JP6130544B1 - 複合構造体の製造方法及び離型剤 - Google Patents
複合構造体の製造方法及び離型剤 Download PDFInfo
- Publication number
- JP6130544B1 JP6130544B1 JP2016072716A JP2016072716A JP6130544B1 JP 6130544 B1 JP6130544 B1 JP 6130544B1 JP 2016072716 A JP2016072716 A JP 2016072716A JP 2016072716 A JP2016072716 A JP 2016072716A JP 6130544 B1 JP6130544 B1 JP 6130544B1
- Authority
- JP
- Japan
- Prior art keywords
- release agent
- composite structure
- mold
- layer
- photocatalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
なお、上述した複合構造体の製造方法において、前記接合剤層形成工程は、前記離型剤層に対してスプレーガンにより前記接合剤を塗布することにより前記接合剤層を形成する工程であってもよいし、前記塗料層形成工程は、前記接合剤層に対してスプレーガンにより前記ウレタン塗料を塗布することにより前記塗料層を形成する工程であってもよい。
また、上述した複合構造体の製造方法においては、離型剤全体を100重量%としたときに、前記石油系溶剤は50重量%以上90重量%以下であり、前記ワックス系離型剤は10重量%以上40重量%以下であり、前記シリコン系離型剤は1重量%以上20重量%以下であり、前記灯油は、0.5重量%以上10重量%以下であるように構成してもよい。
本開示の他の態様は、光触媒を含有するポリウレタン組成物を形成する金型の表面に塗布される離型剤であって、前記離型剤が、石油系溶剤、ワックス系離型剤、シリコン系離型剤、及び灯油を含む、離型剤である。
本実施形態の複合構造体は、光触媒と、ポリウレタン樹脂と、を含む構造体である。複合構造体の製造には、少なくとも、離型剤、接合剤、光触媒、ウレタン樹脂塗料、ウレタン原料が用いられる。以下、これらについて詳細に説明する。
離型剤は、(i)石油系溶剤、(ii)ワックス系離型剤、(iii)シリコン系離型剤、及び、(iv)灯油及び軽油の少なくとも何れか一方、を含む。
また、JIS K 2201に記載される石油系溶剤を用いることができるが、その場合には、特に、4号及び5号に該当するソルベントが適している。
(iii)シリコン系離型剤は、特にその種類を限定されないが、市販されるシリコン形離型剤や、金型を用いた成型加工にて使用可能なシリコン系離型剤であればよい。
(iv)灯油は、例えば、JIS K2203にて規定される1号灯油を用いることができる。もちろん2号灯油であってもよい。なお、ケロシンを主成分とする(例えば90質量%以上含む)材料であってもよい。
なお、灯油と軽油の両方を用いてもよいし、いずれか一方のみを用いてもよい。
これら(i)〜(iv)は、以下のように配合することが望ましい。離型剤全体を100重量%としたときに、(i)は、50〜90重量%とすることができる。望ましくは60重量%以上、さらに望ましくは65重量%以上であり、また、望ましくは80重量%以下、さらに望ましくは75重量%以下である。
離型剤の配合を上記の範囲とすることにより、後述する取出工程において光触媒粒子の接合剤層からの脱落を抑制しつつ、スムーズな取り出しを実現することができる。
接合剤により形成される接合剤層は、光触媒を内包し、またポリウレタン組成物の最表面となる部分であるため、この接合剤層と下地のウレタン層との間の接合力は十分強固であることが必要である。
(1.3)光触媒
光触媒の構成は特に限定されない。例えば、酸化チタンを主成分とする一般的な光触媒材料を用いることができる。なお、光触媒は粒子として接合剤に配合される。なお接合剤の内部で凝集が起こり、凝集体が生成される可能性がある。凝集体の二次粒子径は0.5μm〜10μmの範囲としてもよい。また、10%粒子径と90%粒子径がこの範囲に含まれるような凝集体を形成する光触媒を用いてもよい。
ウレタン樹脂塗料は、ウレタン結合の骨格を持つ塗料であって、本体となるポリウレタンの表面を塗装するための塗料である。
(1.5)ウレタン原料
ウレタン原料は、ポリオール成分を有する第1原料と、イソシアネート成分を有する第2原料と、を含む。
