JP6228840B2 - Cleaning web for electrophotographic copying machine and manufacturing method thereof - Google Patents
Cleaning web for electrophotographic copying machine and manufacturing method thereof Download PDFInfo
- Publication number
- JP6228840B2 JP6228840B2 JP2013269018A JP2013269018A JP6228840B2 JP 6228840 B2 JP6228840 B2 JP 6228840B2 JP 2013269018 A JP2013269018 A JP 2013269018A JP 2013269018 A JP2013269018 A JP 2013269018A JP 6228840 B2 JP6228840 B2 JP 6228840B2
- Authority
- JP
- Japan
- Prior art keywords
- cleaning web
- cleaning
- web
- surface roughness
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、電子写真複写機用クリーニングウェブ及びその製造方法に関するものであり、より詳細には、電子写真複写機の定着ロールなどの被清掃部材に付着したトナーを除去するためのクリーニングウェブ及びその製造方法に関する。 The present invention relates to a cleaning web for an electrophotographic copying machine and a method for manufacturing the same, and more specifically, a cleaning web for removing toner adhering to a member to be cleaned such as a fixing roll of an electrophotographic copying machine and the same. It relates to a manufacturing method.
電子写真複写機の定着ロールの表面に付着した残存トナー等の汚れを除去するために、定着ロールに、ロール巻きしたウェブ状の基材（クリーニングウェブ）を圧接して汚れを拭き取るウェブクリーニングが行われている。トナーとして定着性の余りよくない耐熱トナーを用いる場合、限られた電力（熱量）で高速複写する場合、あるいは、複写画像向上のためにトナーが微粒子化する場合等においては、定着ロール表面にトナーや紙粉が沈着する問題がより発生しやすい状況となる。 In order to remove dirt such as residual toner adhering to the surface of the fixing roll of the electrophotographic copying machine, web cleaning is performed by wiping the dirt by pressing the roll-shaped web-like substrate (cleaning web) against the fixing roll. It has been broken. When using heat-resistant toner that does not have a good fixability as the toner, when copying at high speed with limited power (heat amount), or when the toner becomes fine particles to improve the copy image, the toner on the surface of the fixing roll And the problem of depositing paper dust is more likely to occur.
定着ロールに押圧することによって、定着ロール表面に転写されたトナー及び紙粉を拭き取るクリーニングシートとしては、一般に、全芳香族ポリアミド繊維と未延伸ポリエステル繊維とを適宜配合した繊維ウェブを、熱カレンダーロールによって加熱加圧して製造した不織布が使用されている（特許文献１−３他）。 As a cleaning sheet for wiping off toner and paper powder transferred to the surface of the fixing roll by pressing the fixing roll, generally, a fiber web in which fully aromatic polyamide fibers and unstretched polyester fibers are appropriately blended is used as a thermal calendar roll. Non-woven fabric manufactured by heating and pressurizing by using (Patent Documents 1-3 and others).
上記一般に用いられている全芳香族ポリアミド繊維と未延伸ポリエステル繊維からなる不織布は、厚さを均一にすべく熱圧処理されたものであり、表裏の表面粗さに大きな違いがない。そのため、電子写真複写機における定着ローラ部分に付着したトナーの拭き取りの程度を変更しようとする場合には、クリーニングウェブに含浸されるオイルの付着量を変更する必要があった。 The non-woven fabric composed of the wholly aromatic polyamide fibers and the unstretched polyester fibers that are generally used is subjected to hot-pressure treatment to make the thickness uniform, and there is no significant difference in surface roughness between the front and back surfaces. Therefore, in order to change the degree of wiping off the toner adhering to the fixing roller portion in the electrophotographic copying machine, it is necessary to change the amount of oil impregnated in the cleaning web.
しかしながら、クリーニングウェブに含浸するオイルは、定着ロールにオイルを塗布することによってトナーを定着ロールへ付着しにくくすると同時にクリーニングウェブ自体の拭き取り性を向上することを目的としてクリーニングウェブに含浸されるものである。従って、定着ロールのクリーニング性を良くするためにオイル付着量を多くすると、コストが高くなるばかりか、定着ロールへのオイルの塗布量が増え、オイルが被着体である紙に転写してしまうという問題が起きる。逆に、定着ロールの拭き取り性を低くするためにクリーニングウェブのオイル付着量を少なくすると、オイル塗布量が少なくなり、定着ロールへトナーが固着しやすくなるという問題が発生する。 However, the oil impregnated in the cleaning web is impregnated in the cleaning web for the purpose of making the toner difficult to adhere to the fixing roll by applying oil to the fixing roll and at the same time improving the wiping property of the cleaning web itself. is there. Therefore, increasing the amount of oil attached to improve the cleaning performance of the fixing roll not only increases the cost, but also increases the amount of oil applied to the fixing roll, and the oil is transferred to the paper as the adherend. The problem occurs. Conversely, if the amount of oil adhering to the cleaning web is reduced in order to reduce the wiping property of the fixing roll, there is a problem that the amount of oil applied decreases and the toner is easily fixed to the fixing roll.
