の形成材料に由来する銀の含有量は、５質量％以上であることが好ましく、１０質量％以上であることがより好ましい。このような範囲であることで、形成された導電体（金属銀）は品質により優れたものとなる。前記銀の含有量の上限値は、本発明の効果を損なわない限り特に限定されないが、取り扱い性等を考慮すると２５質量％であることが好ましい。
なお、本明細書において、「金属銀の形成材料に由来する銀」とは、特に断りの無い限り、銀インク組成物の製造時に配合された前記金属銀の形成材料中の銀を意味し、配合後に引き続き金属銀の形成材料を構成している銀と、配合後に金属銀の形成材料が分解して生じた分解物中の銀及び銀自体と、の両方を含む概念とする。
In the silver ink composition, the content of silver derived from the metal silver forming material is preferably 5% by mass or more, and more preferably 10% by mass or more. By being in such a range, the formed conductor (metal silver) becomes superior in quality. The upper limit of the silver content is not particularly limited as long as the effects of the present invention are not impaired, but it is preferably 25% by mass in consideration of handling properties and the like.
In the present specification, “silver derived from a metallic silver forming material” means silver in the metallic silver forming material blended during the production of the silver ink composition, unless otherwise specified. It is a concept that includes both silver constituting the metal silver forming material after blending, and silver and silver itself in the decomposition product generated by decomposition of the metal silver forming material after blending.
［含窒素化合物］
前記含窒素化合物は、炭素数２５以下のアミン化合物（以下、「アミン化合物」と略記することがある）、炭素数２５以下の第４級アンモニウム塩（以下、「第４級アンモニウム塩」と略記することがある）、アンモニア、炭素数２５以下のアミン化合物が酸と反応してなるアンモニウム塩（以下、「アミン化合物由来のアンモニウム塩」と略記することがある）、及びアンモニアが酸と反応してなるアンモニウム塩（以下、「アンモニア由来のアンモニウム塩」と略記することがある）からなる群から選択される一種以上のものである。すなわち、配合される含窒素化合物は、一種のみでよいし、二種以上でもよく、二種以上を併用する場合、その組み合わせ及び比率は、任意に調節できる。
[Nitrogen-containing compounds]
The nitrogen-containing compound is an amine compound having 25 or less carbon atoms (hereinafter sometimes abbreviated as “amine compound”), a quaternary ammonium salt having 25 or less carbon atoms (hereinafter abbreviated as “quaternary ammonium salt”). Ammonia, an ammonium salt formed by reacting an amine compound having 25 or less carbon atoms with an acid (hereinafter sometimes abbreviated as “ammonium salt derived from an amine compound”), and ammonia reacting with an acid. One or more selected from the group consisting of ammonium salts (hereinafter sometimes abbreviated as “ammonium salts derived from ammonia”). That is, the nitrogen-containing compound to be blended may be only one kind, or two or more kinds. When two or more kinds are used in combination, the combination and ratio can be arbitrarily adjusted.
（アミン化合物、第４級アンモニウム塩）
前記アミン化合物は、炭素数が１〜２５であり、第１級アミン、第２級アミン及び第３級アミンのいずれでもよい。また、前記第４級アンモニウム塩は、炭素数が４〜２５である。前記アミン化合物及び第４級アンモニウム塩は、鎖状及び環状のいずれでもよい。また、アミン部位又はアンモニウム塩部位を構成する窒素原子（例えば、第１級アミンのアミノ基（−ＮＨ２）を構成する窒素原子）の数は１個でもよいし、２個以上でもよい。
(Amine compound, quaternary ammonium salt)
The amine compound has 1 to 25 carbon atoms, and may be any of primary amine, secondary amine, and tertiary amine. The quaternary ammonium salt has 4 to 25 carbon atoms. The amine compound and the quaternary ammonium salt may be either chain or cyclic. Further, the number of nitrogen atoms constituting the amine moiety or ammonium salt moiety (for example, the nitrogen atom constituting the amino group (—NH 2 ) of the primary amine) may be one, or two or more.
前記第１級アミンとしては、１個以上の水素原子が置換基で置換されていてもよいモノアルキルアミン、モノアリールアミン、モノ（ヘテロアリール）アミン、ジアミン等が例示できる。 Examples of the primary amine include monoalkylamines, monoarylamines, mono (heteroaryl) amines, and diamines in which one or more hydrogen atoms may be substituted with a substituent.
前記モノアルキルアミンを構成するアルキル基は、直鎖状、分岐鎖状及び環状のいずれでもよく、Ｒにおける前記アルキル基と同様のものが例示でき、炭素数が１〜１９の直鎖状若しくは分岐鎖状のアルキル基、又は炭素数が３〜７の環状のアルキル基であることが好ましい。
好ましい前記モノアルキルアミンとして、具体的には、ｎ−ブチルアミン、ｎ−へキシルアミン、ｎ−オクチルアミン、ｎ−ドデシルアミン、ｎ−オクタデシルアミン、ｓｅｃ−ブチルアミン、ｔｅｒｔ−ブチルアミン、３−アミノペンタン、３−メチルブチルアミン、２−ヘプチルアミン（２−アミノヘプタン）、２−アミノオクタン、２−エチルヘキシルアミン、１，２−ジメチル−ｎ−プロピルアミンが例示できる。
The alkyl group constituting the monoalkylamine may be linear, branched or cyclic, and examples thereof are the same as the alkyl group in R, and are linear or branched having 1 to 19 carbon atoms. It is preferably a chain alkyl group or a cyclic alkyl group having 3 to 7 carbon atoms.
Specific examples of preferable monoalkylamine include n-butylamine, n-hexylamine, n-octylamine, n-dodecylamine, n-octadecylamine, sec-butylamine, tert-butylamine, 3-aminopentane, 3 Examples include -methylbutylamine, 2-heptylamine (2-aminoheptane), 2-aminooctane, 2-ethylhexylamine, and 1,2-dimethyl-n-propylamine.
前記モノアリールアミンを構成するアリール基としては、フェニル基、１−ナフチル基、２−ナフチル基等が例示でき、炭素数が６〜１０であることが好ましい。 Examples of the aryl group constituting the monoarylamine include a phenyl group, a 1-naphthyl group, a 2-naphthyl group, and the like, and preferably has 6 to 10 carbon atoms.
前記モノ（ヘテロアリール）アミンを構成するヘテロアリール基は、芳香族環骨格を構成する原子として、ヘテロ原子を有するものであり、前記ヘテロ原子としては、窒素原子、硫黄原子、酸素原子、ホウ素原子が例示できる。また、芳香族環骨格を構成する前記へテロ原子の数は特に限定されず、１個でもよいし、２個以上でもよい。２個以上である場合、これらへテロ原子は互いに同一でも異なっていてもよい。すなわち、これらへテロ原子は、すべて同じでもよいし、すべて異なっていてもよく、一部だけ異なっていてもよい。
前記ヘテロアリール基は、単環状及び多環状のいずれでもよく、その環員数（環骨格を構成する原子の数）も特に限定されないが、３〜１２員環であることが好ましい。
The heteroaryl group constituting the mono (heteroaryl) amine has a heteroatom as an atom constituting the aromatic ring skeleton, and the heteroatom includes a nitrogen atom, a sulfur atom, an oxygen atom, and a boron atom. Can be illustrated. Moreover, the number of the said hetero atom which comprises an aromatic ring frame is not specifically limited, One may be sufficient and two or more may be sufficient. When there are two or more, these heteroatoms may be the same or different from each other. That is, these heteroatoms may all be the same, may all be different, or may be partially different.
The heteroaryl group may be monocyclic or polycyclic, and the number of ring members (the number of atoms constituting the ring skeleton) is not particularly limited, but is preferably a 3- to 12-membered ring.
前記ヘテロアリール基で、窒素原子を１〜４個有する単環状のものとしては、ピロリル基、ピロリニル基、イミダゾリル基、ピラゾリル基、ピリジル基、ピリミジル基、ピラジニル基、ピリダジニル基、トリアゾリル基、テトラゾリル基、ピロリジニル基、イミダゾリジニル基、ピペリジニル基、ピラゾリジニル基、ピペラジニル基が例示でき、３〜８員環であることが好ましく、５〜６員環であることがより好ましい。
前記ヘテロアリール基で、酸素原子を１個有する単環状のものとしては、フラニル基が例示でき、３〜８員環であることが好ましく、５〜６員環であることがより好ましい。
前記ヘテロアリール基で、硫黄原子を１個有する単環状のものとしては、チエニル基が例示でき、３〜８員環であることが好ましく、５〜６員環であることがより好ましい。
前記ヘテロアリール基で、酸素原子を１〜２個及び窒素原子を１〜３個有する単環状のものとしては、オキサゾリル基、イソオキサゾリル基、オキサジアゾリル基、モルホリニル基が例示でき、３〜８員環であることが好ましく、５〜６員環であることがより好ましい。
前記ヘテロアリール基で、硫黄原子を１〜２個及び窒素原子を１〜３個有する単環状のものとしては、チアゾリル基、チアジアゾリル基、チアゾリジニル基が例示でき、３〜８員環であることが好ましく、５〜６員環であることがより好ましい。
前記ヘテロアリール基で、窒素原子を１〜５個有する多環状のものとしては、インドリル基、イソインドリル基、インドリジニル基、ベンズイミダゾリル基、キノリル基、イソキノリル基、インダゾリル基、ベンゾトリアゾリル基、テトラゾロピリジル基、テトラゾロピリダジニル基、ジヒドロトリアゾロピリダジニル基が例示でき、７〜１２員環であることが好ましく、９〜１０員環であることがより好ましい。
前記ヘテロアリール基で、硫黄原子を１〜３個有する多環状のものとしては、ジチアナフタレニル基、ベンゾチオフェニル基が例示でき、７〜１２員環であることが好ましく、９〜１０員環であることがより好ましい。
前記ヘテロアリール基で、酸素原子を１〜２個及び窒素原子を１〜３個有する多環状のものとしては、ベンゾオキサゾリル基、ベンゾオキサジアゾリル基が例示でき、７〜１２員環であることが好ましく、９〜１０員環であることがより好ましい。
前記ヘテロアリール基で、硫黄原子を１〜２個及び窒素原子を１〜３個有する多環状のものとしては、ベンゾチアゾリル基、ベンゾチアジアゾリル基が例示でき、７〜１２員環であることが好ましく、９〜１０員環であることがより好ましい。
Examples of the monoaryl group having 1 to 4 nitrogen atoms as the heteroaryl group include pyrrolyl group, pyrrolinyl group, imidazolyl group, pyrazolyl group, pyridyl group, pyrimidyl group, pyrazinyl group, pyridazinyl group, triazolyl group, and tetrazolyl group. , A pyrrolidinyl group, an imidazolidinyl group, a piperidinyl group, a pyrazolidinyl group, and a piperazinyl group are preferable, and a 3- to 8-membered ring is preferable, and a 5- to 6-membered ring is more preferable.
Examples of the monoaryl group having one oxygen atom as the heteroaryl group include a furanyl group, preferably a 3- to 8-membered ring, and more preferably a 5- to 6-membered ring.
Examples of the monoaryl group having one sulfur atom as the heteroaryl group include a thienyl group, preferably a 3- to 8-membered ring, and more preferably a 5- to 6-membered ring.
Examples of the monoaryl group having 1 to 2 oxygen atoms and 1 to 3 nitrogen atoms as the heteroaryl group include an oxazolyl group, an isoxazolyl group, an oxadiazolyl group, and a morpholinyl group. It is preferable that it is a 5- to 6-membered ring.
Examples of the monoaryl group having 1 to 2 sulfur atoms and 1 to 3 nitrogen atoms as the heteroaryl group include a thiazolyl group, a thiadiazolyl group, and a thiazolidinyl group, and a 3- to 8-membered ring. Preferably, it is a 5-6 membered ring.
Examples of the polyaryl group having 1 to 5 nitrogen atoms as the heteroaryl group include indolyl group, isoindolyl group, indolizinyl group, benzimidazolyl group, quinolyl group, isoquinolyl group, indazolyl group, benzotriazolyl group, tetra Examples include a zolopyridyl group, a tetrazolopyridazinyl group, and a dihydrotriazolopyridazinyl group, preferably a 7-12 membered ring, and more preferably a 9-10 membered ring.
