JP5960560B2 - 延伸フィルムの製造方法 - Google Patents
延伸フィルムの製造方法 Download PDFInfo
- Publication number
- JP5960560B2 JP5960560B2 JP2012199108A JP2012199108A JP5960560B2 JP 5960560 B2 JP5960560 B2 JP 5960560B2 JP 2012199108 A JP2012199108 A JP 2012199108A JP 2012199108 A JP2012199108 A JP 2012199108A JP 5960560 B2 JP5960560 B2 JP 5960560B2
- Authority
- JP
- Japan
- Prior art keywords
- stretching
- thermoplastic resin
- film
- stretched film
- resin film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
M≦55L−0.6 (1≦M、10≦L)・・・・・(1)
好ましい実施形態においては、上記同時二軸延伸機のクリップサイズ(D(mm))が下記式(2)を満たす。
5≦D≦30・・・・・(2)
好ましい実施形態においては、延伸温度が、上記熱可塑性樹脂フィルムのガラス転移温度(Tg)−10℃以上Tg+60℃以下である。
好ましい実施形態においては、上記TD延伸倍率(M(倍))と、MD収縮率(S(%))とが下記式(3)の関係を満たす。
S≧(1−1/√M)×100 (1≦M)・・・・・(3)
好ましい実施形態においては、上記熱可塑性樹脂フィルムが、MDに熱収縮可能な熱可塑性樹脂基材を含む。
好ましい実施形態においては、上記熱可塑性樹脂フィルムを搬送しながら、TDに固定端延伸する工程をさらに含む。
好ましい実施形態においては、総TD延伸倍率が3.0倍を超える。
熱可塑性樹脂フィルムの形成材料としては、目的に応じて任意の適切な材料を用い得る。例えば、ポリエチレンテレフタレート系樹脂等のエステル系樹脂、シクロオレフィン系樹脂、ポリプロピレン等のオレフィン系樹脂、ポリアミド系樹脂、ポリカーボネート系樹脂、(メタ)アクリル系樹脂、ポリビニルアルコール系樹脂、これらの共重合体樹脂等が挙げられる。これらの中でも、好ましくは、シクロオレフィン系樹脂(例えば、ノルボルネン系樹脂)、非晶質のポリエチレンテレフタレート系樹脂、ポリプロピレン、ポリビニルアルコール系樹脂である。非晶質のポリエチレンテレフタレート系樹脂の具体例としては、ジカルボン酸としてイソフタル酸をさらに含む共重合体や、グリコールとしてシクロヘキサンジメタノールをさらに含む共重合体が挙げられる。
上記熱可塑性樹脂フィルムを搬送しながら、同時二軸延伸機を用いてTDに延伸しながらMDに収縮させる。MD(搬送方向)は、好ましくは、長尺状の熱可塑性樹脂フィルムの長尺方向であり、熱可塑性樹脂フィルムの長尺方向に対して反時計回りに−5°〜+5°の方向を包含し得る。TD(搬送方向に直交する方向)は、好ましくは、長尺状の熱可塑性樹脂フィルムの幅手方向であり、熱可塑性樹脂フィルムの長尺方向に対して反時計回りに85°〜95°の方向を包含し得る。なお、本明細書において、「直交」とは、実質的に直交する場合も包含する。ここで、「実質的に直交」とは、90°±5.0°である場合を包含し、好ましくは90°±3.0°、さらに好ましくは90°±1.0°である。
M≦55L−0.6 (1≦M、10≦L)・・・・・(1)
ここで、本明細書において「クリップ間距離(L)」とは、図1に示すように、隣り合うクリップの端部から端部の距離をいう。
S≧(1−1/√M)×100 (1≦M)・・・・・(3)
本発明の延伸フィルムの製造方法は、その他の工程を含み得る。その他の工程としては、例えば、上記延伸とは別の延伸工程が挙げられる。当該別の延伸工程としては、例えば、上記熱可塑性樹脂フィルムを搬送しながら、TDに固定端延伸する工程が挙げられる。好ましくは、上記収縮・延伸工程後に、TDに固定端延伸する。このように、固定端TD延伸と組み合わせることにより、均一性を保持しながら、より高いTD延伸倍率を達成することができる。なお、収縮・延伸工程において熱可塑性樹脂フィルムにネックインが発生した場合、ネックインした端部を取り除いてから固定端TD延伸するのが好ましい。
