JP5890172B2 - Forming paint for wrap film anti-rewinding film, and method for producing carton having anti-rewinding film - Google Patents
Forming paint for wrap film anti-rewinding film, and method for producing carton having anti-rewinding film Download PDFInfo
- Publication number
- JP5890172B2 JP5890172B2 JP2011285065A JP2011285065A JP5890172B2 JP 5890172 B2 JP5890172 B2 JP 5890172B2 JP 2011285065 A JP2011285065 A JP 2011285065A JP 2011285065 A JP2011285065 A JP 2011285065A JP 5890172 B2 JP5890172 B2 JP 5890172B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- rewinding
- wrap
- wrap film
- carton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、カートンに収納されたラップフィルムのロールからラップフィルムを引き出して切断した後のロール側のラップフィルムの端部を付着させて巻き戻りを防止するラップフィルムの巻き戻り防止膜の形成塗料、巻き戻り防止膜を有するカートンの製造方法に関する。 The present invention, formation of the winding-out return preventing film wrap film for preventing unwinding by attaching the ends of the roll side of the wrap film after the cutting is pulled out wrap film from a roll of wrap film housed in the carton paint, a method for producing a carton having a winding-out back prevention film.
従来、ラップフィルムの巻き戻り防止膜の形成方法としては、ポリエステル系塗料をグラビア印刷で付設し、ポリエステルを主成分とする塗膜として形成する方法が知られている（例えば、特許文献１参照）。また、巻き戻り防止膜形成用のポリエステル系塗料の溶剤として、酢酸エチルやイソプロピルアルコール等が使用できることも知られている（例えば、特許文献２参照） Conventionally, as a method for forming an anti-rewinding film of a wrap film, a method is known in which a polyester-based paint is attached by gravure printing and formed as a coating film containing polyester as a main component (see, for example, Patent Document 1). . It is also known that ethyl acetate, isopropyl alcohol, or the like can be used as a solvent for a polyester-based paint for forming an anti-rewinding film (see, for example, Patent Document 2).
ところで、グラビア印刷は塗料の厚塗りがしやすく、カートンを構成する紙面の凹凸を吸収して、ラップフィルムが密着しやすい平滑な表面の巻き戻り防止膜を形成しやすい利点がある。 By the way, gravure printing has an advantage that it is easy to apply thick paint, absorbs unevenness of the paper surface constituting the carton, and easily forms an anti-rewinding film having a smooth surface to which the wrap film is easily adhered.
しかしながら、グラビア印刷でポリエステル系塗料を付設する場合、溶剤として酢酸エチルを用いると、印刷中に塗料に気泡が発生しやすくなる問題がある。塗料に多量の気泡が生じると、得られる巻き戻り防止膜の表面が気泡によって荒れて、ラップフィルムとの良好な密着性が得られなくなり、巻き戻りを防止しにくくなる。また、溶剤としてイソプロピルアルコールを用いた場合、ポリエステル系塗料に対する溶解力が十分でなく、均一な付設がしにくくなって、やはり良好な密着性を有する巻き戻り防止膜が得にくくなるという問題がある。 However, in the case of attaching a polyester-based paint by gravure printing, if ethyl acetate is used as a solvent, there is a problem that bubbles are easily generated in the paint during printing. When a large amount of bubbles are generated in the paint, the surface of the obtained anti-rewinding film becomes rough due to the bubbles, and good adhesion to the wrap film cannot be obtained, and it becomes difficult to prevent rewinding. In addition, when isopropyl alcohol is used as a solvent, there is a problem that it is difficult to obtain an anti-rewinding film having good adhesion due to insufficient dissolving power with respect to the polyester-based paint, making uniform attachment difficult. .
本発明は、上記従来の問題点に鑑みてなされたもので、ラップフィルムの巻き戻り防止膜を、ポリエステル系塗料を用いたグラビア印刷によりカートンに形成するに際し、塗料を均一に塗布できるようにすると共に、印刷に伴う気泡の発生を防止できるようにし、密着力の良好な表面の平滑性に優れた巻き戻り防止膜が容易に得られる形成方法及びそれに用いる塗料を提供することを目的とする。また、本発明は、表面の平滑性に優れ、確実な巻き戻り防止効果が得やすい巻き戻り防止膜を備えたラップフィルムのカートン及びカートンブランクを提供することも目的とする。 The present invention has been made in view of the above-described conventional problems, and makes it possible to uniformly apply a coating material when forming an anti-rewinding film of a wrap film on a carton by gravure printing using a polyester-based coating material. At the same time, it is an object of the present invention to provide a forming method and a paint used therefor, which can prevent the generation of bubbles associated with printing, and can easily obtain an anti-rewinding film having excellent adhesion and excellent surface smoothness. Another object of the present invention is to provide a carton and a carton blank of a wrap film provided with an anti-rewinding film that is excellent in surface smoothness and easily obtains a reliable anti-rewinding effect.