Examples of the polyaryl group having 1 to 3 sulfur atoms as the heteroaryl group include a dithiaphthalenyl group and a benzothiophenyl group, preferably a 7 to 12 membered ring, preferably a 9 to 10 membered ring. More preferably, it is a ring.
Examples of the polyaryl group having 1 to 2 oxygen atoms and 1 to 3 nitrogen atoms as the heteroaryl group include a benzoxazolyl group and a benzooxadiazolyl group. It is preferable that it is a 9-10 membered ring.
Examples of the polyaryl group having 1 to 2 sulfur atoms and 1 to 3 nitrogen atoms as the heteroaryl group include a benzothiazolyl group and a benzothiadiazolyl group, and is a 7 to 12 membered ring. Preferably, it is a 9-10 membered ring.
前記ジアミンは、アミノ基を２個有していればよく、２個のアミノ基の位置関係は特に限定されない。好ましい前記ジアミンとしては、前記モノアルキルアミン、モノアリールアミン又はモノ（ヘテロアリール）アミンにおいて、アミノ基（−ＮＨ２）を構成する水素原子以外の１個の水素原子が、アミノ基で置換されたものが例示できる。
前記ジアミンは炭素数が１〜１０であることが好ましく、より好ましいものとしてはエチレンジアミン、１，３−ジアミノプロパン、１，４−ジアミノブタンが例示できる。
The diamine only needs to have two amino groups, and the positional relationship between the two amino groups is not particularly limited. As the preferred diamine, in the monoalkylamine, monoarylamine or mono (heteroaryl) amine, one hydrogen atom other than the hydrogen atom constituting the amino group (—NH 2 ) is substituted with an amino group. The thing can be illustrated.
The diamine preferably has 1 to 10 carbon atoms, and more preferable examples include ethylenediamine, 1,3-diaminopropane, and 1,4-diaminobutane.
前記第２級アミンとしては、１個以上の水素原子が置換基で置換されていてもよいジアルキルアミン、ジアリールアミン、ジ（ヘテロアリール）アミン等が例示できる。 Examples of the secondary amine include dialkylamine, diarylamine, di (heteroaryl) amine and the like in which one or more hydrogen atoms may be substituted with a substituent.
前記ジアルキルアミンを構成するアルキル基は、前記モノアルキルアミンを構成するアルキル基と同様であり、炭素数が１〜９の直鎖状若しくは分岐鎖状のアルキル基、又は炭素数が３〜７の環状のアルキル基であることが好ましい。また、ジアルキルアミン一分子中の２個のアルキル基は、互いに同一でも異なっていてもよい。
好ましい前記ジアルキルアミンとして、具体的には、Ｎ−メチル−ｎ−ヘキシルアミン、ジイソブチルアミン、ジ（２−エチルへキシル）アミンが例示できる。
The alkyl group that constitutes the dialkylamine is the same as the alkyl group that constitutes the monoalkylamine, and is a linear or branched alkyl group having 1 to 9 carbon atoms, or 3 to 7 carbon atoms. A cyclic alkyl group is preferred. Two alkyl groups in one molecule of dialkylamine may be the same as or different from each other.
Specific examples of preferable dialkylamine include N-methyl-n-hexylamine, diisobutylamine, and di (2-ethylhexyl) amine.
前記ジアリールアミンを構成するアリール基は、前記モノアリールアミンを構成するアリール基と同様であり、炭素数が６〜１０であることが好ましい。また、ジアリールアミン一分子中の２個のアリール基は、互いに同一でも異なっていてもよい。 The aryl group constituting the diarylamine is the same as the aryl group constituting the monoarylamine, and preferably has 6 to 10 carbon atoms. Two aryl groups in one molecule of diarylamine may be the same as or different from each other.
前記ジ（ヘテロアリール）アミンを構成するヘテロアリール基は、前記モノ（ヘテロアリール）アミンを構成するヘテロアリール基と同様であり、６〜１２員環であることが好ましい。また、ジ（ヘテロアリール）アミン一分子中の２個のヘテロアリール基は、互いに同一でも異なっていてもよい。 The heteroaryl group constituting the di (heteroaryl) amine is the same as the heteroaryl group constituting the mono (heteroaryl) amine, and is preferably a 6-12 membered ring. Two heteroaryl groups in one molecule of di (heteroaryl) amine may be the same or different from each other.
前記第３級アミンとしては、１個以上の水素原子が置換基で置換されていてもよいトリアルキルアミン、ジアルキルモノアリールアミン等が例示できる。 Examples of the tertiary amine include trialkylamine and dialkylmonoarylamine in which one or more hydrogen atoms may be substituted with a substituent.
前記トリアルキルアミンを構成するアルキル基は、前記モノアルキルアミンを構成するアルキル基と同様であり、炭素数が１〜１９の直鎖状若しくは分岐鎖状のアルキル基、又は炭素数が３〜７の環状のアルキル基であることが好ましい。また、トリアルキルアミン一分子中の３個のアルキル基は、互いに同一でも異なっていてもよい。すなわち、３個のアルキル基は、すべてが同じでもよいし、すべてが異なっていてもよく、一部だけが異なっていてもよい。
好ましい前記トリアルキルアミンとして、具体的には、Ｎ，Ｎ−ジメチル−ｎ−オクタデシルアミン、Ｎ，Ｎ−ジメチルシクロヘキシルアミンが例示できる。
The alkyl group constituting the trialkylamine is the same as the alkyl group constituting the monoalkylamine, and is a linear or branched alkyl group having 1 to 19 carbon atoms, or 3 to 7 carbon atoms. The cyclic alkyl group is preferably. Further, the three alkyl groups in one molecule of trialkylamine may be the same as or different from each other. That is, all three alkyl groups may be the same, all may be different, or only a part may be different.
Preferable examples of the trialkylamine include N, N-dimethyl-n-octadecylamine and N, N-dimethylcyclohexylamine.
前記ジアルキルモノアリールアミンを構成するアルキル基は、前記モノアルキルアミンを構成するアルキル基と同様であり、炭素数が１〜６の直鎖状若しくは分岐鎖状のアルキル基、又は炭素数が３〜７の環状のアルキル基であることが好ましい。また、ジアルキルモノアリールアミン一分子中の２個のアルキル基は、互いに同一でも異なっていてもよい。
前記ジアルキルモノアリールアミンを構成するアリール基は、前記モノアリールアミンを構成するアリール基と同様であり、炭素数が６〜１０であることが好ましい。
The alkyl group constituting the dialkyl monoarylamine is the same as the alkyl group constituting the monoalkylamine, and is a linear or branched alkyl group having 1 to 6 carbon atoms, or 3 to 3 carbon atoms. 7 is a cyclic alkyl group. Two alkyl groups in one molecule of dialkyl monoarylamine may be the same or different from each other.
The aryl group constituting the dialkyl monoarylamine is the same as the aryl group constituting the monoarylamine, and preferably has 6 to 10 carbon atoms.
本発明において、前記第４級アンモニウム塩としては、１個以上の水素原子が置換基で置換されていてもよいハロゲン化テトラアルキルアンモニウム等が例示できる。
前記ハロゲン化テトラアルキルアンモニウムを構成するアルキル基は、前記モノアルキルアミンを構成するアルキル基と同様であり、炭素数が１〜１９であることが好ましい。
また、ハロゲン化テトラアルキルアンモニウム一分子中の４個のアルキル基は、互いに同一でも異なっていてもよい。すなわち、４個のアルキル基は、すべてが同じでもよいし、すべてが異なっていてもよく、一部だけが異なっていてもよい。
前記ハロゲン化テトラアルキルアンモニウムを構成するハロゲンとしては、フッ素、塩素、臭素、ヨウ素が例示できる。
好ましい前記ハロゲン化テトラアルキルアンモニウムとして、具体的には、ドデシルトリメチルアンモニウムブロミドが例示できる。
In the present invention, examples of the quaternary ammonium salt include halogenated tetraalkylammonium, in which one or more hydrogen atoms may be substituted with a substituent.
The alkyl group constituting the halogenated tetraalkylammonium is the same as the alkyl group constituting the monoalkylamine, and preferably has 1 to 19 carbon atoms.
Further, the four alkyl groups in one molecule of the tetraalkylammonium halide may be the same as or different from each other. That is, all four alkyl groups may be the same, all may be different, or only a part may be different.
Examples of the halogen constituting the halogenated tetraalkylammonium include fluorine, chlorine, bromine and iodine.
Specific examples of the preferred tetraalkylammonium halide include dodecyltrimethylammonium bromide.
ここまでは、主に鎖状のアミン化合物及び第４級有機アンモニウム塩について説明したが、前記アミン化合物及び第４級アンモニウム塩は、アミン部位又はアンモニウム塩部位を構成する窒素原子が環骨格構造（複素環骨格構造）の一部であるようなヘテロ環化合物であってもよい。すなわち、前記アミン化合物は環状アミンでもよく、前記第４級アンモニウム塩は環状アンモニウム塩でもよい。この時の環（アミン部位又はアンモニウム塩部位を構成する窒素原子を含む環）構造は、単環状及び多環状のいずれでもよく、その環員数（環骨格を構成する原子の数）も特に限定されず、脂肪族環及び芳香族環のいずれでもよい。
環状アミンであれば、好ましいものとして、ピリジンが例示できる。
So far, the chain amine compound and the quaternary organic ammonium salt have been mainly described. However, in the amine compound and the quaternary ammonium salt, the nitrogen atom constituting the amine moiety or the ammonium salt moiety is a ring skeleton structure ( A heterocyclic compound which is a part of a heterocyclic skeleton structure) may be used. That is, the amine compound may be a cyclic amine, and the quaternary ammonium salt may be a cyclic ammonium salt. At this time, the ring (ring containing the nitrogen atom constituting the amine moiety or ammonium salt moiety) structure may be either monocyclic or polycyclic, and the number of ring members (number of atoms constituting the ring skeleton) is also particularly limited. Any of an aliphatic ring and an aromatic ring may be sufficient.
If it is a cyclic amine, a pyridine can be illustrated as a preferable thing.
前記第１級アミン、第２級アミン、第３級アミン及び第４級アンモニウム塩において、「置換基で置換されていてもよい水素原子」とは、アミン部位又はアンモニウム塩部位を構成する窒素原子に結合している水素原子以外の水素原子である。この時の置換基の数は特に限定されず、１個でもよいし、２個以上でもよく、前記水素原子のすべてが置換基で置換されていてもよい。置換基の数が複数の場合には、これら複数個の置換基は互いに同一でも異なっていてもよい。すなわち、複数個の置換基はすべて同じでもよいし、すべて異なっていてもよく、一部だけが異なっていてもよい。また、置換基の位置も特に限定されない。 In the primary amine, secondary amine, tertiary amine and quaternary ammonium salt, the “hydrogen atom optionally substituted with a substituent” means a nitrogen atom constituting an amine moiety or an ammonium salt moiety. A hydrogen atom other than a hydrogen atom bonded to. The number of substituents at this time is not particularly limited, and may be one or two or more, and all of the hydrogen atoms may be substituted with a substituent. When the number of substituents is plural, the plural substituents may be the same as or different from each other. That is, the plurality of substituents may all be the same, may all be different, or only some may be different. Further, the position of the substituent is not particularly limited.
前記アミン化合物及び第４級アンモニウム塩における前記置換基としては、アルキル基、アリール基、ハロゲン原子、シアノ基、ニトロ基、水酸基、トリフルオロメチル基（−ＣＦ３）等が例示できる。ここで、ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が例示できる。 Examples of the substituent in the amine compound and the quaternary ammonium salt include an alkyl group, an aryl group, a halogen atom, a cyano group, a nitro group, a hydroxyl group, and a trifluoromethyl group (—CF 3 ). Here, examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
前記モノアルキルアミンを構成するアルキル基が置換基を有する場合、かかるアルキル基は、置換基としてアリール基を有する、炭素数が１〜９の直鎖状若しくは分岐鎖状のアルキル基、又は置換基として好ましくは炭素数が１〜５のアルキル基を有する、炭素数が３〜７の環状のアルキル基が好ましく、このような置換基を有するモノアルキルアミンとして、具体的には、２−フェニルエチルアミン、ベンジルアミン、２，３−ジメチルシクロヘキシルアミンが例示できる。
また、置換基である前記アリール基及びアルキル基は、さらに１個以上の水素原子がハロゲン原子で置換されていてもよく、このようなハロゲン原子で置換された置換基を有するモノアルキルアミンとしては、２−ブロモベンジルアミンが例示できる。ここで、前記ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が例示できる。
When the alkyl group constituting the monoalkylamine has a substituent, the alkyl group has an aryl group as a substituent, a linear or branched alkyl group having 1 to 9 carbon atoms, or a substituent Preferably, a cyclic alkyl group having 3 to 7 carbon atoms having an alkyl group having 1 to 5 carbon atoms is preferable, and specific examples of monoalkylamine having such a substituent include 2-phenylethylamine , Benzylamine, and 2,3-dimethylcyclohexylamine.
