JP5907839B2 - Laminated body, polarizing plate, optical material, display device and touch panel - Google Patents
Laminated body, polarizing plate, optical material, display device and touch panel Download PDFInfo
- Publication number
- JP5907839B2 JP5907839B2 JP2012190217A JP2012190217A JP5907839B2 JP 5907839 B2 JP5907839 B2 JP 5907839B2 JP 2012190217 A JP2012190217 A JP 2012190217A JP 2012190217 A JP2012190217 A JP 2012190217A JP 5907839 B2 JP5907839 B2 JP 5907839B2
- Authority
- JP
- Japan
- Prior art keywords
- organic
- film
- inorganic composite
- group
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、有機無機複合膜及び接続層を有する積層体、並びに、それを備える偏光板、光学材料、表示装置及びタッチパネルに関する。 The present invention relates to a laminate having an organic-inorganic composite film and a connection layer, and a polarizing plate, an optical material, a display device, and a touch panel including the laminate.
昨今、表示装置の主流はフラットパネルディスプレイ（ＦＰＤ）であり、液晶ディスプレイ（ＬＣＤ）、有機ＥＬディスプレイ（ＥＬＤ）、プラズマディスプレイ（ＰＤＰ）等の種類がある。これらＦＰＤに対する市場ニーズとしては、高品位化、省電力化、薄型化、低価格化等が挙げられる。 In recent years, the mainstream of display devices is a flat panel display (FPD), which includes a liquid crystal display (LCD), an organic EL display (ELD), a plasma display (PDP), and the like. Market needs for these FPDs include high quality, power saving, thinning, and price reduction.
ＦＰＤの表示機能を発現させるためには、ディスプレイ内部に、複数の光学フィルム等の光学部材を組み込み、複数の層を積層する必要がある。粘着剤又は接着剤からなる接続層を設けることで、各層の光軸のズレや、各層同士が擦れて傷つくことを防止することができる。 In order to develop the display function of the FPD, it is necessary to incorporate a plurality of optical members such as a plurality of optical films and stack a plurality of layers inside the display. By providing a connection layer made of a pressure-sensitive adhesive or an adhesive, it is possible to prevent the optical axis of each layer from shifting and the layers from being rubbed and damaged.
また、接続層を介さずに、光学部材を積層すると、光学部材間に空気層ができる。その結果、各光学部材界面と空気層（屈折率１．０）との間に大きな屈折率差ができる。この屈折率差により界面反射が起こると、透過光が減少する。透過光が減少すると品位が低下し、品位を維持しようとすると消費電力の増加を招くため、市場ニーズを満たすためには、この界面反射を抑制する必要がある。 In addition, when optical members are stacked without a connection layer, an air layer is formed between the optical members. As a result, there is a large refractive index difference between each optical member interface and the air layer (refractive index 1.0). When interface reflection occurs due to this difference in refractive index, transmitted light decreases. If the transmitted light decreases, the quality deteriorates, and if the quality is maintained, the power consumption increases. Therefore, in order to satisfy the market needs, it is necessary to suppress this interface reflection.
従来から、光学フィルム等の光学部材間を接続層を介し、複数の光学部材を積層し一体化することで、界面反射を抑制する手法が提案されているが、市場からは更なる高品位化、省電力化、薄型化が求められており、まだニーズを満足するものではない。 Conventionally, a method to suppress interface reflection by laminating and integrating multiple optical members between optical members such as optical films via a connection layer has been proposed. There is a demand for energy saving and thinning, and it still does not satisfy the needs.
そこで、各光学部材界面と空気層との屈折率差を小さくする手段として、ナノインプリント等による微細加工、プリズムシートやマイクロレンズを使用した手法等が提案されている。これらの手法は、優れた光学特性が得られる半面、安定的に大量生産することが困難であり、製造コストが高くなる。また光学フィルム表面に凹凸が形成されるため、積層する際に、凹部に粘着剤や接着剤が入り込み易く、光学特性を損ない易いという問題がある。 Therefore, as means for reducing the refractive index difference between each optical member interface and the air layer, a fine processing using nanoimprint or the like, a method using a prism sheet or a microlens, and the like have been proposed. Although these methods can provide excellent optical characteristics, it is difficult to stably mass-produce them, and the manufacturing cost increases. Moreover, since unevenness | corrugation is formed in the optical film surface, when laminating | stacking, there exists a problem that an adhesive or an adhesive agent will enter easily into a recessed part, and an optical characteristic is easy to be impaired.
逆に、光学部材と空気層との界面の屈折率差を利用すれば、ＦＰＤを高機能化することも可能である。例えば、光の方向を有用な方向に曲げることや、界面に入射する不要な方向の光を反射させて光源側に戻して再反射させ、有用な方向の光に変化させることができるため、この機構を利用して、高品位化、省電力化が可能となる。しかしながら、空気層を維持するためにスペーサー（枠）等を介して光学部材を組み合せると、膜厚が厚くなり、薄型化という市場ニーズに合致しなくなる。スペーサー（枠）等を介さずに、積層体が成形できれば、薄型化が可能となる。 On the contrary, if the refractive index difference at the interface between the optical member and the air layer is utilized, it is possible to make the FPD highly functional. For example, the direction of light can be bent in a useful direction, or light in an unnecessary direction incident on the interface can be reflected and reflected back to the light source side to change to light in a useful direction. Using the mechanism, high quality and power saving can be achieved. However, when optical members are combined through spacers (frames) or the like in order to maintain the air layer, the film thickness becomes thick, and it does not meet the market needs for thinning. If the laminate can be formed without using a spacer (frame) or the like, the thickness can be reduced.
また、昨今のテレビの大型化に伴い、ＬＣＤでは輝度向上のために光源本数が増加する傾向があり、筐体内部が過熱しやすくなっている。このような過熱環境下で、光学フィルム等の薄い光学部材が独立して存在すると、光学部材が熱による変質や歪みが発生し易くなり、ＦＰＤの品位低下の原因となる。過熱環境下での光学部材の変質や歪み防止の観点からも、接続層を介した積層体として一体化させることは有用である。 In addition, with the recent increase in size of televisions, LCDs tend to increase the number of light sources in order to improve brightness, and the interior of the housing is easily overheated. If a thin optical member such as an optical film is present independently in such an overheated environment, the optical member is likely to be altered or distorted by heat, which causes a reduction in the quality of the FPD. It is useful to integrate as a laminated body through the connection layer also from the viewpoint of the deterioration of the optical member and the prevention of distortion in an overheated environment.
つまり、更にＦＰＤの機能を向上させるためには、接続層を介して複数の光学部材を積層して一体化させるとともに、界面反射を制御するための新たな技術を、更に付加することが必要である。 In other words, in order to further improve the function of the FPD, it is necessary to stack and integrate a plurality of optical members via a connection layer, and to add a new technique for controlling interface reflection. is there.
特許文献１では、エアロゲルを用いて低屈折率層を形成した、光学積層フィルムが報告されている。 In patent document 1, the optical laminated film which formed the low-refractive-index layer using the airgel is reported.
特許文献２では、プリズムシートを用いた、光学積層体が報告されている。 In Patent Document 2, an optical laminated body using a prism sheet is reported.
光学フィルム等の光学部材と空気層の界面反射を抑制するためには、光学部材と空気層の間に、ｎｍ〜μｍオーダーの厚みで、屈折率１．０５〜１．３８程度の低屈折率層を設けることで、屈折率を段階的に変化させることが効果的である。 In order to suppress interface reflection between an optical member such as an optical film and the air layer, a low refractive index of about 1.05 to 1.38 with a thickness of nm to μm between the optical member and the air layer. By providing the layer, it is effective to change the refractive index stepwise.
低屈折率層を形成できる材料として、フッ素系樹脂や中空シリカを含むコーティング材等が市販されているが、これらは殆ど屈折率１．３５以上である。 As materials capable of forming a low refractive index layer, coating materials containing fluororesin and hollow silica are commercially available, but these have a refractive index of 1.35 or more.
低屈折率層の屈折率を更に低減させ、より大きな界面反射抑制効果を得るためには、有機無機複合体の粒子間に空隙を形成するなどして、低屈折率層内に空隙を導入する方法が有効であると考えることができる。空気の屈折率は１．００であり、空隙中に空気を含む低屈折率層は非常に低い屈折率を有することとなるからである。 In order to further reduce the refractive index of the low refractive index layer and obtain a larger interface reflection suppression effect, voids are introduced into the low refractive index layer, for example, by forming voids between the particles of the organic-inorganic composite. The method can be considered effective. This is because the refractive index of air is 1.00, and the low refractive index layer containing air in the gap has a very low refractive index.
また超低屈折率の材料として、エアロゲルが知られているが、単独で工業的に成膜することは難しく、生産性の高いＵＶ硬化処理で製造することが困難であることから、工業的実用性に乏しい。 In addition, airgel is known as an ultra-low refractive index material, but it is difficult to industrially form a film alone, and it is difficult to produce it by a highly productive UV curing process. Poor sex.
しかしながら、本発明者らの検討によると、特許文献１の方法の場合、エアロゲルに、バインダーと中空シリカゾルを加えて、ＵＶ硬化（ＵＶ架橋）することで低屈折率層を形成したとされている。しかしながら、そのコーティング液の組成では、ＵＶ架橋のための官能基が十分に含まれないために硬化不良となり、ディスプレイの必須要件である長期信頼性が担保できない。 However, according to studies by the present inventors, in the case of the method of Patent Document 1, it is said that a low refractive index layer is formed by adding a binder and a hollow silica sol to an airgel and performing UV curing (UV crosslinking). . However, the composition of the coating solution does not contain sufficient functional groups for UV crosslinking, resulting in poor curing, and long-term reliability, which is an essential requirement for displays, cannot be guaranteed.
また、成膜のためにバインダー成分等を加えるため、得られる低屈折率層の屈折率の実態は１．３３〜１．３７である。また低屈折率層との屈折率差を維持するため、その下地として屈折率１．５７〜１．６２の、特殊な高屈折率ハードコート層を使用している。一般的なハードコート材を使用した場合の屈折率は１．５０前後であるため、特殊な条件下での使用が開示されているのみである。通常、高屈折率ハードコート材は一般的なハードコート材よりも高価であり、上記低屈折率層の成分である中空シリカゾルは、数十万円／ｋｇ（固形分換算）と非常に高価であることも、低価格化を妨げる要因となる。 Moreover, since the binder component etc. are added for film-forming, the actual condition of the refractive index of the obtained low refractive index layer is 1.33-1.37. In order to maintain the refractive index difference from the low refractive index layer, a special high refractive index hard coat layer having a refractive index of 1.57 to 1.62 is used as the base. Since the refractive index when a general hard coat material is used is around 1.50, the use under special conditions is only disclosed. Usually, a high refractive index hard coat material is more expensive than a general hard coat material, and the hollow silica sol, which is a component of the low refractive index layer, is very expensive at several hundred thousand yen / kg (in terms of solid content). There are also factors that hinder lower prices.
また、特許文献２の方法の場合、プリズムシートの上に、直接、接着層を重ねている。この方法の場合、少しの部分応力でプリズムシートの凹部に接着層が入り込むため、製造が難しく、製造コストが高くなる。 Moreover, in the case of the method of patent document 2, the contact bonding layer is directly piled up on the prism sheet. In the case of this method, since the adhesive layer enters the concave portion of the prism sheet with a slight partial stress, the manufacturing is difficult and the manufacturing cost is increased.
一方で、上述のような問題が生じない低屈折率層を作製する方法として、有機ポリマーの片末端が無機物粒子に結合している有機無機複合体を利用して、効果的に空隙を形成させた有機無機複合膜、つまり、光を散乱せず、透明性が高く、十分な低屈折率化を図れる低屈折率層を形成する方法がある。そしてこのような低屈折率層と接続層とを有する積層体についての具体的な技術事項は、これまで明らかでなかった。 On the other hand, as a method for producing a low refractive index layer that does not cause the above-described problems, an organic / inorganic composite in which one end of an organic polymer is bonded to inorganic particles is used to effectively form voids. There is a method of forming an organic-inorganic composite film, that is, a low refractive index layer that does not scatter light, has high transparency, and can achieve a sufficiently low refractive index. And the concrete technical matter about the laminated body which has such a low refractive index layer and a connection layer was not clear until now.
本発明は、上記事情に鑑みてなされたものであり、透過性に優れた安価な積層体と、それを使用した、高品位の表示装置等を提供することを目的とする。 The present invention has been made in view of the above circumstances, and an object thereof is to provide an inexpensive laminate having excellent permeability and a high-quality display device using the same.
本発明は、以下のものに関する。 The present invention relates to the following.
［１］無機化合物粒子と、前記無機化合物粒子に結合しているポリマーとを含む有機無機複合体を含有する有機無機複合膜と、
粘着剤又は接着剤を含有する接続層と、を有し、
前記有機無機複合膜中の空隙の割合が、前記有機無機複合膜の体積を基準として３〜９０体積％である、積層体。
［２］前記無機化合物粒子が、数珠状に連結した複数の一次粒子を含む鎖状の構造を形成している、［１］に記載の積層体。
［３］前記無機化合物粒子と前記ポリマーとが、下記式１で表される構造を有するカップリング剤を介して結合している、［１］又は［２］に記載の積層体。
Ｘ−Ｓｉ（Ｒ１）（Ｒ２）（Ｒ３） ・・・（式１）
［式中、Ｘは、重合開始基であり、Ｒ１及びＲ２は、それぞれ独立に、炭素原子数が１〜１０のアルキル基であり、Ｒ３は、炭素原子数が１〜１０のアルコキシ基、水素原子、水酸基又はハロゲン原子である。］
［４］前記ポリマーの分子量分布が２．３以下である、［１］〜［３］のいずれかに記載の積層体。
［５］前記ポリマーが、メタクリル酸エステル又はアクリル酸エステルをモノマー単位として含む、［１］〜［４］のいずれかに記載の積層体。
［６］前記ポリマーが、少なくとも１つの架橋性官能基を含む、［１］〜［５］のいずれかに記載の積層体。
［７］前記ポリマーの数平均分子量Ｍｎが、１００００〜１０００００ｇ／ｍｏｌである、［１］〜［６］のいずれかに記載の積層体。
［８］前記無機化合物粒子の含有量が、前記有機無機複合体の全体積を基準として５５〜９４体積％である、［１］〜［７］のいずれかに記載の積層体。
［９］前記有機無機複合膜が、理論屈折率より０．０２０以上低い屈折率を有する、［１］〜［８］のいずれかに記載の積層体。
［１０］前記有機無機複合膜の屈折率が１．３５以下である、［１］〜［９］のいずれか１項に記載の積層体。
［１１］前記有機無機複合膜の最小反射率が１％以下である、［１］〜［１０］のいずれか１項に記載の積層体。
［１２］前記有機無機複合膜が、光硬化又は熱硬化されている、［１］〜［１１］のいずれか１項に記載の積層体。
［１３］前記有機無機複合膜の厚みが、８０ｎｍ〜２μｍである、［１］〜［１２］のいずれか１項に記載の積層体。
［１４］前記粘着剤のガラス転移温度が０℃以下である、［１］〜［１３］のいずれかに記載の積層体。
［１５］前記粘着剤が、アクリル酸エステルとアクリル酸との共重合体を含む、［１］〜［１４］のいずれかに記載の積層体。
［１６］前記接着剤が、硬化型接着剤を含む、［１］〜［１５］のいずれかに記載の積層体。
［１７］導電フィルムを更に有する、［１］〜［１６］のいずれかに記載の積層体。
［１８］偏光子を更に有する、［１］〜［１７］のいずれかに記載の積層体。
［１９］プリズムシート又は拡散板を更に有する、［１］〜［１８］のいずれかに記載の積層体。
［２０］位相差フィルムを更に有する、［１］〜［１９］のいずれかに記載の積層体。
［２１］輝度向上フィルムを更に有する、［１］〜［２０］のいずれかに記載の積層体。
［２２］支持体を更に有し、
前記支持体、前記有機無機複合膜及び前記接続層がこの順で積層した構成を有する、［１］〜［２１］のいずれかに記載の積層体。
［２３］支持体を更に有し、
前記有機無機複合膜及び前記接続層をそれぞれ２以上有し、
前記支持体、第一の前記有機無機複合膜、第一の前記接続層、第二の前記有機無機複合膜及び第二の前記接続層がこの順で積層した構成を有する、［１］〜［２２］のいずれか一項に記載の積層体。
［２４］前記支持体が、トリアセチルセルロースフィルム、ポリエチレンテレフタラートフィルム、アクリルフィルム及び環状ポリオレフィンフィルムからなる群より選択される、［１］〜［２３］のいずれかに記載の積層体。
［２５］［１］〜［２４］のいずれかに記載の積層体を備える、偏光板。
［２６］［１］〜［２４］のいずれかに記載の積層体を備える、光学材料。
［２７］［１］〜［２４］のいずれかに記載の積層体を備える、表示装置。
［２８］［１］〜［２４］のいずれかに記載の積層体を備える、タッチパネル。
[1] An organic-inorganic composite film containing an organic-inorganic composite containing inorganic compound particles and a polymer bonded to the inorganic compound particles;
A connection layer containing an adhesive or an adhesive, and
The laminated body whose ratio of the space | gap in the said organic inorganic composite film is 3-90 volume% on the basis of the volume of the said organic inorganic composite film.
[2] The laminate according to [1], wherein the inorganic compound particles form a chain structure including a plurality of primary particles connected in a bead shape.
[3] The laminate according to [1] or [2], wherein the inorganic compound particles and the polymer are bonded via a coupling agent having a structure represented by the following formula 1.
X-Si (R1) (R2) (R3) (Formula 1)
[Wherein, X is a polymerization initiating group, R 1 and R 2 are each independently an alkyl group having 1 to 10 carbon atoms, R 3 is an alkoxy group having 1 to 10 carbon atoms, hydrogen An atom, a hydroxyl group or a halogen atom. ]
[4] The laminate according to any one of [1] to [3], wherein the polymer has a molecular weight distribution of 2.3 or less.
[5] The laminate according to any one of [1] to [4], wherein the polymer includes a methacrylic acid ester or an acrylic acid ester as a monomer unit.
[6] The laminate according to any one of [1] to [5], wherein the polymer includes at least one crosslinkable functional group.
[7] The laminate according to any one of [1] to [6], wherein the polymer has a number average molecular weight Mn of 10,000 to 100,000 g / mol.
[8] The laminate according to any one of [1] to [7], wherein the content of the inorganic compound particles is 55 to 94% by volume based on the total volume of the organic-inorganic composite.
[9] The laminate according to any one of [1] to [8], wherein the organic-inorganic composite film has a refractive index lower than the theoretical refractive index by 0.020 or more.
[10] The laminate according to any one of [1] to [9], wherein the organic-inorganic composite film has a refractive index of 1.35 or less.
[11] The laminate according to any one of [1] to [10], wherein the organic-inorganic composite film has a minimum reflectance of 1% or less.
[12] The laminate according to any one of [1] to [11], wherein the organic-inorganic composite film is photocured or thermally cured.
[13] The laminate according to any one of [1] to [12], wherein the organic-inorganic composite film has a thickness of 80 nm to 2 μm.
[14] The laminate according to any one of [1] to [13], wherein the pressure-sensitive adhesive has a glass transition temperature of 0 ° C. or lower.
[15] The laminate according to any one of [1] to [14], wherein the pressure-sensitive adhesive includes a copolymer of acrylic acid ester and acrylic acid.
[16] The laminate according to any one of [1] to [15], wherein the adhesive includes a curable adhesive.
[17] The laminate according to any one of [1] to [16], further having a conductive film.
[18] The laminate according to any one of [1] to [17], further comprising a polarizer.
[19] The laminate according to any one of [1] to [18], further comprising a prism sheet or a diffusion plate.
[20] The laminate according to any one of [1] to [19], further comprising a retardation film.
[21] The laminate according to any one of [1] to [20], further including a brightness enhancement film.
[22] Further comprising a support,
The laminate according to any one of [1] to [21], wherein the support, the organic-inorganic composite film, and the connection layer are laminated in this order.
[23] Further comprising a support,
Each having two or more of the organic-inorganic composite film and the connection layer;
The support, the first organic-inorganic composite film, the first connection layer, the second organic-inorganic composite film, and the second connection layer are stacked in this order [1] to [ 22]. The laminate according to any one of [22].
[24] The laminate according to any one of [1] to [23], wherein the support is selected from the group consisting of a triacetyl cellulose film, a polyethylene terephthalate film, an acrylic film, and a cyclic polyolefin film.
[25] A polarizing plate comprising the laminate according to any one of [1] to [24].
[26] An optical material comprising the laminate according to any one of [1] to [24].
[27] A display device comprising the laminate according to any one of [1] to [24].
[28] A touch panel comprising the laminate according to any one of [1] to [24].
本発明によれば、透過性に優れた安価な積層体と、それを使用した、高品位の表示装置等を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the cheap laminated body excellent in the transmittance | permeability and the high quality display apparatus etc. which used it can be provided.
以下、本発明を実施するための形態（以下、本実施形態）について詳細に説明する。なお、本発明は、本実施形態に限定されるものではなく、その要旨の範囲内で種々変形して実施することができる。 Hereinafter, modes for carrying out the present invention (hereinafter referred to as the present embodiment) will be described in detail. In addition, this invention is not limited to this embodiment, It can implement in various deformation | transformation within the range of the summary.
［（Ａ）無機化合物粒子］
無機化合物とは、有機化合物以外の化合物であり、具体的には、一部の炭素化合物除き、炭素以外の元素で構成される化合物を指す。
[(A) Inorganic compound particles]
An inorganic compound is a compound other than an organic compound, and specifically refers to a compound composed of an element other than carbon, excluding some carbon compounds.
無機化合物を構成する元素としては、例えば、周期律表１〜１６族の元素が挙げられる。この元素は、特に限定されるものではないが、周期律表２〜１４族に属する元素が好ましい。その具体例としては、２族元素（Ｍｇ、Ｃａ、Ｂａ等）、３族元素（Ｌａ、Ｃｅ、Ｅｕ、Ａｃ、Ｔｈ等）、４族元素（Ｔｉ、Ｚｒ、Ｈｆ等）、５族元素（Ｖ、Ｎｂ、Ｔａ等）、６族元素（Ｃｒ、Ｍｏ、Ｗ等）、７族元素（Ｍｎ、Ｒｅ等）、８族元素（Ｆｅ、Ｒｕ、Ｏｓ等）、９族元素（Ｃｏ、Ｒｈ、Ｉｒ等）、１０族元素（Ｎｉ、Ｐｄ、Ｐｔ等）、１１族元素（Ｃｕ、Ａｇ、Ａｕ等）、１２族元素（Ｚｎ、Ｃｄ等）、１３族元素（Ａｌ、Ｇａ、Ｉｎ等）、及び１４族元素（Ｓｉ、Ｇｅ、Ｓｎ、Ｐｂ等）が挙げられる。 As an element which comprises an inorganic compound, the element of the periodic table 1-16 group is mentioned, for example. Although this element is not specifically limited, the element which belongs to periodic table group 2-14 is preferable. Specific examples thereof include group 2 elements (Mg, Ca, Ba, etc.), group 3 elements (La, Ce, Eu, Ac, Th, etc.), group 4 elements (Ti, Zr, Hf, etc.), group 5 elements ( V, Nb, Ta, etc.), Group 6 elements (Cr, Mo, W, etc.), Group 7 elements (Mn, Re, etc.), Group 8 elements (Fe, Ru, Os, etc.), Group 9 elements (Co, Rh, etc.) Ir, etc.), Group 10 elements (Ni, Pd, Pt, etc.), Group 11 elements (Cu, Ag, Au, etc.), Group 12 elements (Zn, Cd, etc.), Group 13 elements (Al, Ga, In, etc.), And Group 14 elements (Si, Ge, Sn, Pb, etc.).
これら元素を含む無機化合物としては、例えば、酸化物（複合酸化物を含む）、ハロゲン化物（フッ化物、塩化物、臭化物、ヨウ化物）、オキソ酸塩（硝酸塩、硫酸塩、リン酸塩、ホウ酸塩、過塩素酸塩、炭酸塩等）、一酸化炭素、二酸化炭素及び二硫化炭素等の陰性の元素と上記元素とから形成される化合物、並びに、青酸、青酸塩、シアン酸塩、チオシアン酸塩及び炭化物などの塩が挙げられる。 Examples of inorganic compounds containing these elements include oxides (including complex oxides), halides (fluorides, chlorides, bromides, iodides), oxo acid salts (nitrates, sulfates, phosphates, borons). Acid salts, perchlorates, carbonates, etc.), compounds formed from negative elements such as carbon monoxide, carbon dioxide and carbon disulfide and the above elements, as well as cyanic acid, cyanate, cyanate, thiocyanate And salts such as acid salts and carbides.
炭素化合物のうち、例外的に無機化合物に分類されるものには、例えば、ダイヤモンド、ロンズデーライト、グラファイト、グラフェン、フラーレン類（バックミンスターフラーレン、カーボンナノチューブ、カーボンナノホーン等）、ガラス状炭素、カルビン、アモルファス炭素、カーボンナノフォームなど炭素の同素体等が挙げられる。 Among the carbon compounds, those that are exceptionally classified as inorganic compounds include, for example, diamond, ronsdaylite, graphite, graphene, fullerenes (buckminsterfullerene, carbon nanotube, carbon nanohorn, etc.), glassy carbon, and calvin. And carbon allotropes such as amorphous carbon and carbon nanofoam.
１つの無機化合物粒子は、上記元素のうち１種又は２種以上の含んでいてもよい。複数種の元素は、粒子中に均一に存在していても、偏在していてもよく、ある元素の化合物の粒子の表面が、別の元素の化合物によって被覆されていてもよい。これら無機化合物は、単独で使用しても、複数を組み合わせて使用してもよい。 One inorganic compound particle may contain one or more of the above elements. The plural kinds of elements may be present uniformly or unevenly in the particle, and the surface of the particle of a compound of one element may be coated with a compound of another element. These inorganic compounds may be used alone or in combination.
無機化合物粒子（特に球状粒子）の大きさは、特に限定されるものではないが、平均粒径（粒子の外径の平均値）は好ましくは１〜２００ｎｍである。平均粒径が２００ｎｍより大きいと、有機無機複合体を光学材料として使用したときに、光の散乱などの問題が発生し易くなる傾向があり、平均粒径が１ｎｍ未満であると、無機化合物粒子を構成する物質固有の特性が変化する可能性がある。また、無機化合物粒子間の空隙を効果的に形成することが困難になる。同様の観点から、無機化合物粒子の平均粒径はより好ましくは１〜１５０ｎｍ、更に好ましくは１０〜１００ｎｍである。特に、成膜性の有機無機複合体、及び、それを利用したコーティング膜、成形体、光学材料等に透明性が要求される場合には、粒子の大きさが、レイリー散乱領域に入る必要があるため、無機化合物粒子の平均粒径が１０〜７０ｎｍであることが好ましく、１０〜６０ｎｍであることが更に好ましい。無機化合物粒子の平均粒径の測定方法は後述の実施例において詳細に説明される。 The size of the inorganic compound particles (particularly spherical particles) is not particularly limited, but the average particle size (average value of the outer diameter of the particles) is preferably 1 to 200 nm. When the average particle size is larger than 200 nm, when an organic-inorganic composite is used as an optical material, problems such as light scattering tend to occur. When the average particle size is less than 1 nm, inorganic compound particles There is a possibility that the characteristic characteristic of the substance constituting the material changes. Moreover, it becomes difficult to effectively form voids between the inorganic compound particles. From the same viewpoint, the average particle size of the inorganic compound particles is more preferably 1 to 150 nm, and still more preferably 10 to 100 nm. In particular, when transparency is required for a film-forming organic-inorganic composite, and a coating film, molded product, optical material, etc. using the same, the size of the particle needs to be in the Rayleigh scattering region. Therefore, the average particle size of the inorganic compound particles is preferably 10 to 70 nm, and more preferably 10 to 60 nm. A method for measuring the average particle diameter of the inorganic compound particles will be described in detail in Examples described later.
無機化合物粒子の形状や結晶形は、特に限定されるものではなく、例えば、球状、結晶状、鱗片状、柱状、管状、繊維状、中空状、多孔質状、数珠状等、様々な形状であってよい。中でも、空隙を効果的に形成できる構造という観点から、中空、数珠状、又は球状が好ましい。 The shape and crystal form of the inorganic compound particles are not particularly limited, and for example, various shapes such as spherical, crystalline, scale-like, columnar, tubular, fibrous, hollow, porous, beaded, etc. It may be. Among these, from the viewpoint of a structure that can effectively form voids, a hollow shape, a bead shape, or a spherical shape is preferable.
無機酸化物粒子とは、炭素以外の元素、例えば、Ｓｉ、Ｚｒ、Ｔｉ、Ａｒ、Ｓｎ、Ｃａ、Ｂａ等の酸化物から形成された粒子であれば、特に限定されるものではないが、入手のし易さの観点から、ＳｉＯ２、ＺｒＯ２、ＴｉＯ２、Ａｌ２Ｏ３、ＢａＴｉＯ３、及びＣａＣＯ３が好ましく、特に好ましくは、ＳｉＯ２である。無機化合物は、ＺｒＯ２粒子又はＴｉＯ２粒子と、これら粒子の表面を被覆するＳｉＯ２、及びＡｌ２Ｏ３等とを有していてもよい。これらは、単独で使用しても、複数を組み合わせて使用してもよい。 The inorganic oxide particle is not particularly limited as long as it is a particle formed from an element other than carbon, for example, an oxide such as Si, Zr, Ti, Ar, Sn, Ca, Ba, etc. From the viewpoint of easy handling, SiO 2 , ZrO 2 , TiO 2 , Al 2 O 3 , BaTiO 3 , and CaCO 3 are preferable, and SiO 2 is particularly preferable. The inorganic compound may have ZrO 2 particles or TiO 2 particles, and SiO 2 and Al 2 O 3 that cover the surfaces of these particles. These may be used alone or in combination.
［（Ａ１）：数珠状に連結した複数の一次粒子を含む鎖状の構造を形成する無機化合物粒子］
複数の一次粒子が数珠状に連結した鎖状の構造を有する無機化合物粒子（以下、「数珠状無機化合物粒子」という。）とは、限定されるものではないが、粒子が数珠状に連結及び／又は分岐した形状を持つ。具体的には例えば、図２に示すように、球状のコロイダルシリカが数珠状に連結した鎖状の構造を有するもの、及び連結したコロイダルシリカが分岐したもの（以下、「数珠状シリカ」という。）などを挙げることができる。上記数珠状シリカは球状シリカの一次粒子を２価以上の金属イオンを介在させ粒子−粒子間を結合させたものである。少なくとも３個以上、更に好ましくは５個以上、より好ましくは７個以上の一次粒子が連結されている。数珠状無機化合物粒子は、数珠状に連結した一次粒子が分岐したものも包含する。数珠状無機化合物粒子をＳＥＭ、及びＴＥＭ等の電子顕微鏡を用いて倍率５０，０００〜１００，０００倍で観察したとき、視野に存在する粒子のうち、単独の球状粒子ではなく上記鎖状の構造を有する、及び分岐した構造を有する形態で存在している粒子の数が、少なくとも５０％以上、好ましくは７０％以上、更に好ましくは９０〜１００％の範囲にある。数珠状無機化合物粒子は、その立体的な障害により、他の数珠状無機化合物粒子が空間を密に占めることができず、その結果、より空隙率の高い膜を容易に形成できるため、特に好ましい。更には、上述の数珠状無機化合物粒子のようなＬ／Ｄが大きな無機化合物粒子を使用した場合、無機含有量によっては膜表面に凹凸構造が形成されるため、蓮の葉の表面を水滴が転がるのと同様の優れた撥水性を発現するため、特に好ましい。
[(A1): Inorganic compound particles forming a chain structure including a plurality of primary particles connected in a bead shape]
Inorganic compound particles having a chain structure in which a plurality of primary particles are connected in a bead shape (hereinafter referred to as “bead-like inorganic compound particles”) are not limited, but the particles are connected in a bead shape. / Or has a branched shape. Specifically, for example, as shown in FIG. 2, spherical colloidal silica has a chain structure connected in a bead shape, and connected colloidal silica is branched (hereinafter referred to as “beaded silica”). ) And the like. The beaded silica is obtained by bonding primary particles of spherical silica with particles between particles through interposition of divalent or higher metal ions. At least 3 or more, more preferably 5 or more, more preferably 7 or more primary particles are linked. The beaded inorganic compound particles include those in which primary particles connected in a beaded shape are branched. When rosary inorganic compound particles are observed with an electron microscope such as SEM and TEM at a magnification of 50,000 to 100,000, among the particles present in the field of view, the above chain structure is not a single spherical particle. The number of particles present in a form having a branched structure is at least 50% or more, preferably 70% or more, more preferably 90 to 100%. The bead-like inorganic compound particles are particularly preferred because other bead-like inorganic compound particles cannot occupy the space densely due to their steric hindrance, and as a result, a film having a higher porosity can be easily formed. . Further, when inorganic compound particles having a large L / D such as the above-mentioned bead-shaped inorganic compound particles are used, depending on the inorganic content, an uneven structure is formed on the film surface. It is particularly preferable because it exhibits excellent water repellency similar to rolling.
［（Ａ２）：円形度０．５〜１の無機化合物粒子］
無機化合物粒子間の空隙を効果的に形成できれば、円形度０．５〜１の無機化合物粒子を使用しても良い。均一性維持の観点から、この円形度は、より好ましくは０．７〜１、更に好ましくは０．８５〜１である。円形度の測定方法については後述の実施例において詳細に説明される。
[(A2): Inorganic compound particles having a circularity of 0.5 to 1]
As long as voids between the inorganic compound particles can be effectively formed, inorganic compound particles having a circularity of 0.5 to 1 may be used. From the viewpoint of maintaining uniformity, the circularity is more preferably 0.7 to 1, and still more preferably 0.85 to 1. The method for measuring the circularity will be described in detail in the examples described later.
［（Ａ３）：空洞率５〜８０％の無機化合物粒子］
無機化合物粒子の空洞率は、特に限定されるものではないが、透明性と屈折率制御の容易性の観点から、粒子内の空洞率が５〜８０％である無機化合物粒子を使用しても良い。
[(A3): Inorganic compound particles having a cavity ratio of 5 to 80%]
The void ratio of the inorganic compound particles is not particularly limited, but from the viewpoint of transparency and ease of controlling the refractive index, inorganic compound particles having a void ratio in the particles of 5 to 80% may be used. good.
空洞率が５体積％未満であると、屈折率制御効果が小さく、８０体積％を超えると強度が低くなり、光学材料等に加工した際に破損の可能性がある。一方、空洞率が５〜８０体積％であることにより、屈折率制御能に優れ、見栄えのよいコーティング膜を得ることができる。同様の観点から、この空洞率は、より好ましくは１０〜６０体積％、更に好ましくは１５〜４０体積％である。空洞率は「空洞率（体積％）＝（空洞部分の体積）／（粒子全体の体積）×１００」で表され、空洞率の測定方法については後述の実施例において詳細に説明される。 When the void ratio is less than 5% by volume, the refractive index control effect is small, and when it exceeds 80% by volume, the strength is lowered, and there is a possibility of breakage when processed into an optical material or the like. On the other hand, when the void ratio is 5 to 80% by volume, a coating film having excellent refractive index control ability and good appearance can be obtained. From the same viewpoint, the void ratio is more preferably 10 to 60% by volume, and still more preferably 15 to 40% by volume. The void ratio is expressed by “cavity ratio (volume%) = (volume of the cavity portion) / (volume of the entire particle) × 100”, and the method for measuring the void ratio will be described in detail in Examples described later.
これらの無機化合物粒子の場合、無機化合物粒子間の空隙に加えて、無機化合物粒子内にも空洞が存在する。そのため、より屈折率の低い有機無機複合膜が得られる点で好ましい。その形態は、特に限定されるものではないが、屈折率制御の観点から、管状粒子、中空粒子、多孔質粒子が好ましく、特に好ましくは中空粒子と多孔質粒子である。中でも、入手のし易さの観点から、球状中空シリカ粒子と多孔質シリカが好ましい。 In the case of these inorganic compound particles, there are cavities in the inorganic compound particles in addition to the voids between the inorganic compound particles. Therefore, it is preferable in that an organic-inorganic composite film having a lower refractive index can be obtained. The form is not particularly limited, but from the viewpoint of controlling the refractive index, tubular particles, hollow particles, and porous particles are preferable, and hollow particles and porous particles are particularly preferable. Among these, spherical hollow silica particles and porous silica are preferable from the viewpoint of availability.
上記中空粒子の外殻厚みは特に限定されるものではないが、屈折率と成膜性のバランスの観点から、好ましくは１〜３０ｎｍ、更に好ましくは５〜２０ｎｍ、特に好ましくは７〜１２ｎｍである。 The outer shell thickness of the hollow particles is not particularly limited, but is preferably 1 to 30 nm, more preferably 5 to 20 nm, and particularly preferably 7 to 12 nm from the viewpoint of the balance between the refractive index and the film formability. .
中空粒子の屈折率は、特に限定されるものではないが、屈折率制御効果が得られやすいことから、１．０５〜１．４程度であることが好ましい。屈折率設計と成膜性のバランスの観点からは、無機化合物粒子の屈折率は、より好ましくは１．１〜１．３５、更に好ましくは１．１５〜１．３である。 The refractive index of the hollow particles is not particularly limited, but is preferably about 1.05 to 1.4 because a refractive index control effect is easily obtained. From the viewpoint of the balance between the refractive index design and the film formability, the refractive index of the inorganic compound particles is more preferably 1.1 to 1.35, and still more preferably 1.15 to 1.3.
［（Ｂ）ポリマー］
有機無機複合体を構成するポリマーは、その少なくとも一部は、無機化合物粒子の表面に、後述のカップリング剤（重合開始基を有するカップリング剤）を介して結合している。無機化合物粒子とポリマーとの結合は、結合の強さの観点から、共有結合であることが好ましい。このポリマーは、１種又は２種以上のラジカル重合性モノマーをモノマー単位として含んでいる。また、有機無機複合体は、異なるモノマー単位から構成される複数種のポリマーを含有していてよい。
[(B) Polymer]
At least a part of the polymer constituting the organic-inorganic composite is bonded to the surface of the inorganic compound particles via a coupling agent (coupling agent having a polymerization initiating group) described later. The bond between the inorganic compound particles and the polymer is preferably a covalent bond from the viewpoint of bond strength. This polymer contains one or more radically polymerizable monomers as monomer units. The organic-inorganic composite may contain a plurality of types of polymers composed of different monomer units.
＜カップリング剤＞
本実施形態におけるカップリング剤は、無機化合物粒子表面と、上述の有機ポリマーとを連結するために用いられる化合物である。このカップリング剤は、重合開始基と、無機化合物粒子表面と反応して結合を生成する官能基とを有する化合物であれば、特に限定されるものではない。このときの無機化合物粒子表面は、無機化合物そのものから形成されていてもよいし、表面処理されていてもよい。ここでいう表面処理とは、化学反応、熱処理、光照射、プラズマ照射、放射線照射等により、無機化合物粒子表面を官能基により修飾することである。
<Coupling agent>
The coupling agent in this embodiment is a compound used in order to connect the inorganic compound particle surface and the above-mentioned organic polymer. The coupling agent is not particularly limited as long as it is a compound having a polymerization initiating group and a functional group that reacts with the surface of the inorganic compound particles to form a bond. The surface of the inorganic compound particles at this time may be formed from the inorganic compound itself or may be surface-treated. The surface treatment here is to modify the surface of the inorganic compound particles with a functional group by chemical reaction, heat treatment, light irradiation, plasma irradiation, radiation irradiation or the like.
カップリング剤を、無機化合物粒子表面と結合させる方法としては、特に限定されるものではないが、例えば、無機化合物粒子表面の水酸基とカップリング剤とを反応させる方法や、無機化合物粒子表面の表面処理により導入された官能基とカップリング剤とを反応させる方法がある。無機化合物粒子に結合したカップリング剤に、更にカップリング剤を反応させて、複数のカップリング剤を連結することも可能である。また、カップリング剤の種類によっては、水や触媒を併用してもよい。 The method for bonding the coupling agent to the surface of the inorganic compound particles is not particularly limited. For example, the method of reacting the hydroxyl group on the surface of the inorganic compound particle with the coupling agent, or the surface of the surface of the inorganic compound particle There is a method of reacting a functional group introduced by treatment with a coupling agent. It is also possible to connect a plurality of coupling agents by further reacting the coupling agent bound to the inorganic compound particles with a coupling agent. Depending on the type of coupling agent, water or a catalyst may be used in combination.
カップリング剤が有する官能基は、特に制限はないが、例えば無機化合物粒子表面の水酸基との反応により結合を生成する場合には、リン酸基、カルボキシ基、酸ハライド基、酸無水物基、イソシアネート基、グリシジル基、クロロシリル基、アルコキシシリル基、シラノール基、アミノ基、ホスホニウム基及びスルホニウム基等が挙げられる。中でも、反応性と、酸残存量や着色とのバランスの観点から、好ましいのは、イソシアネート基、クロロシリル基、アルコキシシリル基及びシラノール基であり、更に好ましくは、クロロシリル基及びアルコキシシリル基である。 The functional group possessed by the coupling agent is not particularly limited. For example, when a bond is formed by reaction with a hydroxyl group on the surface of the inorganic compound particle, a phosphate group, a carboxy group, an acid halide group, an acid anhydride group, Examples thereof include an isocyanate group, a glycidyl group, a chlorosilyl group, an alkoxysilyl group, a silanol group, an amino group, a phosphonium group, and a sulfonium group. Among these, from the viewpoint of the balance between the reactivity and the remaining amount of acid and coloring, preferred are an isocyanate group, a chlorosilyl group, an alkoxysilyl group, and a silanol group, and more preferred are a chlorosilyl group and an alkoxysilyl group.
カップリング剤の官能基数は、特に限定されるものではないが、１官能又は２官能であることが好ましく、特に好ましくは１官能である。官能基が２個以上存在すると、カップリング剤の縮合物（副生物）が生成し、その除去が困難になる。また、有機無機複合膜中に未反応の官能基が残存するため、加熱乾燥、加熱加工する工程などによってはアルコールや水などを生成し、膜が発泡する要因となる。また、無機化合物粒子が凝集する要因にもなりうるためである。 The number of functional groups of the coupling agent is not particularly limited, but monofunctional or bifunctional is preferable, and monofunctional is particularly preferable. When two or more functional groups are present, a condensate (by-product) of the coupling agent is generated and it is difficult to remove the functional group. In addition, since unreacted functional groups remain in the organic-inorganic composite film, alcohol, water, etc. are generated depending on the heat drying, heat processing, and the like, causing the film to foam. Moreover, it is because it may become a factor which an inorganic compound particle aggregates.
カップリング剤が有する重合開始基は、重合開始能を有する官能基であれば、特に限定されるものではない。例えば、後述のニトロキシド媒介ラジカル重合（以下、「ＮＭＰ」という。）、原子移動ラジカル重合（以下、「ＡＴＲＰ」という。）、可逆的付加・脱離連鎖移動重合（以下、「ＲＡＦＴ」という。）に用いられる重合開始基が挙げられる。 The polymerization initiating group possessed by the coupling agent is not particularly limited as long as it is a functional group having a polymerization initiating ability. For example, nitroxide-mediated radical polymerization (hereinafter referred to as “NMP”), atom transfer radical polymerization (hereinafter referred to as “ATRP”), and reversible addition / elimination chain transfer polymerization (hereinafter referred to as “RAFT”). And a polymerization initiating group used in the above.
ＮＭＰにおける重合開始基は、ニトロキシド基が結合している基であれば、特に限定されるものではない。 The polymerization initiating group in NMP is not particularly limited as long as it is a group to which a nitroxide group is bonded.
ＡＴＲＰにおける重合開始基は、典型的には、ハロゲン原子を含む基である。ハロゲン原子の結合解離エネルギーが低いことが好ましい。例えば、３級炭素原子に結合したハロゲン原子、ビニル基、ビニリデン基及びフェニル基等の不飽和炭素−炭素結合に隣接する炭素原子に結合したハロゲン原子、カルボニル基、シアノ基及びスルホニル基等のヘテロ原子含有共役性基に直接結合するか又はこれらに隣接する原子に結合したハロゲン原子が導入された基が、好ましい構造として挙げられる。より具体的には、下記一般式（１）で表される有機ハロゲン化物基、及び、一般式（２）で表されるハロゲン化スルホニル基が好適である。 The polymerization initiating group in ATRP is typically a group containing a halogen atom. It is preferable that the bond dissociation energy of the halogen atom is low. For example, a halogen atom bonded to a tertiary carbon atom, a halogen atom bonded to a carbon atom adjacent to an unsaturated carbon-carbon bond such as a vinyl group, a vinylidene group or a phenyl group, a hetero group such as a carbonyl group, a cyano group or a sulfonyl group. A preferable structure includes a group in which a halogen atom bonded directly to an atom-containing conjugated group or bonded to an atom adjacent thereto is introduced. More specifically, an organic halide group represented by the following general formula (1) and a halogenated sulfonyl group represented by the general formula (2) are preferable.
式（１）及び（２）中、Ｒ１及びＲ２は、それぞれ独立に水素原子、置換基を有していてもよい炭素数１〜２０のアルキル基、置換基を有していてもよいアリル基、置換基を有していてもよい炭素数６〜２０のアリール基、アルキルアリール基、又は、置換基を有していてもよいアルキルアリール基を示し、Ｚはハロゲン原子を示す。 In formulas (1) and (2), R 1 and R 2 each independently have a hydrogen atom, a C 1-20 alkyl group that may have a substituent, or a substituent. An allyl group, an aryl group having 6 to 20 carbon atoms that may have a substituent, an alkylaryl group, or an alkylaryl group that may have a substituent, and Z represents a halogen atom.
式（１）の重合開始基は、下記一般式（３）に示されるように、カルボニル基を有するものであってもよい。式（３）中、Ｒ１、Ｒ２及びＺは、式（１）中のＲ１、Ｒ２及びＺと同義である。 The polymerization initiating group of the formula (1) may have a carbonyl group as shown in the following general formula (3). In the formula (3), R 1, R 2 and Z have the same meanings as R 1, R 2 and Z in the formula (1).
式（３）の重合開始基の具体例を下記化学式に示す。 Specific examples of the polymerization initiating group of the formula (3) are shown in the following chemical formula.
ＲＡＦＴにおける重合開始基は、一般的なラジカル重合開始基であれば、特に限定されるものではない。また、ＲＡＦＴ剤として機能するイオウ原子を含有する基を重合開始基として使用することもできる。重合開始基の例としては、トリチオカーボネート、ジチオエステル、チオアミド、チオカルバメート、ジチオカルバメート、チオウラン、チオ尿素、ジチオオキサミド、チオケトン及びトリスルフィドが挙げられる。 The polymerization initiating group in RAFT is not particularly limited as long as it is a general radical polymerization initiating group. Moreover, the group containing the sulfur atom which functions as a RAFT agent can also be used as a polymerization initiating group. Examples of the polymerization initiating group include trithiocarbonate, dithioester, thioamide, thiocarbamate, dithiocarbamate, thiouranium, thiourea, dithiooxamide, thioketone, and trisulfide.
カップリング剤は、下記式１で表される構造を有することが好ましい。
Ｘ−Ｓｉ（Ｒ１）（Ｒ２）（Ｒ３） ・・・（式１）
式１中、Ｘは、上述の重合開始基であり、Ｒ１及びＲ２は、それぞれ独立に、炭素原子数が１〜１０のアルキル基であり、Ｒ３は、炭素原子数が１〜１０のアルコキシ基、水素原子、水酸基又はハロゲン原子である。
The coupling agent preferably has a structure represented by the following formula 1.
X-Si (R1) (R2) (R3) (Formula 1)
In Formula 1, X is the above-mentioned polymerization initiating group, R1 and R2 are each independently an alkyl group having 1 to 10 carbon atoms, and R3 is an alkoxy group having 1 to 10 carbon atoms. , A hydrogen atom, a hydroxyl group or a halogen atom.
好適なカップリング剤の具体例としては、以下のようなシラン化合物がある。
・３−（２−ブロモイソブチロキシ）プロピルジメチルクロロシラン（Ｃａｓ番号：３７０８７０−８１−８）
・プロピオン酸，２−ブロモ−２−メチル−，３−（ジクロロメチルシリル）プロピル エステル（Ｃａｓ番号：１０５７２６０−３９−５）
・プロピオン酸，２−ブロモ−２−メチル−，３−（トリクロロシリル）プロピル エステル（Ｃａｓ番号：６８８３５９−８４−４）
・３−（メトキシジメチルシリルプロピル）−２−ブロモ−２−メチルプロピオネート（Ｃａｓ番号：５３１５０５−２７−８）
・３−（ジメトキシメチルシリルプロピル）−２−ブロモ−２−メチルプロピオネート（Ｃａｓ番号：１１８６６６７−６０−６）
・３−（トリメトキシシリルプロピル）−２−ブロモ−２−メチルプロピオネート（Ｃａｓ番号：３１４０２１−９７−１）
・（３−（２−ブロモイソブチリル）プロピル）ジメチルエトキシシラン（Ｃａｓ番号：２６５１１９−８６−６）
・（３−（２−ブロモイソブチリル）プロピル）メチルジエトキシシラン（Ｃａｓ番号：１１８６６６７−６５−１）
・プロピオン酸，２−ブロモ−２−メチル−，３−（トリエトキシシリル）プロピル エステル（Ｃａｓ番号：８８０３３９−３１−１）
・プロピオン酸，２−ブロモ−，３−（クロロジメチルシリル）プロピル エステル（Ｃａｓ番号：４３８００１−３６−６）
・プロピオン酸，２−ブロモ−，３−（トリクロロシリル）プロピル エステル（Ｃａｓ番号：６６３１７４−６４−９）
・プロピオン酸，２−ブロモ−，３−（メトキシジメチルシリル）プロピル エステル（Ｃａｓ番号：８６１８０７−４６−７）
・（３−（２−ブロモプロピオニル）プロピル）ジメチルエトキシシラン（Ｃａｓ番号：２６５１１９−８５−５）
・（３−（２−ブロモプロピオニル）プロピル）トリエトキシシラン（Ｃａｓ番号：１２３３５１３−０６−８）
Specific examples of suitable coupling agents include the following silane compounds.
3- (2-Bromoisobutyroxy) propyldimethylchlorosilane (Cas number: 370870-81-8)
Propionic acid, 2-bromo-2-methyl-, 3- (dichloromethylsilyl) propyl ester (Cas number: 1057260-39-5)
Propionic acid, 2-bromo-2-methyl-, 3- (trichlorosilyl) propyl ester (Cas number: 688359-84-4)
3- (methoxydimethylsilylpropyl) -2-bromo-2-methylpropionate (Cas number: 531505-27-8)
3- (Dimethoxymethylsilylpropyl) -2-bromo-2-methylpropionate (Cas number: 1186667-60-6)
3- (Trimethoxysilylpropyl) -2-bromo-2-methylpropionate (Cas number: 314021-97-1)
(3- (2-Bromoisobutyryl) propyl) dimethylethoxysilane (Cas number: 265119-86-6)
(3- (2-Bromoisobutyryl) propyl) methyldiethoxysilane (Cas number: 11866667-65-1)
Propionic acid, 2-bromo-2-methyl-, 3- (triethoxysilyl) propyl ester (Cas number: 880339-31-1)
Propionic acid, 2-bromo-, 3- (chlorodimethylsilyl) propyl ester (Cas number: 438001-36-6)
Propionic acid, 2-bromo-, 3- (trichlorosilyl) propyl ester (Cas number: 663174-64-9)
Propionic acid, 2-bromo-, 3- (methoxydimethylsilyl) propyl ester (Cas number: 861807-46-7)
(3- (2-Bromopropionyl) propyl) dimethylethoxysilane (Cas number: 265119-85-5)
(3- (2-Bromopropionyl) propyl) triethoxysilane (Cas number: 1233513-06-8)
上記ポリマーの重合形態は、特に限定されるものではないが、例えば、ホモポリマー、周期共重合ポリマー、ブロック共重合ポリマー、ランダム共重合ポリマー、グラジエント共重合ポリマー、テーパード共重合ポリマー又はグラフト共重合ポリマーが挙げられる。中でも、Ｔｇや屈折率等の物性制御の観点から、共重合ポリマーが好ましい。 The polymerization form of the polymer is not particularly limited. For example, a homopolymer, a periodic copolymer, a block copolymer, a random copolymer, a gradient copolymer, a tapered copolymer, or a graft copolymer Is mentioned. Among these, a copolymer is preferable from the viewpoint of controlling physical properties such as Tg and refractive index.
