JP5722174B2 - 太陽電池用バックシート、及び、太陽電池モジュール - Google Patents
太陽電池用バックシート、及び、太陽電池モジュール Download PDFInfo
- Publication number
- JP5722174B2 JP5722174B2 JP2011200955A JP2011200955A JP5722174B2 JP 5722174 B2 JP5722174 B2 JP 5722174B2 JP 2011200955 A JP2011200955 A JP 2011200955A JP 2011200955 A JP2011200955 A JP 2011200955A JP 5722174 B2 JP5722174 B2 JP 5722174B2
- Authority
- JP
- Japan
- Prior art keywords
- pet
- film
- solar cell
- acid
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
例えば、バックシートの表面にコロナ処理、火炎処理などの表面処理を行うことで、互いの密着性を一時的に高めることができるが、表面処理後の経時変化で密着性が低下したり、表面処理したバックシートがブロッキングを起こす場合がある。
そのため、バックシートに、封止材との接着性をもたらせる機能性層、いわゆる易接着性層を形成することがある。この場合、易接着性層を有するバックシートは、バックシート本来の機能を発現しつつ、易接着性層の機能も発現することが求められる。
本発明によれば、長期に亘り安定的な発電性能が得られる太陽電池モジュールが提供される。
本発明の太陽電池用バックシートは、示差走査熱量測定(DSC)で測定されるプレピーク温度が160℃〜225℃である2軸延伸ポリエチレンテレフタレートフィルムである基材と、前記基材の少なくとも一方の面に設けられ、アクリル樹脂を含むバインダー、カルボジイミド架橋剤に由来する架橋構造部分、及び無機微粒子を含有する塗布層と、前記塗布層上に設けられ、樹脂バインダーを主成分として含有する易接着性層と、を有して構成されたものである。
また、「アクリル樹脂を含むバインダー、カルボジイミド架橋剤に由来する架橋構造部分、及び無機微粒子を含有する塗布層」を、「特定塗布層」とも称する。
ところが、熱固定温度を210℃以下に下げて設定すると、耐候性は改良されるものの、基材であるPETフィルムと、基材上の易接着性層との密着性が損なわれる問題があった。一方、熱固定温度を210℃よりも高くすることで、基材と易接着性層との密着性を向上することができるものの、基材自体の耐候性が損なわれた。
2軸延伸ポリエチレンテレフタレートフィルムは、一般に、原料であるPET原料を、押出機を用いて溶融押出して未延伸フィルムを得た後、未延伸フィルム(「原反」とも称される)をある方向(方向Aとする)に延伸し、さらに、方向Aと異なる方向(通常、直行する方向)に延伸して得られる。未延伸フィルムの延伸において、未延伸フィルムを延伸した後、延伸したまま未延伸フィルムを加熱して時間を置くことで、フィルム中のPET分子の配列を促し、フィルムの物性を制御し易い。このように、未延伸フィルムを延伸したまま加熱して時間を置くことを、熱固定という。
さらに、特定塗布層中のアクリル樹脂を含むバインダーと、易接着性層が含有する樹脂バインダーとは、互いに樹脂のバインダーである点で性質が似るため、特定塗布層と易接着性層との密着性は良いと考えられる。
ただし、本発明においては、プレピーク温度が160℃未満であると、熱固定温度が低く過ぎて熱固定が不充分となるため、プレピーク温度は160℃以上としている。
しかし、本発明の基材上に、特定塗布層が設けられていることで、基材耐候性を、特定塗布層が補完し、耐候性を向上すると考えられる。
ここで、基材(PET)の耐候性(主として、耐加水分解性)は、PETが水分に曝され、加熱されることにより生じ易い。従来のように、易接着性層と基材との密着性が不十分であったときは、太陽電池用バックシートが屋根の上等に設置され、直射日光を浴び、雨曝しになったときに、易接着性層と基材と間に水分が入り込み、日光により加熱されることにより、加水分解が進行したものと考えられる。
すなわち、本発明の基材と、特定塗布層とは、架橋構造部分により強固に結ばれ、密着しているため、雨曝しになったとしても、易接着性層と基材と間に水分が入り込む余地がないと考えられる。本発明においては、特定塗布層と易接着性層とは、基材の少なくとも一方の面に設けられていればよいが、基材の両面に、特定塗布層と易接着性層とが設けられていれば、なおのこと基材が水分から守られ、耐候性は向上すると考えられる。
ただし、本発明においては、プレピーク温度が225℃を超えると、本発明における塗布層を設けていても、もはや耐候性を補完できないため、プレピーク温度は225℃以下としている。
本発明にける基材は、示差走査熱量測定(DSC)で測定されるプレピーク温度が160℃〜225℃である2軸延伸ポリエチレンテレフタレートフィルムである。
2軸延伸とは、未延伸フィルムをある方向(方向A)に延伸した後、方向Aと異なる方向(通常は方向Aと直行する方向)に延伸することをいい、ポリエチレンテレフタレートフィルムが2つの方向に延伸されていることを意味する。
本発明において、プレピーク温度は、示差走査型熱量計〔(株)島津製作所製、DSC−50〕を用いて、常法により求められる値である。
2軸延伸PETフィルムのDSCで測定されるプレピーク温度は、205℃〜225℃であることが好ましい。
また、本発明の基材を構成するPETフィルムは、固有粘度(IV;Intrinsic Viscosity)が0.75dL/g以上であることが好ましい。PETフィルムのIVが0.75dL/g以上であると、PETの結晶化が進みにくく、PETフィルム面にキズができにくい。
PETフィルムの耐加水分解性をより高めて耐候性を向上させる観点から、IV値としては、0.78dL/g以上が好ましく、0.80dL/g以上がより好ましい。
本発明の基材を構成するPETフィルムは、酸価(AV;Acid Value)としては、5eq/トン〜21eq/トンが好ましい。酸価は、6eq/トン〜20eq/トンがより好ましく、7eq/トン〜19eq/トンが更に好ましい。酸価は、「末端カルボキシ基濃度」または「末端COOH量」とも称される。
なお、本明細書中において、「eq/トン」は1トンあたりのモル当量を表す。
AVは、PETフィルムをベンジルアルコール/クロロホルム(=2/3;体積比)の混合溶液に完全溶解させ、指示薬としてフェノールレッドを用い、基準液(0.025N KOH−メタノール混合溶液)で滴定し、その適定量から算出される値である。
さらに、本発明の基材の熱収縮率(加熱条件:150℃で30分間の加熱)は、2.0%以下であることが好ましい。熱収縮率は、後述するように、横延伸工程における熱固定及び/又は熱緩和の各工程での加熱温度(T熱固定及び/又はT熱緩和)を制御することによって上記範囲に調整することができる。
なお、本発明における熱収縮率とは、150℃で30分間の処理前後でのPETフィルムの収縮率(単位%;=処理後のフィルム長/処理前のフィルム長×100)である。
本発明の基材の厚みとしては、180μm〜350μmであることが好ましく、200μm〜320μmがより好ましく、200μm〜290μmが更に好ましい。
2軸延伸後のポリエチレンテレフタレートフィルム(PETフィルム)を構成するPETは、ジカルボン酸成分とジオール成分とを共重合させて合成されるものである。ジカルボン酸成分及びジオール成分の詳細については、後述する。また、PETは、カルボン酸基の数(a)と水酸基の数(b)との合計(a+b)が3以上である多官能モノマー(以下、「3官能以上の多官能モノマー」又は単に「多官能モノマー」ともいう。)に由来する構成単位を含むものであることが好ましい。
PETは、後述のように、例えば(A)ジカルボン酸成分と(B)ジオール成分とを周知の方法でエステル化反応及び/又はエステル交換反応させることによって得ることができ、更に好ましくは、これに3官能以上の多官能モノマーを共重合させて得られる。ジカルボン酸成分、ジオール成分、及び多官能モノマー等の例示や好ましい態様などの詳細については、後述する通りである。
