JP6269477B2 - 有機el表示装置 - Google Patents
有機el表示装置 Download PDFInfo
- Publication number
- JP6269477B2 JP6269477B2 JP2014504828A JP2014504828A JP6269477B2 JP 6269477 B2 JP6269477 B2 JP 6269477B2 JP 2014504828 A JP2014504828 A JP 2014504828A JP 2014504828 A JP2014504828 A JP 2014504828A JP 6269477 B2 JP6269477 B2 JP 6269477B2
- Authority
- JP
- Japan
- Prior art keywords
- retardation film
- layer
- film
- organic
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[1]光出射側から順に、基板、透明電極、発光層及び金属電極層を具備してなる有機EL表示装置であって、
前記基板の光出射側に偏光フィルムと位相差フィルムとを積層してなる円偏光板を備え、
前記位相差フィルムが、
シンジオタクチック構造を有するポリスチレン系重合体およびポリアリーレンエーテルを含む樹脂組成物(A)からなる層を備え、
前記樹脂組成物(A)におけるシンジオタクチック構造を有するポリスチレン系重合体とポリアリーレンエーテルとの割合が、シンジオタクチック構造を有するポリスチレン系重合体:ポリアリーレンエーテルの重量比で、65:35〜55:45であり、
Re450<Re550<Re650の関係を満たし、かつ
波長550nmにおけるNz係数が−0.25〜−0.05である、有機EL表示装置。
(ただし、Re450、Re550、およびRe650はそれぞれ、測定波長450nm、550nm、および650nmにおける位相差フィルムの面内方向のレターデーションを表し、
Nz係数は(nx−nz)/(nx−ny)を表し、
nxは位相差フィルムの面内の遅相軸方向の屈折率を表し、
nyは位相差フィルムの面内の進相軸方向の屈折率を表し、
nzは位相差フィルムの厚み方向の屈折率を表す。)
[3]前記位相差フィルムの波長550nmにおける複屈折Δn(ただし、Δn=nx−nyである)が、0.0020以上0.0050以下である、[1]又は[2]記載の有機EL表示装置。
[4]前記位相差フィルムの厚さが80μm以下である、[1]〜[3]のいずれか一項に記載の有機EL表示装置。
[5]前記ポリアリーレンエーテルがフェニレンエーテル単位を含む重合体を含有する、[1]〜[4]のいずれか一項に記載の有機EL表示装置。
[6]前記位相差フィルムの測定波長550nmにおける面内方向のレターデーションRe550が110nm〜150nmである、[1]〜[5]のいずれか一項に記載の有機EL表示装置。
[7]前記位相差フィルムが、前記樹脂組成物(A)からなる長尺の延伸前フィルムを、その長尺方向に対して40°以上50°以下の範囲に延伸してなるものである、[1]〜[6]のいずれか一項に記載の有機EL表示装置。
[9]前記位相差フィルムが、前記樹脂組成物(A)からなるP1層と、前記P1層に接して設けられた熱可塑性樹脂(B)からなるP2層とを有する長尺の延伸前フィルム積層体を、その長尺方向に対して40°以上50°以下の範囲に延伸して、P1層が延伸されてなるp1層と、P2層が延伸されてなるp2層とを有する位相差フィルム積層体を得た後、p2層を剥離してなるものである、[1]〜[6]のいずれか一項に記載の有機EL表示装置。
[10]前記熱可塑性樹脂(B)が、アクリル樹脂、脂環式構造含有重合体を含む樹脂およびポリカーボネート樹脂から選ばれる少なくとも1種である、[8]又は[9]に記載の有機EL表示装置。