上記ポリマーは、汎用有機溶媒に対する溶解性や熱分解抑制の観点から、アクリル酸エステル類及びメタクリル酸エステル類のホモポリマー又は共重合ポリマーであることが好ましい。 The polymer is preferably a homopolymer or copolymer of acrylic acid esters and methacrylic acid esters from the viewpoint of solubility in general-purpose organic solvents and suppression of thermal decomposition.
ラジカル重合性のモノマーは、原子移動ラジカル重合（以下、「ＡＴＲＰ」という。）、又は可逆的付加・脱離連鎖移動重合（以下、「ＲＡＦＴ」という）で重合可能であることが好ましい。 The radical polymerizable monomer is preferably polymerizable by atom transfer radical polymerization (hereinafter referred to as “ATRP”) or reversible addition / elimination chain transfer polymerization (hereinafter referred to as “RAFT”).
上記モノマーとしては、例えば、エチレン、「ブタ−１，３−ジエン、２−メチルブタ−１，３−ジエン、２−クロロブタ−１，３−ジエンのようなジエン類」、「スチレン、α−メチルスチレン、４−メチルスチレン、４−ヒドロキシスチレン、アセトキシスチレン、４−クロロメチルスチレン２，３，４，５，６−ペンタフルオロスチレン、４−アミノスチレンなどのスチレン類」、「アクリル酸メチル、アクリル酸エチル、アクリル酸ｎ−ブチル、アクリル酸ｔｅｒｔ−ブチル、アクリル酸イソブチル、アクリル酸２−エチルヘキシル、アクリル酸オクチル、アクリル酸オクタデシル、アクリル酸シクロヘキシル、アクリル酸ベンジル、アクリル酸トリメチルシリル、アクリル酸アミド、アクリル酸２−（ジメチルアミノ）エチル、アクリル酸２，２，２−トリフルオロエチル、アクリル酸２，２，３，３，−テトラフルオロプロピル、アクリル酸１，１，１，３，３，３−ヘキサフルオロイソプロピル、アクリル酸１Ｈ，１Ｈ，２Ｈ，２Ｈ−ヘプタデカフルオロデシル、アクリル酸１Ｈ，１Ｈ，３Ｈ−ヘキサフルオロブチル、アクリル酸１Ｈ，１Ｈ，５Ｈ−オクタフルオロペンチル、アクリル酸１Ｈ，１Ｈ−ヘプタフルオロブチル、アクリル酸２−イソシアナトエチル、１，１−（ビスアクリロイルオキシメチル）エチルイソシアネートなどのアクリル酸エステル類」、「メタクリル酸メチル、メタクリル酸エチル、メタクリル酸ｎ−ブチル、メタクリル酸ｔｅｒｔ−ブチル、メタクリル酸イソブチル、メタクリル酸２−エチルヘキシル、メタクリル酸オクチル、メタクリル酸オクタデシル、メタクリル酸シクロヘキシル、メタクリル酸ベンジル、メタクリル酸トリメチルシリル、メタクリル酸アミド、メタクリル酸２−（ジメチルアミノ）エチル、メタクリル酸２−（ジエチルアミノ）エチル、メタクリル酸２，２，２−トリフルオロエチル、メタクリル酸１Ｈ，１Ｈ，２Ｈ，２Ｈ−ヘプタデカフルオロデシル、メタクリル酸１Ｈ，１Ｈ，３Ｈ−ヘキサフルオロブチル、メタクリル酸２，２，３，３，−テトラフルオロプロピル、メタクリル酸１Ｈ，１Ｈ，５Ｈ−オクタフルオロペンチル、メタクリル酸１Ｈ，１Ｈ，７Ｈ−ドデカフルオロペンチル、メタクリル酸２−イソシアナトエチル、メタクリル酸 ２−（０−［１’−メチルプロピリデンアミノ］カルボキシアミノ）エチル、２−［（３，５−ジメチルピラゾリル）カルボニルアミノ］エチルメタクリレートなどのメタクリル酸エステル類」、「アクリル酸２−ヒドロキシエチル、アクリル酸２−ヒドロキシプロピル、アクリル酸３−ヒドロキシプロピル、アクリル酸２−ヒドロキシブチル、アクリル酸３−ヒドロキシブチル、アクリル酸４−ヒドロキシブチル、アクリル酸２−ヒドロキシヘキシル、アクリル酸６−ヒドロキシヘキシル、アクリル酸３−パーフルオロブチル−２−ヒドロキシプロピル、アクリル酸３−パーフルオロヘキシル−２−ヒドロキシプロピル、アクリル酸３−パーフルオロオクチル−２−ヒドロキシプロピル、メタクリル酸２−ヒドロキシエチル、メタクリル酸２−ヒドロキシプロピル、メタクリル酸３−ヒドロキシプロピル、メタクリル酸２−ヒドロキシブチル、メタクリル酸３−ヒドロキシブチル、メタクリル酸４−ヒドロキシブチル、メタクリル酸６−ヒドロキシヘキシル、メタクリル酸シクロヘキシル、メタクリル酸３−パーフルオロブチル−２−ヒドロキシプロピル、メタクリル酸３−パーフルオロヘキシル−２−ヒドロキシプロピル、メタクリル酸３−パーフルオロオクチル−２−ヒドロキシプロピル、アクリルアミド、メタクリルアミド、Ｎ−シクロプロピルアクリルアミド、Ｎ，Ｎ−ジメチルアクリルアミド、Ｎ−ヒドロキシメチルアクリルアミド、Ｎ−イソプロピルアクリルアミド、アクリロニトリル、メタクリロニトリルなどの（メタ）アクリル酸誘導体」、「酢酸ビニル、プロピオン酸ビニル、安息香酸ビニル、酪酸ビニルのようなビニルエステル類」、「ビニルメチルエーテル、ビニルエチルエーテルなどのビニルエーテル類」、「ビニルメチルケトン、ビニルヘキシルケトン、ビニルケトン類、Ｎ−ビニルピロール、Ｎ−ビニルカルバゾル、Ｎ−ビニルインドール、Ｎ−ビニルピロリドンなどのＮ−ビニル化合物」、「アリルアルコール、塩化アリル、酢酸アリル、塩化ビニル、塩化ビニリデンのようなアリル化合物」、「フッ化ビニル、フッ化ビニリデンなどのフッ素アルキル基を有する化合物」、「アクリル酸グリシジル、メタクリル酸グリシジル、４−グリシジルスチレン等の官能性モノマー類」、「アクリル酸アリル、メタクリル酸アリル、ジアクリル酸無水物、ジアクリル酸１，２−エタンジイル、トリアクリル酸ペンタエリスリトール、テトラアクリル酸ペンタエリスリトール、ジビニルベンゼンなどの反応性二重結合を二つ以上有する化合物」などが挙げられる。中でも、コーティング膜や成形体の透明性を特に重視する場合は、スチレン類、アクリル酸エステル又はメタクリル酸エステルを選択することが好ましい。 Examples of the monomer include ethylene, “dienes such as buta-1,3-diene, 2-methylbuta-1,3-diene, 2-chlorobuta-1,3-diene”, “styrene, α-methyl. Styrenes such as styrene, 4-methylstyrene, 4-hydroxystyrene, acetoxystyrene, 4-chloromethylstyrene 2,3,4,5,6-pentafluorostyrene, 4-aminostyrene "," methyl acrylate, acrylic Ethyl acid, n-butyl acrylate, tert-butyl acrylate, isobutyl acrylate, 2-ethylhexyl acrylate, octyl acrylate, octadecyl acrylate, cyclohexyl acrylate, benzyl acrylate, trimethylsilyl acrylate, amide acrylate, acrylic Acid 2- (dimethylamino) ethyl, 2,2,2-trifluoroethyl laurate, 2,2,3,3-tetrafluoropropyl acrylate, 1,1,1,3,3,3-hexafluoroisopropyl acrylate, 1H, 1H acrylic acid , 2H, 2H-heptadecafluorodecyl, 1H, 1H, 3H-hexafluorobutyl acrylate, 1H, 1H, 5H-octafluoropentyl acrylate, 1H, 1H-heptafluorobutyl acrylate, 2-isocyanato acrylate Acrylic esters such as ethyl, 1,1- (bisacryloyloxymethyl) ethyl isocyanate ”,“ methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, tert-butyl methacrylate, isobutyl methacrylate, methacrylic acid 2 ” -Ethylhexyl, octyl methacrylate, methacryl Octadecyl acid, cyclohexyl methacrylate, benzyl methacrylate, trimethylsilyl methacrylate, methacrylic acid amide, 2- (dimethylamino) ethyl methacrylate, 2- (diethylamino) ethyl methacrylate, 2,2,2-trifluoroethyl methacrylate, 1H, 1H, 2H, 2H-heptadecafluorodecyl methacrylate, 1H, 1H, 3H-hexafluorobutyl methacrylate, 2,2,3,3-tetrafluoropropyl methacrylate, 1H, 1H, 5H methacrylate Octafluoropentyl, 1H, 1H, 7H-dodecafluoropentyl methacrylate, 2-isocyanatoethyl methacrylate, 2- (0- [1′-methylpropylideneamino] carboxyamino) ethyl methacrylate, 2-[(3 , 5-Dimethylpi Zolyl) carbonylamino] ethyl methacrylates and the like "," 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, 3-hydroxypropyl acrylate, 2-hydroxybutyl acrylate, 3-hydroxybutyl acrylate " 4-hydroxybutyl acrylate, 2-hydroxyhexyl acrylate, 6-hydroxyhexyl acrylate, 3-perfluorobutyl-2-hydroxypropyl acrylate, 3-perfluorohexyl-2-hydroxypropyl acrylate, acrylic acid 3-perfluorooctyl-2-hydroxypropyl, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, 3-hydroxypropyl methacrylate, 2-hydroxybutyl methacrylate, meta 3-hydroxybutyl crylate, 4-hydroxybutyl methacrylate, 6-hydroxyhexyl methacrylate, cyclohexyl methacrylate, 3-perfluorobutyl-2-hydroxypropyl methacrylate, 3-perfluorohexyl-2-hydroxypropyl methacrylate , 3-perfluorooctyl-2-hydroxypropyl methacrylate, acrylamide, methacrylamide, N-cyclopropylacrylamide, N, N-dimethylacrylamide, N-hydroxymethylacrylamide, N-isopropylacrylamide, acrylonitrile, methacrylonitrile, etc. (Meth) acrylic acid derivatives ”,“ vinyl esters such as vinyl acetate, vinyl propionate, vinyl benzoate, vinyl butyrate ”,“ vinyl methyl ether, vinyl Vinyl ethers such as ethyl ether ”,“ N-vinyl compounds such as vinyl methyl ketone, vinyl hexyl ketone, vinyl ketones, N-vinyl pyrrole, N-vinyl carbazole, N-vinyl indole, N-vinyl pyrrolidone ”,“ allyl ” "Allyl compounds such as alcohol, allyl chloride, allyl acetate, vinyl chloride, vinylidene chloride", "compounds having a fluorine alkyl group such as vinyl fluoride, vinylidene fluoride", "glycidyl acrylate, glycidyl methacrylate, 4-glycidyl Functional monomers such as styrene ”,“ reactions of allyl acrylate, allyl methacrylate, diacrylic anhydride, 1,2-ethanediyl diacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, divinylbenzene, etc. Compounds having a double bond of two or more ", and the like. Among these, when importance is attached to the transparency of the coating film or the molded product, it is preferable to select styrenes, acrylic esters or methacrylic esters.
上記モノマーの中でも、屈折率制御や撥水性／撥油性の付与を目的とする場合、フッ素を含有するモノマーを少なくとも１種以上選択することが好ましく、入手が容易であることから、アクリル酸２，２，２−トリフルオロエチル、アクリル酸２，２，３，３−テトラフルオロプロピル、アクリル酸２，２，３，３，３−ペンタフルオロプロピル、アクリル酸１，１，１，３，３，３−ヘキサフルオロイソプロピル、メタクリル酸２，２，２−トリフルオロエチル、メタクリル酸２，２，３，３−テトラフルオロプロピル、メタクリル酸２，２，３，３，３−ペンタフルオロプロピル、及びメタクリル酸１，１，１，３，３，３−ヘキサフルオロイソプロピルが更に好ましい。 Among the above monomers, for the purpose of controlling the refractive index and imparting water repellency / oil repellency, it is preferable to select at least one monomer containing fluorine. 2,2-trifluoroethyl, acrylic acid 2,2,3,3-tetrafluoropropyl, acrylic acid 2,2,3,3,3-pentafluoropropyl, acrylic acid 1,1,1,3,3 3-hexafluoroisopropyl, 2,2,2-trifluoroethyl methacrylate, 2,2,3,3-tetrafluoropropyl methacrylate, 2,2,3,3,3-pentafluoropropyl methacrylate, and methacryl The acid 1,1,1,3,3,3-hexafluoroisopropyl is more preferred.
フッ素を含有しないモノマーとしては、入手が容易であることから、アクリル酸エステル及びメタクリル酸エステルからなる群より選択される少なくとも１種のモノマーの使用が好ましく、中でも、アクリル酸メチル、アクリル酸エチル、アクリル酸ブチル、メタクリル酸メチル、メタクリル酸エチル及びメタクリル酸ブチルから選ばれるモノマーが好ましい。 As the monomer not containing fluorine, since it is easily available, it is preferable to use at least one monomer selected from the group consisting of acrylic acid esters and methacrylic acid esters. Among them, methyl acrylate, ethyl acrylate, Monomers selected from butyl acrylate, methyl methacrylate, ethyl methacrylate and butyl methacrylate are preferred.
以下に、好ましいモノマーの具体例を化学式で示す。 Specific examples of preferable monomers are shown below by chemical formulas.
上記ポリマーは、有機無機複合体を架橋させる目的で、架橋性官能基を有していても良い。架橋性官能基の種類は、特に限定されるものではないが、反応性の観点から、（メタ）アクリロイル基や、環状エーテル基（エポキシ基、オキセタン基等）などが好ましい。 The polymer may have a crosslinkable functional group for the purpose of crosslinking the organic-inorganic composite. The type of the crosslinkable functional group is not particularly limited, but a (meth) acryloyl group, a cyclic ether group (epoxy group, oxetane group, etc.) and the like are preferable from the viewpoint of reactivity.
本実施形態に用い得る反応性二重結合は、後述する紫外線光等の活性光線の照射によりラジカルを発生する化合物（光ラジカル開始剤）から重合反応を開始して、硬化することができる不飽和結合のことをいう。反応性二重結合としては、（メタ）アクリロイル基（アクリロイル基又はメタクリロイル基）中の炭素−炭素二重結合が好ましい。 The reactive double bond that can be used in this embodiment is an unsaturated compound that can be cured by initiating a polymerization reaction from a compound (photo radical initiator) that generates radicals upon irradiation with actinic rays such as ultraviolet light described later. It means a bond. As the reactive double bond, a carbon-carbon double bond in a (meth) acryloyl group (acryloyl group or methacryloyl group) is preferable.
反応性二重結合をポリマー中に導入する方法としては、反応性二重結合を二つ以上有する化合物をモノマーとして使用してポリマーを合成する方法、官能基を有するモノマーからポリマーを合成した後に、反応性二重結合を有する化合物をその官能基に付加させる方法等が挙げられる。 As a method of introducing a reactive double bond into a polymer, a method of synthesizing a polymer using a compound having two or more reactive double bonds as a monomer, and a method of synthesizing a polymer from a monomer having a functional group, Examples thereof include a method of adding a compound having a reactive double bond to the functional group.
反応性二重結合を二つ以上有する化合物としては、限定されるものではないが、有機ポリマーを合成する際にゲル化等の問題を抑制できる、反応性の異なる二つ以上の二重結合を有する化合物が好ましい。中でも入手が容易な点からアクリル酸アリルがより好ましい。 The compound having two or more reactive double bonds is not limited, but two or more double bonds with different reactivity can be used to suppress problems such as gelation when synthesizing an organic polymer. The compound which has is preferable. Of these, allyl acrylate is more preferable because it is easily available.
反応性二重結合を有する化合物をポリマーに付加させる手法としては、ポリマー中の官能基と反応性二重結合を有する化合物中の官能基を反応させることが好ましい。ポリマー中又は反応性二重結合を有する化合物中の官能基としては、水酸基、アルコキシシリル基、エポキシ基、カルボキシル基、イソシアネート基、アミノ基、アミド基等の官能基が好ましい。これらの官能基の組み合わせとしては、例えば、水酸基−カルボキシル基、アミノ基−カルボキシル基、アミド基−カルボキシル基、アルコキシシリル基−カルボニル基、イソシアネート基−水酸基、エポキシ基−水酸基、アルコキシシリル基−水酸基、アミド基−水酸基、エポキシ基−アミノ基等が挙げられる。 As a technique for adding a compound having a reactive double bond to a polymer, it is preferable to react a functional group in the polymer with a functional group in the compound having a reactive double bond. The functional group in the polymer or the compound having a reactive double bond is preferably a functional group such as a hydroxyl group, an alkoxysilyl group, an epoxy group, a carboxyl group, an isocyanate group, an amino group, or an amide group. Examples of combinations of these functional groups include hydroxyl group-carboxyl group, amino group-carboxyl group, amide group-carboxyl group, alkoxysilyl group-carbonyl group, isocyanate group-hydroxyl group, epoxy group-hydroxyl group, alkoxysilyl group-hydroxyl group. Amide group-hydroxyl group, epoxy group-amino group and the like.
反応性二重結合を有し、かつ水酸基を有する化合物としては、ヒドロキシエチルビニルエーテル、ヒドロキシブチルビニルエーテル、シクロヘキサンジメタノールモノビニルエーテル等のヒドロキシアルキルビニルエーテル類；ジエチレングリコールモノビニルエーテル、トリエチレングリコールモノビニルエーテル、テトラエチレングリコールモノビニルエーテル等のエチレングリコールモノビニルエーテル類；ヒドロキシエチルアリルエーテル、ヒドロキシブチルアリルエーテル、シクロヘキサンジメタノールモノアリルエーテル等のヒドロキシアルキルアリルエーテル類；ヒドロキシエチルカルボン酸ビニルエステル、ヒドロキシブチルカルボン酸ビニルエステル、（（ヒドロキシメチルシクロヘキシル）メトキシ）酢酸ビニルエステル等のヒドロキシアルキルビニルエステル類；ヒドロキシエチルカルボン酸アリルエステル、ヒドロキシブチルカルボン酸アリルエステル、（（ヒドロキシメチルシクロヘキシル）メトキシ）酢酸アリルエステル等のヒドロキシアルキルカルボン酸アリルエステル類；ヒドロキシエチル（メタ）アクリレート等の（メタ）アクリル酸ヒドロキシアルキルエステル類などが好ましい。 Examples of the compound having a reactive double bond and a hydroxyl group include hydroxyalkyl vinyl ethers such as hydroxyethyl vinyl ether, hydroxybutyl vinyl ether, and cyclohexanedimethanol monovinyl ether; diethylene glycol monovinyl ether, triethylene glycol monovinyl ether, tetraethylene glycol Ethylene glycol monovinyl ethers such as monovinyl ether; hydroxyalkyl allyl ethers such as hydroxyethyl allyl ether, hydroxybutyl allyl ether, cyclohexanedimethanol monoallyl ether; hydroxyethyl carboxylic acid vinyl ester, hydroxybutyl carboxylic acid vinyl ester, (( Hydroxymethylcyclohexyl) methoxy) vinyl acetate Hydroxyalkyl vinyl esters such as hydroxyethyl carboxylic acid allyl ester, hydroxybutyl carboxylic acid allyl ester, ((hydroxymethylcyclohexyl) methoxy) acetic acid allyl ester, etc .; hydroxyethyl (meth) acrylate, etc. (Meth) acrylic acid hydroxyalkyl esters are preferred.
反応性二重結合を有し、かつアルコキシシリル基を有する化合物としては、３−（メタ）アクリロイルオキシプロピルトリメトキシシラン、３−（メタ）アクリロイルオキシプロピルメチルジメトキシシラン、トリメトキシシリルプロピルビニルエーテルなどが好ましい。 Examples of the compound having a reactive double bond and having an alkoxysilyl group include 3- (meth) acryloyloxypropyltrimethoxysilane, 3- (meth) acryloyloxypropylmethyldimethoxysilane, and trimethoxysilylpropyl vinyl ether. preferable.
反応性二重結合を有し、かつカルボキシル基（開環してカルボキシル基となるものを含む）を有する化合物としては、（メタ）アクリル酸、イタコン酸、フマル酸、マレイン酸、無水マレイン酸、シトラコン酸、ウンデシレン酸などが好ましい。アミノ基を有する化合物としては、アミノプロピルビニルエーテル、ジエチルアミノエチルビニルエーテル等が好ましい。 As a compound having a reactive double bond and having a carboxyl group (including those that open to become a carboxyl group), (meth) acrylic acid, itaconic acid, fumaric acid, maleic acid, maleic anhydride, Citraconic acid, undecylenic acid and the like are preferable. As the compound having an amino group, aminopropyl vinyl ether, diethylaminoethyl vinyl ether and the like are preferable.
反応性二重結合を有し、かつイソシアネート基を有する化合物としては、２−イソシアネートエチル（メタ）アクリレート、１，１−ビス（アクリロイルメチル）エチルイソシアネート、メタクリル酸 ２−（０−［１’−メチルプロピリデンアミノ］カルボキシアミノ）エチル、２−［（３，５−ジメチルピラゾリル）カルボニルアミノ］エチルメタクリレート等が好ましい。 Examples of the compound having a reactive double bond and an isocyanate group include 2-isocyanatoethyl (meth) acrylate, 1,1-bis (acryloylmethyl) ethyl isocyanate, methacrylic acid 2- (0- [1′- Methylpropylideneamino] carboxyamino) ethyl, 2-[(3,5-dimethylpyrazolyl) carbonylamino] ethyl methacrylate and the like are preferable.
反応性二重結合を有し、かつエポキシ基含を有する化合物としては、グリシジルビニルエーテル、グリシジルカルボン酸ビニルエステル、グリシジルアリルエーテル、グリシジル（メタ）アクリレート等が好ましい。 As the compound having a reactive double bond and having an epoxy group, glycidyl vinyl ether, glycidyl carboxylic acid vinyl ester, glycidyl allyl ether, glycidyl (meth) acrylate and the like are preferable.
特に限定されるものではないが、架橋性官能基としてイソシアネート基を導入する場合、重合反応の容易さと官能基の反応性の観点から、（メタ）アクリル酸２−イソシアナトエチル、メタクリル酸２−（０−［１’−メチルプロピリデンアミノ］カルボキシアミノ）エチル、及び２−［（３，５−ジメチルピラゾリル）カルボニルアミノ］エチルメタクリレート等をモノマー単位の一つとして使用することでポリマーを合成する手法が好ましい。更に、（メタ）アクリル酸２−イソシアナトエチル等を、モノマー単位の一つとして使用してポリマーを合成し、得られたポリマー中のイソシアネート基と、ヒドロキシエチル（メタ）アクリレート等の水酸基を反応させることで、架橋性官能基として、（メタ）アクリロイル基を導入することも可能である。 Although not particularly limited, when an isocyanate group is introduced as a crosslinkable functional group, (meth) acrylic acid 2-isocyanatoethyl, methacrylic acid 2- A polymer is synthesized by using (0- [1′-methylpropylideneamino] carboxyamino) ethyl, 2-[(3,5-dimethylpyrazolyl) carbonylamino] ethyl methacrylate, etc. as one of the monomer units. The technique is preferred. Furthermore, a polymer is synthesized using 2-isocyanatoethyl (meth) acrylate as one of the monomer units, and the isocyanate group in the obtained polymer reacts with a hydroxyl group such as hydroxyethyl (meth) acrylate. By doing so, it is also possible to introduce a (meth) acryloyl group as the crosslinkable functional group.
架橋性官能基として、（メタ）アクリロイル基を導入する場合、重合反応の容易さと官能基の反応性の観点から、２−ヒドロキシエチル（メタ）アクリレート、２−ヒドロキシプロピル（メタ）アクリレート、４−ヒドロキシブチル（メタ）アクリレート等をモノマー単位の一つとして使用することでポリマーを合成した後に、ポリマー中の水酸基と２−イソシアネートエチル（メタ）アクリレート、１，１−（ビスアクリロイルオキシメチル）エチルイソシアネート等のイソシアネート基を反応させる手法がより好ましい。 When a (meth) acryloyl group is introduced as a crosslinkable functional group, 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4- After synthesizing the polymer by using hydroxybutyl (meth) acrylate as one of the monomer units, the hydroxyl group in the polymer and 2-isocyanatoethyl (meth) acrylate, 1,1- (bisacryloyloxymethyl) ethyl isocyanate A method of reacting an isocyanate group such as is more preferable.
また架橋性官能基として、環状エーテル基（エポキシ基等）を導入する場合、重合反応の容易さの観点から、グリリジル（メタ）アクリレートを、モノマー単位の一つとして使用することでポリマーを合成する手法が好ましい。 When a cyclic ether group (such as an epoxy group) is introduced as a crosslinkable functional group, a polymer is synthesized by using glycidyl (meth) acrylate as one of monomer units from the viewpoint of ease of polymerization reaction. The technique is preferred.
上記ポリマーの形状は、特に限定されるものではないが、例えば、鎖状、分岐鎖状、ラダー型、スター型が挙げられる。その他、任意の置換基等を導入し、分散性や相溶性を向上させることも可能である。 The shape of the polymer is not particularly limited, and examples thereof include a chain shape, a branched chain shape, a ladder shape, and a star shape. In addition, it is possible to introduce an arbitrary substituent or the like to improve the dispersibility and compatibility.
上記ポリマーの分子量は、特に限定されるものではないが、その数平均分子量（以下、「Ｍｎ」という。）は、好ましくは４０００〜５０００００ｇ／ｍｏｌ、より好ましくは８０００〜２０００００ｇ／ｍｏｌ、更に好ましくは１００００〜１０００００ｇ／ｍｏｌである。Ｍｎが４０００ｇ／ｍｏｌ未満であると、無機化合物粒子の凝集が起こり易くなる傾向があり、更に、無機化合物粒子の周りに形成されるポリマー層の厚みが薄くなることで膜の形状を保つことが困難になる。５０００００ｇ／ｍｏｌを超えると、無機化合物粒子としての特性が発現されにくくなったり、有機無機複合体間の空隙率が低下したりする傾向がある。 The molecular weight of the polymer is not particularly limited, but the number average molecular weight (hereinafter referred to as “Mn”) is preferably 4000 to 500000 g / mol, more preferably 8000 to 200000 g / mol, and still more preferably. It is 10,000 to 100,000 g / mol. If Mn is less than 4000 g / mol, aggregation of inorganic compound particles tends to occur, and the thickness of the polymer layer formed around the inorganic compound particles can be reduced to maintain the shape of the film. It becomes difficult. When it exceeds 500,000 g / mol, the characteristics as inorganic compound particles are hardly exhibited, and the porosity between the organic-inorganic composite tends to decrease.
上記ポリマーの分子量分布は、質量平均分子量（以下、「Ｍｗ」という。）とＭｎより、Ｍｗ／Ｍｎにより求められる。ここでいうＭｎ及びＭｗは、後述の実施例において詳細に説明されるように、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）により測定される、ポリメタクリル酸メチル換算の値である。 The molecular weight distribution of the polymer is determined by Mw / Mn from the mass average molecular weight (hereinafter referred to as “Mw”) and Mn. Mn and Mw here are polymethyl methacrylate equivalent values measured by gel permeation chromatography (GPC), as will be described in detail in the examples described later.
本実施形態において、有機無機複合体に含まれるポリマーの分子量分布は２．３以下である。無機化合物粒子の分散性、空隙制御、あるいは成膜性の観点から、ポリマーの分子量（鎖長）が揃っていること、つまり、分子量分布が１に近い値であることが好ましい。係る観点から、分子量分布は、好ましくは１．０〜２．２、より好ましくは１．０〜２．１、さらに好ましくは１．０〜１．９、特に好ましくは１．０〜１．８である。 In the present embodiment, the molecular weight distribution of the polymer contained in the organic-inorganic composite is 2.3 or less. From the viewpoints of dispersibility of inorganic compound particles, void control, or film formability, it is preferable that the molecular weight (chain length) of the polymers is uniform, that is, the molecular weight distribution is close to 1. From such a viewpoint, the molecular weight distribution is preferably 1.0 to 2.2, more preferably 1.0 to 2.1, still more preferably 1.0 to 1.9, and particularly preferably 1.0 to 1.8. It is.
重合反応において、連鎖移動反応や二分子停止反応などが起こった場合には、分子量分布が２．３より大きくなる。その場合、フリーポリマーが生成する、あるいは、無機化合物粒子が凝集するなどの不具合が生じる。また、本実施形態の有機無機複合体の塗膜においては、無機化合物粒子に結合したポリマーが主にバインダーとして機能するため、ポリマーの分子量が揃った、より均一なシェル層を形成することが、自己成膜性の観点からも極めて重要である。 In the polymerization reaction, when a chain transfer reaction or a bimolecular termination reaction occurs, the molecular weight distribution becomes larger than 2.3. In that case, problems such as free polymer formation or aggregation of inorganic compound particles occur. Further, in the coating film of the organic-inorganic composite of the present embodiment, the polymer bonded to the inorganic compound particles mainly functions as a binder, so that a more uniform shell layer with a uniform molecular weight of the polymer can be formed. This is also extremely important from the viewpoint of self-film formation.
［有機無機複合体］
有機無機複合体のガラス転移温度（以下、Ｔｇという。）は、特に限定されるものではないが、べたつきを抑制しつつ、良好な成膜性を付与できるという理由から、−１０〜１８０℃であることが好ましく、より好ましくは０〜１６０℃、更に好ましくは２０〜１５０℃、特に好ましくは４０〜１２０℃である。
[Organic inorganic composite]
The glass transition temperature (hereinafter referred to as Tg) of the organic-inorganic composite is not particularly limited. It is preferable to be, more preferably 0 to 160 ° C, still more preferably 20 to 150 ° C, and particularly preferably 40 to 120 ° C.
有機無機複合体のハロゲン含有量とは、臭素及び塩素の合計量を指す。このハロゲン含有量は特に限定されるものではないが、成膜性が良好であるという理由から、当該有機無機複合体の全質量を基準として、０．００１〜２．５質量％であることが好ましく、より好ましくは、０．０１〜１．５質量％、更に好ましくは０．１〜１質量％である。 The halogen content of the organic-inorganic composite refers to the total amount of bromine and chlorine. Although the halogen content is not particularly limited, it may be 0.001 to 2.5% by mass on the basis of the total mass of the organic-inorganic composite because the film formability is good. Preferably, it is 0.01-1.5 mass%, More preferably, it is 0.1-1 mass%.
有機無機複合体の銅含有量は、特に限定されるものではないが、コーティング膜や成形体の着色を抑制するため、０．２質量％以下であることが好ましく、より好ましくは０．０５質量％以下、更に好ましくは０．０２質量％以下、特に好ましくは０．００５質量％以下である。 The copper content of the organic-inorganic composite is not particularly limited, but is preferably 0.2% by mass or less, more preferably 0.05% by mass, in order to suppress coloring of the coating film or the molded product. % Or less, more preferably 0.02 mass% or less, particularly preferably 0.005 mass% or less.
有機無機複合体におけるフッ素含有量は、特に限定されるものではないが、汎用有機溶媒への分散性と、屈折率制御効果、撥水／撥油性、透明性とのバランスを考慮すると、当該有機−無機複合体の全質量を基準として０〜６０質量％であることが好ましく、より好ましくは１〜５０質量％、更に好ましくは、５〜４０質量％である。 The fluorine content in the organic-inorganic composite is not particularly limited, but considering the balance between dispersibility in a general-purpose organic solvent, refractive index control effect, water / oil repellency, and transparency, -It is preferable that it is 0-60 mass% on the basis of the total mass of an inorganic composite body, More preferably, it is 1-50 mass%, More preferably, it is 5-40 mass%.
有機無機複合体における無機化合物粒子の含有量は、特に限定されるものではないが、屈折率制御の観点から、好ましくは５０〜９６質量％、より好ましくは６０〜９３質量％、更に好ましくは７０〜９０質量％、特に好ましくは７５〜８７質量％である。また、屈折率制御と成膜性や成形性の観点から、無機化合物粒子の含有量は、有機無機複合体の全体積を基準として好ましくは３５〜９４体積％、より好ましくは４５〜８８体積％、更に好ましくは５５〜８３体積％、特に好ましくは、６２〜７８体積％である。 The content of the inorganic compound particles in the organic-inorganic composite is not particularly limited, but is preferably 50 to 96% by mass, more preferably 60 to 93% by mass, and still more preferably 70 from the viewpoint of refractive index control. It is -90 mass%, Most preferably, it is 75-87 mass%. Further, from the viewpoint of refractive index control, film formability and moldability, the content of the inorganic compound particles is preferably 35 to 94% by volume, more preferably 45 to 88% by volume based on the total volume of the organic-inorganic composite. More preferably, the content is 55 to 83% by volume, and particularly preferably 62 to 78% by volume.
［有機無機複合体の製造方法］
本実施形態に係る有機無機複合体は、例えば、無機化合物粒子の表面に、重合開始基を有するカップリング剤を結合させる工程と、重合開始基により開始されるラジカル重合により上記ポリマーを形成させる工程と、必要に応じて上記ポリマーに反応性二重結合を有する化合物を付加させる工程と、を備える方法により得ることができる。
[Method for producing organic-inorganic composite]
The organic-inorganic composite according to this embodiment includes, for example, a step of bonding a coupling agent having a polymerization initiating group to the surface of inorganic compound particles, and a step of forming the polymer by radical polymerization initiated by the polymerization initiating group. And a step of adding a compound having a reactive double bond to the polymer as necessary.
無機化合物粒子とカップリング剤との反応により、無機化合物粒子の表面にカップリング剤が導入された表面改質無機化合物粒子が得られる。無機化合物粒子とカップリング剤との反応は、これらが分散又は溶解する反応液中で行うことができる。この時、反応液を加熱してもよい。カップリング剤との反応後、又は、カップリング剤と同時に疎水化剤を加え、反応しても良い。無機粒子表面の残留水酸基と反応するものであれば、疎水化剤の種類は特に限定されるものではないが、例えば、１，１，１，３，３，３−ヘキサメチルジシラザン（ＨＭＤＳ）、クロロトリメチルシラン（ＴＭＳ）、ジメチルエチルクロロシラン、クロロジメチルプロピルシラン、ブチルクロロジメチルシラン、クロロトリエチルシラン、クロロジメチルフェニルシラン、ベンジルクロロジメチルシラン、クロロジメチル（３−フェニルプロピル）シラン、トリメチルエトキシシラン、トリエチルエトキシシラン、ヘキサメチルジシロキサン等が挙げられる。 By the reaction between the inorganic compound particles and the coupling agent, surface-modified inorganic compound particles in which the coupling agent is introduced onto the surface of the inorganic compound particles are obtained. The reaction between the inorganic compound particles and the coupling agent can be performed in a reaction solution in which they are dispersed or dissolved. At this time, the reaction solution may be heated. A hydrophobizing agent may be added and reacted after the reaction with the coupling agent or simultaneously with the coupling agent. The type of hydrophobizing agent is not particularly limited as long as it reacts with residual hydroxyl groups on the surface of the inorganic particles. For example, 1,1,1,3,3,3-hexamethyldisilazane (HMDS) Chlorotrimethylsilane (TMS), dimethylethylchlorosilane, chlorodimethylpropylsilane, butylchlorodimethylsilane, chlorotriethylsilane, chlorodimethylphenylsilane, benzylchlorodimethylsilane, chlorodimethyl (3-phenylpropyl) silane, trimethylethoxysilane, Examples include triethylethoxysilane and hexamethyldisiloxane.
ラジカル重合としては、生成するポリマーの分子量の分散度（分子量分布）を小さくすることができる点で、リビングラジカル重合（以下、「ＬＲＰ」という。）を選択することが好ましい。ＬＲＰとしては、ＮＭＰ、ＡＴＲＰ及びＲＡＦＴがある。一般的に、この中でも、重合開始剤の汎用度、適用可能なモノマーの種類の多さ、重合温度等の点から、ＡＴＲＰが特に好ましい。また、本発明の有機無機複合体においては、無機化合物粒子に結合していないフリーのポリマーの生成を抑制する必要があり、この観点からも、重合制御が容易なＡＴＲＰが特に好ましい。 As radical polymerization, it is preferable to select living radical polymerization (hereinafter referred to as “LRP”) in that the degree of dispersion (molecular weight distribution) of the molecular weight of the polymer to be produced can be reduced. There are NMP, ATRP, and RAFT as LRP. In general, among these, ATRP is particularly preferable from the viewpoint of versatility of the polymerization initiator, the variety of applicable monomers, the polymerization temperature, and the like. Moreover, in the organic-inorganic composite of the present invention, it is necessary to suppress the formation of a free polymer that is not bonded to the inorganic compound particles, and from this viewpoint, ATRP is particularly preferable because of easy polymerization control.
ラジカル重合の方式は特に限定されず、例えば、塊状重合法又は溶液重合法を選択できる。更に、生産性や安全性の観点から、懸濁重合、乳化重合、分散重合、シード重合等の方式を採用してもよい。 The method of radical polymerization is not particularly limited, and for example, a bulk polymerization method or a solution polymerization method can be selected. Furthermore, from the viewpoint of productivity and safety, methods such as suspension polymerization, emulsion polymerization, dispersion polymerization, and seed polymerization may be employed.
重合温度は、特に限定されるものではなく、重合方法及びモノマー種に応じ、適宜、選択することができる。例えばＡＴＲＰやＲＡＦＴの場合、重合温度は好ましくは−５０℃〜２００℃、更に好ましくは０℃〜１５０℃、特に好ましくは２０℃〜１３０℃である。モノマーがアクリル酸エステル及び／又はメタクリル酸エステルを含む場合、５０〜１３０℃で重合を行うと、比較的短時間で精密重合することができる。 The polymerization temperature is not particularly limited, and can be appropriately selected according to the polymerization method and the monomer type. For example, in the case of ATRP or RAFT, the polymerization temperature is preferably −50 ° C. to 200 ° C., more preferably 0 ° C. to 150 ° C., and particularly preferably 20 ° C. to 130 ° C. When the monomer contains an acrylic ester and / or a methacrylic ester, when the polymerization is performed at 50 to 130 ° C., it can be precisely polymerized in a relatively short time.
重合時間は、特に制限されるものではなく、重合方法やモノマー種に応じ、適宜、選択することができるが、例えば、０．５〜４８時間とすることができる。重合時間がこの範囲内にあると、有機無機複合体における無機化合物粒子の含有量が好ましいものとなり、有機無機複合体間に空隙を十分に形成することができ、均一な膜の形成が容易となり、その膜強度が十分なものになり易い傾向にある。同様の観点から、重合時間は、１〜２４時間とすることがより好ましい。 The polymerization time is not particularly limited and can be appropriately selected according to the polymerization method and the monomer type. For example, the polymerization time can be 0.5 to 48 hours. When the polymerization time is within this range, the content of the inorganic compound particles in the organic-inorganic composite becomes preferable, and sufficient gaps can be formed between the organic-inorganic composite, facilitating the formation of a uniform film. The film strength tends to be sufficient. From the same viewpoint, the polymerization time is more preferably 1 to 24 hours.
重合反応は、無溶媒で行っても、溶媒存在下で行ってもよい。溶媒を使用する場合、表面改質無機化合物粒子の分散性と、重合触媒の溶解性とが良好な溶媒が好ましい。溶媒は単独で用いても、複数種を組み合わせて使用してもよい。 The polymerization reaction may be performed without a solvent or in the presence of a solvent. When using a solvent, a solvent having good dispersibility of the surface-modified inorganic compound particles and solubility of the polymerization catalyst is preferable. A solvent may be used independently or may be used in combination of multiple types.
溶媒の種類は、特に限定されるものではないが、例えば、メチルイソブチルケトン（ＭＩＢＫ）、メチルエチルケトン（ＭＥＫ）、アセトン、ジアセトンアルコール、アニソール、トルエン、キシレン、ベンゼン、エチルベンゼン、ジフェニルエーテル、テトラヒドロフラン（ＴＨＦ）、１−プロパノール、２−プロパノール、メタノール、エタノール、１−ブタノール、ｔ−ブタノール、アセトニトリル、ジメチルホルムアミド（ＤＭＦ）、ジメチルアセトアミド、ジメチルスルホキシド（ＤＭＳＯ）、ｎ−メチルピロリドン、１，４−ジオキサン、酢酸エチル、酢酸ｎ−プロピル、酢酸イソプロピル、酢酸ブチル、酢酸イソブチル、酢酸２−メトキシ−１−メチルエチル、酢酸セロソルブ、３−エトキシプロピオン酸エチル、酢酸３−メトキシ−３−メチルブチル、オクタン、シクロヘキサン、ジエチルエーテル、メチルセロソルブ、セロソルブ、ｎ−ブチルセロソルブ、ｔ−ブチルセロソルブ、プロピレングリコールモノエチルエーテル、メチルメトキシブタノール、ジエチレングリコールモノブチルエーテル、エチレングリコール、プロピレングリコール、ジプロピレングリコール、１，３−プロパンジオール、１，４−ブタンジオール、ヘキサン１，６−ジオール、１，２−シクロヘキサンジオール、ミネラルスピリット、水等が挙げられる。 The type of the solvent is not particularly limited. For example, methyl isobutyl ketone (MIBK), methyl ethyl ketone (MEK), acetone, diacetone alcohol, anisole, toluene, xylene, benzene, ethylbenzene, diphenyl ether, tetrahydrofuran (THF) 1-propanol, 2-propanol, methanol, ethanol, 1-butanol, t-butanol, acetonitrile, dimethylformamide (DMF), dimethylacetamide, dimethylsulfoxide (DMSO), n-methylpyrrolidone, 1,4-dioxane, acetic acid Ethyl, n-propyl acetate, isopropyl acetate, butyl acetate, isobutyl acetate, 2-methoxy-1-methylethyl acetate, cellosolve acetate, ethyl 3-ethoxypropionate, 3-methyl acetate Xyl-3-methylbutyl, octane, cyclohexane, diethyl ether, methyl cellosolve, cellosolve, n-butyl cellosolve, t-butyl cellosolve, propylene glycol monoethyl ether, methylmethoxybutanol, diethylene glycol monobutyl ether, ethylene glycol, propylene glycol, dipropylene glycol, Examples include 1,3-propanediol, 1,4-butanediol, hexane 1,6-diol, 1,2-cyclohexanediol, mineral spirit, and water.
溶媒の使用量は、特に限定されるものではないが、例えば、モノマー１００質量部に対し、０〜２０００質量部が好ましく、より好ましくは０〜１０００質量部である。溶媒量が少ないと、反応速度が大きい傾向にあり有利であるが、モノマー種や重合条件によっては、重合溶液粘度が高くなる傾向にある。また、溶媒量が多いと、重合溶液粘度が低くなるが、反応速度が低下するため、適宜、配合比率を調整するのが好ましい。 Although the usage-amount of a solvent is not specifically limited, For example, 0-2000 mass parts is preferable with respect to 100 mass parts of monomers, More preferably, it is 0-1000 mass parts. If the amount of the solvent is small, the reaction rate tends to be large, which is advantageous, but depending on the monomer species and the polymerization conditions, the viscosity of the polymerization solution tends to increase. In addition, when the amount of the solvent is large, the viscosity of the polymerization solution is lowered, but the reaction rate is lowered.
重合反応は、無触媒で行っても、触媒を使用して行ってもよいが、生産性の観点から、触媒を使用することが好ましい。触媒の種類は、特に限定されるものではないが、重合方法やモノマー種等により、任意の触媒を適宜、使用すればよい。例えば、ＡＴＲＰの場合、触媒の種類は、一般的に知られている各種のものの中から、重合方式等に応じて適宜選択すればよい。具体的には、例えば、Ｃｕ（０）、Ｃｕ＋、Ｃｕ２＋、Ｆｅ＋、Ｆｅ２＋、Ｆｅ３＋、Ｒｕ２＋又はＲｕ３＋を含む金属触媒を使用できる。中でも、分子量や分子量分布の高度な制御を達成するためには、特にＣｕ＋を含む１価の銅化合物及び０価の銅が好ましい。その具体例としては、Ｃｕ（０）、ＣｕＣｌ、ＣｕＢｒ等が挙げられる。これらは、単独で使用しても、複数を組み合わせて使用してもよい。触媒の使用量は、重合開始基１モルに対して、通常０．０１〜１００モル、好ましくは０．０１〜５０モル、更に好ましくは０．０１〜１０モルである。 The polymerization reaction may be performed without a catalyst or using a catalyst, but it is preferable to use a catalyst from the viewpoint of productivity. The type of the catalyst is not particularly limited, but any catalyst may be appropriately used depending on the polymerization method, the monomer type, and the like. For example, in the case of ATRP, the type of catalyst may be appropriately selected from various commonly known types according to the polymerization method and the like. Specifically, for example, a metal catalyst containing Cu (0), Cu + , Cu 2+ , Fe + , Fe 2+ , Fe 3+ , Ru 2+ or Ru 3+ can be used. Among these, in order to achieve a high degree of control of molecular weight and molecular weight distribution, a monovalent copper compound containing Cu + and zero-valent copper are particularly preferable. Specific examples thereof include Cu (0), CuCl, CuBr and the like. These may be used alone or in combination. The usage-amount of a catalyst is 0.01-100 mol normally with respect to 1 mol of polymerization start groups, Preferably it is 0.01-50 mol, More preferably, it is 0.01-10 mol.
金属触媒は、通常、有機配位子と併用される。金属への配位原子としては、例えば、窒素原子、酸素原子、リン原子、硫黄原子等が挙げられる。中でも、窒素原子、リン原子が好ましい。有機配位子の具体例としては、２，２’−ビピリジン及びその誘導体、１，１０−フェナントロリン及びその誘導体、テトラメチルエチレンジアミン、Ｎ，Ｎ，Ｎ’，Ｎ”，Ｎ”−ペンタメチルジエチレントリアミン（以下、「ＰＭＤＥＴＡ」という。）、トリス（ジメチルアミノエチル）アミン（以下、「Ｍｅ６ＴＲＥＮ」という。）、トリス（２−ピリジルメチル）アミン、トリフェニルホスフィン、トリブチルホスフィン等が挙げられる。アクリル酸エステル類、メタクリル酸エステル類の重合を行う場合は、ＰＭＤＥＴＡ、Ｍｅ６ＴＲＥＮ、２，２’−ビピリジン及びその誘導体の１つである４，４’−ジ（５−ノニル）−２，２’−ジピリジン（以下、「ｄＮｂｐｙ」という。）が好ましい。有機配位子の具体例を下記化学式に示す。 The metal catalyst is usually used in combination with an organic ligand. Examples of the coordination atom to the metal include a nitrogen atom, an oxygen atom, a phosphorus atom, and a sulfur atom. Of these, a nitrogen atom and a phosphorus atom are preferable. Specific examples of the organic ligand include 2,2′-bipyridine and derivatives thereof, 1,10-phenanthroline and derivatives thereof, tetramethylethylenediamine, N, N, N ′, N ″, N ″ -pentamethyldiethylenetriamine ( Hereinafter, “PMDETA”), tris (dimethylaminoethyl) amine (hereinafter referred to as “Me6TREN”), tris (2-pyridylmethyl) amine, triphenylphosphine, tributylphosphine, and the like can be given. When polymerizing acrylic acid esters and methacrylic acid esters, PMDETA, Me6TREN, 2,2′-bipyridine and one of its derivatives, 4,4′-di (5-nonyl) -2,2 ′ -Dipyridine (hereinafter referred to as “dNbpy”) is preferred. Specific examples of the organic ligand are shown in the following chemical formula.
金属触媒と有機配位子とは、別々に添加して重合系中で混合してもよいし、予め混合してからそれらを重合系中へ添加してもよい。特に、銅化合物を使用する場合は、前者の方法が好ましい。 The metal catalyst and the organic ligand may be added separately and mixed in the polymerization system, or may be mixed in advance and then added to the polymerization system. In particular, when using a copper compound, the former method is preferable.
重合反応において、上記に加え、添加剤を必要に応じて使用することができる。添加剤の種類としては、特に限定されるものではないが、例えば、分散剤・安定剤、乳化剤（界面活性剤）等が挙げられる。 In the polymerization reaction, additives can be used as necessary in addition to the above. The type of additive is not particularly limited, and examples thereof include a dispersant / stabilizer and an emulsifier (surfactant).
分散剤・安定剤は、その機能を有するものであれば特に限定されるものではないが、ポリヒドロキシスチレン、ポリスチレンスルホン酸、ビニルフェノール−（メタ）アクリル酸エステル共重合体、スチレン−（メタ）アクリル酸エステル共重合体、スチレン−ビニルフェノール−（メタ）アクリル酸エステル共重合体等のポリスチレン誘導体；ポリ（メタ）アクリル酸、ポリ（メタ）アクリルアミド、ポリアクリロニトリル、ポチエチル（メタ）アクリレート、ポリブチル（メタ）アクリレート等のポリ（メタ）アクリル酸誘導体；ポリメチルビニルエーテル、ポリエチルビニルエーテル、ポリブチルビニルエーテル、ポリイソブチルビニルエーテル等のポリビニルアルキルエーテル誘導体；セルロース、メチルセルロース、酢酸セルロース、硝酸セルロース、ヒドロキシメチルセルロース、ヒドロキシエチルセルロース、ヒドロキシプロピルセルロース、カルボキシメチルセルロース等のセルロース誘導体；ポリビニルアルコール、ポリビニルブチラール、ポリビニルホルマール、ポリ酢酸ビニル等のポリ酢酸ビニル誘導体；ポリビニルピリジン、ポリビニルピロリドン、ポリエチレンイミン、ポリ−２−メチル−２−オキサゾリン等の含窒素ポリマー誘導体；ポリ塩化ビニル、ポリ塩化ビニリデン等のポリハロゲン化ビニル誘導体；ポリジメチルシロキサン等のポリシロキサン誘導体等の各種疎水性又は親水性の分散剤、安定剤が挙げられる。これらは単独で使用してもよいし、複数を組み合わせて使用してもよい。 The dispersant / stabilizer is not particularly limited as long as it has the function, but polyhydroxystyrene, polystyrene sulfonic acid, vinylphenol- (meth) acrylic acid ester copolymer, styrene- (meth). Polystyrene derivatives such as acrylic acid ester copolymer, styrene-vinylphenol- (meth) acrylic acid ester copolymer; poly (meth) acrylic acid, poly (meth) acrylamide, polyacrylonitrile, potyethyl (meth) acrylate, polybutyl ( Poly (meth) acrylic acid derivatives such as (meth) acrylate; polyvinyl alkyl ether derivatives such as polymethyl vinyl ether, polyethyl vinyl ether, polybutyl vinyl ether, polyisobutyl vinyl ether; cellulose, methyl cellulose, cellulose acetate Cellulose derivatives such as cellulose nitrate, hydroxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, carboxymethyl cellulose; polyvinyl acetate derivatives such as polyvinyl alcohol, polyvinyl butyral, polyvinyl formal, polyvinyl acetate; polyvinyl pyridine, polyvinyl pyrrolidone, polyethyleneimine, poly Nitrogen-containing polymer derivatives such as 2-methyl-2-oxazoline; polyvinyl halide derivatives such as polyvinyl chloride and polyvinylidene chloride; various hydrophobic or hydrophilic dispersants such as polysiloxane derivatives such as polydimethylsiloxane, Stabilizers can be mentioned. These may be used alone or in combination.
