JP6195790B2 - Cleaning web for electrophotographic copier - Google Patents
Cleaning web for electrophotographic copier Download PDFInfo
- Publication number
- JP6195790B2 JP6195790B2 JP2013268878A JP2013268878A JP6195790B2 JP 6195790 B2 JP6195790 B2 JP 6195790B2 JP 2013268878 A JP2013268878 A JP 2013268878A JP 2013268878 A JP2013268878 A JP 2013268878A JP 6195790 B2 JP6195790 B2 JP 6195790B2
- Authority
- JP
- Japan
- Prior art keywords
- cleaning web
- cleaning
- pulp
- wood pulp
- web
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、電子写真複写機用クリーニングウェブに関するものであり、より詳細には、電子写真複写機の定着ロールなどの被清掃部材に付着したトナーを除去するためのクリーニングウェブに関する。 The present invention relates to a cleaning web for an electrophotographic copying machine, and more particularly to a cleaning web for removing toner adhering to a member to be cleaned such as a fixing roll of an electrophotographic copying machine.
電子写真複写機の定着ロールの表面に付着した残存トナー等の汚れを除去するために、定着ロールに、ロール巻きしたウェブ状の基材（クリーニングウェブ）を圧接して汚れを拭き取るウェブクリーニングが行われている。トナーとして定着性の余りよくない耐熱トナーを用いる場合、限られた電力（熱量）で高速複写する場合、あるいは、複写画像向上のためにトナーが微粒子化する場合等においては、定着ロール表面にトナーや紙粉が沈着する問題がより発生しやすい状況となる。 In order to remove dirt such as residual toner adhering to the surface of the fixing roll of the electrophotographic copying machine, web cleaning is performed by wiping the dirt by pressing the roll-shaped web-like substrate (cleaning web) against the fixing roll. It has been broken. When using heat-resistant toner that does not have a good fixability as the toner, when copying at high speed with limited power (heat amount), or when the toner becomes fine particles to improve the copy image, the toner on the surface of the fixing roll And the problem of depositing paper dust is more likely to occur.
定着ロールに押圧することによって、定着ロール表面に転写されたトナー及び紙粉を拭き取るクリーニングシートとしては、一般に、全芳香族ポリアミド繊維と未延伸ポリエステル繊維とを適宜配合した繊維ウェブを、熱カレンダーロールによって加熱加圧して製造した不織布が使用されている（特許文献１−３他）。 As a cleaning sheet for wiping off toner and paper powder transferred to the surface of the fixing roll by pressing the fixing roll, generally, a fiber web in which fully aromatic polyamide fibers and unstretched polyester fibers are appropriately blended is used as a thermal calendar roll. Non-woven fabric manufactured by heating and pressurizing by using (Patent Documents 1-3 and others).
しかるに、全芳香族ポリアミド繊維と未延伸ポリエステル繊維からなる不織布は、高温の定着ロールに晒されるため、熱可塑性樹脂であるポリエステルが軟化し、不織布が定着ロールに接している部分で不織布の伸びが発生し、充分にトナーを拭き取れないという欠点がある。また、全芳香族ポリアミド繊維は、耐熱性があって高温下で使用する場合には好ましいが、材質が硬いために定着ロール表面を摩耗させるおそれがある。 However, since the nonwoven fabric made of wholly aromatic polyamide fibers and unstretched polyester fibers is exposed to a high-temperature fixing roll, the polyester, which is a thermoplastic resin, softens, and the nonwoven fabric stretches at the portion where the nonwoven fabric is in contact with the fixing roll. There is a drawback that the toner is not sufficiently wiped off. Further, the wholly aromatic polyamide fiber has heat resistance and is preferable when used at a high temperature. However, since the material is hard, the surface of the fixing roll may be worn.
そこで本発明は、定着ロールの拭取り性を向上させる共に充分な耐熱性を有し、更に、定着ロール表面の摩耗を軽減し得るクリーニングウェブを提供することを課題とする。 Therefore, an object of the present invention is to provide a cleaning web that improves the wiping property of the fixing roll, has sufficient heat resistance, and can reduce wear on the surface of the fixing roll.