カルボン酸基の数(a)と水酸基の数(b)との合計(a+b)が3以上である多官能モノマーに由来の構成単位としては、後述するように、カルボン酸基の数(a)が3以上のカルボン酸並びにこれらのエステル誘導体や酸無水物等、水酸基数(b)が3以上の多官能モノマー、並びに「一分子中に水酸基とカルボン酸基の両方を有し、カルボン酸基の数(a)と水酸基の数(b)との合計(a+b)が3以上であるオキシ酸類」などを挙げることができる。これらの例示及び好ましい態様などの詳細については、後述する通りである。
また、前記カルボン酸のカルボキシ末端、又は前記「一分子中に水酸基とカルボン酸基の両方を有する多官能モノマー」のカルボキシ末端に、l−ラクチド、d−ラクチド、ヒドロキシ安息香酸などのオキシ酸類及びその誘導体、そのオキシ酸類が複数個連なったもの等を付加させたものも好適である。
これらは、一種単独で用いても、必要に応じて、複数種を併用してもよい。
したがって、3官能以上の多官能モノマーに由来の構成単位の含有比率が0.005モル%以上であることで、耐候性、低熱収縮性、及びPETフィルム上に塗布形成される特定塗布層との密着力がさらに向上し易い。また、3官以上の多官能モノマーに由来の構成単位の含有比率が2.5モル%以下であることで、3官能以上の多官能モノマーに由来の構成単位は嵩高いため、結晶形成し難くなるのが抑制される。その結果として、結晶を介して形成される低移動成分の形成を促し、加水分解性が低下するのを抑制することができる。さらに、3官能以上の多官能モノマーに由来の構成単位の嵩高さにより、フィルム表面の微細凹凸量が増えるためアンカー効果が発現しやすく、PETフィルムと特定塗布層との密着が向上する。また、当該嵩高さにより、増加する自由体積(分子間の隙間)が抑制され、大きな自由体積中をPET分子がすり抜けることで発生する熱収縮を抑制することができる。また、3官能以上の多官能モノマーに由来の構成単位の添加過剰に伴なうガラス転移温度(Tg)の低下も抑制され、耐候性が低下防止にも有効である。
PETフィルムは、更に、オキサゾリン系化合物、カルボジイミド化合物、及びエポキシ化合物から選ばれる末端封止剤に由来する構造部分を有していることが好ましい。なお、「末端封止剤に由来する構造部分」とは、末端封止剤がPET分子末端のカルボン酸と反応して末端に結合している構造をさす。
末端封止剤は、PETフィルムの質量に対して、0.1質量%〜5質量%の範囲で含有されていることが好ましく、より好ましくは0.3質量%〜4質量%であり、さらに好ましくは0.5質量%〜2質量%である。
PETフィルム中における末端封止剤の含有比率が0.1質量%以上であることで、特定塗布層との密着が良好になると共に、AV低下効果による耐候性向上を達成できる上、低熱収縮性も付与することができる。また、PETフィルム中における末端封止剤の含有比率が5質量%以下であると、塗布層との密着が良好になると共に、末端封止剤の添加によりPETのガラス転移温度(Tg)の低下が抑制され、これによる耐候性の低下や熱収縮の増加を抑制することができる。これは、Tgが低下した分、相対的にPETの反応性が増加することで生じる加水分解性の増加を抑制したり、Tg低下で増加するPET分子の運動性が増加し易くなることで生じる熱収縮が抑制されるためである。
また、多官能性カルボジイミドとしては、重合度3〜15のポリカルボジイミドが好ましい。ポリカルボジイミドは、一般に「−R−N=C=N−」等で表される繰り返し単位を有し、前記Rは、アルキレン、アリーレン等の2価の連結基を表す。このような繰り返し単位としては、例えば、1,5−ナフタレンカルボジイミド、4,4'−ジフェニルメタンカルボジイミド、4,4'−ジフェニルジメチルメタンカルボジイミド、1,3−フェニレンカルボジイミド、2,4−トリレンカルボジイミド、2,6−トリレンカルボジイミド、2,4−トリレンカルボジイミドと2,6−トリレンカルボジイミドの混合物、ヘキサメチレンカルボジイミド、シクロヘキサン−1,4−カルボジイミド、キシリレンカルボジイミド、イソホロンカルボジイミド、ジシクロヘキシルメタン−4,4'−カルボジイミド、メチルシクロヘキサンカルボジイミド、テトラメチルキシリレンカルボジイミド、2,6−ジイソプロピルフェニルカルボジイミド及び1,3,5−トリイソプロピルベンゼン−2,4−カルボジイミドなどが挙げられる。
ここで、イソシアネート系ガスは、イソシアネート基をもつガスであり、例えば、ジイソプロピルフェニルイソシアネート、1,3,5−トリイソプロピルフェニルジイソシアネート、2−アミノ−1,3,5−トリイソプロピルフェニル−6−イソシアネート、4,4’−ジシクロヘキシルメタンジイソシアネート、イソホロンジイソシアネート、及びシクロヘキシルイソシアネートなどが挙げられる。
ビスオキサゾリン化合物としては、例えば、2,2'−ビス(2−オキサゾリン)、2,2'−ビス(4−メチル−2−オキサゾリン)、2,2'−ビス(4,4−ジメチル−2−オキサゾリン)、2,2'−ビス(4−エチル−2−オキサゾリン)、2,2'−ビス(4,4'−ジエチル−2−オキサゾリン)、2,2'−ビス(4−プロピル−2−オキサゾリン)、2,2'−ビス(4−ブチル−2−オキサゾリン)、2,2'−ビス(4−ヘキシル−2−オキサゾリン)、2,2'−ビス(4−フェニル−2−オキサゾリン)、2,2'−ビス(4−シクロヘキシル−2−オキサゾリン)、2,2'−ビス(4−ベンジル−2−オキサゾリン)、2,2'−p−フェニレンビス(2−オキサゾリン)、2,2'−m−フェニレンビス(2−オキサゾリン)、2,2'−o−フェニレンビス(2−オキサゾリン)、2,2'−p−フェニレンビス(4−メチル−2−オキサゾリン)、2,2'−p−フェニレンビス(4,4−ジメチル−2−オキサゾリン)、2,2'−m−フェニレンビス(4−メチル−2−オキサゾリン)、2,2'−m−フェニレンビス(4,4−ジメチル−2−オキサゾリン)、2,2'−エチレンビス(2−オキサゾリン)、2,2'−テトラメチレンビス(2−オキサゾリン)、2,2'−ヘキサメチレンビス(2−オキサゾリン)、2,2'−オクタメチレンビス(2−オキサゾリン)、2,2'−デカメチレンビス(2−オキサゾリン)、2,2'−エチレンビス(4−メチル−2−オキサゾリン)、2,2'−テトラメチレンビス(4,4−ジメチル−2−オキサゾリン)、2,2'−9,9'−ジフェノキシエタンビス(2−オキサゾリン)、2,2'−シクロヘキシレンビス(2−オキサゾリン)及び2,2'−ジフェニレンビス(2−オキサゾリン)等を例示することができる。これらの中では、PETとの反応性が良好で耐候性の向上効果が高い観点から、2,2'−ビス(2−オキサゾリン)が最も好ましい。
ビスオキサゾリン化合物は、本発明の効果を損なわない限り、1種単独で用いてもよいし、2種以上を組み合わせて用いてもよい。
本発明の基材の製造方法については、後に詳細に説明する。
本発明の太陽電池用バックシートが有する塗布層(特定塗布層)は、既述の本発明の基材の少なくとも一方の面に設けられた層であり、アクリル樹脂を含むバインダー、カルボジイミド架橋剤に由来する架橋構造部分、及び無機微粒子を含有する。
更に、必要に応じて、界面活性剤、酸化防止剤等を含有していてもよい。
特定塗布層は、本発明の基材の少なくとも一方の面に設けられている。すなわち、本発明の基材表面の片面に設けられていてもよいし、両面に設けられていてもよい。
特定塗布層が含有するバインダーは、少なくともアクリル樹脂を含んでいればよく、さらに、アクリル樹脂以外の樹脂を含んでいてもよい。
特定塗布層中のバインダーは、後述するカルボジイミド架橋剤と反応するカルボキシ基を含み、耐久性に優れるアクリル樹脂を少なくとも含有することで、カルボジイミド架橋剤によって架橋され、屋外で雨曝しにされるような湿熱環境下においても優れた耐久性を有する層となることができる。
特定塗布層は、カルボジイミド架橋剤に由来する架橋構造部分を含有する。
