JP5907416B2 - Method for producing hot work tool steel with excellent toughness - Google Patents
Method for producing hot work tool steel with excellent toughness Download PDFInfo
- Publication number
- JP5907416B2 JP5907416B2 JP2012041513A JP2012041513A JP5907416B2 JP 5907416 B2 JP5907416 B2 JP 5907416B2 JP 2012041513 A JP2012041513 A JP 2012041513A JP 2012041513 A JP2012041513 A JP 2012041513A JP 5907416 B2 JP5907416 B2 JP 5907416B2
- Authority
- JP
- Japan
- Prior art keywords
- steel
- less
- toughness
- hot
- tool steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、プレス金型や鍛造金型、ダイカスト金型、押出工具といった多種の熱間工具に供して最適な、靭性を向上させた熱間工具鋼の製造方法に関するものである。 The present invention relates to a method for producing hot tool steel with improved toughness that is optimal for use in various hot tools such as press dies, forging dies, die casting dies, and extrusion tools.
熱間工具は、高温の被加工材や硬質な被加工材と接触しながら使用されるため、熱疲労や衝撃に耐え得る強度と靭性を兼ね備えている必要がある。そのため、従来、熱間工具の分野で用いられる鋼種（以下、熱間工具鋼という。）には、例えばＪＩＳ鋼種であるＳＫＤ６１系の合金工具鋼が用いられていた。そして、熱間工具鋼を構成する主要元素の添加量を見直して、さらにＡｓ、Ｂｉ、Ｓｎ、Ｚｎ、Ｓｂ等の多種の不純物を規制管理したことで、熱間工具鋼の靭性を向上した手法が提案されている（特許文献１参照）。しかし、多種の不純物元素をそれぞれ規定された範囲内に調整することは、製造コストの向上に繋がり得る。 Since a hot tool is used while being in contact with a high-temperature work material or a hard work material, it must have both strength and toughness that can withstand thermal fatigue and impact. Therefore, conventionally, for example, SKD61-based alloy tool steel, which is a JIS steel type, has been used as a steel type used in the field of hot tools (hereinafter referred to as hot tool steel). And the method of improving the toughness of the hot tool steel by reviewing the addition amount of the main elements constituting the hot tool steel and further regulating and controlling various impurities such as As, Bi, Sn, Zn, Sb Has been proposed (see Patent Document 1). However, adjusting each of the various impurity elements within the specified range can lead to an increase in manufacturing cost.
これに対して、本発明者は、高価で特殊な元素の添加によらず、鉄鋼材料の分野では合金として積極的に添加されてこなかった元素について鋭意調査を行った結果、従来は不純物として扱われていたＺｎを所定の含有量の範囲に添加することによって靭性を大きく改善できることを見いだした（特許文献２参照）。すなわち、質量％で、Ｃ：０．３〜０．５５％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｃｒ：３．００〜５．６５％を含む熱間工具鋼であって、Ｚｎ：０．００１〜０．０１５％の熱間工具鋼である。 On the other hand, the present inventor has conducted intensive investigations on elements that have not been actively added as alloys in the field of steel materials, regardless of the addition of expensive and special elements. It has been found that the toughness can be greatly improved by adding Zn in a predetermined content range (see Patent Document 2). That is, hot work tool steel containing, in mass%, C: 0.3 to less than 0.55%, Si: 1.5% or less, Mn: 1.5% or less, Cr: 3.00 to 5.65% And it is hot tool steel of Zn: 0.001-0.015%.
特許文献２で提案したＺｎ添加の技術は、熱間工具鋼の靭性を向上する新たな手法として、有効である。そして、特許文献２の手法を利用することで、Ｚｎめっきされた鋼のスクラップをリサイクル原料として活用でき、環境負荷の軽減にも好適である。本発明者は、この積極的なＺｎ添加による靭性向上効果に着目して、他の不純物元素による靭性の劣化を補い得る可能性を検討した。これら不純物元素の許容量を適正に高めることができれば、今後排出量が増加すると予想されている不純物含有量の多い低級スクラップの使用率を増加させつつ、不純物除去にかかるエネルギー使用量を低減でき、熱間工具鋼の製造過程でおよぼす環境への負荷を更に低減できる。 The Zn-added technique proposed in Patent Document 2 is effective as a new technique for improving the toughness of hot tool steel. And by utilizing the method of patent document 2, the scrap of Zn-plated steel can be utilized as a recycling raw material, and it is suitable also for reduction of an environmental load. The inventor examined the possibility of compensating for the deterioration of toughness due to other impurity elements, paying attention to the effect of improving toughness by this positive Zn addition. If the permissible amount of these impurity elements can be increased appropriately, the amount of energy used for removing impurities can be reduced while increasing the usage rate of low scrap with a large impurity content, which is expected to increase in the future. It is possible to further reduce the environmental load in the manufacturing process of hot tool steel.
本発明の目的は、環境負荷の軽減が可能な靭性に優れた熱間工具鋼の製造方法を提供することである。 The objective of this invention is providing the manufacturing method of the hot tool steel excellent in the toughness which can reduce an environmental load.
本発明者は、熱間工具鋼に含まれる不純物元素の、靭性および環境に及ぼす影響を調べた。その結果、特にＰ（リン）は、熱間工具鋼の靭性を大きく下げる元素であり、かつ、除去にかかるエネルギーが大きく、そしてこれらの理由から低級スクラップの使用促進も停滞させる、環境への負荷が大きい元素である知見を得た。そこで、この環境負荷を下げるために、Ｐの許容量を上げても十分な靭性が維持できる手法を検討した。その結果、Ｐ含有量の増加による靭性の劣化は、該Ｐ含有量に対する適正量のＺｎ添加によって補えることを突きとめた。そして、この靭性の補完効果が十分に利用できる具体的なＰとＺｎの関係量とともに、該関係量を達成するのに適した成分調整の手法をも明確にできたことで、本発明に到達した。 The inventor examined the influence of impurity elements contained in hot tool steel on toughness and the environment. As a result, in particular, P (phosphorus) is an element that greatly reduces the toughness of hot tool steel, and the energy required for removal is large, and for these reasons, the use of low-grade scrap is also stagnant. The knowledge that is a large element was obtained. Therefore, in order to reduce this environmental load, a method that can maintain sufficient toughness even if the allowable amount of P is increased was examined. As a result, it has been found that the deterioration of toughness due to the increase in the P content can be compensated for by adding an appropriate amount of Zn to the P content. In addition to the specific relationship between P and Zn that can sufficiently utilize this toughness complementation effect, a component adjustment method suitable for achieving the relationship is also clarified, thereby achieving the present invention. did.