更に、従来の熱圧処理されたクリーニングウェブの場合、密度を低くして表面粗さが大きくすると、空隙率が高くなるためにオイルの保持性が悪くなり拭き取り性にムラが生じるという問題だけでなく、強度が低下するという問題も起きる。一方、密度を高くして表面粗さを小さくすると、クリーニングウェブの拭き取り性そのものは向上するものの、オイル付着量が少なくなるため、拭き取り性の向上には限界を伴う。 Furthermore, in the case of a conventional hot-pressed cleaning web, if the density is decreased and the surface roughness is increased, the porosity is increased, so that the oil retention becomes worse and the wiping property becomes uneven. There is also a problem that the strength decreases. On the other hand, when the density is increased and the surface roughness is reduced, the wiping property of the cleaning web itself is improved, but the amount of oil adhesion is reduced, so that improvement of the wiping property is limited.
本発明は、このような従来技術に鑑みてなされたもので、定着ロールの拭取り性を向上させ、且つ、クリーニングウェブの密度やオイルの付着量に依存することなく、ウェブの表裏を変更することで、クリーニング性をコントロールできるクリーニングウェブ及びその製造方法を提供することを課題とする。 The present invention has been made in view of such a conventional technique, and improves the wiping property of the fixing roll, and changes the front and back of the web without depending on the density of the cleaning web and the amount of oil attached. Thus, it is an object of the present invention to provide a cleaning web that can control the cleaning property and a method for manufacturing the same.
上記課題を解決するための請求項１に係る発明は、電子写真複写機における定着ローラ部分に付着したトナーのクリーニング性を、ウェブの表裏を入れ替えることでコントロールするためのクリーニングウェブであって、前記クリーニングウェブは表裏に平滑差を有し、一方の面の表面粗さＲａ１が１．０μｍ以下であり、他方の面の表面粗さＲａ２が２．５μｍ以下であって、前記Ｒａ２とＲａ１との差が０．７μｍ以上であることを特徴とする電子写真複写機用クリーニングウェブである。 The invention according to claim 1 for solving the above-mentioned problem is a cleaning web for controlling the cleaning performance of toner adhering to a fixing roller portion in an electrophotographic copying machine by replacing the front and back of the web. The cleaning web has a smooth difference between the front and back surfaces, the surface roughness Ra1 of one surface is 1.0 μm or less, the surface roughness Ra2 of the other surface is 2.5 μm or less, and the Ra2 and Ra1 An electrophotographic copying machine cleaning web having a difference of 0.7 μm or more.
好ましい実施形態における前記クリーニングウェブは、木材パルプ、及び／又は、非木材パルプを５重量％以上含有する。
また、好ましい実施形態における前記クリーニングウェブは、２００℃雰囲気において２Ｎ／ｃｍ以上の引張強さを有し、また、２００℃雰囲気において１０％以下の破断伸びを有する。
The cleaning web in a preferred embodiment contains 5% by weight or more of wood pulp and / or non-wood pulp.
In addition, the cleaning web in a preferred embodiment has a tensile strength of 2 N / cm or more in a 200 ° C. atmosphere and a breaking elongation of 10% or less in a 200 ° C. atmosphere.
また、好ましい実施形態における前記クリーニングウェブは、そのの厚さが２０〜１２０μｍである。 In the preferred embodiment, the cleaning web has a thickness of 20 to 120 μm.
また、好ましい実施形態における前記クリーニングウェブは、シリコーンオイルを含有する。 In the preferred embodiment, the cleaning web contains silicone oil.