[11]前記長尺の延伸前フィルム積層体が、前記樹脂組成物(A)および前記熱可塑性樹脂(B)を共押出または共流延して得られたものである、[8]〜[10]のいずれか一項に記載の有機EL表示装置。
[12]前記延伸を、前記樹脂組成物(A)のガラス転移温度(Tg)に対し、(Tg−15)℃以上(Tg+1)℃以下の温度で行ったものである、[7]〜[11]のいずれか一項に記載の有機EL表示装置。
前記位相差フィルムは、シンジオタクチック構造を有するポリスチレン系重合体とポリアリーレンエーテルとを含む樹脂組成物(A)からなる層を備える。ここで、ポリスチレン系重合体がシンジオタクチック構造を有する、とは、ポリスチレン系重合体の立体化学構造がシンジオタクチック構造となっていることをいう。また、シンジオタクチック構造とは、炭素−炭素結合で形成される主鎖に対して、側鎖であるフェニル基が、フィッシャー投影式において、交互に反対方向に位置する立体構造のことをいう。
式(I)で表される構造単位を含む重合体が単独重合体である場合、当該単独重合体の好ましい例を挙げると、2,6−ジメチル−1,4−フェニレンエーテル単位(「−(C6H2(CH3)2−O)−」で表される繰り返し単位)を有する単独重合体が挙げられる。
また、ポリアリーレンエーテルは、アリーレンエーテル単位以外の繰り返し単位を含んでいてもよい。この場合、ポリアリーレンエーテルは、アリーレンエーテル単位とそれ以外の構造単位とを有する共重合体となる。ただし、ポリアリーレンエーテル中のアリーレンエーテル単位以外の構造単位の比率は、本発明の効果を著しく損なわない程度に少なくすることが好ましく、通常50重量%以下、好ましくは30重量%以下、より好ましくは20重量%以下であり、特に好ましくは0重量%である。
例えば、樹脂組成物(A)は、シンジオタクチック構造を有するポリスチレン系重合体およびポリアリーレンエーテル以外にも重合体を含んでいてもよい。シンジオタクチック構造を有するポリスチレン系重合体およびポリアリーレンエーテル以外の重合体の量は、シンジオタクチック構造を有するポリスチレン系重合体およびポリアリーレンエーテルの合計量を100重量部として、15重量部以下が好ましく、10重量部以下がより好ましく、5重量部以下が更に好ましく、0重量部が特に好ましい。
本発明に用いる位相差フィルムは、Re450<Re550<Re650の関係を満たす。ここで、Re450、Re550、およびRe650はそれぞれ、測定波長450nm、550nm、および650nmにおける位相差フィルムの面内方向のレターデーションを表す。これは通常、位相差フィルムが逆波長分散性を有することを意味する。このように逆波長分散性を有することにより、この位相差フィルムを有機EL表示装置に適用した場合に、観察角度による色調の変化を小さくしたり、広い波長においてレターデーションの補正等の効果を均質に得られるようにしたりできる。
本発明に用いる位相差フィルムは、樹脂組成物(A)からなる層のみを有するフィルムであってもよい。また、本発明に用いる位相差フィルムは、その光学的機能を阻害しない範囲で、任意に樹脂組成物(A)からなる層の他の層を有していてもよい。このように、樹脂組成物(A)からなる層と樹脂組成物(A)からなる層の他の層とを有する積層体としての位相差フィルムを、以下、「複層位相差フィルム」という場合がある。例えば、複層位相差フィルムは、位相差フィルムの強度を高めるための透明樹脂層を有することができる。かかる透明樹脂層を構成する材料としては、位相差フィルムの強度を補える任意の熱可塑性樹脂(B)を用いることができる。熱可塑性樹脂(B)としては、アクリル樹脂、脂環式構造含有重合体を含む樹脂およびポリカーボネート樹脂から選ばれる少なくとも1種であることがより好ましく、アクリル樹脂または脂環式構造含有重合体を含む樹脂が特に好ましい。また、熱可塑性樹脂(B)は、後述する延伸の条件において、光学異方性が発現しない樹脂であることが、樹脂組成物(A)からなる未延伸のフィルムとの共延伸を容易に行える観点から好ましい。
