JP5929655B2 - 立方晶窒化ホウ素複合多結晶体およびその製造方法、切削工具、ならびに耐摩工具 - Google Patents
立方晶窒化ホウ素複合多結晶体およびその製造方法、切削工具、ならびに耐摩工具 Download PDFInfo
- Publication number
- JP5929655B2 JP5929655B2 JP2012199656A JP2012199656A JP5929655B2 JP 5929655 B2 JP5929655 B2 JP 5929655B2 JP 2012199656 A JP2012199656 A JP 2012199656A JP 2012199656 A JP2012199656 A JP 2012199656A JP 5929655 B2 JP5929655 B2 JP 5929655B2
- Authority
- JP
- Japan
- Prior art keywords
- boron nitride
- cubic boron
- composite polycrystal
- plane
- nitride composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
(実施の形態)
本実施の形態に係る立方晶窒化ホウ素複合多結晶体は、複数の立方晶窒化ホウ素(cBN)と、複数のウルツ鉱型窒化ホウ素(wBN)とを備えている。立方晶窒化ホウ素同士、ウルツ鉱型窒化ホウ素同士、さらに立方晶窒化ホウ素とウルツ鉱型窒化ホウ素とは、いずれも強固に結合し、緻密な複合組織を有している。具体的には、該多結晶体は、0.1体積%以上のウルツ鉱型窒化ホウ素と、残部を構成する立方晶窒化ホウ素と不可避不純物とで構成されている。不可避不純物とは、たとえば窒素、水素、酸素などである。このとき、立方晶窒化ホウ素の平均粒径は500nm以下程度である。該多結晶体は、実質的にバインダー、焼結助剤、触媒などを含んでいない。
Claims (7)
- ウルツ鉱型窒化ホウ素と立方晶窒化ホウ素と不可避不純物とで構成され、
前記ウルツ鉱型窒化ホウ素の含有率が0.1体積%以上であり、
前記立方晶窒化ホウ素の平均粒径は500nm以下であり、
前記立方晶窒化ホウ素の(111)面のX線回折強度I(111)に対する、前記立方晶窒化ホウ素の(220)面のX線回折強度I(220)の比I(220)/I(111)が0.1未満である配向面を備える、立方晶窒化ホウ素複合多結晶体。 - 六方晶窒化ホウ素のX線回折強度が検出限界以下である、請求項1に記載の立方晶窒化ホウ素複合多結晶体。
- 前記配向面におけるヌープ硬度は55GPa以上である、請求項1または2に記載の立方晶窒化ホウ素複合多結晶体。
- 前記立方晶窒化ホウ素の平均粒径は150nm以下である、請求項1〜3のいずれか1項に記載の立方晶窒化ホウ素複合多結晶体。
- 請求項1〜4のいずれか1項に記載の立方晶窒化ホウ素複合多結晶体を備え、前記配向面を刃先のすくい面または逃げ面として使用する、切削工具。
- 請求項1〜4のいずれか1項に記載の立方晶窒化ホウ素複合多結晶体を備え、耐摩耗性を要求される部分に前記配向面を用いた、耐摩工具。
- 出発物質として熱分解窒化ホウ素を準備する工程と、
圧力8GPa以上、かつ、温度1300〜2300℃の条件下において前記熱分解窒化ホウ素を立方晶窒化ホウ素に直接変換させると同時に焼結させる工程とを備え
前記熱分解窒化ホウ素は、(002)面の面間隔が3.35Å以上、3.5Å以下であり、
前記熱分解窒化ホウ素は、c軸に垂直な方向におけるX線回折測定において、(002)面のX線回折強度I (002) に対する、(100)面のX線回折強度I (100) の比I (100) /I (002) が2.0以上である、立方晶窒化ホウ素複合多結晶体の製造方法。