また、上記課題を解決するための請求項６に係る発明は、請求項１乃至５のいずれかに記載のクリーニングウェブを製造するための方法であって、前記クリーニングウェブを、ヤンキードライヤーを有する抄紙機において、前記ヤンキードライヤーを用いて湿紙を乾燥することによって製造することを特徴とするクリーニングウェブの製造方法である。 An invention according to claim 6 for solving the above problem is a method for producing a cleaning web according to any one of claims 1 to 5, wherein the cleaning web is made of paper having a Yankee dryer. A method for producing a cleaning web, characterized in that the web is produced by drying wet paper using the Yankee dryer.
本発明に係るクリーニングウェブは上記のとおりであって、一方の面が、全芳香族ポリアミド繊維と未延伸ポリエステル繊維とを熱圧処理した不織布から成る市販のクリーニングウェブの払拭面より平滑で、他方の面がその払拭面と同等かそれより粗い表面を有するために、一方の平滑面において従来よりも優れた拭き取り効果が得られ、他方の粗い面において従来と遜色ない充分な拭取り効果が得られる。そのため、クリーニングウェブの用途に応じて拭き取りの程度を変更するために、単に、クリーニングウェブの表裏を入れ替えるだけで対応することができる効果がある。 The cleaning web according to the present invention is as described above, and one surface is smoother than the wiping surface of a commercially available cleaning web made of a nonwoven fabric obtained by hot-pressing wholly aromatic polyamide fibers and unstretched polyester fibers, and the other side. This surface has a surface that is equal to or rougher than the wiping surface, so that one surface has a wiping effect superior to that of the conventional surface, and the other rough surface has a sufficient wiping effect comparable to that of the conventional surface. It is done. Therefore, in order to change the degree of wiping according to the use of the cleaning web, there is an effect that can be dealt with by simply replacing the front and back of the cleaning web.
本発明に係る電子写真複写機の定着ローラ等の被清掃部材に付着したトナーを除去（クリーニング）するためのクリーニングウェブは、表裏に平滑差を有することを特徴とするものである。このように表裏に平滑差を有しているために、クリーニングウェブの密度やオイルの付着量を変えることなく、単に、クリーニングウェブの表裏を入れ替えるだけで、定着ロールのクリーニング性をコントロールすることが可能となるのである。以下に、本発明に係るクリーニングウェブにつき、より詳細に説明する。 The cleaning web for removing (cleaning) toner adhering to a member to be cleaned such as a fixing roller of an electrophotographic copying machine according to the present invention has a smooth difference between the front and the back. Since there is a smooth difference between the front and back in this way, it is possible to control the cleaning property of the fixing roll by simply replacing the front and back of the cleaning web without changing the density of the cleaning web or the amount of oil attached. It becomes possible. Hereinafter, the cleaning web according to the present invention will be described in more detail.
本発明のクリーニングウェブは、表面粗さの小さい方の面（以下「Ｒａ１面」とする）の表面粗さＲａ１が１．０μｍ以下であり、表面粗さの大きい方の面（以下「Ｒａ２面」とする）の表面粗さＲａ２が２．５μｍ以下であることを特徴としている。ここにおいて、Ｒａ１面の表面粗さＲａ１が１．０μｍ以下であることにより、その面において従来よりも優れた拭き取り効果が得られ、また、Ｒａ２の面の表面粗さＲａ２が２．５μｍ以下であることにより、その面において、従来のクリーニングウェブと同等の拭き取り効果が得られることになる。 In the cleaning web of the present invention, the surface roughness Ra1 of the surface with the smaller surface roughness (hereinafter referred to as “Ra1 surface”) is 1.0 μm or less, and the surface with the larger surface roughness (hereinafter referred to as “Ra2 surface”). The surface roughness Ra2 is “2.5 μm or less”. Here, when the surface roughness Ra1 of the Ra1 surface is 1.0 μm or less, a wiping effect superior to that of the conventional surface can be obtained on the surface, and the surface roughness Ra2 of the surface of Ra2 is 2.5 μm or less. As a result, the same wiping effect as that of the conventional cleaning web can be obtained.
また、Ｒａ１面の表面粗さＲａ１とＲａ２面の表面粗さＲａ２との差は、好ましくは０．７μｍ以上であり、より好ましくは、１．０μｍ以上である。Ｒａ１とＲａ２との差が０．７μｍ以上である場合は、クリーニングウェブの用途に応じて拭き取りの程度を変更するために、クリーニングウェブの表裏を入れ替えて対応するという観点からして、非常に有効なものとなる。 The difference between the surface roughness Ra1 of the Ra1 surface and the surface roughness Ra2 of the Ra2 surface is preferably 0.7 μm or more, and more preferably 1.0 μm or more. When the difference between Ra1 and Ra2 is 0.7 μm or more, it is very effective from the viewpoint of changing the front and back of the cleaning web in order to change the degree of wiping according to the usage of the cleaning web. It will be something.
