JP5909685B2 - ナノファイバシート、キャパシタ用セパレータ、キャパシタ、およびキャパシタ用セパレータの製造方法 - Google Patents
ナノファイバシート、キャパシタ用セパレータ、キャパシタ、およびキャパシタ用セパレータの製造方法 Download PDFInfo
- Publication number
- JP5909685B2 JP5909685B2 JP2012123713A JP2012123713A JP5909685B2 JP 5909685 B2 JP5909685 B2 JP 5909685B2 JP 2012123713 A JP2012123713 A JP 2012123713A JP 2012123713 A JP2012123713 A JP 2012123713A JP 5909685 B2 JP5909685 B2 JP 5909685B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- nanofiber
- nanofibers
- average
- vicinity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明のさらに他の一局面は、一対の電極と、電極間に介在するセパレータと、電解質と、を具備し、セパレータが、ナノファイバを含み、かつ第1表面およびその反対側の第2表面を有するシート形状を有し、セパレータの面方向におけるナノファイバの最大繊維径の平均を、第1表面近傍および第2表面近傍と、セパレータの厚さ方向の中心部とで比較したとき、第1表面近傍におけるナノファイバの最大繊維径の平均Ds1および第2表面近傍におけるナノファイバの最大繊維径の平均Ds2が、セパレータの厚さ方向の中心部におけるナノファイバの最大繊維径の平均Dcより小さくなっている、キャパシタに関する。セパレータは、1.1≦Dc/Ds1≦2.5、および1.1≦Dc/Ds2≦2.5の関係を充足するか、もしくは、最大繊維径の平均Dcが、60nm〜2μmである。
キャパシタは、一対の電極と、電極間に介在するセパレータと、電解質とを具備する。そして、セパレータとして、電界紡糸法により形成されたナノファイバのマトリックス構造を有し、かつ第1表面およびその反対側の第2表面を有するシート形状を有するもの(以下、単にナノファイバシートともいう)を用いる。
ナノファイバ不織布は、従来、電界紡糸法などにより、基材上にナノファイバを堆積させることにより作製される。そのため、基材の表面に接するナノファイバは、基材の表面の形状が転写されて、少し押し潰された状態になる。これにより、得られる不織布は、基材に接する側の表面の繊維が平らな状態となる。この平らな状態の繊維表面を有する不織布を、キャパシタ用セパレータとして用いると、平らな状態の繊維表面が電極と接した状態となり、接触面積が大きくなるので、接触抵抗が大きくなる。その結果、直流抵抗や交流抵抗(ESR)が大きくなり、キャパシタ特性が低下する。
図1に示されるように、ナノファイバシート1は、第1表面1aと、第1表面1aとは反対側の第2表面2aとを有しており、第1多孔質シートP1と第2多孔質シートP2とを貼り合わせた構造を有している。第1多孔質シートP1と、第2多孔質シートP2とは、基材シートの主面に接触していた表面同士を対向させて接合される。そのため、接合面3aの近傍(具体的には、ナノファイバシート1の厚さ方向の中心部)3では、繊維が少し押し潰された状態となっている。
ナノファイバシートの面方向における最大繊維径とは、1本のナノファイバの繊維断面(繊維の幅方向の断面)を見たときに、ナノファイバシートの面方向における繊維幅のうち、最も大きなものを意味する。最大繊維径の平均とは、ナノファイバシートの厚さ方向の断面において、任意に選択した複数本(例えば、10本)のナノファイバの最大繊維径の平均値を意味する。なお、ナノファイバシートの面方向における最大繊維径を、単に、最大繊維径と称する場合がある。
最大繊維径の平均Dcは、例えば、60nm〜2μm、好ましくは100nm〜1.2μm、さらに好ましくは200〜1000nmである。
