JP5735004B2 - 変性ポリプロピレン組成物およびそれを用いた積層体 - Google Patents
変性ポリプロピレン組成物およびそれを用いた積層体 Download PDFInfo
- Publication number
- JP5735004B2 JP5735004B2 JP2012547888A JP2012547888A JP5735004B2 JP 5735004 B2 JP5735004 B2 JP 5735004B2 JP 2012547888 A JP2012547888 A JP 2012547888A JP 2012547888 A JP2012547888 A JP 2012547888A JP 5735004 B2 JP5735004 B2 JP 5735004B2
- Authority
- JP
- Japan
- Prior art keywords
- modified polypropylene
- weight
- propylene
- layer
- polypropylene composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
〈1〉プロピレン系重合体(A−1)60〜85重量%とメルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が0.01〜40g/10分であり、密度(ASTM D1505)が0.900g/cm3 以下のエチレン・α−オレフィン共重合体(B)10〜30重量%と、不飽和カルボン酸もしくはその誘導体で一部または全部がグラフト変性された変性ポリプロピレン(C)0.01〜10重量%を含有してなる変性ポリプロピレン組成物〔(A−1)+(B)+(C)=100重量%とする。〕であって、
当該プロピレン系重合体(A−1)が、
[1]MFR(230℃、2.16kg荷重) が1〜50(g/10分)、
[2]TREFによる溶出ピーク温度が75℃以下であり、且つ、溶出積算値が20℃で0.1重量%未満、
[3]DSCで求めた融点が135℃以下、
であることを特徴とする変性ポリプロピレン組成物。
であり、好ましくは以下のいずれかである。
〈2〉プロピレン系重合体(A−1)25〜85重量%とプロピレン系重合体(A−2)0〜45重量%と、メルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が0.01〜40g/10分であり、密度(ASTM D1505)が0.900g/cm3 以下のエチレン・α−オレフィン共重合体(B)10〜30重量%と、不飽和カルボン酸もしくはその誘導体で一部または全部がグラフト変性された変性ポリプロピレン(C)0.01〜10重量%を含有してなる変性ポリプロピレン組成物〔(A−1)+(A−2)+(B)+(C)=100重量%とする。〕であって、
当該プロピレン系重合体(A−1)が、
[1]MFR(230℃、2.16kg荷重) が1〜50(g/10分)、
[2]TREFによる溶出ピーク温度が75℃以下であり、且つ、溶出積算値が20℃で0.1重量%未満、
[3]DSCで求めた融点が135℃以下であり、
当該プロピレン系樹脂(A−2)が、TREFによる溶出ピーク温度が75℃を超えるものであることを特徴とする変性ポリプロピレン組成物。
〈3〉前記プロピレン系重合体(A−1)が、メタロセン触媒の存在下にプロピレンの単独重合またはプロピレンとプロピレンを除く炭素数2〜20のα−オレフィンとを共重合して得られる(共) 重合体であることを特徴とする前記の変性ポリプロピレン組成物。
〈4〉前記プロピレン系重合体(A−1)のメルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が2〜6g/10分であることを特徴とする前記の変性ポリプロピレン組成物。
〈5〉前記の変性ポリプロピレン組成物からなる組成物層と、該組成物層の片面または両面上に設けられた樹脂層とからなる2層または3層構造を含む積層体。
〈6〉前記樹脂層が、少なくとも極性基を有するモノマーを含む重合体からなる層を含むことを特徴とする前記の積層体。
〈7〉プロピレン系重合体(A’−1)60〜85重量%とメルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が0.01〜40g/10分であり、密度(ASTM D1505)が0.900g/cm3 以下のエチレン・α- オレフィン共重合体(B)10〜30重量%と、不飽和カルボン酸もしくはその誘導体で一部または全部がグラフト変性された変性ポリプロピレン(C)0.01〜10重量%を含有してなる変性ポリプロピレン組成物〔(A'−1)+(B)+(C)=100重量%とする。〕であって、
当該プロピレン系重合体(A’−1)が、
[1]MFR(230℃、2.16kg荷重)が1〜50(g/10分)、
[2’]TREFによる溶出ピーク温度が75℃以下、
[3]DSCで求めた融点が135℃以下、
であることを特徴とする変性ポリプロピレン組成物。