特定塗布層は、後述するように、特定塗布層を形成するための塗布液を、本発明の基材上に塗布して得た塗布膜を乾燥することにより形成することができる。特定塗布層を形成するための塗布液中には、少なくとも、既述のアクリル樹脂を含むバインダーと、カルボジイミド架橋剤と、後述する無機微粒子とを含有しておく必要がある。当該塗布液中のカルボジイミド架橋剤は、バインダー中のアクリル樹脂と反応し、特定塗布層が形成されたときには、特定塗布層は、バインダーとバインダーとを架橋する架橋構造部分を含有している。かかる架橋構造部分は、カルボジイミド架橋剤に由来する構造部分である。
耐久性に優れたアクリル樹脂を含むバインダー同士が架橋することにより、特定塗布層が湿熱環境下においても優れた耐久性を有する層となることは上述のとおりである。
1官能性カルボジイミドとしては、例えば、ジシクロヘキシルカルボジイミド、ジイソプロピルカルボジイミド、ジメチルカルボジイミド、ジイソブチルカルボジイミド、ジオクチルカルボジイミド、t−ブチルイソプロピルカルボジイミド、ジフェニルカルボジイミド、ジ−t−ブチルカルボジイミド及びジ−β−ナフチルカルボジイミドなどが挙げられ、好ましくはジシクロヘキシルカルボジイミドやジイソプロピルカルボジイミドである。
また、多官能性カルボジイミドとしては、重合度3〜15のポリカルボジイミドが好ましい。ポリカルボジイミドは、一般に「−R−N=C=N−」等で表される繰り返し単位を有し、前記Rは、アルキレン、アリーレン等の2価の連結基を表す。このような繰り返し単位としては、例えば、1,5−ナフタレンカルボジイミド、4,4'−ジフェニルメタンカルボジイミド、4,4'−ジフェニルジメチルメタンカルボジイミド、1,3−フェニレンカルボジイミド、2,4−トリレンカルボジイミド、2,6−トリレンカルボジイミド、2,4−トリレンカルボジイミドと2,6−トリレンカルボジイミドの混合物、ヘキサメチレンカルボジイミド、シクロヘキサン−1,4−カルボジイミド、キシリレンカルボジイミド、イソホロンカルボジイミド、ジシクロヘキシルメタン−4,4'−カルボジイミド、メチルシクロヘキサンカルボジイミド、テトラメチルキシリレンカルボジイミド、2,6−ジイソプロピルフェニルカルボジイミド及び1,3,5−トリイソプロピルベンゼン−2,4−カルボジイミドなどが挙げられる。
特定塗布層は、無機微粒子を含有する。
特定塗布層が無機微粒子を含有することで、太陽電池用バックシートが有する基材と易接着性層との密着力を高めることができる。
特定塗布層が含有し得る無機微粒子は特に制限されず、例えば、クレー、マイカ、酸化チタン、酸化スズ、炭酸カルシウム、カリオン、タルク、湿式シリカ、乾式シリカ、コロイド状シリカ、リン酸カルシウム、硫酸バリウム、アルミナ及びジルコニア等が挙げられる。
酸化スズは、シリカに比較して、粒子形状が不定形であることが多く相対的に表面性が大きいこと、また2次粒子、3次粒子を形成して、複雑な粒塊をつくりやすい傾向にあり、結果として、酸化スズ粒子とバインダー樹脂との結合が、シリカ粒子のそれと比較して強く保持されているものと考えられる。
特定塗布層が含有し得る無機微粒子は、酸化スズ1種であることが特に好ましい。
特定塗布層中の無機微粒子の含有量が、特定塗布層中のバインダーの全質量に対して、50質量%以上であることで、耐候性、および、易接着性層と基材との密着性を向上することができる。
バインダーに対する無機微粒子の含有量が500質量%以下であれば、特定塗布層が粉っぽくなりにくく、易接着性層と本発明の基材との密着性を損ね難い。
本発明の太陽電池用バックシートは、特定塗布層中のアクリル樹脂の酸価をA、カルボジイミド架橋剤の等量をBとするとき、アクリル樹脂に対するカルボジイミド架橋剤の質量比X(カルボジイミド架橋剤/アクリル樹脂)が、AとBとの積AB(=A×B)との間で、下記式(1)を満たすことが好ましい。
(0.8AB)/56100 < X <(2.0AB)/56100 ・・・(1)
カルボジイミド架橋剤の等量Bは、カルボジイミド基1モルを含むカルボジイミド化合物のg数である。
特定塗布層は、さらに界面活性剤を含有していてもよい。
界面活性剤としては、アニオン系やノニオン系等の公知の界面活性剤が挙げられる。特定塗布層中の界面活性剤の含有量は、0.1mg/m2〜15mg/m2が好ましく、より好ましくは0.5mg/m2〜5mg/m2である。
特定塗布層を形成するための塗布液に、上記範囲の量で界面活性剤が含まれていることで、ハジキの発生を抑えて良好に層形成ができるため、本発明の効果をより高めることができる。
特定塗布層には、本発明の目的を損なわない範囲内において、各種添加剤を含有していてもよい。かかる添加剤としては、例えば、紫外線吸収剤、光安定剤、及び酸化防止剤等が挙げられる。
特定塗布層は、バインダー、架橋剤、無機微粒子、及びその他必要に応じて含まれる成分を既述の含有量となるように含有する特定塗布層形成用の塗布液を、本発明の基材の少なくとも一方の面に塗布することにより形成される。
塗布方法としては、例えば、グラビアコーター、バーコーターなどの公知の塗布方法を利用することができる。
塗布液は、塗布溶媒として水を用いた水系でもよいし、トルエンやメチルエチルケトン等の有機溶媒を用いた溶剤系でもよい。中でも、環境負荷の観点から、水を溶媒とすることが好ましい。塗布溶媒は、1種類を単独で用いてもよいし、2種類以上を混合して用いてもよい。好ましい塗布溶媒の例として、水、水/メチルアルコール=95/5(質量比)等がある。
なお、本発明の基材に塗布液を塗布する前に、基材表面に対して、硫酸クロム酸混液による酸エッチング処理、ガス炎による火炎処理、紫外線照射処理、コロナ放電処理、グロー放電処理等の表面処理を施してもよい。
なお、特定塗布層は1層のみの単層で構成されていてもよいし、2層以上の多層であってもよい。特定塗布層が多層である場合は、多層で構成される特定塗布層の全厚みが0.2μm〜8.0μmであることが好ましい。
本発明の太陽電池用バックシートは、既述の特定塗布層上に、易接着性層を有する。
易接着性層は、少なくとも1種の樹脂バインダーを主成分として含有する。
「樹脂バインダーを主成分として含有する」とは、易接着性層が、樹脂バインダーを、易接着性層の固形分質量の50質量%を超える割合で含有することをいう。
易接着性層が含有し得る樹脂バインダーとしては、例えば、ポリエステル、ポリウレタン、アクリル樹脂、ポリオレフィン等を用いることができる。また、アクリル樹脂として、アクリルとシリコーンとの複合樹脂を用いてもよい。中でも、耐久性の観点から、アクリル樹脂、及びポリオレフィンが好ましく、アクリル樹脂を含有する特定塗布層との密着性の観点から、アクリル樹脂がより好ましい。
架橋構造部分を構成する架橋剤の例としては、エポキシ系架橋剤、イソシアネート架橋剤、メラミン架橋剤、カルボジイミド架橋剤、オキサゾリン架橋剤等の架橋剤が挙げられる。これらの中でもエポキシ系架橋剤が好ましい。市販のエポキシ系架橋剤を用いてもよく、例えば、ナガセケムテックス(株)製、デナコールEX−614B等が挙げられる。
架橋剤由来の架橋構造部分の易接着性層中における含有量は、易接着性層中のバインダー全質量に対して5質量%〜50質量%が好ましく、より好ましくは20質量%〜40質量%である。架橋構造部分の含有量が、5質量%以上であることで良好な架橋効果が得られ、易接着性層の強度低下や接着不良が起こりにくく、50質量%以下であることで、易接着性層を塗布形成する場合に、塗布液のポットライフをより長く保つことができる。
なお、易接着性層中の架橋剤に由来する架橋構造部分の含有量は、易接着性層を形成するための塗布液に含有する量に相当する。従って、易接着性層を形成するための塗布液中の架橋剤の含有量は、当該塗布液中のバインダー全質量に対して、5質量%〜50質量%とすることが好ましい。
微粒子としては、シリカ、炭酸カルシウム、酸化マグネシウム、炭酸マグネシウム、酸化錫等の無機微粒子が挙げられる。
他の添加剤としては、ポリスチレン、ポリメチルメタクリレート、シリカ等の公知のマット剤、アニオン系やノニオン系などの公知の界面活性剤などが挙げられる。