上記課題を解決するための請求項１に係る発明は、電子写真複写機における定着ローラ部分に付着したトナーをクリーニングするためのウェブであって、非木材パルプ５〜１００重量％と木材パルプ０〜９５重量％とから構成され、前記非木材パルプは、マニラ麻パルプその他の葉脈繊維由来のパルプであることを特徴とする電子写真複写機用クリーニングウェブである。 The invention according to claim 1 for solving the above problem is a web for cleaning toner adhering to a fixing roller portion in an electrophotographic copying machine, comprising 5 to 100% by weight of non-wood pulp and 0 to 0 of wood pulp. is composed of a 95 wt%, the non-wood pulp is an electrophotographic copying machine for cleaning web, wherein the pulp der Rukoto from Manila hemp pulp and other veins fibers.
好ましい実施形態における前記クリーニングウェブは、２００℃雰囲気において２Ｎ／ｃｍ以上の引張強さを有し、また、２００℃雰囲気において１０％以下の破断伸びを有し、更に、中心線平均粗さＲａが１．５μｍ以下の表面粗さを有するものとされる。 The cleaning web in a preferred embodiment has a tensile strength of 2 N / cm or more in a 200 ° C. atmosphere, has a breaking elongation of 10% or less in a 200 ° C. atmosphere, and further has a center line average roughness Ra. The surface roughness is 1.5 μm or less.
また、好ましい実施形態における前記クリーニングウェブは、その厚さが２０〜１２０μｍであって、厚さを幅方向に２ｃｍ間隔で測定したときの変動係数が３．０％以下である。 In the preferred embodiment, the cleaning web has a thickness of 20 to 120 μm and a coefficient of variation of 3.0% or less when the thickness is measured at intervals of 2 cm in the width direction.
また、好ましい実施形態においては、前記クリーニングウェブは、シリコーンオイルを含有する。 In a preferred embodiment, the cleaning web contains silicone oil.
本発明に係るクリーニングウェブは上記のとおりのものであって、従来のクリーニングウェブに用いられる全芳香族ポリアミド繊維に比べて柔軟な木材パルプや非木材パルプが用いられるために、定着ロール表面の摩耗を軽減することができ、また、非木材パルプは繊維径が細いために、木材パルプと混合されることでウェブ自身にも柔軟性が備わり、且つ、木材パルプや非木材パルプは全芳香族ポリアミド繊維やポリエステル繊維と比べてトナーとの親和性が高いために、充分な拭取り効果が得られ、更に、非木材パルプを５重量％以上含有することで、耐熱性を保有する効果がある。 The cleaning web according to the present invention is as described above, and since soft wood pulp and non-wood pulp are used as compared with wholly aromatic polyamide fibers used in conventional cleaning webs, the surface of the fixing roll is worn. In addition, since non-wood pulp has a thin fiber diameter, the web itself is flexible when mixed with wood pulp, and wood pulp and non-wood pulp are wholly aromatic polyamides. Since the affinity with the toner is higher than that of the fiber or the polyester fiber, a sufficient wiping effect can be obtained. Further, by containing 5% by weight or more of non-wood pulp, there is an effect of retaining heat resistance.
本発明に係る電子写真複写機の定着ローラ等の被清掃部材に付着したトナーを除去（クリーニング）するためのクリーニングウェブは、非木材パルプ５〜１００重量％と木材パルプ０〜９５重量％とから構成されることを特徴としている。そして、このクリーニングウェブは、定着ロール表面の摩耗を軽減しつつ、充分な拭取り性を有し、また、耐熱性を具備するものである。 A cleaning web for removing (cleaning) toner adhered to a member to be cleaned such as a fixing roller of an electrophotographic copying machine according to the present invention comprises 5 to 100% by weight of non-wood pulp and 0 to 95% by weight of wood pulp. It is characterized by being composed. The cleaning web has sufficient wiping properties and heat resistance while reducing wear on the surface of the fixing roll.
