JP6243313B2 - Anisotropic adhesive sheet - Google Patents

Anisotropic adhesive sheet Download PDF

Info

Publication number
JP6243313B2
JP6243313B2 JP2014210585A JP2014210585A JP6243313B2 JP 6243313 B2 JP6243313 B2 JP 6243313B2 JP 2014210585 A JP2014210585 A JP 2014210585A JP 2014210585 A JP2014210585 A JP 2014210585A JP 6243313 B2 JP6243313 B2 JP 6243313B2
Authority
JP
Japan
Prior art keywords
pressure
sensitive adhesive
resin layer
layer
anisotropic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2014210585A
Other languages
Japanese (ja)
Other versions
JP2016079263A (en
Inventor
林　益史
益史 林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujimori Kogyo Co Ltd
Original Assignee
Fujimori Kogyo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujimori Kogyo Co Ltd filed Critical Fujimori Kogyo Co Ltd
Priority to JP2014210585A priority Critical patent/JP6243313B2/en
Priority to CN201510590071.6A priority patent/CN105524565B/en
Priority to KR1020150131456A priority patent/KR101876208B1/en
Priority to TW104131557A priority patent/TWI680174B/en
Publication of JP2016079263A publication Critical patent/JP2016079263A/en
Application granted granted Critical
Publication of JP6243313B2 publication Critical patent/JP6243313B2/en
Priority to KR1020180076817A priority patent/KR102004172B1/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、剥離する方向により異なる剥離性を示して、特定方向に対する強固な接着性と、特定方向以外の方向に対する優れた剥離性とを両立させることができる異方粘着性シートに関するものである。   The present invention relates to an anisotropic pressure-sensitive adhesive sheet that exhibits different peelability depending on the peeling direction, and can achieve both strong adhesiveness in a specific direction and excellent peelability in directions other than the specific direction. .

粘着シートや粘着テープ等の粘着製品は、多くの用途で使用されている。使用用途に合わせて、適当な粘着力の粘着剤を選定して使用しているのが一般的である。永久的に接着させる用途では、粘着力の強い粘着剤が使用され、再剥離される用途では、粘着力の弱い粘着剤が使用されるのが一般的である。しかしながら、壁紙、ウインドーフィルム、マーキングシートなどの製品においては、粘着力が強い粘着剤が必要とされるが、貼り位置の修正時、貼合の際の気泡や異物の噛み込み時、及び粘着製品の貼り替え時などに、容易に剥離したいという、相反する機能を同時に満たすことが求められている。また、ワッペンやシール、各種粘着テープについては、不要時に除去した際に、粘着剤が被着体に残存してしまう問題もある。さらに、宛名ラベルや宅配便の送り状等が貼着された段ボール箱や封筒などの包装容器については、従来は、宛名ラベルなどが貼着したまま廃棄するのが一般的であった。しかし、個人情報の漏えいを防止したいなどの理由で、宛名ラベルなどの個人情報を記載した部分を簡単に剥がして、段ボール箱などの包装容器を廃棄することが求められている。
一方、光学フィルムやディスプレイ用の保護フィルム、金属板や鋼鈑用の保護シートなどは、被着体に貼り合せて使用する時には剥がれないで使用でき、不要時には、被着体から簡単に剥離できる（軽剥離化されている）粘着シートが要望されている。すなわち、永久的に接着させる用途、及び再剥離される用途において、被着体に対して強固に接着し、不要時や貼り合せ修正時に、被着体から簡単に剥がせる粘着製品が求められている。 Adhesive products such as adhesive sheets and adhesive tapes are used in many applications. Generally, an adhesive having an appropriate adhesive strength is selected and used according to the intended use. In applications where permanent adhesion is used, an adhesive having a strong adhesive force is used, and in applications where re-peeling is used, an adhesive having a weak adhesive force is generally used. However, in products such as wallpaper, window film, and marking sheets, adhesives with strong adhesive strength are required. However, when correcting the bonding position, when bubbles or foreign objects are stuck in bonding, and when sticking At the same time, it is required to satisfy the conflicting function that it is desired to easily peel off when changing the product. In addition, the patch, the seal, and the various adhesive tapes have a problem that the adhesive remains on the adherend when removed when unnecessary. Further, conventionally, packaging containers such as cardboard boxes and envelopes to which address labels and courier invoices are attached are generally discarded with the address label attached. However, for the purpose of preventing leakage of personal information, it is required to easily peel off a portion on which personal information such as an address label is written and to discard a packaging container such as a cardboard box.
On the other hand, optical films, protective films for displays, protective sheets for metal plates and steel plates, etc. can be used without being peeled off when used on an adherend, and can be easily peeled off from an adherend when not needed. There is a demand for an adhesive sheet (which is lightly peeled). That is, there is a demand for an adhesive product that adheres firmly to the adherend and can be easily peeled off from the adherend when it is not needed or when correcting bonding in applications that are permanently bonded and re-peeled. Yes.

接着性と剥離性の両立については、従来から種々の提案がされている。例えば、特許文献１には、加熱処理で接着力が低下ないし喪失するようにした加熱剥離型粘着シートとして、基材上に発泡剤含有の粘着層を設けたものが提案されている。また、特許文献２には、放射線照射によって粘着剤を硬化させ、粘着力を著しく低下させる粘着テープが提案されている。しかしながら、このような粘着シートは、紫外線照射装置や加熱装置が設置されていないところでは、軽剥離化の機能を利用できないという問題がある。   Conventionally, various proposals have been made regarding compatibility between adhesiveness and peelability. For example, Patent Document 1 proposes a heat-peelable pressure-sensitive adhesive sheet in which adhesive strength is reduced or lost by heat treatment, in which a foaming agent-containing pressure-sensitive adhesive layer is provided on a base material. Patent Document 2 proposes an adhesive tape that cures the adhesive by irradiation and significantly reduces the adhesive strength. However, such a pressure-sensitive adhesive sheet has a problem that the light peeling function cannot be used in a place where no ultraviolet irradiation device or heating device is installed.

また、剥がす方向により粘着力が異なる粘着シートも、いくつか提案されている。例えば、特許文献３には、部分的に配向および結晶化したエラストマーを用いた感圧粘着製品が提案されている。特許文献４には、基材及び／又は粘着剤層の少なくとも一層中に、異方形状の剛体粒子及び／又は繊維が配向して分散している異方剥離性粘着テープが紹介されている。これらの提案は、軽剥離化の機能を利用するための設備・装置を必要としておらず、作業性が優れているが、粘着剤の材料が特定の物質に限定されるため、粘着剤の特性範囲が限られてしまうという問題があった。   Several pressure-sensitive adhesive sheets having different adhesive strength depending on the peeling direction have been proposed. For example, Patent Document 3 proposes a pressure-sensitive adhesive product using a partially oriented and crystallized elastomer. Patent Document 4 introduces an anisotropic peelable adhesive tape in which anisotropically shaped rigid particles and / or fibers are oriented and dispersed in at least one layer of a base material and / or an adhesive layer. These proposals do not require equipment / equipment for utilizing the light release function, and are excellent in workability, but because the material of the adhesive is limited to specific substances, the characteristics of the adhesive There was a problem that the range was limited.

さらに、特許文献５には、異方可撓性を有する支持体を使用した異方粘着性成形品が提案されている。異方可撓性を有した支持体を使用するもので、粘着剤の材料自体は、特定の物質に制限されないため、粘着剤の特性範囲が限られない利点がある反面、支持体の構造が限定されてしまうという問題があった。   Furthermore, Patent Document 5 proposes an anisotropic pressure-sensitive adhesive molded product using a support having anisotropic flexibility. Since the support having anisotropic flexibility is used, the material of the adhesive itself is not limited to a specific substance, and thus there is an advantage that the characteristic range of the adhesive is not limited, but the structure of the support is There was a problem of being limited.