易接着性層は、少なくとも1種の樹脂バインダーを主成分として含有するシート状の部材であっても、少なくとも1種の樹脂バインダーを主成分として含有する易接着性層形成用塗布液により特定塗布層上に塗布形成される塗布層であってもよい。少なくとも1種の樹脂バインダーを主成分として含有するシート状の部材とする場合は、特定塗布層にそのまま貼り合わせるか、特定塗布層と部材との間に、公知の接着剤を付与することにより貼り合わせてもよい。
易接着性層を形成するための塗布液中の樹脂バインダーや、必要に応じて含み得る架橋剤は、既述の含有量となるように塗布液中に含有していればよい。
塗布液の塗布方法としては、例えば、グラビアコーターやバーコーターなどの公知の方法を利用することができる。塗布に用いる塗布液の溶媒としては、水でもよいし、トルエンやメチルエチルケトンのような有機溶媒でもよい。溶媒は、1種類を単独で用いてもよいし、2種類以上を混合して用いてもよい。
太陽電池用バックシートは、本発明の基材の少なくとも一方の面に、既述の特定塗布層と、易接着性層とを有すればよいが、さらに、日光を反射する反射層や、太陽電池用バックシートに意匠性をもたらす着色層を有していてもよい。
反射層には、例えば、酸化チタン等の白色顔料が含まれていればよく、また、着色層には、一般に、黒色顔料や青色顔料等が含まれている。
従って、本発明の太陽電池用バックシートは、湿熱環境下での破断伸度保持率が高い。例えば、120℃、相対湿度100%(100%RHとも記載する)環境下で48時間静置する加速試験前後における破断伸度保持率は、20%〜90%の範囲である。
上記破断伸度保持率は、具体的には、次のように算出する。
まず、上記加速試験をする前の太陽電池用バックシートと、上記加速試験をした後の太陽電池用バックシートとについて、それぞれJIS−K7127に準拠した方法により破断伸度測定する。加速試験前の太陽電池用バックシートの破断伸度をL前、加速試験後の太陽電池用バックシートの破断伸度をL後としたとき、下記式(L)から算出される。
破断伸度保持率〔%〕=(L後/L前)×100 ・・・式(L)
本発明の基材は、既述のプレピーク温度を有し得る方法であればいずれの方法により作製されてもよい。本発明においては、例えば、以下に示す本発明の基材の製造方法により最も好適に作製することができる。
以下、本発明の基材の製造方法について具体的に説明する。
前記横延伸工程は、縦延伸後のPETフィルムを延伸可能な温度に予熱する予熱工程と、予熱された前記PETフィルムを前記長手方向と直交する幅方向に緊張を与えて横延伸する延伸工程と、前記縦延伸及び前記横延伸を行なった後の前記PETフィルムの最高到達膜面温度を160℃〜225℃の範囲に加熱して熱固定する熱固定工程と、前記熱固定されたPETフィルムを加熱し、PETフィルムの緊張を緩和する熱緩和工程と、熱緩和後のPETフィルムを冷却する冷却工程とを設けて構成されたものである。
フィルム成形工程では、PET原料樹脂をシート状に溶融押出を行ない、キャスティングドラム(「チルロール」、「冷却ロール」とも称される)上で冷却してPETフィルムを成形する。本発明においては、固有粘度(IV)が0.75dL/g以上のPETフィルムが好適に成形される。
(PET原料樹脂)
PET原料樹脂は、PETフィルムの原料となり、PETを含んでいる材料であれば、特に制限されず、PETのほかに、無機粒子や有機粒子のスラリーを含んでいてもよい。また、PET原料樹脂は、触媒由来のチタン元素を含んでいてもよい。
PET原料樹脂に含まれるPETの種類は特に制限されない。
ジカルボン酸成分と、ジオール成分とを用いて合成してもよいし、市販のPETを用いてもよい。
(A)ジカルボン酸成分としては、例えば、マロン酸、コハク酸、グルタル酸、アジピン酸、スベリン酸、セバシン酸、ドデカンジオン酸、ダイマー酸、エイコサンジオン酸、ピメリン酸、アゼライン酸、メチルマロン酸、エチルマロン酸等の脂肪族ジカルボン酸類、アダマンタンジカルボン酸、ノルボルネンジカルボン酸、イソソルビド、シクロヘキサンジカルボン酸、デカリンジカルボン酸、などの脂環族ジカルボン酸、テレフタル酸、イソフタル酸、フタル酸、1,4−ナフタレンジカルボン酸、1,5−ナフタレンジカルボン酸、2,6−ナフタレンジカルボン酸、1,8−ナフタレンジカルボン酸、4,4’−ジフェニルジカルボン酸、4,4’−ジフェニルエーテルジカルボン酸、5−ナトリウムスルホイソフタル酸、フェニルエンダンジカルボン酸、アントラセンジカルボン酸、フェナントレンジカルボン、9,9’−ビス(4−カルボキシフェニル)フルオレン酸等の芳香族ジカルボン酸などのジカルボン酸もしくはそのエステル誘導体が挙げられる。
なお、「芳香族ジカルボン酸を主成分として含有する」とは、ジカルボン酸成分に占める芳香族ジカルボン酸の割合が80質量%以上であることをいう。
また、前記(B)ジオール成分として、脂肪族ジオールの少なくとも1種が用いられる場合が好ましい。脂肪族ジオールとして、エチレングリコールを含むことができ、好ましくはエチレングリコールを主成分として含有する。
なお、主成分とは、ジオール成分に占めるエチレングリコールの割合が80質量%以上であることをいう。
カルボン酸基の数(a)が3以上のカルボン酸(多官能モノマー)の例として、3官能の芳香族カルボン酸としては、例えば、トリメシン酸、トリメリット酸、ピロメリット酸、ナフタレントリカルボン酸、アントラセントリカルボン酸等が、3官能の脂肪族カルボン酸としては、例えば、メタントリカルボン酸、エタントリカルボン酸、プロパントリカルボン酸、ブタントリカルボン酸等が、4官能の芳香族カルボン酸としては、例えば、ベンゼンテトラカルボン酸、ベンゾフェノンテトラカルボン酸、ナフタレンテトラカルボン酸、アントラセンテトラカルボン酸、ペリレンテトラカルボン酸等が、4官能の脂肪族カルボン酸として、例えば、エタンテトラカルボン酸、エチレンテトラカルボン酸、ブタンテトラカルボン酸、シクロペンタンテトラカルボン酸、シクロヘキサンテトラカルボン酸、アダマンタンテトラカルボン酸等が、5官能以上の芳香族カルボン酸として、例えば、ベンゼンペンタカルボン酸、ベンゼンヘキサカルボン酸、ナフタレンペンタカルボン酸、ナフタレンヘキサカルボン酸、ナフタレンヘプタカルボン酸、ナフタレンオクタカルボン酸、アントラセンペンタカルボン酸、アントラセンヘキサカルボン酸、アントラセンヘプタカルボン酸、アントラセンオクタカルボン酸等が、5官能以上の脂肪族カルボン酸として、例えば、エタンペンタカルボン酸、エタンヘプタカルボン酸、ブタンペンタカルボン酸、ブタンヘプタカルボン酸、シクロペンタンペンタカルボン酸、シクロヘキサンペンタカルボン酸、シクロヘキサンヘキサカルボン酸、アダマンタンペンタカルボン酸、アダマンタンヘキサカルボン酸等が挙げられる。
本発明においては、これらのエステル誘導体や酸無水物等が例として挙げられるが、これらに限定されるものではない。
これらは、1種単独で用いても、必要に応じて、複数種を併用してもよい。
これらは、1種単独で用いても、必要に応じて、複数種を併用してもよい。
また、これらの多官能モノマーのカルボキシ末端に、l−ラクチド、d−ラクチド、ヒドロキシ安息香酸などのオキシ酸類及びその誘導体、そのオキシ酸類が複数個連なったもの等を付加させたものも好適に用いられる。
これらは、1種単独で用いても、必要に応じて、複数種を併用してもよい。
Ti系触媒の例としては、テトラ−n−プロピルチタネート、テトラ−i−プロピルチタネート、テトラ−n−ブチルチタネート、テトラ−n−ブチルチタネートテトラマー、テトラ−t−ブチルチタネート、テトラシクロヘキシルチタネート、テトラフェニルチタネート、テトラベンジルチタネート等のチタンアルコキシド、チタンアルコキシドの加水分解により得られるチタン酸化物、チタンアルコキシドと珪素アルコキシドもしくはジルコニウムアルコキシドとの混合物の加水分解により得られるチタン−珪素もしくはジルコニウム複合酸化物、酢酸チタン、蓚酸チタン、蓚酸チタンカリウム、蓚酸チタンナトリウム、チタン酸カリウム、チタン酸ナトリウム、チタン酸−水酸化アルミニウム混合物、塩化チタン、塩化チタン−塩化アルミニウム混合物、チタンアセチルアセトナート、有機酸を配位子とする有機キレートチタン錯体、等が挙げられる。
PET原料樹脂に含まれるチタン元素の量が1ppm以上であると、PETの重量平均分子量(Mw)が上がり、熱分解しにくい。そのため、押出機内で異物が軽減される。PET原料樹脂に含まれるチタン元素の量が50ppm以下であると、Ti系触媒が異物となり難く、PETシートの延伸の際に延伸ムラが軽減される。