乳化剤（界面活性剤）は、その機能を有するものであれば、特に限定されるものではないが、ラウリル硫酸ナトリウムなどのアルキル硫酸エステル塩、ドデシルベンゼンスルホン酸ナトリウムなどのアルキルベンゼンスルホン酸塩、アルキルナフタレンスルホン酸塩、脂肪酸塩、アルキルリン酸塩、アルキルスルホコハク酸塩等のアニオン系乳化剤；アルキルアミン塩、第四級アンモニウム塩、アルキルベタイン、アミンオキサイド等のカチオン系乳化剤；ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルアリルエーテル、ポリオキシエチレンアルキルフェニルエーテル、ソルビタン脂肪酸エステル、グリセリン脂肪酸エステル、ポリオキシエチレン脂肪酸エステル等のノニオン系乳化剤等が挙げられる。これらは単独で使用してもよいし、複数を組み合わせて使用してもよい。 The emulsifier (surfactant) is not particularly limited as long as it has the function, but alkyl sulfate salts such as sodium lauryl sulfate, alkyl benzene sulfonates such as sodium dodecylbenzene sulfonate, and alkyl naphthalene. Anionic emulsifiers such as sulfonates, fatty acid salts, alkyl phosphates, alkylsulfosuccinates; Cationic emulsifiers such as alkylamine salts, quaternary ammonium salts, alkylbetaines, amine oxides; polyoxyethylene alkyl ethers, poly Nonionic series such as oxyethylene alkyl ether, polyoxyethylene alkyl allyl ether, polyoxyethylene alkyl phenyl ether, sorbitan fatty acid ester, glycerin fatty acid ester, polyoxyethylene fatty acid ester Agents and the like. These may be used alone or in combination.
ポリマーに反応性二重結合を有する化合物を付加させる工程としては、ラジカル重合により得られた有機無機複合体を含有する重合溶液に、反応性二重結合を有する化合物を導入して、そのまま反応を行ってもよいし、洗浄精製した有機無機複合体を再度、有機溶媒中に分散させてから反応を行ってもよい。 As a step of adding a compound having a reactive double bond to the polymer, a compound having a reactive double bond is introduced into a polymerization solution containing an organic-inorganic composite obtained by radical polymerization, and the reaction is carried out as it is. Alternatively, the reaction may be performed after the washed and purified organic-inorganic composite is dispersed again in an organic solvent.
ポリマー中の官能基と、反応性二重結合を有する化合物の官能基との反応は、無触媒で行っても、触媒を使用して行ってもよいが、生産性の観点から、触媒を使用することが好ましい。 The reaction between the functional group in the polymer and the functional group of the compound having a reactive double bond may be carried out without a catalyst or with a catalyst, but from the viewpoint of productivity, a catalyst is used. It is preferable to do.
官能基同士の反応中に、反応性二重結合がラジカル反応してゲル化することを抑制するために、反応液に重合禁止剤を導入してもよい。 In order to prevent the reactive double bond from undergoing radical reaction and gelation during the reaction between the functional groups, a polymerization inhibitor may be introduced into the reaction solution.
上述の製造方法であれば、特に限定されるものではないが、以下に代表的な製造方法を示す。 Although it will not specifically limit if it is the above-mentioned manufacturing method, The typical manufacturing method is shown below.
［有機無機複合体の製造方法１：不連続工程による製造方法］
（１）無機化合物粒子の分散液に、重合開始基を有するカップリング剤を加え、所定の温度で反応させ、更に疎水化剤を加えて反応し、表面改質無機化合物粒子の分散液を得る。
（２）室温まで冷却後、上記分散液を所定の溶媒で洗浄し、遠心分離等で固形分を分離・乾燥し、表面改質無機化合物粒子を得る。
（３）上記表面改質無機化合物粒子を、重合溶媒に分散させた後、ラジカル重合性モノマーと触媒を加え、所定の条件で反応し、前記重合開始基により開始されるリビングラジカル重合により、前記無機化合物粒子に結合しているポリマーを形成させ、有機無機複合体１を得る。必要に応じ、（４）以降の反応を行う。
（４）室温まで冷却後、前記有機無機複合体１の反応液に、重合禁止剤を加え、更に反応性二重結合を含む官能基を有する化合物と触媒を加え、所定の条件で反応させた後、溶媒で洗浄し、有機無機複合体２を得る。
[Method for producing organic-inorganic composite 1: production method by discontinuous process]
(1) Add a coupling agent having a polymerization initiating group to a dispersion of inorganic compound particles, react at a predetermined temperature, and further add a hydrophobizing agent to react to obtain a dispersion of surface-modified inorganic compound particles. .
(2) After cooling to room temperature, the dispersion is washed with a predetermined solvent, and the solid content is separated and dried by centrifugation or the like to obtain surface-modified inorganic compound particles.
(3) After the surface-modified inorganic compound particles are dispersed in a polymerization solvent, a radical polymerizable monomer and a catalyst are added, reacted under predetermined conditions, and by living radical polymerization initiated by the polymerization initiating group, A polymer bonded to the inorganic compound particles is formed to obtain the organic-inorganic composite 1. If necessary, the reaction after (4) is performed.
(4) After cooling to room temperature, a polymerization inhibitor was added to the reaction solution of the organic-inorganic composite 1, and a compound having a functional group containing a reactive double bond and a catalyst were further added and reacted under predetermined conditions. Thereafter, the organic-inorganic composite 2 is obtained by washing with a solvent.
［有機無機複合体の製造方法２：連続工程による製造方法］
（１）無機化合物粒子の分散液に、重合開始基を有するカップリング剤を加え、所定の温度で反応させ、更に疎水化剤を加えて反応し、表面改質無機化合物粒子の分散液を得る。
（２）室温まで冷却後、ラジカル重合性モノマーと触媒を加え、所定の条件で反応し、前記重合開始基により開始されるリビングラジカル重合により、前記無機化合物粒子に結合しているポリマーを形成させ、有機無機複合体１を得る。必要に応じ、（３）以降の反応を行う。
（３）室温まで冷却後、前記有機無機複合体１の反応液に、重合禁止剤を加え、更に反応性二重結合を含む官能基を有する化合物と触媒を加え、所定の条件で反応させた後、溶媒で洗浄し、有機無機複合体２を得る。
[Manufacturing method of organic-inorganic composite 2: Manufacturing method by continuous process]
(1) Add a coupling agent having a polymerization initiating group to a dispersion of inorganic compound particles, react at a predetermined temperature, and further add a hydrophobizing agent to react to obtain a dispersion of surface-modified inorganic compound particles. .
(2) After cooling to room temperature, a radical polymerizable monomer and a catalyst are added and reacted under predetermined conditions to form a polymer bonded to the inorganic compound particles by living radical polymerization initiated by the polymerization initiating group. The organic-inorganic composite 1 is obtained. If necessary, the reaction after (3) is performed.
(3) After cooling to room temperature, a polymerization inhibitor is added to the reaction solution of the organic-inorganic composite 1, a compound having a functional group containing a reactive double bond and a catalyst are added, and the reaction is performed under predetermined conditions. Thereafter, the organic-inorganic composite 2 is obtained by washing with a solvent.
［コーティング材］
本実施形態のコーティング材は、前記有機無機複合体を含むものであれば、特に限定されるものではなく、その形態は液体でも固体でも良いが、好ましくは液体である。中でも、有機無機複合体を有機溶媒に分散させたものが好ましい。
[Coating material]
The coating material of the present embodiment is not particularly limited as long as it contains the organic-inorganic composite, and the form may be liquid or solid, but is preferably liquid. Among these, those obtained by dispersing an organic-inorganic composite in an organic solvent are preferable.
コーティング材に使用する有機溶媒は、特に限定されるものではないが、上述の有機無機複合体の分散性が良好で、比較的安全性が高く、汎用的な有機溶媒が好ましい。これらの溶媒は、単独で用いても、複数を混合して使用しても構わない。成膜性と安全性の観点から、有機溶媒の蒸発速度は、酢酸ブチルを１００とした場合に、好ましくは１０〜６００、更に好ましくは２０〜２００である。同様の観点から、有機溶媒の沸点は好ましくは７５〜２００℃、更に好ましくは９０〜１８０℃である。これらは単独で使用しても、２種類以上を組み合わせて使用しても良い。 Although the organic solvent used for a coating material is not specifically limited, The dispersibility of the above-mentioned organic-inorganic composite is favorable, comparatively high safety | security, and a general purpose organic solvent are preferable. These solvents may be used alone or in combination. From the viewpoint of film formability and safety, the evaporation rate of the organic solvent is preferably 10 to 600, more preferably 20 to 200, when butyl acetate is 100. From the same viewpoint, the boiling point of the organic solvent is preferably 75 to 200 ° C, more preferably 90 to 180 ° C. These may be used alone or in combination of two or more.
有機溶媒の例としては、例えば、アセトン、メチルエチルケトン（ＭＥＫ）、ジエチルケトン、メチルイソブチルケトン（ＭＩＢＫ）、ジイソブチルケトン、シクロヘキサノン、ジアセトンアルコール、イソホロン、テトラヒドロフラン（ＴＨＦ）、２−メトキシエタノール（メチルセロソルブ）、２−エトキシエタノール（エチルセロソルブ）、２−ｎ−ブトキシエタノール（ｎ−ブチルセロソルブ）、エチレングリコールモノ―ｔｅｒｔ−ブチルエーテル（ｔ−ブチルセロソルブ）、１−メトキシ−２−プロパノール（プロピレングリコールモノエチルエーテル）、３−メトキシ−３−メチルブタノール（メチルメトキシブタノール）、ジエチレングリコールモノ−ｎ−ブチルエーテル（ジエチレングリコールモノブチルエーテル）、ベンゼン、トルエン、キシレン、アニソール（メトキシベンゼン）、ベンゾトリフルオリド、シクロヘキサン、ヘキサン、ミネラルスピリッド、ベンジルアルコール、メタノール、エタノール、１−プロパノール、２−プロパノール、１−ブタノール、ｔ−ブタノール、酢酸エチル、酢酸イソプロピル、酢酸プロピル、酢酸ブチル、酢酸イソブチル、酢酸２−メトキシ−１−メチルエチル（プロピレングリコールモノメチルエーテルアセタート）、酢酸２−エトキシエチル（酢酸セロソルブ）、３−エトキシプロピオン酸エチル、酢酸３−メトキシブチル、酢酸 ３−メトキシ−３−メチルブチル、ジエチルエーテル、エチレングリコール、プロピレングリコール、１，３−プロパンジオール、アセトニトリル、ジメチルアセトアミド、ジメチルホルムアミド（ＤＭＦ）、ジメチルスルホキシド（ＤＭＳＯ）、ｎ−メチルピロリドン（ＮＭＰ）、ピリジン、１，４−ジオキサン、クロロホルム等が挙げられる。 Examples of organic solvents include, for example, acetone, methyl ethyl ketone (MEK), diethyl ketone, methyl isobutyl ketone (MIBK), diisobutyl ketone, cyclohexanone, diacetone alcohol, isophorone, tetrahydrofuran (THF), 2-methoxyethanol (methyl cellosolve). 2-ethoxyethanol (ethyl cellosolve), 2-n-butoxyethanol (n-butyl cellosolve), ethylene glycol mono-tert-butyl ether (t-butyl cellosolve), 1-methoxy-2-propanol (propylene glycol monoethyl ether), 3-methoxy-3-methylbutanol (methylmethoxybutanol), diethylene glycol mono-n-butyl ether (diethylene glycol monobutyl ether), Zen, toluene, xylene, anisole (methoxybenzene), benzotrifluoride, cyclohexane, hexane, mineral spirit, benzyl alcohol, methanol, ethanol, 1-propanol, 2-propanol, 1-butanol, t-butanol, ethyl acetate, Isopropyl acetate, propyl acetate, butyl acetate, isobutyl acetate, 2-methoxy-1-methylethyl acetate (propylene glycol monomethyl ether acetate), 2-ethoxyethyl acetate (cellosolve acetate), ethyl 3-ethoxypropionate, acetic acid 3- Methoxybutyl, 3-methoxy-3-methylbutyl acetate, diethyl ether, ethylene glycol, propylene glycol, 1,3-propanediol, acetonitrile, dimethylacetamide, dimethyl Examples include formamide (DMF), dimethyl sulfoxide (DMSO), n-methylpyrrolidone (NMP), pyridine, 1,4-dioxane, chloroform and the like.
更に必要に応じ、光重合開始剤、架橋剤、フリーポリマー、添加剤、可塑剤、油脂、乳化剤（界面活性剤）、カップリング剤、酸、アルカリ、モノマー、オリゴマー、ポリマー、顔料、染料、香料、色素等を加えても良い。 If necessary, photopolymerization initiators, crosslinking agents, free polymers, additives, plasticizers, fats and oils, emulsifiers (surfactants), coupling agents, acids, alkalis, monomers, oligomers, polymers, pigments, dyes, fragrances , Pigments and the like may be added.
本実施の形態の光重合開始剤とは、活性光線の照射により、組成物を重合させるものであれば、特に限定されるものではないが、光ラジカル開始剤、光酸発生剤、光塩基発生剤の３つに大別できる。 The photopolymerization initiator of the present embodiment is not particularly limited as long as the composition is polymerized by irradiation with actinic rays, but is not limited to a photoradical initiator, a photoacid generator, or a photobase generator. It can be roughly divided into three types.
光ラジカル開始剤としては、活性光線又は放射線の照射によりラジカルを発生する化合物を用いることが好ましい。このような光ラジカル開始剤を用いることにより、活性光線又は放射線の照射により発生したラジカルにより、前記有機ポリマー中の反応性二重結合の重合反応が生起され、有機無機複合体を硬化することができる。 As the photoradical initiator, it is preferable to use a compound that generates radicals upon irradiation with actinic rays or radiation. By using such a photoradical initiator, a radical generated by irradiation with actinic rays or radiation causes a polymerization reaction of a reactive double bond in the organic polymer, thereby curing the organic-inorganic composite. it can.
このような光ラジカル開始剤としては、アセトフエノン類、ベンゾイン類、ベンゾフエノン類、ケタール類、アントラキノン類、チオキサントン類、アゾ化合物、過酸化物類、２，３−ジアルキルジオン化合物類、ジスルフィド化合物類、チウラム化合物類、フルオロアミン化合物類、オキシムエステル類などが用いられる。光ラジカル開始剤の具体例としては、２，２’−ジエトキシアセトフエノン、ｐ−ジメチルアセトフエノン、１−ヒドロキシシクロへキシルフエニルケトン、１−ヒドロキシジメチルフエニルケトン、２−メチル−４’−メチルチオ−２−モリホリノプロピオフエノン、２−ベンジル−２−ジメチルアミノ−１−（４−モリホリノフエニル）−ブタノン１、２−メチル−１［４−（メチルチオ）フェニル］−２−モリフォリノプロパン−１−オン、α−ヒドロキシアセトフエノン、α−アミノアセトフエノンなどのアセトフエノン類、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ペンゾインイソプロビルエーテル、ベンジルジメチルレタールなどのベンゾイン類、ペンゾフエノン、２，４’−ジクロロベンゾフエノン、４，４’−ジクロロベンゾフエノン、ｐ−クロロベンゾフエノンなどのペンゾフエノン類、１，２−オクタンジオンー１−［４−（フェニルチオ）−２−（０−ペンゾイルオキシム）］、エタノン−１−［９−エチル−６−（２−メチルベンゾイル）−９Ｈ−カルバゾール−３−イル］−１−（０一アセチルオキシム）等のオキシムエステル類などがある。これらの光ラジカル開始剤は単独で用いてもよいし、２種以上組み合わせて使用してもよい。 Such photo radical initiators include acetophenones, benzoins, benzophenones, ketals, anthraquinones, thioxanthones, azo compounds, peroxides, 2,3-dialkyldione compounds, disulfide compounds, thiuram. Compounds, fluoroamine compounds, oxime esters and the like are used. Specific examples of the photo radical initiator include 2,2′-diethoxyacetophenone, p-dimethylacetophenone, 1-hydroxycyclohexyl phenyl ketone, 1-hydroxydimethylphenyl ketone, 2-methyl- 4'-methylthio-2-morpholinopropiophenone, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butanone 1,2-methyl-1 [4- (methylthio) phenyl] Acetophenones such as 2-morpholinopropan-1-one, α-hydroxyacetophenone, α-aminoacetophenone, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzyldimethylletal, etc. Benzoins, benzophenone, 2,4'-dichlorobenzophenone, 4,4'- Penzophenones such as dichlorobenzophenone and p-chlorobenzophenone, 1,2-octanedione-1- [4- (phenylthio) -2- (0-pentoyloxime)], ethanone-1- [9-ethyl There are oxime esters such as -6- (2-methylbenzoyl) -9H-carbazol-3-yl] -1- (0 monoacetyloxime). These photo radical initiators may be used alone or in combination of two or more.
光酸発生剤とは、活性光線又は放射線の照射により、酸を発生する化合物であり、例えば、スルホン酸誘導体、オニウム塩類、カルボン酸エステル類が挙げられる。 The photoacid generator is a compound that generates an acid upon irradiation with actinic rays or radiation, and examples thereof include sulfonic acid derivatives, onium salts, and carboxylic acid esters.
スルホン酸誘導体としては、例えば、ジスルホン類、ジスルホニルジアゾメタン類、ジスルホニルメタン類、スルホニルベンゾイルメタン類、トリフルオロメチルスルホネート誘導体などのイミドスルホネート類、ベンゾインスルホネート類、１−オキシ−２−ヒドロキシ−３−プロピルアルコールのスルホネート類、ピロガロールトリスルホネート類、ベンジルスルホネート類を挙げることができる。具体的には、ジフェニルジスルホン、ジトシルジスルホン、ビス（フェニルスルホニル）ジアゾメタン、ビス（クロルフェニルスルホニル）ジアゾメタン、ビス（キシリルスルホニル）ジアゾメタン、フェニルスルホニルベンゾイルジアゾメタン、ビス（シクロヘキシルスルホニル）メタン、ベンゾイントシラート、１、２−ジフェニル−２−ヒドロキシプロピルトシラート、１、２−ジ（４−メチルメルカプトフェニル）−２−ヒドロキシプロピルトシラート、ピロガロールメチルスルホネート、ピロガロールエチルスルホネート、２，６−ジニトロフェニルメチルトシラート、オルト−ニトロフェニルメチルトシラート、パラ−ニトロフェニルトシラートなどを挙げることができる。 Examples of the sulfonic acid derivatives include disulfones, disulfonyldiazomethanes, disulfonylmethanes, sulfonylbenzoylmethanes, imidesulfonates such as trifluoromethylsulfonate derivatives, benzoinsulfonates, 1-oxy-2-hydroxy-3 -Sulphonates of propyl alcohol, pyrogallol trisulfonates, benzyl sulfonates. Specifically, diphenyldisulfone, ditosyldisulfone, bis (phenylsulfonyl) diazomethane, bis (chlorophenylsulfonyl) diazomethane, bis (xylylsulfonyl) diazomethane, phenylsulfonylbenzoyldiazomethane, bis (cyclohexylsulfonyl) methane, benzoin tosylate 1,2-diphenyl-2-hydroxypropyl tosylate, 1,2-di (4-methylmercaptophenyl) -2-hydroxypropyl tosylate, pyrogallol methyl sulfonate, pyrogallol ethyl sulfonate, 2,6-dinitrophenyl methyl tosylate And lato, ortho-nitrophenyl methyl tosylate, para-nitrophenyl tosylate and the like.
カルボン酸エステルとしては、１、８−ナフタレンジカルボン酸イミドメチルスルホネート、１、８−ナフタレンジカルボン酸イミドトシルスルホネート、１、８−ナフタレンジカルボン酸イミドトリフルオロメチルスルホネート、１、８−ナフタレンジカルボン酸イミドカンファースルホネート、コハク酸イミドフェニルスルホネート、コハク酸イミドトシルスルホネート、コハク酸イミドトリフルオロメチルスルホネート、コハク酸イミドカンファースルホネート、フタル酸イミドトリフルオロスルホネート、シス−５−ノルボルネン−エンド−２，３−ジカルボン酸イミドトリフルオロメチルスルホネートなどを挙げることができる。 As the carboxylic acid ester, 1,8-naphthalenedicarboxylic acid imidomethyl sulfonate, 1,8-naphthalenedicarboxylic acid imidotosyl sulfonate, 1,8-naphthalenedicarboxylic acid imide trifluoromethyl sulfonate, 1,8-naphthalenedicarboxylic acid imide camphor Sulfonate, succinimide phenyl sulfonate, succinimide tosyl sulfonate, succinimide trifluoromethyl sulfonate, succinimide camphor sulfonate, phthalimide trifluorosulfonate, cis-5-norbornene-endo-2,3-dicarboxylic imide Examples thereof include trifluoromethyl sulfonate.
オニウム塩としては、テトラフルオロボレート（ＢＦ４−）、ヘキサフルオロホスフェート（ＰＦ６−）、ヘキサフルオロアンチモネート（ＳｂＦ６−）、ヘキサフルオロアルセネート（ＡｓＦ６−）、ヘキサクロルアンチモネート（ＳｂＣｌ６−）、テトラフェニルボレート、テトラキス（トリフルオロメチルフェニル）ボレート、テトラキス（ペンタフルオロメチルフェニル）ボレート、過塩素酸イオン（ＣｌＯ４−）、トリフルオロメタンスルフォン酸イオン（ＣＦ３ＳＯ３−）、フルオロスルフォン酸イオン（ＦＳＯ３−）、トルエンスルフォン酸イオン、トリニトロベンゼンスルフォン酸アニオン、トリニトロトルエンスルフォン酸アニオン等のアニオンを有するスルホニウム塩またはヨードニウム塩を使用することができる。 Examples of onium salts include tetrafluoroborate (BF 4− ), hexafluorophosphate (PF 6− ), hexafluoroantimonate (SbF 6− ), hexafluoroarsenate (AsF 6− ), hexachloroantimonate (SbCl 6). − ), Tetraphenylborate, tetrakis (trifluoromethylphenyl) borate, tetrakis (pentafluoromethylphenyl) borate, perchlorate ion (ClO 4− ), trifluoromethanesulfonate ion (CF 3 SO 3− ), fluorosulfone acid ion (FSO 3-), using toluene sulfonic acid ion, trinitrobenzene sulfonic acid anion, a sulfonium salt or iodonium salt having an anion such as trinitrotoluene sulfonate anion I can be.
スルホニウム塩としては、例えば、トリフェニルスルホニウムヘキサフルオロアシルネート、トリフェニルスルホニウムヘキサフルオロボレート、トリフェニルスルホニウムテトラフルオロボレート、トリフェニルスルホニウムテトラキス（ペンタフルオベンジル）ボレート、メチルジフェニルスルホニウムテトラフルオロボレート、メチルジフェニルスルホニウムテトラキス（ペンタフルオロベンジル）ボレート、ジメチルフェニルスルホニウムヘキサフルオロホスフェート、トリフェニルスルホニウムヘキサフルオロホスフェート、トリフェニルスルホニウムヘキサフルオロアンチモネート、ジフェニルナフチルスルホニウムヘキサフルオロアルセネート、トリトイルスルホニウムヘキサフルオロホスフェート、アニシルジフェニルスルホニウムヘキサヘキサフルオルアンチモネート、４−ブトキシフェニルジフェニルスルホニウムテトラフルオロボレート、４−ブトキシフェニルジフェニルスルホニウムテトラキス（ペンタフルオロベンジル）ボレート、４−クロロフェニルジフェニルスルホニウムヘキサフルオロアンチモネート、トリス（４−フェノキシフェニル）スルホニウムヘキサフルオロホスフェート、ジ（４−エトキシフェニル）メチルスルホニウムヘキサフルオロアルセネート、４−アセチルフェニルジフェニルスルホニウムテトラフルオロボレート、４−アセチルフェニルジフェニルスルホニウムテトラキス（ペンタフルオロベンジル）ボレート、トリス（４−チオメトキシフェニル）スルホニウムヘキサフルオロホスフェート、ジ（メトキシスルホニルフェニル）メチルスルホニウムヘキサフルオロアンチモネート、ジ（メトキシナフチル）メチルスルホニウムテトラフルオロボレート、ジ（メトキシナフチル）メチルスルホニウムテトラキス（ペンタフルオロベンジル）ボレート、ジ（カルボメトキシフェニル）メチルスルホニウムヘキサフルオロホスフェート、（４−オクチルオキシフェニル）ジフェニルスルホニウムテトラキス（３，５−ビス−トリフルオロメチルフェニル）ボレート、トリス（ドデシルフェニル）スルホニウムテトラキス（３，５−ビス−トリフルオロメチルフェニル）ボレート、４−アセトアミドフェニルジフェニルスルホニウムテトラフルオロボレート、４−アセトアミドフェニルジフェニルスルホニウムテトラキス（ペンタフルオロベンジル）ボレート、ジメチルナフチルスルホニウムヘキサフルオロホスフェート、トリフルオロメチルジフェニルスルホニウムテトラフルオロボレート、トリフルオロメチルジフェニルスルホニウムテトラキス（ペンタフルオロベンジル）ボレート、フェニルメチルベンジルスルホニウムヘキサフルオロホスフェート、１０−メチルフェノキサチイニウムヘキサフルオロホスフェート、５−メチルチアントレニウムヘキサフルオロホスフェート、１０−フェニル−９，９−ジメチルチオキサンテニウムヘキサフルオロホスフェート、１０−フェニル−９−オキソチオキサンテニウムキサンテニウムテトラフルオロボレート、１０−フェニル−９−オキソチオキサンテニウムテトラキス（ペンタフルオロベンジル）ボレート、５−メチル−１０−オキソチアトレニウムテトラフルオロボレート、５−メチル−１０−オキソチアトレニウムテトラキス（ペンタフルオロベンジル）ボレート、および５−メチル−１０，１０−ジオキソチアトレニウムヘキサフルオロホスフェートなどが挙げられる。 Examples of the sulfonium salt include triphenylsulfonium hexafluoroacylate, triphenylsulfonium hexafluoroborate, triphenylsulfonium tetrafluoroborate, triphenylsulfonium tetrakis (pentafluorobenzyl) borate, methyldiphenylsulfonium tetrafluoroborate, methyldiphenylsulfonium. Tetrakis (pentafluorobenzyl) borate, dimethylphenylsulfonium hexafluorophosphate, triphenylsulfonium hexafluorophosphate, triphenylsulfonium hexafluoroantimonate, diphenylnaphthylsulfonium hexafluoroarsenate, tritoylsulfonium hexafluorophosphate, anisyldiphenylsulfate Nitrohexafluoroantimonate, 4-butoxyphenyldiphenylsulfonium tetrafluoroborate, 4-butoxyphenyldiphenylsulfonium tetrakis (pentafluorobenzyl) borate, 4-chlorophenyldiphenylsulfonium hexafluoroantimonate, tris (4-phenoxyphenyl) sulfonium Hexafluorophosphate, di (4-ethoxyphenyl) methylsulfonium hexafluoroarsenate, 4-acetylphenyldiphenylsulfonium tetrafluoroborate, 4-acetylphenyldiphenylsulfonium tetrakis (pentafluorobenzyl) borate, tris (4-thiomethoxyphenyl) Sulfonium hexafluorophosphate, di (methoxysulfonyl phen L) methylsulfonium hexafluoroantimonate, di (methoxynaphthyl) methylsulfonium tetrafluoroborate, di (methoxynaphthyl) methylsulfonium tetrakis (pentafluorobenzyl) borate, di (carbomethoxyphenyl) methylsulfonium hexafluorophosphate, (4- Octyloxyphenyl) diphenylsulfonium tetrakis (3,5-bis-trifluoromethylphenyl) borate, tris (dodecylphenyl) sulfonium tetrakis (3,5-bis-trifluoromethylphenyl) borate, 4-acetamidophenyldiphenylsulfonium tetrafluoro Borate, 4-acetamidophenyldiphenylsulfonium tetrakis (pentafluorobenzyl) borate, dimethylna Butylsulfonium hexafluorophosphate, trifluoromethyldiphenylsulfonium tetrafluoroborate, trifluoromethyldiphenylsulfonium tetrakis (pentafluorobenzyl) borate, phenylmethylbenzylsulfonium hexafluorophosphate, 10-methylphenoxathinium hexafluorophosphate, 5- Methylthiantrenium hexafluorophosphate, 10-phenyl-9,9-dimethylthioxanthenium hexafluorophosphate, 10-phenyl-9-oxothioxanthenium xanthenium tetrafluoroborate, 10-phenyl-9-oxothio Xanthenium tetrakis (pentafluorobenzyl) borate, 5-methyl-10-oxothiatrenium tetra Ruoroboreto, 5-methyl-10-oxo-thia Torre tetrakis (pentafluorobenzyl) borate, and 5-methyl-10,10-and di-oxo-thia tray hexafluorophosphate and the like.
ヨードニウム塩としては、（４−ｎ−デシロキシフェニル）フェニルヨードニウムヘキサフルオロアンチモネート、〔４−（２−ヒドロキシ−ｎ−テトラデシロキシ）フェニル〕フェニルヨードニウムヘキサフルオロアンチモネート、〔４−（２−ヒドロキシ−ｎ−テトラデシロキシ）フェニル〕フェニルヨードニウムトリフルオロスルホネート、〔４−（２−ヒドロキシ−ｎ−テトラデシロキシ）フェニル〕フェニルヨードニウムヘキサフルオロホスフェート、〔４−（２−ヒドロキシ−ｎ−テトラデシロキシ）フェニル〕フェニルヨードニウムテトラキス（ペンタフルオロフェニル）ボレート、ビス（４−ｔ−ブチルフェニル）ヨードニウムヘキサフルオロアンチモネート、ビス（４−ｔ−ブチルフェニル）ヨードニウムヘキサフルオロフォスフェート、ビス（４−ｔ−ブチルフェニル）ヨードニウムトリフルオロスルホネート、ビス（４−ｔ−ブチルフェニル）ヨードニウムテトラフルオロボレート、ビス（ドデシルフェニル）ヨードニウムヘキサフルオロアンチモネート、ビス（ドデシルフェニル）ヨードニウムテトラフルオロボレート、ビス（ドデシルフェニル）ヨードニウムヘキサフルオロフォスフェート、ビス（ドデシルフェニル）ヨードニウムトリフルオロメチルスルフォネート、ジ（ドデシルフェニル）ヨードニウムヘキサフルオロアンチモネート、ジ（ドデシルフェニル）ヨードニウムトリフラート、ジフェニルヨードニウムビスルフェート、４，４’−ジクロロジフェニルヨードニウムビスルフェート、４，４’−ジブロモジフェニルヨードニウムビスルフェート、３，３’−ジニトロジフェニルヨードニウムビスルフェート、４，４’−ジメチルジフェニルヨードニウムビスルフェート、４，４’−ビススクシンイミドジフェニルヨードニウムビスルフェート、３−ニトロジフェニルヨードニウムビスルフェート、４，４’−ジメトキシジフェニルヨードニウムビスルフェート、ビス（ドデシルフェニル）ヨードニウムテトラキス（ペンタフルオロフェニル）ボレート、（４−オクチルオキシフェニル）フェニルヨードニウムテトラキス（３，５−ビス−トリフルオロメチルフェニル）ボレート等が挙げられる。 Examples of the iodonium salt include (4-n-decyloxyphenyl) phenyliodonium hexafluoroantimonate, [4- (2-hydroxy-n-tetradecyloxy) phenyl] phenyliodonium hexafluoroantimonate, [4- (2- Hydroxy-n-tetradecyloxy) phenyl] phenyliodonium trifluorosulfonate, [4- (2-hydroxy-n-tetradecyloxy) phenyl] phenyliodonium hexafluorophosphate, [4- (2-hydroxy-n-tetrade Siloxy) phenyl] phenyliodonium tetrakis (pentafluorophenyl) borate, bis (4-t-butylphenyl) iodonium hexafluoroantimonate, bis (4-t-butylphenyl) iodonium hexafluoro Phosphate, bis (4-t-butylphenyl) iodonium trifluorosulfonate, bis (4-t-butylphenyl) iodonium tetrafluoroborate, bis (dodecylphenyl) iodonium hexafluoroantimonate, bis (dodecylphenyl) iodonium tetrafluoroborate Bis (dodecylphenyl) iodonium hexafluorophosphate, bis (dodecylphenyl) iodonium trifluoromethylsulfonate, di (dodecylphenyl) iodonium hexafluoroantimonate, di (dodecylphenyl) iodonium triflate, diphenyliodonium bissulfate, 4 , 4'-dichlorodiphenyliodonium bisulphate, 4,4'-dibromodiphenyliodonium bisulph 3,3′-dinitrodiphenyliodonium bisulphate, 4,4′-dimethyldiphenyliodonium bisulphate, 4,4′-bissuccinimide diphenyliodonium bisulphate, 3-nitrodiphenyliodonium bisulphate, 4,4′- Examples include dimethoxydiphenyliodonium bisulphate, bis (dodecylphenyl) iodonium tetrakis (pentafluorophenyl) borate, (4-octyloxyphenyl) phenyliodonium tetrakis (3,5-bis-trifluoromethylphenyl) borate, and the like.
その他のオニウム塩としては、芳香族ジアゾニウム塩を使用することができ、例えばｐ−メトキシベンゼンジアゾニウム・ヘキサフルオロアンチモネートなどを使用することができる。 As other onium salts, aromatic diazonium salts can be used. For example, p-methoxybenzenediazonium hexafluoroantimonate can be used.
商業的に入手できるオニウム塩としては、サンエイドＳＩ−６０、ＳＩ−８０、ＳＩ−１００、ＳＩ−６０Ｌ、ＳＩ−８０Ｌ、ＳＩ−１００Ｌ、ＳＩ−Ｌ１４５、ＳＩ−Ｌ１５０、ＳＩ−Ｌ１６０、ＳＩ−Ｌ１１０、ＳＩ−Ｌ１４７（以上、三新化学工業（株）製）、ＵＶＩ−６９５０、ＵＶＩ−６９７０、ＵＶＩ−６９７４、ＵＶＩ−６９９０（以上、ユニオンカーバイド社製）、アデカオプトマーＳＰ−１５０、ＳＰ−１５１、ＳＰ−１７０、ＳＰ−１７１、ＳＰ−１７２（以上、旭電化工業（株）製）、Ｉｒｇａｃｕｒｅ ２６１、Ｉｒｇａｃｕｒｅ２５０（チバスペシャルティケミカルズ（株）製）、ＣＩ−２４８１、ＣＩ−２６２４、ＣＩ−２６３９、ＣＩ−２０６４（以上、日本曹達（株）製）、ＣＤ−１０１０、ＣＤ−１０１１、ＣＤ−１０１２（以上、サートマー社製）、ＤＳ−１００、ＤＳ−１０１、ＤＡＭ−１０１、ＤＡＭ−１０２、ＤＡＭ−１０５、ＤＡＭ−２０１、ＤＳＭ−３０１、ＮＡＩ−１００、ＮＡＩ−１０１、ＮＡＩ−１０５、ＮＡＩ−１０６、ＳＩ−１００、ＳＩ−１０１、ＳＩ−１０５、ＳＩ−１０６、ＰＩ−１０５、ＮＤＩ−１０５、ＢＥＮＺＯＩＮ ＴＯＳＹＬＡＴＥ、ＭＢＺ−１０１、ＭＢＺ−３０１、ＰＹＲ−１００、ＰＹＲ−２００、ＤＮＢ−１０１、ＮＢ−１０１、ＮＢ−２０１、ＢＢＩ−１０１、ＢＢＩ−１０２、ＢＢＩ−１０３、ＢＢＩ−１０９（以上、みどり化学（株）製）、ＰＣＩ−０６１Ｔ、ＰＣＩ−０６２Ｔ、ＰＣＩ−０２０Ｔ、ＰＣＩ−０２２Ｔ（以上、日本化薬（株）製）、ＩＢＰＦ、ＩＢＣＦ（三和ケミカル（株）製）ＣＤ１０１２（サートマー社製）、ＩＢＰＦ、ＩＢＣＦ（以上、三和ケミカル（株）製）、ＢＢＩ−１０１、ＢＢＩ−１０２、ＢＢＩ−１０３、ＢＢＩ−１０９（以上、みどり化学（株）製）、ＵＶＥ１０１４（ゼネラルエレクトロニクス社製）、ＲＨＯＤＯＲＳＩＬ−ＰＩ２０７４（ローディア社製）、ＷＰＩ−１１３、ＷＰＩ−１１６（和光純薬（株）製）等を挙げることができる。また、Ｊ． Ｐｏｌｙｍｅｒ Ｓｃｉｅｎｃｅ：Ｐａｒｔ Ａ：ｐｏｌｙｍｅｒ Ｃｈｅｍｉｓｔｒｙ，Ｖｏｌ．３１， １４７３−１４８２（１９９３）， Ｊ． Ｐｏｌｙｍｅｒ Ｓｃｉｅｎｃｅ：Ｐａｒｔ Ａ：ｐｏｌｙｍｅｒ Ｃｈｅｍｉｓｔｒｙ，Ｖｏｌ．３１， １４８３−１４９１（１９９３）において記述されている方法により製造できるジアリールヨードニウム塩を使用することもできる。これらは、単独でも２種以上を組み合わせて使用することも良い。
光塩基発生剤とは、例えば、非環状のアシルオキシイミノ化合物、非環状のカルバモイルオキシム化合物、カルバモイルヒドロキシルアミン化合物、カルバミン酸化合物、ホルムアミド化合物、アセトアミド化合物、カルバメート化合物、ベンジルカルバメート化合物、ニトロベンジルカルバメート化合物、スルホンアミド化合物、イミダゾール誘導体化合物、アミンイミド化合物、ピリジン誘導体化合物、α−アミノアセトフェノン誘導体化合物、４級アンモニウム塩誘導体化合物、α−ラクトン環誘導体化合物、アミンイミド化合物、フタルイミド誘導体化合物などを用いることができる。なかでも比較的アミンの発生効率が高いアシルオキシイミノ化合物が好ましい。これらは、単独でも２種以上を組み合わせて使用することも良い。
Commercially available onium salts include Sun Aid SI-60, SI-80, SI-100, SI-60L, SI-80L, SI-100L, SI-L145, SI-L150, SI-L160, SI-L110. SI-L147 (manufactured by Sanshin Chemical Industry Co., Ltd.), UVI-6950, UVI-6970, UVI-6974, UVI-6990 (manufactured by Union Carbide), Adekaoptomer SP-150, SP- 151, SP-170, SP-171, SP-172 (above, manufactured by Asahi Denka Kogyo Co., Ltd.), Irgacure 261, Irgacure 250 (manufactured by Ciba Specialty Chemicals Co., Ltd.), CI-2481, CI-2624, CI-2623 CI-2064 (Nippon Soda Co., Ltd.), CD-1010, CD-1011 CD-1012 (manufactured by Sartomer), DS-100, DS-101, DAM-101, DAM-102, DAM-105, DAM-201, DSM-301, NAI-100, NAI-101, NAI- 105, NAI-106, SI-100, SI-101, SI-105, SI-106, PI-105, NDI-105, BENZOIN TOSYLATE, MBZ-101, MBZ-301, PYR-100, PYR-200, DNB -101, NB-101, NB-201, BBI-101, BBI-102, BBI-103, BBI-109 (above, manufactured by Midori Chemical Co., Ltd.), PCI-061T, PCI-062T, PCI-020T, PCI -022T (Nippon Kayaku Co., Ltd.), IBPF, IBCF (Sanwa Chemical Co., Ltd.) )) CD1012 (Sartomer), IBPF, IBCF (above, manufactured by Sanwa Chemical Co., Ltd.), BBI-101, BBI-102, BBI-103, BBI-109 (above, manufactured by Midori Chemical Co., Ltd.) UVE1014 (manufactured by General Electronics), RHODORSIL-PI2074 (manufactured by Rhodia), WPI-113, WPI-116 (manufactured by Wako Pure Chemical Industries, Ltd.), and the like. In addition, J.H. Polymer Science: Part A: Polymer Chemistry, Vol. 31, 1473-1482 (1993), J. MoI. Polymer Science: Part A: Polymer Chemistry, Vol. 31, 1483-1491 (1993) can also be used diaryl iodonium salts which can be prepared. These may be used alone or in combination of two or more.
Photobase generators include, for example, acyclic acyloxyimino compounds, acyclic carbamoyl oxime compounds, carbamoyl hydroxylamine compounds, carbamic acid compounds, formamide compounds, acetamide compounds, carbamate compounds, benzyl carbamate compounds, nitrobenzyl carbamate compounds, Sulfonamide compounds, imidazole derivative compounds, amine imide compounds, pyridine derivative compounds, α-aminoacetophenone derivative compounds, quaternary ammonium salt derivative compounds, α-lactone ring derivative compounds, amine imide compounds, phthalimide derivative compounds, and the like can be used. Of these, acyloxyimino compounds having relatively high amine generation efficiency are preferred. These may be used alone or in combination of two or more.
本実施の形態における硬化剤とは、樹脂組成物を硬化させるために用いられる物質であり、環状エーテル基と反応可能であれば、特に限定されるものではなく、後述の硬化促進剤との併用が好ましい。 The curing agent in the present embodiment is a substance used for curing the resin composition, and is not particularly limited as long as it can react with the cyclic ether group, and is used in combination with a curing accelerator described later. Is preferred.
硬化剤としては、例えば、酸無水物系化合物、アミン系化合物、アミド系化合物、フェノール系化合物等が挙げられ、中でも、酸無水物系化合物が好ましく、カルボン酸無水物がより好ましい。 Examples of the curing agent include acid anhydride compounds, amine compounds, amide compounds, phenol compounds, and the like. Among them, acid anhydride compounds are preferable, and carboxylic acid anhydrides are more preferable.
また、ここで言う酸無水物系化合物には脂環式酸無水物が含まれ、カルボン酸無水物の中でも脂環式カルボン酸無水物が好ましい。これらの物質は、単独で使用しても、複数を組み合わせて使用してもよい。 In addition, the acid anhydride compounds herein include alicyclic acid anhydrides, and among the carboxylic acid anhydrides, alicyclic carboxylic acid anhydrides are preferable. These substances may be used alone or in combination.
硬化剤の具体例としては、例えば、無水フタル酸、無水コハク酸、無水トリメリット酸、無水ピロメリット酸、無水マレイン酸、テトラヒドロ無水フタル酸、メチルテトラヒドロ無水フタル酸、無水メチルナジック酸、ヘキサヒドロ無水フタル酸、メチルヘキサヒドロ無水フタル酸、ジアミノジフェニルメタン、ジエチレントリアミン、トリエチレンテトラミン、ジアミノジフェニルスルホン、イソホロンジアミン、ジシアンジアミド、テトラエチレンペンタミン、ジメチルベンジルアミン、ケチミン化合物、リノレン酸の２量体とエチレンジアミンより合成されるポリアミド樹脂、ビスフェノール類、フェノール類（フェノール、アルキル置換フェノール、ナフトール、アルキル置換ナフトール、ジヒドロキシベンゼン、ジヒドロキシナフタレン等）と各種アルデヒドとの重縮合物、フェノール類と各種ジエン化合物との重合物、フェノール類と芳香族ジメチロールとの重縮合物、又はビスメトキシメチルビフェニルとナフトール類若しくはフェノール類との縮合物等、ビフェノール類及びこれらの変性物、イミダゾール、３フッ化硼素−アミン錯体、グアニジン誘導体等が挙げられる。 Specific examples of the curing agent include, for example, phthalic anhydride, succinic anhydride, trimellitic anhydride, pyromellitic anhydride, maleic anhydride, tetrahydrophthalic anhydride, methyltetrahydrophthalic anhydride, methylnadic anhydride, hexahydroanhydride Synthesis from phthalic acid, methylhexahydrophthalic anhydride, diaminodiphenylmethane, diethylenetriamine, triethylenetetramine, diaminodiphenylsulfone, isophoronediamine, dicyandiamide, tetraethylenepentamine, dimethylbenzylamine, ketimine compound, linolenic acid dimer and ethylenediamine Polyamide resins, bisphenols, phenols (phenol, alkyl-substituted phenol, naphthol, alkyl-substituted naphthol, dihydroxybenzene, dihydroxynaphth A polycondensate of aldehydes with various aldehydes, a polymer of phenols with various diene compounds, a polycondensate of phenols with aromatic dimethylol, or a condensate of bismethoxymethylbiphenyl with naphthols or phenols. Biphenols and their modified products, imidazole, boron trifluoride-amine complex, guanidine derivatives and the like.
脂環式カルボン酸無水物の具体例としては、１，２，３，６−テトラヒドロ無水フタル酸、３，４，５，６−テトラヒドロ無水フタル酸、ヘキサヒドロ無水フタル酸、「４−メチルヘキサヒドロ無水フタル酸／ヘキサヒドロ無水フタル酸＝７０／３０」、４−メチルヘキサヒドロ無水フタル酸、「メチルビシクロ［２．２．１］ヘプタン−２，３−ジカルボン酸無水物／ビシクロ［２．２．１］ヘプタン−２，３−ジカルボン酸無水物」等が挙げられる。 Specific examples of the alicyclic carboxylic acid anhydride include 1,2,3,6-tetrahydrophthalic anhydride, 3,4,5,6-tetrahydrophthalic anhydride, hexahydrophthalic anhydride, “4-methylhexahydro Phthalic anhydride / hexahydrophthalic anhydride = 70/30 ”, 4-methylhexahydrophthalic anhydride,“ methylbicyclo [2.2.1] heptane-2,3-dicarboxylic anhydride / bicyclo [2.2. 1] heptane-2,3-dicarboxylic anhydride "and the like.
また、脂肪族酸無水物の具体例としては、例えば、テトラプロペニル無水コハク酸、オクテニルコハク酸無水物、２，５−ジケトテトラヒドロフラン等が挙げられる。 Specific examples of the aliphatic acid anhydride include tetrapropenyl succinic anhydride, octenyl succinic anhydride, 2,5-diketotetrahydrofuran and the like.
本実施の形態における硬化促進剤とは、硬化反応の促進を目的に使用される硬化触媒を意味し、単独で用いても、複数を組み合わせて使用してもよい。硬化促進剤は、特に限定されるものではないが、３級アミン類及びその塩を選択することが好ましい。 The curing accelerator in the present embodiment means a curing catalyst used for the purpose of promoting the curing reaction, and may be used alone or in combination. Although a hardening accelerator is not specifically limited, It is preferable to select tertiary amines and its salt.
硬化促進剤の具体例としては、以下のものが挙げられる。
（１）３級アミン類：ベンジルジメチルアミン、２，４，６−トリス（ジメチルアミノメチル）フェノール、シクロヘキシルジメチルアミン、トリエタノールアミン等、
（２）イミダゾール類：２−メチルイミダゾール、２−ｎ−ヘプチルイミダゾール、２−ｎ−ウンデシルイミダゾール、２−フェニルイミダゾール、２−フェニル−４−メチルイミダゾール、１−ベンジル−２−メチルイミダゾール、１−ベンジル−２−フェニルイミダゾール、１，２−ジメチルイミダゾール、２−エチル−４−メチルイミダゾール、１−（２−シアノエチル）−２−メチルイミダゾール、１−（２−シアノエチル）−２−ｎ−ウンデシルイミダゾール、１−（２−シアノエチル）−２−フェニルイミダゾール、１−（２−シアノエチル）−２−エチル−４−メチルイミダゾール、２−フェニル−４−メチル−５−ヒドロキシメチルイミダゾール、２−フェニル−４，５−ジ（ヒドロキシメチル）イミダゾール、１−（２−シアノエチル）−２−フェニル−４，５−ジ〔（２’−シアノエトキシ）メチル〕イミダゾール、１−（２−シアノエチル）−２−ｎ−ウンデシルイミダゾリウムトリメリテート、１−（２−シアノエチル）−２−フェニルイミダゾリウムトリメリテート、１−（２−シアノエチル）−２−エチル−４−メチルイミダゾリウムトリメリテート、２，４−ジアミノ−６−〔２’−メチルイミダゾリル−（１’）〕エチル−ｓ−トリアジン、２，４−ジアミノ−６−（２’−ｎ−ウンデシルイミダゾリル）エチル−ｓ−トリアジン、２，４−ジアミノ−６−〔２’−エチル−４’−メチルイミダゾリル−（１’）〕エチル−ｓ−トリアジン、２−メチルイミダゾールのイソシアヌル酸付加物、２−フェニルイミダゾールのイソシアヌル酸付加物、２，４−ジアミノ−６−〔２’−メチルイミダゾリル−（１＆ａｐｏｓ；）〕エチル−ｓ−トリアジンのイソシアヌル酸付加物等、
（３）有機リン系化合物：ジフェニルフォスフィン、トリフェニルフォスフィン、亜リン酸トリフェニル等、
（４）４級フォスフォニウム塩類：ベンジルトリフェニルフォスフォニウムクロライド、テトラ−ｎ−ブチルフォスフォニウムブロマイド、メチルトリフェニルフォスフォニウムブロマイド、エチルトリフェニルフォスフォニウムブロマイド、ｎ−ブチルトリフェニルフォスフォニウムブロマイド、テトラフェニルフォスフォニウムブロマイド、エチルトリフェニルフォスフォニウムヨーダイド、エチルトリフェニルフォスフォニウムアセテート、テトラ−ｎ−ブチルフォスフォニウムｏ，ｏ−ジエチルフォスフォロジチオネート、テトラ−ｎ−ブチルフォスフォニウムベンゾトリアゾレート、テトラ−ｎ−ブチルフォスフォニウムテトラフルオロボレート、テトラ−ｎ−ブチルフォスフォニウムテトラフェニルボレート、テトラフェニルフォスフォニウムテトラッフェニルボレート等、
（５）ジアザビシクロアルケン類：１，８−ジアザビシクロ［５．４．０］ウンデセン−７及びその有機酸塩等、
（６）有機金属化合物：オクチル酸亜鉛、アクチル酸錫、アルミニウムアセチルアセトン錯体等、
（７）４級アンモニウム塩類：テトラエチルアンモニウムブロマイド、テトラ−ｎ−ブチルアンモニウムブロマイド等、
（８）金属ハロゲン化合物：三フッ化ホウ素、ホウ酸トリフェニル等のホウ素化合物；塩化亜鉛、塩化第二錫等。
Specific examples of the curing accelerator include the following.
(1) Tertiary amines: benzyldimethylamine, 2,4,6-tris (dimethylaminomethyl) phenol, cyclohexyldimethylamine, triethanolamine, etc.
(2) Imidazoles: 2-methylimidazole, 2-n-heptylimidazole, 2-n-undecylimidazole, 2-phenylimidazole, 2-phenyl-4-methylimidazole, 1-benzyl-2-methylimidazole, 1 -Benzyl-2-phenylimidazole, 1,2-dimethylimidazole, 2-ethyl-4-methylimidazole, 1- (2-cyanoethyl) -2-methylimidazole, 1- (2-cyanoethyl) -2-n-un Decylimidazole, 1- (2-cyanoethyl) -2-phenylimidazole, 1- (2-cyanoethyl) -2-ethyl-4-methylimidazole, 2-phenyl-4-methyl-5-hydroxymethylimidazole, 2-phenyl -4,5-di (hydroxymethyl) imidazole, 1- (2- Anoethyl) -2-phenyl-4,5-di [(2′-cyanoethoxy) methyl] imidazole, 1- (2-cyanoethyl) -2-n-undecylimidazolium trimellitate, 1- (2-cyanoethyl) ) -2-Phenylimidazolium trimellitate, 1- (2-cyanoethyl) -2-ethyl-4-methylimidazolium trimellitate, 2,4-diamino-6- [2′-methylimidazolyl- (1 ′) )] Ethyl-s-triazine, 2,4-diamino-6- (2'-n-undecylimidazolyl) ethyl-s-triazine, 2,4-diamino-6- [2'-ethyl-4'-methyl Imidazolyl- (1 ′)] ethyl-s-triazine, isocyanuric acid adduct of 2-methylimidazole, isocyanuric acid adduct of 2-phenylimidazole, 2,4-di Mino-6- [2'-methylimidazolyl- - (1 ')] isocyanuric acid adduct of ethyl -s- triazine,
(3) Organophosphorus compounds: diphenylphosphine, triphenylphosphine, triphenyl phosphite, etc.
(4) Quaternary phosphonium salts: benzyltriphenylphosphonium chloride, tetra-n-butylphosphonium bromide, methyltriphenylphosphonium bromide, ethyltriphenylphosphonium bromide, n-butyltriphenylphos Phonium bromide, tetraphenylphosphonium bromide, ethyltriphenylphosphonium iodide, ethyltriphenylphosphonium acetate, tetra-n-butylphosphonium o, o-diethylphosphorodithionate, tetra-n- Butylphosphonium benzotriazolate, tetra-n-butylphosphonium tetrafluoroborate, tetra-n-butylphosphonium tetraphenylborate, tetraphenylphenol Scan follower tetra Tsu tetraphenylborate, etc.,
(5) Diazabicycloalkenes: 1,8-diazabicyclo [5.4.0] undecene-7 and its organic acid salt,
(6) Organometallic compounds: zinc octylate, tin actylate, aluminum acetylacetone complex, etc.