これらのアクリル重合体のうち、ポリメタクリレートが好ましく、中でもポリメチルメタクリレートがより好ましい。
また、アクリル樹脂のガラス転移温度は、樹脂組成物(A)のガラス転移温度をTgAとすると、TgA−10℃以下であることが好ましく、TgA−20℃以下であることがより好ましい。アクリル樹脂のガラス転移温度を前記範囲の上限値以下にすることにより、後述する延伸の温度条件においてP1層の破断を防ぐことができ、Δn、Re550およびRe450/Re550が所望の範囲にある位相差フィルムを容易に得ることができる。
ノルボルネン構造を有する単量体と開環共重合可能な任意の単量体は、1種類を単独で用いてもよく、2種類以上を任意の比率で組み合わせて用いてもよい。
また、脂環式構造含有重合体のガラス転移温度は、樹脂組成物(A)のガラス転移温度をTgAとすると、TgA−10℃以下であることが好ましく、TgA−20℃以下であることがより好ましい。脂環式構造含有重合体のガラス転移温度を前記範囲の上限値以下にすることにより、後述する延伸の温度条件においてP1層の破断を防ぐことができ、Δn、Re550およびRe450/Re550が所望の範囲にある位相差フィルムを容易に得ることができる。
本発明に用いる位相差フィルムは、上記の樹脂組成物(A)からなる層を備える。通常は、樹脂組成物(A)を成形して長尺の延伸前フィルムを製造し、得られた延伸前フィルムに延伸処理を施すことにより、位相差フィルムを得る。ここで、フィルムが「長尺」とは、その幅に対して、少なくとも5倍以上の長さを有するものをいい、好ましくは10倍若しくはそれ以上の長さを有し、具体的にはロール状に巻き取られて保管又は運搬される程度の長さを有するものをいう。このような長尺のフィルムは製造ラインにおいて、長さ方向に連続的に製造工程を行なうことにより得られる。このため、位相差フィルムを製造する場合に、各工程の一部または全部をインラインで簡便且つ効率的に行なうことが可能である。
上記の位相差フィルムは、その少なくとも一方の面に、ハードコート層を有することが好ましい。位相差フィルムはハードコート層を一方の面のみに有していてもよく、両方の面に有していてもよいが、少なくとも偏光フィルムと積層する側の面とは反対側の面にハードコート層を有していることが好ましい。位相差フィルムがハードコート層を有していることにより、円偏光板の反射防止効果や強度をより高めることができる。
本発明に用いる円偏光板は、偏光フィルムと上記の位相差フィルムとを積層してなる。具体的には、位相差フィルムの遅相軸と、偏光フィルムの吸収軸とがなす角が、40°以上50°以下の範囲となるように積層する。
本発明の有機EL表示装置に用いる基板は、透明なものであれば特に限定されず、その厚さは、通常、50μm〜2.0mm程度である。基板に用いられる材料としては、例えば、ガラス材料、樹脂材料、または、これらの複合材料からなるものが挙げられる。前記の複合材料としては、例えば、ガラス板に保護プラスチックフィルムもしくは保護プラスチック層を設けたもの等が用いられる。
透明電極は通常は陽極として用いられ、基板上に形成された信号線、走査線と、駆動素子であるTFT(薄膜トランジスタ)とともに、電極配線パターンを構成するものである。このような透明電極の材質は、通常の有機EL表示装置に使用されるものであれば特に限定されず、例えば金属、合金、これらの混合物等を使用することができる。透明電極の材質の具体例としては、酸化インジウム錫(ITO)、酸化インジウム、酸化インジウム亜鉛(IZO)、酸化亜鉛、酸化第二錫、または金等の薄膜電極材料を挙げることができる。透明電極は正孔が注入し易いように、仕事関数の大きい(4eV以上)透明材料であるITO、IZO、酸化インジウム、金が好ましい。また、透明電極は、シート抵抗が数百Ω/□以下であることが好ましく、材質にもよるが、その厚みは、例えば、0.005μm〜1μm程度とすることが好ましい。