ナノファイバシートにおいて、第1表面近傍における空隙率Ps1と、第2表面近傍における空隙率Ps2とは、0.9≦Ps1/Ps2≦1.1を満たすのが好ましく、0.95≦Ps1/Ps2≦1.05を満たすのがさらに好ましい。Ps1およびPs2がこのような関係を満たす場合、ナノファイバシートの両表面の物性を、より均一にすることができるため、有利である。
ナノファイバシートのマトリックス構造において、ナノファイバ同士は、接点において、互いに接着した状態であってもよく、接着することなく分離していてもよい。ナノファイバ同士は、マトリックス構造中、ランダムに接着していてもよい。
ナノファイバシートでは、両表面の近傍よりも、厚さ方向の中心部近傍において、ナノファイバ同士の接着が多くなっていてもよい。
溶融ポリマーを用いた電界紡糸では、ナノファイバが堆積する際に、完全に固化していないナノファイバ同士が接触した状態で固化すると、接点において、ナノファイバ同士が融着した状態となる。
ナノファイバは、必要に応じて、ポリマー以外に、公知の添加剤を含んでもよい。添加剤の含有量は、例えば、ナノファイバシートの5質量%以下である。
キャパシタとしては、電解質を用いるもの、例えば、アルミ電解キャパシタなどの電解キャパシタ、電気二重層キャパシタ、擬似キャパシタ、リチウムイオンキャパシタなどが例示できる。これらの中でも、特に、電気二重層キャパシタやリチウムイオンキャパシタが好ましい。電解質は、陽イオン、陰イオンおよびこれらを溶解する非水溶媒などを含む。
キャパシタの電極、電極活物質、電解質などは、キャパシタの種類に応じて、適宜選択できる。
合剤層の厚さは、例えば、50〜300μm、さらに好ましくは100〜200μmである。
(電極活物質)
キャパシタでは、一対の電極の少なくとも一方が、電気二重層を形成する分極性材料として炭素質材料を含むことが好ましい。
電気二重層キャパシタでは、双方の電極ともに、活物質として、活性炭が使用される。
リチウムイオンキャパシタでは、陽極の活物質として、リチウムイオンキャパシタ用途で公知の材料、例えば、活性炭、カーボンブラック、黒鉛、カーボンナノチューブ、フラーレンなどの炭素質材料の他、ポリアセン系半導体(PAS)などを使用してもよい。これらは、一種を単独でまたは二種以上を組み合わせて使用できる。これらの活物質のうち、活性炭が好ましい。
結着剤の割合は、活物質100質量部当たり、例えば、0.1〜10質量部、好ましくは1〜5質量部である。
電気二重層キャパシタにおいて使用される電解質としては、硫酸などの酸を含む水系電解質の他、ホウフッ化4級アンモニウム塩(例えばホウフッ化テトラエチルアンモニウム、ホウフッ化トリエチルメチルアンモニウム)などを非水溶媒に溶解させた非水電解質が使用できる。
キャパシタは、キャパシタの種類や形状などに応じて、公知の方法により製造できる。例えば、一対の電極と、これらを隔離するキャパシタ用セパレータとを捲回して電極群を形成し、電極群および電解質をケースに収容することによりキャパシタを製造してもよい。電極群は、捲回したものに限らず、積層したもの、またはつづら折りにしたものであってもよい。電極群の形状は、キャパシタの形状に応じて、円筒型、捲回軸に垂直な端面が長円形である扁平形であってもよい。
ナノファイバシートは、電界紡糸法により、基材シートの主面にナノファイバを堆積させて多孔質シートを形成する工程(A)と、一対の多孔質シートの基材シートの主面と接触していた表面同士を対向させて接合する工程(B)とを経ることにより製造できる。
ナノファイバシートの製造方法は、さらに、工程(A)に先だって、基材シートを、ナノファイバを形成させる空間(ナノファイバ形成空間)に配置または供給する工程(a)、および/または、工程(B)の後に、完成したシートを回収する工程(C)を有していてもよい。
多孔質シートは、電界紡糸法により形成できる。多孔質シートを形成する工程(A)は、具体的には、ナノファイバ形成空間において、樹脂原料(前記例示のポリマー)などの高分子物質を含む原料液から、静電気力によりナノファイバを生成させるとともに、生成したナノファイバを基材シートの主面に堆積させて、ナノファイバのマトリックス構造を有する多孔質シートを形成する工程であってもよい。
溶媒は、樹脂原料を溶解可能で、揮発などにより除去可能なものであれば特に制限されず、樹脂原料の種類に応じて、適宜選択できる。溶媒としては、各種有機溶媒、例えば、アセトンなどのケトン、アセトニトリルなどのニトリル、N,N−ジメチルホルムアミドなどのアミド、テトラヒドロフランなどのエーテル、ジメチルスルホキシドなどのスルホキシド、N−メチル−2−ピロリドンなどが例示できる。非プロトン性極性溶媒が好ましい。