(7) Quaternary ammonium salts: tetraethylammonium bromide, tetra-n-butylammonium bromide, etc.
(8) Metal halide compounds: Boron compounds such as boron trifluoride and triphenyl borate; zinc chloride, stannic chloride and the like.
架橋剤としては、特に限定されるものでは無いが、例えば、（メタ）アクリロイル基を複数個有する化合物が挙げられる。 Although it does not specifically limit as a crosslinking agent, For example, the compound which has multiple (meth) acryloyl groups is mentioned.
（メタ）アクリロイル基を分子内に２個有する（メタ）アクリレート架橋剤としては、エチレングリコールジ（メタ）アクリレート、ブタンジオールジ（メタ）アクリレート、ヘキサンジオールジ（メタ）アクリレート、シクロヘキサンジメタノールジ（メタ）アクリレートなどのアルキレングリコールジ（メタ）アクリレート；トリエチレングリコールジ（メタ）アクリレート、トリプロピレングリコールジ（メタ）アクリレート、テトラエチレングリコールジ（メタ）アクリレート、ポリエチレングリコールジ（メタ）アクリレートなどのポリアルキレングリコールジ（メタ）アクリレートなどが例示される。 Examples of the (meth) acrylate crosslinking agent having two (meth) acryloyl groups in the molecule include ethylene glycol di (meth) acrylate, butanediol di (meth) acrylate, hexanediol di (meth) acrylate, cyclohexanedimethanol di ( Alkylene glycol di (meth) acrylate such as (meth) acrylate; polyethylene such as triethylene glycol di (meth) acrylate, tripropylene glycol di (meth) acrylate, tetraethylene glycol di (meth) acrylate, polyethylene glycol di (meth) acrylate Examples include alkylene glycol di (meth) acrylate.
（メタ）アクリロイル基を分子内に３個有する（メタ）アクリレート架橋剤としては、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレートなどの分岐状アルキル基を有するトリ（メタ）アクリレート；グリセロールプロポキシトリ（メタ）アクリレート、トリメチロールプロパントリエトキシトリ（メタ）アクリレートなどの分岐状アルキレンエーテル基を有するトリ（メタ）アクリレート；トリス（２−ヒドロキシエチル）イソシアヌレートトリ（メタ）アクリレートなど複素環を含有するトリ（メタ）アクリレートなどが例示される。 As a (meth) acrylate crosslinking agent having three (meth) acryloyl groups in the molecule, a tri (meth) acrylate having a branched alkyl group such as trimethylolpropane tri (meth) acrylate or pentaerythritol tri (meth) acrylate ; Tri (meth) acrylates having branched alkylene ether groups such as glycerol propoxy tri (meth) acrylate and trimethylolpropane triethoxytri (meth) acrylate; complex such as tris (2-hydroxyethyl) isocyanurate tri (meth) acrylate Examples thereof include tri (meth) acrylate containing a ring.
（メタ）アクリロイル基を分子内に４個以上有する（メタ）アクリレート架橋剤としては、ジ（トリメチロールプロパン）テトラ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレートなどの複数の分岐状アルキル基を有するポリ（メタ）アクリレート；ジペンタエリスリトールペンタ（メタ）アクリレートなどの複数の分岐状アルキル基と水酸基とを有するポリ（メタ）アクリレートなどが例示される。これらの（メタ）アクリル酸エステル系架橋剤は、単独で用いても、２種以上を組み合わせて用いてもよい。 As the (meth) acrylate crosslinking agent having 4 or more (meth) acryloyl groups in the molecule, a plurality of branched alkyl groups such as di (trimethylolpropane) tetra (meth) acrylate and dipentaerythritol hexa (meth) acrylate Examples include poly (meth) acrylates having a plurality of branched alkyl groups and hydroxyl groups such as dipentaerythritol penta (meth) acrylate. These (meth) acrylic acid ester-based crosslinking agents may be used alone or in combination of two or more.
後述の通りコーティングの手法は、特に限定されるものではないが、大面積にコーティング可能であることや設備コストの抑制が可能であるため、ウエットコート法を採用することが望ましい。そのためには、コーティング材は、上述の有機無機複合体を溶媒に分散させた液体であることが好ましい。 As will be described later, the coating method is not particularly limited, but it is desirable to employ a wet coating method because it can be coated over a large area and the equipment cost can be suppressed. For this purpose, the coating material is preferably a liquid in which the organic-inorganic composite described above is dispersed in a solvent.
コーティング材における固形分濃度（フリーポリマーを含む有機無機複合体の濃度）は、特に限定されるものではないが、分散性と成膜性のバランスから、コーティング材全体質量を基準として、好ましくは１〜５０質量％、更に好ましくは１〜３０質量％、特に好ましくは１〜２０質量％である。固形分濃度は、有機無機複合体をそのまま直接希釈して調整してもよいし、希薄溶液をエバポレーター等で濃縮して調製してもよい。 The solid content concentration in the coating material (concentration of the organic-inorganic composite containing the free polymer) is not particularly limited, but preferably 1 based on the total mass of the coating material from the balance of dispersibility and film forming property. -50 mass%, More preferably, it is 1-30 mass%, Most preferably, it is 1-20 mass%. The solid content concentration may be adjusted by directly diluting the organic-inorganic composite as it is, or may be prepared by concentrating a dilute solution with an evaporator or the like.
［有機無機複合膜］
本実施形態の有機無機複合膜は、有機無機複合体を含み、上記要件を満たす膜であれば、特に限定されるものではない。本発明において「膜」とは、厚みが限定されるものではなく、支持基盤上に形成されたものでもよく、単体で構造を形成しているものであってもよい。
[Organic inorganic composite film]
The organic-inorganic composite film of the present embodiment is not particularly limited as long as it includes an organic-inorganic composite and satisfies the above requirements. In the present invention, the “film” is not limited in thickness, and may be formed on a support base or may form a structure alone.
本発明において「空隙」の用語は、膜を形成している隣り合う２個以上の有機無機複合体無機化合物粒子同士の間に形成されたミクロボイドのことを意味する。「空洞」の用語は、無機化合物粒子自体の内部に形成された空孔を意味し、「空隙」とは区別される。 In the present invention, the term “void” means a microvoid formed between two or more adjacent inorganic compound particles forming a film. The term “cavity” means pores formed inside the inorganic compound particles themselves, and is distinguished from “voids”.
空隙の大きさは、特に限定されるものではないが、光を散乱しない大きさであることが好ましい。つまり、空隙を有する膜であっても、光学的あるいは巨視的には均一な膜とみなすことができる。このため、膜のみかけ体積を基準とする空隙の割合、すなわち空隙率は、膜を形成している有機無機複合体の屈折率（＞１）と、空隙の屈折率（空気の屈折率：１．００）との体積平均に基づいて算出することができる。 The size of the gap is not particularly limited, but is preferably a size that does not scatter light. That is, even a film having voids can be regarded as an optically or macroscopically uniform film. For this reason, the ratio of the voids based on the apparent volume of the film, that is, the void ratio, is the refractive index (> 1) of the organic-inorganic composite forming the film and the refractive index of the void (refractive index of air: 1 .00) and a volume average.
有機無機複合体間に形成された空隙の割合（空隙率）は、当該有機無機複合硬化膜の体積を基準として３〜９０体積％であり、より好ましくは１０〜８５％、さらに好ましくは２０〜８０％である。空隙率が３体積％未満であると、膜の低屈折率化の効果が小さくなる傾向がある。また、空隙率が９０体積％を超えると、膜強度が低下して脆くなるという傾向がある。 The ratio of the voids formed between the organic-inorganic composites (porosity) is 3 to 90% by volume, more preferably 10 to 85%, and still more preferably 20 to 20% based on the volume of the organic-inorganic composite cured film. 80%. When the porosity is less than 3% by volume, the effect of lowering the refractive index of the film tends to be reduced. Moreover, when the porosity exceeds 90 volume%, there exists a tendency for film | membrane intensity | strength to fall and to become weak.
有機無機複合膜の屈折率は、特に限定されるものではないが、後述の方法で測定され、表示装置の品位向上の観点から１．３８以下であることが好ましく、より好ましくは１．３５以下、更に好ましくは１．３０以下、特に好ましくは１．２５以下、そして最も好ましくは１．２０以下である。屈折率が１．３８より大きいと、積層体を表示装置へ組み込んでも、目視では品位の向上が視認できない可能性がある。 The refractive index of the organic-inorganic composite film is not particularly limited, but is measured by a method described later, and is preferably 1.38 or less, more preferably 1.35 or less from the viewpoint of improving the quality of the display device. More preferably, it is 1.30 or less, particularly preferably 1.25 or less, and most preferably 1.20 or less. If the refractive index is greater than 1.38, the improvement in quality may not be visually recognized even when the laminate is incorporated into a display device.
有機無機複合膜の最小反射率は、特に限定されるものではないが、後述の方法で測定され、反射率抑制の観点から１．５％以下であることが好ましく、より好ましくは１％以下、更に好ましくは０．５％以下、特に好ましくは０．２％以下である。最小反射率が１．５％より大きいと、反射防止の効果が得られにくくなる。 The minimum reflectance of the organic-inorganic composite film is not particularly limited, but is measured by the method described later, and is preferably 1.5% or less, more preferably 1% or less, from the viewpoint of suppressing reflectance. More preferably, it is 0.5% or less, and particularly preferably 0.2% or less. When the minimum reflectance is larger than 1.5%, it is difficult to obtain an antireflection effect.
本実施形態の有機無機複合膜は、有機無機複合体を含む膜であれば、特に限定されるものではないが、上述のコーティング材を、後述の手法でコーティングして形成した膜であることが好ましい。一般的には、基材上（例えば、ＰＥＴフィルム、ＴＡＣフィルム、ガラス、アクリル・ポリカーボネート等の樹脂素材、金属、シリコンウエハ、ＬＥＤ、半導体、ＣＤ、ＤＶＤ等、若しくは種々のハードコート層）に、数ｎｍ〜数ｃｍの厚みで形成する。 The organic-inorganic composite film of the present embodiment is not particularly limited as long as it is a film containing an organic-inorganic composite, but may be a film formed by coating the above-described coating material by a method described later. preferable. Generally, on a base material (for example, PET film, TAC film, glass, resin material such as acrylic / polycarbonate, metal, silicon wafer, LED, semiconductor, CD, DVD, or various hard coat layers) It is formed with a thickness of several nm to several cm.
コーティングの手法としては、「蒸着、スパッタリング、イオンプレーディング等のドライコーティング法」や、「印刷、スリットコート、バーコート、アプリケーター塗工、スピンコート、ブレードコート、エアナイフコート、グラビアコート、ロールコート、スプレーコート、ディップコート等のウエットコーティング法」等が、一般的に知られている。また上述の方法以外に、「フィルム成形、ラミネート成形、射出成形、ブロー成形、圧縮成形、回転成形、押出成形、延伸成形等の成形加工法」を応用し、基材の上に、有機無機複合膜を形成する手法もある。これらの手法は、単独でも、複数を組み合わせて使用することも可能である。 Coating methods include “dry coating methods such as vapor deposition, sputtering, ion plating” and “printing, slit coating, bar coating, applicator coating, spin coating, blade coating, air knife coating, gravure coating, roll coating, “Wet coating methods such as spray coating and dip coating” are generally known. In addition to the above-mentioned methods, "organic molding methods such as film molding, laminate molding, injection molding, blow molding, compression molding, rotational molding, extrusion molding, stretch molding, etc." There is also a method of forming a film. These techniques can be used alone or in combination.
「フリーポリマー」とは、無機化合物粒子に結合していないポリマーを意味する。硬化物においては、硬化物を形成する組成物であって、硬化反応前に無機化合物粒子に結合していないポリマー、あるいは低分子量の有機化合物も含まれる。つまり、フリーポリマーは、有機無機複合体無機化合物粒子同士の間に形成される空隙を埋める化合物を意味する。フリーポリマーの測定方法については、後述の実施例において詳細に説明される。 “Free polymer” means a polymer that is not bound to inorganic compound particles. The cured product is a composition that forms a cured product, and includes a polymer that is not bonded to the inorganic compound particles before the curing reaction, or a low molecular weight organic compound. That is, the free polymer means a compound that fills voids formed between organic-inorganic composite inorganic compound particles. The method for measuring the free polymer will be described in detail in the examples below.
本実施形態における、無機化合物粒子に結合していないフリーポリマーの割合は、後述の方法で求められ、無機化合物量に対して効果的に空隙を形成させるという観点から、その割合は好ましくは３０質量％以下、より好ましくは２０質量％以下、更に好ましくは３質量％以下である。上述したように、フリーポリマーの割合が３０質量％以上になると、フリーポリマーが構造体中で均一に分散しないために安定的に製造することが困難になるばかりでなく、有機無機複合体の無機物化合物粒子間に形成される空隙を、フリーポリマーが埋めるため、空隙率が低下してしまう。空隙の屈折率は、１．００で、膜を形成する材料と比較すると、極めて小さな値である。そのため、わずかな空隙率の差で、屈折率が大きく変化するため、フリーポリマー量を制御し、効果的に均一な空隙を形成させることが好ましい。 In the present embodiment, the proportion of the free polymer that is not bonded to the inorganic compound particles is determined by the method described later, and from the viewpoint of effectively forming voids with respect to the amount of the inorganic compound, the proportion is preferably 30 masses. % Or less, more preferably 20% by mass or less, still more preferably 3% by mass or less. As described above, when the ratio of the free polymer is 30% by mass or more, the free polymer is not uniformly dispersed in the structure, and thus it is difficult to stably produce the inorganic polymer. Since the free polymer fills the voids formed between the compound particles, the porosity is lowered. The refractive index of the air gap is 1.00, which is an extremely small value compared to the material forming the film. For this reason, since the refractive index changes greatly due to a slight difference in porosity, it is preferable to control the amount of free polymer to effectively form uniform voids.
本実施の形態における有機無機複合膜の硬化としては、特に限定されるものではないが、エネルギー線硬化又は熱硬化が好ましく、特に好ましくは光硬化である。光硬化の手法は、特に限定されるものではなく、通常、活性光線の刺激により重合開始剤が分解することで重合開始種が発生し、対象物質の重合性官能基を重合するという経過を辿る。 Although it does not specifically limit as hardening of the organic inorganic composite film in this Embodiment, Energy beam hardening or thermosetting is preferable, Especially preferably, it is photocuring. The method of photocuring is not particularly limited, and usually follows a process in which a polymerization initiator is decomposed by the decomposition of a polymerization initiator by stimulation of actinic rays to polymerize a polymerizable functional group of a target substance. .
光硬化とは、活性光線（紫外線、近紫外線、可視光線、近赤外線、赤外線等）を照射することで硬化物を得る方法であり、活性光線の種類としては、特に限定されるものではないが、好ましくは紫外線又は可視光線、より好ましくは紫外線である。 Photocuring is a method of obtaining a cured product by irradiating actinic rays (ultraviolet rays, near ultraviolet rays, visible rays, near infrared rays, infrared rays, etc.), and the type of actinic rays is not particularly limited. , Preferably ultraviolet light or visible light, and more preferably ultraviolet light.
光硬化の中でも、光ラジカル重合タイプは、反応性二重結合の反応性が高く、短い時間で架橋させられる等の利点から、より好ましい。 Among photocuring, the radical photopolymerization type is more preferable because it has high reactivity of reactive double bonds and can be crosslinked in a short time.
上述の光ラジカル重合による架橋に加え、カチオン重合、加熱による架橋反応、有機ポリマーと反応し得る官能基を有する化合物との混合による架橋反応などを組み合わせて用いてもよい。有機無機複合体の架橋は、例えば、有機無機複合体のポリマー中に少なくとも１つの反応性二重結合を有する場合、光ラジカル開始剤から発生したラジカルにより反応性二重結合から重合反応を開始し、ポリマー間、又はポリマーと無機化合物粒子との間に結合を形成させることにより行うことができる。また、架橋剤を含む場合、架橋剤によりポリマー間、又はポリマーと無機化合物粒子との間に結合を形成させることにより行うことができる。なお、ポリマー間、又はポリマーと無機化合物粒子との間の結合は、異なる有機無機複合体のポリマー間、又はポリマーと無機化合物粒子との間での結合が好ましいが、同一の有機無機複合体のポリマー間、又はポリマーと無機化合物粒子との間での結合もあり得る。 In addition to the above-mentioned crosslinking by radical photopolymerization, cationic polymerization, crosslinking reaction by heating, crosslinking reaction by mixing with a compound having a functional group capable of reacting with an organic polymer, and the like may be used in combination. For example, when the organic-inorganic composite has at least one reactive double bond in the polymer of the organic-inorganic composite, the polymerization reaction is initiated from the reactive double bond by a radical generated from the photoradical initiator. , By forming a bond between the polymers or between the polymer and the inorganic compound particles. Moreover, when a crosslinking agent is included, it can be performed by forming a bond between polymers or between a polymer and inorganic compound particles with a crosslinking agent. The bond between the polymers or between the polymer and the inorganic compound particles is preferably a bond between the polymers of different organic-inorganic composites or between the polymer and the inorganic compound particles. There may also be a bond between the polymers or between the polymer and the inorganic compound particles.
活性光線の発生源は、特に限定されるものではなく、例えば、低圧水銀灯、中圧水銀灯、高圧水銀灯、超高圧水銀灯、ＵＶランプ、キセノンランプ、カーボンアーク灯、メタルハライドランプ、蛍光灯、タングステンランプ、アルゴンイオンレーザ、ヘリウムカドミウムレーザ、ヘリウムネオンレーザ、クリプトンイオンレーザ、各種半導体レーザ、ＹＡＧレーザ、エキシマーレーザー、発光ダイオード、ＣＲＴ光源、プラズマ光源、電子線照射器等の各種光源等が挙げられる。 The source of actinic rays is not particularly limited, and for example, low pressure mercury lamp, medium pressure mercury lamp, high pressure mercury lamp, ultra high pressure mercury lamp, UV lamp, xenon lamp, carbon arc lamp, metal halide lamp, fluorescent lamp, tungsten lamp, Examples include argon ion laser, helium cadmium laser, helium neon laser, krypton ion laser, various semiconductor lasers, YAG laser, excimer laser, light emitting diode, CRT light source, plasma light source, and various light sources such as an electron beam irradiator.
照射光強度は、使用する光源の波長などに応じて異なるが、通常、数ｍＷ／ｃｍ２〜１０Ｗ／ｃｍ２の範囲である。照射光強度は、好ましくは、数１０ｍＷ／ｃｍ２〜５Ｗ／ｃｍ２程度の範囲内である。照射量は、反応性二重結合の感度、コーティング膜の厚みや温度などに応じて適宜設定される。 The irradiation light intensity varies depending on the wavelength of the light source used, but is usually in the range of several mW / cm 2 to 10 W / cm 2 . The irradiation light intensity is preferably in the range of about several tens of mW / cm 2 to 5 W / cm 2 . The irradiation amount is appropriately set according to the sensitivity of the reactive double bond, the thickness and temperature of the coating film, and the like.
ここで、熱硬化とは、熱による化学反応により分子間に３次元の架橋結合を生じさせることで硬化させる方法である。熱硬化の方法としては、特に限定されるものではないが、硬化剤や硬化促進剤を使用して熱硬化させる方法、又は、熱カチオン重合開始剤を用いて熱硬化させる方法を選択するのが好ましく、中でも、硬化剤や硬化促進剤を使用して熱硬化させる方法がより好ましい。 Here, thermosetting is a method of curing by causing a three-dimensional cross-linking between molecules by a chemical reaction by heat. The method of thermosetting is not particularly limited, but a method of thermosetting using a curing agent or a curing accelerator or a method of thermosetting using a thermal cationic polymerization initiator is selected. Among them, a method of thermosetting using a curing agent or a curing accelerator is more preferable.
本実施形態に係る有機無機複合膜は、優れた透明性と光学特性を有しており、その指標である、厚み方向の全光線透過率は、特に限定されるものではないが、好ましくは８５〜１００％、より好ましくは８８〜１００％、更に好ましくは９０〜１００％である。同様に、ヘーズの値は、特に限定されるものではないが、好ましくは０〜５％、より好ましくは０〜３％、更に好ましくは０〜２％である。 The organic-inorganic composite film according to the present embodiment has excellent transparency and optical characteristics, and the total light transmittance in the thickness direction, which is an index thereof, is not particularly limited, but is preferably 85. -100%, more preferably 88-100%, still more preferably 90-100%. Similarly, the haze value is not particularly limited, but is preferably 0 to 5%, more preferably 0 to 3%, and still more preferably 0 to 2%.
本実施形態に係る有機無機複合膜は、所望の屈折率を達成し易いことから、光学材料や光学部材として有用である。その代表例としては、反射防止膜やハードコート膜等を挙げることができる。 The organic-inorganic composite film according to the present embodiment is useful as an optical material or an optical member because it easily achieves a desired refractive index. Typical examples thereof include an antireflection film and a hard coat film.
［有機無機複合膜の製造方法］
本実施形態に係る有機無機複合膜の製造方法は、特に限定されるものではないが、以下に代表的な製造方法を示す。
[Method for producing organic-inorganic composite film]
Although the manufacturing method of the organic inorganic composite film which concerns on this embodiment is not specifically limited, The typical manufacturing method is shown below.
［有機無機複合膜の製造方法１：硬化処理無し］
（１）有機無機複合体に、有機溶媒を加えて分散し、コーティング材を得る。
（２）コーティング材を基板上に塗布し、塗布されたコーティング材から有機溶媒を除去することにより有機無機複合膜を形成させる。
[Method for producing organic-inorganic composite film 1: no curing treatment]
(1) An organic solvent is added to and dispersed in the organic-inorganic composite to obtain a coating material.
(2) An organic-inorganic composite film is formed by applying a coating material on a substrate and removing an organic solvent from the applied coating material.
［有機無機複合膜の製造方法２：光硬化（光ラジカル硬化）］
（１）有機無機複合体に、有機溶媒、光ラジカル開始剤を加えて分散し、コーティング材を得る。
（２）コーティング材を基板上に塗布し、塗布されたコーティング材から有機溶媒を除去することにより有機無機複合膜を形成させる。
（３）更に、有機無機複合膜に活性光線を照射し、有機無機複合体を架橋させ（光硬化）、有機無機複合膜を得る。
[Method for producing organic-inorganic composite film 2: photocuring (photoradical curing)]
(1) An organic solvent and a photoradical initiator are added to and dispersed in the organic-inorganic composite to obtain a coating material.
(2) An organic-inorganic composite film is formed by applying a coating material on a substrate and removing an organic solvent from the applied coating material.
(3) Furthermore, the organic / inorganic composite film is irradiated with actinic rays to crosslink the organic / inorganic composite (photocuring) to obtain an organic / inorganic composite film.
［有機無機複合膜の製造方法３：光硬化（光カチオン硬化）］
（１）有機無機複合体に、有機溶媒、光酸発生剤を加えて分散し、コーティング材を得る。
（２）コーティング材を基板上に塗布し、塗布されたコーティング材から有機溶媒を除去することにより有機無機複合膜を形成させる。
（３）更に、有機無機複合膜に活性光線を照射し、有機無機複合体を架橋させ（光硬化）、有機無機複合膜を得る。
[Method for producing organic-inorganic composite film 3: photocuring (photocationic curing)]
(1) An organic solvent and a photoacid generator are added to and dispersed in the organic-inorganic composite to obtain a coating material.
(2) An organic-inorganic composite film is formed by applying a coating material on a substrate and removing an organic solvent from the applied coating material.
(3) Furthermore, the organic / inorganic composite film is irradiated with actinic rays to crosslink the organic / inorganic composite (photocuring) to obtain an organic / inorganic composite film.
［有機無機複合膜の製造方法４：熱硬化（硬化剤及び硬化促進剤による架橋）］
（１）有機無機複合体に、有機溶媒、硬化剤、硬化促進剤を加えて分散し、コーティング材を得る。
（２）コーティング材を基板上に塗布し、塗布されたコーティング材から有機溶媒を除去することにより有機無機複合膜を形成させる。
（３）更に、有機無機複合膜を所定時間加熱し、有機無機複合体を架橋させ（熱硬化）、有機無機複合膜を得る。
[Method for producing organic-inorganic composite film 4: thermal curing (crosslinking with curing agent and curing accelerator)]
(1) An organic solvent, a curing agent and a curing accelerator are added to the organic-inorganic composite and dispersed to obtain a coating material.
(2) An organic-inorganic composite film is formed by applying a coating material on a substrate and removing an organic solvent from the applied coating material.
(3) Further, the organic-inorganic composite film is heated for a predetermined time to crosslink the organic-inorganic composite (thermosetting) to obtain an organic-inorganic composite film.
［接続層］
本実施形態に係る積層体は、粘着剤又は接着剤を含有する層である接続層を有する。接続層としては、粘着剤を含有し、粘着性を付与する層である粘着層が挙げられる。また、接続層としては、接着剤を含有し、接着性を付与する層である接着層も例示できる。
[Connection layer]
The laminated body which concerns on this embodiment has a connection layer which is a layer containing an adhesive or an adhesive agent. Examples of the connection layer include an adhesive layer that contains an adhesive and imparts adhesiveness. Moreover, as a connection layer, the contact bonding layer which is a layer which contains an adhesive agent and provides adhesiveness can also be illustrated.
［粘着層］
本実施形態に係る粘着層は、粘着性を付与する層であれば、特に限定されるものではないが、表示装置への使用を前提とする場合は、透過光を妨げないことが好ましい。具体的に要求される好ましい特性としては、例えば、Ｈａｚｅが低い、入射光の散乱が少ない、光学等方性、長期信頼性等が挙げられる。
[Adhesive layer]
The adhesive layer according to the present embodiment is not particularly limited as long as it is a layer that imparts adhesiveness. However, when it is assumed to be used for a display device, it is preferable not to prevent transmitted light. Specific characteristics specifically required include, for example, low haze, low scattering of incident light, optical isotropy, long-term reliability, and the like.
粘着層のガラス転移温度（以下、Ｔｇと言う。）は、熱変動による積層体の歪み緩和の観点から、好ましくは４０℃以下、より好ましくは２０℃以下、更に好ましくは０℃以下、特に好ましくは−２０℃以下である。 The glass transition temperature (hereinafter referred to as Tg) of the pressure-sensitive adhesive layer is preferably 40 ° C. or less, more preferably 20 ° C. or less, still more preferably 0 ° C. or less, particularly preferably from the viewpoint of relaxing strain of the laminate due to thermal fluctuation. Is −20 ° C. or lower.
また粘着層は、積層する光学部材界面での化学結合が無い、あるいは弱いため、後述の接着層と比較して、積層体や表示装置製造時のリワーク性に優れている。 In addition, since the adhesive layer has no or weak chemical bond at the interface of the optical member to be laminated, it is superior in reworkability at the time of manufacturing a laminate and a display device as compared with an adhesive layer described later.
粘着層を形成する粘着剤の種類は、特に限定されず、例えば、溶剤型粘着剤、非水系エマルジョン型粘着剤、水系粘着剤、ホットメルト粘着剤等が挙げられる。これらは単独で使用しても、複数を組み合せて使用しても良い。 The type of the pressure-sensitive adhesive forming the pressure-sensitive adhesive layer is not particularly limited, and examples thereof include a solvent-type pressure-sensitive adhesive, a non-aqueous emulsion-type pressure-sensitive adhesive, a water-based pressure-sensitive adhesive, and a hot melt pressure-sensitive adhesive. These may be used alone or in combination.
粘着剤としては、粘着性を示す物質であれば、特に限定されず、例えば、ポリアクリル酸エステル、ポリビニルアルコール、シリコーン系ポリマー、ポリエステル、ポリウレタン、ポリアミド、ポリエーテル、フッ素系やゴム系等のポリマーをベースポリマーとする、任意のものを選択できる。 The adhesive is not particularly limited as long as it is a substance exhibiting adhesiveness. For example, polyacrylic acid ester, polyvinyl alcohol, silicone-based polymer, polyester, polyurethane, polyamide, polyether, fluorine-based or rubber-based polymer, etc. Any base polymer can be selected.
また偏光板等に使用する場合は、偏光子や偏光板保護フィルム等に対し、適切な粘着特性を示し、且つ、透明性に優れることから、アクリル酸エステル（共）重合体を含む、溶剤型粘着剤が好ましく用いられる。 In addition, when used for polarizing plates, etc., a solvent type containing an acrylate (co) polymer because it exhibits appropriate adhesive properties for polarizers, polarizing plate protective films, etc., and is excellent in transparency. An adhesive is preferably used.
上記アクリル酸エステルの中でも、粘着性とＴｇのバランスの観点から、アクリル酸ブチル（ｎＢＡ）、アクリル酸エチル（ＥＡ）、アクリル酸２−エチルヘキシル（ＥＨＡ）、アクリル酸イソノニルが好ましく、より好ましくは、ｎＢＡ、ＨＥＡであり、特に好ましくは、ｎＢＡである。 Among the acrylic esters, butyl acrylate (nBA), ethyl acrylate (EA), 2-ethylhexyl acrylate (EHA), and isononyl acrylate are preferable, more preferably, from the viewpoint of the balance between tackiness and Tg. nBA and HEA, particularly preferably nBA.
上記アクリル酸エステルに共重合するコモノマーは、特に限定されるものではないが、凝集力向上の観点から、酢酸ビニル（ＶＡ）、アクリロニトリル（ＡＮ）、アクリルアミド、スチレン（Ｓｔ）、メタクリル酸メチル（ＭＭＡ）、アクリル酸メチル（ＭＡ）等が好適である。 The comonomer copolymerized with the acrylate ester is not particularly limited. From the viewpoint of improving cohesion, vinyl acetate (VA), acrylonitrile (AN), acrylamide, styrene (St), methyl methacrylate (MMA) ), Methyl acrylate (MA) and the like are suitable.
また粘着性・接着性向上の観点から、上記アクリル酸エステルに、官能性モノマーを共重合させても良い。官能性モノマーは、官能基を持つモノマーであれば、特に限定されるものではないが、共重合性と粘着性・接着性の観点から、アクリル酸（ＡＡ）、アクリル酸２−ヒドロキシエチル（ＨＥＡ）、アクリルアミド、メタクリル酸グリシジル（ＧＭＡ）、アクリル酸２−イソシアナトエチル、メタクリル酸２−イソシアナトエチル等が好ましく、より好ましくは、アクリル酸、アクリル酸２−ヒドロキシエチルである。 Further, from the viewpoint of improving the tackiness and adhesiveness, a functional monomer may be copolymerized with the above acrylic ester. The functional monomer is not particularly limited as long as it is a monomer having a functional group, but from the viewpoints of copolymerizability, tackiness and adhesiveness, acrylic acid (AA), 2-hydroxyethyl acrylate (HEA) ), Acrylamide, glycidyl methacrylate (GMA), 2-isocyanatoethyl acrylate, 2-isocyanatoethyl methacrylate and the like, more preferably acrylic acid and 2-hydroxyethyl acrylate.
上記アクリル酸エステル共重合体の中でも、入手のし易さや取扱いの観点から、ｎＢＡ／ＡＡの共重合体や、ｎＢＡ／ＡＡ／ＨＥＡの共重合体が好ましい。 Among the acrylic ester copolymers, an nBA / AA copolymer and an nBA / AA / HEA copolymer are preferable from the viewpoint of easy availability and handling.
粘着層の形態は、特に限定されず、液体、フィルム状、シート状等任意のものを選択できる。 The form of the adhesive layer is not particularly limited, and any form such as a liquid, a film, or a sheet can be selected.
粘着層の付設方法は、特に限定されず、例えば、有機溶媒や水等の適宜な分散媒媒に、ベースポリマー又はその組成物を溶解又は分散させた、粘着剤溶液を調製し、それを流延方式や塗工方式等の適宜な展開方式で、付設面に直接付設する方法や、保護フィルム上に粘着層を形成してそれを付設面に移着する方式などがあげられる。また市販の粘着フィルムや粘着シートを使用しても良い。 The method for attaching the adhesive layer is not particularly limited, and for example, an adhesive solution is prepared by dissolving or dispersing the base polymer or a composition thereof in an appropriate dispersion medium such as an organic solvent or water, and flowing the solution. Examples thereof include a method of directly attaching to the attachment surface by an appropriate development method such as a spreading method and a coating method, and a method of forming an adhesive layer on the protective film and transferring it to the attachment surface. Commercially available adhesive films and adhesive sheets may also be used.
［接着層］
本実施形態に係る接着層は、接着性を付与する層であれば、特に限定されるものではないが、表示装置への使用を前提とする場合は、透過光を妨げないことが好ましい。具体的に要求される好ましい特性としては、例えば、Ｈａｚｅが低い、入射光の散乱が少ない、光学等方性、長期信頼性等が挙げられる。
[Adhesive layer]
The adhesive layer according to the present embodiment is not particularly limited as long as it is a layer that imparts adhesiveness. However, when it is assumed to be used for a display device, it is preferable not to prevent transmitted light. Specific characteristics specifically required include, for example, low haze, low scattering of incident light, optical isotropy, long-term reliability, and the like.
接着層を形成する接着剤としては、特に限定されるものではないが、例えば、硬化型接着剤が挙げられる。硬化型接着剤の代表例としては、紫外線硬化型等の光硬化型接着剤、湿気硬化型接着剤、熱硬化型接着剤等が挙げられ、これらは単独で使用しても、複数を組み合せて使用しても良い。 Although it does not specifically limit as an adhesive agent which forms a contact bonding layer, For example, a curable adhesive is mentioned. Representative examples of curable adhesives include UV curable adhesives, moisture curable adhesives, thermosetting adhesives, and the like. These may be used alone or in combination. May be used.
熱硬化型接着剤の具体例としては、エポキシ樹脂、イソシアネート樹脂およびポリイミド樹脂等の熱硬化性樹脂系接着剤が挙げられる。 Specific examples of the thermosetting adhesive include thermosetting resin adhesives such as epoxy resins, isocyanate resins, and polyimide resins.
湿気硬化型接着剤の具体例としては、イソシアネート樹脂系の湿気硬化型接着剤が挙げられる。湿気硬化型接着剤（特に、イソシアネート樹脂系の湿気硬化型接着剤）が好ましい。湿気硬化型接着剤は、空気中の水分や被着体表面の吸着水、水酸基やカルボキシル基等の活性水素基等と反応して硬化するので、接着剤を塗工後、放置することによって自然に硬化させることが可能であり、操作性に優れる。更に硬化のための加熱が不要であり、加熱収縮の心配が無く、積層する光学フィルム等が極めて薄い場合であっても、積層時の割れ等が防止できる。尚、上記イソシアネート樹脂系接着剤とは、ポリイソシアネート系接着剤、ポリウレタン樹脂接着剤の総称である。 Specific examples of the moisture curable adhesive include isocyanate resin-based moisture curable adhesive. A moisture curable adhesive (especially an isocyanate resin-based moisture curable adhesive) is preferred. Moisture curable adhesives cure by reacting with moisture in the air, adsorbed water on the surface of the adherend, active hydrogen groups such as hydroxyl groups and carboxyl groups, and so on. It can be cured to a high degree of operability. Further, heating for curing is unnecessary, there is no concern about heat shrinkage, and even when the laminated optical film or the like is extremely thin, cracking during lamination can be prevented. The isocyanate resin adhesive is a general term for polyisocyanate adhesives and polyurethane resin adhesives.
上記硬化型接着剤は、例えば、市販の接着剤を使用してもよく、上記の各種硬化型樹脂を溶媒に溶解または分散し、硬化型樹脂接着剤溶液（または分散液）として調製してもよい。用いられる溶媒としては、硬化型樹脂の種類に応じて任意の適切な溶媒が採用され得る。具体例としては、酢酸エチル、メチルエチルケトン（ＭＥＫ）、メチルイソブチルケトン（ＭＩＢＫ）、トルエン、キシレン等が挙げられる。これらは単独で使用しても、複数を組み合せて使用しても良い。 As the curable adhesive, for example, a commercially available adhesive may be used, or the above various curable resins may be dissolved or dispersed in a solvent to prepare a curable resin adhesive solution (or dispersion). Good. As a solvent to be used, any appropriate solvent can be adopted depending on the type of curable resin. Specific examples include ethyl acetate, methyl ethyl ketone (MEK), methyl isobutyl ketone (MIBK), toluene, xylene and the like. These may be used alone or in combination.
接続層には、例えば、天然物や合成物の樹脂類、特に、粘着性付与樹脂や、ガラス繊維、ガラスビーズ、金属粉、その他の無機粉末等からなる充填剤や顔料、着色剤、酸化防止剤などの粘着剤層に添加されることの添加剤を含有していてもよい。また微粒子を含有させ、光拡散性を付与しても良い。 For the connection layer, for example, natural and synthetic resins, in particular, tackifier resins, fillers and pigments made of glass fibers, glass beads, metal powders, other inorganic powders, colorants, antioxidants, etc. An additive to be added to the pressure-sensitive adhesive layer such as an agent may be contained. Further, fine particles may be included to impart light diffusibility.
また接続層は、異なる組成又は種類を使用して、重畳層として付設することができる。また積層体を構成する各層、つまり、支持体、有機無機複合膜、光学部材等の片面に設けても良く、両面に設けても良い。 The connection layer can be attached as a superposition layer using different compositions or types. Further, each layer constituting the laminate, that is, a support, an organic-inorganic composite film, an optical member, or the like may be provided on one side, or may be provided on both sides.
接続層の厚みは、使用目的や接着力などに応じて、適宜設定できる。具体的には、粘着剤層の厚みは、好ましくは２０ｎｍ〜５０μｍ、さらに好ましくは１００ｎｍ〜１０μｍ、更に好ましくは５００ｎｍ〜５μｍである。 The thickness of the connection layer can be appropriately set according to the purpose of use, adhesive strength, and the like. Specifically, the thickness of the pressure-sensitive adhesive layer is preferably 20 nm to 50 μm, more preferably 100 nm to 10 μm, and still more preferably 500 nm to 5 μm.
［支持体］
本実施形態に係る支持体は、その上に有機無機複合膜及び接続層を形成できる、フィルム状、シート状、板状の平板であれば、特に限定されるものではないが、光学材料用途で使用する場合は、透明性が高いものが好ましい。
[Support]
The support according to this embodiment is not particularly limited as long as it is a film-like, sheet-like, or plate-like flat plate on which an organic-inorganic composite film and a connection layer can be formed. When using, a thing with high transparency is preferable.
支持体は、上記の要件を満たすものであれば、特に限定されるものではないが、透明性と光学特性の観点から、例えば、ＴＡＣフィルム（トリアセチルセルロースフィルム）をはじめとするセルロースフィルム、ＰＥＴフィルム（ポリエチレンテレフタラートフィルム）、（メタ）アクリルフィルム、環状ポリオレフィンフィルム（ＣＯＰフィルム）、ＰＰフィルム（ポリプロピレンフィルム）、ポリカーボネート（ＰＣ）フィルム、ガラス基板等が好適である。中でも、ＴＡＣフィルム、ＰＥＴフィルム、（メタ）アクリルフィルム、ＣＯＰフィルムが好ましく、より好ましくは、ＴＡＣフィルムと（メタ）アクリルフィルムである。 The support is not particularly limited as long as it satisfies the above requirements. From the viewpoint of transparency and optical properties, for example, cellulose films including TAC films (triacetyl cellulose films), PET A film (polyethylene terephthalate film), (meth) acrylic film, cyclic polyolefin film (COP film), PP film (polypropylene film), polycarbonate (PC) film, glass substrate and the like are suitable. Among these, a TAC film, a PET film, a (meth) acrylic film, and a COP film are preferable, and a TAC film and a (meth) acrylic film are more preferable.
上記セルロースフィルムの原料としては、例えば、トリアセチルセルロース（ＴＡＣ）、セルロースジアセテート、セルローストリプロピオネート、セルロースジプロピオネート等があげられる。これらの中でも、光学特性と入手のし易さの観点から、ＴＡＣが特に好ましい。ＴＡＣフィルムの市販品の例としては、富士フイルム株式会社製の「ＵＶ−５０」、「ＵＶ−８０」、「ＳＨ−８０」、「ＴＤ−８０Ｕ」、「ＴＤ−ＴＡＣ」、「ＵＺ−ＴＡＣ」や、コニカミノルタ株式会社製の「ＫＣシリーズ」等が挙げられる。 Examples of the raw material for the cellulose film include triacetyl cellulose (TAC), cellulose diacetate, cellulose tripropionate, and cellulose dipropionate. Among these, TAC is particularly preferable from the viewpoints of optical properties and availability. Examples of commercially available TAC films include “UV-50”, “UV-80”, “SH-80”, “TD-80U”, “TD-TAC”, “UZ-TAC” manufactured by FUJIFILM Corporation. And “KC series” manufactured by Konica Minolta, Inc., and the like.
上記（メタ）アクリルフィルムの原料としては、本発明の効果を損なわない範囲内で、任意の適切な（メタ）アクリル系樹脂を採用できる。例えば、ポリメタクリル酸メチル等のポリ（メタ）アクリル酸エステル、メタクリル酸メチル−（メタ）アクリル酸共重合体、メタクリル酸メチル−（メタ）アクリル酸エステル共重合体、メタクリル酸メチル−アクリル酸エステル−（メタ）アクリル酸共重合体、（メタ）アクリル酸メチル−スチレン共重合体（ＭＳ樹脂など）、脂環族炭化水素基を有する重合体（例えば、メタクリル酸メチル−メタクリル酸シクロヘキシル共重合体、メタクリル酸メチル−（メタ）アクリル酸ノルボルニル共重合体など）が挙げられる。具体例としては、例えば、三菱レイヨン株式会社製の「アクリペットＶＨ」や「アクリペットＶＲＬ２０Ａ」、特開２００４−７０２９６号公報に記載の分子内に環構造を有する（メタ）アクリル系樹脂等が挙げられる。 As a raw material of the (meth) acrylic film, any appropriate (meth) acrylic resin can be adopted as long as the effects of the present invention are not impaired. For example, poly (meth) acrylic acid ester such as polymethyl methacrylate, methyl methacrylate- (meth) acrylic acid copolymer, methyl methacrylate- (meth) acrylic acid ester copolymer, methyl methacrylate-acrylic acid ester -(Meth) acrylic acid copolymer, (meth) acrylic acid methyl-styrene copolymer (MS resin, etc.), polymer having an alicyclic hydrocarbon group (for example, methyl methacrylate-cyclohexyl methacrylate copolymer) And methyl methacrylate- (meth) acrylate norbornyl copolymer). Specific examples include, for example, “Acrypet VH” and “Acrypet VRL20A” manufactured by Mitsubishi Rayon Co., Ltd., and (meth) acrylic resins having a ring structure in the molecule described in JP-A-2004-70296. Can be mentioned.
また（メタ）アクリル系樹脂として、ラクトン環構造を有する（メタ）アクリル系樹脂を用いることもできる。ラクトン環構造を有する（メタ）アクリル系樹脂としては、例えば、特開２０００−２３００１６号公報、特開２００１−１５１８１４号公報、特開２００２−１２０３２６号公報、特開２００２−２５４５４４号公報、特開２００５−１４６０８４号公報などに記載のものが挙げられる。 A (meth) acrylic resin having a lactone ring structure can also be used as the (meth) acrylic resin. Examples of the (meth) acrylic resin having a lactone ring structure include, for example, JP 2000-230016, JP 2001-151814, JP 2002-120326, JP 2002-254544, JP The thing as described in 2005-146084 gazette etc. is mentioned.
上記ＣＯＰフィルムの原料としては、例えば、特開平１−２４０５１７号公報、特開平３−１４８８２号公報、特開平３−１２２１３７号公報等に記載の、環状ポリオレフィン樹脂が挙げられる。具体例としては、環状オレフィンの開環（共）重合体、環状オレフィンの付加重合体、環状オレフィンとエチレン、プロピレン等のα−オレフィンとその共重合体、及び、これらを不飽和カルボン酸やその誘導体で変性したグラフト重合体、並びに、それらの水素化物などが挙げられる。環状ポリオレフィン樹脂の市販品としては、例えば、日本ゼオン株式会社製の「ゼオネックス」、「ゼオノア」、ＪＳＲ株式会社製の「アートン」、ＴＯＰＡＳ Ａｄｖａｎｃｅｄ Ｐｏｌｙｍｅｒｓ ＧｍｂＨ社製の「ＴＯＰＡＳ」、三井化学株式会社製の商品名「ＡＰＥＬ」が挙げられ、これらをフィルム化して使用しても良い。 Examples of the raw material for the COP film include cyclic polyolefin resins described in JP-A-1-240517, JP-A-3-14882, JP-A-3-122137, and the like. Specific examples include ring-opening (co) polymers of cyclic olefins, addition polymers of cyclic olefins, cyclic olefins and α-olefins such as ethylene and propylene, and copolymers thereof, and unsaturated carboxylic acids and their Examples thereof include graft polymers modified with derivatives, and hydrides thereof. Examples of commercially available cyclic polyolefin resins include “ZEONEX” and “ZEONOR” manufactured by ZEON Corporation, “ARTON” manufactured by JSR Corporation, “TOPAS” manufactured by TOPAS Advanced Polymers GmbH, and manufactured by Mitsui Chemicals, Inc. Product name “APEL”, and these may be used as a film.
支持体の厚みは、特に限定されるものではないが、積層体の厚みと強度のバランスの観点から、光学材料用途で使用する場合は、好ましくは２０μｍ〜２ｍｍ、より好ましくは３０〜３００μｍ、更に好ましくは４０〜２００μｍである。 The thickness of the support is not particularly limited, but from the viewpoint of the balance between the thickness and strength of the laminate, when used in an optical material application, it is preferably 20 μm to 2 mm, more preferably 30 to 300 μm, and further Preferably it is 40-200 micrometers.
支持体の厚みは 、その用途に応じ、適宜選択することができる。例えば、比較的画面が大きく、生産性と強度が要求される薄型テレビに使用する場合は、６０〜１２０μｍが好ましく、より好ましくは８０〜１００μｍである。また、軽量化が要求される、タッチパネルや携帯電話に使用する場合は、２０μｍ〜６０μｍが好ましく、より好ましくは３０〜４０μｍである。 The thickness of the support can be appropriately selected according to the application. For example, when it is used for a thin television where the screen is relatively large and productivity and strength are required, the thickness is preferably 60 to 120 μm, more preferably 80 to 100 μm. Moreover, when using for a touch panel and a mobile telephone in which weight reduction is requested | required, 20 micrometers-60 micrometers are preferable, More preferably, they are 30-40 micrometers.
上記支持体は、積層体の製造時に剥がして廃棄しても良いし、偏光板保護フィルムやタッチパネル用ガラス基板として、そのまま表示装置に組み込んでも良い。 The said support body may be peeled off and discarded at the time of manufacture of a laminated body, and may be incorporated in a display apparatus as it is as a polarizing plate protective film or a glass substrate for touch panels.
［積層体］
本実施の形態に係る積層体は、有機無機複合膜と接続層とを有する積層体であれば、特に限定されない。
[Laminate]
The laminated body which concerns on this Embodiment will not be specifically limited if it is a laminated body which has an organic inorganic composite film and a connection layer.
積層体は、有機無機複合膜と接続層に加え、更に、支持体；セパレーター；偏光子、偏光板、偏光板保護フィルム、視覚補償フィルム（ＷＶフィルム）、液晶フィルム、液晶層、カラーフィルター、位相差フィルム、輝度向上フィルム、拡散板、プリズムシート、導光板、反射板、導電フィルム、透明電極等の光学部材；等から選択される、一種又は複数の部材と積層することができる。 In addition to the organic-inorganic composite film and the connection layer, the laminate is further a support; separator; polarizer, polarizing plate, polarizing plate protective film, visual compensation film (WV film), liquid crystal film, liquid crystal layer, color filter, position It can be laminated with one or more members selected from a phase difference film, a brightness enhancement film, a diffusion plate, a prism sheet, a light guide plate, a reflection plate, a conductive film, an optical member such as a transparent electrode, and the like.
積層体の構成や、積層の順序は、特に限定されないが、例えば、以下の構成を含むものが例示される。 Although the structure of a laminated body and the order of lamination | stacking are not specifically limited, For example, what includes the following structures is illustrated.
＜構成１＞
下記（ａ）〜（ｃ）が連続して積層した構成を含む、積層体。
（ａ）支持体
（ｂ）有機無機複合膜
（ｃ）接続層
<Configuration 1>
The laminated body containing the structure which the following (a)-(c) laminated | stacked continuously.
(A) Support (b) Organic-inorganic composite film (c) Connection layer
＜構成２＞
上記構成１に、更に、下記（ｄ）及び（ｅ）を積層し、（ａ）〜（ｅ）が連続した構成を含む、積層体。
（ｄ）有機無機複合膜
（ｅ）接続層
<Configuration 2>
The laminated body including the construction in which the following (d) and (e) are further laminated on the configuration 1 and (a) to (e) are continuous.
(D) Organic-inorganic composite film (e) Connection layer
［偏光板］
本実施形態の偏光板は、特定方向に偏光、又は偏波した光だけに限って通過させる板であれば、特に限定されず、例えば、直線偏光板、円偏光板、楕円偏光板等の種類が挙げられる。
[Polarizer]
The polarizing plate of the present embodiment is not particularly limited as long as it is a plate that allows only polarized light in a specific direction or polarized light to pass therethrough. Is mentioned.
偏光板の基本構成としては、例えば、偏光子の両面に偏光板保護フィルムを設けたものが良く知られており、２枚の偏光板保護フィルムのうち１枚の裏側に、粘着層を設けた状態で販売される場合もある。 As a basic configuration of the polarizing plate, for example, a polarizing plate protective film provided on both sides of a polarizer is well known, and an adhesive layer is provided on the back side of one of the two polarizing plate protective films. Sometimes sold in state.
図４は、偏光板の基本構成の一例を示す模式断面図である。偏光板３０は、偏光子３２と、該偏光子３２の両面に設けられた偏光板保護フィルム３１及び３３を備えている。 FIG. 4 is a schematic cross-sectional view showing an example of the basic configuration of the polarizing plate. The polarizing plate 30 includes a polarizer 32 and polarizing plate protective films 31 and 33 provided on both surfaces of the polarizer 32.
図５は、粘着層付偏光板の基本構成の一例を示す模式断面図である。粘着層付偏光板４０は、偏光子４４と、該偏光子４４の両面に設けられた偏光板保護フィルム４３及び４５とを備えている。また、粘着層付偏光板４０においては、偏光板保護フィルム４３の偏光子４４と反対側の面上に粘着層４２が設けられている。なお、粘着層付偏光板４０は、場合により、粘着層４２を介してセパレータ４１が接着されていてもよい。 FIG. 5 is a schematic cross-sectional view showing an example of the basic configuration of the polarizing plate with an adhesive layer. The polarizing plate with an adhesive layer 40 includes a polarizer 44 and polarizing plate protective films 43 and 45 provided on both surfaces of the polarizer 44. Moreover, in the polarizing plate 40 with an adhesion layer, the adhesion layer 42 is provided on the surface on the opposite side to the polarizer 44 of the polarizing plate protective film 43. In addition, as for the polarizing plate 40 with the adhesion layer, the separator 41 may be adhere | attached through the adhesion layer 42 by the case.
偏光子は、特に限定されるものではないが、具体例としては、ヨウ素系偏光子、二色系染料を用いる染料偏光子、ポリエン系偏光子等が挙げられる。ヨウ素系偏光子や染料偏光子は、一般的に、一般に、延伸前又は後にポリビニルアルコール（以下、ＰＶＡと言う。）フィルムを染色することによって製造される。一般には、ポリ酢酸ビニルを鹸化することによって得られたＰＶＡを使用するが、改質ＰＶＡを使用することも可能である。ＰＶＡフィルムの染色は、任意の手段、例えば、ヨウ素−ヨウ化カリウム水溶液中に浸漬させるか、ヨウ素溶液又は染色溶液を、スプレッドコート又は噴霧することによって実施できる。ＰＶＡフィルムの延伸時には、ＰＶＡを架橋結合するための添加剤（例：ホウ酸化合物）を、使用することが好ましい。 The polarizer is not particularly limited, but specific examples include iodine polarizers, dye polarizers using dichroic dyes, polyene polarizers, and the like. In general, iodine-based polarizers and dye polarizers are generally produced by dyeing a polyvinyl alcohol (hereinafter referred to as PVA) film before or after stretching. In general, PVA obtained by saponifying polyvinyl acetate is used, but modified PVA can also be used. The dyeing of the PVA film can be carried out by any means, for example, by dipping in an iodine-potassium iodide aqueous solution, spread coating or spraying with an iodine solution or a dyeing solution. At the time of stretching the PVA film, it is preferable to use an additive (for example, boric acid compound) for cross-linking PVA.