本発明に係るクリーニングウェブが上記のような優れた効果を発揮するのは、以下に述べる理由によるものと推測される。先ず、定着ロール表面の摩耗を軽減するとの作用効果は、本発明に係るクリーニングウェブに用いられる木材パルプや非木材パルプが、従来のクリーニングウェブに用いられる全芳香族ポリアミド繊維に比べて柔軟であることによってもたらされると考えられる。 The reason why the cleaning web according to the present invention exhibits such excellent effects is presumed to be as follows. First, the effect of reducing wear on the surface of the fixing roll is that the wood pulp and non-wood pulp used in the cleaning web according to the present invention are more flexible than the wholly aromatic polyamide fibers used in the conventional cleaning web. It is thought that it is brought about by.
また、拭取り性の向上効果は、本発明において用いられる非木材パルプは、繊維径が細いために、木材パルプと混合されることで、ウェブ自身にも柔軟性が備わることによってもたらされるものと考えられる。この点については更に、木材パルプや非木材パルプは、トナーの被着体である定着シートに通常用いられる紙と同じ素材であるセルロースであり、トナーはセルロース繊維に定着しやすいように改良されているため、全芳香族ポリアミド繊維やポリエステル繊維と比べてトナーとの親和性が高く、そのために充分な拭取り効果が得られるものと考えられる。 In addition, the non-wood pulp used in the present invention has an effect of improving wiping property because the web itself has flexibility by being mixed with wood pulp because the fiber diameter is thin. Conceivable. In this regard, wood pulp and non-wood pulp are cellulose, which is the same material as paper normally used for fixing sheets, which are adherends of toner, and the toner has been improved so that it can be easily fixed to cellulose fibers. Therefore, it is considered that the affinity with the toner is higher than that of the wholly aromatic polyamide fiber or the polyester fiber, so that a sufficient wiping effect can be obtained.
本発明に係るクリーニングウェブの場合、非木材パルプ５〜１００重量％及び木材パルプ０〜９５重量％から構成されることが重要である。それは、非木材パルプを５重量％以上含有することでクリーニングウェブの強度が向上し、高温になった定着ロールにクリーニングウェブを押圧した際に、ウェブの破断が抑制されるからである。 In the case of the cleaning web according to the present invention, it is important that the cleaning web is composed of 5 to 100% by weight of non-wood pulp and 0 to 95% by weight of wood pulp. This is because the strength of the cleaning web is improved by containing 5% by weight or more of non-wood pulp, and the web is prevented from being broken when the cleaning web is pressed against a fixing roll having a high temperature.
非木材パルプと木材パルプの配合比率は、非木材パルプ５〜１００重量％、木材パルプ０〜９５重量％であるが、好ましくは、非木材パルプ１０〜６０重量％、木材パルプ９０〜４０重量％とする。それは、非木材パルプを１０重量％以上配合することにより、大きな強度向上効果が得られ、一方、６０重量％を超えて配合した場合には、クリーニングウェブの地合の均一性が損なわれるおそれがあるからである。 The blending ratio of non-wood pulp and wood pulp is 5 to 100% by weight of non-wood pulp and 0 to 95% by weight of wood pulp, preferably 10 to 60% by weight of non-wood pulp and 90 to 40% by weight of wood pulp. And That is, a large strength improvement effect can be obtained by blending 10% by weight or more of non-wood pulp. On the other hand, when blending exceeds 60% by weight, the uniformity of the formation of the cleaning web may be impaired. Because there is.
本発明において用いる木材パルプは、広葉樹、針葉樹を公知の方法で蒸解して得られるパルプである。これらの木材原料を単独、あるいは、２種以上混合して使用することができる。但し、広葉樹パルプは柔細胞を含んでおり、この柔細胞が定着ロール拭取り時における紙粉発生の原因となりやすい。そのため、本発明において用いる木材パルプは、針葉樹パルプであることが好ましい。 The wood pulp used in the present invention is a pulp obtained by digesting hardwood and softwood by a known method. These wood raw materials can be used alone or in admixture of two or more. However, hardwood pulp contains parenchymal cells, which tend to cause paper dust when the fixing roll is wiped off. Therefore, it is preferable that the wood pulp used in the present invention is a softwood pulp.