基材シートの種類は限定されない。基材シートの主面には、多孔質シートが剥離しやすいように、離型剤のコーティング、粗面化などの公知の離型処理が施されていてもよい。
形成された多孔質シートは、接合工程(B)に供される。接合工程(B)では、一対の多孔質シートが、基材シートの主面と接していた表面同士を対向させた状態で接合され、ナノファイバシートが形成される。
また、一対の多孔質シートは、熱圧着や接着剤などを用いた公知の接合方法により、接合させてもよい。
ナノファイバシートの製造方法は、例えば、
(i)基材シートをナノファイバ形成空間に供給する工程と、
(ii)ナノファイバ形成空間において、溶媒および溶媒に溶解した樹脂原料を含む原料液から静電気力によりナノファイバを生成させるとともに、生成したナノファイバを基材シートの主面に堆積させて、ナノファイバのマトリックス構造を有する多孔質シートを形成する工程と、
(iii)一対の多孔質シートを、基材シートの主面と接触していた表面同士を対向させて接合し、一対の多孔質シートの基材シートの主面と接触していなかった表面をそれぞれ第1表面およびその反対側の第2表面とするナノファイバシートを形成する工程と、を有する。
図3の製造システム100は、ナノファイバシートを製造するための製造ラインを構成している。製造システム100では、基材シートSが製造ラインの上流から下流に搬送される。搬送途中の基材シートSには、多孔質シートP1の形成が随時行われる。
多孔質シート形成装置40では、放出体42が基材シートSの移動方向(図4中の白抜き矢印の方向)に対して斜めに交わるように設置されている。このように放出体42を斜めに設置することで、第2搬送コンベア41と放出体42との対向面積が大きくなるため、多孔質層の生産性を高めることが可能である。なお、放出体42と矢印との成す鋭角θは、特に限定されないが、30〜60°程度とすることが、生産性を十分に向上させる上で好ましい。放出体42は、多孔質シート形成装置40の上方に設置された基材シートSの移動方向と平行な第1支持体48から下方に延びる第2支持体49により、自身の長手方向が基材シートSの主面Saと平行になるように支持されている。
本発明のナノファイバシートの製造方法は、特に、キャパシタ用セパレータの製造に適しているが、他の様々な用途に使用されるナノファイバシートの製造にも利用できる。
(i)第1および第2基材シートを、第1および第2ラインの上流側のナノファイバ形成空間に搬送する工程と、
(ii)ナノファイバ形成空間において、溶媒および溶媒に溶解した樹脂原料を含む原料液から静電気力によりナノファイバを生成させるとともに、生成したナノファイバを搬送される第1および第2基材シートの主面にそれぞれ堆積させて、ナノファイバのマトリックス構造を有する第1および第2多孔質シートを形成する工程と、
(iii)第1および第2ラインの下流側で、搬送される第1および第2多孔質シートから第1および第2基材シートを除去する工程と、
(iv)第1および第2ラインの更に下流側で、搬送される第1および第2多孔質シートの第1および第2基材シートの主面と接触していた表面同士を対向させて接合してナノファイバシートを形成する工程と、を有する。
図6の製造システム300は、第1ラインの最上流に、基材シート供給装置20Aが設けられているとともに、第2ラインの最上流に、基材シート供給装置20Bが設けられている。製造システム300は、図3の製造システム100において、第2多孔質シートP2を、多孔質シート接合装置50の供給リール52aから供給せずに、第1多孔質シートと並行して同様に製造しながら、連続的に、一対の接合ローラ51a,51b間に供給する以外は、図3の製造システム100と同様である。
図6に示すような製造システムでも、図3の場合に準じて、図示しない制御装置により、基材シートS1およびS2、多孔質シートP1およびP2などの搬送速度を一定に制御してもよい。また、多孔質シート接合装置50Aと、ナノファイバシート回収装置70との間に、上記と同様に、予備回収部を配置してもよい。
4:電極群、5a,5b:電極、6a,6b:セパレータ、7a,7b:引き出しリード