であり、好ましくは、
〈8〉エチレン−ビニルアルコール共重合体からなる層(Z)、前記のいずれかの変性ポリプロピレン組成物からなる層(Y)、および未変性ポリプロピレンからなる層(X)が、この順で積層された積層体。
である。
本発明の変性ポリプロピレン組成物を構成する成分の一つであるプロピレン系重合体(A−1)は、[1]MFRが1〜50g/10分を満たし、[2] TREFによる溶出ピーク温度が75℃以下であり、且つ溶出積算値が20℃で0.1重量%以下であり、[3]DSCで求めた融点が135℃以下であるという特徴を有する。
本発明の変性ポリプロピレン組成物に含まれていてもよいプロピレン系重合体(A−2)は、プロピレンの単独重合体あるいはプロピレンと少量のα−オレフィンとの共重合体であり、通常、ポリプロピレンとして製造・販売されている重合体である。これらプロピレン系重合体(A−2)は、単一の重合体であっても、幾つかの異なるプロピレン系重合体の混合物であってもよい。
本発明の変性ポリプロピレン組成物を構成する成分の一つであるエチレン・α- オレフィン共重合体(B)は、メルトフローレート(MFR;ASTM D 1238、230℃、荷重2.16kg)が0.01〜40g/10分、好ましくは0.01〜20g/10分、さらに好ましくは0.1〜10g/10分の範囲内にあり、かつ、密度(ASTM D 1505)が0.900g/cm3以下、好ましくは0.850〜0.900g/cm3、さらに好ましくは0.860〜0.890g/cm3の範囲内にある。
本発明の変性ポリプロピレン組成物を構成する成分の一つである変性ポリプロピレン(C)は、不飽和カルボン酸および/またはその誘導体でグラフト変性されたポリプロピレンである。
本発明の変性ポリプロピレン組成物は、プロピレン系重合体(A−1)25〜85重量%とプロピレン系重合体(A−2)0〜45重量%と、メルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が0.01〜40g/10分であり、密度(ASTM D1505)が0.900g/cm3 以下のエチレン・α- オレフィン共重合体(B)10〜30重量%と、不飽和カルボン酸もしくはその誘導体で一部または全部がグラフト変性された変性ポリプロピレン(C)0.01〜10重量%を含有してなる変性ポリプロピレン組成物〔(A−1)+(A−2)+(B)+(C)=100重量%とする。〕である。
本発明の変性ポリプロピレン組成物は、それ単独で使用することも可能であるが、基材に積層した積層体の構成で、積層体の接着層としても好適に使用し得る。
(1)プロピレン系重合体(A−1)、(A’−1)
(i)プロピレン系重合体(A−1−1)の製造
(1)固体触媒担体の製造
1L枝付フラスコにSiO2(洞海化学社製)300gをサンプリングし、トルエン800mlを入れスラリー化した。次に5L四つ口フラスコへ移液し、トルエン260mlを加えた。メチルアミノキサン(以下MAO)トルエン溶液(アルべマール社製10wt%溶液)を2830ml導入し、室温下で30分間攪拌した。1時間かけて110℃まで昇温し、同温度で4時間攪拌処理を行った。攪拌終了後、室温まで冷却した。冷却後、上澄みトルエンを抜き出し、フレッシュなトルエンで置換し、置換率が95%になるまで置換を行った。
(2)固体触媒成分の製造(担体への金属触媒成分の担持)
グローブボックス内にて、5L四つ口フラスコにジメチルシリレンビス-(2-メチル-4-フェニルインデニル)ジルコニウムジクロリドを2.0g秤取った。フラスコを外へ出し、トルエン0.46Lと前記(1)で調製したMAO/SiO2/トルエンスラリー1.4Lを窒素下で加え、30分間攪拌し担持を行った。得られたジメチルシリレンビス-(2-メチル-4-フェニルインデニル)ジルコニウムジクロリド/MAO/SiO2/トルエンスラリーはn-ヘプタンにて99%置換を行い、最終的なスラリー量を4.5Lとした。この操作は、室温で行った。
(3)前重合[P-1]
前記固体触媒の製造の項で調製した固体触媒成分202g、トリエチルアルミニウム109mL、n-ヘプタン100Lを内容量200Lの攪拌機付きオートクレーブに挿入し、内温15〜20℃に保ちエチレンを2020g挿入し、180分間攪拌しながら反応させた。重合終了後、固体成分を沈降させ、上澄み液の除去およびn-ヘプタンによる洗浄を2回行った。得られた前重合触媒を精製ヘプタンに再懸濁して、固体触媒成分濃度で2g/Lとなるよう、n-ヘプタンにより調整を行った。一部、サンプリングを行い、前重合体の分析を行った。この前重合体は固体触媒成分1g当りポリエチレンを10g含んでいた。
(4)予備重合[P-2]
内容量58Lの管状重合器にプロピレンを57kg/hr、水素を4NL/hr、前重合で製造した触媒スラリーを固体触媒成分として3.5g/hr、トリエチルアルミニウム2.3mL/hrを連続的に供給し、気相の存在しない満液の状態にて重合した。管状反応器の温度は30℃であり、圧力は2.6MPa・Gであった。
(5)本重合[P-3]
