JP5898203B2 - ガラス板 - Google Patents
ガラス板 Download PDFInfo
- Publication number
- JP5898203B2 JP5898203B2 JP2013527668A JP2013527668A JP5898203B2 JP 5898203 B2 JP5898203 B2 JP 5898203B2 JP 2013527668 A JP2013527668 A JP 2013527668A JP 2013527668 A JP2013527668 A JP 2013527668A JP 5898203 B2 JP5898203 B2 JP 5898203B2
- Authority
- JP
- Japan
- Prior art keywords
- glass plate
- glass
- stress
- thickness
- mpa
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
SiO2 55−72%、特には60−71%
Al2O3 2−15%、特には3−12%
Na2O 9−17%、特には10−15%
K2O 0−12%、特には1−10%
MgO 2−13%、特には4−12%
CaO 0−2%、特には0−1%
B2O3 0−1%、特には0%
で含むものである。
SiO2 52−75%、特には65−70%
Al2O3 15−27%、特には18−19.8%
Li2O 2−10%、特には2.5−3.8%
K2O 0−5%、特には0−1%
Na2O 0−5%、特には0−1%
ZnO 0−5%、特には1.2−2.8%
MgO 0−5%、特には0.55−1.5%
BaO 0−5%、特には0−1.4%
SrO 0−3%、特には0−1.4%
TiO2 0−6%、特には1.8−3.2%
ZrO2 0−3%、特には1.0−2.5%
P2O5 0−8%
で含むものである。
SiO2 60−75%
Al2O3 0−4%
Na2O 9−18%
K2O 0−5%
MgO 0−10%
CaO 4−15%
で含むものであってもよい。
− 保護ガラス、表示ウィンドウ、スクリーン又は透明又は不透明装飾要素として、本発明に係る少なくとも1枚のガラス板を含む、電子デバイス、詳細には小型又は携帯デバイス、例えば詳細にはスマートホン、携帯情報端末、デジタルカメラ、マルチメディアプレーヤー、コンピュータ、タブレット、テレビ。
− 本発明に係る少なくとも1枚のガラス板を含む、太陽センサー、熱センサー又は光起電センサー。
SiO2 62%
Al2O3 8%
Na2O 12.5%
K2O 9%
MgO 7.5%
CaO 0.5%。
本発明の実施形態としては、以下の実施形態を挙げることができる。
(付記1)厚みが多くとも2mmで、圧縮下の表面ゾーンと張力下の中央ゾーンを有し、圧縮と張力の間の遷移が発生する深さが少なくとも100μmであり、前記深さと前記厚みの間の比が少なくとも0.1であるガラス板であって、さらに、60Nの荷重の下でのビッカース押込み後、三脚上リング(ring−on−tripod)曲げ試験における破壊時曲げ応力が少なくとも70MPaである、ガラス板。
(付記2)圧縮下の表面ゾーンがイオン交換によって得られた、付記1に記載のガラス板。
(付記3)厚みが多くとも1.1mmでかつ少なくとも0.25mmである、付記1又は2に記載のガラス板。
(付記4)圧縮と張力の間の遷移が発生する深さが少なくとも200μmでかつ多くとも500μmである、付記1〜3のいずれか1項に記載のガラス板。
(付記5)ガラス板の厚み内の応力プロファイルは、最大圧縮応力が少なくとも70MPaとなるものであり、この最大圧縮応力を受けるゾーンが、ガラス板の表面からゼロでない距離のところにある、付記1〜4のいずれか1項に記載のガラス板。
(付記6)ガラス板の厚み内の応力プロファイルは、ガラスの厚みの3分の1を占める中央ゾーン内で、引張応力の強さの相対的変動が少なくとも10%となるものである、付記1〜5のいずれか1項に記載のガラス板。
(付記7)圧縮と張力の間の遷移が発生する深さと厚みの間の比が、少なくとも0.2でかつ多くとも0.4である、付記5又は6に記載のガラス板。
(付記8)パラメータKが多くとも1.4MPa・m 1/2 又は1.3MPa・m 1/2 であり、Kが応力の2乗の張力下の中央ゾーンにおける積分の平方根である、付記1〜7のいずれか1項に記載のガラス板。
(付記9)ガラスがアルミノケイ酸リチウム又はアルミノケイ酸ナトリウムタイプのものである、付記1〜8のいずれか1項に記載のガラス板。
(付記10)その化学組成が、下記酸化物を下記の重量含有率の範囲:
SiO 2 55−72%、特には60−71%
Al 2 O 3 2−15%、特には3−12%
Na 2 O 9−17%、特には10−15%
K 2 O 0−12%、特には1−10%
MgO 2−13%、特には4−12%
CaO 0−2%、特には0−1%
B 2 O 3 0−1%、特には0%
で含むものである、付記9に記載のガラス板。
(付記11)その化学組成が、下記酸化物を下記の重量含有率の範囲:
SiO 2 52−75%、特には65−70%
Al 2 O 3 15−27%、特には18−19.8%