すなわち本発明は、靭性に優れた熱間工具鋼の製造方法であって、０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る第１工程と、前記の熱間工具鋼の成分組成の溶鋼にＺｎを添加する第２工程と、前記のＺｎを添加した溶鋼を鋳造して鋼塊を得る第３工程とからなり、前記の第２工程は、前記の第３工程の鋳造後の鋼塊の成分組成が、Ｚｎ：０．００２５超〜０．０２５質量％、Ｐ：０．００５質量％以上を含み、かつＺｎ／Ｐ：０．５超の熱間工具鋼となるように、Ｚｎを添加するものであることを特徴とする靭性に優れた熱間工具鋼の製造方法である。好ましくは、前記の第１工程で得た溶鋼の成分組成が、質量％で、Ｐ：０．０１％以上を含み、前記の第３工程の鋳造後の鋼塊の成分組成が、質量％で、Ｐ：０．０１％以上を含むものである。また、前記の鋼塊の成分組成は、質量％で、Ｃ：０．３〜０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｃｒ：３．０〜６．０％未満を含む熱間工具鋼であることが好ましい。また、必要に応じて、ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、あるいはさらにＶ：１．５％以下を含んでもよい。 That is, the present invention is a method for producing a hot tool steel having excellent toughness, and includes a first step of obtaining a molten steel having a component composition of hot tool steel containing P of 0.005% by mass or more, and the heat It consists of a second step of adding Zn to the molten steel having the component composition of the inter-tool steel, and a third step of obtaining the steel ingot by casting the molten steel to which the Zn is added. A hot tool in which the composition of the steel ingot after casting in three steps includes Zn: more than 0.0025 to 0.025 mass%, P: 0.005 mass% or more, and Zn / P: more than 0.5 It is a method for producing hot work tool steel excellent in toughness, characterized by adding Zn so as to become steel. Preferably, the component composition of the molten steel obtained in the first step is mass% and includes P: 0.01% or more, and the component composition of the steel ingot after casting in the third step is mass%. , P: contains 0.01% or more. In addition, the composition of the steel ingot is, by mass, C: 0.3 to less than 0.6%, Si: 1.5% or less, Mn: 1.5% or less, Cr: 3.0 to 6 It is preferable that the hot tool steel contains less than 0.0%. If necessary, Mo and W may be contained alone or in combination (Mo + 1 / 2W): 3.5% or less, or V: 1.5% or less.
前記の第３工程の鋳造後の鋼塊の、最も典型的な成分組成は、質量％で、Ｃ：０．３〜０．６％未満、Ｓｉ：１．５％以下、Ｍｎ：１．５％以下、Ｎｉ：１．５％以下（０％を含む）、Ｃｒ：３．０〜６．０％未満、ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、Ｖ：１．５％以下、Ｎｂ：０．３％以下（０％を含む）、Ｃｏ：５．０％以下（０％を含む）、Ｚｎ：０．００２５超〜０．０２５％、Ｐ：０．００５％以上であり、かつＺｎ／Ｐ：０．５超であって、残部Ｆｅおよび不可避的不純物からなる熱間工具鋼である。好ましくはＰ：０．０１％以上である。 The most typical component composition of the steel ingot after casting in the third step is mass%, C: 0.3 to less than 0.6%, Si: 1.5% or less, Mn: 1.5 % Or less, Ni: 1.5% or less (including 0%), Cr: 3.0 to less than 6.0%, Mo and W alone or in combination (Mo + 1 / 2W): 3.5% or less, V : 1.5% or less, Nb: 0.3% or less (including 0%), Co: 5.0% or less (including 0%), Zn: more than 0.0025 to 0.025%, P: 0 0.005% or more and Zn / P: more than 0.5, which is a hot tool steel composed of the remaining Fe and inevitable impurities. Preferably, P: 0.01% or more.
本発明によれば、不純物として熱間工具鋼に含まれるＰを極低値に管理しなくても、十分な靭性を維持できることから、低Ｐ化のためのエネルギー消費量を節約でき、環境への負荷を軽減できる。そして、十分な靭性を維持するためのＺｎ量は、本発明の添加手法によって、その的確な調整が可能である。以上をもって、本発明は、熱間工具鋼の靭性を飛躍的に改善することができ、多種多様な用途・環境に適用が可能な熱間工具鋼の実用化にとって有効な技術となる。 According to the present invention, since sufficient toughness can be maintained without managing P contained in hot tool steel as an impurity to an extremely low value, energy consumption for lowering P can be saved and the environment can be saved. Can reduce the load. And the amount of Zn for maintaining sufficient toughness can be accurately adjusted by the addition method of the present invention. As described above, the present invention can drastically improve the toughness of hot tool steel, and is an effective technique for the practical application of hot tool steel that can be applied to a wide variety of uses and environments.
本発明の大きな特徴は、熱間工具鋼の靭性を向上するために、従来は不純物として扱われていたＺｎを積極的に添加するところにある。そして、靭性を大きく下げる元素であるＰは、本発明の添加Ｚｎ量との関係を明確にしたことで、その含有を特定の範囲で許容するところにある。すなわち、熱間工具鋼に対しては、Ｚｎを合金元素として利用すれば、Ｐの含有量が多くなっても、その靭性向上の効果が発揮できることを見いだしたものである。そして、従来は極低減化が必要であったＰの含有量を本発明では多く許容できることから、原材料の選定においては、高級な低Ｐスクラップの使用量を削減でき、スクラップのリサイクルに好適である。さらに、精錬工程でのＰの除去に必要なエネルギーおよび時間も低減できる。以下、本発明の製造する熱間工具鋼の成分限定の理由について述べる（質量％については、単に％と表記する）。 A major feature of the present invention resides in positively adding Zn, which has been conventionally treated as an impurity, in order to improve the toughness of the hot work tool steel. And P which is an element which greatly reduces toughness is in a place where its inclusion is allowed in a specific range by clarifying the relationship with the amount of added Zn of the present invention. In other words, for hot tool steel, it has been found that if Zn is used as an alloy element, the effect of improving toughness can be exhibited even if the P content increases. In the present invention, a large amount of P, which has conventionally been required to be extremely reduced, can be tolerated. Therefore, in the selection of raw materials, the amount of high-grade low P scrap used can be reduced, which is suitable for scrap recycling. . Furthermore, the energy and time required for removing P in the refining process can be reduced. Hereinafter, the reason for limiting the components of the hot work tool steel manufactured according to the present invention will be described (mass% is simply expressed as%).