一方、本発明において用いる非木材パルプは、ケナフ、亜麻、***、マニラ麻、ジュート、サイザル麻、こうぞ、三椏等の非木材原料を公知の方法で蒸解して得られるパルプである。これらの非木材原料もしくは非木材パルプを、単独あるいは２種以上混合して使用することができるが、シートの拭取り性や、定着ロール拭取り時の加熱による強度劣化面を考慮すると、靭皮繊維由来のパルプであるケナフパルプ、ジュートパルプ、あるいは、葉脈繊維由来のパルプであるマニラ麻パルプ、サイザル麻パルプを用いることが好ましい。その中でも、マニラ麻パルプはセルロースの重合度が高く、熱による強度劣化が少ないので、最も好ましいと言える。 On the other hand, the non-wood pulp used in the present invention is a pulp obtained by digesting non-wood raw materials such as kenaf, flax, cannabis, manila hemp, jute, sisal hemp, gills, and three bases by a known method. These non-wood raw materials or non-wood pulp can be used singly or as a mixture of two or more. However, considering the wiping property of the sheet and the deterioration of strength due to heating when wiping the fixing roll, bast It is preferable to use kenaf pulp, jute pulp, which is a fiber-derived pulp, or Manila hemp pulp or sisal hemp pulp, which is a pulp derived from leaf vein fibers. Among them, Manila hemp pulp is most preferable because it has a high degree of polymerization of cellulose and little strength deterioration due to heat.
本発明に係るクリーニングウェブは、公知の製紙技術によって製造することができる。その製造に用いる抄紙機としては、円網式抄紙機、傾斜短網式抄紙機、長網式抄紙機、ツインワイヤー式抄紙機等を挙げることができるが、要求されるクリーニングウェブの幅方向の厚さのバラつきを考慮すると、円網式抄紙機を用いることが望ましい。 The cleaning web according to the present invention can be manufactured by a known papermaking technique. Examples of the paper machine used for the production include a circular net type paper machine, a slanted short net type paper machine, a long net type paper machine, and a twin wire type paper machine. Considering the thickness variation, it is desirable to use a circular net type paper machine.
原料パルプの叩解度は、クリーニングウェブに求められる特性に応じて設定することができ、通常は３００ＣＳＦ〜６００ＣＳＦの間に調成される。本発明の場合、原料パルプの叩解は、マニラ麻パルプと木材パルプを混合して行ってもよいが、別々に叩解したパルプを混合することとしてもよい。原料パルプには、必要に応じ、ロジンサイズ剤等のサイズ剤、ポリアクリルアミド等の乾燥紙力増強剤、ポリアミド・ポリアミン・エピクロルヒドリンやメラミン樹脂等の湿潤紙力増強剤、硫酸バンドその他の定着剤等の製紙用副資材を、適宜添加することができる。 The beating degree of the raw material pulp can be set according to the characteristics required for the cleaning web, and is usually prepared between 300 CSF and 600 CSF. In the case of the present invention, the beating of the raw material pulp may be performed by mixing Manila hemp pulp and wood pulp, but may be performed by mixing the beaten pulp separately. For raw material pulp, sizing agent such as rosin sizing agent, drying paper strength enhancer such as polyacrylamide, wet paper strength enhancing agent such as polyamide, polyamine, epichlorohydrin and melamine resin, sulfuric acid band and other fixing agents, as required The papermaking auxiliary material can be added as appropriate.
また、クリーニングウェブの強度を向上させるために、サイズプレス装置等によって、スチレン系樹脂、スチレン・アクリル系樹脂、スチレン・マレイン酸樹脂、アルキルケテンダイマー、澱粉、酸化澱粉、ヒドロキシエチル化澱粉、カルボキシメチル化セルロース、カルボキシメチル化グアーガム、リン酸化グアーガム、酸化グアーガム、ポリビニルアルコール、ポリアクリルアミド等の薬品を塗工することとしてもよい。 In order to improve the strength of the cleaning web, a styrene resin, a styrene / acrylic resin, a styrene / maleic resin, an alkyl ketene dimer, starch, oxidized starch, hydroxyethylated starch, carboxymethyl, and the like can be obtained using a size press machine. It is good also as applying chemical | medical agents, such as chlorinated cellulose, carboxymethylated guar gum, phosphorylated guar gum, oxidized guar gum, polyvinyl alcohol, polyacrylamide.
