JP5504622B2 - Lead-acid battery manufacturing method, and lead-acid battery electrode plate strap casting method and casting apparatus used in the manufacturing method - Google Patents
Lead-acid battery manufacturing method, and lead-acid battery electrode plate strap casting method and casting apparatus used in the manufacturing method Download PDFInfo
- Publication number
- JP5504622B2 JP5504622B2 JP2008315640A JP2008315640A JP5504622B2 JP 5504622 B2 JP5504622 B2 JP 5504622B2 JP 2008315640 A JP2008315640 A JP 2008315640A JP 2008315640 A JP2008315640 A JP 2008315640A JP 5504622 B2 JP5504622 B2 JP 5504622B2
- Authority
- JP
- Japan
- Prior art keywords
- molten metal
- level
- metal level
- gear pump
- strap
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、鉛蓄電池の製造方法並びにこの製造方法で用いる鉛蓄電池用極板ストラップ鋳造方法及び鋳造装置に関するものである。 The present invention relates to a method for producing a lead-acid battery, a method for casting an electrode plate strap for a lead-acid battery used in the production method, and a casting apparatus.
周知のように、鉛蓄電池は、正極板と負極板とをセパレータを介して積層して鉛蓄電池用の極板群を構成する極板群構成工程と、極板群の同極性の極板の耳部同士を接続するストラップを鋳造するストラップ鋳造工程と、ストラップが鋳造された極板群を電槽内に収容してセル間を接続し、該電槽内に電解液を注入する組立工程とを行うことにより製造される。 As is well known, the lead-acid battery is composed of a positive electrode plate and a negative electrode plate stacked via a separator to constitute a plate group for a lead-acid battery, and a plate plate of the same polarity as the electrode plate group. A strap casting process for casting a strap for connecting the ears; an assembly process for housing the electrode plate group in which the strap is cast in the battery case, connecting the cells, and injecting an electrolyte into the battery case; It is manufactured by performing.
ストラップ鋳造工程で用いるストラップ鋳造装置は、図１３に示したように構成されている。図１３において、１は鉛合金の溶湯Ｍを生成する鉛溶解槽である。鉛溶解槽１は、ヒータ２を備えていて、該ヒータにより鉛合金を加熱して溶融することにより鉛合金の溶湯Ｍを生成する。３は鋳型、４′は鉛溶解槽１内の溶湯Ｍを溶湯供給路５を通して鋳型３に供給するポンプ、６はポンプ４′を駆動する駆動源、７は鋳型３内の溶湯レベルを調整する溶湯レベル調整部である。
The strap casting apparatus used in the strap casting process is configured as shown in FIG. In FIG. 13, reference numeral 1 denotes a lead melting tank for producing a molten M of lead alloy. The lead melting tank 1 includes a
図１５及び図１６に示されているように、鋳型３は、ストラップを鋳造するためのキャビティ３０１と、キャビティ３０１に隣接配置されてキャビティ３０１との間が堰３０２により仕切られた湯溜り溝３０３と、キャビティ３０１及び湯溜り溝３０３の上方に形成された余剰溶湯収容空間３０４とを有する型凹部３０５と、湯溜り溝３０３より下方に設けられて湯溜り溝３０３内に連通路３０６を通して接続された湯道３０７とを備えている。
As shown in FIGS. 15 and 16, the
鋳型３は、堰３０２の厚み方向の中央部でキャビティ側ユニット３Ａと、湯溜り側ユニット３Ｂとに分割されていて、これらのユニットが断熱層３０９を介して接合されることにより、鋳型３が組立てられている。キャビティ側ユニット３Ａは図示しない冷却手段により冷却され、湯溜り側ユニット３Ｂは図示しない加熱手段により加熱される。
The
図示のポンプ４′は、遠心式の渦巻きポンプからなっていて、その吐出口は、溶湯供給路５を通して湯道３０７の軸線方向（長手方向）の一端に接続されている。湯道３０７の軸線方向の他端は閉鎖されていて、ポンプ４′から湯道３０７内に溶湯Ｍが送給されたときに該溶湯が連通路３０６を通して湯溜り溝３０３内に流入して、湯溜り溝３０３内の溶湯Ｍの液面Ｍａのレベル（溶湯レベル）を上昇させる。ポンプ４′と鋳型の湯溜り溝３０３との間を接続する溶湯供給路５は、ポンプ４′と溶湯レベル調整部７との間を接続するパイプライン５０１と溶湯レベル調整部７との間を接続するパイプライン５０２とからなっている。
The illustrated pump 4 ′ is a centrifugal centrifugal pump, and its discharge port is connected to one end in the axial direction (longitudinal direction) of the
溶湯レベル調整部７は、上端に開口部を有し下端が溶湯供給路５に接続された溶湯開放通路７０１と、溶湯開放通路７０１の開口部を開閉する弁棒７０２及び弁棒７０２を駆動するバルブ駆動機構７０４からなる溶湯レベル調整用バルブ７０３とを備えている。溶湯レベル調整部７は、溶湯開放通路７０１の上端開口部から流出した溶湯を鉛溶解槽１内にオーバフローさせる流出口を備えていて、該流出口のレベルを、鋳型内の湯溜り溝３０３内における溶湯の規定レベルＬ1に一致させた状態で配置されている。
The molten metal
溶湯レベル調整部７のバルブ７０３が開いている状態では、湯溜り溝３０３内の溶湯レベルが規定レベルＬ1を越えたときに溶湯開放通路７０１の上端から流出した溶湯が流出口から鉛溶解槽１内にオーバフローして湯溜り溝３０３内の溶湯レベルを規定レベルＬ1に保つ。また、バルブ７０３が閉じている状態では、溶湯のオーバフローが阻止されるため、湯溜り溝３０３内の溶湯レベルが規定レベルＬ1を越えて上昇するのが許容される。この種の鋳造装置は、例えば特許文献１に記載されている。
In a state in which the
上記の鋳造装置においては、溶湯レベル調整部７のバルブ７０３を開いた状態でポンプ４′を運転して、湯溜り溝３０３内の溶湯レベルを規定レベルＬ1に保持しておく。この過程を待機過程とする。極板群の同極性の耳部同士を接続するストラップを鋳造する際には、先ずバルブ７０３を一定時間の間閉じて湯溜り溝３０３内の溶湯レベルを上昇させることにより湯溜り溝３０３内の溶湯Ｍを堰３０２を越えてキャビティ３０１内に流入させ、キャビティ３０１内が溶湯で満たされる状態にする。このときキャビティ内が確実に溶湯で満たされるようにするため、溶湯レベルが最終的には堰３０２の上端のレベルを越えて型凹部３０５の上端開口部付近に設定された過剰レベルに達するように、バルブ７０３を閉じておく時間を設定する。
In the above casting apparatus, the pump 4 ′ is operated with the
上記のようにして型凹部内の溶湯レベルを過剰レベルまで上昇させた後、バルブ７０３を開いて溶湯レベルを規定レベルＬ1に向けて下降させていき、溶湯レベルが、溶湯中に極板群の耳部を挿入しても型凹部３０５から溶湯があふれ出ることがないレベル以下になるタイミングで、図１５に示すように、極板群１０の複数の同極性の極板の集電体に設けられた耳部１１を、キャビティ３０１の上方から下降させて、キャビティ３０１内に挿入する。このとき型凹部３０５内の溶湯レベルは、型凹部３０５の上端開口部付近まで上昇する。この状態でキャビティ内の溶湯を凝固させるために必要な時間が経過するのを待つ。溶湯レベル調整部７からの溶湯のオーバフローを継続させ、キャビティ内の溶湯が凝固する前に湯溜り溝３０３内の溶湯レベルを規定レベルＬ1まで降下させて待機状態に移行する。極板群の耳部をキャビティ内に挿入した後、キャビティ内の溶湯を凝固させるために必要な時間が経過したときに図１６に示すようにノックアウトピン３０８を押し上げてキャビティ内で成形されたストラップ１２をキャビティから取り出す。
After the molten metal level in the mold recess is raised to an excessive level as described above, the
上記の鋳造装置では、ポンプ４′として渦巻き式の遠心ポンプが用いられているが、特許文献２に示されているように、ポンプ４′として往復動式のプランジャポンプを用いた鋳造装置も知られている。この鋳造装置では、プランジャポンプのピストンを前進させて型凹部内の溶湯レベルを堰の上端より高い過剰レベルまで上昇させた後、プランジャポンプのピストンを後退させて、型凹部内の溶湯レベルを強制的に堰の上端のレベルまで下降させるようにしている。
渦巻き式の遠心ポンプは、図１７に示すように、揚程ｈが大きくなるにつれて吐出量Ｖが低減していくという特性がある。そのため、図１３ないし図１６に示したように構成された鋳造装置のように、溶湯を鋳型に供給するポンプ４′として渦巻き式の遠心ポンプを用いた場合には、図１３に示すように鉛溶解槽内の溶湯レベルが高く、ポンプの揚程ｈが低い場合と、図１４に示すように鉛溶解槽内の溶湯レベルが低く、ポンプの揚程ｈが高い場合とでポンプの吐出量が異なり、鉛溶解槽内の溶湯レベルの変動により、鋳型内への溶湯の供給量に過不足が生じて、鋳造されるストラップの形状が不均一になったり、溶接不良が生じたりするという問題があった。 As shown in FIG. 17, the spiral centrifugal pump has a characteristic that the discharge amount V decreases as the lift h increases. Therefore, when a spiral centrifugal pump is used as the pump 4 'for supplying the molten metal to the mold as in the casting apparatus configured as shown in FIGS. 13 to 16, lead as shown in FIG. The discharge amount of the pump differs depending on whether the molten metal level in the melting tank is high and the pump head h is low, and the molten metal level in the lead melting tank is low and the pump head h is high as shown in FIG. Due to fluctuations in the molten metal level in the lead melting tank, there was an excess or deficiency in the amount of molten metal supplied into the mold, resulting in uneven casting shapes and poor welding. .
