JP5888202B2 - Liquid composition - Google Patents
Liquid composition Download PDFInfo
- Publication number
- JP5888202B2 JP5888202B2 JP2012229274A JP2012229274A JP5888202B2 JP 5888202 B2 JP5888202 B2 JP 5888202B2 JP 2012229274 A JP2012229274 A JP 2012229274A JP 2012229274 A JP2012229274 A JP 2012229274A JP 5888202 B2 JP5888202 B2 JP 5888202B2
- Authority
- JP
- Japan
- Prior art keywords
- tetrafluoroborate
- liquid composition
- etching
- etching component
- lewis acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、窒化シリコン(SiN)等からなる無機薄膜の除去に使用される液状組成物に関する。 The present invention relates to a liquid composition used for removing an inorganic thin film made of silicon nitride (SiN) or the like.
酸化ケイ素(SiO2)やSiN等の無機薄膜は、層間絶縁膜、パッシベーション膜、反射防止膜等として、各種半導体素子や太陽電池等で使用されている。
例えば、太陽電池には変換効率を向上するため、受光面側にSiN膜からなる反射防止膜を形成し、受光面の反対側の面にパッシベーション膜が形成されているものがある。
Inorganic thin films such as silicon oxide (SiO 2 ) and SiN are used in various semiconductor elements, solar cells, and the like as interlayer insulating films, passivation films, antireflection films, and the like.
For example, in some solar cells, an antireflection film made of a SiN film is formed on the light receiving surface side and a passivation film is formed on the surface opposite to the light receiving surface in order to improve conversion efficiency.
太陽電池として一般的な結晶シリコン太陽電池セルの製造では、p型シリコンウェハの表層にn+層となるリン拡散層を形成し、下層のp層との間にpn接合を形成する。その後、n+層上に反射防止膜を形成した後、受光面側及び裏面側に電極を形成し、必要に応じてパッシベーション膜を形成する。
太陽電池の製造では、反射防止膜やパッシベーション膜を形成した後で、電極をn+層に接続することが多いため、これら無機薄膜に開口を設ける必要がある。
In the manufacture of a crystalline silicon solar battery cell that is generally used as a solar battery, a phosphorus diffusion layer that becomes an n + layer is formed on the surface layer of a p-type silicon wafer, and a pn junction is formed between the lower p layer. Thereafter, after forming an antireflection film on the n + layer, electrodes are formed on the light receiving surface side and the back surface side, and a passivation film is formed as necessary.
In the manufacture of solar cells, electrodes are often connected to the n + layer after the formation of an antireflection film or a passivation film, and thus it is necessary to provide openings in these inorganic thin films.
無機薄膜に開口を設ける方法の1つとして、エッチング法がある。エッチング法としては、フォトレジストを用いた方法が一般的である。しかしながら、レジスト膜形成、露光、現像、エッチング、レジスト除去の各工程が必要であり、また、使用する資材が多いため効率的ではない。
また、レーザーによって開口を形成する方法がある。しかしながら、加工位置制御が煩雑であり、加工時間を要するため、生産性が十分ではない。また、レーザーによって下部にあるn+層やウェハ等が損傷する可能性がある。
また、従来、最も一般的な製造方法としては、電極となる金属と、ケイ素酸化物など、ガラスを構成する化合物を含有する導電ペーストを塗布し、加熱によってファイヤースルー(焼成貫通)を起こし、無機薄膜に開口部を形成すると同時に電極とn+層を接続する方法がある。しかしながら、本方法では250℃以上の高温処理が必要なため、n+層やウェハがダメージを受け、発電効率の低下が起こる可能性がある。
尚、無機薄膜をはじめからパターン状に形成する方法が考えられるが、工程が煩雑であることから効率的ではなく、また、パターン形成の精度の点で十分ではない。
One method for providing an opening in an inorganic thin film is an etching method. As an etching method, a method using a photoresist is generally used. However, each step of resist film formation, exposure, development, etching, and resist removal is necessary, and since many materials are used, it is not efficient.
There is also a method of forming an opening with a laser. However, since the processing position control is complicated and requires processing time, productivity is not sufficient. In addition, there is a possibility that the n + layer, the wafer, and the like below are damaged by the laser.
In addition, conventionally, the most common manufacturing method is to apply a conductive paste containing a compound that constitutes glass, such as a metal serving as an electrode and silicon oxide, to cause fire through (fired penetration) by heating, and inorganic There is a method of forming an opening in a thin film and simultaneously connecting an electrode and an n + layer. However, since this method requires high-temperature treatment at 250 ° C. or higher, the n + layer and the wafer may be damaged and power generation efficiency may be reduced.
In addition, although the method of forming an inorganic thin film in the pattern form from the beginning is considered, it is not efficient because the process is complicated, and it is not sufficient in terms of the accuracy of pattern formation.
一方、エッチングペーストを印刷して無機薄膜上にパターン等を形成し、その後、加熱することにより、エッチングペースト下部に開口を形成する方法が提案されている。
無機薄膜を除去する成分(エッチング成分)としては、例えば、特許文献1にはリン酸又はリン酸塩を含むエッチング媒体が記載されている。しかしながら、最適なエッチング温度が250℃以上と高いため、n+層やウェハ等がダメージを受ける可能性がある。
On the other hand, a method has been proposed in which an etching paste is printed to form a pattern or the like on an inorganic thin film, and then heated to form an opening below the etching paste.
As a component (etching component) for removing the inorganic thin film, for example, Patent Document 1 describes an etching medium containing phosphoric acid or phosphate. However, since the optimum etching temperature is as high as 250 ° C. or higher, the n + layer, the wafer, and the like may be damaged.
また、エッチング成分として、アンモニウム、アルカリ金属、およびアンチモンのフッ化物、アンモニウム、アルカリ金属、およびカルシウムの酸性フッ化物、アルキル化アンモニウム、ならびにテトラフルオロホウ酸カリウムの群より選択される少なくとも1種類のフッ素化合物と、任意に、所定の無機鉱酸及び有機酸を含むエッチング媒体を用いる方法が記載されている(特許文献2参照)。しかしながら、フッ素化合物と酸を混合したエッチング媒体は毒性が極めて高いという問題がある。 In addition, as an etching component, at least one fluorine selected from the group consisting of ammonium, alkali metal and antimony fluorides, ammonium, alkali metal and calcium acid fluorides, alkylated ammonium, and potassium tetrafluoroborate A method using a compound and, optionally, an etching medium containing a predetermined inorganic mineral acid and organic acid is described (see Patent Document 2). However, an etching medium in which a fluorine compound and an acid are mixed has a problem of extremely high toxicity.
本発明の目的は、エッチングペーストとして使用でき、低温(250℃以下)でも十分に無機薄膜(SiN層等)を除去できる、新規な液状組成物を提供することである。 An object of the present invention is to provide a novel liquid composition that can be used as an etching paste and can sufficiently remove an inorganic thin film (such as a SiN layer) even at a low temperature (250 ° C. or lower).
