JP5758886B2 - 熱収縮性ポリエステルフィルム - Google Patents
熱収縮性ポリエステルフィルム Download PDFInfo
- Publication number
- JP5758886B2 JP5758886B2 JP2012517408A JP2012517408A JP5758886B2 JP 5758886 B2 JP5758886 B2 JP 5758886B2 JP 2012517408 A JP2012517408 A JP 2012517408A JP 2012517408 A JP2012517408 A JP 2012517408A JP 5758886 B2 JP5758886 B2 JP 5758886B2
- Authority
- JP
- Japan
- Prior art keywords
- particles
- heat
- polyester film
- shrinkable polyester
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明の熱収縮性ポリエステルフィルムの固有粘度は、200mgの試料を20mLの、フェノールおよびテトラクロロエタンの50:50の比の混合溶媒と混合して混合溶液を形成し、この混合溶液を約110℃に1時間加熱した後に、30℃で粘度計を使用して測定した。
本発明の熱収縮性ポリエステルフィルムのガラス転移温度は、試料を20℃/分の加熱速度で加熱した後に、温度計(DSC−7、パーキン・エルマー社(Perking−Elmer Corp.)製)を使用して測定した。
熱収縮性ポリエステルフィルムを20cm×20cmのサイズに切断し、次いで無荷重の状態で、90℃ 0.5℃の熱水の中で熱的に収縮させた。次いで、機械方向(MD)の熱収縮性ポリエステルフィルムの長さおよび横断方向(TD)のそのフィルムの長さを測定し、次いでその熱収縮性ポリエステルフィルムの熱収縮比を下記の式1によって得た。
熱収縮性ポリエステルフィルムのヘーズは、ASTM D−1003に基づいて測定した。熱収縮性ポリエステルフィルムの2つの周辺位置および1つの中央位置から、7つの断片を無作為に抽出した。その後、この7つの断片を5cm×5cmのサイズに切断し、ヘーズメーター(NDH 300A、日本電色工業株式会社(Nihon Denshoku Co.,Ltd.)製)の中へと置き、次いで555nmの波長を有する光を照射し、それぞれのヘーズ値(%)を測定した。最大ヘーズ値および最低ヘーズ値を除く5つのヘーズ値の平均値を算出し、こうして熱収縮性ポリエステルフィルムのヘーズを得た。
熱収縮性ポリエステルフィルムを複数のパターンで印刷し、次いでその端部を互いに付着させ、ラベルを製作した。その後、容器をこのラベルで被覆し、次いで蒸気トンネルに通して、最終製品(ラベルされた容器)を得た。熱収縮性ポリエステルフィルムの収縮均一性は、不良の外観を有するラベルの数および印刷によって撓んだラベルの数を測定することによって評価した。
熱収縮性ポリエステルフィルムのインラインコーティングされた表面およびコーティングされていない表面を、熱勾配テスター(HG−100−2、株式会社東洋精機製作所(Toyoseiki Corp.)製)を使用して、互いに接触させた。その後、A4サイズ(90〜110g/m2に相当する厚さ)の印刷用紙を、加熱用の金属シールがフィルムに密着しないように、熱収縮性ポリエステルフィルムの両方の外側に重ね、次いでこの印刷用紙でラミネートしたフィルムを、異なる温度を有する5つの金属シールの間に置き、次いでプレス下状態で12時間放置した。次いで、フィルムのプレスされたコーティングされた表面およびコーティングされていない表面がブロッキングしたかどうかを観察した。
