JP6250939B2 - マーキングフィルム及びオーバーラミネートフィルム - Google Patents
マーキングフィルム及びオーバーラミネートフィルム Download PDFInfo
- Publication number
- JP6250939B2 JP6250939B2 JP2013048321A JP2013048321A JP6250939B2 JP 6250939 B2 JP6250939 B2 JP 6250939B2 JP 2013048321 A JP2013048321 A JP 2013048321A JP 2013048321 A JP2013048321 A JP 2013048321A JP 6250939 B2 JP6250939 B2 JP 6250939B2
- Authority
- JP
- Japan
- Prior art keywords
- meth
- film
- acrylic
- polymer
- acrylic polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
前記(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーのポリマーブレンドを含み、
前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記ポリマーブレンドが、80万以上の重量平均分子量を有するカルボキシル基含有(メタ)アクリル系ポリマー、80万以上の重量平均分子量を有するアミノ基含有(メタ)アクリル系ポリマー、又はそれらの組み合わせを含む、マーキングフィルムが提供される。
前記レセプターフィルムが、第1面及び前記第1面に対向する第2面を有する第1の(メタ)アクリル系フィルムと、前記第1の(メタ)アクリル系フィルムの第1面に受容された着色剤と、前記第1の(メタ)アクリル系フィルムの第2面に配置された接着層と
を備え、
前記オーバーラミネートフィルムが、第1面及び前記第1面に対向する第2面を有する第2の(メタ)アクリル系フィルムと、前記第2の(メタ)アクリル系フィルムの第1面に配置された表面保護クリア層と、前記第2の(メタ)アクリル系フィルムの第2面に配置された接着層とを備え、
前記オーバーラミネートフィルムが前記オーバーラミネートフィルムの接着層によって前記第1の(メタ)アクリル系フィルムの第1面に接着されており、
前記第1及び第2の(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーの第1及び第2のポリマーブレンドをそれぞれ含み、
前記第1のポリマーブレンドに含まれる前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記第2のポリマーブレンドに含まれる前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記第1及び第2のポリマーブレンドの少なくとも一方が、80万以上の重量平均分子量を有するカルボキシル基含有(メタ)アクリル系ポリマー、80万以上の重量平均分子量を有するアミノ基含有(メタ)アクリル系ポリマー、又はそれらの組み合わせを含む、マーキングフィルムが提供される。
前記(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーのポリマーブレンドを含み、
前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記ポリマーブレンドが、80万以上の重量平均分子量を有するカルボキシル基含有(メタ)アクリル系ポリマー、80万以上の重量平均分子量を有するアミノ基含有(メタ)アクリル系ポリマー、又はそれらの組み合わせを含む、オーバーラミネートフィルムが提供される。
る。
1/Tg=X1/(Tg1+273.15)+X2/(Tg2+273.15)+・・・+Xn/(Tgn+273.15)
(Tg1:成分1のホモポリマーのガラス転移温度
Tg2:成分2のホモポリマーのガラス転移温度
・・・
Tgn:成分nのホモポリマーのガラス転移温度
X1:重合の際に添加した成分1のモノマーの質量分率
X2:重合の際に添加した成分2のモノマーの質量分率
・・・
Xn:重合の際に添加した成分nのモノマーの質量分率
X1+X2+・・・+Xn=1)
伸び率(%)={(L1−100)/100}×100