発光素子の発光層は有機EL表示装置に通常使用されるものであれば特に限定されず、低分子型および高分子型のいずれも用いることができる。発光層は、例えば、透明電極層側から正孔注入層、発光層、および電子注入層が積層された構造、発光層単独からなる構造、正孔注入層と発光層とからなる構造、発光層と電子注入層とからなる構造、さらに、正孔注入層と発光層との間に正孔輸送層を介在させた構造、発光層と電子注入層との間に電子輸送層を介在させた構造等とすることができる。また、発光波長を調整したり、発光効率を向上させる等の目的で、上記の各層に適当な材料をドーピングすることもできる。
金属電極層は通常は陰極として用いられる。金属電極層の材料としては、通常の有機EL表示装置に使用されるものであれば特に限定されず、例えば、金、マグネシウム合金(例えば、MgAg等)、アルミニウムまたはその合金(AlLi、AlCa、AlMg等)、銀等を挙げることができる。金属電極層は、電子が注入し易いように仕事関数の小さい(4eV以下)マグネシウム合金、アルミニウム、銀等が好ましい。このような金属電極層はシート抵抗が数百Ω/□以下が好ましく、このため、金属電極層の厚みは、例えば、0.005μm〜0.5μm程度とすることが好ましい。
フィルムの各層及びフィルム全体の膜厚は、フィルムをエポキシ樹脂に包埋したのち、ミクロトーム(大和工業社製「RUB−2100」)を用いてスライスし、走査電子顕微鏡を用いて断面を観察して測定した。
位相差フィルムの表面をプラスチック用研磨布で研磨して各層を単層にした。この単層の状態として、J.A.Woollam社製分光エリプソメーターM−2000Uを用いて、測定波長450nm、550nmおよび650nmで、各層の遅相軸方向の屈折率nx、各層の面内で遅相軸と直交する方向の屈折率ny及び厚さ方向の屈折率nzをそれぞれ測定した。これらの値と各層の厚さd(nm)を用いて、次式より各波長における各層のレターデーションRe、波長550nmにおけるNz係数および波長550nmにおける複屈折Δnを算出した。
Re=|nx−ny|×d
Nz=(nx−nz)/(nx−ny)
Δn=nx−ny
示差走査熱量計(セイコーインストルメンツ社製EXSTAR6220)を用いて昇温速度20℃/分で測定した。
長尺の位相差フィルムと長尺の偏光子とを連続的に貼り合せる際の、破断の発生の有無を以下の基準で評価した。
A:繰出しから貼り合わせの途中で破断が発生せずに全長で貼り合せ可能であった。
B:繰出しから貼り合わせの途中で破断が数回発生した。
反射板および円偏光板を円偏光板の位相差フィルム側が反射板と接するように積層したモデルで、4x4マトリクスを用いた光学シミュレーションを行うことによりコントラスト及び色味を計算し、コントラスト図及び色味図(色ずれを表す図)として表示した。コントラスト図において、色が濃いほど高コントラストであることを表す。色味図において、色が薄いほど色ずれが大きいことを表す。
A:外の景色の映り込みや色味変化が見られない。
B:外の景色の映り込みや色味変化が僅かに見られる。
C:外の景色の映り込みや色味変化が少し見られる。
D:外の景色の映り込みや色味変化が大きく見られる。
(延伸前フィルムの製造)
シンジオタクチックポリスチレン(出光興産社製「ザレック130ZC」、Mw180,000)58部とポリ(2,6−ジメチル−1,4−フェニレンオキサイド)(アルドリッチ社カタログNo.18242−7)42部と酸化防止剤1部とを2軸押出機で混錬し、透明な樹脂組成物(A)のペレットを作製した。この樹脂組成物(A)のガラス転移温度は134℃であった。
また、前記の樹脂組成物(A)のペレットを、フィルム成型装置の他方の一軸押出機に投入して、溶融させた。