実公昭５０−０１３８７８号公報Japanese Utility Model Publication No. 50-013878 特開昭６０−１９６９５６号公報JP-A-60-196956 特開２０００−５０２３７９号公報JP 2000-502379 A 特開２００４−１８９８４７号公報JP 2004-189847 A 特開平７−０１８２２７号公報JP-A-7-018227

本発明は、上記事情に鑑みてなされたものであって、被着体に対して強固に接着し、不要時や貼り合せ修正時に、被着体から簡単に剥がせる粘着シートを提供するものである。
より具体的には、本発明は、剥離する方向により異なる剥離性を示して、特定方向に対する強固な接着性と、特定方向以外の方向に対する優れた剥離性とを両立させることができる異方粘着性シートを提供することを課題としている。 The present invention has been made in view of the above circumstances, and provides a pressure-sensitive adhesive sheet that adheres firmly to an adherend and can be easily peeled off from the adherend when it is unnecessary or when bonding is corrected. is there.
More specifically, the present invention shows an anisotropic pressure-sensitive adhesive that exhibits different peelability depending on the peeling direction and can achieve both strong adhesiveness in a specific direction and excellent peelability in directions other than the specific direction. The issue is to provide a sex sheet.

この課題を解決するために鋭意検討を行なった結果、基材と粘着剤層の間に樹脂層を設け、樹脂層の粘着剤層と接する表面に凹凸構造を設けることで、粘着シートの粘着力が変化することが分かった。また、この樹脂層表面の凹凸構造のパターンに異方性をつけることで、剥離方向により剥離力（粘着力）が異なる粘着シートができることを見出し、本発明を完成させるに至った。   As a result of intensive studies to solve this problem, the adhesive strength of the pressure-sensitive adhesive sheet is obtained by providing a resin layer between the base material and the pressure-sensitive adhesive layer and providing a concavo-convex structure on the surface of the resin layer that contacts the pressure-sensitive adhesive layer. Was found to change. In addition, it has been found that by giving anisotropy to the pattern of the concavo-convex structure on the surface of the resin layer, a pressure-sensitive adhesive sheet having a different peeling force (adhesive strength) depending on the peeling direction can be obtained, and the present invention has been completed.

上記の課題を解決するため、本発明は、長尺フィルムからなる基材の少なくとも片面に、凹凸構造の断面を有する樹脂層と、該樹脂層の凹凸構造を埋める粘着剤層とが順に積層してなる粘着シートであって、該樹脂層の凹凸構造のパターン形状において、
（ａ）前記基材の長手方向または幅方向に、スジ状に凸部を有し、且つスジ状に平坦な凹部を有することによる異方性、又は、
（ｂ）前記基材の長手方向に対して、斜め方向にスジ状に凸部を有し、且つスジ状に平坦な凹部を有することによる異方性があるとともに、
前記粘着剤層を被着体から剥がす方向により粘着力が異なり、
前記粘着剤層の最も厚い部分の厚みＴ２が、５〜１００μｍであり、かつ、前記粘着剤層の厚みの、最も薄い部分の厚みＴ１と、最も厚い部分の厚みＴ２との比率Ｋが、Ｋ＝Ｔ１／Ｔ２＝０．２〜０．８であり、
前記粘着剤層の被着体に接着される表面が、算術平均表面粗さＲａが５μｍ以下であり、平滑性を有することを特徴とする異方粘着性シートを提供する。 In order to solve the above-mentioned problems, the present invention comprises, on at least one surface of a substrate made of a long film, a resin layer having a concavo-convex cross section and an adhesive layer that fills the concavo-convex structure of the resin layer in order. a pressure-sensitive adhesive sheet comprising Te, the Oite pattern shape of the concavo-convex structure of the resin layer,
(A) Anisotropy by having a convex portion in a stripe shape and a flat concave portion in a stripe shape in the longitudinal direction or the width direction of the substrate, or
(B) With respect to the longitudinal direction of the base material, there is anisotropy due to having a convex portion in a stripe shape in a diagonal direction and having a flat concave portion in a stripe shape,
The adhesive force varies depending on the direction in which the adhesive layer is peeled off from the adherend,
The thickness T2 of the thickest part of the pressure-sensitive adhesive layer is 5 to 100 μm, and the ratio K between the thickness T1 of the thinnest part and the thickness T2 of the thickest part of the pressure-sensitive adhesive layer is K = T1 / T2 = 0.2-0.8,
Provided is an anisotropic pressure-sensitive adhesive sheet characterized in that the surface of the pressure-sensitive adhesive layer bonded to the adherend has an arithmetic average surface roughness Ra of 5 μm or less and has smoothness.

また、被着体をガラス板としたとき、前記樹脂層の凸形状に沿った方向の粘着力τ１と、前記樹脂層の凸形状に直交した方向の粘着力τ２との比率Ｒが、Ｒ＝τ１／τ２＝０．１〜０．５であることを特徴とする異方粘着性シートを提供する。   Further, when the adherend is a glass plate, the ratio R between the adhesive force τ1 in the direction along the convex shape of the resin layer and the adhesive force τ2 in the direction orthogonal to the convex shape of the resin layer is R = An anisotropic pressure-sensitive adhesive sheet is provided, wherein τ1 / τ2 = 0.1 to 0.5.

本発明の異方粘着性シートは、剥離する方向により異なる剥離性を示して、特定方向に対する強固な接着性と、特定方向以外の方向に対する優れた剥離性とを両立させることができる。これにより、被着体に対して強固に接着し、不要時や貼り合せ修正時に、被着体から簡単に剥がせる異方粘着性シートを提供することができる。また、本発明の異方粘着性シートは、基材および粘着剤の、材料の種類に制約を受けないため、種々の用途に使用することができる。   The anisotropic pressure-sensitive adhesive sheet of the present invention exhibits different peelability depending on the peel direction, and can achieve both strong adhesiveness in a specific direction and excellent peelability in directions other than the specific direction. Thereby, it is possible to provide an anisotropic pressure-sensitive adhesive sheet that adheres firmly to the adherend and can be easily peeled off from the adherend when it is unnecessary or when the bonding is corrected. Moreover, since the anisotropic pressure-sensitive adhesive sheet of the present invention is not restricted by the types of materials of the base material and the pressure-sensitive adhesive, it can be used for various applications.

（ａ）及び（ｂ）は、それぞれ、本発明の異方粘着性シートの一例を示した、模式的断面図である。(A) And (b) is typical sectional drawing which showed an example of the anisotropic adhesive sheet of this invention, respectively. （ａ）〜（ｃ）は、それぞれ、本発明の異方粘着性シートの、粘着剤層を積層する前の状態の一例を示した、模式的斜視図である。(A)-(c) is the typical perspective view which showed an example of the state before laminating | stacking an adhesive layer of the anisotropic adhesive sheet of this invention, respectively. （ａ）及び（ｂ）は、それぞれ、本発明の異方粘着性シートを用いた製品の一例を示した、模式的断面図である。(A) And (b) is typical sectional drawing which showed an example of the product using the anisotropic adhesive sheet of this invention, respectively.