[2.複合構造体の製造工程]
図1〜図9に基づいて、複合構造体の製造工程を説明する。なお図1〜図9では、金型1及び複合構造体7を、模式的な断面図として示している。
図1に示す金型1は、キャビティーが形成された下型3と、上型5と、を有しており、アルミ等の金属により形成される。この金型1が、樹脂形成用の型である。
続いて、スプレーガン11aにより、離型剤を塗布する。離型剤は、下型3のキャビティー内と、上型5における下型3と空洞を形成する部分と、に塗布される。スプレーガン11aによる塗布の後、ウエスにて塗布された離型剤が均一となるように拭き取りを行う。これにより、金型1の表面に離型剤層21が形成される。なお、スプレーガン11aはカップガンであり、以下の説明にて登場するスプレーガンも同様である。
図2に示すように、続いて、スプレーガン11bにより、離型剤層21の表面に接合剤を塗布する。但し、ここでは下型3のキャビティー内にのみ塗布する。これにより、離型剤層21上に接合剤層23が形成される。
図3に示すように、続いて、スプレーガン11cにより、下型3のキャビティー内に形成された接合剤層23の表面にウレタン樹脂塗料を塗布する。また、上型5における離型剤層21の表面にもウレタン樹脂塗料を塗布する。これにより、下型3のキャビティー内においては接合剤層23上にウレタン樹脂塗料を含む塗料層25が形成され、上型5では離型剤層21上に塗料層25が形成される。
図4に示すように、続いて、上型5の塗料層25の表面に、芯材27を配置する。この芯材27は、例えば金属により構成されたものを用いることができる。なお、芯材が不要であれば、本工程は行う必要はない。その場合、最終製品において芯材は含まれない。
図5に示すように、続いて、ウレタン注入機13からウレタン原料29を金型1に投入する。より具体的には、ウレタン原料29を下型3のキャビティー内に投入する。このときのウレタン原料29の温度は25℃とする。なお、20〜30℃の範囲において、加熱温度調整してもよい。
図6に示すように、続いて、ウレタン原料29を発泡させる。発泡時間は適宜調整することができるが、例えば30秒としてもよい。
(2.7)取出工程(脱型)
図7に示すように、続いて、金型1から光触媒を含有する生成物である複合構造体7を取り出す。複合構造体7は、図8に示すように、ウレタン層31の表面に、ウレタン層31側から順に塗料層25、接合剤層23、離型剤層21が形成されている。
上述したように、金型1から取り出した複合構造体7の表面には離型剤層21が形成されているため、離型剤層21を拭き取る。これにより、図9に示すように、芯材27側を除く表面の一部において光触媒が分散して配置された複合構造体7が生成される。
[3−1.実施例]
<実施例1>
離型剤として、(i)石油系溶剤を69.7重量%、(ii)ワックス系離型剤を22.5重量%、(iii)シリコン系離型剤を5.6重量%、(iv)灯油2.2重量%配合した。
また、複合構造体7は、表面に光触媒を強固に固定することができる。その理由は、C−Si−C,C−Si−O等の結合が接合剤層とウレタン樹脂塗料との間で形成されているためであると考えられる。
上記実施例1の離型剤における(i)の石油系溶剤の配合量を変更し、上述した製造工程により複合構造体を製造した。石油系溶剤の配合量を60重量%以上とすると、離型剤が積もることが抑制された。また石油系溶剤の配合量を80重量%以下とすると、薄くなり過ぎることなく、離型剤としての機能を十分に発揮することができた。なお、50重量%〜90重量%の範囲で、適当に製造を行うことができた。
離型剤として、上記実施例1の構成から石油系溶剤を除いた構成の離型剤を用い、上述した製造工程により複合構造体を製造した。この場合は、金型へ離型剤を塗布した際に、離型剤濃度が高すぎることにより、金型へ離型剤が積もり厚い層が形成された。これにより、脱型後に金型に離型剤が多く残ることとなるが、残った離型剤は厚さが不均一であるため金型の連続的に使用に適さず、金型の洗浄頻度が高くなってしまうという問題が生じた。
上記実施例1の離型剤における(ii)のワックス系離型剤の配合量を変更し、上述した製造工程により複合構造体を製造した。ワックス系離型剤の配合量を15重量%以上とすると、シリコンによるはじきを抑制でき、かつ金型から製品を取り出す際の十分な離型性を保つことができた。また、ワックス系離型剤の配合量を30重量%以下とすると、離型剤層が厚く積層してしまうことを抑制できた。なお、10〜40重量%の範囲で、十分な効果を奏した。