また、溶融された樹脂組成物(A)を、目開き10μmのリーフディスク形状のポリマーフィルターを通して、フィルム成型装置の他方のマニホールドに供給した。
次いで、この延伸前フィルム積層体をテンター延伸機で、遅相軸がMD方向に対して45°傾いた方向になるように斜め延伸した。延伸時の温度は、樹脂組成物(A)のガラス転移温度より3℃低い温度である131℃、延伸倍率は3.2倍とした。これにより、熱可塑性樹脂(B)からなるp2層/樹脂組成物(A)からなるp1層/熱可塑性樹脂(B)からなるp2層の3層構成の位相差フィルム積層体を得た。各層の厚さ比は、p2層:p1層:p2層=2:1:2であった。次いで、この位相差フィルム積層体から両面のp2層を剥離して、p1層のみからなる厚さが49μmで長尺の位相差フィルムAを得た。得られた位相差フィルムAは巻き取ってフィルムロールとした。位相差フィルムAの配向を確認したところ、遅相軸はMD方向に対して45°傾いていた。この位相差フィルムAは、Re550が140nmであり、かつRe450<Re550<Re650の関係を満たし、Re450/Re550は0.87であった。また、Δnは0.0028であり、Nz係数は−0.12であった。
厚さ80μmの長尺のポリビニルアルコールフイルムを0.3%のヨウ素水溶液中で染色した。その後、4%のホウ酸水溶液及び2%のヨウ化カリウム水溶液中で5倍まで延伸した後、50℃で4分間乾燥させて長尺の偏光子を製造した。
この長尺の偏光子の片面に、上記の位相差フィルムAを、ロールから連続的に繰り出しながら、接着剤を用いてロールラミネーターで貼り合わせた。繰出しから貼り合わせの途中で破断は発生せず、全長で貼り合せ可能であった。これを矩形に切り出して円偏光板Aを製造した。
シンジオタクチックポリスチレンの量を57部、ポリ(2,6−ジメチル−1,4−フェニレンオキサイド)の量を43部とした他は実施例1と同様にして、透明な樹脂組成物(A)のペレットを作製した。この樹脂組成物(A)のガラス転移温度は136℃であった。樹脂組成物(A)としてこれを用いる他は実施例1と同様にして、P2層と、P1層と、P2層とをこの順に備えた3層構造の延伸前フィルム積層体を得た(共押出工程)。各層の厚さ比は、P2層:P1層:P2層=3:1:3であった。
シンジオタクチックポリスチレンの量を64部、ポリ(2,6−ジメチル−1,4−フェニレンオキサイド)の量を36部とした他は実施例1と同様にして、透明な樹脂組成物(A)のペレットを作製した。この樹脂組成物(A)のガラス転移温度は127℃であった。樹脂組成物(A)としてこれを使用し、熱可塑性樹脂(B)として脂環構造含有重合体を含む樹脂(日本ゼオン社製「ゼオノア1060」、ガラス転移温度100℃)のペレットを用いる他は実施例1と同様にして、P2層と、P1層と、P2層とをこの順に備えた3層構造の延伸前フィルム積層体を得た(共押出工程)。各層の厚さ比は、P2層:P1層:P2層=1:1:1であった。
これとは別に、位相差フィルムCを矩形に切り出した。一方、実施例1と同様にして長尺の偏光子を製造し、矩形に切り出した。この偏光子の片面に、上記の位相差フィルムCを、位相差フィルムCの遅相軸と偏光子の延伸方向が45°の角度をなすように、接着剤を用いてロールラミネーターで貼り合わせて円偏光板Cを製造した。この円偏光板Cを用いてコントラスト及び色味の計算並びに有機EL表示装置の視野角特性を評価した。結果を図5、図6および表1に示す。
シンジオタクチックポリスチレン58部に代えて、非晶性ポリスチレン(PSジャパン社製「HH102」ガラス転移温度101℃)57部を用い、ポリ(2,6−ジメチル−1,4−フェニレンオキサイド)の量を43部とした他は実施例1と同様にして透明な樹脂組成物(A’)のペレットを作製した。この樹脂組成物(A’)のガラス転移温度は141℃であった。前記樹脂組成物(A)のペレットに代えて、この樹脂組成物(A’)のペレットを用いる他は実施例1と同様にして、熱可塑性樹脂(B)からなるP2層と、樹脂組成物(A’)からなるP1’層と、熱可塑性樹脂(B)からなるP2層とをこの順に備えた3層構造の延伸前フィルム積層体を得た(共押出工程)。各層の厚さ比は、P2層:P1’層:P2層=2:1:2であった。