本発明によれば、以下の液状組成物等が提供される。
1.ホウ素及び該ホウ素と結合したハロゲンとを構造中に含むルイス酸、前記ルイス酸の塩、並びに前記ルイス酸を発生する化合物から選択される少なくとも1つのエッチング成分と、溶媒と、チキソ性付与剤と、を含有し、
前記エッチング成分は、室温では固体であり、前記チキソ性付与剤の含有率が、全体の0.1〜5.0質量%である、液状組成物。
2.前記エッチング成分の融点が250℃以下であり、不揮発性である、1に記載の液状組成物。
3.前記エッチング成分が、テトラフルオロホウ酸トリフェニルカルベニウム、テトラフルオロホウ酸トロピリウム、テトラフルオロホウ酸ジ−n−ブチルアンモニウム、テトラフルオロホウ酸テトラブチルアンモニウム、テトラフルオロホウ酸トリメチルオキソニウム、テトラフルオロホウ酸トリエチルオキソニウム、1−エチル−2,3−ジメチルイミダゾリウムテトラフルオロホウ酸塩、1−ブチル−1−メチルピロリジニウムテトラフルオロホウ酸塩、メチルトリフルオロホウ酸カリウム、4−ヨードフェニルトリフルオロホウ酸カリウム、(4−メチル−1−ピペラジニル)メチルトリフルオロホウ酸カリウム、トリシクロペンチルフォスフィンテトラフルオロホウ酸、三フッ化ホウ素モノエチルアミン錯体、ピリジン−3−トリフルオロホウ酸カリウム及びテトラフルオロホウ酸ニトロニウムから選択される1以上の化合物である、1又は2に記載の液状組成物。
4.さらに、250℃において不揮発性の液体であり、前記エッチング成分を溶解する化合物を含む1〜3のいずれに記載の液状組成物。
5.前記エッチング成分が、三フッ化ホウ素モノエチルアミン錯体である1〜4のいずれかに記載の液状組成物。
6.前記エッチング成分を溶解する化合物が、ホウ素及び該ホウ素と直接結合したハロゲンとを構造中に含むルイス酸、前記ルイス酸の塩、加熱により前記ルイス酸を発生する化合物、又はイオン液体である、4又は5に記載の液状組成物。
7.前記エッチング成分の含有率が、全体の30〜80質量%である1〜6のいずれかに記載の液状組成物。
8.25℃における蒸気圧が1.34×103Pa未満である溶媒を含む、1〜7のいずれかに記載の液状組成物。
9.前記チキソ性付与剤が、ポリシロキサン、ポリアクリル、ポリアミド、ポリビニルアルコール、アルキル変性セルロース、ペプチド、ポリペプチド、及びこれらのうち2つ以上の構造を有する共重合体から選択される1以上である1〜8のいずれかに記載の液状組成物。
10.上記1〜9のいずれかに記載の液状組成物を使用して、窒化シリコン(SiN)膜を除去する方法。
11.前記液状組成物を、印刷法によりSiN膜上に形成する工程と、加熱によりSiN膜を除去する工程と、を有する、10に記載の方法。
12.上記10又は11に記載の方法を使用して、SiN膜を除去して得られる基板。
According to the present invention, the following liquid composition and the like are provided.
1. At least one etching component selected from a Lewis acid containing boron and a halogen bonded to the boron in the structure, a salt of the Lewis acid, and a compound generating the Lewis acid, a solvent, and a thixotropic agent Containing,
The liquid composition in which the etching component is solid at room temperature and the content of the thixotropic agent is 0.1 to 5.0% by mass of the whole.
2. 2. The liquid composition according to 1, wherein the etching component has a melting point of 250 ° C. or lower and is nonvolatile.
3. The etching component is triphenylcarbenium tetrafluoroborate, tropylium tetrafluoroborate, di-n-butylammonium tetrafluoroborate, tetrabutylammonium tetrafluoroborate, trimethyloxonium tetrafluoroborate, tetrafluoroborate Triethyloxonium acid, 1-ethyl-2,3-dimethylimidazolium tetrafluoroborate, 1-butyl-1-methylpyrrolidinium tetrafluoroborate, potassium methyltrifluoroborate, 4-iodophenyltri Potassium fluoroborate, potassium (4-methyl-1-piperazinyl) methyltrifluoroborate, tricyclopentylphosphine tetrafluoroborate, boron trifluoride monoethylamine complex, pyridine-3-triflu Is one or more compounds selected from potassium Rohou acid and nitronium tetrafluoroborate, 1 or liquid composition according to 2.
4). Furthermore, it is a non-volatile liquid at 250 degreeC, The liquid composition in any one of 1-3 which contains the compound which melt | dissolves the said etching component.
5. The liquid composition according to any one of 1 to 4, wherein the etching component is a boron trifluoride monoethylamine complex.
6). The compound that dissolves the etching component is a Lewis acid containing boron and a halogen directly bonded to the boron in the structure, a salt of the Lewis acid, a compound that generates the Lewis acid by heating, or an ionic liquid. Or the liquid composition of 5.
7). The liquid composition in any one of 1-6 whose content rate of the said etching component is 30-80 mass% of the whole.
The liquid composition in any one of 1-7 containing the solvent whose vapor pressure in 8.25 degreeC is less than 1.34 * 10 < 3 > Pa.
9. The thixotropic agent is one or more selected from polysiloxane, polyacryl, polyamide, polyvinyl alcohol, alkyl-modified cellulose, peptide, polypeptide, and a copolymer having two or more structures among them 1 The liquid composition in any one of -8.
10. A method for removing a silicon nitride (SiN) film using the liquid composition according to any one of 1 to 9 above.
11. 11. The method according to 10, comprising a step of forming the liquid composition on the SiN film by a printing method and a step of removing the SiN film by heating.
12 A substrate obtained by removing the SiN film using the method described in 10 or 11 above.
本発明によれば、新規なエッチング成分を含有する液状組成物が提供できる。本発明の液状組成物を使用することにより、従来よりも低温で無機薄膜を除去できる。 According to the present invention, a liquid composition containing a novel etching component can be provided. By using the liquid composition of the present invention, the inorganic thin film can be removed at a lower temperature than in the prior art.
本発明の液状組成物は、以下の成分(A)〜(C)を含有する。
(A)ホウ素及び該ホウ素と結合したハロゲンとを構造中に含むルイス酸、ルイス酸の塩、並びにルイス酸を発生する化合物から選択される少なくとも1つのエッチング成分
エッチング成分は、無機薄膜を浸食し除去する成分である。本発明では、エッチング成分は室温(25℃)で固体である。
(B)溶媒
(C)チキソ性付与剤
チキソ性付与剤の含有率は、液状組成物全体の0.1〜5.0質量%である。
The liquid composition of the present invention contains the following components (A) to (C).
(A) At least one etching component selected from a Lewis acid containing a boron and a halogen bonded to the boron in the structure, a salt of the Lewis acid, and a compound that generates the Lewis acid. The etching component erodes the inorganic thin film. It is a component to be removed. In the present invention, the etching component is solid at room temperature (25 ° C.).
(B) Solvent (C) Thixotropic agent The content of the thixotropic agent is 0.1 to 5.0% by mass of the entire liquid composition.
本発明では、エッチング成分として上述したルイス酸、又は該ルイス酸の誘導体を使用する。これら成分は加熱により液化して、無機薄膜、特にSiN膜を溶解、除去する。
エッチング成分は、室温では固体であり、無機薄膜の除去温度(エッチング温度で、本願では100℃〜250℃)において液体となる。ここで、液体となるとは、上記温度においてエッチング成分自体が溶融して液体となるように設定することや、後述する成分(D)のように、エッチング温度で液状となる化合物に溶解するように設定することが例示できる。
In the present invention, the aforementioned Lewis acid or a derivative of the Lewis acid is used as an etching component. These components are liquefied by heating to dissolve and remove the inorganic thin film, particularly the SiN film.
The etching component is solid at room temperature and becomes liquid at the removal temperature of the inorganic thin film (etching temperature, 100 ° C. to 250 ° C. in the present application). Here, the term “becomes liquid” means that the etching component itself is melted at the above temperature to become a liquid, or is dissolved in a compound that becomes liquid at the etching temperature, such as component (D) described later. Setting can be exemplified.