・Ｚｎ：０．００２５超〜０．０２５％
Ｚｎは、本発明にとって最も重要な添加元素であり、添加することによって靭性が顕著に向上する。そして、０．００２５％を超えて添加することで、本効果を十分に得ることができる。好ましくは０．００３％以上である。一方、多く添加してもその効果は頭打ちとなる。さらに、過度に添加することで粒界などに極端な偏析が生じると、これは返って靱性を劣化させる要因となり得る。また、添加技術も煩雑になるので、上限は０．０２５％とした。好ましくは０．０２０％以下、さらに好ましくは０．０１５％以下である。
Zn: more than 0.0025 to 0.025%
Zn is the most important additive element for the present invention, and the toughness is remarkably improved by adding Zn. And this effect can fully be acquired by adding exceeding 0.0025%. Preferably it is 0.003% or more. On the other hand, even if a large amount is added, the effect reaches a peak. Furthermore, if excessive segregation occurs at the grain boundary or the like due to excessive addition, this can be a factor that deteriorates toughness. Further, the addition technique becomes complicated, so the upper limit was made 0.025%. Preferably it is 0.020% or less, More preferably, it is 0.015% or less.
・Ｐ：０．００５％以上
Ｐは、焼戻しなどの熱処理時に旧オーステナイト粒界に偏析して粒界を脆化させる元素である。したがって、熱間工具鋼の靭性を向上するためには、通常できるだけ低く管理のされてきた不純物元素である。しかし、本発明では、上述のＺｎ添加による靭性向上効果を最大限に利用することで、Ｐによる靭性の劣化分を補うことができる。そして、このために必要なＺｎ添加の顕著な効果は、後述のＰ含有量に対するＺｎ添加量の調整によって得ることができる。これによって、本発明の熱間工具鋼は０．００５％以上のＰ含有量が許容できる。好ましくは０．０１％以上、さらに好ましくは０．０２％以上であっても、十分な靭性が維持できる。
P: 0.005% or more P is an element that segregates at the prior austenite grain boundaries during the heat treatment such as tempering and embrittles the grain boundaries. Therefore, in order to improve the toughness of hot tool steel, it is an impurity element that has been usually managed as low as possible. However, in the present invention, the toughness degradation effect due to P can be compensated for by making maximum use of the above-described toughness improving effect by the addition of Zn. And the remarkable effect of Zn addition required for this can be acquired by adjustment of Zn addition amount with respect to P content mentioned later. Thereby, the hot tool steel of the present invention can tolerate a P content of 0.005% or more. Even if it is preferably 0.01% or more, more preferably 0.02% or more, sufficient toughness can be maintained.
・Ｚｎ／Ｐ：０．５超
本発明の熱間工具鋼では、０．００５％以上のＰを含有した場合でも、十分な靭性を維持できるだけのＺｎ添加量を確保する必要がある。そのために、Ｐ含有量に対するＺｎ添加量の調整が必要である。具体的には、Ｚｎ／Ｐの値を０．５超とすることで、十分な靭性を確保することができる。好ましくはＺｎ／Ｐ：０．５５超である。なお、０．５５を超えるＺｎ／Ｐ値は、０．０１％以上のＰ、さらには０．０２％以上のＰを含有したときにも好ましい条件である。
-Zn / P: More than 0.5 Even when the hot tool steel of the present invention contains 0.005% or more of P, it is necessary to ensure a Zn addition amount sufficient to maintain sufficient toughness. Therefore, it is necessary to adjust the Zn addition amount with respect to the P content. Specifically, sufficient toughness can be ensured by setting the value of Zn / P to more than 0.5. Preferably it is more than Zn / P: 0.55. A Zn / P value exceeding 0.55 is a preferable condition even when 0.01% or more of P, further 0.02% or more of P is contained.
そして、上記のＰとＺｎの関係を満たした熱間工具鋼を溶解鋳造法で得る場合、これに適した成分調整の手法がある。つまり、種々の手法によって、鋳造時の溶鋼の成分組成を上記のＺｎを含んだものに調整しておけば、これを鋳造することで、本発明による熱間工具鋼の鋼塊が得られる。但し、金属Ｚｎは融点の低い揮発性元素であり、時間の経過とともに溶鋼から抜けていく。したがって、鋳造時の溶鋼で維持すべきＺｎ量に対しては、溶鋼に添加する時点のＺｎ量は、上記の抜け代を考慮して多めに設定することが有効である。しかし、溶鋼中のＺｎ量を制御して、鋳造時のそれを本発明の的確な値に調整するとなると、上記の抜け代を想定しただけの添加手法では再現性が低く、達成が困難である。そこで、本発明では、Ｚｎを他の添加元素と同じタイミングで調整するのではなくて、事前に熱間工具鋼の成分組成に調整して、Ｐ含有量の定まった溶鋼に添加するタイミングとすることで、その後の鋳造までの経過時間を短縮でき、Ｚｎの揮発等によるＺｎ／Ｐ比の変動を抑制することができる。 And when obtaining the hot tool steel which satisfy | filled the relationship of said P and Zn with a melt | dissolution casting method, there exists the method of a component adjustment suitable for this. That is, if the component composition of the molten steel at the time of casting is adjusted to the one containing Zn by various methods, the ingot of the hot tool steel according to the present invention can be obtained by casting this. However, metal Zn is a volatile element having a low melting point and escapes from the molten steel with time. Therefore, for the Zn amount to be maintained in the molten steel at the time of casting, it is effective to set a larger amount of Zn at the time of addition to the molten steel in consideration of the above allowance. However, if the amount of Zn in the molten steel is controlled to adjust it to the exact value of the present invention at the time of casting, it is difficult to achieve by the addition method only assuming the above-mentioned allowance. . Therefore, in the present invention, Zn is not adjusted at the same timing as other additive elements, but is adjusted in advance to the component composition of the hot tool steel and added to the molten steel with a fixed P content. Thus, the elapsed time until the subsequent casting can be shortened, and the fluctuation of the Zn / P ratio due to the volatilization of Zn or the like can be suppressed.
すなわち、具体的には、０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る第１工程と、前記の熱間工具鋼の成分組成の溶鋼にＺｎを添加する第２工程と、前記のＺｎを添加した溶鋼を鋳造して鋼塊を得る第３工程とからなる。そして、第２工程では、第３工程の鋳造後の鋼塊の成分組成が、Ｚｎ：０．００２５超〜０．０２５質量％、Ｐ：０．００５質量％以上を含み、かつＺｎ／Ｐ：０．５超の熱間工具鋼となるように、Ｚｎを添加する熱間工具鋼の製造方法である。前記の第３工程の鋳造後の鋼塊が含むＰは、好ましくは０．０１質量％以上、さらに好ましくは０．０２質量％以上である。以下、各工程について説明する。 Specifically, Zn is added to the first step of obtaining molten steel having a component composition of hot tool steel containing 0.005 mass% or more of P, and to the molten steel having the component composition of hot tool steel. It consists of a 2nd process and the 3rd process which casts the molten steel which added said Zn, and obtains a steel ingot. And in a 2nd process, the component composition of the steel ingot after the casting of a 3rd process contains Zn: more than 0.0025-0.025 mass%, P: 0.005 mass% or more, and Zn / P: This is a method for producing hot tool steel in which Zn is added so that the hot tool steel exceeds 0.5. P contained in the steel ingot after casting in the third step is preferably 0.01% by mass or more, more preferably 0.02% by mass or more. Hereinafter, each step will be described.