偏光板保護フィルムは、特に限定されるものではないが、透明性と光学特性の観点から、ＴＡＣフィルム、（メタ）アクリルフィルム、ＣＯＰフィルム等が用いられる場合が多い。偏光子を挟んで存在する、２枚の偏光板保護フィルムは、同じものを用いても良いし、１枚ずつ違う種類のものを使用しても良い。 The polarizing plate protective film is not particularly limited, but a TAC film, a (meth) acrylic film, a COP film or the like is often used from the viewpoints of transparency and optical properties. The two polarizing plate protective films present with the polarizer sandwiched between them may be the same or different ones may be used.
ＴＡＣフィルムを用いる場合は、ＡＣフィルムを鹸化処理することにより、偏光子と接着するのが一般的であるが、（メタ）アクリルフィルムやＣＯＰフィルムを使用する場合には、偏光子と偏光板保護フィルムは、上述の粘着剤を介して積層される場合が多い。 When using a TAC film, the AC film is generally saponified to adhere to the polarizer. However, when using a (meth) acrylic film or COP film, the polarizer and the polarizing plate are protected. In many cases, the film is laminated via the above-mentioned pressure-sensitive adhesive.
上記基本構成に加え、更に他の光学部材等を積層することで、以下に例示する、他の機能が付加された偏光板も作製可能である。 In addition to the above basic configuration, another optical member or the like is further laminated to produce a polarizing plate with other functions added as exemplified below.
（Ａ）反射防止機能付偏光板
上記基本構成に加え、偏光板保護フィルムの少なくとも１枚に、有機無機複合膜を形成し、反射防止効果を付与することができる。偏光板保護フィルムが反射防止フィルムを兼ねることで、偏光板の製造コストを低減することが可能であり、前記反射防止フィルムを偏光板の最表層に設置すると、外光の映り込みが抑制された偏光板を、製造することができる。
(A) Polarizing plate with antireflection function In addition to the above basic configuration, an organic-inorganic composite film can be formed on at least one polarizing plate protective film to impart an antireflection effect. Since the polarizing plate protective film also serves as an antireflection film, it is possible to reduce the manufacturing cost of the polarizing plate. A polarizing plate can be produced.
図６は、反射防止機能付偏光板の基本構成の一例を示す模式断面図である。反射防止機能付偏光板５０Ａは、偏光板３０の一方面上にハードコート層５３及び有機無機複合膜５４がこの順で設けられ、偏光板３０の他方面上に粘着層５２及びセパレータ５１がこの順で設けられた構成を有する。また、反射防止機能付偏光板５０Ｂは、偏光板３０と、偏光板３０の一方面上に設けられたハードコート層５３及び有機無機複合膜５４とを備える。なお、図６に示す偏光板３０としては、図４に示す偏光板３０と同様のものが例示できる。 FIG. 6 is a schematic cross-sectional view illustrating an example of a basic configuration of a polarizing plate with an antireflection function. In the polarizing plate 50A with an antireflection function, a hard coat layer 53 and an organic-inorganic composite film 54 are provided in this order on one surface of the polarizing plate 30, and an adhesive layer 52 and a separator 51 are provided on the other surface of the polarizing plate 30. It has the structure provided in order. The antireflection function polarizing plate 50 </ b> B includes a polarizing plate 30 and a hard coat layer 53 and an organic-inorganic composite film 54 provided on one surface of the polarizing plate 30. In addition, as the polarizing plate 30 shown in FIG. 6, the thing similar to the polarizing plate 30 shown in FIG. 4 can be illustrated.
偏光板保護フィルムとしてＴＡＣフィルムを使用し、その片側に反射防止処理を施す場合は、支持体の裏側（反射防止膜が設置されない側）の面を、アルカリで、鹸化処理する必要がある。鹸化処理の手法は、特に限定されるものではないが、具体的には、以下の２つの方法が例示できる。 When a TAC film is used as a polarizing plate protective film and an antireflection treatment is performed on one side thereof, the surface on the back side (side on which the antireflection film is not provided) of the support needs to be saponified with an alkali. The method of the saponification treatment is not particularly limited, but specifically, the following two methods can be exemplified.
（１）支持体に、有機無機複合膜（反射防止膜）を形成後、アルカリ液中に１回以上浸漬し、全体を鹸化処理する。
（２）支持体に、有機無機複合膜（反射防止膜）を形成する前、又は、形成した後に、支持体の裏側（反射防止膜が設置されない側）の面に、アルカリ液を塗布し、加熱、水洗、中和等の処理を施すことで、支持体の裏面のみを鹸化処理する。
(1) After forming an organic-inorganic composite film (antireflection film) on the support, it is immersed in an alkaline solution at least once to saponify the whole.
(2) Before or after forming the organic-inorganic composite film (antireflection film) on the support, an alkaline solution is applied to the back side of the support (the side where the antireflection film is not installed), Only the back surface of the support is saponified by applying treatments such as heating, washing and neutralization.
上記（１）の方法は、支持体と同じ工程で処理できるという点では優れているが、有機無機複合膜等が鹸化処理により劣化する可能性があるため、品質的には、上記（２）の方法を選択する方が好ましい。 The method (1) is excellent in that it can be treated in the same step as the support, but the organic-inorganic composite membrane or the like may be deteriorated by the saponification treatment. It is preferable to select this method.
（Ｂ）位相差フィルム付偏光板
上記偏光板の基本構成に、位相差フィルムを積層することで得られる。積層の方式は特に限定されるものではないが、例えば、偏光板と位相差フィルムを接続層を介して積層し、位相差フィルムの反対側（偏光板と積層されていない側）にも接続層を積層することができる。
(B) Polarizing plate with retardation film Obtained by laminating a retardation film on the basic structure of the polarizing plate. The method of lamination is not particularly limited. For example, a polarizing plate and a retardation film are laminated via a connection layer, and the connection layer is also provided on the opposite side of the retardation film (side not laminated with the polarizing plate). Can be laminated.
図７は、位相差フィルム付偏光板の基本構成の一例を示す模式断面図である。位相差フィルム付偏光板６０は、反射防止機能付偏光板５０の一面上に、粘着層６４、位相差フィルム６３、粘着層６２及びセパレータ６１がこの順で積層された構成を有する。なお、図７における反射防止機能付偏光板５０としては、図６における反射防止機能付偏光板５０Ｂと同様のものが例示できる。また、図７では、反射防止機能付偏光板の一方面上に位相差フィルム付偏光板を設けた構成を示したが、位相差フィルム付偏光板は、図４に示す偏光板３０と同様の偏光板の一方面上に粘着層を介して位相差フィルムを設けたものであっても良い。 FIG. 7 is a schematic cross-sectional view showing an example of the basic configuration of a polarizing plate with a retardation film. The polarizing plate with retardation film 60 has a configuration in which an adhesive layer 64, a retardation film 63, an adhesive layer 62, and a separator 61 are laminated in this order on one surface of the polarizing plate 50 with an antireflection function. In addition, as the polarizing plate 50 with an antireflection function in FIG. 7, the thing similar to the polarizing plate 50B with an antireflection function in FIG. 6 can be illustrated. 7 shows a configuration in which a polarizing plate with a retardation film is provided on one surface of a polarizing plate with an antireflection function, the polarizing plate with a retardation film is the same as the polarizing plate 30 shown in FIG. A retardation film may be provided on one surface of the polarizing plate via an adhesive layer.
（Ｃ）視覚補償機能付偏光板
上記偏光板の基本構成に、視覚補償フィルム（ＷＶフィルム）を積層することで得られる。積層の方式は特に限定されるものではないが、例えば、偏光子とＷＶフィルムを積層し、偏光子の片側には偏光板保護フィルムを積層し、ＷＶフィルムの反対側（偏光子と積層されていない側）にも接続層を積層することができる。
(C) Polarizing plate with visual compensation function It is obtained by laminating a visual compensation film (WV film) on the basic structure of the polarizing plate. The lamination method is not particularly limited. For example, a polarizer and a WV film are laminated, a polarizing plate protective film is laminated on one side of the polarizer, and the opposite side of the WV film (laminated with the polarizer). The connection layer can also be laminated on the non-side.
図８は、視覚補償機能付偏光板の基本構成の一例を示す模式断面図である。視覚補償機能付偏光板７０は、偏光子７４の一面上に偏光板保護フィルム７５、ハードコート層７６及び有機無機複合膜７７がこの順で積層され、偏光子７４の他面上にＷＶフィルム７３、粘着層７２及びセパレータ７１がこの順で積層された構成を有する。 FIG. 8 is a schematic cross-sectional view showing an example of a basic configuration of a polarizing plate with a visual compensation function. In the polarizing plate 70 with visual compensation function, a polarizing plate protective film 75, a hard coat layer 76, and an organic-inorganic composite film 77 are laminated in this order on one surface of the polarizer 74, and a WV film 73 is formed on the other surface of the polarizer 74. The adhesive layer 72 and the separator 71 are stacked in this order.
［光学材料］
本実施形態に係る光学材料は、上述の積層体を備えており、表示装置等を形成するために用いられる。
[Optical materials]
The optical material according to the present embodiment includes the above-described laminated body and is used for forming a display device and the like.
光学材料とは、可視光、赤外線、紫外線、Ｘ線、レーザーなどの光をその材料中を通過させる用途に使用する材料一般をさす。光学材料は、様々な用途に用いることが可能である。 The optical material generally refers to a material used for the purpose of passing light such as visible light, infrared light, ultraviolet light, X-rays, and laser through the material. The optical material can be used for various applications.
本実施の形態に係る光学材料の用途は、特に限定されるものではないが、表示装置、タッチパネル、コンピュータ、テレビ、携帯電話、テレビ電話、電子書籍、ゲーム機等の玩具、カーナビゲーションシステム、電子看板、電子表示板、太陽電池、メガネレンズ、カメラレンズ等に、好適に利用できる。 The use of the optical material according to the present embodiment is not particularly limited, but a display device, a touch panel, a computer, a television, a mobile phone, a videophone, an electronic book, a toy such as a game machine, a car navigation system, an electronic It can be suitably used for signboards, electronic display boards, solar cells, eyeglass lenses, camera lenses, and the like.
また、その他用途に使用される光学材料としては、光記録分野では、例えば、ＶＤ（ビデオディスク）、ＣＤ／ＣＤ−ＲＯＭ、ＣＤ−Ｒ／ＲＷ、ＤＶＤ−Ｒ／ＤＶＤ−ＲＡＭ、ＭＯ／ＭＤ、ＰＤ（相変化ディスク）、又は光カード用のディスク基板材料及び周辺材料、ピックアップレンズ、保護フィルム、封止フィルム等が挙げられる。 Further, as optical materials used for other applications, in the optical recording field, for example, VD (video disc), CD / CD-ROM, CD-R / RW, DVD-R / DVD-RAM, MO / MD, Examples include PD (phase change disc) or disc substrate materials and peripheral materials for optical cards, pickup lenses, protective films, and sealing films.
光半導体分野では、例えば、発光ダイオード（ＬＥＤ）、半導体レーザー、フォトダイオード、フォトトランジスタ、ＣＣＤ／ＣＭＯＳセンサ、フォトカプラ、フォトリレー、フォトインタラプタ、及び光通信用デバイス等の周辺材料が挙げられる。 In the field of optical semiconductors, for example, peripheral materials such as light emitting diodes (LEDs), semiconductor lasers, photodiodes, phototransistors, CCD / CMOS sensors, photocouplers, photorelays, photointerrupters, and optical communication devices can be cited.
光学機器分野では、例えば、カメラの撮影レンズ、レンズ用材料、ファインダー、ファインダプリズム、ターゲットプリズム、ファインダーカバー、受光センサーの周辺材料が挙げられる。プロジェクションテレビの投射レンズ、保護フィルムなども例示される。 In the field of optical equipment, for example, a photographing lens of a camera, a lens material, a finder, a finder prism, a target prism, a finder cover, and a peripheral material of a light receiving sensor are exemplified. Examples thereof include projection lenses for projection televisions and protective films.
光部品分野では、例えば、光通信システムでの光スイッチ周辺のファイバー材料、レンズ、導波路、素子の周辺材料が例示される。光コネクタ周辺の光ファイバー材料も例示される。光受動部品及び光回路部品については、レンズ、導波路、ＬＥＤ素子等の周辺材料が例示される。光電子集積回路（ＯＥＩＣ）周辺の基板材料、ファイバー材料、素子の周辺材料も例示される。 In the field of optical components, for example, fiber materials, lenses, waveguides, and peripheral materials of elements around optical switches in an optical communication system are exemplified. An optical fiber material around the optical connector is also exemplified. As for the optical passive component and the optical circuit component, peripheral materials such as a lens, a waveguide, and an LED element are exemplified. Examples of substrate materials, fiber materials, and device peripheral materials around an optoelectronic integrated circuit (OEIC) are also given.
光ファイバー分野では、例えば、装飾ディスプレイ用照明・ライトガイドなど、工業用途のセンサー類、表示・標識類など、また通信インフラ用および家庭内のデジタル機器接続用の光ファイバー等が例示される。 In the field of optical fibers, for example, sensors for industrial use such as illumination / light guides for decorative displays, displays / signs, etc., and optical fibers for communication infrastructure and for connecting home digital devices are exemplified.
半導体集積回路周辺材料では、例えば、ＬＳＩ又は超ＬＳＩ材料用のマイクロリソグラフィー用のレジスト材料が挙げられる。 Examples of the semiconductor integrated circuit peripheral material include resist materials for microlithography for LSI or VLSI material.
次世代の光・電子機能有機材料としては、例えば、次世代ＤＶＤ、有機ＥＬ素子周辺材料、有機フォトリフラクティブ素子、光−光変換デバイスである光増幅素子、光演算素子、有機太陽電池周辺の基板材料、ファイバー材料等が例示される。 Next-generation optical / electronic functional organic materials include, for example, next-generation DVDs, organic EL element peripheral materials, organic photorefractive elements, light-to-light conversion devices, optical amplification elements, optical arithmetic elements, and substrates around organic solar cells. Examples include materials and fiber materials.
［表示装置］
一般的な表示装置とは、コンピュータ、テレビ、携帯電話、タッチパネル、ワードプロセッサー等の機器から出力される、静止画、動画、文字等の画像信号を表示する装置であり、一般的には、ディスプレイ、モニター等と呼ばれている。
[Display device]
A general display device is a device that displays image signals such as still images, moving images, and characters that are output from devices such as computers, televisions, mobile phones, touch panels, and word processors. It is called a monitor.
本実施の形態の表示装置は、上記実施形態に係る積層体を備える表示装置であれば、特に限定されるものではないが、具体的には、例えば、液晶表示装置（ＬＣＤ）、プラズマディスプレイパネル（ＰＤＰ）、有機ＥＬディスプレイ（ＥＬＤ）、無機ＥＬディスプレイや陰極管表示装置（ＣＲＴ）、表面電界ディスプレイ（ＳＥＤ）等の表示装置が好ましく、中でも、ＬＣＤとＥＬＤが特に好ましい。 The display device of the present embodiment is not particularly limited as long as it is a display device including the laminate according to the above-described embodiment. Specifically, for example, a liquid crystal display device (LCD), a plasma display panel, for example. Display devices such as (PDP), organic EL display (ELD), inorganic EL display, cathode ray tube display (CRT), and surface electric field display (SED) are preferred, with LCD and ELD being particularly preferred.
ＬＣＤの種類は、特に限定されるものではないが、透過型、反射型又は半透過型が好ましく用いられる。 The type of LCD is not particularly limited, but a transmissive type, a reflective type or a transflective type is preferably used.
［液晶表示装置（ＬＣＤ）］
本実施形態の液晶表示装置（ＬＣＤ）の形態は、特に限定されるものではないが、液晶セル及びその両側に配置された２枚の偏光板を有し、液晶セルは、２枚の電極基板の間に液晶を担持しているものが好ましい。更に光学異方性層が、液晶セルと一方の偏光板との間に１枚配置されるか、又は液晶セルと双方の偏光板との間に２枚配置されていても良い。
[Liquid Crystal Display (LCD)]
Although the form of the liquid crystal display device (LCD) of this embodiment is not particularly limited, it has a liquid crystal cell and two polarizing plates arranged on both sides thereof, and the liquid crystal cell has two electrode substrates. It is preferable to carry a liquid crystal between them. Further, one optically anisotropic layer may be disposed between the liquid crystal cell and one polarizing plate, or two optically anisotropic layers may be disposed between the liquid crystal cell and both polarizing plates.
本実施形態において、偏光板が反射防止機能付偏光板の場合は、液晶セルが、ツイステットネマチックモード（ＴＮモード）、スーパーツイステットネマチックモード（ＳＴＮモード）、バーティカルアライメントモード（ＶＡモード）、インプレインスイッチングモード（ＩＰＳモード）、オプティカリーコンペンセイテットベンドセルモード（ＯＣＢモード）であることが好ましい。 In this embodiment, when the polarizing plate is a polarizing plate with an antireflection function, the liquid crystal cell has a twisted nematic mode (TN mode), a super twisted nematic mode (STN mode), a vertical alignment mode (VA mode), In-switching mode (IPS mode) and optically compensated bend cell mode (OCB mode) are preferred.
（ＴＮモード）
ＴＮモードの液晶セルでは、電圧無印加時に棒状液晶性分子が実質的に水平配向し、さらに６０〜１２０゜にねじれ配向している。ＴＮモードの液晶セルは、カラーＴＦＴ液晶表示装置として最も多く利用されている。
(TN mode)
In the TN mode liquid crystal cell, rod-like liquid crystal molecules are substantially horizontally aligned when no voltage is applied, and are twisted and aligned at 60 to 120 °. TN mode liquid crystal cells are most frequently used as color TFT liquid crystal display devices.
（ＳＴＮモード）
ＳＴＮモードの液晶セルでは、電圧無印加時において液晶分子の並びのねじれ角が、１８０〜２７０°にねじれ配向し、これにより印加電圧の僅かな差によって大きな配向変化を実現できる。
(STN mode)
In the STN mode liquid crystal cell, the twist angle of the alignment of liquid crystal molecules is twisted to 180 to 270 ° when no voltage is applied, whereby a large change in orientation can be realized by a slight difference in applied voltage.
（ＶＡモード）
ＶＡモードの液晶セルでは、電圧無印加時に棒状液晶性分子が実質的に垂直に配向している。ＶＡモードの液晶セルには、次の（１）〜（４）が含まれる。
（１）棒状液晶性分子を電圧無印加時に実質的に垂直に配向させ、電圧印加時に実質的に水平に配向させる狭義のＶＡモードの液晶セル
（２）視野角拡大のため、ＶＡモードをマルチドメイン化した（ＭＶＡモードの）液晶セル
（３）棒状液晶性分子を電圧無印加時に実質的に垂直配向させ、電圧印加時にねじれマルチドメイン配向させるモード（ｎ−ＡＳＭモード）の液晶セル
（４）ＳＵＲＶＡＩＶＡＬモードの液晶セル
(VA mode)
In a VA mode liquid crystal cell, rod-like liquid crystalline molecules are aligned substantially vertically when no voltage is applied. The VA mode liquid crystal cell includes the following (1) to (4).
(1) A narrowly-defined VA mode liquid crystal cell in which rod-like liquid crystalline molecules are aligned substantially vertically when no voltage is applied and horizontally when a voltage is applied. (2) In order to expand the viewing angle, multiple VA modes are used. Domained liquid crystal cell (MVA mode) (3) Mode (n-ASM mode) liquid crystal cell in which rod-like liquid crystalline molecules are substantially vertically aligned when no voltage is applied and twisted multi-domain alignment is applied when a voltage is applied (4) SURVAVAL mode liquid crystal cell
（ＩＰＳモード）
ＩＰＳモードの液晶セルは、ネマチック液晶に横電界をかけてスイッチングする方式である。
(IPS mode)
The IPS mode liquid crystal cell is a type in which nematic liquid crystal is switched by applying a lateral electric field.
（ＯＣＢモード）
ＯＣＢモードの液晶セルは、棒状液晶性分子を液晶セルの上部と下部とで実質的に逆の方向に（対称的に）配向させるベンド配向モードの液晶セルである。棒状液晶性分子が液晶セルの上部と下部とで対称的に配向しているため、ベンド配向モードの液晶セルは、自己光学補償機能を有する。
(OCB mode)
The OCB mode liquid crystal cell is a bend alignment mode liquid crystal cell in which rod-like liquid crystalline molecules are aligned in a substantially opposite direction (symmetrically) between an upper portion and a lower portion of the liquid crystal cell. Since the rod-like liquid crystal molecules are symmetrically aligned at the upper and lower portions of the liquid crystal cell, the bend alignment mode liquid crystal cell has a self-optical compensation function.
図９は、液晶セルの一例を示す模式断面図である。液晶セル８０は、第一の透明電極８２を一方面上に有する第一の電極基板８１と、第二の透明電極８６を一方面上に有し、第一の電極基板８１と対向して配置された第二の電極基板８７と、第一の透明電極８２と第二の透明電極８６との間に担持された液晶８３と、液晶８３を担持するためのシール材８４と、を備えている。 FIG. 9 is a schematic cross-sectional view showing an example of a liquid crystal cell. The liquid crystal cell 80 has a first electrode substrate 81 having a first transparent electrode 82 on one surface and a second transparent electrode 86 on one surface, and is disposed to face the first electrode substrate 81. A second electrode substrate 87, a liquid crystal 83 carried between the first transparent electrode 82 and the second transparent electrode 86, and a sealing material 84 for carrying the liquid crystal 83. .
図１０は、液晶表示素子の一例を示す模式断面図である。液晶表示素子９０は、液晶セル９２と、液晶セル９２の一方面上に設けられた上側偏光板９８と、液晶セル９２の他方面上に位相差フィルム９１を介して設けられた下側偏光板３０と、を備えている。ここで下側偏光板３０は、図４に示す偏光板３０と同様のものであってよい。また、上側偏光板４０は、液晶セル９２に接する側から、偏光子９３、粘着層９４、偏光板保護フィルム９５、ハードコート層９６及び有機無機複合膜９７を備える。 FIG. 10 is a schematic cross-sectional view showing an example of a liquid crystal display element. The liquid crystal display element 90 includes a liquid crystal cell 92, an upper polarizing plate 98 provided on one surface of the liquid crystal cell 92, and a lower polarizing plate provided on the other surface of the liquid crystal cell 92 via a retardation film 91. 30. Here, the lower polarizing plate 30 may be the same as the polarizing plate 30 shown in FIG. The upper polarizing plate 40 includes a polarizer 93, an adhesive layer 94, a polarizing plate protective film 95, a hard coat layer 96, and an organic-inorganic composite film 97 from the side in contact with the liquid crystal cell 92.
図３は、液晶ディスプレイ（ＬＣＤ）の構成の一例を示す模式断面図である。液晶ディスプレイ１０は、プリズムシート１４の一方面上に拡散シート１３、導光板１２及び反射フィルム１１が順に設けられ、他方面上に偏光板１５、粘着層１６、位相差フィルム１７、粘着層１８、ガラス基板１９、液晶層２０、カラーフィルター２１、ガラス基板２２、粘着層２３、位相差フィルム２４、粘着層２５及び偏光板２６がこの順で積層された構成を有する。 FIG. 3 is a schematic cross-sectional view showing an example of the configuration of a liquid crystal display (LCD). The liquid crystal display 10 includes a diffusion sheet 13, a light guide plate 12, and a reflective film 11 provided in this order on one surface of a prism sheet 14, and a polarizing plate 15, an adhesive layer 16, a retardation film 17, an adhesive layer 18 on the other surface. The glass substrate 19, the liquid crystal layer 20, the color filter 21, the glass substrate 22, the adhesive layer 23, the retardation film 24, the adhesive layer 25, and the polarizing plate 26 are laminated in this order.
［プラズマディスプレイパネル（ＰＤＰ）］
本実施の形態のプラズマディスプレイパネル（ＰＤＰ）は、一般に、ガス、ガラス基板、電極、電極リード材料、厚膜印刷材料、蛍光体により構成される。ガラス基板は、前面ガラス基板と後面ガラス基板の２枚である。２枚のガラス基板には電極と絶縁層を形成する。後面ガラス基板には、さらに蛍光体層を形成する。２枚のガラス基板を組み立てて、その間にガスを封入する。
[Plasma Display Panel (PDP)]
The plasma display panel (PDP) of this embodiment is generally composed of a gas, a glass substrate, an electrode, an electrode lead material, a thick film printing material, and a phosphor. Two glass substrates are a front glass substrate and a rear glass substrate. An electrode and an insulating layer are formed on the two glass substrates. A phosphor layer is further formed on the rear glass substrate. Two glass substrates are assembled and gas is sealed between them.
またＰＤＰの前面に、前面板を配置することがある。前面板はプラズマディスプレイパネルを保護するために充分な強度を備えていることが好ましい。前面板は、プラズマディスプレイパネルと隙間を置いて使用することもできるし、プラズマディスプレイ本体に直貼りして使用することもできる。 Further, a front plate may be disposed on the front surface of the PDP. The front plate preferably has sufficient strength to protect the plasma display panel. The front plate can be used with a gap from the plasma display panel, or can be used by directly pasting the front plate to the plasma display body.
ＰＤＰのような表示装置では、光学フィルターとして、本発明の積層体を反射防止フィルムとして、ディスプレイ表面に直接貼り付けることができる。また、ディスプレイの前に前面板が設けられている場合は、前面板の表側（外側）又は裏側（ディスプレイ側）に光学フィルターとしての反射防止フィルムを貼り付けることもできる。 In a display device such as a PDP, the laminate of the present invention can be directly attached to the display surface as an optical filter as an antireflection film. When a front plate is provided in front of the display, an antireflection film as an optical filter can be attached to the front side (outside) or the back side (display side) of the front plate.
［タッチパネル］
本発明の積層体は、タッチパネルに組み込むことも可能である。タッチパネルとは、ＬＣＤや有機ＥＬディスプレイ等の表示装置と、タッチパッドのような位置入力装置を組み合わせた電子部品であり、画面上の表示を押すことで機器を操作する入力装置である。
[Touch panel]
The laminate of the present invention can be incorporated into a touch panel. A touch panel is an electronic component that combines a display device such as an LCD or an organic EL display and a position input device such as a touch pad, and is an input device that operates a device by pressing a display on a screen.
タッチパネルは、銀行など金融機関ＡＴＭ、自動販売機、携帯電話、携帯情報端末 （ＰＤＡ）、デジタルオーディオプレーヤー、携帯ゲーム機、コピー機、ファックス、カーナビなど、デジタル情報機器等に組み込まれ、使用することが可能である。 The touch panel is incorporated into digital information devices such as banking institutions such as ATMs, vending machines, mobile phones, personal digital assistants (PDAs), digital audio players, portable game machines, copiers, fax machines, car navigation systems, etc. Is possible.
タッチパネルを、構造で分類すると、外付型と内蔵型に大別され、内蔵型は更に、インセル型とオンセル型に分類される。また方式で分類すると、抵抗膜式、静電容量式、光学式、超音波式等に分類される。 When the touch panel is classified by structure, it is roughly classified into an external type and a built-in type, and the built-in type is further classified into an in-cell type and an on-cell type. Further, when classified by the method, it is classified into a resistance film type, a capacitance type, an optical type, an ultrasonic type and the like.
上記構造と方式の組み合わせから、アウトセル型静電容量式、カバーガラス一体型静電容量式、インセル型静電容量式、オンセル型静電容量式、シングルタッチ抵抗膜式、シングルタッチ抵抗膜式等が市場に流通している。 From the combination of the above structure and method, out-cell capacitance type, cover glass integrated capacitance type, in-cell type capacitance type, on-cell type capacitance type, single touch resistive film type, single touch resistive film type, etc. Is in circulation in the market.
［有機ＥＬディスプレイ（ＥＬＤ）］
本発明の積層体を反射防止フィルムとして使用する場合は、有機ＥＬ素子等の保護フィルムとして用いることができる。
[Organic EL display (ELD)]
When using the laminated body of this invention as an antireflection film, it can be used as protective films, such as an organic EL element.
ＥＬＤは、各画素ごとに、発光素子が構成されている。その発光素子は、例えば、金属等の陰電極／電子注入層／電子輸送層／発光層／正孔輸送層／正孔注入層／ＩＴＯ等の陽電極、そしてガラス基板や透明な光学フィルムからなる。 In the ELD, a light emitting element is configured for each pixel. The light emitting element is made of, for example, a negative electrode such as metal / electron injection layer / electron transport layer / light emission layer / hole transport layer / hole injection layer / positive electrode such as ITO, and a glass substrate or a transparent optical film. .
上記のようなサンドイッチ構造はヘテロ構造と呼ばれ、電子と正孔をそれぞれ別の層に閉じ込めることによって効率的な反応を起こすことができる。各層の材料にはジアミン、アントラセン、金属錯体などの有機物が使用されている。 The sandwich structure as described above is called a heterostructure, and an efficient reaction can be caused by confining electrons and holes in separate layers. Organic materials such as diamine, anthracene, and metal complexes are used for the material of each layer.
電極間の各層の厚さは数ｎｍから数百ｎｍであり、一般的には、全体で１μｍ以下の厚さである。また基板もフレキシブルなプラスチック等を利用することにより、フレキシブルディスプレイの製造も可能である。 The thickness of each layer between the electrodes is several nm to several hundred nm, and generally has a thickness of 1 μm or less as a whole. In addition, a flexible display can be manufactured by using a flexible plastic or the like for the substrate.
ＥＬＤは、駆動方式によりアクティブマトリクス型（ＡＭ−ＯＬＥＤ、アモレッド）とパッシブマトリクス型（ＰＭ−ＯＬＥＤ）に 大別され、カラー化方式では、３色方式、色変換方式、カラーフィルター方式の３種に分類される。 ELDs are roughly divided into active matrix type (AM-OLED, Amo Red) and passive matrix type (PM-OLED) according to the driving method, and there are three types of colorization methods: three-color method, color conversion method, and color filter method. being classified.
［光学素子］
本実施形態に係る光学素子とは、光の回折現象を利用した機能素子を指す。本実施形態の光学素子は、この要件を満たすものであれば特に限定されるものではないが、例えば、光学レンズ、光学プリズム、光学フィルター等に適している。
[Optical element]
The optical element according to the present embodiment refers to a functional element that utilizes a light diffraction phenomenon. The optical element of the present embodiment is not particularly limited as long as it satisfies this requirement. For example, the optical element is suitable for an optical lens, an optical prism, an optical filter, and the like.
上記光学レンズ及び光学プリズムとしては、例えば、顕微鏡、内視鏡、望遠鏡等のレンズ、レーザービームプリンターのｆθレンズ、センサー用レンズ等のレーザー走査系レンズ、カメラ及び携帯電話等の撮像系レンズ、ファインダー系のプリズムレンズ、眼鏡レンズ等の全光線透過型レンズ、及び、光ディスクのピックアップレンズが挙げられる。 Examples of the optical lens and optical prism include a lens such as a microscope, an endoscope, and a telescope, an fθ lens of a laser beam printer, a laser scanning system lens such as a sensor lens, an imaging system lens such as a camera and a mobile phone, and a finder. System light transmission lens such as a prism lens and eyeglass lens, and an optical disk pickup lens.
図１１は、プリズムシート内蔵積層フィルムの一例を示す模式断面図である。プリズムシート内蔵積層フィルム１００は、ＰＥＴフィルム１０１の一方面上に設けられたプリズム１０２上に、粘着層１０３、有機無機複合膜１０４、粘着層１０５及び反射型偏光板１０６がこの順に積層された構成を有する。 FIG. 11 is a schematic cross-sectional view showing an example of a prism sheet built-in laminated film. The prism sheet built-in laminated film 100 has a configuration in which an adhesive layer 103, an organic-inorganic composite film 104, an adhesive layer 105, and a reflective polarizing plate 106 are laminated in this order on a prism 102 provided on one surface of a PET film 101. Have
図１２は、プリズムシート代替低屈折率層付ＰＥＴフィルム内蔵積層フィルムの一例を示す模式断面図である。積層フィルム１１０は、プリズムシートの代替品として使用し得るものであり、低屈折率層として有機無機複合膜１１２を備えている。より具体的には、積層フィルム１１０は、ＰＥＴフィルム１１１、有機無機複合膜１１２、粘着層１１３及び反射型偏光板１１４がこの順で積層した構成を有する。 FIG. 12 is a schematic cross-sectional view showing an example of a laminated film containing a PET film with a low refractive index layer instead of a prism sheet. The laminated film 110 can be used as a substitute for the prism sheet, and includes an organic-inorganic composite film 112 as a low refractive index layer. More specifically, the laminated film 110 has a configuration in which a PET film 111, an organic-inorganic composite film 112, an adhesive layer 113, and a reflective polarizing plate 114 are laminated in this order.
図１３は、プリズムシート内蔵積層フィルムの入射光を示す図である。光学装置１２０には、ＰＥＴフィルム１０１の一方面上に設けられたプリズム１０２上に、粘着層１０３、有機無機複合膜１０４、粘着層１０５及び反射型偏光板１０６がこの順に積層された構成を有するプリズムシート内蔵積層フィルムと、ＰＥＴフィルム１０１の他方面側に設置された冷陰極ランプ１２１を備える光源（ＣＣＦＬ）１２２と、を備える。光源１２２から照射された光は、ＰＥＴフィルム１０１の他方面側から（プリズム１０２が設けられた面と反対側の面に）入射する。 FIG. 13 is a diagram showing incident light of the prism sheet built-in laminated film. The optical device 120 has a configuration in which an adhesive layer 103, an organic-inorganic composite film 104, an adhesive layer 105, and a reflective polarizing plate 106 are stacked in this order on a prism 102 provided on one surface of a PET film 101. And a light source (CCFL) 122 including a cold cathode lamp 121 installed on the other surface side of the PET film 101. The light emitted from the light source 122 enters from the other surface side of the PET film 101 (on the surface opposite to the surface on which the prism 102 is provided).
［照明器具］
本実施の形態に係る照明器具とは、各種光源を利用して、何らかの目的をもって特定の場所を明るくする器具であれば、特に限定されるものではない。照明器具は、例えば、白熱電球、蛍光灯、ランプ、ＬＥＤ、又は有機ＥＬを有する。
[lighting equipment]
The lighting fixture according to the present embodiment is not particularly limited as long as it is a fixture that brightens a specific place for some purpose using various light sources. The lighting fixture includes, for example, an incandescent bulb, a fluorescent lamp, a lamp, an LED, or an organic EL.
本実施形態に係る積層体は、有機無機複合膜及び接続層において、本発明の趣旨を逸脱しない範囲で、各種有機樹脂、着色剤、レベリング剤、滑剤、界面活性剤、シリコーン系化合物、反応性希釈剤、非反応性希釈剤、酸化防止剤、光安定剤等を含有していてもよい。また、一般に樹脂用の添加剤（可塑剤、難燃剤、安定剤、帯電防止剤、耐衝撃強化剤、発泡剤、抗菌・防カビ剤、フィラー、防曇剤、架橋剤等）として供される物質を、配合しても差し支えない。また、さらに他の物質が含まれていてもよい。他の物質としては、溶剤、油脂、油脂加工品、天然樹脂、合成樹脂、顔料、染料、色素、剥離剤、防腐剤、接着剤、脱臭剤、凝集剤、洗浄剤、脱臭剤、ｐＨ調整剤、感光材料、インク、電極、めっき液、触媒、樹脂改質剤、可塑剤、柔軟剤、農薬、殺虫剤、殺菌剤、医薬品原料、乳化剤・界面活性剤、防錆剤、金属化合物、フィラー、化粧品・医薬品原料、脱水剤、乾燥剤、不凍液、吸着剤、着色剤、ゴム、発泡剤、着色剤、研磨剤、離型剤、凝集剤、消泡剤、硬化剤、還元剤、フラックス剤、皮膜処理剤、鋳物原料、鉱物、酸・アルカリ、ショット剤、酸化防止剤、表面被覆剤、添加剤、酸化剤、燃料、漂白剤、発光素子、香料、コンクリート、繊維（カーボンファイバー、アラミド繊維、ガラス繊維等）、ガラス、金属、賦形剤、崩壊剤、結合剤、流動化剤、ゲル化剤、安定剤、保存剤、緩衝剤、懸濁化剤、粘稠剤等が挙げられる。 In the organic-inorganic composite film and the connection layer, the laminate according to the present embodiment includes various organic resins, colorants, leveling agents, lubricants, surfactants, silicone compounds, reactivity, and the like without departing from the spirit of the present invention. Diluents, non-reactive diluents, antioxidants, light stabilizers and the like may be included. Also commonly used as additives for plastics (plasticizers, flame retardants, stabilizers, antistatic agents, impact resistance enhancers, foaming agents, antibacterial / antifungal agents, fillers, antifogging agents, crosslinking agents, etc.) Substances can be blended. Further, other substances may be included. Other substances include solvents, fats and oils, processed oils, natural resins, synthetic resins, pigments, dyes, dyes, release agents, preservatives, adhesives, deodorizers, flocculants, cleaning agents, deodorizers, and pH adjusters. , Photosensitive material, ink, electrode, plating solution, catalyst, resin modifier, plasticizer, softener, agrochemical, insecticide, fungicide, pharmaceutical raw material, emulsifier / surfactant, rust inhibitor, metal compound, filler, Cosmetics / pharmaceutical raw materials, dehydrating agent, desiccant, antifreeze, adsorbent, colorant, rubber, foaming agent, colorant, abrasive, mold release agent, flocculant, antifoaming agent, curing agent, reducing agent, flux agent, Film treatment agent, casting raw material, mineral, acid / alkali, shot agent, antioxidant, surface coating agent, additive, oxidant, fuel, bleach, light emitting element, fragrance, concrete, fiber (carbon fiber, aramid fiber, Glass fiber), glass, metal, excipient, disintegrant Binding agents, flow agents, gelling agents, stabilizers, preservatives, buffering agents, suspending agents, thickeners, and the like.
有機樹脂は、特に限定されるものではなく、例えば、エポキシ樹脂、フェノール樹脂、メラミン樹脂、ユリア樹脂、不飽和ポリエステル樹脂、ポリウレタン樹脂、ジアリルフタレート樹脂、シリコン樹脂、アルキド樹脂、アクリル樹脂、ポリエステル樹脂、ポリプロピレン樹脂、ポリスチレン樹脂、ＡＳ樹脂、ＡＢＳ樹脂、ポリカーボネート樹脂、ポリ乳酸樹脂、ポリアセタール樹脂、ポリイミド樹脂、ポリフェニレンサルファイド樹脂、ポリエーテルエーテルケトン樹脂、ポリアミドイミド樹脂、ポリアミド樹脂、ポリフタルアミド樹脂、ポリサルフォン樹脂、ポリアリレート樹脂、ポリエーテルサルフォン樹脂、ポリエーテルイミド樹脂、ポリフェニルサルフォン樹脂、変性ポリフェニレンエーテル樹脂、塩化ビニル樹脂、合成ゴム、ポリエチレンテレフタレート樹脂、液晶ポリマー、ポリテトラフロロエチレン、ポリクロロトリフルオロエチレン樹脂、ポリビニリデンフルオライド樹脂、及びビニルエーテル共重合体が挙げられる。 The organic resin is not particularly limited, for example, epoxy resin, phenol resin, melamine resin, urea resin, unsaturated polyester resin, polyurethane resin, diallyl phthalate resin, silicon resin, alkyd resin, acrylic resin, polyester resin, Polypropylene resin, polystyrene resin, AS resin, ABS resin, polycarbonate resin, polylactic acid resin, polyacetal resin, polyimide resin, polyphenylene sulfide resin, polyetheretherketone resin, polyamideimide resin, polyamide resin, polyphthalamide resin, polysulfone resin, Polyarylate resin, polyethersulfone resin, polyetherimide resin, polyphenylsulfone resin, modified polyphenylene ether resin, vinyl chloride resin, synthetic rubber, Ethylene terephthalate resins, liquid crystal polymers, polytetrafluoroethylene, polychlorotrifluoroethylene resins, polyvinylidene fluoride resins, and vinyl ether copolymers.
着色剤は、着色を目的に使用される物質であれば特に限定されず、例えば、フタロシアニン、アゾ、ジスアゾ、キナクリドン、アントラキノン、フラバントロン、ペリノン、ペリレン、ジオキサジン、縮合アゾ、アゾメチン系の各種有機系色素、酸化チタン、硫酸鉛、クロムエロー、ジンクエロー、クロムバーミリオン、弁殻、コバルト紫、紺青、群青、カーボンブラック、クロムグリーン、酸化クロム、コバルトグリーン等の無機顔料等が挙げられる。これらの着色剤は単独でも、複数を組み合わせて使用してもよい。 The colorant is not particularly limited as long as it is a substance used for the purpose of coloring. For example, phthalocyanine, azo, disazo, quinacridone, anthraquinone, flavantron, perinone, perylene, dioxazine, condensed azo, azomethine-based various organic systems Examples thereof include inorganic pigments such as pigments, titanium oxide, lead sulfate, chromium yellow, zinc yellow, chromium vermilion, valve shells, cobalt purple, bitumen, ultramarine, carbon black, chromium green, chromium oxide, cobalt green and the like. These colorants may be used alone or in combination.
レベリング剤は、特に限定されず、例えば、シリコーン系レベリング剤（ジメチルポリシロキサン、有機変性ポリシロキサン等）、アクリレート系レベリング剤（エチルアクリレート、ブチルアクリレート、２−エチルヘキシルアクリレート、フッ素変性アクリレート、シリコーン変性アクリレート等）、エポキシ化大豆脂肪酸、エポキシ化アビエチルアルコール、水添ひまし油、チタン系カップリング剤等が挙げられる。これらのレベリング剤は単独でも、複数を組み合わせて使用してもよい。 The leveling agent is not particularly limited, and examples thereof include silicone leveling agents (dimethylpolysiloxane, organically modified polysiloxane, etc.), acrylate leveling agents (ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, fluorine-modified acrylate, silicone-modified acrylate). Etc.), epoxidized soybean fatty acid, epoxidized abiethyl alcohol, hydrogenated castor oil, titanium coupling agent and the like. These leveling agents may be used alone or in combination.
滑剤は、特に限定されず、パラフィンワックス、マイクロワックス、ポリエチレンワックス等の炭化水素系滑剤、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、アラキジン酸、ベヘン酸等の高級脂肪酸系滑剤、ステアリルアミド、パルミチルアミド、オレイルアミド、メチレンビスステアロアミド、エチレンビスステアロアミド等の高級脂肪酸アミド系滑剤、硬化ひまし油、ブチルステアレート、エチレングリコールモノステアレート、ペンタエリスリトール（モノ−，ジ−，トリ−，又はテトラ−）ステアレート等の高級脂肪酸エステル系滑剤、セチルアルコール、ステアリルアルコール、ポリエチレングリコール、ポリグリセロール等のアルコール系滑剤、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、アラキジン酸、ベヘン酸、リシノール酸、ナフテン酸等のマグネシウム、カルシウム、カドミウム、バリウム、亜鉛、鉛等の金属塩である金属石鹸類、カルナウバロウ、カンデリラロウ、ミツロウ、モンタンロウ等の天然ワックス類等が挙げられる。これらの滑剤は単独でも、複数を組み合わせて使用してもよい。 The lubricant is not particularly limited, and hydrocarbon lubricants such as paraffin wax, micro wax, polyethylene wax, higher fatty acid lubricants such as lauric acid, myristic acid, palmitic acid, stearic acid, arachidic acid, and behenic acid, stearylamide, Higher fatty acid amide lubricants such as palmitylamide, oleylamide, methylene bisstearamide, ethylene bisstearamide, hydrogenated castor oil, butyl stearate, ethylene glycol monostearate, pentaerythritol (mono-, di-, tri- , Or higher fatty acid ester lubricants such as tetra-stearate, alcohol lubricants such as cetyl alcohol, stearyl alcohol, polyethylene glycol, polyglycerol, lauric acid, myristic acid, palmitic acid, stearic acid, arachi Metal soaps that are metal salts such as magnesium, calcium, cadmium, barium, zinc, lead such as acid, behenic acid, ricinoleic acid, and naphthenic acid, and natural waxes such as carnauba wax, candelilla wax, beeswax, and montan wax . These lubricants may be used alone or in combination.
界面活性剤は、その分子中に溶媒に対して親和性を持たない疎水基と、溶媒に対して親和性を持つ親媒基（通常は親水基）を持つ、両親媒性物質を指す。また、その種類は特に限定されるものではなく、例えば、シリコーン系界面活性剤、フッ素系界面活性剤等が挙げられる。界面活性剤は単独でも、複数を組み合わせて使用してもよい。 The surfactant refers to an amphiphilic substance having a hydrophobic group having no affinity for the solvent in the molecule and an amphiphilic group (usually a hydrophilic group) having an affinity for the solvent. Moreover, the kind is not specifically limited, For example, a silicone type surfactant, a fluorine type surfactant, etc. are mentioned. Surfactants may be used alone or in combination.
シリコーン系化合物は、特に限定されず、例えば、シリコーン樹脂、シリコーン縮合物、シリコーン部分縮合物、シリコーンオイル、シランカップリング剤、シリコーンオイル、ポリシロキサン等が挙げられ、その両末端、片末端、あるいは側鎖に有機基を導入して変性したものも含まれる。その変性の方法も特に限定されず、例えば、アミノ変性、エポキシ変性、脂環式エポキシ変性、カルビノール変性、メタクリル変性、ポリエーテル変性、メルカプト変性、カルボキシル変性、フェノール変性、シラノール変性、ポリエーテル変性、ポリエーテル・メトキシ変性、ジオール変性等が挙げられる。 The silicone-based compound is not particularly limited, and examples thereof include a silicone resin, a silicone condensate, a silicone partial condensate, a silicone oil, a silane coupling agent, a silicone oil, a polysiloxane, and the like. Those modified by introducing an organic group into the side chain are also included. The modification method is not particularly limited. For example, amino modification, epoxy modification, alicyclic epoxy modification, carbinol modification, methacryl modification, polyether modification, mercapto modification, carboxyl modification, phenol modification, silanol modification, polyether modification. , Polyether / methoxy modification, diol modification and the like.
反応性希釈剤は、特に限定されず、例えば、アルキルグリシジルエーテル、アルキルフェノールのモノグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、１、６−ヘキサンジオールジグリシジルエーテル、アルカン酸グリシジルエステル、エチレングリコールジグリシジルエーテル、プロピレングリコールジグリシジルエーテル等が挙げられ、非反応性希釈剤としては、特に限定されず、例えば、ベンジルアルコール、ブチルジグリコール、プロピレングリコールモノメチルエーテル等の高沸点溶剤等が挙げられる。 The reactive diluent is not particularly limited. For example, alkyl glycidyl ether, monoglycidyl ether of alkylphenol, neopentyl glycol diglycidyl ether, 1,6-hexanediol diglycidyl ether, alkanoic acid glycidyl ester, ethylene glycol diglycidyl ether , Propylene glycol diglycidyl ether and the like, and the non-reactive diluent is not particularly limited, and examples thereof include high-boiling solvents such as benzyl alcohol, butyl diglycol and propylene glycol monomethyl ether.
酸化防止剤は、特に限定されず、例えば、トリフェニルホスフェート、フェニルイソデシルホスファイトなどの有機リン系酸化防止剤、ジステアリル−３，３’−チオジプロピネート等の有機イオウ系酸化防止剤、２，６−ジ−ｔｅｒｔ−ブチル−ｐ−クレゾール等のフェノール系酸化防止剤等が挙げられる。 Antioxidant is not particularly limited, for example, organic phosphorus antioxidants such as triphenyl phosphate, phenylisodecyl phosphite, organic sulfur antioxidants such as distearyl-3,3′-thiodipropinate, And phenolic antioxidants such as 2,6-di-tert-butyl-p-cresol.
光安定剤は、特に限定されず、例えば、ベンゾトリアゾール系、ベンゾフェノン系、サリシレート系、シアノアクリルレート系、ニッケル系、トリアジン系等の紫外線吸収剤や、ヒンダードアミン系光安定剤等が挙げられる。 The light stabilizer is not particularly limited, and examples thereof include ultraviolet absorbers such as benzotriazole, benzophenone, salicylate, cyanoacrylate, nickel, and triazine, hindered amine light stabilizers, and the like.
本実施形態に係る積層体の用途は、光学用途に限定されるものではない。例えば、電子材料（碍子類、交流変圧器、開閉機器等の注型及び回路ユニット、各種部品のパッケージ、ＩＣ・ＬＥＤ・半導体等の封止材、発電器、モーター等の回転機コイル、巻線含浸、プリント配線基板、絶縁ボード、中型碍子類、コイル類、コネクター、ターミナル、各種ケース類、電気部品類等）等として用いられ得る。 The use of the laminate according to the present embodiment is not limited to optical use. For example, electronic materials (such as insulators, AC transformers, switchgears and circuit units, package of various parts, IC / LED / semiconductor sealing materials, generators, motors and other rotating machine coils, windings, etc. Impregnation, printed wiring board, insulation board, medium-sized insulators, coils, connectors, terminals, various cases, electrical components, etc.).
以上、本発明の好適な実施形態について説明したが、本発明は上記実施形態に限定されるものではない。 The preferred embodiment of the present invention has been described above, but the present invention is not limited to the above embodiment.
以下に本実施形態をより具体的に説明した実施例を例示する。ただし、本発明はその要旨を超えない限りにおいて以下の実施例に限定されるものではない。 Examples of the present embodiment will be described below more specifically. However, the present invention is not limited to the following examples as long as the gist thereof is not exceeded.
実施例及び比較例における物性の評価は以下の手順で行った。 Evaluation of physical properties in Examples and Comparative Examples was performed according to the following procedure.
＜無機化合物粒子のＨＲ−ＳＴＥＭ撮影＞
（１）０．１ｇの有機無機複合体と、９．９ｇのクロロホルム（和光純薬工業株式会社製）をサンプル瓶にはかりとり、そこに回転子を入れた。内容物をスターラーで３０分間攪拌した後、３０分間超音波処理を施して、サンプル溶液を得た。有機無機複合体がクロロホルムに分散しにくい場合は、適宜、良分散性の溶媒を選択し、クロロホルムの代わりに用いた。
（２）上記サンプル溶液を、グリッド（応研商事株式会社製、「ＳＴＥＭ１００Ｃｕグリッド」）に滴下し、風乾させて、有機無機複合体の膜（有機無機複合膜）を形成させた。
（３）グリッド上の有機無機複合体を、ＨＲ−ＳＴＥＭの透過モードで観察し、撮影を行った。粒子の大きさや形状に応じ、任意の測定倍率を選択した。
<HR-STEM imaging of inorganic compound particles>
(1) 0.1 g of an organic-inorganic composite and 9.9 g of chloroform (manufactured by Wako Pure Chemical Industries, Ltd.) were weighed in a sample bottle, and a rotor was put therein. The contents were stirred with a stirrer for 30 minutes and then subjected to ultrasonic treatment for 30 minutes to obtain a sample solution. When the organic-inorganic composite was difficult to disperse in chloroform, a solvent with good dispersibility was appropriately selected and used instead of chloroform.
(2) The sample solution was dropped on a grid (“STEM100Cu grid” manufactured by Oken Shoji Co., Ltd.) and air-dried to form an organic-inorganic composite film (organic-inorganic composite film).
(3) The organic-inorganic composite on the grid was observed in HR-STEM transmission mode and photographed. An arbitrary measurement magnification was selected according to the size and shape of the particles.
＜無機化合物粒子の円形度＞
（４）上記（１）〜（３）と同様の方法で撮影されたＨＲ−ＳＴＥＭ像を、上記画像解析ソフトによって処理し、無機化合物粒子（粒子の外径）の「円相当径」と「周囲長」を算出した。算出された円相当径及び周囲長に基づき、下記式に従って、粒子２００個各々の円形度を求めた。円形度が０．５以上である場合を「Ａ」、円形度が０．５未満の場合を「Ｂ」と判定した。
円形度＝（円相当径から求めた円周長）／（周囲長） ・・・（１０）
ここで、（円相当径から求めた円周長）＝（円相当径）×πである。
（５）２００個の粒子の円形度のうち、上位５％及び下位５％の数値を除去し、残り９０％の平均値を求め、その値を無機化合物粒子の円形度とした。
<Circularity of inorganic compound particles>
(4) The HR-STEM image photographed by the same method as in the above (1) to (3) is processed by the image analysis software, and the “equivalent circle diameter” and “ The “perimeter” was calculated. Based on the calculated equivalent circle diameter and circumference, the circularity of each of the 200 particles was determined according to the following formula. The case where the circularity was 0.5 or more was determined as “A”, and the case where the circularity was less than 0.5 was determined as “B”.