成分(A)のエッチング成分のうち、ホウ素及び該ホウ素と結合したハロゲンとを構造中に含むルイス酸、ルイス酸の塩、ルイス酸を発生する化合物の具体例としては、テトラフルオロホウ酸トリフェニルカルベニウム、N−フルオロ−N’−クロロメチルトリエチレンジアミンビス(テトラフルオロホウ酸)、テトラフルオロホウ酸1−(クロロ−1−ピロリジニルメチレン)ピロリジニウム、テトラフルオロホウ酸トロピリウム、テトラフルオロホウ酸ジ−n−ブチルアンモニウム、テトラフルオロホウ酸テトラエチルアンモニウム、テトラフルオロホウ酸テトラブチルアンモニウム、テトラフルオロホウ酸テトラメチルアンモニウム、テトラフルオロホウ酸トリメチルオキソニウム、テトラフルオロホウ酸トリエチルオキソニウム、1,3−ビス(2,4,6−トリメチルフェニル)−4,5−ジヒドロイミダゾリウムテトラフルオロホウ酸塩、1−ブチル−3−メチルイミダゾリウムテトラフルオロホウ酸塩、1−ヘキシル−3−メチルイミダゾリウムテトラフルオロホウ酸塩、1−エチル−3−メチルイミダゾリウムテトラフルオロホウ酸塩、1−エチル−2,3−ジメチルイミダゾリウムテトラフルオロホウ酸塩、1−ヘキシル−3−メチルイミダゾリウムテトラフルオロホウ酸塩、1−メチル−3−オクチルイミダゾリウムテトラフルオロホウ酸塩、1−ブチル−2,3−ジメチルイミダゾリウムテトラフルオロホウ酸塩、1,3−ジ−tert−ブチルイミダゾリニウムテトラフルオロホウ酸塩、1−ブチル−1−メチルピペリジニウムテトラフルオロホウ酸、1−ブチル−3−メチルピリジニウムテトラフルオロホウ酸塩、1−ブチルピリジニウムテトラフルオロホウ酸塩、テトラフルオロホウ酸2,4,6−トリメチルピリジニウム、1−ブチル−1−メチルピロリジニウムテトラフルオロホウ酸塩、1−エチル−1−メチルピロリジニウムテトラフルオロホウ酸塩、1−エチル−1−メチルピペリジニウムテトラフルオロホウ酸塩、トリシクロペンチルフォスフィンテトラフルオロホウ酸等のテトラフルオロホウ酸有機塩基塩、
テトラフルオロホウ酸リチウム等のテトラフルオロホウ酸ハロゲン塩、
テトラフルオロホウ酸銅、テトラフルオロホウ酸亜鉛等のテトラフルオロホウ酸金属塩、
メチルトリフルオロホウ酸カリウム、(モルホリン−4−イル)メチルトリフルオロホウ酸カリウム、(3,3−ジメチルブチル)トリフルオロホウ酸カリウム、4−ヨードフェニルトリフルオロホウ酸カリウム、4−フルオロフェニルトリフルオロホウ酸カリウム、フェニルトリフルオロホウ酸カリウム、ピリジン−3−トリフルオロホウ酸カリウム、ビニルトリフルオロホウ酸カリウム、(4−メチル−1−ピペラジニル)メチルトリフルオロホウ酸塩、[(N−tert−ブチルアンモニオ)メチル]トリフルオロホウ酸等のアルキルトリフルオロホウ酸塩、
三フッ化ホウ素モノエチルアミン錯体、三フッ化ホウ素−酢酸錯体、三フッ化ホウ素テトラヒドロフラン錯体、三フッ化ホウ素フェノール錯体、三フッ化ホウ素ジエチルエーテル錯体、三フッ化ホウ素アセトニトリル錯体や三フッ化ホウ素メタノール錯体等の三フッ化ホウ素錯体化合物、
テトラフルオロホウ酸ニトロニウム、三よう化ホウ素、トリス(ペンタフルオロフェニル)ボラン、テトラキス(ペンタフルオロフェニル)ホウ酸塩エチルエーテル錯体等が挙げられる。
Among the etching components of component (A), specific examples of Lewis acid, Lewis acid salt and Lewis acid generating compound containing boron and halogen bonded to boron in the structure include triphenyl tetrafluoroborate. Carbenium, N-fluoro-N′-chloromethyltriethylenediaminebis (tetrafluoroboric acid), 1- (chloro-1-pyrrolidinylmethylene) pyrrolidinium tetrafluoroborate, tropylium tetrafluoroborate, tetrafluoroboric acid Di-n-butylammonium, tetraethylammonium tetrafluoroborate, tetrabutylammonium tetrafluoroborate, tetramethylammonium tetrafluoroborate, trimethyloxonium tetrafluoroborate, triethyloxonium tetrafluoroborate, 1, 3-bis (2,4,6-trimethylphenyl) -4,5-dihydroimidazolium tetrafluoroborate, 1-butyl-3-methylimidazolium tetrafluoroborate, 1-hexyl-3-methylimidazole 1-ethyl-3-methylimidazolium tetrafluoroborate, 1-ethyl-2,3-dimethylimidazolium tetrafluoroborate, 1-hexyl-3-methylimidazolium tetrafluoro Borate, 1-methyl-3-octylimidazolium tetrafluoroborate, 1-butyl-2,3-dimethylimidazolium tetrafluoroborate, 1,3-di-tert-butylimidazolinium tetrafluoro Borate, 1-butyl-1-methylpiperidinium tetrafluoroborate, 1-butyl Til-3-methylpyridinium tetrafluoroborate, 1-butylpyridinium tetrafluoroborate, 2,4,6-trimethylpyridinium tetrafluoroborate, 1-butyl-1-methylpyrrolidinium tetrafluoroborate Tetrafluoroborate organic base salts such as 1-ethyl-1-methylpyrrolidinium tetrafluoroborate, 1-ethyl-1-methylpiperidinium tetrafluoroborate, tricyclopentylphosphine tetrafluoroborate ,
Tetrafluoroborate halogen salts such as lithium tetrafluoroborate,
Tetrafluoroborate metal salts such as copper tetrafluoroborate and zinc tetrafluoroborate,
Potassium methyltrifluoroborate, potassium (morpholin-4-yl) methyltrifluoroborate, potassium (3,3-dimethylbutyl) trifluoroborate, potassium 4-iodophenyltrifluoroborate, 4-fluorophenyltri Potassium fluoroborate, potassium phenyltrifluoroborate, potassium pyridine-3-trifluoroborate, potassium vinyltrifluoroborate, (4-methyl-1-piperazinyl) methyltrifluoroborate, [(N-tert -Butylammonio) methyl] alkyl trifluoroborate such as trifluoroboric acid,
Boron trifluoride monoethylamine complex, boron trifluoride-acetic acid complex, boron trifluoride tetrahydrofuran complex, boron trifluoride phenol complex, boron trifluoride diethyl ether complex, boron trifluoride acetonitrile complex and boron trifluoride methanol Boron trifluoride complex compounds such as complexes,
Examples thereof include nitronium tetrafluoroborate, boron triiodide, tris (pentafluorophenyl) borane, tetrakis (pentafluorophenyl) borate ethyl ether complex, and the like.