触媒成分であるチタン化合物として、有機酸を配位子とする有機キレートチタン錯体の少なくとも1種が用いられることが好ましい。有機酸としては、例えば、クエン酸、乳酸、トリメリット酸、リンゴ酸等を挙げることができる。中でも、クエン酸又はクエン酸塩を配位子とする有機キレート錯体が好ましい。
また、一般に、末端カルボキシ基量が多いほど耐加水分解性が悪化することが知られており、上記の添加方法によって末端カルボキシ基量が少なくなることで、耐加水分解性の向上が期待される。
このようなチタン化合物の例としては、テトラ−n−プロピルチタネート、テトラ−i−プロピルチタネート、テトラ−n−ブチルチタネート、テトラ−n−ブチルチタネートテトラマー、テトラ−t−ブチルチタネート、テトラシクロヘキシルチタネート、テトラフェニルチタネート、テトラベンジルチタネート等のチタンアルコキシド、チタンアルコキシドの加水分解により得られるチタン酸化物、チタンアルコキシドと珪素アルコキシドもしくはジルコニウムアルコキシドとの混合物の加水分解により得られるチタン−珪素もしくはジルコニウム複合酸化物、酢酸チタン、蓚酸チタン、蓚酸チタンカリウム、蓚酸チタンナトリウム、チタン酸カリウム、チタン酸ナトリウム、チタン酸−水酸化アルミニウム混合物、塩化チタン、塩化チタン−塩化アルミニウム混合物、チタンアセチルアセトナート等が挙げられる。
これにより、重合時の着色及びその後の溶融製膜時における着色が少なくなり、従来のアンチモン(Sb)触媒系のPETに比べて黄色味が軽減され、また、透明性の比較的高いゲルマニウム触媒系のPETに比べて遜色のない色調、透明性を持ち、しかも耐熱性に優れたPETを提供できる。また、コバルト化合物や色素などの色調調整材を用いずに高い透明性を有し、黄色味の少ないPETが得られる。
5価のリン化合物として、置換基として芳香環を有しない5価のリン酸エステルの少なくとも一種が用いられる。例えば、炭素数2以下の低級アルキル基を置換基として有するリン酸エステル〔(OR)3−P=O;R=炭素数1又は2のアルキル基〕が挙げられ、具体的には、リン酸トリメチル、リン酸トリエチルが特に好ましい。
PETにマグネシウム化合物を含めることにより、PETの静電印加性が向上する。この場合に着色がおきやすいが、本発明においては、着色を抑え、優れた色調、耐熱性が得られる。
マグネシウム化合物としては、例えば、酸化マグネシウム、水酸化マグネシウム、マグネシウムアルコキシド、酢酸マグネシウム、炭酸マグネシウム等のマグネシウム塩が挙げられる。中でも、エチレングリコールへの溶解性の観点から、酢酸マグネシウムが最も好ましい。
(i)Z=5×(P含有量[ppm]/P原子量)−2×(Mg含有量[ppm]/Mg原子量)−4×(Ti含有量[ppm]/Ti原子量)
(ii)0≦Z≦+5.0
これは、リン化合物はチタンに作用のみならずマグネシウム化合物とも相互作用することから、3者のバランスを定量的に表現する指標となるものである。
前記式(i)は、反応可能な全リン量から、マグネシウムに作用するリン分を除き、チタンに作用可能なリンの量を表現したものである。値Zが正の場合は、チタンを阻害するリンが余剰な状況にあり、逆に負の場合はチタンを阻害するために必要なリンが不足する状況にあるといえる。反応においては、Ti、Mg、Pの各原子1個は等価ではないことから、式中の各々のモル数に価数を乗じて重み付けを施してある。
エステル化反応を一段階で行なう場合、エステル化反応温度は230〜260℃が好ましく、240〜250℃がより好ましい。
エステル化反応を多段階に分けて行なう場合、第一反応槽のエステル化反応の温度は230〜260℃が好ましく、より好ましくは240〜250℃であり、圧力は1.0〜5.0kg/cm2が好ましく、より好ましくは2.0〜3.0kg/cm2である。第二反応槽のエステル化反応の温度は230〜260℃が好ましく、より好ましくは245〜255℃であり、圧力は0.5〜5.0kg/cm2、より好ましくは1.0〜3.0kg/cm2である。さらに3段階以上に分けて実施する場合は、中間段階のエステル化反応の条件は、前記第一反応槽と最終反応槽の間の条件に設定するのが好ましい。
重縮合は、エステル化反応で生成されたエステル化反応生成物を重縮合反応させて重縮合物を生成する。重縮合反応は、1段階で行なってもよいし、多段階に分けて行なうようにしてもよい。
エステル化反応により重合した後に、さらに固相重合することにより、PETフィルムの含水率、結晶化度、PETの酸価、すなわち、PETの末端カルボキシ基の濃度(Acid Value;AV)、固有粘度(Interisic Viscosity;IV)を制御することができる。
したがって、縦延伸及び横延伸に適用するPETフィルムの原料であるPETは、固有粘度が0.75dL/g以上0.9dL/g以下であることが好ましく、さらに触媒(Ti触媒)由来のチタン原子を含有することが好ましい。
PETの固相重合は、連続法(タワーの中に樹脂を充満させ、これを加熱しながらゆっくり所定の時間滞流させた後、順次送り出す方法)でもよく、バッチ法(容器の中に樹脂を投入し、所定の時間加熱する方法)でもよい。
固相重合は、真空中あるいは窒素雰囲気下で行なうことが好ましい。
PETの固相重合温度は、150℃以上250℃以下、より好ましくは170℃以上240℃以下、さらに好ましくは180℃以上230℃以下であることが好ましい。温度が上記範囲内であると、PETの酸価(AV)がより低減する点で好ましい。
また、固相重合時間は、1時間以上100時間以下が好ましく、より好ましくは5時間以上100時間以下、さらに好ましくは10時間以上75時間以下、特に好ましくは15時間以上50時間以下である。固相重合時間が上記範囲内であると、PETの酸価(AV)と固有粘度(IV)とを好ましい範囲に容易に制御できる。
本発明におけるフィルム成形工程では、上記のようにして得られるPET原料樹脂を溶融押出し、さらに冷却してPETフィルムを成形する。
PET原料樹脂の溶融押出は、例えば、1本又は2本以上のスクリュを備えた押出機を用い、PET原料樹脂の融点以上の温度に加熱し、スクリュを回転させて溶融混練しながら行なわれる。PET原料樹脂は、加熱及びスクリュによる混練により、押出機内で溶融してメルトとなる。また、押出機内での熱分解(PETの加水分解)を抑制する観点から、押出機内を窒素置換して、PET原料樹脂の溶融押出しを行なうことが好ましい。押出機は、混練温度が低く抑えられる点で二軸押出機が好ましい。
溶融されたPET原料樹脂(メルト)は、ギアポンプ、濾過器等を通して、押出ダイから押出す。押出ダイは、単に「ダイ」とも称する〔JIS B8650:2006、a)押出成形機、番号134参照〕。
このとき、メルトは、単層で押出してもよいし、多層で押出してもよい。
PET原料樹脂に末端封止剤を含める工程を設けることで、耐候性が向上する上、熱収縮を低く抑えることができる。また、PETフィルムを成形した場合において、PET末端に結合して分子鎖の末端部分が嵩高くなり、フィルム表面の微細凹凸量が増えるため、アンカー効果が発現しやすくなり、PETフィルムと該フィルム上に塗布形成される塗布層との密着が向上する。
末端封止剤の含有比率が0.1質量%以上であることで、AV低下効果による耐候性向上を達成できる上、低熱収縮性及び密着性を付与することができる。また、末端封止剤の含有比率が5質量%以下であると、密着性が向上するほか、末端封止剤の添加によりPETのガラス転移温度(Tg)の低下が抑制され、これによる耐候性の低下や熱収縮の増加を抑制することができる。これは、Tgが低下した分、相対的にPETの反応性が増加することで生じる加水分解性の増加を抑制したり、Tg低下で増加するPET分子の運動性が増加し易くなることで生じる熱収縮が抑制されるためである。
カルボジイミド化合物、エポキシ化合物、及びオキサゾリン系化合物の例示及び好ましい態様等の詳細は、前記「PETフィルム」の項において既述した通りである。
キャスト処理により得られるフィルム状のPET成形体の厚みは、0.5mm〜5mmであることが好ましく、0.7mm〜4.7mmであることがより好ましくは、0.8mm〜4.6mmであることがさらに好ましい。