また従来の鋳造装置では、型凹部内の溶湯レベルを過剰レベルまで上昇させた後、バルブ７０２を開いて溶湯レベル調整部の流出口から溶湯をオーバフローさせることにより、溶湯レベルを低下させ、その過程で極板群の耳部をキャビティ内に挿入しているが、オーバフローによる溶湯レベルの低下は遅いため、ストラップが凝固するまでの間に溶湯レベルを堰３０２の上端よりも下方のレベルまで低下させることができないことがあり、ストラップの厚みが過剰になることがあった。このようにストラップの厚みが過剰になることがある場合には、ストラップと極板の集電体の外骨部との間に必要な距離ｄ（図１６参照）を確保するために、耳部の高さを高く設定しておく必要があるため、極板の高さが高くなって、電池の大型化を招くという問題が生じる。
Further, in the conventional casting apparatus, after the melt level in the mold recess is raised to an excessive level, the melt level is lowered by opening the
特許文献２に示されたように、鉛溶解槽から鋳型に溶湯を供給するポンプとしてプランジャポンプを用いて、プランジャポンプのピストンを前進させて型凹部内の溶湯レベルを堰の上端より高い過剰レベルまで上昇させた後、プランジャポンプのピストンを後退させて、型凹部内の溶湯レベルを強制的に堰の上端のレベルまで下降させるようにすれば、原理的には、渦巻き式の遠心ポンプを用いた場合に生じる上記の問題を解消することができる。
As shown in
しかしながら、プランジャポンプは、ピストンの単位変位量当たりの吐出量及び吸込み量が多いため、吐出量及び吸込み量の微妙なコントロールができないという問題を有している。また特許文献２にも示されているように、プランジャポンプはエアシリンダ等の往復駆動装置により駆動する必要があるが、往復駆動装置は、シリンダに作動流体を供給するタイミングのずれによりピストンの変位量に大きな誤差を生じるため、ポンプの吐出量及び吸込み量を微妙に制御することは困難である。
However, since the plunger pump has a large discharge amount and suction amount per unit displacement of the piston, it has a problem that the discharge amount and suction amount cannot be delicately controlled. Further, as shown in
このように、プランジャポンプを用いた場合には、鋳型の型凹部内の溶湯レベルを過剰レベルから堰の上端レベルまで下降させる際に溶湯レベルを細かく制御することが困難であるため、溶湯レベルが堰のレベルよりも高いレベルまでしか低下しなかったり、湯溜り溝内の溶湯レベルが規定レベルよりも低いレベルまで低下してしまったりするという問題が生じる。溶湯レベルの低下量が不足すると、鋳造されるストラップの厚みが過剰になり、耳部の高さを高くすることが必要になって極板の大形化を招く。また溶湯レベルが規定レベルよりも低いレベルまで低下すると、次にプランジャポンプにより定量の溶湯を鋳型内に送り込んだ際に溶湯の量が不足し、ストラップの厚みが不足したり、溶接不良が生じたりするおそれがある。 Thus, when the plunger pump is used, it is difficult to finely control the molten metal level when lowering the molten metal level in the mold recess of the mold from the excessive level to the upper end level of the weir. There arises a problem that the level is lowered only to a level higher than the level of the weir, or the molten metal level in the hot water ditch is lowered to a level lower than the specified level. If the amount of decrease in the molten metal level is insufficient, the thickness of the strap to be cast becomes excessive, and it becomes necessary to increase the height of the ear portion, leading to an increase in the size of the electrode plate. If the molten metal level is lowered to a level lower than the specified level, the amount of molten metal is insufficient when the fixed amount of molten metal is fed into the mold by the plunger pump, resulting in insufficient thickness of the strap or poor welding. There is a risk.
またプランジャポンプを用いる場合には、待機過程において、鉛溶解槽−ポンプ−溶湯レベル調整部−鉛溶解槽の経路で常時溶湯の循環流を生じさせておくことができないため、待機過程において溶湯供給路５内及び鉛溶解槽１内で溶湯の流動を生じさせておくことができない。溶湯供給路５を構成するパイプラインの内、ポンプ４′と溶湯レベル調整部７との間を接続するパイプライン５０１は、鉛溶解槽１内の溶湯及び溶湯レベル調整部７からオーバフローする溶湯が触れる部分であるため、該パイプライン５０１にはヒータを巻き付けることができない。そのため、パイプライン５０１は、鉛溶解槽１内の溶湯と、溶湯レベル調整部７からオーバフローする溶湯とにより加熱されるだけであり、特にパイプライン５０１の鉛溶解槽内の溶湯から上部に露出している部分は、その加熱が不十分になりがちである。従って、溶湯供給路５内で溶湯の流動が停止すると、上記パイプライン５０１の内部で溶湯が凝固してストラップの鋳造を行うことができなくなり、鉛蓄電池の製造ラインが停止するおそれがある。
Also, when using a plunger pump, it is not possible to keep the molten metal circulating in the lead melting tank-pump-melt level adjusting unit-lead melting tank in the standby process. It is impossible to cause the molten metal to flow in the
また待機過程において鉛溶解槽１内の溶湯の流動が停止すると、溶湯の表面が酸化するため、鉛合金の組成が変化し、鋳造されるストラップの品質を低下させる。ストラップを形成する鉛合金としては、通常鉛アンチモン鉛合金が用いられるが、溶湯の表面で鉛アンチモン合金が酸化するとその酸化物中に大量のアンチモンが取り込まれるため、鉛溶解槽内の溶湯の表面で酸化が進むと、溶湯の表面付近とその内部とで合金の組成が異なる状態が生じ、鋳造されるストラップの品質が悪くなる。 Further, when the flow of the molten metal in the lead melting tank 1 is stopped in the standby process, the surface of the molten metal is oxidized, so that the composition of the lead alloy changes and the quality of the strap to be cast is lowered. Lead antimony lead alloy is usually used as the lead alloy forming the strap, but when the lead antimony alloy is oxidized on the surface of the molten metal, a large amount of antimony is taken into the oxide, so the surface of the molten metal in the lead melting tank When the oxidation proceeds, the alloy composition is different between the vicinity of the molten metal surface and the inside thereof, and the quality of the cast strap deteriorates.
上記２つの理由から、特許文献２に示されたように、鉛溶解槽１から鋳型３に溶湯を供給するポンプとしてプランジャポンプを用いることは好ましくない。
For the above two reasons, as shown in
本発明の目的は、鋳型内での溶湯レベルの制御を正確に行って、鋳型内に供給される溶湯の量に過不足が生じるのを防ぎ、鋳造されるストラップの厚みが過剰になったり、不足したりするのを防いで、極板群の耳部同士の接続部の品質を向上させることができるようにした鉛蓄電池用極板ストラップ鋳造方法及びこの鋳造方法を実施するために用いる鋳造装置を提供することにある。 The purpose of the present invention is to accurately control the molten metal level in the mold to prevent the amount of molten metal supplied into the mold from becoming excessive and insufficient, and the thickness of the strap to be cast becomes excessive, A lead plate battery casting method for a lead-acid battery strap and a casting apparatus used for carrying out this casting method, which can prevent the shortage and improve the quality of the connection part between the ears of the electrode plate group. Is to provide.
本発明の他の目的は、鋳型内に供給される溶湯の量に過不足が生じるのを防いで鋳造されるストラップの厚みが過剰になったり、不足したりするのを防ぐだけでなく、待機過程においても鉛溶解槽内及び溶湯供給路内で常時溶湯の流動を生じさせて、鋳造工程を停止させることを余儀なくされたり、鋳造されるストラップの品質が低下したりするのを防ぐことができるようにした鉛蓄電池用極板ストラップ鋳造方法及びこの鋳造方法を実施するために用いる鋳造装置を提供することにある。 Another object of the present invention is not only to prevent an excess or deficiency in the amount of molten metal supplied into the mold, but also to prevent the cast strap from becoming excessive or insufficient in thickness, as well as waiting. Even in the process, it is possible to prevent the casting process from being forced to stop by constantly causing the molten metal to flow in the lead melting tank and the molten metal supply path, and to reduce the quality of the cast strap. An object of the present invention is to provide an electrode plate strap casting method for a lead storage battery and a casting apparatus used for carrying out this casting method.
本発明の更に他の目的は、極板群の同極性の耳部同士を接続するストラップを鋳造する際にストラップの厚みが過剰になったり、不足したりするおそれをなくすとともに、溶湯供給路内で鉛が凝固してストラップ鋳造工程を停止させることを余儀なくされたり、鉛溶解槽内で溶湯の組成が変化してストラップの品質が低下したりするおそれをなくして、極板群の耳部同士の接続部の品質が高く、信頼性が高い鉛蓄電池を能率よく製造することができるようにした鉛蓄電池の製造方法を提供することにある。 Still another object of the present invention is to eliminate the possibility that the thickness of the strap becomes excessive or insufficient when casting a strap that connects the same-polarity ears of the electrode plate group. In order to eliminate the risk of lead solidifying and the strap casting process being forced to stop, or the composition of the molten metal changing in the lead melting tank and lowering the quality of the strap, It is in providing the manufacturing method of the lead storage battery which enabled it to manufacture efficiently the lead storage battery with high quality of this connection part, and high reliability.
本発明においては、上記の目的を達成するため、鉛蓄電池の極板群の同極性の極板の耳部同士を接続するストラップを鋳造する鉛蓄電池用極板ストラップ鋳造装置に下記の要素を設ける。
（ａ）鉛合金の溶湯を生成する鉛溶解槽。
（ｂ）ストラップを鋳造するためのキャビティと該キャビティに隣接配置されて該キャビティとの間が堰により仕切られた湯溜り溝と前記キャビティ及び湯溜り溝の上方に形成された余剰溶湯収容空間とを有する型凹部と、前記湯溜り溝より下方に設けられて前記湯溜り溝内に接続された湯道とを備えた鋳型。
（ｃ）鉛溶解槽内に開口させられた第１のポートと鋳型の湯道に溶湯供給路を通して接続された第２のポートとを有して、正方向に回転したときに鉛溶解槽内の溶湯を第２のポートから溶湯供給路内に吐出させ、逆方向に回転したときに溶湯供給路内の溶湯を吸引して第１のポートから鉛溶解槽内に吐出させるギアポンプ。
（ｄ）上端に開口部を有し下端が溶湯供給路に接続された溶湯開放通路と溶湯開放通路の上端の開口部を開閉するバルブと溶湯開放通路の開口部から流出した溶湯を鉛溶解槽内にオーバフローさせる溶湯流出口とを備えて、バルブが開いている状態では湯溜り溝内の溶湯レベルが規定レベルを越えたときに溶湯開放通路内の溶湯を溶湯流出口からオーバフローさせて湯溜り溝内の溶湯レベルを規定レベルに保ち、バルブが閉じているときには湯溜り溝内の溶湯レベルが規定レベルを越えて上昇するのを許容する溶湯レベル調整部。
In the present invention, in order to achieve the above-mentioned object, the following elements are provided in a lead-acid battery plate strap casting apparatus for casting a strap for connecting the ears of the same-polarity plate of the lead-acid battery group. .