上記のエッチング成分のうち、テトラフルオロホウ酸トリフェニルカルベニウム、テトラフルオロホウ酸トロピリウム、テトラフルオロホウ酸ジ−n−ブチルアンモニウム、テトラフルオロホウ酸テトラブチルアンモニウム、テトラフルオロホウ酸トリメチルオキソニウム、テトラフルオロホウ酸トリエチルオキソニウム、1−エチル−2,3−ジメチルイミダゾリウムテトラフルオロホウ酸塩、1−ブチル−1−メチルピロリジニウムテトラフルオロホウ酸塩、メチルトリフルオロホウ酸カリウム、4−ヨードフェニルトリフルオロホウ酸カリウム、(4−メチル−1−ピペラジニル)メチルトリフルオロホウ酸カリウム、トリシクロペンチルフォスフィンテトラフルオロホウ酸、三フッ化ホウ素モノエチルアミン錯体、ピリジン−3−トリフルオロホウ酸カリウム、テトラフルオロホウ酸ニトロニウム、三よう化ホウ素、トリス(ペンタフルオロフェニル)ボラン、テトラキス(ペンタフルオロフェニル)ホウ酸リチウムエチルエーテル錯体が好ましい。さらに、テトラフルオロホウ酸ジ−n−ブチルアンモニウム、テトラフルオロホウ酸テトラブチルアンモニウム、三フッ化ホウ素モノエチルアミン錯体が好ましく、特に、三フッ化ホウ素モノエチルアミン錯体が好ましい。 Among the above etching components, triphenylcarbenium tetrafluoroborate, tropylium tetrafluoroborate, di-n-butylammonium tetrafluoroborate, tetrabutylammonium tetrafluoroborate, trimethyloxonium tetrafluoroborate, tetra Triethyloxonium fluoroborate, 1-ethyl-2,3-dimethylimidazolium tetrafluoroborate, 1-butyl-1-methylpyrrolidinium tetrafluoroborate, potassium methyltrifluoroborate, 4-iodo Potassium phenyltrifluoroborate, potassium (4-methyl-1-piperazinyl) methyltrifluoroborate, tricyclopentylphosphine tetrafluoroborate, boron trifluoride monoethylamine complex, pyridine-3-to Potassium fluoroborate, nitronium tetrafluoroborate, triiodide, boron, tris (pentafluorophenyl) borane, lithium tetrakis (pentafluorophenyl) ethyl ether complex borate is preferred. Further, di-n-butylammonium tetrafluoroborate, tetrabutylammonium tetrafluoroborate, and boron trifluoride monoethylamine complex are preferable, and boron trifluoride monoethylamine complex is particularly preferable.
エッチング成分の融点は、250℃以下であり、液化時は不揮発性であることが好ましい。これにより、エッチング成分は無機薄膜の除去温度で単独で液化するため、後述する成分(D)を使用する必要がなく、また、エッチング成分の蒸発によるパターンの変形等が抑制できる。
尚、本発明において「不揮発性である」とは、エッチング温度で処理時間中に50質量%以上のエッチング成分が揮発せずに残存できることを意味し、少なくともエッチング温度以上の沸点を有し、望ましくはエッチング温度での蒸気圧が350Pa以下である場合をいう。
The melting point of the etching component is 250 ° C. or less and is preferably non-volatile when liquefied. Thereby, since the etching component is liquefied independently at the removal temperature of the inorganic thin film, it is not necessary to use the component (D) described later, and deformation of the pattern due to evaporation of the etching component can be suppressed.
In the present invention, “nonvolatile” means that an etching component of 50% by mass or more can remain without volatilization during the processing time at the etching temperature, and has a boiling point of at least the etching temperature, preferably Means a case where the vapor pressure at the etching temperature is 350 Pa or less.
エッチング成分の含有率は、使用時における組成物の性状を考慮して適宜調整すればよい。エッチング成分の含有率は高い方が好ましいが、印刷法にて組成物を塗布することを考慮すると、組成物の粘度やペースト性状の調整が重要となる。エッチング成分の含有率は、液状組成物全体に対して30〜80質量%であることが好ましく、50〜70質量%であることが特に好ましい。 The content of the etching component may be appropriately adjusted in consideration of the properties of the composition at the time of use. Although it is preferable that the content of the etching component is high, in consideration of applying the composition by a printing method, it is important to adjust the viscosity and paste properties of the composition. The content of the etching component is preferably 30 to 80% by mass and particularly preferably 50 to 70% by mass with respect to the entire liquid composition.
エッチング成分は、印刷性向上のため、混合前の粒径が粒径100μm以下であることが好ましい。
尚、ここでの粒径は数平均粒子径であり、SEM観察像における重複せずランダムに選んだ100個の平均値として求められる。具体的には、SEMの試料台上にカーボン粘着テープを貼り付け、その上にエッチング成分を振り掛ける。試料台上のエッチング成分のうち、粘着していないものをエアガンで吹き飛ばす。このエッチング成分の付着したSEM試料台に対し、真空スパッタ装置(例えばION SPUTTER、日立ハイテク製)を用いPtを10〜20nmの厚みでスパッタしてSEM用サンプルとする。このSEM用サンプルをSEM装置(例えばESEM XL30、Philips製)により、印過電圧10kVで観察する。倍率は、平均的なエッチング成分粒子の直径が視野の1割程度を占めように選ぶ。観察された粒子像の中から重なって外形の確認できないエッチング成分を除いた中からランダムに100個選び、それぞれのエッチング成分像に対し外接する並行二直線のうち最大距離となるように選んだ並行二直線間距離を計測する。これら100個の値に対して平均値を求め数平均粒子径とする。尚、1視野の中から100個の粒子が選べない場合には複数視野から計測する。
The etching component preferably has a particle size of 100 μm or less before mixing in order to improve printability.
In addition, the particle size here is a number average particle size, and is obtained as an average value of 100 randomly selected without overlapping in the SEM observation image. Specifically, a carbon adhesive tape is affixed on the SEM sample stage, and an etching component is sprinkled thereon. Of the etching components on the sample stage, those that are not adhered are blown off with an air gun. Using a vacuum sputtering apparatus (for example, ION SPUTTER, manufactured by Hitachi High-Technologies), Pt is sputtered to a thickness of 10 to 20 nm on the SEM sample stage to which the etching component is adhered to obtain a sample for SEM. The sample for SEM is observed with an SEM apparatus (for example, ESEM XL30, manufactured by Philips) at an overload voltage of 10 kV. The magnification is selected so that the average etching component particle diameter occupies about 10% of the field of view. 100 particles randomly selected from the observed particle images, excluding the etching components whose outline cannot be confirmed, and selected to be the maximum distance among the parallel straight lines circumscribing each etching component image Measure the distance between two straight lines. An average value is obtained for these 100 values and is defined as the number average particle diameter. When 100 particles cannot be selected from one field of view, measurement is performed from a plurality of fields.
また、分散後のエッチング成分の粒径(分散粒径)はスクリーン印刷精度の点から100μm以下が好ましく、粘度特性の点から0.01μm以上であることが好ましい。
尚、分散粒径はレーザー散乱法粒度分布測定装置を用い体積平均粒径として求められる。具体的には、ユニバーサルリキッドモジュールを装着したレーザー散乱法粒度分布測定装置(例えば,LS13 320,ベックマンコールタ製)を用い、光源の安定のため本体電源を入れて30分間放置した後、リキッドモジュールに液状組成物で用いている溶媒のみを測定プログラムからRinseコマンドにより導入し、測定プログラムからDe−bubble,Measure Offset,Align,Measure Backgroundを行う。続いて、測定プログラムのMeasure Loadingを用い、液状組成物をリキッドモジュールに測定プログラムがサンプル量LowからOKになるまで添加する。その後、測定プログラムからMeasureを行い、粒度分布を取得する。レーザー散乱法粒度分布測定装置の設定として、Pump Speed:70%、Include PIDS data: ON、Run Length: 90 secondsを用いる。分散媒及び分散質の屈折率には、エッチング成分及び溶媒の屈折率をそれぞれ用いる。
Further, the particle size of the etching component after dispersion (dispersed particle size) is preferably 100 μm or less from the viewpoint of screen printing accuracy, and preferably 0.01 μm or more from the point of viscosity characteristics.
The dispersed particle diameter is obtained as a volume average particle diameter using a laser scattering particle size distribution analyzer. Specifically, using a laser scattering particle size distribution measurement device (for example, LS13 320, manufactured by Beckman Coulter) equipped with a universal liquid module, the main body is turned on for 30 minutes to stabilize the light source, and then the liquid module is used. Only the solvent used in the liquid composition is introduced from the measurement program by the Rinse command, and De-bubble, Measurement Offset, Align, and Measurement Background are performed from the measurement program. Subsequently, using the measurement program Measurement Loading, the liquid composition is added to the liquid module until the measurement program reaches the OK from the sample amount Low. Thereafter, Measurement is performed from the measurement program to obtain a particle size distribution. As settings of the laser scattering method particle size distribution measuring apparatus, Pump Speed: 70%, Include PIDS data: ON, and Run Length: 90 seconds are used. As the refractive index of the dispersion medium and the dispersoid, the refractive indexes of the etching component and the solvent are used, respectively.