MMA60質量部、BMA34質量部、及びDMAEMA6質量部をEtOAc150質量部に溶解させ、重合開始剤としてジメチル−2,2−アゾビス(2−メチルプロピオネート)(商品名V−601、和光純薬工業株式会社製)0.6質量部を加えた後、窒素雰囲気下65℃で24時間反応させ、アミノ基を含有する高Tg(メタ)アクリル系ポリマー1(HAP1)のEtOAc溶液(固形分40%)を調製した。HAP1の重量平均分子量(Mw)は68,000、ガラス転移温度(Tg)は63℃であった。Tgは、各ポリマーがn種類のモノマーから共重合されているとして、FOXの式(下式)より求めた。
1/Tg=X1/(Tg1+273.15)+X2/(Tg2+273.15)+・・・+Xn/(Tgn+273.15)
(Tg1:成分1のホモポリマーのガラス転移温度
Tg2:成分2のホモポリマーのガラス転移温度
・・・
Tgn:成分nのホモポリマーのガラス転移温度
X1:重合の際に添加した成分1のモノマーの質量分率
X2:重合の際に添加した成分2のモノマーの質量分率
・・・
Xn:重合の際に添加した成分nのモノマーの質量分率
X1+X2+・・・+Xn=1)
BA87質量部、AN10質量部及びMAA3質量部を、EtOAc400質量部に溶解させ、重合開始剤として2,2’−アゾビス(2,4−ジメチルバレロニトリル)(商品名V−65、和光純薬工業株式会社製)0.1質量部を加えた後、窒素雰囲気下50℃で24時間反応させ、カルボキシル基を含有する低Tg(メタ)アクリル系ポリマー1(LAP1)のEtOAc溶液(固形分20%)を調製した。LAP1の重量平均分子量(Mw)は2,300,000、ガラス転移温度(Tg)は−41℃であった。
BA94質量部、及びAA6質量部を、トルエン100質量部及びEtOAc100質量部の混合溶液に溶解させ、重合開始剤として2,2’−アゾビス(2,4−ジメチルバレロニトリル)(商品名V−65、和光純薬工業株式会社製)0.2質量部を加えた後、窒素雰囲気下50℃で24時間反応させ、カルボキシル基を含有する低Tg(メタ)アクリル系ポリマー2(LAP2)のトルエン/EtOAc混合溶液(固形分33%)を調製した。LAP2の重量平均分子量(Mw)は760,000、ガラス転移温度(Tg)は−48℃であった。
BA94質量部、及びAA6質量部を、EtOAc620質量部に溶解させ、重合開始剤として2,2’−アゾビス(2,4−ジメチルバレロニトリル)(商品名V−65、和光純薬工業株式会社製)0.1質量部を加えた後、窒素雰囲気下50℃で24時間反応させ、カルボキシル基を含有する低Tg(メタ)アクリル系ポリマー3(LAP3)のEtOAc溶液(固形分14%)を調製した。LAP3の重量平均分子量(Mw)は2,100,000、ガラス転移温度(Tg)は−48℃であった。
EA65質量部、BA25質量部、AN8質量部、HEMA1質量部、及びAA1質量部を、トルエン366質量部及びMEK366質量部の混合溶液に溶解させ、重合開始剤として2,2’−アゾビス(2,4−ジメチルバレロニトリル)(商品名V−65、和光純薬工業株式会社製)0.1質量部を加えた後、窒素雰囲気下50℃で24時間反応させ、カルボキシル基を含有する低Tg(メタ)アクリル系ポリマー4(LAP4)のトルエン/MEK混合溶液(固形分12%)を調製した。LAP4の重量平均分子量(Mw)は1,100,000、ガラス転移温度(Tg)は−23℃であった。
BA58質量部、2EHA36質量部、AN2部、及びAA4質量部を、EtOAc200質量部に溶解させ、重合開始剤として2,2’−アゾビス(2,4−ジメチルバレロニトリル)(商品名V−65、和光純薬工業株式会社製)0.2質量部を加えた後、窒素雰囲気下50℃で24時間反応させ、粘着性ポリマー1(ADH1)のEtOAc溶液(固形分33%)を調製した。ADH1の重量平均分子量(Mw)は500,000、ガラス転移温度(Tg)は−53℃であった。
マーキングフィルムの特性を以下の方法にしたがって評価した。
JIS K 6251に準拠して引張強さ及び伸び率を測定する。マーキングフィルムを長さ150mm×幅25mmに切断して試料とする。引張試験機(株式会社エー・アンド・デイ製テンシロン万能試験機、型番:RTC−1210A)を用い、20℃、初期つかみ間隔100mm、引張速度300mm/分の条件で降伏点(N/25mm)、破断点(N/25mm)及び伸び率(%)を測定する。伸び率は測定した試料が切断したときの標線間距離L1(mm)を測定し、初期つかみ間隔100mmを用いて以下の式から求める。