これとは別に、位相差フィルムDを矩形に切り出した。一方、実施例1と同様にして長尺の偏光子を製造し、矩形に切り出した。この偏光子の片面に、上記の位相差フィルムDを、接着剤を用いてロールラミネーターで貼り合わせて円偏光板Dを製造した。この円偏光板Dを用いてコントラスト及び色味の計算並びに有機EL表示装置の視野角特性を評価した。結果を図7、図8および表1に示す。
シンジオタクチックポリスチレンの量を63部、ポリ(2,6−ジメチル−1,4−フェニレンオキサイド)の量を37部とした他は実施例1と同様にして、透明な樹脂組成物(A)のペレットを作製した。この樹脂組成物(A)のガラス転移温度は129℃であった。この樹脂組成物(A)のペレットを単軸押出機で溶融させ、押出用のダイに供給し、押出成形することにより延伸前フィルムを得た。得られた延伸前フィルムをテンター延伸機で、MD方向およびTD方向に同時二軸延伸した。延伸時の温度は、樹脂組成物(A)のガラス転移温度より3℃高い温度である132℃、延伸倍率はMD方向が1.3倍、TD方向が1.2倍とした。これにより、厚さ62μmの長尺の位相差フィルムEを得た。得られた位相差フィルムEは巻き取ってフィルムロールとした。位相差フィルムEの配向を確認したところ、遅相軸はMD方向に対して垂直であった。この位相差フィルムEは、Re550が142nmであり、かつRe450<Re550<Re650の関係を満たし、Re450/Re550は0.95であった。また、Δnは0.0023であり、Nz係数は−1.00であった。
これとは別に、位相差フィルムEを矩形に切り出した。一方、実施例1と同様にして長尺の偏光子を製造し、矩形に切り出した。この偏光子の片面に、上記の位相差フィルムEを、位相差フィルムEの遅相軸と偏光子の延伸方向が45°の角度をなすように、接着剤を用いてロールラミネーターで貼り合わせて円偏光板Eを製造した。この円偏光板Eを用いてコントラスト及び色味の計算並びに有機EL表示装置の視野角特性を評価した。結果を図9、図10および表1に示す。
シンジオタクチックポリスチレンの量を76部、ポリ(2,6−ジメチル−1,4−フェニレンオキサイド)の量を24部とした他は実施例1と同様にして、透明な樹脂組成物(A)のペレットを作製した。この樹脂組成物(A)のガラス転移温度は115℃であった。この樹脂組成物(A)のペレットを単軸押出機で溶融させ、押出用のダイに供給し、押出成形することにより、厚さ100μmの延伸前フィルムを得た。
セルロースエステルのフィルム(カネカ社製、商品名「KA」)を斜め延伸し、厚さ100μmの長尺の位相差フィルムFを得た。得られた位相差フィルムFは巻き取ってフィルムロールとした。位相差フィルムFの配向を確認すると、遅相軸はMD方向に対して45°傾いていた。この位相差フィルムFは、Re550が140nmであり、かつRe450<Re550<Re650の関係を満たしていた。また、Nz係数は+1.13であった。
Claims (22)
- 光出射側から順に、基板、透明電極、発光層及び金属電極層を具備してなる有機EL表示装置であって、
前記基板の光出射側に偏光フィルムと位相差フィルムとを積層してなる円偏光板を備え、
前記位相差フィルムが、
シンジオタクチック構造を有するポリスチレン系重合体およびポリアリーレンエーテルを含む樹脂組成物(A)からなる層を備え、
前記樹脂組成物(A)におけるシンジオタクチック構造を有するポリスチレン系重合体とポリアリーレンエーテルとの割合が、シンジオタクチック構造を有するポリスチレン系重合体:ポリアリーレンエーテルの重量比で、65:35〜55:45であり、