Circularity = (circumference length obtained from equivalent circle diameter) / (peripheral length) (10)
Here, (circumferential length obtained from equivalent circle diameter) = (equivalent circle diameter) × π.
(5) Of the circularity of 200 particles, the numerical values of the upper 5% and lower 5% were removed, the average value of the remaining 90% was determined, and the value was taken as the circularity of the inorganic compound particles.
＜無機化合物粒子のＬ／Ｄ＞
（６）上記（１）〜（３）と同様の方法で撮影されたＨＲ−ＳＴＥＭ像を、上記画像解析ソフトによって処理し、粒子２００個各々の外径の、「最大長」及び「最小幅」を算出した。図１は、各粒子の最大長及び最小幅の算出方法を示す模式図である。図１に示されるように、「最大長」とは、ＨＲ−ＳＴＥＭ像における粒子の周上の任意の２点間の距離の最大値を指し、「最小幅」とは、粒子が最大長を示す方向に対して垂直な方向における粒子の幅を指す。
（７）求められた最大長Ｌ及び最小幅Ｄを下記式に代入して、粒子２００個各々のＬ／Ｄを求めた。
Ｌ／Ｄ＝（最大長）／（最小幅） ・・・（１１）
（８）２００個の粒子のＬ／Ｄのうち、上位５％及び下位５％の数値を除去し、残り９０％の平均値を求め、その値を無機化合物粒子のＬ／Ｄとした。
<L / D of inorganic compound particles>
(6) The HR-STEM image photographed by the same method as in the above (1) to (3) is processed by the image analysis software, and the “maximum length” and “minimum width” of the outer diameter of each of the 200 particles. Was calculated. FIG. 1 is a schematic diagram showing a method for calculating the maximum length and the minimum width of each particle. As shown in FIG. 1, “maximum length” refers to the maximum value of the distance between any two points on the circumference of the particle in the HR-STEM image, and “minimum width” refers to the maximum length of the particle. The width of the particle in the direction perpendicular to the direction shown.
(7) The obtained maximum length L and minimum width D were substituted into the following formula to determine L / D for each of 200 particles.
L / D = (maximum length) / (minimum width) (11)
(8) From the L / D of 200 particles, the numerical values of the upper 5% and lower 5% were removed, the average value of the remaining 90% was determined, and the value was taken as the L / D of the inorganic compound particles.
＜無機化合物粒子の平均粒径＞
（９）撮影されたＨＲ−ＳＴＥＭ像を、画像解析ソフト（旭化成エンジニアリング株式会社製、「Ａ像くん」）によって処理し、粒子２００個について、各々の粒子の外径の円相当径を求めた。本明細書において、「円相当径」とは、粒子の面積と等しい面積を有する円の直径を指す。
（１０）２００個の粒子の円相当径のうち、上位５％及び下位５％の数値を除去し、残り９０％の平均値を求め、その値を「無機化合物粒子の平均粒径」とした。
<Average particle size of inorganic compound particles>
(9) The photographed HR-STEM image was processed with image analysis software ("A Image-kun" manufactured by Asahi Kasei Engineering Co., Ltd.), and the equivalent circle diameter of the outer diameter of each particle was determined for 200 particles. . In this specification, “equivalent circle diameter” refers to the diameter of a circle having an area equal to the area of the particles.
(10) Of the equivalent circle diameters of 200 particles, numerical values of the upper 5% and lower 5% were removed, and the average value of the remaining 90% was determined, and the value was defined as “average particle diameter of inorganic compound particles”. .
＜中空粒子の外殻厚み＞
（１０）上記（１）〜（３）と同様の方法で撮影されたＨＲ−ＳＴＥＭ像を、上記画像解析ソフトによって処理し、中空粒子２００個について、各々の中空粒子の内径の円相当径を求めた。本明細書において、「円相当径」とは、粒子の面積と等しい面積を有する円の直径を指す。
（１１）２００個の粒子の円相当径のうち、上位５％及び下位５％の数値を除去し、残り９０％の平均値を求め、その値を「中空粒子の平均内径」とした。
（１２）上記で求めた、無機化合物粒子の平均粒径と、中空粒子の平均内径より、中空粒子の外殻厚みを以下の式に従って、算出した。
中空粒子の外殻厚み＝（無機化合物粒子の平均粒径−中空粒子の平均内径）／２ ・・・（６）
<Outer shell thickness of hollow particles>
(10) The HR-STEM image photographed by the same method as in the above (1) to (3) is processed by the image analysis software, and for 200 hollow particles, the equivalent circle diameter of the inner diameter of each hollow particle is set. Asked. In this specification, “equivalent circle diameter” refers to the diameter of a circle having an area equal to the area of the particles.
(11) From the equivalent circle diameter of 200 particles, the numerical values of the upper 5% and lower 5% were removed, the average value of the remaining 90% was determined, and the value was defined as the “average inner diameter of the hollow particles”.
(12) The outer shell thickness of the hollow particles was calculated from the average particle diameter of the inorganic compound particles obtained above and the average inner diameter of the hollow particles according to the following formula.
Outer shell thickness of hollow particles = (average particle diameter of inorganic compound particles−average inner diameter of hollow particles) / 2 (6)
＜中空粒子の空洞率＞
（１３）次いで、上記中空粒子の平均内径から、以下の式に従って、中空粒子の内腔半径ａを求めた。
中空粒子の内腔半径ａ＝中空粒子の平均内径／２ ・・・（７）
（１４）上記無機化合物粒子の平均粒径から、以下の式に従って、無機化合物粒子の半径ｂを求めた。
無機化合物粒子の半径ｂ＝無機化合物粒子の平均粒径／２ ・・・（８）
（１５）上記（１３）〜（１４）で求めた、中空粒子の内腔半径ａ、及び、無機化合物粒子の半径ｂを、以下の式に代入し、無機化合物粒子の空洞率を求めた。
空洞率（％）＝（４πａ３／３）／（４πｂ３／３）×１００ ・・・（９）
<Cavity ratio of hollow particles>
(13) Next, the lumen radius a of the hollow particles was determined from the average inner diameter of the hollow particles according to the following formula.
Hollow radius a of hollow particles a = average inner diameter of hollow particles / 2 (7)
(14) From the average particle diameter of the inorganic compound particles, the radius b of the inorganic compound particles was determined according to the following formula.
Radius b of inorganic compound particles = Average particle diameter of inorganic compound particles / 2 (8)
(15) The hollow radius a of the hollow particles and the radius b of the inorganic compound particles obtained in the above (13) to (14) were substituted into the following formula to obtain the void ratio of the inorganic compound particles.
Void content (%) = (4πa 3/ 3) / (4πb 3/3) × 100 ··· (9)
＜無機化合物粒子の屈折率＞
無機化合物粒子の屈折率は、標準屈折液（Ｃａｒｇｉｌｌ社製）を使用して、以下の方法により求めた。但し、所望の屈折率の標準屈折液が入手出来ない場合は、屈折率既知の試薬で代用した。
（１）無機化合物粒子の分散液をエバポレーターに採り、分散媒を蒸発させた。
（２）これを１２０℃の真空乾燥機で乾燥し、粉末にした。
（３）屈折率既知の標準屈折液を、２〜３滴ガラス板上に滴下し、これに上記粉末を混合した。
（４）上記（３）の操作を種々の標準屈折液で行い、混合液が透明になったときの標準屈折液の屈折率を無機化合物粒子の屈折率とした。
＜表面改質無機化合物粒子のハロゲン含有量の測定＞
表面改質無機化合物粒子のハロゲン含有量を、燃焼処理及びそれに続くイオンクロマトグラフ法により、以下の手順で求めた。
（１）サンプルを酸素気流中で、石英燃焼管を使用して燃焼させ、発生したガスを、吸収液（３％過酸化水素水）に吸収させた。
（２）吸収液を適宜希釈し、吸収液中の臭素イオンと塩素イオンの量を、イオンクロマトグラフ（Ｄａｉｏｎｅｘ社製、「ＩＣＳ−２０００」）で、測定した。
（３）測定された臭素イオン及び塩素イオンの合計量から、表面改質無機化合物の質量に対する、臭素イオン及び塩素イオンの合計量を、ハロゲン含有量として求めた。
<Refractive index of inorganic compound particles>
The refractive index of the inorganic compound particles was determined by the following method using a standard refractive liquid (manufactured by Cargill). However, when a standard refractive liquid having a desired refractive index was not available, a reagent with a known refractive index was substituted.
(1) A dispersion of inorganic compound particles was taken in an evaporator and the dispersion medium was evaporated.
(2) This was dried with a vacuum dryer at 120 ° C. to obtain powder.
(3) Two to three drops of a standard refractive liquid with a known refractive index was dropped on the glass plate, and the above powder was mixed therewith.
(4) The operation of (3) above was carried out with various standard refractive liquids, and the refractive index of the standard refractive liquid when the mixed liquid became transparent was taken as the refractive index of the inorganic compound particles.
<Measurement of halogen content of surface-modified inorganic compound particles>
The halogen content of the surface-modified inorganic compound particles was determined by the following procedure by combustion treatment and subsequent ion chromatography.
(1) The sample was burned in an oxygen stream using a quartz combustion tube, and the generated gas was absorbed in an absorbing solution (3% hydrogen peroxide solution).
(2) The absorbing solution was appropriately diluted, and the amount of bromine ion and chlorine ion in the absorbing solution was measured with an ion chromatograph (manufactured by Daionex, "ICS-2000").
(3) From the measured total amount of bromine ion and chlorine ion, the total amount of bromine ion and chlorine ion with respect to the mass of the surface-modified inorganic compound was determined as the halogen content.
＜ポリマーの比重＞
ＡＳＴＭ Ｄ７９２に準じて測定した。
<Specific gravity of polymer>
Measured according to ASTM D792.
＜ポリマーの分子量及び分子量の分散度＞
ポリマーの分子量及び分子量の分散度を、「分解法」又は「添加法」により求めた。成膜性有機無機複合体が、トルエンに対して易分散の場合は「分解法」で測定を行い、難溶性の場合は「添加法」で測定した。
<Polymer molecular weight and molecular weight dispersion>
The molecular weight of the polymer and the degree of dispersion of the molecular weight were determined by “decomposition method” or “addition method”. When the film-forming organic / inorganic composite was easily dispersed in toluene, measurement was performed by the “decomposition method”, and when it was poorly soluble, measurement was performed by the “addition method”.
［分解法］
（前処理）
無機化合物粒子に結合したポリマーの分子量測定のための前処理として、以下の手順に従って、有機無機複合体に対してふっ化水素酸処理（以下、「ＨＦ処理」という。）を施した。
（１）テフロン（登録商標）製回転子を入れたテフロン（登録商標）製、又は、任意の樹脂製容器に、２ｍＬのトルエン（和光純薬工業株式会社製）と、１５ｍｇの相間移動触媒（Ａｌｄｒｉｃｈ社製、「Ａｌｑｕａｔ３３６」）を加え、攪拌して、相間移動触媒がトルエンに溶解した溶液を得る。
（２）溶液に有機無機複合体のサンプル２００ｍｇを加え、攪拌により溶解させる。
（３）得られた溶液に、更に、２ｍＬのふっ化水素酸（和光純薬工業株式会社製、濃度：４６〜４８％）を加え、室温で２４時間攪拌して、無機化合物粒子からポリマーを分離する。
（４）上記溶液を、炭酸カルシウム（和光純薬工業株式会社製）の水溶液によって中和する。この時、相分離が困難な場合は、さらにトルエン２ｍＬを加えて遠心分離した溶液を使用してもよい。
[Decomposition method]
(Preprocessing)
As a pretreatment for measuring the molecular weight of the polymer bonded to the inorganic compound particles, the hydrofluoric acid treatment (hereinafter referred to as “HF treatment”) was performed on the organic-inorganic composite according to the following procedure.
(1) 2 mL of toluene (manufactured by Wako Pure Chemical Industries, Ltd.) and 15 mg of phase transfer catalyst (in a Teflon (registered trademark) or a resin container containing a Teflon (registered trademark) rotor Aldrich "Alquat 336") is added and stirred to obtain a solution in which the phase transfer catalyst is dissolved in toluene.
(2) A 200 mg sample of an organic-inorganic composite is added to the solution and dissolved by stirring.
(3) Further, 2 mL of hydrofluoric acid (manufactured by Wako Pure Chemical Industries, Ltd., concentration: 46 to 48%) is added to the obtained solution, and the mixture is stirred at room temperature for 24 hours to remove the polymer from the inorganic compound particles. To separate.
(4) The above solution is neutralized with an aqueous solution of calcium carbonate (Wako Pure Chemical Industries, Ltd.). At this time, if phase separation is difficult, a solution obtained by further adding 2 mL of toluene and centrifuging may be used.
（分子量測定）
上記前処理で得られたサンプル溶液について、下記の条件によりゲルパーミエーションクロマトグラフィー（ＧＰＣ）の測定を行った。測定結果から、ポリメタクリル酸メチルスタンダード（創和科学株式会社製）を用いて作成した検量線に基づいて、メインピークのポリメタクリル酸メチル換算の数平均分子量（Ｍｎ）及び質量平均分子量（Ｍｗ）を求めた。
・装置：東ソー株式会社製、「ＨＬＣ−８２２０ＧＰＣ」
・検出器：ＲＩ検出器
・移動相：テトラヒドロフラン
・流量：０．３５ｍＬ／分
・カラム：東ソー株式会社製の「ＴＳＫｇｅｌ ＧＭＨＸＬ」を２本連結したものを用いた。
・カラム温度：４０℃
(Molecular weight measurement)
About the sample solution obtained by the said pre-processing, the measurement of the gel permeation chromatography (GPC) was performed on condition of the following. From the measurement results, the number average molecular weight (Mn) and the mass average molecular weight (Mw) in terms of polymethyl methacrylate of the main peak are based on a calibration curve created using polymethyl methacrylate standard (manufactured by Sowa Kagaku Co., Ltd.). Asked.
・ Equipment: “HLC-8220GPC” manufactured by Tosoh Corporation
-Detector: RI detector-Mobile phase: Tetrahydrofuran-Flow rate: 0.35 mL / min-Column: Two "TSKgel GMHXL" manufactured by Tosoh Corporation were connected.
-Column temperature: 40 ° C
（分子量分布）
ポリメタクリル酸メチル換算の数平均分子量（Ｍｎ）及び質量平均分子量（Ｍｗ）を以下の式に代入して、ポリマーの分子量分布を求めた。分子量分布が２．３１以下である場合を「Ａ」、分子量分布の分散度が２．３１を超える場合を「Ｂ」と判定した。
分子量分布＝Ｍｗ／Ｍｎ ・・・（１２）
(Molecular weight distribution)
The number average molecular weight (Mn) and mass average molecular weight (Mw) in terms of polymethyl methacrylate were substituted into the following formula to determine the molecular weight distribution of the polymer. The case where the molecular weight distribution was 2.31 or less was determined as “A”, and the case where the degree of dispersion of the molecular weight distribution exceeded 2.31 was determined as “B”.
Molecular weight distribution = Mw / Mn (12)
［添加法］
以下の方法で前処理を行い、「分子量測定」と「分子量分布」は、上述の「分解法」と同様の方法で求めた。
（前処理）
以下の手順に従って、無機化合物粒子に結合したポリマーの「分子量」と「分子量分布」を求めた。分子量測定用サンプルとして、実施例とは別に、重合開始剤を添加した状態で有機無機複合体を合成し、重合開始剤の添加により副生するポリマーを測定し、これを無機化合物粒子に結合したポリマーの「分子量」と「分子量分布」とみなした。
[Addition method]
Pretreatment was performed by the following method, and “molecular weight measurement” and “molecular weight distribution” were obtained by the same method as the above-mentioned “decomposition method”.
(Preprocessing)
The “molecular weight” and “molecular weight distribution” of the polymer bonded to the inorganic compound particles were determined according to the following procedure. As a sample for measuring molecular weight, separately from the examples, an organic-inorganic composite was synthesized with a polymerization initiator added, a polymer produced as a by-product by adding a polymerization initiator was measured, and this was bound to inorganic compound particles. The “molecular weight” and “molecular weight distribution” of the polymer were considered.
（１）分子量測定用サンプルの合成
（１−１）実施例と同様の方法で、有機無機複合体の原料を含む溶液を準備した。
（１−２）上記溶液に、モノマー：重合開始剤＝１００：（０．０１〜０．２５）（ｍｏｌ比）となるように、重合開始剤を加えた。重合開始剤は、実施例の重合液中の臭素含有量に対し、約１０〜２０％の臭素含有量となるように配合した。
・重合開始剤：２−ブロモイソ酪酸エチル（ＥＢＩＢ）：Ａｌｄｒｉｃｈ社製
（１−３）上記溶液に触媒溶液を加え、実施例と同様の方法で、測定用サンプル（有機無機複合体と副生ポリマーの混合物）を重合した。
（１−４）フラスコを氷浴に浸して速やかに冷却してから、ヘキサンに投入して攪拌し、静置した。その後、上澄み液を廃棄した。
（１−５）残った沈殿物に、ヘキサンを再び加えて静置し、上澄み液を廃棄した。この操作を更に８回繰り返し、残った沈殿物を、実施例と同様の方法で乾燥した。
（２）上記（１）で得られた、分子量測定用サンプル１ｇに、１０ｍＬの溶媒（例えば、ＭＩＢＫ）を加え、２４時間攪拌した。
（３）上記溶液に適量のＴＨＦを加え、更に１時間攪拌した溶液を、遠心分離した。
（４）上述の「分解法」と同様の方法で、遠心分離後の上澄み液を測定し、「分子量」と「分子量の分散度」を求めた。
(1) Synthesis of Sample for Measuring Molecular Weight (1-1) A solution containing the raw material for the organic-inorganic composite was prepared in the same manner as in the examples.
(1-2) A polymerization initiator was added to the above solution so that monomer: polymerization initiator = 100: (0.01 to 0.25) (mol ratio). The polymerization initiator was blended so as to have a bromine content of about 10 to 20% with respect to the bromine content in the polymerization liquid of the examples.
Polymerization initiator: ethyl 2-bromoisobutyrate (EBIB): manufactured by Aldrich (1-3) A catalyst solution was added to the above solution, and a measurement sample (organic-inorganic composite and by-product polymer) was prepared in the same manner as in the examples. Of the mixture) was polymerized.
(1-4) The flask was immersed in an ice bath and quickly cooled, then poured into hexane, stirred and allowed to stand. Thereafter, the supernatant was discarded.
(1-5) Hexane was added again to the remaining precipitate and allowed to stand, and the supernatant was discarded. This operation was further repeated 8 times, and the remaining precipitate was dried in the same manner as in the example.
(2) To 1 g of the molecular weight measurement sample obtained in (1) above, 10 mL of a solvent (for example, MIBK) was added and stirred for 24 hours.
(3) A suitable amount of THF was added to the above solution, and the solution stirred for 1 hour was centrifuged.
(4) The supernatant liquid after centrifugation was measured by the same method as the “decomposition method” described above, and “molecular weight” and “dispersion degree of molecular weight” were determined.
＜有機無機複合体の「無機化合物粒子に結合しているポリマー」の量＞
（１）サンプル瓶に１０ｇの有機無機複合体をはかりとり、ＭＩＢＫを加えて１００ｍＬとした後、回転子を入れて、内容物をスターラーで２４時間攪拌した。
（２）別のサンプル瓶に、１０ｍＬの上記溶液をはかりとり、ＴＨＦを加えて１００ｍＬに希釈後、回転子を入れて、内容物をスターラーで、更に２４時間攪拌した。
（３）上記溶液を遠沈管に移し、遠心分離機で、６６００ｒｐｍで３０分間処理した。
（４）遠心分離後の上澄み液について、下記の条件によりゲルパーミエーションクロマトグラフィー（ＧＰＣ）の測定を行い、有機無機複合体におけるフリーポリマーを測定した。測定結果から、ポリメタクリル酸メチルスタンダード（創和科学株式会社製）を用いて作成した検量線に基づいて、メインピークのポリメタクリル酸メチル換算の、ピークトップ分子量（Ｍｐ）を求めた。
・装置：東ソー株式会社製、「ＨＬＣ−８２２０ＧＰＣ」
・検出器：ＲＩ検出器
・移動相：テトラヒドロフラン
・流量：０．３５ｍＬ／分
・カラム：東ソー株式会社製の「ＴＳＫｇｅｌ ＧＭＨＸＬ」を２本連結したものを用いた。
・カラム温度：４０℃
（５）上記で得られた、Ｍｐ＞８００のピークを、フリーポリマーとして定量した。定量の際には、Ｍｐが最も近い「定量標準物質」を下記から選択して検量線を作成し、定量標準物質換算で、有機無機複合体中のフリーポリマーの量（質量％）を算出した。またピークが複数ある場合は、それらの合計量を求め、フリーポリマーの量（質量％）とした。
（５−１）定量標準物質：ポリメタクリル酸メチル（創和科学株式会社製）
・ポリメタクリル酸メチル「ＰＭＭＡ８５０（Ｍｐ＝８６０）」
・ポリメタクリル酸メチル「ＰＭＭＡ２Ｋ（Ｍｐ＝２，０００）」
・ポリメタクリル酸メチル「ＰＭＭＡ７Ｋ（Ｍｐ＝７，５００）」
・ポリメタクリル酸メチル「ＰＭＭＡ１１Ｋ（Ｍｐ＝１１，８００）」
・ポリメタクリル酸メチル「ＰＭＭＡ２１Ｋ（Ｍｐ＝２０，８５０）」
・ポリメタクリル酸メチル「ＰＭＭＡ３０Ｋ（Ｍｐ＝３３，５００）」
・ポリメタクリル酸メチル「ＰＭＭＡ４５Ｋ（Ｍｐ＝４６，３００）」
・ポリメタクリル酸メチル「ＰＭＭＡ８５Ｋ（Ｍｐ＝８７，８００）」
・ポリメタクリル酸メチル「ＰＭＭＡ１１０Ｋ（Ｍｐ＝１０７，０００）」
・ポリメタクリル酸メチル「ＰＭＭＡ１３５Ｋ（Ｍｐ＝１３０，０００）」
・ポリメタクリル酸メチル「ＰＭＭＡ１３５Ｋ（Ｍｐ＝１３０，０００）」
・ポリメタクリル酸メチル「ＰＭＭＡ１９０Ｋ（Ｍｐ＝１８５，０００）」
・ポリメタクリル酸メチル「ＰＭＭＡ２２５Ｋ（Ｍｐ＝２４０，０００）」
・ポリメタクリル酸メチル「ＰＭＭＡ３２０Ｋ（Ｍｐ＝３２２，０００）」
・ポリメタクリル酸メチル「ＰＭＭＡ６８０Ｋ（Ｍｐ＝６７０，０００）」
<Amount of “polymer bonded to inorganic compound particles” of organic-inorganic composite>
(1) 10 g of an organic-inorganic composite was weighed into a sample bottle, MIBK was added to make 100 mL, a rotor was added, and the contents were stirred with a stirrer for 24 hours.
(2) In a separate sample bottle, 10 mL of the above solution was weighed, THF was added to dilute to 100 mL, a rotor was added, and the contents were further stirred with a stirrer for 24 hours.
(3) The above solution was transferred to a centrifuge tube and treated with a centrifuge at 6600 rpm for 30 minutes.
(4) About the supernatant liquid after centrifugation, the gel permeation chromatography (GPC) was measured on condition of the following, and the free polymer in an organic inorganic composite was measured. From the measurement results, the peak top molecular weight (Mp) in terms of polymethyl methacrylate of the main peak was determined based on a calibration curve created using polymethyl methacrylate standard (manufactured by Soka Kagaku Co., Ltd.).
・ Equipment: “HLC-8220GPC” manufactured by Tosoh Corporation
-Detector: RI detector-Mobile phase: Tetrahydrofuran-Flow rate: 0.35 mL / min-Column: Two "TSKgel GMHXL" manufactured by Tosoh Corporation were connected.
-Column temperature: 40 ° C
(5) The peak of Mp> 800 obtained above was quantified as a free polymer. At the time of quantification, the “quantitative standard substance” with the closest Mp was selected from the following to create a calibration curve, and the amount (% by mass) of the free polymer in the organic-inorganic complex was calculated in terms of the quantitative standard substance. . Moreover, when there were a plurality of peaks, the total amount thereof was determined and used as the amount (% by mass) of the free polymer.
(5-1) Quantitative reference material: polymethyl methacrylate (manufactured by Soka Kagaku Co., Ltd.)
・ Polymethyl methacrylate "PMMA850 (Mp = 860)"
・ Polymethyl methacrylate "PMMA2K (Mp = 2,000)"
・ Polymethyl methacrylate "PMMA7K (Mp = 7,500)"
・ Polymethyl methacrylate "PMMA11K (Mp = 11,800)"
・ Polymethyl methacrylate "PMMA21K (Mp = 20,850)"
・ Polymethyl methacrylate "PMMA30K (Mp = 33,500)"
・ Polymethyl methacrylate "PMMA45K (Mp = 46,300)"
・ Polymethyl methacrylate "PMMA85K (Mp = 87,800)"
・ Polymethyl methacrylate "PMMA110K (Mp = 107,000)"
・ Polymethyl methacrylate "PMMA135K (Mp = 130,000)"
・ Polymethyl methacrylate "PMMA135K (Mp = 130,000)"
・ Polymethyl methacrylate "PMMA190K (Mp = 185,000)"
・ Polymethyl methacrylate "PMMA225K (Mp = 240,000)"
・ Polymethyl methacrylate "PMMA320K (Mp = 322,000)"
・ Polymethyl methacrylate "PMMA680K (Mp = 670,000)"
（６）有機無機複合体中のポリマー量（無機化合物に結合しているポリマー及びフリーポリマーの量）の測定
熱重量測定装置により、以下の条件で有機無機複合体を加熱したときの質量減量（質量％）をｎ＝３で測定し、その平均値を「有機無機複合体中のポリマー量（無機化合物に結合しているポリマー及びフリーポリマー）」とした。
・装置：株式会社島津製作所、「ＴＧＡ−５０」
・雰囲気：１％酸素含有窒素気流
・試料容器：アルミパン
・温度プログラム：２５℃スタート→２０℃／分で昇温→５００℃に到達→５００℃で１時間保持
（７）上記で得られた「フリーポリマーの量（質量％）」と、「有機無機複合体中のポリマー量（無機化合物に結合しているポリマー及びフリーポリマーの量）（質量％）」から、下記式に従って「無機化合物粒子に結合しているポリマーの量（質量％）」を算出した。
無機化合物粒子に結合しているポリマーの量（質量％）＝（Ａ−Ｂ）／Ａ×１００ ・・・（１３）
ここで、Ａ：有機無機複合体中のポリマー量（無機化合物に結合しているポリマー及びフリーポリマーの量）（質量％）、Ｂ：フリーポリマーの量（質量％）である。
(6) Measurement of amount of polymer in organic-inorganic composite (amount of polymer and free polymer bonded to inorganic compound) Mass loss when organic-inorganic composite is heated under the following conditions with a thermogravimetric measuring device ( Mass%) was measured at n = 3, and the average value was defined as “the amount of polymer in the organic-inorganic composite (polymer and free polymer bonded to the inorganic compound)”.
・ Equipment: Shimadzu Corporation, “TGA-50”
・ Atmosphere: Nitrogen stream containing 1% oxygen ・ Sample container: Aluminum pan ・ Temperature program: Start at 25 ° C. → Temperature rise at 20 ° C./min→Reach 500 ° C. → Hold at 500 ° C. for 1 hour (7) Obtained above From “the amount of free polymer (% by mass)” and “the amount of polymer in the organic-inorganic composite (the amount of polymer and free polymer bonded to the inorganic compound) (% by mass)”, “inorganic compound particles” The amount of polymer bonded to (mass%) "was calculated.
Amount of polymer bonded to inorganic compound particles (mass%) = (A−B) / A × 100 (13)
Here, A: the amount of polymer in the organic-inorganic composite (amount of polymer and free polymer bonded to the inorganic compound) (mass%), B: the amount of free polymer (mass%).
＜ポリマー中の反応性二重結合量＞
ポリマー中の反応性二重結合量は、以下の手順に従って測定した。
（１）ポリマー中の官能基として水酸基を含むモノマー（例えば、メタクリル酸２−ヒドロキシエチル）のモル量を、各々のモノマー転化率から求めた。モノマー転化率は、下記の条件でガスクロマトグラフィー（ＧＣ）により求めた。
・装置：株式会社島津製作所製、「ＧＣ−１４Ｂ」
・検出器：ＦＩＤ
・カラム温度：５０℃→２００℃（昇温速度２０℃／分）、２５０℃で保持
・ＧＣ注入口温度：２３０℃
・検出器温度：２８０℃
・キャリアガス：ヘリウム
（２）官能基として水酸基を含むモノマーと、官能基としてイソシアネート基を含むモノマー（例えば、メタクリル酸２−イソシアネートエチル）の付加反応を行ない、その生成物中に残存する官能基として水酸基を含むモノマーの水酸基量から求めた。水酸基量の測定は、下記の条件で核磁気共鳴装置（ＮＭＲ）により求めた。
・装置：ブルカー社製、「ＤＰＸ−４００」
・溶媒：Ｎ，Ｎ−ジメチルホルムアミドの重水素化体
<Reactive double bond amount in polymer>
The amount of reactive double bonds in the polymer was measured according to the following procedure.
(1) The molar amount of a monomer containing a hydroxyl group as a functional group in the polymer (for example, 2-hydroxyethyl methacrylate) was determined from each monomer conversion rate. Monomer conversion was determined by gas chromatography (GC) under the following conditions.
・ Device: “GC-14B” manufactured by Shimadzu Corporation
・ Detector: FID
Column temperature: 50 ° C. → 200 ° C. (temperature rising rate 20 ° C./min), maintained at 250 ° C. GC inlet temperature: 230 ° C.
-Detector temperature: 280 ° C
Carrier gas: a functional group remaining in the product of the addition reaction of a monomer containing a hydroxyl group as a helium (2) functional group and a monomer containing an isocyanate group as a functional group (for example, 2-isocyanatoethyl methacrylate) As the amount of hydroxyl group of the monomer containing a hydroxyl group. The amount of hydroxyl groups was determined by a nuclear magnetic resonance apparatus (NMR) under the following conditions.
・ Device: “DPX-400” manufactured by Bruker
・ Solvent: Deuterated form of N, N-dimethylformamide
＜有機無機複合体のＴｇの測定＞
示差走査熱量測定装置（ＤＳＣ）により、以下の条件で有機無機複合体のＴｇを求めた。
・装置：ＰｅｒｋｉｎＥｌｍｅｒ社製、「Ｄｉａｍｏｎｄ ＤＳＣ」
・温度プログラム：−４０℃スタート→２０分間保持→２０℃／分で昇温→２００℃
<Measurement of Tg of organic-inorganic composite>
The Tg of the organic-inorganic composite was determined under the following conditions using a differential scanning calorimeter (DSC).
・ Device: “Diamond DSC” manufactured by PerkinElmer
・ Temperature program: Start at -40 ℃ → Hold for 20 minutes → Increase temperature at 20 ℃ / minute → 200 ℃
＜有機無機複合体のハロゲン含有量の測定＞
有機無機複合体のハロゲン含有量は、前述の「表面改質無機化合物粒子のハロゲン含有量の測定」と同様の方法で求めた。
<Measurement of halogen content of organic-inorganic composite>
The halogen content of the organic-inorganic composite was determined by the same method as described above in “Measurement of halogen content of surface-modified inorganic compound particles”.
＜有機無機複合体の銅含有量の測定＞
酸分解及びそれに続くＩＣＰ発光分析法により、以下の手順で、銅含有量を求めた。
（１）サンプルを、硫酸（和光純薬工業株式会社製）、硝酸（和光純薬工業株式会社製）、フッ化水素酸（和光純薬工業株式会社製）で分解した。
（２）更に、硝酸（１＋２）で加温溶解を行った。
（３）上記溶液を希釈し、ＩＣＰ発光分析装置（株式会社島津製作所製、「ＩＣＰＳ−８１００」）で測定した。
<Measurement of copper content of organic-inorganic composite>
The copper content was determined by the following procedure by acid decomposition and subsequent ICP emission analysis.
(1) The sample was decomposed with sulfuric acid (Wako Pure Chemical Industries, Ltd.), nitric acid (Wako Pure Chemical Industries, Ltd.), and hydrofluoric acid (Wako Pure Chemical Industries, Ltd.).
(2) Further, the mixture was heated and dissolved with nitric acid (1 + 2).
(3) The solution was diluted and measured with an ICP emission spectrometer (“ICPS-8100” manufactured by Shimadzu Corporation).
＜有機無機複合体のフッ素含有量の測定＞
燃焼処理及びそれに続くイオンクロマトグラフ法により、以下の手順で、フッ素含有量を求めた。
（１）サンプルを酸素気流下で、石英燃焼管を使用して燃焼させた。このとき、サンプルは必要に応じ、溶解及び／又は希釈してから使用してもよい。
（２）燃焼により発生したガスを、氷冷した吸収液（０．２％ＮａＯＨ水溶液）に吸収させた。
（３）吸収液を適宜希釈し、吸収液中のフッ素イオンの量を、イオンクロマトグラフ（Ｄａｉｏｎｅｘ社製、「ＩＣＳ−２０００」）で、測定した。測定されたフッ素イオンの量から、有機無機複合体の質量に対するフッ素イオンの量をフッ素含有量として求めた。
<Measurement of fluorine content of organic-inorganic composite>
The fluorine content was determined by the following procedure by combustion treatment and subsequent ion chromatography.
(1) The sample was burned using a quartz combustion tube under an oxygen stream. At this time, the sample may be used after being dissolved and / or diluted as necessary.
(2) Gas generated by combustion was absorbed in an ice-cooled absorption liquid (0.2% NaOH aqueous solution).
(3) The absorbing solution was appropriately diluted, and the amount of fluorine ions in the absorbing solution was measured with an ion chromatograph (manufactured by Daionex, "ICS-2000"). From the measured amount of fluorine ions, the amount of fluorine ions relative to the mass of the organic-inorganic composite was determined as the fluorine content.
＜有機無機複合体の無機酸化物含有量の測定＞
熱重量測定装置により、以下の条件で有機無機複合体を加熱したときの質量減量を求めた。
・装置：株式会社島津製作所、「ＴＧＡ−５０」
・雰囲気：１％酸素含有窒素気流
・試料容器：アルミパン
・温度プログラム：２５℃スタート→２０℃／分で昇温→５００℃に到達→５００℃で１時間保持
測定をｎ＝３で行い、それらの平均値を有機−無機複合体の無機酸化物含有量とした。質量％及び体積％の値を下記のように算出した。
<Measurement of inorganic oxide content of organic-inorganic composite>
The mass loss when the organic-inorganic composite was heated under the following conditions was determined by a thermogravimetric apparatus.
・ Equipment: Shimadzu Corporation, “TGA-50”
・ Atmosphere: Nitrogen stream containing 1% oxygen ・ Sample container: Aluminum pan ・ Temperature program: Start at 25 ° C. → Temperature rises at 20 ° C./min→Area reaches 500 ° C. → Holds at 500 ° C. for 1 hour. The average value thereof was defined as the inorganic oxide content of the organic-inorganic composite. The mass% and volume% values were calculated as follows.
（１）質量％
測定された質量減量（質量％）を以下の式に代入し、無機酸化物の含有量（質量％）を算出した。
無機酸化物含有量（質量％）＝１００−質量減量（質量％）
(1) Mass%
The measured weight loss (mass%) was substituted into the following formula to calculate the inorganic oxide content (mass%).
Inorganic oxide content (mass%) = 100-mass loss (mass%)
（２）体積％
（２−１）ポリマーの質量と体積の算出
測定された質量減量（ｍｇ）を、ポリマーの質量（ｍｇ）と見なし、その値を下記式に代入して、ポリマーの体積（μＬ）を算出した。
ポリマーの体積（μＬ）＝｛ポリマーの質量（ｍｇ）｝／｛ポリマーの比重｝
（２−２）無機酸化物の質量と体積の算出
測定された質量減量（ｍｇ）を下記式に代入して、無機酸化物の質量（ｍｇ）を算出した。
無機酸化物の質量（ｍｇ）＝試料量（ｍｇ）−質量減量（ｍｇ）
無機酸化物の質量を下記式に代入して、無機酸化物の体積（μＬ）を算出した。
無機酸化物の体積（μＬ）＝｛無機酸化物の質量（ｍｇ）｝／｛無機酸化物の密度（ｇ／ｃｍ３）｝
（２−３）無機化合物含有量（体積％）の算出
上記のようにして得られた値を下記式に代入して、無機化合物含有量（体積％）を算出した。
(2) Volume%
(2-1) Calculation of polymer mass and volume The measured mass loss (mg) was regarded as the polymer mass (mg), and the value was substituted into the following formula to calculate the polymer volume (μL). .
Polymer volume (μL) = {mass of polymer (mg)} / {specific gravity of polymer}
(2-2) Calculation of mass and volume of inorganic oxide The measured mass loss (mg) was substituted into the following formula to calculate the mass (mg) of the inorganic oxide.
Inorganic oxide mass (mg) = sample amount (mg)-weight loss (mg)
By substituting the mass of the inorganic oxide into the following formula, the volume (μL) of the inorganic oxide was calculated.
Volume of inorganic oxide (μL) = {mass of inorganic oxide (mg)} / {density of inorganic oxide (g / cm 3)}
(2-3) Calculation of inorganic compound content (volume%) The value obtained as described above was substituted into the following formula to calculate the inorganic compound content (volume%).
＜コーティング材の作製＞
有機無機複合体に、任意の有機溶媒を加え、室温で２４時間攪拌処理を行い、有機無機複合体の溶媒分散液を調製した。更に、必要に応じて、光重合開始剤、硬化剤、硬化促進剤、架橋剤、フリーポリマー等を加えて混合し、コーティング材とした。尚、必要に応じ、超音波処理やエバポレーターによる濃縮処理を加えた。
<Production of coating material>
An arbitrary organic solvent was added to the organic-inorganic composite, and the mixture was stirred at room temperature for 24 hours to prepare a solvent dispersion of the organic-inorganic composite. Furthermore, if necessary, a photopolymerization initiator, a curing agent, a curing accelerator, a crosslinking agent, a free polymer, and the like were added and mixed to obtain a coating material. In addition, the ultrasonication and the concentration process by an evaporator were added as needed.
＜コーティング材の固形分濃度＞
以下の手順で、コーティング材の固形分濃度を求めた。
（１）秤量瓶に、コーティング材をはかりとり、内容物の質量（質量Ａ）を記録した。
（２）内容物の流動性が無くなるまで、窒素気流下で、上記秤量瓶を風乾した。
（３）上記秤量瓶を、１０５℃、真空下で、２４時間乾燥させた後、デシケータ内で室温まで冷却した。
（４）秤量瓶の質量をはかり、内容物の質量（質量Ｂ）を記録した。
（５）以下の式により、固形分を求めた。
固形分（質量％）＝（質量Ｂ）／（質量Ａ）×１００
<Solid content concentration of coating material>
The solid content concentration of the coating material was determined by the following procedure.
(1) The coating material was weighed in a weighing bottle, and the content mass (mass A) was recorded.
(2) The weighing bottle was air-dried under a nitrogen stream until the fluidity of the contents disappeared.
(3) The weighing bottle was dried at 105 ° C. under vacuum for 24 hours, and then cooled to room temperature in a desiccator.
(4) The weight of the weighing bottle was measured and the mass (mass B) of the contents was recorded.
(5) Solid content was calculated | required with the following formula | equation.
Solid content (mass%) = (mass B) / (mass A) × 100
＜有機無機複合膜（コーティング膜）の作製＞
以下の手順で、有機無機複合膜（コーティング膜）を作製した。
（１）上述のコーティング材を、適量、はかりとった。
（２）ＰＥＴフィルム又はＴＡＣフィルムの上に、（１）のコーティング材を載せ、速やかにバーコーターで塗工した。但しバーコーターは、乾燥後のコーティング膜厚が１．５〜２μｍ程度になるように、適宜選択した。
・ＰＥＴフィルム：東洋紡績株式会社製、「コスモシャイン４１００」（厚み１００μｍ、全光線透過率９０％、ヘーズ０．９％）
・ＴＡＣフィルム：富士フィルム株式会社製（厚み８０μｍ、全光線透過率９３％、ヘーズ０．７％）
（３）１０分間風乾後、８０℃の防爆型送風乾燥機で、１０分間乾燥した後、必要に応じて、光硬化又は熱硬化を行い、「有機無機複合膜（コーティング膜）」を得た。
・光硬化：窒素下で、乾燥後のコーティング膜に有機無機複合膜側から高圧水銀灯により６００ｍＪ／ｃｍ２の光量でＵＶ光を照射した。
・熱硬化：１００℃の防爆型送風乾燥機で、５時間加熱した。
<Production of organic-inorganic composite film (coating film)>
An organic-inorganic composite film (coating film) was produced by the following procedure.
(1) An appropriate amount of the above-described coating material was weighed.
(2) The coating material of (1) was placed on a PET film or a TAC film, and quickly coated with a bar coater. However, the bar coater was appropriately selected so that the coating film thickness after drying was about 1.5 to 2 μm.
PET film: “Cosmo Shine 4100” manufactured by Toyobo Co., Ltd. (thickness 100 μm, total light transmittance 90%, haze 0.9%)
TAC film: manufactured by Fuji Film Co., Ltd. (thickness 80 μm, total light transmittance 93%, haze 0.7%)
(3) After air drying for 10 minutes, after drying for 10 minutes with an explosion-proof blower at 80 ° C., photocuring or heat curing was performed as necessary to obtain an “organic-inorganic composite film (coating film)”. .
Photocuring: Under nitrogen, the dried coating film was irradiated with UV light from the organic-inorganic composite film side with a high pressure mercury lamp at a light amount of 600 mJ / cm 2 .
Heat curing: Heated with an explosion-proof blower at 100 ° C. for 5 hours.
＜有機無機複合膜（コーティング膜）の外観＞
上記有機無機複合膜（コーティング膜）を目視により観察し、粒子の凝集が実質的に見られない場合を合格（「Ａ」）と判定し、粒子の凝集が見られた場合を「Ｂ」と判定した。
<Appearance of organic / inorganic composite film (coating film)>
The organic-inorganic composite film (coating film) is visually observed, and when the particle aggregation is not substantially observed, it is determined as pass ("A"), and when the particle aggregation is observed is "B". Judged.
＜有機無機複合膜（コーティング膜）の屈折率測定＞
屈折率測定装置を使用し、屈折率を下記条件で測定した。
・装置：Ｍｅｔｒｉｃｏｎ社製、「ＭＯＤＥＬ ２０１０ ＰＲＩＳＭ ＣＯＵＰＬＥＲ」
・モード：シングルフィルムモード
・測定波長：６３３ｎｍ
・屈折率が低く、Ｍｅｔｒｉｃｏｎ社製の装置で測定できない場合は、分光エリプソメーター（Ｊ．Ａ．Ｗｏｏｌｌａｍ社製）で測定を行った。
<Measurement of refractive index of organic / inorganic composite film (coating film)>
The refractive index was measured under the following conditions using a refractive index measuring device.
-Equipment: "METEL 2010 PRISM COUPLER" manufactured by Metricon
・ Mode: Single film mode ・ Measurement wavelength: 633 nm
When the refractive index was low and measurement was not possible using a device manufactured by Metricon, measurement was performed using a spectroscopic ellipsometer (JA Woollam).
＜有機無機複合膜（コーティング膜）の全光線透過率及びヘーズの測定＞
ヘーズメーター（日本電色工業株式会社製、「ＮＤＨ ５０００Ｗ」）を使用し、「ＪＩＳ Ｋ７１０５：プラスチックの光学的特性試験方法」に準じて、コーティング膜の、全光線透過率とヘーズを測定した。
<Measurement of total light transmittance and haze of organic / inorganic composite film (coating film)>
Using a haze meter (manufactured by Nippon Denshoku Industries Co., Ltd., “NDH 5000W”), the total light transmittance and haze of the coating film were measured according to “JIS K7105: Plastic Optical Properties Test Method”.
＜有機無機複合膜の計算屈折率＞
得られた有機無機複合膜の計算屈折率を求めるためにＭａｘｗｅｌｌ−Ｇａｒｎｅｔｔの式を用いた。ポリマーの屈折率は、有機無機複合体中のポリマーと同組成のポリマーを合成し、その屈折率を測定することにより求めた。
<Calculated refractive index of organic-inorganic composite film>
In order to obtain the calculated refractive index of the obtained organic-inorganic composite film, the Maxwell-Garnett equation was used. The refractive index of the polymer was determined by synthesizing a polymer having the same composition as the polymer in the organic-inorganic composite and measuring the refractive index.
無機化合物粒子の屈折率として、上述の＜無機化合物粒子の屈折率＞の方法により測定した屈折率の値を使用し、無機化合物粒子の体積分率として、上述の＜有機無機複合体の無機物含有量の測定＞により測定した無機化合物粒子含有量（体積％）を１００で割った値を使用した。
＜Ｍａｘｗｅｌｌ−Ｇａｒｎｅｔｔの式＞
（ｎａ ２−ｎｍ ２）／（ｎａ ２＋２ｎｍ ２）＝ｑ（ｎｐ ２−ｎｍ ２）／（ｎｐ ２＋２ｎｍ ２） ・・・（８）
但し、式（８）中、ｎａは有機無機複合膜の計算屈折率、ｎｍはポリマーの屈折率、ｎｐは無機化合物粒子の屈折率、ｑは無機化合物粒子の体積分率をそれぞれ表す。
As the refractive index of the inorganic compound particles, the value of the refractive index measured by the method of <refractive index of inorganic compound particles> described above is used. The value obtained by dividing the inorganic compound particle content (% by volume) measured by 100 by 100 was used.
<Maxwell-Garnett equation>
(N a 2 -n m 2) / (n a 2 + 2n m 2) = q (n p 2 -n m 2) / (n p 2 + 2n m 2) ··· (8)
In the formula (8), n a is calculated refractive index of the organic-inorganic composite film, n m is the refractive index of the polymer, n p is the refractive index of the inorganic compound particles, q represents the volume fraction of the inorganic compound particles, respectively .
硬化性組成物の無機化合物粒子、有機ポリマーの代表的な計算値を以下に示す。光重合開始剤は、極微量であるため、計算から除外した。
・ＭＭＡポリマー；屈折率１．４９０、比重１．１９
・ＭＭＡと反応性二重結合からなる共重合ポリマー；モル比が異なる共重合ポリマーの屈折率と比重は、下記値とＭＭＡポリマーから得られる線形近似式から求めた。
ＭＭＡと反応性二重結合のモル比が７７／２３の共重合ポリマー；屈折率１．５０８、比重１．２１
ＭＭＡと反応性二重結合のモル比が４５／５５の共重合ポリマー；屈折率１．５２９、比重１．２３
メタクリル酸エチルと反応性二重結合のモル比が６７／３３の共重合ポリマー；屈折率１．５１４、比重１．１６
アクリル酸ブチルと反応性二重結合のモル比が６０／４０の共重合ポリマー；屈折率１．５１９、比重１．２０
アクリル酸ブチルと反応性二重結合のモル比が７３／２７の共重合ポリマー；屈折率１．５１０、比重１．１９
アクリル酸エチルと反応性二重結合のモル比が４８／５２の共重合ポリマー；屈折率１．５２６、比重１．２４
メタクリル酸２、２、２−トリフルオロエチルと反応性二重結合の５５／４５モル％比の共重合ポリマー；屈折率１．５２２、比重１．３２
・２０ｎｍ球状シリカ、５０ｎｍ球状シリカ、１００ｎｍ球状シリカ、数珠状シリカ；屈折率１．４５０、比重２．２０
・４８ｎｍ中空シリカ；屈折率１．３００、比重１．７３
・６４ｎｍ中空シリカ；屈折率１．２５０、比重１．５５
Typical calculated values of the inorganic compound particles and organic polymer of the curable composition are shown below. Since the photopolymerization initiator was very small, it was excluded from the calculation.
MMA polymer; refractive index 1.490, specific gravity 1.19
-Copolymer composed of MMA and reactive double bond; The refractive index and specific gravity of copolymer having different molar ratios were determined from the following values and a linear approximation obtained from MMA polymer.
Copolymer having a molar ratio of MMA to reactive double bond of 77/23; refractive index 1.508, specific gravity 1.21
Copolymer having a molar ratio of MMA to reactive double bond of 45/55; refractive index 1.529, specific gravity 1.23
Copolymer having a molar ratio of ethyl methacrylate to reactive double bond of 67/33; refractive index 1.514, specific gravity 1.16
Copolymer having a molar ratio of butyl acrylate to reactive double bond of 60/40; refractive index 1.519, specific gravity 1.20
Copolymer having a molar ratio of butyl acrylate to reactive double bond of 73/27; refractive index 1.510, specific gravity 1.19
Copolymer with ethyl acrylate and reactive double bond molar ratio of 48/52; refractive index 1.526, specific gravity 1.24
Copolymer of 55,45 mol% ratio of 2,2,2-trifluoroethyl methacrylate and reactive double bond; refractive index 1.522, specific gravity 1.32
20 nm spherical silica, 50 nm spherical silica, 100 nm spherical silica, beaded silica; refractive index 1.450, specific gravity 2.20
48 nm hollow silica; refractive index 1.300, specific gravity 1.73
64 nm hollow silica; refractive index 1.250, specific gravity 1.55
＜有機無機複合膜の空隙率＞
空隙を有する有機無機複合膜の実測屈折率は、有機無機複合体の屈折率と体積分率との積に、空隙（空気の屈折率１．００）の屈折率と体積分率との積を加算した値と一致する。そのため、空隙率は、下記の式で計算した。
空隙率（％）＝（ｎａ−ｎｂ）／（ｎａ−１）×１００ ・・・（９）
式（９）中、ｎａは有機無機複合体の計算屈折率、ｎｂは有機無機複合膜の実測屈折率をそれぞれ表す。
<Porosity of organic-inorganic composite film>
The measured refractive index of the organic / inorganic composite film having a void is the product of the refractive index and the volume fraction of the organic / inorganic complex, and the product of the refractive index and the volume fraction of the void (air refractive index 1.00). Matches the added value. Therefore, the porosity was calculated by the following formula.
Porosity (%) = (n a −n b ) / (n a −1) × 100 (9)
Wherein (9), n a is calculated refractive index of the organic-inorganic composite, n b represents the actual refractive index of the organic-inorganic composite film, respectively.
＜有機無機複合膜の鉛筆硬度の測定＞
電動鉛筆引っかき硬度試験機（株式会社安田精機製作所製）を使用し、荷重５００ｇで、「ＪＩＳ Ｋ５６００−５−４：塗料一般試験方法−第５部：塗膜の機械的性質−第４節：引っかき硬度（鉛筆法）」に準じて、コーティング膜の、鉛筆硬度を測定した。
＜有機無機複合膜の接触角の測定＞
接触角計（協和界面科学株式会社製）を使用し、液滴法で、コーティング膜の水接触角（水に対する接触角）と、油接触角（ｎ−ヘキサデカンに対する接触角）を測定した。
<Measurement of pencil hardness of organic / inorganic composite film>
Using an electric pencil scratch hardness tester (manufactured by Yasuda Seiki Seisakusyo Co., Ltd.) and with a load of 500 g, “JIS K5600-5-4: Paint General Test Method—Part 5: Mechanical Properties of Coating Film—Section 4: The pencil hardness of the coating film was measured according to “Scratch hardness (pencil method)”.
<Measurement of contact angle of organic-inorganic composite film>
Using a contact angle meter (manufactured by Kyowa Interface Science Co., Ltd.), the water contact angle (contact angle with respect to water) and the oil contact angle (contact angle with respect to n-hexadecane) of the coating film were measured by the droplet method.