本発明のクリーニングウェブには、セルロース繊維、合成繊維等、任意の繊維を使用することができ、それを単独で、もしくは、２種類以上混合して使用することができる。ここで用いるセルロース繊維としては、木材パルプと非木材パルプとを例示することができる。 Arbitrary fibers, such as a cellulose fiber and a synthetic fiber, can be used for the cleaning web of this invention, It can be used individually or in mixture of 2 or more types. As a cellulose fiber used here, wood pulp and non-wood pulp can be illustrated.
木材パルプは、広葉樹、針葉樹を公知の方法で蒸解して得られるパルプである。これらの木材原料を単独で、あるいは、２種以上混合して使用することができる。但し、広葉樹パルプには柔細胞が含まれていて、この柔細胞が定着ロール拭取り時における紙粉発生の原因となりやすい。そのため、本発明において用いる木材パルプとしては、針葉樹パルプを採用することが好ましい。 Wood pulp is pulp obtained by digesting hardwood and softwood by a known method. These wood raw materials can be used alone or in admixture of two or more. However, hardwood pulp contains parenchymal cells, which tend to cause paper dust when the fixing roll is wiped off. Therefore, it is preferable to employ softwood pulp as the wood pulp used in the present invention.
また、非木材パルプは、ケナフ、亜麻、***、マニラ麻、ジュート、サイザル麻、こうぞ、三椏等の非木材原料を公知の方法で蒸解して得られるパルプである。これらの非木材原料又は非木材パルプを単独で、あるいは、２種以上混合して使用することができるが、シートの拭取り性や、定着ロール拭取り時の加熱による強度劣化面を考慮して、靭皮繊維由来のパルプであるケナフパルプ、マニラ麻パルプ、ジュートパルプ、サイザル麻パルプを用いることが好ましい。その中でも、マニラ麻パルプはセルロースの重合度が高く、熱による強度劣化が少ないので、最も好ましい。 The non-wood pulp is a pulp obtained by digesting non-wood raw materials such as kenaf, flax, cannabis, manila hemp, jute, sisal hemp, gills, and three bases by a known method. These non-wood raw materials or non-wood pulp can be used alone or in admixture of two or more, but in consideration of sheet wiping properties and strength deterioration due to heating during fixing roll wiping It is preferable to use kenaf pulp, manila hemp pulp, jute pulp, sisal hemp pulp, which are pulps derived from bast fibers. Among them, Manila hemp pulp is most preferable because it has a high degree of polymerization of cellulose and little deterioration in strength due to heat.
木材パルプや非木材パルプは、トナーの被着体である定着シートに通常用いられる紙と同じ素材であるセルロースであり、トナーはセルロース繊維に定着しやすいように改良されているため、化学合成繊維と比べてトナーとの親和性が高く、そのために充分な拭取り効果が得られるものと考えられる。 Wood pulp and non-wood pulp are cellulose, which is the same material as paper normally used for fixing sheets that are adherends of toner, and the toner has been improved so that it can be easily fixed on cellulose fibers. Therefore, it is considered that the toner has a high affinity with the toner, and therefore, a sufficient wiping effect can be obtained.
合成繊維としては、ビスコースレーヨン、銅アンモニアレーヨン、ポリノジックなどの再生セルロース繊維、ポリエステル繊維、ポリオレフィン繊維、エチレン−酢酸ビニル共重合繊維、エチレン−ポリビニルアルコール共重合繊維、ポリビニルアルコール繊維、ポリ塩化ビニル繊維、ポリアミド繊維、ポリフェニレンサルファイド繊維、ポリアリレート繊維、ポリアミドイミド繊維、フェノール繊維などが例示される。その中では、耐熱性を有する繊維（ポリエチレンテレフタレート、ポリブチレンテレフタレート、全芳香族ポリエステル、全芳香族ポリアミド、ポリフェニレンサルファイド、ポリアリレート、ポリアミドイミド等）を使用することが好ましい。 Synthetic fibers include viscose rayon, copper ammonia rayon, polynosic and other regenerated cellulose fibers, polyester fibers, polyolefin fibers, ethylene-vinyl acetate copolymer fibers, ethylene-polyvinyl alcohol copolymer fibers, polyvinyl alcohol fibers, polyvinyl chloride fibers. And polyamide fiber, polyphenylene sulfide fiber, polyarylate fiber, polyamideimide fiber, phenol fiber and the like. Among them, it is preferable to use heat-resistant fibers (polyethylene terephthalate, polybutylene terephthalate, wholly aromatic polyester, wholly aromatic polyamide, polyphenylene sulfide, polyarylate, polyamideimide, etc.).