(A) A lead melting tank for producing a molten lead alloy.
(B) a cavity for casting the strap, a hot water storage groove disposed adjacent to the cavity and partitioned by a weir, and an excess molten metal storage space formed above the cavity and the hot water storage groove A mold provided with a mold recess and a runner provided below the puddle groove and connected to the puddle groove.
(C) having a first port opened in the lead melting tank and a second port connected to the runner of the mold through the molten metal supply path, and in the lead melting tank when rotated in the forward direction A gear pump that discharges the molten metal from the second port into the molten metal supply path, and sucks the molten metal in the molten metal supply path and discharges it from the first port into the lead melting tank when rotated in the reverse direction.
(D) A molten metal release passage having an opening at the upper end and a lower end connected to the molten metal supply passage, a valve for opening and closing the opening at the upper end of the molten metal release passage, and the molten metal flowing out from the opening of the molten metal release passage When the valve is open, the molten metal in the molten metal release passage overflows from the molten metal outlet when the level of the molten metal in the molten metal groove exceeds the specified level. A molten metal level adjusting unit that maintains the molten metal level in the groove at a specified level and allows the molten metal level in the molten metal groove to rise beyond the specified level when the valve is closed.
ギアポンプは、正方向及び逆方向のいずれの方向にも回転させることができ、溶湯を吐出させることも吸い込むこともできる。更にギアポンプは、ギアの単位回転角度当たりの吐出量及び吸込み量が、プランジャポンプのピストンの単位変位量当たりの吐出量及び吸込み量に比べてはるかに小さく、またギアポンプは、駆動タイミングを正確に制御できる電動機により駆動できるため、ギアポンプを用いれば、溶湯の吐出量及び吸込み量の微妙なコントロールを容易に行うことができる。更に、ギアポンプの吐出量及び吸込み量は揚程の影響を受けないため、ギアポンプを用いると、鉛溶解槽内の溶湯レベルの変化により吐出量が変動して鋳型内への溶湯の供給量に過不足が生じるのを防ぐことができる。 The gear pump can be rotated in either the forward direction or the reverse direction, and can discharge or suck in the molten metal. Furthermore, the gear pump has a much smaller discharge amount and suction amount per unit rotation angle of the gear than the discharge amount and suction amount per unit displacement amount of the piston of the plunger pump, and the gear pump accurately controls the drive timing. Since it can be driven by an electric motor that can be used, if a gear pump is used, delicate control of the discharge amount and the suction amount of the molten metal can be easily performed. Furthermore, since the discharge amount and suction amount of the gear pump are not affected by the head, using the gear pump causes the discharge amount to fluctuate due to the change in the molten metal level in the lead melting tank, and the supply amount of molten metal into the mold is too short Can be prevented.
従って、上記のように鋳造装置を構成すると、鋳型の湯溜り溝内の溶湯レベルを上昇させて型凹部内の溶湯レベルを過剰レベルまで上昇させた後、該溶湯レベルを下降させる際に溶湯レベルの制御を精度よく行うことができ、鋳型のキャビティ内に極板群の耳部を挿入した後、溶湯レベルを堰の上端のレベル以下のレベルまで速やかに、かつ正確に下降させることができる。従って、鋳造されるストラップの厚みが過剰になるのを確実に防ぐことができ、キャビティの形状通りの形状を有するストラップを正確に鋳造することができる。 Therefore, when the casting apparatus is configured as described above, the molten metal level in the mold puddle groove is raised to raise the molten metal level in the mold recess to an excessive level, and then the molten metal level is lowered when the molten metal level is lowered. Can be accurately controlled, and the molten metal level can be quickly and accurately lowered to a level equal to or lower than the level of the upper end of the weir after the ear portion of the electrode plate group is inserted into the cavity of the mold. Therefore, it is possible to reliably prevent the thickness of the strap to be cast from becoming excessive, and it is possible to accurately cast the strap having the shape as the shape of the cavity.
また上記のように鋳造装置を構成すると、待機過程では、鉛溶解槽−ポンプ−溶湯レベル調整部−鉛溶解槽の経路で常時溶湯の循環流を生じさせておくことができるため、鉛溶解槽内で鉛合金の組成が不均一な部分が生じるのを防ぐことができ、鋳造されるストラップの品質が低下するのを防ぐことができる。 In addition, when the casting apparatus is configured as described above, in the standby process, a molten metal circulation flow can be always generated in the lead melting tank-pump-melt level adjusting unit-lead melting tank path. It is possible to prevent a portion having a non-uniform lead alloy composition from occurring, and to prevent deterioration of the quality of the cast strap.
上記の溶湯レベル調整部は、バルブが開いているときに湯溜り溝内の溶湯レベルを、溶湯流出口のレベルに等しくする作用をする。そのため、上記の溶湯レベル調整部は、溶湯流出口のレベル（高さ）を鋳型の湯溜り溝内における溶湯の規定レベルに一致させた状態で配置される。 The molten metal level adjusting unit functions to make the molten metal level in the hot water ditch groove equal to the level of the molten metal outlet when the valve is open. Therefore, the molten metal level adjusting unit is arranged in a state where the level (height) of the molten metal outlet matches the specified level of the molten metal in the molten metal groove of the mold.
上記溶湯レベル調整部においては、溶湯流出口の高さを調整し得るようにしておくのが好ましい。このように構成しておくと、湯溜り溝内の溶湯レベルを、ストラップの鋳造を適性に行うために適したレベルに容易に調整することができる。 In the molten metal level adjusting unit, it is preferable that the height of the molten metal outlet can be adjusted. If comprised in this way, the molten metal level in a hot water ditch | groove can be easily adjusted to the level suitable in order to perform casting of a strap appropriately.
本発明に係わる鉛蓄電池用極板ストラップ鋳造方法は、上記の鋳造装置を用いて、鉛蓄電池の極板群の同極性の極板の耳部同士を接続するストラップを鋳造する方法であって、本発明においては、バルブを開いた状態でギアポンプを正方向に連続回転させて湯溜り溝内の溶湯レベルを規定レベルに保つ待機過程と、バルブを閉じた状態でギアポンプを正方向に回転させることにより湯溜り溝内の溶湯レベルを上昇させて湯溜り溝内の溶湯を堰を越えてキャビティ内に流入させ、最終的には型凹部内の溶湯レベルを堰の上端のレベル以上のレベルまで上昇させる溶湯レベル上昇過程と、バルブを開き、湯溜り溝内の溶湯レベルが堰の上端レベル以下のレベルまで低下するまでの間ギアポンプを逆方向に回転させて溶湯レベル上昇過程で上昇した溶湯レベルを下降させる溶湯レベル下降過程とを行わせて、溶湯レベル下降過程で型凹部内の溶湯レベルが極板群の耳部を溶湯中に挿入しても型凹部から溶湯があふれることがないレベルまで低下したときに極板群の耳部をキャビティ内の溶湯中に挿入し、溶湯レベル下降過程で湯溜り溝内の溶湯レベルが規定レベルまたは設定レベルまで低下したときにギアポンプの回転方向を逆方向から正方向に反転させて待機過程に移行させる。そして、キャビティ内の溶湯を凝固させることによりストラップを鋳造する。 An electrode plate strap casting method for a lead storage battery according to the present invention is a method of casting a strap for connecting the ears of the same polarity electrode plates of the electrode plate group of the lead storage battery using the above casting apparatus, In the present invention, the gear pump is continuously rotated in the forward direction while the valve is open, and the gear pump is rotated in the forward direction while the valve is closed while the molten metal in the sump groove is kept at the specified level. To raise the level of molten metal in the puddle groove and flow the molten metal in the puddle groove over the weir into the cavity, and finally raise the molten metal level in the mold recess to a level higher than the level at the top of the weir. As the melt level rises, the valve is opened and the gear pump is rotated in the reverse direction until the melt level in the sump groove drops to a level below the upper end level of the weir. Even if the molten metal level in the mold depression is inserted into the molten metal in the molten metal level in the molten metal level lowering process, the molten metal does not overflow from the concave mold. Insert the ears of the electrode plate group into the molten metal in the cavity when the level drops to the level, and change the gear pump rotation direction when the molten metal level in the molten metal groove drops to the specified level or set level during the molten metal level lowering process. Invert from the reverse direction to the forward direction and shift to the standby process. Then, the strap is cast by solidifying the molten metal in the cavity.
上記の方法を自動的に実施するため、本発明に係わる鋳造装置には、バルブを開いた状態でギアポンプを正方向に連続回転させて湯溜り溝内の溶湯レベルを規定レベルに保つ待機過程と、バルブを閉じた状態でギアポンプを正方向に回転させることにより湯溜り溝内の溶湯レベルを上昇させて湯溜り溝内の溶湯を堰を越えてキャビティ内に流入させ、最終的には型凹部内の溶湯レベルを堰の上端のレベル以上の過剰レベルまで上昇させる溶湯レベル上昇過程と、バルブを開いた状態でギアポンプを逆方向に回転させて溶湯レベル上昇過程で上昇した溶湯レベルを低下させる溶湯レベル下降過程とを行わせ、溶湯レベル下降過程で前記湯溜り溝内の溶湯レベルが堰の上端レベル以下のレベルまで低下したときにギアポンプの回転方向を逆方向から正方向に反転させて待機過程に移行させるようにバルブ及びギアポンプを制御する制御部を設けておくのが好ましい。 In order to automatically carry out the above method, the casting apparatus according to the present invention includes a standby process in which the gear pump is continuously rotated in the forward direction with the valve opened to maintain the molten metal level in the puddle groove at a specified level. By rotating the gear pump in the forward direction with the valve closed, the level of the molten metal in the puddle groove is raised to flow the molten metal in the puddle groove over the weir into the cavity, and finally the mold recess The melt level rise process that raises the molten metal level to the excess level above the top level of the weir and the melt level that rises in the melt level rise process by rotating the gear pump in the reverse direction with the valve open When the molten metal level in the hot water ditch is lowered to a level below the upper end level of the weir during the molten metal level decreasing process, the rotation direction of the gear pump is reversed. The preferably provided a control unit for controlling the valves and gear pump as is reversed to shift to the standby process in the positive direction is preferred.