・第１工程：０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る工程である。
溶鋼の成分組成を熱間工具鋼のそれに整えておくことで、後述する第２工程を専らＺｎ含有量の調整に特化できる。そして、所定量のＺｎ添加後には、後述する第３工程の鋳造に速やかに移行することができるので、鋳造後の鋼塊のＺｎ含有量を的確に調整することが容易である。なお、本発明の第１工程の「熱間工具鋼の成分組成の溶鋼を得る」とは、後述の第２工程の前には、種々の成分組成に調整された熱間工具鋼の溶鋼の状態にする、という意味である。そして、このときの成分組成は、狙いとする鋼塊の成分組成に調整しておくことが好ましい。さらにこのとき、次のＺｎ添加で使用するＺｎ源の種類（成分組成）によっては、Ｚｎ添加の前後で成分組成が変動するのであれば、この変動代を加味しておくことが好ましい。したがって、溶鋼に施される合金添加などの処理に限るものではなく、例えば溶解前の原材料を準備する作業であってもよい。そして、溶解後には、介在物や不純物を除去する各種の精錬処理を施してもよいものである。なお、第１工程で得た溶鋼が含むＰの含有量は、好ましくは０．０１質量％以上、さらに好ましくは０．０２質量％以上である。
-1st process: It is the process of obtaining the molten steel of the component composition of the hot tool steel containing 0.005 mass% or more of P.
By adjusting the component composition of the molten steel to that of the hot work tool steel, the second step described later can be specialized in adjusting the Zn content exclusively. And since it can transfer to casting of the 3rd process mentioned later immediately after a predetermined amount of Zn addition, it is easy to adjust Zn content of the steel ingot after casting exactly. In the first step of the present invention, “to obtain molten steel having a component composition of hot tool steel” means that before the second step described later, the molten steel of hot tool steel adjusted to various component compositions is used. It means to make a state. And it is preferable to adjust the component composition at this time to the intended component composition of the steel ingot. Further, at this time, depending on the type (component composition) of the Zn source used in the next Zn addition, if the component composition fluctuates before and after the addition of Zn, it is preferable to take this fluctuation into account. Therefore, the process is not limited to alloy addition applied to molten steel, and may be an operation of preparing raw materials before melting, for example. And after melt | dissolution, you may give the various refining process which removes an inclusion and an impurity. In addition, content of P which the molten steel obtained at the 1st process contains becomes like this. Preferably it is 0.01 mass% or more, More preferably, it is 0.02 mass% or more.
・第２工程：第１工程による熱間工具鋼の溶鋼にＺｎを添加する工程である。
本発明では、Ｚｎを添加する第２工程を、上記の第１工程から別けて管理することが重要であることは、上述の通りである。予め熱間工具鋼の成分組成に整えられた溶鋼にＺｎを添加すれば、Ｐに対するＺｎ含有量の調整が容易であり、かつ、後述する第３工程の鋳造に速やかに移行することができる。なお、本発明の第２工程は、Ｚｎを添加する以外の、その他を目的とした処理を排除するものでない。よって、この時には、Ｚｎ以外の元素種について、狙いとする鋼塊の成分組成との間に若干の差があるのであれば、新たな精錬処理を行わない限りで、再度の微調整を行ってもよい。
-2nd process: It is the process of adding Zn to the molten steel of the hot tool steel by a 1st process.
In the present invention, as described above, it is important to manage the second step of adding Zn separately from the first step. If Zn is added to the molten steel that has been previously adjusted to the component composition of the hot tool steel, it is easy to adjust the Zn content with respect to P, and it is possible to quickly shift to casting in the third step described later. In addition, the 2nd process of this invention does not exclude the process for the purpose other than adding Zn. Therefore, at this time, if there is a slight difference between the elemental composition other than Zn and the component composition of the target steel ingot, fine adjustment is performed again unless a new refining treatment is performed. Also good.
・第３工程：第２工程による溶鋼を鋳造して鋼塊を得る工程である。
第１および第２の工程を経た溶鋼を鋳造して鋼塊を得ることで、本発明の成分組成を満たした熱間工具鋼が溶製される。そして、本発明の第３工程の鋳造は、普通造塊法に限らず、連続鋳造法や、その他の特殊造塊法であってもよい。
-3rd process: It is the process of casting the molten steel by a 2nd process, and obtaining a steel ingot.
By casting the molten steel that has undergone the first and second steps to obtain a steel ingot, hot tool steel that satisfies the component composition of the present invention is melted. The casting in the third step of the present invention is not limited to the ordinary ingot casting method, and may be a continuous casting method or other special ingot casting methods.
本発明のＺｎ添加による靭性向上効果は、組織中に炭化物が多く分布すると、これに大きく阻害されて弱くなる。つまり、上記の靭性向上効果は、通常、組織中に多くの炭化物が分布する冷間工具鋼よりも、炭化物が少ない熱間工具鋼で十分に発揮される。したがって、本発明の対象は、熱間工具鋼に限定する。熱間工具鋼は、例えばＪＩＳ−Ｇ−４４０４等に規定される成分組成の鋼をいう。そして、ＪＩＳ等の規格鋼種の他には、従来提案されてきた熱間工具鋼も適用できる。上記の熱間工具鋼に規定される以外の元素種も、必要に応じて添加が可能である。以下は、本発明の製造する熱間工具鋼の好ましい成分組成である。数値限定の理由について述べる。 The toughness improving effect of Zn addition according to the present invention is greatly inhibited and weakened when a large amount of carbide is distributed in the structure. That is, the above-described toughness improving effect is sufficiently exhibited by hot tool steel with less carbides than cold tool steel in which many carbides are distributed in the structure. Therefore, the object of the present invention is limited to hot tool steel. Hot tool steel refers to steel having a composition defined in, for example, JIS-G-4404. In addition to standard steel types such as JIS, conventionally proposed hot work tool steel can also be applied. Element types other than those defined in the above hot work tool steel can be added as necessary. The following are preferred component compositions of the hot work tool steel produced by the present invention. The reason for the numerical limitation will be described.