20,20A,20B:基材シート供給装置、21,21a,21b:第1搬送コンベア、22,22a,22b:供給リール、
70:回収装置、71:搬送ローラ、72:回収リール、
Claims (17)
- ナノファイバを含み、かつ第1表面およびその反対側の第2表面を有するナノファイバシートであって、
前記ナノファイバシートの面方向における前記ナノファイバの最大繊維径の平均を、前記第1表面近傍および前記第2表面近傍と、前記ナノファイバシートの厚さ方向の中心部とで比較したとき、前記第1表面近傍における前記ナノファイバの最大繊維径の平均Ds1および前記第2表面近傍における前記ナノファイバの最大繊維径の平均Ds2が、前記ナノファイバシートの厚さ方向の中心部における前記ナノファイバの最大繊維径の平均Dcより小さく、
1.1≦Dc/Ds1≦2.5、および1.1≦Dc/Ds2≦2.5の関係を充足する、ナノファイバシート。 - ナノファイバを含み、かつ第1表面およびその反対側の第2表面を有するナノファイバシートであって、
前記ナノファイバシートの面方向における前記ナノファイバの最大繊維径の平均を、前記第1表面近傍および前記第2表面近傍と、前記ナノファイバシートの厚さ方向の中心部とで比較したとき、前記第1表面近傍における前記ナノファイバの最大繊維径の平均Ds1および前記第2表面近傍における前記ナノファイバの最大繊維径の平均Ds2が、前記ナノファイバシートの厚さ方向の中心部における前記ナノファイバの最大繊維径の平均Dcより小さく、
前記最大繊維径の平均Dcが、60nm〜2μmである、ナノファイバシート。 - 前記最大繊維径の平均Ds1と、前記最大繊維径の平均Ds2とが、0.9≦Ds1/Ds2≦1.1を満たし、前記第1表面近傍における前記ナノファイバシートの空隙率Ps1と、前記第2表面近傍における前記ナノファイバシートの空隙率Ps2とが、0.9≦Ps1/Ps2≦1.1を満たす、請求項1または請求項2に記載のナノファイバシート。
- 前記ナノファイバシートにおいて、前記ナノファイバ同士がランダムに溶着している、請求項1〜3のいずれか1項に記載のナノファイバシート。
- 前記ナノファイバは、オレフィン樹脂、フッ素樹脂、ポリアミド樹脂、およびポリイミド樹脂よりなる群から選択される少なくとも1種を含む、請求項1〜4のいずれか1項に記載のナノファイバシート。
- 前記ナノファイバシートが、電界紡糸法により形成された前記ナノファイバのマトリックス構造を有する請求項1〜5のいずれか1項に記載のナノファイバシート。
- 前記最大繊維径の平均Dcが、200〜1000nmである、請求項1〜6のいずれか1項に記載のナノファイバシート。
- 1.3≦Dc/Ds1≦2の関係を充足する、請求項1〜7のいずれか1項に記載のナノファイバシート。
- ナノファイバを含み、かつ第1表面およびその反対側の第2表面を有するシート形状のキャパシタ用セパレータであって、
前記セパレータの面方向における前記ナノファイバの最大繊維径の平均を、前記第1表面近傍および前記第2表面近傍と、前記セパレータの厚さ方向の中心部とで比較したとき、前記第1表面近傍における前記ナノファイバの最大繊維径の平均Ds1および前記第2表面近傍における前記ナノファイバの最大繊維径の平均Ds2が、前記セパレータの厚さ方向の中心部における前記ナノファイバの最大繊維径の平均Dcより小さく、
1.1≦Dc/Ds1≦2.5、および1.1≦Dc/Ds2≦2.5の関係を充足する、キャパシタ用セパレータ。 - ナノファイバを含み、かつ第1表面およびその反対側の第2表面を有するシート形状のキャパシタ用セパレータであって、
前記セパレータの面方向における前記ナノファイバの最大繊維径の平均を、前記第1表面近傍および前記第2表面近傍と、前記セパレータの厚さ方向の中心部とで比較したとき、前記第1表面近傍における前記ナノファイバの最大繊維径の平均Ds1および前記第2表面近傍における前記ナノファイバの最大繊維径の平均Ds2が、前記セパレータの厚さ方向の中心部における前記ナノファイバの最大繊維径の平均Dcより小さく、
前記最大繊維径の平均Dcが、60nm〜2μmである、キャパシタ用セパレータ。 - 一対の電極と、前記電極間に介在するセパレータと、電解質と、を具備し、