合成繊維を使用する場合は、熱水溶解性又は熱融着性のバインダー繊維を適宜使用することができる。熱水溶解性バインダー繊維としては、熱水溶解するポリビニルアルコール繊維が例示される。熱融着性のバインダー繊維としては、未延伸のポリエステル、共重合ポリエステル、ポリエチレン、エチレン−酢酸ビニル共重体合、エチレン−ポリビニルアルコール共重合体等の単独、もしくは、複合した繊維を使用することができる。これらの化学合成繊維の繊度は、２．５ｄｔｅｘ以下であることが好ましく、より好ましくは、１．０ｄｔｅｘ以下である。 When using synthetic fibers, hot water-soluble or heat-fusible binder fibers can be used as appropriate. Examples of the hot water-soluble binder fiber include polyvinyl alcohol fibers that dissolve in hot water. As the heat fusible binder fiber, it is possible to use unstretched polyester, copolymer polyester, polyethylene, ethylene-vinyl acetate copolymer, ethylene-polyvinyl alcohol copolymer alone or in combination. it can. The fineness of these chemically synthesized fibers is preferably 2.5 dtex or less, and more preferably 1.0 dtex or less.
本発明のクリーニングウェブは、木材パルプ、及び／又は、非木材パルプを５重量％以上含有することが好ましい。また、本発明のクリーニングウェブは、公知の製紙技術によって製造することができる。その製造に用いる抄紙機としては、円網式抄紙機、傾斜短網式抄紙機、長網式抄紙機、ツインワイヤー式抄紙機等を挙げることができるが、要求されるクリーニングウェブの幅方向の厚さのバラつきを考慮すると、円網式抄紙機を用いることが望ましい。 The cleaning web of the present invention preferably contains 5% by weight or more of wood pulp and / or non-wood pulp. The cleaning web of the present invention can be produced by a known papermaking technique. Examples of the paper machine used for the production include a circular net type paper machine, a slanted short net type paper machine, a long net type paper machine, and a twin wire type paper machine. Considering the thickness variation, it is desirable to use a circular net type paper machine.
本発明においてセルロース繊維を用いる場合の原料パルプの叩解度は、クリーニングウェブに求められる特性に応じて設定することができ、通常は３００ＣＳＦ〜６００ＣＳＦの間に調成される。本発明の場合、原料パルプの叩解は、マニラ麻パルプと木材パルプを混合して行ってもよいが、別々に叩解したパルプを混合することとしてもよい。また、合成繊維を用いる場合は、クリーニングウェブに求められる特性に応じて選択した繊維を水中で分散させた原料スラリーを用いる。その場合、分散助剤等の製紙用副資材を、適宜添加することができる In the present invention, the beating degree of the raw material pulp when cellulose fibers are used can be set according to the properties required for the cleaning web, and is usually adjusted between 300 CSF and 600 CSF. In the case of the present invention, the beating of the raw material pulp may be performed by mixing Manila hemp pulp and wood pulp, but may be performed by mixing the beaten pulp separately. Moreover, when using a synthetic fiber, the raw material slurry which disperse | distributed the fiber selected according to the characteristic calculated | required by the cleaning web in water is used. In that case, a papermaking auxiliary material such as a dispersion aid can be added as appropriate.
原料スラリーには、必要に応じ、ロジンサイズ剤等のサイズ剤、ポリアクリルアミド等の乾燥紙力増強剤、ポリアミド・ポリアミン・エピクロルヒドリンやメラミン樹脂等の湿潤紙力増強剤、硫酸バンド等の定着剤等の製紙用副資材を、適宜添加することができる。 For raw material slurry, sizing agent such as rosin sizing agent, drying paper strength enhancer such as polyacrylamide, wet paper strength enhancing agent such as polyamide, polyamine, epichlorohydrin and melamine resin, fixing agent such as sulfate band, etc. The papermaking auxiliary material can be added as appropriate.