伸び率(%)={(L1−100)/100}×100
試料をJIS K7128−3に準拠して用意する。引張試験機を用い、20℃、引張速度200mm/分の条件で引裂強さを測定する。5回試験を行った平均値を引裂強さ(N/mm)とする。
マーキングフィルムの接着性を高める目的で、プライマー溶液DP900N2(住友スリーエム株式会社製)をカルシウムシリケート板(厚さ6mm)にコーティングし、その上にマーキングフィルムを貼り付ける。ISO5660−1コーンカロリーメーター試験に準拠して試験を行う。パラメータとして発熱速度(kW/m2)及び総発熱量(MJ/m2)をコーンカロリーメーター(株式会社東洋精機製作所製)を用いて測定する。加熱開始後20分間の総発熱量が8MJ/m2以下でありかつ200kW/m2を超える発熱速度を示した時間が合計で10秒以下である場合を合格、それ以外の場合を不合格と判定する。
マーキングフィルムを長さ150mm×幅150mmに切断して試料とする。スキージを用いて試料をスタッコ塗装板(エスケー化研株式会社製)の上に23℃で貼り付ける。試料が貼り付けられたスタッコ塗装板を熱サイクル条件(80℃〜−30℃)にて7日間エージングする。その後、試料を手で素早く引っ張って剥がす。フィルムが破断せずに試料を除去できた場合を良好、フィルムが破断した場合を不良とする。
マーキングフィルムを長さ150mm×幅70mmに切断して試料とする。試料をプレマスク(LD−K1010、日立化成株式会社製)と一緒にスタッコ塗装板(最大表面粗さ約1.5mm(頂部−底部間)、株式会社テストマテリアルズ製)に貼り付けて、プレマスクを取り除く。試料をスタッコ塗装板に対してリベットブラシ(スリーエム社製)を用いて往復3回押しつける。その後、凹凸面に対する追従性を目視で確認する。フィルムが凹凸面に十分追従していれば良好、外観上浮き上がっている部分があれば不良とする。
<レセプターフィルムの作製>
HAP1、LAP2及びCL1を、ミキサー(T.K.オートホモミキサー、特殊機化工業株式会社製)を用いて混合して、透明な(メタ)アクリル系フィルムの前駆体組成物を調製した。HAP1、LAP2及びCL1の比率は不揮発分基準で100:90:0.9であった。この前駆体組成物を、ナイフコータを用いて50μm厚の剥離処理ポリエステルフィルムに塗布し、95℃で5分間、155℃で2分間乾燥して、40μm厚の(メタ)アクリル系フィルムを作製した。
フッ素/アクリル系クリア樹脂溶液(住友スリーエム株式会社製)を、グラビアコータを用いて50μm厚の剥離ポリエステルフィルムに塗布し、155℃で2分間乾燥して、5μm厚の表面保護クリア層を作製した。次に、HAP1、LAP1及びCL1を、ミキサー(T.K.オートホモミキサー、特殊機化工業株式会社製)を用いて混合して、透明な(メタ)アクリル系フィルムの前駆体組成物を調製した。HAP1、LAP1及びCL1の比率は不揮発分基準で100:110:0.22であった。この前駆体組成物を、ナイフコータを用いて表面保護クリア層の表面に塗布し、95℃で5分間、155℃で2分間乾燥して、15μm厚の(メタ)アクリル系フィルムの層を表面保護クリア層の上に積層した。
インクジェットインクを、溶剤型インクジェットプリンター(XC540、ローランド株式会社製)を用いてレセプターフィルムの上に印刷した。インクとしてECO−SOL MAXインク(ローランド株式会社製)を用いた。印刷条件はシアン66%、マゼンタ66%、イエロー66%、及びブラック100%であった。次に、オーバーラミネートフィルムのシリコーン被覆剥離紙を取り除いて、レセプターフィルムの印刷面にオーバーラミネートフィルムを積層して、例1のマーキングフィルムを作製した。
レセプターフィルム及びオーバーラミネートフィルムに使用した低Tg(メタ)アクリル系ポリマー及びHAP1に対する配合比を表3に示したとおりとした以外は、例1と同様にしてマーキングフィルムを作製した。
レセプターフィルム及びオーバーラミネートフィルムに使用した低Tg(メタ)アクリル系ポリマー及びHAP1に対する配合比を表3に示したとおりとし、レセプターフィルムの(メタ)アクリル系フィルムの層の厚さを50μm、接着層の厚さを30μm、オーバーラミネートフィルムの(メタ)アクリル系フィルムの層の厚さを50μm、接着層の厚さを30μmとした以外は、例1と同様にしてマーキングフィルムを作製した。得られたマーキングフィルムの総厚は185μmであった。
[1]