(B)成分である溶媒は、上述したエッチング成分を分散できればよく、特に、制限はない。本発明の液状組成物を、スクリーン印刷を用いて印刷する場合には、印刷中に溶媒の揮発により粘度が変化すると印刷性が変化してしまうことから、25℃における蒸気圧が1.34×103Pa未満、好ましくは、1.0×103Pa・s未満であることが好ましい。
溶媒としては、ノナン、デカン、ドデカン、テトラデカン等の脂肪族炭化水素系溶媒;エチルベンゼン、アニソール、メシチレン、ナフタレン、シクロヘキシルベンゼン、ジエチルベンゼン、フェニルアセトニトリル、フェニルシクロヘキサン、ベンゾニトリル、メシチレン等の芳香族炭化水素系溶媒;酢酸イソブチル、プロピオン酸メチル、プロピオン酸エチル、γ−ブチロラクトン、グリコールスルファイト、乳酸エチル、乳酸エチル等のエステル系溶媒;1−ブタノール、シクロヘキサノール、グリセリン等のアルコ−ル系溶媒;テルピネオール、ターピネオールC、ジヒドロターピネオール、ジヒドロターピニルアセテート、テルソルブDTO−210、テルソルブTHA−90、テルソルブTHA−70、テルソルブTOE−100、ジヒドロキシターピニルオキシエタノール、ターピニルメチルエーテル、ジヒドロターピニルメチルエーテル、テルソルブMTPH等のテルペン系溶媒;シクロヘキサノン、2−ヘキサノン、2−ヘプタノン、2−オクタノン、1,3−ジオキソラン−2−オン、1,5,5−トリメチルシクロヘキセン−3−オン等のケトン系溶媒;ジエチレングリコールエチルエーテル、ジエチレングリコールジエチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノブチルエーテル、プロピレングリコールモノメチルエーテルアセテート、ジエチレングリコールエチルエーテルアセテート、ジエチレングリコールプロピルエーテルアセテート、ジエチレングリコールイソプロピルエーテルアセテート、ジエチレングリコールブチルエーテルアセテート、ジエチレングリコール−t−ブチルエーテルアセテート、トリエチレングリコールメチルエーテルアセテート、トリエチレングリコールエチルエーテルアセテート、トリエチレングリコールプロピルエーテルアセテート、トリエチレングリコールイソプロピルエーテルアセテート、トリエチレングリコールブチルエーテルアセテート、トリエチレングリコール−t−ブチルエーテルアセテート、ジプロピレングリコールジメチルエーテル、ジプロピレングリコールモノブチルエーテル等のアルキレングリコール系溶媒;ジヘキシルエーテル、ブチルフェニルエーテル、ペンチルフェニルエーテル、メトキシトルエン、ベンジルエチルエーテル等のエーテル系溶媒;プロピレンカーボネート、エチレンカーボネート等のカーボネート系溶媒;N,N−ジメチルホルムアミド、N,N−ジメチルアセトアミド、N−メチルピロリドン等のアミド系溶媒,マロノニトリル等のニトリル系溶媒が例示できる。
なかでも、テルピネオール、テルソルブMTPH,γ−ブチロラクトン、N−メチルピロリドン、グリコールスルファイト、プロピレンカーボネートが好ましい。
これらの溶媒は、1種を単独で又は2種以上を組み合わせて使用することができる。
The solvent as the component (B) is not particularly limited as long as it can disperse the above-described etching components. When the liquid composition of the present invention is printed using screen printing, if the viscosity changes due to volatilization of the solvent during printing, the printability changes, so the vapor pressure at 25 ° C. is 1.34 ×. It is less than 10 3 Pa, preferably less than 1.0 × 10 3 Pa · s.
Solvents include aliphatic hydrocarbon solvents such as nonane, decane, dodecane, and tetradecane; aromatic hydrocarbon solvents such as ethylbenzene, anisole, mesitylene, naphthalene, cyclohexylbenzene, diethylbenzene, phenylacetonitrile, phenylcyclohexane, benzonitrile, and mesitylene Solvent; ester solvent such as isobutyl acetate, methyl propionate, ethyl propionate, γ-butyrolactone, glycol sulfite, ethyl lactate, ethyl lactate; alcohol solvent such as 1-butanol, cyclohexanol, glycerin; terpineol, Terpineol C, dihydroterpineol, dihydroterpinel acetate, tersolve DTO-210, tersolve THA-90, tersolve THA-70, tersolve TOE-10 Terpene solvents such as cyclohexanone, 2-hexanone, 2-heptanone, 2-octanone, 1,3-dioxolane-2 Ketone solvents such as -one, 1,5,5-trimethylcyclohexen-3-one; diethylene glycol ethyl ether, diethylene glycol diethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol monopropyl ether, propylene glycol monobutyl ether , Propylene glycol monomethyl ether acetate, diethylene glycol ethyl ether acetate, diethylene glycol propyl acetate Teracetate, diethylene glycol isopropyl ether acetate, diethylene glycol butyl ether acetate, diethylene glycol-t-butyl ether acetate, triethylene glycol methyl ether acetate, triethylene glycol ethyl ether acetate, triethylene glycol propyl ether acetate, triethylene glycol isopropyl ether acetate, triethylene glycol Alkylene glycol solvents such as butyl ether acetate, triethylene glycol-t-butyl ether acetate, dipropylene glycol dimethyl ether, dipropylene glycol monobutyl ether; dihexyl ether, butyl phenyl ether, pentyl phenyl ether, methoxytoluene Ether solvents such as benzyl ethyl ether; carbonate solvents such as propylene carbonate and ethylene carbonate; amide solvents such as N, N-dimethylformamide, N, N-dimethylacetamide and N-methylpyrrolidone, and nitrile solvents such as malononitrile Can be illustrated.
Of these, terpineol, tersolve MTPH, γ-butyrolactone, N-methylpyrrolidone, glycol sulfite, and propylene carbonate are preferable.
These solvents can be used alone or in combination of two or more.
溶媒の含有率は、使用時における組成物の性状を考慮して適宜調整すればよい。通常、液状組成物全体に対して15〜65質量%であることが好ましく、25〜50質量%であることが特に好ましい。 The content of the solvent may be appropriately adjusted in consideration of the properties of the composition at the time of use. Usually, it is preferably 15 to 65% by mass, particularly preferably 25 to 50% by mass, based on the whole liquid composition.
(C)成分であるチキソ性付与剤(チキソ性コントロール材料)は、エッチング成分等が液状組成物に溶解又は分散した際に、水素結合等によりゆるい疑凝集を形成することによりチキソ性を付与する添加剤である。
印刷法によっては、細線描画性のためにチキソ性を付与することが好ましい。チキソ性を付与する方法としては、チキソ性付与剤を使用する方法や、微粒子を分散する方法が挙げられる。これらの方法は、併用してもよい。
Component (C), a thixotropic agent (thixotropic control material), imparts thixotropy by forming loose aggregates due to hydrogen bonding or the like when an etching component or the like is dissolved or dispersed in a liquid composition. It is an additive.
Depending on the printing method, it is preferable to impart thixotropy for fine line drawing. Examples of the method for imparting thixotropy include a method using a thixotropic agent and a method for dispersing fine particles. These methods may be used in combination.
チキソ性付与剤としては、エチルセルロース、BYK−405、410、411、415、420、425、420、430、431等(ビック・ケミー株式会社)、Disparlonチクソトロピック剤シリーズ(楠本化成)等の市販されているものが挙げられる。尚、チキソ性付与剤は、使用する溶媒と目的のチキソ性を得られれば、特に限定はない。
また、ポリシロキサン、ポリアクリル、ポリアミド、ポリビニルアルコール、アルキル変性セルロース、ペプチド、ポリペプチド、及びこれらのうち2つ以上の構造を有する共重合体も好ましい。
As the thixotropic agent, ethyl cellulose, BYK-405, 410, 411, 415, 420, 425, 420, 430, 431, etc. (Bic Chemie Co., Ltd.), Disparlon thixotropic agent series (Enomoto Kasei) and the like are commercially available. Are listed. The thixotropic agent is not particularly limited as long as the solvent to be used and the desired thixotropy can be obtained.