1m×1mのサイズを有する試料を、ジャンボロール(jumbo−roll)またはミルロール(mill−roll)に基づいてフィルムロールの2つの周辺位置および1つの中央位置から選択し、それぞれの試料に形成された200μm以上の直径を有する突起の数を測定した。
熱収縮性ポリエステルフィルムの印刷均一性は、幅560mmおよび長さ2000mを有するフィルムロールに複数のパターンを印刷し、次いで2000mのフィルムロールで、突起の形成に起因する不良に印刷された部分の数を測定することにより、評価した。
<式3>
不良印刷頻度(ea/2000m)=不良に印刷された部分の数/2000(m)
0.67dl/gの固有粘度および76℃のガラス転移温度を有するコポリエステル(COPET)を、触媒としての0.05molの三酸化アンチモン、および50ppmの、2.7μmの平均粒径を有するシリカ(二酸化ケイ素)粉末を使用して、直接エステル化を通して、二塩基酸成分としての100mol%のテレフタル酸と、グリコール成分としての100mol%のエチレングリコールおよび24mol%のネオペンチルグリコールとを縮合し重合させることにより、調製した。
コポリエステル(COPET)を調製するために使用した粒子の種類、サイズおよび量;コポリエステル(COPET)の固有粘度およびガラス転移温度;コポリエステル(COPET)およびポリブチレンテレフタレート(PBT)のブレンド比;インラインコーティング(ILC)プロセスで使用した粒子のサイズおよび量;帯電防止剤の量;機械方向(MD)の未延伸フィルムの延伸条件;ならびに横断方向(TD)の未延伸フィルムの延伸条件を下記の表1に示すように変えたことを除いて、熱収縮性ポリエステルフィルムを実施例1と同様にして形成した。得られた熱収縮性ポリエステルフィルムの材料特性を下記の表3に示す。
インラインコーティング(ILC)プロセスを実施せずに熱収縮性ポリエステルフィルムを形成したことを除いて、実施例1と同様にして、熱収縮性ポリエステルフィルムを形成した。得られた熱収縮性ポリエステルフィルムの材料特性を下記の表3に示す。
コポリエステル(COPET)を調製するために使用した粒子の種類、サイズおよび量;コポリエステル(COPET)の固有粘度およびガラス転移温度;コポリエステル(COPET)およびポリブチレンテレフタレート(PBT)のブレンド比;インラインコーティング(ILC)プロセスで使用した粒子のサイズおよび量;帯電防止剤の量;機械方向(MD)の未延伸フィルムの延伸条件;ならびに横断方向(TD)の未延伸フィルムの延伸条件を下記の表2に示すように変えたことを除いて、熱収縮性ポリエステルフィルムを実施例1と同様にして形成した。得られた熱収縮性ポリエステルフィルムの材料特性を下記の表3に示す。
Claims (14)
- ポリエステル樹脂マトリクスに分散された粒子を含む熱収縮性ポリエステルフィルムであって、
前記粒子は、前記ポリエステル樹脂マトリクスの総重量基準で30〜150ppmの量で含まれ、
前記熱収縮性ポリエステルフィルムは、その表面層上に80〜200nmの平均粒径を有する粒子を含むインラインコーティング層を含み、
前記熱収縮性ポリエステルフィルムは1.0%以下のヘーズを有し;
主収縮方向の前記熱収縮性ポリエステルフィルムの収縮比は、前記熱収縮性ポリエステルフィルムが90℃で10秒間、熱水で処理されるとき、35〜80%であり;
前記主収縮方向に垂直な方向の前記熱収縮性ポリエステルフィルムの収縮比は前記熱収縮性ポリエステルフィルムが90℃で10秒間、熱水で処理されるとき、5%以下であり;
1m×1mの面積を有する試料の中に分布した200μm以上のサイズを有する突起の数は0である、熱収縮性ポリエステルフィルム。 - 前記ポリエステル樹脂マトリクスの中に分散される前記粒子は、1〜5μmの平均粒径を有する、請求項1に記載の熱収縮性ポリエステルフィルム。