フィルム状のPET成形体の厚みを5mm以下とすることで、メルトの蓄熱による冷却遅延を回避し、また、0.5mm以上とすることで、押出しから冷却までの間に、PET中のOH基やCOOH基がPET内部に拡散され、加水分解発生の要因となるOH基及びCOOH基がPET表面に露出することを抑制する。
冷却手段は、上記の中でも、連続運転時のシート表面へのオリゴマー付着防止の観点から、冷風による冷却及びキャストドラムを用いた冷却の少なくとも一方が好ましい。さらには、押出機から押出されたメルトを冷風で冷却すると共に、メルトをキャストドラムに接触させて冷却することが特に好ましい。
本発明の縦延伸工程では、前記フィルム成形工程で成形されたPETフィルムを長手方向に縦延伸する。
また、縦横の延伸倍率の積で表される面積延伸倍率は、延伸前のPETフィルムの面積の6倍〜18倍が好ましく、8倍〜17.5倍であることがより好ましく、10倍〜17倍であることがさらに好ましい。
PETフィルムの延伸時の縦温度(以下、「縦延伸温度」とも称する)は、PETフィルムのガラス転移温度をTgとするとき、Tg−20℃以上Tg+50℃であることが好ましく、より好ましくはTg−10℃以上Tg+40℃以下、さらに好ましくはTg以上Tg+30℃である。
なお、「PETフィルムの長手方向(搬送方向、MD)と直交する方向(TD)」とは、PETフィルムの長手方向(搬送方向、MD)と垂直(90°)をなす方向を意図するものであるが、機械的な誤差などから実質的に長手方向(すなわち搬送方向)に対する角度が90°とみなせる方向(例えば、MD方向に対し90°±5°の方向)が含まれる。
次に、本発明における横延伸工程について詳細に説明する。
本発明における横延伸工程は、縦延伸後のPETフィルムを長手方向に直交する幅方向に横延伸する工程であるが、この横延伸を、縦延伸後のPETフィルムを延伸可能な温度に予熱する予熱工程と、予熱された前記PETフィルムを前記長手方向と直交する幅方向に緊張を与えて横延伸する延伸工程と、前記縦延伸及び前記横延伸を行なった後の前記PETフィルムの最高到達膜面温度を160℃〜225℃の範囲に加熱して熱固定する熱固定工程と、前記熱固定されたPETフィルムを加熱し、PETフィルムの緊張を緩和する熱緩和工程と、熱緩和後のPETフィルムを冷却する冷却工程と、を設けて行なう。
本発明における横延伸工程では、上記構成でPETフィルムが横延伸される態様であればその具体的な手段は制限されないが、上記構成をなす各工程の処理が可能な横延伸装置又は2軸延伸機を用いて行なうことが好ましい。
図1に示すように、2軸延伸機100は、1対の環状レール60a及び60bと、各環状レールに取り付けられ、レールに沿って移動可能な把持部材2a〜2lとを備えている。環状レール60a及び60bは、PETフィルム200を挟んで互いに対称配置されており、把持部材2a〜2lでPETフィルム200を握持し、レールに沿って移動させることによりフィルム幅方向に延伸可能なようになっている。
図1は、2軸延伸機の一例を上面から示す上面図である。
2軸延伸機100は、延伸部20において、PETフィルム200をTD方向に延伸する横延伸を可能とするものであるが、把持部材2a〜2lの移動速度を変化させることにより、PETフィルム200をMD方向にも延伸することができる。すなわち、2軸延伸機100を用いて同時2軸延伸を行なうことも可能である。
予熱工程では、前記縦延伸工程で縦延伸した後のPETフィルムを延伸可能な温度に予熱する。
図1に示すように、予熱部10においてPETフィルム200を予熱する。予熱部10では、PETフィルム200を延伸する前に予め加熱し、PETフィルム200の横延伸を容易に行なえるようにする。
なお、予熱部終了点は、PETフィルム200の予熱を終了する時点、すなわち予熱部10の領域からPETフィルム200が離れる位置をいう。
延伸工程では、前記予熱工程で予熱されたPETフィルムを長手方向(MD方向)と直交する幅方向(TD方向)に緊張を与えて横延伸する。
図1に示すように、延伸部20では、予熱されたPETフィルム200を、少なくともPETフィルム200の長手方向と直交するTD方向に横延伸してPETフィルム200に緊張を与える。
また、PETフィルム200の面積延伸倍率(各延伸倍率の積)は、延伸前のPETフィルム200の面積の6倍〜18倍が好ましく、8倍〜17.5倍であることがより好ましく、10倍〜17倍であることがさらに好ましい。
また、PETフィルム200の横延伸時の膜面温度(以下、「横延伸温度」ともいう。)は、PETフィルム200のガラス転移温度をTgとするとき、Tg−10℃以上Tg+100℃であることが好ましく、より好ましくはTg℃以上Tg+90℃以下、さらに好ましくはTg+10以上Tg+80℃である。
熱固定工程では、既に縦延伸及び横延伸が施された後のPETフィルムを、その最高到達膜面温度を160℃〜225℃の範囲に加熱することで熱固定する。
熱固定温度は、上記同様の理由から、205℃〜225℃の範囲が好ましい。
なお、最高到達膜面温度(熱固定温度)は、PETフィルム200の表面に熱電対を接触させて測定される値である。
このとき、加熱は、熱固定工程での加熱面における加熱直後の表面温度が、加熱面と反対側の非加熱面の表面温度に比べて0.5℃以上5.0℃以下の範囲で高くなるように行なわれることが好ましい。熱固定時の加熱面の温度がその反対側の面より高く、その表裏間の温度差が0.5〜5.0℃であることで、フィルムのカールがより効果的に解消される。カールの解消効果の観点からは、加熱面とその反対側の非加熱面との間の温度差は、0.7〜3.0℃の範囲がより好ましく、0.8℃以上2.0℃以下が更に好ましい。
中でも、滞留時間は、上記同様の理由から、8秒以上40秒以下が好ましく、10秒以上30秒以下がより好ましい。
熱緩和工程は、前記熱固定工程で固定されたPETフィルムを加熱し、PETフィルムの緊張を緩和し、残留歪みを除去する。フィルムの寸法安定性を向上すると共に、得られるPETフィルムのIV値が0.75以上であると、耐加水分解性を両立することができる。
以下、熱緩和時におけるPETフィルム200の表面の最高到達膜面温度を「熱緩和温度(T熱緩和)」ともいう。
T熱緩和が「T熱固定−5℃」以下であると、PETフィルムの耐加水分解性により優れる。また、T熱緩和は、寸法安定性が良好になる点で、100℃以上であることが好ましい。
更には、T熱緩和は、100℃以上で、かつT熱固定よりも15℃以上低い温度領域(100℃≦T熱緩和≦T熱固定−15℃)であることが好ましく、110℃以上で、かつT熱固定よりも25℃以上低い温度領域(110℃≦T熱緩和≦T熱固定−25℃)であることがより好ましく、120℃以上で、かつT熱固定よりも30℃以上低い温度領域(120℃≦T熱緩和≦T熱固定−30℃)であることが特に好ましい。
なお、T熱緩和は、PETフィルム200の表面に熱電対を接触させることで測定される値である。
冷却工程では、前記熱緩和工程で熱緩和した後のPETフィルムを冷却する。
図1に示すように、冷却部50では、熱緩和部40を経たPETフィルム200が冷却される。熱固定部30や熱緩和部40で加熱されたPETフィルム200を冷却することにより、PETフィルム200の形状が固定化される。
ここで、冷却部出口とは、PET200が冷却部50から離れるときの、冷却部50の端部をいい、PETフィルム200を把持する把持部材2(図1では、把持部材2j及び2l)が、PETフィルム200を離すときの位置をいう。
前記冷却工程で冷却されたPETフィルム200は、TD方向両端のクリップで握持された把持部分をカットし、ロール状に巻き取られる。
予熱部20においてPETフィルム200の幅方向(TD)の両端部を、片端部につき、少なくとも2つの把持部材を用いて把持する。例えば、PETフィルム200の幅方向(TD)の片端部の一方を把持部材2a及び2bで把持し、他方を把持部材2c及び2dで把持する。次いで、把持部材2a〜2dを移動させることにより、予熱部20から冷却部50までPETフィルム200を搬送する。