・Ｃ：０．３〜０．６％未満
Ｃは、一部が基地中に固溶して強度を付与し、一部は炭化物を形成することで耐摩耗性や耐焼付き性を高める元素である。また、固溶した侵入型原子であるＣは、ＣｒなどのＣと親和性の大きい置換型原子と共添加した場合、Ｉ（侵入型原子）−Ｓ（置換型原子）効果；溶質原子の引きずり抵抗として作用し、鋼を高強度化する作用も期待される。但し、過度の添加は、靭性や熱間強度の低下を招く。よって、０．３〜０．６％未満とすることが好ましい。より好ましくは、０．５５％未満である。
C: Less than 0.3 to 0.6% C is an element that increases the wear resistance and seizure resistance by partly forming a solid solution in the base to give strength and partly forming carbide. is there. Further, when C, which is a solid interstitial atom, is co-added with a substitution atom having a high affinity with C, such as Cr, the I (interstitial atom) -S (substitution atom) effect; solute atom dragging It acts as a resistance and is also expected to increase the strength of steel. However, excessive addition causes a decrease in toughness and hot strength. Therefore, it is preferable to set it as 0.3 to less than 0.6%. More preferably, it is less than 0.55%.
・Ｓｉ：１．５％以下
Ｓｉは、製鋼時の脱酸剤であるとともに、素材の被削性を高める元素である。これらの効果を得るためには０．２％未満の添加でもよいが、０．２％以上の添加が好ましい。但し、多過ぎるとフェライトの生成をまねくので、好ましくは１．５％以下である。
Si: 1.5% or less Si is a deoxidizing agent during steel making and an element that enhances the machinability of the material. In order to obtain these effects, addition of less than 0.2% may be performed, but addition of 0.2% or more is preferable. However, since it will lead to the formation of ferrite if too much, it is preferably 1.5% or less.
・Ｍｎ：１．５％以下
Ｍｎは、焼入性を高め、フェライトの生成を抑制し、適度の焼入れ焼戻し硬さを得る効果がある。また、非金属介在物のＭｎＳとして存在することで、被削性の向上に大きな効果がある。これらの効果を得るためには０．１％未満の添加でもよいが、０．１％以上の添加が好ましい。但し、多過ぎると基地の粘さを上げて被削性を低下させるので、好ましくは１．５％以下とする。
-Mn: 1.5% or less Mn has the effect of improving hardenability, suppressing the formation of ferrite, and obtaining appropriate quenching and tempering hardness. Moreover, since it exists as MnS of a nonmetallic inclusion, there is a great effect in improving machinability. In order to obtain these effects, addition of less than 0.1% may be performed, but addition of 0.1% or more is preferable. However, if it is too much, the viscosity of the base is increased and the machinability is lowered, so the content is preferably 1.5% or less.
・Ｃｒ：３．０〜６．０％未満
Ｃｒは、焼入性を高め、また炭化物を形成して、基地の強化や耐摩耗性の向上に効果を有する元素である。そして、焼戻し軟化抵抗および高温強度の向上にも寄与する元素である。但し、過度の添加は、焼入性や高温強度の低下を招く。よって、３．０〜６．０％未満が好ましい。より好ましくは、５．６５％以下である。
Cr: 3.0 to less than 6.0% Cr is an element that enhances hardenability and forms carbides and has an effect on strengthening the base and improving wear resistance. And it is an element which contributes also to the improvement of temper softening resistance and high temperature strength. However, excessive addition causes a decrease in hardenability and high temperature strength. Therefore, 3.0 to less than 6.0% is preferable. More preferably, it is 5.65% or less.
・ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下
ＭｏおよびＷは、焼戻しにより微細炭化物を析出または凝集させて強度を付与し、軟化抵抗を向上させるために単独または複合で添加できる。この際の添加量は、ＷがＭｏの約２倍の原子量であることから、（Ｍｏ＋１／２Ｗ）のＭｏ当量で一緒に規定できる（当然、いずれか一方のみの添加としても良いし、双方を共に添加することもできる）。そして、前記した効果を得るためには、（Ｍｏ＋１／２Ｗ）の値で１．０％未満の添加でもよいが、１．０％以上の添加が好ましい。但し、多過ぎると被削性や靭性の低下を招くので、（Ｍｏ＋１／２Ｗ）の値で３．５％以下が好ましい。
Mo and W are single or composite (Mo + 1 / 2W): 3.5% or less Mo and W are single or composite for precipitating or agglomerating fine carbides by tempering to give strength and improving softening resistance. Can be added. The amount of addition at this time can be defined together with the Mo equivalent of (Mo + 1 / 2W) since W is about twice the atomic weight of Mo (of course, either one or both may be added) Can be added together). And in order to acquire an above-described effect, although addition of less than 1.0% may be sufficient as the value of (Mo + 1 / 2W), addition of 1.0% or more is preferable. However, since it will lead to a decrease in machinability and toughness if it is too much, the value of (Mo + 1 / 2W) is preferably 3.5% or less.
・Ｖ：１．５％以下
Ｖは、炭化物を形成し、基地の強化や耐摩耗性を向上する効果を有する。また、焼戻し軟化抵抗を高めるとともに、結晶粒の粗大化を抑制し、靭性の向上に寄与する。これらの効果を得るためには０．５％未満の添加でもよいが、０．５％以上の添加が好ましい。但し、多過ぎると被削性や靭性の低下を招くので、１．５％以下とするのが好ましい。
V: 1.5% or less V has the effect of forming carbides and improving base strengthening and wear resistance. In addition, the temper softening resistance is increased and the coarsening of crystal grains is suppressed, thereby contributing to the improvement of toughness. In order to obtain these effects, addition of less than 0.5% may be performed, but addition of 0.5% or more is preferable. However, since too much will lead to a decrease in machinability and toughness, it is preferably made 1.5% or less.
・Ｎｉ：１．５％以下
Ｎｉは、フェライトの生成を抑制する元素である。また、Ｃ、Ｃｒ、Ｍｎ、Ｍｏ、Ｗなどとともに、熱間工具鋼に優れた焼入性を付与し、焼入時の冷却速度が緩やかな場合でもマルテンサイト主体の組織を形成して、靭性の低下を防ぐための効果的元素である。さらに、基地の本質的な靭性も改善するので、本発明では必要に応じて添加する。但し、多過ぎると基地の粘さを上げて被削性が低下する。よって、添加する場合でも１．５％以下とすることが好ましい。なお、添加する場合は０．１％以上が好ましい。
Ni: 1.5% or less Ni is an element that suppresses the formation of ferrite. Also, together with C, Cr, Mn, Mo, W, etc., it imparts excellent hardenability to hot tool steel and forms a martensite-based structure even when the cooling rate during quenching is slow, resulting in toughness It is an effective element for preventing a decrease in the amount. Furthermore, since the essential toughness of the base is also improved, it is added as necessary in the present invention. However, if it is too much, the base becomes thicker and the machinability decreases. Therefore, even when it is added, the content is preferably 1.5% or less. In addition, when adding, 0.1% or more is preferable.