Li 2 O 2−10%、特には2.5−3.8%
K 2 O 0−5%、特には0−1%
Na 2 O 0−5%、特には0−1%
ZnO 0−5%、特には1.2−2.8%
MgO 0−5%、特には0.55−1.5%
BaO 0−5%、特には0−1.4%
SrO 0−3%、特には0−1.4%
TiO 2 0−6%、特には1.8−3.2%
ZrO 2 0−3%、特には1.0−2.5%
P 2 O 5 0−8%
で含むものである、付記9に記載のガラス板。
(付記12)保護ガラス、表示ウィンドウ、スクリーン又は装飾要素として、付記1〜11のいずれか1項に記載の少なくとも1枚のガラス板を含む、電子デバイス、特には小型又は携帯デバイス、例えば特にはスマートホン、携帯情報端末、デジタルカメラ、マルチメディアプレーヤー、コンピュータ、タブレット、テレビ。
(付記13)付記1〜11のいずれか1項に記載の少なくとも1枚のガラス板を含む、太陽センサー、熱センサー又は光起電センサー。
(付記14)ガラス溶融、成形、切断及びイオン交換ステップを含む、付記1〜11のいずれか1項に記載のガラス板を得るための方法。
(付記15)少なくとも1つのイオン交換ステップが、硝酸塩、硫酸塩、塩化物又はそれらの任意の混合物から選択される溶融カリウム及び/又はナトリウム塩を用いて行われる、付記14に記載の方法。
(付記16)交換温度が少なくとも450℃、特には480℃である、付記15に記載の方法。
Claims (17)
- 厚みが多くとも2mmで、圧縮下の表面ゾーンと張力下の中央ゾーンを有し、圧縮と張力の間の遷移が発生する深さが少なくとも100μmであり、前記深さと前記厚みの間の比が少なくとも0.1であるガラス板であって、さらに、60Nの荷重の下でのビッカース押込み後、三脚上リング(ring−on−tripod)曲げ試験における破壊時曲げ応力が少なくとも70MPaであり、最大圧縮応力が300MPa以下であり、ガラスがアルミノケイ酸ナトリウムタイプのものであるか、又はソーダ−石灰−シリカタイプのものであり、アルミノケイ酸ナトリウムタイプのガラスの化学組成が、下記酸化物を下記の重量含有率の範囲:
SiO 2 55−72%
Al 2 O 3 2−15%
Na 2 O 9−17%
K 2 O 0−12%
MgO 2−13%
CaO 0−2%
B 2 O 3 0−1%
で含むものであり、ソーダ−石灰−シリカタイプのガラスの化学組成が、下記酸化物を下記の重量含有率の範囲:
SiO 2 60−75%
Al 2 O 3 0−4%
Na 2 O 9−18%
K 2 O 0−5%
MgO 0−10%
CaO 4−15%
で含むものである、ガラス板。 - アルミノケイ酸ナトリウムタイプのガラスの前記酸化物が組成全体の少なくとも95重量%を占める、請求項1に記載のガラス板。
- アルミノケイ酸ナトリウムタイプのガラスの前記酸化物が組成全体の少なくとも98重量%を占める、請求項2に記載のガラス板。
- 最大圧縮応力が200MPa以下である、請求項1〜3のいずれか1項に記載のガラス板。
- 圧縮下の表面ゾーンがイオン交換によって得られた、請求項1〜4のいずれか1項に記載のガラス板。
- 厚みが多くとも1.1mmでかつ少なくとも0.25mmである、請求項1〜5のいずれか1項に記載のガラス板。
- 圧縮と張力の間の遷移が発生する深さが少なくとも200μmでかつ多くとも500μmである、請求項1〜6のいずれか1項に記載のガラス板。
- ガラス板の厚み内の応力プロファイルは、最大圧縮応力が少なくとも70MPaとなるものであり、この最大圧縮応力を受けるゾーンが、ガラス板の表面からゼロでない距離のところにある、請求項1〜7のいずれか1項に記載のガラス板。
- ガラス板の厚み内の応力プロファイルは、ガラスの厚みの3分の1を占める中央ゾーン内で、引張応力の強さの相対的変動が少なくとも10%となるものである、請求項1〜8のいずれか1項に記載のガラス板。
- 圧縮と張力の間の遷移が発生する深さと厚みの間の比が、少なくとも0.2でかつ多くとも0.4である、請求項8又は9に記載のガラス板。
- パラメータKが多くとも1.4MPa・m1/2 であり、Kが応力の2乗の張力下の中央ゾーンにおける積分の平方根である、請求項1〜10のいずれか1項に記載のガラス板。
- その化学組成が、下記酸化物を下記の重量含有率の範囲:
SiO2 60−71%
Al2O3 3−12%
Na2O 10−15%
K2O 1−10%
MgO 4−12%
CaO 0−1%
B2O3 0%
で含むものである、請求項1〜11のいずれか1項に記載のガラス板。 - 保護ガラス、表示ウィンドウ、スクリーン又は装飾要素として、請求項1〜12のいずれか1項に記載の少なくとも1枚のガラス板を含む、電子デバイス。
- 請求項1〜12のいずれか1項に記載の少なくとも1枚のガラス板を含む、太陽センサー、熱センサー又は光起電センサー。
- ガラス溶融、成形、切断及びイオン交換ステップを含む、請求項1〜12のいずれか1項に記載のガラス板を得るための方法。
- 少なくとも1つのイオン交換ステップが、硝酸塩、硫酸塩、塩化物又はそれらの任意の混合物から選択される溶融カリウム及び/又はナトリウム塩を用いて行われる、請求項15に記載の方法。
- 交換温度が少なくとも450℃である、請求項16に記載の方法。