＜有機無機複合膜の最小反射率の測定＞
（１）支持体（ＴＡＣフィルム）の上に、有機無機複合体を含むコーティング材を載せ、速やかにバーコーターで塗工し、風乾した。ただしコーターは、所望の膜厚になるように、適宜選択した。
・ＴＡＣフィルム：富士フィルム株式会社製（厚み８０μｍ、全光線透過率９３％、ヘーズ０．７％）
（２）更に９０℃の防爆型送風乾燥機で２分間乾燥後、必要に応じて、ＵＶ硬化、又は、熱硬化を行い、支持体の上に低屈折率層が形成された、サンプルを得た。
分光光度計を使用し、最小反射率を、下記手順で測定した。
（３）サンプルの支持体の裏面を、紙やすりで軽く擦った後、つや消しの黒色スプレーで塗装した。
（４）下記分光光度計で、波長３８０〜７００ｎｍの範囲で、反射率を測定した。
・装置：日立製作所株式会社製、「Ｕ−３４１０」：大型試料室積分球付き
・基準：アルミ蒸着膜における反射率を１００％とした。
（６）波長４５０〜６５０ｎｍの中で、最も低い反射率を、最小反射率とした。
<Measurement of minimum reflectance of organic-inorganic composite film>
(1) A coating material containing an organic-inorganic composite was placed on a support (TAC film), quickly coated with a bar coater, and air-dried. However, the coater was appropriately selected so as to obtain a desired film thickness.
TAC film: manufactured by Fuji Film Co., Ltd. (thickness 80 μm, total light transmittance 93%, haze 0.7%)
(2) Further, after drying for 2 minutes with an explosion-proof blow dryer at 90 ° C., UV curing or heat curing is performed as necessary to obtain a sample in which a low refractive index layer is formed on the support. It was.
Using a spectrophotometer, the minimum reflectance was measured by the following procedure.
(3) The back surface of the sample support was lightly rubbed with sandpaper and then painted with a matte black spray.
(4) The reflectance was measured in the wavelength range of 380 to 700 nm with the following spectrophotometer.
-Apparatus: manufactured by Hitachi, Ltd., "U-3410": with a large sample chamber integrating sphere-Standard: The reflectance in the aluminum vapor deposition film was set to 100%.
(6) The lowest reflectance among the wavelengths of 450 to 650 nm was defined as the minimum reflectance.
＜反射防止機能付偏光板の視認性＞
以下の手順で、視認性の評価を行った。
（１）偏光板を約１０ｃｍ角で切り出し、有機無機複合膜側を上にして、図１１の液晶表示素子の偏光板（図１１の９８上側偏光板）として組み込み、液晶表示素子を作製した。
（２）ライトボックス（ハクバ写真産業株式会社製）の上に、上記液晶表示素子を載せて簡易ＬＣＤを作製した。
（３）液晶表示素子の表示を黒色として、正面からパネルを目視観察し、評価した。判定基準は以下の通り。
・Ａ：ギラつきや映り込み無し。
・Ｂ：ギラつきや映り込み有り。
<Visibility of polarizing plate with antireflection function>
The visibility was evaluated by the following procedure.
(1) A polarizing plate was cut out at a square of about 10 cm, and the liquid crystal display device was produced by incorporating the polarizing plate of the liquid crystal display device of FIG.
(2) A simple LCD was fabricated by placing the liquid crystal display element on a light box (manufactured by Hakuba Photo Industry Co., Ltd.).
(3) The display of the liquid crystal display element was black, and the panel was visually observed from the front and evaluated. Judgment criteria are as follows.
-A: No glare or reflection.
・ B: There is glare and reflection.
＜反射防止機能付偏光板のコントラスト＞
以下の手順で、偏光版のコントラストを評価した。
（１）上記、反射防止機能付偏光板の視認性に使用したサンプルを、暗室に設置した。
（２）暗表示及び明表示の輝度を各々、色彩輝度計（コニカミノルタ株式会社製）で、５度の角度で測定した。
（３）コントラストを、以下の式から算出した。
ここで、コントラスト＝（明表示の輝度／暗表示の輝度）である。
（４）上記で得られたコントラストから、比較例１のコントラストを１００％とした場合の、基準に対するコントラスト向上率を以下の式から算出した。
ここで、コントラスト向上率（％）＝（各実施例及び比較例のコントラスト）／（比較例１のコントラスト）×１００
<Contrast of polarizing plate with antireflection function>
The contrast of the polarizing plate was evaluated by the following procedure.
(1) The sample used for the visibility of the polarizing plate with an antireflection function was placed in a dark room.
(2) The brightness of dark display and bright display was measured at an angle of 5 degrees with a color luminance meter (manufactured by Konica Minolta Co., Ltd.).
(3) The contrast was calculated from the following equation.
Here, contrast = (brightness of bright display / brightness of dark display).
(4) From the contrast obtained above, the contrast improvement rate with respect to the reference when the contrast of Comparative Example 1 was set to 100% was calculated from the following equation.
Here, contrast improvement rate (%) = (contrast of each example and comparative example) / (contrast of comparative example 1) × 100
＜プリズムシート内蔵積層フィルムの輝度評価＞
以下の手順で、プリズムシート内蔵積層フィルム、及びプリズムシート代替低屈折率層付ＰＥＴフィルム内蔵積層フィルム（サンプル）を、液晶バックライトユニット積層体を模した構成で配置して、輝度測定した。液晶バックライトユニット積層体の模式図を図１４に示す。
（１）反射型偏光板がプリズムシートより、出射光側に位置するように、サンプルを配置した。
（２）配置順序としては、光源ボックス（ＣＣＦＬ）側から、厚さ２ｍｍの光拡散板（住友化学株式会社製「スミペックスＲＭ４０２」、図１４の１３２）、サンプル（図１４の１３３）、液晶セル後面偏光板（日東電工株式会社製、「ＮＰＦＳＥＧ１２２４」、図１４の１３４）を順次に重ねて積層体とした。
（３）箱型の測定枠を作製し、枠上部に積層体を積載し、下面より冷陰極管（ＣＣＦＬ）光源（外径１．８ｍｍ、長さ９１ｍｍ、電源５Ｖ、図１４の１３１）２本を点灯させ、積層体を透過する光を、ＨＩ−ＬＡＮＤ’ｓ ＲＩＳＡ ｓｙｓｔｅｍ社製の輝度計（図１４の１３５）を用いて正面輝度を測定した。
（４）比較例５の正面輝度を１００％とした場合の、基準（比較例５）に対する輝度向上率を、以下の式から求め、輝度向上率（％）として算出し、９０％以上であれば「Ａ」、９０％未満であれば「Ｂ」と評価した。
輝度向上率（％）＝（各実施例及び比較例の正面輝度）／（比較例５の正面輝度）×１００
<Luminance evaluation of prism sheet built-in laminated film>
In the following procedure, the prism sheet built-in laminated film and the prism sheet-substituted PET film built-in low refractive index layer-containing laminated film (sample) were arranged in a configuration simulating a liquid crystal backlight unit laminate, and the luminance was measured. A schematic diagram of the liquid crystal backlight unit laminate is shown in FIG.
(1) The sample was arranged so that the reflective polarizing plate was positioned on the outgoing light side from the prism sheet.
(2) As the arrangement order, from the light source box (CCFL) side, a light diffusing plate having a thickness of 2 mm (“SUMIPEX RM402” manufactured by Sumitomo Chemical Co., Ltd., 132 in FIG. 14), sample (133 in FIG. 14), liquid crystal cell A rear polarizing plate (manufactured by Nitto Denko Corporation, “NPFSEG1224”, 134 in FIG. 14) was sequentially stacked to form a laminate.
(3) A box-shaped measurement frame is prepared, a stacked body is mounted on the upper part of the frame, and a cold cathode tube (CCFL) light source (outer diameter 1.8 mm, length 91 mm, power supply 5 V, 131 in FIG. 14) 2 from the lower surface The book was turned on, and the front luminance of the light transmitted through the laminate was measured using a luminance meter (135 in FIG. 14) manufactured by HI-LAND's RISA system.
(4) When the front luminance of Comparative Example 5 is set to 100%, the luminance improvement rate with respect to the reference (Comparative Example 5) is obtained from the following formula, and is calculated as the luminance improvement rate (%). If it was less than 90%, it was evaluated as “B”.
Luminance improvement rate (%) = (Front luminance of each example and comparative example) / (Front luminance of comparative example 5) × 100
＜プリズムシート内蔵積層フィルムの弛み評価＞
アルミニウム製の枠体の各辺２箇所、合計８箇所に、５００ｍｍ×８００ｍｍの光学機能層一体化品（サンプル）をピンで固定し、８５℃の乾燥機で３０分加熱し、取り出した時のサンプルを肉眼で観察した。この際、サンプルに弛みが認められなかったものは「Ａ」、認められたものは「Ｂ」と評価した。
<Slack evaluation of prism sheet built-in laminated film>
When an optical functional layer integrated product (sample) of 500 mm × 800 mm is fixed with a pin at two places on each side of the aluminum frame, a total of eight places, heated with a dryer at 85 ° C. for 30 minutes, and taken out The sample was observed with the naked eye. At this time, the sample in which no slack was observed was evaluated as “A”, and the sample in which slack was observed was evaluated as “B”.
＜原材料＞
実施例及び比較例で使用した原材料の内容を以下の（１）〜（１３）に示す。
（１）無機化合物粒子溶液
（１−１）数珠状シリカ溶液Ａ
・商品名：日産化学工業株式会社製、「ＭＥＫ−ＳＴ−ＵＰ」
・２０質量％数珠状シリカ粒子／ＭＥＫ溶液
・空洞率：０％
・屈折率：１．４５
・球状のシリカが数珠状に連結して形成された長鎖の構造。図２に数珠状無機化合物粒子のＴＥＭ写真を示す。
（１−２）数珠状シリカ溶液Ｂ
・商品名：日産化学工業株式会社製、「ＭＩＢＫ−ＳＴ−ＵＰ」
・２０質量％数珠状シリカ粒子／ＭＩＢＫ溶液
・空洞率：０％
・屈折率：１．４５
（１−３）中空シリカ溶液Ｃ
・商品名：日揮触媒化成株式会社製、「スルーリア２３２０」
・２０質量％中空シリカ粒子／ＭＩＢＫ溶液
・平均粒径４８ｎｍ、外殻厚み８．５ｎｍ
・空洞率：２７％
・屈折率：１．３０
・Ｌ／Ｄ：１．１
<Raw materials>
The contents of the raw materials used in the examples and comparative examples are shown in the following (1) to (13).
(1) Inorganic compound particle solution (1-1) Beaded silica solution A
・ Product name: “MEK-ST-UP”, manufactured by Nissan Chemical Industries, Ltd.
・ 20% by mass beaded silica particles / MEK solution ・ Cavity: 0%
-Refractive index: 1.45
A long chain structure formed by connecting spherical silica in a rosary shape. FIG. 2 shows a TEM photograph of the beaded inorganic compound particles.
(1-2) Beaded silica solution B
・ Product name: “MIBK-ST-UP”, manufactured by Nissan Chemical Industries, Ltd.
・ 20% by mass beaded silica particles / MIBK solution ・ Cavity: 0%
-Refractive index: 1.45
(1-3) Hollow silica solution C
・ Product name: JGC Catalysts & Chemicals Co., Ltd. “Thru rear 2320”
20% by mass hollow silica particles / MIBK solution Average particle size 48 nm, outer shell thickness 8.5 nm
・ Cavity ratio: 27%
-Refractive index: 1.30
L / D: 1.1
（２）シラン化合物
（２−１）３−（２−ブロモイソブチロキシ）プロピルジメチルクロロシラン（以下、「ＢＰＳ」という。）
公知の方法（特開２００６−０６３０４２号公報等）を参考に、下記化学式（１０）で表されるＢＰＳを合成した。
（２−２）（３−（２−ブロモイソブチリル）プロピル）ジメチルエトキシシラン（以下、「ＢＩＤＳ」という。）
公知の方法（特開２００６−２５７３０８号公報）に従って、下記化学式（１１）で表されるＢＩＤＳを合成した。
（２−３）１，１，１，３，３，３−ヘキサメチルジシラザン（以下、「ＨＭＤＳ」という。）：東京化成工業株式会社製
(2) Silane compound (2-1) 3- (2-bromoisobutyroxy) propyldimethylchlorosilane (hereinafter referred to as “BPS”)
BPS represented by the following chemical formula (10) was synthesized with reference to a known method (JP 2006-063042 A).
(2-2) (3- (2-bromoisobutyryl) propyl) dimethylethoxysilane (hereinafter referred to as “BIDS”)
BIDS represented by the following chemical formula (11) was synthesized according to a known method (Japanese Patent Laid-Open No. 2006-257308).
(2-3) 1,1,1,3,3,3-hexamethyldisilazane (hereinafter referred to as “HMDS”): manufactured by Tokyo Chemical Industry Co., Ltd.
（３）重合触媒
（３−１）臭化銅（Ｉ）（ＣｕＢｒ）：和光純薬工業株式会社製
（３−２）臭化銅（ＩＩ）（ＣｕＢｒ２）：和光純薬工業株式会社製
(3) Polymerization catalyst (3-1) Copper bromide (I) (CuBr): Wako Pure Chemical Industries, Ltd. (3-2) Copper bromide (II) (CuBr 2 ): Wako Pure Chemical Industries, Ltd.
（４）配位子
（４−１）Ｎ，Ｎ，Ｎ’，Ｎ”，Ｎ”−ペンタメチルジエチレントリアミン（以下、「ＰＭＤＥＴＡ」という。）：Ａｌｄｒｉｃｈ社製
(4) Ligand (4-1) N, N, N ′, N ″, N ″ -pentamethyldiethylenetriamine (hereinafter referred to as “PMDETA”): manufactured by Aldrich
（５）モノマー
以下の（５−７）〜（５−１０）以外のモノマーは、アルミナカラムを通じて重合禁止剤を除去した後、１時間以上窒素バブリングして、脱酸素処理を行ってから使用した。アルミナカラムが使用できない場合は、蒸留等の公知の方法で、重合禁止剤を除去してもよい。
（５−１）メタクリル酸メチル（以下、「ＭＭＡ」ともいう。）：東京化成工業株式会社製
（５−２）メタクリル酸エチル（以下、「ＥＭＡ」ともいう。）：東京化成工業株式会社製
（５−３）メタクリル酸２、２、２−トリフルオロエチル（以下、「ＴＦＥＭＡ」ともいう。）：東京化成工業株式会社製
（５−４）メタクリル酸グリシジル（以下、「ＧＭＡ」ともいう。）：東京化成工業株式会社製
（５−５）メタクリル酸２−ヒドロキシエチル（以下、「ＨＥＭＡ」ともいう。）：東京化成工業株式会社製
（５−６）２−アクリロイルオキシエチルイソシアネート（以下、「ＡＯＩ」ともいう。）：昭和電工株式会社
（５−７）２−メタクリロイルオキシエチルイソシアネート（以下、「ＭＯＩ」ともいう。）：昭和電工株式会社
（５−８）アクリル酸ｎ−ブチル（以下、「ｎＢＡ」ともいう。）：東京化成工業株式会社製
（５−９）アクリル酸２−ヒドロキシエチル（以下、「ＨＥＡ」ともいう。）：東京化成工業株式会社製
（５−１０）アクリル酸（以下、「ＡＡ」ともいう。）：東京化成工業株式会社製
(5) Monomer Monomers other than the following (5-7) to (5-10) were used after removing the polymerization inhibitor through an alumina column and then bubbling with nitrogen for 1 hour or more to perform deoxygenation treatment. . When an alumina column cannot be used, the polymerization inhibitor may be removed by a known method such as distillation.
(5-1) Methyl methacrylate (hereinafter also referred to as “MMA”): manufactured by Tokyo Chemical Industry Co., Ltd. (5-2) Ethyl methacrylate (hereinafter also referred to as “EMA”): manufactured by Tokyo Chemical Industry Co., Ltd. (5-3) 2,2,2-trifluoroethyl methacrylate (hereinafter also referred to as “TFEMA”): Tokyo Chemical Industry Co., Ltd. (5-4) glycidyl methacrylate (hereinafter also referred to as “GMA”). ): Tokyo Chemical Industry Co., Ltd. (5-5) 2-hydroxyethyl methacrylate (hereinafter also referred to as “HEMA”): Tokyo Chemical Industry Co., Ltd. (5-6) 2-acryloyloxyethyl isocyanate (hereinafter referred to as “HEMA”) (Also referred to as “AOI”): Showa Denko KK (5-7) 2-methacryloyloxyethyl isocyanate (hereinafter also referred to as “MOI”): Showa Denko KK (5- ) N-butyl acrylate (hereinafter also referred to as “nBA”): Tokyo Chemical Industry Co., Ltd. (5-9) 2-hydroxyethyl acrylate (hereinafter also referred to as “HEA”): Tokyo Chemical Industry Co., Ltd. Manufactured (5-10) acrylic acid (hereinafter also referred to as “AA”): manufactured by Tokyo Chemical Industry Co., Ltd.
（６）溶剤等
（６−１）メタノール：和光純薬工業株式会社製
（６−２）メチルイソブチルケトン（以下、「ＭＩＢＫ」という。）：和光純薬工業株式会社製
（６−３）メチルエチルケトン（以下、「ＭＥＫ」という。）：和光純薬工業株式会社製
（６−４）テトラヒドロフラン（以下、「ＴＨＦ」という。）：和光純薬工業株式会社製
（６−５）ジメチルホルムアミド（以下、「ＤＭＦ」という。）：和光純薬工業株式会社製
（６−６）ｎ−メチルピロリドン（以下、「ＮＭＰ」という。）：和光純薬工業株式会社製
（６−７）ヘキサン：和光純薬工業株式会社製
（６−８）シクロヘキサノン：和光純薬工業株式会社製
（６−９）メチルセロソルブ：和光純薬工業株式会社製
（６−１０）イソプロピルアルコール（以下、「ＩＰＡ」という。）：和光純薬工業株式会社製
(6) Solvents, etc. (6-1) Methanol: Wako Pure Chemical Industries, Ltd. (6-2) Methyl isobutyl ketone (hereinafter referred to as “MIBK”): Wako Pure Chemical Industries, Ltd. (6-3) Methyl ethyl ketone (Hereinafter referred to as “MEK”): Wako Pure Chemical Industries, Ltd. (6-4) tetrahydrofuran (hereinafter referred to as “THF”): Wako Pure Chemical Industries, Ltd. (6-5) dimethylformamide (hereinafter, referred to as “THK”) (Referred to as “DMF”): Wako Pure Chemical Industries, Ltd. (6-6) n-methylpyrrolidone (hereinafter referred to as “NMP”): Wako Pure Chemical Industries, Ltd. (6-7) Hexane: Wako Pure Chemical Industries, Ltd. (6-8) cyclohexanone manufactured by Kogyo Co., Ltd .: (6-9) methyl cellosolve manufactured by Wako Pure Chemical Industries, Ltd. (6-10) isopropyl alcohol (hereinafter referred to as “IPA”) manufactured by Wako Pure Chemical Industries, Ltd. ): Manufactured by Wako Pure Chemical Industries, Ltd.
（７）メタノール−水混合溶液
（７−１）メタノール−水混合溶液−１：７７容量％のメタノールと、２３容量％のイオン交換水とを含む混合溶液
（７−２）メタノール−水混合溶液−２：８０容量％のメタノールと、２０容量％のイオン交換水とを含む混合溶液
(7) Methanol-water mixed solution (7-1) Methanol-water mixed solution-1: Mixed solution containing 77% by volume of methanol and 23% by volume of ion-exchanged water (7-2) Methanol-water mixed solution -2: Mixed solution containing 80% by volume methanol and 20% by volume ion-exchanged water
（８）重合開始剤
（８−１）２−ブロモイソ酪酸エチル（以下、「ＥＢＩＢ」ともいう。）：Ａｌｄｒｉｃｈ社製
（８−２）アゾビスイソブチロニトリル（以下、「ＡＩＢＮ」ともいう。）：和光純薬工業株式会社製
(8) Polymerization initiator (8-1) Ethyl 2-bromoisobutyrate (hereinafter also referred to as “EBIB”): (8-2) Azobisisobutyronitrile (hereinafter also referred to as “AIBN”) manufactured by Aldrich. ): Wako Pure Chemical Industries, Ltd.
（９）付加反応触媒
・ジブチル錫ジラウレート（以下、ＤＢＴＤＬと言う。）：和光純薬工業株式会社製
(9) Addition reaction catalyst / dibutyltin dilaurate (hereinafter referred to as DBTDL): Wako Pure Chemical Industries, Ltd.
（１０）重合禁止剤
・２，６−ジ−ｔｅｒｔ−ブチルフェノール：東京化成工業株式会社製
(10) Polymerization inhibitor, 2,6-di-tert-butylphenol: manufactured by Tokyo Chemical Industry Co., Ltd.
（１１）光ラジカル開始剤
（１１−１）１−ヒドロキシ−シクロヘキシル−フェニル−ケトン（イルガキュア１８４）：ＢＡＳＦ社製
（１１−２）２−メチル−１−（４−メチルチオフェニル）−２−モルフォリノプロパン−１−オン（イルガキュア９０７）：ＢＡＳＦ社製
(11) Photoradical initiator (11-1) 1-hydroxy-cyclohexyl-phenyl-ketone (Irgacure 184): (11-2) 2-methyl-1- (4-methylthiophenyl) -2-morpho manufactured by BASF Linopropan-1-one (Irgacure 907): manufactured by BASF
（１２）光酸発生剤
・ＣＰＩ−１００Ｐ（商標名）：サンアプロ株式会社製
(12) Photoacid generator CPI-100P (trade name): manufactured by San Apro Co., Ltd.
（１３）フッ素系添加剤
・ＫＹ−１２０３（商標名）：信越化学工業株式会社製
(13) Fluorine-based additive / KY-1203 (trade name): manufactured by Shin-Etsu Chemical Co., Ltd.
＜表面改質無機化合物粒子−１の合成（ＢＰＳ改質数珠状シリカ粒子Ａ１の合成）＞
以下の手順に従って、ＢＰＳ改質数珠状シリカ粒子Ａ１（ＢＰＳが表面に結合した、数珠状シリカ粒子Ａ１）を合成した。
（１）冷却管を接続し、回転子を入れた二口フラスコの内部を、窒素置換した。
（２）窒素下で、フラスコ内に８６容量％の数珠状シリカ溶液Ａを導入し、更に、７容量％のＢＰＳを導入し、攪拌を開始した。
（３）上記フラスコを８５℃のオイルバスに浸し、攪拌しながら３６時間反応を行った。
（４）反応液を室温まで冷却した後、窒素下で７容量％のＨＭＤＳを導入した。
（５）室温で２時間攪拌後、８０℃で８時間攪拌して反応を行い、反応液を室温まで冷却した。
（６）反応液を遠沈管に移し、遠心分離機（株式会社久保田製作所製、型式：７７００）を用いて、１００００ｒｐｍ、１０℃で、３０分間、遠心分離を行った。
（７）遠沈管内の上澄み液をメタノール−水混合溶液−２に投入、混合し、静置後、上澄み液を廃棄した。
（８）沈殿物に窒素を吹き込み、残留する液体を揮発させた後、少量のＴＨＦを加え、攪拌により沈殿物をＴＨＦに溶解させた。
（９）上記溶液をメタノールに投入して攪拌し、静置した後、上澄み液を廃棄した。
（１０）残った沈殿物にメタノールを加えて攪拌し、静置した後、上澄み液を廃棄した。更にこの操作を１０回繰り返した。
（１１）上記沈殿物に窒素を吹きこみながら、一晩風乾することにより、液体を揮発させ、固形物を得た。
（１２）上記固形物を、８０℃、真空下で、２４時間乾燥させて、ＢＰＳ改質２０ｎｍ球状シリカ粒子を得た。
（１３）ハロゲン含有量は、２．２質量％であった。塩素は検出されなかったため、臭素含有量をハロゲン含有量として示した。
<Synthesis of Surface Modified Inorganic Compound Particles-1 (Synthesis of BPS Modified Beaded Silica Particles A1)>
According to the following procedure, BPS modified beaded silica particles A1 (beaded silica particles A1 with BPS bonded to the surface) were synthesized.
(1) A cooling pipe was connected, and the inside of the two-necked flask containing the rotor was replaced with nitrogen.
(2) Under nitrogen, 86 vol% beaded silica solution A was introduced into the flask, and further 7 vol% BPS was introduced, and stirring was started.
(3) The flask was immersed in an 85 ° C. oil bath and reacted for 36 hours with stirring.
(4) After cooling the reaction solution to room temperature, 7 vol% HMDS was introduced under nitrogen.
(5) After stirring at room temperature for 2 hours, the reaction was carried out by stirring at 80 ° C. for 8 hours, and the reaction solution was cooled to room temperature.
(6) The reaction solution was transferred to a centrifuge tube and centrifuged at 10,000 rpm, 10 ° C. for 30 minutes using a centrifuge (manufactured by Kubota Corporation, model: 7700).
(7) The supernatant liquid in the centrifuge tube was added to and mixed with the methanol-water mixed solution-2, and after standing, the supernatant liquid was discarded.
(8) Nitrogen was blown into the precipitate to volatilize the remaining liquid, a small amount of THF was added, and the precipitate was dissolved in THF by stirring.
(9) The above solution was added to methanol, stirred and allowed to stand, and then the supernatant was discarded.
(10) Methanol was added to the remaining precipitate, stirred and allowed to stand, and then the supernatant was discarded. This operation was further repeated 10 times.
(11) Air was dried overnight while blowing nitrogen into the precipitate, thereby volatilizing the liquid and obtaining a solid.
(12) The solid was dried at 80 ° C. under vacuum for 24 hours to obtain BPS-modified 20 nm spherical silica particles.
(13) The halogen content was 2.2% by mass. Since no chlorine was detected, the bromine content is shown as the halogen content.
＜表面改質無機化合物粒子−２の合成（ＢＰＳ改質数珠状シリカ粒子Ａ２の合成）＞
配合量を以下のように変更した以外は、上述の＜表面改質無機化合物粒子−１の合成＞と同様の方法で、ＢＰＳ改質数珠状シリカ粒子Ａ２を合成した。
配合量：数珠状シリカ溶液（９２．７容量％）、ＢＰＳ（０．２容量％）、ＨＭＤＳ（７．１容量％）
ハロゲン含有量は、０．１８質量％であった。
<Synthesis of Surface Modified Inorganic Compound Particles-2 (Synthesis of BPS Modified Beaded Silica Particles A2)>
BPS modified beaded silica particles A2 were synthesized in the same manner as in <Synthesis of Surface Modified Inorganic Compound Particles-1> except that the blending amount was changed as follows.
Blending amount: beaded silica solution (92.7% by volume), BPS (0.2% by volume), HMDS (7.1% by volume)
The halogen content was 0.18% by mass.
＜表面改質無機化合物粒子−３の合成（ＢＰＳ改質５０ｎｍ中空シリカ粒子の合成）＞
中空シリカ溶液Ｃ（平均粒径４８ｎｍ）（８６容量％）、ＢＰＳ（７容量％）、ＨＭＤＳ（７容量％）に、配合量を変更し、上記表面改質無機化合物粒子−１の合成と同様の方法で、ＢＰＳ改質５０ｎｍ中空シリカ粒子（ＢＰＳが表面に結合した、５０ｎｍ中空シリカ粒子）を合成した。ＢＰＳ改質５０ｎｍ中空シリカ粒子のハロゲン含有量は、１．０質量％であった。塩素は検出されなかったため、臭素含有量をハロゲン含有量として示した。
<Synthesis of surface-modified inorganic compound particles-3 (synthesis of BPS-modified 50 nm hollow silica particles)>
Similar to the synthesis of the surface-modified inorganic compound particles-1 by changing the blending amount to hollow silica solution C (average particle size 48 nm) (86% by volume), BPS (7% by volume), and HMDS (7% by volume) In this way, BPS-modified 50 nm hollow silica particles (50 nm hollow silica particles having BPS bonded to the surface) were synthesized. The halogen content of the BPS-modified 50 nm hollow silica particles was 1.0% by mass. Since no chlorine was detected, the bromine content is shown as the halogen content.
［製造例１：数珠状ＳｉＯ２−ｇ−ｐ（ＴＦＥＭＡ−ｃｏ−ＨＥＭＡ）、熱可塑］
有機無機複合体Ａを、表１の配合に従って、以下の手順で製造した。各成分の濃度は、全成分の合計量を基準とした数値である。得られた有機無機複合体Ａの評価結果を表６に示す。
（１）回転子を入れたシュレンクフラスコに、ＣｕＢｒ及びＣｕＢｒ２を加え、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した後、少量のＭＩＢＫを窒素下で導入し、攪拌した。
（２）上記溶液に、ＰＭＤＥＴＡを加え、６０℃で攪拌したものを、触媒溶液とした。
（３）冷却管を接続し、回転子を入れた別のシュレンクフラスコに、ＢＰＳ改質５０ｎｍ中空シリカ粒子を投入した。
（４）シュレンクフラスコに冷却管を接続し、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した。
（５）フラスコに、窒素下で残りの溶媒（ＭＩＢＫ）を導入して攪拌後、超音波洗浄機で１０分間処理した後、更にモノマー（ＴＦＥＭＡ及びＨＥＭＡ）を導入し、６０℃のオイルバスに浸し、攪拌した。
（６）更に、上記で調製した触媒溶液を、窒素下で導入後、反応液を２０分間攪拌し、重合反応を行った。
（７）フラスコを氷浴に浸して速やかに冷却してから、メタノール（メタノールのみで固形分が析出しにくい場合は、ヘキサンを使用しても良い。）に投入して攪拌し、沈殿物が沈みにくい場合は、遠心分離で分離して、静置した。
（８）静置後、上澄み液を廃棄した後、残った沈殿物に、メタノールを再び加えて静置し、上澄み液を廃棄した。この操作を更に８回繰り返した。
（９）残った沈殿物に窒素を吹きこみながら、一晩風乾することにより、液体を揮発させ、固形物を得た。
（１０）上記固形物を、真空下、８０℃で２４時間乾燥させて、有機無機複合体Ａを得た。
[Production Example 1: Beaded SiO 2 -gp (TFEMA-co-HEMA), thermoplastic]
The organic-inorganic composite A was produced according to the following procedure according to the formulation shown in Table 1. The concentration of each component is a numerical value based on the total amount of all components. The evaluation results of the obtained organic / inorganic composite A are shown in Table 6.
(1) to the Schlenk flask containing a rotor, added CuBr and CuBr 2, and three times to purged with nitrogen inside the flask from the vacuum treatment, and the inner atmosphere of the flask was deoxygenated, a small amount of MIBK nitrogen Introduced below and stirred.
(2) A catalyst solution was prepared by adding PMDETA to the above solution and stirring at 60 ° C.
(3) BPS-modified 50 nm hollow silica particles were charged into another Schlenk flask with a condenser connected and a rotor.
(4) A cooling tube was connected to the Schlenk flask, and the inside of the flask was subjected to vacuum treatment and then replaced with nitrogen three times to deoxygenate the inside of the flask.
(5) The remaining solvent (MIBK) was introduced into the flask under nitrogen and stirred, then treated with an ultrasonic cleaner for 10 minutes, and then monomers (TFEMA and HEMA) were further introduced into an oil bath at 60 ° C. Immerse and stir.
(6) Further, after introducing the catalyst solution prepared above under nitrogen, the reaction solution was stirred for 20 minutes to carry out a polymerization reaction.
(7) Immerse the flask in an ice bath and quickly cool it, then add it to methanol (in the case where it is difficult to precipitate solids only with methanol, hexane may be used) and stir. When it was difficult to sink, it was separated by centrifugation and allowed to stand.
(8) After standing, the supernatant was discarded, and then methanol was added again to the remaining precipitate and left standing, and the supernatant was discarded. This operation was further repeated 8 times.
(9) Air was dried overnight while blowing nitrogen into the remaining precipitate, thereby volatilizing the liquid and obtaining a solid.
(10) The solid was dried at 80 ° C. for 24 hours under vacuum to obtain an organic-inorganic composite A.
（１１）有機無機複合体ＡのＴｇを上述の方法で測定したところ、８２℃であった。
（１２）有機無機複合体Ａのハロゲン含有量を、上述の方法で測定したところ、０．５質量％であった。塩素は検出されなかったため、臭素含有量をハロゲン含有量として示した。
（１３）有機無機複合体Ａのフッ素含有量を、上述の方法で測定したところ、２０質量％であった。
（１４）有機無機複合体Ａを構成するポリマーの数平均分子量（Ｍｎ）及び質量平均分子量（Ｍｗ）を上述の方法で測定したところ、Ｍｎ＝１２，９００、Ｍｗ＝２１，９００、Ｍｗ／Ｍｎ＝１．７０（≦２．３）であり、鎖長が揃ったポリマー鎖が無機化合物粒子に結合していることがわかった。
（１５）有機無機複合体Ａのフリーポリマー量を測定したところ、フリーポリマーは３質量％であった。
（１６）有機無機複合体Ａの無機化合物粒子含有量を上述の方法で測定したところ、無機化合物粒子含有量は、５２質量％及び４６体積％であった。
（１７）固形分が約１０質量％となるように、有機無機複合体Ａに、ＭＥＫとＭＩＢＫを５：５（容積比）で混合した溶媒を添加し、上述の方法でコーティング材を得た。
（１８）上記コーティング材を使用し、上述の方法で、ＰＥＴフィルムに、塗工、乾燥し、有機無機複合膜（コーティング膜）を得た。得られた膜の外観を目視で確認したところ、無機化合物粒子の凝集は見られず、透明性を維持していた。
（１９）膜の全光線透過率とヘーズを、上述の方法で測定したところ、全光線透過率は９１％、ヘーズは２．０％であった。
（２０）上述の方法で有機無機複合膜（コーティング膜）の屈折率を測定したところ１．３３であり、理論屈折率（１．３７）と比較して、顕著に低い値を示した。
（２１）上述の方法で、有機無機複合膜の空隙率を求めたところ、更に屈折率の値から求めた空隙率は９％であった。このことから、屈折率の制御ができることが判明した。
（２２）上述のコーティング材を使用して、ＰＥＴフィルムの代わりに、ＴＡＣフィルムを使用して、上述と同様の方法で、コーティング膜を作製し、評価した結果、ＰＥＴフィルムと同様、良好な結果が得られた。
(11) The Tg of the organic-inorganic composite A was measured by the above method and found to be 82 ° C.
(12) The halogen content of the organic-inorganic composite A was measured by the method described above, and it was 0.5% by mass. Since no chlorine was detected, the bromine content is shown as the halogen content.
(13) The fluorine content of the organic-inorganic composite A was measured by the method described above, and was 20% by mass.
(14) When the number average molecular weight (Mn) and the mass average molecular weight (Mw) of the polymer constituting the organic-inorganic composite A were measured by the above-described methods, Mn = 12,900, Mw = 21,900, Mw / Mn = 1.70 (≦ 2.3), and it was found that polymer chains having a uniform chain length were bonded to the inorganic compound particles.
(15) When the amount of the free polymer of the organic-inorganic composite A was measured, the free polymer was 3% by mass.
(16) When the inorganic compound particle content of the organic-inorganic composite A was measured by the method described above, the inorganic compound particle content was 52% by mass and 46% by volume.
(17) A solvent in which MEK and MIBK were mixed at a 5: 5 (volume ratio) was added to the organic-inorganic composite A so that the solid content was about 10% by mass, and a coating material was obtained by the method described above. .
(18) The coating material was used, and the PET film was coated and dried by the above-described method to obtain an organic-inorganic composite film (coating film). When the appearance of the obtained film was visually confirmed, no aggregation of the inorganic compound particles was observed, and the transparency was maintained.
(19) When the total light transmittance and haze of the film were measured by the above-described method, the total light transmittance was 91% and the haze was 2.0%.
(20) When the refractive index of the organic-inorganic composite film (coating film) was measured by the method described above, it was 1.33, which was significantly lower than the theoretical refractive index (1.37).
(21) When the porosity of the organic-inorganic composite film was determined by the above method, the porosity determined from the refractive index value was 9%. From this, it was found that the refractive index can be controlled.
(22) Using the above-described coating material, using a TAC film instead of a PET film, and producing and evaluating a coating film by the same method as described above, results are as good as a PET film. was gotten.
［製造例２：数珠状ＳｉＯ２−ｇ−ｐＧＭＡ、光カチオン硬化］
有機無機複合体Ｂを、表１の配合に従って、以下の方法で製造し、評価した。得られた有機無機複合体Ｂの評価結果を表４に示す。
（１）回転子を入れたシュレンクフラスコに、ＣｕＢｒ及びＣｕＢｒ２を加え、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した後、少量のＭＥＫを窒素下で導入し、溶液を攪拌した。
（２）上記溶液に、ＰＭＤＥＴＡを加え、５０℃で攪拌したものを、触媒溶液とした。
（３）冷却管を接続し、回転子を入れた別のシュレンクフラスコに、ＢＰＳ改質数珠状シリカ粒子Ａ１を投入した。
（４）シュレンクフラスコに冷却管を接続し、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した。
（５）フラスコに、窒素下で残りのＭＥＫ溶媒を導入し、超音波洗浄機で１０分間処理した後、ＧＭＡモノマーを導入し、５０℃のオイスバスに浸し、攪拌した。
（６）更に、上記で調製した触媒溶液を、窒素下で導入後、反応液を７時間攪拌し、重合反応を行った。
（７）フラスコを氷浴に浸して速やかに冷却してから、ヘキサンに投入して攪拌し、沈殿物が沈みにくい場合は、遠心分離で分離して、静置した。
（８）静置後、上澄み液を廃棄した後、残った沈殿物に、ヘキサンを再び加えて静置し、上澄み液を廃棄した。この操作を更に２回繰り返した。
（９）残った沈殿物に窒素を吹きこみながら、一晩風乾することにより、液体を揮発させ、有機無機複合体を得た。
[Production Example 2: Beaded SiO 2 -g-pGMA, photocationic curing]
The organic-inorganic composite B was produced and evaluated by the following method according to the formulation in Table 1. Table 4 shows the evaluation results of the obtained organic-inorganic composite B.
(1) The operation of adding CuBr and CuBr 2 to a Schlenk flask containing a rotor, evacuating the inside of the flask and then substituting with nitrogen was repeated three times to deoxygenate the flask, and then a small amount of MEK was added to nitrogen. Introduced below and stirred the solution.
(2) A catalyst solution was prepared by adding PMDETA to the above solution and stirring at 50 ° C.
(3) The BPS modified beaded silica particles A1 were put into another Schlenk flask connected with a cooling pipe and containing a rotor.
(4) A cooling tube was connected to the Schlenk flask, and the inside of the flask was subjected to vacuum treatment and then replaced with nitrogen three times to deoxygenate the inside of the flask.
(5) The remaining MEK solvent was introduced into the flask under nitrogen and treated with an ultrasonic cleaner for 10 minutes, and then the GMA monomer was introduced, immersed in a 50 ° C. ois bath and stirred.
(6) Furthermore, after introducing the catalyst solution prepared above under nitrogen, the reaction solution was stirred for 7 hours to conduct a polymerization reaction.
(7) The flask was immersed in an ice bath and quickly cooled, and then poured into hexane and stirred. If the precipitate was difficult to sink, it was separated by centrifugation and allowed to stand.
(8) After standing, after discarding the supernatant, hexane was added again to the remaining precipitate and left standing, and the supernatant was discarded. This operation was repeated two more times.
(9) Air was dried overnight while blowing nitrogen into the remaining precipitate, whereby the liquid was volatilized to obtain an organic-inorganic composite.
（１０）有機無機複合体を構成するポリマーの数平均分子量（Ｍｎ）を上述の方法で測定したところ、Ｍｎ＝３８，３００であった。更に、分子量分布（Ｍｗ／Ｍｎ）を算出したところ、Ｍｗ／Ｍｎ＝１．９１（≦２．３）であり、鎖長が揃ったポリマー鎖が、無機化合物粒子に結合していることがわかった。
（１１）有機無機複合体のフリーポリマー量を測定したところ、フリーポリマーは０質量％であった。
（１２）更に、有機無機複合体、光酸発生剤（「ＣＰＩ−１００Ｐ」）、ＭＥＫを混合し、上述の方法でコーティング材を得た。光酸発生剤を、有機無機複合体中の有機ポリマー量に対して５質量％となるように導入した。また、有機無機複合組成物（有機無機複合体と光酸発生剤）の固形分濃度が１０質量％となるように、溶媒（容積比で、ＭＥＫ：メチルセロソルブ＝５：５で混合したもの）を加えた。
（１３）上記コーティング材を使用し、上述の方法で、ＰＥＴフィルムに、塗工、乾燥し、空気下で、ＵＶ照射することで有機無機複合膜を得た。評価結果を表５に示す。得られた有機無機複合膜の外観を目視で確認したところ、無機物化合粒子の凝集やクラックは見られず、透明性を維持していた。
（１４）有機無機複合膜の全光線透過率とヘーズを、上述の方法で測定したところ、屈折率は１．１６、全光線透過率は９１％、ヘーズは０．３％であった。
（１５）上述の方法で有機無機複合膜の空隙率を計算したところ、６５％であり、高い空隙率を示した。
(10) When the number average molecular weight (Mn) of the polymer constituting the organic-inorganic composite was measured by the method described above, it was Mn = 38,300. Further, when the molecular weight distribution (Mw / Mn) was calculated, it was found that Mw / Mn = 1.91 (≦ 2.3), and the polymer chain with the uniform chain length was bonded to the inorganic compound particles. It was.
(11) When the amount of the free polymer of the organic-inorganic composite was measured, the free polymer was 0% by mass.
(12) Further, an organic-inorganic composite, a photoacid generator (“CPI-100P”), and MEK were mixed, and a coating material was obtained by the method described above. The photoacid generator was introduced so as to be 5% by mass with respect to the amount of the organic polymer in the organic-inorganic composite. Also, a solvent (mixed in a volume ratio of MEK: methyl cellosolve = 5: 5) so that the solid content concentration of the organic-inorganic composite composition (organic-inorganic composite and photoacid generator) is 10% by mass. Was added.
(13) Using the above coating material, the PET film was coated and dried by the above-described method, and an organic-inorganic composite film was obtained by UV irradiation under air. The evaluation results are shown in Table 5. When the appearance of the obtained organic-inorganic composite film was visually confirmed, no aggregation or cracking of inorganic compound particles was observed, and transparency was maintained.
(14) The total light transmittance and haze of the organic-inorganic composite film were measured by the above-described method. The refractive index was 1.16, the total light transmittance was 91%, and the haze was 0.3%.
(15) When the porosity of the organic-inorganic composite film was calculated by the above method, it was 65%, indicating a high porosity.
［製造例３：数珠状ＳｉＯ２−ｇ−ｐ（ＥＭＡ／ＨＥＭＡ／ＡＯＩ）、光ラジカル硬化］
有機無機複合体Ｃを、表１及び表３の配合に従って、以下の手順で製造した。得られた有機無機複合体及び有機無機複合膜の評価結果を、表４及び５に示す。
（１）回転子を入れたシュレンクフラスコに、ＣｕＢｒ及びＣｕＢｒ２加え、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した後、少量のＭＩＢＫを窒素下で導入し、溶液を攪拌した。
（２）上記溶液に、ＰＭＤＥＴＡを加え、４０℃で攪拌したものを、触媒溶液とした。
（３）冷却管を接続し、回転子を入れた別のシュレンクフラスコに、ＢＰＳ改質数珠状シリカＡ２粒子を投入した。
（４）シュレンクフラスコに冷却管を接続し、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した。
（５）フラスコに、窒素下で残りのＭＩＢＫ溶媒を導入し、５時間攪拌した後、ＥＭＡとＨＥＭＡのモル比が５０／５０で、全モノマー重量が、表面改質無機化合物粒子に対して約７８質量％（ＥＭＡモノマーとＨＥＭＡモノマー）になるようにモノマーを導入し、８０℃のオイスバスに浸し、攪拌した。
（６）更に、上記で調製した触媒溶液を、窒素下で導入後、反応液を２２時間攪拌し、重合反応を行った。
（７）フラスコを氷浴に浸して速やかに冷却してから、ヘキサンに投入して攪拌し、沈殿物が沈みにくい場合は、遠心分離で分離して、静置した。
（８）静置後、上澄み液を廃棄した後、残った沈殿物に、ＭＩＢＫを加えて再分散させた後、ヘキサンを加えて静置し、上澄み液を廃棄した。この操作を更に２回繰り返し、最後にヘキサンで洗浄し、上澄み液を廃棄することで未反応のモノマーを除去した。
（９）表４の配合に従って、残った沈殿物に重合禁止剤とＭＥＫ溶媒を加えて、溶液が透明になるまで攪拌を行なった。
（１０）次いで、溶液を６０℃に加熱した後、２−アクリロイルオキシエチルイソシアネート（以下、ＡＯＩと言う。）とＤＢＴＤＬを加えて、６時間攪拌し、ＨＥＭＡとＡＯＩの付加反応を行なった。
（１１）フラスコを氷浴に浸して速やかに冷却してから、ヘキサンに投入して攪拌し、静置した。沈殿物が沈みにくい場合は、遠心分離で分離を行なった。
（１２）上澄み液を廃棄した後、残った沈殿物に、ＭＥＫ／メタノール混合溶媒（容量比で、ＭＥＫ：メタノール＝１：１で混合）を加えて再分散させた後、ヘキサンを加えて静置し、上澄み液を廃棄した。この操作を更に２回繰り返し、最後にヘキサンで洗浄し、上澄み液を廃棄することで未反応のモノマーを除去した。
（１３）残った沈殿物に窒素を吹きこみながら、風乾することにより、液体を揮発させ、有機無機複合体Ｃを得た。
[Production Example 3: beaded SiO 2 -gp (EMA / HEMA / AOI), photo radical curing]
The organic-inorganic composite C was produced according to the following procedure in accordance with the formulations shown in Tables 1 and 3. The evaluation results of the obtained organic-inorganic composite and organic-inorganic composite film are shown in Tables 4 and 5.
(1) After adding CuBr and CuBr 2 to a Schlenk flask containing a rotor, vacuuming the inside of the flask and then replacing with nitrogen three times, the flask was deoxygenated, and then a small amount of MIBK was placed under nitrogen. And the solution was stirred.
(2) A catalyst solution was prepared by adding PMDETA to the above solution and stirring at 40 ° C.
(3) A BPS modified beaded silica A2 particle was charged into another Schlenk flask with a condenser connected and a rotor.
(4) A cooling tube was connected to the Schlenk flask, and the inside of the flask was subjected to vacuum treatment and then replaced with nitrogen three times to deoxygenate the inside of the flask.
(5) The remaining MIBK solvent was introduced into the flask under nitrogen, and after stirring for 5 hours, the molar ratio of EMA to HEMA was 50/50, and the total monomer weight was approximately about the surface-modified inorganic compound particles. Monomers were introduced so as to be 78% by mass (EMA monomer and HEMA monomer), immersed in an 80 ° C. ois bath, and stirred.
(6) Further, after introducing the catalyst solution prepared above under nitrogen, the reaction solution was stirred for 22 hours to carry out a polymerization reaction.
(7) The flask was immersed in an ice bath and quickly cooled, and then poured into hexane and stirred. If the precipitate was difficult to sink, it was separated by centrifugation and allowed to stand.
(8) After standing, the supernatant was discarded, and then MIBK was added to the remaining precipitate for redispersion, followed by addition of hexane and standing, and the supernatant was discarded. This operation was repeated two more times. Finally, the mixture was washed with hexane, and the supernatant was discarded to remove unreacted monomers.
(9) According to the formulation in Table 4, a polymerization inhibitor and MEK solvent were added to the remaining precipitate, and stirring was performed until the solution became transparent.
(10) Next, after the solution was heated to 60 ° C., 2-acryloyloxyethyl isocyanate (hereinafter referred to as AOI) and DBTDL were added and stirred for 6 hours to carry out an addition reaction between HEMA and AOI.
(11) The flask was immersed in an ice bath and quickly cooled, then poured into hexane, stirred and allowed to stand. When the precipitate was difficult to sink, it was separated by centrifugation.
(12) After discarding the supernatant, add MEK / methanol mixed solvent (mixed at a volume ratio of MEK: methanol = 1: 1) to the remaining precipitate and re-disperse it, and then add hexane to static. And the supernatant was discarded. This operation was repeated two more times. Finally, the mixture was washed with hexane, and the supernatant was discarded to remove unreacted monomers.
(13) Air was dried while blowing nitrogen into the remaining precipitate, whereby the liquid was volatilized and an organic-inorganic composite C was obtained.
（１４）有機無機複合体Ｃを構成するポリマーの数平均分子量（Ｍｎ）を上述の方法で測定したところ、Ｍｎ＝６３，２００であった。更に、分子量分布（Ｍｗ／Ｍｎ）を算出したところ、Ｍｗ／Ｍｎ＝２．００（≦２．３）であり、鎖長が揃ったポリマー鎖が、無機物化合物粒子に結合していることがわかった。
（１５）有機無機複合体Ｃのフリーポリマー量を測定したところ、０質量％であった。
（１６）有機無機複合体Ｃ、光ラジカル開始剤（質量比で、「イルガキュア１８４」：「イルガキュア９０７」＝４：１で混合したもの）、溶媒（容量比で、ＭＥＫ：シクロヘキサノン＝８：２で混合したもの）を混合し、上述の方法でコーティング材を得た。光ラジカル開始剤は、有機無機複合体中の有機ポリマー量に対して５質量％となるように導入した。また、有機無機複合組成物（有機無機複合体と光ラジカル開始剤）の固形分濃度が１０質量％となるように、溶媒を加えた。
（１７）上記コーティング材の凝集物を上述の方法で確認したところ、分散不良の固形物等は見られなかった。
（１８）上記コーティング材を使用し、上述の方法で、ＰＥＴフィルムに、塗工、乾燥し、窒素下で、ＵＶ照射することで有機無機複合硬化膜を得た。得られた有機無機複合膜の外観を目視で確認したところ、無機化合物粒子の凝集やクラックは見られず、透明性を維持していた。
（１９）有機無機複合膜の全光線透過率とヘーズを、上述の方法で測定したところ、全光線透過率は９２％、ヘーズは０．５％であった。
（２０）有機無機複合膜の屈折率を上述の方法で測定したところ、１．２６であり、上述の方法で計算される屈折率の値（１．４８）と比較して、低い値を示した。このことから、空隙を有する有機無機複合膜が形成されていることが判明した。
（２１）有機無機複合膜の空隙率を上述の方法で計算したところ、４６％であり、高い空隙率を示した。
(14) When the number average molecular weight (Mn) of the polymer constituting the organic-inorganic composite C was measured by the above-described method, Mn = 63,200. Further, when the molecular weight distribution (Mw / Mn) was calculated, it was found that Mw / Mn = 2.00 (≦ 2.3), and the polymer chains having the same chain length were bonded to the inorganic compound particles. It was.
(15) When the amount of the free polymer of the organic-inorganic composite C was measured, it was 0% by mass.
(16) Organic / inorganic composite C, photoradical initiator (mass ratio: “Irgacure 184”: “Irgacure 907” = 4: 1), solvent (volume ratio, MEK: cyclohexanone = 8: 2) And a coating material was obtained by the method described above. The photo radical initiator was introduced so as to be 5% by mass with respect to the amount of the organic polymer in the organic-inorganic composite. Moreover, the solvent was added so that the solid content concentration of the organic-inorganic composite composition (organic-inorganic composite and photoradical initiator) would be 10% by mass.
(17) When the above-mentioned aggregates of the coating material were confirmed by the above-mentioned method, no solid matter having poor dispersion was found.
(18) Using the above coating material, the PET film was coated and dried by the method described above, and UV-irradiated under nitrogen to obtain an organic-inorganic composite cured film. When the appearance of the obtained organic-inorganic composite film was visually confirmed, no aggregation or cracking of the inorganic compound particles was observed, and the transparency was maintained.
(19) When the total light transmittance and haze of the organic-inorganic composite film were measured by the above-described method, the total light transmittance was 92% and the haze was 0.5%.
(20) The refractive index of the organic-inorganic composite film measured by the above method is 1.26, which is lower than the refractive index value (1.48) calculated by the above method. It was. From this, it was found that an organic-inorganic composite film having voids was formed.
(21) When the porosity of the organic-inorganic composite film was calculated by the above-described method, it was 46%, indicating a high porosity.