・Ｎｂ：０．３％以下
Ｎｂは、炭化物を形成し、基地の強化や耐摩耗性を向上する効果を有する。また、焼戻し軟化抵抗を高めるとともに、結晶粒の粗大化を抑制し、靭性の向上に寄与するので、本発明では必要に応じて添加する。但し、多過ぎると被削性や靭性の低下を招く。よって、添加する場合でも０．３％以下とするのが好ましい。添加する場合は０．０５％以上が好ましい。
-Nb: 0.3% or less Nb has the effect of forming a carbide | carbonized_material and improving the reinforcement | strengthening of a base and abrasion resistance. In addition, the temper softening resistance is increased and the coarsening of the crystal grains is suppressed to contribute to the improvement of toughness. Therefore, in the present invention, it is added as necessary. However, if too much, machinability and toughness are reduced. Therefore, even when it is added, the content is preferably 0.3% or less. When adding, 0.05% or more is preferable.
・Ｃｏ：５．０％以下
Ｃｏは、本発明による熱間工具鋼を工具として使用中、その昇温時の表面に極めて緻密で密着性の良い保護酸化皮膜を形成する。この酸化皮膜は、相手材との間の金属接触を防ぎ、工具表面の温度上昇を抑制するとともに、優れた耐摩耗性をもたらす。よって、本発明では必要に応じて添加する。但し、多過ぎると靭性を低下させるので、添加する場合でも５．０％以下とするのが好ましい。添加する場合は０．３％以上が好ましい。
Co: 5.0% or less Co forms a protective oxide film that is extremely dense and has good adhesion on the surface when the hot tool steel according to the present invention is used as a tool. This oxide film prevents metal contact with the counterpart material, suppresses temperature rise on the tool surface, and provides excellent wear resistance. Therefore, in this invention, it adds as needed. However, if it is too much, the toughness is lowered, so even if it is added, it is preferably 5.0% or less. When adding, 0.3% or more is preferable.
不可避的不純物として鋼中に残留する可能性のある主な元素は、Ｓ、Ｃｕ、Ａｌ、Ｃａ、Ｍｇ、Ｏ（酸素）、Ｎ（窒素）等である。本発明のＺｎ添加による作用効果を効果的に得るためには、これらの元素はできるだけ低い方が好ましい。しかし一方で、介在物の形態制御や、その他の機械的特性、そして製造効率の向上といった付加的な作用効果を得るためには、多少の含有および／または添加をすることができる。この場合、Ｓ≦０．０１％、Ｃｕ≦０．２５％、Ａｌ≦０．０２５％、Ｃａ≦０．０１％、Ｍｇ≦０．０１％、Ｏ≦０．０１％、Ｎ≦０．０３％の範囲であれば十分に許容でき、本発明の好ましい規制上限である。 The main elements that may remain in the steel as inevitable impurities are S, Cu, Al, Ca, Mg, O (oxygen), N (nitrogen), and the like. In order to effectively obtain the effects of the addition of Zn of the present invention, these elements are preferably as low as possible. However, on the other hand, in order to obtain additional functions and effects such as control of the shape of inclusions, other mechanical properties, and improvement in production efficiency, some inclusions and / or additions can be made. In this case, S ≦ 0.01%, Cu ≦ 0.25%, Al ≦ 0.025%, Ca ≦ 0.01%, Mg ≦ 0.01%, O ≦ 0.01%, N ≦ 0.03 % Range is sufficiently acceptable and is the preferred upper limit of regulation of the present invention.
本発明に係る熱間工具鋼は、Ｚｎ添加による靭性向上効果を十分に発揮するための一形態として、例えば、鋳造後の鋼塊を加工して鋼材に仕上げる間に均質化熱処理を施すことが好ましい。あるいはさらに、焼入れ焼戻し硬さは５０ＨＲＣ以下とすることが好ましい。より好ましくは４８ＨＲＣ以下である。 The hot tool steel according to the present invention may be subjected to a homogenization heat treatment while processing a steel ingot after casting into a steel material, for example, as a form for sufficiently exerting the toughness improving effect by addition of Zn. preferable. Alternatively, the quenching and tempering hardness is preferably 50 HRC or less. More preferably, it is 48 HRC or less.
真空誘導溶解炉によって、まず０．００５質量％以上のＰを含有する熱間工具鋼の成分組成に調整した溶鋼を維持した。このときの成分組成は、次のＺｎ添加（つまり、Ｚｎ源の投入）を行った後で、狙いとする鋼塊の成分組成になるように調整した。そして、Ｚｎめっき鋼板をＺｎ源に用いて、この溶鋼にＺｎを添加して、鋳造し、７〜１０ｋｇの鋼塊を作製した。表１に鋳造後の鋼塊の成分組成を示す。Ｚｎ含有量は蛍光Ｘ線分析で測定した。本発明鋼は、一般的に使用されている熱間工具鋼ＪＩＳ−ＳＫＤ６１（Ｐ規格：０．０３０％以下）の成分組成に、本発明のＺｎ／Ｐ比を満たすようＺｎを添加して、Ｐの含有量を多く許容したものである。なお、全ての鋼塊において、Ｓ、Ｃｕ、Ａｌ、Ｃａ、Ｍｇ、Ｏ、Ｎは無添加であり（但し、Ａｌは溶解工程における脱酸剤として添加した場合を含む。）、Ｓ≦０．０１％、Ｃｕ≦０．２５％、Ａｌ≦０．０２５％、Ｃａ≦０．０１％、Ｍｇ≦０．０１％、Ｏ≦０．０１％、Ｎ≦０．０３％であった。そして、鋳造前にＺｎを添加した本発明鋼のＰおよびＺｎの含有量は、所定の関係に的確に調整することができた。これに対して、上記の真空誘導溶解の初期にＺｎを添加した場合、Ｚｎが蒸発し、鋳造前の溶鋼中には所定量のＺｎを維持できなった。 The molten steel adjusted to the component composition of the hot tool steel containing 0.005 mass% or more of P was first maintained with the vacuum induction melting furnace. The component composition at this time was adjusted so that it might become the target component composition of the steel ingot after the next Zn addition (that is, injection of Zn source). Then, using a Zn-plated steel sheet as a Zn source, Zn was added to the molten steel and cast to produce a steel ingot of 7 to 10 kg. Table 1 shows the composition of the steel ingot after casting. Zn content was measured by fluorescent X-ray analysis. The steel of the present invention is made by adding Zn so as to satisfy the Zn / P ratio of the present invention to the component composition of the commonly used hot work tool steel JIS-SKD61 (P standard: 0.030% or less), A large amount of P is allowed. In all the steel ingots, S, Cu, Al, Ca, Mg, O, and N are not added (including the case where Al is added as a deoxidizer in the melting step), and S ≦ 0. The results were 01%, Cu ≦ 0.25%, Al ≦ 0.025%, Ca ≦ 0.01%, Mg ≦ 0.01%, O ≦ 0.01%, and N ≦ 0.03%. And the content of P and Zn in the steel of the present invention to which Zn was added before casting could be accurately adjusted to a predetermined relationship. On the other hand, when Zn was added at the initial stage of the above-described vacuum induction melting, Zn evaporated, and a predetermined amount of Zn could not be maintained in the molten steel before casting.