以下、実施の形態に基づいて、本発明を詳しく説明する。
図１は、本発明の異方粘着性シートの、概念を示した、模式的断面図である。この異方粘着性シート１０は、基材１の片方の表面に、樹脂層２が形成されている。この樹脂層２の表面には、粘着剤層３が形成されている。樹脂層２は、粘着剤層３側の表面に、凹凸構造を有している。図１（ａ）の場合、樹脂層２の下部２ａが基材１の表面に連続して形成され、樹脂層２の上部２ｂのみが凹凸構造を有している。図１（ｂ）の場合、樹脂層２は、基材１の表面に不連続に形成され、樹脂層２の形成されていない箇所では、粘着剤層３が基材１の表面に接触可能である。 Hereinafter, the present invention will be described in detail based on embodiments.
FIG. 1 is a schematic cross-sectional view showing the concept of the anisotropic pressure-sensitive adhesive sheet of the present invention. The anisotropic pressure-sensitive adhesive sheet 10 has a resin layer 2 formed on one surface of a substrate 1. An adhesive layer 3 is formed on the surface of the resin layer 2. The resin layer 2 has an uneven structure on the surface on the pressure-sensitive adhesive layer 3 side. In the case of FIG. 1A, the lower part 2a of the resin layer 2 is continuously formed on the surface of the substrate 1, and only the upper part 2b of the resin layer 2 has an uneven structure. In the case of FIG. 1B, the resin layer 2 is formed discontinuously on the surface of the base material 1, and the adhesive layer 3 can contact the surface of the base material 1 at a location where the resin layer 2 is not formed. is there.

本発明に係わる異方粘着性シート１０に使用される基材１としては、特に限定されるものではなく、紙、樹脂フィルム、樹脂シート、金属含有シート、無機物含有シート、またはそれらを積層したシートなど、いずれも使用できる。紙基材としては、上質紙、クレーコート紙、アートコート紙、樹脂コート紙、グラシン紙、ポリエチレンラミネート紙などが挙げられる。また、樹脂フィルムの基材としては、ポリエチレンフィルム、ポリプロピレンフィルム、ポリエステルフィルム、ポリアミドフィルム、アクリルフィルム、ポリカーボネートフィルム、ポリイミドフィルム、塩化ビニルフィルム、塩化ビニリデンフィルム、ポリスチレンフィルムなどの樹脂フィルムが挙げられる。樹脂シートの基材としては、ポリオレフィンシート、塩化ビニルシート、ポリエステルシート、ポリアミドシートなどが挙げられる。金属含有シートとしては、アルミ箔、銅箔、ステンレス箔などの金属箔、金属箔と樹脂フィルムとの積層シート、アルミ蒸着シートなどの金属蒸着シート（蒸着フィルムでもよい）、金属粒子を含有した樹脂シートなどが挙げられる。無機物（化合物）含有シートとしては、アルミナ蒸着シート、シリカ蒸着シートといった無機物蒸着シート（蒸着フィルムでもよい）などが挙げられる。   The substrate 1 used for the anisotropic pressure-sensitive adhesive sheet 10 according to the present invention is not particularly limited, and is a paper, a resin film, a resin sheet, a metal-containing sheet, an inorganic-containing sheet, or a sheet obtained by laminating them. Any of them can be used. Examples of the paper substrate include high-quality paper, clay-coated paper, art-coated paper, resin-coated paper, glassine paper, and polyethylene laminated paper. Moreover, as a base material of a resin film, resin films, such as a polyethylene film, a polypropylene film, a polyester film, a polyamide film, an acrylic film, a polycarbonate film, a polyimide film, a vinyl chloride film, a vinylidene chloride film, a polystyrene film, are mentioned. Examples of the base material of the resin sheet include a polyolefin sheet, a vinyl chloride sheet, a polyester sheet, and a polyamide sheet. Examples of metal-containing sheets include metal foils such as aluminum foil, copper foil, and stainless steel foil, laminated sheets of metal foil and resin film, metal vapor-deposited sheets such as aluminum vapor-deposited sheets (or vapor-deposited films), and resins containing metal particles A sheet etc. are mentioned. Examples of the inorganic substance (compound) -containing sheet include an inorganic vapor deposition sheet (may be a vapor deposition film) such as an alumina vapor deposition sheet and a silica vapor deposition sheet.

基材１の材質や厚みは、特に限定されるものではなく、使用用途に合わせた材質、厚みであれば良い。このため、本願明細書において、シート及びフィルムの用語は、特に厚みの区別なく使用されることがあり、一方の用語が他方の意味を包含し得る。
また、樹脂層２の塗工性及び密着性の向上のために、基材１の樹脂層２側の表面に、必要に応じて、コロナ処理、プラズマ処理などによる表面改質や、アンカーコート剤の塗付などの易接着処理を施してもよい。 The material and thickness of the substrate 1 are not particularly limited, and may be any material and thickness suitable for the intended use. For this reason, in this specification, the terms of sheet and film are sometimes used without distinction of thickness, and one term can encompass the meaning of the other.
Further, in order to improve the coating property and adhesion of the resin layer 2, the surface of the substrate 1 on the resin layer 2 side may be modified as necessary by corona treatment, plasma treatment or the like, or an anchor coating agent. Easy adhesion treatment such as coating may be performed.

基材１の樹脂層２とは反対側の表面に、用途に応じた表面処理を施しても良い。例えば、粘着テープの用途では、シリコーンなどの離型剤を塗布して離型剤層を形成してもよい。また、ウインドーフィルムの用途では、ハードコート剤や汚れ防止剤、赤外線（熱線）カット剤や紫外線カット剤などの塗布層を形成してもよい。ラベル、壁紙、シール、ワッペン、ステッカー等の用途では、各種印刷層や、受像層、保護層などを施して良い。   The surface of the substrate 1 on the side opposite to the resin layer 2 may be subjected to a surface treatment according to the use. For example, in the use of an adhesive tape, a release agent layer such as silicone may be applied to form a release agent layer. Moreover, in the use of a window film, you may form application layers, such as a hard-coat agent, a stain | pollution | contamination prevention agent, an infrared rays (heat ray) cutting agent, and an ultraviolet-ray cutting agent. In applications such as labels, wallpaper, stickers, patches, stickers, etc., various printed layers, image receiving layers, protective layers, etc. may be applied.

本発明に係わる異方粘着性シート１０に使用される樹脂層２は、異方粘着性を発現させるために重要な構成要素である。図２に、本発明の異方粘着性シートの、粘着剤層を積層する前の状態の一例を示した。図２（ａ）では、樹脂層２の上部２ｂの断面形状が、略半円状の凸形状をしている。図２（ｂ）では、樹脂層２の上部２ｂの断面形状が、略矩形状の凸形状をしている。図２（ｃ）では、樹脂層２の上部２ｂの断面形状が、略三角状の凸形状をしている。図２の各図は、図１（ａ）のように、樹脂層２の下部２ａが連続している場合を示すが、図１（ｂ）のように、樹脂層２が不連続に形成されていてもよい。
本発明に係わる異方粘着性シート１０は、樹脂層２が、粘着剤層３側の表面に凹凸構造を有し、かつ、この凹凸構造のパターンが異方性（縦、横もしくは斜めに見たときの凹凸構造のパターン形状が異なる）を有することを特徴とする。 The resin layer 2 used in the anisotropic pressure-sensitive adhesive sheet 10 according to the present invention is an important component for developing anisotropic pressure-sensitive adhesiveness. In FIG. 2, an example of the state before laminating | stacking an adhesive layer of the anisotropic adhesive sheet | seat of this invention was shown. In FIG. 2A, the cross-sectional shape of the upper part 2b of the resin layer 2 is a substantially semicircular convex shape. In FIG. 2B, the cross-sectional shape of the upper part 2b of the resin layer 2 is a substantially rectangular convex shape. In FIG. 2C, the cross-sectional shape of the upper part 2b of the resin layer 2 is a substantially triangular convex shape. Each figure of FIG. 2 shows the case where the lower part 2a of the resin layer 2 is continuous as shown in FIG. 1A, but the resin layer 2 is formed discontinuously as shown in FIG. 1B. It may be.
In the anisotropic pressure-sensitive adhesive sheet 10 according to the present invention, the resin layer 2 has a concavo-convex structure on the surface on the pressure-sensitive adhesive layer 3 side, and the pattern of the concavo-convex structure is anisotropic (vertically, horizontally or obliquely viewed). The pattern shape of the concavo-convex structure is different).