In addition, the aryl group and the alkyl group which are substituents may further have one or more hydrogen atoms substituted with halogen atoms, and as monoalkylamines having such substituents substituted with halogen atoms, And 2-bromobenzylamine. Here, examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
前記モノアリールアミンを構成するアリール基が置換基を有する場合、かかるアリール基は、置換基としてハロゲン原子を有する、炭素数が６〜１０のアリール基が好ましく、このような置換基を有するモノアリールアミンとして、具体的には、ブロモフェニルアミンが例示できる。ここで、前記ハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子が例示できる。 When the aryl group constituting the monoarylamine has a substituent, the aryl group is preferably an aryl group having 6 to 10 carbon atoms having a halogen atom as the substituent, and monoaryl having such a substituent. Specific examples of the amine include bromophenylamine. Here, examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.
前記ジアルキルアミンを構成するアルキル基が置換基を有する場合、かかるアルキル基は、置換基として水酸基又はアリール基を有する、炭素数が１〜９の直鎖状若しくは分岐鎖状のアルキル基が好ましく、このような置換基を有するジアルキルアミンとして、具体的には、ジエタノールアミン、Ｎ−メチルベンジルアミンが例示できる。 When the alkyl group constituting the dialkylamine has a substituent, the alkyl group is preferably a linear or branched alkyl group having 1 to 9 carbon atoms and having a hydroxyl group or an aryl group as a substituent, Specific examples of the dialkylamine having such a substituent include diethanolamine and N-methylbenzylamine.
前記アミン化合物は、ｎ−プロピルアミン、ｎ−ブチルアミン、ｎ−へキシルアミン、ｎ−オクチルアミン、ｎ−ドデシルアミン、ｎ−オクタデシルアミン、ｓｅｃ−ブチルアミン、ｔｅｒｔ−ブチルアミン、３−アミノペンタン、３−メチルブチルアミン、２−ヘプチルアミン、２−アミノオクタン、２−エチルヘキシルアミン、２−フェニルエチルアミン、エチレンジアミン、１，３−ジアミノプロパン、１，４−ジアミノブタン、Ｎ−メチル−ｎ−ヘキシルアミン、ジイソブチルアミン、Ｎ−メチルベンジルアミン、ジ（２−エチルへキシル）アミン、１，２−ジメチル−ｎ−プロピルアミン、Ｎ，Ｎ−ジメチル−ｎ−オクタデシルアミン又はＮ，Ｎ−ジメチルシクロヘキシルアミンであることが好ましい。
そして、これらアミン化合物の中でも、２−エチルヘキシルアミンは、前記カルボン酸銀との相溶性に優れ、銀インク組成物の高濃度化に特に適しており、さらに銀細線の表面粗さの低減に特に適したものとして挙げられる。
The amine compound is n-propylamine, n-butylamine, n-hexylamine, n-octylamine, n-dodecylamine, n-octadecylamine, sec-butylamine, tert-butylamine, 3-aminopentane, 3-methyl. Butylamine, 2-heptylamine, 2-aminooctane, 2-ethylhexylamine, 2-phenylethylamine, ethylenediamine, 1,3-diaminopropane, 1,4-diaminobutane, N-methyl-n-hexylamine, diisobutylamine, N-methylbenzylamine, di (2-ethylhexyl) amine, 1,2-dimethyl-n-propylamine, N, N-dimethyl-n-octadecylamine or N, N-dimethylcyclohexylamine is preferred. .
Among these amine compounds, 2-ethylhexylamine is excellent in compatibility with the silver carboxylate, particularly suitable for increasing the concentration of the silver ink composition, and particularly for reducing the surface roughness of the silver fine wire. Listed as suitable.
（アミン化合物由来のアンモニウム塩）
本発明において、前記アミン化合物由来のアンモニウム塩は、前記アミン化合物が酸と反応してなるアンモニウム塩であり、前記酸は、塩酸、硫酸、硝酸等の無機酸でもよいし、酢酸等の有機酸でもよく、酸の種類は特に限定されない。
前記アミン化合物由来のアンモニウム塩としては、ｎ−プロピルアミン塩酸塩、Ｎ−メチル−ｎ−ヘキシルアミン塩酸塩、Ｎ，Ｎ−ジメチル−ｎ−オクタデシルアミン塩酸塩等が例示できるが、これらに限定されない。
(Ammonium salts derived from amine compounds)
In the present invention, the ammonium salt derived from the amine compound is an ammonium salt obtained by reacting the amine compound with an acid, and the acid may be an inorganic acid such as hydrochloric acid, sulfuric acid or nitric acid, or an organic acid such as acetic acid. However, the type of acid is not particularly limited.
Examples of the ammonium salt derived from the amine compound include, but are not limited to, n-propylamine hydrochloride, N-methyl-n-hexylamine hydrochloride, N, N-dimethyl-n-octadecylamine hydrochloride and the like. .
（アンモニア由来のアンモニウム塩）
本発明において、前記アンモニア由来のアンモニウム塩は、アンモニアが酸と反応してなるアンモニウム塩であり、ここで酸としては、前記アミン化合物由来のアンモニウム塩の場合と同じものが例示できる。
前記アンモニア由来のアンモニウム塩としては、塩化アンモニウム等が例示できるが、これに限定されない。
(Ammonium salt derived from ammonia)
In the present invention, the ammonium salt derived from ammonia is an ammonium salt formed by reacting ammonia with an acid, and examples of the acid include the same ones as in the case of the ammonium salt derived from the amine compound.
Examples of the ammonium salt derived from ammonia include ammonium chloride, but are not limited thereto.
本発明においては、前記アミン化合物、第４級アンモニウム塩、アミン化合物由来のアンモニウム塩及びアンモニア由来のアンモニウム塩は、それぞれ一種を単独で使用してもよいし、二種以上を併用してもよい。二種以上を併用する場合、その組み合わせ及び比率は、任意に調節できる。
そして、前記含窒素化合物としては、前記アミン化合物、第４級アンモニウム塩、アミン化合物由来のアンモニウム塩及びアンモニア由来のアンモニウム塩からなる群から選択される一種を単独で使用してもよいし、二種以上を併用してもよい。二種以上を併用する場合、その組み合わせ及び比率は、任意に調節できる。
In the present invention, the amine compound, the quaternary ammonium salt, the ammonium salt derived from the amine compound and the ammonium salt derived from ammonia may be used singly or in combination of two or more. . When using 2 or more types together, the combination and ratio can be adjusted arbitrarily.
And as said nitrogen-containing compound, you may use individually by 1 type selected from the group which consists of said amine compound, quaternary ammonium salt, ammonium salt derived from an amine compound, and ammonium salt derived from ammonia, More than one species may be used in combination. When using 2 or more types together, the combination and ratio can be adjusted arbitrarily.
銀インク組成物において、前記含窒素化合物の配合量は、前記金属銀の形成材料の配合量１モルあたり０．３〜１５モルであることが好ましく、０．３〜５モルであることがより好ましい。前記含窒素化合物の前記配合量がこのような範囲であることで、銀インク組成物は安定性がより向上し、導電体（金属銀）の品質がより向上する。さらに、高温による加熱処理を行わなくても、より安定して導電体を形成できる。 In the silver ink composition, the compounding amount of the nitrogen-containing compound is preferably 0.3 to 15 mol, more preferably 0.3 to 5 mol, per mol of the metal silver forming material. preferable. When the blending amount of the nitrogen-containing compound is within such a range, the silver ink composition is further improved in stability and the quality of the conductor (metal silver) is further improved. Furthermore, the conductor can be formed more stably without performing heat treatment at a high temperature.
［還元性化合物］
銀インク組成物は、前記金属銀の形成材料以外に、さらに還元性化合物が配合されてなるものである。還元性化合物を配合することで、前記銀インク組成物は、金属銀をより形成し易くなり、例えば、低温での加熱処理でも十分な導電性を有する導電体（金属銀）を形成できる。
[Reducing compounds]
The silver ink composition is obtained by further blending a reducing compound in addition to the metal silver forming material. By blending the reducing compound, the silver ink composition can more easily form metallic silver, and for example, a conductor (metal silver) having sufficient conductivity can be formed even by heat treatment at a low temperature.
前記還元性化合物は、シュウ酸（ＨＯＯＣ−ＣＯＯＨ）、ヒドラジン（Ｈ２Ｎ−ＮＨ２）及び下記一般式（５）で表される化合物（化合物（５））からなる群から選択される一種以上のものである。すなわち、配合される還元性化合物は、一種のみでもよいし、二種以上でもよく、二種以上を併用する場合、その組み合わせ及び比率は任意に調節できる。
Ｈ−Ｃ（＝Ｏ）−Ｒ２１ ・・・・（５）
（式中、Ｒ２１は、炭素数２０以下のアルキル基、アルコキシ基若しくはＮ，Ｎ−ジアルキルアミノ基、水酸基又はアミノ基である。）
The reducing compound is one or more selected from the group consisting of oxalic acid (HOOC-COOH), hydrazine (H 2 N—NH 2 ), and a compound represented by the following general formula (5) (compound (5)). belongs to. That is, the reducing compound to be blended may be one kind or two or more kinds. When two or more kinds are used in combination, the combination and ratio can be arbitrarily adjusted.
HC (= O) -R 21 (5)
(In the formula, R 21 represents an alkyl group having 20 or less carbon atoms, an alkoxy group, an N, N-dialkylamino group, a hydroxyl group, or an amino group.)
Ｒ２１における炭素数２０以下のアルキル基は、炭素数が１〜２０であり、直鎖状、分岐鎖状及び環状のいずれでもよく、前記一般式（１）のＲにおける前記アルキル基と同様のものが例示できる。 The alkyl group having 20 or less carbon atoms in R 21 has 1 to 20 carbon atoms, and may be linear, branched or cyclic, and is the same as the alkyl group in R of the general formula (1) The thing can be illustrated.
Ｒ２１における炭素数２０以下のアルコキシ基は、炭素数が１〜２０であり、Ｒ２１における前記アルキル基が酸素原子に結合してなる一価の基が例示できる。 The alkoxy group having 20 or less carbon atoms in R 21 has 1 to 20 carbon atoms, and examples thereof include monovalent groups in which the alkyl group in R 21 is bonded to an oxygen atom.
Ｒ２１における炭素数２０以下のＮ，Ｎ−ジアルキルアミノ基は、炭素数が２〜２０であり、窒素原子に結合している２個のアルキル基は、互いに同一でも異なっていてもよく、該アルキル基はそれぞれ炭素数が１〜１９である。ただし、これら２個のアルキル基の炭素数の合計値が２〜２０である。
窒素原子に結合している前記アルキル基は、それぞれ直鎖状、分岐鎖状及び環状のいずれでもよく、炭素数が１〜１９である点以外は、前記一般式（１）のＲにおける前記アルキル基と同様のものが例示できる。
The N, N-dialkylamino group having 20 or less carbon atoms in R 21 has 2 to 20 carbon atoms, and the two alkyl groups bonded to the nitrogen atom may be the same as or different from each other, Each alkyl group has 1 to 19 carbon atoms. However, the total value of the carbon number of these two alkyl groups is 2-20.
The alkyl group bonded to the nitrogen atom may be linear, branched or cyclic, respectively, and the alkyl in R of the general formula (1) except that it has 1 to 19 carbon atoms. The thing similar to group can be illustrated.