上記の各過程は、鋳型内の溶湯レベルを検出するレベルセンサを設けて、レベルセンサにより検出される溶湯レベルを規定レベルや設定レベルに一致させるようにギアポンプを制御することにより行わせることができる。レベルセンサとしては、超音波式や静電式等の非接触式のセンサを用いるのが好ましい。 Each of the above processes can be performed by providing a level sensor for detecting the melt level in the mold and controlling the gear pump so that the melt level detected by the level sensor matches the specified level or the set level. . As the level sensor, it is preferable to use a non-contact type sensor such as an ultrasonic type or an electrostatic type.
ギアポンプの吐出量及び吸い込み量は、揚程の影響を受けず、ギアポンプの回転速度とギアポンプの単位回転角度当たりの吐出量とから正確に計算することができ、鋳型内の溶湯レベルを所定のレベルにするために必要なギアポンプの駆動タイミング及び駆動時間は演算により正確に求めることができるため、上記の鋳造方法の各過程は、バルブ及びギアポンプを駆動するタイミングとギアポンプを駆動する時間とを管理することにより正確に行うことができる。このように、ギアポンプを駆動するタイミングと駆動する時間とを管理することにより各工程を行わせるようにすれば、溶湯レベルを検出するセンサを設けることなく、バルブ及びギアポンプを駆動するタイミングを所定のシーケンスで制御するだけで、各工程を行わせることができる。 The discharge amount and suction amount of the gear pump are not affected by the head, and can be accurately calculated from the rotation speed of the gear pump and the discharge amount per unit rotation angle of the gear pump, and the molten metal level in the mold is set to a predetermined level. Since the driving timing and driving time of the gear pump necessary for the above can be accurately calculated by calculation, each process of the casting method described above manages the timing for driving the valve and the gear pump and the time for driving the gear pump. Can be performed more accurately. Thus, if each process is performed by managing the timing for driving the gear pump and the driving time, the timing for driving the valve and the gear pump can be set to a predetermined level without providing a sensor for detecting the melt level. Each process can be performed only by controlling in sequence.
そのため、本発明に係わる鋳造方法の好ましい態様では、前記の構成を有する鉛蓄電池用極板ストラップ鋳造装置を用いて、バルブを開いた状態でギアポンプを正方向に連続回転させて湯溜り溝内の溶湯レベルを規定レベルに保つ待機過程と、型凹部内の溶湯レベルを前記堰の上端のレベル以上に設定された過剰レベルまで上昇させるために必要な時間の間バルブを閉じた状態でギアポンプを正方向に回転させて前記型凹部内の溶湯レベルを上昇させる溶湯レベル上昇過程と、溶湯レベル上昇過程が終了した後バルブを開いた状態で湯溜り溝内の溶湯レベルを堰の上端レベル以下のレベルまで低下させるために必要な時間の間ギアポンプを逆方向に回転させて型凹部内の溶湯レベルを下降させる溶湯レベル下降過程とを行わせて、溶湯レベル下降過程で型凹部内の溶湯レベルが極板群の耳部を溶湯中に挿入しても型凹部から溶湯があふれることがないレベルまで低下するタイミングで極板群の耳部をキャビティ内の溶湯中に挿入し、溶湯レベル下降過程が終了した後にギアポンプの回転方向を逆方向から正方向に反転させて待機過程に移行させる。キャビティ内の溶湯を硬化させることによりストラップを鋳造する。 Therefore, in a preferred embodiment of the casting method according to the present invention, using the electrode storage strap casting apparatus for a lead storage battery having the above-described configuration, the gear pump is continuously rotated in the forward direction with the valve opened, and the inside of the puddle groove is Waiting process to keep the molten metal level at the specified level, and the gear pump with the valve closed for the time required to raise the molten metal level in the mold recess to the excess level set above the top level of the weir. The molten metal level rising process in which the molten metal level in the mold recess is increased by rotating in the direction of the mold, and the molten metal level in the hot water ditching groove is lower than the upper end level of the weir with the valve opened after the molten metal level increasing process is completed. The melt level is lowered by rotating the gear pump in the opposite direction for the time required to lower the melt level to lower the melt level in the mold recess. During the descending process, the molten metal level in the mold recess is lowered to a level at which the molten metal does not overflow from the mold recess even if the molten metal is inserted into the molten metal. After the molten metal level lowering process is completed, the rotation direction of the gear pump is reversed from the reverse direction to the forward direction to shift to the standby process. The strap is cast by curing the molten metal in the cavity.
上記の鋳造方法を自動的に実施するため、本発明に係わる鋳造装置には、バルブを開いた状態でギアポンプを正方向に連続回転させて前記湯溜り溝内の溶湯レベルを規定レベルに保つ待機過程と、湯溜り溝内の溶湯レベルを堰を越えてキャビティ内に流入させてキャビティ内を溶湯で満たした状態にするために必要な時間の間バルブを閉じた状態でギアポンプを正方向に回転させて型凹部内の溶湯レベルを上昇させる溶湯レベル上昇過程と、溶湯レベル上昇過程が終了した後バルブを開いた状態で湯溜り溝内の溶湯レベルを堰の上端レベル以下のレベルまで低下させるために必要な時間の間ギアポンプを逆方向に回転させて型凹部内の溶湯レベルを下降させる溶湯レベル下降過程とを行わせ、溶湯レベル下降過程が終了した後にギアポンプの回転方向を逆方向から正方向に反転させて待機過程に移行させるようにバルブ及びギアポンプを制御する制御部を設けるのが好ましい。 In order to automatically carry out the above casting method, the casting apparatus according to the present invention has a standby state in which the gear pump is continuously rotated in the forward direction with the valve opened to maintain the molten metal level in the hot water ditch groove at a specified level. Rotate the gear pump in the forward direction with the valve closed for the time required for the process and the level of the melt in the puddle groove to flow into the cavity past the weir and fill the cavity with the melt. In order to lower the molten metal level in the hot water ditch groove to a level below the upper end level of the weir with the valve opened after the molten metal level increasing process to raise the molten metal level in the mold recess and the molten metal level rising process is completed The gear pump is rotated in the opposite direction for the time required for the melt to lower the melt level in the mold recess and the melt level lowering process is performed. Preferably, the rolling direction from the reverse direction is reversed in the forward direction is provided a control unit for controlling the valves and gear pump so as to shift to the standby process.
鋳型内への溶湯の供給を迅速に行わせるため、上記制御部は、待機過程ではギアポンプを第１の回転速度で正方向に回転させ、溶湯レベル上昇過程ではギアポンプを第１の回転速度よりも高い第２の回転速度で正方向に回転させ、溶湯レベル下降過程ではギアポンプを逆方向に回転させるように構成するのが好ましい。 In order to promptly supply the molten metal into the mold, the control unit rotates the gear pump in the forward direction at the first rotational speed in the standby process, and the gear pump is operated at a speed higher than the first rotational speed in the molten metal level increasing process. It is preferable to rotate the gear pump in the forward direction at a high second rotation speed and to rotate the gear pump in the reverse direction in the process of lowering the melt level.
本発明に係わる鉛蓄電池の製造方法では、正極板と負極板とをセパレータを介して積層して鉛蓄電池用の極板群を構成する極板群構成工程と、上記のいずれかの鋳造方法により極板群の同極性の極板の耳部同士を接続するストラップを鋳造するストラップ鋳造工程と、ストラップが鋳造された極板群を電槽内に収容してセル間を接続し、該電槽内に電解液を注入する組立工程とを行って鉛蓄電池を製造する。 In the method for manufacturing a lead storage battery according to the present invention, the positive electrode plate and the negative electrode plate are laminated via a separator to form an electrode plate group for a lead storage battery, and any one of the above casting methods. A strap casting process for casting a strap for connecting the ears of the same polarity electrode plates of the electrode plate group, and the electrode plate group in which the strap is cast is accommodated in the battery case, and the cells are connected to each other. A lead storage battery is manufactured by performing an assembly process of injecting an electrolytic solution into the inside.
本発明では、溶湯を吐出させることも吸い込むこともでき、溶湯の吐出量及び吸込み量の微妙なコントロールを容易に行うことができる上に、吐出量及び吸込み量が揚程の変化の影響を受けないギアポンプを用いて溶湯を鋳型に供給するので、鋳型内に供給する溶湯に過不足が生じるのを防ぐことができる。 In the present invention, the molten metal can be discharged or sucked, and the delicate control of the molten metal discharge amount and the suction amount can be easily performed, and the discharge amount and the suction amount are not affected by the change in the head. Since the molten metal is supplied to the mold using the gear pump, it is possible to prevent the molten metal supplied into the mold from being excessive or insufficient.
また本発明においては、鋳型の湯溜り溝内の溶湯レベルを上昇させて型凹部内の溶湯レベルを過剰レベルまで上昇させた後、ギアポンプを逆方向に回転させることにより溶湯レベルを強制的に下降させるので、鋳型のキャビティ内に極板群の耳部を挿入した後、溶湯レベルを堰の上端レベル以下のレベルまで速やかに、かつ正確に下降させることができる。従って本発明によれば、鋳造されるストラップの厚みが過剰になるのを確実に防ぐことができ、キャビティの形状通りの形状を有するストラップを正確に鋳造することができる。 In the present invention, the molten metal level in the mold pool is raised to raise the molten metal level in the mold recess to an excessive level, and then the gear pump is rotated in the reverse direction to forcibly lower the molten metal level. Therefore, after inserting the ear | edge part of an electrode group in the cavity of a casting_mold | template, a molten metal level can be fall | descended rapidly and correctly to the level below the upper end level of a weir. Therefore, according to the present invention, it is possible to reliably prevent the thickness of the strap to be cast from becoming excessive, and it is possible to accurately cast the strap having the shape as the shape of the cavity.