前記の(3)予重合で得られたスラリーを内容量1000Lの攪拌機付きベッセル重合器へ送り、更に重合を行った。重合器へは、プロピレンを50kg/hr、エチレンを2.0kg/hr、水素を気相部の水素濃度が0.15mol%になるように供給した。重合温度60℃、圧力2.5MPa・Gで重合を行った。
(6)得られたプロピレン・エチレンランダム共重合体を以下の成形・加工方法[a1]ペレット化法に準拠してペレット化を行い、プロピレン系重合体(A−1−1)を得た。
(ii)プロピレン系重合体(A−1−2)
予重合を以下の様に変えた以外はプロピレン系重合体(A−1−1)と同様の方法で行った。
(4)予備重合[P-2]
内容量58Lの管状重合器にプロピレンを57kg/hr、水素を4NL/hr、前重合で製造した触媒スラリーを固体触媒成分として4.7g/hr、トリエチルアルミニウム3.1mL/hrを連続的に供給し、気相の存在しない満液の状態にて重合した。管状反応器の温度は30℃であり、圧力は2.6MPa・Gであった。
(6)得られたプロピレン系重合体(A−1−2)を以下の成形・加工方法[a1]ペレット化法に準拠してペレット化を行い、プロピレン系重合体(A−1−2)を得た。
(i)プロピレン系重合体(A−2−1)
株式会社プライムポリマー製ランダムポリプロピレン(商品名 F327):MFR=7.2g/10分、密度=0.900g/cm3、TREFによる溶出ピーク温度:95.2℃、TREFによる20℃での溶出積算値:0.4重量%
(3)エチレン・α−オレフィン共重合体(B)
(i)エチレン・プロピレン共重合体(B−1)
三井化学株式会社製エチレン・プロピレンランダム共重合体(商品名:タフマーP−0680):MFR=7.0g/10分、密度=0.870g/cm3
(4)変性ポリプロピレン(C)
(i)変性プロピレン単独重合体(C−1)
反応溶媒としてトルエンを用い、トルエン5.7リットル当たり825gのプロピレン単独重合体を160℃で溶解させた。次に、このトルエン溶液に無水マレイン酸のトルエン溶液(4.13g/250ml)およびジクミルペルオキシド(DPC)のトルエン溶液(0.33g/50ml)を別々の導管から4時間かけて除々に供給した。
(5)プロピレン系重合体(E)
(i)プロピレン系重合体(E−1)
日本ポリプロ株式会社製メタロセン系ポリプロピレン(商品名:WINTEC WFX4TA):MFR=7.0g/10分、密度=0.900g/cm3、TREFによる溶出ピーク温度:80.4℃、TREF20℃での溶出積算値:0.1重量%未満
[分析方法]
[m1]プロピレン系ランダム共重合体中のエチレン濃度Px(mol%)
プロピレン系ランダム共重合体中のエチレン濃度Px(mol%)を測定するために、サンプル20〜30mgを1,2,4−トリクロロベンゼン/重ベンゼン(2:1)溶液0.6mlに溶解後、炭素核磁気共鳴分析(13C-NMR)を行った。プロピレン、エチレン、α-オレフィンの定量はダイアッド連鎖分布より求めた。例えば、プロピレン−エチレン共重合体の場合、PP=Sαα、EP=Sαγ+Sαβ、EE=1/2(Sβδ+Sδδ)+1/4Sγδを用い、以下の計算式(Eq-7)および(Eq-8)により求めた。
プロピレン(mol%)=(PP+1/2EP)x100/(PP+1/2EP)+(1/2EP+EE)・・・(Eq-7)
エチレン(mol%)=(1/2EP+EE)x100/(PP+1/2EP)+(1/2EP+EE)・・・(Eq-8)
その他、α-オレフィンとの帰属については、Macromolecules1982,15,1150、Macromolecules1991,24,4813、J.Appl.Polym.Sci.,1991,42,399等の公開情報を参照した。
[m2]融点(Tm)
示差走査熱量計(DSC、パーキンエルマー社製)を用いて測定を行った。ここで、第3stepにおける吸熱ピークを融点(Tm)と定義した。
(測定条件)
第1step : 10℃/分で240℃まで昇温し、10分間保持する。
第2step : 10℃/分で60℃まで降温する。
第3step : 10℃/分で240℃まで昇温する。
[m3]分子量分布(Mw/Mn)[重量平均分子量(Mw)、数平均分子量(Mn)]
ウォーターズ社製GPC150C Plusを用い以下の様にして測定した。分離カラムは、TSKgel GMH6-HT及びTSKgel GMH6-HTLであり、カラムサイズはそれぞれ内径7.5mm、長さ600mmであり、カラム温度は140℃とし、移動相にはo-ジクロロベンゼン(和光純薬工業)および酸化防止剤としてBHT(和光純薬工業)0.025重量%を用い、1.0ml/minで移動させ、試料濃度は0.1重量%とし、試料注入量は500マイクロリットルとし、検出器として示差屈折計を用いた。標準ポリスチレンは、分子量がMw<1000およびMw>4×106については東ソー社製を用い、1000≦Mw≦4×106についてはプレッシャーケミカル社製を用いた。