前記還元性化合物として、ヒドラジンは、一水和物（Ｈ２Ｎ−ＮＨ２・Ｈ２Ｏ）を用いてもよい。 As the reducing compound, hydrazine may be a monohydrate (H 2 N—NH 2 .H 2 O).
前記還元性化合物で好ましいものとしては、ギ酸（Ｈ−Ｃ（＝Ｏ）−ＯＨ）；ギ酸メチル（Ｈ−Ｃ（＝Ｏ）−ＯＣＨ３）、ギ酸エチル（Ｈ−Ｃ（＝Ｏ）−ＯＣＨ２ＣＨ３）、ギ酸ブチル（Ｈ−Ｃ（＝Ｏ）−Ｏ（ＣＨ２）３ＣＨ３）等のギ酸エステル；プロパナール（Ｈ−Ｃ（＝Ｏ）−ＣＨ２ＣＨ３）、ブタナール（Ｈ−Ｃ（＝Ｏ）−（ＣＨ２）２ＣＨ３）、ヘキサナール（Ｈ−Ｃ（＝Ｏ）−（ＣＨ２）４ＣＨ３）等のアルデヒド；ホルムアミド（Ｈ−Ｃ（＝Ｏ）−ＮＨ２）、Ｎ，Ｎ−ジメチルホルムアミド（Ｈ−Ｃ（＝Ｏ）−Ｎ（ＣＨ３）２）等のホルムアミド類（式「Ｈ−Ｃ（＝Ｏ）−Ｎ（−）−」で表される基を有する化合物）；シュウ酸が例示できる。 Preferred examples of the reducing compound include formic acid (HC (═O) —OH); methyl formate (HC (═O) —OCH 3 ), ethyl formate (HC (═O) —OCH). Formic acid esters such as 2 CH 3 ) and butyl formate (HC (═O) —O (CH 2 ) 3 CH 3 ); propanal (HC (═O) —CH 2 CH 3 ), butanal (H Aldehydes such as —C (═O) — (CH 2 ) 2 CH 3 ) and hexanal (HC— (O) — (CH 2 ) 4 CH 3 ); formamide (HC— (O) —NH 2 ), N, N-dimethylformamide (HC (═O) —N (CH 3 ) 2 ) and other formamides (groups represented by the formula “HC (═O) —N (—) —”) And oxalic acid.
銀インク組成物において、還元剤の配合量は、前記金属銀の形成材料の配合量１モルあたり０．０４〜３．５モルであることが好ましく、０．０６〜２．５モルであることがより好ましい。還元剤の前記配合量がこのような範囲であることで、銀インク組成物は、より容易に、より安定して導電体（金属銀）を形成できる。 In the silver ink composition, the compounding amount of the reducing agent is preferably 0.04 to 3.5 mol, and preferably 0.06 to 2.5 mol per 1 mol of the metal silver forming material. Is more preferable. When the blending amount of the reducing agent is within such a range, the silver ink composition can form a conductor (metal silver) more easily and more stably.
［アルコール］
銀インク組成物は、前記金属銀の形成材料以外に、更に、後述する炭素数１〜７の有機溶媒に該当しないアルコールが配合されてなるものが好ましい。
[alcohol]
In addition to the metallic silver forming material, the silver ink composition preferably further contains an alcohol that does not correspond to an organic solvent having 1 to 7 carbon atoms described later.
前記アルコールは、下記一般式（２）で表されるアセチレンアルコール類（以下、「アセチレンアルコール（２）」と略記することがある）であることが好ましい。 The alcohol is preferably an acetylene alcohol represented by the following general formula (2) (hereinafter sometimes abbreviated as “acetylene alcohol (2)”).
（アセチレンアルコール（２））
アセチレンアルコール（２）は、前記一般式（２）で表される。
式中、Ｒ’及びＲ’’は、それぞれ独立に炭素数１〜２０のアルキル基、又は１個以上の水素原子が置換基で置換されていてもよいフェニル基である。
Ｒ’及びＲ’’における炭素数１〜２０のアルキル基は、直鎖状、分岐鎖状及び環状のいずれでもよく、環状である場合、単環状及び多環状のいずれでもよい。Ｒ’及びＲ’’における前記アルキル基としては、Ｒにおける前記アルキル基と同様のものが例示できる。
(Acetylene alcohol (2))
The acetylene alcohol (2) is represented by the general formula (2).
In the formula, R ′ and R ″ are each independently an alkyl group having 1 to 20 carbon atoms, or a phenyl group in which one or more hydrogen atoms may be substituted with a substituent.
The alkyl group having 1 to 20 carbon atoms in R ′ and R ″ may be linear, branched or cyclic, and when it is cyclic, it may be monocyclic or polycyclic. Examples of the alkyl group in R ′ and R ″ include the same alkyl groups as in R.
Ｒ’及びＲ’’におけるフェニル基の水素原子が置換されていてもよい前記置換基としては、炭素数が１〜１６の飽和又は不飽和の一価の脂肪族炭化水素基、該脂肪族炭化水素基が酸素原子に結合してなる一価の基、フッ素原子、塩素原子、臭素原子、水酸基、シアノ基、フェノキシ基等が例示でき、Ｒにおけるフェニル基の水素原子が置換されていてもよい前記置換基と同様である。そして、置換基の数及び位置は特に限定されず、置換基の数が複数である場合、これら複数個の置換基は互いに同一でも異なっていてもよい。 Examples of the substituent in which the hydrogen atom of the phenyl group in R ′ and R ″ may be substituted include a saturated or unsaturated monovalent aliphatic hydrocarbon group having 1 to 16 carbon atoms, the aliphatic carbonization Examples thereof include a monovalent group formed by bonding a hydrogen group to an oxygen atom, a fluorine atom, a chlorine atom, a bromine atom, a hydroxyl group, a cyano group, a phenoxy group, and the like, and the hydrogen atom of the phenyl group in R may be substituted. This is the same as the substituent. And the number and position of a substituent are not specifically limited, When there are two or more substituents, these several substituents may mutually be same or different.
Ｒ’及びＲ’’は、炭素数１〜２０のアルキル基であることが好ましく、炭素数１〜１０の直鎖状又は分岐鎖状のアルキル基であることがより好ましい。 R ′ and R ″ are preferably an alkyl group having 1 to 20 carbon atoms, and more preferably a linear or branched alkyl group having 1 to 10 carbon atoms.
好ましいアセチレンアルコール（２）としては、３，５−ジメチル−１−ヘキシン−３−オール、３−メチル−１−ブチン−３−オール、３−メチル−１−ペンチン−３−オールが例示できる。 Examples of preferable acetylene alcohol (2) include 3,5-dimethyl-1-hexyn-3-ol, 3-methyl-1-butyn-3-ol, and 3-methyl-1-pentyn-3-ol.
アセチレンアルコール（２）を用いる場合、銀インク組成物において、アセチレンアルコール（２）の配合量は、前記金属銀の形成材料の配合量１モルあたり０．０３〜０．７モルであることが好ましく、０．０５〜０．３モルであることがより好ましい。アセチレンアルコール（２）の前記配合量がこのような範囲であることで、銀インク組成物の安定性がより向上する。 When acetylene alcohol (2) is used, the amount of acetylene alcohol (2) in the silver ink composition is preferably 0.03 to 0.7 mole per mole of the metal silver forming material. 0.05 to 0.3 mol is more preferable. When the blending amount of acetylene alcohol (2) is within such a range, the stability of the silver ink composition is further improved.
前記アルコールは、一種を単独で使用してもよいし、二種以上を併用してもよい。二種以上を併用する場合で、その組み合わせ及び比率は、任意に調節できる。 The said alcohol may be used individually by 1 type, and may use 2 or more types together. When two or more kinds are used in combination, the combination and ratio can be arbitrarily adjusted.
［その他の成分］
銀インク組成物は、前記金属銀の形成材料、含窒素化合物、還元剤及びアルコール以外の、その他の成分が配合されてなるものでもよい。
銀インク組成物における前記その他の成分は、目的に応じて任意に選択でき、特に限定されず、好ましいものとしては、アルコール以外の溶媒が例示でき、配合成分の種類や量に応じて任意に選択できる。
銀インク組成物における前記その他の成分は、一種を単独で使用してもよいし、二種以上を併用してもよい。二種以上を併用する場合で、その組み合わせ及び比率は、任意に調節できる。
[Other ingredients]
The silver ink composition may contain other components other than the metallic silver forming material, nitrogen-containing compound, reducing agent, and alcohol.
The other components in the silver ink composition can be arbitrarily selected according to the purpose, and are not particularly limited. Preferred examples thereof include solvents other than alcohol, and can be arbitrarily selected according to the type and amount of compounding components. it can.
One of these other components in the silver ink composition may be used alone, or two or more thereof may be used in combination. When two or more kinds are used in combination, the combination and ratio can be arbitrarily adjusted.
銀インク組成物において、配合成分の総量に対する前記その他の成分の配合量の割合は、１０質量％以下であることが好ましく、５質量％以下であることがより好ましく、０質量％、すなわちその他の成分を配合しなくても、銀インク組成物は十分にその効果を発現する。 In the silver ink composition, the ratio of the blending amount of the other components to the total blending component is preferably 10% by mass or less, more preferably 5% by mass or less, and 0% by mass, ie, other Even if the component is not blended, the silver ink composition exhibits its effect sufficiently.
銀インク組成物は、配合成分がすべて溶解していてもよいし、一部又は全ての成分が溶解せずに分散した状態であってもよいが、配合成分がすべて溶解していることが好ましく、溶解していない成分は均一に分散していることが好ましい。 In the silver ink composition, all the compounding components may be dissolved, or some or all of the components may be dispersed without dissolving, but it is preferable that all the compounding components are dissolved. The undissolved component is preferably dispersed uniformly.
［銀インク組成物の製造方法］
本発明はまた、前記銀インク組成物の製造方法であって、前記カルボン酸銀と、前記含窒素化合物と、を混合し、第一の混合物を得る第１工程と、前記第一の混合物又は前記第一の混合物と二酸化炭素とを混合して得られる第二の混合物と、炭素数１〜７の有機溶媒に溶解又は分散された前記還元性化合物と、を混合し、銀インク組成物を得る第２工程と、を含む、製造方法を提供する。
[Method for producing silver ink composition]
The present invention is also a method for producing the silver ink composition, wherein the silver carboxylate and the nitrogen-containing compound are mixed to obtain a first mixture, and the first mixture or A silver ink composition is prepared by mixing a second mixture obtained by mixing the first mixture and carbon dioxide and the reducing compound dissolved or dispersed in an organic solvent having 1 to 7 carbon atoms. And a second step of obtaining a manufacturing method.
炭素数１〜７の有機溶媒としては、例えば２５℃で前記還元性化合物と任意の割合で混合した時に均一な相を形成する化合物が好ましい。
炭素数１〜７の有機溶媒は、例えば２５℃で前記含窒素化合物及び前記還元性化合物と任意の割合で混合した時に均一な相を形成する化合物であることがより好ましい。
炭素数１〜７の有機溶媒として、より具体的には、メタノール、エタノール、プロパノール、ブタノール、ペンタノール、ヘキサノール、ヘプタノール、イソプロパノール等のアルコール；アセトン、メチルエチルケトン、メチルプロピルケトン、メチルブチルケトン、メチルペンチルケトン、シクロヘキサノン等のケトン；ジエチルエーテル、ジプロピルエーテル、テトラヒドロフラン、ジオキサン等のエーテル；ＤＭＳＯ（ジメチルスルホキシド）等のスルホキシド等が挙げられる。これらの有機溶媒は、一種を単独で使用してもよいし、二種以上を併用してもよい。
As the organic solvent having 1 to 7 carbon atoms, for example, a compound that forms a uniform phase when mixed with the reducing compound at an arbitrary ratio at 25 ° C. is preferable.
The organic solvent having 1 to 7 carbon atoms is more preferably a compound that forms a uniform phase when mixed with the nitrogen-containing compound and the reducing compound at an arbitrary ratio at 25 ° C., for example.
More specifically, examples of the organic solvent having 1 to 7 carbon atoms include alcohols such as methanol, ethanol, propanol, butanol, pentanol, hexanol, heptanol, and isopropanol; acetone, methyl ethyl ketone, methyl propyl ketone, methyl butyl ketone, and methyl pentyl. Examples include ketones such as ketone and cyclohexanone; ethers such as diethyl ether, dipropyl ether, tetrahydrofuran, and dioxane; sulfoxides such as DMSO (dimethyl sulfoxide). These organic solvents may be used individually by 1 type, and may use 2 or more types together.