上記の一方では、本発明のＺｎ添加による効果を説明するために、表１の比較例１〜６も準備した。これらの比較鋼は、もとよりＺｎを添加せずに（比較鋼６を除く）、ＳＫＤ６１のＰの含有量のみを増加したものである。そして、Ｓ、Ｃｕ、Ａｌ、Ｃａ、Ｍｇ、Ｏ、Ｎは無添加であり（但し、Ａｌは溶解工程における脱酸剤として添加した場合を含む。）、Ｓ≦０．０１％、Ｃｕ≦０．２５％、Ａｌ≦０．０２５％、Ｃａ≦０．０１％、Ｍｇ≦０．０１％、Ｏ≦０．０１％、Ｎ≦０．０３％であった。 On the other hand, Comparative Examples 1 to 6 in Table 1 were also prepared in order to explain the effect of the addition of Zn of the present invention. These comparative steels are obtained by increasing only the P content of SKD61 without adding Zn (except comparative steel 6). And S, Cu, Al, Ca, Mg, O, and N are not added (however, including the case where Al is added as a deoxidizing agent in the dissolving step), S ≦ 0.01%, Cu ≦ 0 .25%, Al ≦ 0.025%, Ca ≦ 0.01%, Mg ≦ 0.01%, O ≦ 0.01%, and N ≦ 0.03%.
これらの鋼塊に１２５０℃で５時間の均質化熱処理を施した後、１１５０℃で熱間鍛造して２０ｍｍ厚さ×６０ｍｍ幅×約５００〜８００ｍｍ長さの鋼材を作製した。そして、８６０℃で焼なまし処理したのち、下記の評価に用いるシャルピー衝撃試験片のサイズに加工して、１０３０℃から油焼入れ処理し、種々の温度で焼戻し処理して、それぞれの調質硬さにおける靭性の評価試料とした。 These steel ingots were subjected to a homogenization heat treatment at 1250 ° C. for 5 hours, and then hot forged at 1150 ° C. to produce a steel material having a thickness of 20 mm × 60 mm width × about 500 to 800 mm. Then, after annealing at 860 ° C., it is processed into the size of Charpy impact test piece used for the following evaluation, oil quenching from 1030 ° C., and tempering at various temperatures. The toughness evaluation sample was used.
［試験１］
本発明鋼１、３、５〜７および比較鋼１、３〜６について、それぞれの硬さにおける室温での２ｍｍＵノッチシャルピー衝撃試験の結果を図１に示す。シャルピー試験片は、ＡＳＴＭ Ｅ３９９−９０に準拠したＴ−Ｌ方向とした。それぞれ同水準のＰを含んだ本発明鋼１、３および比較鋼１と、本発明鋼５および比較鋼３、そして本発明鋼６、７および比較鋼４の組合せにおいて、本発明のＺｎ／Ｐ比を満たすようにＺｎを添加した本発明鋼１、３、５〜７は、Ｚｎを添加しなかった比較鋼１、３、４に比べて、シャルピー衝撃値が優れている。しかも、本発明鋼６は、０．０２％を超える高濃度のＰを含有しているにもかかわらず、Ｚｎを添加したことで、Ｐが０．０１％未満の比較鋼１と同レベルの靭性を維持している。比較鋼６は、同水準のＰを含む比較鋼５にＺｎを添加したものであるが、本発明のＺｎ／Ｐを満たさず、靭性の向上が見られない。
[Test 1]
FIG. 1 shows the results of a 2 mm U notch Charpy impact test at room temperature for each of the present invention steels 1, 3, 5 to 7 and comparative steels 1 and 3 to 6. The Charpy test piece was in the TL direction in accordance with ASTM E399-90. In the combination of the inventive steels 1, 3 and comparative steel 1 containing the same level of P, the inventive steel 5 and comparative steel 3, and the inventive steels 6, 7 and comparative steel 4, the Zn / P of the invention Inventive steels 1, 3, and 5-7 added with Zn so as to satisfy the ratio are superior in Charpy impact value compared to comparative steels 1, 3, and 4 that did not contain Zn. Moreover, although the steel 6 of the present invention contains Zn at a high concentration exceeding 0.02%, the addition of Zn results in the same level as the comparative steel 1 having a P of less than 0.01%. Maintains toughness. The comparative steel 6 is obtained by adding Zn to the comparative steel 5 containing the same level of P, but does not satisfy the Zn / P of the present invention, and no improvement in toughness is observed.
［試験２］
本発明鋼２、４〜７および比較鋼２〜６について、４５ＨＲＣの硬さに調質したときの、室温から４００℃の間での２ｍｍＶノッチシャルピー衝撃試験の結果を図２に示す。シャルピー試験片は、ＡＳＴＭ Ｅ３９９−９０に準拠したＴ−Ｌ方向とした。それぞれ同水準のＰを含んだ本発明鋼２、４および比較鋼２と、本発明鋼５および比較鋼３、そして本発明鋼６、７および比較鋼４の組合せにおいて、本発明のＺｎ／Ｐ比を満たすようにＺｎを添加した本発明鋼２、４〜７は、いずれの試験温度でも、同水準のＰを含んだ比較鋼２〜４に比べて、シャルピー衝撃値が優れている。そして、０．０２％を超える高濃度のＰを含有しながらも、Ｚｎを添加したことで本発明のＺｎ／Ｐを満足した本発明鋼６は、Ｐが０．０１％未満の比較鋼２と同レベルの靭性を維持している。
[Test 2]
FIG. 2 shows the results of a 2 mmV notch Charpy impact test between room temperature and 400 ° C. when the steels of the present invention 2, 4 to 7 and comparative steels 2 to 6 were tempered to a hardness of 45 HRC. The Charpy test piece was in the TL direction in accordance with ASTM E399-90. In the combination of the present invention steels 2, 4 and comparative steel 2 containing the same level of P, the present invention steel 5 and comparative steel 3, and the present invention steels 6, 7 and comparative steel 4, the Zn / P of the present invention Inventive steels 2, 4 to 7 to which Zn is added so as to satisfy the ratio are superior in Charpy impact value compared to comparative steels 2 to 4 containing P at the same level at any test temperature. And this invention steel 6 which satisfied Zn / P of this invention by adding Zn while containing P with a high density | concentration exceeding 0.02% is comparative steel 2 with P less than 0.01%. Maintains the same level of toughness.