本発明に係わる異方粘着性シートの粘着力は、粘着剤と被着体の界面との接着力（１）と、粘着剤層内部の粘着剤層を変形させるのに要する応力（２）との合算値と考えられる。本発明は、粘着剤層を変形させるのに要する応力（２）を、剥離方向に応じて差をつけることで、異方粘着性を発揮させることをコンセプトとしている。樹脂層２の表面に凹凸構造を設けることで、粘着剤層３の厚みを変え、異方粘着性シート１０を剥離する際に、外力で変形する粘着剤層の体積を変化させて、剥離する方向に応じて粘着力に差が出るようにしている。このため、樹脂層２に使用する樹脂の貯蔵弾性率は、粘着剤層３に使用する粘着剤の貯蔵弾性率よりも大きいことが必要となる。   The pressure-sensitive adhesive force of the anisotropic pressure-sensitive adhesive sheet according to the present invention includes the adhesive force (1) between the pressure-sensitive adhesive and the adherend and the stress (2) required to deform the pressure-sensitive adhesive layer inside the pressure-sensitive adhesive layer. It is considered the sum of The present invention is based on the concept of exerting anisotropic adhesiveness by making a difference in the stress (2) required to deform the pressure-sensitive adhesive layer according to the peeling direction. By providing a concavo-convex structure on the surface of the resin layer 2, the thickness of the pressure-sensitive adhesive layer 3 is changed, and when the anisotropic pressure-sensitive adhesive sheet 10 is peeled off, the volume of the pressure-sensitive adhesive layer deformed by an external force is changed and peeled off. The adhesive strength varies depending on the direction. For this reason, the storage elastic modulus of the resin used for the resin layer 2 needs to be larger than the storage elastic modulus of the adhesive used for the adhesive layer 3.

樹脂層２に使用する樹脂は、特に限定されるものではなく、凹凸構造を形成、保持できるものであれば使用できる。具体的には、アクリル樹脂、ポリエステル樹脂、エポキシ樹脂、オレフィン樹脂、ポリアミド樹脂、ポリイミド樹脂、ポリビニルアルコール樹脂、酢酸ビニル樹脂、硝化綿（ニトロセルロース）、アルキッド樹脂、フェノール樹脂、フッ素樹脂、シリコーン樹脂などが挙げられる。   The resin used for the resin layer 2 is not particularly limited, and any resin that can form and hold a concavo-convex structure can be used. Specifically, acrylic resin, polyester resin, epoxy resin, olefin resin, polyamide resin, polyimide resin, polyvinyl alcohol resin, vinyl acetate resin, nitrified cotton (nitrocellulose), alkyd resin, phenol resin, fluorine resin, silicone resin, etc. Is mentioned.

基材１に樹脂層２を形成する方法は、公知の方法を用いればよく、基材１に樹脂塗料をコーティングする方法や、基材１に樹脂を溶融押出して積層する方法（押出ラミネート法）、あらかじめ樹脂シートを作製し、基材１と接着剤を用いて積層する方法（ドライラミネート法）などが挙げられる。   As a method of forming the resin layer 2 on the base material 1, a known method may be used. A method of coating the base material 1 with a resin paint or a method of melt-extruding and laminating a resin on the base material 1 (extrusion laminating method). Examples thereof include a method of preparing a resin sheet in advance and laminating using the base material 1 and an adhesive (dry laminating method).

本発明に係わる異方粘着性シート１０は、樹脂層２が、粘着剤層３側の表面に凹凸構造を有し、かつ、この凹凸構造のパターンが異方性（縦、横もしくは斜めに見たときの凹凸構造のパターン形状が異なる）を有することを特徴とする。異方性を有する凹凸構造のパターン形状としては、長尺フィルムからなる基材１の流れ方向または幅方向に、スジ状（縦縞状や横縞状）に凸部（または凹部）を設けるパターン形状が最も一般的である。このほか、長尺フィルムからなる基材１の流れ方向に対して、斜め方向にスジ状に凸部（または凹部）を設けるパターン形状や、円柱状の凹パターンを縦方向または横方向に不連続に並べたパターン形状、などが挙げられる。   In the anisotropic pressure-sensitive adhesive sheet 10 according to the present invention, the resin layer 2 has a concavo-convex structure on the surface on the pressure-sensitive adhesive layer 3 side, and the pattern of the concavo-convex structure is anisotropic (vertically, horizontally or obliquely viewed). The pattern shape of the concavo-convex structure is different). As the pattern shape of the concavo-convex structure having anisotropy, there is a pattern shape in which convex portions (or concave portions) are formed in stripes (vertical stripes or horizontal stripes) in the flow direction or width direction of the substrate 1 made of a long film. The most common. In addition, a pattern shape in which convex portions (or concave portions) are formed in stripes in an oblique direction with respect to the flow direction of the base material 1 made of a long film, or a cylindrical concave pattern is discontinuous in the vertical direction or the horizontal direction. The pattern shape arranged in the above.

樹脂層２に、異方性を有する凹凸構造のパターンを形成する方法としては、公知の方法を用いればよい。例えば、基材１上に溶融した樹脂を押出し、パターンをつけた冷却ロールで押さえ、冷却ロールのパターンを転写する方法、基材１上に樹脂塗料をグラビア工法にてパターン塗工する方法、基材１上に、熱可塑性樹脂または紫外線硬化樹脂を均一に塗工し、パターンを切った型を押し当ててパターン形状を樹脂表面に転写する方法などいずれでもよい。   A known method may be used as a method for forming a pattern of an uneven structure having anisotropy on the resin layer 2. For example, a method of extruding a melted resin on the substrate 1 and pressing it with a patterned cooling roll to transfer the pattern of the cooling roll, a method of applying a resin paint pattern on the substrate 1 by a gravure method, Any method may be used in which a thermoplastic resin or an ultraviolet curable resin is uniformly coated on the material 1, and a pattern shape is transferred to the resin surface by pressing a pattern cut pattern.

樹脂層２の厚みは、特に限定されることはなく、パターンの形状やパターン部の凹部分の深さ、粘着剤の被膜物性などにより、適当な厚みを選定すればよい。樹脂層２の厚みは、３〜５０μｍ程度にするのが一般的である。３μｍ未満では剥離方向による粘着力の差が発現し難く、５０μｍを超えると、コスト面で不利になり、樹脂層２の加工性が劣るなどの点から、好ましくはない。   The thickness of the resin layer 2 is not particularly limited, and an appropriate thickness may be selected depending on the shape of the pattern, the depth of the concave portion of the pattern portion, the film properties of the adhesive, and the like. The thickness of the resin layer 2 is generally about 3 to 50 μm. If the thickness is less than 3 μm, it is difficult to develop a difference in adhesive strength depending on the peeling direction. If the thickness exceeds 50 μm, it is disadvantageous in terms of cost, and the processability of the resin layer 2 is inferior.