上記の還元性化合物を、炭素数１〜７の有機溶媒に溶解又は分散した状態で、上記の第一の混合物に混合することにより、銀インク組成物のチキソトロピー性を向上させることができる。 The thixotropic property of the silver ink composition can be improved by mixing the reducing compound in the first mixture in a state of being dissolved or dispersed in an organic solvent having 1 to 7 carbon atoms.
炭素数１〜７の有機溶媒の量は、還元性化合物１モルあたり０．２モル以上であることが好ましく、０．３モル以上であることがより好ましく、０．４モル以上であることが更に好ましい。炭素数１〜７の有機溶媒の量が多いほど銀インク組成物のチキソトロピー性が向上する傾向にある。炭素数１〜７の有機溶媒の量の上限は、還元性化合物１モルあたり約２モルである。これ以上添加しても、更なるチキソトロピー性の向上は見られない傾向にあり、また銀インク組成物の銀濃度が低下してしまう場合がある。 The amount of the organic solvent having 1 to 7 carbon atoms is preferably 0.2 mol or more per mol of the reducing compound, more preferably 0.3 mol or more, and 0.4 mol or more. Further preferred. As the amount of the organic solvent having 1 to 7 carbon atoms increases, the thixotropic property of the silver ink composition tends to improve. The upper limit of the amount of the organic solvent having 1 to 7 carbon atoms is about 2 moles per mole of the reducing compound. Even if it is added more than this, no further improvement in thixotropy tends to be observed, and the silver concentration of the silver ink composition may decrease.
炭素数１〜７の有機溶媒は、第２工程中に揮発して消失してしまうものであることがより好ましい。このような有機溶媒であると、銀インク組成物の銀濃度が低下することがない。 The organic solvent having 1 to 7 carbon atoms is more preferably one that volatilizes and disappears during the second step. With such an organic solvent, the silver concentration of the silver ink composition does not decrease.
第２工程において、炭素数１〜７の有機溶媒に溶解又は分散された還元性化合物は、滴下しながら混合することが好ましい。また、滴下速度の変動を抑制すると、金属銀層の表面粗さをより低減できる傾向にある。 In the second step, the reducing compound dissolved or dispersed in the organic solvent having 1 to 7 carbon atoms is preferably mixed while dropping. Moreover, when the fluctuation | variation of dripping speed is suppressed, it exists in the tendency which can reduce the surface roughness of a metal silver layer more.
第１工程及び第２工程のいずれの工程においても、必要に応じてその他の成分を更に混合してもよい。また、第２工程で得られた銀インク組成物はそのまま使用してもよいし、必要に応じて引き続き公知の精製操作を行ってもよい。 In any of the first step and the second step, other components may be further mixed as necessary. Further, the silver ink composition obtained in the second step may be used as it is, or a known refining operation may be performed as necessary.
本発明においては、上記の各成分の混合時において、導電性を阻害する不純物が生成しないか、又はこのような不純物の生成量を極めて少ない量に抑制できるため、精製操作を行わなくても十分な導電性を有する金属銀層が得られる。 In the present invention, when the above components are mixed, impurities that inhibit conductivity are not generated, or the amount of such impurities generated can be suppressed to an extremely small amount. A metallic silver layer having excellent conductivity can be obtained.
第１工程及び第２工程における材料の混合時の混合方法は特に限定されず、撹拌子又は撹拌翼等を回転させて混合する方法；ミキサー、三本ロール、ニーダー又はビーズミル等を使用して混合する方法；超音波を加えて混合する方法等、公知の方法から適宜選択すればよい。 The mixing method at the time of mixing the materials in the first step and the second step is not particularly limited, and a method of mixing by rotating a stirring bar or a stirring blade; mixing using a mixer, three rolls, a kneader, a bead mill or the like The method to perform; You may select suitably from well-known methods, such as the method of adding and mixing an ultrasonic wave.
前記銀インク組成物は、混合成分がすべて溶解していてもよいし、一部の成分が溶解せずに分散した状態であってもよいが、混合成分がすべて溶解していることが好ましく、溶解していない成分は均一に分散していることが好ましい。溶解していない成分を均一に分散させる場合には、例えば、上記の三本ロール、ニーダー又はビーズミル等を用いて分散させる方法を適用するのが好ましい。 In the silver ink composition, all the mixed components may be dissolved or a part of the components may be dispersed without dissolving, but it is preferable that all the mixed components are dissolved, It is preferable that the components which are not dissolved are uniformly dispersed. In the case of uniformly dispersing the undissolved component, for example, it is preferable to apply a method of dispersing using the above-described three-roll, kneader or bead mill.
第１工程及び第２工程における混合温度は、各混合成分が劣化しない限り特に限定されないが、−５〜６０℃であることが好ましい。そして、混合温度は、混合成分の種類及び量に応じて、混合して得られた混合物が撹拌し易い粘度となるように、適宜調節するとよい。
また、第１工程及び第２工程における混合時間は、各混合成分が劣化しない限り特に限定されず、例えば１０分〜３６時間であり、例えば０．５〜１２時間である。
Although the mixing temperature in a 1st process and a 2nd process is not specifically limited unless each mixing component deteriorates, It is preferable that it is -5-60 degreeC. And mixing temperature is good to adjust suitably according to the kind and quantity of a mixing component so that the mixture obtained by mixing may become the viscosity which is easy to stir.
Moreover, the mixing time in a 1st process and a 2nd process is not specifically limited unless each mixing component deteriorates, For example, it is 10 minutes-36 hours, for example, is 0.5 to 12 hours.
第２工程において、混合物の温度が高い場合、この混合物は、後述する銀インク組成物の加熱処理時と同様の状態になるため、前記還元性化合物による前記カルボン酸銀の分解促進作用によって、前記カルボン酸銀の少なくとも一部において金属銀の形成が開始されることがあると推測される。このような金属銀を含有する銀インク組成物は、積層体の製造時において、金属銀を含有しない銀インク組成物よりも温和な条件で後処理を行うことにより、金属銀層を形成できることがある。また、還元性化合物の配合量が十分に多い場合にも、同様に温和な条件で後処理を行うことにより、金属銀層を形成できることがある。このように、前記カルボン酸銀の分解を促進する条件を採用することで、後処理として、より低温での加熱処理で、あるいは加熱処理を行わずに常温での乾燥処理のみで、金属銀層を形成できることがある。また、このような金属銀を含有する銀インク組成物は、金属銀を含有しない銀インク組成物と同様に取り扱うことができ、特に取り扱い性が劣ることもない。 In the second step, when the temperature of the mixture is high, the mixture is in the same state as in the heat treatment of the silver ink composition described later, and therefore, by the decomposition promoting action of the silver carboxylate by the reducing compound, It is speculated that the formation of metallic silver may be initiated in at least part of the silver carboxylate. Such a silver ink composition containing metallic silver can form a metallic silver layer by performing post-treatment under milder conditions than a silver ink composition not containing metallic silver during the production of the laminate. is there. Moreover, even when the compounding amount of the reducing compound is sufficiently large, a metallic silver layer may be formed by performing post-treatment under the same mild conditions. Thus, by adopting conditions that promote the decomposition of the silver carboxylate, as a post-treatment, the metal silver layer can be obtained by a heat treatment at a lower temperature or only by a drying treatment at room temperature without performing the heat treatment. Can be formed. Moreover, the silver ink composition containing such metal silver can be handled in the same manner as the silver ink composition not containing metal silver, and the handleability is not particularly inferior.
［二酸化炭素］
銀インク組成物は、さらに二酸化炭素が供給されてなるものでもよい。このような銀インク組成物は高粘度となり、例えば、フレキソ印刷法、スクリーン印刷法、グラビア印刷法、グラビアオフセット印刷法、パッド印刷法等の、インクを厚盛りすることが必要な印刷法への適用に好適である。
[carbon dioxide]
The silver ink composition may be further supplied with carbon dioxide. Such a silver ink composition has a high viscosity. For example, a flexographic printing method, a screen printing method, a gravure printing method, a gravure offset printing method, a pad printing method, etc. Suitable for application.
二酸化炭素は、銀インク組成物製造時のいずれの時期に供給してもよい。
例えば、カルボン酸銀及び含窒素化合物が配合されてなる第一の混合物に、二酸化炭素を供給して第二の混合物とし、第二の混合物に、さらに炭素数１〜７の有機溶媒に溶解又は分散された還元性化合物を配合して、銀インク組成物を製造してもよい。また、前記アルコール又はその他の成分を配合する場合、これらは、第一の混合物及び第二の混合物のいずれか一方又は両方の製造時に配合でき、目的に応じて任意に選択できる。
Carbon dioxide may be supplied at any time during the production of the silver ink composition.
For example, carbon dioxide is supplied to a first mixture in which silver carboxylate and a nitrogen-containing compound are blended to form a second mixture, and the second mixture is further dissolved in an organic solvent having 1 to 7 carbon atoms. A silver ink composition may be produced by blending the dispersed reducing compound. Moreover, when mix | blending the said alcohol or another component, these can be mix | blended at the time of manufacture of any one or both of a 1st mixture and a 2nd mixture, and can be arbitrarily selected according to the objective.
前記第一の混合物は、配合成分が異なる点以外は、上記の銀インク組成物と同様の方法で製造できる。 The first mixture can be produced by the same method as the above silver ink composition except that the blending components are different.
第一の混合物は、配合成分がすべて溶解していてもよいし、一部の成分が溶解せずに分散した状態であってもよいが、配合成分がすべて溶解していることが好ましく、溶解していない成分は均一に分散していることが好ましい。 The first mixture may have all of the compounding components dissolved, or may be in a state of being dispersed without dissolving some of the components, but preferably all of the compounding components are dissolved and dissolved. It is preferable that the components not dispersed are uniformly dispersed.
第一の混合物製造時の配合温度は、各配合成分が劣化しない限り特に限定されないが、−５〜６０℃であることが好ましい。また、配合時間は、配合成分の種類や配合時の温度に応じて適宜調節すればよいが、例えば１０分〜３６時間であり、例えば０．５〜１２時間である。 Although the compounding temperature at the time of manufacture of a 1st mixture is not specifically limited unless each compounding component deteriorates, It is preferable that it is -5-60 degreeC. Moreover, what is necessary is just to adjust suitably according to the kind of compounding component, and the temperature at the time of mixing | blending, for example, but it is 10 minutes-36 hours, for example, is 0.5 to 12 hours.
第一の混合物に供給される二酸化炭素（ＣＯ２）は、ガス状及び固形状（ドライアイス）のいずれでもよく、ガス状及び固形状の両方でもよい。二酸化炭素が供給されることにより、この二酸化炭素が第一の混合物に溶け込み、第一の混合物中の成分に作用することで、得られる第二の混合物の粘度が上昇すると推測される。 Carbon dioxide (CO 2 ) supplied to the first mixture may be either gaseous or solid (dry ice), or both gaseous and solid. By supplying carbon dioxide, it is estimated that this carbon dioxide dissolves in the first mixture and acts on the components in the first mixture, thereby increasing the viscosity of the obtained second mixture.
二酸化炭素ガスの供給は、液体中にガスを吹き込む公知の各種方法で行えばよく、適した供給方法を適宜選択すればよい。例えば、配管の一端を第一の混合物中に浸漬し、他端を二酸化炭素ガスの供給源に接続して、この配管を通じて二酸化炭素ガスを第一の混合物に供給する方法が例示できる。この時、配管の端部から直接二酸化炭素ガスを供給してもよいが、例えば、多孔質性のものなど、ガスの流路となり得る空隙部が多数設けられ、導入されたガスを拡散させて微小な気泡として放出することが可能なガス拡散部材を配管の端部に接続し、このガス拡散部材を介して二酸化炭素ガスを供給してもよい。また、第一の混合物の製造時と同様の方法で、第一の混合物を撹拌しながら二酸化炭素ガスを供給してもよい。このようにすることで、効率的に二酸化炭素を供給できる。 Carbon dioxide gas may be supplied by various known methods of blowing gas into the liquid, and a suitable supply method may be selected as appropriate. For example, a method in which one end of a pipe is immersed in the first mixture, the other end is connected to a carbon dioxide gas supply source, and the carbon dioxide gas is supplied to the first mixture through the pipe. At this time, the carbon dioxide gas may be supplied directly from the end of the pipe. For example, a plurality of voids that can serve as gas flow paths, such as a porous one, are provided to diffuse the introduced gas. A gas diffusion member that can be discharged as minute bubbles may be connected to the end of the pipe, and the carbon dioxide gas may be supplied through the gas diffusion member. Moreover, you may supply a carbon dioxide gas, stirring the 1st mixture by the method similar to the time of manufacture of a 1st mixture. By doing in this way, carbon dioxide can be supplied efficiently.