In addition, polysiloxane, polyacryl, polyamide, polyvinyl alcohol, alkyl-modified cellulose, peptide, polypeptide, and a copolymer having two or more of these structures are also preferable.
微粒子としては、有機微粒子や、金属酸化物粒子等の無機微粒子が挙げられる。微粒子を添加することで、粘度やチキソ性を適宜調整でき、印刷性(例えば、細線描画性や形状保持性)やエッチング性を制御することができる。また、無機薄膜のエッチング温度まで加熱すると、エッチング成分は液状になるが、粒子により流動性が抑制され印刷されたSiN液状組成物の形状が変形することを防ぐ。 Examples of the fine particles include organic fine particles and inorganic fine particles such as metal oxide particles. By adding fine particles, viscosity and thixotropy can be appropriately adjusted, and printability (for example, fine line drawing property and shape retention) and etching property can be controlled. Further, when heated to the etching temperature of the inorganic thin film, the etching component becomes liquid, but the fluidity is suppressed by the particles and the shape of the printed SiN liquid composition is prevented from being deformed.
有機微粒子としては例えば、ポリスチレンビーズ、ポリエチレン粒子、アクリル粒子、ポリシロキサン樹脂粒子、イソプレンゴム粒子、ポリアミド粒子を例示することができる。
無機微粒子としては、酸化銅、水酸化銅、酸化鉄、アルミナ、酸化亜鉛、酸化鉛、マグネシア、酸化スズ等の金属酸化物粒子、炭酸カルシウム、カーボン、シリカ、マイカ、スメクタイトを例示することができる。
また、表面が電気的に引き合う粒子であれば液状組成物中で疑凝集を形成することから、同様の効果が期待できる。
Examples of the organic fine particles include polystyrene beads, polyethylene particles, acrylic particles, polysiloxane resin particles, isoprene rubber particles, and polyamide particles.
Examples of the inorganic fine particles include metal oxide particles such as copper oxide, copper hydroxide, iron oxide, alumina, zinc oxide, lead oxide, magnesia, tin oxide, calcium carbonate, carbon, silica, mica, and smectite. .
Further, if the surface is an electrically attracting particle, a similar effect can be expected because a pseudo-aggregation is formed in the liquid composition.
微粒子の一次粒子形状は、概球状、針状、板状、米粒状等から選択できる。特に、チキソ性付与を目的とする場合は、針状、板状、米粒状、数珠状の形状が好ましい。
尚、微粒子の分散のため、目的の機能を損なわない範囲で、分散助剤や分散安定剤を添加することができる。
微粒子の長径(長辺)は10nm〜10μmが好ましい。
尚、微粒子の長径(長辺)は前述のエッチング成分の粒径をSEM観察像から求める方法と同様の方法で求められる。
The primary particle shape of the fine particles can be selected from a substantially spherical shape, a needle shape, a plate shape, a rice grain shape and the like. In particular, for the purpose of imparting thixotropy, a needle shape, a plate shape, a rice grain shape, or a bead shape is preferable.
For dispersion of the fine particles, a dispersion aid or a dispersion stabilizer can be added as long as the target function is not impaired.
The major axis (long side) of the fine particles is preferably 10 nm to 10 μm.
The major axis (long side) of the fine particles can be obtained by a method similar to the method for obtaining the particle size of the etching component from the SEM observation image.
チキソ性付与剤の含有率は、液体組成物全体に対して0.1〜5.0質量%である。0.1質量%未満ではチキソ性の発現に十分な効果が得られなくなる。一方、5.0質量%を超えると粘度が高くなりすぎることがある。チキソ性付与剤の含有率は、特に、1.0〜4.0質量%であることが好ましい。 The content rate of a thixotropic agent is 0.1-5.0 mass% with respect to the whole liquid composition. If it is less than 0.1% by mass, a sufficient effect for the expression of thixotropy cannot be obtained. On the other hand, if it exceeds 5.0 mass%, the viscosity may become too high. The content of the thixotropic agent is particularly preferably 1.0 to 4.0% by mass.
本発明の液状組成物は、さらに、250℃において不揮発性の液体であり、エッチング成分を溶解する化合物(成分(D))を含んでもよい。これにより、エッチング成分として使用できる化合物の選択肢を増やすことができる。また、無機薄膜の除去温度をより低温にでき、エッチング速度も向上する。
成分(D)としては、ホウ素及び該ホウ素と結合したハロゲンとを構造中に含むルイス酸、該ルイス酸の塩、該ルイス酸を発生する化合物、又はイオン液体が挙げられる。
ホウ素及び該ホウ素と結合したハロゲンとを構造中に含むルイス酸、該ルイス酸の塩、及び該ルイス酸を発生する化合物は、上述したエッチング成分と同様である。上記例から、エッチング成分を溶解するものを選択すればよい。
The liquid composition of the present invention is a non-volatile liquid at 250 ° C. and may further contain a compound (component (D)) that dissolves the etching component. Thereby, the choice of the compound which can be used as an etching component can be increased. Moreover, the removal temperature of the inorganic thin film can be made lower, and the etching rate is also improved.
Examples of the component (D) include a Lewis acid containing boron and a halogen bonded to the boron in the structure, a salt of the Lewis acid, a compound that generates the Lewis acid, or an ionic liquid.
The Lewis acid containing boron and halogen bonded to the boron in the structure, the salt of the Lewis acid, and the compound generating the Lewis acid are the same as the etching component described above. What is necessary is just to select what melt | dissolves an etching component from the said example.
イオン液体(イオン性液体)としては、公知のものが使用できるが、イオン液体のアニオンに、フッ素を含有することが好ましい。具体的には、アニオンはテトラフルオロホウ酸イオン、ヘキサフルオロリン酸イオン等が挙げられる。
また、イオン液体のカチオンとしては、イミダゾリウムカチオン、ピリジニウムカチオン等が挙げられる。
As the ionic liquid (ionic liquid), known ones can be used, but it is preferable that the anion of the ionic liquid contains fluorine. Specifically, examples of the anion include tetrafluoroborate ion and hexafluorophosphate ion.
Examples of the cation of the ionic liquid include an imidazolium cation and a pyridinium cation.