離型剤として、上記実施例の構成からワックス系離型剤を除いた構成の離型剤を用い、上述した製造工程により複合構造体を形成した。この場合は、離型剤塗布後、塗料を塗布する際に、金型表面が離型剤のシリコンの影響で塗料をはじいてしまい、接合剤層の形成や光触媒の分布に偏りが生じてしまうという問題が生じた。
上記実施例1の離型剤における(iii)のシリコン系離型剤の配合量を変更し、上述した製造工程により複合構造体を製造した。
離型剤として、上記実施例の構成からシリコン系離型剤を除いた構成の離型剤を用い、上述した製造工程により複合構造体を形成した。この場合は、脱型の際に光触媒及び接合剤層が金型に貼りつき、脱型が困難となった。また、金型へ多くの光触媒が残ってしまうという問題が生じた。
上記実施例1の離型剤における(iv)の灯油の配合量を変更し、上述した製造工程により複合構造体を製造した。灯油の配合量を0.5重量%以上とすると、十分な拭き取り性能を発揮できた。また灯油の配合量を5重量%以下とすると、灯油成分の残存による影響を低減できた。
離型剤として、上記実施例の構成から灯油を除いた構成の離型剤を用い、上述した製造工程により複合構造体を形成した。この場合は、塗布した離型剤をふき取る際に、その他の溶剤の揮発が早く、均一にふき取りが実施できないという問題が生じた。
(4a)複合構造体の製造工程において、本実施形態にて説明した離型剤による離型剤層を金型に形成することにより、光触媒の露出度が高く、また分散性の良い複合構造体を製造することができる。
(4b)複合構造体では、光触媒粒子はシランカップリング剤等により強固にウレタン樹脂塗料に接合される。よって、光触媒粒子の脱落を高度に抑制することができる。
[5.その他の実施形態]
以上本発明の実施形態について説明したが、本発明は、上記実施形態に何ら限定されることはなく、本発明の技術的範囲に属する限り種々の形態をとり得ることはいうまでもない。
また、離型剤層21、複合構造体7を構成する接合剤層23、塗料層25、ウレタン層31を構成する原材料は上記実施形態の組成に限定されず、配合の変更、他の原材料の追加など、適宜調整を行うことができる。また各層間に、上述した層以外の層や物質が配置されていてもよい。
Claims (6)
- 光触媒を含有する複合構造体の製造方法であって、
樹脂形成用の型の表面に、離型剤を含む離型剤層を形成する離型剤層形成工程と、
前記離型剤層形成工程にて形成された前記離型剤層上に、光触媒粒子を含有する接合剤を含む接合剤層を形成する接合剤層形成工程と、
前記接合剤層形成工程にて形成された前記接合剤層上に、ウレタン樹脂塗料を含む塗料層を形成する塗料層形成工程と、
ウレタン原料を、前記離型剤層形成工程から前記塗料層形成工程までの工程が行われた前記型の内部に投入する投入工程と、を備え、
前記接合剤は、シランカップリング剤、チタネートカップリング剤、及びシロキサン
を含む群から選択される少なくともいずれか1種を含み、
前記離型剤は、消防法の危険物第四類第1石油類に該当する石油系溶剤、ワックス系離型剤、シリコン系離型剤、並びに、灯油及び軽油のうち少なくともいずれか一方、を含む、複合構造体の製造方法。 - 請求項1に記載の複合構造体の製造方法であって、
前記接合剤層形成工程は、前記離型剤層に対してスプレーガンにより前記接合剤を塗布することにより前記接合剤層を形成する工程である、複合構造体の製造方法。 - 請求項1又は請求項2に記載の複合構造体の製造方法であって、
前記塗料層形成工程は、前記接合剤層に対してスプレーガンにより前記ウレタン樹脂塗料を塗布することにより前記塗料層を形成する工程である、複合構造体の製造方法。 - 請求項1から請求項3のいずれか1項に記載の複合構造体の製造方法であって、
離型剤全体を100重量%としたときに、前記石油系溶剤は50重量%以上90重量%以下であり、前記ワックス系離型剤は10重量%以上40重量%以下であり、前記シリコン系離型剤は1重量%以上20重量%以下であり、前記灯油は、0.5重量%以上10重量%以下である、複合構造体の製造方法。 - 請求項1から請求項4のいずれか1項に記載の複合構造体の製造方法であって、
前記複合構造体における光触媒粒子は、粒子径が0.5μm〜10μmの範囲である凝集体を形成している、複合構造体の製造方法。 - 光触媒を含有するポリウレタン組成物を形成する金型の表面に塗布される離型剤であって、
前記離型剤は、消防法の危険物第四類第1石油類に該当する石油系溶剤、ワックス系離型剤、シリコン系離型剤、及び灯油を含む、離型剤。