二酸化炭素ガスの供給量は、供給先の第一の混合物の量や、目的とする銀インク組成物又は第二の混合物の粘度に応じて適宜調節すればよく、特に限定されない。例えば、２０〜２５℃において、超音波式粘度計（ＣＢＣ社製「ＶＩＳＣＯＭＡＴＥ ＶＭ−１０Ａ」）で測定した粘度が５Ｐａ・ｓ以上である銀インク組成物を１００〜１０００ｇ程度得るためには、二酸化炭素ガスを１００Ｌ以上供給することが好ましく、２００Ｌ以上供給することがより好ましい。なお、ここでは銀インク組成物の２０〜２５℃における粘度について説明したが、銀インク組成物の使用時の温度は、２０〜２５℃に限定されるものではなく、任意に選択できる。 The supply amount of the carbon dioxide gas is not particularly limited as long as it is appropriately adjusted according to the amount of the first mixture at the supply destination and the viscosity of the target silver ink composition or the second mixture. For example, in order to obtain about 100 to 1000 g of a silver ink composition having a viscosity of 5 Pa · s or more measured at 20 to 25 ° C. with an ultrasonic viscometer (“VISCOMATE VM-10A” manufactured by CBC), It is preferable to supply 100 L or more of carbon gas, and it is more preferable to supply 200 L or more. In addition, although the viscosity at 20-25 degreeC of a silver ink composition was demonstrated here, the temperature at the time of use of a silver ink composition is not limited to 20-25 degreeC, It can select arbitrarily.
二酸化炭素ガスの流量は、必要とされる二酸化炭素ガスの供給量を考慮して適宜調節すればよいが、第一の混合物１ｇあたり０．５ｍＬ／分以上であることが好ましく、１ｍＬ／分以上であることがより好ましい。流量の上限値は特に限定されないが、取り扱い性等を考慮すると、混合物１ｇあたり４０ｍＬ／分であることが好ましい。
そして、二酸化炭素ガスの供給時間は、必要とされる二酸化炭素ガスの供給量や、流量を考慮して適宜調節すればよい
The flow rate of carbon dioxide gas may be appropriately adjusted in consideration of the required supply amount of carbon dioxide gas, but is preferably 0.5 mL / min or more per 1 g of the first mixture, and is 1 mL / min or more. It is more preferable that The upper limit value of the flow rate is not particularly limited, but is preferably 40 mL / min per 1 g of the mixture in consideration of handling properties and the like.
The carbon dioxide gas supply time may be appropriately adjusted in consideration of the required carbon dioxide gas supply amount and flow rate.
二酸化炭素ガス供給時の第一の混合物の温度は、５〜７０℃であることが好ましく、７〜６０℃であることがより好ましく、１０〜５０℃であることが特に好ましい。前記温度が前記下限値以上であることで、より効率的に二酸化炭素を供給でき、前記温度が前記上限値以下であることで、不純物が少ないより良好な品質の銀インク組成物が得られる。 The temperature of the first mixture at the time of supplying carbon dioxide gas is preferably 5 to 70 ° C, more preferably 7 to 60 ° C, and particularly preferably 10 to 50 ° C. When the temperature is equal to or higher than the lower limit value, carbon dioxide can be supplied more efficiently, and when the temperature is equal to or lower than the upper limit value, a silver ink composition having better quality with fewer impurities can be obtained.
二酸化炭素ガスの流量及び供給時間、並びに二酸化炭素ガス供給時の前記温度は、それぞれの値を相互に考慮しながら適した範囲に調節すればよい。例えば、前記温度を低めに設定しても、二酸化炭素ガスの流量を多めに設定するか、二酸化炭素ガスの供給時間を長めに設定することで、あるいはこの両方を行うことで、効率的に二酸化炭素を供給できる。また、二酸化炭素ガスの流量を少なめに設定しても、前記温度を高めにするか、二酸化炭素ガスの供給時間を長めに設定することで、あるいはこの両方を行うことで、効率的に二酸化炭素を供給できる。すなわち、二酸化炭素ガスの流量、二酸化炭素ガス供給時の前記温度として例示した上記数値範囲の中の数値を、二酸化炭素ガスの供給時間も考慮しつつ柔軟に組み合わせることで、良好な品質の銀インク組成物が効率的に得られる。 The flow rate and supply time of the carbon dioxide gas, and the temperature at the time of supplying the carbon dioxide gas may be adjusted to a suitable range while considering each value. For example, even if the temperature is set lower, the carbon dioxide gas flow rate is set higher, the carbon dioxide gas supply time is set longer, or both are performed efficiently. Can supply carbon. Moreover, even if the flow rate of carbon dioxide gas is set to a small value, the carbon dioxide gas can be efficiently produced by increasing the temperature, setting the carbon dioxide gas supply time longer, or both. Can supply. That is, a silver ink of good quality can be obtained by flexibly combining the numerical values in the above numerical range exemplified as the flow rate of carbon dioxide gas and the temperature at the time of carbon dioxide gas supply while considering the supply time of carbon dioxide gas. A composition is obtained efficiently.
二酸化炭素ガスの供給は、第一の混合物を撹拌しながら行うことが好ましい。このようにすることで、供給した二酸化炭素ガスがより均一に第一の混合物中に拡散し、より効率的に二酸化炭素を供給できる。
この時の撹拌方法は、二酸化炭素を用いない上記の銀インク組成物の製造時における前記混合方法の場合と同様でよい。
The carbon dioxide gas is preferably supplied while stirring the first mixture. By doing in this way, the supplied carbon dioxide gas diffuses more uniformly in the first mixture, and carbon dioxide can be supplied more efficiently.
The stirring method at this time may be the same as in the case of the mixing method at the time of producing the above silver ink composition not using carbon dioxide.
ドライアイス（固形状二酸化炭素）の供給は、第一の混合物中にドライアイスを添加することで行えばよい。ドライアイスは、全量を一括して添加してもよいし、分割して段階的に（添加を行わない時間帯を挟んで連続的に）添加してもよい。
ドライアイスの使用量は、上記の二酸化炭素ガスの供給量を考慮して調節すればよい。
ドライアイスの添加中及び添加後は、第一の混合物を撹拌することが好ましく、例えば、二酸化炭素を用いない上記の銀インク組成物の製造時と同様の方法で撹拌することが好ましい。このようにすることで、効率的に二酸化炭素を供給できる。
撹拌時の温度は、二酸化炭素ガス供給時と同様でよい。また、撹拌時間は、撹拌温度に応じて適宜調節すればよい。
The supply of dry ice (solid carbon dioxide) may be performed by adding dry ice to the first mixture. The total amount of dry ice may be added all at once, or may be added stepwise (continuously across a time zone during which no addition is performed).
What is necessary is just to adjust the usage-amount of dry ice in consideration of the supply amount of said carbon dioxide gas.
During and after the addition of dry ice, the first mixture is preferably stirred. For example, the first mixture is preferably stirred in the same manner as in the production of the above silver ink composition without using carbon dioxide. By doing in this way, carbon dioxide can be supplied efficiently.
The temperature at the time of stirring may be the same as that at the time of supplying carbon dioxide gas. Moreover, what is necessary is just to adjust stirring time suitably according to stirring temperature.
第二の混合物の粘度は、銀インク組成物又は第二の混合物の取り扱い方法など、目的に応じて適宜調節すればよく、特に限定されない。例えば、銀インク組成物をスクリーン印刷法、フレキソ印刷法等の高粘度インクを使用する印刷法へ適用する場合には、第二の混合物の２０〜２５℃における粘度は、３Ｐａ・ｓ以上であることが好ましい。なお、ここでは第二の混合物の２０〜２５℃における粘度について説明したが、第二の混合物の使用時の温度は、２０〜２５℃に限定されるものではなく、任意に選択できる。 The viscosity of the second mixture may be appropriately adjusted depending on the purpose, such as a silver ink composition or a method of handling the second mixture, and is not particularly limited. For example, when the silver ink composition is applied to a printing method using a high viscosity ink such as a screen printing method or a flexographic printing method, the viscosity of the second mixture at 20 to 25 ° C. is 3 Pa · s or more. It is preferable. In addition, although the viscosity at 20-25 degreeC of the 2nd mixture was demonstrated here, the temperature at the time of use of a 2nd mixture is not limited to 20-25 degreeC, It can select arbitrarily.
前記第二の混合物に炭素数１〜７の有機溶媒に溶解又は分散された還元性化合物を配合し、さらに必要に応じてアルコール及びその他の成分からなる群から選択される一種以上を配合して、銀インク組成物とすることができる。
このときの銀インク組成物は、配合成分が異なる点以外は、二酸化炭素を用いない上記の銀インク組成物と同様の方法で製造できる。そして、得られた銀インク組成物は、配合成分がすべて溶解していてもよいし、一部の成分が溶解せずに分散した状態であってもよいが、配合成分がすべて溶解していることが好ましく、溶解していない成分は均一に分散していることが好ましい。
In the second mixture, a reducing compound dissolved or dispersed in an organic solvent having 1 to 7 carbon atoms is blended, and if necessary, one or more selected from the group consisting of alcohol and other components is blended. And a silver ink composition.
The silver ink composition at this time can be manufactured by the same method as the above silver ink composition not using carbon dioxide except that the blending components are different. The obtained silver ink composition may have all of the compounding components dissolved therein or may be in a state where some of the components are dispersed without dissolving, but all of the compounding components are dissolved. Preferably, the undissolved component is preferably dispersed uniformly.
前記炭素数１〜７の有機溶媒に溶解又は分散された還元性化合物の配合時の温度は、各配合成分が劣化しない限り特に限定されないが、−５〜６０℃であることが好ましい。そして、配合時の温度は、配合成分の種類及び量に応じて、配合して得られた混合物が撹拌し易い粘度となるように、適宜調節するとよい。
また、配合時間は、配合成分の種類や配合時の温度に応じて適宜調節すればよいが、例えば、０．５〜１２時間であることが好ましい。
Although the temperature at the time of the mixing | blending of the reducing compound melt | dissolved or disperse | distributed to the said C1-C7 organic solvent is not specifically limited unless each compounding component deteriorates, It is preferable that it is -5-60 degreeC. And the temperature at the time of mixing | blending is good to adjust suitably so that the mixture obtained by mix | blending may become the viscosity which is easy to stir according to the kind and quantity of a mixing | blending component.
Moreover, what is necessary is just to adjust a compounding time suitably according to the kind of compounding component, and the temperature at the time of a compounding, For example, it is preferable that it is 0.5 to 12 hours.
前記その他の成分は、先に説明したように、前記第一の混合物及び第二の混合物のいずれかの製造時に配合されてもよく、両方の製造時に配合されてもよい。すなわち、第一の混合物及び第二の混合物を経て銀インク組成物を製造する過程において、二酸化炭素以外の配合成分の総量に対する前記その他の成分の配合量の割合（［その他の成分（質量）］／［カルボン酸銀、含窒素化合物、炭素数１〜７の有機溶媒に溶解又は分散された還元性化合物、アルコール、及びその他の成分（質量）］×１００）は、１０質量％以下であることが好ましく、５質量％以下であることがより好ましく、０質量％、すなわちその他の成分を配合しなくても、銀インク組成物は十分にその効果を発現する。 As described above, the other components may be blended during the production of either the first mixture or the second mixture, or may be blended during the production of both. That is, in the process of producing the silver ink composition through the first mixture and the second mixture, the ratio of the blended amount of the other components to the total amount of blended components other than carbon dioxide ([other components (mass)] / [Silver carboxylate, nitrogen-containing compound, reducing compound dissolved or dispersed in an organic solvent having 1 to 7 carbon atoms, alcohol, and other components (mass)] × 100) is 10% by mass or less However, it is more preferably 5% by mass or less, and 0% by mass, that is, the silver ink composition exhibits its effect sufficiently even when other components are not blended.