実施例１に記載した方法と同様の方法で、表２の成分組成を有する鋼塊を作製した。本発明鋼Ａは、熱間工具鋼の成分組成に、本発明のＺｎ／Ｐ比を満たすようＺｎを添加したものである。そして、比較鋼Ｂは、Ｚｎを添加しなかった以外は、本発明鋼Ａに同等の成分組成としたものである。なお、両方の鋼塊において、Ｓ、Ｃｕ、Ａｌ、Ｃａ、Ｍｇ、Ｏ、Ｎは無添加であり（但し、Ａｌは溶解工程における脱酸剤として添加した。）、Ｓ≦０．０１％、Ｃｕ≦０．２５％、Ａｌ≦０．０２５％、Ｃａ≦０．０１％、Ｍｇ≦０．０１％、Ｏ≦０．０１％、Ｎ≦０．０３％であった。 A steel ingot having the component composition shown in Table 2 was produced in the same manner as described in Example 1. Invention steel A is obtained by adding Zn to the component composition of hot work tool steel so as to satisfy the Zn / P ratio of the present invention. And the comparison steel B is set as the component composition equivalent to this invention steel A except not adding Zn. In both steel ingots, S, Cu, Al, Ca, Mg, O, and N were not added (however, Al was added as a deoxidizer in the melting step), S ≦ 0.01%, Cu ≦ 0.25%, Al ≦ 0.025%, Ca ≦ 0.01%, Mg ≦ 0.01%, O ≦ 0.01%, and N ≦ 0.03%.
次に、これらの鋼塊に実施例１と同様の熱間鍛造および各種の熱処理を行って、それぞれの硬さに調質したシャルピー衝撃試験片を作製した。そして、実施例１で実施したシャルピー衝撃試験１、２を実施して、それぞれの試料の靭性を評価した。 Next, these steel ingots were subjected to the same hot forging and various heat treatments as in Example 1 to prepare Charpy impact test pieces conditioned to the respective hardness. And the Charpy impact tests 1 and 2 implemented in Example 1 were implemented, and the toughness of each sample was evaluated.
［試験１］
本発明鋼Ａおよび比較鋼Ｂについて、それぞれの硬さにおける室温での２ｍｍＵノッチシャルピー衝撃試験の結果を図３に示す。シャルピー試験片は、ＡＳＴＭ Ｅ３９９−９０に準拠したＬ−Ｓ方向とした。これらの鋼は、Ｎｉが添加されていることで、もとより靭性の高いものである。そして、この上に、本発明のＺｎ／Ｐ比を満たすようにＺｎを添加した本発明鋼Ａは、Ｚｎを添加しなかった比較鋼Ｂに比べて、シャルピー衝撃値が優れている。
[Test 1]
FIG. 3 shows the results of the 2 mm U-notch Charpy impact test at room temperature for the steel A of the present invention and the comparative steel B. The Charpy test piece was in the LS direction in accordance with ASTM E399-90. These steels have high toughness due to the addition of Ni. And this invention steel A which added Zn so that the Zn / P ratio of this invention may be satisfy | filled on this is excellent in the Charpy impact value compared with the comparative steel B which did not add Zn.
［試験２］
本発明鋼Ａおよび比較鋼Ｂについて、４５ＨＲＣの硬さに調質したときの、室温から４００℃の間での２ｍｍＶノッチシャルピー衝撃試験の結果を図４に示す。シャルピー試験片は、ＡＳＴＭ Ｅ３９９−９０に準拠したＬ−Ｓ方向とした。もとより靭性の高い両方の鋼において、さらに本発明のＺｎ／Ｐ比を満たすようにＺｎを添加した本発明鋼Ａは、いずれの試験温度でも、Ｚｎを添加しなかった比較鋼Ｂに比べて、シャルピー衝撃値が優れている。
[Test 2]
FIG. 4 shows the result of a 2 mmV notch Charpy impact test between room temperature and 400 ° C. when the steel A of the present invention and the comparative steel B were tempered to a hardness of 45 HRC. The Charpy test piece was in the LS direction in accordance with ASTM E399-90. The steel A of the present invention in which Zn was added so as to satisfy the Zn / P ratio of the present invention in both steels having higher toughness as compared with the comparative steel B in which Zn was not added at any test temperature, Excellent Charpy impact value.
Claims (3)
０．００５質量％以上のＰを含有する熱間工具鋼の成分組成の溶鋼を得る第１工程と、
前記の熱間工具鋼の成分組成の溶鋼にＺｎを添加する第２工程と、
前記のＺｎを添加した溶鋼を鋳造して鋼塊を得る第３工程とからなり、
前記の第２工程は、前記の第３工程の鋳造後の鋼塊の成分組成が、Ｚｎ：０．００２５超〜０．０２５質量％、Ｐ：０．００５質量％以上を含み、かつＺｎ／Ｐ：０．５超の熱間工具鋼となるように、Ｚｎを添加するものであり、
前記の第３工程の鋳造後の鋼塊の成分組成が、質量％で、
Ｃ：０．３〜０．６％未満、
Ｓｉ：１．５％以下、
Ｍｎ：１．５％以下、
Ｎｉ：１．５％以下（０％を含む）、
Ｃｒ：３．０〜６．０％未満、
ＭｏおよびＷは単独または複合で（Ｍｏ＋１／２Ｗ）：３．５％以下、
Ｖ：１．５％以下、
Ｎｂ：０．３％以下（０％を含む）、
Ｃｏ：５．０％以下（０％を含む）、
Ｚｎ：０．００２５超〜０．０２５％、
Ｐ：０．００５％以上であり、
かつＺｎ／Ｐ：０．５超であって、
残部Ｆｅおよび不可避的不純物からなる熱間工具鋼であることを特徴とする靭性に優れた熱間工具鋼の製造方法。 A method for producing hot work tool steel with excellent toughness,
A first step of obtaining a molten steel having a component composition of hot tool steel containing 0.005 mass% or more of P;
A second step of adding Zn to the molten steel having the component composition of the hot tool steel;
It consists of a third step of casting the molten steel added with Zn to obtain a steel ingot,
In the second step, the composition of the steel ingot after casting in the third step includes Zn: more than 0.0025 to 0.025 mass%, P: 0.005 mass% or more, and Zn / P: as a 0.5 greater than hot work tool steels state, and are not adding Zn,
The component composition of the steel ingot after casting in the third step is mass%,
C: 0.3 to less than 0.6%,
Si: 1.5% or less,
Mn: 1.5% or less,
Ni: 1.5% or less (including 0%),
Cr: 3.0 to less than 6.0%,
Mo and W are single or composite (Mo + 1 / 2W): 3.5% or less,
V: 1.5% or less,
Nb: 0.3% or less (including 0%),
Co: 5.0% or less (including 0%),
Zn: more than 0.0025 to 0.025%,
P: 0.005% or more,
And Zn / P: more than 0.5,
Remainder Fe and manufacturing method of toughness excellent hot work tool steels Oh wherein Rukoto with unavoidable hot work tool steel consisting of impurities.