本発明の第一は、カートンに収納されたラップフィルムのロールからラップフィルムを引き出して切断した後のロール側のラップフィルムの端部を付着させて巻き戻りを防止するラップフィルムの巻き戻り防止膜をグラビア印刷により形成する巻き戻り防止膜の形成塗料において、
酢酸エチル８０〜６０重量部と、イソプロピルアルコール２０〜４０重量部とを合計が１００重量部となるように混合した混合溶剤で希釈された紫外線硬化型のポリエステル系ワニスであることを特徴とするラップフィルムの巻き戻り防止膜の形成塗料を提供するものである。
The first aspect of the present invention is a wrap film anti-rewinding film for preventing rewinding by attaching an end portion of a wrap film on the roll side after the wrap film is drawn and cut from a roll of wrap film stored in a carton. In the paint for forming the anti-rewinding film formed by gravure printing,
A wrap characterized by being a UV curable polyester varnish diluted with a mixed solvent in which 80 to 60 parts by weight of ethyl acetate and 20 to 40 parts by weight of isopropyl alcohol are mixed so that the total amount becomes 100 parts by weight. The present invention provides a paint for forming a film unwinding prevention film.
また、本発明の第二は、ラップフィルムカートンの製造方法であって、
酢酸エチル８０〜６０重量部と、イソプロピルアルコール２０〜４０重量部とを合計が１００重量部となるように混合した混合溶剤で希釈した紫外線硬化型のポリエステル系ワニスを用いて、グラビア印刷によって、収納されたラップフィルムのロールからラップフィルムを引き出して切断した後のロール側のラップフィルムの端部を付着させて巻き戻りを防止する巻き戻り防止膜を形成する工程を有することを特徴とするラップフィルムのカートンの製造方法を提供するものである。
The second of the present invention is a method for producing a wrap film carton,
Using a 80 to 60 parts by weight of ethyl acetate, polyester varnish ultraviolet curable total and isopropyl alcohol 20 to 40 parts by weight was diluted with a mixed solvent were mixed to obtain 100 parts by weight, depending on gravure printing, A wrap having a step of forming an anti-rewinding film for preventing rewinding by attaching an end portion of a wrap film on the roll side after the wrap film is pulled out and cut from a roll of wrap film stored therein. A method for producing a carton for a film is provided.
上記本発明の第二は、前記ポリエステル系ワニスを用いて、前記ラップフィルムカートンから引き出したラップフィルムを切断する際に指や手の平が添えられる箇所に滑り止め用の膜を形成する工程を有することをその好ましい態様として含むものである。The second aspect of the present invention includes the step of forming a non-slip film at a location where a finger or palm is attached when the wrap film drawn from the wrap film carton is cut using the polyester varnish. Is included as a preferred embodiment thereof.
本発明の第一においては、イソプロピルアルコールがグラビア印刷中の塗料の泡立ち防止効果をもたらし、酢酸エチルが塗料の良好な溶解性をもたらす。つまり、イソプロピルアルコールと酢酸エチルが相互に欠点を補い合うものと考えられる。従って、本発明によると、塗料を均一に塗布できると共に、印刷に伴う気泡の発生を防止することができ、密着力の良好な表面の平滑性に優れた巻き戻り防止膜が得られる。 Oite the first aspect of the present invention results in a prevention effect foaming isopropyl alcohol of paint in gravure printing, ethyl acetate results in good solubility of the paint. That is, it is considered that isopropyl alcohol and ethyl acetate compensate for each other's drawbacks. Therefore, according to the present invention, it is possible to uniformly apply the coating material, to prevent generation of bubbles accompanying printing, and to obtain an anti-rewinding film excellent in surface smoothness with good adhesion.
また、本発明の第二においては、表面の平滑性に優れ、確実な巻き戻り防止効果が得やすい巻き戻り防止膜を備えたラップフィルムのカートンが得られる。 In the second aspect of the present invention, excellent smoothness of the surface, reliable rewinding preventing effect is obtained carton of the wrap film with easily obtained unwinding prevention film.