二酸化炭素が供給されてなる銀インク組成物は、例えば、銀インク組成物をスクリーン印刷法、フレキソ印刷法等の高粘度インクを使用する印刷法へ適用する場合には、２０〜２５℃における粘度が、１Ｐａ・ｓ以上であることが好ましい。 The silver ink composition to which carbon dioxide is supplied is, for example, a viscosity at 20 to 25 ° C. when the silver ink composition is applied to a printing method using a high viscosity ink such as a screen printing method or a flexographic printing method. Is preferably 1 Pa · s or more.
＜導電体＞
前記銀インク組成物を用いて、金属銀を主成分とする導電体を形成することができる。ここで、「金属銀を主成分とする」とは、金属銀の比率が、見かけ上金属銀だけからなるとみなし得る程度に十分に高いことを意味し、例えば、導電体中の金属銀の比率は９９質量％以上であることが好ましい。
<Conductor>
Using the silver ink composition, a conductor mainly composed of metallic silver can be formed. Here, “having metallic silver as a main component” means that the ratio of metallic silver is sufficiently high so that it can be regarded as being composed solely of metallic silver. For example, the ratio of metallic silver in a conductor Is preferably 99% by mass or more.
前記導電体は、例えば、基材上に銀インク組成物を付着させ、乾燥処理や加熱（焼成）処理等の後処理を適宜選択して行うことで製造できる。加熱処理は、乾燥処理を兼ねて行ってもよい。
基材は、フィルム状又はシート状であることが好ましく、厚さが１０〜５０００μｍであることが好ましい。
The conductor can be produced, for example, by attaching a silver ink composition on a substrate and appropriately performing post-treatment such as drying or heating (firing). The heat treatment may be performed also as a drying treatment.
The substrate is preferably in the form of a film or a sheet, and preferably has a thickness of 10 to 5000 μm.
基材の材質は、目的に応じて適宜選択すればよく、特に限定されないが、好ましいものとして具体的には、ポリエチレン（ＰＥ）、ポリプロピレン（ＰＰ）、ポリ塩化ビニル（ＰＶＣ）、ポリ塩化ビニリデン（ＰＶＤＣ）、ポリメチルペンテン（ＰＭＰ）、ポリシクロオレフィン、ポリスチレン（ＰＳ）、ポリ酢酸ビニル（ＰＶＡｃ）、ポリメタクリル酸メチル（ＰＭＭＡ）等のアクリル樹脂、ＡＳ樹脂、ＡＢＳ樹脂、ポリアミド（ＰＡ）、ポリイミド、ポリアミドイミド（ＰＡＩ）、ポリアセタール、ポリエチレンテレフタレート（ＰＥＴ）、ポリブチレンテレフタレート（ＰＢＴ）、ポリトリメチレンテレフタレート（ＰＴＴ）、ポリエチレンナフタレート（ＰＥＮ）、ポリブチレンナフタレート（ＰＢＮ）、ポリフェニレンスルファイド（ＰＰＳ）、ポリスルホン（ＰＳＦ）、ポリエーテルスルホン（ＰＥＳ）、ポリエーテルケトン（ＰＥＫ）、ポリエーテルエーテルケトン（ＰＥＥＫ）、ポリカーボネート（ＰＣ）、ポリウレタン、ポリフェニレンエーテル（ＰＰＥ）、変性ポリフェニレンエーテル（ｍ−ＰＰＥ）、ポリアリレート、エポキシ樹脂、メラミン樹脂、フェノール樹脂、尿素樹脂等の合成樹脂が例示できる。
また、基材の材質としては、上記以外にも、ガラス、シリコン等のセラミックスや、紙が例示できる。
また、基材は、ガラスエポキシ樹脂、ポリマーアロイ等の、二種以上の材質からなるものでもよい。
The material of the base material may be appropriately selected according to the purpose and is not particularly limited, but specific examples of preferable materials include polyethylene (PE), polypropylene (PP), polyvinyl chloride (PVC), and polyvinylidene chloride ( PVDC), polymethylpentene (PMP), polycycloolefin, polystyrene (PS), polyvinyl acetate (PVAc), acrylic resin such as polymethyl methacrylate (PMMA), AS resin, ABS resin, polyamide (PA), polyimide , Polyamideimide (PAI), polyacetal, polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polytrimethylene terephthalate (PTT), polyethylene naphthalate (PEN), polybutylene naphthalate (PBN), polyphenylene sulfide (PPS), polysulfone (PSF), polyethersulfone (PES), polyetherketone (PEK), polyetheretherketone (PEEK), polycarbonate (PC), polyurethane, polyphenylene ether (PPE), modified polyphenylene ether (m- PPE), polyarylate, epoxy resin, melamine resin, phenol resin, urea resin, and other synthetic resins can be exemplified.
In addition to the above, the material of the substrate can be exemplified by ceramics such as glass and silicon, and paper.
The base material may be made of two or more kinds of materials such as glass epoxy resin and polymer alloy.
基材は、単層からなるものでもよいし、二層以上の複数層からなるものでもよい。基材が複数層からなる場合、これら複数層は、互いに同一でも異なっていてもよい。すなわち、すべての層が同一であってもよいし、すべての層が異なっていてもよく、一部の層のみが異なっていてもよい。そして、複数層が互いに異なる場合、これら複数層の組み合わせは特に限定されない。ここで、複数層が互いに異なるとは、各層の材質及び厚さの少なくとも一方が互いに異なることを意味する。
なお、基材が複数層からなる場合には、各層の合計の厚さが、上記の好ましい基材の厚さとなるようにするとよい。
The substrate may be composed of a single layer, or may be composed of two or more layers. When a base material consists of multiple layers, these multiple layers may be the same as or different from each other. That is, all the layers may be the same, all the layers may be different, or only some of the layers may be different. And when several layers differ from each other, the combination of these several layers is not specifically limited. Here, the plurality of layers being different from each other means that at least one of the material and the thickness of each layer is different from each other.
In addition, when a base material consists of multiple layers, it is good to make it the total thickness of each layer be the thickness of said preferable base material.
銀インク組成物は、例えば、印刷法、塗布法、浸漬法等の公知の方法で基材上に付着させることができる。
前記印刷法としては、スクリーン印刷法、フレキソ印刷法、オフセット印刷法、ディップ式印刷法、インクジェット式印刷法、ディスペンサー式印刷法、グラビア印刷法、グラビアオフセット印刷法、パッド印刷法等が例示できる。
前記塗布法としては、スピンコーター、エアーナイフコーター、カーテンコーター、ダイコーター、ブレードコーター、ロールコーター、ゲートロールコーター、バーコーター、ロッドコーター、グラビアコーター等の各種コーターや、ワイヤーバー等を用いる方法が例示できる。
A silver ink composition can be made to adhere on a base material by well-known methods, such as a printing method, the apply | coating method, and the immersion method, for example.
Examples of the printing method include screen printing method, flexographic printing method, offset printing method, dip printing method, ink jet printing method, dispenser printing method, gravure printing method, gravure offset printing method, pad printing method and the like.
Examples of the coating method include spin coaters, air knife coaters, curtain coaters, die coaters, blade coaters, roll coaters, gate roll coaters, bar coaters, rod coaters, gravure coaters, and other methods such as wire bars. It can be illustrated.
銀インク組成物の乾燥処理は、公知の方法で行えばよく、例えば、常圧下、減圧下及び送風条件下のいずれで行ってもよく、大気下及び不活性ガス雰囲気下のいずれでおこなってもよい。そして、乾燥温度も特に限定されず、加熱乾燥及び常温乾燥のいずれでもよい。加熱処理が不要な場合の好ましい乾燥方法としては、１８〜３０℃で大気下において乾燥させる方法が例示できる。 The silver ink composition may be dried by a known method. For example, the silver ink composition may be dried under normal pressure, reduced pressure, or air blowing conditions, and may be performed in the air or in an inert gas atmosphere. Good. Also, the drying temperature is not particularly limited, and may be either heat drying or room temperature drying. As a preferable drying method when the heat treatment is unnecessary, a method of drying in the atmosphere at 18 to 30 ° C. can be exemplified.
銀インク組成物を加熱処理する場合、加熱処理時の温度は、好ましくは１００℃以下、より好ましくは９０℃以下とすることができる。加熱処理時の温度の下限値は、金属銀を効率的に形成できる限り特に限定されないが、５０℃であることが好ましい。
また、加熱時間は、加熱温度に応じて適宜調節すればよく、例えば、０．１〜６時間とすることができる。
When the silver ink composition is heat-treated, the temperature during the heat treatment is preferably 100 ° C. or lower, more preferably 90 ° C. or lower. Although the lower limit of the temperature at the time of heat processing is not specifically limited as long as metallic silver can be formed efficiently, it is preferable that it is 50 degreeC.
Moreover, what is necessary is just to adjust a heating time suitably according to heating temperature, for example, can be 0.1 to 6 hours.
前記導電体は、金属銀が十分に形成され、導電性が高い、すなわち体積抵抗率が低いものとすることができ、例えば、体積抵抗率を好ましくは２５００μΩ・ｃｍ以下、より好ましくは１０００μΩ・ｃｍ以下、特に好ましくは３００μΩ・ｃｍとすることができる。 The conductor may be sufficiently formed of metallic silver and have high conductivity, that is, low volume resistivity. For example, the volume resistivity is preferably 2500 μΩ · cm or less, more preferably 1000 μΩ · cm. Hereinafter, it is particularly preferably set to 300 μΩ · cm.
また、前記導電体は、表面粗さを十分に低減することができ、好ましくは６００ｎｍ以下、より好ましくは３００ｎｍ以下、さらに好ましくは２５０ｎｍ以下、特に好ましくは２００ｎｍ以下、最も好ましくは１００ｎｍ以下とすることができる。
なお、本明細書において「表面粗さ」とは、算術平均粗さ（Ｒａ）を意味し、粗さ曲線からその平均線の方向に基準長さｌだけを抜き取り、この抜取り部分の平均線の方向にＸ軸を、縦倍率の方向にＹ軸を取り、粗さ曲線をｙ＝ｆ（ｘ）で表したときに、以下の式によって求められた値をナノメートル（ｎｍ）単位で表示したものである。以下、この表面粗さを「表面粗さＲａ」と記載することがある。
Further, the conductor can sufficiently reduce the surface roughness, and is preferably 600 nm or less, more preferably 300 nm or less, further preferably 250 nm or less, particularly preferably 200 nm or less, and most preferably 100 nm or less. Can do.
In this specification, “surface roughness” means arithmetic average roughness (Ra), and only the reference length l is extracted from the roughness curve in the direction of the average line, and the average line of the extracted portion is measured. When the X axis is taken in the direction, the Y axis is taken in the direction of the vertical magnification, and the roughness curve is expressed by y = f (x), the value obtained by the following formula is displayed in nanometer (nm) units. Is. Hereinafter, this surface roughness may be referred to as “surface roughness Ra”.
上記の積層体は、高温での加熱処理を行うことなく製造可能であり、金属銀層の厚さを十分に薄くすることができ、さらに十分に低減された体積抵抗率及び表面粗さを示すことから、例えば、通信機器の配線板として好適である。 The above laminate can be manufactured without heat treatment at high temperature, the thickness of the metal silver layer can be sufficiently reduced, and further exhibits sufficiently reduced volume resistivity and surface roughness. Therefore, for example, it is suitable as a wiring board for communication equipment.
次に実施例を示して本発明をさらに詳細に説明するが、本発明は以下の実施例に限定されるものではない。 EXAMPLES Next, although an Example is shown and this invention is demonstrated further in detail, this invention is not limited to a following example.
［実施例１］
（銀インク組成物の作製）
液温が５０℃以下となるように、ビーカー中で２−エチルヘキシルアミンに２−メチルアセト酢酸銀を添加して、メカニカルスターラーを用いて１５分間撹拌することにより、液状物を得た。
[Example 1]
(Preparation of silver ink composition)
A liquid substance was obtained by adding silver 2-methylacetoacetate to 2-ethylhexylamine in a beaker so that the liquid temperature was 50 ° C. or lower and stirring for 15 minutes using a mechanical stirrer.