上記のように、把持部材2a−2b間の間隔、及び把持部材2c−2d間の間隔を、MD方向上流側よりも下流側で狭めることで、PETフィルム200のMD方向の緩和を行なうことができる。したがって、MD方向の緩和を熱固定部30又は熱緩和部40で行なう場合は、把持部材2a〜2dが熱固定部30又は熱緩和部40に到達したときに、把持部材2a〜2dの移動速度を遅くして、PETフィルム200の搬送速度を小さくし、把持部材2a−2b間の間隔、及び把持部材2c−2d間の間隔を、予熱部における間隔よりも狭めればよい。
本発明の太陽電池用バックシートの製造方法は、示差走査熱量測定(DSC)で測定されるプレピーク温度が160℃〜225℃である2軸延伸ポリエチレンテレフタレートフィルムである基材上の少なくとも一方の面に、アクリル樹脂を含むバインダーと、カルボジイミド架橋剤と、無機微粒子とを少なくとも含有する第1層形成用塗布液を塗布して、第1層を塗布形成する第1層形成工程と、前記第1層上に、樹脂バインダーを主成分として含有する第2層を形成する第2層形成工程とを有して構成される。
なお、本発明の太陽電池用バックシートの製造方法において、第1層とは、既述の特定塗布層に相当し、第2層とは、既述の易接着性層に相当する。
また、第2層形成工程に用いる易接着性のシート状部材および易接着性のシート状部材の貼り合わせ方法、並びに、易接着性層形成用の塗布液の詳細および塗布方法も記述のとおりである。
太陽電池モジュールは、一般に、太陽光の光エネルギーを電気エネルギーに変換する太陽電池素子を、太陽光が入射する透明性の基板と既述の本発明のポリエステルフィルム(太陽電池用バックシート)との間に配置して構成されている。具体的な実施態様として、電気を取り出すリード配線(不図示)で接続された発電素子(太陽電池素子)をエチレン・酢酸ビニル共重合体系(EVA系)樹脂等の封止剤で封止し、これを、ガラス等の透明基板と、本発明のポリエステルフィルム(バックシート)との間に挟んで互いに張り合わせることによって構成される態様に構成されてもよい。
実施例および比較例で用いたPET(原料または基材)の固有粘度(IV)及び酸価(AV)は次のようにして得た。
固有粘度(IV)は、PETを、1,1,2,2−テトラクロルエタン/フェノール(=2/3[質量比])混合溶媒に溶解し、該混合溶媒中の25℃での溶液粘度から求めた。
酸価(AV)は、PETをベンジルアルコール/クロロホルム(=2/3;体積比)の混合溶液に完全溶解させ、指示薬としてフェノールレッドを用い、基準液(0.025N KOH−メタノール混合溶液)で滴定し、その適定量から算出した。
(基材の製造)
以下の手順により、太陽電池バックシート用基材フィルムの基材を形成した。
先ず、Tiを触媒として重縮合した固有粘度0.66のポリエチレンテレフタレート(PET)を含水率50ppm以下に乾燥したものを、PET原料(PET原料1)として用いた。なお、PETの含水率は、微量水分計(カールフィッシャー法)を用いて25℃にて測定した値である。
溶融樹脂を、ダイから静電印加されたチルロール(冷却ロール)上に吐出し、未延伸フィルム(非結晶ベース)を得た。得られた非結晶ベースを、非結晶ベースの搬送方向(MD)に延伸(縦延伸)した。その後、MDと直交する幅方向(TD)に延伸(横延伸)し、225℃で熱固定して、厚さ125μmのPET基材1を得た。
PET基材1に対して、接触式膜厚測定計(アンリツ社製)を用い、縦延伸した方向(PET基材1の長手方向)に0.5mにわたり等間隔に50点をサンプリングし、さらにフィルム幅方向(長手方向に直交する方向)に、PET基材1の全幅にわたり等間隔(幅方向に50等分)に50点をサンプリングした後、これらの100点の厚みを測定した。これら100点の平均の厚みを求め、PET基材1の厚みとした。
得られたPET基材1を搬送速度105m/分で搬送し、PET基材1の両面に対して730J/m2の条件でコロナ放電処理を行った。
コロナ放電処理を行ったPET基材1の片面に、下記第1層塗布液(1)をバーコート法により乾燥質量が233mg/m2となるように塗布して塗布膜1を得た後、塗布膜1を180℃で1分乾燥して第1層を形成した。
・ポリアクリルバインダー(バインダー) 19.1部
〔東亜合成化学(株)製、ジュリマーET−410、固形分30%〕
・カルボジイミド化合物(カルボジイミド架橋剤) 9.0部
〔日清紡ケミカル(株)製、カルボジライトV−02−L2、固形分20%〕
・界面活性剤A 15.0部
〔三洋化成工業(株)製、ナロアクティーCL−95の1%水溶液〕
・無機フィラー(無機微粒子) 73.0部
〔三菱マテリアル電子化成(株)製、TDL−1、酸化スズ17%水溶液〕
・蒸留水 全体が1,000部になるように添加
得られた第1層の上に、乾燥重量が65.9mg/m2となるように、下記第2層塗布液(1)をバーコート法により塗布して塗布膜2を得た後、塗布膜2を170℃で1分乾燥することにより第2層を形成した。
・ポリアクリルバインダー(樹脂バインダー) 21.0部
〔東亜合成化学(株)製、ジュリマーET−410、固形分30%〕
・エポキシ化合物 221.8部
〔ナガセケムテックス(株)製、デナコールEX−614B、固形分1%〕
・界面活性剤A 25.0部
〔三洋化成工業(株)製、ナロアクティーCL−95の1%水溶液〕
・蒸留水 全体が1,000部になるように添加
表1に第1層および第2層の成分構成を示す。なお、「第1層(塗布層)」欄において、架橋剤と微粒子の量〔%〕は、層中の全固形分質量に対する質量比である。
−耐候性評価(破断応力、破断伸度)−
太陽電池バックシート1について、120℃、100%RH環境下で48時間静置する加速試験(加速試験1)前後における破断応力と破断伸度とを測定した。破断応力および破断伸度は、太陽電池バックシート1テンシロン万能試験機(STROGRAPH VE50、東洋精機製作所社製)を用いて、JIS−K7127に準拠した方法により引っ張り試験を行い、破断点での応力と伸度を求めた。
破断伸度保持率〔%〕=(L後/L前)×100 ・・・式(L)
破断応力保持率〔%〕=(N後/N前)×100 ・・・式(N)
5:破断伸度保持率、破断応力保持率がともに80%以上
4:破断伸度保持率、破断応力保持率がともに70%以上80%未満
3:破断伸度保持率、破断応力保持率がともに60%以上70%未満
2:破断伸度保持率、破断応力保持率がともに50%以上60%未満
1:破断伸度保持率、破断応力保持率がともに50%未満
接着剤を用いて、太陽電池バックシート1の、易接着性層と基材との密着性を評価した。
まず、太陽電池バックシート1から、長さ120mm、幅50mmの2枚のサンプルを切り出した。太陽電池バックシート1から切り出したサンプルを、試験サンプル(A)と称する。
次に、基材フィルムの厚みを120μmとした以外は同様の方法で易接着性層を設けた剥離試験用フィルムを作製し、長さ120mm、幅50mmの2枚のサンプルを切り出した。剥離試験用フィルムから切り出したサンプルを、試験サンプル(B)と称する。
なお、180°剥離試験は、105℃、100%RH環境下で48時間静置する加速試験(加速試験2)前の接着サンプルおよび、加速試験2後の接着サンプル各々について行なった。
この際に、剥離力を連続的に測定し、連続的に測定した値のうち最大値を求めた。この試験を、3つの接着サンプルについて行い、それぞれ最大値を測定した。そして、測定された3つの最大値の平均値を、太陽電池バックシート1と接着剤との接着力として得て、太陽電池バックシート1における基材と易接着性層との接着性の指標とした。評価結果を表1に示した。
なお、加速試験2前の接着サンプルについての評価結果を「密着性」欄のA欄に示し、加速試験2後の接着サンプルについての評価結果を「密着性」欄のB欄に示した。
得られた接着力に基づき、以下の評価基準で「接着性」を評価した。実用上許容されるのはレベル3から5に分類されるものである。
5;界面が剥離せずに、試料が破断するもの
4;剥離力が20N以上のもの
3;剥離力が15N以上20N未満のもの
2;剥離力が10N以上15N未満のもの
1;剥離力が10N未満のもの、または、加速試験2中に剥離が起こったもの