本発明のクリーニングウェブは、公知の乾燥ドライヤーによって湿紙を乾燥して製造することができるが、ウェブに表裏差を付与できるヤンキードライヤーによって乾燥するようにすることが好ましい。そのようにすることで、表裏の表面粗さに差を有するクリーニングウェブを容易に製造することが可能となる。 The cleaning web of the present invention can be produced by drying wet paper with a known drying drier, but it is preferable that the cleaning web be dried with a Yankee drier capable of imparting a difference between the front and the back of the web. By doing so, it becomes possible to easily manufacture a cleaning web having a difference in surface roughness between the front and back surfaces.
また、クリーニングウェブの強度を向上させるために、サイズプレス装置等によって、スチレン系樹脂、スチレン・アクリル系樹脂、スチレン・マレイン酸樹脂、アルキルケテンダイマー、澱粉、酸化澱粉、ヒドロキシエチル化澱粉、カルボキシメチル化セルロース、カルボキシメチル化グアーガム、リン酸化グアーガム、酸化グアーガム、ポリビニルアルコール、ポリアクリルアミド等の薬品を塗工することとしてもよい。更に、本発明の表裏差の範囲を超えない範囲で、熱処理を行うこともできる。 In order to improve the strength of the cleaning web, a styrene resin, a styrene / acrylic resin, a styrene / maleic resin, an alkyl ketene dimer, starch, oxidized starch, hydroxyethylated starch, carboxymethyl, and the like can be obtained using a size press machine. It is good also as applying chemical | medical agents, such as chlorinated cellulose, carboxymethylated guar gum, phosphorylated guar gum, oxidized guar gum, polyvinyl alcohol, polyacrylamide. Furthermore, the heat treatment can also be performed within a range not exceeding the range of the front-back difference of the present invention.
本発明に係るクリーニングウェブは、２００℃雰囲気において２Ｎ／ｃｍ以上の引張強さを有するものである。２Ｎ／ｃｍ以上の引張強さがあれば、実用上問題なく使用することができるが、好ましくは３．５Ｎ／ｃｍ以上、更に好ましくは、７Ｎ／ｃｍ以上の引張強さを有するものとする。 The cleaning web according to the present invention has a tensile strength of 2 N / cm or more in a 200 ° C. atmosphere. If it has a tensile strength of 2 N / cm or more, it can be used practically without any problem, but preferably has a tensile strength of 3.5 N / cm or more, more preferably 7 N / cm or more.
本発明に係るクリーニングウェブは、２００℃雰囲気において１０％以下の破断伸びを有するものであることが好ましい。全芳香族ポリアミド繊維６０重量％と、延伸ポリエステル繊維５重量％と、未延伸ポリエステル繊維３５重量％とから成る不織布に熱圧加工を行って製造される従来のクリーニングウェブの場合は、２００℃雰囲気において熱可塑性樹脂であるポリエステルが軟化するために、４０％を超える破断伸びを示すことが確認された。これに対し、ＮＢＰＫとマニラ麻とを用いたシートの２００℃雰囲気における破断伸びは、５％以下であることが確認された。 The cleaning web according to the present invention preferably has a breaking elongation of 10% or less in a 200 ° C. atmosphere. In the case of a conventional cleaning web manufactured by subjecting a nonwoven fabric comprising 60% by weight of wholly aromatic polyamide fiber, 5% by weight of stretched polyester fiber, and 35% by weight of unstretched polyester fiber to 200 ° C. atmosphere It was confirmed that the polyester, which is a thermoplastic resin, softens, and thus exhibits a break elongation exceeding 40%. On the other hand, it was confirmed that the elongation at break in a 200 ° C. atmosphere of a sheet using NBPK and Manila hemp is 5% or less.
本発明のクリーニングウェブは、厚さが２０〜１２０μｍであって、厚さを幅方向に２ｃｍ間隔で測定したときの変動係数が、３．０％以下であることが望ましい。 The cleaning web of the present invention preferably has a thickness of 20 to 120 μm and a coefficient of variation of 3.0% or less when the thickness is measured at intervals of 2 cm in the width direction.