着色剤を受容可能な第1面及び前記第1面に対向する第2面を有する(メタ)アクリル系フィルムと、前記(メタ)アクリル系フィルムの第2面に配置された接着層とを備えるレセプターフィルムを含むマーキングフィルムであって、
前記(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーのポリマーブレンドを含み、
前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記ポリマーブレンドが、80万以上の重量平均分子量を有するカルボキシル基含有(メタ)アクリル系ポリマー、80万以上の重量平均分子量を有するアミノ基含有(メタ)アクリル系ポリマー、又はそれらの組み合わせを含む、マーキングフィルム。
[2]
前記(メタ)アクリル系フィルムの第1面に着色剤が受容されている、請求項1に記載のマーキングフィルム。
[3]
レセプターフィルム及びオーバーラミネートフィルムを含むマーキングフィルムであって、
前記レセプターフィルムが、第1面及び前記第1面に対向する第2面を有する第1の(メタ)アクリル系フィルムと、前記第1の(メタ)アクリル系フィルムの第1面に受容された着色剤と、前記第1の(メタ)アクリル系フィルムの第2面に配置された接着層と
を備え、
前記オーバーラミネートフィルムが、第1面及び前記第1面に対向する第2面を有する第2の(メタ)アクリル系フィルムと、前記第2の(メタ)アクリル系フィルムの第1面に配置された表面保護クリア層と、前記第2の(メタ)アクリル系フィルムの第2面に配置された接着層とを備え、
前記オーバーラミネートフィルムが前記オーバーラミネートフィルムの接着層によって前記第1の(メタ)アクリル系フィルムの第1面に接着されており、
前記第1及び第2の(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーの第1及び第2のポリマーブレンドをそれぞれ含み、
前記第1のポリマーブレンドに含まれる前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記第2のポリマーブレンドに含まれる前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記第1及び第2のポリマーブレンドの少なくとも一方が、80万以上の重量平均分子量を有するカルボキシル基含有(メタ)アクリル系ポリマー、80万以上の重量平均分子量を有するアミノ基含有(メタ)アクリル系ポリマー、又はそれらの組み合わせを含む、マーキングフィルム。
[4]
前記第2のポリマーブレンドが、80万以上の重量平均分子量を有するカルボキシル基含有(メタ)アクリル系ポリマー、80万以上の重量平均分子量を有するアミノ基含有(メタ)アクリル系ポリマー、又はそれらの組み合わせを含む、請求項3に記載のマーキングフィルム。
[5]
前記マーキングフィルムの総厚が100μm以下である、請求項1〜4のいずれか一項に記載のマーキングフィルム。
[6]
前記(メタ)アクリル系フィルムが難燃剤を含まない、請求項1〜5のいずれか一項に記載のマーキングフィルム。
[7]
ISO5660−1コーンカロリーメーター試験で不燃性である、請求項1〜6のいずれか一項に記載のマーキングフィルム。
[8]
JIS K 7128−3に準拠して測定したときの20℃での引裂強さが35N/mm以上である、請求項1〜7のいずれか一項に記載のマーキングフィルム。
[9]
JIS K 6251に準拠して測定したときの20℃での伸び率が50%以上である、請求項1〜8のいずれか一項に記載のマーキングフィルム。
[10]
第1面及び前記第1面に対向する第2面を有する(メタ)アクリル系フィルムと、前記(メタ)アクリル系フィルムの第1面に配置された表面保護クリア層と、前記(メタ)アクリル系フィルムの第2面に配置された接着層とを備えるオーバーラミネートフィルムであって、
前記(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーのポリマーブレンドを含み、
前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記ポリマーブレンドが、80万以上の重量平均分子量を有するカルボキシル基含有(メタ)アクリル系ポリマー、80万以上の重量平均分子量を有するアミノ基含有(メタ)アクリル系ポリマー、又はそれらの組み合わせを含む、オーバーラミネートフィルム。
[11]
前記(メタ)アクリル系フィルムが難燃剤を含まない、請求項10に記載のオーバーラミネートフィルム。