成分(D)の具体例としては、1,3−ビス(2,4,6−トリメチルフェニル)−4,5−ジヒドロイミダゾリウムテトラフルオロホウ酸塩、1−ブチル−3−メチルイミダゾリウムテトラフルオロホウ酸塩、1−ヘキシル−3−メチルイミダゾリウムテトラフルオロホウ酸塩、1−エチル−3−メチルイミダゾリウムテトラフルオロホウ酸塩、1−エチル−2,3−ジメチルイミダゾリウムテトラフルオロホウ酸塩、1−ヘキシル−3−メチルイミダゾリウムテトラフルオロホウ酸塩、1−メチル−3−オクチルイミダゾリウムテトラフルオロホウ酸塩、1−ブチル−2,3−ジメチルイミダゾリウムテトラフルオロホウ酸塩、1,3−ジ−tert−ブチルイミダゾリニウムテトラフルオロホウ酸塩、1−エチル−3−メチルイミダゾリウムヘキサフルオロリン酸塩、1−メチル−3−オクチルイミダゾリウムヘキサフルオロリン酸塩等のイミダゾリウム塩、
1−ブチル−3−メチルピリジニウムテトラフルオロホウ酸塩、1−ブチルピリジニウムテトラフルオロホウ酸塩、テトラフルオロホウ酸2,4,6−トリメチルピリジニウム、1−ブチル−4−メチルピリジニウムヘキサフルオロリン酸塩等のピリジニウム塩、
1−ブチル−1−メチルピペリジニウムテトラフルオロホウ酸、1−エチル−1−メチルピペリジニウムテトラフルオロホウ酸塩、1−ブチル−1−メチルピペリジニウムヘキサフルオロリン酸塩等のピペリジニウム塩、
1−ブチル−1−メチルピロリジニウムテトラフルオロホウ酸塩、1−エチル−1−メチルピロリジニウムテトラフルオロホウ酸塩、1−ブチル−1−メチルピロリジニウムヘキサフルオロリン酸塩等のピロリジニウム塩、等が好ましい。
Specific examples of component (D) include 1,3-bis (2,4,6-trimethylphenyl) -4,5-dihydroimidazolium tetrafluoroborate, 1-butyl-3-methylimidazolium tetrafluoro Borate, 1-hexyl-3-methylimidazolium tetrafluoroborate, 1-ethyl-3-methylimidazolium tetrafluoroborate, 1-ethyl-2,3-dimethylimidazolium tetrafluoroborate 1-hexyl-3-methylimidazolium tetrafluoroborate, 1-methyl-3-octylimidazolium tetrafluoroborate, 1-butyl-2,3-dimethylimidazolium tetrafluoroborate, 1, 3-di-tert-butylimidazolinium tetrafluoroborate, 1-ethyl-3-methylimidazole Ium hexafluorophosphate, 1-methyl-3-imidazolium salts such as octyl imidazolium hexafluorophosphate,
1-butyl-3-methylpyridinium tetrafluoroborate, 1-butylpyridinium tetrafluoroborate, 2,4,6-trimethylpyridinium tetrafluoroborate, 1-butyl-4-methylpyridinium hexafluorophosphate Pyridinium salt, etc.
Piperidinium salts such as 1-butyl-1-methylpiperidinium tetrafluoroborate, 1-ethyl-1-methylpiperidinium tetrafluoroborate, 1-butyl-1-methylpiperidinium hexafluorophosphate ,
Pyrrolidinium such as 1-butyl-1-methylpyrrolidinium tetrafluoroborate, 1-ethyl-1-methylpyrrolidinium tetrafluoroborate, 1-butyl-1-methylpyrrolidinium hexafluorophosphate Salt, etc. are preferred.
成分(D)の含有率は、液体組成物全体に対して3.0〜64.0質量%であることが好ましく、特に、5.0〜56.0質量%が好ましい。 It is preferable that the content rate of a component (D) is 3.0-64.0 mass% with respect to the whole liquid composition, and 5.0-56.0 mass% is especially preferable.
本発明の液状組成物は、上述した各成分の他に、必要に応じて任意に、基板への濡れ性調整剤、粒子分散剤、脱泡剤、柚子肌等を防止するための外観向上剤(レベリング剤)、均一乾燥促進のための添加剤等の添加剤や、ドーピング剤、pH調整剤等を添加することができる。 In addition to the above-described components, the liquid composition of the present invention optionally has an appearance improving agent for preventing wettability adjusting agents, particle dispersants, defoaming agents, cocoon skin, etc. (Leveling agents), additives such as additives for promoting uniform drying, doping agents, pH adjusting agents, and the like can be added.
本発明の液状組成物は、上述した(A)〜(C)成分、及び、必要に応じて配合される上記添加剤等を混合することにより製造できる。
液状組成物の均一性を向上させるために、プロペラ撹拌、超音波分散装置(例、日本精機製作所製、超音波ホモジナイザー)、自転公転ミキサー(例、シンキー製、泡取り錬太郎)、高速乳化・分散機(例、プライミクス社製TKホモミクサーシリーズ)、らいかい機、3本ロールミル、ビーズミル、サンドミル、ポットミル等の分散機を使用して混合させることが好ましい。尚、分散はこれら装置を単独で、又は組合せて実施することができる。
The liquid composition of the present invention can be produced by mixing the above-mentioned components (A) to (C) and the above-mentioned additives blended as necessary.
In order to improve the uniformity of the liquid composition, propeller agitation, ultrasonic dispersion device (eg, Nippon Seiki Seisakusho, Ultrasonic Homogenizer), revolving mixer (eg, Shinky, Awatake Rentaro), high speed emulsification It is preferable to mix using a disperser such as a disperser (eg, TK homomixer series manufactured by PRIMIX Co., Ltd.), a rake machine, a three-roll mill, a bead mill, a sand mill, or a pot mill. In addition, dispersion | distribution can implement these apparatuses individually or in combination.
分散後、組成物中に気泡が発生した場合は、減圧下への放置、減圧下での撹拌脱泡等により液状組成物中の気泡を除去することができる。 When air bubbles are generated in the composition after dispersion, the air bubbles in the liquid composition can be removed by standing under reduced pressure, stirring and degassing under reduced pressure, or the like.
本発明の液状組成物は、無機薄膜、特にSiN膜のエッチングペーストとして好適に使用できる。
本発明の液状組成物は、例えば、有版印刷として、スクリーン印刷、フレキソ印刷、マイクロコンタクトプリント等、無版印刷として、インクジェット印刷、スリット印刷、ディスペンサ印刷等に適用できる。
なかでも、非接触でパターニング可能な印刷方法が、印刷圧力の印加による基板の損傷を回避できるため好ましい。
The liquid composition of the present invention can be suitably used as an etching paste for inorganic thin films, particularly SiN films.
The liquid composition of the present invention can be applied to, for example, plate printing, screen printing, flexographic printing, microcontact printing, etc., and plateless printing, inkjet printing, slit printing, dispenser printing, and the like.
In particular, a printing method capable of patterning without contact is preferable because damage to the substrate due to application of a printing pressure can be avoided.
液状組成物の粘度は、印刷方法や印刷装置に依存することから、特に限定されず、各々の印刷法に適するように調製することができる。
例えば、スクリーン印刷では25℃における粘度が、100mPa・s以上であることが好ましく、特に、1Pa・s以上であることが好ましい。
インクジェット印刷では、3〜20mPa・sが一般的に好ましい範囲である。
The viscosity of the liquid composition is not particularly limited because it depends on a printing method and a printing apparatus, and can be prepared so as to be suitable for each printing method.
For example, in screen printing, the viscosity at 25 ° C. is preferably 100 mPa · s or more, and particularly preferably 1 Pa · s or more.
In inkjet printing, 3 to 20 mPa · s is generally a preferred range.
液状組成物を使用して、SiN膜を除去する方法は、本発明の液状組成物を、印刷法によりSiN膜上に形成する工程(印刷工程)と、加熱によりSiN膜を除去する工程(エッチング工程)と、を有する。
SiN膜は、CMOS等の半導体素子の層間絶縁膜、パッシベーション膜等や、太陽電池等の反射防止膜等として使用されている。SiN膜は化学蒸着法(CVD)等、公知の方法で形成される。尚、「SiN」は化学量論比(Si:N)が1:1であることを意味するものではない。
The method of removing the SiN film using the liquid composition includes a step of forming the liquid composition of the present invention on the SiN film by a printing method (printing step) and a step of removing the SiN film by heating (etching). Step).
The SiN film is used as an interlayer insulating film of a semiconductor element such as a CMOS, a passivation film, an antireflection film of a solar cell, or the like. The SiN film is formed by a known method such as chemical vapor deposition (CVD). “SiN” does not mean that the stoichiometric ratio (Si: N) is 1: 1.
印刷工程では、上述した公知の印刷法により、液状組成物をSiN膜上の所望のパターンを形成する。パターンの下部に位置するSiN膜が最終的に除去(エッチング)される。
印刷後、必要であれば加熱や減圧により、液状組成物の溶媒を揮発、除去する。溶媒の除去は、エッチング工程における加熱と兼ねてもよいが、それぞれの温度条件が異なる場合もあるため、適宜選択する。
In the printing step, a desired pattern on the SiN film is formed from the liquid composition by the known printing method described above. The SiN film located under the pattern is finally removed (etched).