上述した液状物に、反応液の温度が５０℃以下となるように、ギ酸のエタノール溶液を３０分間かけて滴下した。ギ酸１モルあたりのエタノールの量は、０．２５モルであった。ギ酸の滴下終了後、２５℃にて反応液をさらに１．５時間撹拌することにより、実施例１の銀インク組成物を得た。２−メチルアセト酢酸銀の配合量１モルあたりの２−エチルヘキシルアミン及びギ酸の配合量は、それぞれ０．４モル及び０．７モルであった。 An ethanol solution of formic acid was added dropwise to the above-mentioned liquid over 30 minutes so that the temperature of the reaction solution was 50 ° C. or lower. The amount of ethanol per mole of formic acid was 0.25 mole. After completion of the formic acid dropwise addition, the reaction liquid was further stirred at 25 ° C. for 1.5 hours to obtain a silver ink composition of Example 1. The blending amounts of 2-ethylhexylamine and formic acid per mole of silver 2-methylacetoacetate were 0.4 mole and 0.7 mole, respectively.
（粘度の測定）
得られた銀インク組成物について、レオメータ（Ａｎｔｏｎ Ｐａａｒ社製「ＭＣＲ−３０１」）を用いて、２５℃で、せん断速度１０ｓ−１である場合のせん断粘度及びせん断速度１０００ｓ−１である場合のせん断粘度を測定した。ここで、レオメータのコーンプレートとしては、ＣＰ−２５−２（直径２５ｍｍ、コーン角度２°）を用いた。測定したせん断粘度の比［せん断速度１０ｓ−１で測定した粘度（Ｐａ・ｓ）／せん断速度１０００ｓ−１で測定した粘度（Ｐａ・ｓ）］を計算し、チキソトロピー指数を求めた。結果を表１に示す。
（銀濃度の測定）
実施例１の銀インク組成物を定量してるつぼに入れ、４００℃で３時間加熱処理した。加熱処理後にるつぼ内に残った金属銀を定量し、銀インク組成物中の銀濃度（質量％）を算出した。結果を表１に示す。
(Measurement of viscosity)
About the obtained silver ink composition, using a rheometer (“MCR-301” manufactured by Anton Paar), the shear viscosity when the shear rate is 10 s −1 and the shear rate is 1000 s −1 at 25 ° C. Shear viscosity was measured. Here, CP-25-2 (
(Measurement of silver concentration)
The silver ink composition of Example 1 was quantitatively placed in a crucible and heat treated at 400 ° C. for 3 hours. The metallic silver remaining in the crucible after the heat treatment was quantified, and the silver concentration (mass%) in the silver ink composition was calculated. The results are shown in Table 1.
［実施例２］
ギ酸１モルあたりのエタノールの量を、０．３７５モルに変更した以外は実施例１と同様にして実施例２の銀インク組成物を作製し、チキソトロピー指数及び銀濃度を求めた。結果を表１に示す。
[Example 2]
A silver ink composition of Example 2 was prepared in the same manner as in Example 1 except that the amount of ethanol per mol of formic acid was changed to 0.375 mol, and the thixotropy index and silver concentration were determined. The results are shown in Table 1.
［実施例３］
ギ酸１モルあたりのエタノールの量を、０．５モルに変更した以外は実施例１と同様にして実施例３の銀インク組成物を作製し、チキソトロピー指数及び銀濃度を求めた。結果を表１に示す。
[Example 3]
A silver ink composition of Example 3 was prepared in the same manner as in Example 1 except that the amount of ethanol per mol of formic acid was changed to 0.5 mol, and the thixotropy index and silver concentration were determined. The results are shown in Table 1.
［実施例４］
ギ酸の希釈を、ギ酸１モルあたり０．５モルのメタノールで行った点以外は実施例１と同様にして実施例４の銀インク組成物を作製し、チキソトロピー指数及び銀濃度を求めた。結果を表１に示す。
[Example 4]
A silver ink composition of Example 4 was prepared in the same manner as in Example 1 except that formic acid was diluted with 0.5 mole of methanol per mole of formic acid, and the thixotropic index and silver concentration were determined. The results are shown in Table 1.
［実施例５］
ギ酸の希釈を、ギ酸１モルあたり０．５モルのアセトンで行った点以外は実施例１と同様にして実施例５の銀インク組成物を作製し、チキソトロピー指数及び銀濃度を求めた。結果を表１に示す。
[Example 5]
A silver ink composition of Example 5 was prepared in the same manner as in Example 1 except that formic acid was diluted with 0.5 mol of acetone per mol of formic acid, and the thixotropic index and silver concentration were determined. The results are shown in Table 1.
［比較例１］
ギ酸の希釈を行わなかった点以外は実施例１と同様にして比較例１の銀インク組成物を作製し、チキソトロピー指数及び銀濃度を求めた。結果を表１に示す。
[Comparative Example 1]
A silver ink composition of Comparative Example 1 was prepared in the same manner as in Example 1 except that formic acid was not diluted, and the thixotropy index and silver concentration were determined. The results are shown in Table 1.
実施例１〜５の銀インク組成物は、比較例１のものと比較して、向上したチキソトロピー指数を示した。また、実施例１〜５の銀インク組成物は、比較例１の銀インク組成物と比較して、銀濃度が同等かより高かったことから、有機溶媒は揮発して消失し、銀インク組成物中には残存していないと考えられた。 The silver ink compositions of Examples 1-5 exhibited an improved thixotropy index compared to that of Comparative Example 1. Further, since the silver ink compositions of Examples 1 to 5 had the same or higher silver concentration than the silver ink composition of Comparative Example 1, the organic solvent volatilized and disappeared, and the silver ink composition It was thought that it did not remain in the product.
図１は、実施例１〜５及び比較例１の銀インク組成物のチキソトロピー指数と、有機溶媒の量（ギ酸１モルあたりのモル数）との関係を示すグラフである。有機溶媒の量が多いほど銀インク組成物のチキソトロピー指数が高くなる傾向が見られた。 FIG. 1 is a graph showing the relationship between the thixotropy index of the silver ink compositions of Examples 1 to 5 and Comparative Example 1 and the amount of organic solvent (number of moles per mole of formic acid). There was a tendency that the thixotropy index of the silver ink composition increased as the amount of the organic solvent increased.
本発明によれば、より低温での加熱処理によって、十分な導電性を有する金属銀を形成可能であり、向上したチキソトロピー性を有する銀インク組成物及びその製造方法を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the silver ink composition which can form the metal silver which has sufficient electroconductivity by heat processing at lower temperature, and has the improved thixotropic property, and its manufacturing method can be provided.
Claims (2)
Ｙ １ はそれぞれ独立にフッ素原子、塩素原子、臭素原子又は水素原子であり；Ｒ １ は炭素数１〜１９の脂肪族炭化水素基又はフェニル基であり；Ｒ ２ は炭素数１〜２０の脂肪族炭化水素基であり；Ｒ ３ は炭素数１〜１６の脂肪族炭化水素基であり；Ｒ ４ 及びＲ ５ はそれぞれ独立に炭素数１〜１８の脂肪族炭化水素基であり；Ｒ ６ は炭素数１〜１９の脂肪族炭化水素基、水酸基又は式「ＡｇＯ−」で表される基であり；
Ｘ １ はそれぞれ独立に水素原子、炭素数１〜２０の脂肪族炭化水素基、ハロゲン原子、１個以上の水素原子が置換基で置換されていてもよいフェニル基若しくはベンジル基、シアノ基、Ｎ−フタロイル−３−アミノプロピル基、２−エトキシビニル基、又は一般式「Ｒ ７ Ｏ−」、「Ｒ ７ Ｓ−」、「Ｒ ７ −Ｃ（＝Ｏ）−」若しくは「Ｒ ７ −Ｃ（＝Ｏ）−Ｏ−」で表される基であり；
Ｒ ７ は、炭素数１〜１０の脂肪族炭化水素基、チエニル基、又は１個以上の水素原子が置換基で置換されていてもよいフェニル基若しくはジフェニル基である。）
炭素数２５以下のアミン化合物、炭素数２５以下の第４級アンモニウム塩、アンモニア及び前記アミン化合物又はアンモニアが酸と反応してなるアンモニウム塩からなる群から選択される１種以上の含窒素化合物と、
シュウ酸、ヒドラジン及び下記一般式（５）で表される化合物からなる群から選択される１種以上の還元性化合物と、が配合されてなり、
Ｈ−Ｃ（＝Ｏ）−Ｒ２１…（５）
（式中、Ｒ２１は、炭素数２０以下のアルキル基、アルコキシ基若しくはＮ，Ｎ−ジアルキルアミノ基、水酸基又はアミノ基である。）
下記式（Ｔ１）で定義されるチキソトロピー指数が１５以上であることを特徴とする銀インク組成物。
チキソトロピー指数＝（２５℃、せん断速度１０ｓ−１で測定した粘度）／（２５℃、せん断速度１０００ｓ−１で測定した粘度）…（Ｔ１） Β-ketocarboxylate silver represented by the following general formula (1):
Y 1 is each independently a fluorine atom, a chlorine atom, a bromine atom or a hydrogen atom; R 1 is an aliphatic hydrocarbon group having 1 to 19 carbon atoms or a phenyl group; R 2 is an aliphatic having 1 to 20 carbon atoms R 3 is an aliphatic hydrocarbon group having 1 to 16 carbon atoms; R 4 and R 5 are each independently an aliphatic hydrocarbon group having 1 to 18 carbon atoms; R 6 is An aliphatic hydrocarbon group having 1 to 19 carbon atoms, a hydroxyl group or a group represented by the formula “AgO—”;
X 1 is independently a hydrogen atom, an aliphatic hydrocarbon group having 1 to 20 carbon atoms, a halogen atom, a phenyl group or benzyl group in which one or more hydrogen atoms may be substituted with a substituent, a cyano group, N - phthaloyl-3-aminopropyl group, 2-ethoxyethyl vinyl group, or the general formula "R 7 O -", "R 7 S -", "R 7 -C (= O) -" or "R 7 -C ( ═O) —O— ”;
R 7 is an aliphatic hydrocarbon group having 1 to 10 carbon atoms, a thienyl group, or a phenyl group or diphenyl group in which one or more hydrogen atoms may be substituted with a substituent. )
One or more nitrogen-containing compounds selected from the group consisting of an amine compound having 25 or less carbon atoms, a quaternary ammonium salt having 25 or less carbon atoms, ammonia and an ammonium salt obtained by reacting the amine compound or ammonia with an acid; ,
Oxalic acid, hydrazine and one or more reducing compounds selected from the group consisting of compounds represented by the following general formula (5) are blended:
H-C (= O) -R 21 ... (5)
(In the formula, R 21 represents an alkyl group having 20 or less carbon atoms, an alkoxy group, an N, N-dialkylamino group, a hydroxyl group, or an amino group.)
A silver ink composition having a thixotropy index defined by the following formula (T1) of 15 or more.
Thixotropic index = (viscosity measured at 25 ° C., shear rate 10 s −1 ) / (viscosity measured at 25 ° C., shear rate 1000 s −1 ) (T1)
前記β−ケトカルボン酸銀と、前記含窒素化合物と、を混合し、第一の混合物を得る第１工程と、
前記第一の混合物又は前記第一の混合物と二酸化炭素とを混合して得られる第二の混合物に、炭素数１〜７の有機溶媒に溶解又は分散された前記還元性化合物を滴下しながら混合し、銀インク組成物を得る第２工程と、を含み、
前記第２工程において、前記有機溶媒が揮発して消失する、製造方法。 A method for producing the silver ink composition according to claim 1,
Wherein the β- keto silver carboxylate, said mixed with a nitrogen-containing compound, and a first step of obtaining a first mixture,
The second mixture obtained by mixing the carbon dioxide the first mixture or said first mixture, mixing while dropping the reducing compound, dissolved or dispersed in an organic solvent having 1 to 7 carbon atoms and, a second step of obtaining a silver ink composition, only including,
In the second step, the organic solvent volatilizes and disappears .