また本発明によれば、待機過程では、鉛溶解槽−ポンプ−溶湯レベル調整部−鉛溶解槽の経路で常時溶湯の循環流を生じさせておくことができるため、溶湯供給路５内で溶湯が冷却されて凝固するおそれを無くすことができ、溶湯供給路内で溶湯が凝固することによりストラップの鋳造工程を停止せざるを得ない事態が生じるのを防ぐことができる。また鉛溶解槽内で常時溶湯の流動を生じさせておくことができるため、鉛溶解槽内で溶湯の表面の酸化が進んで鉛合金の組成が不均一な部分が生じるのを防ぐことができ、鉛合金の組成が不均一になることにより鋳造されるストラップの品質が低下するのを防ぐことができる。 Further, according to the present invention, in the standby process, a molten metal circulation flow can be constantly generated through the route of the lead melting tank-pump-melt level adjusting unit-lead melting tank. It is possible to eliminate the possibility that the strap is cooled and solidified, and the situation in which the casting process of the strap has to be stopped due to the solidification of the molten metal in the molten metal supply path can be prevented. Moreover, since the flow of the molten metal can be constantly generated in the lead melting tank, it is possible to prevent the surface of the molten metal from being oxidized in the lead melting tank and causing a portion where the composition of the lead alloy is not uniform. Further, it is possible to prevent the quality of the strap cast from being deteriorated due to the non-uniform composition of the lead alloy.
鉛蓄電池を製造する方法においては、正極板と負極板とをセパレータを介して積層して鉛蓄電池用の極板群を構成する極板群構成工程と、極板群の同極性の極板の耳部同士を接続するストラップを鋳造するストラップ鋳造工程と、ストラップが鋳造された極板群を電槽内に収容してセル間を接続し、該電槽内に電解液を注入する組立工程とを行う。本発明に係わるストラップ鋳造方法及び鋳造装置は、上記ストラップ鋳造工程でストラップを鋳造する際に用いる。 In the method of manufacturing a lead storage battery, a positive electrode plate and a negative electrode plate are laminated via a separator to form an electrode plate group forming step for forming a plate group for a lead storage battery; and A strap casting process for casting a strap for connecting the ears; an assembly process for housing the electrode plate group in which the strap is cast in the battery case, connecting the cells, and injecting an electrolyte into the battery case; I do. The strap casting method and casting apparatus according to the present invention are used when casting a strap in the strap casting step.
以下図面を参照して、本発明に係わるストラップ鋳造装置の好ましい実施形態を、同鋳造装置を用いて行うストラップ鋳造方法とともに詳細に説明する。
図１は、本発明に係わる鉛蓄電池用極板ストラップ鋳造装置の一実施形態の全体的な構成を示したものである。同図において、１はヒータ２により鉛合金を加熱して鉛合金の溶湯Ｍを生成する鉛溶解槽、３は鋳型、４は鉛溶解槽１内の溶湯Ｍを溶湯供給路５を通して鋳型３に供給するポンプ、６はポンプ４を駆動する駆動源、７はポンプ４と鋳型３との間を接続する溶湯供給路５の途中に設けられて鋳型３内の溶湯レベルを調整する溶湯レベル調整部である。
A preferred embodiment of a strap casting apparatus according to the present invention will be described below in detail with a strap casting method performed using the casting apparatus with reference to the drawings.
FIG. 1 shows the overall configuration of an embodiment of an electrode plate strap casting apparatus for a lead storage battery according to the present invention. In the figure, 1 is a lead melting tank in which a lead alloy is heated by a
図２に示したように、鋳型３は、ストラップを鋳造するためのキャビティ３０１と、キャビティ３０１に隣接配置されてキャビティ３０１との間が堰３０２により仕切られた湯溜り溝３０３と、キャビティ３０１及び湯溜り溝３０３の上方に形成された余剰溶湯収容空間３０４とからなる型凹部３０５と、湯溜り溝３０３より下方に設けられて湯溜り溝３０３内に連通路３０６を通して接続された湯道３０７とを備えている。湯道３０７の一端は外部に開口していて、この湯道の一端の開口部に溶湯供給路５を構成するパイプラインが接続される。湯道３０７の他端は閉鎖されていて、溶湯供給路５から湯道３０７内に溶湯が供給された際に、湯道３０７内の溶湯が連通路３０６を通して押し上げられて湯溜り３０３内に流入するようになっている。
As shown in FIG. 2, the
鋳型３は、堰３０２の厚み方向の中央部でキャビティ側ユニット３Ａと、湯溜り側ユニット３Ｂとに分割されていて、これらのユニットが断熱層３０９を介して相互に接合されることにより鋳型３が組立てられている。キャビティ側ユニット３Ａ内には冷却媒体を通す冷却媒体通路３１０が設けられ、この冷却媒体通路を通して流される冷却媒体により、キャビティ側ユニット３Ａが冷却される。また湯溜り側ユニット３Ｂ内に設けられた穴にヒータ３１１が挿入され、該ヒータにより湯溜り側ユニットが溶湯を溶融状態に保つために必要な温度まで加熱される。キャビティ側ユニット３Ａには、キャビティ３０１内で鋳造されたストラップを取り出す際に用いるノックアウトピン３０８が取り付けられている。
The
なお図２には、キャビティ３０１及び湯溜り３０３が一組だけ示されているが、極板群には正極板と負極板とがあり、正極板の耳部同士を接続する正極ストラップと負極板の耳部同士を接続する負極ストラップとの双方を鋳造する必要があるため、実際には、正極ストラップ及び負極ストラップをそれぞれ鋳造するために、２組のキャビティ３０１及び湯溜り３０３が正負極板の耳部の位置に対応して配置される。図２は鋳型の半部（一方の極性のストラップを鋳造する部分）のみを示している。実際には、図示のキャビティ側ユニット３Ａの左側に極板群の他方の極性のストラップを鋳造するための他のキャビティ側ユニットが配置され、該他のキャビティ側ユニットの左側に、他の湯溜り側ユニットが配置される。
FIG. 2 shows only one set of the
本発明においては、ポンプ４がギアポンプからなっている。ギアポンプは、図３に示すように、第１のギア収容室４０１と第２のギア収容室４０２とを対称に有するほぼ繭形のポンプハウジング４０３を備えていて、第１のギア収容室４０１及び第２のギア収容室４０２内にそれぞれ駆動ギア４０５及び従動ギア４０６が収容されている。駆動ギア４０５及び従動ギア４０６はそれぞれポンプハウジング４０３の側板に回転自在に支持された回転軸４０７及び４０８に取り付けられていて、第１のギア収容室４０１と第２のギア収容室４０２とがオーバラップする部分で互いに噛み合わされている。ポンプハウジング４０３の第１のギア収容室４０１と第２のギア収容室４０２とをつなぐ部分から駆動ギア４０５及び従動ギア４０６が並ぶ方向に対して直角な方向に沿って、互いに反対方向に突出するように第１のポート４０９及び第２のポート４１０が設けられている。ギアポンプ４の第１のポート４０９は鉛溶解槽１内の溶湯Ｍ中に開口させられ、第２のポート４１０は溶湯供給路５の一部を構成するパイプライン５０１と、溶湯レベル調整部７と、溶湯供給路５の他の部分を構成するパイプライン５０２とを通して鋳型３の湯道３０７に接続されている。ギアポンプ４を駆動する駆動源６は電動機からなり、該電動機によりギアポンプ４の駆動ギア４０５が回転駆動される。
In the present invention, the pump 4 is a gear pump. As shown in FIG. 3, the gear pump includes a substantially bowl-shaped
図示のギアポンプは、駆動ギア４０５が図３において時計方向（この方向を正方向とする。）に回転したときに鉛溶解槽１内の溶湯Ｍを第１のポート４０９から吸い込んで第２のポート４１０から吐出させる。また駆動ギア４０５が図３において反時計方向（この方向を逆方向とする。）に回転したときに溶湯供給路５内の溶湯を吸い込んで鉛溶解槽１内に戻す。
The illustrated gear pump sucks the molten metal M in the lead melting tank 1 from the
ギアポンプ４は、ギアの回転方向を切り換えることにより、吐出方向を自由に切り換えることができるという特徴を有し、また吐出量が揚程の影響を受けないという特徴を有する。ギアポンプの単位回転角度当たりの吐出量及び吸込み量は、プランジャポンプのピストンの単位変位量当たりの吐出量及び吸込み量に比べて少ないため、吐出量及び吸込み量の微妙なコントロールが可能である。 The gear pump 4 has a feature that the discharge direction can be freely switched by switching the rotation direction of the gear, and the discharge amount is not affected by the head. Since the discharge amount and the suction amount per unit rotation angle of the gear pump are smaller than the discharge amount and the suction amount per unit displacement amount of the piston of the plunger pump, the discharge amount and the suction amount can be delicately controlled.
