JP6140833B2 - 多層光学フィルム、その製造方法およびこれを含む偏光板 - Google Patents
多層光学フィルム、その製造方法およびこれを含む偏光板 Download PDFInfo
- Publication number
- JP6140833B2 JP6140833B2 JP2015541709A JP2015541709A JP6140833B2 JP 6140833 B2 JP6140833 B2 JP 6140833B2 JP 2015541709 A JP2015541709 A JP 2015541709A JP 2015541709 A JP2015541709 A JP 2015541709A JP 6140833 B2 JP6140833 B2 JP 6140833B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- optical film
- film layer
- multilayer optical
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
[式2] Rth=(nz−ny)× d
上記[式1]及び[式2]において、
nxは、光学フィルムの面方向屈折率のうち最大の屈折率であり、
nyは、光学フィルムの面方向屈折率のうちnxと垂直な方向の屈折率であり、
nzは、厚さ方向の屈折率であり、
dは、フィルムの厚さである。
(1)樹脂組成物の製造
メチルメタクリレート92重量部、N−フェニルマルレイミド5重量部、α−メチルスチレン2重量部及びメタクリレート1重量部で構成された単量体混合物1000gを準備して、5リットルの反応器に蒸留水2000g、5%ポリビニルアルコール溶液8.4g(POVAL PVA217、Kuraray社)、ホウ酸0.1g、n−オクチルメルカプタン2.5g及び2,2’−アゾビスイソブチロニトリル1.5gと混合して、400rpmで攪拌しながら水相に分散させた。
次に、上記樹脂組成物100重量部にトリアジン系紫外線吸収剤(Tinuvin−1577、BASF社)1重量部を入れて、固体ミキサー(Solid Mixer)で2分間混合した後、上記原料混合物を原料ホッパー(hopper)から第2押出機までを窒素置換した24φの押出機に供給して260℃で溶融し、原料ペレット(pellet)を製造した。
製造例1において、同一の組成及び方法で樹脂組成物を製造した。
製造例1において、同一の組成及び方法で樹脂組成物を製造した。
製造例1において、同一の組成及び方法で樹脂組成物を製造した。
製造例2において、同一の組成及び方法で樹脂組成物を製造した。
製造例1において、アクリロニトリル及びスチレン共重合体樹脂ペレット(82TR,LG Chem.)を用いたこと以外には、同一の方法で樹脂組成物を製造した。
製造例1において、ポリカーボネート樹脂ペレット(LUPOY,LG Chem.)を用いたこと以外には、同一の方法で樹脂組成物を製造した。
製造例1において、同一の組成及び方法で樹脂組成物を製造した。
製造例1によって製造された原料ペレットを80℃で6時間熱風乾燥し、260℃で第2押出機で溶融して、第1フィルム層及び第3フィルム層を形成した。また、製造例2によって製造された原料ペレットを80℃で6時間熱風乾燥し、265℃で第1押出機で溶融して、第2フィルム層を形成した。
実施例1において、製造例2によって製造された原料ペレットを用いて第1フィルム層及び第3フィルム層を形成し、製造例1によって製造された原料ペレットを用いて第2フィルム層を形成したこと以外には、同一の方法で厚さ54μmの多層光学フィルムを製造した。
実施例1において、製造例1によって製造された原料ペレットを用いて第1フィルム層及び第3フィルム層を形成し、製造例3によって製造された原料ペレットを用いて第2フィルム層を形成したこと以外には、同一の方法で厚さ55μmの多層光学フィルムを製造した。
実施例1において、製造例1によって製造された原料ペレットを用いて第1フィルム層及び第3フィルム層を形成し、製造例5によって製造された原料ペレットを用いて第2フィルム層を形成したこと以外には、同一の方法で厚さ58μmの多層光学フィルムを製造した。
実施例1において、製造例2によって製造された原料ペレットを用いて第1フィルム層及び第3フィルム層を形成し、製造例3によって製造された原料ペレットを用いて第2フィルム層を形成したこと以外には、同一の方法で厚さ53μmの多層光学フィルムを製造した。