10 レセプターフィルム
20 オーバーラミネートフィルム
12、22 (メタ)アクリル系フィルム
14、24 接着層
16 着色剤
26 表面保護クリア層
Claims (11)
- 着色剤を受容可能な第1面及び前記第1面に対向する第2面を有する(メタ)アクリル系フィルムと、前記(メタ)アクリル系フィルムの第2面に配置された接着層とを備えるレセプターフィルムを含むマーキングフィルムであって、
前記(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーのポリマーブレンドを含み、
前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記カルボキシル基含有(メタ)アクリル系ポリマーが、110万以上の重量平均分子量を有する、マーキングフィルム。 - 前記(メタ)アクリル系フィルムの第1面に着色剤が受容されている、請求項1に記載のマーキングフィルム。
- レセプターフィルム及びオーバーラミネートフィルムを含むマーキングフィルムであって、
前記レセプターフィルムが、第1面及び前記第1面に対向する第2面を有する第1の(メタ)アクリル系フィルムと、前記第1の(メタ)アクリル系フィルムの第1面に受容された着色剤と、前記第1の(メタ)アクリル系フィルムの第2面に配置された接着層と
を備え、
前記オーバーラミネートフィルムが、第1面及び前記第1面に対向する第2面を有する第2の(メタ)アクリル系フィルムと、前記第2の(メタ)アクリル系フィルムの第1面に配置された表面保護クリア層と、前記第2の(メタ)アクリル系フィルムの第2面に配置された接着層とを備え、
前記オーバーラミネートフィルムが前記オーバーラミネートフィルムの接着層によって前記第1の(メタ)アクリル系フィルムの第1面に接着されており、
前記第1及び第2の(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーの第1及び第2のポリマーブレンドをそれぞれ含み、
前記第1のポリマーブレンドに含まれる前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記第2のポリマーブレンドに含まれる前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記第1及び第2のポリマーブレンドの少なくとも一方の前記カルボキシル基含有(メタ)アクリル系ポリマーが、110万以上の重量平均分子量を有する、マーキングフィルム。 - 前記第2のポリマーブレンドが、80万以上の重量平均分子量を有するカルボキシル基含有(メタ)アクリル系ポリマー、80万以上の重量平均分子量を有するアミノ基含有(メタ)アクリル系ポリマー、又はそれらの組み合わせを含む、請求項3に記載のマーキングフィルム。
- 前記マーキングフィルムの総厚が100μm以下である、請求項1〜4のいずれか一項に記載のマーキングフィルム。
- 前記(メタ)アクリル系フィルムが難燃剤を含まない、請求項1〜5のいずれか一項に記載のマーキングフィルム。
- ISO5660−1コーンカロリーメーター試験で不燃性である、請求項1〜6のいずれか一項に記載のマーキングフィルム。
- JIS K 7128−3に準拠して測定したときの20℃での引裂強さが35N/mm以上である、請求項1〜7のいずれか一項に記載のマーキングフィルム。
- JIS K 6251に準拠して測定したときの20℃での伸び率が50%以上である、請求項1〜8のいずれか一項に記載のマーキングフィルム。
- 第1面及び前記第1面に対向する第2面を有する(メタ)アクリル系フィルムと、前記(メタ)アクリル系フィルムの第1面に配置された表面保護クリア層と、前記(メタ)アクリル系フィルムの第2面に配置された接着層とを備えるオーバーラミネートフィルムであって、
前記(メタ)アクリル系フィルムが、カルボキシル基含有(メタ)アクリル系ポリマー及びアミノ基含有(メタ)アクリル系ポリマーのポリマーブレンドを含み、
前記カルボキシル基含有(メタ)アクリル系ポリマー及び前記アミノ基含有(メタ)アクリル系ポリマーの一方のガラス転移温度(Tg)が0℃以上でありかつ他方のガラス転移温度(Tg)が0℃以下であり、
前記カルボキシル基含有(メタ)アクリル系ポリマーが、110万以上の重量平均分子量を有する、オーバーラミネートフィルム。 - 前記(メタ)アクリル系フィルムが難燃剤を含まない、請求項10に記載のオーバーラミネートフィルム。