また、樹脂層２の粘着剤層３と接する表面に、粘着剤層の投錨力のアップのために、コロナ処理、プラズマ処理などによる表面改質や、アンカーコート層を設けるなどの易接着処理を行っても良い。   In addition, in order to increase the anchoring force of the pressure-sensitive adhesive layer on the surface of the resin layer 2 that is in contact with the pressure-sensitive adhesive layer 3, surface modification by corona treatment, plasma treatment, etc., or easy adhesion treatment such as providing an anchor coat layer is performed. You can go.

本発明に係わる異方粘着性シート１０に使用される粘着剤層３は、被着体表面に接着し、使用時には強固に接着し、使用後、もしくは不要時や貼り合せ修正時には、軽く剥離できることが求められている。使用時に強固に接着するために、粘着剤層３の表面は平滑であることが望ましい。具体的には、粘着剤層３の表面の算術平均表面粗さＲａが５μｍ以下であることが望ましい。算術平均表面粗さＲａが５μｍを超える場合には、被着体に対する密着性が悪くなったり、被着体に異方粘着性シート１０を貼合する際に、気泡が混入する恐れがある。   The pressure-sensitive adhesive layer 3 used in the anisotropic pressure-sensitive adhesive sheet 10 according to the present invention adheres to the adherend surface, adheres firmly when used, and can be peeled lightly after use or when not needed or when bonding is corrected. Is required. In order to adhere firmly during use, the surface of the pressure-sensitive adhesive layer 3 is desirably smooth. Specifically, it is desirable that the arithmetic average surface roughness Ra of the surface of the pressure-sensitive adhesive layer 3 is 5 μm or less. When the arithmetic average surface roughness Ra exceeds 5 μm, the adhesion to the adherend may be deteriorated, or bubbles may be mixed when the anisotropic adhesive sheet 10 is bonded to the adherend.

粘着剤の種類は、特に限定されないが、アクリル系粘着剤、ウレタン系粘着剤、ゴム系粘着剤、シリコーン系粘着剤など、使用用途に合わせた粘着剤を使用すれば良い。粘着剤層３の厚みは、特に限定されることはないが、５〜１００μｍ程度にすることが多い。粘着剤層３の厚みが、５μｍ未満であると、樹脂層２の凹凸構造を埋めるのが難しく、１００μｍを超えると性能面では問題ないが、価格が高くなることが問題となる。   The type of the pressure-sensitive adhesive is not particularly limited, but a pressure-sensitive adhesive suitable for the intended use may be used, such as an acrylic pressure-sensitive adhesive, a urethane-based pressure-sensitive adhesive, a rubber-based pressure-sensitive adhesive, or a silicone-based pressure-sensitive adhesive. The thickness of the pressure-sensitive adhesive layer 3 is not particularly limited, but is often about 5 to 100 μm. When the thickness of the pressure-sensitive adhesive layer 3 is less than 5 μm, it is difficult to fill the uneven structure of the resin layer 2, and when it exceeds 100 μm, there is no problem in performance, but the problem is that the price is increased.

樹脂層２の厚み、粘着剤層３の厚み、及び樹脂層２のパターン（凹部の深さや幅、間隔など）形状により、異方粘着性の度合い（樹脂層２の凸形状に沿った方向の粘着力τ１と、樹脂層２の凸形状に直交した方向の粘着力τ２との比率Ｒ）が変化する。異方粘着性を発現させるためには、樹脂層２の厚み、粘着剤層３の厚み、及び樹脂層２のパターン形状の設計が重要となる。異方粘着性シート１０は、粘着剤層３の表面が平滑であることから、樹脂層２が厚い部分での粘着剤層３の厚みが、樹脂層２がない部分、または樹脂層２が薄い部分に比べて、薄くなる。粘着剤層３の厚い部分と薄い部分が混在することにより、異方粘着性を発現している。この粘着剤層３の厚みの、最も薄い部分の厚みＴ１と、最も厚い部分の厚みＴ２との比率Ｋは、Ｋ＝Ｔ１／Ｔ２＝０．２〜０．８であることが望ましい。Ｋが０．２未満のとき、および０．８を超えるときは、異方粘着性が発現し難くなる。   Depending on the thickness of the resin layer 2, the thickness of the pressure-sensitive adhesive layer 3, and the pattern of the resin layer 2 (depth, width, interval, etc. of the recesses), the degree of anisotropic adhesion (in the direction along the convex shape of the resin layer 2) The ratio R) of the adhesive force τ1 and the adhesive force τ2 in the direction orthogonal to the convex shape of the resin layer 2 changes. In order to develop anisotropic adhesiveness, the design of the thickness of the resin layer 2, the thickness of the pressure-sensitive adhesive layer 3, and the pattern shape of the resin layer 2 is important. Since the anisotropic pressure-sensitive adhesive sheet 10 has a smooth surface of the pressure-sensitive adhesive layer 3, the thickness of the pressure-sensitive adhesive layer 3 in the portion where the resin layer 2 is thick is thin, or the portion where the resin layer 2 is not present or the resin layer 2 is thin. Thinner than the part. When the thick part and the thin part of the adhesive layer 3 coexist, anisotropic adhesiveness is expressed. The ratio K of the thickness T1 of the thinnest portion and the thickness T2 of the thickest portion of the pressure-sensitive adhesive layer 3 is desirably K = T1 / T2 = 0.2 to 0.8. When K is less than 0.2 or more than 0.8, anisotropic tackiness is hardly exhibited.

粘着剤は、主剤のみからなる１液型の粘着剤でも、主剤と硬化剤を配合してなる２液型の粘着剤でもよい。必要に応じて、シランカップリング剤などの密着性向上剤や、粘着特性の改善のための粘着付与剤（タッキファイヤー）、耐久性向上のための酸化防止剤や紫外線吸収剤、帯電防止効果を付与する帯電防止剤、硬化反応を促進させる触媒、粘着シートの着色や遮光性の付与のための顔料やフィラーなどを添加しても良い。   The pressure-sensitive adhesive may be a one-component pressure-sensitive adhesive composed of only the main agent or a two-component pressure-sensitive adhesive obtained by blending the main agent and the curing agent. Adhesion improvers such as silane coupling agents, tackifiers for improving adhesive properties (tackfire), antioxidants and UV absorbers for improving durability, and antistatic effects as needed You may add the antistatic agent to provide, the catalyst which accelerates | stimulates hardening reaction, the pigment, filler, etc. for coloring of an adhesive sheet or provision of light-shielding property.

粘着剤層３に添加する硬化剤としては、イソシアネート化合物、エポキシ化合物、メラミン化合物、金属キレート化合物などが挙げられる。また、粘着付与剤としては、ロジン系、クマロンインデン系、テルペン系、石油系、フェノール系などが挙げられる。   As a hardening | curing agent added to the adhesive layer 3, an isocyanate compound, an epoxy compound, a melamine compound, a metal chelate compound, etc. are mentioned. Examples of the tackifier include rosin, coumarone indene, terpene, petroleum, and phenol.

粘着剤層３の形成方法としては、公知の方法を用いればよい。具体的には、基材１と樹脂層２が積層されたシートに、リバースコーティング、コンマコーティング、グラビアコーティング、スロットダイコーティング、メイヤーバーコーティング、エアーナイフコーティングなどの、公知の塗工方法を用いて粘着剤を塗布し、その後、乾燥・硬化を行えばよい。粘着剤の種類によっては、紫外線などの放射線を照射しても良い。また、粘着剤の硬化を促進するために所定の温度でエージング（養生）を行っても良い。   As a method for forming the pressure-sensitive adhesive layer 3, a known method may be used. Specifically, using a known coating method such as reverse coating, comma coating, gravure coating, slot die coating, Mayer bar coating, air knife coating, etc. on a sheet in which the substrate 1 and the resin layer 2 are laminated. What is necessary is just to apply | coat an adhesive and to dry and harden | cure after that. Depending on the type of adhesive, radiation such as ultraviolet rays may be applied. Moreover, in order to accelerate | stimulate hardening of an adhesive, you may age (curing) at predetermined temperature.