CFCは組成分別を行う温度上昇溶離分別(TREF)部と、分子量分別を行うGPC部とを備えた下記装置を用いて、下記条件で測定し、40℃以下溶出成分の量を算出した。
測定装置 : CFC T-150A型、三菱油化(株)製、商標
カラム : Shodex AT-806MS(3本)
溶解液 : o-ジクロロベンゼン
流速 : 1.0 ml/min
試料濃度 : 0.3 wt/vol%(0.1%BHT入り)
注入量 : 0.5 ml
溶解性 : 完全溶解
検出器 : 赤外吸光検出法、3.42μ(2924cm-1)、NaCl板
溶出温度 :0〜135℃、28フラクション[0, 10, 20, 30, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 94, 97, 100, 103, 106, 109, 112, 115, 118, 121, 124, 127, 135 ℃]
[m5]メルトフローレート(MFR)
ASTM D-1238の方法により230℃、荷重2.16kgで測定した。
[m6]曲げ弾性率
ASTM D-790に準拠して測定した。
[m7]引張弾性率
ASTM D-638に準拠して測定した。
[m8]接着強度
剥離雰囲気温度23℃、剥離速度300mm/分、ピール幅15mmの条件でT型剥離して求めた。
[a1]プロピレン系ランダム共重合体粒子のペレット化法
プロピレン系ランダム共重合体100重量部に、酸化防止剤としてテトラキス[メチレン-3(3,5-ジ-t-ブチル-4-ヒドロキシフェニル)プロピオネート]メタンを0.1重量部、2,4-ビス(1,1-ジメチル)-フォスフェイトフェノールを0.1重量部、中和剤としてステアリン酸カルシウムを0.1重量部、合成シリカを0.15重量部、エルカ酸アミドを0.1重量部 配合し、KTX-30二軸押出機を用いて、樹脂温250℃で溶融混練してプロピレン系ランダム共重合体のペレット化を行った。
(1)変性ポリプロピレン組成物(S-1)の製造
プロピレン系重合体(A−2−1)68重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-1)を得た。
(2)積層構造体(F-1)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-1)、株式会社クラレ製エチレン−ビニルアルコール共重合体(EVOH)(グレードF101A; MFR=1.6g/10分、密度=1190kg/m3)を供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-1)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルムからなる積層体)を製造した。
(1)変性ポリプロピレン組成物(S-2)の製造
プロピレン系重合体(A−2−1)48重量%、プロピレン系重合体(A−1−1)20重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-2)を得た。
(2)積層構造体(F-2)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-2)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-2)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-3)の製造
プロピレン系重合体(A−2−1)33重量%、プロピレン系重合体(A−1−1)35重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-3)を得た。
(2)積層構造体(F-3)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-3)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-3)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-4)の製造
プロピレン系重合体(A−2−1)18重量%、プロピレン系重合体(A−1−1)50重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-4)を得た。
(2)積層構造体(F-4)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-4)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-4)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-5)の製造
プロピレン系重合体(A−1−1)68重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-5)を得た。