After printing, if necessary, the solvent of the liquid composition is volatilized and removed by heating or reduced pressure. The removal of the solvent may be combined with the heating in the etching step, but is appropriately selected because each temperature condition may be different.
エッチング工程では、100〜250℃、より好ましくは100〜200℃で1〜60分間加熱する。250℃を超えると、例えば、太陽電池の場合、n+層等の内にドープされているドーパントが拡散し、P型/N型界面に相互拡散層が生じ、太陽電池の特性が低下する場合がある。 In an etching process, it heats at 100-250 degreeC, More preferably, 100-200 degreeC for 1 to 60 minutes. When the temperature exceeds 250 ° C., for example, in the case of a solar cell, the dopant doped in the n + layer or the like diffuses, and an interdiffusion layer is formed at the P-type / N-type interface, which may deteriorate the characteristics of the solar cell. is there.
エッチング工程後、残留物がある場合は、残留物を取り除くための洗浄工程を設ける。
洗浄工程としては、純水を用いた超音波洗浄、ブラシ洗浄、スプレー洗浄、流水洗浄等が挙げられる。
If there is a residue after the etching process, a cleaning process is provided to remove the residue.
Examples of the cleaning step include ultrasonic cleaning using pure water, brush cleaning, spray cleaning, running water cleaning, and the like.
本発明のSiN膜を除去する方法は、SiN膜を有する基板に適用できる。基板としては、Siを主成分とする場合、ガラス(クオーツ、窓ガラス、ホウケイ酸ガラス、無アルカリガラス)、シリコンウェハ等を例示できる。使用目的よっては不純物を含んでもよく、酸化されていてもよい。また、表面の形状は問わない。 The method for removing a SiN film of the present invention can be applied to a substrate having a SiN film. Examples of the substrate include glass (quartz, window glass, borosilicate glass, non-alkali glass), silicon wafer, and the like when Si is the main component. Depending on the purpose of use, it may contain impurities or may be oxidized. Moreover, the shape of the surface does not matter.
本発明の方法を使用して、SiN膜を除去して得られる基板は、各種半導体装置や太陽電池の中間加工品となる。例えば、太陽電池であれば、SiN膜を除去した後に、金属ペースト等使用して給電配線(電極)を形成することにより太陽電池が作製できる。尚、露出したシリコン表面にリン等のドーパントをドーピングしてn+部を形成してもよい。 The substrate obtained by removing the SiN film using the method of the present invention becomes an intermediate processed product of various semiconductor devices and solar cells. For example, in the case of a solar cell, a solar cell can be produced by forming a power supply wiring (electrode) using a metal paste or the like after removing the SiN film. The n + portion may be formed by doping an exposed silicon surface with a dopant such as phosphorus.
実施例1
(1)液状組成物の調製
三フッ化ホウ素モノエチルアミン錯体(融点88℃)(和光純薬工業株式会社)25gを自動乳鉢で9時間すりつぶし、100μmのふるいを通して三フッ化ホウ素モノエチルアミン錯体の微粉末を得た。
三フッ化ホウ素モノエチルアミン錯体の微粉末6.87g、シリカ粒子(AEROSIL R202,日本アエロジル)0.13g、及びテルピネオール異性体混合3.5gを、メノウ乳鉢で混ぜ合わせて液状組成物(SiNエッチングペースト)を得た。
Example 1
(1) Preparation of liquid composition Boron trifluoride monoethylamine complex (melting point: 88 ° C.) (Wako Pure Chemical Industries, Ltd.) 25 g was ground in an automatic mortar for 9 hours and passed through a 100 μm sieve. A powder was obtained.
Boron trifluoride monoethylamine complex powder 6.87g, silica particles (AEROSIL R202, Nippon Aerosil) 0.13g, and terpineol isomer mixture 3.5g are mixed in an agate mortar to form a liquid composition (SiN etching paste) )
(2)SiNエッチングペーストの印刷及びSiN膜のエッチング
鏡面上にPE−CVDによりSiO2を150nm、及び、SiNを90nm積層したP型シリコンウェハ(1〜50Ω)(水戸精工株式会社)をSiN付きシリコン基板として用いた。
SiNエッチングペーストをスクリーン印刷により、SiN膜上に5cm×5cmの正方形と、幅が50μm、75μm、及び100μmである直線を印刷した。
印刷したSiN膜付きシリコン基板を、200℃に加熱したホットプレート上で30分加熱処理した後、放冷し、超純水中で超音波洗浄した。
エッチング処理後のSiN付きシリコン基板では、印刷部の下部のSiN膜が除去されていた。
(2) Printing of SiN etching paste and etching of SiN film P-type silicon wafer (1-50Ω) (Mito Seiko Co., Ltd.) with 150 nm of SiO 2 and 90 nm of SiN laminated on the mirror surface by PE-CVD with SiN Used as a silicon substrate.
A 5 cm × 5 cm square and straight lines having widths of 50 μm, 75 μm, and 100 μm were printed on the SiN film by screen printing of the SiN etching paste.
The printed silicon substrate with the SiN film was heat-treated for 30 minutes on a hot plate heated to 200 ° C., then allowed to cool and ultrasonically cleaned in ultrapure water.
In the SiN-attached silicon substrate after the etching process, the SiN film at the lower part of the printing part has been removed.
実施例2
シリカ粒子の代わりに、長粒状(粒子径200nm、アスペクト比3)の酸化銅ナノ粒子(自家合成品)を0.35g用いた以外は実施例1と同様に液状組成物を作製し、印刷、エッチングした。
その結果、エッチング処理後のSiN付きシリコン基板では、印刷部の下部のSiN膜が除去されていた。
Example 2
Instead of silica particles, a liquid composition was prepared in the same manner as in Example 1 except that 0.35 g of long-grained (particle diameter 200 nm, aspect ratio 3) copper oxide nanoparticles (in-house synthesized product) was used, and printing, Etched.
As a result, in the silicon substrate with SiN after the etching process, the SiN film at the bottom of the printing part was removed.
実験例
実施例1と同じSiN膜上に、表1に示すフッ化ホウ素試薬を少量載せ、200℃のホットプレートで30分間加熱した。加熱時(200℃)の状態とSiN膜のエッチング結果を表1に示す。
Experimental Example A small amount of the boron fluoride reagent shown in Table 1 was placed on the same SiN film as in Example 1 and heated on a hot plate at 200 ° C. for 30 minutes. Table 1 shows the state of heating (200 ° C.) and the etching results of the SiN film.
本発明の液状組成物は、窒化シリコン(SiN)等からなる無機薄膜の除去に好適である。
本発明のSiN膜を除去する方法は、各種半導体素子や太陽電池の製造工程に使用できる。
The liquid composition of the present invention is suitable for removing an inorganic thin film made of silicon nitride (SiN) or the like.
The method of removing the SiN film of the present invention can be used for manufacturing processes of various semiconductor elements and solar cells.
Claims (12)
溶媒と、
チキソ性付与剤と、を含有する、窒化シリコンの除去に用いる液状組成物であって、
前記エッチング成分は、前記除去の温度において液化する粒子として含まれ、
前記チキソ性付与剤の含有率が、全体の0.1〜5.0質量%である、液状組成物。 At least one etching component selected from a Lewis acid containing in its structure boron and a halogen bonded to the boron, a salt of the Lewis acid, and a compound that generates the Lewis acid;
A solvent,
A liquid composition used for removing silicon nitride , comprising a thixotropic agent ,
The etching component is included as particles that liquefy at the removal temperature,
The liquid composition whose content rate of the said thixotropy imparting agent is 0.1-5.0 mass% of the whole.
加熱によりSiN膜を除去する工程と、を有する、請求項10に記載の方法。 Forming the liquid composition on the SiN film by a printing method;
And removing the SiN film by heating.