溶湯レベル調整部７は、溶湯供給路５の途中に挿入されて、鋳型内の溶湯レベルを調整する働きをする。図４ないし図６に示したように、本実施形態で用いる溶湯レベル調整部７は、直方体状に形成された金属ブロック７００を備え、金属ブロック７００内に上下方向に伸びる溶湯開放通路７０１と、横方向に伸びる溶湯流路７０５とが直交した状態で設けられている。溶湯開放通路７０１の下端はパイプライン５０１を通してギアポンプ４の第２のポート４１０に接続されている。溶湯流路７０５の一端は金属ブロック７００にねじ込まれたネジ７０６により閉鎖され、他端はパイプライン５０２を通して鋳型の湯道３０７に接続されている。
The melt
溶湯開放通路７０１は上端に開口部７０１ａを有している。溶湯開放通路７０１の上方には、溶湯開放通路７０１の上端の開口部の周縁部に当接して溶湯開放通路７０１の開口部７０１ａを閉じた状態にする閉位置と、溶湯開放通路の開口部７０１ａの周縁部から離れて該開口部を開いた状態にする開位置との間を上下に変位する弁棒７０２と、弁棒７０２を閉位置と開位置との間で変位させる弁棒駆動機構７０４（図１参照）とが設けられ、弁棒７０２と、弁棒駆動機構７０４とにより溶湯レベル調整バルブ７０３が構成されている。
The molten
金属ブロック７００の上端には、両端が水平方向に開口した溝７０７が設けられている。溝７０７の一端は、端板７１０により閉鎖されている。端板７１０は、溝７０７の両側にそれぞれ位置させて金属ブロック７００に固定されたスタッド７０８，７０８とこれらのスタッドに螺合されたナット７０９，７０９とにより金属ブロック７００に固定されている。
At the upper end of the
溝７０７の他端側には、溶湯流出口７１１を有するコの字形の流出口形成板７１２が、上下方向の位置を調整し得るようにして取り付けられている。流出口形成板７１２は、溝７０７の両側にそれぞれ位置させて金属ブロック７００に固定されたスタッド７１３，７１３とこれらのスタッドに螺合されたナット７１４，７１４とにより金属ブロック７００に取り付けられている。図４に示されているように、スタッド７１３，７１３を貫通させるために流出口形成板７１２に設けられた孔７１５は、上下方向に伸びる長孔となっている。従って、ナット７１４を緩めた状態で板７１２を上下に変位させることにより、溶湯流出口７１１のレベルを、長孔７１５の長さにより決まる一定の範囲内で調節することができる。
A U-shaped
図６に示したように、溶湯レベル調整部７は、溶湯流出口７１１のレベル（溶湯流出口の下端のレベル）が、鋳型３内の湯溜り溝３０３内に設定する溶湯の規定レベルＬ1に一致するように、その上下位置が調整された状態で配置される。
As shown in FIG. 6, the molten metal
湯溜り溝内の溶湯レベルを規定レベルＬ1に保つ際には、弁棒７０２を上昇させてバルブ７０３を開いておく。このとき溶湯レベル調整部７は、湯溜り溝３０３内の溶湯レベルが規定レベルＬ1を越えたときに溶湯開放通路７０１内の溶湯を溶湯流出口７１１から鉛溶解槽１内にオーバフローさせて湯溜り溝３０３内の溶湯レベルを規定レベルＬ1に保つ。また鋳型内の溶湯レベルを規定レベルを越えて上昇させる際には、バルブ７０３を閉じる。このとき溶湯のオーバフローが阻止されるため、溶湯レベル調整部７はギアポンプ４から湯道３０７への溶湯の供給に伴って湯溜り溝３０３内の溶湯レベルが規定レベルを越えて上昇するのを許容する。
When the molten metal level in the hot water storage groove is kept at the specified level L1, the
本発明に係わる鋳造方法では、待機過程と、溶湯レベル上昇過程と、溶湯レベル下降過程とを行い、溶湯レベル下降過程において、鋳型内の溶湯レベルが、極板群の耳部をキャビティ内に挿入しても溶湯が鋳型からあふれ出るおそれがないレベルまで低下したときに、キャビティ内に極板群の耳部を挿入してストラップの鋳造を行う。 In the casting method according to the present invention, a standby process, a molten metal level increasing process, and a molten metal level decreasing process are performed. In the molten metal level decreasing process, the molten metal level in the mold is inserted into the cavity of the electrode plate group. Even when the molten metal drops to a level where there is no risk of overflowing from the mold, the strap is cast by inserting the ear portion of the electrode plate group into the cavity.
待機過程では、溶湯レベル調整部７の弁棒７０２を上げてバルブ７０３を開いた状態でギアポンプ４を正方向に比較的低い第１の回転速度（例えば８０ｒｐｍ）で連続回転させることにより、図７に示すように、湯溜り溝３０３内の溶湯レベルを規定レベルＬ1に保ち、この状態で極板群１０が搬送されてきてキャビティの上方に位置決めされるのを待つ。
In the standby process, the
鋳型３の上方には、極板群構成工程で構成された極板群が、コンベアにより、その耳部を下方に向けた状態で搬送されてくる。鋳型３の上方に耳部１１を下方に向けた極板群１０が搬送されてきて、図７に示すように、キャビティ３０１の上方に対応する耳部１１が位置決めされた状態になったときに、溶湯レベル上昇過程を開始させる。溶湯レベル上昇過程では、溶湯レベル調整部７の弁棒７０２を下げてバルブ７０３を閉じた状態にし、ギアポンプ４の回転速度を第１の回転速度よりも高い第２の回転速度（例えば１６０ｒｐｍ）まで上昇させて、型凹部３０５内の溶湯レベルを堰３０２の上端のレベル以上に設定された過剰レベルまで上昇させるために必要な時間の間ギアポンプ４を正方向に回転させる。これにより、湯溜り溝３０３内の溶湯レベルを上昇させ、溶湯Ｍを堰３０２を越えてキャビティ３０１内に流入させる。溶湯がキャビティ３０１内を満たした後も溶湯レベルの上昇を継続させ、最終的に溶湯レベルを堰３０２の上端のレベル以上に設定された過剰レベルまで上昇させる。本実施形態では、型凹部３０５の上端の開口部のレベルを過剰レベルＬ2（図８参照）としている。図８に示した例では、型凹部内に過剰レベルＬ2まで供給された溶湯Ｍの表面が表面張力で盛り上がった状態にある。
Above the
溶湯レベル上昇過程で溶湯レベルを過剰レベルＬ2まで上昇させた後、溶湯レベル下降過程に移行する。溶湯レベル下降過程では、弁棒７０２を上げてバルブ７０３を開いた状態にすると同時に、ギアポンプ４の回転方向を反転させて、湯溜り溝３０３内の溶湯レベルを堰３０２の上端レベル以下のレベルまで低下させるために必要な時間の間ギアポンプ４を逆方向に回転させて、溶湯供給路５内の溶湯をポンプ４で吸い込むことにより、型凹部内の溶湯レベルを強制的に下降させる。
After the molten metal level is raised to the excess level L2 in the molten metal level increasing process, the process proceeds to the molten metal level decreasing process. In the molten metal level lowering process, the
上記溶湯レベル下降過程において、型凹部内の溶湯レベルが極板群１０の耳部１１を溶湯中に挿入しても型凹部から溶湯があふれることがないレベルまで低下するタイミングで、極板群１０を保持している治具に下降指令を与えて、極板群１０の耳部１１をキャビティ３０１内の溶湯中に挿入する。極板群１０の耳部を溶湯中に挿入することにより型凹部内の溶湯レベルが再び上昇するが、ギアポンプ４が溶湯供給路５内の溶湯を吸い込むので、溶湯レベルは速やかに低下していく。図９に示すように、湯溜り溝３０３内の溶湯レベルが堰３０２の上端レベル以下のレベルまで低下したときに溶湯レベル下降過程を終了する。
In the molten metal level lowering process, at the timing when the molten metal level in the mold recess is lowered to such a level that the molten metal does not overflow from the mold recess even when the
溶湯レベル下降過程を終了した後、ギアポンプ４の回転方向を逆方向から正方向に反転させて待機過程に移行させる。溶湯レベル下降過程においてギアポンプ４を逆方向に回転させる時間は、極板群の耳部１１をキャビティ３０１内に挿入した際に生じる溶湯レベルの再上昇を考慮して設定しておく。
After the melt level lowering process is completed, the rotation direction of the gear pump 4 is reversed from the reverse direction to the forward direction to shift to the standby process. The time for rotating the gear pump 4 in the reverse direction in the process of lowering the melt level is set in consideration of the re-rise of the melt level that occurs when the
溶湯レベル下降過程の終了時にギアポンプ４の回転方向を正方向に反転させる処理を行っても、ポンプは直ちには反転しないため、湯溜まり溝３０３内の溶湯レベルが規定レベルＬ1に達するまでギアポンプ４を逆方向に駆動してからその回転方向を反転させるようにすると、湯溜り溝内の溶湯レベルが規定レベルよりも低いレベルまで低下するおそれがある。湯溜り溝内の溶湯レベルが規定レベルよりも低いレベルまで低下するおそれを無くすためには、湯溜り溝３０３内の溶湯レベルが規定レベルＬ1よりも僅かに高く設定された設定レベルに達したときにギアポンプ４を反転させる処理を行うようにするのが好ましい。
Even if the process of reversing the rotational direction of the gear pump 4 to the positive direction at the end of the molten metal level lowering process is performed, the pump does not reverse immediately. Therefore, the gear pump 4 is kept until the molten metal level in the hot
鋳造されるストラップの厚みが過剰になるのを防ぐためには、できるだけ速やかに湯溜り内の溶湯レベルを堰３０２の上端レベル以下のレベルまで下げる必要がある。従って上記設定レベルは堰３０２の上端レベルと規定レベルＬ1との間に設定するのが好ましい。
In order to prevent the thickness of the cast strap from becoming excessive, it is necessary to lower the molten metal level in the hot water pool to a level below the upper end level of the
キャビティ３０１内の溶湯が凝固してストラップ１２が鋳造された後に、図１０に示すようにノックアウトピン３０８を上昇させて鋳造されたストラップ１２を鋳型から外し、ストラップが鋳造された極板群１０をコンベアにより次の工程（組立工程）に搬送する。
After the molten metal in the
上記のように、本実施形態では、溶湯を吐出させることも吸い込むこともでき、溶湯の吐出量及び吸込み量の微妙なコントロールを容易に行うことができる上に、吐出量及び吸込み量が揚程の変化の影響を受けないギアポンプ４を用いて鉛溶解槽１から鋳型３に溶湯を供給するため、鋳型内に供給する溶湯に過不足が生じるのを防ぐことができる。
As described above, in the present embodiment, the molten metal can be discharged or sucked, and the discharge amount and the suction amount of the molten metal can be easily controlled, and the discharge amount and the suction amount are high. Since the molten metal is supplied from the lead melting tank 1 to the
また本実施形態においては、鋳型３の湯溜り溝３０３内の溶湯レベルを上昇させて型凹部内の溶湯レベルを過剰レベルまで上昇させた後、ギアポンプ４を逆方向に回転させることにより溶湯レベルを強制的に下降させるので、鋳型のキャビティ３０１内に極板群の耳部１１を挿入した後、溶湯レベルを堰３０２の上端レベル以下のレベルまで速やかに、かつ正確に下降させることができる。従って、鋳造されるストラップの厚みが過剰になるのを確実に防ぐことができ、キャビティの形状通りの形状を有するストラップを正確に鋳造することができる。
In the present embodiment, the melt level in the hot