熱可塑性樹脂フィルムとして、長尺状で未延伸のシクロオレフィン系樹脂フィルム(厚み:150μm、フィルム幅:400mm、Tg:123℃、JSR社製、商品名「ARTON5」)を用いた。この熱可塑性樹脂フィルムを、図1に示すように、同時二軸延伸機を用いて、MDに35%収縮させると同時に、TDに5.0倍に140℃で空中延伸し、延伸フィルムを得た。具体的には、テンター入口の搬送方向のクリップ間距離L1を70mm、延伸後の搬送方向のクリップ間距離L2を37mm、クリップサイズDを25mmとした(収縮率35(%)={1−(37(mm)+25(mm))/(70(mm)+25(mm)}×100)。
上記熱可塑性樹脂フィルムを、図1に示すように、同時二軸延伸機を用いて、MDに35%収縮させると同時に、TDに4.0倍に140℃で空中延伸した。同時二軸延伸機のテンター入口の搬送方向のクリップ間距離L1を100mm、延伸後の搬送方向のクリップ間距離L2を56mm、クリップサイズDを25mmとした。
その後、ネックインした端部を切り除いた熱可塑性樹脂フィルムを、固定端延伸機を用いて、総TD延伸倍率が5.0倍となるように延伸し、延伸フィルムを得た。固定端延伸機のクリップ間距離Lを5mm、クリップサイズDを50mmとした。
同時二軸延伸機によるTD延伸倍率を3.5倍とし、テンター入口の搬送方向のクリップ間距離L1を150mm、延伸後の搬送方向のクリップ間距離L2を89mmとしたこと以外は、実施例2と同様にして延伸フィルムを作製した。
同時二軸延伸機によるTD延伸倍率を2.5倍とし、MD収縮率を30%(テンター入口の搬送方向のクリップ間距離L1:200mm、延伸後の搬送方向のクリップ間距離L2:133mm)としたこと以外は、実施例2と同様にして延伸フィルムを作製した。
同時二軸延伸機による延伸の際、MD収縮率を5%(延伸後の搬送方向のクリップ間距離L2:65mm)としたこと以外は、実施例1と同様にして延伸フィルムを作製した。
同時二軸延伸機による延伸の際、MD収縮率を5%(延伸後の搬送方向のクリップ間距離L2:94mm)としたこと以外は、実施例2と同様にして延伸フィルムを作製した。
同時二軸延伸機による延伸の際、MD収縮率を20%(延伸後の搬送方向のクリップ間距離L2:115mm)としたこと以外は、実施例3と同様にして延伸フィルムを作製した。
同時二軸延伸機による延伸の際、MD収縮率を5%(延伸後の搬送方向のクリップ間距離L2:189mm)としたこと以外は、実施例4と同様にして延伸フィルムを作製した。
1.ネックイン度合
延伸処理後のフィルム端辺の内方への湾曲度合い(TDネックイン長さ)を測定し、フィルム最大幅に対する割合(%)を下記式により算出した。
ネックイン度合(%)=(TDネックイン長さ)/(フィルム最大幅)
2.フィルム厚み均一領域
得られた延伸フィルムにおいて、厚みが±2μmの範囲を厚み均一領域とし、厚み均一領域が占める割合を下記式により算出した。
フィルム厚み均一領域(%)=(厚みが均一な幅)/{(熱可塑性樹脂フィルムの幅)×(総TD延伸倍率)}×100
(評価基準)
◎:80%以上
○:70%以上、80%未満
×:70%未満
Claims (7)
- 熱可塑性樹脂フィルムを搬送しながら、同時二軸延伸機を用いてTDに延伸しながらMDに収縮させる工程を含み、
TD延伸倍率(M(倍))と、TD延伸倍率がM倍のときの同時二軸延伸機の搬送方向のクリップ間距離(L(mm))が下記式(1)の関係を満たす、延伸フィルムの製造方法:
M≦55L−0.6 (1≦M、10≦L)・・・・・(1)。 - 前記同時二軸延伸機のクリップサイズ(D(mm))が下記式(2)を満たす、請求項1に記載の延伸フィルムの製造方法:
5≦D≦30・・・・・(2)。 - 延伸温度が、前記熱可塑性樹脂フィルムのガラス転移温度(Tg)−10℃以上Tg+60℃以下である、請求項1または2に記載の延伸フィルムの製造方法。
- 前記TD延伸倍率(M(倍))と、MD収縮率(S(%))とが下記式(3)の関係を満たす、請求項1から3のいずれかに記載の延伸フィルムの製造方法:
S≧(1−1/√M)×100 (1≦M)・・・・・(3)。 - 前記熱可塑性樹脂フィルムが、MDに熱収縮可能な熱可塑性樹脂基材を含む、請求項1から4のいずれかに記載の延伸フィルムの製造方法。
- 前記熱可塑性樹脂フィルムを搬送しながら、TDに固定端延伸する工程をさらに含む、請求項1から5のいずれかに記載の延伸フィルムの製造方法。
- 総TD延伸倍率が3.0倍を超える、請求項1から6のいずれかに記載の延伸フィルムの製造方法。