(2)積層構造体(F-5)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-5)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-5)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-6)の製造
プロピレン系重合体(A−1−1)88重量%、エチレン・プロピレン共重合体(B−1)5重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-6)を得た。
(2)積層構造体(F-6)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-6)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-6)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-7)の製造
プロピレン系重合体(A−2−1)48重量%、プロピレン系重合体(A−1−2)20重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-7)を得た。
(2)積層構造体(F-7)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-7)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-7)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-8)の製造
プロピレン系重合体(A−2−1)33重量%、プロピレン系重合体(A−1−2)35重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-8)を得た。
(2)積層構造体(F-8)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-8)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-8)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-9)の製造
プロピレン系重合体(A−2−1)18重量%、プロピレン系重合体(A−1−2)50重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-9)を得た。
(2)積層構造体(F-9)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-9)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-9)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-10)の製造
プロピレン系重合体(A−1−2)68重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-9)を得た。
(2)積層構造体(F-10)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-10)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-10)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-11)の製造
プロピレン系重合体(A−1−2)88重量%、エチレン・プロピレン共重合体(B−1)5重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-11)を得た。
(2)積層構造体(F-11)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-11)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-11)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(1)変性ポリプロピレン組成物(S-12)の製造
プロピレン系重合体(E−1)68重量%、エチレン・プロピレン共重合体(B−1)25重量%、変性プロピレン単独重合体(C−1)7重量%を予備混合し、単軸押出機(ダイ径65mmφ、L/D=28)を用いて220℃の温度で溶融混練した後ストランド状に押出し、切断してペレットを製造し、変性ポリプロピレン組成物(S-12)を得た。
(2)積層構造体(F-12)の製造