本発明では、グラビア印刷により、巻き戻り防止膜の形成塗料の塗膜を、ラップフィルムのロールを収納するカートンを構成する紙面に形成し、この塗膜の硬化膜を巻き戻り防止膜とする。塗膜の形成位置は、通常、カートンに収納されたロールから引き出したラップフィルムをカートンに付属する切断歯で切断する時に、ラップフィルムのロール側の切断端部が押し付けられる本体前面板部分である。このような箇所に巻き戻り防止膜を形成しておくと、ラップフィルムの切断端部が平滑な巻き戻り防止膜の表面に付着することで、カートン内へ引き込まれてロール表面に付着してしまうことを防止することができる。 In the present invention, the coating film of the coating material for forming the anti-rewinding film is formed on the paper surface of the carton that houses the roll of the wrap film by gravure printing, and the cured film of this coating film is used as the anti-rewinding film. The formation position of the coating film is usually the main body front plate portion to which the cut end portion on the roll side of the wrap film is pressed when the wrap film drawn from the roll stored in the carton is cut with the cutting teeth attached to the carton. . If the anti-rewinding film is formed in such a place, the cut end portion of the wrap film adheres to the surface of the smooth anti-rewinding film and is drawn into the carton and adheres to the roll surface. This can be prevented.
本発明で使用する巻き戻り防止膜の形成塗料としては、溶剤で希釈したポリエステル系塗料であって、紫外線硬化型の透明塗料（ワニス）が用いられる。 As the coating material for forming the anti-rewinding film used in the present invention, a polyester-based coating material diluted with a solvent and an ultraviolet curable transparent coating material (varnish) is used .
塗料を希釈する溶剤としては、酢酸エチルとイソプロピルアルコールを混合した混合溶剤が用いられる。両者の混合比率は、酢酸エチルが８０〜６０重量部、イソプロピルアルコールが２０〜４０重量部で、両者の合計が１００重量部となる比率である。酢酸エチルの配合量が多過ぎると、印刷時に塗料が泡立ちやすくなり、イソプロピルアルコールの配合量が多過ぎると、塗料の溶解性が悪くなる。 The solvent for diluting the paint, a mixed solvent obtained by mixing ethyl acetate and isopropyl alcohol. The mixing ratio of both is such that ethyl acetate is 80 to 60 parts by weight, isopropyl alcohol is 20 to 40 parts by weight, and the total of both is 100 parts by weight. When the blending amount of ethyl acetate is too large, the coating tends to foam during printing, and when the blending amount of isopropyl alcohol is too large, the solubility of the coating is deteriorated.
上記混合溶剤による塗料の希釈は、印刷速度によっても相違するが、塗料の濃度で９０〜７０重量％程度で、粘度ではザーンカップＮｏ．３で１８〜２０秒となる粘度であることが好ましい。 Dilution by that paint in the mixed solvent is also differs by the printing speed, in the order of 90 to 70% by weight concentration of the coating material, Zahn in viscosity cup No. 3, the viscosity is preferably 18 to 20 seconds.
巻き戻り防止膜の形成に際しては、カートンを構成する紙面の凹凸を吸収しやすい肉厚の塗膜を形成するために、塗料にトリアセチレンセルロース等のレベリング剤を添加することが行われる。しかし、本発明によると、泡による表面の荒れのない肉厚の塗膜を形成することができると共に、塗膜がカートンを構成する紙面の凹凸を吸収しやすく、このようなレベリング剤の添加を省略しても、表面が平滑でラップフィルムに対する良好な密着性を発揮する巻き戻り防止膜を形成することができる。 In forming the anti-rewinding film, a leveling agent such as triacetylene cellulose is added to the coating material in order to form a thick coating film that easily absorbs the unevenness of the paper surface constituting the carton. However, according to the present invention, it is possible to form a thick coating film with no rough surface due to foam, and the coating film easily absorbs irregularities on the paper surface constituting the carton. Even if omitted, it is possible to form an anti-rewinding film that has a smooth surface and exhibits good adhesion to the wrap film.
本発明により形成した巻き戻り防止膜によれば、ポリ塩化ビニリデンのラップフィルム、ポリエチレンのラップフィルム、ポリメチルペンテンのラップフィルムのいずれに対しても良好な巻き戻り防止効果を得ることができる。 According to the anti-rewinding film formed according to the present invention, a good anti-rewinding effect can be obtained for any of the polyvinylidene chloride wrap film, polyethylene wrap film, and polymethylpentene wrap film.
本発明のラップフィルムの巻き戻り防止膜の形成方法により巻き戻り防止膜を形成したカートンとカートンブランクの一例を図１及び図２で説明する。図２における一点鎖線は折りラインを示す。 One example of a carton and a carton blank in which a rewinding prevention film is formed by the method for forming a wrapping film rewinding prevention film of the present invention will be described with reference to FIGS. The dashed-dotted line in FIG. 2 shows a fold line.