実施例1において、製造例2によって製造された原料ペレットを用いて第1フィルム層及び第3フィルム層を形成し、製造例4によって製造された原料ペレットを用いて第2フィルム層を形成したこと以外には、同一の方法で厚さ54μmの多層光学フィルムを製造した。
実施例1において、製造例4によって製造された原料ペレットを用いて第1フィルム層及び第3フィルム層を形成したこと以外には、同一の方法で厚さ57μmの多層光学フィルムを製造した。
実施例1において、製造例6によって製造された原料ペレットを用いて第1フィルム層及び第3フィルム層を形成したこと以外には、同一の方法で厚さ54μmの多層光学フィルムを製造した。
実施例1において、製造例7によって製造された原料ペレットを用いて第1フィルム層及び第3フィルム層を形成したこと以外には、同一の方法で厚さ52μmの多層光学フィルムを製造した。
実施例1において、第1フィルム層ないし第3フィルム層をいずれも製造例2によって製造された原料ペレットを用いて形成したこと以外には、同一の方法で厚さ52μmの多層光学フィルムを製造した。
実施例1において、製造例8によって製造された原料ペレットを第1押出機を用いてフィルムを形成したことを除いては、同一の方法で厚さ51μmの単層光学フィルムを製造した。
上記実施例1及び比較例1ないし10による多層光学フィルムの製造過程でロールの汚染有無を測定して、その結果を下記[表2]に示す。ロールの汚染有無は、フィルム成膜1時間後、キャスティングロールの表面を観察して、紫外線吸収剤による汚染度を肉眼で確認する方法で測定した。このとき、キャスティングロールの汚染度は、ロール表面を肉眼で観察したとき、濁った部分が存在する場合、「○」と表示し、ガラス面のようにきれいな状態を維持する場合、「×」と表示した。
上記実施例1及び比較例1ないし10による多層光学フィルムの製造過程でフィルムの外観不良の有無を測定して、その結果を下記[表2]に示す。フィルムの外観不良の測定は、キャスティングロールを経た上記光学フィルムに対して肉眼観察を通じてフィルムの外観不良の有無を確認する方法で行った。このとき、成膜されたフィルムの各層の間に波模様の不良が存在する場合、「×」と表示し、ガラス面のようにきれいな状態を維持する場合、「○」と表示した。
上記実施例1及び比較例1ないし10によって製造された光学フィルムに対して、直進光透過度を測定して、その結果を下記[表2]に示す。このとき、光学フィルムの直進光透過度は、UV−Visible Spectrophotometer(U−3310,Hitachi,Japan)を用いて、積分球を装着しない状態で測定した。
上記実施例1及び比較例1ないし10によって製造された光学フィルムに対して、フィルムの衝撃強度を測定して、その結果を下記[表2]に示す。このとき、上記衝撃強度は、Drop Impact Tester装備を用いて一定重さの金属ボールを落下させてフィルムが破断する高さを測定し、このように測定された高さに該当する位置エネルギーをフィルムの単位体積に換算して衝撃強度に変換した。
20 第2フィルム層
30 第3フィルム層
Claims (15)
- 熱可塑性アクリル系樹脂組成物100重量部に対して、
トリアジン系紫外線吸収剤0.01重量部以上2.0重量部未満を含む熱可塑性アクリル系樹脂組成物で形成された第1フィルム層;
トリアゾール系、ベンゾフェノン系、オキサニリド系及びシアノアクリル系紫外線吸収剤からなる群より選択された1種以上の紫外線吸収剤0.1重量部ないし5.0重量部を含む熱可塑性アクリル系樹脂組成物で形成された第2フィルム層;及び
トリアジン系紫外線吸収剤0.01重量部以上2.0重量部未満を含む熱可塑性アクリル系樹脂組成物で形成された第3フィルム層を含む多層光学フィルムであって、
前記第1フィルム層及び前記第3フィルム層の熱可塑性アクリル系樹脂組成物はトリアゾール系紫外線吸収剤を含まず、
各フィルム層を構成する熱可塑性アクリル系樹脂組成物のガラス転移温度の差は、2℃以下であり、
前記第1フィルム層及び第3フィルム層は、前記多層光学フィルムの厚さを60μmに換算して測定した場合、290nmの波長で直進光透過率が3%ないし12%であり、
前記第2フィルム層は、前記多層光学フィルムの厚さを60μmに換算して測定した場合、290nmの波長で直進光透過率が0.1%ないし7%であり、