本発明のクリーニングウェブは、定着ロールに対して押圧することによりトナー等を払拭できるものであるが、クリーニングウェブにオイルを含有させると、クリーニングとオイル塗布を同時に行うことのできるクリーニングシートとすることができる。この場合のオイルとしては、トナーの離型性に優れるシリコーンオイルが好適であり、例えば、メチルシリコーンオイル、ジメチルシリコーンオイル、エチルシリコーンオイル、フェニルシリコーンオイル、アミノ変性シリコーンオイル、エポキシ変性シリコーンオイル、メルカプト変性シリコーンオイル、３
， ３ ， ３ − トリフロロプロピルシリコーンオイル等のシリコーンオイルを単独で、あるいは、その複数を混合したものを用いることができる。
The cleaning web of the present invention can wipe toner and the like by pressing against the fixing roll. However, when the cleaning web contains oil, the cleaning web can be cleaned and coated with oil simultaneously. Can do. As the oil in this case, a silicone oil excellent in toner releasability is suitable. For example, methyl silicone oil, dimethyl silicone oil, ethyl silicone oil, phenyl silicone oil, amino-modified silicone oil, epoxy-modified silicone oil, mercapto Modified silicone oil, 3
, 3, 3-Trifluoropropyl silicone oil or other silicone oils can be used alone, or a mixture thereof can be used.
なお、オイルの付着量はクリーニングウェブの厚さ等によって異なるが、１〜１００ｇ／ｍ２であることが好ましく、２〜６０ｇ／ｍ２であることがより好ましい。これは、２ｇ／ｍ２未満ではオイル塗布量が少なくなるおそれがあり、６０ｇ／ｍ２を超えると、定着ロールに塗布されないオイル量が多くなる可能性があるからである。また、オイルの粘度は、定着ロール表面におけるオイルの拡散性に優れるように、常温（２５℃）での粘度が１０〜５０，０００センチストークスであることが好ましい。 Incidentally, the adhesion amount of oil varies depending on the thickness or the like of the cleaning web is preferably 1 to 100 g / m 2, and more preferably 2~60g / m 2. This is because if the amount is less than 2 g / m 2 , the amount of oil applied may decrease, and if it exceeds 60 g / m 2 , the amount of oil not applied to the fixing roll may increase. Further, the viscosity of the oil is preferably 10 to 50,000 centistokes at room temperature (25 ° C.) so that the oil diffusibility on the surface of the fixing roll is excellent.
≪実施例１≫
３５０ＣＳＦに叩解したＮＢＫＰを８０重量％と、４５０ＣＳＦに叩解したマニラ麻パルプ２０重量％とを混合し、ロジン系サイズ剤０．２重量％、ポリアミドエピクロルヒドリン系湿潤紙力剤１．５重量％、硫酸バンド０．３重量％を順次添加混合して、紙料とした。この紙料を、円網ヤンキー式抄紙機を用いて坪量２３ｇ／ｍ２、厚さ４０μｍとなるよう抄造し、実施例１のクリーニングウェブを作成した。
Example 1
80% by weight of NBKP beaten in 350CSF and 20% by weight of Manila hemp pulp beaten in 450CSF are mixed, 0.2% by weight of rosin sizing agent, 1.5% by weight of polyamide epichlorohydrin wet paper strength agent, and a sulfate band 0.3% by weight was sequentially added and mixed to obtain a paper stock. This stock was made using a circular yankee type paper machine so as to have a basis weight of 23 g / m 2 and a thickness of 40 μm, and a cleaning web of Example 1 was prepared.
≪実施例２≫
３５０ＣＳＦに叩解したＮＢＫＰを５０重量％と、４５０ＣＳＦに叩解したマニラ麻パルプ５０重量％とを混合した以外は、実施例１と同様にして、実施例２のクリーニングウェブを作成した。
<< Example 2 >>
A cleaning web of Example 2 was prepared in the same manner as Example 1 except that 50% by weight of NBKP beaten to 350 CSF and 50% by weight of Manila hemp pulp beaten to 450 CSF were mixed.
≪比較例１≫
市販のアラミド繊維とポリエステル繊維とから成るクリーニングウェブを比較例１として、試験に供した。この市販のクリーニングウェブは、０．９ｄｔｅｘの全芳香族ポリアミド６０重量％と、３．３ｄｔｅｘの延伸ポリエステル繊維５重量％と、１．２ｄｔｅｘの未延伸ポリエステルを混合した乾式不織布を、４０μｍの厚さになるよう熱圧処理されたものであった。
≪Comparative example 1≫
A commercially available cleaning web made of aramid fibers and polyester fibers was used as Comparative Example 1 for the test. This commercially available cleaning web was prepared by mixing a dry nonwoven fabric obtained by mixing 60% by weight of a 0.9 dtex wholly aromatic polyamide, 5% by weight of 3.3 dtex of stretched polyester fiber, and 1.2 dtex of unstretched polyester with a thickness of 40 μm. It was what was hot-pressed to become.