Re450<Re550<Re650の関係を満たし、かつ
波長550nmにおけるNz係数が−0.25〜−0.05である、有機EL表示装置。
(ただし、Re450、Re550、およびRe650はそれぞれ、測定波長450nm、550nm、および650nmにおける位相差フィルムの面内方向のレターデーションを表し、
Nz係数は(nx−nz)/(nx−ny)を表し、
nxは位相差フィルムの面内の遅相軸方向の屈折率を表し、
nyは位相差フィルムの面内の進相軸方向の屈折率を表し、
nzは位相差フィルムの厚み方向の屈折率を表す。) - 前記位相差フィルムのRe450/Re550が0.80以上0.90以下である、請求項1記載の有機EL表示装置。
- 前記位相差フィルムの波長550nmにおける複屈折Δn(ただし、Δn=nx−nyである)が、0.0020以上0.0050以下である、請求項1又は2記載の有機EL表示装置。
- 前記位相差フィルムの厚さが80μm以下である、請求項1〜3のいずれか一項に記載の有機EL表示装置。
- 前記ポリアリーレンエーテルがフェニレンエーテル単位を含む重合体を含有する、請求項1〜4のいずれか一項に記載の有機EL表示装置。
- 前記位相差フィルムの測定波長550nmにおける面内方向のレターデーションRe550が110nm〜150nmである、請求項1〜5のいずれか一項に記載の有機EL表示装置。
- 前記樹脂組成物(A)中の、前記シンジオタクチック構造を有するポリスチレン系重合体およびポリアリーレンエーテル以外の重合体の量が、0重量部である、請求項1〜6のいずれか一項に記載の有機EL表示装置。
- 前記樹脂組成物(A)におけるシンジオタクチック構造を有するポリスチレン系重合体とポリアリーレンエーテルとの割合が、シンジオタクチック構造を有するポリスチレン系重合体:ポリアリーレンエーテルの重量比で、58:42〜55:45である、請求項1〜7のいずれか一項に記載の有機EL表示装置。
- 前記位相差フィルムが、前記樹脂組成物(A)からなる長尺の延伸前フィルムを、その長尺方向に対して40°以上50°以下の範囲に延伸してなるものである、請求項1〜8のいずれか一項に記載の有機EL表示装置。
- 前記位相差フィルムが、前記樹脂組成物(A)からなるP1層と、前記P1層に接して設けられた熱可塑性樹脂(B)からなるP2層とを有する長尺の延伸前フィルム積層体を、その長尺方向に対して40°以上50°以下の範囲に延伸してなるものである、請求項1〜8のいずれか一項に記載の有機EL表示装置。
- 前記熱可塑性樹脂(B)が、アクリル樹脂、脂環式構造含有重合体を含む樹脂およびポリカーボネート樹脂から選ばれる少なくとも1種である、請求項10に記載の有機EL表示装置。
- 前記長尺の延伸前フィルム積層体が、前記樹脂組成物(A)および前記熱可塑性樹脂(B)を共押出または共流延して得られたものである、請求項10又は11に記載の有機EL表示装置。
- 前記熱可塑性樹脂(B)が、アクリル樹脂又は脂環式構造含有重合体を含む樹脂であり、
前記熱可塑性樹脂(B)のガラス転移温度が、前記樹脂組成物(A)のガラス転移温度TgA−10℃以下である、請求項10〜12のいずれか一項に記載の有機EL表示装置。 - 請求項1〜8のいずれか一項に記載の有機EL表示装置の製造方法であって、
前記樹脂組成物(A)からなるP1層と、前記P1層に接して設けられた熱可塑性樹脂(B)からなるP2層とを有する長尺の延伸前フィルム積層体を、その長尺方向に対して40°以上50°以下の範囲に延伸して、P1層が延伸されてなるp1層と、P2層が延伸されてなるp2層とを有する位相差フィルム積層体を得た後、p2層を剥離して前記位相差フィルムを得ることを含む、有機EL表示装置の製造方法。 - 前記熱可塑性樹脂(B)が、アクリル樹脂、脂環式構造含有重合体を含む樹脂およびポリカーボネート樹脂から選ばれる少なくとも1種である、請求項14に記載の有機EL表示装置の製造方法。