前記多層光学フィルムは、前記多層光学フィルムの厚さを60μmに換算して測定した場合、290nmの波長で直進光透過率が0.01%ないし5%であり、
前記熱可塑性アクリル系樹脂組成物は、熱可塑性アクリル系樹脂が、共重合体100重量部を基準に70〜98重量部のアルキル(メタ)アクリレート系単位及び0.1〜10重量部のスチレン系単位を含む共重合体を含む、多層光学フィルム。 - 前記第1フィルム層及び第3フィルム層の紫外線吸収剤は、重量平均分子量が300ないし2000である請求項1に記載の多層光学フィルム。
- 前記第1フィルム層及び第3フィルム層は、光学フィルムの厚さを60μmに換算して測定した場合、380nmの波長で直進光透過率が10%ないし30%である請求項1に記載の多層光学フィルム。
- 前記第2フィルム層の紫外線吸収剤は、重量平均分子量が100ないし1000である請求項1に記載の多層光学フィルム。
- 前記第2フィルム層は、光学フィルムの厚さを60μmに換算して測定した場合、380nmの波長で直進光透過率が1%ないし15%である請求項1に記載の多層光学フィルム。
- 前記熱可塑性アクリル系樹脂組成物は、前記熱可塑性アクリル系樹脂が主鎖にカーボネート部を持つ芳香族系樹脂をさらに含むものである請求項1に記載の多層光学フィルム。
- 前記多層光学フィルムは、380nmの波長で紫外線透過率が0.1%ないし10%である請求項1に記載の多層光学フィルム。
- 前記多層光学フィルムは、第1フィルム層、第2フィルム層及び第3フィルム層を共押出したものである請求項1に記載の多層光学フィルム。
- 前記多層光学フィルムは、光学フィルムの厚さを60μmに換算して測定した場合、550nmの波長で直進光透過率が85%ないし100%である請求項1に記載の多層光学フィルム。
- 前記多層光学フィルムは、光学フィルムの厚さを60μmに換算して測定した場合、380nmの波長で直進光透過率が0.1%ないし15%である請求項1に記載の多層光学フィルム。
- 熱可塑性アクリル系樹脂組成物100重量部に対して、
トリアジン系紫外線吸収剤0.01重量部以上2.0重量部未満を含む熱可塑性アクリル系樹脂組成物で形成された第1フィルム層;
トリアゾール系、ベンゾフェノン系、オキサニリド系及びシアノアクリル系紫外線吸収剤からなる群より選択された1種以上の紫外線吸収剤0.1重量部ないし5.0重量部を含む熱可塑性アクリル系樹脂組成物で形成された第2フィルム層;及び
トリアジン系紫外線吸収剤0.01重量部以上2.0重量部未満を含む熱可塑性アクリル系樹脂組成物で形成された第3フィルム層を共押出するステップ、及び
前記共押出されたフィルムを延伸するステップを含む多層光学フィルムの製造方法であって、
前記第1フィルム層及び前記第3フィルム層の熱可塑性アクリル系樹脂組成物はトリアゾール系紫外線吸収剤を含まず、
各フィルム層を構成する熱可塑性アクリル系樹脂組成物のガラス転移温度の差は、2℃以下であり、
前記第1フィルム層及び第3フィルム層は、前記多層光学フィルムの厚さを60μmに換算して測定した場合、290nmの波長で直進光透過率が3%ないし12%であり、
前記第2フィルム層は、前記多層光学フィルムの厚さを60μmに換算して測定した場合、290nmの波長で直進光透過率が0.1%ないし7%であり、
前記多層光学フィルムは、前記多層光学フィルムの厚さを60μmに換算して測定した場合、290nmの波長で直進光透過率が0.01%ないし5%であり、
前記熱可塑性アクリル系樹脂組成物は、熱可塑性アクリル系樹脂が、共重合体100重量部を基準に70〜98重量部のアルキル(メタ)アクリレート系単位及び0.1〜10重量部のスチレン系単位を含む共重合体を含む、製造方法。 - 前記延伸するステップは、前記共押出されたフィルムを縦方向(MD)に1.3倍ないし3.5倍延伸するものである請求項11に記載の多層光学フィルムの製造方法。
- 前記延伸するステップは、前記共押出されたフィルムを横方向(TD)に1.3倍ないし3.5倍延伸するものである請求項11に記載の多層光学フィルムの製造方法。
- 前記延伸するステップは、前記多層光学フィルムの各フィルム層のうち最も高いガラス転移温度を有するフィルムのガラス転移温度+30℃以内の温度で延伸するものである請求項11に記載の多層光学フィルムの製造方法。
- 偏光子;及び
前記偏光子の少なくとも一面に備えられた保護フィルムを含む偏光板であって、
前記保護フィルムのうち少なくとも一つが、請求項1ないし10のいずれか一項に記載の多層光学フィルムである偏光板。