本発明の異方粘着性シートは、剥がす方向により粘着力が異なることが特徴である。被着体をガラス板としたとき、樹脂層２の凸形状に沿った方向での粘着力τ１と、樹脂層２の凸形状に直交した方向での粘着力τ２との比率Ｒが、Ｒ＝τ１／τ２＝０．１〜０．５であることが望ましい。Ｒが０．５を超える場合（言い換えればτ２がτ１の２倍未満の場合）には、粘着シートを使用する時の被着体に対する接着性と、不要時や貼り合せ修正時の剥離性との両立が難しくなる。また、粘着シートを使用する時の被着体に対する接着性と、不要時や貼り合せ修正時の剥離性との両立を考えた場合、Ｒが小さいことが望まれるが、Ｒが０．１未満であると異方性の度合いが大きすぎ、剥離方向の許容角度が狭くなる恐れがある。   The anisotropic pressure-sensitive adhesive sheet of the present invention is characterized in that the adhesive force varies depending on the peeling direction. When the adherend is a glass plate, the ratio R between the adhesive force τ1 in the direction along the convex shape of the resin layer 2 and the adhesive force τ2 in the direction orthogonal to the convex shape of the resin layer 2 is R = It is desirable that τ1 / τ2 = 0.1 to 0.5. When R exceeds 0.5 (in other words, when τ2 is less than twice τ1), the adhesiveness to the adherend when using the pressure-sensitive adhesive sheet, and the peelability when unnecessary or when correcting the bonding It becomes difficult to achieve both. Moreover, when considering coexistence of the adhesion to the adherend when using the pressure-sensitive adhesive sheet and the releasability at the time of unnecessary or bonding correction, R is desired to be small, but R is less than 0.1. If so, the degree of anisotropy is too large, and the allowable angle in the peeling direction may be narrowed.

粘着剤層３の表面には、粘着剤層３を保護する目的で剥離フィルムや剥離紙を貼合したり、基材１の樹脂層２とは反対側の表面にシリコーンなどの離型剤を処理し、ロール（テープ）巻きにしたりするのが一般的である。図３に、剥離フィルム（剥離紙）を貼合した製品例とロール（テープ）巻き形状の製品例の、模式的断面図を示す。図３（ａ）は、粘着剤層３の表面を剥離剤層４が覆うように、支持体５の片面に剥離剤層４を設けた剥離シート２０を、異方粘着性シート１０に貼合した例である。図３（ｂ）は、基材１の樹脂層２とは反対側の表面に剥離剤層４を設け、ロール巻きにすると、粘着剤層３の表面を剥離剤層４が覆うようにした例である。なお、粘着シート、粘着テープ、粘着フィルムの語は、しばしばロール巻きの有無、厚みや幅などによって区別されることがあるが、本願明細書において、粘着シート及び異方粘着性シートの語は、特に区別なく広義で使用されるものであり、粘着テープ、粘着フィルムなどの形態を包含する。   On the surface of the pressure-sensitive adhesive layer 3, a release film or release paper is bonded for the purpose of protecting the pressure-sensitive adhesive layer 3, or a release agent such as silicone is applied to the surface of the substrate 1 opposite to the resin layer 2. Generally, it is processed and rolled into a roll (tape). In FIG. 3, the typical sectional drawing of the product example which bonded the peeling film (release paper) and the product example of roll (tape) winding shape is shown. In FIG. 3A, the release sheet 20 provided with the release agent layer 4 on one side of the support 5 is bonded to the anisotropic adhesive sheet 10 so that the release agent layer 4 covers the surface of the adhesive layer 3. This is an example. FIG. 3B shows an example in which the release agent layer 4 is provided on the surface of the substrate 1 opposite to the resin layer 2 and the release agent layer 4 covers the surface of the pressure-sensitive adhesive layer 3 when rolled. It is. The terms adhesive sheet, adhesive tape, and adhesive film are often distinguished by the presence or absence of roll winding, thickness, width, etc., but in the present specification, the terms adhesive sheet and anisotropic adhesive sheet are: It is used in a broad sense without particular distinction, and includes forms such as an adhesive tape and an adhesive film.

樹脂層２の凹凸構造の凹み部を、粘着剤層３で埋める必要があることから、基材１と樹脂層２が積層されたシートに、直接粘着剤を塗布することが望ましいが、樹脂層２の凹凸構造や粘着剤の粘度（重合度）によっては、離型フィルムまたは離型紙に粘着剤を塗布した後、基材１と樹脂層２が積層されたシートの樹脂層２の面に貼合しても良い。また、テープ形状の製品の場合には、基材１の表面に離型処理を施した基材１と樹脂層２が積層されたシートの、基材１側表面に粘着剤を塗布し、テープ巻きをしても良い。凹凸構造の断面を有する樹脂層２と、樹脂層２の凹凸構造を埋める粘着剤層３を、基材１の両面に設けることも可能である。   Since it is necessary to fill the concave portion of the concavo-convex structure of the resin layer 2 with the pressure-sensitive adhesive layer 3, it is desirable to directly apply the pressure-sensitive adhesive to the sheet on which the substrate 1 and the resin layer 2 are laminated. Depending on the concavo-convex structure of 2 and the viscosity (degree of polymerization) of the adhesive, after applying the adhesive to the release film or release paper, it is applied to the surface of the resin layer 2 of the sheet on which the substrate 1 and the resin layer 2 are laminated. May be combined. In the case of a tape-shaped product, an adhesive is applied to the surface of the base material 1 side of the sheet in which the base material 1 and the resin layer 2 subjected to the release treatment are laminated on the surface of the base material 1, and the tape You may roll it. It is also possible to provide the resin layer 2 having a concavo-convex cross section and the pressure-sensitive adhesive layer 3 filling the concavo-convex structure of the resin layer 2 on both surfaces of the substrate 1.