［製造例４：数珠状ＳｉＯ２−ｇ−ｐ（ＭＭＡ／ＨＥＭＡ／ＡＯＩ）、全工程一環合成、光ラジカル硬化］
以下の手順に従って、ＢＩＤＳ改質数珠状シリカ粒子／ＭＩＢＫ溶液（ＢＩＤＳが表面に結合した、数珠状シリカ粒子／ＭＩＢＫ溶液）を合成し、連続して、表１の配合に従って、有機無機複合体Ｄを製造し、評価した。
（１）冷却管を接続し、回転子を入れた二口フラスコの内部を、窒素置換した。
（２）窒素下で、フラスコ内に９８．９容量％の数珠状シリカ溶液Ｂ（「ＭＩＢＫ−ＳＴ−ＵＰ」）を導入し、更に、０．１容量％のＢＩＤＳを導入し、攪拌を開始した。
（３）上記フラスコを１１０℃のオイルバスに浸し、攪拌しながら２４時間反応を行った。
（４）反応液を室温まで冷却した後、窒素下で１．０容量％のＨＭＤＳを導入した。
（５）室温で２時間攪拌後、８０℃で８時間攪拌して反応を行い、反応液を室温まで冷却したものを、ＢＩＤＳ改質数珠状シリカ溶液とした。一部を洗浄乾燥し、ハロゲン含有量を測定したところ、０．１質量％であった。塩素は検出されなかったため、臭素含有量をハロゲン含有量として示した。
（６）引き続き、表１の配合に従って、更に、モノマー、触媒溶液等を加え、８０℃で３時間重合した後、室温まで冷却し、重合液とした。
（７）更に引き続き、表３の配合に従って、６０℃で６時間、付加反応を行い、室温まで冷却した。
（８）上記反応液を、製造例３と同様の方法で洗浄・乾燥し、有機無機複合体Ｄを得た。評価結果を表４に示す。
（９）更に、有機無機複合体Ｄを使用して、製造例３と同様の方法で、コーティング材と有機無機複合膜を製造し、評価した結果を表５に示す。基材は、ＴＡＣフィルム上に、ハードコート層を形成したものを用いた。
[Production Example 4: bead-like SiO2-gp (MMA / HEMA / AOI), synthesis in all steps, photocuring]
According to the following procedure, a BIDS modified beaded silica particle / MIBK solution (a beaded silica particle / MIBK solution in which BIDS is bonded to the surface) was synthesized. Were manufactured and evaluated.
(1) A cooling pipe was connected, and the inside of the two-necked flask containing the rotor was replaced with nitrogen.
(2) Under nitrogen, 98.9% by volume of beaded silica solution B (“MIBK-ST-UP”) was introduced into the flask, 0.1% by volume of BIDS was further introduced, and stirring was started. did.
(3) The flask was immersed in an oil bath at 110 ° C. and reacted for 24 hours with stirring.
(4) After cooling the reaction solution to room temperature, 1.0 vol% HMDS was introduced under nitrogen.
(5) After stirring at room temperature for 2 hours, the reaction was carried out by stirring at 80 ° C. for 8 hours, and the reaction solution was cooled to room temperature to obtain a BIDS modified beaded silica solution. A portion was washed and dried, and the halogen content was measured and found to be 0.1% by mass. Since no chlorine was detected, the bromine content is shown as the halogen content.
(6) Subsequently, in accordance with the composition shown in Table 1, a monomer, a catalyst solution, and the like were further added, and after polymerization at 80 ° C. for 3 hours, the mixture was cooled to room temperature to obtain a polymerization solution.
(7) Further, according to the formulation shown in Table 3, the addition reaction was performed at 60 ° C. for 6 hours and cooled to room temperature.
(8) The reaction solution was washed and dried in the same manner as in Production Example 3 to obtain an organic-inorganic composite D. The evaluation results are shown in Table 4.
(9) Further, using the organic-inorganic composite D, a coating material and an organic-inorganic composite film were manufactured in the same manner as in Production Example 3, and the evaluation results are shown in Table 5. The substrate used was a TAC film on which a hard coat layer was formed.
［比較製造例１］
表２及び３の配合に従って、以下の手順で、フリーラジカル重合による有機無機複合体αを合成した。得られた有機無機複合体αを、製造例１と同様の方法で評価した。評価結果を表６に示す。
（１）回転子を入れたシュレンクフラスコに、ＡＩＢＮを加え、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した後、少量のＭＥＫを窒素下で導入し、攪拌したものを、触媒溶液とした。
（２）冷却管を接続し、回転子を入れた別のシュレンクフラスコに、ＣＰＳ改質２０ｎｍ球状シリカ粒子を投入した。
（３）シュレンクフラスコに冷却管を接続し、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した。
（４）フラスコに、窒素下で残りのＭＩＢＫ溶媒を導入し、５時間攪拌した後、ＭＭＡとＨＥＭＡのモル比が９０／１０で、全モノマー重量が、表面改質無機化合物粒子に対して７８質量％（ＭＭＡモノマーとＨＥＭＡモノマー）
になるようにモノマーを導入し、８０℃のオイスバスに浸し、攪拌した。
（５）更に、上記で調製した触媒溶液を、窒素下で導入後、反応液を６時間攪拌し、重合反応を行った。
（６）フラスコを氷浴に浸して速やかに冷却してから、ヘキサンに投入して攪拌し、沈殿物が沈みにくい場合は、遠心分離で分離して、静置した。
（７）静置後、上澄み液を廃棄した後、残った沈殿物に、ＭＩＢＫを加えて再分散させた後、ヘキサンを加えて静置し、上澄み液を廃棄した。この操作を更に２回繰り返し、最後にヘキサンで洗浄し、上澄み液を廃棄することで未反応のモノマーを除去した。
（８）残った沈殿物に２、６−ジ−ｔｅｒｔ−ブチルメチルフェノールとＭＥＫ溶媒を加えて、溶液が透明になるまで攪拌を行なった。
（９）次いで、溶液を６０℃に加熱した後、２−メタクリロイルオキシエチルイソシアネート（以下、ＭＯＩと言う。）とＤＢＴＤＬを加えて、６時間攪拌し、ＨＥＭＡとＭＯＩの付加反応を行なった。
（１０）フラスコを氷浴に浸して速やかに冷却してから、ヘキサンに投入して攪拌し、静置した。沈殿物が沈みにくい場合は、遠心分離で分離を行なった。
（１１）上澄み液を廃棄した後、残った沈殿物に、ＭＥＫを加えて再分散させた後、ヘキサンを加えて静置し、上澄み液を廃棄した。この操作を更に２回繰り返し、最後にヘキサンで洗浄し、上澄み液を廃棄することで未反応のモノマーを除去した。
（１２）残った沈殿物に窒素を吹きこみながら、風乾することにより、液体を揮発させ、有機無機複合体αを得た。
[Comparative Production Example 1]
According to the formulations shown in Tables 2 and 3, an organic-inorganic composite α by free radical polymerization was synthesized by the following procedure. The obtained organic-inorganic composite α was evaluated in the same manner as in Production Example 1. The evaluation results are shown in Table 6.
(1) Add AIBN to a Schlenk flask containing a rotor, vacuum the inside of the flask, and then replace with nitrogen three times. After deoxidizing the flask, a small amount of MEK is introduced under nitrogen. The stirred solution was used as a catalyst solution.
(2) CPS-modified 20 nm spherical silica particles were charged into another Schlenk flask with a condenser connected and a rotor.
(3) A cooling tube was connected to the Schlenk flask, and the inside of the flask was evacuated and then purged with nitrogen three times to deoxygenate the flask.
(4) The remaining MIBK solvent was introduced into the flask under nitrogen and stirred for 5 hours. The molar ratio of MMA to HEMA was 90/10, and the total monomer weight was 78 with respect to the surface-modified inorganic compound particles. Mass% (MMA monomer and HEMA monomer)
Then, the monomer was introduced so as to be immersed in an 80 ° C. ois bath and stirred.
(5) Furthermore, after introducing the catalyst solution prepared above under nitrogen, the reaction solution was stirred for 6 hours to conduct a polymerization reaction.
(6) The flask was immersed in an ice bath and quickly cooled, and then poured into hexane and stirred. If the precipitate was difficult to sink, it was separated by centrifugation and allowed to stand.
(7) After standing, the supernatant was discarded, and then MIBK was added to the remaining precipitate for redispersion, followed by addition of hexane and standing, and the supernatant was discarded. This operation was repeated two more times. Finally, the mixture was washed with hexane, and the supernatant was discarded to remove unreacted monomers.
(8) 2,6-Di-tert-butylmethylphenol and MEK solvent were added to the remaining precipitate and stirred until the solution became transparent.
(9) Next, after the solution was heated to 60 ° C., 2-methacryloyloxyethyl isocyanate (hereinafter referred to as MOI) and DBTDL were added and stirred for 6 hours to carry out an addition reaction between HEMA and MOI.
(10) The flask was immersed in an ice bath and quickly cooled, then poured into hexane, stirred and allowed to stand. When the precipitate was difficult to sink, it was separated by centrifugation.
(11) After discarding the supernatant, MEK was added to the remaining precipitate for redispersion, and hexane was added and allowed to stand, and the supernatant was discarded. This operation was repeated two more times. Finally, the mixture was washed with hexane, and the supernatant was discarded to remove unreacted monomers.
(12) The remaining precipitate was air-dried while blowing nitrogen, thereby volatilizing the liquid to obtain an organic-inorganic composite α.
（１３）ポリマーの分子量は、有機無機複合体αがゲル化したため完全に溶解しなかったが、溶解成分のみを測定したところ分子量分布は２．３より大きかった。その有機無機複合体αを使用し、上述の方法で、コーティング液を調整した結果、明らかに溶解していない凝集物が沈殿していた。このコーティング液から得られたコーティング膜の外観を目視で確認したところ、粒子の凝集が見られ、微白濁を呈していた。得られた有機無機複合膜の評価結果を表６に示す。 (13) The molecular weight of the polymer was not completely dissolved because the organic-inorganic composite α was gelled. However, when only the dissolved component was measured, the molecular weight distribution was larger than 2.3. As a result of using the organic-inorganic composite α and adjusting the coating solution by the above-described method, aggregates that were clearly not dissolved were precipitated. When the appearance of the coating film obtained from this coating solution was visually confirmed, the particles were aggregated and slightly clouded. Table 6 shows the evaluation results of the obtained organic-inorganic composite film.
［比較製造例２］
無機化合物粒子を配合せずに、表２の配合に従って、重合反応を行い、ｐ（ＭＭＡ−ｃｏ−ＨＥＭＡ）共重合ポリマーを合成し、表３の配合に従って、製造例３と同様に、反応性二重結合を有する化合物を付加させた。得られた有機ポリマーとＢＰＳ改質数珠状シリカ粒子Ａ１の混合コーティング膜を作成し、製造例３と同様の方法で評価した。
（１）回転子を入れたシュレンクフラスコに、ＣｕＢｒを加え、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した後、少量のＭＥＫを窒素下で導入し、攪拌した。
（２）上記溶液に、ＰＭＤＥＴＡを加え、４０℃で攪拌したものを、触媒溶液とした。
（３）回転子を入れたシュレンクフラスコを、内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した後、少量のＭＩＢＫとＥＢＩＢを窒素下で導入し、攪拌したものを、重合開始剤溶液とした。
（４）回転子を入れた、別のシュレンクフラスコに、冷却管を接続し、フラスコ内部を真空処理してから窒素置換する操作を３回繰り返して、フラスコ内を脱酸素した。
（５）フラスコに、窒素下で残りのＭＩＢＫ溶媒、モノマー（ＭＭＡとＨＥＭＡ）を導入し、８０℃のオイスバスに浸し、攪拌した。
（６）更に、上記で調製した触媒溶液と重合開始剤溶液を、窒素下で導入後、反応液を１０時間攪拌し、重合反応を行った。
（７）フラスコを氷浴に浸して速やかに冷却してから、ヘキサンに投入して攪拌し、静置した。その後、上澄み液を廃棄した。
（８）残った沈殿物に、ヘキサンを再び加えて静置し、上澄み液を廃棄した。この操作を更に２回繰り返した。
（９）残った沈殿物に窒素を吹きこみながら、一晩風乾することにより、液体を揮発させ、沈殿物「ｐ（ＭＭＡ−ｃｏ−ＨＥＭＡ）」を得た。
（１０）残った沈殿物に２、６−ジ−ｔｅｒｔ−ブチルメチルフェノールとＭＥＫ溶媒を加えて、溶液が透明になるまで攪拌を行なった。
（１１）次いで、溶液を６０℃に加熱した後、２−アクリロイルオキシエチルイソシアネート（ＡＯＩ）とＤＢＴＤＬを加えて、６時間攪拌し、ＨＥＭＡとＡＯＩの付加反応を行なった。
（１２）フラスコを氷浴に浸して速やかに冷却してから、ヘキサンに投入して攪拌し、静置した。沈殿物が沈みにくい場合は、遠心分離で分離を行なった。
（１３）上澄み液を廃棄した後、残った沈殿物に、ＭＥＫを加えて再分散させた後、ヘキサンを加えて静置し、上澄み液を廃棄した。この操作を更に２回繰り返し、最後にヘキサンで洗浄し、上澄み液を廃棄することで未反応のモノマーを除去した。
（１４）残った沈殿物に窒素を吹きこみながら、風乾することにより、液体を揮発させ、フリーポリマー「ｐ（ＭＭＡ／ＨＥＭＡ／ＡＯＩ）」を得た。
[Comparative Production Example 2]
Without blending inorganic compound particles, a polymerization reaction was performed according to the blending in Table 2 to synthesize a p (MMA-co-HEMA) copolymer, and according to the blending in Table 3, the reactivity was similar to Production Example 3. A compound having a double bond was added. A mixed coating film of the obtained organic polymer and BPS modified beaded silica particles A1 was prepared and evaluated in the same manner as in Production Example 3.
(1) The operation of adding CuBr to a Schlenk flask containing a rotor, evacuating the flask and then substituting with nitrogen was repeated three times. And stirred.
(2) A catalyst solution was prepared by adding PMDETA to the above solution and stirring at 40 ° C.
(3) The operation of evacuating the Schlenk flask containing the rotor and then substituting with nitrogen was repeated three times to deoxygenate the flask, and then a small amount of MIBK and EBIB were introduced under nitrogen and stirred This was used as a polymerization initiator solution.
(4) A cooling tube was connected to another Schlenk flask containing a rotor, and the inside of the flask was subjected to vacuum treatment and then purged with nitrogen three times to deoxygenate the inside of the flask.
(5) The remaining MIBK solvent and monomers (MMA and HEMA) were introduced into the flask under nitrogen, immersed in an 80 ° C. ois bath, and stirred.
(6) Furthermore, after introducing the catalyst solution and the polymerization initiator solution prepared above under nitrogen, the reaction solution was stirred for 10 hours to perform a polymerization reaction.
(7) The flask was immersed in an ice bath and quickly cooled, and then poured into hexane, stirred and allowed to stand. Thereafter, the supernatant was discarded.
(8) Hexane was added again to the remaining precipitate and allowed to stand, and the supernatant was discarded. This operation was repeated two more times.
(9) Air was dried overnight while blowing nitrogen into the remaining precipitate, whereby the liquid was volatilized to obtain a precipitate “p (MMA-co-HEMA)”.
(10) 2,6-Di-tert-butylmethylphenol and MEK solvent were added to the remaining precipitate and stirred until the solution became transparent.
(11) Next, the solution was heated to 60 ° C., 2-acryloyloxyethyl isocyanate (AOI) and DBTDL were added, and the mixture was stirred for 6 hours to carry out an addition reaction between HEMA and AOI.
(12) The flask was immersed in an ice bath and quickly cooled, and then poured into hexane, stirred and allowed to stand. When the precipitate was difficult to sink, it was separated by centrifugation.
(13) After discarding the supernatant, MEK was added to the remaining precipitate for redispersion, and hexane was added and allowed to stand, and the supernatant was discarded. This operation was repeated two more times. Finally, the mixture was washed with hexane, and the supernatant was discarded to remove unreacted monomers.
(14) The remaining precipitate was air-dried while blowing nitrogen, thereby volatilizing the liquid to obtain a free polymer “p (MMA / HEMA / AOI)”.
（１５）ポリマーの数平均分子量（Ｍｎ）を上述の方法で測定したところ、Ｍｎ＝６１，２００であった。更に、分子量分布（Ｍｗ／Ｍｎ）を算出したところ、Ｍｗ／Ｍｎ＝１．８５（≦２．３）であった。評価結果を表４に示す。
（１６）上記フリーポリマーに、無機含量が９０質量％になるようにＢＰＳ改質数珠状シリカ粒子Ａ１を加えて、実施例３と同様の方法で、有機ポリマーとＢＰＳ改質数珠状シリカ粒子Ａ１の混合物で、有機無機複合膜を作成し、評価した。
（１７）得られた有機無機複合膜の外観を目視で確認したところ、微白濁を呈していた。有機無機複合硬化膜の全光線透過率とヘーズを、上述の方法で測定したところ、全光線透過率は８２％、ヘーズは１０．１％であった。また、密着性も低下した。得られた有機無機複合硬化膜の評価結果を表６に示す。
(15) When the number average molecular weight (Mn) of the polymer was measured by the above-mentioned method, it was Mn = 61,200. Furthermore, when the molecular weight distribution (Mw / Mn) was calculated, it was Mw / Mn = 1.85 (≦ 2.3). The evaluation results are shown in Table 4.
(16) BPS modified beaded silica particles A1 are added to the free polymer so that the inorganic content is 90% by mass, and the organic polymer and BPS modified beaded silica particles A1 are processed in the same manner as in Example 3. An organic-inorganic composite film was prepared and evaluated using the above mixture.
(17) When the appearance of the obtained organic-inorganic composite film was visually confirmed, it was slightly clouded. When the total light transmittance and haze of the organic-inorganic composite cured film were measured by the above-described method, the total light transmittance was 82% and the haze was 10.1%. Moreover, the adhesiveness also decreased. Table 6 shows the evaluation results of the obtained organic-inorganic composite cured film.
［比較製造例３］
表２及び３に従い、重合停止時間を１４時間とした以外は、製造例３と同様の方法で有機無機複合体βを、製造し、評価した。得られた有機無機複合体βの無機含量は、４７質量％であり、屈折率を低下させる効果は見られなかった。得られた有機無機複合膜の評価結果を、表６に示す。
[Comparative Production Example 3]
According to Tables 2 and 3, an organic-inorganic composite β was produced and evaluated in the same manner as in Production Example 3 except that the polymerization stop time was 14 hours. The inorganic content of the obtained organic-inorganic composite β was 47% by mass, and no effect of reducing the refractive index was observed. Table 6 shows the evaluation results of the obtained organic-inorganic composite film.
［比較製造例４］
表２及び３に従い、重合停止時間を１５分とした以外は、実施例３と同様の方法で、有機無機複合体γを製造し、評価した。得られた有機無機複合体γの無機含量は９６質量％であり、外観を目視で確認したところ、微白濁を呈していた。また、得られた有機無機複合膜が脆く、破損してしまい、屈折率等の評価ができなかった。評価結果を表６に示す。
[Comparative Production Example 4]
According to Tables 2 and 3, an organic-inorganic composite γ was produced and evaluated in the same manner as in Example 3 except that the polymerization stop time was 15 minutes. The obtained organic-inorganic composite γ had an inorganic content of 96% by mass, and the appearance was visually confirmed to show a slight cloudiness. Further, the obtained organic-inorganic composite film was brittle and damaged, and the refractive index and the like could not be evaluated. The evaluation results are shown in Table 6.
［比較製造例５］
製造例３の有機無機複合体Ｃ（６５質量％）に、比較製造例２のフリーポリマー「ｐ（ＭＭＡ／ＨＥＭＡ／ＡＯＩ）」（３５質量％）を加え、製造例３と同様の方法で、コーティング材と有機無機複合膜を作製し、評価した。得られた有機無機複合膜には、屈折率を低下させる効果は見られなかった。評価結果を、表６に示す。
[Comparative Production Example 5]
To the organic-inorganic composite C (65% by mass) of Production Example 3, the free polymer “p (MMA / HEMA / AOI)” (35% by mass) of Comparative Production Example 2 was added, and the same method as in Production Example 3, A coating material and an organic / inorganic composite film were prepared and evaluated. In the obtained organic-inorganic composite film, the effect of reducing the refractive index was not observed. The evaluation results are shown in Table 6.
［製造例５］（偏光子の作製）
以下の手順で、偏光子を作製した。
（１）ＰＶＡフィルム（完全鹸化タイプ、鹸化度９９．９％以上、重合度２４００、厚み４５μｍ）を、３０℃の純水に浸漬した後、ヨウ素／ヨウ化カリウム／純水の質量比が０．０２／２／１００の水溶液に３０℃で浸漬した。
（２）次いで、ヨウ化カリウム／ホウ酸／純水の質量比が１２／５／１００の水溶液に ５７℃で浸漬した。
（３）更に、８℃の純水で洗浄した後、６５℃で乾燥し、厚さ約２０μｍの偏光子を得た。延伸は、主に、ヨウ素染色及びホウ酸処理の工程で行い、トータル延伸倍率は５．５倍であった。
[Production Example 5] (Production of polarizer)
A polarizer was produced by the following procedure.
(1) A PVA film (complete saponification type, saponification degree of 99.9% or more, polymerization degree 2400, thickness 45 μm) is immersed in pure water at 30 ° C., and then the mass ratio of iodine / potassium iodide / pure water is 0. It was immersed in an aqueous solution of 02/2/100 at 30 ° C.
(2) Next, it was immersed at 57 ° C. in an aqueous solution having a mass ratio of potassium iodide / boric acid / pure water of 12/5/100.
(3) Further, after washing with pure water at 8 ° C., it was dried at 65 ° C. to obtain a polarizer having a thickness of about 20 μm. Stretching was mainly performed in the iodine staining and boric acid treatment steps, and the total stretching ratio was 5.5 times.
［製造例６］（低屈折率コーティング材Ｃの作製）
４質量％の製造例３の有機無機複合体Ｃ、０．１６質量％のフッ素系添加剤（ＫＹ−１２０３）、０．０４質量％の光ラジカル開始剤（イルガキュア１８４とイルガキュア９０７を、４：１の質量比で混合したもの）にＭＥＫを加えて１００質量％とし、混合攪拌した。
上記溶液に、ＭＥＫ：シクロヘキサノンが８：２（容積比）となるように、シクロヘキサノンを加えて混合した。
[Production Example 6] (Production of low refractive index coating material C)
4% by mass of the organic-inorganic composite C of Production Example 3, 0.16% by mass of a fluorine-based additive (KY-1203), 0.04% by mass of a photoradical initiator (Irgacure 184 and Irgacure 907, 4: MEK was added to 100% by mass and mixed and stirred.
To the above solution, cyclohexanone was added and mixed so that MEK: cyclohexanone was 8: 2 (volume ratio).
［製造例７］（反射防止機能付ＴＡＣフィルムの作製）
以下の手順で、基材を作製し、評価した。
（１）４８質量％の日本合成化学株式会社製、「紫光ＵＶ−７６４０Ｂ」と、２質量％の光重合開始剤（イルガキュア１８４）と、５０質量％のＭＥＫを混合し、ハードコート材溶液を作製した。
（２）ＴＡＣフィルム（富士フィルム株式会社製、厚み４０μｍ）に、上記ハードコート材溶液をバーコーターでコーティングし、風乾後、８０℃×１分間熱風乾燥し、更に窒素下で、積算光量５００ｍＪ／ｃｍ２となるようにＵＶ照射した。
（３）上記ハードコート層の厚みは約５μｍ、屈折率は１．５０であった。
（４）有機無機複合膜が約１００〜１１０ｎｍの厚みとなるように、製造例６の低屈折率コーティング材Ｃを、バーコーターでコーティングし、（２）と同様の条件で乾燥、ＵＶ硬化を行った。
（５）有機無機複合膜の屈折率は１．２６、最小反射率は０．０５％であった。
[Production Example 7] (Preparation of TAC film with antireflection function)
The substrate was prepared and evaluated according to the following procedure.
(1) 48% by mass of Nippon Synthetic Chemical Co., Ltd. “purple UV-7640B”, 2% by mass of a photopolymerization initiator (Irgacure 184) and 50% by mass of MEK are mixed, Produced.
(2) A TAC film (Fuji Film Co., Ltd., thickness 40 μm) is coated with the above hard coat material solution with a bar coater, air-dried, hot-air dried at 80 ° C. for 1 minute, and further under nitrogen, an integrated light quantity of 500 mJ / and UV irradiation so that the cm 2.
(3) The hard coat layer had a thickness of about 5 μm and a refractive index of 1.50.
(4) The low refractive index coating material C of Production Example 6 is coated with a bar coater so that the organic-inorganic composite film has a thickness of about 100 to 110 nm, and dried and UV cured under the same conditions as in (2). went.
(5) The refractive index of the organic-inorganic composite film was 1.26, and the minimum reflectance was 0.05%.
［実施例１］
以下の手順に従って、積層体（反射防止機能付偏光板）を作製し、評価した。
（１）製造例７の反射防止機能付ＴＡＣフィルムの裏側（有機無機複合膜が積層されていない面）に、１．５ｍｏｌ／ＬのＮａＯＨ／ＩＰＡ溶液で処理し、乾燥させた後、流水で洗浄し、再乾燥させた。
（２）上記フィルムの鹸化した面に、ＰＶＡ系接着剤を介して、製造例５の偏光子を貼り付けた。
（３）更に（２）の偏光子のもう片方の面に、片側だけ鹸化処理したＴＡＣフィルムを使用し、鹸化処理面を、上記ＰＶＡ接着剤を介して積層し、図６の５０Ｂの構成の積層体（反射防止機能付偏光板）を得た。
（４）評価結果を、表７に示す。本積層体は比較例１の基準に対し、視認性とコントラストが顕著に向上することがわかった。
[Example 1]
A laminate (polarizing plate with antireflection function) was prepared and evaluated according to the following procedure.
(1) Treated with 1.5 mol / L NaOH / IPA solution on the back side (surface on which the organic-inorganic composite film is not laminated) of the anti-reflection function TAC film of Production Example 7 and dried, and then with running water Washed and re-dried.
(2) The polarizer of Production Example 5 was attached to the saponified surface of the film via a PVA adhesive.
(3) Further, a TAC film saponified only on one side is used on the other side of the polarizer of (2), and the saponified surface is laminated via the PVA adhesive, and the structure of 50B in FIG. A laminate (polarizing plate with antireflection function) was obtained.
(4) Table 7 shows the evaluation results. It was found that the visibility and contrast of the laminate were significantly improved with respect to the reference of Comparative Example 1.
［比較例１］
実施例１で使用した、製造例３の有機無機複合体Ｃの代わりに、比較製造例２のｐ（ＭＭＡ／ＨＥＭＡ／ＡＯＩ）を使用した以外は、実施例１と同様の方法で、積層体（反射防止機能付偏光板）を作製し、評価した結果を、表７に示す。
本積層体は、実施例１と比較して、明らかに視認性とコントラストが劣っていた。
[Comparative Example 1]
In the same manner as in Example 1 except that p (MMA / HEMA / AOI) in Comparative Production Example 2 was used instead of the organic-inorganic composite C in Production Example 3 used in Example 1, a laminate. Table 7 shows the results of producing and evaluating (polarizing plate with antireflection function).
This laminate was clearly inferior in visibility and contrast as compared with Example 1.
［比較例２］
実施例１で使用した、製造例３の有機無機複合体Ｃの代わりに、比較製造例４の有機無機複合体γを使用した以外は、実施例１と同様の方法で、積層体（反射防止機能付偏光板）を作製し、評価した結果を表７に示す。
本積層体は、実施例１と比較して、膜が脆く透明性に劣るため、視認性やコントラストが劣るだけでなく、測定箇所によるバラつきが大きいことがわかった。
[Comparative Example 2]
In the same manner as in Example 1 except that the organic-inorganic composite γ of Comparative Production Example 4 was used instead of the organic-inorganic composite C of Production Example 3 used in Example 1, the laminate (antireflection) Table 7 shows the results of producing and evaluating a polarizing plate with a function.
Compared with Example 1, this laminated body was not only poor in visibility and contrast but also inconsistent depending on the measurement location because the film was brittle and inferior in transparency.
［比較例３］
実施例１で使用した、製造例３の有機無機複合体Ｃの代わりに、比較製造例５の組成物を使用した以外は、実施例１と同様の方法で、積層体（反射防止機能付偏光板）を作製し、評価した結果を、表７に示す。
本積層体は、実施例１と比較して、視認性やコントラストが劣っていた。
[Comparative Example 3]
In the same manner as in Example 1 except that the composition of Comparative Production Example 5 was used instead of the organic-inorganic composite C of Production Example 3 used in Example 1, the laminate (polarized light with antireflection function) was used. Table 7 shows the results of producing and evaluating the plate.
This laminate was inferior in visibility and contrast as compared to Example 1.
［製造例８（アクリル系粘着剤シート）］
以下の手順で、アクリル系粘着剤シートを作製した。
（１）ベースポリマーとして、ｎＢＡ／ＡＡ／ＨＥＡ＝１００／５／０．２（質量比）のの共重合体からなる、Ｍｗ＝約１８０万のアクリル酸エステル共重合体を合成した。アクリル酸エステル共重合体のＴｇは、−４０℃であった。
（２）上記アクリル酸エステル共重合体溶液（３０質量％）に、イソシアネート系多官能性化合物（日本ポリウレタン社製、「コロネートＬ」を、ポリマー固形分１００部に対して４部、シランカップリング剤（信越シリコーン株式会社製、「ＫＢＭ−４０３」）を０．５部、粘度調整のための溶剤（酢酸エチル）を加え、粘着剤溶液（固形分１２％）を調製した。当該粘着剤溶液を、離型フィルム（三菱化学株式会社製、「ダイヤホイルＭＲＦ３８」）上に塗布した後、熱風循環式オーブンで乾燥して、粘着剤シートを形成した。
[Production Example 8 (acrylic pressure-sensitive adhesive sheet)]
An acrylic pressure-sensitive adhesive sheet was prepared by the following procedure.
(1) As a base polymer, an acrylic acid ester copolymer having Mw = about 1.8 million was composed of a copolymer of nBA / AA / HEA = 100/5 / 0.2 (mass ratio). The Tg of the acrylic ester copolymer was −40 ° C.
(2) Into the acrylic ester copolymer solution (30% by mass), 4 parts of an isocyanate-based polyfunctional compound (manufactured by Nippon Polyurethane Co., Ltd., “Coronate L” with respect to 100 parts of polymer solid content, silane coupling 0.5 parts of an adhesive (manufactured by Shin-Etsu Silicone Co., Ltd., “KBM-403”) and a solvent for adjusting viscosity (ethyl acetate) were added to prepare an adhesive solution (solid content 12%). Was coated on a release film (“Diafoil MRF38” manufactured by Mitsubishi Chemical Corporation), and then dried in a hot air circulation oven to form an adhesive sheet.
［実施例２］
実施例１のＰＶＡ系接着剤の代わりに、製造例８のアクリル系粘着剤シートを使用して、実施例１と同様の方法で、積層体（反射防止機能付偏光板）を作製し、評価した結果を、表７に示す。本積層体は比較例１の基準に対し、視認性とコントラストが顕著に向上することがわかった。
[Example 2]
Using the acrylic pressure-sensitive adhesive sheet of Production Example 8 instead of the PVA-based adhesive of Example 1, a laminate (polarizing plate with antireflection function) was produced and evaluated in the same manner as in Example 1. The results are shown in Table 7. It was found that the visibility and contrast of the laminate were significantly improved with respect to the reference of Comparative Example 1.
［製造例９］（低屈折率コーティング材Ａ）
６質量％の製造例１の有機無機複合体Ａ、にＭＥＫを加えて１００質量％とし、混合攪拌した。
上記溶液に、ＭＥＫ：シクロヘキサノンが８：２（容積比）となるように、シクロヘキサノンを加えて混合した。
[Production Example 9] (Low refractive index coating material A)
MEK was added to 6% by mass of the organic-inorganic composite A of Production Example 1 to make 100% by mass, and the mixture was stirred.
To the above solution, cyclohexanone was added and mixed so that MEK: cyclohexanone was 8: 2 (volume ratio).
［製造例１０］
以下の手順で、有機無機複合膜と粘着層を有する積層体を作製した。
（１）離型フィルムとして、表面が平滑なテフロン（登録商標）シートの上に、製造例９の低屈折率コーティング材Ａをコーティングし、風乾後、８０℃×１分間熱風乾燥した。
（２）得られた有機無機複合膜の厚みは約３８０ｎｍ、屈折率は１．３３であった。
（３）上記有機無機複合膜の片面に、製造例８の粘着剤シート（厚み２〜５μｍ）を積層し、積層体を得た。
[Production Example 10]
The laminated body which has an organic inorganic composite film and the adhesion layer was produced in the following procedures.
(1) As a release film, a low refractive index coating material A of Production Example 9 was coated on a Teflon (registered trademark) sheet having a smooth surface, air-dried, and then hot-air dried at 80 ° C. for 1 minute.
(2) The thickness of the obtained organic-inorganic composite film was about 380 nm and the refractive index was 1.33.
(3) The pressure-sensitive adhesive sheet of Production Example 8 (thickness 2 to 5 μm) was laminated on one side of the organic-inorganic composite film to obtain a laminate.
［実施例３］（プリズムシート内蔵積層フィルム）
以下の手順で、図１１のプリズムシート内蔵積層フィルムを作製し、評価した。
（１）反射型偏光板（住友スリーエム株式会社製、「ＤＢＥＦ−Ｄ２」）の裏面に、上記製造例１０の積層体を重ね、接着層を形成した。
（２）プリズムシート（住友スリーエム株式会社製、「ＢＥＦ３−Ｔ」）の凸部が、接着層内に納まるように、（１）の積層体を貼り付け、プリズムシート内蔵積層フィルムを作製し、評価した結果を表８に示す。
[Example 3] (Laminated film with built-in prism sheet)
The prism sheet built-in laminated film of FIG. 11 was prepared and evaluated by the following procedure.
(1) On the back surface of the reflective polarizing plate (manufactured by Sumitomo 3M Limited, “DBEF-D2”), the laminate of Production Example 10 was stacked to form an adhesive layer.
(2) The laminate of (1) is pasted so that the convex part of the prism sheet (manufactured by Sumitomo 3M Co., Ltd., “BEF3-T”) fits in the adhesive layer, to produce a prism sheet built-in laminated film, Table 8 shows the evaluation results.
［実施例４］（プリズムシート内蔵積層フィルム）
実施例３の反射型偏光板の裏面（光源側）に、ＥＶＡ系熱可塑性接着剤を、厚さが約１０μｍとなるように溶融塗布し、実施例３のプリズムシートの凸部が、接着層内に納まるように、（１）の積層体を貼り付け、プリズムシート内蔵積層フィルムを作製し、評価した結果を表８に示す。
[Example 4] (Laminated film with built-in prism sheet)
An EVA thermoplastic adhesive was melt-applied to the back surface (light source side) of the reflective polarizing plate of Example 3 so that the thickness was about 10 μm, and the convex portion of the prism sheet of Example 3 was formed as an adhesive layer. Table 8 shows the results obtained by pasting the laminated body of (1) so as to fit in, producing a prism sheet built-in laminated film, and evaluating it.
［比較例４］
実施例４の反射型偏光板とプリズムシートを、接着剤を介さずに積層し、プリズムシート内蔵積層フィルムを作製した。実施例４と同様の方法で、評価した結果を表８に示す。輝度は良好なものの、粘着層や接着層を介さないために、弛みが生じる問題が発生した。
[Comparative Example 4]
The reflective polarizing plate of Example 4 and the prism sheet were laminated without using an adhesive to produce a prism sheet built-in laminated film. Table 8 shows the results of evaluation performed in the same manner as in Example 4. Although the luminance was good, there was a problem that slackness occurred because no adhesive layer or adhesive layer was interposed.
［比較例５］
ＥＶＡ系接着剤の厚みが２００μｍとなるように塗布し、加熱由着した以外は、実施例４と同様の方法で、プリズムシート内蔵積層フィルムを作製し、評価した結果を表８に示す。実施例４と比較して、明らかに輝度が劣ることが判明した。
[Comparative Example 5]
Table 8 shows the results of producing and evaluating a prism sheet built-in laminated film by the same method as in Example 4 except that the EVA adhesive was applied to a thickness of 200 μm and was heated. As compared with Example 4, it was found that the luminance was clearly inferior.
［製造例１１］（ウレタン系接着剤溶液）
ウレタン系接着剤（東洋モートン株式会社製、「ＴＭ−Ｋ５１」）と、硬化剤（東洋モートン株式会社製、「ＣＡＴ−ＲＴ８５」）を、８８：１２（質量比）で混合し、溶媒で希釈したものを、接着剤溶液とした。
[Production Example 11] (urethane adhesive solution)
A urethane-based adhesive (Toyo Morton Co., Ltd., “TM-K51”) and a curing agent (Toyo Morton Co., Ltd., “CAT-RT85”) are mixed at 88:12 (mass ratio) and diluted with a solvent. This was used as an adhesive solution.
［製造例１２］（低屈折率コーティング材Ｂの作製）
１５質量％の製造例２の有機無機複合体Ｂ、０．１５質量％の光酸発生剤に、ＭＥＫを加えて１００質量％とし、混合攪拌した。
上記溶液に、ＭＥＫ：メチルセロソルブが５：５（容積比）となるように、メチルセロソルブを加えて混合した。
[Production Example 12] (Production of low refractive index coating material B)
MEK was added to 15% by mass of the organic-inorganic composite B of Production Example 2 and 0.15% by mass of the photoacid generator to make 100% by mass, and the mixture was stirred.
To the above solution, methyl cellosolve was added and mixed so that MEK: methyl cellosolve was 5: 5 (volume ratio).
［製造例１３］（低屈折率層付ＰＥＴフィルム）
下記の手順で、低屈折率層付ＰＥＴフィルムを作製した。
（１）製造例１２の低屈折率コーティング材Ｂを、ＰＥＴフィルム（東洋紡績株式会社製、「コスモシャインＡ４１００」）上にコーティングし、風乾後、８０℃×１分間熱風乾燥し、積算光量５００ｍＪ／ｃｍ２となるように、ＵＶ照射した。
（２）上記有機無機複合膜の厚みは約１μｍであり、屈折率は１．１６であった。
[Production Example 13] (PET film with a low refractive index layer)
A PET film with a low refractive index layer was prepared by the following procedure.
(1) The low refractive index coating material B of Production Example 12 is coated on a PET film (Toyobo Co., Ltd., “Cosmo Shine A4100”), air-dried, then hot-air dried at 80 ° C. for 1 minute, and an integrated light quantity of 500 mJ UV irradiation was performed so as to be / cm 2 .
(2) The thickness of the organic-inorganic composite film was about 1 μm, and the refractive index was 1.16.
［実施例５］
プリズムシートの代わりに、製造例１３の低屈折率層付ＰＥＴフィルムを使用して、図１２の、プリズムシート代替低屈折率層付ＰＥＴフィルム内蔵積層フィルムを作製し、実施例３と同様の方法で評価した。
（１）反射型偏光板（住友スリーエム株式会社製、「ＤＢＥＦ−Ｄ２」）の裏面に、製造例１２の接着剤をコーティングし、乾燥させて、接着層を形成した。
（２）プリズムシートの代わりに、製造例１３の低屈折率層付ＰＥＴフィルムを使用して、図１２の、プリズムシート代替低屈折率層付ＰＥＴフィルム内蔵積層フィルムを作製し、評価した結果を表８に示す。基準となる比較例５と比較して、輝度が向上した。
[Example 5]
Using the PET film with a low refractive index layer of Production Example 13 instead of the prism sheet, the prism film-substitute laminated film with a low refractive index layer shown in FIG. 12 was produced, and the same method as in Example 3 was used. It was evaluated with.
(1) The adhesive of Production Example 12 was coated on the back surface of a reflective polarizing plate (“DBEF-D2” manufactured by Sumitomo 3M Limited), and dried to form an adhesive layer.
(2) Using the PET film with a low refractive index layer of Production Example 13 instead of the prism sheet, the result is shown in FIG. Table 8 shows. Compared with the comparative example 5 used as a reference | standard, the brightness | luminance improved.
［製造例１４］（低屈折率コーティング材Ｄの作製）
１５質量％の製造例４の有機無機複合体Ｄ、０．１５質量％の光ラジカル開始剤（イルガキュア１８４とイルガキュア９０７を、４：１の質量比で混合したもの）にＭＥＫを加えて１００質量％とし、混合攪拌した。
上記溶液に、ＭＥＫ：メチルセロソルブが５：５（容積比）となるように、メチルセロソルブを加えて混合した。
[Production Example 14] (Production of low refractive index coating material D)
MEK was added to 15% by mass of the organic-inorganic composite D of Production Example 4, 0.15% by mass of a photoradical initiator (Irgacure 184 and Irgacure 907 mixed at a mass ratio of 4: 1), and 100% by mass. % And mixed and stirred.
To the above solution, methyl cellosolve was added and mixed so that MEK: methyl cellosolve was 5: 5 (volume ratio).
［製造例１５］（低屈折率層付ＰＥＴフィルム）
下記の手順で、低屈折率層付ＰＥＴフィルムを作製した。
（１）製造例１４の低屈折率コーティング材Ｄを、ＰＥＴフィルム（東洋紡績株式会社製、「コスモシャインＡ４１００」）上にコーティングし、風乾後、８０℃×１分間熱風乾燥し、積算光量５００ｍＪ／ｃｍ２となるように、ＵＶ照射した。
（２）上記有機無機複合膜の厚みは約１μｍであり、屈折率は１．２３であった。
[Production Example 15] (PET film with a low refractive index layer)
A PET film with a low refractive index layer was prepared by the following procedure.
(1) The low refractive index coating material D of Production Example 14 is coated on a PET film (Toyobo Co., Ltd., “Cosmo Shine A4100”), air-dried, then hot-air dried at 80 ° C. for 1 minute, and an integrated light quantity of 500 mJ UV irradiation was performed so as to be / cm 2 .
(2) The thickness of the organic-inorganic composite film was about 1 μm, and the refractive index was 1.23.
［実施例６］
実施例５と同様の方法で、製造例１３の低屈折率層付ＰＥＴフィルムの代わりに、製造例１５の低屈折率ＰＥＴフィルムを使用して、プリズムシート代替低屈折率層付ＰＥＴフィルム内蔵積層フィルムを作製し、評価した結果を表８に示す。基準となる比較例５と比較して、輝度が向上した。
[Example 6]
In the same manner as in Example 5, instead of the PET film with a low refractive index layer of Production Example 13, the PET film with the low refractive index layer of Production Example 15 was used and the prism sheet substitute laminated PET film with a low refractive index layer was incorporated. Table 8 shows the results of producing and evaluating the film. Compared with the comparative example 5 used as a reference | standard, the brightness | luminance improved.
［比較製造例６］（低屈折率コーティング材γの作製）
製造例１４の有機無機複合体Ｄの代わりに、比較製造例３の有機無機複合体γを使用した以外は、製造例１４と同様の方法で、低屈折率コーティング材γを作製した。
[Comparative Production Example 6] (Preparation of low refractive index coating material γ)
A low refractive index coating material γ was produced in the same manner as in Production Example 14 except that the organic-inorganic composite γ of Comparative Production Example 3 was used instead of the organic-inorganic composite D of Production Example 14.
［比較製造例７］（低屈折率層付ＰＥＴフィルム）
製造例１５の低屈折率コーティング材Ｄの代わりに、比較製造例６の低屈折率コーティング材γを使用した以外は、製造例１５と同様の方法で、低屈折率層付ＰＥＴフィルムを作製し、評価した。屈折率は１．４９であった。
[Comparative Production Example 7] (PET film with low refractive index layer)
A PET film with a low refractive index layer was prepared in the same manner as in Production Example 15 except that the low refractive index coating material γ of Comparative Production Example 6 was used instead of the low refractive index coating material D of Production Example 15. ,evaluated. The refractive index was 1.49.
［比較例６］
製造例１５の低屈折率層付ＰＥＴフィルムの代わりに、比較製造例７の低屈折率層付ＰＥＴフィルムを使用した以外は、実施例６と同様の方法で、プリズムシート代替低屈折率層付ＰＥＴフィルム内蔵積層フィルムを作製し、評価した結果を表８に示す。基準となる比較例５と輝度は同等であり、輝度向上の効果は得られなかった。
[Comparative Example 6]
Instead of the PET film with a low refractive index layer of Production Example 15, the same method as in Example 6 was used, except that the PET film with a low refractive index layer of Comparative Production Example 7 was used. Table 8 shows the results of producing and evaluating a laminated film containing a PET film. The luminance was the same as that of Comparative Example 5 serving as a reference, and the effect of improving luminance was not obtained.
表３〜８に示される実験結果から、低屈折率の有機無機複合膜と、粘着層又は接着層を有する積層体を使用することで、透明性に優れる安価な積層体と、高品位の表示装置が提供できることがわかった。 From the experimental results shown in Tables 3 to 8, by using a laminate having a low refractive index organic-inorganic composite film and an adhesive layer or an adhesive layer, an inexpensive laminate excellent in transparency and a high-quality display It turns out that the device can provide.
本実施形態に係る、透過性に優れた安価な積層体は、例えば、表示装置及び光学材料として有用なものである。 The inexpensive laminate according to the present embodiment, which is excellent in transparency, is useful as a display device and an optical material, for example.
１０…液晶ディスプレイ、１１…反射フィルム、１２…導光板、１３…拡散シート、１４…プリズムシート、１５…偏光板、１６…粘着層、１７…位相差フィルム、１８…粘着層、１９…ガラス基板、２０…液晶層、２１…カラーフィルター、２２…ガラス基板、２３…粘着層、２４…位相差フィルム、２５…粘着層、２６…偏光板、３０…偏光板、３１…偏光板保護フィルム、３２…偏光子、３３…偏光板保護フィルム、４０…粘着層付偏光板、４１…セパレータ、４２…粘着層、４３…偏光板保護フィルム、４４…偏光子、４５…偏光板保護フィルム、５０Ａ，５０Ｂ…反射防止機能付偏光板、５１…セパレータ、５２…粘着層、５３…ハードコート層、５４…有機無機複合膜、６０…位相差フィルム付偏光板、６１…セパレータ、６２…粘着層、６３…位相差フィルム、６４…粘着層、７０…視覚補償フィルム付偏光板、７１…セパレータ、７２…粘着層、７３…ＷＶフィルム、７４…偏光子、７５…偏光板保護フィルム、７６…ハードコート層、７７…有機無機複合膜、８０…液晶セル、８１…第一の電極基板、８２…第一の透明電極、８３…液晶、８４…シール材、８６…第一の透明電極、８７…第一の電極基板、９０…液晶表示素子、９１…位相差フィルム、９２…液晶、９３…偏光子、９４…粘着層、９５…偏光板保護フィルム、９６…ハードコート層、９７…有機無機複合膜、９８…上側偏光板、１００…プリズムシート内蔵積層フィルム、１０１…ＰＥＴフィルム、１０２…プリズム、１０３…粘着層、１０４…有機無機複合膜、１０５…粘着層、１０６…反射型偏光板、１１０…プリズムシート代替低屈折率層付ＰＥＴフィルム内蔵積層フィルム、１１１…ＰＥＴフィルム、１１２…有機無機複合膜、１１３…粘着層、１１４…反射型偏光板、１２０…光学装置、１２１…冷陰極ランプ、１２２…光源、１２３…ＰＥＴフィルム、１２４…プリズム、１２５…粘着層、１２６…有機無機複合膜、１２７…粘着層、１２８…反射型偏光板、１３１…冷陰極管光源、１３２…光拡散板、１３３…サンプル、１３４…液晶セル後面偏光板、１３５…輝度計。 DESCRIPTION OF SYMBOLS 10 ... Liquid crystal display, 11 ... Reflective film, 12 ... Light guide plate, 13 ... Diffusion sheet, 14 ... Prism sheet, 15 ... Polarizing plate, 16 ... Adhesive layer, 17 ... Retardation film, 18 ... Adhesive layer, 19 ... Glass substrate 20 ... liquid crystal layer, 21 ... color filter, 22 ... glass substrate, 23 ... adhesive layer, 24 ... retardation film, 25 ... adhesive layer, 26 ... polarizing plate, 30 ... polarizing plate, 31 ... polarizing plate protective film, 32 DESCRIPTION OF SYMBOLS ... Polarizer, 33 ... Polarizing plate protective film, 40 ... Polarizing plate with adhesive layer, 41 ... Separator, 42 ... Adhesive layer, 43 ... Polarizing plate protective film, 44 ... Polarizer, 45 ... Polarizing plate protective film, 50A, 50B ... Polarizing plate with antireflection function, 51 ... Separator, 52 ... Adhesive layer, 53 ... Hard coat layer, 54 ... Organic-inorganic composite film, 60 ... Polarizing plate with retardation film, 61 ... Separator, 62 Adhesive layer, 63 ... retardation film, 64 ... adhesive layer, 70 ... polarizing plate with visual compensation film, 71 ... separator, 72 ... adhesive layer, 73 ... WV film, 74 ... polarizer, 75 ... polarizing plate protective film, 76 ... Hard coat layer, 77 ... Organic-inorganic composite film, 80 ... Liquid crystal cell, 81 ... First electrode substrate, 82 ... First transparent electrode, 83 ... Liquid crystal, 84 ... Sealing material, 86 ... First transparent electrode, 87 ... first electrode substrate, 90 ... liquid crystal display element, 91 ... retardation film, 92 ... liquid crystal, 93 ... polarizer, 94 ... adhesive layer, 95 ... polarizing plate protective film, 96 ... hard coat layer, 97 ... organic Inorganic composite film, 98 ... upper polarizing plate, 100 ... laminated prism film, 101 ... PET film, 102 ... prism, 103 ... adhesive layer, 104 ... organic inorganic composite film, 105 ... adhesive layer, 106 ... reflection Polarizing plate 110 ... Laminated prism film with low refractive index layer with prism sheet replacement, 111 ... PET film, 112 ... Organic-inorganic composite film, 113 ... Adhesive layer, 114 ... Reflective polarizing plate, 120 ... Optical device, 121 ... Cold cathode lamp, 122 ... light source, 123 ... PET film, 124 ... prism, 125 ... adhesive layer, 126 ... organic-inorganic composite film, 127 ... adhesive layer, 128 ... reflective polarizing plate, 131 ... cold cathode tube light source, 132 ... Light diffusing plate, 133 ... sample, 134 ... liquid crystal cell rear polarizing plate, 135 ... luminance meter.
Claims (28)
粘着剤又は接着剤を含有する接続層と、を有し、
前記有機無機複合膜中の空隙の割合が、前記有機無機複合膜の体積を基準として３〜９０体積％である、積層体。
A connection layer containing an adhesive or an adhesive, and
The laminated body whose ratio of the space | gap in the said organic inorganic composite film is 3-90 volume% on the basis of the volume of the said organic inorganic composite film.
Ｘ−Ｓｉ（Ｒ１）（Ｒ２）（Ｒ３） ・・・（式１）
［式中、Ｘは、前記有機ハロゲン化物基を含む重合開始基であり、Ｒ１及びＲ２は、それぞれ独立に、炭素原子数が１〜１０のアルキル基であり、Ｒ３は、炭素原子数が１〜１０のアルコキシ基、水素原子、水酸基又はハロゲン原子である。］ It said coupling agent has a structure represented by the following formula 1, the laminated body according to claim 1 or 2.
X-Si (R1) (R2) (R3) (Formula 1)
[ Wherein , X is a polymerization initiating group containing the organic halide group , R 1 and R 2 are each independently an alkyl group having 1 to 10 carbon atoms, and R 3 is 1 carbon atom. -10 alkoxy groups, hydrogen atoms, hydroxyl groups or halogen atoms. ]
前記支持体、前記有機無機複合膜及び前記接続層がこの順で積層した構成を有する、請求項１〜２１のいずれか１項に記載の積層体。 Further comprising a support,
The laminated body according to any one of claims 1 to 21, wherein the support, the organic-inorganic composite film, and the connection layer have a structure in which the support is laminated in this order.
前記有機無機複合膜及び前記接続層をそれぞれ２以上有し、
前記支持体、第一の前記有機無機複合膜、第一の前記接続層、第二の前記有機無機複合膜及び第二の前記接続層がこの順で積層した構成を有する、請求項１〜２２のいずれか一項に記載の積層体。 Further comprising a support,
Each having two or more of the organic-inorganic composite film and the connection layer;
The support, the first organic-inorganic composite film, the first connection layer, the second organic-inorganic composite film, and the second connection layer are stacked in this order. The laminate according to any one of the above.