本発明に係るクリーニングウェブは、２００℃雰囲気において２Ｎ／ｃｍ以上の引張強さを有するものとする。２Ｎ／ｃｍ以上の引張強さがあれば、実用上問題なく使用することができるが、好ましくは３．５Ｎ／ｃｍ以上、更に好ましくは、７Ｎ／ｃｍ以上の引張強さを有するものとする。 The cleaning web according to the present invention has a tensile strength of 2 N / cm or more in a 200 ° C. atmosphere. If it has a tensile strength of 2 N / cm or more, it can be used practically without any problem, but preferably has a tensile strength of 3.5 N / cm or more, more preferably 7 N / cm or more.
また、本発明に係るクリーニングウェブは、２００℃雰囲気において１０％以下の破断伸びを有するものであることが好ましい。全芳香族ポリアミド繊維６０重量％と、延伸ポリエステル繊維５重量％と、未延伸ポリエステル繊維３５重量％とから成る不織布に熱圧加工を行った従来のクリーニングウェブの場合は、２００℃雰囲気において熱可塑性樹脂であるポリエステルが軟化するために、４０％を超える破断伸びを示すことが確認された。これに対し、木材パルプにＮＢＰＫを用い、非木材パルプにマニラ麻を用いたシートの場合の２００℃雰囲気における破断伸びは、５％以下であることが確認された。 In addition, the cleaning web according to the present invention preferably has a breaking elongation of 10% or less in an atmosphere at 200 ° C. In the case of a conventional cleaning web obtained by hot pressing a non-woven fabric composed of 60% by weight of wholly aromatic polyamide fiber, 5% by weight of stretched polyester fiber, and 35% by weight of unstretched polyester fiber, thermoplasticity in an atmosphere at 200 ° C. It was confirmed that the polyester, which is a resin, softens, and thus exhibits an elongation at break exceeding 40%. On the other hand, it was confirmed that the elongation at break in a 200 ° C. atmosphere was 5% or less in the case of a sheet using NBPK for wood pulp and manila hemp for non-wood pulp.
更に、本発明のクリーニングウェブの表面粗さは、中心線平均粗さＲａが１．５μｍ以下であることが好ましい。通常、クリーニングウェブは、表面粗さが小さいほど拭き取り性が向上するが、その反面、拭き取りの耐久性（拭き取り回数）が低下する。クリーニングウェブは、その使用方法によっては耐久性が必要とされる場合がある。従来のカレンダー処理されたクリーニングウェブの場合、その要請に応えるためには、密度を低くして空隙率を高くする必要があった。しかし、密度を低くすると、表面粗さが大きくなるために拭き取り性能が低下し、また、強度も低下するという問題が起こる。即ち、従来のクリーニングウェブの場合は、拭き取り性と拭き取り耐久性とを両立させることに限界があった。 Further, the surface roughness of the cleaning web of the present invention is preferably such that the center line average roughness Ra is 1.5 μm or less. Usually, the smaller the surface roughness of the cleaning web, the better the wiping property, but on the other hand, the wiping durability (the number of wiping operations) decreases. The cleaning web may be required to have durability depending on how it is used. In the case of a conventional calendered cleaning web, it was necessary to reduce the density and increase the porosity in order to meet the demand. However, when the density is lowered, the surface roughness increases, so that the wiping performance is lowered and the strength is also lowered. That is, in the case of the conventional cleaning web, there was a limit in achieving both wiping performance and wiping durability.