次に、実施例により、本発明をさらに説明する。
（実施例１）
厚みが５０μｍの、片面に易接着処理を施したポリエステルフィルム（東洋紡（株）製エステルＡ−１５９７）の易接着処理面に、紫外線硬化型ハードコートコーティング剤（大日精化工業（株）製セイカビーム（登録商標）ＰＥＴ ＨＣ−３０１）を、乾燥後の厚みが８μｍになるようにメイヤバーにて塗布し、１００℃の熱風循環式オーブンにて１分間乾燥し、溶剤を除去した。その後、ハードコートコーティング剤塗布面に、櫛（櫛歯の太さ１ｍｍ、間隔０．７ｍｍのヘアーコーム）を擦りつけることで、塗工流れ方向にスジ状の均一な溝（縦縞パターン）をつけた後、紫外線照射器（メタルハライドランプ使用）にて積算光量１５００ｍＪ／ｃｍ２の条件にて紫外線を照射してハードコートコーティング剤を硬化した。得られた溝パターンを形成したハードコートコーティング層に、粘着剤（一方社油脂工業（株）製アクリル系粘着剤（ＡＳ−４０９）１００重量部に日本ポリウレタン工業（株）製イソシアネート系硬化剤（コロネート（登録商標）ＨＬ）３重量部を添加）を、アプリケーターを用いて乾燥後の厚み（ポリエステルフィルム表面から粘着剤層の表面までの厚み）が２０μｍとなるように塗布し、１００℃の熱風循環式オーブンにて２分間乾燥させ、粘着剤中の溶剤を除去した。その後、粘着剤層の表面に、厚みが２５μｍのＰＥＴフィルム基材にシリコーン系剥離剤を処理したセパレーター（三菱樹脂（株）製ダイヤホイルＭＲＦ−２５）を貼合して異方粘着性シートを作製した。得られた異方粘着性シートを５０℃の熱風循環式オーブンにて、５日間保温することで、エージングを行い、粘着剤を硬化させ、実施例１の異方粘着性シートを作製した。 Next, the present invention will be further described with reference to examples.
Example 1
An ultraviolet curable hard coat coating agent (Seika Beam, manufactured by Dainichi Seika Kogyo Co., Ltd.) is applied to an easy-adhesion-treated surface of a polyester film (Ester A-1597 manufactured by Toyobo Co., Ltd.) having a thickness of 50 μm and subjected to easy adhesion processing (Registered trademark) PET HC-301) was applied with a Mayer bar so that the thickness after drying was 8 μm, and dried in a hot air circulation oven at 100 ° C. for 1 minute to remove the solvent. After that, by rubbing a comb (hair comb with a comb tooth thickness of 1 mm and an interval of 0.7 mm) on the hard coat coating agent application surface, stripe-like uniform grooves (vertical stripe pattern) are made in the coating flow direction. After that, the hard coat coating agent was cured by irradiating with an ultraviolet ray with an ultraviolet irradiator (using a metal halide lamp) under the condition of an integrated light quantity of 1500 mJ / cm 2 . To the hard coat coating layer in which the groove pattern was formed, 100 parts by weight of an adhesive (on the other hand, Afro Kogyo Co., Ltd. acrylic adhesive (AS-409), an isocyanate curing agent (manufactured by Nippon Polyurethane Industry Co., Ltd.) Add 3 parts by weight of Coronate (registered trademark) HL) using an applicator so that the thickness after drying (thickness from the surface of the polyester film to the surface of the pressure-sensitive adhesive layer) is 20 μm, and hot air at 100 ° C. It was dried in a circulation oven for 2 minutes to remove the solvent in the adhesive. Then, the separator (Mitsubishi Resin Co., Ltd. Diafoil MRF-25) which processed the silicone type release agent on the surface of the adhesive layer is bonded to a PET film substrate having a thickness of 25 μm, and the anisotropic adhesive sheet is attached. Produced. The obtained anisotropic pressure-sensitive adhesive sheet was kept in a hot-air circulating oven at 50 ° C. for 5 days, thereby performing aging and curing the pressure-sensitive adhesive. Thus, the anisotropic pressure-sensitive adhesive sheet of Example 1 was produced.

（実施例２）
粘着剤として、一方社油脂工業（株）製アクリル系粘着剤（ＡＳ−４０９）１００重量部に日本ポリウレタン工業（株）製イソシアネート系硬化剤（コロネート（登録商標）ＨＬ）１重量部を添加した粘着剤を用い、粘着剤層の厚みを１６μｍにした以外は実施例１と同様にして、実施例２の異方粘着性シートを作製した。 (Example 2)
As an adhesive, 1 part by weight of an isocyanate-based curing agent (Coronate (registered trademark) HL) manufactured by Nippon Polyurethane Industry Co., Ltd. was added to 100 parts by weight of an acrylic adhesive (AS-409) manufactured by Yushi Co., Ltd. An anisotropic pressure-sensitive adhesive sheet of Example 2 was produced in the same manner as in Example 1 except that the pressure-sensitive adhesive was used and the thickness of the pressure-sensitive adhesive layer was 16 μm.

（実施例３）
ハードコートコーティング剤塗布面に、櫛（ヘアーコーム）を擦りつけることで、塗工流れに対して直角方向にスジ状の均一な溝（横縞パターン）をつけた以外は実施例１と同様にして、実施例３の異方粘着性シートを作製した。 (Example 3)
The same as in Example 1 except that a streak-like uniform groove (horizontal stripe pattern) was formed in the direction perpendicular to the coating flow by rubbing a comb (hair comb) on the hard coat coating agent application surface. The anisotropic pressure-sensitive adhesive sheet of Example 3 was produced.

（実施例４）
粘着剤層の厚みを１２μｍにした以外は実施例１と同様にして、実施例４の異方粘着性シートを作製した。 Example 4
An anisotropic pressure-sensitive adhesive sheet of Example 4 was produced in the same manner as in Example 1 except that the thickness of the pressure-sensitive adhesive layer was changed to 12 μm.

（比較例１）
ハードコートコーティング層を施さなかった以外は実施例１と同様にして、比較例１の粘着シートを作製した。 (Comparative Example 1)
A pressure-sensitive adhesive sheet of Comparative Example 1 was produced in the same manner as in Example 1 except that the hard coat coating layer was not applied.

（比較例２）
ハードコートコーティング剤塗布面に、櫛（ヘアーコーム）を擦りつけることで、塗工流れ方向及び塗工流れに対して直角方向に、それぞれスジ状の均一な溝（格子縞パターン）をつけた以外は実施例１と同様にして、比較例２の粘着シートを作製した。 (Comparative Example 2)
By rubbing a comb (hair comb) on the hard coat coating agent application surface, except for adding stripe-like uniform grooves (plaid pattern) in the direction perpendicular to the coating flow direction and the coating flow, respectively. In the same manner as in Example 1, a pressure-sensitive adhesive sheet of Comparative Example 2 was produced.

（比較例３）
粘着剤層の厚みを９μｍにした以外は実施例１と同様にして、比較例３の粘着シートを作製した。 (Comparative Example 3)
A pressure-sensitive adhesive sheet of Comparative Example 3 was produced in the same manner as in Example 1 except that the thickness of the pressure-sensitive adhesive layer was 9 μm.

以下、評価試験の方法および結果について示す。
＜異方粘着性シート及び粘着シートの粘着力の測定方法＞
異方粘着性シートまたは粘着シートから塗工流れ方向に対して、平行方向（縦）と垂直方向（横）のサンプル（幅２５ｍｍ、長さ１５０ｍｍ）を採取する。サンプルのセパレーターを剥がし、２ｋｇのゴムローラーを用いてガラス板に貼合する。２３℃×５０％ＲＨの試験環境にて１時間放置後、引張試験機を用いて３００ｍｍ／分の剥離速度で１８０°の方向に、サンプルを剥離したときの強度を測定し、これをサンプルの粘着力（Ｎ／２５ｍｍ）とした。 The evaluation test methods and results are shown below.
<Measurement method of anisotropic adhesive sheet and adhesive strength of adhesive sheet>
Samples (width: 25 mm, length: 150 mm) in the parallel direction (vertical) and vertical direction (horizontal) are collected from the anisotropic pressure-sensitive adhesive sheet or pressure-sensitive adhesive sheet in the coating flow direction. The sample separator is peeled off and bonded to a glass plate using a 2 kg rubber roller. After leaving for 1 hour in a test environment of 23 ° C. × 50% RH, the strength when the sample was peeled in the direction of 180 ° at a peeling speed of 300 mm / min was measured using a tensile tester. The adhesive strength (N / 25 mm) was used.

＜粘着剤の表面粗さ（算術平均表面粗さＲａ）測定方法＞
サンプルのセパレーターを剥がし、粘着剤層表面の表面粗さ（算術平均表面粗さＲａ）を、レーザー顕微鏡（オリンパス(株)製ＬＥＸＴ ＯＬＳ４０００）にて倍率５倍で非接触にて測定し、ｎ＝３の測定の平均値をサンプルの表面粗さとした。 <Method for measuring surface roughness of adhesive (arithmetic average surface roughness Ra)>
The sample separator was peeled off, and the surface roughness (arithmetic average surface roughness Ra) of the pressure-sensitive adhesive layer surface was measured in a non-contact manner at a magnification of 5 with a laser microscope (OLYMPUS LEXT OLS4000), n = The average value of the three measurements was the surface roughness of the sample.