前記セパレータが、ナノファイバを含み、かつ第1表面およびその反対側の第2表面を有するシート形状を有し、
前記セパレータの面方向における前記ナノファイバの最大繊維径の平均を、前記第1表面近傍および前記第2表面近傍と、前記セパレータの厚さ方向の中心部とで比較したとき、前記第1表面近傍における前記ナノファイバの最大繊維径の平均Ds1および前記第2表面近傍における前記ナノファイバの最大繊維径の平均Ds2が、前記セパレータの厚さ方向の中心部における前記ナノファイバの最大繊維径の平均Dcより小さく、
1.1≦Dc/Ds1≦2.5、および1.1≦Dc/Ds2≦2.5の関係を充足する、キャパシタ。 - 一対の電極と、前記電極間に介在するセパレータと、電解質と、を具備し、
前記セパレータが、ナノファイバを含み、かつ第1表面およびその反対側の第2表面を有するシート形状を有し、
前記セパレータの面方向における前記ナノファイバの最大繊維径の平均を、前記第1表面近傍および前記第2表面近傍と、前記セパレータの厚さ方向の中心部とで比較したとき、前記第1表面近傍における前記ナノファイバの最大繊維径の平均Ds1および前記第2表面近傍における前記ナノファイバの最大繊維径の平均Ds2が、前記セパレータの厚さ方向の中心部における前記ナノファイバの最大繊維径の平均Dcより小さく、
前記最大繊維径の平均Dcが、60nm〜2μmである、キャパシタ。 - 前記一対の電極の少なくとも一方が、電気二重層を形成する分極性材料として炭素質材料を含み、
前記電解質が、陽イオン、陰イオンおよびこれらを溶解する非水溶媒を含む、請求項11または12に記載のキャパシタ。 - (i)基材シートをナノファイバ形成空間に供給する工程と、
(ii)前記ナノファイバ形成空間において、溶媒および前記溶媒に溶解した樹脂原料を含む原料液から静電気力によりナノファイバを生成させるとともに、前記生成したナノファイバを前記基材シートの主面に堆積させて、ナノファイバのマトリックス構造を有する多孔質シートを形成する工程と、
(iii)一対の前記多孔質シートを、前記基材シートの主面と接触していた表面同士を対向させて接合し、前記一対の多孔質シートの前記基材シートの主面と接触していなかった表面をそれぞれ第1表面およびその反対側の第2表面とするキャパシタ用セパレータを形成する工程と、を有する、キャパシタ用セパレータの製造方法。 - 前記工程(iii)において、前記一対の多孔質シートの少なくとも前記基材シートの主面と接触していた表面近傍が前記溶媒を含んだ状態で、前記一対の多孔質シートを接合し、一方の前記多孔質シートのナノファイバと、他方の前記多孔質シートのナノファイバとを溶着させる、請求項14に記載のキャパシタ用セパレータの製造方法。
- 第1および第2ラインの上流から下流にそれぞれ長尺の第1および第2基材シートを搬送し、上流側で、前記第1および第2基材シートの主面にそれぞれ第1および第2多孔質シートを形成し、下流側で、前記第1および第2多孔質シートを対向させて接合する、キャパシタ用セパレータの製造方法であって、
(i)前記第1および第2基材シートを、前記第1および第2ラインの上流側のナノファイバ形成空間に搬送する工程と、
(ii)前記ナノファイバ形成空間において、溶媒および前記溶媒に溶解した樹脂原料を含む原料液から静電気力によりナノファイバを生成させるとともに、前記生成したナノファイバを搬送される前記第1および第2基材シートの主面にそれぞれ堆積させて、ナノファイバのマトリックス構造を有する第1および第2多孔質シートを形成する工程と、
(iii)前記第1および第2ラインの下流側で、搬送される前記第1および第2多孔質シートから前記第1および第2基材シートを除去する工程と、
(iv)前記第1および第2ラインの更に下流側で、搬送される前記第1および第2多孔質シートの前記第1および第2基材シートの主面と接触していた表面同士を対向させて接合してナノファイバシートを形成する工程と、を有する、キャパシタ用セパレータの製造方法。 - 前記工程(iv)において、前記第1および第2多孔質シートの少なくとも前記第1および第2基材シートの主面と接触していた表面近傍が前記溶媒を含んだ状態で、前記第1および第2多孔質シートを接合し、前記第1多孔質シートのナノファイバと、前記第2多孔質シートのナノファイバとを溶着させる、請求項16に記載のキャパシタ用セパレータの製造方法。