また本実施形態では、待機過程で、鉛溶解槽１−ポンプ４−溶湯レベル調整部７−鉛溶解槽１の経路で常時溶湯の循環流を生じさせておくことができるため、溶湯供給路５を構成するパイプラインの内、ポンプ４と溶湯レベル調整部７との間を接続するパイプライン５０１内で溶湯が冷却されて凝固するおそれを無くすことができ、溶湯供給路内で溶湯が凝固することによりストラップの鋳造工程を停止せざるを得ない事態が生じるのを防ぐことができる。また鉛溶解槽１内で常時溶湯の流動を生じさせておくことができるため、鉛溶解槽内で溶湯の表面の酸化が進んで鉛合金の組成が不均一な部分が生じるのを防ぐことができ、鉛合金の組成が不均一になることにより鋳造されるストラップの品質が低下するのを防ぐことができる。
Moreover, in this embodiment, since it is possible to always cause a circulating flow of the molten metal through the route of the lead melting tank 1 -pump 4 -melt level adjusting unit 7 -lead melting tank 1 in the standby process, the molten
上記の鋳造方法を自動的に実施するため、本発明に係わる鋳造装置には、図１１に示すようにバルブ７０３を制御するバルブ制御部１５と、ギアポンプ４を制御するポンプ制御部１６とを備えた制御部１７を設けておくのが好ましい。
In order to automatically perform the above casting method, the casting apparatus according to the present invention includes a valve control unit 15 for controlling the
この制御部１７は、バルブ７０３を開いた状態でギアポンプ４を正方向に連続回転させて湯溜り溝３０３内の溶湯レベルを規定レベルに保つ待機過程と、バルブ７０３を閉じた状態でギアポンプ４を正方向に回転させることにより湯溜り溝内の溶湯レベルを上昇させて湯溜り溝内の溶湯を堰３０２を越えてキャビティ３０１内に流入させ、最終的には型凹部内の溶湯レベルを堰７０２の上端のレベル以上の過剰レベルまで上昇させる溶湯レベル上昇過程と、バルブ７０３を開いた状態でギアポンプ４を逆方向に回転させることにより溶湯レベル上昇過程で上昇した溶湯レベルを低下させて、湯溜り溝３０３内の溶湯レベルが堰３０２の上端レベル以下になったときにギアポンプの回転方向を逆方向から正方向に反転させる溶湯レベル下降過程とを行うようにバルブ７０３及びギアポンプ４を制御するとともに、溶湯レベル下降過程でキャビティ内に極板群の耳部を挿入しても型凹部から溶湯があふれ出るおそれがないレベルまで型凹部内の溶湯レベルが低下したときに極板群の耳部をキャビティ内に挿入することを指令する極板耳部降下指令を発生させるように構成される。
The
上記の各過程における溶湯レベルの制御は、鋳型内の溶湯レベルを検出するレベルセンサを設けて、レベルセンサにより検出される溶湯レベルを規定レベルや設定レベルに一致させるようにギアポンプを制御することにより行わせてもよく、上記の実施形態の説明で述べたように、バルブ７０３及びギアポンプ４を駆動するタイミングとギアポンプを駆動する時間とを管理することにより行ってもよい。
The control of the molten metal level in each of the above processes is performed by providing a level sensor for detecting the molten metal level in the mold and controlling the gear pump so that the molten metal level detected by the level sensor matches the specified level or the set level. Alternatively, as described in the above description of the embodiment, the timing for driving the
バルブ７０３及びギアポンプ４を駆動するタイミングとギアポンプを駆動する時間とを管理することにより各過程を行う場合には、上記制御部１７が、バルブ７０３を開いた状態でギアポンプ４を正方向に連続回転させて湯溜り溝３０３内の溶湯レベルを規定レベルに保つ待機過程と、湯溜り溝３０３内の溶湯レベルを堰３０２を越えてキャビティ３０１内に流入させてキャビティ内を溶湯で満たした後溶湯レベルを堰の上端のレベルよりも高く設定された過剰レベルまで上昇させるために必要な時間の間バルブ７０３を閉じた状態でギアポンプ４を正方向に回転させて型凹部内の溶湯レベルを上昇させる溶湯レベル上昇過程と、溶湯レベル上昇過程が終了した後バルブを開いた状態で湯溜り溝内の溶湯レベルを堰の上端レベル以下のレベルまで低下させるために必要な時間の間ギアポンプを逆方向に回転させて型凹部内の溶湯レベルを下降させる溶湯レベル下降過程とを行わせて、溶湯レベル下降過程が終了した後にギアポンプの回転方向を逆方向から正方向に反転させて待機過程に移行させるようにバルブ７０３及びギアポンプ４を制御するとともに、溶湯レベル下降過程でキャビティ内に極板群の耳部を挿入しても型凹部から溶湯があふれ出るおそれがないレベルまで型凹部内の溶湯レベルが低下したときに極板群の耳部をキャビティ内に挿入することを指令する極板耳部降下指令を発生させるように構成される。
When performing each process by managing the timing for driving the
上記制御部は、コンピュータに所定のプログラムを実行させることにより実現することができる。図１２は、上記の制御部を構成するためにコンピュータに実行させるプログラムのアルゴリズムの一例を示したフローチャートである。このアルゴリズムに従う場合には、ステップＳ１でバルブ７０３を開き、ステップＳ２でギアポンプ４を第１の回転速度（低速度）で正方向に回転させて待機過程を行わせる。次いでステップＳ３で、現在のタイミングが溶湯レベルの上昇を開始するタイミング（レベル上昇開始タイミング）であるか否かを判定する。レベル上昇開始タイミングは、ストラップの鋳造に備えて極板群１０の耳部１１をキャビティ３０１の上方に位置決めする動作が完了したときのタイミング（例えば、極板群を搬送するコンベアが、極板群の位置決めを完了したことを示す位置決め完了信号を発生するタイミング）である。
The control unit can be realized by causing a computer to execute a predetermined program. FIG. 12 is a flowchart illustrating an example of an algorithm of a program that is executed by a computer to configure the control unit. When this algorithm is followed, the
ステップＳ３で現在のタイミングがレベル上昇開始タイミングではないと判定されたときには、レベル上昇開始タイミングが到来するのを待つ。ステップＳ３でレベル上昇開始タイミングであると判定されたときには、ステップＳ４に進んでバルブ７０３を閉じ、ステップＳ５でギアポンプ４の回転速度を第２の回転速度に上昇させて、ギアポンプを正方向に回転させる。これにより溶湯レベル上昇過程が開始される。
When it is determined in step S3 that the current timing is not the level rise start timing, the system waits for the level rise start timing to arrive. If it is determined in step S3 that the level increase start timing is reached, the process proceeds to step S4, the
次いでステップＳ６で現在のタイミングがレベル上昇終了タイミングであるか否かを判定する。レベル上昇終了タイミングは、ステップＳ４でバルブ７０３を閉じた後、湯溜り溝３０３内の溶湯レベルを堰３０２を越えてキャビティ３０１内に流入させてキャビティ内を溶湯で満たし、更に溶湯レベルを堰の上端のレベルよりも高く設定された過剰レベルまで上昇させるために必要な時間が経過したときのタイミングである。
Next, in step S6, it is determined whether or not the current timing is the level rise end timing. After the
ステップＳ６で現在のタイミングがレベル上昇終了タイミングであると判定されたときには、ステップＳ７に進んでバルブ７０３を開き、ステップＳ８でギアポンプ４の回転方向を反転させて、ギアポンプ４を一定の回転速度で逆方向に回転させる。これにより溶湯レベル上昇過程を終了し、溶湯レベル下降過程を開始する。
When it is determined in step S6 that the current timing is the level increase end timing, the process proceeds to step S7, the
次いでステップＳ９で現在のタイミングが極板耳部挿入タイミングであるか否かを判定する。極板耳部挿入タイミングは、極板群の耳部をキャビティ内に挿入しても溶湯が型凹部からあふれるおそれがないレベルまで溶湯レベルが低下したときのタイミングである。ステップＳ９で現在のタイミングが極板耳部挿入タイミングであると判定されたときにステップＳ１０に進んで極板耳部降下指令を発生し、極板群１０を下降させて耳部１１をキャビティ３０１内に挿入する。
Next, in step S9, it is determined whether or not the current timing is the electrode plate ear insertion timing. The electrode tab insertion timing is the timing when the molten metal level is lowered to a level at which the molten metal does not overflow from the mold recess even when the electrode tabs are inserted into the cavity. If it is determined in step S9 that the current timing is the electrode ear insertion timing, the process proceeds to step S10 to generate an electrode plate lowering command, and the
次いでステップＳ１１で現在のタイミングがレベル下降終了タイミングであるか否かを判定する。レベル下降終了タイミングは、ステップＳ８でギアポンプの逆方向への回転を開始した後、型凹部内の溶湯レベルを堰３０２の上端レベル以下のレベルまで低下させるために必要な時間が経過したときのタイミングである。
Next, in step S11, it is determined whether or not the current timing is the level lowering end timing. The level lowering end timing is the timing when the time necessary for lowering the molten metal level in the mold recess to a level lower than the upper end level of the
ステップＳ１１で現在のタイミングがレベル下降終了タイミングであると判定されたときに溶湯レベル下降過程を終了し、ステップＳ１２に進んで鋳造工程の稼働を休止させることを指令する鋳造工程稼動休止指令が発生しているか否かを判定する。その結果鋳造工程稼働休止指令が発生していない場合には、ステップＳ２に戻って待機過程に移行する。ステップＳ１２で鋳造工程稼働休止指令が発生していると判定されたときにはステップＳ１３でポンプを停止させてこのプログラムを終了する。 When it is determined in step S11 that the current timing is the level lowering end timing, a molten metal level lowering process is ended, and a casting process operation stop command is issued to instruct to stop the operation of the casting process by proceeding to step S12. It is determined whether or not. As a result, if the casting process operation stop command has not been generated, the process returns to step S2 and shifts to a standby process. If it is determined in step S12 that a casting process operation stop command has been issued, the pump is stopped in step S13 and the program is terminated.