図１及び図２において、１は本体前面板、２は本体底面板、３は本体背面板、４は本体側面板である。図２にのみ示される５，６は、それぞれ本体側面板４の内側に宛われる本体内側片である。これらは、ラップフィルムを巻き取ったロール（図示されていない）を収納する本体を構成する。また、７は蓋上面板、８は蓋前面板、９は蓋側面板である。図２のみに示される１０は、蓋側面板９の内側に宛われる蓋内側片である。これらは、上記本体に被さる蓋体を構成する。
1 and 2,
１１は蓋前面板８に形成されたミシン目等の切り離しラインで、図１（ａ）に示されるように、この切り離しライン１１に沿って蓋前面板８の下部を切り取ることで、カートンが開封されると同時に、残された蓋前面板８の下縁に切断歯１２が露出される。
ラップフィルムを使用する場合、カートンを開封し、蓋体を図１（ｂ）に示されるように上方へ引き上げ、収納されているロールからラップフィルムを必要長さだけ引き出す。ラップフィルムをカートンから引き出した後、蓋体を閉じ、蓋前面板８と本体前面板１の間にラップフィルムを挟み付けながら、ラップフィルムに切断歯１２を押し付ける。これにより、ラップフィルムを切断して、蓋前面板８より外方へ引き出されているラップフィルムをそのロールから分離することができる。
When using a wrap film, the carton is opened, the lid is lifted upward as shown in FIG. 1 (b), and the wrap film is pulled out from the roll accommodated by a required length. After the wrap film is pulled out from the carton, the lid is closed and the
１３は巻き戻り防止膜で、上記切断後、ラップフィルムのロール側切断端部が引き込まれてロールに張り付いてしまうのを防止するためのもので、本例においては本体前面板１の上部に設けられている。このような位置に設けておくと、切断時にラップフィルムを蓋前面板８との間に挟み付けた時に、切断歯１２よりロール側のラップフィルムを巻き戻り防止膜１３へ密着させることができる。
本発明に係る巻き戻り防止膜１３は、カートンの適当な箇所に付設することで、カートンを手に持つ際の滑り止め用として用いることもできる。この滑り止め用として設ける場合、付設位置としては、引き出したラップフィルムを切断する際に指や手の平が添えられる箇所が好ましい。具体的には、本体底面板２、本体背面板３及び蓋前面板８のそれぞれの長さ方向中央部や、本体背面板３と蓋上面板７間のコーナー部、蓋上面板７と蓋前面板８間のコーナー部、本体背面板３及び蓋上面板７の長さ方向両端部を挙げることができる。また、巻き戻り防止膜１３は、図１（ｂ）に示されるような本体前面板１の上部中央部のみだけでなく、本体前面板１の上部全長に亘って設けることもできる。
The
実施例１〜３、比較例１〜３
紫外線硬化型のポリエステル系ワニスを用いたグラビア印刷で巻き戻り防止膜の形成を行った。ポリエステル系ワニスは、酢酸エチルとイソプロピルアルコール（ＩＰＡ）を混合した混合溶剤で濃度約７０重量％に希釈した。酢酸エチルとＩＰＡの配合比率は表１に記載の通りとした。
Examples 1-3, Comparative Examples 1-3
An anti-rewinding film was formed by gravure printing using an ultraviolet curable polyester-based varnish. The polyester varnish was diluted to a concentration of about 70% by weight with a mixed solvent in which ethyl acetate and isopropyl alcohol (IPA) were mixed. The blending ratio of ethyl acetate and IPA was as shown in Table 1.
まず、上記混合溶剤によるポリエステル系ワニスの希釈状態を観察し、ポリエステル系ワニスが十分溶解しているか否かを評価した。評価結果を表１に示す。表１の希釈状態の評価の欄における「○」はポリエステル系ワニスが十分溶解している場合を示し、「△」はポリエステル系ワニスの溶解状態がやや不十分な場合を示し、「×」はポリエステル系ワニスの溶解状態が明らかに不十分な場合を示す。 First, the dilution state of the polyester varnish with the mixed solvent was observed to evaluate whether the polyester varnish was sufficiently dissolved. The evaluation results are shown in Table 1. “◯” in the column of evaluation of the diluted state in Table 1 indicates a case where the polyester varnish is sufficiently dissolved, “Δ” indicates a case where the dissolved state of the polyester varnish is slightly insufficient, and “×” indicates The case where the dissolution state of the polyester varnish is clearly insufficient is shown.