得られた実施例１〜４の異方粘着性シート及び比較例１〜３の粘着シートについて、測定した測定結果を表１及び表２に示した。表１及び表２の「パターン層」とは、ハードコートコーティング剤から形成した樹脂層である。
比較例１、２については、樹脂パターンの異方性がないため、Ｒは便宜上、粘着力（縦）／粘着力（横）とした。 Tables 1 and 2 show the measured results of the anisotropic pressure-sensitive adhesive sheets obtained in Examples 1 to 4 and the pressure-sensitive adhesive sheets in Comparative Examples 1 to 3. The “pattern layer” in Tables 1 and 2 is a resin layer formed from a hard coat coating agent.
In Comparative Examples 1 and 2, since there is no anisotropy of the resin pattern, R is defined as adhesive strength (vertical) / adhesive strength (horizontal) for convenience.

Figure 0006243313
Figure 0006243313

Figure 0006243313
Figure 0006243313

表１、表２に示した測定結果から、以下のことが分かる。
本発明に係わる実施例１〜４の異方粘着性シートは、縦・横の剥離する方向により異なる粘着力（剥離性）を示している。一方、樹脂層を設けなかった比較例１および樹脂層に格子縞をつけた比較例２の粘着シートは、縦・横の剥離する方向に影響を受けず、どちらもほぼ同等な粘着力（剥離性）となった。また、粘着剤層の表面が平滑でない（さらに粘着剤層の厚みの、最も薄い部分の厚みＴ１と、最も厚い部分の厚みＴ２との比率Ｋが０．１であった）比較例３の粘着シートも、縦・横の剥離する方向に影響を受けず、どちらもほぼ同等な粘着力（剥離性）となった。 From the measurement results shown in Tables 1 and 2, the following can be understood.
The anisotropic pressure-sensitive adhesive sheets of Examples 1 to 4 according to the present invention exhibit different adhesive forces (peelability) depending on the longitudinal and lateral peeling directions. On the other hand, the adhesive sheet of Comparative Example 1 in which the resin layer was not provided and Comparative Example 2 in which the resin layer was provided with lattice stripes was not affected by the vertical and horizontal peeling directions, and both had substantially the same adhesive force (peelability). ) Further, the pressure-sensitive adhesive layer has a non-smooth surface (the ratio K between the thickness T1 of the thinnest portion and the thickness T2 of the thickest portion of the pressure-sensitive adhesive layer was 0.1). The sheet was also not affected by the vertical and horizontal peeling directions, and both had almost the same adhesive strength (peelability).

本発明は、使用時には被着体に強固に接着し、不要時や貼り合せ修正時に、被着体から簡単に剥がせる異方粘着性シートを提供するものである。
本発明に係わる異方粘着性シートは、基材や粘着剤の材質に制約を受けることがなく、かつ、剥離する方向により異なる剥離性を有するものである。そのため、例えば、壁紙、ウインドーフィルム、マーキングシート、ラベル、ワッペン、粘着テープ、宛名ラベル、宅配便の送り状、光学フィルムやディスプレイ用の保護フィルム、金属板や鋼鈑用の保護シートなどの各種用途に使用することができる。 The present invention provides an anisotropic pressure-sensitive adhesive sheet that adheres firmly to an adherend during use and can be easily peeled off from the adherend when it is not needed or when bonding is corrected.
The anisotropic pressure-sensitive adhesive sheet according to the present invention is not restricted by the material of the base material or the pressure-sensitive adhesive, and has different peelability depending on the peeling direction. Therefore, for example, various applications such as wallpaper, window film, marking sheet, label, emblem, adhesive tape, address label, courier invoice, protective film for optical film and display, protective sheet for metal plates and steel plates, etc. Can be used for

１…基材、２…樹脂層、２ａ…樹脂層の下部、２ｂ…樹脂層の上部、３…粘着剤層、４…剥離剤層、５…剥離シートの支持体、１０…異方粘着性シート、２０…剥離シート。 DESCRIPTION OF SYMBOLS 1 ... Base material, 2 ... Resin layer, 2a ... Lower part of resin layer, 2b ... Upper part of resin layer, 3 ... Adhesive layer, 4 ... Release agent layer, 5 ... Support of release sheet, 10 ... Anisotropic adhesiveness Sheet, 20 ... release sheet.

Claims (2)

長尺フィルムからなる基材の少なくとも片面に、凹凸構造の断面を有する樹脂層と、該樹脂層の凹凸構造を埋める粘着剤層とが順に積層してなる粘着シートであって、
該樹脂層の凹凸構造のパターン形状において、
（ａ）前記基材の長手方向または幅方向に、スジ状に凸部を有し、且つスジ状に平坦な凹部を有することによる異方性、又は、
（ｂ）前記基材の長手方向に対して、斜め方向にスジ状に凸部を有し、且つスジ状に平坦な凹部を有することによる異方性があるとともに、
前記粘着剤層を被着体から剥がす方向により粘着力が異なり、
前記粘着剤層の最も厚い部分の厚みＴ２が、５〜１００μｍであり、かつ、前記粘着剤層の厚みの、最も薄い部分の厚みＴ１と、最も厚い部分の厚みＴ２との比率Ｋが、Ｋ＝Ｔ１／Ｔ２＝０．２〜０．８であり、
前記粘着剤層の被着体に接着される表面が、算術平均表面粗さＲａが５μｍ以下であり、平滑性を有することを特徴とする異方粘着性シート。 A pressure-sensitive adhesive sheet in which a resin layer having a cross-section of a concavo-convex structure and an adhesive layer that fills the concavo-convex structure of the resin layer are sequentially laminated on at least one side of a base material made of a long film,
Oite pattern shape of the concavo-convex structure of the resin layer,
(A) Anisotropy by having a convex portion in a stripe shape and a flat concave portion in a stripe shape in the longitudinal direction or the width direction of the substrate, or
(B) With respect to the longitudinal direction of the base material, there is anisotropy due to having a convex portion in a stripe shape in a diagonal direction and having a flat concave portion in a stripe shape,
The adhesive force varies depending on the direction in which the adhesive layer is peeled off from the adherend,
The thickness T2 of the thickest part of the pressure-sensitive adhesive layer is 5 to 100 μm, and the ratio K between the thickness T1 of the thinnest part and the thickness T2 of the thickest part of the pressure-sensitive adhesive layer is K = T1 / T2 = 0.2-0.8,
An anisotropic pressure-sensitive adhesive sheet, wherein the surface of the pressure-sensitive adhesive layer bonded to the adherend has an arithmetic average surface roughness Ra of 5 μm or less and has smoothness. 被着体をガラス板としたとき、前記樹脂層の凸形状に沿った方向の粘着力τ１と、前記樹脂層の凸形状に直交した方向の粘着力τ２との比率Ｒが、Ｒ＝τ１／τ２＝０．１〜０．５であることを特徴とする請求項１に記載の異方粘着性シート。   When the adherend is a glass plate, the ratio R between the adhesive force τ1 in the direction along the convex shape of the resin layer and the adhesive force τ2 in the direction orthogonal to the convex shape of the resin layer is R = τ1 / The anisotropic pressure-sensitive adhesive sheet according to claim 1, wherein τ2 = 0.1 to 0.5.
JP2014210585A 2014-10-15 2014-10-15 Anisotropic adhesive sheet Active JP6243313B2 (en)