＜表面粗さの測定＞
クリーニングウェブの表面粗さは、ＪＩＳ Ｂ０６０１（１９９４）に準じ、ミツトヨ製表面粗さ測定器ＳＪ−４０２を用い、クリーニングウェブの表面及び裏面をそれぞれ測定した。平滑でクリーニングウェブとして通常使用する面であって、表面粗さの小さいＲａ１面の表面粗さをＲａ１、表面粗さの大きいＲａ２面の表面粗さをＲａ２として示した。測定条件は、基準長さ５ｍｍ、測定速度０．５ｍｍ／秒、カットオフ値（λｃ）０．８ｍｍ、カットオフ値（λｓ）２．５μｍとした。
<Measurement of surface roughness>
The surface roughness of the cleaning web was measured according to JIS B0601 (1994) by using a Mitutoyo surface roughness measuring instrument SJ-402. The surface roughness of the Ra1 surface, which is smooth and normally used as a cleaning web, is indicated as Ra1, and the surface roughness of the Ra2 surface where the surface roughness is large is indicated as Ra2. The measurement conditions were a standard length of 5 mm, a measurement speed of 0.5 mm / second, a cutoff value (λc) of 0.8 mm, and a cutoff value (λs) of 2.5 μm.
実施例１、２及び比較例１のクリーニングウェブについて、常温（２５℃）での粘度が２５０ センチストークスのシリコーンオイルを、付着量が６．５ｇ／ｍ２となるよう含浸させ、市販のクリーニング機構を有する複写機（株式会社リコー製ｉｍａｇｉｏ ＭＰ５０００）のクリーニングウェブに供した。グレースケール４０％の濃度にて５，０００枚を連続印刷し、クリーニングウェブのトナーの付着の程度を、比較例１の表面粗さの小さいＲａ１面の場合よりもトナーによる着色の程度が濃い（クリーニングウェブの拭き取り性が良い）ものを○、比較例１の表面粗さの小さいＲａ１面の場合とトナーによる着色の程度が同等のものを△として評価した。 The cleaning webs of Examples 1 and 2 and Comparative Example 1 were impregnated with a silicone oil having a viscosity of 250 centistokes at room temperature (25 ° C.) so that the adhesion amount was 6.5 g / m 2. Was used for a cleaning web of a copier having the above (Imagio MP5000, manufactured by Ricoh Co., Ltd.). 5,000 sheets are continuously printed at a density of 40% gray scale, and the degree of toner adhesion on the cleaning web is darker than that of the Ra1 surface having a small surface roughness in Comparative Example 1 ( The case where the cleaning web had good wiping property was evaluated as ◯, and the case of the Ra1 surface having a small surface roughness in Comparative Example 1 and the coloration degree equivalent to the toner were evaluated as Δ.
この表から明らかなように、本発明による実施例１及び実施例２の場合は、表面粗さＲａ１が、比較例１のクリーニングウェブにおける表面粗さの小さいＲａ１面のＲａ１より小さいＲａ１面において、比較例１のＲａ１面よりも優れたクリーニング特性が得られたのみならず、表面粗さＲａ２が、比較例１のクリーニングウェブにおける表面粗さの小さいＲａ１面のＲａ１より大きいＲａ２面において、比較例１のＲａ１面と同等のクリーニング特性が得られることを確認することができ、これにより本発明の有用性、即ち、クリーニングウェブの用途に応じて拭き取りの程度を変更するために、単に、クリーニングウェブの表裏を入れ替えて対応することができることを確認することができた。 As is apparent from this table, in the case of Example 1 and Example 2 according to the present invention, the surface roughness Ra1 is smaller than the Ra1 surface of the Ra1 surface having a small surface roughness in the cleaning web of Comparative Example 1, Not only cleaning characteristics superior to the Ra1 surface of Comparative Example 1 were obtained, but also the surface roughness Ra2 was higher than Ra1 of the Ra1 surface having a smaller surface roughness in the cleaning web of Comparative Example 1, and was a comparative example. In order to change the degree of wiping depending on the usefulness of the present invention, that is, the use of the cleaning web, it can be confirmed that the cleaning web can be obtained simply by using the cleaning web. I was able to confirm that it was possible to respond by swapping the front and back.
Claims (7)