しかるに、本発明に係るクリーニングウェブの場合は、クリーニングウェブの空隙率を高くすることなく拭き取り耐久性が良好となり、且つ、表面粗さが小さいために拭き取り性に優れたクリーニングウェブとなる。 However, in the case of the cleaning web according to the present invention, the wiping durability is good without increasing the porosity of the cleaning web, and the surface roughness is small, so that the cleaning web is excellent in wiping property.
本発明のクリーニングウェブは、厚さが２０〜１２０μｍであって、厚さを幅方向に２ｃｍ間隔で測定したときの厚さの変動係数が３．０％以下であり、式（１）によって得られる地合い係数が２．０以下であることが望ましい。厚さの変動係数が３．０％以上もしくは地合い係数が２．０以上であると、定着ロールの拭き取り時に拭き取りムラが発生しやすくなる。
（式１）地合い係数＝地合い指数÷平均透過率
The cleaning web of the present invention has a thickness of 20 to 120 μm, and has a coefficient of variation of thickness of 3.0% or less when the thickness is measured at intervals of 2 cm in the width direction. It is desirable that the formed texture coefficient is 2.0 or less. When the variation coefficient of thickness is 3.0% or more or the texture coefficient is 2.0 or more, wiping unevenness is likely to occur when the fixing roll is wiped.
(Formula 1) Ground coefficient = ground index / average transmittance
＜地合い係数の測定＞
クリーニングウェブの地合いを、下記の測定機器及び測定ソフトウェアを用い、読み取り部の測定範囲を流れ方向１８ｃｍ、幅方向２５ｃｍとして測定を行った。測定により得られた地合い指数は、ウェブの厚さに起因する光の透過の影響を受けるため、式１に示すように地合い指数を平均透過率で除し、地合い係数として評価した。
測定機器：野村商事（株）製フォーメーションテスターＦＭＴ−ＭＩＩＩ
ソフトウェア：ＦＭＴ−ＭＩＩＩ ｖｅｒ２．７
測定範囲：流れ方向１８ｃｍ、幅方向２５ｃｍ
<Measurement of ground coefficient>
The texture of the cleaning web was measured using the following measuring equipment and measurement software, with the reading unit measuring range of 18 cm in the flow direction and 25 cm in the width direction. Since the texture index obtained by the measurement is affected by light transmission caused by the thickness of the web, the texture index was divided by the average transmittance as shown in Equation 1 and evaluated as a texture coefficient.
Measuring equipment: Formation tester FMT-MIII manufactured by Nomura Corporation
Software: FMT-MIII ver2.7
Measurement range: 18cm in the flow direction, 25cm in the width direction
本発明のクリーニングウェブは、定着ロールに対して押圧することにより、トナー等を払拭できるものであるが、クリーニングウェブにオイルを含有させると、クリーニングとオイル塗布を同時に行うことのできるクリーニングシートとすることができる。ここで用いるオイルとしては、トナーの離型性に優れるシリコーンオイルが好適であり、例えば、メチルシリコーンオイル、ジメチルシリコーンオイル、エチルシリコーンオイル、フェニルシリコーンオイル、アミノ変性シリコーンオイル、エポキシ変性シリコーンオイル、メルカプト変性シリコーンオイル、３
， ３ ， ３ − トリフロロプロピルシリコーンオイル等のシリコーンオイルを単独で、又は混合して用いることができる。
The cleaning web of the present invention can wipe toner and the like by pressing against the fixing roll. However, when the cleaning web contains oil, the cleaning web can be cleaned and coated with oil simultaneously. be able to. As the oil used here, a silicone oil excellent in toner releasability is suitable. For example, methyl silicone oil, dimethyl silicone oil, ethyl silicone oil, phenyl silicone oil, amino-modified silicone oil, epoxy-modified silicone oil, mercapto Modified silicone oil, 3
Silicone oil such as, 3, 3-trifluoropropyl silicone oil can be used alone or in combination.