- 前記長尺の延伸前フィルム積層体が、前記樹脂組成物(A)および前記熱可塑性樹脂(B)を共押出または共流延して得られたものである、請求項14又は15に記載の有機EL表示装置の製造方法。
- 前記延伸を、前記樹脂組成物(A)のガラス転移温度(Tg)に対し、(Tg−15)℃以上(Tg+1)℃以下の温度で行ったものである、請求項14〜16のいずれか一項に記載の有機EL表示装置の製造方法。
- 請求項1〜8のいずれか一項に記載の有機EL表示装置の製造方法であって、
前記樹脂組成物(A)からなる長尺の延伸前フィルムを、その長尺方向に対して40°以上50°以下の範囲に延伸して前記位相差フィルムを得ることを含み、
前記延伸を、前記樹脂組成物(A)のガラス転移温度(Tg)に対し、(Tg−15)℃以上(Tg+1)℃以下の温度で行う、有機EL表示装置の製造方法。 - 請求項1〜8のいずれか一項に記載の有機EL表示装置の製造方法であって、
前記樹脂組成物(A)からなるP1層と、前記P1層に接して設けられた熱可塑性樹脂(B)からなるP2層とを有する長尺の延伸前フィルム積層体を、その長尺方向に対して40°以上50°以下の範囲に延伸して前記位相差フィルムを得ることを含み、
前記延伸を、前記樹脂組成物(A)のガラス転移温度(Tg)に対し、(Tg−15)℃以上(Tg+1)℃以下の温度で行う、有機EL表示装置の製造方法。 - シンジオタクチック構造を有するポリスチレン系重合体およびポリアリーレンエーテルを含む樹脂組成物(A)からなる層と、前記樹脂組成物(A)からなる層と接し、熱可塑性樹脂(B)からなる層とを備え、
前記樹脂組成物(A)におけるシンジオタクチック構造を有するポリスチレン系重合体とポリアリーレンエーテルとの割合が、シンジオタクチック構造を有するポリスチレン系重合体:ポリアリーレンエーテルの重量比で、65:35〜55:45であり、
Re450<Re550<Re650の関係を満たし、かつ
波長550nmにおけるNz係数が−0.25〜−0.05である、位相差フィルム。
(ただし、Re450、Re550、およびRe650はそれぞれ、測定波長450nm、550nm、および650nmにおける位相差フィルムの面内方向のレターデーションを表し、
Nz係数は(nx−nz)/(nx−ny)を表し、
nxは位相差フィルムの面内の遅相軸方向の屈折率を表し、
nyは位相差フィルムの面内の進相軸方向の屈折率を表し、
nzは位相差フィルムの厚み方向の屈折率を表す。) - 偏光フィルムと、位相差フィルムとを含む円偏光板であって、
前記位相差フィルムの遅相軸と、前記偏光フィルムの吸収軸とがなす角が、40°以上50°以下であり、
前記位相差フィルムが、
シンジオタクチック構造を有するポリスチレン系重合体およびポリアリーレンエーテルを含む樹脂組成物(A)からなる層と、前記樹脂組成物(A)からなる層と接し、熱可塑性樹脂(B)からなる層とを備え、
前記樹脂組成物(A)におけるシンジオタクチック構造を有するポリスチレン系重合体とポリアリーレンエーテルとの割合が、シンジオタクチック構造を有するポリスチレン系重合体:ポリアリーレンエーテルの重量比で、65:35〜55:45であり、
Re450<Re550<Re650の関係を満たし、かつ
波長550nmにおけるNz係数が−0.25〜−0.05である、円偏光板。
(ただし、Re450、Re550、およびRe650はそれぞれ、測定波長450nm、550nm、および650nmにおける位相差フィルムの面内方向のレターデーションを表し、
Nz係数は(nx−nz)/(nx−ny)を表し、
nxは位相差フィルムの面内の遅相軸方向の屈折率を表し、
nyは位相差フィルムの面内の進相軸方向の屈折率を表し、
nzは位相差フィルムの厚み方向の屈折率を表す。) - 前記熱可塑性樹脂(B)が、アクリル樹脂である、請求項21に記載の円偏光板。