実施例1で用いたPET基材1の製造において、未延伸フィルム(非結晶ベース)の熱固定温度を225℃から215℃に変更した他は同様にして、厚さ125μmのPET基材2を得た。
次いで、太陽電池バックシート1の製造において、PET基材1に代えて、PET基材2を用いた他は同様にして、実施例2の太陽電池バックシート2を製造した。
得られた太陽電池バックシート2について、太陽電池バックシート1と同様の評価方法および評価基準にて、耐候性と密着性の評価を行い、表1に評価結果を示した。
実施例1の太陽電池バックシート1の製造において、第1層塗布液(1)を用いる代わりに、下記の第1層塗布液(2)を用いた他は同様にして、実施例3の太陽電池バックシート3を製造した。
得られた太陽電池バックシート3について、太陽電池バックシート1と同様の評価方法および評価基準にて、耐候性と密着性の評価を行い、表1に評価結果を示した。
・ポリアクリルバインダー(バインダー) 19.1部
〔東亜合成化学(株)製、ジュリマーET−410、固形分30%〕
・カルボジイミド化合物(カルボジイミド架橋剤) 13.5部
〔日清紡ケミカル(株)製、カルボジライトV−02−L2、固形分20%〕
・界面活性剤A 15.0部
〔三洋化成工業(株)製、ナロアクティーCL−95の1%水溶液〕
・無機フィラー(無機微粒子) 73.0部
〔三菱マテリアル電子化成(株)製、TDL−1、酸化スズ17%水溶液〕
・蒸留水 全体が1,000部になるように添加
実施例1の太陽電池バックシート1の製造において、第1層塗布液(1)を用いる代わりに、下記の第1層塗布液(3)を用いた他は同様にして、実施例4の太陽電池バックシート4を製造した。
得られた太陽電池バックシート4について、太陽電池バックシート1と同様の評価方法および評価基準にて、耐候性と密着性の評価を行い、表1に評価結果を示した。
・ポリアクリルバインダー(バインダー) 19.1部
〔東亜合成化学(株)製、ジュリマーET−410、固形分30%〕
・カルボジイミド化合物(カルボジイミド架橋剤) 9.0部
〔日清紡ケミカル(株)製、カルボジライトV−02−L2、固形分20%〕
・界面活性剤A 15.0部
〔三洋化成工業(株)製、ナロアクティーCL−95の1%水溶液〕
・無機フィラー(無機微粒子) 109.5部
〔三菱マテリアル電子化成(株)製、TDL−1、酸化スズ17%水溶液〕
・蒸留水 全体が1,000部になるように添加
実施例1で用いたPET基材1の製造において、未延伸フィルム(非結晶ベース)の熱固定温度を225℃から150℃に変更した他は同様にして、厚さ125μmのPET基材101を得た。
次いで、太陽電池バックシート1の製造において、PET基材1に代えてPET基材101を用い、さらに、第1層塗布液(1)を用いる代わりに、下記の第1層塗布液(101)を用いた他は同様にして、比較例1の太陽電池バックシート101を製造した。
得られた太陽電池バックシート101について、太陽電池バックシート1と同様の評価方法および評価基準にて、耐候性と密着性の評価を行い、表1に評価結果を示した。
・ポリアクリルバインダー(バインダー) 19.1部
〔東亜合成化学(株)製、ジュリマーET−410、固形分30%〕
・オキサゾリン化合物(オキサゾリン系架橋剤) 4.5部
〔エポクロスWS−700、日本触媒(株)製、固形分25%〕
・界面活性剤A 15.0部
〔三洋化成工業(株)製、ナロアクティーCL−95の1%水溶液〕
・無機フィラー(無機微粒子) 36.5部
〔三菱マテリアル電子化成(株)製、TDL−1、酸化スズ17%水溶液〕
・蒸留水 全体が1,000部になるように添加
比較例1の太陽電池バックシート101の製造において、PET基材101に代えてPET基材1を用いた他は同様にして、比較例2の太陽電池バックシート102を製造した。
得られた太陽電池バックシート102について、太陽電池バックシート1と同様の評価方法および評価基準にて、耐候性と密着性の評価を行い、表1に評価結果を示した。
比較例2の太陽電池バックシート102の製造において、第1層塗布液(101)を用いる代わりに、下記の第1層塗布液(102)を用いた他は同様にして、比較例3の太陽電池バックシート103を製造した。第1層塗布液(102)は、特開2011−146659号公報の白色層用水系組成物1の調製を参考に調製したものである。
得られた太陽電池バックシート103について、太陽電池バックシート1と同様の評価方法および評価基準にて、耐候性と密着性の評価を行い、表1に評価結果を示した。
・ポリアクリルバインダー(バインダー) 7.2部
〔東亜合成化学(株)製、ジュリマーET−410、固形分30%〕
・オキサゾリン化合物(オキサゾリン系架橋剤) 2.0部
〔エポクロスWS−700、日本触媒(株)製、固形分25%〕
・界面活性剤A 3.0部
〔三洋化成工業(株)製、ナロアクティーCL−95の1%水溶液〕
・シリカフィラー(無機微粒子、体積平均粒径40nm) 1.8部
〔アエロジルOX−50、日本アエロジル(株)製、固形分10%〕
・下記白色顔料分散液1 71.0部
・蒸留水 15.0部
・二酸化チタン(白色顔料、体積平均粒径0.3μm)
〔タイペークR−780−2、石原産業(株)製、固形分100%〕39.7部
・ポリビニルアルコール(水系バインダーB)
〔PVA−105、(株)クラレ製、固形分10%〕 49.7部
・界面活性剤
〔デモールEP、花王(株)製、固形分25%〕 0.5部
・蒸留水 10.1部
実施例1〜実施例4および比較例1〜比較例3で用いたPET基材1、2および101について、示差走査型熱量計〔(株)島津製作所製、DSC−50〕を用いて示差走査熱量測定(DSC)を行い、各PET基材のプレピーク温度を測定した。測定結果を表1に示す。
太陽電池用バックシート1〜4の製造に用いた第1層中のアクリル樹脂とカルボジイミド架橋剤との質量比X(「第1層中のカルボジイミド架橋剤の質量」/「第1層中のアクリル樹脂の質量」)、アクリル樹脂の酸価A、及びカルボジイミド等量Bを表1に示した。
厚さ3mmの強化ガラスと、EVAシート(三井化学ファブロ(株)製のSC50B)と、結晶系太陽電池セルと、EVAシート(三井化学ファブロ(株)製のSC50B)と、実施例1〜実施例4で作製した太陽電池用バックシートとをこの順に重ね合わせ、真空ラミネータ(日清紡(株)製、真空ラミネート機)を用いてホットプレスすることによりEVAと接着させ、結晶系の太陽電池モジュール1〜4を作製した。このとき、太陽電池用バックシートを、その易接着性層がEVAシートと接触するように配置し、接着は以下に示す方法により行なった。
真空ラミネータを用い、128℃で3分間の真空引きした後、2分間加圧して仮接着した。その後、ドライオーブンにて150℃で30分間、本接着処理を施した。
10・・・予熱部
20・・・延伸部
30・・・熱固定部
40・・・熱緩和部
50・・・冷却部
60・・・環状レール
100・・・2軸延伸機
200・・・ポリエステルフィルム
Claims (3)
- 示差走査熱量測定(DSC)で測定されるプレピーク温度が160℃〜225℃である2軸延伸ポリエチレンテレフタレートフィルムである基材と、
前記基材の少なくとも一方の面に設けられ、アクリル樹脂を含むバインダー、カルボジイミド架橋剤に由来する架橋構造部分、及び無機微粒子を含有する塗布層と、
前記塗布層上に設けられ、樹脂バインダーを主成分として含有する易接着性層と、
を有し、
前記アクリル樹脂の酸価をA、前記カルボジイミド架橋剤の等量をBとするとき、前記アクリル樹脂に対する前記カルボジイミド架橋剤の質量比X(前記カルボジイミド架橋剤/前記アクリル樹脂)が、前記Aと前記Bとの積ABとの間で、下記式(1)を満たす太陽電池用バックシート。
(0.8AB)/56100 < X <(2.0AB)/56100 ・・・(1) - 前記無機微粒子が、酸化スズを主成分とし、前記塗布層中の前記無機微粒子の含有量が、前記バインダーの全質量に対して、50質量%〜500質量%である請求項1に記載の太陽電池用バックシート。
- 太陽光が入射する透明性の基板と、前記基板の一方の側に配された太陽電池素子と、該太陽電池素子の前記基板が配された側と反対側に配された請求項1又は請求項2に記載の太陽電池用バックシートと、を備えた太陽電池モジュール。