なお、オイルの付着量はクリーニングウェブの厚さなどによって異なるが、１〜１
０ ０ ｇ ／ ｍ２であることが好ましく、より好ましくは２〜６０ｇ／ｍ２である。それが２ｇ／ｍ２未満ではオイル塗布量が少なくなり、６０ｇ／ｍ２を超えると定着ロールに塗布されないオイル量が多くなる。また、オイルの粘度は、定着ロール表面におけるオイルの拡散性に優れるように、常温（２５℃）での粘度が１
０ 〜 ５０ ， ０ ０ ０ センチストークスであることが好ましい。
In addition, although the adhesion amount of oil changes with thickness of a cleaning web, etc., it is 1-1.
It is preferably 0 0 g / m 2 , more preferably 2 to 60 g / m 2 . If it is less than 2 g / m 2 , the amount of oil applied decreases, and if it exceeds 60 g / m 2 , the amount of oil not applied to the fixing roll increases. The viscosity of the oil is 1 at room temperature (25 ° C.) so that the oil diffusibility on the surface of the fixing roll is excellent.
It is preferably 0 to 50, 0 0 0 centistokes.
＜表面粗さの測定＞
クリーニングウェブの表面粗さは、ＪＩＳ Ｂ０６０１（１９９４）に準じ、ミツトヨ製表面粗さ測定器ＳＪ−４０２を用い、クリーニングウェブの表面及び裏面をそれぞれ測定した。平滑で、クリーニングウェブとして通常使用する面であって表面粗さの小さい方をＲａ１、表面粗さの大きい方をＲａ２とした。測定条件は、基準長さ５ｍｍ、測定速度０．５ｍｍ／秒、カットオフ値（λｃ）０．８ｍｍ、カットオフ値（λｓ）２．５μｍとした。
<Measurement of surface roughness>
The surface roughness of the cleaning web was measured according to JIS B0601 (1994) by using a Mitutoyo surface roughness measuring instrument SJ-402. A smooth surface that is normally used as a cleaning web and having a smaller surface roughness was designated as Ra1, and a surface having a larger surface roughness was designated as Ra2. The measurement conditions were a standard length of 5 mm, a measurement speed of 0.5 mm / second, a cutoff value (λc) of 0.8 mm, and a cutoff value (λs) of 2.5 μm.
≪実施例１≫
３５０ＣＳＦに叩解したＮＢＫＰを８０重量％と、４５０ＣＳＦに叩解したマニラ麻パルプ２０重量％とを混合し、ロジン系サイズ剤０．２重量％、ポリアミドエピクロルヒドリン系湿潤紙力剤１．５重量％、硫酸バンド０．３重量％を順次添加混合して、紙料とした。この紙料を、円網抄紙機を用いて坪量２３ｇ／ｍ２、厚さ４０μｍとなるように抄造し、実施例１のクリーニングウェブを作成した。
Example 1
80% by weight of NBKP beaten in 350CSF and 20% by weight of Manila hemp pulp beaten in 450CSF are mixed, 0.2% by weight of rosin sizing agent, 1.5% by weight of polyamide epichlorohydrin wet paper strength agent, and a sulfate band 0.3% by weight was sequentially added and mixed to obtain a paper stock. This stock was made using a circular paper machine so that the basis weight was 23 g / m 2 and the thickness was 40 μm, and the cleaning web of Example 1 was prepared.
≪実施例２≫
３５０ＣＳＦに叩解したＮＢＫＰを５０重量％と、４５０ＣＳＦに叩解したマニラ麻パルプ５０重量％とを混合した以外は、実施例１と同様にして、実施例２のクリーニングウェブを作成した。
<< Example 2 >>
A cleaning web of Example 2 was prepared in the same manner as Example 1 except that 50% by weight of NBKP beaten to 350 CSF and 50% by weight of Manila hemp pulp beaten to 450 CSF were mixed.
≪比較例１≫
３５０ＣＳＦに叩解したＮＢＫＰのみを使用した以外は、実施例１と同様にして、比較例１のクリーニングウェブを作成した。
≪Comparative example 1≫
A cleaning web of Comparative Example 1 was prepared in the same manner as Example 1 except that only NBKP beaten to 350 CSF was used.