次に、希釈状態の評価が「○」だった場合について、希釈したポリエステル系ワニスをグラビア印刷機のインク容器へ供給し、ポリエステル系ワニスの状態を目視観察しながらラップカートンブランクへの印刷を行い、ポリエステル系ワニスの泡発生状態を評価した。評価結果を表１に示す。表１の気泡状態の評価の欄における「○」は印刷開始後１時間経過後も泡の発生がほとんど認められなかった場合を示し、「×」は印刷開始後３０分程度で泡の増大が認められた場合を示す。なお、気泡状態の評価が「○」の場合、印刷開始から１時間経過後の印刷で得られた巻き戻り防止膜でもラップフィルムに対する良好な密着性が得られたが、気泡状態の評価が「×」の場合、印刷開始から１時間経過後の印刷で得られた巻き戻り防止膜は表面が荒れており、評価が「○」の場合に比してラップフィルムへの密着力が劣っていた。 Next, when the evaluation of the diluted state is “◯”, the diluted polyester varnish is supplied to the ink container of the gravure printing machine, and printing on the wrap carton blank is performed while visually observing the state of the polyester varnish. The foam generation state of the polyester varnish was evaluated. The evaluation results are shown in Table 1. “◯” in the column of the bubble state evaluation in Table 1 indicates a case where almost no bubbles were observed even after 1 hour from the start of printing, and “×” indicates that the bubbles increased in about 30 minutes after the start of printing. The case where it is recognized is shown. In addition, when the evaluation of the bubble state was “◯”, good adhesion to the wrap film was obtained even with the anti-rewinding film obtained by printing 1 hour after the start of printing, but the evaluation of the bubble state was “ In the case of “×”, the surface of the anti-rewinding film obtained by printing after 1 hour from the start of printing was rough, and the adhesion to the wrap film was inferior compared to the case where the evaluation was “◯”. .
なお、最初に希釈状態を評価し、希釈状態の評価が「○」とはならなかった場合については、均一な巻き戻り防止膜を得ることが困難であるとして、気泡状態の評価は行わなかった。 In addition, when the diluted state was evaluated first, and the evaluation of the diluted state was not “◯”, the bubble state was not evaluated as it was difficult to obtain a uniform anti-rewinding film. .
１ 本体前面板
２ 本体底面板
３ 本体背面板
４ 本体側面板
５，６ 本体内側片
７ 蓋上面板
８ 蓋前面板
９ 蓋側面板
１０ 蓋内側片
１１ 切り離しライン
１２ 切断歯
１３ 巻き戻り防止膜
DESCRIPTION OF
Claims (3)
酢酸エチル８０〜６０重量部と、イソプロピルアルコール２０〜４０重量部とを合計が１００重量部となるように混合した混合溶剤で希釈された紫外線硬化型のポリエステル系ワニスであることを特徴とするラップフィルムの巻き戻り防止膜の形成塗料。 Winding to form a wrap film anti-rewinding film by gravure printing that prevents the film from rewinding by attaching the end of the wrap film on the roll side after the wrap film is pulled out from the roll of wrap film stored in the carton and cut. In the paint for forming the anti-return film,
A wrap characterized by being a UV curable polyester varnish diluted with a mixed solvent in which 80 to 60 parts by weight of ethyl acetate and 20 to 40 parts by weight of isopropyl alcohol are mixed so that the total amount becomes 100 parts by weight. Forming paint for film unwinding prevention film.
酢酸エチル８０〜６０重量部と、イソプロピルアルコール２０〜４０重量部とを合計が１００重量部となるように混合した混合溶剤で希釈した紫外線硬化型のポリエステル系ワニスを用いて、グラビア印刷によって、収納されたラップフィルムのロールからラップフィルムを引き出して切断した後のロール側のラップフィルムの端部を付着させて巻き戻りを防止する巻き戻り防止膜を形成する工程を有することを特徴とするラップフィルムのカートンの製造方法。 A method of manufacturing a wrap film carton,
Using a 80 to 60 parts by weight of ethyl acetate, polyester varnish ultraviolet curable total and isopropyl alcohol 20 to 40 parts by weight was diluted with a mixed solvent were mixed to obtain 100 parts by weight, depending on gravure printing, A wrap having a step of forming an anti-rewinding film for preventing rewinding by attaching an end portion of a wrap film on the roll side after the wrap film is pulled out and cut from a roll of wrap film stored therein. Film carton manufacturing method.