- 前記粒子は、炭酸カルシウム粒子、炭酸マグネシウム粒子、炭酸バリウム粒子、硫酸バリウム粒子、リン酸リチウム粒子、リン酸カルシウム粒子、リン酸マグネシウム粒子、酸化アルミニウム粒子、酸化ケイ素粒子、酸化チタン粒子、酸化ジルコニウム粒子、カオリン粒子、タルク粒子、フッ化リチウム粒子、シュウ酸のアルカリ土類金属塩粒子、アルカリ土類金属塩粒子、亜鉛塩粒子、マンガン塩粒子、ジビニルベンゼン、スチレン、(メタ)アクリル酸などのビニルモノマーのホモポリマーまたはコポリマーの粒子、ポリテトラフルオロエチレン粒子、ベンゾグアナミン樹脂粒子、熱硬化性尿素樹脂粒子、熱硬化性フェノール樹脂粒子、ケイ素樹脂粒子、および架橋ポリスチレン粒子から選択される少なくとも1つを含む、請求項1または請求項2に記載の熱収縮性ポリエステルフィルム。
- 前記インラインコーティング層は、0.01〜0.10重量%の粒子を含むコーティング溶液を使用して形成される、請求項1に記載の熱収縮性ポリエステルフィルム。
- 前記インラインコーティング層はバインダー樹脂を含む、請求項1に記載の熱収縮性ポリエステルフィルム。
- 前記インラインコーティング層は帯電防止剤を含む、請求項1に記載の熱収縮性ポリエステルフィルム。
- 前記ポリエステル樹脂マトリクスは、テレフタル酸、シュウ酸、マロン酸、コハク酸、アジピン酸、スベリン酸、アゼライン酸、セバシン酸、フタル酸、イソフタル酸、ナフタレンジカルボン酸およびジフェニルエーテルジカルボン酸などの1以上のジカルボン酸を含むジカルボン酸成分と、エチレングリコール、ネオペンチルグリコール、プロピレングリコール、トリメチレングリコール、テトラメチレングリコール、ヘキサメチレングリコール、ジエチレングリコール、ポリアルキレングリコール、1,4−シクロヘキサンジメタノールなどの1以上のジオールを含むジオール成分とを重合することにより得られるコポリエステルから選択される少なくとも1つ;またはホモポリエステルおよび前記コポリエステルの混合物を含む、請求項1に記載の熱収縮性ポリエステルフィルム。
- 前記コポリエステルは、前記ジカルボン酸成分の全量基準で80mol%以上のテレフタル酸、および前記ジオール成分の全量基準で14〜24mol%のジオール(エチレングリコールを除く)を含む、請求項7に記載の熱収縮性ポリエステルフィルム。
- ホモポリエステルおよびコポリエステルの前記混合物は、前記ジカルボン酸成分の全量基準で80mol%以上のテレフタル酸、および前記ジオール成分の全量基準で20〜36mol%のジオール(エチレングリコールを除く)を含む、請求項7に記載の熱収縮性ポリエステルフィルム。
- 前記コポリエステルは、67〜77℃のガラス転移温度および0.60〜0.70dl/gの固有粘度を有する、請求項7に記載の熱収縮性ポリエステルフィルム。
- 前記ホモポリエステルは、ポリブチレンテレフタレートまたはポリエチレンテレフタレートである、請求項7に記載の熱収縮性ポリエステルフィルム。
- 前記コポリエステルは、前記ポリエステル樹脂マトリクスの全量基準で85〜93重量%の量で含まれる、請求項7に記載の熱収縮性ポリエステルフィルム。
- 熱収縮性ポリエステルフィルムを形成する方法であって、前記熱収縮性ポリエステルフィルムは、ポリエステルを押出および延伸することにより形成され、前記方法は、
30〜150ppmの、1〜5μmの平均粒径を有する粒子を含有するポリエステルを200〜350℃で押出してポリエステルシートを形成する工程と;
前記ポリエステルシートを0.01〜0.10重量%の、80〜200nmの平均粒径を有しかつバインダー樹脂の中に分散された粒子を含むコーティング溶液でコーティングする工程と;
前記ポリエステルシートを80〜100℃で予備加熱する工程と;
予備加熱した前記ポリエステルシートを70〜95℃で横断方向に延伸する工程と、
を含む方法。 - 前記コーティング溶液は帯電防止剤を含む、請求項13に記載の方法。