≪比較例２≫
市販のアラミド繊維とポリエステル繊維とからなるクリーニングウェブを比較例２として、試験に供した。このクリーニングウェブは、０．９デシテックスの全芳香族ポリアミド６０重量％と、３．３デシテックスの延伸ポリエステル繊維５重量％と、１．２デシテックスの未延伸ポリエステルを混合した乾式不織布を、４０μｍの厚さになるよう熱圧処理したものであった。
≪Comparative example 2≫
A commercially available cleaning web composed of aramid fibers and polyester fibers was used as Comparative Example 2 for the test. This cleaning web was prepared by mixing a dry nonwoven fabric prepared by mixing 60% by weight of 0.9 dtex total aromatic polyamide, 5% by weight of 3.3 dtex stretched polyester fiber, and 1.2 dtex unstretched polyester with a thickness of 40 μm. It was what was hot-pressed so that it might be.
比較例１は、３５０ＣＳＦに叩解したＮＢＫＰのみを使用したため、２００℃雰囲気において大きく引張強さが低下した。比較例２は、アラミド繊維とポリエステル繊維とから成るものであるため、２００℃雰囲気における破断伸びが４０％以上にも達した。 Since Comparative Example 1 used only NBKP beaten to 350 CSF, the tensile strength was greatly reduced in an atmosphere of 200 ° C. Since the comparative example 2 consists of an aramid fiber and a polyester fiber, the breaking elongation in a 200 degreeC atmosphere reached even 40% or more.
実施例１、２及び比較例１、２のクリーニングウェブについて、それぞれ表面粗さの小さい方の面（Ｒａ１面）を用い、常温（２５℃）での粘度が２５０ センチストークスのシリコーンオイルを、付着量が６．５ｇ／ｍ２となるよう含浸させ、市販のクリーニング機構を有する複写機（株式会社リコー製ｉｍａｇｉｏ ＭＰ５０００）のクリーニングウェブに供した。 For the cleaning webs of Examples 1 and 2 and Comparative Examples 1 and 2, a surface having a smaller surface roughness (Ra1 surface) was used, and a silicone oil having a viscosity of 250 centistokes at room temperature (25 ° C.) was attached. It was impregnated so as to have an amount of 6.5 g / m 2, and used for a cleaning web of a copying machine having a commercially available cleaning mechanism (Imagio MP5000 manufactured by Ricoh Co., Ltd.).
そして、グレースケール４０％の濃度にて５，０００枚を連続印刷し、クリーニングウェブのトナーの付着の程度を評価した。その評価は、比較例２よりも、トナーによる着色の程度が濃い（クリーニングウェブの拭き取り性が良い）ものを○、比較例２とトナーによる着色の程度が同等のものを△とする方法によって行った。その結果は、表１に示すとおり、本発明に係る実施例１と実施例２の場合は○の評価であったのに対し、比較例１と比較例２の場合は△の評価であった。 Then, 5,000 sheets were continuously printed at a density of 40% gray scale, and the degree of toner adhesion on the cleaning web was evaluated. The evaluation was carried out by a method in which the coloration with the toner was darker than that of Comparative Example 2 (the cleaning web had good wiping property), and the coloration with the same coloration level as in Comparative Example 2 and the toner was Δ. It was. As shown in Table 1, the results were evaluated as “good” in the case of Example 1 and Example 2 according to the present invention, whereas in the case of Comparative Example 1 and Comparative Example 2, the result was “Δ”. .
この試験結果から、木材パルプと非木材パルプから成る本発明に係るクリーニングウェブは、非木材パルプを含むために、定着ロールの熱による強度低下と破断伸びの上昇を抑えることができて、クリーニングウェブへのトナーの付着の程度が多い、即ち、定着ロールに対するクリーニング特性の優れたクリーニングウェブであることを確認することができた。 From this test result, the cleaning web according to the present invention made of wood pulp and non-wood pulp contains non-wood pulp, so that it is possible to suppress a decrease in strength due to heat of the fixing roll and an increase in elongation at break. It was confirmed that the cleaning web had a high degree of toner adhesion to the toner, that is, excellent cleaning characteristics for the fixing roll.
Claims (6)