三台の押出機を1つのダイに結合した押出成形装置を用いて、それぞれの押出機に、プロピレン系重合体(A−2−1)、上記の(1)で得た変性ポリプロピレン組成物(S-12)、上記EVOHを供給し、押し出し時の最高温度を共に240℃になるように設定して、押出成形装置のTダイ(ダイ幅は350mm)から、プロピレン系重合体(A−2−1)(160μm)/変性ポリプロピレン組成物(S-12)(40μm)/EVOH(40μm)の順に積層した三層構造になるようにして5m/minの成形速度で共押出成形を行って、(X)層がプロピレン系重合体層、(Y)層が変性ポリプロピレン組成物層、(Z)層がEVOH層である3層からなる積層構造体(積層フィルム)を製造した。
(X)/(Y)/(Z)=160/40/40(μm) @5m/min(延伸前後の接着力測定)
(X)/(Y)/(Z)=40/10/20(μm) @20m/min
(X)/(Y)/(Z)=20/5/10(μm) @40m/min
(X)/(Y)/(Z)=10/2.5/5(μm) @80m/min
Claims (8)
- プロピレン系重合体(A−1)60〜85重量%とメルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が0.01〜40g/10分であり、密度(ASTM D1505)が0.900g/cm3以下のエチレン・α−オレフィン共重合体(B)10〜30重量%と、不飽和カルボン酸もしくはその誘導体で一部または全部がグラフト変性された変性ポリプロピレン(C)0.01〜10重量%を含有してなる変性ポリプロピレン組成物〔(A−1)+(B)+(C)=100重量%とする。〕であって、
当該プロピレン系重合体(A−1)が、
[1]MFR(230℃、2.16kg荷重)が1〜50(g/10分)、
[2]TREFによる溶出ピーク温度が75℃以下であり、且つ溶出積算値が20℃で0.1重量%未満、
[3]DSCで求めた融点が135℃以下、
であることを特徴とする変性ポリプロピレン組成物。 - プロピレン系重合体(A−1)25〜85重量%とプロピレン系重合体(A−2)0〜45重量%と、メルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が0.01〜40g/10分であり、密度(ASTM D1505)が0.900g/cm3以下のエチレン・α−オレフィン共重合体(B)10〜30重量%と、不飽和カルボン酸もしくはその誘導体で一部または全部がグラフト変性された変性ポリプロピレン(C)0.01〜10重量%を含有してなる変性ポリプロピレン組成物〔(A−1)+(A−2)+(B)+(C)=100重量%とする。〕であって、当該プロピレン系重合体(A−1)が、
[1]MFR(230℃、2.16kg荷重)が1〜50(g/10分)、
[2]TREFによる溶出ピーク温度が75℃以下であり、且つ溶出積算値が20℃で0.1重量%未満、
[3]DSCで求めた融点が135℃以下であり、
当該プロピレン系重合体(A−2)が、TREFによる溶出ピーク温度が75℃を超えるものであることを特徴とする変性ポリプロピレン組成物。 - 前記プロピレン系重合体(A−1)が、下記一般式(I)で示されるメタロセン触媒の存在下にプロピレンの単独重合またはプロピレンとプロピレンを除く炭素数2〜20のα−オレフィンとを共重合して得られる(共)重合体であることを特徴とする請求項1または2に記載の変性ポリプロピレン組成物。
Yは第14族元素である。Mは第4族遷移金属である。Qはハロゲン、炭化水素基、アニオン配位子または孤立電子対で配位可能な中性配位子から同一または異なる組合せで選ばれる。jは1〜4の整数である。) - 前記プロピレン系重合体(A−1)のメルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が2〜6g/10分であることを特徴とする請求項1または2に記載の変性ポリプロピレン組成物。
- 請求項1または2に記載の変性ポリプロピレン組成物からなる組成物層と、該組成物層の片面または両面上に設けられた樹脂層とからなる2層または3層構造を含む積層体。
- 前記樹脂層が、少なくとも極性基を有するモノマーを構成単位として含む重合体からなる層を含むことを特徴とする請求項5に記載の積層体。
- プロピレン系重合体(A'−1)60〜85重量%とメルトフローレート(MFR;ASTM D1238,230℃、2.16kg荷重)が0.01〜40g/10分であり、密度(ASTM D1505)が0.900g/cm3以下のエチレン・α−オレフィン共重合体(B)10〜30重量%と、不飽和カルボン酸もしくはその誘導体で一部または全部がグラフト変性された変性ポリプロピレン(C)0.01〜10重量%を含有してなる変性ポリプロピレン組成物〔(A'−1)+(B)+(C)=100重量%とする。〕であって、
当該プロピレン系重合体(A'−1)が、
[1]MFR(230℃、2.16kg荷重)が1〜50(g/10分)、
[2']TREFによる溶出ピーク温度が75℃以下、
[3]DSCで求めた融点が135℃以下、
であることを特徴とする変性ポリプロピレン組成物。 - エチレン−ビニルアルコール共重合体からなる層(Z)、請求項1、2、7のいずれか1項に記載の変性ポリプロピレン組成物からなる層(Y)、および未変性ポリプロピレンからなる層(X)が、この順で積層された積層体。