上記の実施形態では、溶湯上昇過程における溶湯レベルの上限である溶湯の過剰レベルを、型凹部３０５の上端開口部のレベルに設定しているが、本発明はこのように過剰レベルを設定する場合に限定されない。本発明で用いるギアポンプ４は、その吐出量が揚程の変化の影響を受けないため、溶湯レベル上昇過程で鋳型に供給する溶湯の量にそれほど余裕を持たせておく必要はない。そのため、過剰レベルＬ2は、型凹部３０５の上端開口部と堰３０２の上端との間に設定してもよい。
In the above embodiment, the excessive level of the molten metal, which is the upper limit of the molten metal level in the molten metal rising process, is set to the level of the upper end opening of the
１ 鉛溶解槽
２ ヒータ
３ 鋳型
３０１ キャビティ
３０２ 堰
３０３ 湯溜り溝
３０４ 余剰溶湯収容空間
３０５ 型凹部
３０６ 連通路
３０７ 湯道
３０８ ノックアウトピン
３０９ 断熱層
３１０ 冷却媒体通路
４ ギアポンプ
４０１ 第１のギア収容室
４０２ 第２のギア収容室
４０３ ポンプハウジング
４０５ 駆動ギア
４０６ 従動ギア
４０７ 回転軸
４０８ 回転軸
４０９ 第１のポート
４１０ 第２のポート
５ 溶湯供給路
５０１ パイプライン
５０２ パイプライン
６ 駆動源
７ 溶湯レベル調整部
７０１ 溶湯開放通路
７０１ａ 開口部
７０２ 弁棒
７０３ バルブ
７０７ 溝
７１０ 端板
７１１ 溶湯流出口
７１２ 流出口形成板
７１５ 長孔
DESCRIPTION OF SYMBOLS 1
Claims (9)
鉛合金の溶湯を生成する鉛溶解槽と、
前記ストラップを鋳造するためのキャビティと該キャビティに隣接配置されて該キャビティとの間が堰により仕切られた湯溜り溝と前記キャビティ及び湯溜り溝の上方に形成された余剰溶湯収容空間とを有する型凹部と、前記湯溜り溝より下方に設けられて前記湯溜り溝内に接続された湯道とを備えた鋳型と、
前記鉛溶解槽内に開口させられた第１のポートと前記鋳型の湯道に溶湯供給路を通して接続された第２のポートとを有して、正方向に回転したときに前記鉛溶解槽内の溶湯を前記第２のポートから前記溶湯供給路内に吐出させ、逆方向に回転したときに前記溶湯供給路内の溶湯を吸引して前記第１のポートから前記鉛溶解槽内に吐出させるギアポンプと、
上端に開口部を有し下端が前記溶湯供給路に接続された溶湯開放通路と前記溶湯開放通路の上端の開口部を開閉するバルブと前記溶湯開放通路の開口部から流出した溶湯を前記鉛溶解槽内にオーバフローさせる溶湯流出口とを備えて、前記バルブが開いている状態では前記湯溜り溝内の溶湯レベルが規定レベルを越えたときに前記溶湯開放通路内の溶湯を前記溶湯流出口からオーバフローさせて前記湯溜り溝内の溶湯レベルを規定レベルに保ち、前記バルブが閉じているときには前記湯溜り溝内の溶湯レベルが規定レベルを越えて上昇するのを許容する溶湯レベル調整部と、
を備えた鉛蓄電池用極板ストラップ鋳造装置。 An electrode plate strap casting device for a lead storage battery that casts a strap that connects the ears of the same polarity electrode plates of the electrode plate group of the lead storage battery,
A lead melting tank for producing molten lead alloy;
A cavity for casting the strap, a hot water storage groove disposed adjacent to the cavity and partitioned by a weir, and an excess molten metal storage space formed above the cavity and the hot water storage groove. A mold provided with a mold recess and a runner provided below the puddle groove and connected to the puddle groove;
The lead melting tank has a first port opened in the lead melting tank and a second port connected to the runner of the mold through a molten metal supply path, and rotates in the forward direction. The molten metal in the molten metal supply path is discharged from the second port into the molten metal supply path, and the molten metal in the molten metal supply path is sucked and discharged from the first port into the lead melting tank when rotated in the reverse direction. A gear pump,
A molten metal release passage having an opening at the upper end and a lower end connected to the molten metal supply passage, a valve for opening and closing the upper opening of the molten metal release passage, and the molten metal flowing out from the opening of the molten metal release passage are dissolved in the lead. A molten metal outlet for overflowing the tank, and when the valve is open, the molten metal in the molten metal release passage is removed from the molten metal outlet when the molten metal level in the molten metal groove exceeds a specified level. A molten metal level adjusting unit that overflows to maintain the molten metal level in the hot water ditch groove at a specified level, and that allows the molten metal level in the hot water ditch groove to rise above a specified level when the valve is closed;
Electrode plate strap casting device for lead storage batteries.
請求項１に記載された鉛蓄電池用極板ストラップ鋳造装置を用い、
前記バルブを開いた状態で前記ギアポンプを正方向に連続回転させて前記湯溜り溝内の溶湯レベルを前記規定レベルに保つ待機過程と、前記バルブを閉じた状態で前記ギアポンプを正方向に回転させることにより前記湯溜り溝内の溶湯レベルを上昇させて前記湯溜り溝内の溶湯を前記堰を越えて前記キャビティ内に流入させ、最終的には前記型凹部内の溶湯レベルを前記堰の上端のレベル以上のレベルまで上昇させる溶湯レベル上昇過程と、前記バルブを開き、前記湯溜り溝内の溶湯レベルが前記堰の上端レベル以下のレベルまで低下するまでの間前記ギアポンプを逆方向に回転させて前記溶湯レベル上昇過程で上昇した溶湯レベルを下降させる溶湯レベル下降過程とを行わせ、
前記溶湯レベル下降過程で前記型凹部内の溶湯レベルが前記極板群の耳部を溶湯中に挿入しても前記型凹部から溶湯があふれることがないレベルまで低下したときに前記極板群の耳部を前記キャビティ内の溶湯中に挿入し、
前記溶湯レベル下降過程で前記湯溜り溝内の溶湯レベルが前記規定レベルまたは設定レベルまで低下したときに前記ギアポンプの回転方向を逆方向から正方向に反転させて前記待機過程に移行させ、
前記キャビティ内の溶湯を凝固させることにより前記ストラップを鋳造する鉛蓄電池用極板ストラップ鋳造方法。 A method of casting a strap for connecting the ears of electrode plates of the same polarity of the electrode plate group of a lead storage battery,
Using the electrode plate strap casting apparatus for a lead storage battery according to claim 1,
A standby process in which the gear pump is continuously rotated in the forward direction with the valve opened to maintain the molten metal level in the hot water ditch groove at the specified level, and the gear pump is rotated in the forward direction with the valve closed. As a result, the molten metal level in the puddle groove is raised so that the molten metal in the puddle groove flows over the weir and into the cavity, and finally the molten metal level in the mold recess is set to the upper end of the weir. The molten metal level is raised to a level equal to or higher than the level, and the valve is opened, and the gear pump is rotated in the reverse direction until the molten metal level in the hot water ditch is lowered to a level lower than the upper end level of the weir. And a molten metal level lowering process for lowering the molten metal level raised in the molten metal level rising process,
When the molten metal level in the mold recess is lowered to a level at which the molten metal does not overflow from the mold recess even when the ear portion of the electrode plate group is inserted into the molten metal in the molten metal level lowering process. Insert the ear into the molten metal in the cavity,
When the molten metal level in the molten metal groove is lowered to the specified level or set level in the molten metal level lowering process, the rotational direction of the gear pump is reversed from the reverse direction to the forward direction to shift to the standby process,
An electrode plate strap casting method for a lead storage battery, wherein the strap is cast by solidifying molten metal in the cavity.
請求項１に記載された鉛蓄電池用極板ストラップ鋳造装置を用い、
前記バルブを開いた状態で前記ギアポンプを正方向に連続回転させて前記湯溜り溝内の溶湯レベルを前記規定レベルに保つ待機過程と、前記型凹部内の溶湯レベルを前記堰の上端のレベル以上に設定された過剰レベルまで上昇させるために必要な時間の間バルブを閉じた状態でギアポンプを正方向に回転させて前記型凹部内の溶湯レベルを上昇させる溶湯レベル上昇過程と、溶湯レベル上昇過程が終了した後前記バルブを開いた状態で前記湯溜り溝内の溶湯レベルを前記堰の上端レベル以下のレベルまで低下させるために必要な時間の間前記ギアポンプを逆方向に回転させて前記型凹部内の溶湯レベルを下降させる溶湯レベル下降過程とを行わせ、
前記溶湯レベル下降過程で前記型凹部内の溶湯レベルが前記極板群の耳部を溶湯中に挿入しても前記型凹部から溶湯があふれることがないレベルまで低下するタイミングで前記極板群の耳部を前記キャビティ内の溶湯中に挿入し、
前記溶湯レベル下降過程が終了した後に前記ギアポンプの回転方向を逆方向から正方向に反転させて前記待機過程に移行させ、
前記キャビティ内の溶湯を凝固させることにより前記ストラップを鋳造する鉛蓄電池用極板ストラップ鋳造方法。 A method of casting a strap for connecting the ears of electrode plates of the same polarity of the electrode plate group of a lead storage battery,
Using the electrode plate strap casting apparatus for a lead storage battery according to claim 1,
A standby process in which the gear pump is continuously rotated in the forward direction with the valve opened to maintain the molten metal level in the hot water ditch groove at the specified level, and the molten metal level in the mold recess is equal to or higher than the upper end level of the weir. A melt level increasing process in which the gear pump is rotated in the forward direction while the valve is closed for the time necessary to increase to the excessive level set in the above, and the molten metal level in the mold recess is increased, and the molten metal level increasing process When the valve is opened, the gear recess is rotated in the reverse direction for a time required to lower the molten metal level in the hot water ditch to a level lower than the upper end level of the weir. A molten metal level lowering process for lowering the molten metal level inside,
In the process of lowering the molten metal level, the molten metal level in the mold recess decreases to a level at which the molten metal does not overflow from the mold recess even when the ear portion of the electrode plate group is inserted into the molten metal. Insert the ear into the molten metal in the cavity,
After the molten metal level lowering process is completed, the rotational direction of the gear pump is reversed from the reverse direction to the forward direction to shift to the standby process,
An electrode plate strap casting method for a lead storage battery, wherein the strap is cast by solidifying molten metal in the cavity.
前記ストラップ鋳造工程では、請求項６ないし８のいずれか１つに記載された鋳造方法により前記ストラップを鋳造する鉛蓄電池の製造方法。 A positive electrode plate and a negative electrode plate are laminated via a separator to form an electrode plate group forming step for a lead storage battery, and a strap for connecting the ears of the electrode plates of the same polarity of the electrode plate group. A lead-acid battery is manufactured by carrying out a casting process of casting a strap and an assembly process in which a group of electrode plates on which the strap is cast is accommodated in a battery case, and the cells are connected to each other, and an electrolytic solution is injected into the battery case. A method for manufacturing a lead storage battery, wherein, in the strap casting step, the strap is cast by the casting method according to any one of claims 6 to 8.